JP2003225032A - Fish and shellfish farming net having effect of preventing adhesion of diatom - Google Patents
Fish and shellfish farming net having effect of preventing adhesion of diatomInfo
- Publication number
- JP2003225032A JP2003225032A JP2002028184A JP2002028184A JP2003225032A JP 2003225032 A JP2003225032 A JP 2003225032A JP 2002028184 A JP2002028184 A JP 2002028184A JP 2002028184 A JP2002028184 A JP 2002028184A JP 2003225032 A JP2003225032 A JP 2003225032A
- Authority
- JP
- Japan
- Prior art keywords
- net
- diatom
- fish
- melting point
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、海水に長期間接触
して使用された時に、珪藻類の付着が極めて少ない魚介
類養殖網に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fish and aquaculture net with extremely little adherence of diatoms when used in contact with seawater for a long period of time.
【０００２】[0002]
【従来の技術】海水中で長期間使用される魚介類養殖網
としては、例えばハマチ、マダイ、トラフグ、ヒラメ等
の稚魚養殖用モジ網；アコヤ貝、ホタテ貝、牡蠣等の貝
類養殖用籠等の網地がある。これらの網地は、海水に接
触するうちに短期間にその表面に種々の珪藻類が付着す
る。そして珪藻類の付着により網地の目が詰まり、酸素
欠乏やエラムシ・ハダムシ等の寄生虫病の発生等、魚介
類への大きな障害をきたすこととなる。BACKGROUND OF THE INVENTION As a seafood culture net that is used for a long time in seawater, for example, a moji net for larvae such as yellowtail, red sea bream, trufflefish and flounder; a cage for shellfish culture such as pearl oysters, scallops and oysters There is a net. Various kinds of diatoms adhere to the surface of these nets in a short period of time while contacting with seawater. The attachment of diatoms causes clogging of the net, which causes major obstacles to fish and shellfish, such as oxygen deficiency and the occurrence of parasitic diseases such as aphids and wasabi.
【０００３】海水に接触して使用される定置網や養殖生
け簀等は、上記のような水棲生物の付着を防止するため
の対策として、トリブチルスズオキシド、トリフェニル
スズオキシド、トリフェニルスズアセテート、トリフェ
ニルスズクロライド等の有機スズ化合物や、銅、銀、亜
鉛、ニッケルなどの金属やその化合物、または窒素硫黄
系、ハロゲン系等の有機化合物を含有させた塗料を塗布
する方法が広く知られている。しかしながら、防汚塗料
を処理する際に、防汚成分自体や有機溶媒に起因する激
しい不快臭、刺激臭を伴い、更に作業者の健康を害する
という問題があり、塗料塗布が不要で、防汚効果が長期
間持続する製品が強く要望されている。また、これらの
防汚塗料は海水中への薬剤溶出速度が大きく、そのため
養殖魚介類が死亡する場合があり、特に稚魚や貝類には
使用できなかった。Stationary nets, aquaculture cages, and the like used in contact with seawater have tributyltin oxide, triphenyltin oxide, triphenyltin acetate, triphenyltin as measures to prevent the adhesion of aquatic organisms as described above. A method of applying a coating material containing an organic tin compound such as chloride, a metal such as copper, silver, zinc, nickel or a compound thereof, or an organic compound such as nitrogen-sulfur-based or halogen-based is widely known. However, when treating the antifouling paint, there is a problem that it causes a severe unpleasant odor and an irritating odor caused by the antifouling component itself and the organic solvent and further impairs the health of workers. There is a strong demand for products that have long-lasting effects. In addition, these antifouling paints have a high rate of drug elution into seawater, which may cause death of cultured seafood, and thus cannot be used especially for fry and shellfish.
【０００４】そこで、上記のような弊害を防止する手段
として、３日毎にモジ網、生け簀籠の交換を行い、珪藻
が付着した網の洗浄・補修を行う必要が有り、その作業
に多大な労力と時間が費やされてきた。Therefore, as a means for preventing the above-mentioned harmful effects, it is necessary to replace the moji nets and cages every three days to clean and repair the nets to which the diatom has adhered, which is a great effort. And time has been spent.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、塗料
塗布が不要で、魚介類や人体に対する安全性が高く、耐
久性があり、珪藻の付着を長期に亘って防止することが
可能な魚介類養殖網を提供することにある。SUMMARY OF THE INVENTION The object of the present invention is that it is unnecessary to apply a paint, has high safety to seafood and human body, is durable, and can prevent diatoms from adhering for a long period of time. It is to provide a fish culture net.
【０００６】[0006]
【課題を解決するための手段】上記の目的は、ビス（２
−ピリジンチオール−１−オキシド）金属塩を含有する
熱可塑性樹脂により被覆されてなる樹脂被覆糸が、モジ
リ目を形成してなる魚介類養殖網を提供することによっ
て達成される。[Means for Solving the Problems]
-Pyridinethiol-1-oxide) A resin-coated yarn, which is coated with a thermoplastic resin containing a metal salt, is achieved by providing a fish and shellfish aquaculture net formed by forming a gauze pattern.
【０００７】[0007]
【発明の実施の形態】本発明においては、被覆樹脂中に
ビス（２−ピリジンチオール−１−オキシド）金属塩を
含有していることが重要であり、金属塩としては、銅、
亜鉛、マグネシウム、カルシウム、ナトリウム等の塩が
挙げられる。BEST MODE FOR CARRYING OUT THE INVENTION In the present invention, it is important that the coating resin contains a bis (2-pyridinethiol-1-oxide) metal salt.
Examples include salts of zinc, magnesium, calcium, sodium and the like.
【０００８】かかる化合物の熱可塑性樹脂への含有量
は、珪藻付着防止効果を考慮して、０．１〜３０質量％
の範囲であることが好ましい。含有量を多くしても効果
の向上は認められず、また少なすぎても効果は奏されな
い。より好ましい含有量は３〜１０質量％の範囲であ
る。The content of such a compound in the thermoplastic resin is 0.1 to 30% by mass in consideration of the effect of preventing diatom adhesion.
It is preferably in the range of. Even if the content is increased, the effect is not improved, and if it is too small, the effect is not exhibited. A more preferable content is in the range of 3 to 10% by mass.
【０００９】上述の化合物を含有する熱可塑性樹脂は、
ジオール変性もしくは酸変性の芳香族ポリエステルであ
ることが、後述する芯糸を形成するポリマーとの融点ま
たは軟化点差を利用した熱融着性の点、上述の化合物と
の混練性等の点で好ましい。なお、ここで変性とは共重
合を意味するものである。ポリエステルとしては、ポリ
エチレンテレフタレート、ポリブチレンテレフタレー
ト、ポリトリメチレンテレフタレート、ポリヘキサメチ
レンテレフタレート等のポリエステルを用いることがで
きるが、熱融着性、融点、繊維強度の点からは、テレフ
タル酸と１，６−ヘキサンジオールからなるポリヘキサ
メチレンテレフタレートを用いることが好ましい。該ポ
リエステルを変性させ得るジオール成分は、エチレング
リコール、ジエチレングリコール、１，４−ブタンジオ
ール、ネオペンチルグリコール、シクロヘキサン−１，
４−ジメタノール等であり、該ポリエステルを構成する
ジオール成分の１０〜５０モル％の範囲であることが好
ましく、ポリエチレングリコール、ポリテトラメチレン
グリコール等は該ポリエステルを構成するジオール成分
の１〜２０質量％の範囲であることが好ましい。Thermoplastic resins containing the above compounds are
A diol-modified or acid-modified aromatic polyester is preferable from the viewpoint of heat fusion property utilizing the difference in melting point or softening point with the polymer forming the core yarn described later, kneading property with the above compound, and the like. . Here, the modification means copolymerization. Polyesters such as polyethylene terephthalate, polybutylene terephthalate, polytrimethylene terephthalate and polyhexamethylene terephthalate can be used as the polyester, but terephthalic acid and 1,6 It is preferable to use polyhexamethylene terephthalate composed of -hexanediol. The diol component capable of modifying the polyester includes ethylene glycol, diethylene glycol, 1,4-butanediol, neopentyl glycol, cyclohexane-1,
4-dimethanol or the like, preferably in the range of 10 to 50 mol% of the diol component constituting the polyester, and polyethylene glycol, polytetramethylene glycol or the like is 1 to 20 mass of the diol component constituting the polyester. It is preferably in the range of%.
【００１０】該ポリエステルを変性させ得る酸成分とし
ては、例えば、イソフタル酸、ナフタレン−２，６−ジ
カルボン酸、フタル酸、α，β−（４−カルボキシフェ
ノキシ）エタン、４，４−ジカルボキシフェニル、５−
ナトリウムスルホイソフタル酸などの芳香族ジカルボン
酸もしくはアジピン酸、セバシン酸などの脂肪族ジカル
ボン酸、またはこれらのエステル類であり、該ポリエス
テルを構成する酸成分の５〜５０モル％の範囲であるこ
とが好ましい。Examples of the acid component capable of modifying the polyester include isophthalic acid, naphthalene-2,6-dicarboxylic acid, phthalic acid, α, β- (4-carboxyphenoxy) ethane and 4,4-dicarboxyphenyl. , 5-
An aromatic dicarboxylic acid such as sodium sulfoisophthalic acid or an adipic acid, an aliphatic dicarboxylic acid such as sebacic acid, or an ester thereof, which is in the range of 5 to 50 mol% of the acid component constituting the polyester. preferable.
【００１１】また、該変性ポリエステルは、融点が１５
０℃以下、溶融粘度が１００００ポイズ以下（１６０
℃、キャピラリー長１０mm、キャピラリー径１mm、剪断
速度１０００sec-1の条件）であることが望ましい。融
点が１５０℃を越える場合には、熱溶融による上述の化
合物との混練、紡糸、成形の各工程で１８０℃を越えて
熱をかける必要が生じ、上述の化合物が気化、または分
解して、その効果が低下してしまう場合がある。また溶
融粘度も、あまり高過ぎると混練、紡糸、成形の各工程
で１８０℃以上の剪断熱が生じ、上述の化合物の気化、
分解を招く場合が生じる。より好ましい融点は１４０℃
以下、溶融粘度は２０００〜５０００ポイズの範囲であ
る。The modified polyester has a melting point of 15
0 ° C or less, melt viscosity of 10,000 poise or less (160
C., capillary length 10 mm, capillary diameter 1 mm, shear rate 1000 sec.sup.- 1 ) are desirable. When the melting point is higher than 150 ° C, it is necessary to apply heat higher than 180 ° C in each step of kneading, spinning, and molding with the above compound by heat melting, and the above compound vaporizes or decomposes, The effect may be reduced. Further, if the melt viscosity is too high, shearing heat insulation of 180 ° C. or higher occurs in each step of kneading, spinning, and molding, and vaporization of the above compound,
It may cause decomposition. More preferable melting point is 140 ° C
Hereinafter, the melt viscosity is in the range of 2000 to 5000 poise.
【００１２】変性ポリエステルの中には融点が高いもの
があるが、この場合には融点降下剤としてポリブテン、
液状ポリエステル等の中分子ポリマーを使用することが
できる。該融点降下剤の添加量は、融点が１５０℃以下
に下がる程度に、また溶融粘度が１００００ポイズ以下
に下がる程度の量を添加させれば、特に限定されるもの
ではない。Some modified polyesters have a high melting point. In this case, polybutene as a melting point depressant,
A medium molecular weight polymer such as liquid polyester can be used. The addition amount of the melting point depressant is not particularly limited as long as the melting point is reduced to 150 ° C. or lower and the melt viscosity is reduced to 10,000 poise or lower.
【００１３】また、これら熱可塑性樹脂中には、本発明
の効果を損なわない範囲であれば、相溶化剤、可塑剤、
紫外線吸収剤、導電性改良剤、結晶化遅延剤等の改質剤
や着色顔料等の添加剤を適宜含有させることができる。In these thermoplastic resins, a compatibilizer, a plasticizer, and a compatibilizer may be used as long as the effects of the present invention are not impaired.
An ultraviolet absorber, a conductivity improver, a modifier such as a crystallization retarder, and an additive such as a color pigment may be appropriately contained.
【００１４】上述の熱可塑性樹脂が被覆されてなる芯糸
を形成するポリマーとしては、その融点または軟化点が
該熱可塑性樹脂の融点または軟化点より５０℃以上高い
ポリマーが好ましく、かかる融点または軟化点を有する
ポリマーであれば特に限定されるものではないが、該熱
可塑性樹脂からなる被膜が芯糸と剥離しないもの、被覆
糸としての強度を保持するものが好ましい。The polymer forming the core yarn coated with the above-mentioned thermoplastic resin is preferably a polymer having a melting point or softening point higher by 50 ° C. or more than the melting point or softening point of the thermoplastic resin, and such melting point or softening point is preferable. It is not particularly limited as long as it is a polymer having dots, but it is preferable that the coating film made of the thermoplastic resin does not separate from the core yarn, and that the strength of the coated yarn is maintained.
【００１５】本発明においては、後述するレピア織機の
工程通過性を良好なものとするために、被覆剥離を生じ
させることがないように被覆樹脂と芯糸とが接着してい
ることが望ましく、被覆樹脂と芯糸との間に空隙は存在
しないことが望ましい。融点または軟化点差が５０℃未
満の場合には、溶融押出被覆、後述する経糸と緯糸との
交点の熱融着の際に、溶断や著しい収縮が発生し、加工
が不可能となる。In the present invention, it is desirable that the coating resin and the core yarn are adhered to each other so as not to cause peeling of the coating, in order to improve the process passability of the rapier loom described later. It is desirable that there be no void between the coating resin and the core yarn. When the difference in melting point or softening point is less than 50 ° C., melt-extrusion coating or heat fusion at an intersection point between a warp and a weft described later causes fusing and significant shrinkage, which makes processing impossible.
【００１６】以上のような観点から、被覆樹脂として上
述の変性ポリエステル組成物を使用し、芯糸としてポリ
エチレンテレフタレート、ポリブチレンテレフタレート
等の飽和ポリエステル、ポリアリレート、全芳香族ポリ
エステル、全芳香族アラミド等を用いることが好まし
い。From the above viewpoints, the above modified polyester composition is used as the coating resin, and the core yarn is saturated polyester such as polyethylene terephthalate and polybutylene terephthalate, polyarylate, wholly aromatic polyester, wholly aromatic aramid and the like. Is preferably used.
【００１７】熱可塑性樹脂を芯糸に被覆する方法として
は、該樹脂を溶媒に溶解して芯糸表面に塗布する被覆方
法もあるが、本発明においては溶融押出法により芯糸に
被覆することが好ましい。As a method for coating the core yarn with the thermoplastic resin, there is a coating method in which the resin is dissolved in a solvent and applied on the surface of the core yarn. In the present invention, the core yarn is coated by the melt extrusion method. Is preferred.
【００１８】また芯糸は、フィラメント糸、紡績糸の形
態を問わず、これらからなる合撚糸等も目的に応じて使
用することができる。該フィラメント糸はモノフィラメ
ントでもマルチフィラメントでもよい。The core yarn may be filament yarn or spun yarn in any form, and a plied yarn made of these may be used depending on the purpose. The filament yarn may be monofilament or multifilament.
【００１９】本発明の網の製造方法については、上述の
化合物が含有された熱可塑性樹脂で芯糸が被覆されてな
る樹脂被覆糸が、モジリ目を形成するような網を製造で
きる方法であれば特に制限されるものではない。本発明
の網を製造する方法の一例を示すと、まず、二軸混練押
出機を使用して、前記構造式に記載の化合物さらには必
要に応じてその他の化合物と熱可塑性樹脂とを均一に混
合しダイに導き、芯糸表面に被覆させる。被覆樹脂と芯
糸との接着性を高めるためには、加圧型ダイを使用する
ことが好ましい。芯糸を形成するポリマーと、上記化合
物を含む熱可塑性樹脂との融点または軟化点の差を５０
℃以上にすることによって、柔軟且つ断面形状が不均一
の芯糸表面にほぼ均一に上記熱可塑性樹脂組成物を被覆
することができる。その上、被覆樹脂との接触によって
軟化した芯糸にかかる余分な変形や摩擦による断糸を抑
制することができる。Regarding the method for producing the net of the present invention, any method can be used in which the resin-coated yarn obtained by coating the core yarn with the thermoplastic resin containing the above-mentioned compound forms a net having a perforation. It is not particularly limited. As an example of the method for producing the net of the present invention, first, by using a twin-screw kneading extruder, the compound described in the structural formula and further other compounds as necessary and the thermoplastic resin are homogenized. Mix and lead to a die to coat the surface of the core yarn. In order to improve the adhesiveness between the coating resin and the core yarn, it is preferable to use a pressure die. The difference in melting point or softening point between the polymer forming the core yarn and the thermoplastic resin containing the above compound is 50
By setting the temperature to be not lower than 0 ° C, the surface of the core yarn which is soft and has a non-uniform cross-sectional shape can be almost uniformly coated with the thermoplastic resin composition. Moreover, it is possible to suppress excessive deformation applied to the core yarn softened by the contact with the coating resin and breakage due to friction.
【００２０】芯糸の走行速度、ドラフト率は適宜設定す
ることができ、ドラフトを受けた樹脂被覆糸は冷却ゾー
ンに導かれ、冷却固化され巻き取られる。次に、得られ
た被覆糸を用いてレピア織機等により絡み織でメッシュ
を作製する。この際に、緯糸がモジリ目を形成するので
ある。そして乾式加熱により、経糸と緯糸との交点を熱
融着させることにより、網を得ることができる。経糸と
緯糸との交点を熱融着させることにより、目ズレを防ぐ
ことができ、網としての用をなすことができる。The running speed and draft rate of the core yarn can be set as appropriate, and the resin-coated yarn that has undergone the draft is guided to the cooling zone, cooled and solidified and wound up. Next, using the obtained coated yarn, a mesh is produced by a entangled weave with a rapier loom or the like. At this time, the weft forms a perforation. Then, the net can be obtained by heat-sealing the intersections of the warp and the weft by dry heating. By heat-sealing the intersections of the warp and the weft, misalignment can be prevented and it can be used as a net.
【００２１】本発明の網は、一見織物のように経糸と緯
糸を交差して織り込み、正方形の網目を持った網であ
る。細目網分野を中心として使用することができ、イリ
コのパッチ網やハマチの稚魚、マダイ、ヒラメ、トラフ
グ等の養殖網（生け簀網）、海苔網、ワカメ網、アコヤ
貝・ホタテ貝・牡蠣等の養殖籠などに有用である。The net according to the present invention is a net having a square mesh formed by intersecting and weaving warp threads and weft threads like a woven fabric. It can be used mainly in the field of fine netting, such as irico patch netting, yellowtail juvenile fish, red sea bream, flounder, aquaculture net (trails), seaweed net, wakame net, pearl oyster, scallop, oyster, etc. It is useful for aquaculture cages.
【００２２】[0022]
【実施例】以下、実施例により本発明を詳述するが、本
発明はこれら実施例により何等限定されるものではな
い。尚、実施例中の各評価は、以下の方法により測定さ
れたものである。
（１）珪藻付着状況の判定基準
作製した網を５０ｃｍ×５０ｃｍの銅枠に取り付け、鹿
児島県東町の海中に水深１ｍの位置で懸垂し、経時的に
珪藻の付着状況を観察し、次の５段階で評価した。
判定基準
５：珪藻の付着が全く観察されなかった。
４：対象物の表面全体の１０％程度に珪藻の付着が認め
られた。
３：対象物の表面全体の２０％程度に珪藻の付着が認め
られた。
２：対象物の表面全体の５０％程度に珪藻の付着が認め
られた。
１：対象物の表面全体に珪藻の付着が見られた。
（２）ポリマーの融点（℃）
示差操作熱量計（メトラー社製、ＴＣプロセッサーＴＣ
１０Ａ型）を用いて測定した。
（３）ポリマーの溶融粘度（ポイズ）
キャピログラフ（東洋精機社製、キャピログラフ１Ｃ）
を用いて、１６０℃における溶融粘度を測定した。The present invention will be described in detail below with reference to examples, but the present invention is not limited to these examples. The evaluations in the examples are measured by the following methods. (1) Criteria for diatom adhesion status The prepared net is attached to a copper frame of 50 cm x 50 cm, suspended in the sea in Higashi Town, Kagoshima Prefecture at a depth of 1 m, and the diatom adhesion status is observed over time. The grade was evaluated. Criterion 5: No adhesion of diatom was observed. 4: Adhesion of diatom was recognized on about 10% of the entire surface of the object. 3: Adhesion of diatom was recognized on about 20% of the entire surface of the object. 2: Adhesion of diatom was recognized on about 50% of the entire surface of the object. 1: Adhesion of diatom was found on the entire surface of the object. (2) Melting point of polymer (° C) Differential operation calorimeter (TC processor TC manufactured by METTLER CORPORATION)
10A type). (3) Melt viscosity of polymer (poise) Capirograph (Toyo Seiki Co., Capirograph 1C)
Was used to measure the melt viscosity at 160 ° C.
【００２３】実施例１
イソフタル酸を１０モル％共重合したポリヘキサメチレ
ンテレフタレート（［η］＝０．８６、融点１３５℃、
溶融粘度３５００ポイズ）に、ビス（２−ピリジンチオ
ール−１−オキシド）亜鉛塩を１０質量％、アジピン酸
系液状ポリエステル（旭電化製アデカサイザーＰＮ−３
５０：２５℃粘度１００００ｃｐ）を１５質量％、カー
ボンよりなる黒色顔料を０．４質量％含有させ、熱溶融
樹脂被覆装置を用いて、ポリアリレートマルチフィラメ
ント（クラレ製：融点３２０℃、１１００ｄｔｅｘ／２
００フィラメント、８０Ｔ／Ｍ片撚）１００質量部に対
し、２００質量部被覆し、３３００ｄｔｅｘの樹脂被覆
糸を得た。次に、該樹脂被覆糸を使用してレピア織機に
て絡み織で経糸密度４本×２／吋、緯糸密度４本×２／
吋のメッシュを作製し、１５１℃で３０秒加熱して経
糸、及び緯糸の交点を熱融着させ網を得た。この網につ
いて珪藻付着試験を行った結果、海中浸漬３ヶ月間充分
な防汚効果を示した。Example 1 Polyhexamethylene terephthalate copolymerized with 10 mol% of isophthalic acid ([η] = 0.86, melting point 135 ° C.,
10% by mass of bis (2-pyridinethiol-1-oxide) zinc salt in a melt viscosity of 3500 poise, adipic acid liquid polyester (Adeka Sizer PN-3 manufactured by Asahi Denka Co., Ltd.)
50: 25 ° C. viscosity 10000 cp) 15% by mass, carbon black pigment 0.4% by mass, using a hot-melt resin coating device, polyarylate multifilament (Kuraray: melting point 320 ° C., 1100 dtex / 2)
100 parts by mass of 00 filaments and 80 T / M single twist) were coated with 200 parts by mass to obtain a resin-coated yarn of 3300 dtex. Next, using the resin-coated yarn, a warp weave density of 4 yarns x 2 / inch and a weft yarn density of 4 yarns 2 /
An inch mesh was prepared and heated at 151 ° C. for 30 seconds to heat-bond the intersections of the warp and the weft to obtain a net. As a result of carrying out a diatom adhesion test on this net, it showed a sufficient antifouling effect for 3 months of immersion in the sea.
【００２４】実施例２
実施例１のビス（２−ピリジンチオール−１−オキシ
ド）亜鉛塩を、ビス（２−ピリジンチオール−１−オキ
シド）銅塩に変更したこと以外は、実施例１と同様に防
汚性網を得た。この網について珪藻付着試験を行った結
果、海中浸漬３ヶ月間充分な防汚効果を示した。Example 2 Same as Example 1 except that the bis (2-pyridinethiol-1-oxide) zinc salt of Example 1 was changed to bis (2-pyridinethiol-1-oxide) copper salt. I got an antifouling net. As a result of carrying out a diatom adhesion test on this net, it showed a sufficient antifouling effect for 3 months of immersion in the sea.
【００２５】実施例３
実施例１で使用したイソフタル酸を１０モル％共重合し
たポリヘキサメチレンテレフタレートを、エチレングリ
コールを２０モル％共重合したポリヘキサメチレンテレ
フタレート（［η］＝０．８１、融点１３７℃、溶融粘
度３３００ポイズ）に変更したこと以外は、実施例１と
同様に防汚性網を得た。この網について珪藻付着試験を
行った結果、海中浸漬３ヶ月間充分な防汚効果を示し
た。Example 3 Polyhexamethylene terephthalate copolymerized with 10 mol% of isophthalic acid used in Example 1 and polyhexamethylene terephthalate copolymerized with 20 mol% of ethylene glycol ([η] = 0.81, melting point) An antifouling net was obtained in the same manner as in Example 1 except that the temperature was changed to 137 ° C and the melt viscosity was 3300 poise). As a result of carrying out a diatom adhesion test on this net, it showed a sufficient antifouling effect for 3 months of immersion in the sea.
【００２６】実施例４
実施例１で使用したイソフタル酸を１０モル％共重合し
たポリヘキサメチレンテレフタレートを、１，４−ブタ
ンジオールを３０モル％共重合したポリヘキサメチレン
テレフタレート（［η］＝０．８６、融点１２６℃、溶
融粘度４０００ポイズ）に変更したこと以外は、実施例
１と同様に防汚性網を得た。この網について珪藻付着試
験を行った結果、海中浸漬３ヶ月間充分な防汚効果を示
した。Example 4 Polyhexamethylene terephthalate copolymerized with 10 mol% of isophthalic acid used in Example 1 and polyhexamethylene terephthalate copolymerized with 30 mol% of 1,4-butanediol ([η] = 0) .86, melting point 126 ° C., melt viscosity 4000 poises), except that an antifouling net was obtained in the same manner as in Example 1. As a result of carrying out a diatom adhesion test on this net, it showed a sufficient antifouling effect for 3 months of immersion in the sea.
【００２７】比較例１
実施例１のビス（２−ピリジンチオール−１−オキシ
ド）亜鉛塩を、ジンクジメチルジチオカーバメートに変
更したこと以外は実施例１と同様に防汚性網を得た。こ
の網について珪藻付着試験を行った結果、海中浸漬３ヶ
日間で珪藻が大量に付着し、目詰まりして使用できない
状態になった。Comparative Example 1 An antifouling net was obtained in the same manner as in Example 1 except that the bis (2-pyridinethiol-1-oxide) zinc salt of Example 1 was changed to zinc dimethyldithiocarbamate. As a result of conducting a diatom adhesion test on this net, a large amount of diatom adhered within 3 days of immersion in the sea, and clogging became unusable.
【００２８】比較例２
ナイロンマルチフィラメント製の目合９０経の稚魚養殖
用モジ網について珪藻付着試験を行った結果、海中浸漬
３ヶ日間で珪藻が大量に付着し、目詰まりして使用でき
ない状態になった。Comparative Example 2 As a result of a diatom adhesion test conducted on a nylon multi-filament moth net having a mesh size of 90 and for fry aquaculture, a large amount of diatom adhered after 3 days of submersion in the sea, and clogging became unusable. Became.
【００２９】[0029]
【発明の効果】本発明の網は、長期間海中に浸漬しても
珪藻類の付着が全く無く、魚介類養殖網に最適である。INDUSTRIAL APPLICABILITY The net of the present invention has no adhesion of diatoms even if it is immersed in the sea for a long period of time, and is most suitable for a fish and shellfish aquaculture net.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｄ０３Ｄ 15/00 Ｄ０３Ｄ 15/00 Ｅ Ｇ 19/00 19/00 Ｄ０６Ｍ 13/355 Ｄ０６Ｍ 13/355 15/507 15/507 Ｚ Ｆターム(参考） 2B104 AA01 AA05 AA06 AA24 AA25 AA26 BA06 BA13 CC29 DB24 2B106 AA01 AA08 EA16 ED01 HA16 HC03 4L033 AA07 AB05 AC10 AC15 BA57 CA46 4L048 AA20 AA27 AB07 AC18 BA08 CA00 DA24 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) D03D 15/00 D03D 15/00 EG 19/00 19/00 D06M 13/355 D06M 13/355 15/507 15/507 ZF term (reference) 2B104 AA01 AA05 AA06 AA24 AA25 AA26 BA06 BA13 CC29 DB24 2B106 AA01 AA08 EA16 ED01 HA16 HC03 4L033 AA07 AB05 AC10 AC15 BA57 CA46 4L048 AA20 AA27 AB07 AC18 BA08 CA00 DA24
Claims (2)
シド）金属塩を含有する熱可塑性樹脂により被覆されて
なる樹脂被覆糸が、モジリ目を形成してなることを特徴
とする魚介類養殖網。1. A fish and shellfish aquaculture net, characterized in that a resin-coated thread coated with a thermoplastic resin containing a bis (2-pyridinethiol-1-oxide) metal salt forms a perforation. .
融点または軟化点より、被覆樹脂の融点または軟化点が
５０℃以上低い請求項１に記載の魚介類養殖網。2. The seafood culture net according to claim 1, wherein the melting point or softening point of the coating resin is 50 ° C. or more lower than the melting point or softening point of the polymer forming the core yarn of the resin coated yarn.