JP2003180510A - Weight for curtain and production method for the same - Google Patents
Weight for curtain and production method for the sameInfo
- Publication number
- JP2003180510A JP2003180510A JP2001382014A JP2001382014A JP2003180510A JP 2003180510 A JP2003180510 A JP 2003180510A JP 2001382014 A JP2001382014 A JP 2001382014A JP 2001382014 A JP2001382014 A JP 2001382014A JP 2003180510 A JP2003180510 A JP 2003180510A
- Authority
- JP
- Japan
- Prior art keywords
- stainless steel
- weight
- curtain
- pellet
- pellets
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明はカーテン用ウェイト
およびその製造方法に関し、特に、縫製後の縫い針残留
検査において検出装置が誤動作しないカーテン用ウェイ
トおよびその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a curtain weight and a method for manufacturing the curtain weight, and more particularly to a curtain weight and a method for manufacturing the curtain weight in which a detection device does not malfunction in a sewing needle residual inspection after sewing.
【０００２】[0002]
【従来の技術】カーテンには、吊り下げたカーテン生地
の襞やウェーブ形状を美しく保つために、カーテン生地
の裾部に、各種のウェイトが取り付けられている。例え
ば、レースカーテン用のウェイトとしては、レースカー
テンの優美なウェーブを保つために、多数の金属製ペレ
ットを布製のチューブ内に所定間隔で収納した屈曲自在
のウェイトテープが用いられている。2. Description of the Related Art Various weights are attached to the hem of the curtain material to keep the folds and the wavy shape of the hanging curtain material. For example, as a weight for a lace curtain, a bendable weight tape in which a large number of metal pellets are housed at predetermined intervals in a cloth tube is used in order to keep the elegant wave of the lace curtain.
【０００３】図９は従来のウェイトテープ６０の断面図
を示す。図９において、６１は鉛からなる略円柱状の金
属製ペレットで、これら多数の金属製ペレット６１，６
１…が、布製のチューブ６２内に所定間隔で収納されて
いる。なお、チューブ６２内で金属製ペレット６１，６
１相互間の間隔寸法を一定にするために、金属製ペレッ
ト６１，６１間を糸で連結する場合もある。このように
金属製ペレット６１，６１間を糸で連結する場合は、金
属製ペレット６１のかしめ加工によって糸で連結し易く
するために、特に金属製ペレット６１は柔らかい材質の
鉛製としている。FIG. 9 shows a sectional view of a conventional weight tape 60. In FIG. 9, 61 is a substantially cylindrical metal pellet made of lead, and a large number of these metal pellets 61, 6
1 are stored in a cloth tube 62 at predetermined intervals. In the tube 62, metal pellets 61, 6
In order to keep the distance between the metal pellets 1 constant, the metal pellets 61, 61 may be connected by a thread. When the metal pellets 61, 61 are thus connected by a thread, the metal pellet 61 is made of lead, which is a soft material, in order to facilitate the connection by the thread by crimping the metal pellet 61.
【０００４】[0004]
【発明が解決しようとする課題】ところで、金属製ペレ
ット６１を鉛製とした場合、鉛の毒性のために、金属製
ペレット６１の製造工程における保険衛生上はもちろん
のこと、使用済みの金属製ペレット６１が廃棄された場
合、環境を汚染するため環境保護の観点からも問題があ
った。By the way, when the metal pellet 61 is made of lead, due to the toxicity of lead, not only from the viewpoint of health and hygiene in the manufacturing process of the metal pellet 61, but also from the used metal. When the pellet 61 is discarded, it pollutes the environment, which is problematic from the viewpoint of environmental protection.
【０００５】また、上記のウェイトテープ６０を使用し
たレースカーテンでは、図１０に示すように、レースカ
ーテン７０の裾部７０ａがクネクネと不自然に曲がって
おり、レースカーテン７０本来の優美なウェーブが得ら
れなかった。この原因を調べたところ、従来のウェイト
テープ６０は、金属製ペレット６１が、上歯と下歯を有
する押し切り型の切断具で切断された状態のまま使用さ
れており、しかも、その金属製ペレット６１の中心軸ｙ
が、図１１に示すように、押し切り型の切断具による切
断方向などによって屈曲しているため、この屈曲によっ
て、ウェイトテープ６０に不規則的な曲がりが生じ、こ
の曲がりに起因してレースカーテン７０本来の優美なウ
ェーブが損なわれることが分かった。Further, in the lace curtain using the weight tape 60, as shown in FIG. 10, the hem 70a of the lace curtain 70 is bent unnaturally, and the graceful wave inherent to the lace curtain 70 is formed. I couldn't get it. As a result of investigating the cause, the conventional weight tape 60 shows that the metal pellet 61 is used in a state of being cut by a push-cut type cutting tool having upper teeth and lower teeth, and the metal pellet 61 is used. 61 central axis y
However, as shown in FIG. 11, since the weight tape 60 is bent due to the cutting direction of the push-cut type cutting tool or the like, the weight tape 60 is bent irregularly, and the race curtain 70 is caused by this bending. It turns out that the original graceful wave is spoiled.
【０００６】また、このような従来のレースカーテン用
ウェイトテープ６０では、図１２に示すように、巻取り
具８０に巻き取った状態においても、ウェイトテープ６
０が不定形な曲がりを有しているため、隣接するチェー
ン６０，６０相互間での間隔寸法が不均一になり、しか
も、この曲がりに起因して隣接するチェーン６０，６０
相互間の金属製ペレット６１，６１相互間の間隔寸法も
乱れるため、著しく美観が損なわれて商品価値が低下す
るため、商取引上も問題であった。Further, in such a conventional lace curtain weight tape 60, as shown in FIG. 12, the weight tape 6 is wound even when wound on the winding tool 80.
Since 0 has an indefinite bend, the spacing between adjacent chains 60, 60 becomes non-uniform, and due to this bend, adjacent chains 60, 60
Since the spacing between the metal pellets 61, 61 is also disturbed, the aesthetic appearance is significantly impaired and the commercial value is lowered, which is also a problem in commercial transactions.
【０００７】この原因は、金属製ペレット６１を製造す
る際に、長尺の線材を切断具により切断する場合の切断
具が不適切なことに加えて、金属製ペレット６１の端部
が切断具による切断および破断によるバリを有する異形
状のままになっているため、チューブ６２に収納した場
合に、金属製ペレット６１の中心軸ｙの曲がりに応じた
方向に沿ってチューブ６２に曲がりが生じる結果、ウェ
イトテープ６０にも曲がりが生じるためである。This is due to the fact that when the metal pellet 61 is manufactured, the cutting tool for cutting a long wire with a cutting tool is inappropriate, and the end of the metal pellet 61 is a cutting tool. Since it remains in a different shape with burrs due to cutting and breaking, the tube 62 is bent along the direction corresponding to the bending of the central axis y of the metal pellet 61 when stored in the tube 62. This is because the weight tape 60 also bends.
【０００８】さらに、レースカーテン７０では、その裾
部にウェイトテープ６０を縫い込んだ場合に、その両端
部の始末方法として、チューブ６２の両端部から金属製
ペレット６１を３〜４個抜いて、この金属製ペレット６
１を抜いたチューブ６２をレースカーテン７０の裾部と
ともに折り返して縫い付けるようにしている。Further, in the lace curtain 70, when the weight tape 60 is sewn to the hem, as a method of terminating both ends of the lace curtain 70, 3 to 4 metal pellets 61 are removed from both ends of the tube 62, This metal pellet 6
The tube 62 from which 1 has been removed is folded back and sewn together with the hem of the lace curtain 70.
【０００９】ところが、図８に示す従来のウェイトテー
プ６０では、金属製ペレット６１が前述のようにその中
心軸ｙが曲がっていることと、その両端部に切断バリを
有することとに起因して、チューブ６２の両端部から金
属製ペレット６１を抜き取る作業が極めて困難で、この
レースカーテン７０の裾部両端部の始末加工作業にかな
りの工数が必要であり、原価高騰の要因になっていた上
記の鉛の毒性による安全衛生上および環境保護上の問題
点を解決するために、金属製ペレットを鉛製からステン
レス鋼製とすることが考えられる。ところが、金属製ペ
レットを鉛製からステンレス鋼製とした場合は、製造工
程での安全衛生上の問題点および環境保護上の問題点は
解決されるが、レースカーテンの美しい襞を保つこと
や、カーテン裾部の始末加工に関する問題点は何ら解決
されないばかりでなく、却って、ステンレス鋼製ペレッ
トの場合は、鉛製ペレットに比較して硬度が大きいた
め、その問題点は極めて深刻である。However, in the conventional weight tape 60 shown in FIG. 8, the metal pellet 61 has its center axis y bent as described above, and has cutting burrs at both ends thereof. The work of removing the metal pellet 61 from both ends of the tube 62 is extremely difficult, and a considerable number of man-hours are required for the finishing work of both ends of the hem of the lace curtain 70, which causes a cost increase. In order to solve safety and health and environmental protection problems due to the toxicity of lead, it is conceivable to change the metal pellet from lead to stainless steel. However, when the metal pellets are made from lead to stainless steel, the safety and hygiene problems in the manufacturing process and the environmental protection problems are solved, but keeping the beautiful folds of the lace curtain, Not only are the problems associated with the finishing of the curtain skirts not solved, but rather, stainless steel pellets have a greater hardness than lead pellets, which is a serious problem.
【００１０】また、ステンレス鋼には、フェライト系、
マルテンサイト系およびオーステナイト系などの種類が
あり、一般に、フェライト系およびマルテンサイト系ス
テンレス鋼は常温で磁性があり、オーステナイト系ステ
ンレス鋼は常温では磁性がないとされている。Further, stainless steel includes ferrite type
There are types such as martensitic and austenitic stainless steels. Generally, ferritic and martensitic stainless steels are magnetic at room temperature, and austenitic stainless steels are not magnetic at room temperature.
【００１１】しかしながら、オーステナイト系ステンレ
ス鋼でも、Ｎｉが多い場合は組織が安定であるが、Ｎｉ
が少ないステンレス鋼を固溶化熱処理後に急冷した場合
は、組織が不安定な準オーステナイト相を呈し、これに
切断などの冷間加工を施すと組織の安定性が崩れて、一
部またはほとんどがマルテンサイト相に変態して、磁性
を帯びるものがあることが分かった。元々高い磁性を有
するステンレス鋼は元より、このような加工によって磁
性を帯びるステンレス鋼は、後述するように、カーテン
用ウェイトの材料として、好ましくないことが分かっ
た。However, even in the austenitic stainless steel, the structure is stable when the amount of Ni is large.
When a stainless steel with a small amount of solid solution is rapidly cooled after solution heat treatment, the structure exhibits an unstable quasi-austenite phase, and if cold working such as cutting is applied to it, the stability of the structure collapses and some or most of the martensite is martensitic. It turns out that some of them are transformed into a site phase and have magnetism. It was found that stainless steel, which originally has high magnetism, is not preferable as the material for the curtain weight, as will be described later.
【００１２】すなわち、カーテンは縫製後に、万一、カ
ーテン布地内に縫い針が残留していると、カーテンの包
装時、取り付け時、使用時などに、残留した縫い針によ
って、包装作業者、取り付け業者、使用者などを傷付け
る恐れがある。そのため、縫製後のカーテンに対して、
磁気センサによって、縫い針が残留していないかどうか
の検査を行なっている。In other words, if sewing needles remain in the curtain fabric after sewing, it is possible for the packaging operator to install the curtain by the remaining sewing needles during packaging, mounting, or use of the curtain. There is a risk of damaging the contractor or user. Therefore, for the curtain after sewing,
A magnetic sensor is used to check if there are any remaining sewing needles.
【００１３】ところが、磁性を有するステンレス鋼製の
ウェイトを採用すると、縫い針が残留していなくても、
磁気センサがステンレス鋼製ウェイトの磁性に反応し
て、縫い針検出信号を出力してしまうことが分かった。
また、加工前の状態では非磁性ないし磁気センサに反応
しない程度の低磁性を有するステンレス鋼であっても、
切断などの加工によってその結晶にすべりが生じて、加
工硬化を起すとともに磁性を帯びる場合があること、お
よび加工による磁性の帯びる強度は加工率に影響される
ことが分かった。However, if a magnetic weight made of stainless steel is adopted, even if the sewing needle does not remain,
It was found that the magnetic sensor outputs a sewing needle detection signal in response to the magnetism of the stainless steel weight.
In addition, even if the stainless steel has a non-magnetic property or a low magnetic property that does not react with the magnetic sensor in the state before processing,
It was found that the crystal may slip due to processing such as cutting to cause work hardening and become magnetized, and that the strength of magnetism due to processing is affected by the processing rate.
【００１４】したがって、本発明は、ステンレス鋼を用
いることによって、鉛製ウェイトのような毒性がなく、
しかも、切断などの加工を施されたものであっても、磁
性が磁気センサに反応しない一定レベル以下のカーテン
用ウェイトを提供することを目的とする。Therefore, according to the present invention, by using stainless steel, there is no toxicity unlike lead weights.
Moreover, it is an object of the present invention to provide a curtain weight whose magnetism does not react with a magnetic sensor and whose level is below a certain level even if it has been subjected to processing such as cutting.
【００１５】[0015]
【課題を解決するための手段】本発明の請求項１に記載
されたカーテン用ウェイトは、透磁率が１．０１μ以下
のステンレス鋼製であることを特徴とするものである。The curtain weight described in claim 1 of the present invention is characterized by being made of stainless steel having a magnetic permeability of 1.01 μ or less.
【００１６】ここで、「透磁率が１．０１μ以下のステ
ンレス鋼」なる用語は、もともと非磁性のステンレス
鋼、切断などの加工により磁性を帯びてもその透磁率が
１．０１μ以下のステンレス鋼、および加工によって透
磁率が１．０１μを超えてしまったものを焼き鈍すこと
によって透磁率を１．０１μ以下に低減したものなどを
含むことを意味するものである。Here, the term "stainless steel having a magnetic permeability of 1.01 μ or less" is originally a non-magnetic stainless steel, or a stainless steel having a magnetic permeability of 1.01 μ or less even if it is magnetized by processing such as cutting. , And that whose magnetic permeability is reduced to 1.01 μ or less by annealing those whose magnetic permeability exceeds 1.01 μ by processing.
【００１７】前記「加工」なる用語は、線材や板材など
を切断する切断加工、線材などをプレスして扁平化する
プレス加工などを含むものである。これらの加工におい
ては、その「加工率」によって透磁率の増大量が変化す
る。The term "working" includes cutting work for cutting a wire or plate, pressing work for pressing a wire, etc. to flatten it. In these processes, the amount of increase in magnetic permeability changes depending on the "process rate".
【００１８】「加工率」とは、例えば、切断加工であれ
ば、加工前の断面積（Ａ0）と加工後の断面積（Ａ1）の
差（Ａ0−Ａ1）を、加工前の断面積（Ａ0）で割った百
分率で表す。すなわち、加工率＝（Ａ0−Ａ1）／Ａ0×
１００％で表わされる。また、プレス加工であれば、プ
レス前の高さ寸法（Ｔ0）と加工後の高さ寸法（Ｔ1）差
（Ｔ0−Ｔ1）を、加工前の高さ寸法（Ｔ0）で割った百
分率で表す。すなわち、加工率＝（Ｔ0−Ｔ1）／Ｔ0×
１００％で表わされる。[0018] The "working rate", for example, if the cutting, the difference in cross-sectional area after processing and cross-sectional area before processing (A 0) (A 1) to (A 0 -A 1), before processing It is expressed as a percentage divided by the cross-sectional area (A 0 ). That is, processing rate = (A 0 −A 1 ) / A 0 ×
It is expressed as 100%. Further, in the case of press working, the height dimension (T 0 ) before pressing and the height dimension (T 1 ) after working (T 0 −T 1 ) are calculated by the height dimension (T 0 ) before working. Expressed as a percentage divided. That is, processing rate = (T 0 −T 1 ) / T 0 ×
It is expressed as 100%.
【００１９】ステンレス鋼線材を切断する場合の加工率
は、ほぼ２０％に相当するので、加工によって透磁率が
高くなる材質のステンレス鋼を用いる場合は、加工率２
０％時の透磁率が１．０１μ以下のステンレス鋼を用い
ればよい。この「透磁率が１．０１μ以下」の根拠は、
透磁率が１．０１μを超えると、ステンレス鋼に着磁性
が表れて、縫い針の残留検査で磁気センサが反応して、
誤った検出結果が得られる恐れがあるので、このような
誤動作を防止するためである。Since the processing rate when cutting a stainless steel wire corresponds to approximately 20%, when using stainless steel whose material has a high magnetic permeability, the processing rate is 2%.
A stainless steel having a magnetic permeability of 0% at 1.01 μ or less may be used. The basis of this "permeability is 1.01μ or less" is
When the magnetic permeability exceeds 1.01μ, the stainless steel appears magnetized and the magnetic sensor reacts in the residual inspection of the sewing needle,
This is to prevent such an erroneous operation because an erroneous detection result may be obtained.
【００２０】なお、磁気センサの感度を低下させれば、
より磁性の高いステンレス鋼でも磁気センンサに反応し
なくなるが、カーテン等ウェイトに比較して、遥かに小
体積の縫い針を磁気センサで検出することが困難になる
ことが分かった。If the sensitivity of the magnetic sensor is lowered,
It was found that even stainless steel, which is more magnetic, does not react to the magnetic sensor, but it is more difficult to detect a sewing needle with a much smaller volume than a weight such as a curtain with a magnetic sensor.
【００２１】上記のカーテン用ウェイトによれば、ステ
ンレス鋼製ウェイトであるから、鉛製ウェイトのような
毒性がなく、製造過程における衛生上の問題がないのみ
ならず、万一、廃棄されても環境を汚染することがない
ので環境汚染の問題がない。また、カーテン内にウェイ
トを縫い込んだ後に、磁気センサによる縫い針の残留検
査を実施しても、ウェイトの磁性が小さいために、磁気
センサが誤って縫い針の検出信号を発することがなく、
縫い針が残留している場合のみ、磁気センサが正確に反
応して、確実に縫い針の残留の有無を検出することがで
きる。According to the above-mentioned curtain weight, since it is a stainless steel weight, it is not toxic like lead weights and has no sanitary problems in the manufacturing process. There is no problem of environmental pollution because it does not pollute the environment. Even after the weight is sewn into the curtain, the magnetic sensor does not erroneously emit a sewing needle detection signal because the magnetism of the weight is small even if a residual needle inspection of the sewing needle is performed using a magnetic sensor.
Only when the sewing needle remains, the magnetic sensor accurately reacts, and it is possible to reliably detect whether or not the sewing needle remains.
【００２２】本発明の請求項２に記載のカーテン用ウェ
イトは、前記ステンレス鋼の材質が、窒素、モリブデン
および銅の群の中から選択された１種またはそれ以上を
含むか、ニッケルを１１％以上含むものであることを特
徴とするものである。In the curtain weight according to claim 2 of the present invention, the stainless steel material contains one or more selected from the group consisting of nitrogen, molybdenum and copper, or contains 11% nickel. It is characterized by including the above.
【００２３】上記の窒素、モリブデンおよび銅の群の中
から選択された１種またはそれ以上を含むステンレス鋼
によるカーテン用ウェイトによれば、窒素、モリブデン
および銅の添加によって組織が安定になって、常温時の
磁性が小さく抑えられるとともに、加工率２０％時の透
磁率が１．０１μ以下に抑えられて、磁気センサによる
縫い針の残留検査において、磁気センサが誤動作するこ
とがない。According to the curtain weight made of stainless steel containing one or more selected from the group of nitrogen, molybdenum and copper, the structure is stabilized by the addition of nitrogen, molybdenum and copper. The magnetism at room temperature is suppressed to a low level, and the magnetic permeability at a processing rate of 20% is suppressed to 1.01 μ or less, so that the magnetic sensor does not malfunction in the residual inspection of the sewing needle by the magnetic sensor.
【００２４】また、ニッケルの含有量が１１％以上のス
テンレス鋼によるカーテン用ウェイトによれば、安定な
組織のオーステナイト相が得られて、常温時の磁性が小
さく抑えられるとともに、加工率２０％時の透磁率が
１．０１μ以下に抑えられて、磁気センサによる縫い針
の残留検査において、磁気センサが誤動作することがな
い。Further, according to the curtain weight made of stainless steel having a nickel content of 11% or more, the austenite phase having a stable structure can be obtained, the magnetism at room temperature can be suppressed small, and the working rate at 20%. The magnetic permeability is suppressed to 1.01 μm or less, and the magnetic sensor does not malfunction in the residual inspection of the sewing needle by the magnetic sensor.
【００２５】本発明の請求項３に記載されたカーテン用
ウェイトは、ＳＵＳ３０３Ａ，ＳＵＳ３０３Ｃｕ，ＳＵ
Ｓ３０４Ｊ３，ＳＵＳ３０４Ｎ１，ＳＵＳ３０４Ｎ２，
ＳＵＳ３０４ＬＮ，ＳＵＳ３０５，ＳＵＳ３０５Ｊ１，
ＳＵＳ３０９Ｓ，ＳＵＳ３１０Ｓ，ＳＵＳ３１６，ＳＵ
Ｓ３１６Ｆ，ＳＵＳ３１６Ｌ，ＳＵＳ３１６Ｎ，ＳＵＳ
３１６ＬＮ，ＳＵＳ３１６Ｊ１，ＳＵＳ３１６Ｊ１Ｌ，
ＳＵＳ３１７，ＳＵＳ３１７Ｌ，ＳＵＳ３１７Ｊ１，Ｓ
ＵＳＸＭ７およびＮＳＳ２１−１０Ｍの群の中から選択
されたものであることを特徴とするものである。The weight for a curtain according to claim 3 of the present invention is SUS303A, SUS303Cu, SU.
S304J3, SUS304N1, SUS304N2
SUS304LN, SUS305, SUS305J1,
SUS309S, SUS310S, SUS316, SU
S316F, SUS316L, SUS316N, SUS
316LN, SUS316J1, SUS316J1L,
SUS317, SUS317L, SUS317J1, S
It is characterized by being selected from the group of USXM7 and NSS21-10M.
【００２６】なお、上記のＮＳＳ２１−１０Ｍは、窒素
を含む日新鋼業株式会社製ステンレス鋼の商品名であ
る。The NSS21-10M is a trade name of stainless steel manufactured by Nisshin Steel Co., Ltd. containing nitrogen.
【００２７】上記のＳＵＳ３０４Ｎ１，ＳＵＳ３０４Ｎ
２，ＳＵＳ３０４ＬＮ，ＮＳＳ２１−１０Ｍは、窒素を
０．１０〜０．３５％含む。The above-mentioned SUS304N1 and SUS304N
2, SUS304LN, NSS21-10M contains 0.10 to 0.35% of nitrogen.
【００２８】また、上記のＳＵＳ３１６，ＳＵＳ３１６
Ｆ，ＳＵＳ３１６Ｌ，ＳＵＳ３１７，ＳＵＳ３１７Ｌ，
ＳＵＳ３１７Ｊ１は、モリブデンを２．００〜６．００
％含む。Further, the above-mentioned SUS316, SUS316
F, SUS316L, SUS317, SUS317L,
SUS317J1 contains molybdenum from 2.00 to 6.00.
% Included.
【００２９】また、上記のＳＵＳ３０３Ａ，ＳＵＳ３０
３Ｃｕ，ＳＵＳ３０４Ｊ３，ＳＵＳＸＭ７は、銅を１．
００〜４．００％含む。In addition, the above-mentioned SUS303A, SUS30
3Cu, SUS304J3, SUSXM7 are copper 1.
Contains from 0.00 to 4.00%.
【００３０】さらに、上記のＳＵＳ３１６Ｎ，ＳＵＳ３
１６ＬＮは、窒素を０．１０〜０．２２％およびモリブ
デンを２．００〜３．００％含む。Further, the above-mentioned SUS316N, SUS3
16LN contains 0.10 to 0.22% nitrogen and 2.00 to 3.00% molybdenum.
【００３１】また、上記のＳＵＳ３１６Ｊ１，ＳＵＳ３
１６Ｊ１Ｌは、モリブデンを１．２０〜２．７５％およ
び銅を１．００〜２．５０％含む。The above-mentioned SUS316J1, SUS3
16J1L contains 1.20 to 2.75% molybdenum and 1.00 to 2.50% copper.
【００３２】さらにまた、上記のＳＵＳ３０５，ＳＵＳ
３０５Ｊ１，ＳＵＳ３０９Ｓ，ＳＵＳ３１０Ｓは、ニッ
ケッルを１０．５０〜２２．０％含む高ニッケルステン
レス鋼である。Furthermore, the above-mentioned SUS305, SUS
305J1, SUS309S and SUS310S are high nickel stainless steels containing 10.50 to 22.0% nickel.
【００３３】上記のステンレス鋼から選択されたカーテ
ン用ウェイトによれば、いずれも常温時の磁性が小さく
抑えられるとともに、加工率２０％時の透磁率が１．０
１μ以下に抑えられて、磁気センサによる縫い針の残留
検査において、磁気センサが誤動作することがない。According to the curtain weights selected from the above stainless steels, the magnetism at room temperature can be suppressed to be small, and the magnetic permeability at a working rate of 20% is 1.0.
It is suppressed to 1 μm or less, and the magnetic sensor does not malfunction in the residual inspection of the sewing needle by the magnetic sensor.
【００３４】なお、窒素を含有するステンレス鋼は、延
性の低下を抑えながら強度を高めることができるので、
ウェイトの傷や変形を防止できる。また、モリブデンを
含有するステンレス鋼は、ウェイトの耐食性や耐粒界腐
食性を向上できる。さらに、銅を含有するステンレス鋼
は、冷間加工性が向上するので、同一の加工率に対する
透磁率の増大を低く抑えられるとともに、耐硫性も向上
するので、温泉地などの硫黄成分の多い所での使用に適
している。したがって、上記の各種ステンレス鋼は、カ
ーテン用ウェイトの用途、すなわち、カーテンの使用場
所などによって、適宜、使い分ければよい。Since nitrogen-containing stainless steel can enhance the strength while suppressing the decrease in ductility,
It can prevent the weight from being damaged or deformed. Further, the stainless steel containing molybdenum can improve the corrosion resistance and intergranular corrosion resistance of the weight. Furthermore, since stainless steel containing copper has improved cold workability, the increase in magnetic permeability for the same workability can be suppressed to a low level, and the sulfur resistance is also improved, so there are many sulfur components in hot springs and the like. Suitable for local use. Therefore, the above-mentioned various stainless steels may be properly used depending on the use of the curtain weight, that is, the place of use of the curtain.
【００３５】本発明の請求項４に記載のカーテン用ウェ
イトの製造方法は、加工によって透磁率が１．０１μを
超えたステンレス鋼製カーテン用ウェイトを、焼き鈍し
によって透磁率を１．０１μ以下に低減することを特徴
とするものである。In the method for manufacturing a curtain weight according to claim 4 of the present invention, the stainless steel curtain weight having a magnetic permeability of more than 1.01μ by processing is annealed to reduce the magnetic permeability to 1.01μ or less. It is characterized by doing.
【００３６】上記のカーテン用ウェイトの製造方法によ
れば、いったん切断やプレスなどの加工により透磁率が
１．０１μを超えたステンレス鋼であっても、焼き鈍し
によって、加工時に生じた組織の変化が復元されて、透
磁率を１．０１μ以下に低減できるので、加工前のステ
ンレス鋼の選択範囲が広がり、上記の窒素、モリブデン
および銅などを含有するステンレス鋼や、高ニッケルス
テンレス鋼などの高価なステンレス鋼を採用しないで、
安価なステンレス鋼を採用できる。According to the above-described method of manufacturing a curtain weight, even if the stainless steel has a magnetic permeability of more than 1.01 μ due to processing such as cutting or pressing, the change in the structure caused during processing is caused by annealing. Since it is restored and the magnetic permeability can be reduced to 1.01μ or less, the selection range of the stainless steel before processing is widened, and the above-mentioned stainless steel containing nitrogen, molybdenum, copper, etc., or high-nickel stainless steel, etc. Do not adopt stainless steel,
Inexpensive stainless steel can be used.
【００３７】[0037]
【発明の実施の形態】以下、本発明のカーテン用ウェイ
トの実施形態に係るウェイトテープと、その製造方法例
について、図１〜図７を参照して説明する。BEST MODE FOR CARRYING OUT THE INVENTION A weight tape according to an embodiment of a curtain weight of the present invention and an example of a manufacturing method thereof will be described below with reference to FIGS.
【００３８】図1は本発明の実施形態に係るウェイトテ
ープ１の拡大断面図を示す。図１において、２は非磁性
ステンレス鋼製、または加工率２０％時の磁化率が１．
０１μ以下のステンレス鋼製、または焼き鈍しによって
透磁率が１．０１μ以下に低減されたステンレス鋼製ペ
レットで、図２（Ａ）に示すように、中心軸ｘが一直線
状の直円柱形状で、かつ、その両端部が垂直面２ａ，２
ｂに形成されている。このステンレス鋼製ペレット２は
布製などの柔軟性チュ−ブ３内に所定ピッチ間隔で収納
されている。FIG. 1 shows an enlarged sectional view of the weight tape 1 according to the embodiment of the present invention. In FIG. 1, 2 is made of non-magnetic stainless steel, or has a magnetic susceptibility of 1. when the processing rate is 20%.
A pellet made of a stainless steel of 01 μ or less, or a stainless steel having a magnetic permeability reduced to 1.01 μ or less by annealing, and having a straight axis of a straight line with a central axis x as shown in FIG. , Both ends of which are vertical surfaces 2a, 2
It is formed in b. The stainless steel pellets 2 are housed in a flexible tube 3 made of cloth or the like at a predetermined pitch.
【００３９】図３（Ａ）（Ｂ）は、上記のステンレス鋼
製ペレット２の製造方法について説明する工程図であ
る。すなわち、図３（Ａ）に示すように、適当な直径の
ステンレス鋼線材２０を用意し、このステンレス鋼線材
２０を適当な長さに切断して、図２（Ａ）に示すよう
な、ステンレス鋼製ペレット２を製造する。この切断
は、従来のような上歯と下歯を有する押し切り型の切断
具を使用しないで、例えば、鋸を使用する。実際には、
ステンレス鋼線材２０を１本ずつ切断しないで、多数の
ステンレス鋼線材２０を束ねて、一括して同時に切断す
ることが望ましい。このような鋸による切断では、加工
硬化はほとんど生じず、したがって、加工による透磁率
の増大を無視できる。3 (A) and 3 (B) are process drawings for explaining a method of manufacturing the above-mentioned stainless steel pellet 2. That is, as shown in FIG. 3A, a stainless steel wire rod 20 having an appropriate diameter is prepared, the stainless steel wire rod 20 is cut into an appropriate length, and the stainless steel wire rod as shown in FIG. The steel pellet 2 is manufactured. For this cutting, for example, a saw is used without using a conventional push-cut type cutting tool having upper and lower teeth. actually,
It is desirable to bundle a large number of stainless steel wire rods 20 and cut them all at once, instead of cutting the stainless steel wire rods 20 one by one. In such cutting with a saw, work hardening hardly occurs, and therefore, an increase in magnetic permeability due to work can be ignored.
【００４０】また、押し切り型の切断具を使用する場合
は、図３（Ａ）に示すように、適当な直径寸法のステン
レス鋼線材２０を用意し、このステンレス鋼線材２０を
１本ずつ押し切り型の切断具で適当な長さに切断して、
図３（Ｂ）に示すような、ステンレス鋼製ペレット２’
を製造する。When a push-cut type cutting tool is used, as shown in FIG. 3 (A), a stainless steel wire rod 20 having an appropriate diameter is prepared, and the stainless steel wire rods 20 are pushed one by one. Cut to an appropriate length with the cutting tool of
As shown in FIG. 3 (B), a stainless steel pellet 2 '.
To manufacture.
【００４１】前述のように、このステンレス鋼線材２０
の切断時の加工率はほぼ２０％程度であり、また、透磁
率が１．０１μを超えると着磁性を帯びるので、ステン
レス鋼線材２０の材質として、非磁性ステンレス鋼また
はこの切断による加工率ほぼ２０％時の透磁率が１．０
１μ以下となるステンレス鋼線材２０を採用する。As described above, this stainless steel wire rod 20
The processing rate at the time of cutting is about 20%, and if the magnetic permeability exceeds 1.01 μ, it is magnetized. Therefore, as the material of the stainless steel wire rod 20, non-magnetic stainless steel or a processing rate by this cutting is almost the same. Permeability at 20% is 1.0
A stainless steel wire rod 20 having a size of 1 μ or less is adopted.
【００４２】このようなステンレス鋼は、窒素，モリブ
デンおよび銅の群の中から選択された１種または２種以
上を含むステンレス鋼によって実現される。具体的に
は、日本工業規格のＳＵＳ３０３Ａ，ＳＵＳ３０３Ｃ
ｕ，ＳＵＳ３０４Ｎ１，ＳＵＳ３０４Ｎ２，ＳＵＳ３０
４ＬＮ，ＳＵＳ３０４Ｊ３，ＳＵＳ３０５，ＳＵＳ３０
５Ｊ１，ＳＵＳ３０９Ｓ，ＳＵＳ３１０Ｓ，ＳＵＳ３１
６，ＳＵＳ３１６Ｆ，ＳＵＳ３１６Ｌ，ＳＵＳ３１６
Ｎ，ＳＵＳ３１６ＬＮ，ＳＵＳ３１６Ｊ１，ＳＵＳ３１
６Ｊ１Ｌ，ＳＵＳ３１７，ＳＵＳ３１７Ｌ，ＳＵＳ３１
７Ｊ１，ＳＵＳＸＭ７の群の中から選択することによっ
て得られる。Such a stainless steel is realized by a stainless steel containing one or more selected from the group of nitrogen, molybdenum and copper. Specifically, Japanese Industrial Standards SUS303A, SUS303C
u, SUS304N1, SUS304N2, SUS30
4LN, SUS304J3, SUS305, SUS30
5J1, SUS309S, SUS310S, SUS31
6, SUS316F, SUS316L, SUS316
N, SUS316LN, SUS316J1, SUS31
6J1L, SUS317, SUS317L, SUS31
It is obtained by selecting from the group of 7J1 and SUSXM7.
【００４３】なお、ＳＵＳ３０３ＡはＪＩＳにはない
が、ＳＵＳ３０３の炭素（Ｃ）を０．１５％以下から
０．０８％以下に低減し、マンガン（Ｍｎ）を０．２０
％から０．２５％に増大するとともに、モリブデン（Ｍ
ｏ）を０．０６％以下および銅（Ｃｕ）を１．００〜
４．００％添加したものである。Although SUS303A is not in JIS, carbon (C) of SUS303 is reduced from 0.15% or less to 0.08% or less, and manganese (Mn) is 0.20.
% To 0.25%, and molybdenum (M
o) is 0.06% or less and copper (Cu) is 1.00 to 1.00
4.00% was added.
【００４４】また、上記のようなステンレス鋼は、オー
ステナイト相が安定な高ニッケルステンレス鋼であって
もよい。本発明において「高ニッケル」なる用語は、ニ
ッケルの含有量が１１％以上のものを意味する。The stainless steel as described above may be high nickel stainless steel having a stable austenitic phase. In the present invention, the term “high nickel” means a nickel content of 11% or more.
【００４５】このような高ニッケルステンレス鋼は、Ｓ
ＵＳ３０５，ＳＵＳ３０５Ｊ１，ＳＵＳ３０９Ｓ，ＳＵ
Ｓ３１０Ｓの中から選択することによって得られる。Such high nickel stainless steel is
US305, SUS305J1, SUS309S, SU
It is obtained by selecting from S310S.
【００４６】表１に、上記の各種ステンレス鋼の化学組
成を示し、図４に代表的なステンレス鋼の加工率と磁化
率・透磁率の関係図を示す。なお、表１および図４にお
いては、上記のステンレス鋼以外に、比較例として、窒
素、モリブデン、銅を含まないＳＵＳ３０４のニッケル
（Ｎｉ）成分を、ＪＩＳの範囲内（８．００〜１０．５
０％）で変化させた、ＳＵＳ３０４Ｈ（Ｎｉ：８．００
〜９．００％），ＳＵＳ３０４Ｍ（Ｎｉ：９．００〜１
０．００％），ＳＵＳ３０４Ｓ（Ｎｉ：１０．００〜１
０．５０％）を併せて示している。Table 1 shows the chemical compositions of the above various stainless steels, and FIG. 4 is a diagram showing the relationship between the workability and the magnetic susceptibility / permeability of typical stainless steels. In addition, in Table 1 and FIG. 4, in addition to the above-mentioned stainless steel, as a comparative example, a nickel (Ni) component of SUS304 containing no nitrogen, molybdenum, or copper was used within the range of JIS (8.00 to 10.5).
0%), SUS304H (Ni: 8.00)
~ 9.00%), SUS304M (Ni: 9.00-1)
0.00%), SUS304S (Ni: 10.00 to 1)
0.50%) is also shown.
【００４７】[0047]
【表１】 [Table 1]
【００４８】この表１および図４から明らかなように、
比較例である窒素、モリブデン、銅のいずれも含まない
ＳＵＳ３０４（ＳＵＳ３０４Ｈ，ＳＵＳ３０４Ｍ，ＳＵ
Ｓ３０４Ｓ）は、いずれも加工率２０％時の透磁率が
１．０１μを超えているのに対して、窒素（Ｎ）を０．
１０〜０．３５％含むＳＵＳ３０４Ｎ１およびＮＳＳ２
１−１０Ｍや、モリブデン（Ｍｏ）を２．００〜３．０
０％含むＳＵＳ３１６や、銅を１．００〜３．００％含
むＳＵＳ３０４Ｊ３においては、いずれも加工率２０％
時の透磁率が１．０１μを下回っている。As is clear from Table 1 and FIG.
Comparative example SUS304 (SUS304H, SUS304M, SU) containing neither nitrogen, molybdenum nor copper
S304S) has a magnetic permeability of more than 1.01 μ at a working rate of 20%, while nitrogen (N) is less than 0.
SUS304N1 and NSS2 containing 10 to 0.35%
1-10M or molybdenum (Mo) 2.00-3.0
In both SUS316 containing 0% and SUS304J3 containing 1.00 to 3.00% copper, the processing rate is 20%.
The magnetic permeability at that time is less than 1.01μ.
【００４９】このステンレス鋼線材２０を押し切り型の
切断具で切断した状態のステンレス鋼製ペレット２’
は、上記の鋸による切断と異なり、一部を歯で切り込む
とともに、残部を歯の押圧力で破断することによって切
断するものであるため、若干中心軸が曲がっている可能
性が高く、かつ、その両端部は、図３（Ｂ）に示すよう
に、切断面および破断面からなる異形状２ａ’，２ｂ’
をしている。This stainless steel wire rod 20 is a stainless steel pellet 2'cut with a push-cut type cutting tool.
Is different from the above saw cutting, in that a part is cut with teeth and the rest is broken by the pressing force of the teeth, so it is highly possible that the central axis is slightly bent, and As shown in FIG. 3 (B), both ends thereof have different shapes 2a ′ and 2b ′ composed of a cut surface and a fracture surface.
Are doing
【００５０】そのため、このステンレス鋼製ペレット
２’を柔軟性チューブ３内に収容してウェイトテープを
製作する際のステンレス鋼製ペレット２’の柔軟性チュ
ーブ３内への収納作業、およびこのウェイトテープをカ
ーテンの裾部に縫い込んだ後に、柔軟性チューブ３から
３〜４個のステンレス鋼製ペレット２’を抜き取って、
柔軟性チューブ３をカーテン地とともに折り返して縫製
する、始末作業時のステンレス鋼製ペレット２’の柔軟
性チューブ３からの抜き取り作業は、図９に示す従来の
ウェイトテープ６０と同様に、異形状２ａ’，２ｂ’部
分が柔軟性チューブ３の内面に引っ掛かるため困難であ
る。そこで、図３（Ｂ）のステンレス鋼製ペレット２’
の整形を行なう。Therefore, when the stainless steel pellet 2'is housed in the flexible tube 3 to produce a weight tape, the stainless steel pellet 2'is housed in the flexible tube 3 and the weight tape. After sewn into the hem of the curtain, pull out 3-4 stainless steel pellets 2'from the flexible tube 3,
As with the conventional weight tape 60 shown in FIG. 9, the operation of removing the stainless steel pellets 2 ′ from the flexible tube 3 when the flexible tube 3 is folded and sewn together with the curtain material and sewn at the time of the terminating work is performed with the irregular shape 2 a It is difficult because the ', 2b' portions are caught on the inner surface of the flexible tube 3. Therefore, the stainless steel pellet 2'of FIG.
Is shaped.
【００５１】このステンレス鋼製ペレット２’の整形に
は２種類ある。すなわち、第１の整形は、切断によって
ステンレス鋼製ペレット２’の中心軸が曲がっているの
を真っ直ぐにする軸心整形である。第２の整形は、ステ
ンレス鋼製ペレット２’の両端部を、例えば、垂直面に
する両端部整形である。There are two types of shaping of this stainless steel pellet 2 '. That is, the first shaping is axial centering that straightens the bent central axis of the stainless steel pellet 2'by cutting. The second shaping is shaping of both ends of the stainless steel pellet 2'to make vertical surfaces, for example.
【００５２】図５は、上記第１の軸心整形を行なう整形
機４０であって、定盤４１および往復動盤４２で構成さ
れており、定盤４１の上に多数のステンレス鋼製ペレッ
ト２’を横倒し状に並べて、その上から往復動盤４２を
適当な押圧力で押し当てて往復動作させることによっ
て、定盤４１および往復動盤４２の間でステンレス鋼製
ペレット２’を転動させて、その中心軸ｘを真っ直ぐに
整形するものである。FIG. 5 shows a shaping machine 40 for performing the first axial center shaping, which comprises a surface plate 41 and a reciprocating plate 42, on which a large number of stainless steel pellets 2 are formed. 'Is arranged sideways, and the reciprocating plate 42 is pressed against it with an appropriate pressing force to reciprocate to roll the stainless steel pellets 2'between the platen 41 and the reciprocating plate 42. Then, the central axis x is straightened.
【００５３】図６（Ａ）は、上記第２の整形を行なう両
端部整形機５０の一部を断面で示した正面図であり、下
研削盤５１および上研削盤５２で構成されている。図６
（Ｂ）は上研削盤５２を除いた平面図である。前述のよ
うにして、中心軸ｘが一直線状に整形されたステンレス
鋼製ペレット２’は、多数を倒立状にしてバインド線５
３によって括られている。なお、上記バインド線５３に
代えて、粘着テープを用いてもよいし、あるいは、各ス
テンレス鋼製ペレット２’，２’間をワックスなどの接
着剤で一時的に結合してもよい。あるいは、多数のステ
ンレス鋼製ペレット２’を円筒状などの枠内に詰め込ん
でもよい。FIG. 6 (A) is a front view showing a cross section of a part of the both-ends shaping machine 50 for performing the second shaping, which is composed of a lower grinding machine 51 and an upper grinding machine 52. Figure 6
(B) is a plan view of the upper grinding machine 52 removed. As described above, the stainless steel pellets 2 ′ having the central axis x shaped in a straight line are made up of a large number of inverted pellets 2 ′.
It is bounded by 3. Instead of the bind wire 53, an adhesive tape may be used, or the stainless steel pellets 2 ', 2'may be temporarily bonded with an adhesive such as wax. Alternatively, a large number of stainless steel pellets 2'may be packed in a cylindrical frame or the like.
【００５４】このステンレス鋼製ペレット２’をその両
端部を上下にして、下研削盤５１と上研削盤５２との間
に挟み込み、下研削盤５１と上研削盤５２とを互いに押
圧力を加えながら逆方向に回転させる。すると、各ステ
ンレス鋼製ペレット２’の両端部が下研削盤５１と上研
削盤５２とによって研削されて、前述の図２（Ａ）に示
すように、垂直面２ａ，２ｂに形成される。The stainless steel pellet 2'is sandwiched between the lower grinder 51 and the upper grinder 52 with both ends thereof facing up and down, and the lower grinder 51 and the upper grinder 52 are pressed against each other. While rotating in the opposite direction. Then, both ends of each of the stainless steel pellets 2'are ground by the lower grinder 51 and the upper grinder 52 to form vertical surfaces 2a and 2b as shown in FIG. 2 (A).
【００５５】ステンレス鋼製ペレット２は、従来の鉛製
ペレットに比較して毒性がなく、ステンレス鋼製ペレッ
ト２の製造工程での保険衛生上の問題点がないのみなら
ず、使用後にステンレス鋼製ペレット２が万一廃棄され
た場合でも、環境に悪影響を与えることがなく、環境保
護にもなる。The stainless steel pellets 2 are less toxic than the conventional lead pellets and have no health and hygiene problems in the manufacturing process of the stainless steel pellets 2. Even if the pellet 2 is discarded, it does not adversely affect the environment and protects the environment.
【００５６】また、ステンレス鋼製ペレット２を柔軟性
チューブ３内に収容する際には、ステンレス鋼製ペレッ
ト２の中心軸ｘが真っ直ぐであり、かつ、図３（Ｂ）に
示すような異形部２ａ’，２ｂ’が無いので、極めて容
易に収納することができ、ウェイトテープ1の製造時間
が著しく短縮できる。When accommodating the stainless steel pellets 2 in the flexible tube 3, the central axis x of the stainless steel pellets 2 is straight and the deformed portion as shown in FIG. Since there are no 2a 'and 2b', they can be stored very easily and the manufacturing time of the weight tape 1 can be significantly shortened.
【００５７】さらに、ステンレス鋼製ペレット２を柔軟
性チューブ３内に収容したウェイトテープ１をカーテン
の裾部に縫い込んだ後に、柔軟性チューブ３内から３〜
４個のステンレス鋼製ペレット２を抜き取る作業も、前
記同様に、ステンレス鋼製ペレット２の中心軸ｘが真っ
直ぐであり、かつ、図３（Ｂ）に示すような異形部２
ａ’，２ｂ’が無いので、極めて容易に行なうことがで
き、始末作業時間を著しく短縮できる。Furthermore, after the weight tape 1 containing the stainless steel pellets 2 accommodated in the flexible tube 3 is sewn into the hem of the curtain, the weight tape 1 is removed from inside the flexible tube 3 to 3 to 3.
Also in the work of extracting the four stainless steel pellets 2, the central axis x of the stainless steel pellets 2 is straight and the deformed portion 2 as shown in FIG.
Since there are no a'and 2b ', it can be performed extremely easily, and the time required for cleaning up can be significantly shortened.
【００５８】さらにまた、ステンレス鋼製ペレット２を
柔軟性チューブ３内に収容したウェイトテープ１をカー
テンの裾部に縫い込んでカーテンを完成した後に、磁気
センサによって縫い針の残留検査を実施しても、ステン
レス鋼製ペレット２の磁性が小さいために、磁気センサ
が誤動作することがない。Furthermore, after the weight tape 1 containing the stainless steel pellets 2 accommodated in the flexible tube 3 is sewn on the hem of the curtain to complete the curtain, the residual inspection of the sewing needle is performed by the magnetic sensor. However, since the magnetism of the stainless steel pellet 2 is small, the magnetic sensor does not malfunction.
【００５９】図７は上記のウェイトテープ１を取り付け
たレースカーテン１０の斜視図である。このウェイトテ
ープ１を使用したレースカーテン１０では、その裾部１
０ａが優美なウェーブを描いており、レースカーテン１
０本来の優美な雰囲気が確保されている。FIG. 7 is a perspective view of the lace curtain 10 to which the weight tape 1 is attached. In the lace curtain 10 using this weight tape 1, the hem 1
0a draws an elegant wave, and lace curtain 1
The original graceful atmosphere is secured.
【００６０】この理由は、前述のように、ステンレス鋼
製ペレット２の中心軸ｘが真っ直ぐな直円柱形状で、か
つ、その両端部が垂直面２ａ，２ｂに形成されているた
め、このステンレス鋼製ペレット２を収納したウェイト
テープ１にあっても、ステンレス鋼製ペレット２が一直
線状に並び、ウェイトテープ１として、長さ方向と直交
するあらゆる方向に対して、均等な屈曲性を有するた
め、レースカーテン１０のウェイトとして用いた場合
に、レースカーテン１０のウェ−ブに沿って自然な屈曲
をするためである。The reason for this is that, as described above, the stainless steel pellet 2 has the shape of a right circular cylinder with the central axis x being straight, and both end portions thereof are formed on the vertical surfaces 2a and 2b. Even in the weight tape 1 containing the pellets 2 made of stainless steel, since the pellets 2 made of stainless steel are aligned in a straight line and the weight tape 1 has uniform bendability in all directions orthogonal to the length direction, This is because when it is used as a weight of the lace curtain 10, it naturally bends along the wave of the lace curtain 10.
【００６１】このようなウェイトテープ１は、従来のよ
うな見苦しい不自然な曲がりが生じないので、図８に示
すように、巻取り具３０に巻き取った場合でも、ウェイ
トテープ１の曲がりがなく一直線状になり、隣接するウ
ェイトテープ１，１間の間隔寸法が一定になる。しか
も、隣接するウェイトテープ１，１相互間でステンレス
鋼製ペレット２，２のピッチ間隔の乱れも生じないの
で、美観が増し商取引上の商品価値が飛躍的に向上す
る。Since such a weight tape 1 does not have the unsightly and unnatural bending as in the conventional case, as shown in FIG. 8, even when wound on the winding tool 30, the weight tape 1 does not bend. The weight tapes 1 and 1 are in a straight line, and the distance between the adjacent weight tapes 1 is constant. Moreover, since the pitch interval between the stainless steel pellets 2 is not disturbed between the adjacent weight tapes 1 and 1, the appearance is increased and the commercial value of the commercial transaction is dramatically improved.
【００６２】なお、ステンレス鋼製ペレット２は、その
両端部を図２（Ａ）に示すように、垂直面２ａ，２ｂに
形成する場合のみならず、図２（Ｂ）に示すように、半
球面２ｃ，２ｄに形成してもよい。このような半球面２
ｃ，２ｄは、前記図５に示す整形機４０によるステンレ
ス鋼製ペレット２’の整形後、図示しないバレル研磨機
のバレル内に多数のステンレス鋼製ペレット２’を収容
してバレルを回転させて、ステンレス鋼製ペレット
２’，２’同士の共磨り、またはステンレス鋼製ペレッ
ト２’とともに適当な研磨剤を混入して研磨することに
よって、容易に形成することができる。The stainless steel pellet 2 is not limited to the case where both ends thereof are formed on the vertical surfaces 2a and 2b as shown in FIG. 2 (A), but also as shown in FIG. 2 (B). It may be formed on the surfaces 2c and 2d. Such a hemisphere 2
After shaping the stainless steel pellets 2 ′ by the shaping machine 40 shown in FIG. 5, c and 2 d are obtained by accommodating a large number of stainless steel pellets 2 ′ in the barrel of a barrel grinder (not shown) and rotating the barrel. , The stainless steel pellets 2 ′ and 2 ′ are co-polished, or the stainless steel pellets 2 ′ are mixed together with a suitable abrasive to be polished, whereby they can be easily formed.
【００６３】また、図示を省略するが、ステンレス鋼製
ペレット２の両端部は、上記の垂直面状および半球面状
に限られるものではなく、各種の対称形状にすることが
できる。例えば、図２（Ａ）の両端部が垂直面２ａ，２
ｂ状のステンレス鋼製ペレット２’に短時間のバレル研
磨を施すことによって、垂直面２ａ，２ｂの角部に面取
りを形成することができる。あるいは、テーパ状、台形
状、砲弾形状など、任意の対称形状になし得るものであ
る。Although not shown, both ends of the stainless steel pellet 2 are not limited to the above-mentioned vertical plane shape and hemispherical plane shape, but may be various symmetrical shapes. For example, both ends of FIG. 2 (A) have vertical surfaces 2a, 2
By chamfering the b-shaped stainless steel pellets 2 ′ for a short time, chamfers can be formed at the corners of the vertical surfaces 2a and 2b. Alternatively, it can be formed in any symmetrical shape such as a tapered shape, a trapezoidal shape, and a shell shape.
【００６４】さらに、上記実施形態は、カーテン用ウェ
イトテープについて説明したが、本発明はこのカーテン
用ウェイトテープに限定されるものではなく、カーテン
裾部の両側に縫い込む各種カーテン用ウェイトなどにも
適用できるものである。Further, although the above embodiment has been described with respect to the curtain weight tape, the present invention is not limited to this curtain weight tape, and may be applied to various curtain weights sewn on both sides of the curtain hem. It is applicable.
【００６５】[0065]
【発明の効果】本発明のカーテン用ウェイトは、カーテ
ンに取り付けられるウェイトにおいて、前記ウェイト
が、透磁率が１．０１μ以下のステンレス鋼製であるこ
とを特徴とするものであるから、従来の鉛製ウェイトに
比較して、毒性がないため製造過程での衛生上の問題点
がないのみならず、万一、廃棄されても環境汚染の問題
点がない。しかも、このカーテン用ウェイトをカーテン
生地に縫い込んだ後で、磁気センサによって縫い針の残
留検査を実施しても、磁気センサがステンレス鋼製ペレ
ットに反応して誤動作することがない。The curtain weight of the present invention is a weight attached to a curtain, characterized in that the weight is made of stainless steel having a magnetic permeability of 1.01 μ or less. Compared with weights made from plastics, they are not toxic and therefore not only have sanitary problems in the manufacturing process, but also have no environmental pollution problems if they are discarded. Moreover, even after the curtain weight is sewn into the curtain material and the residual inspection of the sewing needle is performed by the magnetic sensor, the magnetic sensor does not malfunction due to the reaction with the stainless steel pellet.
【図１】本発明のカーテン用ウェイトの一実施形態に係
るウェイトテープの拡大断面図である。FIG. 1 is an enlarged cross-sectional view of a weight tape according to an embodiment of a curtain weight of the present invention.
【図２】（Ａ）は図１のウェイトテープにおけるステン
レス鋼製ペレットの拡大断面図、（Ｂ）は他の実施形態
に係るステンレス鋼製ペレットの拡大断面図である。2A is an enlarged sectional view of a stainless steel pellet in the weight tape of FIG. 1, and FIG. 2B is an enlarged sectional view of a stainless steel pellet according to another embodiment.
【図３】（Ａ）はステンレス鋼製ペレットの製造工程を
説明するステンレス鋼線材の正面図、（Ｂ）はステンレ
ス鋼製ペレットの製造工程を説明する押し切り型の切断
具で切断したステンレス鋼製ペレットの断面図である。FIG. 3 (A) is a front view of a stainless steel wire rod explaining a manufacturing process of a stainless steel pellet, and FIG. 3 (B) is a stainless steel wire cut by a push-cut type cutting tool explaining a manufacturing process of a stainless steel pellet. It is sectional drawing of a pellet.
【図４】各種ステンレス鋼の加工率と磁化率・透磁率と
の関係図である。FIG. 4 is a diagram showing the relationship between the workability and the magnetic susceptibility / permeability of various stainless steels.
【図５】ステンレス鋼製ペレットの第１の整形工程につ
いて説明する軸心整形機の正面図である。FIG. 5 is a front view of an axial centering machine for explaining a first shaping step of stainless steel pellets.
【図６】（Ａ）は図２（Ａ）のステンレス鋼製ペレット
両端部における第２の整形工程について説明する両端部
整形機の正面図、（Ｂ）は（Ａ）において上研削盤を除
いた平面図である。6 (A) is a front view of a both-ends shaping machine for explaining a second shaping process at both ends of the stainless steel pellet of FIG. 2 (A), and FIG. 6 (B) is the same as FIG. FIG.
【図７】図１のウェイトテープを用いたレースカーテン
の斜視図である。FIG. 7 is a perspective view of a lace curtain using the weight tape of FIG.
【図８】図１のウェイトテープを巻取り具に巻き取った
状態の平面図である。FIG. 8 is a plan view showing a state where the weight tape shown in FIG. 1 is wound around a winding tool.
【図９】従来のウェイトテープの断面図である。FIG. 9 is a cross-sectional view of a conventional weight tape.
【図１０】従来のウェイトテープを縫い付けたレースカ
ーテンの斜視図である。FIG. 10 is a perspective view of a conventional lace curtain sewn with a weight tape.
【図１１】従来のウェイトテープにおける金属製ペレッ
トの拡大断面図である。FIG. 11 is an enlarged cross-sectional view of a metal pellet in a conventional weight tape.
【図１２】従来のウェイトテープを巻取り具に巻き取っ
た状態の平面図である。FIG. 12 is a plan view of a conventional weight tape wound on a winding tool.
１ カーテン用ウェイト（ウェイトテープ） ２、２’ ステンレス鋼製ペレット ２ａ，２ｂ 垂直面 ２ｃ，２ｄ 半球面 ３ 柔軟性チューブ １０ レースカーテン ２０ ステンレス鋼線材 ３０ 巻取り具 ４０ 軸心整形機 ５０ 両端部整形機 ｘ ステンレス鋼製ペレットの中心軸 1 Curtain weight (weight tape) 2, 2'stainless steel pellets 2a, 2b vertical plane 2c, 2d hemisphere 3 Flexible tube 10 lace curtains 20 stainless steel wire rod 30 Winding tool 40 axial centering machine 50 both ends shaping machine x Stainless steel pellet center axis
Claims (4)
いて、前記ウェイトが、透磁率が１．０１μ以下のステ
ンレス鋼製であることを特徴とするカーテン用ウェイ
ト。1. A weight attached to a curtain, wherein the weight is made of stainless steel having a magnetic permeability of 1.01 μ or less.
ブデンおよび銅の群の中から選択された１種またはそれ
以上を含むか、ニッケルを１１％以上含むものであるこ
とを特徴とする請求項１に記載のカーテン用ウェイト。2. The material of the stainless steel contains one or more selected from the group consisting of nitrogen, molybdenum and copper, or contains 11% or more of nickel. Curtain weight as described.
３Ａ，ＳＵＳ３０３Ｃｕ，ＳＵＳ３０４Ｊ３，ＳＵＳ３
０４Ｎ１，ＳＵＳ３０４Ｎ２，ＳＵＳ３０４ＬＮ，ＳＵ
Ｓ３０５，ＳＵＳ３０５Ｊ１，ＳＵＳ３０９Ｓ，ＳＵＳ
３１０Ｓ，ＳＵＳ３１６，ＳＵＳ３１６Ｆ，ＳＵＳ３１
６Ｌ，ＳＵＳ３１６Ｎ，ＳＵＳ３１６ＬＮ，ＳＵＳ３１
６Ｊ１，ＳＵＳ３１６Ｊ１Ｌ，ＳＵＳ３１７，ＳＵＳ３
１７Ｌ，ＳＵＳ３１７Ｊ１，ＳＵＳＸＭ７およびＮＳＳ
２１−１０Ｍの群の中から選択されたものであることを
特徴とする請求項１または２に記載のカーテン用ウェイ
ト。3. The material of the stainless steel is SUS30
3A, SUS303Cu, SUS304J3, SUS3
04N1, SUS304N2, SUS304LN, SU
S305, SUS305J1, SUS309S, SUS
310S, SUS316, SUS316F, SUS31
6L, SUS316N, SUS316LN, SUS31
6J1, SUS316J1L, SUS317, SUS3
17L, SUS317J1, SUSXM7 and NSS
21-10M The weight for curtains of Claim 1 or 2 selected from the group of 21-10M.
たステンレス鋼製カーテン用ウェイトを、焼き鈍しによ
って透磁率を１．０１μ以下に低減することを特徴とす
るカーテン用ウェイトの製造方法。4. A method for manufacturing a curtain weight, wherein the stainless steel curtain weight having a magnetic permeability of more than 1.01 μ by working is reduced to 1.01 μ or less by annealing.