JP2005028618A - Manufacturing method of surface protective film - Google Patents
Manufacturing method of surface protective film Download PDFInfo
- Publication number
- JP2005028618A JP2005028618A JP2003193451A JP2003193451A JP2005028618A JP 2005028618 A JP2005028618 A JP 2005028618A JP 2003193451 A JP2003193451 A JP 2003193451A JP 2003193451 A JP2003193451 A JP 2003193451A JP 2005028618 A JP2005028618 A JP 2005028618A
- Authority
- JP
- Japan
- Prior art keywords
- polyethylene
- protective film
- film
- surface protective
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】
【発明の属する技術分野】
本発明は、光学製品用樹脂フィルム、樹脂シート又は樹脂板等の表面に仮着させ、これらの表面を保護するとともに、これらをロール状に巻き取ったり、又は積み重ねた際にブロッキングすることを防止する効果を併せ持つポリエチレン系表面保護フィルム及びその製造方法に関する。
【0002】
【従来の技術】
従来表面保護フィルムは、樹脂板、金属板等(以下被着物という)の運搬、保管や加工時に異物の混入を防止したり、表面に傷がついたりすることを防止するために被着物の表面に仮着され、被着物が製品として使用される時には用済みとなり剥離除去される。したがって表面保護フィルムには、被着物との密着性又は粘着性が必要であるとともに、剥離させた時には被着物に表面保護フィルムの成分が残存付着していないことが要求される。
【0003】
近年、液晶基盤ガラス、液晶表示用偏光フィルム、薄型表示装置フィルム、位相差フィルム、光拡散シート、DVD等の光ディスク構成フィルムや、電子・光学用途向け精密ファインコート面板等の光学製品の開発が進展している。これらの光学製品は非常に緻密な構造制御がなされるものが多く、傷や異物に対して非常に敏感である。また例えば光学フィルムをロール状に巻き取ると、光学フィルム自身がブロッキングを起こすという問題が生じている。従ってこれらの光学製品用の表面を保護すると同時にブロッキングを防止する表面保護フィルムが求められている。
さらに環境問題の観点から、剥離された大量の表面保護フィルムは何らかの形で再利用されることが好ましく、単一樹脂で構成された表面保護フィルムが求められている。
【0004】
従来からポリエチレン系の表面保護フィルムはよく知られている。そのひとつの例として、熱可塑性樹脂からなる基材層の片面に、エチレン−酢酸ビニル共重合体(EVA)と特定のポリエチレン系樹脂との混合物が積層された表面保護フィルムが知られており、加熱による粘着力の上昇問題を解決し、フィッシュアイ発生による被保護物のへこみや気泡の巻込等の問題を生じないことが開示されている(例えば、特許文献1参照。)。
【0005】
また、特定のエチレン・α−オレフィン共重合体と低密度ポリエチレン又は高密度ポリエチレンとの組成物からなる表面保護フィルムが、粘着性に優れ、保護される物品への汚染性が少なく透明性にも優れることが開示されている(例えば、特許文献2参照。)。
【0006】
【特許文献1】
特開平9−132764号公報
【特許文献2】
特開平11−228755号公報
【0007】
【発明が解決しようとする課題】
しかし、上記の表面保護フィルムでは、前述したブロッキング防止性やリサイクル性の要求を満足させることは難しい。すなわち、エチレン−酢酸ビニル共重合体と特定のポリエチレン系樹脂を用いたものでは単一樹脂としてリサイクルすることが困難であり、またエチレン−酢酸ビニル共重合体は残存付着物を発生しやすいという問題点が存在する。また特定のエチレン・α−オレフィン共重合体と低密度ポリエチレン又は高密度ポリエチレンとの組成物からなる表面保護フィルムにおいてはブロッキング防止効果について何ら開示されていない。
【0008】
本発明は、使用後のリサイクルが可能なように、樹脂としてポリエチレンのみに限定し、被着物との密着性又は粘着性を満足し、かつ被着物のブロッキングを防止可能なポリエチレン表面保護フィルム及びその製造方法を提供することを目的とする。
【0009】
【課題を解決するための手段】
本発明者らは全てポリエチレンからなり、被着物への貼り合わせができ、かつ被着物に貼り合わせられた後、ロールフィルム状に巻き取られたり、又は積み重ねられたりしてもブロッキングすることがないポリエチレン表面保護フィルムを提供するための手段として鋭意検討した結果、ある条件を満たす樹脂、加工条件において本目的を達成できることを見出し本発明に到達したものである。すなわち、本発明は次のとおりである。
【0010】
(1)Tダイから溶融押出しされた単層又は2層以上からなるポリエチレン溶融膜を巻き取るポリエチレン表面保護フィルムの製造方法において、該ポリエチレン溶融膜が、Tダイから押し出された後、冷却ロール表面の粗さが十点平均粗さRzで0.5μm以下である鏡面冷却ロールと表面がゴムである押し付けロールとで挟まれることを特徴とする、ポリエチレン表面保護フィルムの製造方法。
【0011】
(2)ポリエチレン溶融膜の、冷却ロールに接触する層を構成するポリエチレンが、スウェル比が1.45以下である低密度ポリエチレンであり、270℃以上の温度でTダイから溶融膜が押し出されることを特徴とする(1)記載のポリエチレン表面保護フィルムの製造方法。
【0012】
(3)(1)又は(2)のいずれかの方法により得られたポリエチレン表面保護フィルム。以下、本発明を詳細に説明する。
【0013】
【発明の実施の形態】
本発明のポリエチレン表面保護フィルムは、樹脂成分として全てポリエチレンからなり、使用後はポリエチレン樹脂として回収し、再生樹脂の使用が可能な用途に再利用することが可能である。
【0014】
本発明に用いられるポリエチレン樹脂としては、低密度ポリエチレン、直鎖状低密度ポリエチレン、超低密度ポリエチレン、高密度ポリエチレン、中密度ポリエチレンなどを用いることができる。
【0015】
なかでも冷却ロールに接触する層を構成するポリエチレン樹脂としては、スウェル比が1.45以下である低密度ポリエチレンを用いることが被着物との密着性や、剥離後の被着物への残存物がない点で特に好ましい。スウェル比が1.45以下である低密度ポリエチレンを用いる場合には、270℃以上の温度でTダイから溶融押出しすると被着物との密着性が高まり好ましい。温度の上限については特に制限はないが、高温過ぎるとフィッシュアイやこげが発生しやすくなるため、320℃以下であることが好ましい。
【0016】
本発明のポリエチレン表面保護フィルムは、ポリエチレン溶融膜がTダイから押し出された後、冷却ロール表面の粗さが十点平均粗さで0.5μm以下である鏡面冷却ロールと表面がゴムである押し付けロールとで挟まれる。
十点平均粗さは、JIS B0601−1994に規定されている。
【0017】
冷却ロールの表面粗さが、十点平均粗さで0.5μmを超えると被着物への貼り合わせ面の平滑性が悪く、被着物への貼り合わせが不十分となりやすくなる。
【0018】
本発明においては溶融膜が冷却ロールで冷却されるだけではなく、同時に押し付けロールで押し付けることが必須である。押し付けロールで押し付けないと冷却ロールと反対側のフィルム表面もある程度の粘着性、又は密着性を発現するため、被着物に貼り合わせた後巻き取ったり、積み重ねるとブロッキングを起こしてしまう。
【0019】
押し付けロールの表面がゴムであると、フィルム表面が磨硝子状となり、被着物との粘着性がなく、ブロッキングを防ぐことが可能であるとともに表面保護フィルムの加工時においてもフィルムが滑りやすくなるためにきれいに巻き取りやすくなる。さらに被着物への貼り合わせ時に、表面保護フィルムを繰り出す際に表面保護フィルム同士のブロッキングも軽減されているため繰り出しやすくなる。
【0020】
押し付けロール表面のゴムの種類は特に制限はなく、シリコーンゴムやネオプレンゴムなどが好適に用いられる。
【0021】
本発明の表面保護フィルムには、必要に応じて酸化防止剤や熱安定剤を添加することが可能であるが、被着物への残存付着物の観点から極力少ないことが望ましく、500ppm以下、好ましくは250ppm以下に抑制することが望ましい。紫外線吸収剤、帯電防止剤、金属不活性剤などの添加剤も使用してもよいが、被着物への残存付着物の観点から使用しないことが望ましい。滑剤、抗ブロッキング剤は使用しないことが望ましい。これらの添加剤は低密度ポリエチレン等のポリエチレン系樹脂に予め練り込まれたマスターバッチの形態であってもよく、本発明の効果を損なわない限りマスターバッチのベースポリエチレン系樹脂の種類に特に制限はない。
【0022】
本発明のポリエチレン表面保護フィルムを2層以上の多層とする場合は、共押出しにより多層とすればよい。
【0023】
本発明のポリエチレン表面保護フィルムは、樹脂板、金属板の他、液晶基盤ガラス、液晶表示用偏光フィルム、薄型表示装置フィルム、位相差フィルム、光拡散シート、DVD等の光ディスク構成フィルムや、電子・光学用途向け精密ファインコート面板等の表面保護フィルムとして好適に用いられる。
【0024】
【実施例】
以下、本発明を実施例に基づき説明するが、本発明はこれらの実施例に限定されるものではない。
【0025】
スウェル比は次の方法で測定した。JIS K7210に準じて測定温度190℃、荷重2.16kgの条件でメルトフローレートを測定する方法と同じ方法で押し出されたストランドをカットし、ストランド最下端部から5mm上の部分の直径を、90度異なる2つの方向でマイクロメーターを用いて測定して平均値を計算した。3本のストランドについて、それぞれ同様に平均値を求め、3つの平均値をさらに平均し、この平均値をオリフィスの内径で除した値をスウェル比とした。
【0026】
実施例1
ポリエチレン樹脂として三井住友ポリオレフィン社製低密度ポリエチレンであるスミカセンCE3506(スウェル比 1.33)を用い、加工温度290℃にて単層で90mmφの押出機を用いてTダイから溶融押出しし、十点平均粗さ(Rz)が0.1μmである鏡面冷却ロールと表面がシリコーンゴムである押し付けロールで挟み、巻き取り機で巻き取ることにより厚さ40μmのポリエチレン表面保護フィルムを得た。
得られたポリエチレン表面保護フィルムを、ゴムローラー(荷重:1.3kg/25mm幅)でポリカーボネート板に貼り合わせた。被着物に貼り合わせる側である冷却ロール側はポリカーボネート板に貼り合わせることが可能であったが、ブロッキングを防止することを目的とする押し付けロール側は全く粘着性を示さず、貼り合わせができなかった。また冷却ロール側をポリカーボネート板に貼り合わせ、60℃で97日間保持した後、ポリエチレン表面フィルムを剥がし、ポリカーボネート板の表面を観察したが、付着物や曇りは全くみられなかった。さらに表面保護フィルムの冷却ロール側面をポリエステルフィルムに貼り合わせたものを4枚積み重ね、重さ2.65kg、幅10cmのゴムローラーで押し付けても、押し付けロール側面とポリエステルフィルム面との間にブロッキングは全く見られなかった。
【0027】
比較例1
十点平均粗さが1.5μmであるセミマット冷却ロールを用いた他は実施例1と同様の方法でポリエチレン表面保護フィルムを得た。得られたポリエチレン表面保護フィルムは、冷却面側及び押し付けロール側ともに粘着性がなく、ポリカーボネート板に貼り合わせることができなかった。
【0028】
比較例2
押し付けロールを用いなかったこと以外は実施例1と同様の方法でポリエチレン表面保護フィルムを得た。得られたポリエチレン表面保護フィルムは、冷却面側はポリカーボネート板に貼り合わせることができ、また反対面側もやや弱いながらもポリカーボネート板に貼り合わせることができた。表面保護フィルムの冷却ロール側面をポリエステルフィルムに貼り合わせたものを4枚積み重ね、重さ2.65kg、幅10cmのゴムローラーで押し付けたところ、ブロッキングが見られた。
【0029】
【発明の効果】
以上述べたように本発明の条件を満足する表面保護フィルムでは、片面は被着物に貼り合わせることができ、反対面は全く貼り付けることができないため、被着物に貼り合わせた状態で巻き取ったり積み重ねてもブロッキングを生じることがなく、また被着物に付着物が残ることもない。[0001]
BACKGROUND OF THE INVENTION
The present invention temporarily attaches to the surface of a resin film for optical products, a resin sheet or a resin plate, and protects these surfaces and prevents them from being blocked when rolled up or stacked. It is related with the polyethylene-type surface protection film which has the effect to do, and its manufacturing method.
[0002]
[Prior art]
Conventional surface protection films are used to prevent the introduction of foreign materials during the transportation, storage, and processing of resin plates, metal plates, etc. (hereinafter referred to as adherends) and to prevent the surface from being damaged. When the adherend is used as a product, it is used and peeled off. Therefore, the surface protective film is required to have adhesion or adhesiveness with the adherend, and when peeled, the surface protective film component is required not to adhere to the adherend.
[0003]
In recent years, progress has been made in the development of optical products such as liquid crystal substrate glass, polarizing films for liquid crystal displays, thin display device films, retardation films, light diffusion sheets, optical disc components such as DVDs, and precision fine-coated face plates for electronic and optical applications. is doing. Many of these optical products have very precise structure control, and are very sensitive to scratches and foreign matters. Further, for example, when the optical film is rolled up, there is a problem that the optical film itself causes blocking. Accordingly, there is a need for a surface protective film that protects the surface for these optical products and at the same time prevents blocking.
Furthermore, from the viewpoint of environmental problems, it is preferable that a large amount of the peeled surface protective film is reused in some form, and a surface protective film composed of a single resin is required.
[0004]
Conventionally, a polyethylene-based surface protective film is well known. As one example, a surface protective film is known in which a mixture of an ethylene-vinyl acetate copolymer (EVA) and a specific polyethylene resin is laminated on one side of a base material layer made of a thermoplastic resin, It is disclosed that the problem of increase in adhesive force due to heating is solved, and problems such as dents in protected objects and entrainment of bubbles due to the generation of fish eyes are not caused (for example, see Patent Document 1).
[0005]
In addition, the surface protective film made of a composition of a specific ethylene / α-olefin copolymer and low-density polyethylene or high-density polyethylene is excellent in adhesiveness, has little contamination to the article to be protected, and is also transparent. It is disclosed that it is excellent (for example, refer to Patent Document 2).
[0006]
[Patent Document 1]
Japanese Patent Laid-Open No. 9-132864 [Patent Document 2]
Japanese Patent Laid-Open No. 11-228755
[Problems to be solved by the invention]
However, with the above surface protective film, it is difficult to satisfy the aforementioned requirements for antiblocking and recyclability. That is, it is difficult to recycle as a single resin using an ethylene-vinyl acetate copolymer and a specific polyethylene resin, and the ethylene-vinyl acetate copolymer tends to generate residual deposits. There is a point. In addition, there is no disclosure of an anti-blocking effect in a surface protective film comprising a composition of a specific ethylene / α-olefin copolymer and low density polyethylene or high density polyethylene.
[0008]
The present invention is limited to polyethylene as a resin so that recycling after use is possible, a polyethylene surface protective film that satisfies adhesion or adhesion to an adherend and prevents blocking of the adherend, and its An object is to provide a manufacturing method.
[0009]
[Means for Solving the Problems]
The present inventors are all made of polyethylene, and can be bonded to an adherend, and after being bonded to the adherend, they are not blocked even when wound into a roll film or stacked. As a result of intensive studies as a means for providing a polyethylene surface protective film, the present inventors have found that this object can be achieved in a resin that satisfies certain conditions and processing conditions. That is, the present invention is as follows.
[0010]
(1) In a method for producing a polyethylene surface protective film for winding a polyethylene melt film composed of a single layer or two or more layers melt-extruded from a T die, the surface of a cooling roll after the polyethylene melt film is extruded from the T die A method for producing a polyethylene surface protective film, characterized in that the surface roughness is sandwiched between a mirror surface cooling roll having a 10-point average roughness Rz of 0.5 μm or less and a pressing roll whose surface is rubber.
[0011]
(2) The polyethylene constituting the layer of the polyethylene melt film that contacts the cooling roll is low density polyethylene having a swell ratio of 1.45 or less, and the melt film is extruded from the T die at a temperature of 270 ° C. or more. (1) The manufacturing method of the polyethylene surface protection film as described in (1) characterized by these.
[0012]
(3) A polyethylene surface protective film obtained by the method of (1) or (2). Hereinafter, the present invention will be described in detail.
[0013]
DETAILED DESCRIPTION OF THE INVENTION
The polyethylene surface protective film of the present invention is composed entirely of polyethylene as a resin component, and can be recovered as a polyethylene resin after use and reused for applications in which a recycled resin can be used.
[0014]
As the polyethylene resin used in the present invention, low density polyethylene, linear low density polyethylene, ultra-low density polyethylene, high density polyethylene, medium density polyethylene and the like can be used.
[0015]
Among them, as the polyethylene resin constituting the layer in contact with the cooling roll, it is possible to use low-density polyethylene having a swell ratio of 1.45 or less, adhesion to the adherend, and residue on the adherend after peeling. This is particularly preferable. In the case of using low density polyethylene having a swell ratio of 1.45 or less, it is preferable to perform melt extrusion from a T die at a temperature of 270 ° C. or higher because adhesion with an adherend is increased. Although there is no restriction | limiting in particular about the upper limit of temperature, If it is too high, it will become easy to generate | occur | produce a fish eye and a burn, and it is preferable that it is 320 degrees C or less.
[0016]
The polyethylene surface protective film of the present invention has a mirror surface cooling roll having a 10-point average roughness of 0.5 μm or less and a rubber surface on the surface after the polyethylene melt film is extruded from the T-die. It is sandwiched between rolls.
The ten-point average roughness is defined in JIS B0601-1994.
[0017]
When the surface roughness of the cooling roll exceeds 0.5 μm in terms of 10-point average roughness, the smoothness of the bonding surface to the adherend is poor, and the bonding to the adherend tends to be insufficient.
[0018]
In the present invention, it is essential that the molten film is not only cooled by the cooling roll but also simultaneously pressed by the pressing roll. If it is not pressed with a pressing roll, the film surface on the side opposite to the cooling roll will also exhibit a certain degree of tackiness or adhesion, so that it is blocked when it is wound or stacked after being attached to an adherend.
[0019]
If the surface of the pressing roll is rubber, the film surface becomes polished glass, there is no adhesion to the adherend, it is possible to prevent blocking, and the film becomes slippery even when processing the surface protection film It becomes easy to wind up neatly. Furthermore, since the blocking between the surface protective films is reduced when the surface protective film is unwound at the time of bonding to the adherend, it is easy to unwind.
[0020]
The type of rubber on the surface of the pressing roll is not particularly limited, and silicone rubber or neoprene rubber is preferably used.
[0021]
In the surface protective film of the present invention, it is possible to add an antioxidant or a heat stabilizer as necessary, but it is desirable that the amount is as small as possible from the viewpoint of residual deposits on the adherend, preferably 500 ppm or less, preferably Is preferably suppressed to 250 ppm or less. Additives such as ultraviolet absorbers, antistatic agents, and metal deactivators may also be used, but it is desirable not to use them from the viewpoint of residual deposits on the adherend. It is desirable not to use a lubricant or an anti-blocking agent. These additives may be in the form of a masterbatch previously kneaded into a polyethylene resin such as low-density polyethylene, and there are no particular restrictions on the type of base polyethylene resin in the masterbatch unless the effects of the present invention are impaired. Absent.
[0022]
What is necessary is just to make a multilayer by coextrusion when making the polyethylene surface protection film of this invention a multilayer of two or more layers.
[0023]
The polyethylene surface protective film of the present invention is not only a resin plate and a metal plate, but also a liquid crystal substrate glass, a polarizing film for liquid crystal display, a thin display device film, a retardation film, a light diffusion sheet, an optical disk constituting film such as a DVD, It is suitably used as a surface protective film such as a precision fine coat face plate for optical applications.
[0024]
【Example】
EXAMPLES Hereinafter, although this invention is demonstrated based on an Example, this invention is not limited to these Examples.
[0025]
The swell ratio was measured by the following method. The strand extruded by the same method as the method for measuring the melt flow rate under the conditions of a measurement temperature of 190 ° C. and a load of 2.16 kg according to JIS K7210 is cut, and the diameter of the portion 5 mm above the lowermost end of the strand is 90 The average value was calculated by measuring with a micrometer in two different directions. The average value was similarly obtained for each of the three strands, the three average values were further averaged, and the value obtained by dividing the average value by the inner diameter of the orifice was taken as the swell ratio.
[0026]
Example 1
Sumikasen CE3506 (swell ratio 1.33), a low-density polyethylene manufactured by Sumitomo Mitsui Polyolefin Co., Ltd. is used as the polyethylene resin, and melt extruded from the T die using a 90 mmφ single-layer extruder at a processing temperature of 290 ° C. A polyethylene surface protective film having a thickness of 40 μm was obtained by sandwiching between a mirror surface cooling roll having an average roughness (Rz) of 0.1 μm and a pressing roll having a surface made of silicone rubber and winding it with a winder.
The obtained polyethylene surface protective film was bonded to a polycarbonate plate with a rubber roller (load: 1.3 kg / 25 mm width). The cooling roll side, which is the side to be bonded to the adherend, could be bonded to the polycarbonate plate, but the pressing roll side for the purpose of preventing blocking showed no tackiness and could not be bonded. It was. Further, the cooling roll side was bonded to a polycarbonate plate and held at 60 ° C. for 97 days, and then the polyethylene surface film was peeled off. The surface of the polycarbonate plate was observed, but no deposits or fogging were observed. Furthermore, even if four sheets of the surface protection film with the cooling roll side bonded to the polyester film are stacked and pressed with a rubber roller weighing 2.65 kg and having a width of 10 cm, blocking is not possible between the pressing roll side and the polyester film side. It was not seen at all.
[0027]
Comparative Example 1
A polyethylene surface protective film was obtained in the same manner as in Example 1 except that a semi-matt cooling roll having a 10-point average roughness of 1.5 μm was used. The obtained polyethylene surface protective film was not sticky on both the cooling surface side and the pressing roll side, and could not be bonded to the polycarbonate plate.
[0028]
Comparative Example 2
A polyethylene surface protective film was obtained in the same manner as in Example 1 except that the pressing roll was not used. The obtained polyethylene surface protective film was able to be bonded to the polycarbonate plate on the cooling surface side and to the polycarbonate plate although the opposite surface side was somewhat weak. When four sheets of the surface protective film with the cooling roll side surface bonded to the polyester film were stacked and pressed with a rubber roller having a weight of 2.65 kg and a width of 10 cm, blocking was observed.
[0029]
【The invention's effect】
As described above, in the surface protective film that satisfies the conditions of the present invention, one side can be bonded to the adherend, and the opposite side cannot be attached at all. Even if they are stacked, blocking does not occur, and deposits do not remain on the adherend.
Claims (3)