JP2003172661A - Temperature history indicator - Google Patents
Temperature history indicatorInfo
- Publication number
- JP2003172661A JP2003172661A JP2001372977A JP2001372977A JP2003172661A JP 2003172661 A JP2003172661 A JP 2003172661A JP 2001372977 A JP2001372977 A JP 2001372977A JP 2001372977 A JP2001372977 A JP 2001372977A JP 2003172661 A JP2003172661 A JP 2003172661A
- Authority
- JP
- Japan
- Prior art keywords
- indicator
- temperature
- ink layer
- temperature history
- heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、所定の温度を超え
る温度履歴を経たかを色調の変化で検知するために用い
られるインジケータに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an indicator used for detecting whether a temperature history has exceeded a predetermined temperature by a change in color tone.
【０００２】[0002]
【従来の技術】加工食品のような製品は、製造の際に油
や湯で所定温度以上に加熱しなければならない。生鮮食
材、冷蔵品、医薬品のような製品は、流通や保管の際に
所定温度を超えてしまうと腐敗、劣化または分解する。2. Description of the Related Art Products such as processed foods must be heated to a predetermined temperature or higher with oil or hot water during production. Products such as fresh foods, refrigerated products, and pharmaceuticals will rot, deteriorate, or decompose if they exceed a predetermined temperature during distribution or storage.
【０００３】そこで、製品が所定温度を超える温度履歴
を経たかを検知するために、色調の変化で示すインジケ
ータが用いられる。インジケータは、例えば図５に示す
ように、所定温度で熱溶融する物質を含有する隠蔽性イ
ンキ層２１が、吸収性の紙片２２上に付されて透明な樹
脂フィルム２０で被覆されている。インジケータが所定
温度に達すると、溶融状態となった物質を紙片２２が吸
収する。その結果、紙片２２が目視できるようになる。
インジケータは、色調が変化したと観察される。Therefore, in order to detect whether or not the product has passed a temperature history exceeding a predetermined temperature, an indicator indicated by a change in color tone is used. For example, as shown in FIG. 5, the indicator has a concealable ink layer 21 containing a substance that melts at a predetermined temperature, which is applied onto an absorbent paper piece 22 and covered with a transparent resin film 20. When the indicator reaches a predetermined temperature, the paper piece 22 absorbs the molten substance. As a result, the paper piece 22 becomes visible.
The indicator is observed to have changed color.
【０００４】このインジケータの樹脂フィルム２０は、
インキ層２１と紙片２２との厚みのために盛上がり、皺
が寄っているうえ、歪んで応力がかかり密着性が悪くな
っている。インジケータを製品の湾曲面や角に貼り付け
る場合、樹脂フィルム２０は一層皺が寄り、一層応力が
かかる。インジケータに付着した油や水が、樹脂フィル
ム２０の皺から浸入したり、応力のかかった樹脂フィル
ム２０を剥離させたりして、インキ層２１と接触し熱溶
融物質を溶解させて紙片２２に吸収させる結果、紙片２
２が目視できるようになる。また、盛上がった樹脂フィ
ルムは他の製品等と強く擦れ易いため、その圧力によっ
て熱溶融物質が潰され半透明化する結果、紙片１２が目
視できるようになる。これによりインジケータの色調変
化となって観察されるので、所定の温度履歴を経たと誤
認してしまう。The resin film 20 of this indicator is
Due to the thickness of the ink layer 21 and the paper piece 22, it rises, wrinkles, and is distorted and stressed, resulting in poor adhesion. When the indicator is attached to the curved surface or corner of the product, the resin film 20 becomes more wrinkled and more stressed. Oil or water adhering to the indicator penetrates from the wrinkles of the resin film 20 or peels off the stressed resin film 20 and comes into contact with the ink layer 21 to dissolve the heat-melting substance and absorb it into the paper piece 22. As a result, 2 pieces of paper
2 becomes visible. Further, since the raised resin film easily rubs strongly against other products and the like, the pressure causes the heat-melted substance to be crushed and becomes translucent, so that the paper piece 12 becomes visible. As a result, the color tone of the indicator is changed and observed, so that it is erroneously recognized that a predetermined temperature history has passed.
【０００５】[0005]
【発明が解決しようとする課題】本発明は前記の課題を
解決するためになされたもので、所定温度を超える温度
履歴を経たかを、明瞭な色調の変化で正確に表示するた
めに用いられ、耐水性、耐油性および耐擦性に優れた平
坦な温度履歴インジケータを提供することを目的とす
る。SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and is used for accurately displaying whether a temperature history exceeding a predetermined temperature has been passed by a clear change in color tone. An object of the present invention is to provide a flat temperature history indicator having excellent water resistance, oil resistance and abrasion resistance.
【０００６】[0006]
【課題を解決するための手段】前記の目的を達成するた
めになされた本発明の温度履歴インジケータは、実施例
に対応する図１を参照して説明すると、記録温度を融点
とする熱溶融性物質を含有した隠蔽性インキ層１１が付
され、溶融状態の熱溶融性物質を不可逆的に吸収し得る
紙製基材１２が、それと略同じ厚みの中敷シート１４の
穴に嵌まって支持体シート１６に貼付されており、イン
キ層１１と中敷シート１４とが透明な樹脂製の保護フィ
ルム１０で平坦に被覆されている。The temperature history indicator of the present invention made to achieve the above object will be described below with reference to FIG. 1 corresponding to an embodiment. A paper base material 12 having a concealing ink layer 11 containing a substance and capable of irreversibly absorbing a heat-melting substance in a molten state is fitted into a hole of an insole sheet 14 having substantially the same thickness as that of the substrate 12 and is supported. It is attached to the body sheet 16, and the ink layer 11 and the insole sheet 14 are evenly covered with the transparent protective film 10 made of resin.
【０００７】保護フィルム１０は、平坦であるので皺が
寄っておらず歪み応力がかかっていないので、インキ層
１１や中敷シート１４にしっかりと密着しており剥離し
難い。そのため熱溶融性物質が外界の油等と接触せず溶
解しない。また、インジケータ１が他の製品等と擦れて
も、中敷シート１４が緩衝材となるので、インキ層１１
の熱溶融性物質に強い圧力がかからず熱溶融性物質が潰
されない。その結果、このインジケータ１は、所定温度
を超える温度履歴を経たときにだけ、色調が変化する。Since the protective film 10 is flat and has no wrinkles and no strain stress, it is firmly adhered to the ink layer 11 and the insole sheet 14 and is difficult to peel off. Therefore, the heat-fusible substance does not come into contact with the external oil or the like and does not dissolve. Further, even if the indicator 1 rubs against other products or the like, the insole sheet 14 functions as a cushioning material.
No strong pressure is applied to the heat-meltable substance, and the heat-meltable substance is not crushed. As a result, the color tone of the indicator 1 changes only when the temperature history exceeds a predetermined temperature.
【０００８】熱溶融性物質は、インジケータ１の色調が
変化する温度を決定する成分であって、常圧下で記録す
べき温度に相当する融点を有し、融点以上に加熱される
と熱溶融されて、粒状または粉末状から液状に変化する
物質である。熱溶融性物質の存在により当初インキ層１
１が紙製基材１２を隠蔽している。この物質が熱溶融す
ると、紙製基材１２に不可逆的に吸収される結果、基材
１２が現れ目視できるようになり、インジケータ１の色
調の変化が観察される。その後、温度が低下し熱溶融性
物質が凝固しても、インジケータ１はもとの色調に戻ら
ないので、温度履歴の記録として保存することができ
る。The heat-fusible substance is a component that determines the temperature at which the color tone of the indicator 1 changes, has a melting point corresponding to the temperature to be recorded under normal pressure, and is melted when heated above the melting point. It is a substance that changes from granular or powder form to liquid form. Initially ink layer 1 due to the presence of heat fusible substances
1 hides the paper base material 12. When this substance is melted by heat, it is irreversibly absorbed by the paper base material 12, and as a result, the base material 12 appears and becomes visible, and a change in the color tone of the indicator 1 is observed. After that, even if the temperature is lowered and the heat-meltable substance is solidified, the indicator 1 does not return to the original color tone, so that it can be stored as a record of the temperature history.
【０００９】温度履歴インジケータ１は、図２または図
３に示すように、中敷シート１４が、確認すべき温度で
可逆的に変色する示温剤を含有するインキ層１９を有し
ていてもよい。このインキ層１９は中敷シート１４のい
ずれかの面に塗布されて形成される。In the temperature history indicator 1, as shown in FIG. 2 or 3, the insole sheet 14 may have an ink layer 19 containing a temperature indicating agent that reversibly changes color at the temperature to be confirmed. . The ink layer 19 is formed by being applied to either surface of the insole sheet 14.
【００１０】温度履歴インジケータ１は、図４に示すよ
うに、支持体シート１６が、確認すべき温度で可逆的に
変色する示温剤を含有するインキ層１９を有していても
よい。In the temperature history indicator 1, as shown in FIG. 4, the support sheet 16 may have an ink layer 19 containing a temperature indicator which reversibly changes color at the temperature to be confirmed.
【００１１】このインジケータ１は、熱溶融性物質を含
有するインキ層１１によって不可逆的に色調が変色する
ときの温度と、示温剤を含有するインキ層１９によって
可逆的に色調が変色するときの温度との同一または異な
る温度についての履歴を、別々に検知することができ
る。この示温剤は、例えば温度に応じ結晶転位により可
逆的に変色する無機顔料である。The indicator 1 has a temperature at which the color tone is irreversibly changed by the ink layer 11 containing a heat-melting substance and a temperature at which the color tone is reversibly changed by the ink layer 19 containing a temperature indicator. History for the same or different temperatures can be detected separately. The temperature indicator is an inorganic pigment that reversibly changes color due to crystal rearrangement depending on temperature.
【００１２】温度履歴インジケータ１は、明瞭な色調の
変化で温度履歴を正確に表示することができ、耐水性、
耐油性および耐擦性に優れている。The temperature history indicator 1 can accurately display the temperature history with a clear change in color tone,
Excellent oil resistance and abrasion resistance.
【００１３】[0013]
【発明の実施の形態】以下、本発明の温度履歴インジケ
ータ１の実施例を詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the temperature history indicator 1 of the present invention will be described in detail below.
【００１４】温度履歴インジケータ１は、以下のように
して製造される。The temperature history indicator 1 is manufactured as follows.
【００１５】先ず、熱溶融性物質含有インキを調製す
る。所望の大きさに粉砕した粒状または粉末状の熱溶融
性物質と、インキビヒクルと、熱溶融性物質を溶解しな
いがインキビヒクルを溶解する溶媒とを混練機で均一に
混練すると、インキが得られる。First, a heat-meltable substance-containing ink is prepared. An ink is obtained by uniformly kneading a granular or powdery heat-meltable substance crushed to a desired size, an ink vehicle, and a solvent that does not dissolve the heat-meltable substance but dissolves the ink vehicle in a kneader. .
【００１６】熱溶融性物質は、脂肪酸誘導体、アルコー
ル誘導体、エーテル誘導体、アルデヒド誘導体、ケトン
誘導体、アミン誘導体、アミド誘導体、ニトリル誘導
体、炭化水素誘導体、チオール誘導体、スルフィド誘導
体から選ばれる少なくとも１種類が用いられる。As the heat-fusible substance, at least one selected from fatty acid derivatives, alcohol derivatives, ether derivatives, aldehyde derivatives, ketone derivatives, amine derivatives, amide derivatives, nitrile derivatives, hydrocarbon derivatives, thiol derivatives and sulfide derivatives is used. To be
【００１７】次に、調製したこのインキをコーターアプ
リケーターにより紙に塗布する。この紙は、普通紙、和
紙、またはケント紙が用いられる。紙は、熱溶融性物質
の色と異なる色、例えば黒色に着色されていると、イン
ジケータの色調の変化が一層明瞭となるので好ましい。Next, the prepared ink is applied to paper by a coater applicator. As this paper, plain paper, Japanese paper, or Kent paper is used. It is preferable that the paper is colored in a color different from the color of the heat-fusible substance, for example, black, because the change in the color tone of the indicator becomes clearer.
【００１８】この紙を丸く小さく裁断し、熱溶融性物質
含有インキ層１１が付された小片の紙製基材１２を形成
する。This paper is cut into small round pieces to form small pieces of paper base material 12 to which the ink layer 11 containing a heat-fusible substance is applied.
【００１９】支持体シート１６の両面に、粘着剤を付し
て粘着剤層１５・１７を形成し、下側の粘着剤層１７に
剥離シート１８を付しておく。A pressure sensitive adhesive is applied to both sides of the support sheet 16 to form pressure sensitive adhesive layers 15 and 17, and a release sheet 18 is attached to the lower pressure sensitive adhesive layer 17.
【００２０】上面に剥離紙（不図示）の付された粘着剤
層１３を有する中敷シート１４に、ポンチにより、前記
の小片の紙製基材１２よりも僅かに大きな穴をあける。
この中敷シート１４とそれに付された粘着剤層１３との
厚みは、前記の小片の紙製基材１２とそれに付されたイ
ンキ層１１との厚みに同じにする。The insole sheet 14 having the pressure-sensitive adhesive layer 13 with release paper (not shown) on its upper surface is punched to make a slightly larger hole than the small paper substrate 12.
The thickness of the insole sheet 14 and the pressure-sensitive adhesive layer 13 attached to it is set to be the same as the thickness of the small-sized paper base material 12 and the ink layer 11 attached thereto.
【００２１】支持体シート１６の上面の粘着剤層１５
に、中敷シート１４の下面を貼り合わせる。中敷シート
１４の穴に、インキ層１１の付された小片の紙製基材１
２を嵌める。Adhesive layer 15 on top of support sheet 16
Then, the lower surface of the insole sheet 14 is attached. A small piece of paper base material 1 with the ink layer 11 attached to the holes of the insole sheet 14
Insert 2.
【００２２】中敷シート１４の上面の粘着剤層１３から
剥離紙（不図示）を剥がす。露出した粘着剤層１３を介
し中敷シート１４と、インキ層１１とを、保護フィルム
１０で平坦に被覆すると、温度履歴インジケータ１が得
られる。A release paper (not shown) is peeled off from the adhesive layer 13 on the upper surface of the insole sheet 14. When the insole sheet 14 and the ink layer 11 are flatly covered with the protective film 10 via the exposed pressure-sensitive adhesive layer 13, the temperature history indicator 1 is obtained.
【００２３】インキに含有されている熱溶融性物質とし
て用いる脂肪酸誘導体は、ミリスチン酸、パルミチン
酸、アジピン酸、オクタン酸、トリコサン酸、テトラト
リアコンタン酸、２，３−ジメチルノナン酸、２３−メ
チルテトラコサン酸、２−ヘキセン酸、ブラシン酸、２
−メチル−２−ドデセン酸、β−エレオステアリン酸、
ベヘノール酸、ｃｉｓ−９，１０−メチレンオクタデカ
ン酸、ショールムーグリン酸、３，３’−チオジプロピ
オン酸−ｎ−ドデシル、トリラウリン、パルミチン酸ア
ニリド、ステアリン酸アミド、ステアリン酸亜鉛、サリ
チル酸アニリド、Ｎ−アセチル−Ｌ−グルタミン酸、カ
プロン酸−β−ナフチルアミド、エナント酸フェニルヒ
ドラジド、アラキン酸−ｐ−クロルフェナシル、ギ酸コ
レステリル、１−アセト−２，３−ジステアリン、チオ
ラウリン酸−ｎ−ペンタデシル、ステアリン酸塩化物、
無水パルミチン酸、ステアリン酸−酢酸無水物、コハク
酸、セバシン酸ベンジルアンモニウム塩、２−ブロム吉
草酸、α−スルホステアリン酸メチルナトリウム塩、２
−フルオルアラキン酸が挙げられる。The fatty acid derivative used as the heat-fusible substance contained in the ink is myristic acid, palmitic acid, adipic acid, octanoic acid, tricosanoic acid, tetratriacontanoic acid, 2,3-dimethylnonanoic acid, 23-methyl. Tetracosanoic acid, 2-hexenoic acid, brassic acid, 2
-Methyl-2-dodecenoic acid, β-eleostearic acid,
Behenolic acid, cis-9,10-methyleneoctadecanoic acid, shoalmoogric acid, 3,3′-thiodipropionic acid-n-dodecyl, trilaurin, palmitic acid anilide, stearic acid amide, zinc stearate, salicylic acid anilide, N -Acetyl-L-glutamic acid, caproic acid-β-naphthylamide, enanthic acid phenylhydrazide, arachidic acid-p-chlorphenacyl, cholesteryl formate, 1-aceto-2,3-distearin, thiolauric acid-n-pentadecyl, stearic acid. object,
Palmitic anhydride, stearic acid-acetic anhydride, succinic acid, sebacic acid benzyl ammonium salt, 2-bromovaleric acid, α-sulfostearic acid methyl sodium salt, 2
Includes fluoroarachidic acid.
【００２４】同じくアルコール誘導体は、オクタデシル
アルコール、コレステリン、Ｄ−マンニット、ガラクチ
トール、ヘプタトリアコンタノール、ヘキサデカン−２
−オール、１−ｔｒａｎｓ−２−オクタデセノール、β
−エレオステアリルアルコール、シクロエイコサノー
ル、ｄ（＋）セロビオース、ｐ，ｐ’−ビフェノール、
リボフラビン、４−クロロ−２−メチルフェノール、２
−ブロモ−１−インダノールが挙げられる。Similarly, the alcohol derivative is octadecyl alcohol, cholesterin, D-mannitol, galactitol, heptatriacontanol, hexadecane-2.
-All, 1-trans-2-octadecenol, β
-Eleostearyl alcohol, cycloeicosanol, d (+) cellobiose, p, p'-biphenol,
Riboflavin, 4-chloro-2-methylphenol, 2
-Bromo-1-indanol may be mentioned.
【００２５】同じくエーテル誘導体は、ジヘキサデシル
エーテル、ジオクタデシルエーテル、シチジン、アデノ
シン、フェノキシ酢酸ナトリウム、１，３−ビス（４−
ヒドロキシフェノキシ）ベンゼン、アルミニウムトリエ
トキシドが挙げられる。Similarly, ether derivatives include dihexadecyl ether, dioctadecyl ether, cytidine, adenosine, sodium phenoxyacetate, 1,3-bis (4-
Examples thereof include hydroxyphenoxy) benzene and aluminum triethoxide.
【００２６】同じくアルデヒド誘導体は、ステアリンア
ルデヒド、パララウリルアルデヒド、パラステアリンア
ルデヒド、ナフトアルデヒド、ｐ−クロロベンズアルデ
ヒド、フタルアルデヒド、４−ニトロベンズアルデヒド
が挙げられる。Similarly, examples of the aldehyde derivative include stearaldehyde, paralauryl aldehyde, para stearaldehyde, naphthaldehyde, p-chlorobenzaldehyde, phthalaldehyde and 4-nitrobenzaldehyde.
【００２７】同じくケトン誘導体は、ステアロン、ドコ
サン−２−オン、フェニルヘプタデシルケトン、シクロ
ノナデカン、ビニルヘプタデシルケトン、４，４−ビス
ジメチルアミノベンゾフェノン、ビス（２，４−ペンタ
ンジオナイト）カルシウム、１−クロロアントラキノン
が挙げられる。Similarly, the ketone derivatives include stearone, docosane-2-one, phenylheptadecyl ketone, cyclononadecane, vinylheptadecyl ketone, 4,4-bisdimethylaminobenzophenone, bis (2,4-pentanedionite) calcium, 1 -Chloroanthraquinone.
【００２８】同じくアミン誘導体は、トリコシルアミ
ン、ジオクタデシルアミン、Ｎ，Ｎ−ジメチルオクチル
アミン、ヘプタデカメチレンイミン、ナフチルアミン、
ｐ−アミノ安息香酸エチル、ｏ−トリチオ尿素、スルフ
ァメタジン、硝酸グアニジン、ｐ−クロロアニリン、プ
ロピルアミン塩酸塩が挙げられる。Similarly, amine derivatives include tricosylamine, dioctadecylamine, N, N-dimethyloctylamine, heptadecamethyleneimine, naphthylamine,
Examples include ethyl p-aminobenzoate, o-trithiourea, sulfamethazine, guanidine nitrate, p-chloroaniline, and propylamine hydrochloride.
【００２９】同じくアミド誘導体は、ヘキシルアミド、
オクタコシルアミド、Ｎ−メチルドデシルアミド、Ｎ−
メチルヘプタコシルアミド、α−シアノアセトアミド、
サリチルアミド、ジシアンジアミド、２−ニトロベンズ
アミド、Ｎ−ブロモアセトアミドが挙げられる。Similarly, the amide derivative is hexylamide,
Octacosylamide, N-methyldodecylamide, N-
Methylheptacosylamide, α-cyanoacetamide,
Examples include salicylamide, dicyandiamide, 2-nitrobenzamide, and N-bromoacetamide.
【００３０】同じくニトリル誘導体は、ペンタデカンニ
トリル、マルガロニトリル、２−ナフトニトリル、ｏ−
ニトロフェノキシ酢酸、３−ブロモベンゾニトリル、３
−シアンピリジン、４−シアノフェノールが挙げられ
る。Similarly, nitrile derivatives include pentadecane nitrile, margaro nitrile, 2-naphtho nitrile and o-.
Nitrophenoxyacetic acid, 3-bromobenzonitrile, 3
-Cyan pyridine, 4-cyanophenol are mentioned.
【００３１】同じく炭化水素誘導体は、ヘキサデカン、
１−ノナトリアコンテン、ｔｒａｎｓ−ｎ−２−オクタ
デセン、ヘキサトリアコンチルベンゼン、２−メチルナ
フタレン、ビセン、塩化シアヌル、１−フルオロノナデ
カン、１−クロロエイコサン、１−ヨードペンタデカ
ン、１−ブロモヘプタデカン、１，２，４，５−テトラ
キス（ブロモメチル）ベンゼンが挙げられる。Similarly, the hydrocarbon derivative is hexadecane,
1-Nonatriacontene, trans-n-2-octadecene, hexatriacontylbenzene, 2-methylnaphthalene, bisene, cyanuric chloride, 1-fluorononadecane, 1-chloroeicosane, 1-iodopentadecane, 1-bromo Examples include heptadecane and 1,2,4,5-tetrakis (bromomethyl) benzene.
【００３２】同じくチオール誘導体は、ペンタデカンチ
オール、エイコサンチオール、２−ナフタレンチオー
ル、２−メルカプトエチルエーテル、２−ニトロベンゼ
ンスルフェニルクロリドが挙げられる。Similarly, examples of the thiol derivative include pentadecanethiol, eicosanethiol, 2-naphthalenethiol, 2-mercaptoethyl ether, and 2-nitrobenzenesulfenyl chloride.
【００３３】同じくスルフィド誘導体は、１，３−ジア
チン、２，１１−ジチア[３，３]パラシクロファン、ビ
ス（４−ヒドロキシ−３−メチルフェニル）スルフィ
ド、４，４−ジピリジルスルフィド、４−メチルメルカ
プトフェノールが挙げられる。Similarly, the sulfide derivative is 1,3-diatine, 2,11-dithia [3,3] paracyclophane, bis (4-hydroxy-3-methylphenyl) sulfide, 4,4-dipyridylsulfide, 4- Methyl mercaptophenol may be mentioned.
【００３４】インキビヒクルは、例えばメチルセルロー
ス、エチルセルロース、ヒドロキシメチルセルロース、
カルボキシメチルセルロース、アクリル樹脂、フェノー
ル樹脂、ナイロン、ポリビニルアルコールが用いられ、
市販のＰＡＳ８００メジウム（十条化工社製）、ハイセ
ットマットメジウム（ミノグループ製）が用いられても
よい。The ink vehicle is, for example, methyl cellulose, ethyl cellulose, hydroxymethyl cellulose,
Carboxymethyl cellulose, acrylic resin, phenolic resin, nylon, polyvinyl alcohol are used,
Commercially available PAS800 medium (manufactured by Jujo Kako Co., Ltd.) or Hiset mat medium (manufactured by Mino Group) may be used.
【００３５】熱溶融性物質含有インキの溶媒は、例えば
水、エタノール、ブタノール、酢酸エチル、酢酸イソア
ミル、メチルエチルケトン、メチルイソブチルケトン、
キシレン、ジエチルベンゼン、トルエン、ブチルセロソ
ルブ、エチルセロソルブ、ミネラルスピリットが用いら
れる。The solvent of the ink containing a heat-meltable substance is, for example, water, ethanol, butanol, ethyl acetate, isoamyl acetate, methyl ethyl ketone, methyl isobutyl ketone,
Xylene, diethylbenzene, toluene, butylcellosolve, ethylcellosolve, mineral spirits are used.
【００３６】保護フィルム１０、中敷シート１４、支持
体シート１６は、セルロース、セルロース誘導体、ポリ
オレフィン、ポリ塩化ビニル、ポリ塩化ビニリデン、ポ
リビニルアルコール、ポリエステル、ポリスチレン、塩
酸ゴム、ポリアミド、フッ素樹脂、ポリブテン、ポリビ
ニルブチラール、ポリエチレンオキサイド、ポリウレタ
ン、セルロースアセテートブチレート、ヒドロキシエチ
ルセルロース、ポリイミドのいずれかの透明な樹脂シー
トが用いられる。中敷シート１４、支持体シート１６は
金属箔であってもよい。The protective film 10, the insole sheet 14, and the support sheet 16 are made of cellulose, cellulose derivative, polyolefin, polyvinyl chloride, polyvinylidene chloride, polyvinyl alcohol, polyester, polystyrene, hydrochloric acid rubber, polyamide, fluororesin, polybutene, A transparent resin sheet of any one of polyvinyl butyral, polyethylene oxide, polyurethane, cellulose acetate butyrate, hydroxyethyl cellulose and polyimide is used. The insole sheet 14 and the support sheet 16 may be metal foil.
【００３７】なお、温度履歴インジケータ１は、中敷シ
ート１４が、図２に示すように透明な支持体シート１６
側に、または図３に示すように透明な保護フィルム１０
側に、可逆的に変色する示温剤を含有するインキ層１９
を有するものであってもよい。また、透明な支持体シー
ト１６が、図４に示すように中敷シート１４側に、可逆
的に変色する示温剤を含有するインキ層１９を有するも
のであってもよい。In the temperature history indicator 1, the insole sheet 14 is a transparent support sheet 16 as shown in FIG.
Transparent protective film 10 on the side or as shown in FIG.
On the side, an ink layer 19 containing a reversible color changing agent
May be included. Further, the transparent support sheet 16 may have an ink layer 19 containing a temperature indicating agent that reversibly changes color on the side of the insole sheet 14 as shown in FIG.
【００３８】この示温剤には、ヨウ化水銀金属錯塩類、
コレステリック系液晶、電子供与性呈色性有機化合物と
有機酸とアルコール類との組み合わせによりなる混合組
成物が挙げられる。小片の紙製基材１２に付された不可
逆的に変色する熱溶融性物質含有インキ層１１と、中敷
シート１４に付された可逆的に変色する示温剤含有イン
キ層１９とにより、同一または異なる温度の履歴を確認
することができる。This temperature indicator includes mercuric iodide metal complex salts,
A cholesteric liquid crystal, a mixed composition composed of a combination of an electron-donating color-developing organic compound, an organic acid and an alcohol may be mentioned. The heat-fusible substance-containing ink layer 11 that is irreversibly discolored on the small-sized paper substrate 12 and the reversibly color-changing temperature-increasing agent-containing ink layer 19 on the insole sheet 14 are the same or You can check the history of different temperatures.
【００３９】前記の実施例に従い、本発明を適用する温
度履歴インジケータを試作した例を以下の実施例１およ
び２に、本発明を適用外のインジケータの試作の例を比
較例に示す。Examples of temperature history indicators to which the present invention is applied according to the above-mentioned examples are shown in Examples 1 and 2 below, and an example of an indicator to which the present invention is not applied is shown as a comparative example.
【００４０】（実施例１）熱溶融性物質であるステアリ
ン酸の白色結晶３０重量部と、メチルセルロースの４％
水溶液７０重量部とからなるインキを調製した。インキ
を黒色の紙上へ塗布しインキ層を形成した。この紙を適
当な大きさに裁断して基材とし、ポリエステル製の支持
体シート上に貼り合わされているポリエステル製の中敷
シートの穴へ嵌めた。粘着剤層と、インキ層とを、ポリ
エステル製の保護フィルムで平坦に被覆して、温度履歴
インジケータを得た。(Example 1) 30 parts by weight of white crystals of stearic acid, which is a heat-meltable substance, and 4% of methylcellulose.
An ink consisting of 70 parts by weight of an aqueous solution was prepared. The ink was applied onto black paper to form an ink layer. This paper was cut into an appropriate size, used as a base material, and fitted into the holes of the polyester insole sheet laminated on the polyester support sheet. The pressure-sensitive adhesive layer and the ink layer were evenly covered with a protective film made of polyester to obtain a temperature history indicator.
【００４１】温度履歴インジケータを、金属製四角柱の
角に貼付し、室温下、マシン油中に１箇月浸漬した後、
取り出した。インジケータを観察したが、インジケータ
の色調の変化は認められず、保護フィルムの剥離も認め
られなかった。これを、６０℃に加熱したところ、イン
ジケータは、白色から黒色へ色調が変化した。別に得た
温度履歴インジケータの表面を金属片で擦ったり、金属
ローラーで加圧したところ、インジケータは、色調が変
化しなかった。A temperature history indicator was attached to the corner of a metal square pole and immersed in machine oil for 1 month at room temperature.
I took it out. When the indicator was observed, no change in the color tone of the indicator was observed and peeling of the protective film was not observed. When this was heated to 60 ° C., the color tone of the indicator changed from white to black. When the surface of the separately obtained temperature history indicator was rubbed with a metal piece or pressed with a metal roller, the color tone of the indicator did not change.
【００４２】（実施例２）中敷シートの下面に、テトラ
ヨード水銀酸銅錯塩を含み、７０℃未満で赤色であり７
０℃以上で暗赤紫色に可逆的に変色するインキ層を付し
たこと以外は実施例１と同様にして、温度履歴インジケ
ータを得た。(Example 2) The lower surface of the insole sheet contains a tetraiodomercuric acid copper complex salt and is red at a temperature of less than 70 ° C.
A temperature history indicator was obtained in the same manner as in Example 1 except that an ink layer that reversibly changed color to dark reddish purple at 0 ° C or higher was added.
【００４３】この温度履歴インジケータを、実施例１と
同様にしてマシン油中に浸漬後、観察したが、インジケ
ータの色調の変化、および保護フィルムの剥離は認めら
れなかった。６０℃に加熱したところ、インジケータ
は、熱溶融性物質含有インキ層の部位が白色から黒色へ
色調変化し、示温剤含有インキ層の部位が色調変化しな
かった。次いで７０℃に加熱したところ、色調変化し示
温剤含有インキ層の部位が赤色から暗赤紫へ色調変化し
た。放冷すると、示温剤含有インキ層の部位がもとの赤
色に復色した。一方、溶融性物質含有インキ層の部位
は、一旦黒色となった後は元の色調へ戻らなかった。別
に得た温度履歴インジケータの表面を金属片で擦った
り、金属ローラーで加圧したところ、インジケータは、
色調が変化しなかった。This temperature history indicator was observed after being immersed in machine oil in the same manner as in Example 1, but no change in the color tone of the indicator and peeling of the protective film were observed. When heated to 60 ° C., the indicator changed the color tone of the part of the ink layer containing the heat-fusible substance from white to black and did not change the color tone of the part of the ink layer containing the temperature indicator. Then, when it was heated to 70 ° C., the color tone changed and the color tone of the portion of the ink layer containing the temperature indicator changed from red to dark reddish purple. When left to cool, the site of the ink layer containing the temperature indicator returned to the original red color. On the other hand, the region of the ink layer containing the fusible substance did not return to the original color tone once it became black. When the surface of the temperature history indicator obtained separately was rubbed with a metal piece or pressed with a metal roller, the indicator was
The color tone did not change.
【００４４】（比較例）中敷シートを用いずに、保護シ
ートで熱溶融性物質含有インキ層と支持体シートとを被
覆したこと以外は実施例１と同様にして温度履歴インジ
ケータを得た。Comparative Example A temperature history indicator was obtained in the same manner as in Example 1 except that the protective sheet was used to cover the ink layer containing the heat-fusible substance and the support sheet without using the insole sheet.
【００４５】この温度履歴インジケータを、実施例１と
同様にしてマシン油中に浸漬後、観察したところ、保護
フィルムの一部が剥離しており、インジケータの色調の
変化が認められた。別に得た温度履歴インジケータの表
面を金属片で擦ったり、金属ローラーで加圧したとこ
ろ、インジケータは白色から灰色への色調の変化が認め
られた。This temperature history indicator was dipped in machine oil in the same manner as in Example 1 and observed. As a result, a part of the protective film was peeled off, and a change in the color tone of the indicator was observed. When the surface of the separately obtained temperature history indicator was rubbed with a metal piece or pressed with a metal roller, the indicator was observed to change in color tone from white to gray.
【００４６】なお、実施例に記載の温度履歴インジケー
タを試作する際、支持体シートまたは中敷シートと粘着
剤層とは、市販の粘着剤層付樹脂フィルムであるユポタ
ック（大日本インキ化学工業(株)製の商品名）を用いて
もよい。In the trial production of the temperature history indicator described in the examples, the support sheet or insole sheet and the adhesive layer were Yupotac (Dainippon Ink and Chemicals, Inc.) which is a commercially available resin film with an adhesive layer. (Trade name) manufactured by K.K.
【００４７】[0047]
【発明の効果】以上、詳細に説明したように本発明の温
度履歴インジケータは、加工食品製造の油や湯での加熱
工程において所定温度以上に加熱されたことの確認、水
気のある生鮮食品、結露し易い冷蔵品の流通時や保存時
において所定温度を超えていないことの確認、複雑な形
状の電気機材等の製品の過熱による故障の予知や安全の
確認のために使用される。As described above in detail, the temperature history indicator of the present invention is used for confirming that the temperature history indicator of the present invention has been heated to a predetermined temperature or higher in the process of heating with oil or hot water for the production of processed food, fresh food with moisture, It is used to confirm that the temperature does not exceed the specified temperature during the distribution and storage of refrigerated items that are subject to dew condensation, to predict failures due to overheating of products with complicated shapes such as electrical equipment, and to confirm safety.
【００４８】この温度履歴インジケータは、耐水性およ
び耐油性に優れ、油や水が付着しても誤認しないもので
ある。またインジケータは、製品の湾曲部や角に貼付し
て用いることができ、耐擦性に優れ、擦られても誤認を
生じないものである。This temperature history indicator is excellent in water resistance and oil resistance and does not erroneously be recognized even if oil or water adheres. Further, the indicator can be used by being attached to a curved portion or a corner of a product, has excellent abrasion resistance, and does not cause misidentification even when rubbed.
【００４９】温度履歴インジケータは、所定温度を超え
る温度履歴を経たかを、明瞭な色調の変化で正確に表示
できる。The temperature history indicator can accurately display whether or not the temperature history exceeds a predetermined temperature by a clear change in color tone.
【図１】本発明を適用する温度履歴インジケータの実施
例を示す断面図である。FIG. 1 is a sectional view showing an embodiment of a temperature history indicator to which the present invention is applied.
【図２】本発明を適用する温度履歴インジケータの別な
実施例を示す断面図である。FIG. 2 is a sectional view showing another embodiment of the temperature history indicator to which the present invention is applied.
【図３】本発明を適用する温度履歴インジケータの別な
実施例を示す断面図である。FIG. 3 is a cross-sectional view showing another embodiment of the temperature history indicator to which the present invention is applied.
【図４】本発明を適用する温度履歴インジケータの別な
実施例を示す断面図である。FIG. 4 is a cross-sectional view showing another embodiment of the temperature history indicator to which the present invention is applied.
【図５】本発明を適用外の温度履歴インジケータの断面
図である。FIG. 5 is a cross-sectional view of a temperature history indicator to which the present invention is not applied.
１は温度履歴インジケータ、１０は保護フィルム、１１
は熱溶融性物質含有インキ層、１２は紙製基材、１３は
粘着剤層、１４は中敷シート、１５は粘着剤層、１６は
支持体シート、１７は粘着剤層、１８は剥離シート、１
９は示温剤含有インキ層、２０は樹脂フィルム、２１は
熱溶融性物質含有インキ層、２２は紙片である。1 is a temperature history indicator, 10 is a protective film, 11
Is a heat-fusible substance-containing ink layer, 12 is a paper base material, 13 is an adhesive layer, 14 is an insole sheet, 15 is an adhesive layer, 16 is a support sheet, 17 is an adhesive layer, and 18 is a release sheet. 1
Reference numeral 9 is a temperature indicating agent-containing ink layer, 20 is a resin film, 21 is a heat-fusible substance-containing ink layer, and 22 is a piece of paper.
Claims (2)
含有した隠蔽性インキ層が付され、溶融状態の該熱溶融
性物質を不可逆的に吸収し得る紙製基材が、それと略同
じ厚みの中敷シートの穴に嵌まって支持体シートに貼付
されており、該インキ層と該中敷シートとが透明な樹脂
製の保護フィルムで平坦に被覆されていることを特徴と
する温度履歴インジケータ。1. A paper base material having a concealable ink layer containing a heat-meltable substance having a recording temperature as a melting point and capable of irreversibly absorbing the heat-meltable substance in a molten state is substantially the same. The temperature is characterized in that the ink layer and the insole sheet are fitted on the holes of the insole sheet and attached to the support sheet, and the ink layer and the insole sheet are flatly covered with a transparent resin protective film. History indicator.
が、確認すべき温度で可逆的に変色する示温剤を含有す
るインキ層を有していることを特徴とする請求項１に記
載の温度履歴インジケータ。2. The temperature according to claim 1, wherein the insole sheet or the support sheet has an ink layer containing a temperature indicator that reversibly changes color at a temperature to be confirmed. History indicator.