JP2003175574A - Film for overlap packaging - Google Patents
Film for overlap packagingInfo
- Publication number
- JP2003175574A JP2003175574A JP2001376854A JP2001376854A JP2003175574A JP 2003175574 A JP2003175574 A JP 2003175574A JP 2001376854 A JP2001376854 A JP 2001376854A JP 2001376854 A JP2001376854 A JP 2001376854A JP 2003175574 A JP2003175574 A JP 2003175574A
- Authority
- JP
- Japan
- Prior art keywords
- propylene
- film
- olefin copolymer
- olefin
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明はヒートシール強度、
溶断シール強度、ラミネート強度、厚薄精度等に優れた
オーバーラップ包装用フィルムに関する。TECHNICAL FIELD The present invention relates to heat seal strength,
The present invention relates to an overwrap packaging film excellent in fusing seal strength, laminating strength, thickness accuracy and the like.
【０００２】[0002]
【従来の技術】二軸延伸ポリプロピレンフィルム（以下
ＯＰＰフィルムと呼ぶことがある）は、その優れた透明
性、機械的強度、防湿性、剛性等を活かして包装材料を
はじめ広い分野で使用されている。しかし、ＯＰＰフイ
ルムは単層ではヒートシール可能温度が高くしかもヒー
トシールの適正な温度範囲が狭いという欠点がある。そ
こで、ＯＰＰフイルムのヒートシール性を改善するため
に、ＯＰＰフイルムの片面又は両面に低融点のプロピレ
ン・エチレン共重合体層を積層した二軸延伸複合フィル
ム（特公昭４９−１４３４３号公報）、特定の三元ラン
ダム共重合体層をヒートシール層としたフィルム（特公
平８−５１７４号公報）、特定のプロピレン・１−ブテ
ンランダム共重合体と結晶性プロピレン・α―オレフィ
ンランダム共重合体との組成物を積層したポリプロピレ
ン複合フィルム（特公昭６１−４２６２６号公報）等、
ポリプロピレンに比べて低融点の樹脂を積層させる方法
が多数提案され、且つ、幅広く使用されている。2. Description of the Related Art Biaxially oriented polypropylene films (hereinafter sometimes referred to as OPP films) have been used in a wide range of fields including packaging materials by taking advantage of their excellent transparency, mechanical strength, moisture resistance and rigidity. There is. However, the OPP film has a drawback that a single layer has a high heat-sealable temperature and a proper heat-seal temperature range is narrow. Therefore, in order to improve the heat-sealing property of the OPP film, a biaxially stretched composite film in which a low melting point propylene / ethylene copolymer layer is laminated on one side or both sides of the OPP film (Japanese Patent Publication No. 49-14343), is specified. Of the ternary random copolymer layer as a heat seal layer (Japanese Patent Publication No. 8-5174), a specific propylene / 1-butene random copolymer and a crystalline propylene / α-olefin random copolymer A polypropylene composite film in which the composition is laminated (Japanese Patent Publication No. 61-42626), and the like,
Many methods of laminating a resin having a melting point lower than that of polypropylene have been proposed and widely used.
【０００３】しかしながら、かかる方法で得られる複合
フィルムは、複合フィルム故、用途によっては、ヒート
シール性がしばしば問題となり、ヒートシール性の改良
が常に望まれている。However, since the composite film obtained by such a method is a composite film, the heat-sealing property is often a problem depending on the application, and improvement of the heat-sealing property is always desired.
【０００４】[0004]
【発明が解決しようとする課題】そこで本発明は、オー
バーラップ特性に優れた二軸延伸多層ポリプロピレンフ
ィルムを開発することを目的として種々検討した結果、
ＯＰＰフィルムの原料としてプロピレン単独重合体とプ
ロピレン・エチレンランダム共重合体とからなるプロピ
レン重合体組成物とすることにより二軸延伸フィルムの
厚薄精度が改良され、その結果、ヒートシール強度、溶
断シール強度、ラミネート強度に優れたオーバーラップ
包装用フィルムを得ることができた。Therefore, the present invention has been variously studied for the purpose of developing a biaxially stretched multilayer polypropylene film excellent in overlap characteristics, and as a result,
By using a propylene polymer composition composed of a propylene homopolymer and a propylene / ethylene random copolymer as a raw material for the OPP film, the thickness accuracy of the biaxially stretched film is improved, and as a result, the heat seal strength and the fusion seal strength It was possible to obtain an overwrap packaging film having excellent laminate strength.
【０００５】[0005]
【発明の概要】本発明は、二軸延伸されたα―オレフィ
ン含有量が０．１〜１．８モル％の範囲にある、プロピ
レン単独重合体（Ａ）とプロピレン・α−オレフィン共
重合体（Ｂ）とのプロピレン重合体組成物から得られ得
る基層の両面にプロピレン・α−オレフィン共重合体
（Ｃ）層が積層されてなることを特徴とするオーバーラ
ップ包装用フィルムをである。SUMMARY OF THE INVENTION The present invention provides a propylene homopolymer (A) and a propylene / α-olefin copolymer having a biaxially stretched α-olefin content of 0.1 to 1.8 mol%. A wrapping film for wrapping, characterized in that a propylene / α-olefin copolymer (C) layer is laminated on both sides of a base layer which can be obtained from the propylene polymer composition with (B).
【０００６】本発明は、前記プロピレン重合体組成物
が、プロピレン単独重合体（Ａ）９５〜１０重量％及び
プロピレン・α−オレフィン共重合体（Ｂ）５〜９０重
量％とからなる組成物であるオーバーラップ包装用フィ
ルムを提供するものである。In the present invention, the propylene polymer composition comprises a propylene homopolymer (A) of 95 to 10% by weight and a propylene / α-olefin copolymer (B) of 5 to 90% by weight. An overwrap packaging film is provided.
【０００７】本発明は、又、二軸延伸されたα―オレフ
ィン含有量が０．１〜１．８モル％の範囲にある、プロ
ピレン単独重合体（Ａ）とプロピレン・α−オレフィン
共重合体（Ｂ）とのプロピレン重合体組成物から得られ
得る基層の両面に融点が８０〜１５５℃の範囲のプロピ
レン・α−オレフィン共重合体（Ｃ）層が積層されてな
るオーバーラップ包装用フィルムを提供するものであ
る。The present invention also provides a propylene homopolymer (A) and a propylene / α-olefin copolymer having a biaxially stretched α-olefin content in the range of 0.1 to 1.8 mol%. A film for overlapping packaging in which a propylene / α-olefin copolymer (C) layer having a melting point in the range of 80 to 155 ° C. is laminated on both sides of a base layer which can be obtained from the propylene polymer composition with (B). It is provided.
【０００８】本発明は、又、基層の両表面層に積層され
たプロピレン・α−オレフィン共重合体（Ｃ）層が、ブ
ロッキング防止剤を含んでなるオーバーラップ包装用フ
ィルムを提供するものである。The present invention also provides an overwrap packaging film in which the propylene / α-olefin copolymer (C) layer laminated on both surface layers of the base layer contains an antiblocking agent. .
【０００９】[0009]
【発明の具体的説明】プロピレン単独重合体（Ａ）
本発明に係わるプロピレン単独重合体（Ａ）は、プロピ
レンの単独重合体からなり、通常、ＭＦＲ（メルトフロ
ーレート；ＡＳＴＭ Ｄ−１２３８ 荷重２１６０ｇ、
温度２３０℃）が、通常０．５〜１０ｇ／１０分、好ま
しくは２〜５ｇ／１０分の範囲にある。DETAILED DESCRIPTION OF THE INVENTION Propylene Homopolymer (A) The propylene homopolymer (A) according to the present invention comprises a propylene homopolymer and is usually MFR (melt flow rate; ASTM D-1238, load 2160 g,
The temperature (230 ° C.) is usually in the range of 0.5 to 10 g / 10 minutes, preferably 2 to 5 g / 10 minutes.
【００１０】プロピレン・α−オレフィン共重合体
（Ｂ）
本発明に係わるプロピレン・α−オレフィン共重合体
（Ｂ）は、α―オレフィン含有量が０．４〜２．２モル
％、好ましくは０．６〜１．８モル％のプロピレンとの
ランダム共重合体である。α―オレフィンの含有量が
０．４モル％未満のものでは、ニ軸延伸する際の延伸性
が改良されず、一方、２．２モル％を越えると得られる
オーバーラップ包装用フィルムが剛性に劣る。α―オレ
フィンとしては、エチレン、１−ブテン、１−ヘキセ
ン、４−メチル・１−ペンテン、１−オクテン等が例示
できる。これらの中では、エチレンが好ましい。又、Ｍ
ＦＲ（メルトフローレート；ＡＳＴＭ Ｄ−１２３８
荷重２１６０ｇ、温度２３０℃）はオーバーラップ包装
用フィルムとすることができる限り特に限定はされない
が、通常０．５〜１０ｇ／１０分、好ましくは２〜５ｇ
／１０分の範囲にある。 Propylene / α-olefin copolymer
(B) The propylene / α-olefin copolymer (B) according to the present invention contains propylene having an α-olefin content of 0.4 to 2.2 mol%, preferably 0.6 to 1.8 mol%. Is a random copolymer of. When the content of α-olefin is less than 0.4 mol%, the stretchability during biaxial stretching is not improved, while when it exceeds 2.2 mol%, the resulting overlapping packaging film becomes rigid. Inferior. Examples of the α-olefin include ethylene, 1-butene, 1-hexene, 4-methyl / 1-pentene, 1-octene and the like. Of these, ethylene is preferred. Also, M
FR (Melt flow rate; ASTM D-1238)
The load is 2160 g, and the temperature is 230 ° C.) is not particularly limited as long as it can be used as an overwrap packaging film, but is usually 0.5 to 10 g / 10 minutes, preferably 2 to 5 g.
/ 10 minutes.
【００１１】プロピレン・α−オレフィン共重合体
（Ｃ）
本発明に係わるプロピレン・α−オレフィン共重合体
（Ｃ）は、好ましくは融点が８０〜１５５℃、更に好ま
しくは９０〜１４５℃の範囲にあるプロピレンとのラン
ダム共重合体であり、融点が１５５℃を越えるものは、
得られるオーバーラップ包装用フィルムの低温ヒートシ
ール性、溶断シール強度、ラミネート強度が改良されな
い虞があり、一方、８０℃未満のものは、得られるオー
バーラップ包装用フィルムにべたが発生し、ブロッキン
グし易くなる傾向にある。又、かかるプロピレン・α−
オレフィン共重合体（Ｃ）は、通常、α―オレフィン含
有量が、１〜４０モル％、好ましくは２〜３５モル％の
範囲にある。α―オレフィンの含有量がかかる範囲にあ
ると、低温ヒートシール性、ラミネート強度、耐ブロッ
キング性等のバランスに優れたオーバーラップ包装用フ
ィルムが得られる。プロピレンと共重合するα―オレフ
ィンとしては、エチレン、１−ブテン、１−ヘキセン、
４−メチル・１−ペンテン、１−オクテン等が例示でき
る。具体的な共重合体としては、プロピレン・エチレン
ランダム共重合体、プロピレン・エチレン・１−ブテン
ランダム共重合体、プロピレン・１−ブテンランダム共
重合体等が挙げられる。これら共重合体は、単独で用い
ても良いし、二種以上を混合して用いても良い。 Propylene / α-olefin copolymer
(C) The propylene / α-olefin copolymer (C) according to the present invention is preferably a random copolymer with propylene having a melting point of 80 to 155 ° C, more preferably 90 to 145 ° C. If the melting point exceeds 155 ° C,
There is a possibility that the low-temperature heat-sealing property, the fusion-sealing strength, and the laminating strength of the obtained overwrap packaging film may not be improved. On the other hand, if it is less than 80 ° C, the obtained overwrap packaging film becomes sticky and blocks. It tends to be easier. Also, such propylene / α-
The olefin copolymer (C) usually has an α-olefin content of 1 to 40 mol%, preferably 2 to 35 mol%. When the content of α-olefin is within such a range, an overwrap packaging film having an excellent balance of low temperature heat sealability, laminate strength, blocking resistance and the like can be obtained. Examples of the α-olefin copolymerized with propylene include ethylene, 1-butene, 1-hexene,
4-methyl / 1-pentene, 1-octene, etc. can be illustrated. Specific examples of the copolymer include a propylene / ethylene random copolymer, a propylene / ethylene / 1-butene random copolymer, a propylene / 1-butene random copolymer and the like. These copolymers may be used alone or in combination of two or more.
【００１２】本発明に係るプロピレン・α−オレフィン
共重合体（Ｃ）には、得られるオーバーラップ包装用フ
ィルムの低温ヒートシール性をさらに改良するために、
１−ブテン・エチレンランダム共重合体、１―ブテン・
プロピレンランダム共重合体、低結晶性のエチレン・１
−ブテンランダム共重合体等を混合してもよい。The propylene / α-olefin copolymer (C) according to the present invention has the following properties in order to further improve the low-temperature heat-sealing property of the resulting overwrap packaging film.
1-butene / ethylene random copolymer, 1-butene /
Propylene Random Copolymer, Low Crystalline Ethylene-1
-A butene random copolymer or the like may be mixed.
【００１３】本発明に係るプロピレン・α−オレフィン
共重合体（Ｃ）には耐熱安定剤、耐候安定剤、紫外線吸
収剤、滑剤、スリップ剤、核剤、ブロッキング防止剤、
帯電防止剤、防曇剤、顔料、染料、無機または有機の充
填剤等の通常ポリオレフィンに用いる各種添加剤を本発
明の目的を損なわない範囲で添加しておいてもよい。The propylene / α-olefin copolymer (C) according to the present invention includes a heat resistance stabilizer, a weather resistance stabilizer, an ultraviolet absorber, a lubricant, a slip agent, a nucleating agent, an antiblocking agent,
Various additives usually used for polyolefins such as antistatic agents, antifogging agents, pigments, dyes, inorganic or organic fillers may be added within a range not impairing the object of the present invention.
【００１４】中でも、ブロッキング防止剤を０．０１〜
３．０重量％、好ましくは０．０５〜１．０重量％を添
加しておくと、透明性に優れ、且つブロッキング防止性
を有するオーバーラップ包装用フィルムとすることがで
きる。ブロッキング防止剤の量が０．０１重量％未満で
は、得られるオーバーラップ包装用フィルムのブロッキ
ング防止効果が充分でなく、一方、３．０重量％を越え
ると、得られるオーバーラップ包装用フィルムの透明性
が劣る傾向にある。かかるブロッキング防止剤として
は、種々公知のもの、例えば、シリカ、タルク、雲母、
ゼオライトや更には金属アルコキシドを焼成して得た金
属酸化物等の無機化合物粒子、ポリメタクリル酸メチ
ル、メラミンホルマリン樹脂、メラミン尿素樹脂、ポリ
エステル樹脂等の有機化合物粒子等を用い得る。これら
の中でも、シリカ、ポリメタクリル酸メチルがアンチブ
ロッキング性、透明性の面から特に好ましい。Among them, the anti-blocking agent is 0.01 to
By adding 3.0% by weight, preferably 0.05 to 1.0% by weight, it is possible to obtain an overwrap packaging film having excellent transparency and antiblocking property. When the amount of the anti-blocking agent is less than 0.01% by weight, the blocking preventing effect of the obtained overwrapping film is not sufficient, while when it exceeds 3.0% by weight, the transparency of the obtained overwrapping film is transparent. The sex tends to be inferior. As such an antiblocking agent, various known agents such as silica, talc, mica,
Inorganic compound particles such as metal oxides obtained by firing zeolite or metal alkoxide, organic compound particles such as polymethylmethacrylate, melamine formalin resin, melamine urea resin, polyester resin and the like can be used. Among these, silica and polymethylmethacrylate are particularly preferable in terms of antiblocking property and transparency.
【００１５】重合体の製造方法
本発明に係わるプロピレン単独重合体（Ａ）、プロピレ
ン・α−オレフィン共重合体（Ｂ）及びプロピレン・α
−オレフィン共重合体（Ｃ）は種々公知の方法、例え
ば、典型的には固体状チタン触媒成分と有機金属化合物
触媒成分から形成される触媒、あるいはこれら両成分お
よび電子供与体から形成される触媒を用いて製造するこ
とができる。 Production Method of Polymer Propylene homopolymer (A), propylene / α-olefin copolymer (B) and propylene / α according to the present invention
The olefin copolymer (C) can be produced by various known methods, for example, a catalyst typically formed from a solid titanium catalyst component and an organometallic compound catalyst component, or a catalyst formed from both components and an electron donor. Can be used for manufacturing.
【００１６】固体状チタン触媒成分としては、各種方法
で製造された三塩化チタンまたは三塩化チタン組成物、
あるいはマグネシウム、ハロゲン、電子供与体、好まし
くは芳香族カルボン酸エステルまたはアルキル基含有エ
ーテルおよびチタンを必須成分とする、比表面積が好適
には１００ｍ２／ｇ以上の担体付チタン触媒成分が挙げ
られる。特に後者の担体付触媒成分を用いて製造された
重合体が好適である。As the solid titanium catalyst component, titanium trichloride or a titanium trichloride composition produced by various methods,
Alternatively, a carrier-supported titanium catalyst component having a specific surface area of preferably 100 m 2 / g or more, which contains magnesium, halogen, an electron donor, preferably an aromatic carboxylic acid ester or an alkyl group-containing ether and titanium as essential components, can be mentioned. In particular, a polymer produced by using the latter catalyst component with a carrier is suitable.
【００１７】有機金属化合物触媒成分としては、有機ア
ルミニウム化合物が好適であり、具体的には、トリアル
キルアルミニウム、ジアルキルアルミニウムハライド、
アルキルアルミニウムセスキハライド、アルキルアルミ
ニウムジハライドなどが挙げられる。これらの化合物の
うち、好適な有機金属化合物触媒成分は、使用する上記
チタン触媒成分の種類によって異なる。The organometallic compound catalyst component is preferably an organoaluminum compound, specifically, trialkylaluminum, dialkylaluminum halide,
Examples thereof include alkyl aluminum sesquihalide and alkyl aluminum dihalide. Among these compounds, a suitable organometallic compound catalyst component varies depending on the type of the titanium catalyst component used.
【００１８】電子供与体は、窒素、リン、イオウ、酸
素、ケイ素、ホウ素などを含む有機化合物であり、好適
な具体例としては、これらの元素を有する有機エステ
ル、有機エーテルなどを挙げることができる。The electron donor is an organic compound containing nitrogen, phosphorus, sulfur, oxygen, silicon, boron and the like, and preferable specific examples thereof include organic esters and organic ethers having these elements. .
【００１９】担体付触媒成分を用いた重合体の製造方法
に関しては、たとえば特開昭50- 108385号、特開昭50-
126590号、特開昭51-20297号、特開昭51-28189号、特開
昭52- 151691号などの各公報に開示されている。Regarding the method of producing a polymer using a catalyst component with a carrier, for example, JP-A-50-108385 and JP-A-50-
No. 126590, JP-A-51-20297, JP-A-51-28189, JP-A-52-151691 and the like.
【００２０】本発明に係わるＩｓｏが高いプロピレン単
独重合体およびプロピレン・α−オレフィン共重合体
は、またシングルサイト触媒を用いても製造することが
できる。シングルサイト触媒は、活性点が均一（シング
ルサイト）である触媒であり、例えばメタロセン触媒
（いわゆるカミンスキー触媒）やブルックハート触媒な
どがあげられる。例えばメタロセン触媒は、メタロセン
系遷移金属化合物と、有機アルミニウム化合物および上
記メタロセン系遷移金属化合物と反応してイオン対を形
成する化合物からなる群から選ばれる少なくとも一種の
化合物とからなる触媒であり、無機物に担持されていて
もよい。The propylene homopolymer and propylene / α-olefin copolymer having a high Iso according to the present invention can also be produced by using a single site catalyst. The single-site catalyst is a catalyst having a uniform active site (single site), and examples thereof include a metallocene catalyst (so-called Kaminsky catalyst) and a Brookhart catalyst. For example, a metallocene catalyst is a catalyst composed of a metallocene-based transition metal compound and at least one compound selected from the group consisting of an organoaluminum compound and a compound that reacts with the metallocene-based transition metal compound to form an ion pair, and an inorganic substance It may be supported on.
【００２１】前記メタロセン系遷移金属化合物として
は、例えば特開平５−２０９０１４号、特開平６−１０
０５７９号、特開平１−３０１７０４号、特開平３−１
９３７９６号、特開平５−１４８２８４号等に記載され
た化合物などがあげられる。Examples of the metallocene-based transition metal compound include, for example, JP-A-5-209014 and JP-A-6-10.
0579, JP-A-1-301704, JP-A3-1
Examples thereof include the compounds described in JP-A No. 93796, JP-A No. 5-148284 and the like.
【００２２】有機アルミニウム化合物としては、アルキ
ルアルミニウム、または鎖状あるいは環状アルミノキサ
ン等があげられる。上記鎖状あるいは環状アルミノキサ
ンは、アルキルアルミニウムと水とを接触させることに
より生成される。例えば重合時にアルキルアルミニウム
を加えておいて、後で水を添加するか、あるいは錯塩の
結晶水または有機、無機化合物の吸着水とアルキルアル
ミニウムとを反応させることにより得られる。Examples of the organoaluminum compound include alkylaluminum, chain or cyclic aluminoxane, and the like. The chain or cyclic aluminoxane is produced by contacting alkylaluminum and water. For example, it can be obtained by adding alkylaluminum at the time of polymerization and then adding water, or by reacting water of crystallization of a complex salt or adsorbed water of an organic or inorganic compound with alkylaluminum.
【００２３】前記メタロセン系遷移金属化合物と反応し
てイオン対を形成する化合物は、例えば特表平１−５０
１９５０号、特開平３−２０７７０４号等に記載された
化合物などがあげられる。シングルサイト触媒を担持さ
せる前記無機物としては、シリカゲル、ゼオライト、珪
藻土等があげられる。The compound which reacts with the metallocene-based transition metal compound to form an ion pair is, for example, JP-A-1-50.
Examples thereof include compounds described in 1950, JP-A-3-207704 and the like. Examples of the inorganic material supporting the single-site catalyst include silica gel, zeolite, diatomaceous earth and the like.
【００２４】重合方法としては、塊状重合、溶液重合、
懸濁重合、気相重合等があげられる。これらの重合はバ
ッチ法であっても連続法であっても良い。重合条件は通
常、重合温度；−１００〜＋２５０℃、重合時間；５分
〜１０時間、反応圧力；常圧〜３００Ｋｇ／ｃｍ２（ゲ
ージ圧）である。Polymerization methods include bulk polymerization, solution polymerization,
Examples include suspension polymerization and gas phase polymerization. These polymerizations may be a batch method or a continuous method. The polymerization conditions are usually a polymerization temperature of −100 to + 250 ° C., a polymerization time of 5 minutes to 10 hours, and a reaction pressure of atmospheric pressure to 300 Kg / cm 2 (gauge pressure).
【００２５】プロピレン重合体組成物
本発明に係わるプロピレン重合体組成物は、プロピレン
単独重合体（Ａ）とプロピレン・α−オレフィン共重合
体（Ｂ）とから得られ得る組成物で、α―オレフィン含
有量が０．１〜１．８モル％、好ましくは０．２〜１．
５モル％の範囲にあり、好ましくはプロピレン単独重合
体（Ａ）が９５〜１０重量％、更に好ましくは９０〜２
０重量％の範囲、プロピレン・α−オレフィン共重合体
（Ｂ）５〜９０重量％、更に好ましくは１０〜８０重量
％の範囲にある。α―オレフィン含有量が０．１モル％
未満、更にはプロピレン・α−オレフィン共重合体
（Ｂ）が５重量％未満では、オーバーラップ包装用フィ
ルムを得る場合の延伸温度幅の改良効果が少ない虞があ
るので、厚薄精度に優れたオーバーラップ包装用フィル
ムにならない場合があり、又、プロピレン・α−オレフ
ィン共重合体（Ｃ）層と積層した場合に、溶断シール強
度、ラミネート強度が改良されない場合がある。一方、
α―オレフィン含有量が１．８モル％を越えると、更に
は９５重量％を越えると得られるオーバーラップ包装用
フィルムの剛性、機械的強度等が低下する虞がある。 Propylene Polymer Composition The propylene polymer composition according to the present invention is a composition obtainable from a propylene homopolymer (A) and a propylene / α-olefin copolymer (B). The content is 0.1 to 1.8 mol%, preferably 0.2 to 1.
It is in the range of 5 mol%, preferably 95 to 10% by weight of the propylene homopolymer (A), and more preferably 90 to 2%.
The amount is 0% by weight, the propylene / α-olefin copolymer (B) is 5 to 90% by weight, and more preferably 10 to 80% by weight. α-olefin content is 0.1 mol%
If the propylene / α-olefin copolymer (B) is less than 5% by weight, the effect of improving the stretching temperature range in obtaining the overwrap packaging film may be small. It may not be a film for wrap packaging, and when laminated with a propylene / α-olefin copolymer (C) layer, the fusion-cut seal strength and laminate strength may not be improved. on the other hand,
If the α-olefin content exceeds 1.8 mol%, and if it exceeds 95% by weight, the resulting overwrap packaging film may have reduced rigidity, mechanical strength and the like.
【００２６】本発明に係わるプロピレン重合体組成物
は、プロピレン単独重合体（Ａ）とプロピレン・α−オ
レフィン共重合体（Ｂ）とを種々公知の方法で混合する
ことにより得られる。例えば、予めプロピレン単独重合
体（Ａ）とプロピレン・α−オレフィン共重合体（Ｂ）
とを夫々別個に重合して得たものを、機械的に混合する
方法、混合した後溶融混練する方法、あるいはプロピレ
ン単独重合体（Ａ）若しくはプロピレン・α−オレフィ
ン共重合体（Ｂ）とを重合した後、引き続きプロピレン
・α−オレフィン共重合体（Ｂ）若しくはプロピレン単
独重合体（Ａ）を重合する方法等により得られる。The propylene polymer composition according to the present invention can be obtained by mixing the propylene homopolymer (A) and the propylene / α-olefin copolymer (B) by various known methods. For example, propylene homopolymer (A) and propylene / α-olefin copolymer (B) are previously prepared.
And the propylene homopolymer (A) or the propylene / α-olefin copolymer (B). After the polymerization, the propylene / α-olefin copolymer (B) or the propylene homopolymer (A) may be subsequently polymerized.
【００２７】本発明のプロピレン単独重合体（Ａ）、プ
ロピレン・α−オレフィン共重合体（Ｂ）若しくはプロ
ピレン重合体組成物には、夫々にあるいは何れかに、耐
熱安定剤、耐候安定剤、紫外線吸収剤、滑剤、スリップ
剤、核剤、ブロッキング防止剤、帯電防止剤、防曇剤、
顔料、染料、無機または有機の充填剤等の通常ポリオレ
フィンに用いる各種添加剤を本発明の目的を損なわない
範囲で添加しておいてもよい。In the propylene homopolymer (A), propylene / α-olefin copolymer (B) or propylene polymer composition of the present invention, a heat resistance stabilizer, a weather resistance stabilizer, an ultraviolet ray stabilizer, an ultraviolet light stabilizer, or an ultraviolet light stabilizer may be used. Absorbent, lubricant, slip agent, nucleating agent, antiblocking agent, antistatic agent, antifogging agent,
Various additives usually used for polyolefins such as pigments, dyes and inorganic or organic fillers may be added within a range not impairing the object of the present invention.
【００２８】オーバーラップ包装用フィルム
本発明のオーバーラップ包装用フィルムの厚さは用途に
より種々決められるものであり、特に限定はされない
が、通常、プロピレン重合体組成物層が１０〜１００μ
ｍ、好ましくは１３〜５０μｍの範囲、プロピレン・α
−オレフィン共重合体（Ｃ）層が０．１〜１５μｍ、好
ましくは０．３〜１０μｍの範囲にある。Overwrap packaging film The thickness of the overwrap packaging film of the present invention is variously determined depending on the application and is not particularly limited, but usually the propylene polymer composition layer is 10 to 100 μm.
m, preferably in the range of 13 to 50 μm, propylene · α
The olefin copolymer (C) layer is in the range of 0.1 to 15 μm, preferably 0.3 to 10 μm.
【００２９】本発明のオーバーラップ包装用フィルムは
必要に応じて片面あるいは両面をコロナ処理、火炎処理
等の表面処理をしてもよい。The overwrap packaging film of the present invention may be subjected to surface treatment such as corona treatment or flame treatment on one side or both sides, if necessary.
【００３０】本発明のオーバーラップ包装用フィルム
は、プロピレン重合体（Ａ）とプロピレン・α―オレフ
ィン共重合体（Ｂ）とから得られ得るプロピレン重合体
組成物層の両面にプロピレン・α−オレフィン共重合体
（Ｃ）とを共押出し成形して得られる多層シートを、公
知の同時二軸延伸法あるいは逐次二軸延伸法等の二軸延
伸フィルム製造方法により得られる。二軸延伸の条件
は、公知のＯＰＰフィルムの製造条件、例えば、逐次二
軸延伸法では、縦延伸温度を１２５℃〜１４５℃、延伸
倍率を４．５〜６倍の範囲、横延伸温度を１６５〜１９
０℃、延伸倍率を９〜１１倍の範囲にすればよい。The overlap packaging film of the present invention comprises a propylene polymer composition layer obtained from a propylene polymer (A) and a propylene / α-olefin copolymer (B) on both sides of the propylene / α-olefin. A multilayer sheet obtained by co-extrusion with the copolymer (C) is obtained by a known biaxially stretched film production method such as a simultaneous biaxial stretching method or a sequential biaxial stretching method. The biaxial stretching conditions include known OPP film production conditions. For example, in the sequential biaxial stretching method, the longitudinal stretching temperature is 125 ° C. to 145 ° C., the stretching ratio is 4.5 to 6 times, and the transverse stretching temperature is 165-19
It suffices to set the stretching ratio at 0 ° C. to 9 to 11 times.
【００３１】本発明に係わるプロピレン重合体組成物
は、特に、逐次二軸延伸フィルム製造方法で、横延伸の
温度範囲を従来に比べ７℃と広くすることができ、横延
伸操作が容易となり、得られるオーバーラップ包装用フ
ィルムの厚薄精度、例えば、ＯＰＰフィルムの基準厚み
に対する厚薄ばらつき（２σ）をプロピレン重合体
（Ａ）単独から得られるオーバーラップ包装用フィルム
に対し２０〜５０％低減できる。その結果、得られるオ
ーバーラップ包装用フィルムのラミネート強度、溶断シ
ール強度、ヒートシール強度が改善される。In the propylene polymer composition according to the present invention, the temperature range of transverse stretching can be widened to 7 ° C. as compared with the conventional method in the method for producing a biaxially stretched film, and the transverse stretching operation becomes easy. Thickness accuracy of the obtained overwrap packaging film, for example, thickness variation (2σ) with respect to the reference thickness of the OPP film can be reduced by 20 to 50% with respect to the overwrap packaging film obtained from the propylene polymer (A) alone. As a result, the laminate strength, fusing seal strength, and heat seal strength of the resulting overwrap packaging film are improved.
【００３２】[0032]
【発明の効果】本発明のオーバーラップ包装用フィルム
は、二軸延伸する際の均一延伸性、広温度域延伸性等の
延伸性が改良されており、また、本発明のオーバーラッ
プ包装用フィルムは厚薄精度が良好であるために高速包
装時のフィルム供給不良（スティッキング）を起こしづ
らくなり、不良発生率を格段に抑える事が可能となる。INDUSTRIAL APPLICABILITY The overwrap packaging film of the present invention has improved stretchability such as uniform stretchability during biaxial stretching and wide temperature range stretchability, and the overwrap packaging film of the present invention. Since the thickness accuracy is good, it becomes difficult to cause film supply failure (sticking) during high-speed packaging, and it is possible to significantly reduce the failure occurrence rate.
【００３３】また、本発明のオーバーラップ包装用フィ
ルムは厚薄精度に優れ、ベタがなく、高剛性、透明性に
優れており、ラミネート強度、溶断シール強度、ヒート
シール強度が改善されているので、従来オーバーラップ
包装用フィルムが使用されているあらゆる用途、例えば
チョコレート、ガム、キャンデー等の菓子類、たばこ、
化粧品等の嗜好品、カセットテープ、ビデオテープ、Ｃ
Ｄ、ＣＤＲ、ＤＶＤ、ゲームソフト等の記録材料、およ
びそれらの集積包装材料等の箱物包装の包装用フィルム
として好適に使用できる。Further, the film for overlapping packaging of the present invention is excellent in thickness accuracy, is not sticky, is excellent in high rigidity and transparency, and is improved in laminate strength, fusing seal strength and heat seal strength. All applications where films for overlapping wrapping are conventionally used, such as chocolate, gum, confectionery such as candy, tobacco,
Luxury items such as cosmetics, cassette tapes, video tapes, C
It can be suitably used as a packaging film for box packaging such as recording materials such as D, CDR, DVD, game software, and their integrated packaging materials.
【００３４】[0034]
【実施例】次に実施例を挙げて本発明を更に具体的に説
明するが、本発明はその要旨を越えない限りこれらの実
施例に制約されるものではない。EXAMPLES Next, the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples as long as the gist thereof is not exceeded.
【００３５】実施例及び比較例における物性値等は、以
下の評価方法により求めた。
（評価方法）
１）弾性率：ＪＩＳ Ｋ ７１２７に準じて測定した。
２）フィルム厚みムラ：規定幅の標準偏差を測定した
３）静摩擦係数：Ｎｏ１６２スリップテスター（安田精
機製作所製）を用いて測定した。
４）表面固有抵抗：デジタル超抵抗測定器Ｒ８３４０
（アドバンテスト社製）を用いて測定した。
５）ヒートシール強度：コロナ処理面／非コロナ処理面
を重ね合わせヒートシールテスター（東洋精機社製）を
用い、下記表中の温度に設定し、ヒートシール圧力０．
１ＭＰａ、０．５秒間の条件でヒートシールし、１５ｍ
ｍ幅に切り出し引張り試験機（東洋精機社製）を用い引
張速度３００ｍｍ／分で測定した。
６）オーバーラップ適性：Ｗ３２２包装試験機（東京自
働機械製作所製）を用いてサイドシール、口、及び胴貼
りシール温度１３５℃、ショット数２００個／分にて包
装し、その包装品の状況にて評価した。○：包装可能
×：包装出来ずPhysical properties and the like in Examples and Comparative Examples were determined by the following evaluation methods. (Evaluation Method) 1) Elastic Modulus: Measured according to JIS K 7127. 2) Film thickness unevenness: standard deviation of a specified width was measured. 3) Static friction coefficient: No 162 slip tester (manufactured by Yasuda Seiki Seisakusho). 4) Surface resistivity: Digital super resistance measuring instrument R8340
(Manufactured by Advantest). 5) Heat sealing strength: Using a heat seal tester (manufactured by Toyo Seiki Co., Ltd.) by superposing the corona-treated surface / non-corona-treated surface, set the temperature in the table below, and set the heat-sealing pressure to 0.
Heat seal under the condition of 1 MPa and 0.5 seconds for 15 m
Measurement was performed at a tensile speed of 300 mm / min using a tensile tester (manufactured by Toyo Seiki Co., Ltd.) cut into m widths. 6) Overlap suitability: W322 packaging tester (manufactured by Tokyo Jikiki Kikai Seisakusho) was used to package the side seal, mouth, and body seal temperature at 135 ° C and the number of shots at 200 pieces / min. Was evaluated. ○: Packable
×: Cannot be packaged
【００３６】実施例１
＜基層：プロピレン重合体組成物層＞プロピレン単独重
合体（ＭＦＲ＝３．０ｇ／１０分）４０重量％に対しプ
ロピレン・エチレンランダム共重合体（エチレン含有量
１．３モル％ ＭＦＲ＝３．０ｇ／１０分）を６０重量
％配合したエチレン含有量が０．８モル％のポリプロプ
レン樹脂組成物に酸化防止剤としてテトラキス［メチレ
ンー３−（３’、５’―ジーｔ―ブチルー４’ヒドロキ
シフェニル）プロピオネート］メタン（日本チバガイキ
ー社製品 製品名イルガノックス１０１０）１０００ｐ
ｐｍ ステアリン酸カルシウム（日本油脂製）１０００
ｐｐｍ、帯電防止剤としてステアリン酸モノグリセリド
（理研ビタミン製）６０００ｐｐｍ、ステアリルジエタ
ノールアミン（東邦化学製）２０００ｐｐｍを加えたプ
ロピレン重合体組成物を用意した。
＜両被覆層：プロピレン・α−オレフィン共重合体組成
物層＞両被覆層を構成する重合体として、エチレン含有
量：４．０モル％、ブテンー１含有量：１．１モル％、
融点１３８℃、ＭＦＲ：７ｇ／１０分のプロピレン・エ
チレン・１−ブテンランダム共重合体：８０重量％と、
プロピレン含有量：７１．１モル％、融点：１１０℃、
ＭＦＲ：７．０ｇ／１０分のプロピレン・１−ブテンラ
ンダム共重合体：２０重量％の組成物に、ポリメチルメ
タクリレート粒子からなるアンチ・ブロッキング剤を
０．１０重量％、耐熱安定剤としてテトラキス［メチレ
ンー３−（３’、５’―ジーｔ―ブチルー４’ヒドロキ
シフェニル）プロピオネート］メタン（日本チバガイキ
ー社製品 製品名イルガノックス１０１０）１０００ｐ
ｐｍ及びステアリン酸カルシウム（日本油脂製）１００
０ｐｐｍを加えたプロピレン・α−オレフィン共重合体
組成物を用意した。
＜オーバーラップ包装用フィルムの成形＞先に示したプ
ロピレン・α−オレフィン共重合体組成物／プロピレン
重合体組成物／プロピレン・α−オレフィン共重合体組
成物を押出量比（１／１０／１）になるよう各々スクリ
ュー押出機を用いて溶融押出しマルチマニホールドタイ
プＴ−ダイを用いて賦形、冷却ロール上にて急冷し厚さ
約１．３ｍｍの多層シートを得た。この多層シートを約
１２５℃まで加熱しフィルム流れ方向（縦方向）に５倍
延伸した。この５倍延伸したシートを１５５℃まで加熱
した後流れ方向に対して直交する方向（横方向）に９倍
延伸した。このオーバーラップ包装用フィルムの片面に
コロナ処理を施し、基層の厚さ：２５μｍ、被覆層の厚
さ：各々２．５μｍ（合計厚さ：３０μｍ）のオーバー
ラップ包装用フィルムを得た。かかるオーバーラップ包
装用フィルムの物性等を前記記載の方法で測定した。結
果を表１に示す。 Example 1 <Base layer: propylene polymer composition layer> 40% by weight of a propylene homopolymer (MFR = 3.0 g / 10 min), a propylene / ethylene random copolymer (ethylene content: 1.3 mol). % MFR = 3.0 g / 10 minutes) was added to a polypropylene resin composition having an ethylene content of 0.8 mol% containing 60% by weight of tetrakis [methylene-3- (3 ′, 5′-di-t) as an antioxidant. -Butyl-4'hydroxyphenyl) propionate] methane (Product name Irganox 1010, manufactured by Ciba-Gaiki Co., Japan) 1000p
pm Calcium stearate (made by NOF Corporation) 1000
ppm, stearic acid monoglyceride (manufactured by Riken Vitamin) 6000 ppm as an antistatic agent, and stearyldiethanolamine (manufactured by Toho Kagaku) 2000 ppm were added to prepare a propylene polymer composition. <Both coating layers: Propylene / α-olefin copolymer composition layer> As a polymer constituting both coating layers, ethylene content: 4.0 mol%, butene-1 content: 1.1 mol%,
A propylene / ethylene / 1-butene random copolymer having a melting point of 138 ° C. and an MFR of 7 g / 10 min: 80% by weight,
Propylene content: 71.1 mol%, melting point: 110 ° C.,
MFR: 7.0 g / 10 min propylene / 1-butene random copolymer: 20% by weight of a composition, 0.10% by weight of an anti-blocking agent composed of polymethylmethacrylate particles, and tetrakis [ Methylene-3- (3 ', 5'-di-t-butyl-4'hydroxyphenyl) propionate] methane (Product name Irganox 1010, manufactured by Ciba-Gaiki Co., Japan) 1000p
pm and calcium stearate (made by NOF Corporation) 100
A propylene / α-olefin copolymer composition containing 0 ppm was prepared. <Molding of Overwrap Packaging Film> The extrusion ratio (1/10/1) of the propylene / α-olefin copolymer composition / propylene polymer composition / propylene / α-olefin copolymer composition shown above is used. 3) was melt-extruded using a screw extruder, shaped using a multi-manifold type T-die, and rapidly cooled on a cooling roll to obtain a multilayer sheet having a thickness of about 1.3 mm. This multilayer sheet was heated to about 125 ° C. and stretched 5 times in the film flow direction (longitudinal direction). The sheet stretched 5 times was heated to 155 ° C., and then stretched 9 times in the direction (transverse direction) orthogonal to the flow direction. A corona treatment was applied to one surface of this overlapping packaging film to obtain an overlapping packaging film having a base layer thickness of 25 μm and a coating layer thickness of 2.5 μm (total thickness: 30 μm). The physical properties and the like of the overwrap packaging film were measured by the methods described above. The results are shown in Table 1.
【００３７】比較例１
実施例１で用いた基層樹脂をプロピレン単独重合体に変
えた他は実施例１と同様に行い、厚さ３０μｍのオーバ
ーラップ包装用フィルムを得た。かかるオーバーラップ
包装用フィルムの物性等を前記記載の方法で測定した。
結果を表１に示す。 Comparative Example 1 A wrapping film having a thickness of 30 μm was obtained in the same manner as in Example 1 except that the base layer resin used in Example 1 was changed to a propylene homopolymer. The physical properties and the like of the overwrap packaging film were measured by the methods described above.
The results are shown in Table 1.
【００３８】表１ Table 1
【００３９】表１の結果から明らかなように、本発明の
プロピレン単独重合体（Ａ）とプロピレン・α―オレフ
ィン共重合体（Ｂ）とから得られ得るプロピレン重合体
組成物を基層としたオーバーラップ包装用フィルムは、
比較例１に示したオーバーラップ包装用フィルムに比
べ、フィルムの厚みむらが低減されており、又、同一温
度でのヒートシール強度も強くなることが分かる。As is clear from the results in Table 1, a propylene polymer composition obtained from the propylene homopolymer (A) of the present invention and the propylene / α-olefin copolymer (B) was used as a base layer. The film for wrap packaging is
It can be seen that, compared with the film for overlapping packaging shown in Comparative Example 1, the uneven thickness of the film is reduced and the heat-sealing strength at the same temperature becomes stronger.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） // Ｂ２９Ｋ 23:00 Ｂ２９Ｋ 23:00 Ｂ２９Ｌ 9:00 Ｂ２９Ｌ 9:00 Ｆターム(参考） 3E086 AB02 AC07 AC22 AD13 BA04 BA15 BA33 BA35 BB58 BB90 CA07 CA40 4F100 AK07A AK64A AK64B AK64C AK66A AK66B AK66C AL05A BA03 BA06 BA10B BA10C BA15 CA17 EH20 EJ38 GB15 GB23 GB41 GB48 JA04B JA04C JK01 JK06 JL12 YY00A YY00B YY00C 4F210 AA09 AA09C AA11 AA11C AA11E AB07 AG01 AG03 QC05 QC06 QC07 QG01 QG15 QG18 4J002 BB12W BB14X BB15X GF00 GG02 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) // B29K 23:00 B29K 23:00 B29L 9:00 B29L 9:00 F term (reference) 3E086 AB02 AC07 AC22 AD13 BA04 BA15 BA33 BA35 BB58 BB90 CA07 CA40 4F100 AK07A AK64A AK64B AK64C AK66A AK66B AK66C AL05A BA03 BA06 BA10B BA10C BA15 CA17 EH20 EJ38 GB15 GB11 GB11A11A00A11A00A11A11A00A11A11A00A11A11A11A11A11A11A00 QG01 QG15 QG18 4J002 BB12W BB14X BB15X GF00 GG02
Claims (8)
０．１〜１．８モル％の範囲にある、プロピレン単独重
合体（Ａ）とプロピレン・α−オレフィン共重合体
（Ｂ）とのプロピレン重合体組成物から得られ得る基層
の両面にプロピレン・α−オレフィン共重合体（Ｃ）層
が積層されてなることを特徴とするオーバーラップ包装
用フィルム。1. A propylene homopolymer (A) and a propylene / α-olefin copolymer (B) having a biaxially stretched α-olefin content of 0.1 to 1.8 mol%. A film for overlapping packaging, comprising a propylene / α-olefin copolymer (C) layer laminated on both sides of a base layer obtainable from the propylene polymer composition.
重量％であり、プロピレン・α−オレフィン共重合体
（Ｂ）が５〜９０重量％とから得られ得るプロピレン重
合体組成物である請求項１記載のオーバーラップ包装用
フィルム。2. A propylene homopolymer (A) is 95-10.
The wrapping film for wrapping according to claim 1, which is a propylene polymer composition which can be obtained from the propylene / α-olefin copolymer (B) in an amount of 5 to 90% by weight.
（Ｂ）のα―オレフィン含有量が０．４〜２．２モル％
である請求項２記載のオーバーラップ包装用フィルム。3. The propylene / α-olefin copolymer (B) has an α-olefin content of 0.4 to 2.2 mol%.
The film for overlapping packaging according to claim 2, which is
（Ｂ）のα−オレフィンがエチレン及び／又は１−ブテ
ンである請求項２若しくは３記載のオーバーラップ包装
用フィルム。4. The overlap packaging film according to claim 2, wherein the α-olefin of the propylene / α-olefin copolymer (B) is ethylene and / or 1-butene.
含有量が０．２〜１．５モル％である請求項４記載のオ
ーバーラップ包装用フィルム。5. The overwrap packaging film according to claim 4, wherein the ethylene content in the propylene polymer composition is 0.2 to 1.5 mol%.
（Ｃ）層の融点が８０〜１５５℃の範囲にある請求項１
〜５の何れかに記載のオーバーラップ包装用フィルム。6. The melting point of the propylene / α-olefin copolymer (C) layer is in the range of 80 to 155 ° C.
The film for overlapping packaging according to any one of to 5.
（Ｃ）がブロッキング防止剤を含んでなる請求項１若し
くは６項記載の二軸延伸多層ポリプロピレンフィルム。7. The biaxially stretched multilayer polypropylene film according to claim 1, wherein the propylene / α-olefin copolymer (C) contains an antiblocking agent.
ン・α−オレフィン共重合体（Ｃ）層とを共押出し成形
して得られる多層シートをニ軸延伸することにより得ら
れ得る請求項１〜７の何れかに記載のオーバーラップ包
装用フィルム。8. A multi-layer sheet obtained by co-extruding a propylene homopolymer composition layer and a propylene / α-olefin copolymer (C) layer, which can be obtained by biaxial stretching. 7. The film for overlapping packaging according to any one of 7.