JP2004003719A

JP2004003719A - Negative ion generating clip for air conditioner, wind-direction baffle plate for air conditioner and negative ion generation tape

Info

Publication number: JP2004003719A
Application number: JP2002159060A
Authority: JP
Inventors: Kimihiro Takahashi; 高橋　公弘
Original assignee: TAKAHASHI TOSO KOGYOSHO KK
Current assignee: TAKAHASHI TOSO KOGYOSHO KK
Priority date: 2002-05-31
Filing date: 2002-05-31
Publication date: 2004-01-08
Anticipated expiration: 2022-05-31
Also published as: JP3625287B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide an air environment in a vehicle or house with rich negative ion which is favorable for human health. <P>SOLUTION: In this negative ion generating clip 20 for air conditioner, a metal sheet made of an iron material, an aluminum material, a stainless steel material, etc. is bent into the U-shape by press processing and so on, and on a wind-direction baffle plate at an air blowing-out part of an air conditioner, a negative ion generating powdery paint is applied on an air contact face (on the surfaces of a folded part 22 and a clip plates 21A and 21B) in the state where a pair of the clip plates 21A and 21B are interposed. Since this clip is so processed that a gap between the clip plates 21A and 21B gets gradually narrower from the folded part 22 to a tip end 23 in press processing, a main body functions also as a spring and stably attached to the wind direction baffle plate. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は、エアコン用マイナスイオン発生クリップ、エアコン用風向調節板、エアコン用マイナスイオン発生テープに関する。
【０００２】
【従来の技術】
一般に、マイナスイオンに富んだ空気は人体内の酸化物をアルカリ性に中和して、細胞を活性化させ、人体の生理作用を快調にするとともに、人間が本来持っている自然治癒力を高める働きがあるとされ、注目されている。
【０００３】
ところで、ＯＡ機器や電化製品に囲まれた室内や、タバコの煙が立ち込める空間、排気ガス等で大気の汚染された空間では、プラスイオンが増加しマイナスイオンが不足している状態になり、このような環境下では人体には、めまい、頭痛、肩こり、吐き気、イライラ、不眠といった不快な症状が現れると言われている。
【０００４】
そこで、最近ではマイナスイオンを発生させる機能を持ったエアコン等が開発されるに至っている。従来、エアコン用のマイナスイオン発生方法としては、放電を利用した方法が一般的であった。
【０００５】
【発明が解決しようとする課題】
しかし、放電を用いる方法によればマイナスイオンを非常に多量に発生できる反面、人体に有害とされるオゾンが発生するという問題並びに放電を利用するためその分エアコンの消費電力が増大してしまうという問題があった。
【０００６】
そこで、本発明はオゾン等の有害物を発生させるおそれがなく、しかも省エネルギーであり、エアコンに簡易に取り付け等できる、各種のマイナスイオン発生用具を提供することを目的としている。
【０００７】
【課題を解決するための手段】
本発明のエアコン用マイナスイオン発生クリップは、エアコンの風向調節板に簡単に装着できるものであり、エアコンの風向調節板に挟み込むための挟み板部を有し、少なくとも挟み板部の空気接触面にマイナスイオン発生粉体塗料が塗布されて成るものである。
【０００８】
このマイナスイオン発生粉体塗料は、マイナスイオンを効率良く発生させるために、マイナスイオン発生剤と、マイナスイオンの発生を誘発する誘発剤とを含むものであることが好ましい。
【０００９】
人体に最も快適とされる滝周辺や森林内で自然発生しているマイナスイオンの発生量（１５００〜５０００個／ｃｃ）を得るためには、マイナスイオン発生剤としては、酸化鉄エローイオン粉末、誘発剤としては遠赤外線発生源セラミックス粉末を用いることが適しているが、これには限らず、例えば、マイナスイオン発生剤としてトルマリン粉末を用いてもよいと考えられる。
【００１０】
また、本発明のエアコンの風向調節板は、当該風向調節板そのものを、マイナスイオン発生粉体が添加された樹脂を一体成形して形成した点を特徴とする。係るエアコンの風向調節板は、エアコンメーカーや部品メーカーが製造してエアコンに組み込むことで提供できるものである。
【００１１】
さらに、本発明のエアコン用マイナスイオン発生テープは、エアコンの空気吹き出し部に貼着されるもので、その空気接触面にマイナスイオン発生粉体塗料が塗布されて成ることを特徴とする。
【００１２】
【発明の実施の形態】
以下、本発明の実施の形態について図面を参照しながら説明する。本発明のエアコン用マイナスイオン発生クリップは、例えば、カー用エアコンや室内用エアコンの空気吹き出し部の風向調節板に簡単に装着でき、かつ取り外し可能で、しかもマイナスイオン発生粉体塗料が塗布されているため、人体に最も快適とされる滝周辺や森林内と同等量のマイナスイオンを発生することができるものである。
【００１３】
図１は、本発明のエアコン用マイナスイオン発生クリップの構造を示す斜視図である。図１（ａ）に示すように、このエアコン用マイナスイオン発生クリップ２０は、鉄材、アルミニウム材、ステンレス材等から成る金属板をプレス加工等によりＵ字状に曲成し、かつエアコンの空気吹き出し部の風向調節板に、一対の挟み板２１Ａ，２１Ｂを挟み込んだ状態における、空気接触面（折り曲げ部２２及び挟み板２１Ａ、２１Ｂの表面）にマイナスイオン発生粉体塗料が塗布されて成るものである。
【００１４】
また、このクリップはプレス加工時に折り曲げ部２２から先端２３に向かい、挟み板２１Ａ、２１Ｂの間の間隙が次第に狭くなるように加工されているため、本体がバネとしても機能し、風向調節板に安定に装着される。
【００１５】
このエアコン用マイナスイオン発生クリップの形態には種々の変形を加えることができる。例えば、図１（ｂ）に示すエアコン用マイナスイオン発生クリップ３０は、全体としては同様にＵ字状に曲成されているが、折り曲げ部３２は、直線的に折り曲げ加工されている。また、折り曲げ部３２から先端３３に向かい、挟み板３１Ａ、３１Ｂの間の間隙が次第に狭くなるように加工され、バネ性を持たせると共に、風向調節板への挟入を容易にするために、その先端３３は、間隙が拡がるように折り曲げ加工が成されている。
【００１６】
なお、エアコン用マイナスイオン発生クリップ２０，３０の各部の寸法は、利用される風向調節板のサイズに合わせて自由に決めることができる。また、エアコン用マイナスイオン発生クリップの材質は金属に限らず、プラスチック等の樹脂であってもよい。この場合には、射出成形により上記のようなクリップ形態に成形される。
【００１７】
次に、図１に示したクリップの空気接触面に塗布されるマイナスイオン発生粉体塗料の組成及び塗布方法について説明する。このマイナスイオン粉体塗料は、マイナスイオン発生剤と、このマイナスイオン発生剤からのマイナスイオンの発生を誘発、促進する作用を有する誘発剤とを含むものである。これは、マイナスイオン発生剤だけでは十分なマイナスイオンを発生することができないため、特殊な誘発剤を添加したものである。
【００１８】
さらに詳しくは、本発明者が実験的に用いたマイナスイオン発生粉体塗料の組成例は、顔料（所望の着色に応じて、例えば白系の酸化チタン、レッド系の有機顔料、ブルー系無機顔料）、マイナスイオン発生剤として酸化鉄エローイオンの粉末、誘発剤として遠赤外線発生源セラミックスを重量比で３５．２％、ポリエステル樹脂（硬化剤を含む）を重量比で８３．６％、その他、流れ調整剤等の添加剤を重量比で１．２％、それぞれ含むものである。しかしながら、この組成比に限定されるものではなく、適宜必要なマイナスイオン発生量に応じて、マイナスイオン発生剤、誘発剤の重量比を増減してもよい。また、マイナスイオン発生剤として、トルマリン粉末を用いてもよいと考えられる。
【００１９】
なお、遠赤外線発生源セラミックスはマイナスイオン誘発剤としての機能に加えて、遠赤外線を放射するため人体等の保温効果、血流促進効果等も併せて期待できる。
【００２０】
上記のように調合されたマイナスイオン発生粉体塗料をクリップ本体の空気接触面（例えば、折り曲げ部２２及び挟み板２１Ａ、２１Ｂの表面）に静電粉体塗装法により、５０μｍ〜７０μｍ程度の厚さにスプレー塗布する。この際、前処理としてクリップの材質に応じて、リン酸亜鉛、リン酸鉄、クロメート、ノンクロメート等を用いた化成処理を施すことが好ましい。また、焼き付け処理としてクリップ本体の温度を例えば１８０℃程度に加熱する共に、この過熱状態を２０分程度の間保持することが好ましい。
【００２１】
また、このマイナスイオン発生クリップの製造工程を簡単に説明すると、まず素材となる金属板をプレス加工により、例えば図１（ａ）または（ｂ）に示すようなＵ字形状に成形し、その後、装着状態での空気接触面に、マイナスイオン発生粉体塗料を静電粉体塗装法によりスプレー塗布する。もちろん、空気接触面の裏面も含めて本体全面に塗布してもよいが、空気接触面のみに塗布しただけでも十分なマイナスイオンが発生することを確認した。なお、プレス加工後に上記塗装処理を行う理由は、逆の手順で製造すると、プレス切削面に塗料が塗布されないこと、及びプレス時に金属板の切削端にバリが発生し、バリを除去する際に塗料が剥げ落ちてしまうおそれがあること等である。
【００２２】
また、上述のマイナスイオン発生クリップは、基本的には本体にマイナスイオン発生粉体塗料を塗布したものであるが、マイナスイオン発生粉体が添加された樹脂を例えば、図１（ａ）、（ｂ）のような形態となるよう、Ｕ字状に一体成形してもよい。この場合には、例えば溶融樹脂にマイナスイオン発生剤として、酸化鉄エローイオン粉末、誘発剤として、遠赤外線発生源セラミックス粉末を適量添加して均一組成となるように練り込む。そして、射出成形により、所望の形状のマイナスイオン発生クリップを作製する。
【００２３】
以下では、エアコン用マイナスイオン発生クリップの利用形態について説明するが、まず、カー用エアコンへの適用例について説明する。図２は、自動車の室内の前面パネル周辺を示す図である。
【００２４】
図に示すように、前面パネル１にはカー用エアコンの空気吹き出し部１０が、例えば４つ設けられている。図３に、マイナスイオン発生クリップ２０が装着された状態の空気吹き出し部１０の拡大図を示す。図３（ａ）は、空気吹き出し部１０の全体図、図３（ｂ）はマイナスイオン発生クリップ２０が挟み込まれた一枚の上下風向調節板１１を取り出して示した図である。また、図４は図３におけるＸ−Ｘ線に沿った、空気吹き出し部１０の内部断面構造を示す図である。
【００２５】
この空気吹き出し部１０は、水平方向に架け渡された５枚の上下風向調節板１１と、これらの上下風向調節板１１の背後に設置され、垂直方向に掛け渡された５枚の左右風向調節板１２を有している。５枚の上下風向調節板１１は、空気吹き出し部１０の左端に設置された連動板１３に、上下回転可能に係合されている。１つの上下風向調節板１１に設けられた風向調節レバー１４を上下方向に移動操作することで、連動板１３が上下方向に移動し、これに伴って５枚の上下風向調節板１１が連動して上下回転するように構成されている。
【００２６】
また、５枚の左右風向調節板１２は空気吹き出し部１０の上端に設置された連動板１５に、左右回転可能に係合されている。１つの左右風向調節板１２に設けられた風向調節レバー１４を左右方向に移動操作することで、連動板１５が左右方向に移動し、これに伴って５枚の上下風向調節板１１が連動して左右回転するように構成されている。
【００２７】
ここで、本発明のマイナスイオン発生クリップ２０の装着状態を説明すると、このクリップは、上下風向調節板１１に挟み込まれる。図では、５枚の上下風向調節板１１の全部に２つずつマイナスイオン発生クリップ２０が装着されているが、その数は適宜増減することができる。自動車に搭載されたエアコン（不図示）からの空気流は上下風向調節板１１、左右風向調節板１２の向きに沿うように吹き出されるので、上下風向調節板１１にマイナスイオン発生クリップ２０を装着することにより、車室内にマイナスイオンに富んだ空気が送られる。本発明者が、空気イオンカウンターを用いて、車内のマイナスイオン量を測定したところ、１９００〜２０００個／ｃｃという、人体に最も快適とされる滝周辺や森林内と同等のマイナスイオン量が得られることが明らかになった。
【００２８】
なお、上記の実施形態では、図１（ａ）のマイナスイオン発生クリップ２０を装着する例について述べたが、図１（ｂ）のマイナスイオン発生クリップ３０についても同様に装着され、同様の効果が得られるものである。また、カー用エアコンの種類によっては、上下風向調節板１１が上下回転動作をせず、空気吹き出し部そのものが回転するタイプもあるが、そのようなタイプにも同様に適用することができる。
【００２９】
また、マイナスイオン発生クリップ２０，３０は、ユーザー側が既存のカー用エアコンの風向調節板にそれを取り付け可能というコンセプトで開発したものであるが、カー用エアコンの風向調節板自体を、上述した組成のマイナスイオン発生粉体（マイナスイオン発生剤及び誘発剤）が添加された樹脂を射出成形により一体成形して作製することもできる。
【００３０】
この場合には、例えば溶融樹脂にマイナスイオン発生剤として、酸化鉄エローイオン粉末、誘発剤として、遠赤外線発生源セラミックス粉末を適量添加して均一組成となるように練り込む。そして、射出成形により、所望の形状の上下風向調節板１１や左右風向調節板１２を作製する。
【００３１】
このように、上下風向調節板１１や左右風向調節板１２を一体成形して供給すれば、ユーザー側ではマイナスイオン発生クリップ２０，３０を用いなくても、自動的にマイナスイオンに富んだ健康的な車内空気環境を得ることができるようになる。
【００３２】
次に、本発明のマイナスイオン発生テープについて説明する。このマイナスイオン発生テープは、エアコンの空気吹き出し部に貼着されるもので、その空気接触面に、上述したマイナスイオン発生粉体塗料が塗布されて成る。
【００３３】
テープ材は薄い紙や樹脂等が適当であり、一方の面は接着剤が塗布された粘着面であり空気吹き出し部の風向調節板等の面に貼り合わされ、他方の面は空気接触面でマイナスイオン発生粉体塗料が塗布される。エアコンのユーザーは、このマイナスイオン発生テープを風向調整板のサイズや形状に合わせて切り貼りすることができるので利便性が高い。
【００３４】
カー用エアコンの空気吹き出し部１０への適用例について、図５及び図６を参照しながら説明する。図５は、マイナスイオン発生テープ４０が貼着された空気吹き出し部１０を示す図であり、特に図５（ａ）は空気吹き出し部１０の全体図、図５（ｂ）は上下風向調節板１１を取り出して示した図である。また、図６は図５におけるＸ−Ｘ線に沿った、空気吹き出し部１０の内部断面構造を示す図である。マイナスイオン発生テープ４０は、上下風向調節板の片面、あるいは両面に貼着される。
【００３５】
上述した本発明のマイナスイオン発生クリップ２０、マイナスイオン発生テープ４０は、カー用エアコンに限らず、一般室内用のエアコンの空気吹き出し部や、ファンヒーター等の空気吹き出し部にも装着あるいは貼着することができ、上記と同様のマイナスイオン効果を得ることができる。
【００３６】
図７は、一般室内用エアコン５０を示す斜視図であり、図８は図７中の左右風向調整板５２の拡大斜視図である。この一般室内用エアコン５０の下部に併設された空気吹き出し口５１には、多数の左右風向調整板５２が設けられ、その向きを左右回転させることで自動的に風向調整が行われるように構成されている。
【００３７】
そして、左右風向調整板５２には、例えば図１（ａ）のものと同様に形成されたマイナスイオン発生クリップ２０Ａが装着され（図７、図８（ａ））、又はマイナスイオン発生テープ４０Ａが貼着される。こうして、空気吹き出し口５１からはマイナスイオンに富んだ空気が吹き出されるので、人体に良好な室内空気環境を実現することができるようになる。
【００３８】
また、左右風向調整板５２自体を、上述した組成のマイナスイオン発生粉体（マイナスイオン発生剤及び誘発剤）が添加された樹脂を射出成形により一体成形して作製することもできる。
【００３９】
【発明の効果】
本発明のエアコン用マイナスイオン発生クリップによれば、カー用や一般室内用エアコンの風向調節板に簡便に装着することができ、人体の健康に良好なマイナスイオンに富んだ車内あるいは室内の空気環境を実現することができる。しかも、マイナスイオン発生源として特殊塗料を用いているので、オゾンなどの有害物質を発生するおそれがなく、しかも電力等を必要としない利点も有している。
【００４０】
また、本発明のエアコンの風向調節板は、マイナスイオン発生粉体が添加された樹脂を一体成形して形成しているので、エアコンを運転するだけで、マイナスイオンに富んだ健康的な空気環境を実現することができる。
【００４１】
さらに、本発明のエアコン用マイナスイオン発生テープによれば、マイナスイオン発生粉体塗料が塗布されているので、エアコン用マイナスイオン発生クリップの効果に加え、このマイナスイオン発生テープを風向調整板のサイズや形状に合わせて切り貼りすることができるので、マイナスイオン発生用具として利便性の高いものである。
【図面の簡単な説明】
【図１】本発明の実施形態に係るエアコン用マイナスイオン発生クリップの構造を示す斜視図である。
【図２】自動車の室内の前面パネル周辺を示す図である。
【図３】図２の空気吹き出し部１０の拡大図である。
【図４】図３におけるＸ−Ｘ線に沿った空気吹き出し部１０の内部断面構造を示す図である。
【図５】本発明の実施形態に係るマイナスイオン発生テープ４０が貼着された空気吹き出し部１０を示す図ある。
【図６】図５におけるＸ−Ｘ線に沿った、空気吹き出し部１０の内部断面構造を示す図である。
【図７】一般室内用エアコン５０を示す斜視図である。
【図８】図７中の左右風向調整板５２の拡大斜視図である。
【符号の説明】
１　全面パネル１　　１０　カー用エアコンの空気吹き出し部
１１　上下風向調節板　　１２　左右風向調節板　　１３　連動板
１４　風向調節レバー　　１５　連動板
２０　エアコン用マイナスイオン発生クリップ　　２１　挟み板
２２　折り曲げ部　　２３　先端
３０　エアコン用マイナスイオン発生クリップ　　３１　挟み板
３２　折り曲げ部　　３３　先端　　４０　マイナスイオン発生テープ
５０　一般室内用エアコン　　５１　空気吹き出し口
５２　左右風向調節板[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a negative ion generating clip for an air conditioner, a wind direction adjusting plate for an air conditioner, and a negative ion generating tape for an air conditioner.
[0002]
[Prior art]
In general, air rich in negative ions neutralizes oxides in the human body to alkalinity, activates cells, improves the physiology of the human body, and enhances the natural healing power inherent in humans. It is said that there is attention.
[0003]
By the way, in a room surrounded by OA equipment and appliances, in a space where tobacco smoke can enter, and in a space where the atmosphere is polluted by exhaust gas, etc., positive ions increase and negative ions are in short supply. Under such circumstances, it is said that the human body exhibits unpleasant symptoms such as dizziness, headache, stiff shoulders, nausea, irritation, and insomnia.
[0004]
Therefore, an air conditioner or the like having a function of generating negative ions has recently been developed. Conventionally, as a method of generating negative ions for an air conditioner, a method using discharge has been generally used.
[0005]
[Problems to be solved by the invention]
However, according to the method using discharge, a very large amount of negative ions can be generated, but on the other hand, ozone, which is harmful to the human body, is generated, and the power consumption of the air conditioner increases due to the use of discharge. There was a problem.
[0006]
Accordingly, an object of the present invention is to provide various negative ion generating tools which do not generate harmful substances such as ozone, are energy-saving, and can be easily attached to an air conditioner.
[0007]
[Means for Solving the Problems]
The negative ion generating clip for an air conditioner of the present invention can be easily attached to a wind direction adjusting plate of an air conditioner, has a sandwiching plate portion for sandwiching the air direction adjusting plate of the air conditioner, and has at least an air contact surface of the sandwiching plate portion. It is formed by applying a negative ion generating powder coating material.
[0008]
The negative ion generating powder coating preferably contains a negative ion generating agent and an inducing agent for inducing the generation of negative ions in order to generate negative ions efficiently.
[0009]
In order to obtain the amount of negative ions generated naturally around the waterfall and in the forest, which is most comfortable for the human body (1500 to 5000 cells / cc), iron oxide yellow ion powder was used as the negative ion generator. It is suitable to use a far-infrared ray source ceramic powder as the agent, but the present invention is not limited to this. For example, tourmaline powder may be used as a negative ion generator.
[0010]
Further, the airflow direction adjusting plate of the air conditioner of the present invention is characterized in that the airflow direction adjusting plate itself is formed by integrally molding a resin to which negative ion generating powder is added. Such a wind direction adjusting plate of an air conditioner can be provided by being manufactured by an air conditioner manufacturer or a component manufacturer and incorporated into the air conditioner.
[0011]
Further, the negative ion generating tape for an air conditioner of the present invention is attached to an air blowing portion of an air conditioner, and is characterized in that a negative ion generating powder coating is applied to an air contact surface thereof.
[0012]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, embodiments of the present invention will be described with reference to the drawings. The negative ion generating clip for an air conditioner of the present invention can be easily attached to a wind direction adjusting plate of an air blowing portion of a car air conditioner or an indoor air conditioner, and can be detached, and coated with a negative ion generating powder paint. Therefore, it can generate the same amount of negative ions as the waterfall around the waterfall or in the forest, which is the most comfortable for the human body.
[0013]
FIG. 1 is a perspective view showing a structure of a negative ion generating clip for an air conditioner of the present invention. As shown in FIG. 1A, the negative ion generating clip 20 for an air conditioner is formed by bending a metal plate made of an iron material, an aluminum material, a stainless steel material or the like into a U-shape by pressing or the like, and blowing air from the air conditioner. The air-contact surface (the surface of the bent portion 22 and the sandwiching plates 21A and 21B) is coated with a negative ion generating powder paint in a state where the pair of sandwiching plates 21A and 21B are sandwiched between the wind direction adjusting plates of the section. is there.
[0014]
In addition, since this clip is processed so that the gap between the sandwiching plates 21A and 21B gradually narrows from the bent portion 22 to the tip 23 at the time of press working, the body also functions as a spring, and serves as a wind direction adjusting plate. Stablely mounted.
[0015]
Various modifications can be made to the form of the negative ion generating clip for an air conditioner. For example, the negative ion generating clip 30 for an air conditioner shown in FIG. 1B is similarly bent in a U-shape as a whole, but the bent portion 32 is bent straight. Further, from the bent portion 32 toward the tip 33, the gap between the sandwiching plates 31A, 31B is processed so as to gradually narrow, and while having a spring property, in order to facilitate insertion into the wind direction adjusting plate, The tip 33 is bent so as to widen the gap.
[0016]
The size of each part of the negative ion generating clips 20 and 30 for the air conditioner can be freely determined according to the size of the wind direction adjusting plate to be used. Further, the material of the negative ion generating clip for the air conditioner is not limited to metal, but may be resin such as plastic. In this case, it is molded into the above-described clip form by injection molding.
[0017]
Next, the composition and application method of the negative ion generating powder coating applied to the air contact surface of the clip shown in FIG. 1 will be described. This negative ion powder coating material contains a negative ion generator and an inducer having an action of inducing and promoting the generation of negative ions from the negative ion generator. This is because a special inducing agent is added because a sufficient amount of anion cannot be generated by the anion generating agent alone.
[0018]
More specifically, examples of the composition of the negative ion generating powder coating used experimentally by the present inventor include pigments (for example, white titanium oxide, red organic pigments, and blue inorganic pigments depending on the desired coloring). , Powder of iron oxide yellow ion as a negative ion generator, far-infrared ray source ceramics as an inducer, 35.2% by weight, polyester resin (including curing agent) 83.6% by weight, flow control 1.2% by weight of an additive such as an agent. However, the composition ratio is not limited to this, and the weight ratio of the negative ion generator and the inducing agent may be increased or decreased according to the necessary amount of generated negative ions. It is also considered that tourmaline powder may be used as the anion generator.
[0019]
The far-infrared ray source ceramics emits far-infrared rays in addition to the function as a negative ion inducing agent, and thus can be expected to have an effect of keeping a human body warm and promoting blood flow.
[0020]
The negative ion-generating powder coating prepared as described above is applied to the air contact surface of the clip body (for example, the surface of the bent portion 22 and the sandwich plates 21A and 21B) by the electrostatic powder coating method to have a thickness of about 50 μm to 70 μm. Spray it on. At this time, it is preferable to perform a chemical conversion treatment using zinc phosphate, iron phosphate, chromate, non-chromate, or the like as a pretreatment depending on the material of the clip. In addition, it is preferable that the temperature of the clip body is heated to, for example, about 180 ° C. as the baking process, and the overheated state is maintained for about 20 minutes.
[0021]
Also, the manufacturing process of the negative ion generating clip will be briefly described. First, a metal plate as a material is formed into a U-shape as shown in FIG. 1A or 1B by press working, and thereafter, The negative ion generating powder coating is spray-coated on the air contact surface in the mounted state by an electrostatic powder coating method. Of course, the coating may be applied to the entire surface of the main body including the back surface of the air contact surface, but it was confirmed that sufficient negative ions were generated only by applying to the air contact surface alone. The reason for performing the above-mentioned coating process after press working is that if the manufacturing is performed in the reverse procedure, no paint is applied to the cut surface of the press, and burrs are generated on the cut end of the metal plate at the time of pressing, and when removing burrs This is because the paint may come off.
[0022]
Further, the above-described negative ion generating clip is basically formed by applying a negative ion generating powder coating material to the main body, and a resin to which the negative ion generating powder is added is, for example, shown in FIGS. It may be integrally formed into a U-shape so as to have the form as shown in b). In this case, for example, iron oxide yellow ion powder as a negative ion generator and far-infrared ray source ceramic powder as an inducer are added to the molten resin and kneaded so as to have a uniform composition. Then, a negative ion generating clip having a desired shape is manufactured by injection molding.
[0023]
In the following, a use form of the negative ion generating clip for an air conditioner will be described. First, an application example to a car air conditioner will be described. FIG. 2 is a diagram showing the vicinity of a front panel in the interior of an automobile.
[0024]
As shown in the figure, the front panel 1 is provided with, for example, four air blowing units 10 of a car air conditioner. FIG. 3 shows an enlarged view of the air blowing section 10 with the negative ion generating clip 20 attached. FIG. 3A is an overall view of the air blowing unit 10, and FIG. 3B is a diagram illustrating a single vertical air direction adjusting plate 11 in which a negative ion generating clip 20 is sandwiched. FIG. 4 is a diagram showing the internal cross-sectional structure of the air blowing unit 10 along the line XX in FIG.
[0025]
The air blow-out unit 10 is provided with five vertical wind direction adjusting plates 11 bridged in the horizontal direction, and is installed behind the vertical wind direction adjusting plates 11 and five vertical wind direction adjusting plates 11 It has a plate 12. The five vertical wind direction adjustment plates 11 are engaged with an interlocking plate 13 installed at the left end of the air blowing unit 10 so as to be vertically rotatable. By operating the wind direction adjusting lever 14 provided on one vertical wind direction adjusting plate 11 in the vertical direction, the interlocking plate 13 moves in the vertical direction, and the five vertical wind direction adjusting plates 11 move in conjunction with this. It is configured to rotate up and down.
[0026]
The five left and right wind direction adjusting plates 12 are rotatably engaged with an interlocking plate 15 installed at the upper end of the air blowing unit 10. By operating the wind direction adjusting lever 14 provided on one left and right wind direction adjusting plate 12 in the left and right direction, the interlocking plate 15 is moved in the left and right direction, and accordingly, the five vertical wind direction adjusting plates 11 are interlocked. It is configured to rotate left and right.
[0027]
Here, the attached state of the negative ion generating clip 20 of the present invention will be described. The clip is sandwiched between the vertical wind direction adjusting plates 11. In the figure, two negative ion generating clips 20 are attached to all of the five vertical wind direction adjusting plates 11, but the number can be increased or decreased as appropriate. An airflow from an air conditioner (not shown) mounted on the automobile is blown out along the direction of the vertical wind direction adjusting plate 11 and the horizontal wind direction adjusting plate 12, so that the negative ion generating clip 20 is attached to the vertical wind direction adjusting plate 11. By doing so, air rich in negative ions is sent into the vehicle interior. When the present inventor measured the amount of negative ions in the vehicle using an air ion counter, the amount of negative ions of 1900 to 2000 cells / cc was obtained, which is equivalent to that of a waterfall area or a forest, which is considered to be the most comfortable for the human body. It became clear that it could be done.
[0028]
In the above embodiment, the example in which the negative ion generating clip 20 of FIG. 1A is mounted has been described. However, the negative ion generating clip 30 of FIG. It is obtained. Also, depending on the type of car air conditioner, there is a type in which the vertical wind direction adjusting plate 11 does not perform a vertical rotation operation and the air blowing portion itself rotates, but the present invention can be similarly applied to such a type.
[0029]
The negative ion generating clips 20 and 30 were developed with the concept that the user can attach it to the wind direction adjusting plate of an existing car air conditioner. The resin to which the negative ion generating powder (the negative ion generating agent and the inducing agent) is added may be integrally molded by injection molding.
[0030]
In this case, for example, iron oxide yellow ion powder as a negative ion generator and far-infrared ray source ceramic powder as an inducer are added to the molten resin and kneaded so as to have a uniform composition. Then, a vertical shape adjusting plate 11 and a horizontal direction adjusting plate 12 having a desired shape are manufactured by injection molding.
[0031]
In this way, if the vertical wind direction adjusting plate 11 and the left and right wind direction adjusting plate 12 are integrally formed and supplied, the user can automatically use the negative ion generating clips 20 and 30 without the use of the negative ion generating clips 20 and 30 to automatically provide a healthy and rich negative ion. It becomes possible to obtain a suitable vehicle air environment.
[0032]
Next, the negative ion generating tape of the present invention will be described. The negative ion generating tape is adhered to an air blowing portion of an air conditioner, and is formed by applying the above-described negative ion generating powder coating to the air contact surface.
[0033]
The tape material is suitably thin paper or resin, etc., one surface is an adhesive surface coated with an adhesive and is bonded to the surface of the air blowing part such as the wind direction adjustment plate, and the other surface is a negative air contact surface. An ion generating powder coating is applied. The user of the air conditioner can cut and paste the negative ion generating tape according to the size and shape of the wind direction adjusting plate, so that the convenience is high.
[0034]
An example of application of the car air conditioner to the air blowing unit 10 will be described with reference to FIGS. 5A and 5B are views showing the air blowing unit 10 to which the negative ion generating tape 40 is adhered. In particular, FIG. 5A is an overall view of the air blowing unit 10, and FIG. It is the figure which took out and showed. FIG. 6 is a diagram showing the internal cross-sectional structure of the air blowing unit 10 along the line XX in FIG. The negative ion generating tape 40 is attached to one side or both sides of the vertical wind direction adjusting plate.
[0035]
The negative ion generating clip 20 and the negative ion generating tape 40 of the present invention described above are attached or attached not only to an air conditioner for a car but also to an air blowing part of an air conditioner for a general room or a fan heater. And the same negative ion effect as described above can be obtained.
[0036]
FIG. 7 is a perspective view showing the general indoor air conditioner 50, and FIG. 8 is an enlarged perspective view of the left and right wind direction adjusting plate 52 in FIG. A large number of left and right wind direction adjusting plates 52 are provided at an air outlet 51 provided in the lower part of the general indoor air conditioner 50, and the air direction is automatically adjusted by rotating the direction horizontally. ing.
[0037]
Then, a negative ion generating clip 20A formed in the same manner as that of FIG. 1A is attached to the left and right wind direction adjusting plate 52 (FIGS. 7 and 8A), or a negative ion generating tape 40A is attached. Affixed. Thus, since air rich in negative ions is blown out from the air blowout port 51, a favorable indoor air environment for the human body can be realized.
[0038]
Further, the left and right wind direction adjusting plate 52 itself can be manufactured by integrally molding a resin to which the negative ion generating powder (the negative ion generating agent and the inducing agent) having the above-described composition is added by injection molding.
[0039]
【The invention's effect】
ADVANTAGE OF THE INVENTION According to the negative ion generating clip for air conditioners of this invention, it can be easily attached to the wind direction adjusting plate of the air conditioner for cars or general indoors, and the air environment in a car or room rich in negative ions that is good for human health. Can be realized. Moreover, since the special paint is used as the negative ion generating source, there is no risk of generating harmful substances such as ozone, and there is an advantage that no electric power or the like is required.
[0040]
In addition, since the airflow direction adjusting plate of the air conditioner of the present invention is formed by integrally molding a resin to which negative ion generating powder is added, a healthy air environment rich in negative ions can be obtained simply by operating the air conditioner. Can be realized.
[0041]
Furthermore, according to the negative ion generating tape for an air conditioner of the present invention, since the negative ion generating powder coating is applied, in addition to the effect of the negative ion generating clip for the air conditioner, the negative ion generating tape is sized to the size of the wind direction adjusting plate. Since it can be cut and pasted according to the shape and shape, it is highly convenient as a tool for generating negative ions.
[Brief description of the drawings]
FIG. 1 is a perspective view showing a structure of a negative ion generating clip for an air conditioner according to an embodiment of the present invention.
FIG. 2 is a diagram showing the vicinity of a front panel in the interior of an automobile.
FIG. 3 is an enlarged view of the air blowing unit 10 of FIG.
4 is a diagram showing an internal cross-sectional structure of the air blowing unit 10 along the line XX in FIG.
FIG. 5 is a view showing the air blowing unit 10 to which the negative ion generating tape 40 according to the embodiment of the present invention is attached.
6 is a diagram showing the internal cross-sectional structure of the air blowing unit 10 along the line XX in FIG.
FIG. 7 is a perspective view showing a general indoor air conditioner 50.
8 is an enlarged perspective view of the left and right wind direction adjusting plate 52 in FIG.
[Explanation of symbols]
DESCRIPTION OF SYMBOLS 1 Front panel 1 10 Air blowing part of car air conditioner 11 Vertical wind direction adjusting plate 12 Left and right wind direction adjusting plate 13 Interlocking plate 14 Wind direction adjusting lever 15 Interlocking plate 20 Negative ion generating clip for air conditioner 21 Clamping plate 22 Bending portion 23 Tip 30 Air conditioner Negative ion generating clip 31 Nipping plate 32 Bending part 33 Tip 40 Negative ion generating tape 50 General room air conditioner 51 Air outlet 52 Left and right wind direction adjusting plate

Claims

エアコンの風向調節板に装着されるエアコン用マイナスイオン発生クリップであって、前記風向調節板に挟み込むための挟み板部を有し、少なくとも前記挟み板部の空気接触面にマイナスイオン発生粉体塗料が塗布されて成ることを特徴とするエアコン用マイナスイオン発生クリップ。An air-conditioning negative ion generating clip mounted on a wind direction adjusting plate of an air conditioner, comprising a sandwiching plate portion for sandwiching the air direction adjusting plate, and a negative ion generating powder coating at least on an air contact surface of the sandwiching plate portion. A negative ion generating clip for air conditioners, characterized in that the clip is applied.

エアコンの風向調節板に挟み込み可能なエアコン用マイナスイオン発生クリップであって、金属板をＵ字状に曲成し、本体の空気接触面にマイナスイオン発生粉体塗料が塗布されて成ることを特徴とするエアコン用マイナスイオン発生クリップ。A negative ion generating clip for an air conditioner that can be inserted into a wind direction adjusting plate of an air conditioner, wherein a metal plate is bent into a U shape, and a negative ion generating powder paint is applied to an air contact surface of a main body. A negative ion generating clip for air conditioners.

前記マイナスイオン発生粉体塗料は、マイナスイオン発生剤と、マイナスイオンの発生を誘発する誘発剤とを含むことを特徴とする請求項１又は２記載のエアコン用マイナスイオン発生クリップ。The negative ion generating clip for an air conditioner according to claim 1 or 2, wherein the negative ion generating powder coating material includes a negative ion generating agent and an inducing agent for inducing generation of negative ions.

前記マイナスイオン発生剤は酸化鉄エローイオン粉末であり、前記誘発剤は遠赤外線発生源セラミックス粉末であることを特徴とする請求項３記載のエアコン用マイナスイオン発生クリップ。The negative ion generating clip for an air conditioner according to claim 3, wherein the negative ion generating agent is iron oxide yellow ion powder, and the inducing agent is far infrared ray generating source ceramic powder.

エアコンの風向調節板に挟み込み可能なエアコン用マイナスイオン発生クリップであって、マイナスイオン発生粉体が添加された樹脂をＵ字状に一体成形して成ることを特徴とするエアコン用マイナスイオン発生クリップ。A negative ion generating clip for an air conditioner that can be inserted into a wind direction adjusting plate of an air conditioner, wherein the resin to which a negative ion generating powder is added is integrally formed in a U-shape, and the negative ion generating clip for an air conditioner is provided. .

マイナスイオン発生粉体が添加された樹脂を一体成形して成ることを特徴とするエアコン用風向調節板。A wind direction adjusting plate for an air conditioner, which is formed by integrally molding a resin to which a negative ion generating powder is added.

前記マイナスイオン発生粉体は、マイナスイオン発生剤とマイナスイオンの発生を誘発する誘発剤とを含むことを特徴とする請求項６記載のエアコン用風向調節板。The airflow direction adjusting plate according to claim 6, wherein the negative ion generating powder includes a negative ion generating agent and an inducing agent for inducing generation of negative ions.

前記マイナスイオン発生剤が酸化鉄エローイオン粉末であり、前記誘発剤が遠赤外線発生源セラミックス粉末であることを特徴とする請求項７記載のエアコン用風向調節板。8. The air conditioner for an air conditioner according to claim 7, wherein the negative ion generator is iron oxide yellow ion powder, and the inducer is a far-infrared source ceramic powder.

エアコンの空気吹き出し部に貼着されるエアコン用マイナスイオン発生テープであって、その空気接触面にマイナスイオン発生粉体塗料が塗布されて成ることを特徴とするエアコン用マイナスイオン発生テープ。A negative ion generating tape for an air conditioner, which is attached to an air blowing portion of an air conditioner, wherein a negative ion generating powder paint is applied to an air contact surface thereof.

前記マイナスイオン発生粉体塗料は、マイナスイオン発生剤と、マイナスイオンの発生を誘発する誘発剤とを含むことを特徴とする請求項９記載のエアコン用マイナスイオン発生テープ。The negative ion generating tape for an air conditioner according to claim 9, wherein the negative ion generating powder coating material includes a negative ion generating agent and an inducing agent for inducing generation of negative ions.

前記マイナスイオン発生剤は酸化鉄エローイオン粉末であり、前記誘発剤は遠赤外線発生源セラミックス粉末であることを特徴とする請求項１０記載のエアコン用マイナスイオン発生テープ。The negative ion generating tape for an air conditioner according to claim 10, wherein the negative ion generating agent is iron oxide yellow ion powder, and the inducer is a far infrared ray generating source ceramic powder.