JP2004109458A - Display member utilizing hydrophilic function and method for forming the same - Google Patents
Display member utilizing hydrophilic function and method for forming the same Download PDFInfo
- Publication number
- JP2004109458A JP2004109458A JP2002271619A JP2002271619A JP2004109458A JP 2004109458 A JP2004109458 A JP 2004109458A JP 2002271619 A JP2002271619 A JP 2002271619A JP 2002271619 A JP2002271619 A JP 2002271619A JP 2004109458 A JP2004109458 A JP 2004109458A
- Authority
- JP
- Japan
- Prior art keywords
- display
- hydrophilic
- water
- coating agent
- function
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】
【発明の属する技術分野】
本発明は、例えば、基材上に親水性コーティング剤で文字や図形などの表示対象を描くように塗布することによって、基材上に親水機能を有する部分と有しない部分を作成し、その親水機能の有無により宣伝広告などの表示を行わせる表示部材及びその作成方法に関するものである。
【０００２】
【従来の技術】
従来から、基材上に光触媒などの親水性コーティング剤を塗布して、基材表面に親水性を付与し、濡れ性の向上による水滴付着防止、防曇性といった機能や、基材表面が汚れ難くなるという防汚機能などを発揮するようにした製品は、数多く存在している。
【０００３】
また、光触媒以外の親水性コーティング剤としては、アルコキシシラン等の加水分解性シラン化合物にスルホン酸基等の親水性官能基を導入した化合物を被膜形成成分とするコーティング液がある（例えば、特許文献１参照）。
【０００４】
【特許文献１】
特開２００２−６０６９２号公報
【０００５】
【発明が解決しようとする課題】
従来技術では、基材上に親水機能や撥水機能などを付与した部材は作成されていたが、その機能目的は主に防汚や耐候性といったものであり、その機能を利用して親水性コーティング剤で表示対象を描くことにより、宣伝広告などの表示手段とすることは、これまで行われていなかった。
【０００６】
本発明は上記の諸点に鑑みなされたもので、本発明の目的は、例えば、基材上に親水性コーティング剤で文字や図形などの表示対象を描くように塗布することによって、基材上に親水機能を有する部分と有しない部分を作成し、その親水機能の有無により宣伝広告などの表示を行わせる表示部材及びその作成方法を提供することにある。
【０００７】
【課題を解決するための手段】
上記の目的を達成するために、本発明の親水機能を利用した表示部材は、基材に対し、親水性コーティング剤で文字、図形又は記号又はこれらの結合からなる表示対象を描くように塗布することによって、基材上に親水性を有する表示部分と親水性を有しない背景部分を作成し、その親水機能の有無により水滴の付着しない表示対象を浮かび上がらせるように構成されている。
【０００８】
また、本発明の表示部材は、表面が撥水性を有する基材に対し、親水性コーティング剤で文字、図形又は記号又はこれらの結合からなる表示対象を描くように塗布することによって、基材上に親水性を有する表示部分と逆に撥水性を有する背景部分を作成し、撥水性を有する背景部分に対して親水性を有する表示対象を水滴付着の有無により顕著に浮かび上がらせるようにしたことを特徴としている。
【０００９】
上記の表示部材においては、特に防汚機能を有する親水性コーティング剤を用いて、基材上に汚れの付着しにくい表示部分を作成することで、汚れの付着しやすい背景部分との防汚機能の差により表示対象を顕著に浮かび上がらせることが可能である。
【００１０】
また、本発明の表示部材は、基材に対して文字、図形又は記号又はこれらの結合からなる表示対象を描くに際し、基材の表示対象以外の部分に親水性コーティング剤を塗布することによって、基材上に親水性を有する背景部分と親水性を有しない表示部分を作成し、その親水機能の有無により水滴の付着しやすい表示対象を浮かび上がらせるようにしたことを特徴としている。
【００１１】
上記の表示部材においては、撥水性材料で文字、図形又は記号又はこれらの結合からなる表示対象を描くように塗布することによって、基材上に親水性を有する背景部分と逆に撥水性を有する表示部分を作成し、親水性を有する背景部分に対して撥水性を有する表示対象を水滴付着の有無により顕著に浮かび上がらせるようにすることができる。
【００１２】
これらの表示部材においては、特に防汚機能を有する親水性コーティング剤を用いて、基材上に汚れの付着しにくい背景部分を作成することで、この背景部分との防汚機能の差により表示対象を顕著に浮かび上がらせることが可能である。また、表示対象は、一例として、宣伝広告を目的とした文字、図形又は記号又はこれらの結合とすることができる。
【００１３】
本発明の親水機能を利用した表示部材の作成方法は、基材に対し、親水性コーティング剤で文字、図形又は記号又はこれらの結合からなる表示対象を描くように塗布して、基材上に親水性を有する表示部分と親水性を有しない背景部分を作成し、その親水機能の有無により水滴の付着しない表示対象を浮かび上がらせて表示を行わせる部材とすることを特徴としている。
【００１４】
また、本発明の表示部材の作成方法は、表面が撥水性を有する基材に対し、親水性コーティング剤で文字、図形又は記号又はこれらの結合からなる表示対象を描くように塗布して、基材上に親水性を有する表示部分と逆に撥水性を有する背景部分を作成し、撥水性を有する背景部分に対して親水性を有する表示対象を水滴付着の有無により顕著に浮かび上がらせて表示を行わせる部材とすることを特徴としている。
【００１５】
上記の方法においては、親水性コーティング剤として防汚機能を有する親水性コーティング剤を用い、基材上に汚れの付着しにくい表示部分を作成することで、汚れの付着しやすい背景部分との防汚機能の差により表示対象を顕著に浮かび上がらせることが好ましい。
【００１６】
また、本発明の表示部材の作成方法は、基材に対して文字、図形又は記号又はこれらの結合からなる表示対象を描くに際し、基材の表示対象以外の部分に親水性コーティング剤を塗布して、基材上に親水性を有する背景部分と親水性を有しない表示部分を作成し、その親水機能の有無により水滴の付着しやすい表示対象を浮かび上がらせて表示を行わせる部材とすることを特徴としている。
【００１７】
上記の方法においては、撥水性材料で文字、図形又は記号又はこれらの結合からなる表示対象を描くように塗布して、基材上に親水性を有する背景部分と逆に撥水性を有する表示部分を作成し、親水性を有する背景部分に対して撥水性を有する表示対象を水滴付着の有無により顕著に浮かび上がらせて表示を行わせる部材とすることができる。
【００１８】
これらの方法においては、親水性コーティング剤として防汚機能を有する親水性コーティング剤を用い、基材上に汚れの付着しにくい背景部分を作成することで、この背景部分との防汚機能の差により表示対象を顕著に浮かび上がらせることが可能である。
【００１９】
【発明の実施の形態】
以下、本発明の実施の形態について説明するが、本発明は下記の実施の形態に何ら限定されるものではなく、適宜変更して実施することが可能なものである。例えば、図１に示すような宣伝広告部材を考えた場合、宣伝広告媒体となる基材１０上に、図及び文字等からなる宣伝広告を目的とした表示対象１２を描くように親水性コーティング剤を塗布する。
【００２０】
例えば、宣伝広告媒体となる基材１０としてガラスなどの透明基板を用い、この透明基板上に、宣伝広告を目的とした表示対象１２である図や文字（図１では、一例として、「川崎重工」の文字及びそのシンボルマーク）を親水性コーティング剤で描いた場合、雨などの水が付いていない状態では無色透明で何も見えない透明物であるが、雨などの水が付着すると、濡れ性のよい図や文字の表示対象１２の部分には水滴が付着せず、濡れ性の悪い背景部分の基材１０上には水滴が付着していくため、全体として宣伝広告部材の表面に付着する水滴の有無によって、宣伝広告を目的とした表示対象１２を浮かび上がらせることができる。なお、図１では、便宜上、表示対象１２を黒塗りとしている。なお、宣伝広告対象となる図や文字等を親水性塗料で塗布しても、同様の効果が得られる。
また、宣伝広告媒体となる基材１０としてアクリル板などの撥水性を有する透明基材を用いた場合は、背景となる撥水性部分に対して表示対象を描いた親水性部分が顕著に浮かび上がり、より一層、その親水性の有無によって水滴付着箇所がくっきりと見えるようになり、その効果は非常に大きくなる。
【００２１】
親水性コーティング剤、親水性塗料としては、一例として、カルボン酸基のような親水性官能基を有する化合物をアルコール又は高分子系有機溶媒（例えば、ポリビニルアルコール等）に溶解させたコーティング液、親水機能を有するジルコニウム酸化物を主成分とする分散液、酸化チタンを主成分とする光触媒を含有する親水機能を保有した液などを用いることができる。
また、親水性コーティング剤、親水性塗料のような液ではなく、表面処理により基材上を親水化させる方法もある。例えば、酸素プラズマ処理などによって、親水性の官能基を基材表面に導入することで、表面（表示部分）を親水化させることも可能である。
【００２２】
次に、例えば、宣伝広告媒体となる基材１０として塗装鋼板などを用い、この塗装鋼板上に、宣伝広告を目的とした表示対象１２である図や文字（図１では、一例として、「川崎重工」の文字及びそのシンボルマーク）を上述したような親水性コーティング剤（又は親水性塗料）で描いた場合について説明する。なお、上記のように、表面処理により基材上を親水化させてもよい。
表示対象１２である図や文字の部分のみに無色透明の親水性コーティング剤を塗布すると、この部材を汚れやすい屋外などで使用するにつれて、濡れ性のよい図や文字の表示対象１２の部分には雨筋汚れなどの汚れが付着しにくく、濡れ性の悪い背景部分の基材１０上にはそのような汚れが付着していくため、汚れの付着度合の差により、基材１０上に宣伝広告を目的とした表示対象１２を浮かび上がらせることができる。もちろん、水滴付着の有無によっても表示対象１２を浮かび上がらせることができる。
また、宣伝広告媒体となる基材１０として、塗装鋼板等の基材に撥水性のフッ素系塗料などを塗布したものを用いた場合は、撥水性の背景部分が特に汚れやすくなるため、その汚れ付着度合の違いがより一層明白になり、撥水性の背景部分に対して表示対象を描いた親水性部分が顕著に浮かび上がり、その効果は非常に大きくなる。
【００２３】
以上説明した方法においては、親水性コーティング剤（又は親水性塗料）を使用する箇所、又は酸素プラズマ処理などにより親水性官能基を導入する箇所を、表示対象１２である図や文字ではなく、逆に背景部分となる基材１０としても、水滴付着箇所や汚れ付着度合が表示対象１２と基材１０とで逆になるだけで、表示手段としては同様の効果が得られる。
【００２４】
例えば、図２において、宣伝広告媒体となる基材１０に対し、図及び文字等からなる宣伝広告を目的とした表示対象１２を描くに際し、基材１０上の表示対象１２以外の部分、すなわち、背景部分１４に親水性コーティング剤を塗布する。一例として、宣伝広告媒体となる基材１０としてガラスなどの透明基板を用い、この透明基板上に、宣伝広告を目的とした表示対象１２である図や文字（図２では、一例として、「川崎重工」の文字及びそのシンボルマーク）を描く場合、上述したような親水性コーティング剤を表示対象１２以外の背景部分１４に塗布する。この場合、雨などの水が付いていない状態では無色透明で何も見えない透明物であるが、雨などの水が付着すると、濡れ性のよい背景部分１４には水滴が付着せず、濡れ性の悪い図や文字の表示対象１２の部分には水滴が付着していくため、全体として宣伝広告部材の表面に付着する水滴の有無によって、宣伝広告を目的とした表示対象１２を浮かび上がらせることができる。なお、図２では、便宜上、表示対象１２を黒塗りとしている。なお、背景部分１４に上述したような親水性塗料を塗布しても、同様の効果が得られる。また、上述のように、表面処理により基材上を親水化させてもよい。
【００２５】
また、表示対象１２である図や文字等を撥水性コーティング剤で描くように塗布すれば、背景となる親水性部分に対して表示対象を描いた撥水性部分が顕著に浮かび上がり、より一層、その親水性の有無によって水滴付着箇所がくっきりと見えるようになり、その効果は非常に大きくなる。撥水性コーティング剤としては、一例として、フルオロアルキル基を有する化合物（例えば、ポリテトラフルオロエチレンなど）を用いることができる。なお、基材１０としてアクリル板などの撥水性を有する透明基材を用いても、同様の効果が得られる。
【００２６】
次に、例えば、宣伝広告媒体となる基材１０として塗装鋼板などを用い、この塗装鋼板上に、宣伝広告を目的とした表示対象１２である図や文字（図２では、一例として、「川崎重工」の文字及びそのシンボルマーク）を描く場合、上述したような親水性コーティング剤を表示対象１２以外の背景部分１４に塗布する。なお、上記のように、表面処理により基材上を親水化させてもよい。
表示対象１２である図や文字の部分以外の背景部分１４に無色透明の親水性コーティング剤を塗布すると、この部材を汚れやすい屋外などで使用するにつれて、濡れ性のよい背景部分１４には雨筋汚れなどの汚れが付着しにくく、濡れ性の悪い図や文字の表示対象１２の部分にはそのような汚れが付着していくため、汚れの付着度合の差により、基材１０上に宣伝広告を目的とした表示対象１２を浮かび上がらせることができる。もちろん、水滴付着の有無によっても表示対象１２を浮かび上がらせることができる。
【００２７】
また、表示対象１２である図や文字等を上述したような撥水性コーティング剤で描くように塗布すれば、撥水性の表示対象１２が特に汚れやすくなるため、その汚れ付着度合の違いがより一層明白になり、親水性の背景部分１４に対して表示対象１２を描いた撥水性部分が顕著に浮かび上がり、その効果は非常に大きくなる。なお、基材１０として、塗装鋼板等の基材に撥水性のフッ素系塗料などを塗布したものを用いても、同様の効果が得られる。
また、以上説明した実施の形態では、宣伝広告を目的とした表示対象について説明しているが、表示対象は、宣伝広告を目的とするものに限定されず、あらゆる目的で表示を行う場合を対象とすることができる。
【００２８】
【発明の効果】
本発明は上記のように構成されているので、つぎのような効果を奏する。
（１） 基材上に親水性コーティング剤で文字や図形などの表示対象を描くように塗布することによって、基材上に親水機能を有する部分と有しない部分を作成し、その親水機能の有無により宣伝広告などの表示を行わせることができる。
（２） 特に防汚機能を有する親水性コーティング剤を用いることで、基材上に汚れの付着しにくい表示部分と汚れの付着しやすい背景部分ができ、その防汚機能の差により表示対象を顕著に浮かび上がらせ、宣伝広告などの表示を行わせることができる。
（３） 基材として撥水性を有する基材を用いる場合は、背景となる撥水性部分と表示対象を描いた親水性部分の水滴付着の有無や汚れ付着度合の違いがより一層明白になり、背景部分に対して表示対象がより顕著に浮かび上がり、その効果は非常に大きくなる。
（４） 親水性コーティング剤を使用する箇所を、表示対象である図や文字等ではなく、逆に背景部分となる基材としても、水滴付着箇所や汚れ付着度合が表示対象と基材とで逆になるだけで、表示手段としては同様の効果が得られる。
【図面の簡単な説明】
【図１】本発明の親水機能を利用した表示部材の一例である宣伝広告部材を示す模式図である。
【図２】本発明の親水機能を利用した表示部材の他の例である宣伝広告部材を示す模式図である。
【符号の説明】
１０ 基材
１２ 表示対象
１４ 背景部分[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention, for example, by applying a hydrophilic coating agent on a substrate so as to draw a display object such as a character or a graphic, to create a portion having a hydrophilic function and a portion having no hydrophilic function on the substrate, the hydrophilic The present invention relates to a display member for displaying an advertisement or the like depending on the presence or absence of a function and a method for producing the same.
[0002]
[Prior art]
Conventionally, a hydrophilic coating agent such as a photocatalyst is applied on a substrate to impart hydrophilicity to the substrate surface, prevent water droplet adhesion by improving wettability, prevent fogging, and stain the substrate surface. There are many products that exhibit an antifouling function, which is difficult.
[0003]
Further, as a hydrophilic coating agent other than the photocatalyst, there is a coating liquid containing, as a film-forming component, a compound obtained by introducing a hydrophilic functional group such as a sulfonic acid group into a hydrolyzable silane compound such as an alkoxysilane. 1).
[0004]
[Patent Document 1]
JP-A-2002-60692
[Problems to be solved by the invention]
In the prior art, members with a hydrophilic function or a water-repellent function were created on a substrate, but the purpose of the function is mainly antifouling and weather resistance. Until now, it has not been used as a display means such as an advertisement by drawing a display object with a coating agent.
[0006]
The present invention has been made in view of the above points, an object of the present invention is, for example, by applying a hydrophilic coating agent on a substrate to draw a display object such as characters and figures, on the substrate It is an object of the present invention to provide a display member that creates a portion having a hydrophilic function and a portion not having the hydrophilic function, and displays an advertisement or the like based on the presence or absence of the hydrophilic function, and a method for producing the same.
[0007]
[Means for Solving the Problems]
In order to achieve the above object, the display member utilizing the hydrophilic function of the present invention is applied to a substrate with a hydrophilic coating agent so as to draw a display object consisting of characters, figures or symbols or a combination thereof. Thus, a display portion having hydrophilicity and a background portion having no hydrophilicity are formed on the base material, and a display object to which water droplets do not adhere is made to emerge depending on the presence or absence of the hydrophilic function.
[0008]
In addition, the display member of the present invention is applied to a substrate having a water-repellent surface with a hydrophilic coating agent so as to draw a display object consisting of characters, figures, or symbols or a combination thereof, so that the substrate is coated on the substrate. A background portion having water repellency is created on the contrary to a display portion having hydrophilicity, and a display object having hydrophilicity with respect to the background portion having water repellency is made to remarkably emerge depending on the presence or absence of water droplets. Features.
[0009]
In the display member described above, a display portion to which dirt is hardly adhered is formed on a substrate by using a hydrophilic coating agent having an antifouling function, so that an antifouling function with a background portion to which dirt is easily adhered. , It is possible to remarkably raise the display target.
[0010]
Further, the display member of the present invention, when drawing a display object consisting of characters, graphics or symbols or a combination thereof on the base material, by applying a hydrophilic coating agent to a portion other than the display target of the base material, The present invention is characterized in that a background portion having hydrophilicity and a display portion having no hydrophilicity are formed on a substrate, and a display object to which water droplets easily adhere is made to emerge depending on the presence or absence of the hydrophilic function.
[0011]
In the above display member, by applying a character, a graphic or a symbol or a display object composed of a combination thereof with a water-repellent material so as to draw the object, it has a water-repellency opposite to the background portion having hydrophilicity on the base material. By forming a display portion, a display object having water repellency with respect to a background portion having hydrophilicity can be made to prominently appear depending on whether or not water droplets adhere.
[0012]
In these display members, a hydrophilic coating agent having an antifouling function is used to create a background portion on which dirt does not easily adhere to the base material. It is possible to make the subject stand out significantly. The display target can be, for example, a character, a graphic, a symbol, or a combination thereof for the purpose of advertising.
[0013]
The method for producing a display member utilizing the hydrophilic function of the present invention is applied to a base material with a hydrophilic coating agent so as to draw a display object consisting of characters, figures or symbols or a combination thereof, and is applied on the base material. It is characterized in that a display portion having hydrophilicity and a background portion having no hydrophilicity are formed, and a display object to which water droplets are not adhered is displayed depending on the presence or absence of the hydrophilicity so as to perform display.
[0014]
In addition, the method for producing a display member of the present invention is characterized in that a substrate having a water-repellent surface is coated with a hydrophilic coating agent so as to draw a display object consisting of characters, figures, or symbols or a combination thereof, and Create a background portion having water repellency on the opposite side of the display portion having hydrophilicity on the material, and display the display object having hydrophilicity against the background portion having water repellency by prominently prominent depending on the presence or absence of water droplets. It is characterized in that it is a member to be performed.
[0015]
In the above method, a hydrophilic coating agent having an antifouling function is used as a hydrophilic coating agent, and a display portion on which dirt is hardly adhered is formed on a base material, thereby preventing a background portion on which dirt is easily adhered from being formed. It is preferable that the display target is remarkably raised due to the difference in the stain function.
[0016]
Further, in the method of producing a display member of the present invention, when drawing a display object consisting of characters, graphics, or symbols or a combination thereof on a base material, applying a hydrophilic coating agent to a portion other than the display target of the base material. By creating a background portion having hydrophilicity and a display portion having no hydrophilicity on the base material, the display target that is likely to adhere to water droplets depending on the presence or absence of the hydrophilic function is made to be a member that performs display. Features.
[0017]
In the above method, a display portion having a water-repellent material is applied by drawing a character, a figure or a symbol or a display object composed of a combination thereof, so that a display portion having a water-repellent property is provided on the base material in contrast to a hydrophilic background portion. Is formed, and a display object having water repellency with respect to a background portion having hydrophilicity can be made to be a member that performs display by prominently rising depending on the presence or absence of water droplets.
[0018]
In these methods, a hydrophilic coating agent having an antifouling function is used as a hydrophilic coating agent, and a background portion on which dirt is hardly adhered is formed on the substrate, so that the difference in the antifouling function from the background portion is obtained. Thereby, the display target can be remarkably raised.
[0019]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, embodiments of the present invention will be described. However, the present invention is not limited to the following embodiments, and can be implemented with appropriate modifications. For example, when an advertisement member as shown in FIG. 1 is considered, a hydrophilic coating agent is drawn on a base material 10 serving as an advertisement medium so as to draw a display object 12 for the purpose of advertisement including figures and characters. Is applied.
[0020]
For example, a transparent substrate made of glass or the like is used as a base material 10 serving as an advertisement medium, and on this transparent substrate, a figure or a character which is a display target 12 for the purpose of an advertisement (in FIG. 1, as an example, “Kawasaki Heavy Industries Is drawn with a hydrophilic coating agent, it is colorless and transparent in the absence of water, such as rain, and is transparent. However, if water such as rain adheres, it becomes wet. Water droplets do not adhere to the portion of the display object 12 with good figures and characters, and water droplets adhere to the base material 10 in the background portion having poor wettability, and thus adhere to the surface of the advertisement member as a whole. Depending on the presence or absence of the water droplets, the display target 12 for the purpose of advertising can be made to emerge. In FIG. 1, the display object 12 is painted black for convenience. Note that the same effect can be obtained even when a figure, a character, or the like to be subjected to the advertisement is applied with a hydrophilic paint.
Also, when a transparent substrate having a water repellency such as an acrylic plate is used as the substrate 10 serving as an advertising medium, the hydrophilic portion depicting the display object stands out from the water repellent portion serving as the background. Further, depending on the presence / absence of the hydrophilic property, the location where the water droplet adheres can be clearly seen, and the effect becomes very large.
[0021]
Examples of the hydrophilic coating agent and the hydrophilic paint include a coating solution obtained by dissolving a compound having a hydrophilic functional group such as a carboxylic acid group in an alcohol or a polymer organic solvent (for example, polyvinyl alcohol). A dispersion liquid containing a zirconium oxide having a function as a main component, a liquid containing a photocatalyst containing a titanium oxide as a main component and having a hydrophilic function, or the like can be used.
There is also a method of making the surface of a substrate hydrophilic by surface treatment instead of a liquid such as a hydrophilic coating agent or a hydrophilic paint. For example, the surface (display portion) can be made hydrophilic by introducing a hydrophilic functional group into the surface of the base material by oxygen plasma treatment or the like.
[0022]
Next, for example, a painted steel plate or the like is used as a base material 10 serving as an advertising medium, and figures and characters (in FIG. 1, as an example, “Kawasaki A description will be given of a case in which the characters “heavy work” and its symbol mark) are drawn with the above-described hydrophilic coating agent (or hydrophilic paint). As described above, the surface of the substrate may be made hydrophilic by surface treatment.
When a colorless and transparent hydrophilic coating agent is applied only to the portion of the figure or character that is the display object 12, as this member is used outdoors or the like where it is easily soiled, the portion of the display object 12 of the figure or character with good wettability is applied. Since dirt such as rain streak dirt does not easily adhere to the base material 10 in the background portion having poor wettability, such a dirt adheres to the base material 10. The display object 12 for the purpose of (1) can be raised. Of course, the display target 12 can also be raised depending on whether or not water droplets are attached.
Further, when a substrate such as a coated steel plate coated with a water-repellent fluorine-based paint or the like is used as the substrate 10 serving as an advertising medium, the background portion of the water-repellent is particularly easily stained. The difference in the degree of adhesion becomes even more apparent, and the hydrophilic portion depicting the display object stands out against the water-repellent background portion, and the effect becomes extremely large.
[0023]
In the method described above, the location where a hydrophilic coating agent (or hydrophilic paint) is used, or the location where a hydrophilic functional group is introduced by oxygen plasma treatment or the like is not indicated by the figure or character that is the display object 12 but by the reverse. In addition, the same effect can be obtained as the display means for the substrate 10 as the background portion, except that the locations of water droplets and the degree of contamination are reversed between the display target 12 and the substrate 10.
[0024]
For example, in FIG. 2, when drawing a display target 12 for the purpose of advertisement including figures and characters on a base material 10 serving as an advertisement medium, a portion other than the display target 12 on the base material 10, that is, A hydrophilic coating agent is applied to the background portion 14. As an example, a transparent substrate such as glass is used as a base material 10 serving as an advertisement medium, and a figure or a character as a display target 12 for the purpose of an advertisement (in FIG. 2, as an example, “Kawasaki In the case of drawing the character “Heavy Work” and its symbol mark), the above-described hydrophilic coating agent is applied to the background portion 14 other than the display target 12. In this case, the transparent material is colorless and transparent when there is no water such as rain, but when water such as rain adheres, water drops do not adhere to the background portion 14 having good wettability, and Since water droplets adhere to portions of the display object 12 of poorly-characterized figures or characters, the display object 12 for the purpose of advertising is raised depending on the presence or absence of water droplets adhering to the surface of the advertising material as a whole. Can be. In FIG. 2, the display target 12 is painted black for convenience. The same effect can be obtained by applying the above-described hydrophilic paint to the background portion 14. Further, as described above, the surface of the substrate may be made hydrophilic by surface treatment.
[0025]
In addition, if the drawing or the character as the display object 12 is applied so as to be drawn with the water-repellent coating agent, the water-repellent portion of the display object is remarkably drawn with respect to the hydrophilic portion serving as the background. Depending on the presence or absence of the hydrophilicity, the location where the water droplets adhere can be clearly seen, and the effect becomes very large. As an example of the water-repellent coating agent, a compound having a fluoroalkyl group (for example, polytetrafluoroethylene or the like) can be used. The same effect can be obtained by using a transparent substrate having water repellency such as an acrylic plate as the substrate 10.
[0026]
Next, for example, a painted steel plate or the like is used as a base material 10 serving as an advertising medium, and a figure or a character which is a display object 12 for the purpose of advertising (for example, in FIG. In the case of drawing the character “Heavy Work” and its symbol mark), the above-described hydrophilic coating agent is applied to the background portion 14 other than the display target 12. As described above, the surface of the substrate may be made hydrophilic by surface treatment.
When a colorless and transparent hydrophilic coating agent is applied to the background portion 14 other than the portion of the figure or the character which is the display object 12, as this member is used outdoors or the like which is easily contaminated, the background portion 14 having good wettability is provided with a rain streak. Dirt such as dirt does not easily adhere, and such dirt adheres to the portion of the display target 12 of the figure or character with poor wettability. The display object 12 for the purpose of (1) can be raised. Of course, the display target 12 can also be raised depending on whether or not water droplets are attached.
[0027]
In addition, if the display target 12 such as a figure or a character is applied so as to be drawn with the above-described water-repellent coating agent, the water-repellent display target 12 is particularly easily stained, so that the difference in the degree of stain adhesion is further increased. The water-repellent portion that depicts the display object 12 becomes noticeable with respect to the hydrophilic background portion 14, and the effect becomes very large. The same effect can be obtained by using a substrate such as a coated steel plate coated with a water-repellent fluorine-based paint or the like as the substrate 10.
Further, in the above-described embodiment, the display target for the purpose of the advertisement is described, but the display target is not limited to the purpose of the advertisement, and the display target is a case where the display is performed for any purpose. It can be.
[0028]
【The invention's effect】
The present invention is configured as described above, and has the following effects.
(1) By applying a hydrophilic coating agent on a base material so as to draw a display object such as a character or a figure, a portion having a hydrophilic function and a portion having no hydrophilic function are created on the base material, and the presence or absence of the hydrophilic function is provided. Thus, a display such as a publicity advertisement can be performed.
(2) In particular, by using a hydrophilic coating agent having an antifouling function, a display portion to which dirt does not easily adhere and a background portion to which dirt easily adheres are formed on the base material. It can be remarkably emphasized and display of advertisements and the like can be performed.
(3) When a substrate having water repellency is used as the substrate, the difference between the presence or absence of water droplets and the degree of dirt adhesion between the background water-repellent portion and the hydrophilic portion depicting the display object becomes more apparent. The display object appears more remarkably with respect to the background portion, and the effect becomes very large.
(4) Even when the location where the hydrophilic coating agent is used is not a figure or a character to be displayed, but a base material which is a background portion, the location where water droplets are attached and the degree of adhesion of dirt are different between the display target and the base material. The same effect can be obtained as the display means only by reversing the above.
[Brief description of the drawings]
FIG. 1 is a schematic view showing an advertisement member which is an example of a display member utilizing the hydrophilic function of the present invention.
FIG. 2 is a schematic view showing an advertising member which is another example of a display member utilizing the hydrophilic function of the present invention.
[Explanation of symbols]
10 Base material 12 Display object 14 Background part
Claims (13)