JP2003292641A - Film made of biodegradable resin - Google Patents
Film made of biodegradable resinInfo
- Publication number
- JP2003292641A JP2003292641A JP2002098824A JP2002098824A JP2003292641A JP 2003292641 A JP2003292641 A JP 2003292641A JP 2002098824 A JP2002098824 A JP 2002098824A JP 2002098824 A JP2002098824 A JP 2002098824A JP 2003292641 A JP2003292641 A JP 2003292641A
- Authority
- JP
- Japan
- Prior art keywords
- biodegradable resin
- film
- biodegradable
- resin
- acid amide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、 カレンダー成
形、押出成形、インフレーション成形等により成形され
た、土壌中等の自然環境中で分解される生分解性樹脂製
フィルムに関するもので、主として木材の虫燻蒸用シー
ト、農業マルチフィルムに使用されるものである。TECHNICAL FIELD The present invention relates to a biodegradable resin film formed by calendering, extrusion, inflation, etc., which is decomposed in the natural environment such as soil. It is used for sheet and agricultural mulch film.
【0002】[0002]
【従来の技術】一般的な合成樹脂を使用した各種プラス
チック製品の廃棄にあたっては、焼却処分による有害ガ
スの発生問題があり、また、投棄された場合に長時間に
わたって分解されないため、この廃棄物によって自然環
境が破壊されるという問題が年々深刻化してきている。
そこで近年においては、土壌中や海中に存在する微生物
の作用によって、短時間で容易に分解される種々の生分
解性樹脂が提案され、それらを用いた各種製品が開発さ
れ、実用化されつつある。2. Description of the Related Art When disposing of various plastic products using general synthetic resins, there is a problem that harmful gas is generated by incineration, and when discarded, they are not decomposed for a long time. The problem of destroying the natural environment is becoming more serious every year.
Therefore, in recent years, various biodegradable resins that are easily decomposed in a short time by the action of microorganisms existing in soil or sea have been proposed, and various products using them have been developed and put into practical use. .
【0003】農業用マルチングフィルムは、畑等の土の
表面を覆い、植物の生育を促進させたり、雑草の防除等
に使用される農業用フィルムである。このようなフィル
ムは、野菜等が生育したり、収穫されたりすると、取り
除かれ破棄される。しかし、この破棄されたフィルムを
回収するのにも多大な労力と時間を要するので作物等の
生産コストの上昇にもつながり問題がある。また、回収
されたフィルムを処理する方法としては、焼却処分が一
般的であったが、ダイオキシン等の環境問題となる。そ
のため、回収等の労力を要さず、使用したその場で、土
に鋤込むことができて、時間と共に分解される生分解性
樹脂製シートを使用する必要性が生じてきている。Agricultural mulching film is an agricultural film used for covering the surface of soil such as fields to promote the growth of plants and to control weeds. Such a film is removed and discarded when vegetables or the like grow or are harvested. However, it takes a lot of labor and time to collect the discarded film, which causes a problem of increasing the production cost of crops and the like. Further, as a method for treating the recovered film, incineration is generally used, but it causes environmental problems such as dioxins. Therefore, it is necessary to use a biodegradable resin sheet that can be plowed into the soil on the spot where it is used without requiring labor such as recovery and is decomposed with time.
【0004】また、各種大型製品等の輸出入の運搬に際
して、フォークリフトによる運搬では木材パレットが使
用されている。この木材パレット中に有害な害虫が潜ん
でいる場合が多く、そのまま木材パレットを諸外国へ搬
送すると、かかる害虫を諸外国へ移住させる結果とな
り、その国の自然環境の破壊につながる問題を抱えてい
る。特に、マツキボシゾウムシ、マツノキクイムシ、マ
ツノマダラカミキリ等の甲虫である松喰い虫は、松の生
育に対して多大な被害を与えるものであり、殊に日本お
よびアメリカから搬送される輸入製品用の木材パレット
にこのような松喰い虫が混在していることが多いと、世
界各国から問題提起されており、その木材の消毒が望ま
れている。In addition, when carrying out the import and export of various large products, a wood pallet is used in the transportation by a forklift. In many cases, harmful pests are lurking in this wood pallet, and if the wood pallet is directly transported to other countries, it will result in the migration of these pests to other countries, leading to the problem of destroying the natural environment of the country. There is. In particular, pine worms, which are beetles such as pine weevil, pine beetle, pine beetle, etc., cause a great deal of damage to the growth of pine trees, especially for imported products transported from Japan and the United States. Problems such as the mixture of such pine eaters in wood pallets are often raised by various countries around the world, and disinfection of the wood is desired.
【0005】かかる害虫の駆除は、多くの場合、切出し
た直後の木材を野外に積み上げ、樹脂シートを被せて密
閉包囲し、殺虫剤を燻蒸することにより行われている。
その害虫の燻蒸は、1ヶ月間以上とある程度長期間にわ
たるが、薬剤燻蒸が終了した時点で、燻蒸用シートは廃
棄処分される。薬剤燻蒸は多くの場合材木を伐採した山
林等で行われることより、焼却処分されているが、今日
の環境問題の要請を考慮すると、焼却処分は好ましいも
のではなく、したがって生分解性樹脂を用いた燻蒸用シ
ートが要望されつつある。In many cases, the extermination of such pests is carried out by stacking timber immediately after being cut out in the field, covering it with a resin sheet to hermetically surround it, and fumigating an insecticide.
Fumigation of the pests lasts for a certain period of time, such as one month or more, but the fumigation sheet is discarded when the chemical fumigation is completed. Chemical fumigation is often incinerated because it is carried out in forests where timber has been cut down, but in view of today's environmental problems, incineration is not preferable, so biodegradable resin is used. There is a growing demand for fumigation sheets.
【0006】そのような生分解性樹脂として今日使用さ
れているものは、例えば、ポリ乳酸、ポリカプロラクト
ン、ポリブチレンサクシネート、ポリヒドロキシバリレ
ートのような脂肪族ポリエステルおよびその誘導体であ
り、比較的低融点の樹脂である。したがって、これらの
生分解性樹脂を用いてシート、フィルム等に成形する場
合には、押出成形、射出成形、インフレーション成形、
ブロー成形等によってなされる。What are used today as such biodegradable resins are, for example, aliphatic polyesters and their derivatives such as polylactic acid, polycaprolactone, polybutylene succinate, polyhydroxyvalerate, etc. It is a low melting point resin. Therefore, when using these biodegradable resins to form sheets, films, etc., extrusion molding, injection molding, inflation molding,
It is made by blow molding or the like.
【0007】しかしながら、従来において、上記の生分
解性樹脂より成形されたフィルムは、展張時や使用中に
裂けやすく、木材の虫燻蒸用シート、農業マルチフィル
ムとして使用しにくいものであった。また、これらの樹
脂を使用したフィルムは、表面にベタツキがあり、ロー
ル状に巻いたり、シート状にして重ねたりした場合に、
フィルム同士が粘着してしまい、使用する場合に扱いに
くい物であった。However, conventionally, a film formed from the above-mentioned biodegradable resin is easy to tear during spreading and during use, and it is difficult to use it as a sheet for wood fumigation or an agricultural mulch film. In addition, the film using these resins has stickiness on the surface, and when wound in a roll shape or stacked in a sheet shape,
The films adhered to each other and were difficult to handle when used.
【0008】[0008]
【発明が解決使用する課題】本発明は、上記の問題を生
分解性を確保し、木材の虫燻蒸用シート、農業マルチフ
ィルムとして使用する場合に、展張時や使用時に裂けた
りせず、さらに、耐熱性を有するためにフィルム成形時
の成形性にすぐれ、巻き取り性、一定寸法のシートとし
たときの重ね置き時問題のない生分解性樹脂製フィルム
を提供することを課題とする。DISCLOSURE OF THE INVENTION The present invention solves the above problems by ensuring biodegradability, and when used as a sheet for fumigation of wood or an agricultural mulch film, does not tear during spreading or use, and further It is an object of the present invention to provide a biodegradable resin film which has heat resistance and is excellent in moldability during film molding, and has no wind-up property and does not pose a problem when stacked into a sheet having a certain size.
【0009】[0009]
【課題を解決するための手段】すなわち請求項1の発明
に係わる生分解性樹脂製フィルムは、生分解性樹脂に無
機充填材が0.1〜10重量部、脂肪酸アミドが0.0
1〜1重量部添加されて、引張破壊伸びが400〜12
00%、エレメンドルフ引裂強度が200N/cm以上
で、生分解性樹脂製フィルム同士の動摩擦係数が0.1
〜0.7であることを特徴とするものである。That is, in the biodegradable resin film according to the invention of claim 1, the biodegradable resin contains 0.1 to 10 parts by weight of an inorganic filler and 0.0 to 10 parts by weight of fatty acid amide.
Addition of 1 to 1 part by weight, tensile breaking elongation is 400 to 12
00%, Elemendorff tear strength is 200 N / cm or more, and the coefficient of dynamic friction between biodegradable resin films is 0.1.
It is characterized by being ~ 0.7.
【0010】請求項2の発明は、上記請求項1の生分解
性樹脂製フィルムにおいて、生分解性樹脂の主成分が、
少なくとも1,4−ブタンジオールとテレフタール酸と
の共重合体樹脂であることを特徴とするものである。According to a second aspect of the present invention, in the biodegradable resin film according to the first aspect, the main component of the biodegradable resin is
It is a copolymer resin of at least 1,4-butanediol and terephthalic acid.
【0011】請求項3の発明は、上記請求項2の生分解
性樹脂製フィルムにおいて、生分解性樹脂において、主
成分とする、少なくとも1,4−ブタンジオールとテレ
フタール酸との共重合体樹脂のほかに、他の生分解性樹
脂が添加されていることを特徴とするものである。According to a third aspect of the present invention, in the biodegradable resin film according to the second aspect, a copolymer resin of at least 1,4-butanediol and terephthalic acid, which is a main component of the biodegradable resin, is used. In addition to the above, another biodegradable resin is added.
【0012】[0012]
【発明の実施の形態】本発明の生分解性樹脂製フィルム
は、JIS K 7121の測定に準ずる引張破壊伸び
が400〜1200%であるために、成形後のロールへ
の巻き取り時や、使用の際の展張時に作業性の良いフィ
ルムとして使用できる。引張破壊伸びが400%未満で
あると、展張の際に引っ張り過重により、切れやすくな
ってしまい使用しずらいものとなってしまう。一方、引
張破壊伸びが1200%を超えると、伸びすぎてしまい
展張作業性の低下や、農業用マルチフィルムとして使用
する場合に、土に鋤込むときの機械に絡みついてしまう
可能性がある。BEST MODE FOR CARRYING OUT THE INVENTION The biodegradable resin film of the present invention has a tensile breaking elongation of 400 to 1200% according to the measurement of JIS K 7121. It can be used as a film with good workability during stretching. If the tensile elongation at break is less than 400%, it tends to be broken due to excessive pulling force at the time of spreading, which makes it difficult to use. On the other hand, if the tensile elongation at break exceeds 1200%, there is a possibility that it will be excessively elongated and the workability for spreading will be reduced, and that when it is used as an agricultural mulch film, it may become entangled with the machine when it is plowed into the soil.
【0013】また、JIS K 7128−2の測定に
準ずるエレメンドルフ引裂強度が200N/cm以上で
あるために、フィルムの成形時や展張時にフィルムにで
きてしまった穴や、農業用マルチフィルムとしてあけら
れた穴などがある場合でも、引っ張り加重によって、そ
の部分からフィルムが裂けにくくなっている。[0013] Further, since the Elementmendorf tear strength according to the measurement of JIS K 7128-2 is 200 N / cm or more, holes formed in the film at the time of molding or spreading of the film, or punched as an agricultural mulch film. Even if there are holes in the film, the film is less likely to tear from that part due to the tensile load.
【0014】さらに、JIS K 7125の測定に準
ずる生分解性樹脂製フィルム同士の動摩擦係数が0.1
〜0.7であるために、ロールに巻いたり、一定長さの
シートとして複数枚を重ねた場合にも支障のない生分解
性樹脂製フィルムとなっている。動摩擦係数が0.1未
満であると、ロールに巻いた状態でフィルムが横滑りし
たしまって、巻きが崩れてしまったり、一定長さにカッ
トしたシートを折り畳んで山積みするのができなくって
しまう。一方、動摩擦係数が0.7を超えるとフィルム
同士が粘着した状態になってしまい、ロール巻きのフィ
ルムを解反しにくくなり、貼着により作業性が低下した
り、被覆物に巻き付いて、破れ等が発生しやすくなって
しまう。Furthermore, the coefficient of kinetic friction between the biodegradable resin films according to the measurement of JIS K 7125 is 0.1.
Since it is ˜0.7, it is a biodegradable resin film that does not cause any trouble when wound on a roll or when a plurality of sheets having a certain length are stacked. If the coefficient of kinetic friction is less than 0.1, the film will slip sideways in a state of being wound on a roll, the winding will be broken, or it will be impossible to fold and cut sheets cut into a certain length. On the other hand, if the coefficient of dynamic friction exceeds 0.7, the films will stick to each other, making it difficult to unwind the roll-wound film, and the workability will decrease due to sticking, or the film will wind around the coating and break. Is likely to occur.
【0015】本発明の生分解性フィルムには、生分解性
樹脂自体がスリップ性や耐熱性が通常の塩化ビニルフィ
ルム等と比較する劣るために、スリップ性や耐熱性を向
上させるために、無機充填材が0.1〜10重量部、脂
肪酸アミドが0.01〜1重量部添加されている。無機
充填材の添加量が、0.1重量部未満であると、動摩擦
係数が大きくなってしまいスリップ性に問題があり、さ
らに、耐熱性が悪く、成形性が低下してしまう、一方1
0重量部を超えるとフィルムの引張強度の低下となって
しまう。脂肪酸アミドの添加量が0.01未満である
と、スリップ性、耐熱性の面で問題があり好ましくな
く、1重量部を超えると、成形時に樹脂が滑りやすくな
り、フィルム成形しにくいものとなってしまう。In the biodegradable film of the present invention, since the biodegradable resin itself is inferior in slip property and heat resistance to ordinary vinyl chloride film and the like, an inorganic material is used in order to improve slip property and heat resistance. 0.1 to 10 parts by weight of filler and 0.01 to 1 part by weight of fatty acid amide are added. If the amount of the inorganic filler added is less than 0.1 parts by weight, the dynamic friction coefficient becomes large, which causes a problem of slip property, and further, the heat resistance is poor and the moldability is deteriorated.
If it exceeds 0 parts by weight, the tensile strength of the film will decrease. If the amount of the fatty acid amide added is less than 0.01, there is a problem in terms of slip properties and heat resistance, and if it exceeds 1 part by weight, the resin becomes slippery during molding, making it difficult to form a film. Will end up.
【0016】無機充填材としては、タルク、マイカ、シ
リカ、ハイドロタルサイト、長石、酸化チタン、酸化亜
鉛、炭酸カルシウム、水酸化マグネシウム、水酸化アル
ミニウム等を単独または、複合して使用することができ
る。As the inorganic filler, talc, mica, silica, hydrotalcite, feldspar, titanium oxide, zinc oxide, calcium carbonate, magnesium hydroxide, aluminum hydroxide or the like can be used alone or in combination. .
【0017】脂肪酸アミドとしては、エルカ酸アミド、
パルミチン酸アミド、オレイン酸アミド、ステアリン酸
アミド、メチレンビスステアリン酸アミド、エチレンビ
スステアリン酸アミド、エチレンビスオレイン酸アミ
ド、エチレンビスエルカ酸アミド等を単独または複合し
て使用することができる。As the fatty acid amide, erucic acid amide,
Palmitic acid amide, oleic acid amide, stearic acid amide, methylenebisstearic acid amide, ethylenebisstearic acid amide, ethylenebisoleic acid amide, ethylenebiserucic acid amide and the like can be used alone or in combination.
【0018】本願に使用する生分解性樹脂としては、少
なくとも1,4−ブタンジオールとテレフタール酸との
共重合体樹脂からなる生分解性樹脂樹脂を使用すること
が好ましい。例えば、1,4−ブタンジオールとテレフ
タール酸とアジピン酸の共重合体樹脂であるポリブチレ
ンアジペートテレフタレート、1,4−ブタンジオール
とテレフタール酸とコハク酸の共重合体樹脂であるポリ
ブチレンサクシネートテレフタレート等が好ましく使用
できる。As the biodegradable resin used in the present application, it is preferable to use a biodegradable resin resin composed of at least a copolymer resin of 1,4-butanediol and terephthalic acid. For example, polybutylene adipate terephthalate which is a copolymer resin of 1,4-butanediol, terephthalic acid and adipic acid, and polybutylene succinate terephthalate which is a copolymer resin of 1,4-butanediol, terephthalic acid and succinic acid. Etc. can be preferably used.
【0019】また、生分解性速度の改質を目的として、
少なくとも1,4−ブタンジオールとテレフタール酸と
の共重合体樹脂からなる生分解性樹脂樹脂に、他の生分
解性樹脂を、所望により添加してもよい。その配合割合
としては、生分解性樹脂100重量部とすると50重量
部未満であることが好ましい。他の生分解性樹脂の添加
量が50重量部を超えると、本発明の引張破壊伸び値、
エルメンドルフ引裂強さ、動摩擦係数を満足したならな
い。他の生分解性樹脂としては、少なくとも1,4−ブ
タンジオールとテレフタール酸との共重合体樹脂からな
る生分解性樹脂樹脂より、生分解性の面で優れているも
のが好ましい。例えば、ポリブチレンサクシネート、ポ
リブチレンサクシネートアジペート、ポリ乳酸、ポリブ
チレンサクシネートカーボネート、ポリカプロラクトン
等を単独又は複数を組み合わせて使用することができ
る。Further, for the purpose of modifying the biodegradability,
If desired, other biodegradable resin may be added to the biodegradable resin made of a copolymer resin of at least 1,4-butanediol and terephthalic acid. The blending ratio is preferably less than 50 parts by weight when 100 parts by weight of the biodegradable resin is used. When the addition amount of other biodegradable resin exceeds 50 parts by weight, the tensile breaking elongation value of the present invention,
Elmendorf tear strength and dynamic friction coefficient must not be satisfied. As the other biodegradable resin, those which are more excellent in biodegradability than the biodegradable resin made of at least a copolymer resin of 1,4-butanediol and terephthalic acid are preferable. For example, polybutylene succinate, polybutylene succinate adipate, polylactic acid, polybutylene succinate carbonate, polycaprolactone and the like can be used alone or in combination.
【0020】さらに、耐候性を向上させるために、本発
明に使用される生分解性樹脂に、紫外線吸収剤を添加し
てもよい。例えば、サリチル酸エステル、ベンゾトリア
ゾール、ヒドロキシベンゾフェノン、アクリロニトリル
置換体等が挙げられる。これらの紫外線吸収剤は、単独
又は2種以上を混合して使用することができる。具体的
には、2,4−ジヒドロキシベンゾフェノン、2−ヒド
ロキシ−4−メトキシベンゾフェノン、2−ヒドロキシ
−4−エトキシベンゾフェノン、2−ヒドロキシ−4−
オクトキシベンゾフェノン、5,5’−メチレンビス
(2−ヒドロキシ−4−メトキシベンゾフェノン)等の
2−ヒドロキシベンゾフェノン類;2−(2’−ヒドロ
キシ−5’−メチルフェニル)ベンゾトリアゾール、2
−(2’−ヒドロキシ−3’,5’−ジ−tert−ブ
チルフェニル)−5−クロロベンゾトリアゾール、2−
(2’−ヒドロキシ−3’−tert−ブチル−5’−
メチルフェニル)−5−クロロベンゾトリアゾール、2
−(2’−ヒドロキシ−5’−tert−オクチルフェ
ニル)ベンゾトリアゾール、2−(2’−ヒドロキシ−
3’,5’−ジクミルフェニル)ベンゾトリアゾール、
2,2’−メチレンビス(4−tert−オクチル−6
−ベンゾトリアゾール)フェノール等の2−(2’−ヒ
ドロキシフェニル)ベンゾトリアゾール類;フェニルサ
リチレート、レゾルシノールモノベンゾエート、2,4
−ジ−tert−ブチルフェニル−3’,5’−ジ−t
ert−ブチル−4’−ヒドロキシベンゾエート、ヘキ
サデシル−3,5−ジ−tert−ブチル−4−ヒドロ
キシベンゾエート等のベンゾエート類;2−エトキシ−
4’−ドデシルオキザニリド等のオキザニリド類;エチ
ル−α−シアノ−β、β−ジフェニルアクリレート、メ
チル−2−シアノ−3−メチル−3−(p−メトキシフ
ェニル)アクリレート等のシアノアクリレート類が挙げ
られる。 これらの紫外線吸収剤は、単独で使用しても
よいし、2種以上を組み合わせて使用しても良い。添加
量としては、0.05〜5重量部程度でよい。Further, in order to improve weather resistance, an ultraviolet absorber may be added to the biodegradable resin used in the present invention. Examples thereof include salicylic acid ester, benzotriazole, hydroxybenzophenone, and acrylonitrile-substituted products. These ultraviolet absorbers can be used alone or in admixture of two or more. Specifically, 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-ethoxybenzophenone, 2-hydroxy-4-
2-Hydroxybenzophenones such as octoxybenzophenone and 5,5′-methylenebis (2-hydroxy-4-methoxybenzophenone); 2- (2′-hydroxy-5′-methylphenyl) benzotriazole, 2
-(2'-hydroxy-3 ', 5'-di-tert-butylphenyl) -5-chlorobenzotriazole, 2-
(2'-hydroxy-3'-tert-butyl-5'-
Methylphenyl) -5-chlorobenzotriazole, 2
-(2'-hydroxy-5'-tert-octylphenyl) benzotriazole, 2- (2'-hydroxy-
3 ', 5'-dicumylphenyl) benzotriazole,
2,2'-methylenebis (4-tert-octyl-6)
2- (2′-hydroxyphenyl) benzotriazoles such as -benzotriazole) phenol; phenylsalicylate, resorcinol monobenzoate, 2,4
-Di-tert-butylphenyl-3 ', 5'-di-t
Benzoates such as ert-butyl-4′-hydroxybenzoate and hexadecyl-3,5-di-tert-butyl-4-hydroxybenzoate; 2-ethoxy-
Oxanilides such as 4′-dodecyloxanilide; cyanoacrylates such as ethyl-α-cyano-β, β-diphenyl acrylate and methyl-2-cyano-3-methyl-3- (p-methoxyphenyl) acrylate Can be mentioned. These ultraviolet absorbers may be used alone or in combination of two or more. The amount added may be about 0.05 to 5 parts by weight.
【0021】またさらに、必要に応じて、可塑剤、顔
料、酸化防止剤、滑剤、帯電防止剤、有機充填材、防曇
剤、光安定剤等の添加剤を添加してもよい。Further, if necessary, additives such as a plasticizer, a pigment, an antioxidant, a lubricant, an antistatic agent, an organic filler, an antifogging agent and a light stabilizer may be added.
【0022】本発明の生分解樹脂製フィルの成形方法と
しては、通常のフィルム成形で使用されている、カレン
ダー法、押出法、インフレーション法等を適用すること
ができる。本発明の生分解性樹脂製フィルムの厚さとし
ては、0.01〜0.5mm程度が好ましい。0.01
mm未満であると、充分な強度が得られず、0.5mm
を超えると生分解性の面で遅くなり、重量も重くなり好
ましくない。As the method for molding the biodegradable resin fill of the present invention, a calendering method, an extrusion method, an inflation method or the like which is used in ordinary film molding can be applied. The thickness of the biodegradable resin film of the present invention is preferably about 0.01 to 0.5 mm. 0.01
If it is less than mm, sufficient strength cannot be obtained and 0.5 mm
When it exceeds, the biodegradability becomes slow and the weight becomes heavy, which is not preferable.
【0023】以上のように本発明の生分解樹脂製フィル
ムは、引裂き強度に優れ、展張時等において、フィルム
を引っ張っても、破れ等の発生する可能性が低く、作業
性に優れたフィルムである。また、耐熱性、スリップ性
に優れるために、フィルム同士がロールに巻いた状態や
積層時において付着するおそれが低いために、解反作業
性や、積層時に崩れにくいものとなっている。必要に応
じて、紫外線吸収剤を添加することで、生分解性を有し
ながらも、地中以外の使用においては、長期の使用を可
能としたなる。As described above, the biodegradable resin film of the present invention is excellent in tear strength, has a low possibility of tearing even when the film is pulled at the time of stretching, and has excellent workability. is there. Further, since the films are excellent in heat resistance and slip property, there is little possibility that the films will be attached to each other in a state of being wound on a roll or during lamination, and therefore, it is difficult to be disentangled and workable and is not easily collapsed during lamination. By adding an ultraviolet absorber as needed, it is possible to use it for a long period of time when it is used in a place other than underground even though it has biodegradability.
【0024】[0024]
【実施例】以下に、本発明の具体的実施例を説明する
が、本発明の範囲はこれらの実施例に限定されるもので
はない。EXAMPLES Hereinafter, specific examples of the present invention will be described, but the scope of the present invention is not limited to these examples.
【0025】[0025]
【表1】 [Table 1]
【0026】[0026]
【表2】 [Table 2]
【0027】表1及び表における用語及び物性の測定方
法以下の内容となっている。
PBS:ポリブチレンサクシネート(ビオーレ#100
1:昭和高分子社製)
PBSA:ポリブチレンサクシネートアジペート(ビオ
ネーレ#3001:昭和高分子社製)
PLA:ポリ乳酸(レイシア:三井化学社製)
PEC:ポリブチレンサクシネートカーボネート(ユー
ペック:三菱ガス化学社製)
PCL:ポリカプロラクトン(セルグリーンPH7:ダ
イセル化学社製)
PBAT:ポリブチレンアジペートテレフタレート(エ
コフレックス:BASF社製)
引張破壊伸び(%):JIS K 7127に準ずる測
定方法
エレメンドルフ引裂強度(N/cm):JIS K 7
128−2に準ずる測定方法
動摩擦係数:JIS K 7125に準ずる測定で、同
種のフィルム間で測定。Table 1 and terms used in Table 1 and methods for measuring physical properties are as follows. PBS: Polybutylene succinate (Biore # 100
1: Showa High Polymer Co., Ltd.) PBSA: Polybutylene succinate adipate (Bionere # 3001: Showa High Polymer Co., Ltd.) PLA: Polylactic acid (Lacea: Mitsui Chemicals, Inc.) PEC: Polybutylene succinate carbonate (UPEC: Mitsubishi Gas) Chemical Co., Ltd. PCL: Polycaprolactone (Cellgreen PH7: Daicel Chemical Co., Ltd.) PBAT: Polybutylene adipate terephthalate (Ecoflex: BASF Co., Ltd.) Tensile Fracture Elongation (%): Measurement Method According to JIS K 7127 Elemendorff Tear Strength (N / cm): JIS K 7
Measurement method according to 128-2 Dynamic friction coefficient: Measurement according to JIS K 7125, between films of the same type.
【0028】表1及び表2に示す配合にて、生分解性樹
脂組成物を作成し、その樹脂組成物をもちいて、インフ
レーション成型機にて0.1mm厚のフィルムを作成し
た。その得られたフィルムについて、引張破壊伸び、エ
レメンドルフ引裂強さ、動摩擦係数について測定し、表
1に示す測定結果を得た。これにより、無機充填材や脂
肪酸アミドを加えないと、動摩擦係数が本発明のものよ
り劣り、添加量が多いと、物性やスベリ性で問題とな
る。A biodegradable resin composition was prepared according to the formulations shown in Tables 1 and 2, and a film having a thickness of 0.1 mm was prepared by an inflation molding machine using the resin composition. The resulting film was measured for tensile breaking elongation, Elemendorf tear strength and dynamic friction coefficient, and the measurement results shown in Table 1 were obtained. As a result, unless an inorganic filler or fatty acid amide is added, the dynamic friction coefficient is inferior to that of the present invention, and if the addition amount is large, problems with physical properties and slipperiness occur.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) // C08L 101/16 C08L 101/16 Fターム(参考) 4F071 AA45 AB01 AC12 AF15Y AF16Y AF22Y AH01 BB04 BB06 BB09 BC01 4J002 CF051 CF071 DE076 DE106 DE136 DE146 DE236 DE286 DJ016 DJ046 DJ056 EP017 EP027 FD050 GA01 4J200 AA06 AA19 BA09 BA19 CA01 DA01 EA04 EA05 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) // C08L 101/16 C08L 101/16 F term (reference) 4F071 AA45 AB01 AC12 AF15Y AF16Y AF22Y AH01 BB04 BB06 BB09 BC01 4J002 CF051 CF071 DE076 DE106 DE136 DE146 DE236 DE286 DJ016 DJ046 DJ056 EP017 EP027 FD050 GA01 4J200 AA06 AA19 BA09 BA19 CA01 DA01 EA04 EA05
Claims (3)
0重量部、脂肪酸アミド脂が0.01〜1重量部添加さ
れて、引張破壊伸びが400〜1200%、エレメンド
ルフ引裂強度が200N/cm以上で、生分解性樹脂製
フィルム同士の動摩擦係数が0.1〜0.7であること
を特徴とする生分解性樹脂製フィルム。1. A biodegradable resin containing 0.1 to 1 inorganic filler.
0 parts by weight, 0.01 to 1 parts by weight of fatty acid amide fat are added, the tensile elongation at break is 400 to 1200%, the Elemendorf tear strength is 200 N / cm or more, and the dynamic friction coefficient between biodegradable resin films is A biodegradable resin film, characterized in that it is 0.1 to 0.7.
1,4−ブタンジオールとテレフタール酸との共重合体
樹脂であることを特徴とする請求項1記載の生分解性樹
脂製フィルム。2. The biodegradable resin film according to claim 1, wherein the main component of the biodegradable resin is a copolymer resin of at least 1,4-butanediol and terephthalic acid.
少なくとも1,4−ブタンジオールとテレフタール酸と
の共重合体樹脂のほかに、他の生分解性樹脂が添加され
ていることを特徴とする請求項2記載の生分解性樹脂フ
ィルム。3. A biodegradable resin, which comprises as a main component,
The biodegradable resin film according to claim 2, wherein other biodegradable resin is added in addition to at least the copolymer resin of 1,4-butanediol and terephthalic acid.