JP2003278091A - Bulky paper - Google Patents
Bulky paperInfo
- Publication number
- JP2003278091A JP2003278091A JP2002082428A JP2002082428A JP2003278091A JP 2003278091 A JP2003278091 A JP 2003278091A JP 2002082428 A JP2002082428 A JP 2002082428A JP 2002082428 A JP2002082428 A JP 2002082428A JP 2003278091 A JP2003278091 A JP 2003278091A
- Authority
- JP
- Japan
- Prior art keywords
- lyocell
- paper
- bulky
- pulp
- beaten
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、嵩高紙に関するも
のであり、さらに詳しくは、特に嵩があり、平滑性に優
れ、繊維の特性を利用して紙力を補うことが可能な、印
刷用紙、情報用紙、塗工紙用原紙などに使用できる嵩高
紙に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a high-bulk paper, and more particularly, to a printing paper which is particularly bulky, has excellent smoothness, and is capable of supplementing paper strength by utilizing the characteristics of fibers. , Bulk paper that can be used as information paper, base paper for coated paper, and the like.
【０００２】[0002]
【従来の技術】近年、紙は省資源、物流の面から軽量化
の傾向にある。また、環境保全・循環型社会構築への取
り組みから脱墨パルプの利用が積極的に行われている。
しかし、脱墨パルプの比率を高めると紙は薄くなり、白
色度、不透明度が低下することから、裏抜けが悪くなる
という問題が生じる。これらのことから、紙を嵩高にす
ることは避けて通れない問題である。2. Description of the Related Art In recent years, paper tends to be lighter in terms of resource saving and physical distribution. In addition, the use of deinked pulp is being actively promoted as part of efforts to protect the environment and build a recycling-based society.
However, if the proportion of deinked pulp is increased, the paper becomes thinner and the whiteness and opacity decrease, which causes a problem of poor strike-through. For these reasons, making paper bulky is an unavoidable problem.
【０００３】紙の主原料には製紙用パルプが用いられて
いる。一般的に製紙用パルプには木材パルプが使用され
ている。その中でも、化学処理によって非セルロース成
分を多量に除去した化学パルプが用いられることが多
い。化学パルプの場合、繊維が剛直なために、未叩解で
抄紙を行うと繊維間接触面積が小さくなり、嵩高な紙が
形成される。そのため、一般的に嵩高効果を得るには軽
叩解パルプが使用される。しかし、嵩の増加に伴い、表
面の平滑性の低下、強度の低下といった問題が生じる。Papermaking pulp is used as a main raw material of paper. Wood pulp is generally used as the pulp for papermaking. Among them, chemical pulp in which a large amount of non-cellulose components are removed by chemical treatment is often used. In the case of chemical pulp, since the fibers are rigid, when papermaking is performed without beating, the contact area between fibers becomes small and bulky paper is formed. Therefore, lightly beaten pulp is generally used to obtain a bulky effect. However, as the bulk increases, problems such as a decrease in surface smoothness and a decrease in strength occur.
【０００４】また、機械的な処理だけを行って製造され
る機械パルプは、化学パルプより繊維が剛直なため、嵩
高効果を得るには有利である。しかし、機械パルプは紙
の黄色化の原因となるリグニンを多く含んでおり、紙の
退色は避けられない。そのため、上質紙や保存性が要求
される用途には用いることができない。Further, mechanical pulp produced only by mechanical treatment is more advantageous in obtaining a bulky effect because fibers are more rigid than chemical pulp. However, mechanical pulp contains a large amount of lignin, which causes yellowing of paper, and discoloration of paper is unavoidable. Therefore, it cannot be used for high-quality paper or applications requiring storability.
【０００５】非木材パルプも剛直なパルプ原料の一つで
ある。そのため、非木材パルプを配合することも嵩高効
果を得る手段の一つである。しかし、非木材パルプは得
られる時期や原産地が限られているため、安定供給する
のが難しく、大量生産を行うことは難しい。Non-wood pulp is also one of the rigid pulp raw materials. Therefore, blending non-wood pulp is one of the means for obtaining the bulky effect. However, it is difficult to stably supply non-wood pulp, and it is difficult to mass-produce it because the time and place of origin of non-wood pulp are limited.
【０００６】機械的な面における嵩高効果は、抄造時に
おけるプレス線圧の軽減や、カレンダー処理をソフトに
するなどの手段によって得ることができる。しかしなが
ら、機械的な処理だけでは限界があり、満足のいく嵩高
効果が得られていないのが現状である。The bulkiness in the mechanical aspect can be obtained by means such as reduction of the pressing linear pressure during papermaking or softening of the calendering process. However, there is a limit to the mechanical treatment alone, and a satisfactory bulking effect is not obtained at present.
【０００７】さらに近年では、嵩高剤の添加によって紙
の嵩を出す手段も行われている。嵩高剤には、親水基と
疎水基を持つ化合物である界面活性剤がよく用いられ
る。しかし、嵩高剤のみによる嵩高効果は小さく、満足
のいく水準には達していない。また、嵩高剤は繊維間の
水素結合を阻害することで嵩高効果を生み出すため、紙
力の低下が著しく、それを補うために紙力剤などを用い
る必要がある。Further, in recent years, a means for increasing the bulk of paper by adding a bulking agent has been used. A surfactant, which is a compound having a hydrophilic group and a hydrophobic group, is often used as the bulking agent. However, the bulking effect of the bulking agent alone is small and has not reached a satisfactory level. Further, since the bulking agent produces a bulking effect by inhibiting hydrogen bonding between fibers, the paper strength is remarkably reduced, and it is necessary to use a paper strength agent or the like to compensate for it.
【０００８】[0008]
【発明が解決しようとする課題】本発明の課題は、嵩が
高く、平滑性に優れ、繊維の特性を利用して紙力を補う
ことが可能な、印刷用紙、情報用紙、塗工紙用原紙など
に使用できる嵩高紙を提供することである。The object of the present invention is for printing papers, information papers, coated papers, which are bulky, excellent in smoothness, and capable of supplementing paper strength by utilizing the characteristics of fibers. It is to provide a bulky paper that can be used as a base paper.
【０００９】[0009]
【課題を解決するための手段】本発明者は、未叩解のリ
ヨセルまたは叩解したリヨセルを含有する紙料を抄紙す
ることによって、上記目的の嵩高紙が得られることを見
出し、完成に至ったものである。Means for Solving the Problems The present inventor has found that a bulky paper for the above-mentioned purpose can be obtained by making a paper stock containing unbeaten lyocell or beaten lyocell, and completed the invention. Is.
【００１０】すなわち、本発明の嵩高紙は、繊維長２ｍ
ｍ以下、繊維径２．４ｄｔｅｘ以下のリヨセルを含有し
てなることを特徴とするものである。That is, the bulky paper of the present invention has a fiber length of 2 m.
It is characterized by containing Lyocell having a fiber diameter of 2.4 m or less and a fiber diameter of 2.4 dtex or less.
【００１１】本発明において、リヨセルが、未叩解のリ
ヨセルであり、かつ全パルプに対して１０〜１５質量％
含有してなることを特徴とするものである。In the present invention, lyocell is an unbeaten lyocell and is 10 to 15% by mass based on the total pulp.
It is characterized by containing.
【００１２】また、本発明において、リヨセルが、カナ
ダ標準濾水度４５０ｍｌ以下に叩解されたリヨセルであ
り、かつリヨセルが全パルプに対して１６〜３５質量％
含有してなることを特徴とするものである。In the present invention, the lyocell is lyocell beaten to a Canadian standard freeness of 450 ml or less, and the lyocell is 16 to 35 mass% with respect to the total pulp.
It is characterized by containing.
【００１３】[0013]
【発明の実施の形態】以下、本発明の嵩高紙について、
詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION The bulky paper of the present invention will be described below.
The details will be described.
【００１４】本発明において、用いられる「リヨセル」
とは、ＩＳＯ規格および日本のＪＩＳ規格に定められて
いる繊維用語で、セルロース誘導体を経ずに直接有機溶
剤に溶解させて紡糸することによって得られる再生セル
ロース系繊維である。有機溶剤としては、アミンオキサ
イド系のものが使用されている。リヨセルはパルプと同
じセルロースであり、退色もしないため紙中に配合して
も問題はない。また、リヨセルは、レーヨン、キュプラ
などの他の再生セルロース系繊維とは異なり、叩解可能
という特徴を持つ。この理由は製造方法にある。レーヨ
ンがセルロース誘導体を経由して製造されるのに対し、
リヨセルはセルロースのままで有機溶媒に溶解させて繊
維状に再生されるため、セルロース分子の重合度低下が
少ないまま分子が再配向される。そのため、紡糸時に繊
維軸方向に分子がきれいに並ぶことにより叩解が可能と
なる。ここで、叩解とは、水とともに機械的に処理する
ことによって繊維の切断やフィブリル化が起き、シート
にした場合に良好な特性を発現することを意味する。"Lyocell" used in the present invention
Is a fiber term defined in ISO standard and Japanese JIS standard, and is a regenerated cellulose fiber obtained by directly dissolving in an organic solvent and spinning without passing through a cellulose derivative. As the organic solvent, an amine oxide type is used. Lyocell is the same cellulose as pulp and does not fade, so there is no problem in mixing it in paper. Also, unlike other regenerated cellulosic fibers such as rayon and cupra, lyocell has the characteristic that it can be beaten. The reason for this lies in the manufacturing method. While rayon is produced via a cellulose derivative,
Lyocell is regenerated into fibrous form by dissolving it in an organic solvent as it is as cellulose, so that the molecules are reoriented while the decrease in the degree of polymerization of cellulose molecules is small. Therefore, beating can be achieved by neatly aligning the molecules in the fiber axis direction during spinning. Here, beating means that fibers are cut or fibrillated by mechanical treatment with water, and good properties are expressed when a sheet is formed.
【００１５】他の再生セルロース系繊維であるレーヨン
を用いても嵩高効果は得られる。しかし、その効果はリ
ヨセルと比較すると小さい。さらに、配合することで紙
力が低下した場合、レーヨンは叩解できないため繊維の
特性を利用して紙力を補うことはできない。それに対
し、リヨセルを用いた場合、条件に応じて適度に叩解す
ることができ、紙力の問題が改善され、かつ嵩高な紙を
抄造することが可能となる。The use of rayon, which is another regenerated cellulosic fiber, can provide the bulky effect. However, its effect is smaller than that of Lyocell. Further, when the paper strength is lowered by the blending, rayon cannot be beaten, so that the paper strength cannot be supplemented by utilizing the characteristics of the fiber. On the other hand, when Lyocell is used, it can be beaten appropriately according to the conditions, the problem of paper strength is improved, and bulky paper can be produced.
【００１６】本発明において、リヨセルの繊維長は、２
ｍｍ以下とすることが重要である。なぜなら、２ｍｍよ
りも長い繊維が多くなると地合が著しく悪くなるためで
ある。また、２ｍｍよりも長い繊維はよれやすく、実機
においてスクリーンに詰まる可能性があり、これがワイ
ヤーパートに流れ出た場合、固まりとなることから製品
に悪影響をもたらすためである。In the present invention, the fiber length of lyocell is 2
It is important to be less than or equal to mm. The reason for this is that when the number of fibers longer than 2 mm increases, the formation becomes significantly worse. Fibers longer than 2 mm tend to twist and may be clogged in the screen in an actual machine, and if they flow out to the wire part, they will be solidified and adversely affect the product.
【００１７】本発明において、リヨセルの繊維径は、
２．４ｄｔｅｘ以下とすることが重要であり、より好ま
しい繊維径としては１．７ｄｔｅｘ以下である。これ
は、リヨセルの繊維径が太すぎると紙表面の平滑性が悪
くなり、印刷などに悪影響をもたらすからである。In the present invention, the fiber diameter of Lyocell is
It is important that the fiber diameter is 2.4 dtex or less, and a more preferable fiber diameter is 1.7 dtex or less. This is because if the fiber diameter of Lyocell is too large, the smoothness of the paper surface deteriorates, which adversely affects printing and the like.
【００１８】未叩解のリヨセル、例えば、カナダ標準濾
水度７００ｍｌ以上、をパルプ中に配合する場合、これ
までにない高い嵩高効果が得られる。その反面、配合量
を増やすと表面平滑性と紙力の低下が著しくなるという
欠点も存在する。そのため、未叩解のリヨセルを用いる
場合、嵩高効果、表面平滑性、紙力の関係を考慮し、適
度な配合量とする必要がある。配合量としては１０〜１
５質量％であることが好ましい。ここで、リヨセルの配
合量が１０質量％未満では嵩高の効果が小さいため好ま
しくなく、また配合量が１５質量％を超えて多い場合は
紙力の低下や表面平滑性の低下が顕著となるため好まし
くない。When lyocell which has not been beaten, for example, Canadian standard freeness of 700 ml or more is mixed in the pulp, a high bulking effect which has never been obtained can be obtained. On the other hand, there is also a drawback that the surface smoothness and the paper strength decrease remarkably when the compounding amount is increased. Therefore, when using unbeaten Lyocell, it is necessary to consider the relationship among the bulkiness effect, the surface smoothness, and the paper strength, and to select an appropriate amount. As the compounding amount, 10 to 1
It is preferably 5% by mass. Here, if the blending amount of Lyocell is less than 10% by mass, the effect of bulkiness is small, which is not preferable, and if the blending amount is more than 15% by mass, the paper strength and the surface smoothness are significantly reduced. Not preferable.
【００１９】また、本発明における嵩高紙として、カナ
ダ標準濾水度４５０ｍｌ以下に叩解したリヨセルを用い
る場合、未叩解のリヨセルよりもさらに多く配合するこ
とができる。これにより、未叩解のリヨセルを用いた場
合よりもさらに高い嵩高効果を得ることができ、且つ、
表面平滑性が高く、紙力の強い嵩高紙を作製できる。When lyocell beaten to a Canadian standard freeness of 450 ml or less is used as the bulky paper in the present invention, more lyocell than unbeaten lyocell can be added. As a result, it is possible to obtain an even higher bulking effect than in the case of using unbeaten lyocell, and
Bulky paper with high surface smoothness and strong paper strength can be produced.
【００２０】リヨセルを叩解して用いる場合、その配合
量は１６〜３５質量％であることが好ましい。ここで、
リヨセルの配合量が１６質量％未満では嵩高の効果が小
さいため好ましくなく、また、配合量が３５質量％を超
えて多い場合、表面平滑性の低下や紙力の低下が顕著と
なるため好ましくない。When Lyocell is beaten and used, the blending amount thereof is preferably 16 to 35% by mass. here,
When the amount of lyocell is less than 16% by mass, the bulkiness effect is small, which is not preferable. When the amount of lyocell is more than 35% by mass, the surface smoothness and paper strength are remarkably reduced, which is not preferable. .
【００２１】本発明の嵩高紙は、リヨセル以外の原料パ
ルプとして、化学パルプ、機械パルプ、非木材パルプ、
脱墨パルプなどを単独もしくは任意の割合で混合して使
用する。抄紙機は特に限定されず、長網抄紙機、ツイン
ワイヤー抄紙機、円網抄紙機、多層抄紙機、ヤンキー抄
紙機などを使用できる。抄紙時のｐＨは、酸性、中性、
アルカリ性のいずれでもよい。The bulky paper of the present invention is used as a raw material pulp other than lyocell as chemical pulp, mechanical pulp, non-wood pulp,
Deinked pulp or the like is used alone or mixed at an arbitrary ratio. The paper machine is not particularly limited, and a Fourdrinier paper machine, a twin wire paper machine, a cylinder paper machine, a multi-layer paper machine, a Yankee paper machine and the like can be used. PH during papermaking is acidic, neutral,
It may be alkaline.
【００２２】さらに、本発明の嵩高紙は必要に応じて、
硫酸バンド、サイズ剤、澱粉、歩留まり向上剤、着色
剤、染料、填料、紙力増強剤、消泡剤、低密度化剤など
を含有してもよい。また、各種のサイズプレスやコータ
ーなどの装置で紙の表面に澱粉、ラテックス、表面サイ
ズ剤、顔料、染料などを塗布することも可能である。Further, the high-bulk paper of the present invention, if necessary,
It may contain a sulfuric acid band, a sizing agent, a starch, a yield improving agent, a coloring agent, a dye, a filler, a paper strengthening agent, a defoaming agent, a low density agent and the like. It is also possible to apply starch, latex, surface sizing agents, pigments, dyes, etc. to the surface of the paper with various size presses and coaters.
【００２３】以上のように、繊維長が２ｍｍ以下、繊維
径が２．４ｄｔｅｘ以下のリヨセルを未叩解の場合に１
０〜１５質量％、カナダ標準濾水度４５０ｍｌ以下に叩
解した場合に１６〜３５質量％配合することにより、表
面平滑性が良く、紙力の強い嵩高紙が得られる。この嵩
高紙については印刷用紙、情報用紙、塗工紙用原紙など
に使用することができる。As described above, when the lyocell having a fiber length of 2 mm or less and a fiber diameter of 2.4 dtex or less is not beaten, 1
By adding 0 to 15 mass% and 16 to 35 mass% when beaten to a Canadian standard freeness of 450 ml or less, bulky paper having good surface smoothness and strong paper strength can be obtained. This bulky paper can be used as printing paper, information paper, base paper for coated paper, and the like.
【００２４】[0024]
【実施例】以下に実施例を挙げて本発明をより具体的に
説明するが、勿論これらに限定されるものではない。な
お、実施例において示す「部」および「％」は、特に明
示しない限り、質量部および質量％を示す。The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples. In addition, "parts" and "%" shown in the examples represent parts by mass and% by mass, unless otherwise specified.
【００２５】下記の実施例１〜８および比較例１〜１０
における方法によって作製した嵩高紙について、下記の
評価方法により測定し、評価を行った。結果は表１およ
び表２に示した。The following Examples 1-8 and Comparative Examples 1-10
The bulky paper produced by the method in 1. was measured and evaluated by the following evaluation method. The results are shown in Tables 1 and 2.
【００２６】評価方法：
〈密度〉ＪＩＳ Ｐ８１１８に準拠して測定した。密度
０．６５ｇ/ｃｍ3以下であれば本発明における嵩高紙で
ある。Evaluation method: <Density> The density was measured according to JIS P8118. If the density is 0.65 g / cm 3 or less, it is the bulky paper in the present invention.
【００２７】〈引張り強さ〉ＪＩＳ Ｐ８１１３に準拠
して測定した。引張り強さ３ｋＮ/ｍ以上であれば紙力
の強い嵩高紙である。<Tensile Strength> The tensile strength was measured according to JIS P8113. If the tensile strength is 3 kN / m or more, it is a bulky paper with strong paper strength.
【００２８】〈ベック平滑度〉ＪＩＳ Ｐ８１１９に準
拠して測定した。ベック平滑度３．５秒以上であること
が本発明における表面平滑性の高い嵩高紙である。<Beck's smoothness> Measured according to JIS P8119. A Beck's smoothness of 3.5 seconds or more is the bulky paper having high surface smoothness in the present invention.
【００２９】＜未叩解のリヨセルを使用＞
実施例１
カナダ標準濾水度３９０ｍｌの広葉樹晒クラフトパルプ
（以下、ＬＢＫＰと記す）を６０％、カナダ標準濾水度
４８０ｍｌの針葉樹晒クラフトパルプ（以下、ＮＢＫＰ
と記す）を３０％、繊維長２ｍｍ、繊維径１．７ｄｔｅ
ｘの未叩解のリヨセルを１０％配合し、これに炭酸カル
シウム６部、硫酸バンド０．７部、カチオン澱粉１部、
内添サイズ剤０．０３部、カチオン性ポリアクリルアミ
ド０．０３部、無機顔料０．０９部を添加した紙料を角
型手抄機で絶乾坪量５４ｇ/ｍ2となるように抄紙し、実
施例１の嵩高紙を作製した。脱水はロールプレス（線圧
２５ｋｇ/ｃｍ2）を用いて行い、乾燥はシリンダードラ
イヤーを用いて１０５℃で２分間行った。<Use of unbeaten Lyocell> Example 1 60% of hardwood bleached kraft pulp with Canadian standard freeness of 390 ml (hereinafter referred to as LBKP), 60% of softwood bleached kraft pulp with Canadian standard freeness of 480 ml (hereinafter, NBKP
30%, fiber length 2 mm, fiber diameter 1.7 dte
10% of unbeaten lyocell of x was mixed with 6 parts of calcium carbonate, 0.7 part of sulfuric acid band, 1 part of cationic starch,
Papermaking with 0.03 parts of internal sizing agent, 0.03 parts of cationic polyacrylamide, and 0.09 parts of inorganic pigment was paper-made with a square-type paper machine to have an absolute dry basis weight of 54 g / m 2. The bulky paper of Example 1 was produced. Dehydration was performed using a roll press (linear pressure 25 kg / cm 2 ), and drying was performed using a cylinder dryer at 105 ° C. for 2 minutes.
【００３０】実施例２
上記実施例１におけるパルプ配合を表１に示す配合量と
した以外は実施例１と同様にして実施例２の嵩高紙を作
製した。Example 2 A bulky paper of Example 2 was prepared in the same manner as in Example 1 except that the pulp content in Example 1 was changed to the compounding amount shown in Table 1.
【００３１】実施例３
上記実施例１で使用したリヨセルの繊維径を２．４ｄｔ
ｅｘとした以外は実施例１と同様にして実施例３の嵩高
紙を作製した。Example 3 The fiber diameter of the lyocell used in Example 1 was 2.4 dt.
The bulky paper of Example 3 was produced in the same manner as in Example 1 except that ex was changed.
【００３２】実施例４
上記実施例３におけるパルプ配合を表１に示す配合量と
した以外は実施例３と同様にして実施例４の嵩高紙を作
製した。Example 4 A bulky paper of Example 4 was prepared in the same manner as in Example 3 except that the pulp content in Example 3 was changed to that shown in Table 1.
【００３３】比較例１
上記実施例１におけるパルプ配合を表１に示す配合量に
した以外は実施例１と同様にして比較例１の嵩高紙を作
製した。Comparative Example 1 A bulky paper of Comparative Example 1 was produced in the same manner as in Example 1 except that the pulp content in Example 1 was changed to the compounding amount shown in Table 1.
【００３４】比較例２
上記実施例１で使用したリヨセルの繊維径を３．０ｄｔ
ｅｘとし、パルプ配合を表１に示す配合量とした以外は
実施例１と同様にして比較例２の嵩高紙を作製した。Comparative Example 2 The fiber diameter of the lyocell used in Example 1 was 3.0 dt.
The bulky paper of Comparative Example 2 was produced in the same manner as in Example 1 except that ex was set and the pulp content was changed to the blending amount shown in Table 1.
【００３５】比較例３
上記実施例１で使用したリヨセルの繊維径を３．０ｄｔ
ｅｘとした以外は実施例１と同様にして比較例３の嵩高
紙を作製した。Comparative Example 3 The fiber diameter of the lyocell used in Example 1 was 3.0 dt.
The bulky paper of Comparative Example 3 was produced in the same manner as in Example 1 except that ex was changed.
【００３６】比較例４
上記実施例２で使用したリヨセルの繊維径を３．０ｄｔ
ｅｘとした以外は実施例２と同様にして比較例４の嵩高
紙を作製した。Comparative Example 4 The fiber diameter of the lyocell used in Example 2 was 3.0 dt.
The bulky paper of Comparative Example 4 was produced in the same manner as in Example 2 except that ex was changed to ex.
【００３７】比較例５
上記実施例１で使用したリヨセルに代えて、繊維長２ｍ
ｍ、繊維径１．７ｄｔｅｘの未叩解のレーヨンを使用し
た以外は実施例１と同様にして比較例５の嵩高紙を作製
した。Comparative Example 5 Instead of the lyocell used in Example 1 above, the fiber length was 2 m.
The bulky paper of Comparative Example 5 was produced in the same manner as in Example 1 except that unbeaten rayon having a fiber diameter of 1.7 dtex and a fiber diameter of 1.7 m was used.
【００３８】[0038]
【表１】 [Table 1]
【００３９】評価：表１に示した実施例１〜４、比較例
１〜５の結果から明らかなように、繊維長２ｍｍ以下、
繊維径２．４ｄｔｅｘ以下の未叩解のリヨセルを適量配
合することで表面平滑性が高く、紙力の強い嵩高紙を作
製できることがわかる。Evaluation: As is clear from the results of Examples 1 to 4 and Comparative Examples 1 to 5 shown in Table 1, the fiber length is 2 mm or less,
It can be seen that by adding an appropriate amount of unbeaten lyocell having a fiber diameter of 2.4 dtex or less, a bulky paper having high surface smoothness and strong paper strength can be produced.
【００４０】実施例１、３、比較例３および実施例２、
４、比較例４から明らかなように、リヨセルの繊維径の
違いによる嵩高効果には大きな違いはない。しかし、繊
維径が２．４ｄｔｅｘを超えた場合、表面平滑性が低下
する。そのため、繊維径を２．４ｄｔｅｘ以下とするこ
とが好ましい。Examples 1 and 3, Comparative Example 3 and Example 2,
4. As is clear from Comparative Example 4, there is no significant difference in the bulking effect due to the difference in the fiber diameter of Lyocell. However, when the fiber diameter exceeds 2.4 dtex, the surface smoothness deteriorates. Therefore, it is preferable that the fiber diameter is 2.4 dtex or less.
【００４１】比較例２、３、４から明らかなように、リ
ヨセルの配合量を減らすと嵩高効果が小さくなる。逆
に、配合量を増やすと嵩高効果は高くなるものの、紙力
と表面平滑性が低下する。そのため、配合量を１０〜１
５質量％とすることが好ましい。As is clear from Comparative Examples 2, 3, and 4, the bulkiness effect decreases when the amount of lyocell blended is reduced. On the contrary, if the compounding amount is increased, the bulkiness effect is enhanced, but the paper strength and the surface smoothness are degraded. Therefore, the blending amount is 10 to 1
It is preferably 5% by mass.
【００４２】実施例１と比較例５の結果から明らかなよ
うに、同じ形状のレーヨンを同量配合してもリヨセルほ
ど高い嵩高効果は得られない。そのため、再生セルロー
ス系繊維の中でもリヨセルを用いることが好ましい。As is clear from the results of Example 1 and Comparative Example 5, even if the same amount of rayon having the same shape is blended, the bulkiness effect as high as that of Lyocell cannot be obtained. Therefore, it is preferable to use Lyocell among the regenerated cellulose fibers.
【００４３】＜叩解したリヨセルを使用＞
実施例５および実施例６
上記実施例１で使用したリヨセルをカナダ標準濾水度３
９０ｍｌに叩解し、パルプ配合を表２に示す配合量とし
た以外は実施例１と同様にして実施例５、６の嵩高紙を
作製した。<Using Beated Lyocell> Example 5 and Example 6 The lyocell used in the above Example 1 was used as Canadian Standard Freeness 3
Bulky papers of Examples 5 and 6 were produced in the same manner as in Example 1 except that the pulp was beaten to 90 ml and the pulp content was changed to the content shown in Table 2.
【００４４】実施例７および実施例８
上記実施例３で使用したリヨセルをカナダ標準濾水度４
５０ｍｌに叩解し、パルプ配合を表２に示す配合量とし
た以外は実施例３と同様にして実施例７、８の嵩高紙を
作製した。Examples 7 and 8 The lyocell used in Example 3 above was subjected to Canadian standard freeness 4
Bulky papers of Examples 7 and 8 were produced in the same manner as in Example 3 except that the pulp was beaten to 50 ml and the pulp content was changed to the content shown in Table 2.
【００４５】比較例６〜比較例８
上記比較例２で使用したリヨセルをカナダ標準濾水度４
５０ｍｌに叩解し、パルプ配合を表２に示す配合量とし
た以外は比較例２と同様にして比較例６、７、８の嵩高
紙を作製した。Comparative Examples 6 to 8 The lyocell used in the above Comparative Example 2 was prepared according to Canadian Standard Freeness 4
Bulky papers of Comparative Examples 6, 7 and 8 were produced in the same manner as Comparative Example 2 except that the pulp was beaten to 50 ml and the pulp content was changed as shown in Table 2.
【００４６】比較例９および比較例１０
上記比較例２で使用したリヨセルをカナダ標準濾水度４
８０ｍｌに叩解し、パルプ配合を表２に示す配合量とし
た以外は比較例２と同様にして比較例９、１０を作製し
た。Comparative Example 9 and Comparative Example 10 The lyocell used in the above Comparative Example 2 was converted to Canadian standard freeness 4
Comparative Examples 9 and 10 were prepared in the same manner as Comparative Example 2 except that the mixture was beaten to 80 ml and the pulp content was changed to the blending amount shown in Table 2.
【００４７】[0047]
【表２】 [Table 2]
【００４８】評価：本発明の実施例５〜８と比較例６〜
１０の結果から明らかなように、配合するリヨセルの量
および叩解度を工夫することにより、表面平滑性が高
く、紙力の強い嵩高紙を得ることができるのは明らかで
ある。Evaluation: Examples 5 to 8 of the present invention and Comparative Example 6 to
As is clear from the result of No. 10, it is apparent that a bulky paper having high surface smoothness and strong paper strength can be obtained by devising the amount of the lyocell to be blended and the beating degree.
【００４９】実施例２、６および実施例４、８の結果か
ら明らかなように、叩解したリヨセルを用いることで、
未叩解のリヨセルを用いた場合よりもさらに嵩高な、表
面平滑性が高く、紙力の強い嵩高紙を製作することがで
きる。また、リヨセルの配合量を増やすことで低下する
紙力を、リヨセルの叩解可能という繊維の特性を利用し
て補っているため、紙力剤などの薬品を必要としないこ
とも特徴である。As is clear from the results of Examples 2 and 6 and Examples 4 and 8, by using beaten lyocell,
It is possible to produce a bulky paper having a higher surface smoothness and a stronger paper strength, which is more bulky than the case of using an unbeaten Lyocell. Further, since the paper strength, which is reduced by increasing the blending amount of lyocell, is compensated for by utilizing the fiber property that lyocell can be beaten, it is also characterized in that a chemical such as a paper strength agent is not required.
【００５０】実施例５、７、比較例６および実施例６、
８、比較例７の結果から明らかなように、繊維径を太く
するほど表面平滑性が低下する。そのため、リヨセルを
叩解して用いる場合においても、繊維径は２．４ｄｔｅ
ｘ以下とするのが好ましい。Examples 5 and 7, Comparative Example 6 and Example 6,
8, as is clear from the results of Comparative Example 7, the larger the fiber diameter, the lower the surface smoothness. Therefore, the fiber diameter is 2.4 dte even when Lyocell is beaten and used.
It is preferably x or less.
【００５１】比較例６、７、８の結果から明らかなよう
に、リヨセルを叩解して用いる場合においても配合量を
増やすほど嵩高効果は高くなる。しかし、それとともに
表面平滑性と紙力は低下する。そのため、リヨセルの配
合量は１６〜３５質量％とすることが好ましい。As is clear from the results of Comparative Examples 6, 7 and 8, the bulkiness effect increases as the compounding amount increases even when lyocell is beaten and used. However, along with that, the surface smoothness and the paper strength decrease. Therefore, the blending amount of Lyocell is preferably 16 to 35% by mass.
【００５２】比較例６、９および比較例７、１０の結果
から明らかなように、リヨセルの濾水度の値を高くする
と嵩高効果は高くなるが、表面平滑性と紙力が低下す
る。配合量を１６〜３５質量％とする場合は表面平滑性
が良く、紙力の強い嵩高紙を得るためにカナダ標準濾水
度は４５０ｍｌ以下とすることが好ましい。As is clear from the results of Comparative Examples 6 and 9 and Comparative Examples 7 and 10, when the freeness value of Lyocell is increased, the bulkiness effect increases, but the surface smoothness and paper strength decrease. When the blending amount is 16 to 35% by mass, the surface smoothness is good, and the Canadian standard freeness is preferably 450 ml or less in order to obtain bulky paper having strong paper strength.
【００５３】[0053]
【発明の効果】上記結果から明らかなように、本発明の
嵩高紙は未叩解のリヨセルまたは叩解したリヨセルを含
有することで、表面平滑性が高く、紙力が強い嵩高紙が
得られることを特徴としている。また、繊維の特性を利
用して紙力を補うことができるため、紙力剤などの薬品
を必要としない。As is clear from the above results, the bulky paper of the present invention contains un-beaten lyocell or beaten lyocell to obtain bulky paper having high surface smoothness and strong paper strength. It has a feature. Further, since the paper strength can be supplemented by utilizing the characteristics of the fiber, a chemical such as a paper strength agent is not required.
Claims (3)
ｘ以下のリヨセルを含有してなることを特徴とする嵩高
紙。1. A fiber length of 2 mm or less and a fiber diameter of 2.4 dte.
A bulky paper characterized by containing less than x lyocell.
かつ全パルプに対して１０〜１５質量％含有してなるこ
とを特徴とする請求項１記載の嵩高紙。2. The lyocell is an unbeaten lyocell,
The bulky paper according to claim 1, characterized in that the content is 10 to 15% by mass based on the total pulp.
ｌ以下に叩解されたリヨセルであり、かつ全パルプに対
して１６〜３５質量％含有してなることを特徴とする請
求項１記載の嵩高紙。3. Lyocell has a Canadian standard freeness of 450 m.
The bulky paper according to claim 1, which is lyocell beaten to 1 or less, and is contained in an amount of 16 to 35 mass% with respect to the total pulp.