JP2003176365A - Molded resin product - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a molded resin product expressing quite new design effect. <P>SOLUTION: The molded resin product is molded by injection molding a raw material comprising a pigment expressing interference colors by incident lights, a black and/or dark colored colorant and a polypropylene resin composition. The molded resin product expresses predetermined interference colors with the pigment by irradiating lights, is full of brilliance as a whole and expresses design effect quite different from that of conventional molded resin products. <P>COPYRIGHT: (C)2003,JPO

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、日用品として好適
な樹脂成形品に関するものであり、特にボールペン等の
文房具の様に手にとって使用し、且つ趣味的要素の強い
物品に適する樹脂成形品に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a resin molded product suitable for daily necessities, and more particularly to a resin molded product suitable for use in a hand such as a stationery such as a ballpoint pen and having a strong hobby element. Is.

【０００２】[0002]

【従来の技術】ボールペンの軸やキャップ等の文房具
は、ポリプロピレン樹脂やポリスチレン樹脂等の熱可塑
性樹脂を原料とする射出成形によって成形されることが
多い。実用的な面から見れば、文房具等の樹脂成形品
は、上記したポリプロピレン樹脂に老化防止剤等の機能
上必要な添加剤を加えて射出成形すれば十分な性能を発
揮する。しかしながらポリプロピレン樹脂は、本来、乳
白色半透明の樹脂でありポリスチレン樹脂は無色透明の
樹脂であるため、これらの樹脂をそのまま射出成形した
成形品は、意匠的な面白みに欠ける。2. Description of the Related Art A stationery such as a ball-point pen shaft or a cap is often formed by injection molding using a thermoplastic resin such as polypropylene resin or polystyrene resin. From a practical point of view, resin molded articles such as stationery exhibit sufficient performance if they are injection-molded by adding the above-mentioned polypropylene resin with additives necessary for functions such as an antioxidant. However, since polypropylene resin is originally a milky white translucent resin and polystyrene resin is a colorless and transparent resin, a molded article obtained by injection molding of these resins as they are lacks in design fun.

【０００３】そのため特に文房具等の手に取って使用す
る樹脂成形品においては、意匠的効果を発揮させるため
に、赤や青等の顔料を配合し、成形品を特定の色に着色
する等の手段が講じられる。また或いは、射出成形を行
う際の樹脂ペレットに、異なる色のものを混合し、成形
品の表面に流れ模様や斑模様を表出させる方法もある。
さらに他の方策として、アルミニウム等の金属粉を樹脂
に混合し、メタリック調の成形品に仕上げる方策が知ら
れている。Therefore, in particular, for resin molded articles such as stationery that are used by hand, in order to exert a design effect, pigments such as red and blue are blended to color the molded article in a specific color. Measures are taken. Alternatively, there is also a method in which resin pellets used for injection molding are mixed with different colors to expose a flow pattern or spot pattern on the surface of the molded product.
As another method, a method is known in which a metal powder such as aluminum is mixed with a resin to form a metallic-like molded product.

【０００４】[0004]

【発明が解決しようとする課題】樹脂成形品に意匠的面
白みを付加する方策としては、上記した様な特定の一色
に成形品を着色するか、斑模様にするといった方法、あ
るいはアルミニウム等の金属粉を配合する方法しか採用
されていない。そこで本発明は、全く新たな意匠効果を
発揮することができる樹脂成形品を提供することを目的
とするものである。As a measure for adding a design interest to a resin molded product, a method of coloring the molded product in one specific color as described above or forming a mottled pattern, or a metal such as aluminum. Only the method of mixing powder is adopted. Then, this invention aims at providing the resin molded product which can exhibit a completely new design effect.

【０００５】[0005]

【課題を解決するための手段】そして上記した課題を解
決するため、本出願人は先にガラスフレーク顔料を含有
した樹脂成形品を開発し、出願した（特願２０００−２
１９１８３号）。上記した樹脂成形品では、含有するガ
ラスフレーク顔料が入射光によって光の干渉を起こし、
特有の色や虹色に輝く。そのため樹脂成形品はキラキラ
と輝き、美しい。そして本出願人が、さらに研究を重ね
たところ、樹脂成形品の素地を黒色の着色すると反射光
や干渉光の輝きがさらに増すことが判明した。また樹脂
成形品の素地を暗色に着色しても同様の効果があること
が分かった。さらに顔料の発する干渉色と樹脂成形品の
素地を同系色にしても同様の効果があることが分かっ
た。また顔料が太陽光に対して緑色の干渉色を呈し、素
地が太陽光に対して緑色に発色するものである組み合わ
せの場合に特に輝きが増すことが分かった。さらに、樹
脂成型品の素地を透明あるいは半透明とすることによっ
ても、反射光や干渉光の輝きが増すことが判明した。In order to solve the above problems, the present applicant previously developed and applied for a resin molded product containing a glass flake pigment (Japanese Patent Application No. 2000-2).
19183). In the above-mentioned resin molded product, the glass flake pigment contained causes light interference by incident light,
Shines in a unique color or rainbow. Therefore, the resin molded product shines brightly and is beautiful. Further, the applicant of the present invention has conducted further research and found that if the base material of the resin molded product is colored black, the brightness of reflected light and interference light is further increased. It was also found that the same effect can be obtained by coloring the base material of the resin molded product in a dark color. Further, it has been found that the same effect can be obtained even if the interference color generated by the pigment and the base material of the resin molded product are similar colors. It has also been found that the combination of the pigment and the base material which exhibits a green interference color with respect to the sunlight and the substrate develops a green color with respect to the sunlight has a particularly high brightness. Furthermore, it has been found that the brilliance of reflected light and interference light is increased by making the base material of the resin molded product transparent or translucent.

【０００６】請求項１に記載の発明は、上記した知見に
基づくものであり、入射光に対して干渉色を呈する顔料
と、黒色の着色剤を含む樹脂組成物を成形してなること
を特徴とする樹脂成形品である。The invention according to claim 1 is based on the above-mentioned findings, and is characterized by being formed by molding a resin composition containing a pigment exhibiting an interference color with respect to incident light and a black colorant. It is a resin molded product.

【０００７】また黒色の着色剤はカーボンブラックであ
ることが望ましい（請求項３）。The black colorant is preferably carbon black (claim 3).

【０００８】本発明の樹脂成形品では、入射光に対して
干渉色を呈する顔料が配合されている。そのため本発明
の樹脂成形品は、顔料が輝いて見える。そして本発明の
樹脂成形品は、黒色の着色剤を含む。そのため顔料の輝
きが際立つ。この理由は、下記の通りであると予想され
る。すなわち本発明の樹脂成形品では、入射光に対して
干渉色を呈する顔料が配合されているが、光の干渉は、
顔料の表面及び内部の双方で反射が起こることによって
発生する。干渉色を呈する顔料は、一般に図１の様に基
礎となる物質５の表面に薄い皮膜７が設けられたもので
ある。入射光の一部は顔料自体の表面で反射する。また
他の入射光は顔料表面の皮膜を通過する。顔料表面の皮
膜を通過した光は、皮膜７と基礎物質５の間で反射する
（第１層間反射）。そして前記した表面反射と第１層間
反射が干渉し、干渉色が発生する。The resin molded product of the present invention contains a pigment exhibiting an interference color with respect to incident light. Therefore, in the resin molded product of the present invention, the pigment looks bright. The resin molded product of the present invention contains a black colorant. Therefore, the brightness of the pigment is outstanding. The reason for this is expected to be as follows. That is, in the resin molded product of the present invention, a pigment exhibiting an interference color with respect to incident light is mixed, but light interference is
It is caused by reflection occurring both on the surface and inside the pigment. A pigment exhibiting an interference color is generally one in which a thin film 7 is provided on the surface of a base substance 5 as shown in FIG. Part of the incident light is reflected by the surface of the pigment itself. Other incident light passes through the film on the surface of the pigment. The light that has passed through the coating on the surface of the pigment is reflected between the coating 7 and the basic substance 5 (first interlayer reflection). Then, the surface reflection and the first interlayer reflection interfere with each other to generate an interference color.

【０００９】またさらに光の一部は図１（ａ）（ｂ）の
様に基礎物質５の内部にも光が入り込み、基礎物質５の
裏面側と裏面側の皮膜７との境界部分で反射する（第２
層間反射）。さらに皮膜７の裏面側においても光が反射
する（裏面反射）。そして前記した第２層間反射と裏面
反射についても相互に干渉し、干渉光を発する。Further, part of the light also enters the inside of the basic substance 5 as shown in FIGS. 1 (a) and 1 (b), and is reflected at the boundary between the back surface of the basic material 5 and the film 7 on the back surface. Do (second
Interlayer reflection). Further, light is reflected also on the back surface side of the film 7 (back surface reflection). The above-mentioned second interlayer reflection and back surface reflection also interfere with each other and emit interference light.

【００１０】しかしながら実際上は、入射光の全てが前
記した「顔料自体の表面（表面反射）」「皮膜７と基礎
物質５の境界部（第１層間反射）」「基礎物質５の裏面
側と裏面側の皮膜７との境界部分（第２層間反射）」及
び「皮膜７の裏面側（裏面反射）」で反射し尽くされる
訳ではなく、多くの光が顔料を貫通する。そして樹脂内
の何らかの物質と衝突し、図１（ｂ）の様に反射（樹脂
内反射）が起きる。ところがこの顔料を通過した後に反
射した光（樹脂内反射）は、干渉には寄与しない。その
ためこの樹脂内反射光によって折角の干渉光がかき消さ
れ、干渉光の輝きが鈍いものとなってしまう。これに対
して請求項１に記載の発明では、樹脂成形品が黒色の着
色剤を含むものであるから、顔料を通過した光は樹脂中
に吸収され、反射しない。そのため本発明では、干渉を
妨げていた樹脂内反射光が減少し、干渉光の輝きが際立
つ。そのため本発明によると、従来技術の単一色の樹脂
成形品や、流れ模様の樹脂成形品とは明らかに異なる意
匠効果が得られる。However, in reality, all of the incident light is the above-mentioned "surface of the pigment itself (surface reflection)", "boundary between the film 7 and the basic substance 5 (first interlayer reflection)", "back side of the basic substance 5". The light is not completely reflected by the boundary portion (second interlayer reflection) with the coating 7 on the back surface side and the "back surface side (back surface reflection) of the coating 7", and a large amount of light penetrates the pigment. Then, it collides with some substance in the resin and reflection (reflection inside the resin) occurs as shown in FIG. However, the light reflected after passing through this pigment (reflection inside the resin) does not contribute to interference. Therefore, the reflected light in the resin obscures the interference light at a sharp angle, and the brightness of the interference light becomes dull. On the other hand, according to the first aspect of the invention, since the resin molded product contains the black colorant, the light passing through the pigment is absorbed in the resin and is not reflected. Therefore, in the present invention, the reflected light inside the resin that has interfered with the interference is reduced, and the brilliance of the interference light is outstanding. Therefore, according to the present invention, a design effect that is clearly different from the conventional single-color resin molded product and the flow pattern resin molded product can be obtained.

【００１１】請求項２に記載の発明は、入射光を反射す
る顔料と、黒色の着色剤とを含む樹脂組成物を成形して
なることを特徴とする樹脂成型品である。A second aspect of the present invention is a resin molded product obtained by molding a resin composition containing a pigment that reflects incident light and a black colorant.

【００１２】また、上記した樹脂成型品に含有される黒
色の着色剤には、カーボンブラックが好適に使用できる
（請求項３）。Further, carbon black can be suitably used as the black colorant contained in the above resin molded product (claim 3).

【００１３】本発明の樹脂成型品に含有されている顔料
は、入射光を反射するものであり光輝性を有する。ま
た、本発明の樹脂成型品は地色が黒色であるため、顔料
以外の場所に入射した光の大部分は、樹脂成型品自身に
吸収され、顔料の輝きを鈍化させない。即ち、本発明の
樹脂成型品は、顔料の輝きがひときわ強調されたもので
ある。従って、本発明の樹脂成型品は、従来の樹脂成型
品には見られない意匠効果を有する。The pigment contained in the resin molded product of the present invention reflects incident light and has glitter. Further, since the ground color of the resin molded product of the present invention is black, most of the light incident on a place other than the pigment is absorbed by the resin molded product itself and does not slow down the brilliance of the pigment. That is, in the resin molded product of the present invention, the brilliance of the pigment is remarkably emphasized. Therefore, the resin molded product of the present invention has a design effect that is not found in conventional resin molded products.

【００１４】また同様の目的を達成するための請求項４
に記載の発明は、入射光に対して干渉色を呈する顔料
と、暗色の着色剤を含む樹脂組成物を成形してなること
を特徴とする樹脂成形品である。A fourth aspect of the present invention for achieving the same object.
The invention described in (1) is a resin molded product obtained by molding a resin composition containing a pigment exhibiting an interference color with respect to incident light and a dark colorant.

【００１５】本発明の樹脂成形品では、暗色の着色剤を
含む樹脂組成物が使用されている。ここで「暗色」と
は、色の３属性である色相、彩度、明度の内、明度が低
いものを指し、彩度および色相はいかなるものであって
も良い。In the resin molded product of the present invention, a resin composition containing a dark colorant is used. Here, the “dark color” refers to one having a low lightness among the three attributes of color, hue, saturation, and lightness, and any color saturation and hue may be used.

【００１６】本発明の樹脂成形品についても、暗色の着
色剤によって干渉を妨げていた樹脂内反射光が減少し、
干渉光の輝きが際立つ。Also in the resin molded product of the present invention, the reflected light in the resin, which has interfered with the interference due to the dark colorant, is reduced,
The brightness of the interference light is outstanding.

【００１７】請求項５に記載の発明は、入射光を反射す
る顔料と、暗色の着色剤を含む樹脂組成物を成形してな
ることを特徴とする樹脂成形品である。According to a fifth aspect of the present invention, there is provided a resin molded product obtained by molding a resin composition containing a pigment that reflects incident light and a dark colorant.

【００１８】本発明の樹脂成形品に使用されている着色
剤は暗色であるため、入射光の大部分を吸収し、反射光
をほとんど出さない。一方、本発明の樹脂成型品に含有
されている顔料は、入射光を反射するものである。本発
明の樹脂成型品は地色が暗色であるため、顔料以外の場
所に入射した光の大部分は、樹脂成型品自身に吸収さ
れ、顔料の輝きを鈍化させない。即ち、本発明の樹脂成
型品は、顔料の輝きがひときわ強調されたものであり、
従来の樹脂成型品とは全く異なる意匠効果を有する。Since the colorant used in the resin molded product of the present invention is a dark color, it absorbs most of the incident light and emits almost no reflected light. On the other hand, the pigment contained in the resin molded product of the present invention reflects incident light. Since the ground color of the resin molded product of the present invention is dark, most of the light incident on a place other than the pigment is absorbed by the resin molded product itself and does not slow down the brilliance of the pigment. That is, the resin molded product of the present invention is one in which the brilliance of the pigment is remarkably emphasized,
It has a completely different design effect from conventional resin molded products.

【００１９】また請求項６に記載の発明は、入射光によ
って干渉色を呈する顔料と、前記干渉色との色相の相違
がマンセル表色法に基づく１００分割中の１０以内であ
る着色剤を含有する樹脂組成物を成形してなることを特
徴とする樹脂成形品である。The invention according to claim 6 includes a pigment exhibiting an interference color due to incident light, and a colorant having a hue difference with the interference color within 10 out of 100 divisions based on the Munsell color method. It is a resin molded product obtained by molding the resin composition.

【００２０】本発明の樹脂組成物についても、入射光に
よって干渉色を呈する顔料が配合されている。そして本
発明の樹脂組成物では、干渉色との色相の相違がマンセ
ル表色法に基づく１００分割中の１０以内である着色剤
も配合されている。すなわち樹脂成形物の全体が、干渉
色と同系色に着色されている。そのため干渉色の色彩が
周囲の地色に溶け込み、輝きだけが強調される。そのた
め本発明の樹脂成形物は、輝きが際立つ。The resin composition of the present invention is also blended with a pigment exhibiting an interference color by incident light. Further, in the resin composition of the present invention, a colorant having a hue difference from the interference color within 10 out of 100 divisions based on the Munsell color method is also blended. That is, the entire resin molded product is colored in a color similar to the interference color. Therefore, the color of the interference color blends with the surrounding ground color, and only the shine is emphasized. Therefore, the resin molded product of the present invention has outstanding brilliance.

【００２１】さらに請求項７に記載の発明は、太陽光に
対して緑色の干渉色を呈する顔料と、太陽光に対して緑
色に発色する着色剤を含む樹脂組成物を成形してなるこ
とを特徴とする樹脂成形品である。Further, the invention according to claim 7 is formed by molding a resin composition containing a pigment exhibiting a green interference color with respect to sunlight and a colorant which develops green with respect to sunlight. It is a characteristic resin molded product.

【００２２】本発明の樹脂成形品では、太陽光に対して
緑色の干渉色を呈する顔料が配合され、さらに樹脂の地
色が緑色に着色されている。すなわち樹脂成形物の全体
が、干渉色と同系色たる緑色に着色されている。そのた
め干渉色の色彩が周囲の地色に溶け込み、輝きだけが強
調される。そのため本発明の樹脂成形物は、輝きが際立
つ。In the resin molded product of the present invention, a pigment exhibiting a green interference color against sunlight is blended, and the background color of the resin is colored green. That is, the entire resin molded product is colored green, which is a color similar to the interference color. Therefore, the color of the interference color blends with the surrounding ground color, and only the shine is emphasized. Therefore, the resin molded product of the present invention has outstanding brilliance.

【００２３】請求項８に記載の発明は、入射光に対して
干渉色を呈する顔料を含有し、全体が透明あるいは半透
明であることを特徴とする樹脂成型品である。The invention described in claim 8 is a resin molded product characterized in that it contains a pigment exhibiting an interference color with respect to incident light, and is entirely transparent or semitransparent.

【００２４】本発明の樹脂成型品においても、入射光の
一部は樹脂表面近傍にある顔料に入射し、「顔料自体の
表面（表面反射）」「皮膜７と基礎物質５の境界部（第
１層間反射）」「基礎物質５の裏面側と裏面側の皮膜７
との境界部分（第２層間反射）」及び「皮膜７の裏面側
（裏面反射）」で反射した後、配合されている顔料に特
有の干渉色を呈する。Also in the resin molded product of the present invention, a part of the incident light is incident on the pigment in the vicinity of the surface of the resin, and "the surface of the pigment itself (surface reflection)""the boundary between the film 7 and the basic substance 5 (first 1 Interlayer reflection) "" Backside of basic substance 5 and backside coating 7 "
Boundary portion (2nd interlayer reflection) "and" back surface side of coating 7 (back surface reflection) ", and then exhibits an interference color peculiar to the blended pigment.

【００２５】一方、前記入射光の残部や顔料を透過した
光は、樹脂成型品の内部側にある顔料において反射さ
れ、特有の干渉色を有する反射光として樹脂成型品の外
部に放出される。本発明の樹脂成型品は、全体が透明あ
るいは半透明であるため、樹脂内における光の減衰が僅
かである。そのため、樹脂成型品の内部側の顔料におい
て反射され放出される干渉光は、樹脂表面近傍にある顔
料で発生した干渉光を増幅する。よって、本発明の樹脂
成型品は干渉色が鮮明であり、従来の樹脂成型品とは明
らかに異なる意匠効果を有する。On the other hand, the remainder of the incident light and the light that has passed through the pigment are reflected by the pigment inside the resin molded product and emitted to the outside of the resin molded product as reflected light having a specific interference color. The resin molded product of the present invention is transparent or translucent as a whole, so that light attenuation in the resin is slight. Therefore, the interference light reflected and emitted by the pigment on the inner side of the resin molded product amplifies the interference light generated by the pigment in the vicinity of the resin surface. Therefore, the resin molded product of the present invention has a clear interference color and has a design effect which is clearly different from that of the conventional resin molded product.

【００２６】請求項９に記載の発明は、入射光を反射す
る顔料を含有し、全体が透明あるいは半透明であること
を特徴とする樹脂成型品である。[0026] A ninth aspect of the present invention is a resin molded product, which contains a pigment that reflects incident light and is transparent or semitransparent as a whole.

【００２７】本発明の樹脂成型品は、全体が透明あるい
は半透明であるため、入射光は樹脂成型品の表面近傍に
ある顔料のみならず、樹脂成型品のの内部側にある顔料
にもほとんど減衰することなく到達できる。また、樹脂
成型品の内部側において反射した反射光も、ほとんど減
衰することなく樹脂成型品の外部に放出される。よっ
て、本発明の樹脂成型品は、不透明とした場合に比べて
光の反射に寄与する顔料の総表面積が大きく、反射光の
光量が多い。Since the resin molded product of the present invention is transparent or translucent as a whole, incident light is not only applied to the pigment in the vicinity of the surface of the resin molded product but also to the pigment on the inner side of the resin molded product. Can be reached without decay. Further, the reflected light reflected on the inner side of the resin molded product is emitted to the outside of the resin molded product with almost no attenuation. Therefore, in the resin molded product of the present invention, the total surface area of the pigment that contributes to the reflection of light is large and the amount of reflected light is large as compared with the case where the resin molded product is made opaque.

【００２８】上記した「入射光によって干渉色を呈する
顔料」としては、ガラスを金属及び／又は金属酸化物に
よって被覆したガラスフレーク顔料を使用することがで
きる（請求項１０）。As the above-mentioned "pigment exhibiting interference color by incident light", a glass flake pigment obtained by coating glass with a metal and / or a metal oxide can be used (claim 10).

【００２９】また顔料として無機物質を金属及び／又は
金属酸化物によって被覆した金属被覆無機顔料を使用す
ることもできる（請求項１１）。A metal-coated inorganic pigment obtained by coating an inorganic substance with a metal and / or a metal oxide may be used as the pigment (claim 11).

【００３０】また顔料として顔料は無機物質を金属及び
／又は金属酸化物と、有機顔料によって被覆した金属被
覆無機顔料を採用することもできる（請求項１２）。Further, as the pigment, a metal-coated inorganic pigment obtained by coating an inorganic substance with a metal and / or a metal oxide and an organic pigment can be adopted (claim 12).

【００３１】また顔料の被覆の厚さが干渉色を生じる厚
さであることが望ましい（請求項１３）。Further, it is desirable that the thickness of the pigment coating is a thickness that produces an interference color (claim 13).

【００３２】さらに顔料の被覆は光の一部が透過可能で
あることが望ましい（請求項１４）。Furthermore, it is desirable that the pigment coating allows a part of light to pass therethrough (claim 14).

【００３３】また樹脂成形品は、全体が半透明であって
も構わない（請求項１５）。The resin molded product may be semitransparent as a whole (Claim 15).

【００３４】顔料の平均粒径は、５．０〜５００μｍで
あることが推奨される。また顔料は樹脂組成物全量中に
１．０〜５．０重量％含まれることが望ましい（請求項
１６）。The average particle size of the pigment is recommended to be 5.0 to 500 μm. Further, it is desirable that the pigment is contained in an amount of 1.0 to 5.0% by weight in the total amount of the resin composition (claim 16).

【００３５】前記したガラスフレーク顔料や金属被覆無
機顔料などの顔料は、粒子が偏平形状を有し、個々にば
らつきを有する事が多い。このため、粒子の大きさを表
すには、平均の粒子径やメジアンの粒子径を用いるのが
適切である。本発明の樹脂成形品に含有される顔料の平
均粒径は５．０〜５００μｍが好適である。顔料の平均
粒径が５．０μｍ未満の場合は、フレーク粒子が小さす
ぎるため光輝性が劣る。また顔料の平均粒径が５００μ
ｍを超えると樹脂中への分散性が劣る。The pigments such as the glass flake pigments and the metal-coated inorganic pigments described above have flat particles and often have individual variations. Therefore, it is appropriate to use the average particle diameter or the median particle diameter to represent the particle size. The average particle size of the pigment contained in the resin molded product of the present invention is preferably 5.0 to 500 μm. When the average particle size of the pigment is less than 5.0 μm, the flake particles are too small and the glitter is poor. The average particle size of the pigment is 500μ
When it exceeds m, the dispersibility in the resin is poor.

【００３６】また前記した様に顔料は、樹脂成形品に使
用する樹脂組成物の全量中０．５〜１０．０重量％含ま
れていることが好ましい。顔料が樹脂組成物の全量中
０．５重量％未満の場合は光輝性が充分でない。顔料が
樹脂組成物の全量中１０．０重量％を超えると、樹脂の
流動性が劣り成形性が低下すると共に、樹脂成形品の全
域が顔料で埋まり、該顔料と着色剤の組み合わせにより
発現する意匠的効果が薄れてしまう。よって、顔料の最
適配合量は１．０〜５．０重量％である。As described above, the pigment is preferably contained in the resin composition used for the resin molded product in an amount of 0.5 to 10.0% by weight. When the amount of the pigment is less than 0.5% by weight based on the total amount of the resin composition, the luster is not sufficient. When the amount of the pigment exceeds 10.0% by weight based on the total amount of the resin composition, the fluidity of the resin is poor and the moldability is reduced, and the entire resin molded product is filled with the pigment, which is exhibited by the combination of the pigment and the colorant. The design effect is diminished. Therefore, the optimum blending amount of the pigment is 1.0 to 5.0% by weight.

【００３７】[0037]

【発明の実施の形態】本発明の樹脂成形品では、入射光
に対して干渉色を呈する顔料が及び特定の着色剤が配合
されている。入射光に対して干渉色を呈する顔料として
は、ガラスフレーク顔料や金属被覆無機顔料が知られて
いる。以下ガラスフレーク顔料と金属被覆無機顔料及び
着色剤について説明する。 （ガラスフレーク顔料）ガラスフレーク顔料は、金属又
は金属酸化物がガラスに被覆された鏡状の物体であり、
当該顔料は入射光に対して所定の干渉色でキラキラと輝
く顔料である。すなわち本発明で用いられるガラスフレ
ーク顔料は、フレーク状ガラスが金属又は金属酸化物な
どで被覆された構造からなり、光輝感を有する顔料とし
て定義される。ガラスフレーク顔料を含有する樹脂成形
物は、顔料の反射光が呈する光輝感に溢れた干渉色によ
り、独特の意匠効果を発揮する。BEST MODE FOR CARRYING OUT THE INVENTION The resin molded product of the present invention contains a pigment exhibiting an interference color with respect to incident light and a specific colorant. Glass flake pigments and metal-coated inorganic pigments are known as pigments that exhibit an interference color with respect to incident light. The glass flake pigment, the metal-coated inorganic pigment and the colorant will be described below. (Glass flake pigment) A glass flake pigment is a mirror-like object in which a metal or a metal oxide is coated on glass,
The pigment is a pigment that glitters with a predetermined interference color with respect to incident light. That is, the glass flake pigment used in the present invention is defined as a pigment having a brilliant sensation, which has a structure in which flaky glass is coated with a metal or a metal oxide. The resin molded product containing the glass flake pigment exhibits a unique design effect due to the interference color that is reflected by the pigment and is full of glitter.

【００３８】ガラスを被覆する金属あるいは金属酸化物
は銀、ニッケル、チタン、クロム、モリブデン、真鍮、
銀合金、酸化チタンなど、ガラス上に被覆した場合に入
射光に対して所定の干渉色の反射光を呈するものであれ
ばいかなるものであっても良い。また、金属あるいは金
属酸化物によるガラスの被覆は無電解メッキ法やスパッ
タリング法などいかなる手法を用いても良い。The metal or metal oxide coating the glass is silver, nickel, titanium, chromium, molybdenum, brass,
Any material such as silver alloy or titanium oxide may be used as long as it exhibits reflected light of a predetermined interference color with respect to incident light when it is coated on glass. Further, any method such as an electroless plating method or a sputtering method may be used for coating the glass with the metal or the metal oxide.

【００３９】上記したガラスフレーク顔料の内、ガラス
を被覆する金属が銀又はニッケルであるものは、特に光
の反射率が高く、輝きが強い。さらにガラスをチタンに
よって被覆した顔料は、光の干渉により入射光に対して
特有の色、又は虹色の干渉色を呈する。また、ガラスを
酸化チタンによって被覆した顔料は、特有の色あるいは
虹色の干渉色を呈する。また、上記した種々の顔料が発
する反射光は、ガラスの表面平滑性が高いため強く光輝
感がある。ガラスフレーク顔料の内でもガラスを銀やニ
ッケル、チタン、酸化チタンによって被覆したものは特
に光輝感が高く、当該ガラスフレーク顔料を含有する樹
脂成形品はより一層特異な意匠効果が得られる。Among the above-mentioned glass flake pigments, those in which the metal coating the glass is silver or nickel have particularly high light reflectance and strong brilliance. Further, the pigment obtained by coating the glass with titanium exhibits a unique color with respect to incident light or interference color of rainbow due to light interference. Further, a pigment obtained by coating glass with titanium oxide exhibits a unique color or an iridescent interference color. Further, the reflected light emitted by the above-mentioned various pigments has a strong glittering feeling because the surface smoothness of the glass is high. Among glass flake pigments, glass coated with silver, nickel, titanium, or titanium oxide has a particularly high glittering feeling, and a resin molded product containing the glass flake pigment has a more unique design effect.

【００４０】ガラスフレーク顔料の中で、フレーク状ガ
ラスが無電解メッキ法により金属で被覆されたものがあ
り、実例を挙げると、銀で被覆された日本板硝子株式会
社製の商品名「メタシャインRCFSX −5480PS」、「メタ
シャインRCFSX −5230PS」、「メタシャインRCFSX −51
50PS」（以上 同社コード９０２３〜９０２５）、「メ
タシャインRCFSX −5090PS02」、「メタシャインRCFSX
−5090PS06」、「メタシャインRCFSX −5030PS」があ
る。また同じく日本板硝子株式会社製であって、ニッケ
ルで被覆されたガラスフレーク顔料、商品名「メタシャ
インRCFSX −5480NS 又は同NB」、「メタシャインRCFS
X −5230NS 又は同NB」、「メタシャインRCFSX −5150
NS 又は同NB」、「メタシャインRCFSX −5090NS 又は
同NB」、「メタシャインRCFSX −5030NS 又は同NB」
（以上 同社コード９０４１〜９０４５ ９０５０〜９
０５４）が採用可能である。さらにチタンで被覆された
ガラスフレーク顔料、商品名「メタシャインRCFSX−509
0RC」（同社コード８０５２，８０５３ ８０６９〜８
０７１）が採用可能である。また、酸化チタンをフレー
ク状ガラスに被覆した顔料の一例として、商品名「メタ
シャインRC9555 又は同9548 又は同9548」Among the glass flake pigments, there is one in which flaky glass is coated with a metal by an electroless plating method. As an example, silver-coated glass manufactured by Nippon Sheet Glass Co., Ltd. under the trade name "Metashine RCFSX" is used. -5480PS, Metashine RCFSX-5230PS, Metashine RCFSX-51
50PS "(above company code 9023 to 9025)," Metashine RCFSX -5090PS02 "," Metashine RCFSX "
-5090PS06 "and" Metashine RCFSX-5030PS "are available. Also made by Nippon Sheet Glass Co., Ltd., a glass flake pigment coated with nickel, trade name "Metashine RCFSX-5480NS or NB", "Metashine RCFS".
X-5230NS or NB '', `` Metashine RCFSX-5150
NS or the same NB "," Metashine RCFSX-5090NS or the same NB "," Metashine RCFSX-5030NS or the same NB "
(Company code 9041 to 9045 9050 to 9
054) can be adopted. Glass flake pigment further coated with titanium, trade name "Metashine RCFSX-509
0RC "(Company code 8052, 8053 8069-8
071) can be adopted. In addition, as an example of a pigment in which flake glass is coated with titanium oxide, the trade name is "Metashine RC9555 or 9548 or 9548".

【００４１】また、フレーク状ガラスがスパッタリング
法により金属で被覆されたガラスフレーク顔料も使用す
ることができる。例えば、銀で被覆された東洋アルミニ
ウム社製の商品名「クリスタルカラーGF2125」、「クリ
スタルカラーGF2125−M 」、「クリスタルカラーGF214
0」、「クリスタルカラーGF2140−M 」がある。また、
ニッケル・クロム・モリブデンで被覆された同社製の商
品名「クリスタルカラーGF2525」、「クリスタルカラー
GF2525−M 」、「クリスタルカラーGF2540」、「クリス
タルカラーGF2540−M 」がある。また、真鍮で被覆され
た同社製の商品名「GF250 」、銀合金で被覆された同社
製の商品名「GF1345」、チタンで被覆された同社製の商
品名「GF1445」がある。なお、上記において金属あるい
は金属酸化物で表面が被覆されたガラスフレーク顔料と
して例示したものは、いずれも干渉効果があり、樹脂成
形品中で特有の色又は虹色に輝くが、より干渉効果の高
いガラスを酸化チタンによって被覆した顔料が本発明に
用いる顔料として好適である。Further, it is also possible to use a glass flake pigment in which a glass flake is coated with a metal by a sputtering method. For example, product names "Crystal Color GF2125", "Crystal Color GF2125-M", and "Crystal Color GF214" manufactured by Toyo Aluminum Co., Ltd., which are coated with silver.
0 "and" Crystal Color GF2140-M "are available. Also,
The product name "Crystal Color GF2525", which is coated with nickel, chromium and molybdenum, "Crystal Color"
GF2525-M "," Crystal Color GF2540 "and" Crystal Color GF2540-M "are available. In addition, there is a product name "GF250" manufactured by the company coated with brass, a product name "GF1345" manufactured by the company coated with silver alloy, and a product name "GF1445" manufactured by the company coated with titanium. Incidentally, those exemplified as the glass flake pigment whose surface is coated with a metal or a metal oxide in the above all have an interference effect, and shine in a peculiar color or a rainbow color in the resin molded product, but have a more interference effect. A pigment obtained by coating high glass with titanium oxide is suitable as the pigment used in the present invention.

【００４２】本発明ではガラスフレーク顔料の平均粒径
は５．０〜５００μｍが好適である。ガラスフレーク顔
料の平均粒径が５．０μｍ未満の場合は、フレーク粒子
が小さすきるため光輝性が劣り、また５００μｍを超え
ると樹脂中への分散性が劣る。In the present invention, the average particle size of the glass flake pigment is preferably 5.0 to 500 μm. When the average particle size of the glass flake pigment is less than 5.0 μm, the flake particles are small and the glitter is poor, and when it exceeds 500 μm, the dispersibility in the resin is poor.

【００４３】本発明のガラスフレーク顔料は、樹脂成形
品の成形に使用する樹脂組成物の全量中０．５〜２０．
０重量％含まれていることが好ましい。上記ガラスフレ
ーク顔料が樹脂組成物全量中０．５重量％未満の場合は
光輝性が充分でない。ガラスフレーク顔料が成形品を成
形する樹脂組成物の全量中２０．０重量％を超えると、
樹脂の流動性が劣り、成形性が低下する。ガラスフレー
ク顔料の最適配合量は１．０〜１０．０重量％である。
特に、樹脂成形品の透過性が要求される場合は、ガラス
フレーク顔料の最適配合量は更に低い値となる。則ち、
顔料が樹脂組成物の全量中１０．０重量％を超えると、
樹脂成形品の全域が顔料で埋まり透過性が低減する。顔
料の最適配合量は１．０〜５．０重量％である。The glass flake pigment of the present invention is 0.5 to 20.% of the total amount of the resin composition used for molding a resin molded product.
It is preferably contained in an amount of 0% by weight. If the glass flake pigment is less than 0.5% by weight in the total amount of the resin composition, the glitter is not sufficient. When the glass flake pigment exceeds 20.0% by weight in the total amount of the resin composition forming the molded article,
The fluidity of the resin is poor and the moldability is reduced. The optimum blending amount of the glass flake pigment is 1.0 to 10.0% by weight.
In particular, when the transparency of the resin molded product is required, the optimum blending amount of the glass flake pigment becomes a lower value. In other words,
When the pigment exceeds 10.0% by weight in the total amount of the resin composition,
The entire area of the resin molded product is filled with the pigment, and the permeability is reduced. The optimum blending amount of the pigment is 1.0 to 5.0% by weight.

【００４４】（金属被覆無機顔料）金属被覆無機顔料
は、無機物質を金属及び／又は金属酸化物によって被覆
したものである。金属被覆無機顔料は、光が入射すると
光輝性が高く干渉色を有する反射光を発する。よって前
記顔料を含有する樹脂成形物は、干渉色が際立ち、光輝
性に溢れた独特の意匠効果を有する。なお、無機物質の
表面を被覆する被覆面は、単層であっても２層以上の多
層であっても良い。被覆面が多層の場合は、各被覆面で
それぞれ干渉色を呈するため、干渉色がより一層強調さ
れる。(Metal-Coated Inorganic Pigment) The metal-coated inorganic pigment is an inorganic substance coated with a metal and / or a metal oxide. The metal-coated inorganic pigment emits reflected light having high interference and interference color when light enters. Therefore, the resin molded product containing the pigment has a unique design effect in which the interference color is conspicuous and the luster is overflowing. The coating surface for coating the surface of the inorganic substance may be a single layer or a multilayer of two or more layers. When the coating surface is a multi-layer, the interference color is further emphasized because each coating surface exhibits an interference color.

【００４５】前記金属被覆無機顔料に用いられる無機物
質には、雲母が好適に用いられる。また、前記無機物質
を被覆する金属及び／又は金属酸化物としては、チタン
や酸化チタン、酸化鉄などが好適に使用できる。特に雲
母を酸化チタンおよび酸化鉄で被覆した金属被覆無機顔
料は、酸化チタンにより形成される被覆面により、反射
光が干渉し特有の色あるいは虹色の干渉色を呈する。ま
た、前記顔料には酸化鉄により構成される被覆面が存在
するため、当該被覆面により前記干渉色がより一層強調
される。よって、前記顔料を含有する本発明の樹脂成形
品は、干渉色が強調され、光輝感に溢れたものである。Mica is preferably used as the inorganic substance used in the metal-coated inorganic pigment. Further, as the metal and / or metal oxide coating the inorganic substance, titanium, titanium oxide, iron oxide and the like can be preferably used. In particular, a metal-coated inorganic pigment obtained by coating mica with titanium oxide and iron oxide exhibits a unique color or an iridescent interference color due to interference of reflected light due to the coating surface formed of titanium oxide. Further, since the pigment has a coated surface composed of iron oxide, the interference color is further emphasized by the coated surface. Therefore, the resin-molded product of the present invention containing the pigment has an interference color emphasized and a glittering feeling.

【００４６】また金属被覆無機顔料の一種として、無機
物質を金属や金属酸化物の被覆層と有機顔料の被覆層を
有するものが知られている。As one type of metal-coated inorganic pigment, one having a coating layer of a metal or metal oxide and a coating layer of an organic pigment is known.

【００４７】金属酸化物等の被覆層と有機顔料の被覆層
を有する金属被覆無機顔料は、金属及び／又は金属酸化
物により構成される被覆面において、光輝性が高く特有
の干渉色の反射光を呈する。また、前記反射光は、有機
顔料により構成される被覆面により、さらに強調され
る。よって、本発明の樹脂成形品は、干渉色が際立ち光
輝感に溢れたものである。A metal-coated inorganic pigment having a coating layer of a metal oxide or the like and a coating layer of an organic pigment has a high brilliance on a coating surface composed of a metal and / or a metal oxide, and reflects light of a specific interference color. Present. Further, the reflected light is further emphasized by the coating surface composed of the organic pigment. Therefore, the resin molded product of the present invention has a remarkable interference color and a bright feeling.

【００４８】金属酸化物等の被覆層と有機顔料の被覆層
を有する金属被覆無機顔料においても、無機物質として
は雲母が好適である。また、特に雲母を酸化チタンおよ
び有機顔料によって被覆した金属被覆無機顔料は、酸化
チタンにより構成される被覆面が光輝性が高く特有の干
渉色の反射光を発し、有機顔料により構成される被覆面
が、前記反射光の干渉色をさらに強調する。よって、前
記顔料を含有する本発明の樹脂成形品は干渉色が際立ち
光輝感に溢れたものとなる。Mica is also suitable as the inorganic substance in the metal-coated inorganic pigment having a coating layer of a metal oxide or the like and a coating layer of an organic pigment. Further, in particular, a metal-coated inorganic pigment obtained by coating mica with titanium oxide and an organic pigment has a coating surface composed of titanium oxide, which has a high brilliance and emits reflected light of a specific interference color, and a coating surface composed of an organic pigment. Further enhances the interference color of the reflected light. Therefore, the resin molded product of the present invention containing the above-mentioned pigment has a strikingly bright glittering interference color.

【００４９】金属被覆無機顔料の中で、金属蒸着等で金
属及び又は金属酸化物が被覆された無機顔料として構成
されているものの実例を挙げれば、酸化鉄（III ）が被
覆されたアルミニウムがあり、例えばＢＡＳＦ株式会社
製の商品名「Paliocrom GoldL2000/L2002」、「Paliocr
om Gold L2020/L2022」、「Paliocrom Gold L2025」、
「Paliocrom Gold L2800」がある。また酸化鉄（III ）
が被覆された雲母を用いることができる。例えばＢＡＳ
Ｆ株式会社製の商品名「Paliocrom Red Gold L2500」、
「Paliocrom Red L4000」がある。また、アルミ−マ
ンガン被覆の雲母状酸化鉄（III ）を用いることができ
る。例えばＢＡＳＦ株式会社製の商品名「Paliocrom Co
pper L3000」及び「Paliocrom Copper L3001」がある。
また、還元二酸化チタンが被覆された雲母を用いること
ができる。例えばＢＡＳＦ株式会社製の商品名「Palioc
rom Blue Silver L6000 」、「Paliocrom BlueSilver L
6001 」がある。また、二酸化チタンが被覆された雲母
も用いることができる。Of the metal-coated inorganic pigments, examples of inorganic pigments coated with metals and / or metal oxides by metal vapor deposition include aluminum coated with iron (III) oxide. , For example, product name "Paliocrom Gold L2000 / L2002" manufactured by BASF Corporation, "Paliocr
om Gold L2020 / L2022 "," Paliocrom Gold L2025 ",
There is "Palioc rom Gold L2800". Also iron oxide (III)
Mica coated with can be used. For example BAS
Product name "Paliocrom Red Gold L2500" manufactured by F Co., Ltd.,
There is "Palioc rom Red L4000". Further, aluminum-manganese-coated mica-like iron oxide (III) can be used. For example, the product name "Paliocrom Co" manufactured by BASF Ltd.
There are "pper L3000" and "Paliocrom Copper L3001".
Further, mica coated with reduced titanium dioxide can be used. For example, the product name "Palioc" manufactured by BASF Ltd.
rom Blue Silver L6000, Paliocrom BlueSilver L
There is 6001 ". Further, mica coated with titanium dioxide can also be used.

【００５０】また、本発明の樹脂成形品に含有される顔
料として、還元二酸化チタンが被覆された雲母を用いる
ことができる。例えばＢＡＳＦ株式会社製の商品名「Pa
liocromBlueSilverL6000」、「PaliocromBlueSilverL60
01」がある。また、酸化チタンおよび酸化鉄によって雲
母を被覆した顔料である、エンゲルハード社製の商品名
「Santa Fe DesertBlush 」（同社コード ９３６２
Ｚ）、「Santa Fe Plum」（同社コード ９６６３
Ｚ）、「Santa Fe KiwiGreen 」（同社コード ９８６
２Ｚ）、「Santa Fe AdobeGreen」（同社コード ９８
６３Ｚ）などを用いることもできる。また、エンゲルハ
ード社製商品名「Dynacolor BB 」（同社コード ９６
３９ＺＢ１５Ｃ）、「Dynacolor GB 」（同社コード
９６３９ＺＧ７Ｃ）、「Dynacolor RB 」（同社コード
９６３９ＺＶ１９Ａ）などの酸化チタンおよび有機顔
料を雲母に被覆した顔料も本発明の樹脂成形品に含有さ
れる顔料として好適に使用できる。As the pigment contained in the resin molded product of the present invention, mica coated with reduced titanium dioxide can be used. For example, the product name "Pas manufactured by BASF Ltd.
liocromBlueSilverL6000, PaliocromBlueSilverL60
There is 01 ”. In addition, a pigment whose mica is coated with titanium oxide and iron oxide, manufactured by Engelhard Co., Ltd. under the trade name “Santa Fe Desert Blush” (Company code 9362).
Z), "Santa Fe Plum" (company code 9663
Z), "Santa Fe KiwiGreen" (company code 986)
2Z), "Santa Fe Adobe Green" (Company code 98
63Z) can also be used. In addition, Engelhard's product name "Dynacolor BB" (Company code 96
39ZB15C), "Dynacolor GB" (Company code
Pigments in which titanium oxide and organic pigments are coated with mica, such as 9639ZG7C) and "Dynacolor RB" (Company code 9639ZV19A), can be preferably used as the pigment contained in the resin molded product of the present invention.

【００５１】上記の金属被覆無機顔料の平均粒径も、ガ
ラスフレーク顔料と同様に、５．０〜５００μｍが好適
である。平均粒径が５．０μｍ未満の場合は、上記の無
機顔料粒子が小さ過ぎるため光輝性が劣り、また５００
μｍを超えると樹脂中への分散性が劣る。The average particle size of the above-mentioned metal-coated inorganic pigment is preferably 5.0 to 500 μm, like the glass flake pigment. If the average particle size is less than 5.0 μm, the above-mentioned inorganic pigment particles are too small and the glittering property is inferior.
If it exceeds μm, the dispersibility in the resin is poor.

【００５２】金属被覆無機顔料の配合量も、ガラスフレ
ーク顔料と同様に、樹脂成形品を成形する樹脂組成物の
全量中０．５〜２０．０重量％含まれていることが好ま
しい。上記の無機顔料が樹脂組成物の全量中０．５重量
％未満の場合は光輝性が充分でない。上記の無機顔料が
樹脂組成物の全量中２０．０重量％を超えると、樹脂の
流動性が劣り、成形性が低下する。上記の金属被覆無機
顔料の最適配合量は１．０〜１０．０重量％である。ま
た、樹脂成形品の透過性が要求される場合は、金属被覆
無機顔料の最適配合量は更に低い値となる。則ち、顔料
が樹脂組成物の全量中１０．０重量％を超えると、樹脂
成形品の全域が顔料で埋まり透過性が低減する。金属被
覆無機顔料の最適配合量は１．０〜５．０重量％であ
る。As with the glass flake pigment, the metal-coated inorganic pigment is preferably contained in an amount of 0.5 to 20.0% by weight based on the total amount of the resin composition for molding the resin molded article. When the amount of the above-mentioned inorganic pigment is less than 0.5% by weight in the total amount of the resin composition, the luster is not sufficient. When the above-mentioned inorganic pigment exceeds 20.0% by weight in the total amount of the resin composition, the fluidity of the resin is poor and the moldability is deteriorated. The optimum compounding amount of the above metal-coated inorganic pigment is 1.0 to 10.0% by weight. When the resin molded product is required to have transparency, the optimum blending amount of the metal-coated inorganic pigment becomes a lower value. That is, when the pigment exceeds 10.0 wt% in the total amount of the resin composition, the entire area of the resin molded product is filled with the pigment, and the permeability is reduced. The optimum amount of the metal-coated inorganic pigment is 1.0 to 5.0% by weight.

【００５３】（金属粉・金属被覆膜）入射光に対して反
射光を呈する金属粉も、本発明の樹脂成型品に配合する
顔料として使用できる。具体的には、アルミニウム、
銀、ニッケル、チタン、クロム、モリブデン、真鍮、銀
合金などが挙げられ、そのうちでもアルミニウムが最も
好適に使用できる。なお、金属粉はいかなる形状を有し
ていても良いが、光の反射面積をより多くすべくフレー
ク状とすることが好ましい。また、表面が鏡面加工され
るとともに、染料などで着色された金属粉は、一層強い
光輝感が得られる。本発明に用いる金属粉の一例とし
て、尾池工業製の商品名「エルジー」シリーズの品番H2
5 のsilver、同品番DG Gold 、同品番Green 、同品番Bl
ue、同品番Red 、同品番Maroon、同品番Black などが例
示できる。(Metallic Powder / Metal Covering Film) Metallic powder that exhibits reflected light with respect to incident light can also be used as a pigment to be added to the resin molded product of the present invention. Specifically, aluminum,
Examples thereof include silver, nickel, titanium, chromium, molybdenum, brass and silver alloy, and among them, aluminum can be most preferably used. The metal powder may have any shape, but it is preferable that the metal powder has a flake shape so as to increase the light reflection area. In addition, the surface of the metal powder is mirror-finished, and the metal powder colored with a dye or the like gives a stronger glittering feeling. As an example of the metal powder used in the present invention, part number H2 of the product name “ELGY” series manufactured by Oike Kogyo Co., Ltd.
5 silver, same part number DG Gold, same part number Green, same part number Bl
Examples include ue, the same product number Red, the same product number Maroon, and the same product number Black.

【００５４】また、入射光に対して反射光を呈する金属
を被覆したフィルムも、本発明の樹脂成型品に配合する
顔料として使用できる。フィルムに被覆する金属として
は、アルミニウム、銀、ニッケル、チタン、クロム、モ
リブデン、真鍮、銀合金などが挙げられ、そのうちでも
アルミニウムが最も好適に使用できる。本発明に用いる
金属被覆膜の一例として、尾池工業性の商品名「エルジ
ー#500」などが例示できる。A film coated with a metal exhibiting reflected light with respect to incident light can also be used as a pigment to be incorporated in the resin molded product of the present invention. Examples of the metal with which the film is coated include aluminum, silver, nickel, titanium, chromium, molybdenum, brass, and silver alloy, and among these, aluminum can be most preferably used. As an example of the metal coating film used in the present invention, the product name “ELGY # 500” manufactured by Oike Kogyo Co., Ltd. can be exemplified.

【００５５】（着色剤）本発明の樹脂成形品に用いる着
色剤は、当該樹脂成形品に含有される顔料が入射光によ
り発する干渉色と同系統の色相、すなわち当該干渉色と
の色相の相違がマンセル表色法に基づく１００分割中の
１０以内の色相を有するものとすることができる。一例
として、太陽光が入射光である時、緑色の色相を呈する
着色剤として、Ｃ．Ｉ．ＧＮ Pigment Green-7 があ
る。また、同様に黒色の色相を呈する着色剤として、
Ｃ．Ｉ．ＧＮ Pigment Black-7 やＣ．Ｉ．ＧＮ Pigm
ent Black-28がある。(Colorant) The colorant used in the resin molded product of the present invention has the same hue as that of the interference color generated by the incident light of the pigment contained in the resin molded product, that is, the difference in hue from the interference color. Can have a hue within 10 of 100 divisions based on the Munsell color method. As an example, as a colorant exhibiting a green hue when sunlight is incident light, C.I. I. There is GN Pigment Green-7. In addition, as a colorant that similarly exhibits a black hue,
C. I. GN Pigment Black-7 and C.I. I. GN Pigm
There is ent Black-28.

【００５６】本発明に採用される樹脂としては、射出成
形や押し出し成形が可能な熱可塑性樹脂のいずれもが使
用可能である。具体的には、ポリエチレン樹脂、ポリプ
ロピレン樹脂、ポリスチレン樹脂、ＡＢＳ樹脂、メタク
リル樹脂、塩化ビニール樹脂、ポリエチレンテレフタレ
ート樹脂、ポリブチレンテレフタレート樹脂、ＡＳ樹
脂、ＥＶＡ樹脂、セルロースアセテート樹脂、ポリカー
ボネート樹脂、ポリアミド樹脂、ポリアセタール樹脂、
変成ポリフェニレンオキサイド樹脂、ポリサンフォン樹
脂等が挙げられる。As the resin used in the present invention, any of thermoplastic resins capable of injection molding and extrusion molding can be used. Specifically, polyethylene resin, polypropylene resin, polystyrene resin, ABS resin, methacrylic resin, vinyl chloride resin, polyethylene terephthalate resin, polybutylene terephthalate resin, AS resin, EVA resin, cellulose acetate resin, polycarbonate resin, polyamide resin, polyacetal. resin,
Modified polyphenylene oxide resin, polysanfon resin and the like can be mentioned.

【００５７】（その他の添加物）なお、本発明において
はその他必要に応じて、成形する樹脂組成物中に耐候性
安定剤、耐熱安定剤、帯電防止剤、発泡剤、離型剤、滑
剤、核剤、可塑剤、老化防止剤、塩酸吸収剤、酸化防止
剤等を添加することができる。また他の顔料を添加する
こともできる。(Other Additives) In the present invention, if necessary, in the resin composition to be molded, a weather resistance stabilizer, a heat resistance stabilizer, an antistatic agent, a foaming agent, a release agent, a lubricant, Nucleating agents, plasticizers, antioxidants, hydrochloric acid absorbents, antioxidants and the like can be added. Further, other pigments can be added.

【００５８】[0058]

【実施例】（実施例１）樹脂としてポリプロピレン（商
品名 MG03B 日本ポリケム株式会社製）を採用し、こ
の樹脂に全体の１重量％に相当する酸化チタン被覆ガラ
スフレーク顔料（商品名 メタシャインRCFSX-5090RC
品番8069 日本板硝子株式会社製、チタン被覆 平均粒
径約９０μｍ）および黒色の着色剤（Ｃ．Ｉ．ＧＮ Pi
gment Black-7 ）を配合し、これを計量後ブレンダーで
混合し、さらに押出機で溶融混練りしてペレット化し
た。そしてさらにこれを射出成形して、図２に示すよう
にボールペンのキャップ３と本体軸４を成形した。なお
ボールペンの本体軸４とは、インキが充填されるインキ
芯３の外側に配される部材であり、筆記の際に使用者が
手で保持する部材である。成形したボールペンのキッャ
プ３及び本体軸４は、具体的にはサクラクレパス製「ボ
ールサイン」（商品名）であり、キャップ３の頂部は球
面状をしている。Example 1 Polypropylene (trade name MG03B manufactured by Nippon Polychem Co., Ltd.) was adopted as a resin, and 1% by weight of the whole resin was coated with titanium oxide-coated glass flake pigment (trade name Metashine RCFSX-). 5090RC
Product number 8069, manufactured by Nippon Sheet Glass Co., Ltd., titanium coating, average particle size of about 90 μm, and black colorant (CIGN Pi)
gment Black-7) was blended, measured, mixed with a blender, and melt-kneaded with an extruder to form pellets. Then, this was further injection-molded to mold the cap 3 and the main body shaft 4 of the ball-point pen as shown in FIG. The main body shaft 4 of the ball-point pen is a member arranged outside the ink core 3 filled with ink, and is a member held by a user by hand during writing. The cap 3 and the main body shaft 4 of the molded ballpoint pen are specifically "Ballsign" (trade name) made by Sakura Crepas, and the top of the cap 3 is spherical.

【００５９】キャップ３及び本体軸４を光が反射する方
向から見たとき、干渉により無数の微小で点状の輝きが
認められ、従来の樹脂成形品よりも金属的でつややかな
な光沢を有するものであった。When the cap 3 and the main body shaft 4 are viewed from the direction in which light is reflected, an infinite number of minute, point-like shines are recognized due to interference, and they have a more metallic and glossy luster than conventional resin molded products. It was a thing.

【００６０】（実施例２）実施例１において、ガラスフ
レーク顔料を変えて、前記と同様のキッャプ３と本体軸
４を射出成形した。使用した顔料はガラスフレーク顔料
（商品名 RCFSX5090RC 品番８０５２ 日本板硝子株
式会社製、チタン被覆 平均粒径約９０μｍ）である。
また、着色剤は黒色を呈するＣ．Ｉ．ＧＮ Pigment Bl
ack-7 である。この例では、キャップ３及び本体軸４を
光が反射する方向から見たとき、無数の微小な金色の点
の輝きが認められ、従来の樹脂成形品に比べ干渉色が際
立ち光輝感に溢れたものであった。前記実施例１と輝き
の色が異なって見えるのは、ガラスフレーク顔料のチタ
ンの被覆厚さが異なるためである。前記したように本発
明は光の干渉を利用している。則ち、ガラスフレークに
被覆するチタンの厚さを変えることにより、干渉によっ
て増強される波長が異なり、これによって違った色相に
輝くものである。(Example 2) The cap 3 and the main body shaft 4 similar to those described above were injection molded by changing the glass flake pigment in Example 1. The pigment used was a glass flake pigment (trade name: RCFSX5090RC, product number 8052, manufactured by Nippon Sheet Glass Co., Ltd., titanium-coated average particle size of about 90 μm).
Further, the colorant is C.I. I. GN Pigment Bl
It is ack-7. In this example, when the cap 3 and the main body shaft 4 are viewed from the direction in which light is reflected, innumerable minute gold-colored spots are recognized, and the interference color is more prominent and brighter than the conventional resin molded product. It was a thing. The brilliant color looks different from that of Example 1 because the coating thickness of titanium of the glass flake pigment is different. As described above, the present invention utilizes light interference. That is, by changing the thickness of titanium coated on the glass flakes, the wavelength enhanced by interference is different, which causes different hues to shine.

【００６１】（実施例３）樹脂としてポリプロピレン
（商品名 MG03B 日本ポリケム株式会社製）を採用
し、この樹脂に全体の１重量％に相当する酸化チタンお
よび酸化鉄を雲母に被覆した顔料（商品名 Santa Fe
9863Z エンゲルハード社製、平均粒径約１７μｍ）お
よび黒色の着色剤Ｃ．Ｉ．ＧＮ Pigment Black-7 を配
合し、これを計量後ブレンダーで混合し、さらに押出機
で溶融混練りしてペレット化した。そしてさらにこれを
射出成形して前記実施例１と同様に図２に示すようなボ
ールペンのキャップ３と本体軸４を成形した。Example 3 Polypropylene (trade name MG03B manufactured by Nippon Polychem Co., Ltd.) was used as a resin, and a pigment (trade name) obtained by coating mica with titanium oxide and iron oxide corresponding to 1% by weight of the whole resin was used. Santa Fe
9863Z Engelhard Co., average particle size of about 17 μm) and black colorant C.I. I. GN Pigment Black-7 was blended, weighed and mixed with a blender, and further melt-kneaded with an extruder to form pellets. Then, this was injection-molded to form the ball-point pen cap 3 and the main body shaft 4 as shown in FIG.

【００６２】本実施例のキャップ３および本体軸４に
は、酸化チタンおよび酸化鉄を雲母に被覆した顔料が無
数に散りばめられている。本実施例において用いられた
前記顔料は、干渉色が緑色の顔料であり、光を照射する
と反射光が干渉し、きらきらとした光輝性の高い光を発
する。そのため、キャップ３や本体軸４を光が反射する
方向から見ると、全体的に干渉色が緑で金属的であり、
従来の樹脂成形品に比べてつややかな光沢を呈する。In the cap 3 and the main body shaft 4 of this embodiment, innumerable pigments in which mica is coated with titanium oxide and iron oxide are scattered. The pigment used in this example is a pigment having an interference color of green, and when it is irradiated with light, the reflected light interferes with each other and emits a glittering and highly glittering light. Therefore, when the cap 3 and the main body shaft 4 are viewed from the direction in which light is reflected, the overall interference color is green and metallic,
It has a more glossy luster than conventional resin molded products.

【００６３】（実施例４）さらに前記した実施例２と同
様に、樹脂および黒色の着色剤は変更せず、顔料の種類
のみを酸化チタンおよび酸化鉄を雲母に被覆した顔料
（商品名 Santa Fe9663Z エンゲルハード社製、平均
粒径約１７μｍ）に変更し、図２に示すようなボールペ
ンのキャップ３と本体軸４を成形した。(Example 4) Further, as in the case of Example 2 described above, the resin and the black colorant were not changed, and only pigments of titanium oxide and iron oxide were coated with mica (trade name: Santa Fe9663Z). The average particle size was about 17 μm manufactured by Engelhard Co., Ltd., and the cap 3 and the main body shaft 4 of the ballpoint pen as shown in FIG. 2 were molded.

【００６４】本実施例のキャップ３および本体軸４も、
前記実施例２と同様に酸化チタンおよび酸化鉄を雲母に
被覆した顔料が無数に散りばめられている。本実施例に
おいて用いられた前記顔料は、プラム色の顔料であり、
光を照射すると反射光が干渉し、きらきらとした光輝性
の高い光を発する。ここで本実施形態において用いた顔
料が、前記実施例２と輝きの色が異なって見えるのは、
顔料の酸化鉄の被覆厚さが異なるため、干渉によって増
強される反射光の波長が異なるためである。よって前記
顔料を含有する本実施例のキャップ３および本体軸４
は、光が反射する方向から見ると、全体的にプラム色で
あり、従来の樹脂成形品に比べてつややかな光沢を呈す
る。The cap 3 and the main body shaft 4 of this embodiment are also
As in the case of Example 2, innumerable pigments in which mica is coated with titanium oxide and iron oxide are scattered. The pigment used in this example is a plum pigment.
When irradiated with light, the reflected light interferes with each other and emits light with a high brilliance. Here, the pigment used in this embodiment has a different brilliant color from that of Example 2 because
This is because the coating thickness of the iron oxide of the pigment is different and the wavelength of the reflected light that is enhanced by interference is different. Therefore, the cap 3 and the main body shaft 4 of the present embodiment containing the pigment.
When viewed from the direction in which light is reflected, is a plum color as a whole, and exhibits a glossy luster compared to conventional resin molded products.

【００６５】（実施例５）樹脂としてポリプロピレン
（商品名 MG03B 日本ポリケム株式会社製）を採用
し、この樹脂に全体の１重量％に相当する酸化チタンお
よび有機顔料を雲母に被覆した顔料（商品名 Dynacolo
r BB エンゲルハード社製）および黒色の着色剤Ｃ．
Ｉ．ＧＮ Pigment Black-7 を配合し、前記実施例１と
同様の手法により図２に示すようなボールペンのキャッ
プ３と本体軸４を成形した。(Example 5) Polypropylene (trade name MG03B manufactured by Nippon Polychem Co., Ltd.) was used as a resin, and a pigment (trade name) in which mica was coated with titanium oxide and an organic pigment corresponding to 1% by weight of the whole resin Dynacolo
r BB Engelhard) and a black colorant C.I.
I. GN Pigment Black-7 was blended and a ball-point pen cap 3 and a main body shaft 4 as shown in FIG. 2 were molded in the same manner as in Example 1.

【００６６】酸化チタンおよび有機顔料を雲母に被覆し
た顔料は青色の顔料であり、光を照射すると反射光が干
渉し、きらきらとした光輝性の高い光を発する。よっ
て、当該顔料が無数に散りばめられた本実施例のキャッ
プ３および本体軸４は、光を照射するときらきらとした
光輝性の高い点状の光を発し、全体的に青色で従来の樹
脂成形品に比べてつややかな光沢を呈する。The pigment in which mica is coated with titanium oxide and an organic pigment is a blue pigment, and when irradiated with light, the reflected light interferes with each other and emits glittering light having high glitter. Therefore, the cap 3 and the main body shaft 4 of the present embodiment, in which the pigment is scattered innumerably, emits a point light having a high brilliance when irradiating light, and is blue in color and is a conventional resin molded product. It has a glossy luster compared to.

【００６７】（実施例６）樹脂としてポリプロピレン
（商品名 MG03B 日本ポリケム株式会社製）を採用
し、この樹脂に全体の２重量％に相当するチタン被覆ガ
ラスフレーク顔料（商品名 メタシャインRCFSX −5090
RC 品番８０５３ 日本板硝子株式会社製、チタン被覆
平均粒径約９０μｍ）および着色料Ｃ．Ｉ．ＧＮ Pi
gment Green-7を配合し、前記実施例１と同様の手法に
より図２に示すようなボールペンのキャップ３と本体軸
４を成形した。Example 6 Polypropylene (trade name MG03B manufactured by Nippon Polychem Co., Ltd.) was used as a resin, and a titanium-coated glass flake pigment (trade name Metashine RCFSX-5090 corresponding to 2% by weight of the whole resin was used for this resin.
RC product number 8053 manufactured by Nippon Sheet Glass Co., Ltd., titanium coating, average particle size of about 90 μm) and colorant C.I. I. GN Pi
gment Green-7 was blended and a ball-point pen cap 3 and a main body shaft 4 as shown in FIG. 2 were molded by the same method as in Example 1.

【００６８】成形されたキャップ３及び本体軸４は、い
ずれも着色料によって緑色に着色された半透明体であ
る。また、キャップ３及び本体軸４が含有している顔料
は、干渉色が緑色である。ここで、該干渉色と前記着色
料との色相の差は、マンセル表色法に基づく１００分割
中の１０以内の同系統の色相である。よって、本実施例
のキャップ３および本体軸４は、干渉色の色彩が、樹脂
の地色に溶け込み、輝きだけが強調され、従来の樹脂成
形品とは全く異なる、趣き深い独特の色感が得られる。Both the molded cap 3 and the main body shaft 4 are semitransparent bodies colored in green with a coloring agent. The interference color of the pigment contained in the cap 3 and the main body shaft 4 is green. Here, the difference in hue between the interference color and the colorant is within 10 within 100 divisions based on the Munsell color system, and is a hue of the same system. Therefore, in the cap 3 and the main body shaft 4 of the present embodiment, the color of the interference color is blended with the background color of the resin, and only the shine is emphasized, giving a distinctive and unique color feeling completely different from the conventional resin molded product. can get.

【００６９】（実施例７）樹脂としてポリプロピレン
（商品名 MG03B 日本ポリケム株式会社製）を採用
し、この樹脂にアルミ蒸着フィルム（商品名 エルジー
#500 尾池工業製）および黒色の着色剤Ｃ．Ｉ．ＧＮ
Pigment Black-7 を配合し、上記と同様の手法によりボ
ールペンのキャップ３と本体軸４を成形した。(Example 7) Polypropylene (trade name MG03B manufactured by Nippon Polychem Co., Ltd.) was adopted as a resin, and an aluminum vapor-deposited film (trade name ERJ) was used for this resin.
# 500 made by Oike Kogyo) and a black colorant C.I. I. GN
Pigment Black-7 was blended and the cap 3 and the main body shaft 4 of the ballpoint pen were molded by the same method as above.

【００７０】本実施例のキャップ３及び本体軸４は、顔
料であるアルミ蒸着フィルムに入射した光が光輝性の高
い反射光を発し、さらに顔料以外の部分に入射した光は
着色剤に吸収される。そのため、キャップ３及び本体軸
４は、顔料による反射光が際だち、従来の樹脂成形品に
は見られない独特の意匠効果を有する。In the cap 3 and the main body shaft 4 of this embodiment, the light incident on the aluminum vapor-deposited film which is a pigment emits reflected light having a high brilliance, and the light incident on the portion other than the pigment is absorbed by the colorant. It Therefore, the cap 3 and the main body shaft 4 have a unique design effect which is not seen in the conventional resin molded product because the reflected light from the pigment is conspicuous.

【００７１】（実施例８）樹脂としてポリプロピレン
（商品名 MG03B 日本ポリケム株式会社製）を採用
し、この樹脂に酸化チタンおよび酸化鉄を雲母に被覆し
た顔料（商品名 Dynacolor BB エンゲルハード社
製）および緑色の着色剤Ｃ．Ｉ．ＧＮ PigmentGreen-7
を配合し、全体が半透明となるようにキャップ３と本
体軸４を成形した。(Example 8) Polypropylene (trade name MG03B manufactured by Nippon Polychem Co., Ltd.) was used as a resin, and a pigment (trade name Dynacolor BB Engelhard Co.) coated with titanium oxide and iron oxide on the resin was used. Green colorant C.I. I. GN Pigment Green-7
Was mixed, and the cap 3 and the main body shaft 4 were molded so as to be semitransparent.

【００７２】本実施例において配合されている顔料は、
青色の干渉色を呈する顔料であり、光を照射すると反射
光が干渉し、光輝性の高い光を発する。また、本実施例
のキャップ３および本体軸４は半透明であるため、樹脂
成型品の表面近傍にある顔料による干渉光が、内部側に
ある顔料による干渉光を増幅する。よって、当該顔料が
無数に散りばめられた本実施例のキャップ３および本体
軸４は、光を照射するとひときわ光輝性に富み鮮明な点
状の光を発する。The pigments used in this example are
It is a pigment that exhibits a blue interference color, and when irradiated with light, the reflected light interferes with each other to emit light with high glitter. Further, since the cap 3 and the main body shaft 4 of this embodiment are semitransparent, the interference light due to the pigment near the surface of the resin molded product amplifies the interference light due to the pigment on the inside side. Therefore, the cap 3 and the main body shaft 4 of the present embodiment, in which the pigment is scattered innumerably, emits a sharp dot-like light which is extremely bright when irradiated with light.

【００７３】（実施例９）樹脂としてポリプロピレン
（商品名 MG03B 日本ポリケム株式会社製）を採用
し、この樹脂にフレーク状のアルミニウム（商品名 エ
ルジー 品番 H25 Silver 尾池工業製）および緑色の
着色剤Ｃ．Ｉ．ＧＮ Pigment Green-7 を配合し、全体
が半透明となるようにキャップ３と本体軸４を成形し
た。(Example 9) Polypropylene (trade name MG03B manufactured by Nippon Polychem Co., Ltd.) was adopted as a resin, and in this resin, flaky aluminum (trade name ERJ product number H25 Silver manufactured by Oike Kogyo Co., Ltd.) and a green colorant C were used. ． I. GN Pigment Green-7 was blended, and the cap 3 and the main body shaft 4 were molded so that the whole was semi-transparent.

【００７４】本実施例のキャップ３および本体軸４は、
共に全体が緑色で半透明であり、きらとした点状の光が
無数に認められる。キャップ３および本体軸４において
認められる光は極めて光輝性が高い。これは全体が透明
あるいは半透明であり、樹脂内で光がほとんど減衰しな
いため、光の反射に寄与する顔料の総表面積が大きいた
めである。The cap 3 and the body shaft 4 of this embodiment are
Both are entirely green and semi-transparent, and innumerable glittering spots of light are observed. The light observed on the cap 3 and the main body shaft 4 is extremely bright. This is because the whole is transparent or semi-transparent and the light is hardly attenuated in the resin, so that the total surface area of the pigment that contributes to the reflection of light is large.

【００７５】[0075]

【発明の効果】入射光に対して干渉色を呈する顔料と、
黒色及び／又は暗色の着色剤を含有する樹脂成形品は、
顔料が入射光によって干渉色を発し、さらに当該顔料を
透過した入射光が着色剤に吸収されるため、光輝性が高
く美しい。[Effect of the Invention] A pigment exhibiting an interference color with respect to incident light,
The resin molded product containing a black and / or dark colorant is
The pigment emits an interference color by the incident light, and the incident light transmitted through the pigment is absorbed by the colorant.

【００７６】また、本発明の樹脂成形品は、入射光によ
って干渉色を呈する顔料と、前記干渉色との色相の相違
がマンセル表色法に基づく１００分割中の１０以内であ
る着色剤を含有する樹脂成形品は、着色剤の呈する色相
と前記顔料の干渉色の色相とのコントラストにより、趣
き深い独特の色感が得られる。Further, the resin molded product of the present invention contains a pigment exhibiting an interference color by incident light and a colorant having a hue difference with the interference color within 10 out of 100 divisions based on the Munsell color method. The resin molded product obtained has a distinctive and unique color feeling due to the contrast between the hue exhibited by the colorant and the hue of the interference color of the pigment.

【００７７】入射光を反射する顔料と、黒色及び／又は
暗色の着色剤を配合し樹脂成形品を成形すれば、顔料以
外の部分に入射する光の大部分を着色剤で吸収できるた
め、顔料の発する反射光を際だたせることができる。When a resin molded product is molded by mixing a pigment that reflects incident light and a black and / or dark colorant, the colorant can absorb most of the light that is incident on parts other than the pigment. The reflected light emitted by can be highlighted.

【００７８】入射光に対して干渉色を呈する顔料を配合
し、全体が透明あるいは半透明となるように樹脂成型品
を成形すれば、顔料の呈する干渉色を鮮明にすることが
できる。The interference color exhibited by the pigment can be made clear by blending a pigment exhibiting an interference color with respect to the incident light and molding the resin molded product so as to be transparent or semitransparent as a whole.

【００７９】入射光を反射する顔料を配合し、全体が透
明あるいは半透明となるように樹脂成型品を成形すれ
ば、顔料の呈する反射光の光輝性を高めることができ
る。By mixing a pigment that reflects incident light and molding the resin molded product so that the whole is transparent or semi-transparent, the glitter of the reflected light exhibited by the pigment can be enhanced.

【図面の簡単な説明】[Brief description of drawings]

【図１】（ａ）は黒色及び／又は暗色の着色剤を含有す
る樹脂成形品の表面近傍における光の入射および反射の
様子を示す概念図であり、（ｂ）は黒色及び／又は暗色
の着色剤を含有しない樹脂成形品の表面近傍における光
の入射および反射の様子を示す概念図である。FIG. 1A is a conceptual diagram showing how light is incident and reflected in the vicinity of the surface of a resin molded product containing a black and / or dark colorant, and FIG. 1B is a black and / or dark color diagram. FIG. 3 is a conceptual diagram showing how light is incident and reflected near the surface of a resin molded product that does not contain a colorant.

【図２】本発明の樹脂成形品の一例を示す斜視図であ
る。FIG. 2 is a perspective view showing an example of a resin molded product of the present invention.

【符号の説明】[Explanation of symbols]

１ 樹脂成形品 ２ 顔料 ３ キャップ ４ 本体軸 ５ 基礎物質 ７ 皮膜 1 Resin molded product 2 pigments 3 caps 4 body axis 5 Basic substances 7 film

───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4F071 AA20 AB03 AB06 AB17 AB28 AD02 AD05 AE09 AF29 AF30 AF32 AF33 AF34 AG12 BA01 BB05 BC05 4J002 AB021 BB031 BB041 BB121 BC031 BC061 BC071 BD031 BE031 BG051 BG061 BN151 CB001 CF061 CF071 CG001 CH071 CL001 CN031 DA037 DJ056 DL006 FA016 FB076 FD096    ─────────────────────────────────────────────────── ─── Continued front page    F-term (reference) 4F071 AA20 AB03 AB06 AB17 AB28                       AD02 AD05 AE09 AF29 AF30                       AF32 AF33 AF34 AG12 BA01                       BB05 BC05                 4J002 AB021 BB031 BB041 BB121                       BC031 BC061 BC071 BD031                       BE031 BG051 BG061 BN151                       CB001 CF061 CF071 CG001                       CH071 CL001 CN031 DA037                       DJ056 DL006 FA016 FB076                       FD096

Claims (16)

【特許請求の範囲】[Claims] 【請求項１】 入射光に対して干渉色を呈する顔料と、
黒色の着色剤を含む樹脂組成物を成形してなることを特
徴とする樹脂成形品。1. A pigment exhibiting an interference color with respect to incident light,
A resin molded product obtained by molding a resin composition containing a black colorant. 【請求項２】 入射光を反射する顔料と、黒色の着色剤
とを含む樹脂組成物を成形してなることを特徴とする樹
脂成型品。2. A resin molded article, which is obtained by molding a resin composition containing a pigment that reflects incident light and a black colorant. 【請求項３】 黒色の着色剤はカーボンブラックである
ことを特徴とする請求項１又は２に記載の樹脂成形品。3. The resin molded product according to claim 1, wherein the black colorant is carbon black. 【請求項４】 入射光に対して干渉色を呈する顔料と、
暗色の着色剤を含む樹脂組成物を成形してなることを特
徴とする樹脂成形品。4. A pigment exhibiting an interference color with respect to incident light,
A resin molded product obtained by molding a resin composition containing a dark colorant. 【請求項５】 入射光を反射する顔料と、暗色の着色剤
を含む樹脂組成物を成形してなることを特徴とする樹脂
成形品。5. A resin molded product obtained by molding a resin composition containing a pigment that reflects incident light and a dark colorant. 【請求項６】 入射光によって干渉色を呈する顔料と、
前記干渉色との色相の相違がマンセル表色法に基づく１
００分割中の１０以内である着色剤を含有する樹脂組成
物を成形してなることを特徴とする樹脂成形品。6. A pigment exhibiting an interference color by incident light,
The difference in hue from the interference color is based on the Munsell color method 1
A resin molded product obtained by molding a resin composition containing a colorant that is within 10 of 00 divisions. 【請求項７】 太陽光に対して緑色の干渉色を呈する顔
料と、太陽光に対して緑色に発色する着色剤を含む樹脂
組成物を成形してなることを特徴とする樹脂成形品。7. A resin molded article, which is obtained by molding a resin composition containing a pigment exhibiting a green interference color with respect to sunlight and a colorant that develops green with respect to sunlight. 【請求項８】 入射光に対して干渉色を呈する顔料を含
有し、全体が透明あるいは半透明であることを特徴とす
る樹脂成型品。8. A resin molded product comprising a pigment exhibiting an interference color with respect to incident light and being entirely transparent or semitransparent. 【請求項９】 入射光を反射する顔料を含有し、全体が
透明あるいは半透明であることを特徴とする樹脂成型
品。9. A resin molded product comprising a pigment that reflects incident light and is entirely transparent or semi-transparent. 【請求項１０】 顔料はガラスを金属及び／又は金属酸
化物によって被覆したガラスフレーク顔料であることを
特徴とする請求項１乃至９のいずれかに記載の樹脂成形
品。10. The resin molded article according to claim 1, wherein the pigment is a glass flake pigment obtained by coating glass with a metal and / or a metal oxide. 【請求項１１】 顔料は無機物質を金属及び／又は金属
酸化物によって被覆した金属被覆無機顔料であることを
特徴とする請求項１乃至９のいずれかに記載の樹脂成形
品。11. The resin molded product according to claim 1, wherein the pigment is a metal-coated inorganic pigment obtained by coating an inorganic substance with a metal and / or a metal oxide. 【請求項１２】 顔料は無機物質を金属及び／又は金属
酸化物と、有機顔料によって被覆した金属被覆無機顔料
であることを特徴とする請求項１乃至９のいずれかに記
載の樹脂成形品。12. The resin molded article according to claim 1, wherein the pigment is a metal-coated inorganic pigment obtained by coating an inorganic substance with a metal and / or a metal oxide, and an organic pigment. 【請求項１３】 顔料の被覆の厚さが干渉色を生じる厚
さであることを特徴とする請求項１０乃至１２のいずれ
かに記載の樹脂成形品。13. The resin molded article according to claim 10, wherein the thickness of the coating of the pigment is a thickness that produces an interference color. 【請求項１４】 顔料の被覆は光の一部が透過可能であ
ることを特徴とする請求項１０乃至１２のいずれかに記
載の樹脂成形品。14. The resin molded product according to claim 10, wherein the pigment coating allows a part of light to pass therethrough. 【請求項１５】 全体が半透明であることを特徴とする
請求項１乃至１４のいずれかに記載の樹脂成形品。15. The resin molded product according to claim 1, which is semitransparent as a whole. 【請求項１６】 前記顔料の平均粒径が５．０〜５００
μｍであり、且つ、当該顔料が樹脂組成物全量中に１．
０〜５．０重量％含まれることを特徴とする請求項１乃
至１５のいずれかに記載の樹脂成形品。16. The pigment has an average particle size of 5.0 to 500.
μm, and the pigment is 1.
The resin molded product according to claim 1, wherein the resin molded product is contained in an amount of 0 to 5.0% by weight.