JP2003292903A - Coating composition, method for forming coating film and coated material - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To obtain a coating composition having excellent transparency and high chroma and not causing a framing phenomenon in an edge part, to provide a method for forming a coating film and to obtain a coated material. <P>SOLUTION: In the coating composition for base coating containing dye (A), the coating composition has the mass ratio of the dye (A) to a coating film-forming resin (B) satisfying the condition of (A)/(B) of 0.01/99.99-25/75. The method for forming a coating film comprises coating or not coating a substrate with a primer layer, coating the substrate with a base coating layer using the coating composition and coating the base coating layer with a top coating layer using a clear coating. The coated material is coated by the method for forming the coating film. <P>COPYRIGHT: (C)2004,JPO

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、塗料組成物、塗膜
形成方法及び塗装物に関する。さらに詳しくは、本発明
は、優れた透明感を有し、彩度が高く、エッジ部位に額
縁現象が発生しない塗料組成物、塗膜形成方法及び塗装
物に関する。TECHNICAL FIELD The present invention relates to a coating composition, a coating film forming method and a coated article. More specifically, the present invention relates to a coating composition, a coating film forming method, and a coated product, which have excellent transparency, have high saturation, and do not cause a frame phenomenon at an edge portion.

【０００２】[0002]

【従来の技術】自動車、オートバイ、パーソナルコンピ
ュータ、携帯電話などの塗装物品においては、高い意匠
性が必要とされ、彩度が高く、白ぼけ感がなく透明感に
優れたデザインが求められている。従来から、このよう
なデザインを発現するために、特許第２５８５９９１号
公報に記載されているような、ベースコート層を塗装し
たのち、染料を含有するカラークリヤー塗料を用いてト
ップコート層を塗装する塗膜形成方法が知られており、
キャンディートーンと呼ばれている。顔料と異なり、透
明性の高い染料を含有するカラークリヤー塗料をトップ
コートに用いると、白ぼけ感がなく、透明感が感じら
れ、さらに染料の発色性が良好なために、高い彩度を得
ることができる。しかし、ベースコート用塗料を塗装し
たのち、染料を含有するカラークリヤー塗料を用いてト
ップコート層を形成すると、塗装品のエッジ部位の膜厚
が厚くなるために、色調が濃く仕上がるいわゆる額縁現
象が発生する。この額縁現象のために、塗装ラインでカ
ラーマッチングをすることが困難であり、不良率が高い
という欠点があった。また、染料を含有するカラークリ
ヤー塗料ではなく、顔料を含有するカラークリヤー塗料
をトップコート層として用いると、額縁現象の発生はな
いが、顔料による白ぼけ感が発現し、透明感が劣るとい
う欠点があった。特開平３−１２２６３号公報には、透
明感及び深み感のある漆調という特殊な色調を得る塗膜
の形成方法として、電着塗料及び中塗り塗料を塗装して
焼き付けた塗膜上に、ベースコート及び透明クリヤーを
ウェットオンウェットで塗装し焼き付け、次いでカラー
クリヤー及び透明クリヤーをウェットオンウェットで塗
装して焼き付ける４コート２ベーク方式が提案されてい
る。しかし、４コート２ベーク方式は工程が長いので、
簡略な工程で、透明感と彩度に優れ、エッジ部位に額縁
現象が発生しない塗膜を形成する方法が求められてい
た。2. Description of the Related Art Painted articles such as automobiles, motorcycles, personal computers, and mobile phones are required to have high designability, high saturation, and a design with excellent transparency without white blur. . Conventionally, in order to develop such a design, as described in Japanese Patent No. 2585991, a base coat layer is applied, and then a top coat layer is applied using a color clear paint containing a dye. A film forming method is known,
It is called candy tone. Unlike pigments, when a color clear paint containing a highly transparent dye is used for the top coat, there is no white blur feeling, there is a feeling of transparency, and since the color development of the dye is good, high saturation is obtained. be able to. However, if the top coat layer is formed using color clear paint containing dye after coating the base coat paint, the film thickness at the edge of the coated product becomes thicker, resulting in a so-called frame phenomenon that gives a deeper color tone. To do. Due to this frame phenomenon, it is difficult to perform color matching on the coating line, and there is a defect that the defective rate is high. Further, when a color clear paint containing a pigment is used as the top coat layer instead of a color clear paint containing a dye, a frame phenomenon does not occur, but a white blur effect is exhibited by the pigment, resulting in poor transparency. was there. Japanese Unexamined Patent Publication No. 3-12263 discloses a method of forming a coating film that obtains a special color tone such as a lacquer tone having a transparent feeling and a deep feeling, on a coating film baked by coating an electrodeposition paint and an intermediate coating paint, A four-coat, two-bake method has been proposed in which a base coat and a transparent clear are applied wet-on-wet and baked, and then a color clear and a transparent clear are applied wet-on-wet and baked. However, because the 4 coat 2 bake method has a long process,
There has been a demand for a method of forming a coating film which is excellent in transparency and saturation and which does not cause a frame phenomenon at an edge portion in a simple process.

【０００３】[0003]

【発明が解決しようとする課題】本発明は、優れた透明
感を有し、彩度が高く、エッジ部位に額縁現象が発生し
ない塗料組成物、塗膜形成方法及び塗装物を提供するこ
とを目的としてなされたものである。DISCLOSURE OF THE INVENTION The present invention provides a coating composition, a coating film forming method, and a coated product which have excellent transparency, high saturation, and a frame phenomenon that does not occur at the edge portion. It was done for the purpose.

【０００４】[0004]

【課題を解決するための手段】本発明者らは、上記の課
題を解決すべく鋭意研究を重ねた結果、染料を含有する
ベースコート用塗料を塗装したのち、クリヤー塗料を用
いてトップコート層を塗装することにより、彩度が高
く、白ぼけ感がなく透明感に優れた塗膜を、エッジ部位
に額縁現象を発生させることなく、安定して形成し得る
ことを見いだし、この知見に基づいて本発明を完成する
に至った。すなわち本発明は、（１）染料(Ａ)を含有し
てなるベースコート用塗料組成物において、染料(Ａ)と
塗膜形成樹脂(Ｂ)との質量比が、(Ａ)／(Ｂ)＝０.０１
／９９.９９〜２５／７５の条件を満たすことを特徴と
する塗料組成物、（２）基材に、第１項記載の塗料組成
物を用いてベースコート層を塗装したのち、クリヤー塗
料を用いてトップコート層を塗装することを特徴とする
塗膜形成方法、（３）基材に、プライマー層を塗装し、
第１項記載の塗料組成物を用いてベースコート層を塗装
したのち、クリヤー塗料を用いてトップコート層を塗装
することを特徴とする塗膜形成方法、及び、（４）第２
項又は第３項記載の塗膜形成方法により塗装されてなる
ことを特徴とする塗装物、を提供するものである。さら
に、本発明の好ましい態様として、（５）ベースコート
用塗料組成物が、光輝性顔料を含有する第１項記載の塗
料組成物、及び、（６）光輝性顔料が、アルミニウム顔
料である第５項記載の塗料組成物、を挙げることができ
る。Means for Solving the Problems As a result of intensive studies to solve the above problems, the inventors of the present invention applied a base coat paint containing a dye and then applied a clear paint to form a top coat layer. It was found that by coating, a coating film with high saturation, no white blur and excellent transparency can be stably formed without causing a frame phenomenon at the edge part, and based on this finding The present invention has been completed. That is, the present invention provides (1) a coating composition for a base coat containing the dye (A), wherein the mass ratio of the dye (A) and the coating film forming resin (B) is (A) / (B) = 0.01
/99.99 to 25/75, a coating composition characterized in that (2) a substrate is coated with a base coat layer using the coating composition according to the first item, and then a clear coating is used. Coating method for coating a top coat layer, (3) coating a primer layer on a substrate,
A method for forming a coating film, which comprises coating a base coat layer with the coating composition according to item 1 and then coating a top coat layer with a clear coating, and (4) second
Item 3. A coated article, characterized by being coated by the method for forming a coating film according to item 3 or 3. Furthermore, as a preferred embodiment of the present invention, (5) the coating composition for a base coat contains a bright pigment, the coating composition according to the first aspect, and (6) the bright pigment is an aluminum pigment. The coating composition described in the above item can be mentioned.

【０００５】[0005]

【発明の実施の形態】本発明の塗料組成物は、染料(Ａ)
を含有してなるベースコート用塗料組成物において、染
料(Ａ)と塗膜形成樹脂(Ｂ)との質量比が、(Ａ)／(Ｂ)＝
０.０１／９９.９９〜２５／７５の条件を満たす塗料組
成物である。本発明の塗膜形成方法は、基材に、該塗料
組成物を用いてベースコート層を塗装したのち、クリヤ
ー塗料を用いてトップコート層を塗装する塗膜形成方
法、又は、基材に、プライマー層を塗装し、上記の塗料
組成物を用いてベースコート層を塗装したのち、クリヤ
ー塗料を用いてトップコート層を塗装する塗膜形成方法
である。本発明の塗装物は、上記の塗膜形成方法により
塗装されてなる塗装物である。本発明に用いる染料(Ａ)
に特に制限はなく、例えば、アゾ染料、アントラキノン
染料、インジゴ染料、フタロシアニン染料、カルボニウ
ム染料、キノンイミン染料、メチン染料、キノリン染
料、ニトロ染料などを挙げることができる。これらの中
で、有機溶剤に溶解する含金属錯塩染料は、耐候性と耐
水性に優れるので、特に好適に用いることができる。本
発明に用いる染料(Ａ)の市販品としては、例えば、ＢＡ
ＳＦ社のＺＡＰＯＮシリーズ、ＩＣＩ社のランプロノー
ルシリーズ、オリエント化学(株)のＶＡＲＩＦＡＳＴ
ＣＯＬＯＲＳ、クラリエント(株)のＳＡＶＩＮＹＬシリ
ーズ、田岡化学(株)のＯＲＥＯＳＯＬ ＦＡＳＴ ＣＯＬ
ＯＲＳ、チバ・スペシャリティー・ケミカルズ(株)のＯＲ
ＡＳＯＬシリーズなどを挙げることができる。本発明に
おいて、染料(Ａ)は、１種を単独で用いることができ、
あるいは、２種以上を組み合わせて用いることもでき
る。BEST MODE FOR CARRYING OUT THE INVENTION The coating composition of the present invention comprises a dye (A)
In the coating composition for a base coat containing the following, the mass ratio of the dye (A) and the coating film forming resin (B) is (A) / (B) =
It is a coating composition satisfying the conditions of 0.01 / 99.99 to 25/75. The coating film forming method of the present invention is a coating film forming method in which a base coat layer is applied to a substrate using the coating composition, and then a top coat layer is applied using a clear paint, or a primer is applied to the substrate. This is a method for forming a coating film in which a layer is applied, a base coat layer is applied using the above coating composition, and then a top coat layer is applied using a clear paint. The coated article of the present invention is a coated article coated by the above coating film forming method. Dye (A) used in the present invention
Is not particularly limited, and examples thereof include an azo dye, anthraquinone dye, indigo dye, phthalocyanine dye, carbonium dye, quinoneimine dye, methine dye, quinoline dye, and nitro dye. Among these, metal-containing complex salt dyes which are soluble in an organic solvent are excellent in weather resistance and water resistance, and thus can be particularly preferably used. Examples of commercially available dye (A) used in the present invention include BA
SF's ZAPON series, ICI's Lampronol series, Orient Chemical Co., Ltd. VARIFAST
COLORs, Clavient's SAVINYL series, Taoka Chemical's OREOSOL FAST COL
ORS, OR of Ciba Specialty Chemicals Co., Ltd.
Examples include the ASOL series. In the present invention, the dye (A) can be used alone,
Alternatively, two or more kinds can be used in combination.

【０００６】本発明に用いる塗膜形成樹脂(Ｂ)に特に制
限はなく、例えば、アクリル樹脂、ポリエステル樹脂、
アルキッド樹脂、繊維素系樹脂、ポリオレフィン樹脂、
塩素化ポリオレフィン樹脂、フッ素樹脂、シリコーン樹
脂などを挙げることができる。これらの樹脂は、１種を
単独で用いることができ、あるいは、２種以上を組み合
わせて用いることもできる。また、これらの樹脂は、非
架橋のラッカータイプとして用いることができ、あるい
は、アミノ樹脂、(ブロック)ポリイソシアネート化合
物、エポキシ化合物などの架橋形成樹脂と組み合わせ
て、架橋硬化型として用いることもできる。本発明の塗
料組成物は、染料(Ａ)と塗膜形成樹脂(Ｂ)との質量比
が、(Ａ)／(Ｂ)＝０.０１／９９.９９〜２５／７５であ
り、より好ましくは、０.１／９９.９〜１５／８５であ
る。染料(Ａ)の含有量が少なく、(Ａ)／(Ｂ)が０.０１
／９９.９９未満であると、塗膜の彩度が低くなるおそ
れがある。染料(Ａ)の含有量が多く、(Ａ)／(Ｂ)が２５
／７５を超えると、塗膜の耐湿性が低下するおそれがあ
る。The coating film forming resin (B) used in the present invention is not particularly limited, and examples thereof include acrylic resin, polyester resin,
Alkyd resin, fibrous resin, polyolefin resin,
Examples include chlorinated polyolefin resins, fluororesins, silicone resins and the like. These resins can be used individually by 1 type, or can also be used in combination of 2 or more type. Further, these resins can be used as a non-crosslinked lacquer type, or can be used as a crosslinkable curable type in combination with a crosslink forming resin such as an amino resin, a (block) polyisocyanate compound or an epoxy compound. In the coating composition of the present invention, the mass ratio of the dye (A) and the coating film forming resin (B) is (A) / (B) = 0.01 / 99.99 to 25/75, and more preferably Is 0.1 / 99.9 to 15/85. Dye (A) content is low, and (A) / (B) is 0.01
If it is less than 99.99, the saturation of the coating film may be low. High content of dye (A), 25 (A) / (B)
If it exceeds / 75, the moisture resistance of the coating film may decrease.

【０００７】本発明の塗料組成物には、光輝性顔料を含
有させることができる。光輝性顔料としては、例えば、
ノンリーフィング型アルミニウムフレーク、ニッケルフ
レーク、銅フレーク、チタンフレーク、ガラスフレーク
などのフレーク、パールマイカ、着色パールマイカなど
のマイカ粉末、シリカフレーク、アルミナフレークなど
の偏光性顔料、金属、二酸化チタンなどで被覆されたガ
ラスフレーク顔料、着色アルミニウムフレーク顔料、金
属酸化物被覆アルミナフレーク顔料、金属酸化物被覆シ
リカフレーク顔料、微粒子酸化チタン顔料、板状酸化鉄
などを挙げることができる。本発明の塗料組成物は、必
要に応じて、その他の着色顔料や各種添加剤などを含有
させることができる。着色顔料としては、例えば、アゾ
レーキ系顔料、フタロシアニン系顔料、インジゴ系顔
料、ペリノン系顔料、ペリレン系顔料、キノフタロン系
顔料、ジオキサジン系顔料、キナクリドン系顔料などの
有機顔料や、黄鉛、黄色酸化鉄、ベンガラ、二酸化チタ
ンなどの無機顔料を挙げることができる。添加剤として
は、例えば、ベンゾトリアゾール、蓚酸アニリド系など
の紫外線吸収剤、フェノール系などの酸化防止剤、シリ
コーン系などのレベリング剤、ワックス、有機ベントナ
イトなどの粘性制御剤、硬化触媒などを挙げることがで
きる。The coating composition of the present invention may contain a bright pigment. As the bright pigment, for example,
Non-leafing type aluminum flakes, nickel flakes, copper flakes, titanium flakes, glass flakes and other flakes, pearl mica, colored pearl mica and other mica powder, silica flakes, alumina flakes and other polarizing pigments, metals, titanium dioxide, etc. Glass flake pigments, colored aluminum flake pigments, metal oxide-coated alumina flake pigments, metal oxide-coated silica flake pigments, fine particle titanium oxide pigments, and plate-shaped iron oxide. The coating composition of the present invention may contain other color pigments, various additives, and the like, if necessary. Examples of color pigments include organic pigments such as azo lake pigments, phthalocyanine pigments, indigo pigments, perinone pigments, perylene pigments, quinophthalone pigments, dioxazine pigments, quinacridone pigments, yellow lead, and yellow iron oxide. , Red iron oxide, titanium dioxide and the like. Examples of the additive include benzotriazole, anilide oxalate-based ultraviolet absorbers, phenol-based antioxidants, silicone-based leveling agents, waxes, viscosity control agents such as organic bentonite, and curing catalysts. You can

【０００８】本発明の塗料組成物は、有機溶剤に溶解し
て使用することが好ましい。使用する有機溶剤として
は、例えば、芳香族炭化水素系溶剤、エステル系溶剤、
ケトン系溶剤、アルコール系溶剤、エーテル系溶剤など
を挙げることができる。本発明の塗膜形成方法の第一の
態様においては、基材に本発明の塗料組成物を用いてベ
ースコート層を塗装したのち、クリヤー塗料を用いてト
ップコート層を塗装する。ベースコート層とトップコー
ト層は、ウェットオンウェットで、２コート１ベーク方
式により塗装することができる。本発明の塗膜形成方法
の第二の態様においては、基材にプライマー層を塗装
し、本発明の塗料組成物を用いてベースコート層を塗装
したのち、クリヤー塗料を用いてトップコート層を塗装
する。プライマー層とベースコート層とトップコート層
は、ウェットオンウェットで、３コート１ベーク方式に
より塗装することができる。プライマー層を形成するこ
とにより、素材との密着性を向上することができる。本
発明方法によれば、優れた透明感を有し、彩度が高く、
鮮やかなキャンディートーンを有する塗膜を安定して容
易に形成することができる。本発明の塗膜形成方法にお
いては、霧化式塗装機を用い、エアスプレー方式、静電
方式などにより塗装することが好ましい。The coating composition of the present invention is preferably used by dissolving it in an organic solvent. Examples of the organic solvent used include aromatic hydrocarbon solvents, ester solvents,
Examples thereof include ketone solvents, alcohol solvents, ether solvents and the like. In the first embodiment of the coating film forming method of the present invention, a base coat layer is applied to a substrate using the coating composition of the present invention, and then a top coat layer is applied using a clear paint. The base coat layer and the top coat layer can be applied wet-on-wet by a two-coat one-bake method. In the second aspect of the coating film forming method of the present invention, a primer layer is applied to a substrate, a base coat layer is applied using the coating composition of the present invention, and then a top coat layer is applied using a clear paint. To do. The primer layer, the base coat layer, and the top coat layer can be applied wet-on-wet by a 3-coat 1-bake method. By forming the primer layer, the adhesion to the material can be improved. According to the method of the present invention, it has excellent transparency and high saturation,
A coating film having a bright candy tone can be stably and easily formed. In the coating film forming method of the present invention, it is preferable to use an atomization type coating machine and coat by an air spray method, an electrostatic method or the like.

【０００９】本発明方法を適用する被塗物に特に制限は
なく、例えば、鉄、アルミニウム、マグネシウム又はこ
れらの合金を含む金属類、ガラス、コンクリートなどの
無機材料、ポリエチレン、ポリプロピレン、エチレン−
酢酸ビニル共重合体、ポリアミド、アクリル樹脂、ポリ
エステル、塩化ビニル樹脂、塩化ビニリデン樹脂、ポリ
カーボネート、ポリウレタン、アクリロニトリル−ブタ
ジエン−スチレン共重合体などの樹脂成形品、各種ＦＲ
Ｐなどのプラスチック材料、木材、紙などを挙げること
ができる。なお、これら被塗基材には、予め適宜なプラ
イマーやプレコート処理を施すことができる。本発明の
塗装物は、白ぼけ感がなく優れた透明感を有し、彩度が
高く、エッジ部に額縁現象がなく、耐湿性に優れ、高温
高湿の環境で使用しても、ブリスター、白化、艶引けな
どの変化を生ずるおそれが少ない。The article to which the method of the present invention is applied is not particularly limited, and examples thereof include metals such as iron, aluminum, magnesium or alloys thereof, inorganic materials such as glass and concrete, polyethylene, polypropylene, ethylene-
Vinyl acetate copolymer, polyamide, acrylic resin, polyester, vinyl chloride resin, vinylidene chloride resin, polycarbonate, polyurethane, acrylonitrile-butadiene-styrene copolymer and other resin molded products, various FR
Examples thereof include plastic materials such as P, wood, and paper. In addition, an appropriate primer or precoat treatment can be applied to these coated substrates in advance. The coated article of the present invention has an excellent transparency with no white blur, has a high saturation, does not have a frame phenomenon at the edge portion, has excellent moisture resistance, and is a blister even when used in a high temperature and high humidity environment. It is less likely to cause changes such as whitening and glossiness.

【００１０】[0010]

【実施例】以下に、実施例を挙げて本発明をさらに詳細
に説明するが、本発明はこれらの実施例によりなんら限
定されるものではない。なお、実施例及び比較例におい
て、透明感、彩度、エッジ部位の額縁現象は、下記の基
準にしたがって、塗膜の外観評価の有資格者１０人によ
り行い、その平均値を算出した。 （１）透明感 ３；クリヤーと同等の透明性を有している。 ２；少し、白ぼけている。 １；白ぼけている。 （２）彩度 ２；彩度が高い。 １；彩度が低い。 （３）エッジ部位の額縁現象 センター部位を標準とし、エッジから１cm以内の部位の
色変化を判定する。 ２；色に変化がない。 １；色が濃く、額縁現象が発生している。 （４）耐湿性 塗装板を、５０℃、相対湿度９８％の雰囲気下で１２０
時間曝露試験し、塗膜の変化を観察する。 ○；塗膜に変化がない。 ×；ブリスター、白化、艶引けなどが発生する。The present invention will be described in more detail below with reference to examples, but the present invention is not limited to these examples. In the examples and comparative examples, the transparency, the saturation, and the frame phenomenon of the edge portion were performed by 10 persons who were qualified to evaluate the appearance of the coating film according to the following criteria, and the average value thereof was calculated. (1) Transparency 3; Transparency equivalent to clear. 2; It is slightly blurred. 1; It is blurred. (2) Saturation 2: High saturation. 1; Saturation is low. (3) Frame phenomenon of edge part The center part is the standard, and the color change of the part within 1 cm from the edge is judged. 2; There is no change in color. 1; The color is dark and the frame phenomenon occurs. (4) The moisture-resistant coated plate is placed in an atmosphere of 50 ° C. and 98% relative humidity for 120
A time exposure test is performed, and changes in the coating film are observed. ◯: There is no change in the coating film. ×: Blister, whitening, and gloss loss occur.

【００１１】製造例１（ベースコート用塗料Ａ） 赤色染料Ａ［ＩＣＩ社、ランプロノ−ルレッド２ＢＲ］
３質量部をメチルエチルケトン１０質量部に溶解し、染
料溶液を調製した。この染料溶液１３質量部、アクリル
樹脂［大日本インキ化学工業(株)、アクリディックＡ−
１９０、加熱残分５０質量％］３０質量部、アルミペー
スト［昭和アルミパウダー(株)、ＳＡＰ５６１ＰＳ、加
熱残分６５質量％］５質量部及びセルロースアセテート
ブチレート［イーストマン・ケミカルズ社、ＣＡＢ５３
１−１］の３０質量％酢酸エチル溶液１０質量部を順次
加えて撹拌した。次に、ポリイソシアネート化合物［住
友バイエルウレタン(株)、スミジュールＮ−７５、加熱
残分７５質量％］５質量部を加え、さらにキシレンと酢
酸イソブチルとの質量比５０：５０の混合溶剤３７質量
部を加えて撹拌し、ベースコート用塗料Ａを調製した。 製造例２（ベースコート用塗料Ｂ） アクリル樹脂［大日本インキ化学工業(株)、アクリディ
ックＡ−１９０、加熱残分５０質量％］２０質量部と有
機赤色顔料［チバ・ガイギー社、クロモフタルレッドＡ
３Ｂ］３質量部とを、ガラスビーズを分散媒体とするア
トライターで粒径が５μｍ以下になるまで分散し、赤色
着色ペーストを調製した。上記のアクリル樹脂１０質量
部、アルミペースト［昭和アルミパウダー(株)、ＳＡＰ
５６１ＰＳ、加熱残分６５質量％］５質量部、セルロー
スアセテートブチレート［イーストマン・ケミカルズ
社、ＣＡＢ５３１−１］の３０質量％酢酸エチル溶液１
０質量部及び上記の赤色着色ペースト２３質量部を順次
加えて撹拌した。次に、ポリイソシアネート化合物［住
友バイエルウレタン(株)、スミジュールＮ−７５、加熱
残分７５質量％］５質量部を加え、さらにキシレンと酢
酸イソブチルとの質量比５０：５０の混合溶剤４７質量
部を加えて撹拌し、ベースコート用塗料Ｂを調製した。 製造例３〜５（ベースコート用塗料Ｃ〜Ｅ） 第１表に示す配合により、製造例１又は製造例２と同様
にして、ベースコート用塗料Ｃ〜Ｅを調製した。製造例
１〜５で調製したベースコート用塗料Ａ〜Ｅの配合組成
を、第１表に示す。Production Example 1 (Base coat paint A) Red dye A [Lampronol Red 2BR manufactured by ICI]
3 parts by mass was dissolved in 10 parts by mass of methyl ethyl ketone to prepare a dye solution. 13 parts by weight of this dye solution, acrylic resin [Dainippon Ink and Chemicals, Inc., Acridic A-
190, heating residue 50% by mass] 30 parts by mass, aluminum paste [Showa Aluminum Powder Co., Ltd., SAP561PS, heating residue 65% by mass] 5 parts by mass and cellulose acetate butyrate [Eastman Chemicals, CAB53].
1-1], and 10 parts by mass of a 30% by mass ethyl acetate solution were sequentially added and stirred. Next, 5 parts by mass of a polyisocyanate compound [Sumitomo Bayer Urethane Co., Ltd., Sumidule N-75, heating residue 75% by mass] was added, and 37% by mass of a mixed solvent of xylene and isobutyl acetate in a mass ratio of 50:50. Parts were added and stirred to prepare base coat paint A. Production Example 2 (Base coat paint B) 20 parts by mass of acrylic resin [Dainippon Ink and Chemicals, Inc., Acridic A-190, heating residue 50% by mass] and organic red pigment [Ciba Geigy Co., Chromophthal red] A
3B] 3 parts by mass were dispersed with an attritor using glass beads as a dispersion medium until the particle size became 5 μm or less, to prepare a red colored paste. 10 parts by mass of the above acrylic resin, aluminum paste [Showa Aluminum Powder Co., SAP
561PS, heating residue 65 mass%] 5 mass parts, cellulose acetate butyrate [Eastman Chemicals, CAB531-1] 30 mass% ethyl acetate solution 1
0 parts by mass and 23 parts by mass of the above red colored paste were sequentially added and stirred. Next, 5 parts by mass of a polyisocyanate compound [Sumitomo Bayer Urethane Co., Ltd., Sumidule N-75, heating residue 75% by mass] was added, and further 47% by mass of a mixed solvent of xylene and isobutyl acetate in a mass ratio of 50:50. Parts were added and stirred to prepare base coat paint B. Manufacture Examples 3 to 5 (Base coat paints C to E) With the formulations shown in Table 1, base coat paints C to E were prepared in the same manner as in Manufacture Example 1 or Manufacture Example 2. Table 1 shows the composition of the base coat paints A to E prepared in Production Examples 1 to 5.

【００１２】[0012]

【表１】 [Table 1]

【００１３】［注］ １）赤色染料Ａ：ＩＣＩ社、ランプロノ−ルレッド２Ｂ
Ｒ ２）赤色染料Ｂ：ＢＡＳＦ社、ＺＡＰＯＮ レッド３３
５ ３）有機赤色顔料：チバ・ガイギー社、クロモフタルレ
ッドＡ３Ｂ ４）アクリル樹脂：大日本インキ化学工業(株)、アクリ
ディックＡ−１９０、加熱残分５０質量％ ５）アルミペースト：昭和アルミパウダー(株)、ＳＡＰ
５６１ＰＳ、加熱残分６５質量％ ６）セルロースアセテートブチレート：イーストマン・
ケミカルズ社、ＣＡＢ５３１−１ ７）ポリイソシアネート化合物：住友バイエルウレタン
(株)、スミジュールＮ−７５、加熱残分７５質量％ 製造例６（トップコート用塗料Ａ） トップコート用塗料として、アクリルウレタン樹脂系塗
料［日本油脂ＢＡＳＦコーティングス(株)、ハイウレタ
ンＮｏ.６５００クリヤー、２液型クリヤー塗料］を用
いた。その主剤と硬化剤の質量比は、４／１である。希
釈シンナー（キシレン／トルエン＝７０／３０、質量
比）で、塗料粘度が２０秒（フォードカップ＃４；２５
℃）になるように希釈し、トップコート用塗料Ａを調製
した。 製造例７（トップコート用塗料Ｂ） 赤色染料Ａ［ＩＣＩ社、ランプロノールレッド２ＢＲ］
１質量部をメチルエチルケトン４質量部に溶解し、染料
溶液を調製した。この染料溶液５質量部とアクリルウレ
タン樹脂系塗料［日本油脂ＢＡＳＦコーティングス
(株)、ハイウレタンＮｏ.６５００クリヤー、２液型ク
リヤー塗料］９５質量部とを混合した。この場合、主剤
と硬化剤の質量比は、４／１である。次に、希釈シンナ
ー（キシレン／トルエン＝７０／３０、質量比）で、塗
料粘度が２０秒（フォードカップ＃４；２５℃）になる
ように希釈し、トップコート用塗料Ｂを調製した。 製造例８（トップコート用塗料Ｃ） アクリルウレタン樹脂系塗料［日本油脂ＢＡＳＦコーテ
ィングス(株)、ハイウレタンＮｏ.６５００クリヤー、
２液型クリヤー塗料］の主剤５０質量部、キシレン３０
質量部及び有機赤色顔料［チバ・ガイギー社、クロモフ
タルレッドＡ３Ｂ］１質量部とを、ガラスビーズを分散
媒体とするアトライターで粒径が５μｍ以下になるまで
分散し、赤色着色ペーストを調製した。この赤色着色ペ
ースト８１質量部に、アクリルウレタン樹脂系塗料［日
本油脂ＢＡＳＦコーティングス(株)、ハイウレタンＮ
ｏ.６５００クリヤー、２液型クリヤー塗料］の主剤３
０質量部と硬化剤２０質量部を混合した。次に、希釈シ
ンナー（キシレン／トルエン＝７０／３０、質量比）
で、塗料粘度が２０秒（フォードカップ＃４；２５℃）
になるように希釈し、トップコート用塗料Ｃを調製し
た。 製造例９（プライマー） ２液型アクリルウレタン塗料［日本油脂ＢＡＳＦコーテ
ィングス(株)、ハイウレタンＮｏ.５０００プライマー
黒］の主剤と硬化剤を質量比６／１で混合し、希釈シン
ナー（キシレン／トルエン＝７０／３０、質量比）で、
塗料粘度が１５秒（フォードカップ＃４；２５℃）にな
るように希釈して、プライマーを調製した。[Note] 1) Red dye A: Lampronol Red 2B, manufactured by ICI.
R 2) Red dye B: BASF, ZAPON red 33
5 3) Organic red pigment: Ciba Geigy, Chromophtal red A3B 4) Acrylic resin: Dainippon Ink and Chemicals, Inc., Acridic A-190, heating residue 50 mass% 5) Aluminum paste: Showa aluminum powder Ltd., SAP
561PS, heating residue 65 mass% 6) Cellulose acetate butyrate: Eastman
Chemicals, CAB531-1 7) Polyisocyanate compound: Sumitomo Bayer Urethane
Co., Ltd., Sumidule N-75, heating residue 75% by mass Production Example 6 (top coat paint A) As a top coat paint, acrylic urethane resin-based paint [NOF BASF Coatings Co., Ltd., High Urethane No. .6500 clear, two-pack clear paint] was used. The mass ratio of the main agent to the curing agent is 4/1. With diluted thinner (xylene / toluene = 70/30, mass ratio), paint viscosity is 20 seconds (Ford cup # 4; 25
C.) to prepare Topcoat Coating Material A. Production Example 7 (Paint B for topcoat) Red dye A [ICI, Lampronol Red 2BR]
1 part by mass was dissolved in 4 parts by mass of methyl ethyl ketone to prepare a dye solution. 5 parts by mass of this dye solution and acrylic urethane resin-based paint [NOF BASF Coatings]
95 parts by weight of Hi Urethane No. 6500 clear, 2 liquid type clear paint]. In this case, the mass ratio of the main agent and the curing agent is 4/1. Next, a top coat paint B was prepared by diluting with a diluted thinner (xylene / toluene = 70/30, mass ratio) so that the paint viscosity would be 20 seconds (Ford cup # 4; 25 ° C.). Production Example 8 (Paint C for top coat) Acrylic urethane resin-based paint [NOF BASF Coatings Co., Ltd., High Urethane No. 6500 Clear,
50 parts by weight of main component of 2 component type clear paint, xylene 30
Part by mass and 1 part by mass of an organic red pigment [Chiba Geigy, Chromophtal red A3B] were dispersed with an attritor using glass beads as a dispersion medium until the particle size became 5 μm or less to prepare a red colored paste. . Acrylic urethane resin-based paint [NOF BASF Coatings Co., Ltd., Hi Urethane N] was added to 81 parts by mass of this red colored paste.
o.6500 clear, 2 component clear paint]
0 parts by mass and 20 parts by mass of the curing agent were mixed. Next, diluted thinner (xylene / toluene = 70/30, mass ratio)
And the paint viscosity is 20 seconds (Ford Cup # 4; 25 ° C)
Was diluted so that the coating composition C for topcoat was prepared. Production Example 9 (Primer) A two-component acrylic urethane paint [NOF BASF Coatings Co., Ltd., High Urethane No. 5000 Primer Black] was mixed with the base material and the curing agent at a mass ratio of 6/1, and diluted thinner (xylene / Toluene = 70/30, mass ratio),
A primer was prepared by diluting it so that the viscosity of the paint was 15 seconds (Ford cup # 4; 25 ° C).

【００１４】実施例１ ＡＢＳ基材［日本Ａ＆Ｌ(株)、クララスチックＭＶＦ、
７cm×１２cm×３mm」を、イソプロピルアルコールを用
いて脱脂して被塗物とし、希釈シンナー（キシレン／ト
ルエン＝７０／３０、質量比）で、塗料粘度が１５秒
（フォードカップ＃４；２５℃）になるように希釈した
ベースコート用塗料Ａを乾燥膜厚１５μｍとなるように
エアスプレーで塗装し、室温にて１０分間放置した。次
いで、トップコート用塗料Ａを乾燥膜厚２５μｍとなる
ようにエアスプレーで塗装し、室温にて１０分間放置し
たのち、７５℃で３０分間焼き付け、塗装板を得た。室
温にて７２時間放置したのち、耐湿試験を行った。塗装
板は、クリヤーと同等の透明感を有し、彩度は高く、エ
ッジ部位の額縁現象は認められなかった。耐湿試験にお
いて、塗膜に変化は生じなかった。 実施例２ ベースコート用塗料Ａの代わりに、ベースコート用塗料
Ｃを用いた以外は、実施例１と同様にして塗装板を作製
し、評価を行った。 実施例３ ベースコート用塗料Ａの代わりに、ベースコート用塗料
Ｄを用いた以外は、実施例１と同様にして塗装板を作製
し、評価を行った。 実施例４ ＡＢＳ基材［日本Ａ＆Ｌ(株)、クララスチックＭＶＦ、
７cm×１２cm×３mm」を、イソプロピルアルコールを用
いて脱脂して被塗物とし、プライマーを乾燥膜厚１０μ
ｍになるようにエアスプレーで塗装し、室温にて１０分
間放置したのち、ベースコート用塗料Ｃを乾燥膜厚１５
μｍとなるようにエアスプレーで塗装し、室温にて１０
分間放置した。次いで、トップコート用塗料Ａを乾燥膜
厚２５μｍとなるようにエアスプレーで塗装し、室温に
て１０分間放置したのち、７５℃で３０分間焼き付け、
塗装板を得た。得られた塗装板について、実施例１と同
様にして評価を行った。Example 1 ABS substrate [Japan A & L Co., Clarastic MVF,
7 cm x 12 cm x 3 mm "was degreased with isopropyl alcohol to give a coated object, diluted thinner (xylene / toluene = 70/30, mass ratio), and a paint viscosity of 15 seconds (Ford cup # 4; 25 ° C). The coating composition A for base coat diluted so as to be 1) was coated with an air spray so as to have a dry film thickness of 15 μm, and left at room temperature for 10 minutes. Next, the top coat coating material A was applied by air spraying so as to have a dry film thickness of 25 μm, left at room temperature for 10 minutes, and then baked at 75 ° C. for 30 minutes to obtain a coated plate. After left at room temperature for 72 hours, a moisture resistance test was conducted. The coated plate had a transparency equivalent to that of clear, high saturation, and no frame phenomenon at the edge part was observed. No change occurred in the coating film in the moisture resistance test. Example 2 A coated plate was prepared and evaluated in the same manner as in Example 1 except that the base coat coating material C was used in place of the base coat coating material A. Example 3 A coated plate was prepared and evaluated in the same manner as in Example 1 except that the base coat paint D was used in place of the base coat paint A. Example 4 ABS substrate [Japan A & L Co., Clarastic MVF,
"7 cm x 12 cm x 3 mm" is degreased with isopropyl alcohol to be the coated object, and the primer is a dry film thickness of 10μ.
m by air spray and leave at room temperature for 10 minutes, then apply base coat paint C to dry film thickness 15
Paint with air spray so that it becomes μm,
Let stand for a minute. Next, the top coat coating material A is applied by air spraying so as to have a dry film thickness of 25 μm, left at room temperature for 10 minutes, and then baked at 75 ° C. for 30 minutes.
A coated board was obtained. The obtained coated plate was evaluated in the same manner as in Example 1.

【００１５】比較例１ ベースコート用塗料Ａの代わりに、ベースコート用塗料
Ｂを用いた以外は、実施例１と同様にして塗装板を作製
し、評価を行った。塗装板は、クリヤーと同等の透明感
を有し、エッジ部位の額縁現象は認められなかったが、
彩度が低かった。耐湿試験において、塗膜に変化は生じ
なかった。 比較例２ ベースコート用塗料Ａの代わりに、ベースコート用塗料
Ｂを用い、トップコート用塗料Ａの代わりに、トップコ
ート用塗料Ｂを用いた以外は、実施例１と同様にして塗
装板を作製し、評価を行った。 比較例３ ベースコート用塗料Ａの代わりに、ベースコート用塗料
Ｂを用い、トップコート用塗料Ａの代わりに、トップコ
ート用塗料Ｃを用いた以外は、実施例１と同様にして塗
装板を作製し、評価を行った。 比較例４ ベースコート用塗料Ａの代わりに、ベースコート用塗料
Ｅを用いた以外は、実施例１と同様にして塗装板を作製
し、評価を行った。実施例１〜４及び比較例１〜４の結
果を、第２表に示す。Comparative Example 1 A coated plate was prepared and evaluated in the same manner as in Example 1 except that the base coat coating material B was used in place of the base coat coating material A. The coated plate had a transparency similar to that of clear, and no frame phenomenon was observed at the edge part.
The saturation was low. No change occurred in the coating film in the moisture resistance test. Comparative Example 2 A coated plate was prepared in the same manner as in Example 1 except that the base coat paint B was used in place of the base coat paint A, and the top coat paint B was used in place of the top coat paint A. , Evaluated. Comparative Example 3 A coated plate was prepared in the same manner as in Example 1 except that the base coat paint B was used in place of the base coat paint A, and the top coat paint C was used in place of the top coat paint A. , Evaluated. Comparative Example 4 A coated plate was prepared and evaluated in the same manner as in Example 1 except that the base coat coating material E was used in place of the base coat coating material A. The results of Examples 1 to 4 and Comparative Examples 1 to 4 are shown in Table 2.

【００１６】[0016]

【表２】 [Table 2]

【００１７】第２表に見られるように、染料(Ａ)と塗膜
形成樹脂(Ｂ)の固形分の質量比が８／９２〜１４／８６
であるベースコート用塗料Ａ、Ｃ又はＤを塗装し、クリ
ヤーのトップコート用塗料Ａを用いてトップコート層を
形成した実施例１〜４の塗膜は、透明感に優れ、彩度が
高く、額縁現象が発生せず、耐湿性試験においても塗膜
に変化が生じていない。これに対して、有機赤色顔料を
含有するベースコート用塗料Ｂとクリヤーのトップコー
ト用塗料Ａを塗装した比較例１の塗膜は彩度が低く、有
機赤色顔料を含有するベースコート用塗料Ｂと染料を含
有するカラークリヤーのトップコート用塗料Ｂを塗装し
た比較例２の塗膜には額縁現象が発生し、有機赤色顔料
を含有するベースコート用塗料Ｂと有機赤色顔料を含有
するトップコート用塗料Ｃを塗装した比較例３の塗膜は
白ぼけている。また、染料(Ａ)と塗膜形成樹脂(Ｂ)の固
形分の質量比が３１／６９であるベースコート用塗料Ｅ
とクリヤーのトップコート用塗料Ａを塗装した比較例４
の塗膜は、耐湿性試験において艶引けが発生している。As can be seen from Table 2, the mass ratio of the solid contents of the dye (A) and the coating film forming resin (B) is 8/92 to 14/86.
The coating films of Examples 1 to 4 in which the base coat paints A, C or D which are the following are applied and the top coat layer is formed using the clear top coat paint A have excellent transparency and high saturation. No frame phenomenon occurred, and there was no change in the coating film even in the moisture resistance test. On the other hand, the coating film of Comparative Example 1 in which the base coat coating material B containing the organic red pigment and the clear topcoat coating material A were applied had low saturation, and the base coating coating material B containing the organic red pigment and the dye A frame phenomenon occurs in the coating film of Comparative Example 2 in which the color clear top coat coating material B containing the above is applied, and the base coat coating material B containing the organic red pigment and the top coat coating material C containing the organic red pigment. The coating film of Comparative Example 3 coated with is blurred. In addition, the base coating composition E in which the mass ratio of the solid contents of the dye (A) and the coating film forming resin (B) is 31/69.
Comparative Example 4 in which Paint A for clear and clear top coat was applied
The coating film of No. 2 has glossiness in the moisture resistance test.

【００１８】[0018]

【発明の効果】本発明の塗料組成物、塗膜形成方法によ
れば、彩度が高く、白ぼけ感がなく透明感に優れた塗装
物を、エッジ部位に額縁現象を発生させることなく、安
定して製造することができる。EFFECTS OF THE INVENTION According to the coating composition and the method for forming a coating film of the present invention, it is possible to obtain a coated article having high saturation, no white blur and excellent transparency without causing a frame phenomenon at the edge portion. It can be manufactured stably.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 岡山 太一 神奈川県茅ヶ崎市甘沼200−１−306 ヴィ スタヒル Ｆターム(参考） 4D075 AE03 CA38 CA43 CB04 CB06 CB09 DB01 DB02 DB07 DB12 DB13 DB18 DB21 DB36 DB38 DB40 DB43 DB48 DB50 DB53 DB61 DC11 DC21 DC24 EA07 EA23 EA41 EA43 EB13 EB15 EB16 EB22 EB31 EB32 EB35 EB36 EB38 EB42 EC11 EC54 4J038 CG141 DG191 DG261 EA011 HA066 KA08 NA01    ─────────────────────────────────────────────────── ─── Continued front page    (72) Inventor Taichi Okayama             200-1-306 VI, Kanuma, Chigasaki City, Kanagawa Prefecture             Stahill F-term (reference) 4D075 AE03 CA38 CA43 CB04 CB06                       CB09 DB01 DB02 DB07 DB12                       DB13 DB18 DB21 DB36 DB38                       DB40 DB43 DB48 DB50 DB53                       DB61 DC11 DC21 DC24 EA07                       EA23 EA41 EA43 EB13 EB15                       EB16 EB22 EB31 EB32 EB35                       EB36 EB38 EB42 EC11 EC54                 4J038 CG141 DG191 DG261 EA011                       HA066 KA08 NA01

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】染料（Ａ）を含有してなるベースコート用
塗料組成物において、染料（Ａ）と塗膜形成樹脂（Ｂ）
との質量比が、（Ａ）／（Ｂ）＝０.０１／９９.９９〜
２５／７５の条件を満たすことを特徴とする塗料組成
物。1. A base coat coating composition containing a dye (A), which comprises a dye (A) and a film-forming resin (B).
Mass ratio with (A) / (B) = 0.01 / 99.99-
A coating composition which satisfies the condition of 25/75. 【請求項２】基材に、請求項１記載の塗料組成物を用い
てベースコート層を塗装したのち、クリヤー塗料を用い
てトップコート層を塗装することを特徴とする塗膜形成
方法。2. A method for forming a coating film, which comprises coating a base coat layer on a substrate with the coating composition according to claim 1 and then coating a top coat layer with a clear coating. 【請求項３】基材に、プライマー層を塗装し、請求項１
記載の塗料組成物を用いてベースコート層を塗装したの
ち、クリヤー塗料を用いてトップコート層を塗装するこ
とを特徴とする塗膜形成方法。3. A base material coated with a primer layer,
A method for forming a coating film, which comprises applying a base coat layer using the coating composition described above and then applying a top coat layer using a clear paint. 【請求項４】請求項２又は請求項３記載の塗膜形成方法
により塗装されてなることを特徴とする塗装物。4. A coated article, which is coated by the coating film forming method according to claim 2 or 3.