JP2003333941A - Weed-proof sheet - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a weed-proof sheet having shading properties without emitting toxic gases during combustion and having water permeability without collecting rainwater due to rainfall, etc., on the sheet surface and further flame retardance. <P>SOLUTION: The weed-proof sheet is a laminated sheet prepared by laminating a thermoplastic resin film having a plurality of water-permeable holes onto at least one surface of a sheet composed of a woven or a knitted fabric or a nonwoven fabric of a thermoplastic resin. At least one of the thermoplastic resin sheet and film is compounded with a flame retardant composed of a nitrogen-containing compound represented by general formula (1) H(R<SB>1</SB>)N-(CH<SB>2</SB>)<SB>a</SB>- N(R<SB>2</SB>)-(CH<SB>2</SB>)<SB>b</SB>-N(R<SB>2</SB>')-(CH<SB>2</SB>)<SB>c</SB>-N(R<SB>1</SB>)H [wherein, R<SB>1</SB>is a triazine derivative group represented by general formula (2) (wherein, R<SB>3</SB>s denote each a 1-10C alkyl group or a hydrogen atom; and R<SB>4</SB>s denote each a 5-10C cycloalkyl group or the 5-10C cycloalkyl group substituted with a 1-4C alkyl group) and containing piperidyl groups; R<SB>2</SB>and R<SB>2</SB>' denote each R<SB>1</SB>or a hydrogen atom; and a, b and c denote each a positive number of 2-5]. <P>COPYRIGHT: (C)2004,JPO

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、農業分野や土木分
野にて雑草等の繁殖を抑えるために用いられる防草シー
トに関するものである。詳しくは、本発明は、遮光性と
透水性を有し、且つ、難燃性を備えた防草シートに関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a weed control sheet used for suppressing the growth of weeds in the fields of agriculture and civil engineering. More specifically, the present invention relates to a grass sheet having light shielding properties, water permeability, and flame retardancy.

【０００２】[0002]

【従来の技術】従来より様々な除草手段や防草手段を用
いて、建物、構造物や街路樹等周辺の雑草の生育防止を
して美観を維持している。例えば、除草手段としては、
除草剤の散布が行われているが、一時的にしか効力がな
く、また、除草剤が一般に有毒であることから、周囲へ
の公害問題が発生するという問題があった。また、防草
手段として、砂利等を敷設する方法があるが、砂利では
均一な遮光をするためには厚く敷設する必要があり、ま
た、砂利の隙間から雑草の種子が侵入し、その隙間より
雑草が成長するという問題があった。この問題点を改善
する方法として、ビニールシートやフイルムに不織布、
織物を貼り合わせて補強した積層シートを敷設する方法
が提案されている。2. Description of the Related Art Conventionally, weeds around buildings, structures, street trees and the like have been prevented from growing by using various weeding and weeding means to maintain the appearance. For example, as weeding means,
Herbicides are sprayed, but they are only temporarily effective, and the herbicides are generally toxic, causing problems of pollution to the surroundings. As a means of weed control, there is a method of laying gravel, etc., but in gravel, it is necessary to lay thickly in order to provide uniform shading, and weed seeds enter through gaps in gravel, and There was a problem that weeds grew. As a solution to this problem, non-woven fabrics are used for vinyl sheets and films.
There has been proposed a method of laying a laminated sheet reinforced by bonding a woven fabric.

【０００３】[0003]

【発明が解決しようとする課題】しかしながら、上記積
層シートでは、砂利の場合のような問題点はないが、該
シートには透水性がなく遮水性であるために、降雨等に
よる雨水がシート表面に溜まるいう問題点があった。さ
らに、該シートは可燃性であり、難燃性を備えておら
ず、煙草のポイ捨て等による火が該シートに着火する恐
れがあり、火災予防の観点より、該シートに難燃化処理
が施されていることが要望される。本発明は、上記の問
題点に着目してなされたもので、燃焼時に有毒ガスの発
生がなく、遮光性を有し、且つ、降雨等による雨水がシ
ート表面に溜まることのない透水性を有し、さらに、難
燃性を備えた防草シートを提供することを目的とする。However, the above-mentioned laminated sheet does not have a problem as in the case of gravel, but since the sheet has no water permeability and is water-blocking, rainwater due to rainfall or the like is not exposed to the sheet surface. There was a problem that accumulates. Further, since the sheet is flammable and does not have flame retardancy, there is a risk that a fire caused by littering of cigarettes and the like may ignite the sheet. From the viewpoint of fire prevention, the sheet is subjected to a flame retarding treatment. It is requested that it is done. The present invention has been made in view of the above problems, has no toxic gas generated during combustion, has a light-shielding property, and has a water permeability such that rainwater due to rainfall does not collect on the sheet surface. Further, it is another object of the present invention to provide a grass-proof sheet having flame retardancy.

【０００４】[0004]

【課題を解決するための手段】本発明者は、上記のよう
な課題を解決すべく、鋭意検討を重ねた結果、熱可塑性
樹脂に特定のトリアジン誘導体を難燃剤として少量添加
し、且つ、複数の透孔を有する熱可塑性樹脂フイルムの
積層シートとすることにより、上記目的が達成されるこ
とを見出し、本発明を完成するに至った。即ち、本発明
の要旨は、熱可塑性樹脂の織編布または不織布からなる
シートの少なくとも片面に、複数の透水孔を有する熱可
塑性樹脂フイルムをラミネートしてなる積層シートであ
って、上記熱可塑性樹脂のシート及びフイルムの少なく
とも一方に下記一般式（１）で示される窒素含有化合物
からなる難燃剤を配合してなることを特徴とする防草シ
ート、に存する。 H(R₁)Nー(CH₂)_aーN(R₂)ー(CH₂)_bーN(R_2')ー(CH₂)_cーN(R₁)H （１） （式中、R₁は下記一般式(２)で示されるピペリジル基を
含有するトリアジン誘導体基であり、R_2、R_2'は R₁また
は水素原子を表し、ａ，ｂ及びｃはそれぞれ、２〜５の
正数を表す。）Means for Solving the Problems The present inventors have conducted intensive studies in order to solve the above-mentioned problems, and as a result, have added a small amount of a specific triazine derivative to a thermoplastic resin as a flame retardant, and It has been found that the above object can be achieved by forming a laminated sheet of a thermoplastic resin film having the above-mentioned pores, and the present invention has been completed. That is, the gist of the present invention is a laminated sheet obtained by laminating a thermoplastic resin film having a plurality of water-permeable holes on at least one surface of a sheet made of a woven or knitted fabric or a nonwoven fabric of a thermoplastic resin, And a flame retardant comprising a nitrogen-containing compound represented by the following general formula (1) in at least one of the sheet and the film. H (R ₁₎ N over (CH _{2) a} chromatography N (R ₂₎ over (CH _{2) b} over N (R _{2 ')} over (CH _{2) c} over _{N (R 1) H (1} ) ( in the formula , R ₁ is a triazine derivative group containing a piperidyl group represented by the following general formula (2), R _{2 and} R _{2 ′} represent R ₁ or a hydrogen atom, and a, b and c each represent 2 to 5 Represents a positive number of.)

【化３】 （式中、R₃は炭素原子数１〜１０のアルキル基または水
素原子を表し、R₄は炭素原子数５〜１０のシクロアルキ
ル基または炭素原子数１〜４のアルキル基で置換された
炭素原子数５〜１０のシクロアルキル基を表す。）Embedded image (Wherein, R ₃ represents an alkyl group having 1 to 10 carbon atoms or a hydrogen atom, and R ₄ represents a carbon atom substituted with a cycloalkyl group having 5 to 10 carbon atoms or an alkyl group having 1 to 4 carbon atoms. Represents a cycloalkyl group having 5 to 10 atoms.)

【０００５】[0005]

【発明の実施の形態】本発明において、織編布または不
織布からなるシートに使用される熱可塑性樹脂として
は、ポリオレフィン、ナイロン、ポリエステル等が挙げ
られる。ポリオレフィンとしては、具体的には、高密度
ポリエチレン、中密度ポリエチレン、分岐状低密度ポリ
エチレン、直鎖状低密度ポリエチレン、メタロセン触媒
を用いて製造されたエチレン・α−オレフィン共重合体
などのポリエチレン系樹脂や、プロピレン単独重合体、
エチレン−プロピレンブロック共重合体、エチレン−プ
ロピレンランダム共重合体などのポリプロピレン系樹脂
などが挙げられるが、これらのうちでは、延伸効果にす
ぐれた、高密度ポリエチレン、プロピレン単独重合体な
どが好ましい。BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, examples of the thermoplastic resin used for a sheet made of a woven or knitted fabric or a nonwoven fabric include polyolefin, nylon, and polyester. As the polyolefin, specifically, high-density polyethylene, medium-density polyethylene, branched low-density polyethylene, linear low-density polyethylene, polyethylene-based copolymers such as ethylene-α-olefin copolymers produced using a metallocene catalyst Resin, propylene homopolymer,
Examples thereof include polypropylene resins such as an ethylene-propylene block copolymer and an ethylene-propylene random copolymer, and among these, a high-density polyethylene, a propylene homopolymer, and the like having excellent stretching effects are preferable.

【０００６】本発明に使用される難燃剤としては、下記
一般式(１)で示される窒素含有化合物が用いられる。 H(R₁)Nー(CH₂)_aーN(R₂)ー(CH₂)_bーN(R_2')ー(CH₂)_cーN(R₁)H （１） （式中、R₁は下記一般式（２）で示されるピペリジル基
を含有するトリアジン誘導体基であり、R_2、R_2'は R₁ま
たは水素原子を表し、ａ，ｂ及びｃはそれぞれ、２〜５
の正数を表す。）[0006] As the flame retardant used in the present invention, a nitrogen-containing compound represented by the following general formula (1) is used. H (R ₁₎ N over (CH _{2) a} chromatography N (R ₂₎ over (CH _{2) b} over N (R _{2 ')} over (CH _{2) c} over _{N (R 1) H (1} ) ( in the formula , R ₁ is a triazine derivative group containing a piperidyl group represented by the following general formula (2), R _{2 and} R _{2 ′} represent R ₁ or a hydrogen atom, and a, b and c each represent 2 to 5
Represents a positive number. )

【化４】 （式中、R₃は炭素原子数１〜１０のアルキル基または水
素原子を表し、R₄は炭素原子数５〜１０のシクロアルキ
ル基または炭素原子数１〜４のアルキル基で置換された
炭素原子数５〜１０のシクロアルキル基を表す。）Embedded image (Wherein, R ₃ represents an alkyl group having 1 to 10 carbon atoms or a hydrogen atom, and R ₄ represents a carbon atom substituted with a cycloalkyl group having 5 to 10 carbon atoms or an alkyl group having 1 to 4 carbon atoms. Represents a cycloalkyl group having 5 to 10 atoms.)

【０００７】上記一般式(１)で示される窒素含有化合物
として、下記一般式(３)で示される窒素含有化合物が好
ましく、特に下記一般式(３)と下記一般式(４)の組み合
わせのものが好ましい。 H(R₁)Nー(CH₂)₃ーN(R₁)ー(CH₂)₂ーNHー(CH₂)₃ーN(R₁)H （３） 即ち、上記一般式(３)で示される窒素含有化合物は、上
記一般式(１)において、Ｒ_１が上記一般式(２)で示され
るピペリジル基を含有するトリアジン誘導体基であり、
R₂がR₁であり、R_2'が水素原子であり、ａ，ｂ及びｃが
それぞれ、３，２，３の正数である窒素含有化合物であ
る。As the nitrogen-containing compound represented by the general formula (1), a nitrogen-containing compound represented by the following general formula (3) is preferable, and particularly, a combination of the following general formulas (3) and (4) Is preferred. H (R ₁₎ N over (CH _{2) 3} over N (R ₁₎ over (CH _{2) 2} over NH chromatography (CH _{2) 3} over N (R ₁₎ H (3) In other words, the general formula (3) In the general formula (1), R ₁ is a triazine derivative group containing a piperidyl group represented by the general formula (2),
R ₂ is R ₁ , R _{2 ′} is a hydrogen atom, and a, b and c are nitrogen-containing compounds having positive numbers of 3, 2, and 3, respectively.

【化５】 （式中、R₃は炭素原子数１〜１０のアルキル基または水
素原子を表し、R₄は炭素原子数５〜１０のシクロアルキ
ル基または炭素原子数１〜４のアルキル基で置換された
炭素原子数５〜１０のシクロアルキル基を表す。）Embedded image (Wherein, R ₃ represents an alkyl group having 1 to 10 carbon atoms or a hydrogen atom, and R ₄ represents a carbon atom substituted with a cycloalkyl group having 5 to 10 carbon atoms or an alkyl group having 1 to 4 carbon atoms. Represents a cycloalkyl group having 5 to 10 atoms.)

【０００８】上記難燃剤の配合割合は、上記熱可塑性樹
脂に対して０．１〜５重量％、好ましくは０．５〜４重
量％の範囲である。上記配合量が上記範囲未満では難燃
性が不十分であり、上記範囲を超えると難燃性の効果が
それ以上向上せず、逆にコストアップにつながるので好
ましくない。The proportion of the flame retardant is 0.1 to 5% by weight, preferably 0.5 to 4% by weight, based on the thermoplastic resin. If the amount is less than the above range, the flame retardancy is insufficient. If the amount is more than the above range, the effect of the flame retardancy is not further improved, which leads to an increase in cost.

【０００９】上記難燃剤を熱可塑性樹脂に配合する方法
としては、フィルムを成形する際に熱可塑性樹脂と難燃
剤をヘンシェルミキサーなどの混合機で混合して、ある
いは所定割合の熱可塑性樹脂と難燃剤をそれぞれ直接押
出機に供給して混練するなどの公知の方法を採用するこ
とができる。しかし、ベースとなる熱可塑性樹脂と同種
または同系の樹脂に予め高濃度の難燃剤を含有させたマ
スターバッチを製造し、フィルム成形時に所定の含有量
に調整してフィルム成形を行なう、いわゆるマスターバ
ッチ法を採用することが好ましい。As a method of blending the above flame retardant with the thermoplastic resin, the thermoplastic resin and the flame retardant are mixed by a mixer such as a Henschel mixer at the time of forming a film, or a predetermined ratio of the thermoplastic resin is mixed with the thermoplastic resin. A known method such as directly supplying the fuel to the extruder and kneading the same can be employed. However, a master batch in which a high-concentration flame retardant is previously contained in the same or similar resin as the base thermoplastic resin is manufactured, and the film is formed by adjusting the content to a predetermined content when forming the film. It is preferable to adopt the method.

【００１０】上記織編布に用いる延伸糸の形態として
は、フィルムをスリットして延伸したフラットヤーン
や、フラットヤーンを割繊したスプリットヤーン、また
円形または異形ノズルから押し出したフィラメントを延
伸したモノフィラメントや、低繊度フィラメントを収束
したマルチフィラメントなどの単層型あるいは多層型、
芯鞘型、並列型等の複合糸条など制限なく採用される。The form of the drawn yarn used for the woven or knitted fabric may be a flat yarn obtained by slitting a film, a split yarn obtained by splitting a flat yarn, a monofilament obtained by drawing a filament extruded from a circular or irregular nozzle. , Single-layer type or multi-layer type such as multi-filament which converged low fineness filament,
A composite yarn such as a core-sheath type, a parallel type or the like can be used without any limitation.

【００１１】延伸糸の製造方法はとくに限定されるもの
ではなく、公知の製造方法により一軸延伸を施した延伸
糸を形成する。例えば、フラットヤーンの場合には、上
記熱可塑性樹脂、特にポリプロピレンや高密度ポリエチ
レン等のポリオレフィン樹脂を押出機に投入して、Ｔダ
イフラット法またはインフレーション法により無定形状
態で押出し、冷却固化したフィルムは、約５〜３０ｍｍ
幅にスリットした後、延伸処理し、次いで熱処理してフ
ラットヤーンを形成する。この際の延伸処理は高融点の
熱可塑性樹脂の融点以下、低融点の熱可塑性樹脂の軟化
点以上の温度下に行われるが、加熱法としては、熱ロー
ル式、熱板式、熱風式等いずれの方法も採用できる。ス
リットされた熱可塑性樹脂フイルムは加熱され、前後ロ
ールの周速度差により延伸を行う。延伸倍率は３〜１５
倍、好ましくは５〜１０倍の範囲である。この延伸倍率
が３倍未満では防草シートを構成するフラットヤーンの
充分な強度が得られなくなり、一方、延伸倍率が１５倍
を超えると延伸方向の配向が強すぎてフラットヤーンが
割れ易くなり、また生産効率が極端に劣ることなどが想
定されるThe method for producing a drawn yarn is not particularly limited, and a drawn yarn that has been subjected to uniaxial drawing by a known production method is formed. For example, in the case of a flat yarn, the thermoplastic resin, in particular, a polyolefin resin such as polypropylene or high-density polyethylene is charged into an extruder, and is extruded in an amorphous state by a T-die flat method or an inflation method, and is cooled and solidified. Is about 5-30mm
After slitting to a width, it is stretched and then heat treated to form a flat yarn. The stretching process at this time is performed at a temperature equal to or lower than the melting point of the high melting point thermoplastic resin, and at a temperature equal to or higher than the softening point of the low melting point thermoplastic resin. As a heating method, any of a hot roll method, a hot plate method, a hot air method, etc. Method can also be adopted. The slit thermoplastic resin film is heated and stretched by the peripheral speed difference between the front and rear rolls. Stretch ratio is 3-15
Times, preferably 5 to 10 times. If the draw ratio is less than 3 times, sufficient strength of the flat yarn constituting the weed prevention sheet cannot be obtained, while if the draw ratio exceeds 15 times, the orientation in the drawing direction is too strong and the flat yarn is easily broken, It is also assumed that production efficiency is extremely poor

【００１２】上記延伸糸の単糸繊度は、通常５００〜２
０００デシテクス（以下、ｄｔと略す）、好ましくは８
００〜１６００ｄｔの範囲内である。上記単糸繊度が５
００ｄｔ未満では、引張強度が不十分となり防草シート
を展張施工する際に破損するなどの支障を生じ、２００
０ｄｔを超えると編成や織成効率に劣ると共に、得られ
るシート体の柔軟性に欠け、凹凸を有する防草シートが
敷設面に密着できなくなる。The single yarn fineness of the drawn yarn is usually 500 to 2
000 dtex (hereinafter abbreviated as dt), preferably 8
It is in the range of 00 to 1600 dt. The single yarn fineness is 5
If it is less than 00 dt, the tensile strength will be insufficient, causing problems such as breakage when the grass sheet is stretched and constructed, and
If it exceeds 0 dt, the knitting and weaving efficiency is inferior, and the obtained sheet body lacks flexibility, and the grass sheet having irregularities cannot be adhered to the laying surface.

【００１３】本発明においては、上記で得られた熱可塑
性樹脂製延伸糸を経緯糸に用いて織成して織編布を形成
してシート状物とする。織編布の組織としては、特に限
定されるものではなく、織物では、例えば、平織、綾
織、模紗織、絽織、絡み織などが挙げられ、編物ではラ
ッセル編、トリコット編み、ミラニーズ編等が挙げられ
る。In the present invention, the drawn yarn of the thermoplastic resin obtained as described above is woven using warp yarns to form a woven or knitted fabric to form a sheet. The structure of the woven or knitted fabric is not particularly limited, and the woven fabric includes, for example, plain weave, twill weave, mosaic weave, rou weave, entangled weave, and the like, and the knitted fabric includes Russell knit, tricot knit, and Miranese knit. No.

【００１４】また、上記熱可塑性樹脂の不織布として
は、熱可塑性樹脂、特にポリオレフィンを用いて溶融押
出された繊維状物をランダムに積み重ね、溶融状態の繊
維状物同士を溶融接着させてシート化するメルトブロー
方式や、冷却された繊維状物同士を熱エンボスロールに
より溶融接着させてシート化するスパンボンド方式のい
ずれも使用できる。また、熱可塑性樹脂製延伸糸を所定
間隔で経緯に並べて配置し、重ね合わせて交差部を接着
して積層不織布を形成したシート状物としたものでもよ
い。As the non-woven fabric of the thermoplastic resin, fibrous materials melt-extruded using a thermoplastic resin, particularly polyolefin, are randomly stacked, and the fibrous materials in a molten state are melt-bonded to form a sheet. Any of a melt blow method and a spun bond method in which cooled fibrous materials are melt-bonded with a hot embossing roll to form a sheet can be used. Alternatively, a sheet-like material may be used in which drawn yarns made of a thermoplastic resin are arranged side by side at predetermined intervals at predetermined intervals, overlapped and bonded at the intersection to form a laminated nonwoven fabric.

【００１５】本発明においては、上記熱可塑性樹脂の織
編布または不織布からなるシートの少なくとも片面に、
好ましくは両面に上記一般式（１）で示される窒素含有
化合物からなる難燃剤を含有し、且つ、複数の透水孔を
有する熱可塑性樹脂フイルムをラミネートして積層シー
トを形成する。In the present invention, at least one surface of a sheet made of a woven or knitted fabric or a non-woven fabric of the thermoplastic resin,
Preferably, a laminated sheet is formed by laminating a thermoplastic resin film containing a flame retardant comprising a nitrogen-containing compound represented by the above general formula (1) on both surfaces and having a plurality of water-permeable holes.

【００１６】上記熱可塑性樹脂としては、ポリオレフィ
ン、ナイロン、ポリエステル等が挙げられ、ポリオレフ
ィンが好適である。ポリオレフィンとしては、高密度ポ
リエチレン、中密度ポリエチレン、分岐状低密度ポリエ
チレン、直鎖状低密度ポリエチレン、メタロセン触媒を
用いて製造されたエチレン・α−オレフィン共重合体、
エチレンー酢酸ビニル共重合体、エチレンーアクリル酸
エステル共重合体などのポリエチレン系樹脂や、プロピ
レン単独重合体、エチレン−プロピレンブロック共重合
体、エチレン−プロピレンランダム共重合体などのポリ
プロピレン系樹脂などが挙げられ、これらは単独または
２種以上組み合わせて用いられる。上記ポリオレフィン
樹脂のＭＦＲは、好ましくは１〜５０ｇ／１０分、より
好ましくは５〜３０ｇ／１０分である。Examples of the thermoplastic resin include polyolefin, nylon, polyester and the like, with polyolefin being preferred. As the polyolefin, high-density polyethylene, medium-density polyethylene, branched low-density polyethylene, linear low-density polyethylene, ethylene-α-olefin copolymer produced using a metallocene catalyst,
Examples include polyethylene-based resins such as ethylene-vinyl acetate copolymer and ethylene-acrylate copolymer, and polypropylene-based resins such as propylene homopolymer, ethylene-propylene block copolymer, and ethylene-propylene random copolymer. These are used alone or in combination of two or more. The MFR of the polyolefin resin is preferably 1 to 50 g / 10 minutes, more preferably 5 to 30 g / 10 minutes.

【００１７】上記熱可塑性樹脂に上記一般式（１）で示
される窒素含有化合物からなる難燃剤を配合する方法と
しては、上記熱可塑性樹脂と難燃剤を混合して直接ラミ
ネート押出機に供給してもよいし、予め熱可塑性樹脂中
に高濃度の難燃材を含有するマスターバッチを製造し、
このマスターバッチとして供給してもよい。As a method of blending a flame retardant comprising a nitrogen-containing compound represented by the general formula (1) with the thermoplastic resin, the thermoplastic resin and the flame retardant are mixed and supplied directly to a laminating extruder. Alternatively, a master batch containing a high concentration of flame retardant in a thermoplastic resin is manufactured in advance,
It may be supplied as this master batch.

【００１８】上記難燃剤の配合割合は、上記熱可塑性樹
脂ラミネート層の総重量に対して０．１〜５重量％、好
ましくは０．５〜４重量％の範囲である。上記配合量が
上記範囲未満では難燃性が不十分であり、上記範囲を超
えると難燃性の効果がそれ以上向上せず、逆にコストア
ップにつながるので好ましくない。The compounding ratio of the flame retardant is in the range of 0.1 to 5% by weight, preferably 0.5 to 4% by weight, based on the total weight of the thermoplastic resin laminate layer. If the amount is less than the above range, the flame retardancy is insufficient. If the amount is more than the above range, the effect of the flame retardancy is not further improved, which leads to an increase in cost.

【００１９】上記複数の透水孔を有する熱可塑性樹脂フ
イルムとしては、穴空きフイルムがが挙げられる。穴空
きフイルムは、上記ポリオレフィン樹脂、難燃剤及び発
泡剤の組成物を溶融押出し、発泡成形することにより、
溶融樹脂内に含有されている発泡剤の熱分解や蒸発など
による発泡破壊により溶融フイルムに複数の孔が形成さ
れ、複数の透水孔を有する穴空きフイルムが得られる。
発泡剤としては、水または熱分解型の発泡剤が用いられ
るが、水が安価であり好ましい。発泡剤としては、アゾ
ジカルボンアミド、アゾビスホルムアミド、ジニトロソ
ペンタメチレンテトラミン、トルエンスルホニルヒドラ
ジド等の熱分解型の発泡剤が通常用いられるが、プロパ
ン、ブタン、ペンタン、ヘキサンなどの低沸点炭化水素
などを用いることもできる。発泡剤の添加量は、押出の
速度や分解温度に起因する発泡気泡の状態を設定するこ
とで適宜決められる。難燃剤の添加量としては、通常
０．１〜１０重量％、好ましくは１〜５重量％の範囲で
ある。発泡剤の添加量が０．１重量％未満では発泡剤の
効果が低下して、本発明の効果が得られない。また、穴
空きフイルムとして、通常のフイルム成形後、穴開けロ
ールのよって複数箇所に穴を形成したものであってもよ
い。As the thermoplastic resin film having a plurality of water-permeable holes, there is a perforated film. The perforated film is formed by melt-extruding the composition of the polyolefin resin, the flame retardant and the foaming agent, and foam-molding.
A plurality of holes are formed in the molten film due to foam destruction due to thermal decomposition or evaporation of the foaming agent contained in the molten resin, and a perforated film having a plurality of water-permeable holes is obtained.
As the foaming agent, water or a pyrolytic foaming agent is used, but water is preferable because it is inexpensive. As the foaming agent, thermal decomposition type foaming agents such as azodicarbonamide, azobisformamide, dinitrosopentamethylenetetramine, and toluenesulfonylhydrazide are usually used, and low-boiling hydrocarbons such as propane, butane, pentane, and hexane are used. Can also be used. The amount of the foaming agent to be added can be determined as appropriate by setting the state of the foam cells due to the extrusion speed and decomposition temperature. The addition amount of the flame retardant is usually in the range of 0.1 to 10% by weight, preferably 1 to 5% by weight. If the amount of the foaming agent is less than 0.1% by weight, the effect of the foaming agent is reduced, and the effect of the present invention cannot be obtained. Alternatively, the perforated film may be one in which holes are formed at a plurality of locations by a perforating roll after normal film forming.

【００２０】上記透水孔は、雨水が溜まらない限り、そ
の形状や大きさは制限されない。その形状としては、円
形、楕円形、四角形、台形等いずれでもよく、その大き
さは円形換算で、直径が０．１〜３０ｍｍ、望ましく
は、３〜１５ｍｍの範囲内であり、その孔の個数は３〜
５０００個／ｍ^２、望ましくは１０〜１０００個／ｍ ^２
の範囲内である。As long as rainwater does not accumulate in the above-mentioned water-permeable holes,
The shape and size of are not limited. The shape is a circle
Shape, ellipse, square, trapezoid, etc.
The diameter is 0.1 to 30 mm, preferably in circular form.
Is in the range of 3 to 15 mm, and the number of holes is 3 to
5000 pieces / m², Desirably 10 to 1000 pieces / m ²
Is within the range.

【００２１】上記複数の透水孔を有する熱可塑性樹脂フ
イルムを上記熱可塑性樹脂の織編布または不織布からな
るシートの少なくともラミネートする方法としては、公
知の押出ラミネート法、ドライラミネート法、熱圧着ラ
ミネート法などが採用できるが、押出ラミネート法が成
形性の点で好ましい。上記織編布／ラミネート層との構
成比率としては、重量比で、通常５／１〜１／５の範囲
であり、ラミネート層の厚みとしては、通常１０〜１０
０μｍの範囲、好ましくは２０〜８０μｍの範囲であ
る。As a method of laminating the above-mentioned thermoplastic resin film having a plurality of water-permeable holes at least on a sheet made of a woven or knitted fabric or non-woven fabric of the above-mentioned thermoplastic resin, a known extrusion lamination method, dry lamination method, thermocompression lamination method For example, extrusion lamination is preferable in terms of moldability. The composition ratio with the woven / knitted fabric / laminate layer is usually in the range of 5/1 to 1/5 by weight, and the thickness of the laminate layer is usually 10 to 10
It is in the range of 0 μm, preferably in the range of 20 to 80 μm.

【００２２】こうして得られる防草シートは、その目付
重量が５０〜５００ｇ／ｍ^２範囲が好ましく、さらに好
ましくは８０〜２００ｇ／ｍ^２の範囲である。この目付
重量が５０ｇ／ｍ^２未満では防草シートとして敷設され
ても風などにより飛散し易くなり、目付重量が５００ｇ
／ｍ^２を超えると重くなり過ぎて取扱いに困難となる。The thus obtained herbicidal sheet preferably has a basis weight of 50 to 500 g / m ² , more preferably 80 to 200 g / m ² . If the basis weight is less than 50 g / m ² , even if it is laid as a grass sheet, it is easy to be scattered by wind and the like, and the basis weight is 500 g.
If it exceeds / m ² , it will be too heavy and difficult to handle.

【００２３】また、防草シートの物性として、その引張
強度が１００ｋｇｆ／５ｃｍ以上であることが望まし
い。この引張強度が１００ｋｇｆ／５ｃｍ未満では防草
シートの展張または敷設作業時に強度不足で破損を生じ
るなどの問題が生じ、またコンクリート等の下敷きとし
て敷設する場合にも地盤沈下などにより亀裂を生じるお
それがある。さらに、その引裂強度が２０ｋｇｆ以上で
あることが好ましい。この引裂強度が２０ｋｇｆ未満で
は、ススキなどのイネ科の成長力の強い植物の成長力に
抗し切れずに突刺され引き裂かれてしまうなどの問題も
発生する。Further, as a physical property of the weed prevention sheet, it is desirable that the tensile strength is 100 kgf / 5 cm or more. If the tensile strength is less than 100 kgf / 5 cm, there is a problem that the strength of the grass sheet may be damaged due to insufficient strength at the time of spreading or laying work, and a crack may be caused due to ground subsidence when laying as an underlay of concrete or the like. is there. Further, the tear strength is preferably 20 kgf or more. If the tear strength is less than 20 kgf, there is a problem that the plant is pierced and torn without being able to withstand the growing power of a plant having a strong growing power of grasses such as Japanese grass.

【００２４】本発明の防草シートが雑草の生育を抑制す
るという所期の目的を達成するためには、その遮光率が
８０％以上、望ましくは９０％以上であることが肝要で
ある。つまり、地表面に敷設したシート状物が太陽光を
効果的に遮断することによって内部の雑草の繁茂を防止
できるのであって、遮光率が８０％未満のものであると
本来の期待される効果が充分に発揮されないことが想定
される。このために、上記熱可塑性樹脂の織編布または
不織布からなるシート及び必要に応じて熱可塑性樹脂フ
イルムには、光透過性を抑制しまた意匠性を考慮して各
種顔料を配合することができる。顔料としては、フタロ
シアニン系、シアニン系、スチレン系、アントラキノン
系、キノフタリン系などの有機顔料およびカーボンブラ
ック、チタンブラック、酸化チタンなどの無機顔料が挙
げられる。これらの中で、遮光性と耐候性を向上させ、
分散性が良好で低廉なものとしてカーボンブラックが好
ましい。ここで顔料の配合量は、ポリオレフィン中に
０．１〜３重量％、好ましくは０．３〜１．５重量％と
するのがよい。In order for the weed control sheet of the present invention to achieve the intended purpose of suppressing the growth of weeds, it is important that the light-shielding ratio is 80% or more, preferably 90% or more. In other words, the sheet-like material laid on the ground surface effectively blocks sunlight, thereby preventing the growth of weeds inside. The originally expected effect is that the shading rate is less than 80%. Is not sufficiently exhibited. For this purpose, various pigments can be blended into the sheet made of the woven or knitted fabric or the non-woven fabric of the thermoplastic resin and, if necessary, the thermoplastic resin film in consideration of the light transmittance and the design. . Examples of the pigment include phthalocyanine-based, cyanine-based, styrene-based, anthraquinone-based, and quinophthaline-based organic pigments, and inorganic pigments such as carbon black, titanium black, and titanium oxide. Among these, improve the light-shielding properties and weather resistance,
Carbon black is preferable because of its good dispersibility and low cost. Here, the compounding amount of the pigment is 0.1 to 3% by weight, preferably 0.3 to 1.5% by weight in the polyolefin.

【００２５】また、上記防草シートは、長期間日光に晒
されるために高い耐候性が必要とされている。本発明で
用いる難燃剤は、ピペリジル基を有するトリアジン誘導
体であり、それ自身がヒンダードアミン系の光安定剤と
して働くため、非常に高い耐候性を有する。さらに、耐
候性を改良する方法としては、紫外線吸収剤や光安定剤
等の耐候剤を添加する方法を採用することもできる。In addition, the above-mentioned grass sheet is required to have high weather resistance because it is exposed to sunlight for a long time. The flame retardant used in the present invention is a triazine derivative having a piperidyl group, and itself functions as a hindered amine-based light stabilizer, and thus has extremely high weather resistance. Further, as a method for improving the weather resistance, a method of adding a weather agent such as an ultraviolet absorber or a light stabilizer can also be adopted.

【００２６】紫外線吸収剤の具体例としては、具体的に
は２-エチルヘキシル-２-シアノ-３,３’−ジフェニル
アクリレート、エチル-２-シアノ-３,３’-ジフェニル
アクリレート、オクチル-２-シアノ-３,３’-ジフェニ
ルアクリレート等のシアノアクリレート系紫外線吸収
剤、２,４-ジヒドロキシベンゾフェノン、２-ヒドロキ
シ-４-メトキシベンゾフェノン、２-ヒドロキシ-４-オ
クトキシベンゾフェノン等のベンゾフェノン系紫外線吸
収剤、２-（２′-ヒドロキシ -５′-メチルフェニル）
ベンゾトリアゾール、２-（２′-ヒドロキシ-５′-t-オ
クチルフェニル）ベンゾトリアゾール等のベンゾトリア
ゾール系紫外線吸収剤、レゾルシノールモノベンゾエー
ト、２,４-ジ-t-ブチルフェニル-３′-５′-ジ-t-ブチ
ル-４′-ヒドロキシベンゾエート等のベンゾエート系紫
外線吸収剤などが挙げられる。紫外線吸収剤の配合割合
は、熱可塑性樹脂に対して０.０５〜５重量％の範囲、
好ましくは０.１〜１重量％の範囲であるSpecific examples of the ultraviolet absorber include 2-ethylhexyl-2-cyano-3,3'-diphenyl acrylate, ethyl-2-cyano-3,3'-diphenyl acrylate, octyl-2- Cyanoacrylate-based ultraviolet absorbers such as cyano-3,3'-diphenylacrylate, benzophenone-based ultraviolet absorbers such as 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, and 2-hydroxy-4-octoxybenzophenone 2,2- (2'-hydroxy-5'-methylphenyl)
Benzotriazole UV absorbers such as benzotriazole, 2- (2'-hydroxy-5'-t-octylphenyl) benzotriazole, resorcinol monobenzoate, 2,4-di-t-butylphenyl-3'-5 ' And benzoate ultraviolet absorbers such as -di-t-butyl-4'-hydroxybenzoate. The blending ratio of the ultraviolet absorber is in the range of 0.05 to 5% by weight based on the thermoplastic resin,
Preferably it is in the range of 0.1 to 1% by weight.

【００２７】ヒンダードアミン系光安定剤としては、ビ
ス（２,２,６,６-テトラメチル-４-ピペリジル）セバケ
ート、テトラキス（２,２,６,６-テトラメチル-４-ピペ
リジル）-１,２,３,４-ブタンテトラカルボキシレー
ト、ビス（１,２,２,６,６-ペンタメチル-４-ピペリジ
ル）・ジ（トリデシル）-１,２,３,４-ブタンテトラカ
ルボキシレート、１-（２-ヒドロキシエチル）-２,２,
６,６-テトラメチル-４-ピペリジノールとコハク酸ジエ
チルの重縮合物等が挙げられる。光安定剤の配合割合
は、熱可塑性樹脂にに対して０．０５〜５重量％の範
囲、さらに好ましくは０.１〜１重量％の範囲である。As hindered amine light stabilizers, bis (2,2,6,6-tetramethyl-4-piperidyl) sebacate, tetrakis (2,2,6,6-tetramethyl-4-piperidyl) -1, 2,3,4-butanetetracarboxylate, bis (1,2,2,6,6-pentamethyl-4-piperidyl) di (tridecyl) -1,2,3,4-butanetetracarboxylate, 1- (2-hydroxyethyl) -2,2,
And polycondensates of 6,6-tetramethyl-4-piperidinol and diethyl succinate. The compounding ratio of the light stabilizer is in the range of 0.05 to 5% by weight, more preferably in the range of 0.1 to 1% by weight, based on the thermoplastic resin.

【００２８】本発明の熱可塑性樹脂には、本発明の趣旨
を逸脱しない範囲において、酸化防止剤、分散剤、滑
剤、帯電防止剤、顔料、無機充填剤、架橋剤、発泡剤、
核剤等の通常用いられる添加剤を配合してもよい。The thermoplastic resin of the present invention contains an antioxidant, a dispersant, a lubricant, an antistatic agent, a pigment, an inorganic filler, a cross-linking agent, a foaming agent, without departing from the spirit of the present invention.
A commonly used additive such as a nucleating agent may be blended.

【００２９】[0029]

【実施例】以下に実施例によって本発明の防草シートを
具体的に説明する。 実施例１ 高密度ポリエチレン（密度＝０．９５０ｇ／ｃｍ³、Ｍ
ＦＲ＝０．６ｇ／１０分）に対し、上記一般式(３)及び
一般式(４)で示されるものを組み合わせた窒素含有化合
物からなる難燃剤２重量％及びカーボンブラック１重量
％を配合した組成物をＴダイ法でフィルムに形成後、１
０ｍｍ幅にスリットし、延伸倍率９倍に延伸して繊度１
１００ｄｔのフラットヤーンを得た。このフラットヤー
ンを経緯に用いて、スルザー型織機で経緯１４本×１４
本／２．５４ｃｍの打込密度で、平織のフラットヤーン
織布を形成した。このようにして得られた織布の片面
に、分岐状低密度ポリエチレン（ＭＦＲ＝８.０ｇ／１
０分、密度＝０.９１７ｇ／ｃｍ^３）に上記一般式(３)
及び一般式(４)で示されるものを組み合わせた窒素含有
化合物からなる難燃剤を２重量％、発泡剤としてアゾジ
カルボンアミド１重量％及びカーボンブラック１重量％
を配合した混合物を用いて押出ラミネート法にて溶融温
度２４０℃で複数の透水孔を有するポリエチレンラミネ
ート層を積層した。複数の透水孔を有するポリエチレン
ラミネート層の厚みは５０μｍであった。得られた積層
シートにつき、難燃性試験において、ＪＩＳＡ１３２２
による燃焼試験では炭化長４５ｍｍで防炎１級に合格で
あった。また、該積層シートを敷設して防草シートとし
て使用したところ、降雨時に雨水が複数の透水孔から下
に流れ、シート表面に溜まることがなかった。EXAMPLES Hereinafter, the weed control sheet of the present invention will be described in detail with reference to examples. Example 1 High-density polyethylene (density = 0.950 g / cm ³ , M
FR = 0.6 g / 10 min), 2% by weight of a flame retardant composed of a nitrogen-containing compound obtained by combining those represented by the general formulas (3) and (4) and 1% by weight of carbon black. After forming the composition into a film by the T-die method,
Slit to 0 mm width, stretch to 9 times draw ratio, fineness 1
A 100 dt flat yarn was obtained. Using this flat yarn for the process, a Sulzer-type loom uses a process of 14
A plain yarn woven flat yarn woven fabric was formed at a pitch of 2.5 / 2.54 cm. On one surface of the woven fabric thus obtained, a branched low-density polyethylene (MFR = 8.0 g / 1)
0 min, density = 0.917 g / cm ³⁾ in the general formula (3)
2% by weight of a flame retardant comprising a nitrogen-containing compound obtained by combining the compound represented by the general formula (4) and 1% by weight of azodicarbonamide as a blowing agent and 1% by weight of carbon black
A polyethylene laminate layer having a plurality of water-permeable holes was laminated at a melting temperature of 240 ° C. by an extrusion lamination method using a mixture containing the above. The thickness of the polyethylene laminate layer having a plurality of water-permeable holes was 50 μm. The obtained laminated sheet was subjected to a flame retardancy test according to JISA1322.
In the combustion test, the carbonization length was 45 mm and the flameproof grade 1 was passed. Further, when the laminated sheet was laid and used as a grass-proof sheet, rainwater flowed down from the plurality of water-permeable holes during rainfall, and did not accumulate on the sheet surface.

【００３０】参考例１ 実施例１において、難燃剤をメラミンシアヌレート（商
品名：ＭＣ−６１０、日産化学株式会社製）に変え、上
記ポリプロピレンに対し、メラミンシアヌレート１０％
を配合して行ったこと以外は同様にして行った。その結
果、得られた防草シートの難燃性試験では炭化長１５０
ｍｍ以上で、ＪＩＳＡ１３２２の防炎１級に不合格であ
ったReference Example 1 In Example 1, the flame retardant was changed to melamine cyanurate (trade name: MC-610, manufactured by Nissan Chemical Co., Ltd.).
Was carried out in the same manner except that the above was blended. As a result, in the flame retardancy test of the obtained grass-proof sheet, the carbonization length was 150.
mm or more, did not pass the JISA1322 flame protection class 1

【００３１】参考例２ 実施例１において、難燃剤を臭素系難燃剤デカブロムジ
フェニルエーテルと三酸化アンチモンを３：１の比率の
混合物に変え、上記ポリプロピレンに対し、１０％を配
合して行ったこと以外は同様にして行った。その結果、
得られた防草シートの難燃性試験では炭化長８０ｍｍ
で、ＪＩＳＡ１３２２の防炎１級に不合格であった。Reference Example 2 The procedure of Example 1 was repeated, except that the flame retardant was changed to a mixture of the brominated flame retardant decabrom diphenyl ether and antimony trioxide at a ratio of 3: 1 and 10% was blended with the above polypropylene. Other than that, it carried out similarly. as a result,
In the flame retardancy test of the obtained grass sheet, the carbonization length was 80 mm.
Therefore, it did not pass the flameproof grade 1 of JISA1322.

【００３２】[0032]

【発明の効果】以上説明したように、本発明は、熱可塑
性樹脂の織編布または不織布からなるシートの少なくと
も片面に複数の透水孔を有する熱可塑性樹脂フイルムを
ラミネートしてなる積層シートであって、該熱可塑性樹
脂脂のシート及びフイルムの少なくとも一方に上記一般
式（１）で示される窒素含有化合物からなる難燃剤を配
合することにより、ハロゲン系難燃剤やりん系難燃剤の
ように有毒ガスの発生の恐れがない、遮光性を有し、且
つ、難燃性を備えた防草シートを提供することができ
る。As described above, the present invention relates to a laminated sheet obtained by laminating a thermoplastic resin film having a plurality of water-permeable holes on at least one surface of a sheet made of a woven or knitted fabric of a thermoplastic resin. By blending a flame retardant comprising a nitrogen-containing compound represented by the above general formula (1) into at least one of the thermoplastic resin fat sheet and the film, the flame retardant such as a halogen-based flame retardant or a phosphorus-based flame retardant is blended. It is possible to provide a grass-proof sheet having a light-shielding property and a flame-retardant property, without fear of generating toxic gas.

───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2B024 DA02 DB03 DB04 FB01 4H028 AA29 AA30 AA44 BA06    ────────────────────────────────────────────────── ─── Continuation of front page    F term (reference) 2B024 DA02 DB03 DB04 FB01                 4H028 AA29 AA30 AA44 BA06

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 熱可塑性樹脂の織編布または不織布から
なるシートの少なくとも片面に、複数の透水孔を有する
熱可塑性樹脂フイルムをラミネートしてなる積層シート
であって、上記熱可塑性樹脂のシート及びフイルムの少
なくとも一方に下記一般式（１）で示される窒素含有化
合物からなる難燃剤を配合してなることを特徴とする防
草シート。 H(R₁)Nー(CH₂)_aーN(R₂)ー(CH₂)_bーN(R_2')ー(CH₂)_cーN(R₁)H （１） （式中、R₁は下記一般式(２)で示されるピペリジル基を
含有するトリアジン誘導体基であり、R_2、R_2'は R₁また
は水素原子を表し、ａ，ｂ及びｃはそれぞれ、２〜５の
正数を表す。） 【化１】 （式中、R₃は炭素原子数１〜１０のアルキル基または水
素原子を表し、R₄は炭素原子数５〜１０のシクロアルキ
ル基または炭素原子数１〜４のアルキル基で置換された
炭素原子数５〜１０のシクロアルキル基を表す。）1. A laminated sheet obtained by laminating a thermoplastic resin film having a plurality of water-permeable holes on at least one surface of a sheet made of a woven or knitted fabric or a nonwoven fabric of a thermoplastic resin, wherein the thermoplastic resin sheet and A grass sheet comprising at least one of a film and a flame retardant comprising a nitrogen-containing compound represented by the following general formula (1). H (R ₁₎ N over (CH _{2) a} chromatography N (R ₂₎ over (CH _{2) b} over N (R _{2 ')} over (CH _{2) c} over _{N (R 1) H (1} ) ( in the formula , R ₁ is a triazine derivative group containing a piperidyl group represented by the following general formula (2), R _{2 and} R _{2 ′} represent R ₁ or a hydrogen atom, and a, b and c each represent 2 to 5 Represents a positive number of.) (Wherein, R ₃ represents an alkyl group having 1 to 10 carbon atoms or a hydrogen atom, and R ₄ represents a carbon atom substituted with a cycloalkyl group having 5 to 10 carbon atoms or an alkyl group having 1 to 4 carbon atoms. Represents a cycloalkyl group having 5 to 10 atoms.) 【請求項２】 難燃剤の配合量が熱可塑性樹脂に対して
０．１〜５重量％の範囲である請求項１に記載の防草シ
ート。2. The herbicidal sheet according to claim 1, wherein the amount of the flame retardant is in the range of 0.1 to 5% by weight based on the thermoplastic resin. 【請求項３】 複数の透水孔を有する熱可塑性樹脂フイ
ルムが熱可塑性樹脂を発泡剤の存在下で、溶融押出し、
発泡成形したものである請求項１または２に記載の防草
シート。3. A thermoplastic resin film having a plurality of water-permeable holes, wherein the thermoplastic resin is melt-extruded in the presence of a foaming agent.
The weed prevention sheet according to claim 1 or 2, which is formed by foam molding. 【請求項４】 難燃剤が下記一般式（３）で示される窒
素含有化合物である請求項１〜３のいずれかに記載の防
草シート。 H(R₁)Nー(CH₂)₃ーN(R₁)ー(CH₂)₂ーNHー(CH₂)₃ーN(R₁)H （３） （式中、R₁は下記一般式(４)で示されるピペリジル基を
含有するトリアジン誘導体基である。） 【化２】 4. The herbicidal sheet according to claim 1, wherein the flame retardant is a nitrogen-containing compound represented by the following general formula (3). H (R ₁₎ N over (CH _{2) 3} over N (R ₁₎ over (CH _{2) 2} over NH chromatography (CH _{2) 3} over _{N (R 1) H (3} ) ( wherein, R ₁ is the following It is a triazine derivative group containing a piperidyl group represented by the general formula (4).)