JP2004175034A - Sheet or film having light insulating effect - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a heat insulating sheet or film showing a light insulating effect. <P>SOLUTION: The heat insulating sheet or film having a light insulating effect is one having 0.3-2.0 of an optical density and 40-100 of brightness, which is obtained by coating with a resin composition comprising the following components (A), (B), and (C): the component (A) of an acrylic resin, an unsaturated polyester resin, an epoxy resin, a silicone resin or a rubbery resin, which contains functional groups and shows a fluidizability at 25°C, the component (B) of a cross-linking agent containing at least 2 functional groups reactive with the component (A), and optionally the component (C) of a filler such as glass beads, hollow glass balloon and microcapsule, followed by curing. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は、工場、住宅等の建築物の屋根や外壁、コンテナ、冷凍車等の運搬車輌の屋根や外壁、さらには船舶、プラント、物置、畜舎等の屋根や外壁等に適用することにより、日光の照射による内部温度の上昇を防ぐとともに、デザインや美観をも向上させることができる光線遮蔽効果を有する遮熱性シートまたはフィルムに関する。
【０００２】
【従来の技術】
建築物や建造物の屋根や外壁は、風雨や日光に曝されており、劣化しやすいことから、かかる劣化を防止し、また外観的な美観を向上させるために、通常は塗料による塗装保護が行われている。また近年は、作業性の向上のために、予め用途に応じたカラーフィルムまたはシートを作成しておき、これを屋根や外壁に配設することによって、塗料による塗装と同様の効果を簡便に得る手法が行われるようになってきた。特に、住宅などの建造物は常に日光に曝されていることからみれば、夏場には居住性向上のために家屋内部の温度の向上を抑える作用があるフィルムまたはシートを家屋の屋根や外壁に配設し、温度調整のために使用するエアコン等の電力消費量を節減することは、地球環境の面からも好ましく、冷房費用の節減にもつながるものである。
【０００３】
また、近年では流通革新に伴い、商品を低温状態で輸送するためのコンテナ、冷凍車が汎用されてきているが、コンテナ、車輌の冷凍・保冷効果を有効に高めるためには、遮熱性の高いフィルムまたはシートを配設することが要望されるようになってきている。さらに、施設または園芸等の被覆に用いられる野外展張用のフィルムまたはシートの分野においても、透明性と共に遮熱性を兼ね備えた製品の要望がなされている状態にある。最近では、このような遮熱性が要求されると共に、建造物、車輌、施設等に対して種々の色彩を付与することによる美観の向上が要求されてきている。
【０００４】
ところで、遮熱性を有するフィルムまたはシートを提供する技術は、古くから行われており、例えば、プラスチック樹脂に対してアルミニウム化合物またはジイモニウム系化合物を特定量含有させることにより遮熱性をもたせたシート（特許文献１）、熱可塑性樹脂フィルムの片面に金属がドープされた無機酸化物微粒子を含有する層を設け、さらに親水性無機コロイド粒子を含有する層を設けることにより遮熱性を高めた屋外展張用フィルム（特許文献２）、また熱可塑性樹脂フィルムに遮熱特性をもたせた塗料を２種以上混合して成形される遮熱性カラーフィルム（特許文献３）などが知られている。
【０００５】
【特許文献１】特開平８−８１５６７号公報
【特許文献２】特開平１０−２５０００２号公報
【特許文献３】特開２００２−１２６７９号公報
【０００６】
この場合に使用される樹脂成分としては、塩化ビニル系樹脂等の熱可塑性樹脂を使用したものが多い。塩化ビニル系樹脂を使用したフィルムまたはシートは、可塑剤を添加し所望の可撓性を付与しているが、添加される可塑剤によっては環境ホルモンへの影響の問題がある。また、可塑剤等の添加剤や低分子量成分からなるフィルムでは、長期使用にあたってこれらの成分がブリードアウトしてしまい、耐候性等に悪影響を及ぼす可能性がある。
【０００７】
一方、熱可塑性樹脂を使用したフィルムまたはシートにあっては、使用している環境が軟化点または融点付近の温度になった場合には、フィルムの形態を保持することができなくなる可能性が高く、外観だけでなく、遮熱効果も低下する可能性がある。
【０００８】
また、熱可塑性樹脂の成形は、通常、カレンダーロールで圧延したり、押出機により成形したりするが、ガラスビーズ等を添加した場合には、ガラスビーズ等が破損し、遮熱効果を低下させたり、成形機のロール等に傷が付くなどの問題がある。
【０００９】
またさらに、遮熱効果を有する塗料を塗布する方法では、遮熱等の機能を付加させた塗料自体が、一般的な塗料に比較して高価なものであり、経済性の面で好ましいものとはいえず、更に安価な手段が望まれていた。さらに、遮熱効果を有する塗料を塗布する場合には、塗料を厚く塗るために何度も重ね塗りが行われており、非常に手間がかかる作業である。
【００１０】
また、カレンダーや押出成形によるフィルムまたはシートの成形方法にあっては、フィルムやシートに機械方向への配向性がでてしまい、使用時の熱などによりフィルムまたはシートにカール等が現れる傾向があり、遮熱効果を確保することが困難となる傾向がある。
【００１１】
【発明が解決しようとする課題】
本発明は、上記の現状に鑑み、これまで提案されている遮熱性フィルムの種々の問題点を解決したものであって、優れた遮熱性を有するとともに、これまで問題視されていた各欠点を解決した遮熱性のフィルムまたはシートを提供することを課題とする。
【００１２】
【課題を解決するための手段】
したがって、その基本的な一つの態様としての請求項１に記載の本発明は、（Ａ）成分として、２５℃のもとで流動性を有し、官能基を有するアクリル樹脂、不飽和ポリエステル樹脂、エポキシ樹脂、シリコン樹脂またはゴム系樹脂成分からなり、
（Ｂ）成分として、上記の（Ａ）成分の官能基と反応する官能基を分子中に２個以上有する樹脂成分からなり、
（Ａ）成分と（Ｂ）成分からなる組成物を、離型性を有する紙または離型性を有するフィルム、基材にコーティングし、硬化させることによりフィルム状やシート状、層状に形成され、
該フィルムやシート、層状物の光学濃度が０．３〜２．０であり、かつ、明度が４０〜１００であることを特徴とする光線遮蔽材料である。
【００１３】
また、別の基本的態様としての請求項２に記載の本発明は、（Ａ）成分として、２５℃のもとで流動性を有し、官能基を有するアクリル樹脂、不飽和ポリエステル樹脂、エポキシ樹脂、シリコン樹脂またはゴム系樹脂成分からなり、
（Ｂ）成分として、上記の（Ａ）成分の官能基と反応する官能基を分子中に２個以上有する樹脂成分からなり、
（Ｃ）成分として、ガラスビーズ、中空ガラスバルーンおよびマイクロカプセルから選ばれる１種以上のものであり、
（Ａ）成分、（Ｂ）成分および（Ｃ）成分からなる組成物を、離型性を有する紙または離型性を有するフィルム、基材にコーティングし、硬化させることによりフィルム状やシート状、層状に形成され、
該フィルムやシート、層状物の光学濃度が０．３〜２．０であり、かつ、明度が２０〜１００であることを特徴とする光線遮蔽材料である。
【００１４】
すなわち、本発明は、（Ａ）成分として特定の官能基を有する樹脂を使用し、かかる（Ａ）成分と反応する官能基を分子中に２個以上有する樹脂を（Ｂ）成分として使用して、（Ａ）成分と（Ｂ）成分を反応させることにより硬化させ、その光学濃度が０．３〜２．０の範囲内にあり、かつ明度を２０〜１００であるフィルムやシート、層状に成形し、日光照射・太陽光線の通過を抑制させることにより、遮熱性をもたせようとする点に一つの特徴を有するものである。
【００１５】
更に本発明にあっては、上記の（Ａ）成分および（Ｂ）成分に加え、さらに（Ｃ）成分としてガラスビーズ、中空ガラスバルーン、マイクロカプセル等の充填材を添加することにより、フィルム、シートまたは層状物を通過する太陽光線等を、フィルム、シートまたは層内において乱反射させることにより、遮熱効果を確保する点にまた一つの特徴を有するものである。
【００１６】
より具体的な請求項３に記載の本発明は、請求項１または２に記載の発明において、（Ａ）成分として使用する樹脂が、アクリル樹脂である光線遮蔽材料である。
【００１７】
また請求項４に記載の本発明は、請求項１ないし３に記載の発明において、（Ａ）成分の樹脂が有する官能基が、水酸基、カルボキシル基、グリシジル基またはアミノ基である樹脂を使用する光線遮蔽材料である。
【００１８】
さらに、請求項５に記載の本発明は、請求項１ないし３に記載の発明において、（Ａ）成分の樹脂と反応する（Ｂ）成分の樹脂が、イソシアネート化合物または酸無水物化合物である光線遮蔽材料である。
【００１９】
【発明の実施の形態】
本発明は、上記したように光線遮蔽効果により遮熱性を有する硬化樹脂フィルムまたはシートである。かかるフィルムまたはシートは基本的に、（Ａ）成分として、２５℃のもとで流動性を有し、官能基を含有するアクリル樹脂、不飽和ポリエステル樹脂、エポキシ樹脂、シリコン樹脂またはゴム系樹脂成分からなり、
（Ｂ）成分として、上記のＡ成分の官能基と反応する官能基を分子中に２個以上有する樹脂からなり、さらにこれに加えて、
（Ｃ）成分として、ガラスビーズ、中空ガラスバルーン、マイクロカプセル等の充填材を含有する樹脂組成物を離形紙または基材にコーティングし、硬化させることにより成形されたシートまたはフィルムである。
【００２０】
この場合の（Ａ）成分としては、２５℃のもとで流動性を有する樹脂であり、樹脂としては液状の樹脂成分であることを必須とする。かかる官能基を含有するアクリル樹脂、不飽和ポリエステル樹脂、エポキシ樹脂、シリコン樹脂またはゴム系樹脂としては、例えば以下のものを挙げることができる。
【００２１】
アクリル系樹脂は、アクリル系単量体を重合したり、アクリル系単量体と共重合可能な単量体をアクリル系単量体と共重合したりすることによって得られる。特にアクリル酸エステルを主成分としたアクリル系樹脂が好ましい。このようなアクリル系樹脂を合成するために使用するアクリル系単量体としては、次のようなものが挙げられる。アクリル酸、メタアクリル酸等のアクリル酸；（メタ）アクリル酸アルキルエステルとしては、（メタ）アクリル酸メチル、（メタ）アクリル酸エチル、（メタ）アクリル酸プロピル、（メタ）アクリル酸ブチル、（メタ）アクリル酸ペンチル、（メタ）アクリル酸ヘキシル、（メタ）アクリル酸−２−エチルヘキシル、（メタ）アクリル酸オクチル、（メタ）アクリル酸ノニル、（メタ）アクリル酸デシル、（メタ）アクリル酸ドデシル等が挙げられる。
【００２２】
本発明で使用するアクリル系単量体は、（メタ）アクリル酸アルキルエステルの１種類の単量体でも良いが、２種以上の単量体を組み合わせても良い。更に、（メタ）アクリル酸アルキルエステル以外の単量体を組み合わせても良く、例えば以下に示す単量体を挙げることができる。（メタ）アクリル酸および（メタ）アクリル酸アルカリ金属塩などの塩；（メタ）アクリル酸フェニル、（メタ）アクリル酸ベンジルのような（メタ）アクリル酸アリールエステル；（メタ）アクリル酸メトキシエチル、（メタ）アクリル酸エトキシエチル、（メタ）アクリル酸プロポキシエチル、（メタ）アクリル酸ブトキシエチル、（メタ）アクリル酸エトキシプロピルのような（メタ）アクリル酸アルコキシアルキル；エチレングリコールのジ（メタ）アクリル酸エステル、ジエチレングリコールのジ（メタ）アクリル酸エステル、トリエチレングリコールのジ（メタ）アクリル酸エステル、ポリエチレングリコールのジ（メタ）アクリル酸エステル、プロピレングリコールのジ（メタ）アクリル酸エステル、ジプロピレングリコールのジ（メタ）アクリル酸エステル、トリプロピレングリコールのジ（メタ）アクリル酸エステルのような（ポリ）アルキレングリコールのジ（メタ）アクリル酸エステル；（メタ）アクリロニトリル；酢酸ビニル；塩化ビニル；塩化ビニリデン；（メタ）アクリル酸−２−クロロエチルのようなハロゲン化ビニル化合物；（メタ）アクリル酸シクロヘキシルのような脂環式アルコールの（メタ）アクリル酸エステル；２−ビニル−２−オキサゾリン、２−ビニル−５−メチル−２−オキサゾリン、２−イソプロペニル−２−オキサゾリンのようなオキサゾリン基含有重合性化合物；（メタ）アクリロイルアジリジン、（メタ）アクリル酸−２−アジリジニルエチルのようなアジリジン基含有重合性化合物；アリルグリシジルエーテル、（メタ）アクリル酸グリシジルエーテル、（メタ）アクリル酸−２−エチルグリシジルエーテルのようなエポキシ基含有ビニル単量体；（メタ）アクリル酸−２−ヒドロキシエチル、（メタ）アクリル酸−３−ヒドロキシプロピル、（メタ）アクリル酸−２−ヒドロキシプロピル、（メタ）アクリル酸−４−ヒドロキシブチル、（メタ）アクリル酸ポリプロピレングリコールまたはポリエチレングリコールとのモノエステル、ラクトン類と（メタ）アクリル酸−２−ヒドロキシエチルとの付加物のようなヒドロキシル基含有ビニル化合物；フッ素置換（メタ）アクリル酸アルキルエステル等の含フッ素ビニル単量体；（メタ）アクリル酸を除く、イタコン酸、クロトン酸、マレイン酸、フマル酸のような不飽和カルボン酸、これらの塩並びにこれらの（部分）エステル化合物および酸無水物；２−クロルエチルビニルエーテル、モノクロロ酢酸ビニルのような反応性ハロゲン含有ビニル単量体；（メタ）アクリルアミド、Ｎ−メチロール（メタ）アクリルアミド、Ｎ−メトキシエチル（メタ）アクリルアミド、Ｎ−ブトキシメチル（メタ）アクリルアミドのようなアミド基含有ビニル単量体；ビニルトリメトキシシラン、γ−メタクリロキシプロピルトリメトキシシラン、アリルトリメトキシシラン、トリメトキシシリルプロピルアリルアミン、２−メトキシエトキシトリメトキシシランのような有機ケイ素基含有ビニル化合物単量体；並びに、エチルデンノルボルネン、ピペリジン、イソプレン、ペンタジエン、ビニルシクロヘキセン、クロロプレン、ブタジエン、メチルブタジエン、シクロブタジエン、メチルブタジエンのようなジエン化合物；が挙げられる。
【００２３】
さらに、トリメチロールプロパントリ（メタ）アクリル酸エステルのような多価（メタ）アクリル酸エステル、ジビニルベンゼン、エチレングリコールジ（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、ジメチロールトリシクロデカンジ（メタ）アクリレート、２，２−ビス［４−（（メタ）アクリロキシエトキシ）フェニル］プロパン等のような分子内に重合性不飽和基を２個以上有する単量体を組み合わせて、多分岐構造の重合体としても良い。
【００２４】
飽和ポリエステルとしては、グリコールと二塩基酸からなるものやラクトンの開環重合によるものが挙げられる。
グリコール単位としては、例えばエチレングリコール、プロピレングリコール、１，３−プロパンジオール、２−メチル−１，３−プロパンジオール、１，２−ブタンジオール、１，３−ブタンジオール、１，４−ブタンジオール、ネオペンチルグリコール、１，６−ヘキサンジオール、ジクロヘキサンジメタノール、２，４，４−トリメチル−１，３−ペンタンジオール等に代表されるアルキレングリコール類；ジエチレングリコール、ポリエチレングリコール、ジプロピレングリコール、ポリプロピレングリコール、ポリブチレングリコール等に代表されるポリアルキレングリコール類；ビスフェノールＡ、ビスフェノールＦ、ビスフェノールＳ、テトラブロモビスフェノールＡ等に代表される２価フェノールとエチレンオキサイドやプロピレンオキサイドに代表されるアルキレンオキサイドとの付加反応生成物などがある。
【００２５】
また飽和二塩基酸としては、例えば、オルトフタル酸、テレフタル酸、イソフタル酸、テトラヒドロフタル酸、メチルテトラヒドロフタル酸、ヘキサヒドロフタル酸、メチルヘキサヒドロフタル酸、エンドメチレンテトラヒドロフタル酸、テトラクロロフタル酸、テトラブロモフタル酸、ニトロフタル酸、マロン酸、コハク酸、アジピン酸、アゼライン酸、１，１２−ドデカン２酸、ハイミック酸、ヘット酸、２，６−ナフタレンジカルボン酸、２，７−ナフタレンジカルボン酸、４，４’−ビフェニルジカルボン酸およびこれらの酸無水物等が挙げられる。
【００２６】
ラクトンとしては、β−ラクトン、γ−ラクトン、δ−ラクトン、ε−ラクトン等が挙げられる。
【００２７】
エポキシ樹脂としては、フェノールノボラック型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、ビスフェノールＡ型エポキシ樹脂、ビスフェノールＦ型エポキシ樹脂、ビスフェノールＡＤ型エポキシ樹脂、脂環式エポキシ樹脂等が挙げられる。
【００２８】
シリコン樹脂としては、１液性のシリコン、ビニル基を有するオルガノシロキサンとＨ−Ｓｉ基を２個以上有するオルガノシロキサンとの２液性シリコンが挙げられる。オレガノシロキサンとしては、例えば、３員環以上の各種環状体が挙げられる。具体的には、ヘキサメチルシクロトリシロキサン、オクタメチルシクロテトラシロキサン、デカメチルシクロペンタシロキサン、ドデカメチルシクロへキサシロキサン、トリメチルトリフェニルシクロトリシロキサン、テトラメチルテトラフェニルシクロテトラシロキサン、オクタフェニルシクロテトラシロキサン等が挙げられる。
【００２９】
これらの樹脂成分は、２５℃のもとで流動性を有するものである。すなわち、本発明が提供するシートまたはフィルムはその製造がコーティングで行われることより、離形紙上あるいは基材上にコーティングされる条件として、２５℃のもとで流動性を有する樹脂である。
【００３０】
本発明にあっては、上記した樹脂成分のなかでも、特に官能基として水酸基、カルボキシル基、グシリジル基またはアミノ基を有するアクリル系樹脂を用いることにより、効果的に光線遮蔽効果により遮熱性が得られることが判明した。
【００３１】
一方、上記した（Ａ）成分である樹脂成分中の官能基と反応を行い、架橋構造を形成する架橋剤成分としてのＢ成分は、例えば、イソシアネート化合物、あるいは酸無水物化合物を挙げることができる。
【００３２】
これらのイソシアネート化合物または酸無水物化合物は、（Ａ）成分と架橋反応する、樹脂業界で一般的に使用されているイソシアネート化合物、あるいは酸無水物化合物を例示することができる。
【００３３】
本発明が提供するフィルムまたはシートを構成する組成物にあっては、上記した（Ａ）成分としての樹脂成分、ならびに架橋剤としての（Ｂ）成分に加え、光線を透過させない機能を有する顔料を添加させることもできる。かかる顔料の光線を透過させない機能は、顔料の隠蔽力として当業者間に周知されており、かかる隠蔽力は、光学濃度して把握することができる。本発明にあっては、組成物中に添加する顔料の隠蔽力を利用して、効果的に光線遮蔽効果を発揮し、より優れた遮熱性が得られることが判明した。そのような顔料としては、具体的には、鉛白、黄鉛、群青、酸化チタン等が挙げられ、なかでも酸化チタンを添加させることにより、効果的に光線遮蔽効果により遮熱性が得られる。かかる顔料としての酸化チタンの粒子は、好ましくは０．５μｍ〜１００μｍ程度のものが使用される。
なお、成分（Ａ）１００重量部に対する顔料の添加量としては、３〜１５重量部程度含有させるのがよい。３重量部未満では遮熱効果が弱い場合があり、また１５重量部を超えて添加してもそれほどの遮熱効果の増大が認められず、かえってシートまたはフィルムへの成形性に問題が生じる傾向がある。
【００３４】
なお本発明が提供するフィルムまたはシートにあっては、耐候性を上げるために、光安定化剤を添加しても良い。そのような光安定化剤としては、ヒンダートアミン系光安定化剤、ベンゾトリアゾール系化合物、ベンゾチアゾール系化合物等の紫外線吸収剤を挙げることができる。
【００３５】
本発明が提供する上記の（Ａ）および（Ｂ）成分を必須とする組成物を硬化させて得たフィルムまたはシートにあっては、そのままでも充分に光線遮蔽効果を発揮し、優れた遮熱性を有するものであるが、より効果的な遮熱性を確保するために、上記成分に加えて、（Ｃ）成分としてガラスビーズ、中空ガラスバルーン、マイクロカプセル等の充填材を組成物中に含有させることができる。
【００３６】
かかる充填剤は、光を反射させ、遮熱効果をより高めるものであり、そのなかでもガラスビーズ、中空ガラスバルーンを使用するのが好ましく、充填材としての粒子は、１μｍ〜１５０μｍ程度、好ましくは５μｍ〜１００μｍ、より好ましくは８μｍ〜８０μｍ程度のものが使用される。
粒径が１５０μｍを超えると組成物の調製時あるいはフィルムへの成型時の作業性が悪化し、また１μｍ未満のものを使用しても、充填剤の添加による所望の遮熱効果を得ることが困難となる。
その添加量としては、好ましくは５〜２０重量部程度であり、好ましくは１０〜１５重量部程度である。５重量部未満であると充分な遮熱効果を得ることができず、また２０重量部を超える場合には、フィルムまたはシートへの成形が困難となる傾向がある。
【００３７】
本発明のフィルムまたはシートには、粘着剤層を設けてもよい。粘着剤層の成形方法は、一般に行われる方法が使用できる。
【００３８】
そのなかでも、本発明が提供する光線遮蔽材料としての好ましい態様は、（Ａ）成分として、２５℃のもとで流動性を有し、官能基として水酸基、カルボキシル基、グリシジル基、アミノ基から選ばれる少なくとも１種以上を有するアクリル系樹脂成分からなり、
（Ｂ）成分として、上記のＡ成分の官能基と反応する官能基を分子中に２個以上有するイソシアネート化合物または酸無水物化合物からなり、
（Ｃ）成分として、ガラスビーズ、中空ガラスバルーン、マイクロカプセルから選ばれる１種以上のものであり、
（Ａ）成分、（Ｂ）成分、（Ｃ）成分にさらに顔料を加えた組成物を離形紙または基材にコーティングし、硬化させることによりフィルム状やシート状、層状に形成され、
該フィルムやシート、層の光学濃度が０．３〜２．０であり、かつ、明度が４０〜１００であることを特徴とする光線遮蔽材料である。
【００３９】
本発明にあっては、以上の（Ａ）、（Ｂ）および（Ｃ）成分、さらには所望により顔料成分、および触媒等からなる組成物を混合し、硬化させることによりフィルムまたはシート状に成形される。かかる硬化条件としては、温度による硬化、紫外線の作用による硬化、加硫剤による硬化等で行うことができる。
【００４０】
具体的には、コーティング法により離型性を有する紙またはフィルム上に組成物をコーティングし、その後、例えば加熱硬化させることにより、目的とする本発明のフィルムまたはシートを得ることができる。
なお、本発明のフィルムまたはシートにあっては、それぞれ目的に応じその厚みは一概に限定できないが、０．１〜２ｍｍ厚、通常０．５〜１．０ｍｍ厚に成形される。
【００４１】
【実施例】
以下に本発明を実施例によりさらに詳細に説明するが、本発明はこれら実施例に限定されるものではない。
【００４２】
実施例１〜２６／比較例１〜３：
下記表１および表２に示した組成（重量部）により、それぞれ実施例および比較例の遮熱性シートを作成した。
なお、各実施例１〜２６の遮熱性シートはナイフコーティング法により層厚１ｍｍのシートとして成形し、比較例１〜３のシートは、カレンダーロール法により層厚１ｍｍに成形した。
【００４３】
なお、表中のアスタリスクは以下の成分である。
＊１：アクリル系樹脂：ＵＨ−２０３２（東亜合成社製）
＊２：不飽和ポリエステル系樹脂：１，１２−ト゛テ゛カン二酸とホ゜リカーホ゛ネートシ゛オール（ＰＬＡＣＣＥＬ（ダイセル化学工業社製）とのポリエステル
＊３：エポキシ系樹脂：エピコート８２７（ジャパンエポキシレジン社製）
＊４：シリコン系樹脂：ＣＹ５２−２８３（東レダウコーニング社製）
＊５：ゴム系樹脂：エチレンプロピレンゴム
＊６：イソシアネート化合物：コロネート１０４０（日本ポリウレタン工業社製）
＊７：酸無水物：無水コハク酸
＊８：エポキシ化合物：デコナールＥＸ−２１２（ナガセ化成工業社製）
【００４４】
得られた各実施例および比較例のシートの光学濃度および明度を合せて表中に示した。
【００４５】
【表１】

【００４６】
【表２】

【００４７】
なお、各製造されたシート層断面を電子顕微鏡（×５０）により観察したところ、実施例１〜２６の遮熱性シートは、シート層内に充填剤の中空ガラスバルーン、ガラスビーズまたはマイクロカプセルが破損することなく均一に分散されているものであったが、比較例１〜３のシートにあっては、シート層内で部分的に中空ガラスバルーンまたはガラスビーズが破損されていることが観察された。
【００４８】
１．遮熱性能試験Ａ：
上記各実施例および比較例で製造した遮熱性シートを用いて、実際の遮熱性能試験（白熱灯照射試験）を行った。
高さ１５０ｍｍ、巾２２０ｍｍ、長さ３１０ｍｍ、厚み３０ｍｍの発泡スチロール箱の上面に、各実施例および比較例で得た遮熱性シートを貼付した鋼板を設置し、サンプル（遮熱シート）上方３００ｍｍの高さから２００Ｗの白熱灯を４０分間照射した後の、サンプル裏面および箱内部の温度を観察した。
その結果を合せて表中に示した。
なお、比較としてセラミック反射テープを貼付した例、遮熱塗料（ホワイト）を塗付した例および鋼板のみの例を、同一の条件下で検討した。それらの裏面温度および箱内温度は以下の表３に示すとおりであった。
【００４９】
【表３】

【００５０】
本発明の遮熱性シートは、その光線遮蔽効果による遮熱性がかなり優れたものであって、遮熱塗料と同程度の遮熱性能を示し、また、比較として実施したセラミック熱反射テープより優れたものであった。特に遮熱性シートの裏面温度は、鋼板のみの裏面温度に比べ約２０℃低いものであり、かなりの熱を反射しているものであった。
【００５１】
２．分光反射率試験
自記分光光度計Ｕ−４０００（日立製作所社製）を用いて、アルミナ白色基板を反射率１００％とし、３５０〜２１００ｎｍの範囲で、上記実施例９で得た遮熱性シートの分光反射率を測定し、ＪＩＳ Ａ ５７５９付表３を用いて日射反射率を計算した。比較として、遮熱（熱反射）塗料（ホワイト）を塗布したシートについても測定した。
その結果、本発明の遮熱性シートの日射反射率は８７．７％であり、遮熱（熱反射）塗料（ホワイト）を塗布したシートの日射反射率は８７．８％と、同等の日射反射率を示した。
【００５２】
なお、分光反射率のチャートからは、本発明の遮熱性シートと遮熱（熱反射）塗料（ホワイト）を塗布したシートの両者とも近赤外光領域（８５０〜１１００ｎｍ）での日射反射率はほぼ同等のチャートを示したが、１１００ｎｍ以上の波長領域では両者にばらつきのチャートが観察され、１６００ｎｍ以上の波長領域では本発明の遮熱性シートの反射率は低下していた。なお、１６００ｎｍ以上の波長領域での反射率の低下は熱エネルギーとしての波長領域ではないことから、この低下は遮熱性に影響を及ぼさない部分であった。
【００５３】
３．実地試験
市販の犬小屋を用いて、その屋根、外板部分に実施例９で得た遮熱性シートを両面接着テープにて隈なく配設し、遮熱シートを配設しない犬小屋とともに、直射日光があたる状態で野外に１０日間両者を放置し、快晴日における両者の屋根裏面温度と外気温との差を測定した。
その結果、遮熱性シートを配設した屋根裏面温度は、遮熱性シートを配設しない屋根裏面温度に比較して低いものであり、両者に最大１７℃程度の温度差が認められた。
以上の結果から判断すると、本発明の遮熱性シートは、その光線遮蔽効果による遮熱性がかなり優れたものであることが確認された。
【００５４】
４．遮熱性能試験Ｂ：
上記の各試験の結果、本発明の各実施例で製造された遮熱性シートの光線遮蔽効果による遮熱性が優れたものであったことより、実施例１と同様の樹脂組成によりシート層厚、顔料（酸化チタン）の添加量、充填剤（中空ガラスバルーン）の添加量を変化させた遮熱性シートを製造し、前記遮熱性能試験Ａの白熱灯照射試験と同様の試験を行い、各遮熱性シート裏面の温度と、そのときの箱内の温度を測定した。
その結果を、次表４にまとめて示した。また、そのときの光学濃度を合せて示した。
【００５５】
【表４】

【００５６】
上記の表中の結果からも判明するように、本発明の遮熱性シートは、充填剤（中空ガラスバルーン）および顔料（酸化チタン）の両者を含有させた場合、シート層厚を０．３〜１．５ｍｍと変化させたものであっても、ほぼ同様の遮熱性能が得られていることが理解される。
また、シート層厚を１．０ｍｍとし顔料（酸化チタン）の添加量を変化させた場合、顔料の添加量が樹脂１００重量部に対して３重量部以上添加させことで所望の遮熱性能が得られていることが理解される。
【００５７】
【発明の効果】
以上記載のように、本発明は上記した（Ａ）成分、（Ｂ）成分および（Ｃ）成分を含有する組成物をコーティングし硬化させて成形したシートまたはフィルムであるが、それらの成分を配合することにより、光線遮蔽効果による遮熱性が達成される。
特に本発明が提供するシートまたはフィルムの遮熱性効果は、これまで提案されている遮熱塗料と同程度のものであり、したがってより簡便な方法により、工場、住宅等の建築物の屋根や外板、あるいはコンテナ、冷凍車等の運搬車輌の屋根や外壁、さらには船舶、プラント、物置、畜舎等の屋根や外壁等に適用することができる利点を有している。
また、得られたシートまたはフィルムを適当な形状により裁断し、デザインや美観をも向上させることができる利点を有し、その産業上の利用性は多大なものである。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention is applied to roofs and outer walls of buildings such as factories and houses, roofs and outer walls of containers, transport vehicles such as refrigerated vehicles, and further, roofs and outer walls of ships, plants, sheds, livestock sheds and the like, The present invention relates to a heat-shielding sheet or film having a light-shielding effect capable of preventing an increase in internal temperature due to irradiation of sunlight and improving a design and an appearance.
[0002]
[Prior art]
The roofs and exterior walls of buildings and structures are exposed to the weather and sunlight, and are liable to deteriorate.Therefore, paint protection with paint is usually applied to prevent such deterioration and improve the aesthetic appearance. Is being done. In recent years, in order to improve workability, a color film or sheet corresponding to the intended use is prepared in advance, and is disposed on a roof or an outer wall, so that the same effect as that of a paint can be easily obtained. Techniques are being implemented. In particular, considering that buildings such as houses are always exposed to sunlight, in summer, a film or sheet that has the effect of suppressing an increase in the temperature of the interior of the house to improve the livability is applied to the roof or outer wall of the house. It is preferable from the viewpoint of the global environment to reduce the power consumption of an air conditioner or the like which is provided and used for temperature control, and this also leads to a reduction in cooling costs.
[0003]
In recent years, containers and refrigeration vehicles for transporting goods in low-temperature conditions have been widely used in accordance with distribution innovation, but in order to effectively enhance the freezing and cooling effects of containers and vehicles, high heat shielding properties are required. There is an increasing demand for providing films or sheets. Furthermore, in the field of films or sheets for outdoor expansion used for covering facilities or horticulture, there is a demand for a product having both transparency and heat shielding properties. In recent years, such heat shielding properties have been required, and an improvement in aesthetic appearance by imparting various colors to buildings, vehicles, facilities, and the like has been required.
[0004]
By the way, a technique of providing a film or sheet having heat shielding properties has been used for a long time. For example, a sheet having heat shielding properties by adding a specific amount of an aluminum compound or a diimonium-based compound to a plastic resin (Patent Literature 1) A film for outdoor expansion in which a layer containing metal-doped inorganic oxide fine particles is provided on one surface of a thermoplastic resin film, and a layer containing hydrophilic inorganic colloid particles is further provided to enhance heat shielding properties. (Patent Document 2) and a heat-insulating color film (Patent Document 3) formed by mixing two or more kinds of paints each having a heat-insulating property on a thermoplastic resin film are known.
[0005]
[Patent Document 1] Japanese Patent Application Laid-Open No. 8-81567
[Patent Document 2] JP-A-10-250002
[Patent Document 3] JP-A-2002-12679
[0006]
In many cases, a thermoplastic resin such as a vinyl chloride resin is used as a resin component used in this case. A film or sheet using a vinyl chloride-based resin has a desired flexibility by adding a plasticizer. However, depending on the added plasticizer, there is a problem of affecting environmental hormones. In addition, in the case of a film comprising additives such as a plasticizer and low molecular weight components, these components may bleed out during long-term use, which may adversely affect weather resistance and the like.
[0007]
On the other hand, in the case of a film or sheet using a thermoplastic resin, if the environment in use is at a temperature near the softening point or melting point, there is a high possibility that the form of the film cannot be maintained. However, not only the appearance but also the heat-shielding effect may be reduced.
[0008]
In addition, molding of a thermoplastic resin is usually performed by rolling with a calender roll or molding with an extruder, but when glass beads or the like are added, the glass beads or the like are damaged, and the heat shielding effect is reduced. And the rolls of the molding machine are scratched.
[0009]
Furthermore, in the method of applying a paint having a heat-shielding effect, the paint itself having a function such as heat-shielding is more expensive than a general paint, and is preferable in terms of economy. Nevertheless, cheaper means have been desired. Furthermore, when applying a paint having a heat-shielding effect, repetitive coating is performed many times in order to apply the paint thickly, which is a very laborious operation.
[0010]
In the method of forming a film or sheet by calendering or extrusion molding, the film or sheet tends to be oriented in the machine direction, and the film or sheet tends to curl due to heat during use. However, it tends to be difficult to secure the heat shielding effect.
[0011]
[Problems to be solved by the invention]
The present invention has been made in view of the above-mentioned current situation, and has solved various problems of the heat-shielding films that have been proposed so far, and has excellent heat-shielding properties. It is an object to provide a heat-insulating film or sheet that has been solved.
[0012]
[Means for Solving the Problems]
Therefore, the present invention according to claim 1, which is one of the basic aspects, comprises, as the component (A), an acrylic resin having a fluidity at 25 ° C and having a functional group, and an unsaturated polyester resin. , Consisting of epoxy resin, silicone resin or rubber resin component,
The component (B) comprises a resin component having two or more functional groups in the molecule that react with the functional group of the component (A),
The composition comprising the component (A) and the component (B) is coated on a release paper or a release film, or a substrate, and cured to form a film, sheet, or layer,
A light shielding material characterized in that the optical density of the film, sheet or layered product is 0.3 to 2.0 and the brightness is 40 to 100.
[0013]
Further, the present invention according to claim 2 as another basic embodiment is characterized in that, as the component (A), an acrylic resin having a fluidity at 25 ° C. and having a functional group, an unsaturated polyester resin, an epoxy resin, Made of resin, silicone resin or rubber-based resin component,
The component (B) comprises a resin component having two or more functional groups in the molecule that react with the functional group of the component (A),
Component (C) is one or more selected from glass beads, hollow glass balloons and microcapsules,
The composition comprising the component (A), the component (B) and the component (C) is coated on a release paper or a release film or a substrate and cured to form a film or sheet. Formed in layers,
The light shielding material is characterized in that the film, sheet or layered material has an optical density of 0.3 to 2.0 and a lightness of 20 to 100.
[0014]
That is, the present invention uses a resin having a specific functional group as the component (A), and uses a resin having two or more functional groups that react with the component (A) in the molecule as the component (B). And curing by reacting the components (A) and (B) to form a film, sheet or layer having an optical density in the range of 0.3 to 2.0 and a brightness of 20 to 100. In addition, it has one feature in that it is intended to provide heat insulation by suppressing sunlight irradiation and passage of sunlight.
[0015]
Further, in the present invention, in addition to the above-mentioned components (A) and (B), a film, a sheet, and the like are further added by adding a filler such as glass beads, hollow glass balloons, and microcapsules as the component (C). Another feature is that the solar light or the like passing through the layered material is irregularly reflected in the film, the sheet, or the layer to secure a heat shielding effect.
[0016]
More specifically, the present invention described in claim 3 is a light shielding material in which the resin used as the component (A) is an acrylic resin in the invention described in claim 1 or 2.
[0017]
According to a fourth aspect of the present invention, in the first to third aspects of the present invention, a resin in which the functional group of the component (A) is a hydroxyl group, a carboxyl group, a glycidyl group, or an amino group is used. It is a light shielding material.
[0018]
Furthermore, the present invention described in claim 5 is the invention according to claims 1 to 3, wherein the resin of the component (B) reacting with the resin of the component (A) is an isocyanate compound or an acid anhydride compound. It is a shielding material.
[0019]
BEST MODE FOR CARRYING OUT THE INVENTION
The present invention is a cured resin film or sheet having a heat shielding property due to a light shielding effect as described above. Such a film or sheet basically has, as the component (A), an acrylic resin, an unsaturated polyester resin, an epoxy resin, a silicone resin or a rubber-based resin having fluidity at 25 ° C. and containing a functional group. Consisting of
The component (B) comprises a resin having two or more functional groups in the molecule that react with the functional group of the above-mentioned component A.
(C) A sheet or film formed by coating a resin composition containing a filler such as glass beads, hollow glass balloons, and microcapsules on a release paper or a base material and curing the resin composition.
[0020]
In this case, the component (A) is a resin having fluidity at 25 ° C., and the resin must be a liquid resin component. Examples of the acrylic resin, unsaturated polyester resin, epoxy resin, silicone resin or rubber-based resin containing such a functional group include the following.
[0021]
The acrylic resin is obtained by polymerizing an acrylic monomer or copolymerizing a monomer copolymerizable with the acrylic monomer with the acrylic monomer. Particularly, an acrylic resin containing an acrylate ester as a main component is preferable. Examples of the acrylic monomer used for synthesizing such an acrylic resin include the following. Acrylic acid such as acrylic acid and methacrylic acid; examples of the alkyl (meth) acrylate include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, Pentyl (meth) acrylate, hexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, octyl (meth) acrylate, nonyl (meth) acrylate, decyl (meth) acrylate, dodecyl (meth) acrylate And the like.
[0022]
The acrylic monomer used in the present invention may be one type of (meth) acrylic acid alkyl ester, or may be a combination of two or more types. Further, monomers other than the alkyl (meth) acrylate may be combined, and examples thereof include the following monomers. Salts such as (meth) acrylic acid and alkali metal (meth) acrylate; aryl (meth) acrylates such as phenyl (meth) acrylate and benzyl (meth) acrylate; methoxyethyl (meth) acrylate; Alkoxyalkyl (meth) acrylates such as ethoxyethyl (meth) acrylate, propoxyethyl (meth) acrylate, butoxyethyl (meth) acrylate, and ethoxypropyl (meth) acrylate; di (meth) acryl of ethylene glycol Acid ester, di (meth) acrylate of diethylene glycol, di (meth) acrylate of triethylene glycol, di (meth) acrylate of polyethylene glycol, di (meth) acrylate of propylene glycol, dipropylene glycol Di (meth) acrylates of (poly) alkylene glycols, such as di (meth) acrylate, tripropylene glycol di (meth) acrylate; (meth) acrylonitrile; vinyl acetate; vinyl chloride; vinylidene chloride; Vinyl halide compounds such as 2-chloroethyl (meth) acrylate; (meth) acrylates of alicyclic alcohols such as cyclohexyl (meth) acrylate; 2-vinyl-2-oxazoline, 2-vinyl- Oxazoline group-containing polymerizable compounds such as 5-methyl-2-oxazoline and 2-isopropenyl-2-oxazoline; aziridine group-containing such as (meth) acryloylaziridine and (meth) acrylate-2-aziridinylethyl Polymerizable compound; allyl glycidyl ether, (meta Epoxy group-containing vinyl monomers such as glycidyl acrylate and 2-ethyl glycidyl (meth) acrylate; 2-hydroxyethyl (meth) acrylate, 3-hydroxypropyl (meth) acrylate, ( 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, monoesters of polypropylene glycol or polyethylene glycol (meth) acrylate, lactones and 2-hydroxyethyl (meth) acrylate Hydroxyl-containing vinyl compounds such as adducts of fluorinated vinyl monomers such as alkyl esters of fluorine-substituted (meth) acrylic acid; of itaconic acid, crotonic acid, maleic acid and fumaric acid, excluding (meth) acrylic acid Such unsaturated carboxylic acids, their salts and their (Partial) ester compounds and acid anhydrides; reactive halogen-containing vinyl monomers such as 2-chloroethyl vinyl ether and vinyl monochloroacetate; (meth) acrylamide, N-methylol (meth) acrylamide, N-methoxyethyl (meth) ) Amide group-containing vinyl monomers such as acrylamide and N-butoxymethyl (meth) acrylamide; vinyltrimethoxysilane, γ-methacryloxypropyltrimethoxysilane, allyltrimethoxysilane, trimethoxysilylpropylallylamine, 2-methoxy Organosilicon group-containing vinyl compound monomers such as ethoxytrimethoxysilane; and ethyldenorbornene, piperidine, isoprene, pentadiene, vinylcyclohexene, chloroprene, butadiene, methylbutadiene, B butadiene, diene compounds such as methyl butadiene; and the like.
[0023]
Furthermore, poly (meth) acrylates such as trimethylolpropane tri (meth) acrylate, divinylbenzene, ethylene glycol di (meth) acrylate, neopentyl glycol di (meth) acrylate, dimethylol tricyclodecane Hyperbranched by combining monomers having two or more polymerizable unsaturated groups in the molecule, such as (meth) acrylate, 2,2-bis [4-((meth) acryloxyethoxy) phenyl] propane and the like. It may be a polymer having a structure.
[0024]
Examples of the saturated polyester include those composed of glycol and dibasic acid and those obtained by ring-opening polymerization of lactone.
Examples of the glycol unit include ethylene glycol, propylene glycol, 1,3-propanediol, 2-methyl-1,3-propanediol, 1,2-butanediol, 1,3-butanediol, and 1,4-butanediol. , Neopentyl glycol, 1,6-hexanediol, dichlorohexanedimethanol, 2,4,4-trimethyl-1,3-pentanediol, etc .; alkylene glycols; diethylene glycol, polyethylene glycol, dipropylene glycol, polypropylene Glycols and polyalkylene glycols such as polybutylene glycol; dihydric phenols such as bisphenol A, bisphenol F, bisphenol S, and tetrabromobisphenol A; The like addition reaction products of an alkylene oxide represented by pyrene oxide.
[0025]
Examples of the saturated dibasic acid include, for example, orthophthalic acid, terephthalic acid, isophthalic acid, tetrahydrophthalic acid, methyltetrahydrophthalic acid, hexahydrophthalic acid, methylhexahydrophthalic acid, endomethylenetetrahydrophthalic acid, tetrachlorophthalic acid, Tetrabromophthalic acid, nitrophthalic acid, malonic acid, succinic acid, adipic acid, azelaic acid, 1,12-dodecane diacid, hymic acid, hetonic acid, 2,6-naphthalenedicarboxylic acid, 2,7-naphthalenedicarboxylic acid, 4,4′-biphenyldicarboxylic acid and acid anhydrides thereof.
[0026]
Examples of the lactone include β-lactone, γ-lactone, δ-lactone, ε-lactone and the like.
[0027]
Examples of the epoxy resin include a phenol novolak epoxy resin, a cresol novolak epoxy resin, a bisphenol A epoxy resin, a bisphenol F epoxy resin, a bisphenol AD epoxy resin, an alicyclic epoxy resin, and the like.
[0028]
Examples of the silicone resin include one-part silicon and two-part silicon composed of an organosiloxane having a vinyl group and an organosiloxane having two or more H-Si groups. Examples of the oreganosiloxane include, for example, various cyclic bodies having three or more membered rings. Specifically, hexamethylcyclotrisiloxane, octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, dodecamethylcyclohexasiloxane, trimethyltriphenylcyclotrisiloxane, tetramethyltetraphenylcyclotetrasiloxane, octaphenylcyclotetrasiloxane And the like.
[0029]
These resin components have fluidity at 25 ° C. That is, the sheet or film provided by the present invention is a resin having fluidity at 25 ° C. as a condition of being coated on a release paper or a base material because its production is performed by coating.
[0030]
In the present invention, among the above-mentioned resin components, by using an acrylic resin having a hydroxyl group, a carboxyl group, a glycidyl group or an amino group as a functional group, heat-shielding properties are effectively obtained by a light-shielding effect. It turned out to be.
[0031]
On the other hand, the component B as a cross-linking agent component which reacts with a functional group in the resin component as the component (A) to form a cross-linked structure can be, for example, an isocyanate compound or an acid anhydride compound. .
[0032]
These isocyanate compounds or acid anhydride compounds can be exemplified by an isocyanate compound or an acid anhydride compound commonly used in the resin industry, which undergoes a crosslinking reaction with the component (A).
[0033]
In the composition constituting the film or sheet provided by the present invention, in addition to the resin component as the component (A) and the component (B) as the cross-linking agent, a pigment having a function of not transmitting light is used. It can also be added. Such a function of the pigment that does not transmit light is known to those skilled in the art as the hiding power of the pigment, and the hiding power can be grasped by optical density. In the present invention, it has been found that the light-shielding effect is effectively exhibited by utilizing the hiding power of the pigment added to the composition, and more excellent heat-shielding properties can be obtained. Specific examples of such pigments include lead white, graphite, ultramarine blue, titanium oxide, and the like. In particular, by adding titanium oxide, heat shielding properties can be obtained effectively by a light shielding effect. The titanium oxide particles as the pigment preferably have a particle size of about 0.5 μm to 100 μm.
The amount of the pigment added to 100 parts by weight of the component (A) is preferably about 3 to 15 parts by weight. If the amount is less than 3 parts by weight, the heat-shielding effect may be weak. If the amount exceeds 15 parts by weight, the heat-shielding effect is not so much increased. There is.
[0034]
In the film or sheet provided by the present invention, a light stabilizer may be added in order to increase weather resistance. Examples of such a light stabilizer include a hindered amine-based light stabilizer, a benzotriazole-based compound, and a benzothiazole-based ultraviolet absorber.
[0035]
The film or sheet obtained by curing the composition comprising the above-mentioned components (A) and (B) provided by the present invention exhibits a sufficient light-shielding effect as it is and has excellent heat-shielding properties. In order to ensure more effective heat shielding properties, a filler such as glass beads, hollow glass balloons, and microcapsules is added to the composition as the component (C) in addition to the above components. be able to.
[0036]
Such a filler reflects light and further enhances the heat shielding effect. Among them, glass beads and hollow glass balloons are preferably used, and particles as the filler are about 1 μm to 150 μm, preferably about 1 μm to 150 μm. Those having a size of 5 μm to 100 μm, more preferably about 8 μm to 80 μm are used.
When the particle size exceeds 150 μm, the workability at the time of preparing the composition or molding into a film is deteriorated, and even if the particle size is less than 1 μm, a desired heat shielding effect by adding a filler may be obtained. It will be difficult.
The addition amount is preferably about 5 to 20 parts by weight, preferably about 10 to 15 parts by weight. If the amount is less than 5 parts by weight, a sufficient heat shielding effect cannot be obtained, and if it exceeds 20 parts by weight, it tends to be difficult to form a film or a sheet.
[0037]
The film or sheet of the present invention may be provided with an adhesive layer. As a method for forming the pressure-sensitive adhesive layer, a generally used method can be used.
[0038]
Among them, a preferred embodiment of the light-shielding material provided by the present invention is that the component (A) has fluidity at 25 ° C. and has a hydroxyl group, a carboxyl group, a glycidyl group, or an amino group as a functional group. Consisting of at least one selected acrylic resin component,
The component (B) comprises an isocyanate compound or an acid anhydride compound having two or more functional groups in the molecule that react with the functional group of the component A,
Component (C) is at least one selected from glass beads, hollow glass balloons, and microcapsules,
A composition obtained by further adding a pigment to the component (A), the component (B), and the component (C) is coated on a release paper or a base material and cured to form a film, sheet, or layer,
The light shielding material is characterized in that the film, sheet or layer has an optical density of 0.3 to 2.0 and a lightness of 40 to 100.
[0039]
In the present invention, the above components (A), (B) and (C), and if desired, a composition comprising a pigment component and a catalyst are mixed and cured to form a film or sheet. Is done. Such curing conditions include curing by temperature, curing by the action of ultraviolet rays, and curing by a vulcanizing agent.
[0040]
Specifically, the desired film or sheet of the present invention can be obtained by coating the composition on a paper or film having releasability by a coating method and then, for example, heat-curing the composition.
In addition, the thickness of the film or sheet of the present invention cannot be unequivocally limited depending on the purpose, but is formed into a thickness of 0.1 to 2 mm, usually 0.5 to 1.0 mm.
[0041]
【Example】
Hereinafter, the present invention will be described in more detail with reference to Examples, but the present invention is not limited to these Examples.
[0042]
Examples 1-26 / Comparative Examples 1-3:
With the compositions (parts by weight) shown in Tables 1 and 2 below, heat-shielding sheets of Examples and Comparative Examples were prepared, respectively.
The heat-insulating sheets of Examples 1 to 26 were formed into a sheet having a layer thickness of 1 mm by a knife coating method, and the sheets of Comparative Examples 1 to 3 were formed to a layer thickness of 1 mm by a calendar roll method.
[0043]
The asterisks in the table are the following components.
* 1: Acrylic resin: UH-2032 (Toa Gosei Co., Ltd.)
* 2: Unsaturated polyester resin: Polyester of 1,12-tolcanedioic acid and polycarbonate carbonate (PLACCEL (manufactured by Daicel Chemical Industries, Ltd.)
* 3: Epoxy resin: Epicoat 827 (manufactured by Japan Epoxy Resin)
* 4: Silicone resin: CY52-283 (manufactured by Dow Corning Toray)
* 5: Rubber resin: ethylene propylene rubber
* 6: Isocyanate compound: Coronate 1040 (manufactured by Nippon Polyurethane Industry Co., Ltd.)
* 7: Acid anhydride: succinic anhydride
* 8: Epoxy compound: Deconal EX-212 (manufactured by Nagase Kasei Kogyo)
[0044]
The optical density and lightness of the sheets obtained in each of Examples and Comparative Examples are shown together in the table.
[0045]
[Table 1]

[0046]
[Table 2]

[0047]
In addition, when the cross section of each manufactured sheet layer was observed with an electron microscope (× 50), the heat-shielding sheets of Examples 1 to 26 showed that the hollow glass balloon, glass beads, or microcapsules of the filler were broken in the sheet layer. It was observed that the hollow glass balloons or glass beads were partially broken in the sheet layers in the sheets of Comparative Examples 1 to 3, although they were uniformly dispersed without performing. .
[0048]
1. Heat insulation performance test A:
An actual heat-shielding performance test (incandescent lamp irradiation test) was performed using the heat-insulating sheets manufactured in the above Examples and Comparative Examples.
On the upper surface of a styrofoam box having a height of 150 mm, a width of 220 mm, a length of 310 mm, and a thickness of 30 mm, a steel plate to which the heat-shielding sheets obtained in the respective Examples and Comparative Examples were attached was installed, and a height of 300 mm above the sample (heat-shielding sheet). Then, after irradiating the incandescent lamp of 200 W for 40 minutes, the temperature of the back surface of the sample and the inside of the box were observed.
The results are shown in the table.
As a comparison, an example in which a ceramic reflective tape was applied, an example in which a heat-shielding paint (white) was applied, and an example in which only a steel plate was used were examined under the same conditions. The back surface temperature and the temperature inside the box were as shown in Table 3 below.
[0049]
[Table 3]

[0050]
The heat-shielding sheet of the present invention has excellent heat-shielding properties due to its light-shielding effect, exhibits a heat-shielding performance comparable to that of the heat-shielding paint, and is superior to the ceramic heat-reflective tapes used for comparison. Was something. In particular, the back surface temperature of the heat shielding sheet was about 20 ° C. lower than the back surface temperature of the steel sheet alone, and reflected considerable heat.
[0051]
2. Spectral reflectance test
Using an automatic recording spectrophotometer U-4000 (manufactured by Hitachi, Ltd.), the reflectance of the heat-shielding sheet obtained in Example 9 was measured in the range of 350 to 2100 nm using an alumina white substrate of 100% reflectance. Then, the solar reflectance was calculated using JIS A 5759 Appendix Table 3. For comparison, a sheet coated with a heat-shielding (heat-reflecting) paint (white) was also measured.
As a result, the solar reflectance of the heat-insulating sheet of the present invention was 87.7%, and the solar reflectance of the sheet coated with the heat-shielding (heat-reflective) paint (white) was 87.8%, which is equivalent to the solar reflectance. Rate.
[0052]
From the chart of the spectral reflectance, both the heat-shielding sheet of the present invention and the sheet coated with the heat-shielding (heat reflection) paint (white) have a solar reflectance in the near infrared region (850 to 1100 nm). Although almost the same chart was shown, in the wavelength region of 1100 nm or more, a variation chart was observed between them, and in the wavelength region of 1600 nm or more, the reflectance of the heat shielding sheet of the present invention was reduced. Since the decrease in reflectance in the wavelength region of 1600 nm or more is not in the wavelength region as thermal energy, this decrease is a portion that does not affect the heat shielding property.
[0053]
3. Field test
Using a commercially available kennel, the heat-insulating sheet obtained in Example 9 was completely disposed on the roof and the outer plate with a double-sided adhesive tape, and together with the doghouse without the heat-insulating sheet, direct sunlight Both were allowed to stand outdoors for 10 days in the hit state, and the difference between the roof back surface temperature and the outside air temperature on a clear day was measured.
As a result, the temperature of the backside of the roof where the heat insulating sheet was provided was lower than the temperature of the backside of the roof where the heat insulating sheet was not provided, and a maximum temperature difference of about 17 ° C. was recognized between the two.
Judging from the above results, it was confirmed that the heat-shielding sheet of the present invention had excellent heat-shielding properties due to its light-shielding effect.
[0054]
4. Heat insulation performance test B:
As a result of each of the above tests, the heat-insulating sheet produced in each of the examples of the present invention had excellent heat-shielding properties due to the light-shielding effect. A heat-insulating sheet was manufactured in which the amount of the pigment (titanium oxide) added and the amount of the filler (hollow glass balloon) were varied, and the same test as the incandescent lamp irradiation test of the heat-insulating performance test A was performed. The temperature of the back surface of the thermal sheet and the temperature in the box at that time were measured.
The results are summarized in Table 4 below. The optical density at that time is also shown.
[0055]
[Table 4]

[0056]
As can be seen from the results in the above table, the heat-insulating sheet of the present invention has a sheet layer thickness of 0.3 to 0.3 when both the filler (hollow glass balloon) and the pigment (titanium oxide) are contained. It is understood that substantially the same heat shielding performance was obtained even when the thickness was changed to 1.5 mm.
When the thickness of the sheet layer is 1.0 mm and the amount of the pigment (titanium oxide) is changed, the desired amount of the pigment (titanium oxide) is added in an amount of 3 parts by weight or more based on 100 parts by weight of the resin. It is understood that it has been obtained.
[0057]
【The invention's effect】
As described above, the present invention is a sheet or film formed by coating and curing a composition containing the above-mentioned components (A), (B) and (C). By doing so, heat shielding by the light ray shielding effect is achieved.
In particular, the heat-shielding effect of the sheet or film provided by the present invention is almost the same as that of the heat-shielding paints that have been proposed so far. Therefore, the roof and exterior of buildings such as factories and houses can be manufactured by a simpler method. The present invention has an advantage that it can be applied to a roof or an outer wall of a board, a transport vehicle such as a container or a freezer, and a roof or an outer wall of a ship, a plant, a shed, a barn, and the like.
Further, the obtained sheet or film has an advantage that it can be cut into a suitable shape to improve the design and appearance, and its industrial applicability is enormous.

Claims (5)

（Ａ）成分として、２５℃のもとで流動性を有し、官能基を有するアクリル樹脂、不飽和ポリエステル樹脂、エポキシ樹脂、シリコン樹脂またはゴム系樹脂成分からなり、
（Ｂ）成分として、上記の（Ａ）成分の官能基と反応する官能基を分子中に２個以上有する樹脂成分からなり、
（Ａ）成分と（Ｂ）成分からなる組成物を、離型性を有する紙または離型性を有するフィルム、基材にコーティングし、硬化させることによりフィルム状やシート状、層状に形成され、
該フィルムやシート、層状物の光学濃度が０．３〜２．０であり、かつ、明度が４０〜１００であることを特徴とする光線遮蔽材料。The component (A) comprises an acrylic resin, an unsaturated polyester resin, an epoxy resin, a silicone resin or a rubber-based resin component having fluidity at 25 ° C. and having a functional group,
The component (B) comprises a resin component having two or more functional groups in the molecule that react with the functional group of the component (A),
The composition comprising the component (A) and the component (B) is coated on a release paper or a release film, or a substrate, and cured to form a film, sheet, or layer,
A light-shielding material, wherein the optical density of the film, sheet, or layered material is 0.3 to 2.0, and the lightness is 40 to 100. （Ａ）成分として、２５℃のもとで流動性を有し、官能基を有するアクリル樹脂、不飽和ポリエステル樹脂、エポキシ樹脂、シリコン樹脂またはゴム系樹脂成分からなり、
（Ｂ）成分として、上記の（Ａ）成分の官能基と反応する官能基を分子中に２個以上有する樹脂成分からなり、
（Ｃ）成分として、ガラスビーズ、中空ガラスバルーンおよびマイクロカプセルから選ばれる１種以上のものであり、
（Ａ）成分、（Ｂ）成分および（Ｃ）成分からなる組成物を、離型性を有する紙または離型性を有するフィルム、基材にコーティングし、硬化させることによりフィルム状やシート状、層状に形成され、
該フィルムやシート、層状物の光学濃度が０．３〜２．０であり、かつ、明度が２０〜１００であることを特徴とする光線遮蔽材料。The component (A) comprises an acrylic resin, an unsaturated polyester resin, an epoxy resin, a silicone resin or a rubber-based resin component having fluidity at 25 ° C. and having a functional group,
The component (B) comprises a resin component having two or more functional groups in the molecule that react with the functional group of the component (A),
Component (C) is one or more selected from glass beads, hollow glass balloons and microcapsules,
The composition comprising the component (A), the component (B) and the component (C) is coated on a release paper or a release film or a substrate and cured to form a film or sheet. Formed in layers,
A light shielding material characterized in that the film, sheet or layered material has an optical density of 0.3 to 2.0 and a lightness of 20 to 100. （Ａ）成分の樹脂がアクリル樹脂である請求項１または２に記載の光線遮蔽材料。The light shielding material according to claim 1 or 2, wherein the resin as the component (A) is an acrylic resin. （Ａ）成分の樹脂が有する官能基が、水酸基、カルボキシル基、グリシジル基およびアミノ基から選ばれる少なくとも１種以上である請求項１〜３のいずれか１項に記載の光線遮蔽材料。The light shielding material according to any one of claims 1 to 3, wherein the functional group of the resin as the component (A) is at least one selected from a hydroxyl group, a carboxyl group, a glycidyl group, and an amino group. （Ｂ）成分が、イソシアネート化合物または酸無水物である請求項１〜４のいずれか１項に記載の光線遮蔽材料。The light shielding material according to any one of claims 1 to 4, wherein the component (B) is an isocyanate compound or an acid anhydride.