JP2004142780A

JP2004142780A - Lid material

Info

Publication number: JP2004142780A
Application number: JP2002309378A
Authority: JP
Inventors: Hirofumi Kawai; 河合　広文; Yukihiro Nakamura; 中村　行宏
Original assignee: Toppan Printing Co Ltd
Current assignee: Toppan Inc
Priority date: 2002-10-24
Filing date: 2002-10-24
Publication date: 2004-05-20

Abstract

<P>PROBLEM TO BE SOLVED: To provide a lid material mainly made of paper for use of a container for instant noodles or the like, which keeps conventional peeling strength in unsealing, does not increase in manufacturing cost, and is free from breakage of the lid material itself. <P>SOLUTION: The lid material 1 having an unsealing pull-tab along its outer periphery for sealing the upper end opening of a container body 2 has its outermost layer made of a paper layer 10, its intermediate layer made of an aluminum foil 20 and its innermost layer made of a sealant layer 30. The paper layer 10 and the aluminum foil 20 are stuck via an adhesive resin layer 14 formed by extruding a molten straight-chain low density polyethylene, thereby providing the lid material 1. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は、上端に開口部を有し、かつ上端周縁にフランジ部を有する容器本体の、前記フランジ部のシール密封に適した蓋材に関するものであり、特に即席麺等を収納し、熱湯を注いで食する容器の開口部をシール密封する紙を主体とした蓋材に関する。
【０００２】
【従来の技術】
従来、例えば即席麺や即席スープ等を収納する発泡ビーズ成形ポリスチレン容器で、上端に開口部を有し、かつ上端周縁にフランジ部を有する容器本体の前記フランジ部をシール等で密封する紙を主体とした蓋材として、紙層の下面にアルミニウム箔、易ピール性のシーラント層が積層されたものが知られ、その開封（開口）は、外周縁の開封用プルタブを摘んで引っ張り上げて、シーラント層面から剥離して成されるようになっている。
【０００３】
上記従来の蓋材の構成と積層する工程を更に具体的に説明すると、例えば図３の側断面積層図に示すように、表面に印刷層（１１）を有する最外層の紙層（１０）としては、坪量７９．１ｇ／ｍ２　の片アート紙、中間層には厚さ６μｍのアルミニウム箔（２０）、最内層の易ピール性のシーラント層（３０）として、厚さ２５μｍ程度の易剥離性樹脂、例えば低密度ポリエチレン樹脂にポリスチレンやポリブデン等ポリオレフインに対し不相溶性成分を混合したものなどがポリエチレンの押出しラミネートによって積層されているもので、上記紙層（１０）とアルミニウム箔（２０）とを溶融ポリエチレン樹脂を押し出した厚さ１５μｍのサンドポリエチレン層（１５）でラミネート（接着）せしめ、さらに上記アルミニウム箔（２０）面に上記易剥離性樹脂を押し出してシーラント層（３０）とするのが一般的である。
【０００４】
【発明が解決しようとする課題】
しかしながら、上記構成の従来の蓋材において、その開封（開口）に際し、例えば図４の斜視図に示すように、外周縁の開封用プルタブ（１２）を摘んで引っ張り上げて、容器本体（２）のフランジ部（２１）から、蓋材（１）のシーラント層面（３０ａ）を剥離すると、フランジ部（２１）から部分的に剥離されずに、その部分で蓋材（１）に破れが発生し、蓋材の一部（１ａ）がフランジ部（２１）に部分的に残ったりして、正常な開封ができない場合があるという問題があった。
【０００５】
これは、蓋材（１）自体の引裂き強度の弱さがあるのに加え、例えば内容物の充填ラインでのシール温度やその圧力のばらつき、あるいは容器本体とのズレなどにより、このシーラント層面（３０ａ）とフランジ部（２１）との接着強度が向上するためであり、それに顧客による剥離（引っ張り上げ）の速度等によっても発生するものであるが、少なくとも顧客がいかなる速度や力で剥離しても、引き裂き破れなどが起こったりせず、正常な開封ができるようにしなければならない。
【０００６】
従って上記問題解決の対策として、例えばシーラント層の剥離強度（接着強度）を低くするという方法があるが、この剥離強度をあまり低くすると輸送中等不必要時に剥がれたりするので好ましくなく、また、例えば図３に示す紙層（１０）とサンドポリエチレン層（１５）との間にポリエチレンテレフタレートフィルムをドライラミネーション用接着剤を介して積層したものとし、蓋材自体を破れにくくする方法もあるが、そのための工程数や材料（原反）が増える等によって製造コストが嵩むという問題があった。
【０００７】
本発明は、かかる従来技術の問題点を解決するものであり、その課題とするところは、紙を主体とし、容器の開口部をシール密封する蓋材において、その開封に際し、従来の剥離強度（容器のフランジ部と蓋材との）を維持しつつ、製造コストも嵩まず、蓋材自体に破れの発生が全くない蓋材を提供することにある。
【０００８】
【課題を解決するための手段】
本発明に於いて上記課題を達成するために、まず請求項１の発明では、容器本体の上縁開口部をシール密封する積層体で、外周縁に開封用プルタブを有する蓋材において、前記積層体は、最外層が紙層で、中間層がアルミニウム箔で、最内層がシーラント層でなり、前記最外層の紙層と中間層のアルミニウム箔とが直鎖状低密度ポリエチレンでなる接着性樹脂層を介して接着されていることを特徴とする蓋材としたものである。
【０００９】
上記請求項１の発明によれば、上記容器本体の上縁開口部をシール密封する積層体は、最外層が紙層で、中間層がアルミニウム箔で、最内層がシーラント層でなり、前記最外層の紙層と中間層のアルミニウム箔とが直鎖状低密度ポリエチレンでなる接着性樹脂層を介して接着されていて、特に耐引き裂き性（破断強さと伸び）があり、かつ接着性をも有する直鎖状低密度ポリエチレンでなる接着性樹脂層が紙層とアルミニウム箔との間に積層されているので、外周縁にある開封用プルタブを引っ張り上げて容器本体のフランジ部からシーラント層面で剥離すると、蓋材自体が破れることがなく正常な開封を可能にする蓋材とすることができる。
【００１０】
また、請求項２の発明では、上記直鎖状低密度ポリエチレンでなる接着性樹脂層は、直鎖状低密度ポリエチレンの溶融押出しで形成されていることを特徴とする請求項１記載の蓋材としたものである。
【００１１】
上記請求項２の発明によれば、直鎖状低密度ポリエチレンでなる接着性樹脂層は、直鎖状低密度ポリエチレンの溶融押出しで形成されているので、製造コストが嵩まずに紙層とアルミニウム箔とが一体化され、蓋材の剥離開封に際し、蓋材自体が破れにくくなり、かつ所定の接着強度が得られるので、この直鎖状低密度ポリエチレンでなる接着性樹脂層から剥離することがないので、より正常な開封を可能にする蓋材を提供できる。
【００１２】
【発明の実施の形態】
以下本発明の実施の形態を図面を用いて詳細に説明する。
【００１３】
本発明は、図１の斜視図に示すように、上端に開口部を有し、かつ上端周縁にフランジ部（２１）を有する容器本体（１０）の、そのフランジ部（２１）のシール密封に適した紙を主体とした蓋材（１）で、外周縁に開封用プルタブ（１２）を有し、特に例えば内容物として即席麺を収納し、その即席麺を食するに際し、その開封用プルタブ（１２）を摘んで引っ張り上げ、蓋材（１）の半分程度を開封し、その開封（開口）された部分から熱湯を注いで再度閉封し、しばらくした（略３分）後全開して食するための即席麺等容器の蓋材（１）に関するものである。
【００１４】
そこで上記請求項１に係る発明は、例えば図２（ａ）の側断面積層図に示すように、最外層が、表面に印刷層（１１）を有する紙層（１０）で、中間層がアルミニウム箔（２０）で、内容物に接する最内層がシーラント層（３０）でなる蓋材（１）において、この最外層の紙層（１０）と中間層のアルミニウム箔（２０）との間に直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）が積層されている蓋材（１）である。
【００１５】
このように破断強さと伸び性に優れることによる耐引裂き性を有し、さらに接着性もある直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）を最外層の紙層（１０）と中間層のアルミニウム箔（２０）との間に積層することによって、耐引裂き性（耐破れ性）が向上し、開封に際し、蓋材（１）自体の破れがなく、かつシーラント層に従来の易剥離性が維持されているので、容易に正常な開封が可能な蓋材（１）とすることができる。
【００１６】
また、例えば図２（ｂ）の側断面積層図に示すように、最外層が、表面に印刷層（１１）を有する紙層（１０）で、中間層がアルミニウム箔（２０）で、内容物に接する最内層がシーラント層（３０）でなる蓋材（１）において、この最外層の紙層（１０）と中間層のアルミニウム箔（２０）との間に直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）が積層されているのに加え、さらに中間層のアルミニウム箔（２０）と最内層のシーラント層（３０）との間に薄手の直鎖状低密度ポリエチレンでなる接着性樹脂層（１４ａ）が積層されている蓋材（１）とすることもできる。
【００１７】
このように耐引裂き性（耐破れ性）と接着性のある薄手の直鎖状低密度ポリエチレンでなる接着性樹脂層（１４ａ）を中間層のアルミニウム箔（２０）と最内層のシーラント層（３０）との間にも積層することによって、耐引裂き性（耐破れ性）がより向上し、よって開封に際し、更に蓋材（１）自体の破れがなくなり、かつ従来の易剥離性が維持され、容易に正常な開封が可能な蓋材（１）とすることができる。
【００１８】
また、請求項２に係る発明では、図２（ａ）および図２（ｂ）に示す直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）は直鎖状低密度ポリエチレンの溶融押出しで形成され、最外層の紙層（１０）と中間層のアルミニウム箔（２０）とを接着せしめている蓋材（１）としたものである。
【００１９】
上記のように直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）を融押出しで形成し接着せしめていることによって、例えば図３に示す従来の蓋材に比べて製造コストが嵩まず、かつ紙層（１０）とアルミニウム箔（２０）とが一体化され、蓋材自体がより破れにくくなり、かつ所定の接着強度が得られるので、この直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）から剥離したりすることもなく、正常な開封を可能にする蓋材（１）とすることができる。
【００２０】
以下に本発明の蓋材を構成する各層の材料等について説明する。
まず、上記本発明の蓋材（１）を構成する紙層（１０）としては、少なくとも表面が白色で多色印刷適性を有するものが好ましく、例えば坪量５０ｇ／ｍ２　〜１２０ｇ／ｍ２　程度、好ましくは７５ｇ／ｍ２　〜１００ｇ／ｍ２　程度の両アート紙、片アート紙あるいは両面コート紙、片面コート紙などを好適に使用することができる。
【００２１】
また、上記本発明の蓋材（１）を構成するアルミニウム箔（２０）としては、厚さ５〜９μｍ程度のもので、内容物（例えば乾燥麺等）を保護するための遮光性、ガスバリア性を有し、さらにこの蓋材の開封に際し、略半分を容器フランジ部から剥離すると、蓋材が外側にカールした状態を保つ性質（デットホールド性という）を有していて、その状態で熱湯を注いだりすることができる好適な材料として用いられる。
【００２２】
また、上記紙層（１０）とアルミニウム箔（２０）との間に設ける直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）としては、厚さ１５〜３０μｍの直鎖状低密度ポリエチレンでなり、この用途の場合はチーグラー・ナッタなどの触媒によるもの、あるいはシングルサイト触媒によるいずれのものでも構わない。この層の厚さが１５μｍに満たないと耐引裂き性（耐破れ性）に欠け、３０μｍを越えると押出しがしにくくなり、かつ材料コストが嵩むので好ましくない。
【００２３】
また、上記アルミニウム箔（２０）とシーラント層（３０）との間に設けられる場合の薄手の直鎖状低密度ポリエチレンでなる接着性樹脂層（１４ａ）は、厚さ１５μｍ程度とし、この場合のシーラント層（３０）の厚さを通常より５μｍ程度薄くした方が好ましい。
【００２４】
また、最内層のシーラント層（３０）としては、低温ヒートシール性と易剥離性（イージーピール性）を有するものが用いられ、例えば、厚さ２０μｍ〜５０μｍ程度の上記のような直鎖低密度ポリエチレン（ＬＬＤＰＥ）や低密度ポリエチレン（ＬＤＰＥ）、無延伸ポリプロピレン（ＣＰＰ）等のポリオレフィン系熱可塑性樹脂単独でも用いることができるが、これら樹脂のみでは接着性と易剥離性のバランスがとれないことが多いので、例えばこれらポリオレフィン系樹脂にポリスチレンやポリブデン等からなり、このポリオレフィン系樹脂に対し不相溶性成分を混合したものが好適に使用される。また、エチレン−酢酸ビニル共重合体、エチレン−アクリル酸共重合体等からなるホットメルト接着剤を塗布量１５〜２５ｇ／ｍ２　程度で設けてもよく、これらシーラント層（３０）によって、容器本体（２）のフランジ部（２１）との十分な密着性（接着性）と低温ヒートシール性、さらに易剥離性（イージーピール性）を有する蓋材（１）とすることができる。
【００２５】
【実施例】
次に実施例により、本発明を具体的に説明する。
【００２６】
まず実施例としての蓋材を作成するに当たり、以下の予備試験を行った。
〈予備試験〉
最外層の紙層（１０）に、坪量７９．１ｇ／ｍ２　の片アート紙を用い、中間層には厚さ６μｍのアルミニウム箔（２０）を用いて、この紙層（１０）とアルミニウム箔（２０）との間に、下記条件で厚さ２５μｍの直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）を形成した。
使用樹脂：シングルサイト触媒による直鎖状低密度ポリエチレン；ハーモレックスＮＨ７２５Ｎ、ＮＨ７４５Ｎ（日本ポリオレフィン社製）
接着温度としての押出用ダイスの直下温度：３００℃、３１０℃、３２０℃
処理条件：オゾン照射有り、無し
上記条件で形成した直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）の接着強度を測定し、表１に示した。
【００２７】
【表１】

【００２８】
上記表１から、オゾン照射有りでは、安定して所望の２．０Ｎ以上の接着強度が得られ、オゾン照射が無い場合でも樹脂温度を上げることによって２．０Ｎ近傍の接着強度が得られるものであった。
【００２９】
〈実施例１〉
最外層の紙層（１０）に、坪量７９．１ｇ／ｍ２　の片アート紙を用い、中間層には厚さ６μｍのアルミニウム箔（２０）を用いて、この紙層（１０）とアルミニウム箔（２０）との間に、シングルサイト触媒による直鎖状低密度ポリエチレン；ハーモレックスＮＨ７４５Ｎ（日本ポリオレフィン社製）を押出用ダイスの直下温度３００℃で押し出し、オゾン処理を行い厚さ２５μｍの直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）を形成した。
【００３０】
続いて上記で得られたアルミニウム箔（２０）面にドライラミネーション用接着剤を介して、ポリエチレンに不相溶性成分であるポリブデンを混合した厚さ２５μｍのイージーピールフィルム：ＣＦ７６０１（東レ合成社製）をシーラント層（３０）として加圧接着して積層体とし、その積層体を小断ちし、打ち抜いて１００ｍｍφの蓋材（１）を得た。
【００３１】
上記で得られた蓋材（１）を、発泡ビーズ成形ポリスチレン容器のフランジ部（２１）にヒートシールで密封して容器サンプルを作成した。
【００３２】
〈比較例１〉
上記直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）に代え、図３に示すように、溶融ポリエチレン樹脂を押し出して、その厚さが１５μｍのサンドポリエチレン層（１５）とした以外は、実施例１と同様にして容器サンプルを作成した。
【００３３】
上記実施例１および比較例１で得られたそれぞれ１０個の容器サンプルについて、蓋材の剥離試験を行ったところ、実施例１の容器サンプルでは１０個全てが、蓋材自体が破れることがなく正常な開封をするものであった。これに対し比較例１の容器サンプルでは１０個中の３個が蓋材自体に破れが発生し、正常な開封ができないものであった。なお実施例１に於ける直鎖状低密度ポリエチレンでなる接着性樹脂層（１４）の接着強度は、上記表１の如く平均２．５５Ｎでこの層の部分から剥離するという問題のないものであった。
【００３４】
【発明の効果】
本発明は以上の構成であるから、下記に示す如き効果がある。
即ち、上記請求項１に係る発明においては、容器本体の上縁開口部をシール密封する積層体で、外周縁に開封用プルタブを有する蓋材において、前記容器本体の上縁開口部をシール密封する積層体は、最外層が紙層で、中間層がアルミニウム箔で、最内層がシーラント層でなり、前記最外層の紙層と中間層のアルミニウム箔とが直鎖状低密度ポリエチレンでなる接着性樹脂層を介して接着されていて、特に耐引き裂き性（破断強さと伸び）があり、かつ接着性をも有する直鎖状低密度ポリエチレンでなる接着性樹脂層が紙層とアルミニウム箔との間に積層されているので、外周縁にある開封用プルタブを引っ張り上げて容器本体のフランジ部からシーラント層面で剥離すると、蓋材自体が破れることがなく正常な開封とすることができる。
【００３５】
また、上記請求項１に係る発明においては、直鎖状低密度ポリエチレンでなる接着性樹脂層は、直鎖状低密度ポリエチレンの溶融押出しで形成されているので、製造コストが嵩まずに紙層とアルミニウム箔とが一体化され、蓋材の剥離開封に際し、蓋材自体が破れにくくなり、かつ所定の接着強度が得られるので、この直鎖状低密度ポリエチレンでなる接着性樹脂層から剥離することがないので、より正常な開封を可能にする蓋材を提供できる。
【００３６】
従って本発明は、即席麺等を収納し、そのフランジ部にシール密封する紙を主体とした蓋材で、そのシール部から剥離して開封し、熱湯等を注いで食する容器の蓋材として、優れた実用上の効果を発揮する。
【図面の簡単な説明】
【図１】本発明の蓋材が適用される容器の一実施の形態を示す斜視図である。
【図２】本発明の蓋材の一実施の形態を示すもので、
（ａ）は、その側断面図であり、
（ｂ）は、他の事例の側断面図である。
【図３】従来の蓋材の一事例を側断面で表した説明図である。
【図４】従来の蓋材が適用される容器の開封状態の一事例を説明するための斜視図である。
【符号の説明】
１‥‥蓋材
１ａ‥‥フランジ部に残った蓋材の一部
２‥‥容器本体
１０‥‥紙層
１１‥‥印刷層
１２‥‥開封用蓋材
１４‥‥直鎖状低密度ポリエチレンでなる接着性樹脂層
１４ａ‥‥薄手の直鎖状低密度ポリエチレンでなる接着性樹脂層
１５‥‥サンドポリエチレン層
２０‥‥アルミニウム箔
２１‥‥フランジ部
３０‥‥シーラント層
３０ａ‥‥シーラント層面[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a container body having an opening at an upper end and a flange at an upper end periphery, which is suitable for sealing and sealing the flange, particularly for storing instant noodles and the like, and boiling water. The present invention relates to a lid material mainly made of paper for sealing an opening of a container to be poured and eaten.
[0002]
[Prior art]
Conventionally, for example, a foamed bead-shaped polystyrene container for storing instant noodles, instant soups and the like, which has an opening at the upper end and is mainly made of paper for sealing the flange portion of the container body having a flange portion at the upper peripheral edge with a seal or the like. As a cover material, a material in which an aluminum foil and an easily peelable sealant layer are laminated on the lower surface of a paper layer is known, and the opening (opening) is performed by picking up an opening pull tab on an outer peripheral edge and pulling up the sealant. It is made to peel off from the layer surface.
[0003]
The process of laminating the above-mentioned conventional lid member and the laminating step will be described more specifically. For example, as shown in the side sectional lamination diagram of FIG. 3, the outermost paper layer (10) having the printed layer (11) on the surface is used as Is a piece of art paper having a basis weight of 79.1 g / m 2, an aluminum foil (20) having a thickness of 6 μm as an intermediate layer, and an easily peelable layer having a thickness of about 25 μm as an innermost easily peelable sealant layer (30). A resin, for example, a low-density polyethylene resin mixed with an incompatible component to polyolefin such as polystyrene or polybutene is laminated by extrusion lamination of polyethylene. The paper layer (10) and the aluminum foil (20) Is laminated (adhered) with a 15 μm-thick sand polyethylene layer (15) extruded from a molten polyethylene resin, and further on the aluminum foil (20) surface. Generally, the easily peelable resin is extruded to form a sealant layer (30).
[0004]
[Problems to be solved by the invention]
However, in the conventional lid member having the above configuration, when opening (opening) the container body (2) by pinching and pulling up the opening pull tab (12) on the outer peripheral edge as shown in, for example, a perspective view of FIG. When the sealant layer surface (30a) of the lid material (1) is peeled off from the flange portion (21), the lid material (1) is broken at that portion without being partially peeled off from the flange portion (21). In addition, there has been a problem that a part of the lid material (1a) partially remains in the flange part (21), and normal opening cannot be performed.
[0005]
This is because the lid material (1) itself has a weak tearing strength, and in addition, due to variations in the sealing temperature and its pressure in the filling line of the contents or deviation from the container body, etc., this sealant layer surface ( This is because the adhesive strength between the flange 30a) and the flange portion (21) is improved, and this is also caused by the speed of peeling (pulling up) by the customer. Also, it must be possible to open normally without tearing or tearing.
[0006]
Therefore, as a countermeasure for solving the above problem, for example, there is a method of reducing the peel strength (adhesive strength) of the sealant layer. However, if the peel strength is too low, the sealant layer is unnecessarily peeled off during transportation or the like, which is not preferable. There is also a method in which a polyethylene terephthalate film is laminated between a paper layer (10) and a sand polyethylene layer (15) shown in No. 3 via an adhesive for dry lamination to make the lid itself difficult to tear. There is a problem that the manufacturing cost increases due to an increase in the number of processes and materials (raw materials).
[0007]
The present invention has been made to solve the problems of the prior art, and an object of the present invention is to provide a cover material mainly made of paper, which seals and seals an opening of a container. It is an object of the present invention to provide a lid material which maintains the flange portion of the container and the lid material, does not increase the production cost, and has no break in the lid material itself.
[0008]
[Means for Solving the Problems]
In order to achieve the above object in the present invention, first, in the invention according to claim 1, a laminated body for sealing and sealing an opening at an upper edge of a container body, wherein the lid having an opening pull tab on an outer peripheral edge thereof is provided. The body is an adhesive resin in which the outermost layer is a paper layer, the intermediate layer is an aluminum foil, the innermost layer is a sealant layer, and the outermost paper layer and the intermediate layer aluminum foil are linear low-density polyethylene. The lid material is characterized by being adhered via a layer.
[0009]
According to the first aspect of the present invention, in the laminate for sealing and sealing the upper edge opening of the container body, the outermost layer is a paper layer, the intermediate layer is an aluminum foil, and the innermost layer is a sealant layer. The paper layer of the outer layer and the aluminum foil of the intermediate layer are adhered through an adhesive resin layer made of linear low-density polyethylene, and particularly have tear resistance (breaking strength and elongation) and also have an adhesive property. Since the adhesive resin layer made of linear low-density polyethylene is laminated between the paper layer and the aluminum foil, the pull-up tab for opening on the outer peripheral edge is pulled up and peeled off from the flange portion of the container body on the sealant layer surface Then, it is possible to obtain a lid material that allows normal opening without breaking the lid material itself.
[0010]
In the invention according to claim 2, the adhesive resin layer made of the linear low-density polyethylene is formed by melt extrusion of the linear low-density polyethylene. It is what it was.
[0011]
According to the second aspect of the present invention, since the adhesive resin layer made of linear low-density polyethylene is formed by melt-extrusion of linear low-density polyethylene, the production cost is not increased and the paper layer and the aluminum layer are formed. The foil is integrated, and when the lid material is peeled and opened, the lid material itself is not easily broken, and a predetermined adhesive strength is obtained, so that the linear low-density polyethylene can be peeled from the adhesive resin layer. Since there is no cover material, it is possible to provide a lid material that enables more normal opening.
[0012]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.
[0013]
As shown in the perspective view of FIG. 1, the present invention is used for sealing and sealing a flange portion (21) of a container body (10) having an opening at an upper end and having a flange portion (21) at an upper peripheral edge. A suitable paper-based lid material (1) having an opening pull tab (12) on the outer peripheral edge, and particularly for storing instant noodles as contents, for example, when eating the instant noodles. (12) is picked up and pulled up, about half of the lid material (1) is opened, hot water is poured from the opened (opened) portion, and then closed again. After a while (about 3 minutes), the lid is fully opened. The present invention relates to a lid material (1) for a container for eating instant noodles.
[0014]
Therefore, the invention according to claim 1 is, for example, as shown in the side sectional view of FIG. 2 (a), wherein the outermost layer is a paper layer (10) having a printed layer (11) on the surface, and the intermediate layer is aluminum. In the foil (20), in the cover material (1) in which the innermost layer in contact with the contents is the sealant layer (30), the cover material (1) is placed directly between the outermost paper layer (10) and the intermediate aluminum foil (20). This is a lid (1) on which an adhesive resin layer (14) made of a chain low-density polyethylene is laminated.
[0015]
As described above, the adhesive resin layer (14) made of linear low-density polyethylene having tear resistance due to its excellent breaking strength and elongation properties and also having adhesiveness is provided between the paper layer (10) as the outermost layer and the intermediate layer. By laminating between the layer and the aluminum foil (20), the tear resistance (breaking resistance) is improved, and upon opening, the lid material (1) itself is not broken and the sealant layer is easily peeled off by the conventional method. Since the properties are maintained, the lid material (1) that can be easily opened normally can be obtained.
[0016]
For example, as shown in the side sectional view of FIG. 2B, the outermost layer is a paper layer (10) having a printed layer (11) on the surface, the intermediate layer is an aluminum foil (20), and the contents are In the cover material (1) in which the innermost layer in contact with the sealant layer (30) is a sealant layer (30), an adhesive made of linear low-density polyethylene is interposed between the outermost paper layer (10) and the intermediate aluminum foil (20). Adhesive resin made of thin linear low-density polyethylene between the aluminum foil (20) of the intermediate layer and the sealant layer (30) of the innermost layer in addition to the lamination of the conductive resin layer (14). The cover material (1) in which the layer (14a) is laminated can also be used.
[0017]
As described above, the adhesive resin layer (14a) made of a thin linear low-density polyethylene having tear resistance (tear resistance) and adhesive properties is applied to the intermediate aluminum foil (20) and the innermost sealant layer (30). ), The tear resistance (tear resistance) is further improved, so that upon opening, the lid material (1) itself does not tear, and the conventional easy peelability is maintained. The lid (1) can be easily opened normally.
[0018]
In the invention according to claim 2, the adhesive resin layer (14) made of linear low-density polyethylene shown in FIGS. 2 (a) and 2 (b) is formed by melt extrusion of linear low-density polyethylene. The cover material (1) is formed by bonding the outermost paper layer (10) and the intermediate aluminum foil (20).
[0019]
Since the adhesive resin layer (14) made of linear low-density polyethylene is formed by melt-extrusion and bonded as described above, the production cost is not increased as compared with, for example, the conventional lid material shown in FIG. In addition, since the paper layer (10) and the aluminum foil (20) are integrated, the lid material itself is less likely to be torn, and a predetermined adhesive strength is obtained, so that the adhesive resin layer made of this linear low-density polyethylene The cover (1) can be opened normally without peeling off from (14).
[0020]
Hereinafter, materials and the like of each layer constituting the lid material of the present invention will be described.
First, as the paper layer (10) constituting the lid material (1) of the present invention, one having at least a white surface and having multicolor printing aptitude is preferable, for example, a basis weight of about 50 g / m2 to 120 g / m2, and preferably about 50 g / m2 to 120 g / m2. Can be preferably used both art paper, single art paper, double-side coated paper, single-side coated paper of about 75 g / m 2 to 100 g / m 2.
[0021]
The aluminum foil (20) constituting the lid material (1) of the present invention has a thickness of about 5 to 9 μm, and is a light-shielding property and a gas barrier property for protecting contents (for example, dried noodles). In addition, when the lid is opened, substantially half of the lid is peeled off from the container flange, and the lid has a property of keeping a curled outward state (called dead hold property). Used as a suitable material that can be poured.
[0022]
The adhesive resin layer (14) made of linear low-density polyethylene provided between the paper layer (10) and the aluminum foil (20) may be a linear low-density polyethylene having a thickness of 15 to 30 μm. In this case, the catalyst may be a catalyst such as Ziegler-Natta or a single-site catalyst. If the thickness of this layer is less than 15 μm, tear resistance (breaking resistance) is lacking, and if it exceeds 30 μm, extrusion becomes difficult and the material cost increases, which is not preferable.
[0023]
The adhesive resin layer (14a) made of thin linear low-density polyethylene provided between the aluminum foil (20) and the sealant layer (30) has a thickness of about 15 μm. It is preferable to make the thickness of the sealant layer (30) about 5 μm thinner than usual.
[0024]
As the innermost sealant layer (30), one having low-temperature heat sealability and easy peelability (easy peelability) is used. For example, a linear low-density layer having a thickness of about 20 μm to 50 μm as described above is used. Polyolefin-based thermoplastic resins such as polyethylene (LLDPE), low-density polyethylene (LDPE), and unstretched polypropylene (CPP) can be used alone, but these resins alone may not balance adhesion and easy-peelability. For this reason, for example, a mixture of such a polyolefin-based resin made of polystyrene, polybutene, or the like, and an incompatible component mixed with the polyolefin-based resin is preferably used. Further, a hot melt adhesive composed of an ethylene-vinyl acetate copolymer, an ethylene-acrylic acid copolymer, or the like may be provided at a coating amount of about 15 to 25 g / m 2, and the sealant layer (30) allows the container body ( The cover material (1) having sufficient adhesion (adhesion) to the flange portion (21), low-temperature heat sealability, and easy peelability (easy peelability) of 2) can be obtained.
[0025]
【Example】
Next, the present invention will be specifically described with reference to examples.
[0026]
First, the following preliminary test was performed to prepare a lid material as an example.
<Preliminary test>
For the outermost paper layer (10), use art paper having a basis weight of 79.1 g / m2, and for the intermediate layer, use an aluminum foil (20) having a thickness of 6 μm. An adhesive resin layer (14) made of a linear low-density polyethylene having a thickness of 25 μm was formed between the adhesive resin layer and (20) under the following conditions.
Resin used: linear low-density polyethylene with single-site catalyst; Harmolex NH725N, NH745N (manufactured by Nippon Polyolefin Co., Ltd.)
Temperature immediately below the extrusion die as the bonding temperature: 300 ° C., 310 ° C., 320 ° C.
Treatment conditions: with and without ozone irradiation The adhesive strength of the adhesive resin layer (14) made of the linear low-density polyethylene formed under the above conditions was measured.
[0027]
[Table 1]

[0028]
From Table 1 above, it can be seen that with ozone irradiation, a desired adhesive strength of 2.0 N or more is stably obtained, and even without ozone irradiation, an adhesive strength of around 2.0 N can be obtained by increasing the resin temperature. there were.
[0029]
<Example 1>
For the outermost paper layer (10), use art paper having a basis weight of 79.1 g / m2, and for the intermediate layer, use an aluminum foil (20) having a thickness of 6 μm. Between (20) and a single-site catalyst, linear low-density polyethylene; Harmolex NH745N (manufactured by Nippon Polyolefin Co., Ltd.) is extruded at a temperature of 300 ° C. immediately below an extrusion die, subjected to ozone treatment, and subjected to a 25 μm-thick linear chain. An adhesive resin layer (14) made of a low-density polyethylene was formed.
[0030]
Subsequently, an easy peel film having a thickness of 25 μm obtained by mixing polybutene, which is an incompatible component with polyethylene, on the surface of the aluminum foil (20) obtained above via an adhesive for dry lamination: CF7601 (manufactured by Toray Gosei Co., Ltd.) As a sealant layer (30) by pressure bonding to form a laminate, and the laminate was cut into small pieces and punched out to obtain a lid material (1) having a diameter of 100 mm.
[0031]
The lid material (1) obtained above was sealed by heat sealing on the flange portion (21) of the polystyrene container molded with foam beads to prepare a container sample.
[0032]
<Comparative Example 1>
In place of the adhesive resin layer (14) made of the linear low-density polyethylene, as shown in FIG. 3, a molten polyethylene resin was extruded to form a sand polyethylene layer (15) having a thickness of 15 μm. A container sample was prepared in the same manner as in Example 1.
[0033]
When a peeling test of the lid material was performed on each of the ten container samples obtained in Example 1 and Comparative Example 1, all of the ten container samples of Example 1 did not break the lid material itself. It was a normal opening. On the other hand, in the container sample of Comparative Example 1, three out of ten containers had tears in the lid material itself, and could not be opened normally. The adhesive strength of the adhesive resin layer (14) made of linear low-density polyethylene in Example 1 was 2.55 N on average, as shown in Table 1 above, with no problem of peeling from this layer portion. there were.
[0034]
【The invention's effect】
The present invention having the above configuration has the following effects.
That is, in the invention according to the first aspect, in the lid member having the opening pull-tab on the outer peripheral edge, the upper edge opening of the container main body is sealed and sealed in the laminate that seals and seals the upper edge opening of the container main body. In the laminate, the outermost layer is a paper layer, the intermediate layer is an aluminum foil, the innermost layer is a sealant layer, and the outermost paper layer and the intermediate aluminum foil are bonded by a linear low-density polyethylene. The adhesive resin layer made of a linear low-density polyethylene having a tear resistance (breaking strength and elongation) and also having an adhesive property is bonded to the paper layer and the aluminum foil through the adhesive resin layer. Since it is laminated in between, when the pull tab for opening on the outer peripheral edge is pulled up and peeled off from the flange portion of the container body on the surface of the sealant layer, the lid material itself can be opened normally without being broken.
[0035]
Further, in the invention according to claim 1, since the adhesive resin layer made of linear low-density polyethylene is formed by melt extrusion of linear low-density polyethylene, the production cost does not increase and the paper layer is formed. And the aluminum foil are integrated, and when the lid material is peeled and opened, the lid material itself is not easily broken, and a predetermined adhesive strength is obtained, so that the linear low-density polyethylene is peeled off from the adhesive resin layer. Since there is no such thing, it is possible to provide a lid material that enables more normal opening.
[0036]
Therefore, the present invention is a lid material mainly made of paper for storing instant noodles and the like, and sealing and sealing the flange portion thereof. The lid material is peeled off from the seal portion and opened, and poured as boiling water or the like as a lid material for a container. It has excellent practical effects.
[Brief description of the drawings]
FIG. 1 is a perspective view showing an embodiment of a container to which a lid material of the present invention is applied.
FIG. 2 shows an embodiment of the lid material of the present invention,
(A) is a side sectional view thereof,
(B) is a side sectional view of another case.
FIG. 3 is an explanatory diagram showing an example of a conventional lid member in a side cross section.
FIG. 4 is a perspective view illustrating an example of an opened state of a container to which a conventional lid member is applied.
[Explanation of symbols]
1 lid material 1a part of the lid material remaining in the flange portion 2 container body 10 paper layer 11 printing layer 12 opening lid material 14 linear low-density polyethylene Adhesive resin layer 14a１４adhesive resin layer 15 made of thin linear low-density polyethylene ‥‥ sand polyethylene layer 20 ‥‥ aluminum foil 21 ‥‥ flange 30 ‥‥ sealant layer 30a ‥‥ sealant layer surface

Claims

容器本体の上縁開口部をシール密封する積層体で、外周縁に開封用プルタブを有する蓋材において、前記積層体は、最外層が紙層で、中間層がアルミニウム箔で、最内層がシーラント層でなり、前記最外層の紙層と中間層のアルミニウム箔とが直鎖状低密度ポリエチレンでなる接着性樹脂層を介して接着されていることを特徴とする蓋材。In a lid member that seals and seals an opening at an upper edge of a container body, the lid member having an opening pull tab on an outer peripheral edge thereof, wherein the outermost layer is a paper layer, an intermediate layer is an aluminum foil, and an innermost layer is a sealant. A lid material, wherein the outermost paper layer and the intermediate aluminum foil are adhered via an adhesive resin layer made of linear low-density polyethylene.

上記直鎖状低密度ポリエチレンでなる接着性樹脂層は、直鎖状低密度ポリエチレンの溶融押出しで形成されていることを特徴とする請求項１記載の蓋材。The lid material according to claim 1, wherein the adhesive resin layer made of the linear low-density polyethylene is formed by melt extrusion of the linear low-density polyethylene.