JP2003165278A - Thermal transfer film and thermal transfer recording medium - Google Patents
Thermal transfer film and thermal transfer recording mediumInfo
- Publication number
- JP2003165278A JP2003165278A JP2001367204A JP2001367204A JP2003165278A JP 2003165278 A JP2003165278 A JP 2003165278A JP 2001367204 A JP2001367204 A JP 2001367204A JP 2001367204 A JP2001367204 A JP 2001367204A JP 2003165278 A JP2003165278 A JP 2003165278A
- Authority
- JP
- Japan
- Prior art keywords
- thermal transfer
- layer
- recording medium
- image
- transfer film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、基材上の一方の面
に、熱可塑性樹脂を主成分とする熱転写層を基材から最
も遠い位置に形成した熱転写フィルムと、基材上の少な
くとも一方に熱可塑性樹脂と着色剤とを含有する熱転写
インク層を形成した熱転写記録媒体とを組み合わせて画
像形成する、熱転写フィルム及び熱転写記録媒体に関す
るものである。TECHNICAL FIELD The present invention relates to a thermal transfer film having a thermal transfer layer containing a thermoplastic resin as a main component on one surface of a base material at a position farthest from the base material, and at least one of the surface of the base material. The present invention relates to a thermal transfer film and a thermal transfer recording medium for forming an image by combining with a thermal transfer recording medium having a thermal transfer ink layer containing a thermoplastic resin and a colorant.
【０００２】[0002]
【従来の技術】熱転写方式は、可変情報を簡便に記録す
ることができるため、各種の用途で広く利用されてい
る。この方式は、基材上に色材層が設けられた熱転写フ
ィルムと、必要に応じて受容層が設けられた被転写体と
を、サーマルヘッド等の加熱デバイスとプラテンロール
との間に圧接し、画像情報に応じて加熱デバイスの発熱
部分を選択的に発熱させ、熱転写フィルム上の色材層に
含まれる色材を被転写体に移行させることにより画像を
記録する方式である。この方法は、溶融熱転写方式と昇
華熱転写方式に大別される。2. Description of the Related Art The thermal transfer system is widely used for various purposes because it can record variable information easily. In this method, a thermal transfer film in which a color material layer is provided on a base material and a transfer target in which a receiving layer is provided as necessary are pressed between a heating device such as a thermal head and a platen roll. In this method, an image is recorded by selectively heating the heating portion of the heating device according to the image information and transferring the color material contained in the color material layer on the thermal transfer film to the transfer target. This method is roughly classified into a melt heat transfer method and a sublimation heat transfer method.
【０００３】溶融熱転写方式は、溶融インキ層を担持し
た熱転写フィルムを、上述したような加熱手段によって
加熱し、軟化した溶融インキ層成分を天然繊維紙または
プラスチックシート等の被転写体上に転写させて画像を
形成する方法である。ここで用いる溶融インキ層は、顔
料等の色材を熱溶融性のワックスまたは樹脂等のバイン
ダーに分散させたものであり、プラスチックフィルム等
の基材に担持させている。形成される画像は、高濃度で
鮮鋭性に優れており、文字、線画等の２値画像の記録に
適している。In the melt heat transfer system, a heat transfer film carrying a melted ink layer is heated by the above-mentioned heating means to transfer the softened melted ink layer component onto a transfer object such as natural fiber paper or a plastic sheet. Is a method of forming an image. The molten ink layer used here is a color material such as a pigment dispersed in a hot-melt wax or a binder such as a resin, and is carried on a substrate such as a plastic film. The formed image has high density and excellent sharpness, and is suitable for recording binary images such as characters and line drawings.
【０００４】昇華転写方式は、昇華染料層を担持した熱
転写フィルムを、上述のような加熱手段によって加熱
し、染料層中に含まれる昇華染料を昇華させて被転写体
上に設けられた受容層に移行させて画像を形成する方法
である。ここで用いられる昇華染料は、色材として用い
る昇華染料をバインダー樹脂に溶解または分散させたも
のであり、プラスチックフィルム等の基材フィルムに担
持させている。この方式は、サーマルヘッド等の加熱デ
バイスに加えるエネルギー量によって、ドット単位で染
料の移行量を制御できるため、濃度変調による階調再現
が可能である。In the sublimation transfer system, a thermal transfer film carrying a sublimation dye layer is heated by the above-mentioned heating means to sublimate the sublimation dye contained in the dye layer to provide a receiving layer provided on a transfer target. It is a method of forming an image by shifting to. The sublimation dye used here is a sublimation dye used as a coloring material dissolved or dispersed in a binder resin, and is carried on a base film such as a plastic film. In this method, the amount of energy transferred to a heating device such as a thermal head can control the amount of dye transfer in dot units, so that gradation reproduction by density modulation is possible.
【０００５】このように、溶融熱転写方式は、文字や数
字等の画像を容易に且つくっきりと形成することがで
き、また、昇華転写方式は、階調表現に優れ顔写真等の
画像を精密に美しく形成することができるといった、そ
れぞれに特徴がある。ところが、溶融熱転写方式による
画像は、耐久性、特に耐摩耗性に劣るという欠点があ
る。また、昇華転写方式による画像は、通常の印刷イン
キによるものとは異なり、ビヒクルが無いために、耐光
性、耐候性、耐摩耗性、耐薬品性等の耐久性に劣るとい
う問題がある。As described above, the fusion thermal transfer method can easily and clearly form an image such as letters and numbers, and the sublimation transfer method is excellent in gradation expression and can precisely form an image such as a facial photograph. Each has its own characteristics, such as being beautifully formed. However, the image obtained by the fusion heat transfer method has a drawback that it is inferior in durability, particularly abrasion resistance. Further, an image obtained by the sublimation transfer method has a problem that it is inferior in durability such as light resistance, weather resistance, abrasion resistance and chemical resistance because it does not have a vehicle, unlike an image formed by a normal printing ink.
【０００６】そこで、上記の問題に対して、特開平９−
１１６７４号公報等で記載しているように、熱転写画像
の情報の上に、保護層を転写して、耐久性をもたせるこ
とが行なわれている。上記の保護層の転写は、転写され
る保護層を均一に、かつ指定した位置に指定した大きさ
で正確に、転写する必要がある。そのために、保護層転
写の感度を向上させるために、保護層を構成する樹脂の
ガラス転移温度や熱軟化温度を低めにする結果、保護層
転写シートの保存性が低下し、保護層転写シートの巻取
り保管中にブロッキングが発生しやすい等の問題があ
る。Therefore, in order to solve the above problem, Japanese Patent Laid-Open No. 9-
As described in Japanese Patent No. 11674, etc., a protective layer is transferred onto the information of the thermal transfer image so as to have durability. In the transfer of the above-mentioned protective layer, it is necessary to transfer the transferred protective layer uniformly and accurately in a designated position at a designated size. Therefore, in order to improve the sensitivity of the protective layer transfer, as a result of lowering the glass transition temperature and the thermal softening temperature of the resin forming the protective layer, the storage stability of the protective layer transfer sheet decreases, There is a problem that blocking easily occurs during winding and storage.
【０００７】[0007]
【発明が解決しようとする課題】したがって、本発明
は、このような問題に着目してなされたものであり、得
られる画像形成物の耐摩耗性、耐光性等の耐久性に優
れ、かつ転写感度が良好で、巻取り保管中のブロッキン
グを防止した熱転写フィルム及び熱転写記録媒体を提供
することを目的とする。SUMMARY OF THE INVENTION Therefore, the present invention has been made in view of such a problem, and the obtained image formed article has excellent durability such as abrasion resistance and light resistance, and can be transferred. An object of the present invention is to provide a thermal transfer film and a thermal transfer recording medium which have good sensitivity and prevent blocking during winding and storage.
【０００８】[0008]
【課題を解決するための手段】上記目的を達成するため
に、本発明は、基材上の一方の面に、熱可塑性樹脂を主
成分とする熱転写層を基材から最も遠い位置に形成した
熱転写フィルムと、基材上の少なくとも一方に熱可塑性
樹脂と着色剤とを含有する熱転写インク層を形成した熱
転写記録媒体とを、熱転写フィルムの熱転写層と熱転写
記録媒体の熱転写インク層が対向するように重ね合せ、
像様に加熱することによって熱転写記録媒体の熱転写イ
ンク層または熱転写インク層に含有する着色剤を像様に
熱転写フィルムの熱転写層に転写することで一旦熱転写
フィルムに逆像を画像形成した後、画像形成された熱転
写フィルムの熱転写層と被画像形成体の画像形成面とを
対向するように重ね合せ、熱転写フィルムの熱転写層と
は反対側から加熱することによって、画像形成された熱
転写層ごと被画像形成体に転写することによって、被画
像形成体に画像形成する画像形成方法に用いる熱転写フ
ィルム及び熱転写記録媒体において、熱転写フィルムの
熱転写層に含有される熱可塑性樹脂と、熱転写記録媒体
の熱転写インク層に含有される熱可塑性樹脂とが、いず
れもメタクリレート系モノマーの単独重合体または共重
合体であることを特徴とする。In order to achieve the above-mentioned object, the present invention forms a thermal transfer layer containing a thermoplastic resin as a main component on one surface of a substrate at a position farthest from the substrate. A thermal transfer film and a thermal transfer recording medium in which a thermal transfer ink layer containing a thermoplastic resin and a colorant is formed on at least one side of a substrate so that the thermal transfer layer of the thermal transfer film and the thermal transfer ink layer of the thermal transfer recording medium face each other. On the
By imagewise heating, the thermal transfer ink layer of the thermal transfer recording medium or the colorant contained in the thermal transfer ink layer is imagewise transferred to the thermal transfer layer of the thermal transfer film to form a reverse image on the thermal transfer film. The thermal transfer layer of the formed thermal transfer film and the image forming surface of the image forming body are superposed so as to face each other, and heating is performed from the side opposite to the thermal transfer layer of the thermal transfer film, so that the image formed thermal transfer layer is imaged together. In a thermal transfer film and a thermal transfer recording medium used in an image forming method for forming an image on an image forming body by transferring to a formed body, a thermoplastic resin contained in the thermal transfer layer of the thermal transfer film and a thermal transfer ink layer of the thermal transfer recording medium. That the thermoplastic resin contained in is a homopolymer or copolymer of methacrylate monomers. And butterflies.
【０００９】前記に記載の熱転写フィルムの熱転写層に
含有されるメタクリレート系モノマーの単独重合体また
は共重合体のガラス転移点が４０〜１１０℃、数平均分
子量が１５０００〜８００００であることが好ましく、
得られる画像形成物の耐久性向上、転写感度の向上、巻
取り保管中の耐ブロッキング性の向上等が図られ、優れ
た効果を発揮できる。また、前記に記載の熱転写フィル
ムの熱転写層に含有されるメタクリレート系モノマーの
単独重合体または共重合体、または熱転写記録媒体の熱
転写インク層に含有されるメタクリレート系モノマーの
単独重合体または共重合体の少なくともいずれか一方
に、メタクリレート成分としてイソブチルメタクリレー
ト、ノルマルブチルメタクリレート、及びターシャリー
ブチルメタクリレートから選ばれる少なくとも１種以上
を含有することが好ましく、得られる画像形成物で熱転
写層が保護層となった時の耐摩耗性、耐光性等の耐久性
により優れたものとなる。The homopolymer or copolymer of the methacrylate monomer contained in the thermal transfer layer of the thermal transfer film described above preferably has a glass transition point of 40 to 110 ° C. and a number average molecular weight of 15,000 to 80,000,
The resulting image-formed product has improved durability, improved transfer sensitivity, improved blocking resistance during winding and storage, and the like, and can exhibit excellent effects. Further, a homopolymer or copolymer of a methacrylate monomer contained in the thermal transfer layer of the thermal transfer film described above, or a homopolymer or copolymer of a methacrylate monomer contained in the thermal transfer ink layer of the thermal transfer recording medium. It is preferable that at least one of them contains at least one or more selected from isobutyl methacrylate, normal butyl methacrylate, and tertiary butyl methacrylate as a methacrylate component. In the obtained image-formed product, the thermal transfer layer became a protective layer. It becomes more excellent in durability such as abrasion resistance and light resistance at the time.
【００１０】前記に記載の熱転写フィルムの熱転写層に
含有されるメタクリレート系モノマーの単独重合体また
は共重合体、または熱転写記録媒体の熱転写インク層に
含有されるメタクリレート系モノマーの単独重合体また
は共重合体の少なくともいずれか一方が、メチルメタク
リレート／イソブチルメタクリレート共重合体であるこ
とが好ましく、得られる画像形成物で熱転写層が保護層
となった時の耐摩耗性、耐光性等の耐久性や、転写性、
定着性が優れ、また、ガラス転移点を４０〜１１０℃、
数平均分子量を１５０００〜８００００の範囲のメタク
リレート系モノマーの共重合体に調整しやすい。A homopolymer or copolymer of a methacrylate monomer contained in the thermal transfer layer of the thermal transfer film described above, or a homopolymer or a copolymer of a methacrylate monomer contained in the thermal transfer ink layer of the thermal transfer recording medium. At least one of the coalesces is preferably a methylmethacrylate / isobutylmethacrylate copolymer, and the resulting image-formed product has abrasion resistance when the thermal transfer layer serves as a protective layer, durability such as light resistance, Transferability,
It has excellent fixability and has a glass transition point of 40 to 110 ° C.
It is easy to adjust the number average molecular weight of the copolymer of the methacrylate monomer in the range of 15,000 to 80,000.
【００１１】[0011]
【作用】本発明の熱転写フィルム及び熱転写記録媒体
は、基材上の一方の面に、熱可塑性樹脂を主成分とする
熱転写層を基材から最も遠い位置に形成した熱転写フィ
ルムと、基材上の少なくとも一方に熱可塑性樹脂と着色
剤とを含有する熱転写インク層を形成した熱転写記録媒
体とを、互いに熱転写層と熱転写インク層が対向するよ
うに重ね合せ、像様に加熱することによって熱転写記録
媒体の熱転写インク層または熱転写インク層に含有する
着色剤を像様に熱転写フィルムの熱転写層に転写するこ
とで一旦熱転写フィルムに逆像を画像形成した後、画像
形成された熱転写フィルムの熱転写層と被画像形成体の
画像形成面とを対向するように重ね合せ、画像形成され
た熱転写層ごと被画像形成体に転写することによって、
被画像形成体に画像形成するものであり、熱転写フィル
ムの熱転写層に含有される熱可塑性樹脂と、熱転写記録
媒体の熱転写インク層に含有される熱可塑性樹脂とが、
いずれもメタクリレート系モノマーの単独重合体または
共重合体とした。これにより、熱転写フィルムの熱転写
層と熱転写記録媒体の熱転写インク層との両者の相溶性
が高くなり、熱転写層に転写される熱転写インク層の定
着性が高まり、得られる画像形成物の耐摩耗性、耐光性
等の耐久性に優れたものとなる。The thermal transfer film and the thermal transfer recording medium of the present invention include a thermal transfer film having a thermal transfer layer mainly composed of a thermoplastic resin formed on one surface of a substrate at a position farthest from the substrate, and the thermal transfer film on the substrate. A thermal transfer recording medium on which a thermal transfer ink layer containing a thermoplastic resin and a colorant is formed on at least one of the above, so that the thermal transfer layer and the thermal transfer ink layer face each other, and the image is heated in an imagewise manner to perform thermal transfer recording. The thermal transfer ink layer of the medium or the colorant contained in the thermal transfer ink layer is image-wise transferred to the thermal transfer layer of the thermal transfer film to form an inverse image on the thermal transfer film, and then the thermal transfer layer of the imaged thermal transfer film is formed. By superposing the image forming surface of the image formed body so as to face each other and transferring the image formed thermal transfer layer to the image formed body,
An image is formed on the image forming body, and the thermoplastic resin contained in the thermal transfer layer of the thermal transfer film and the thermoplastic resin contained in the thermal transfer ink layer of the thermal transfer recording medium,
All of them were homopolymers or copolymers of methacrylate monomers. As a result, the compatibility of both the thermal transfer layer of the thermal transfer film and the thermal transfer ink layer of the thermal transfer recording medium is increased, the fixability of the thermal transfer ink layer transferred to the thermal transfer layer is enhanced, and the abrasion resistance of the resulting image-formed product is increased. , And has excellent durability such as light resistance.
【００１２】[0012]
【発明の実施の形態】以下に、好ましい実施の形態を挙
げて、本発明を更に詳しく説明する。図１は、本発明の
熱転写フィルム１である一つの実施形態を示す断面図で
あり、基材２上に熱転写層３が設けられ、その熱転写層
３が基材２から最も遠い位置にある。この熱転写フィル
ム１は熱転写層３と接するように被転写体を対向させ
て、基材２の裏面側からサーマルヘッドやレーザー等に
よる加熱により、被転写体に熱転写層３が転写される。
図２は本発明の熱転写フィルム１である他の実施形態を
示す断面図であり、基材２上に離型層４、熱転写層３が
この順に積層し、熱転写層３が基材２から最も遠い位置
にある。そして、基材２の他方の面に背面層６を設けた
ものである。図２の熱転写フィルムの場合、熱転写フィ
ルム１の熱転写層３と接するように被転写体を対向させ
て、背面層６側からサーマルヘッドやレーザー等による
加熱により、被転写体に熱転写層３が転写され、離型層
４は基材２側に残存する。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in more detail below with reference to preferred embodiments. FIG. 1 is a cross-sectional view showing one embodiment of the thermal transfer film 1 of the present invention, in which a thermal transfer layer 3 is provided on a base material 2, and the thermal transfer layer 3 is at the farthest position from the base material 2. In this thermal transfer film 1, the transfer target is opposed to be in contact with the thermal transfer layer 3, and the thermal transfer layer 3 is transferred to the transfer target from the back surface side of the base material 2 by heating with a thermal head or a laser.
FIG. 2 is a cross-sectional view showing another embodiment of the thermal transfer film 1 of the present invention, in which the release layer 4 and the thermal transfer layer 3 are laminated in this order on the base material 2, and the thermal transfer layer 3 is most It is in a distant position. Then, the back surface layer 6 is provided on the other surface of the base material 2. In the case of the thermal transfer film of FIG. 2, the transfer target is placed so as to be in contact with the thermal transfer layer 3 of the thermal transfer film 1, and the thermal transfer layer 3 is transferred to the transfer target from the back layer 6 side by heating with a thermal head or a laser. The release layer 4 remains on the base material 2 side.
【００１３】図３は本発明の熱転写フィルム１である他
の実施形態を示す断面図であり、基材２上に剥離層５、
熱転写層３がこの順に積層し、熱転写層３が基材２から
最も遠い位置にある。図３の熱転写フィルムの場合、熱
転写フィルム１の熱転写層３と接するように被転写体を
対向させて、基材２の裏面側からサーマルヘッドやレー
ザー等による加熱により、被転写体に剥離層５、熱転写
層３が転写される。また、図４は本発明の熱転写フィル
ム１である他の実施形態を示す断面図であり、基材２上
に離型層４、剥離層５、熱転写層３がこの順に積層し、
熱転写層３が基材２から最も遠い位置にある。図４の熱
転写フィルムの場合、熱転写フィルム１の熱転写層３と
接するように被転写体を対向させて、基材２の裏面側か
らサーマルヘッドやレーザー等による加熱により、被転
写体に剥離層５、熱転写層３が転写され、離型層４は基
材２側に残存する。FIG. 3 is a sectional view showing another embodiment of the thermal transfer film 1 of the present invention.
The thermal transfer layers 3 are laminated in this order, and the thermal transfer layers 3 are located farthest from the base material 2. In the case of the thermal transfer film shown in FIG. 3, the transfer target is placed so as to be in contact with the thermal transfer layer 3 of the thermal transfer film 1, and the release layer 5 is applied to the transfer target by heating from the back side of the base material 2 with a thermal head or a laser. The thermal transfer layer 3 is transferred. FIG. 4 is a cross-sectional view showing another embodiment of the thermal transfer film 1 of the present invention, in which a release layer 4, a release layer 5, and a thermal transfer layer 3 are laminated in this order on a substrate 2.
The thermal transfer layer 3 is located farthest from the base material 2. In the case of the thermal transfer film shown in FIG. 4, the transfer target is placed so as to be in contact with the thermal transfer layer 3 of the thermal transfer film 1, and the release layer 5 is applied to the transfer target by heating from the back side of the substrate 2 with a thermal head or a laser. The thermal transfer layer 3 is transferred, and the release layer 4 remains on the base material 2 side.
【００１４】また、本発明の熱転写記録媒体は、基材上
の少なくとも一方に熱可塑性樹脂と着色剤とを含有する
熱転写インク層を形成した構成であり、その熱転写記録
媒体と、熱転写フィルムとを組み合わせて画像形成を行
なう。その画像形成方法の一例を説明する概略図を図５
に示した。基材２１上の一方に熱転写層３を設けた、す
なわち基材２１上の一方の面に熱転写層３を、基材２１
から最も遠い位置に形成した熱転写フィルム１と、基材
２２上の少なくとも一方に熱可塑性樹脂と着色剤とを含
有する熱転写インク層８を形成した熱転写記録媒体７と
を、熱転写フィルム１の熱転写層３と熱転写記録媒体７
の熱転写インク層８が対向するように重ね合せ、像様に
加熱する。その加熱条件は、サーマルヘッド１１による
加熱で、熱転写フィルム１と熱転写記録媒体７を、サー
マルヘッド１１とプラテンロール１２との間に挟み込
み、この場合は熱転写記録媒体７の熱転写インク層８の
設けてある面と反対側からサーマルヘッド１１で像様に
加熱する。（図５（１）参照）The thermal transfer recording medium of the present invention has a structure in which a thermal transfer ink layer containing a thermoplastic resin and a colorant is formed on at least one side of a substrate, and the thermal transfer recording medium and the thermal transfer film are formed. Image formation is performed in combination. FIG. 5 is a schematic diagram illustrating an example of the image forming method.
It was shown to. The thermal transfer layer 3 is provided on one side of the base material 21, that is, the thermal transfer layer 3 is provided on one side of the base material 21.
The thermal transfer film 1 formed at the position farthest from the thermal transfer recording medium 7 and the thermal transfer recording medium 7 having the thermal transfer ink layer 8 containing the thermoplastic resin and the colorant formed on at least one side of the substrate 22. 3 and thermal transfer recording medium 7
The thermal transfer ink layers 8 are superposed so as to face each other, and are heated imagewise. The heating condition is that the thermal transfer film 1 and the thermal transfer recording medium 7 are sandwiched between the thermal head 11 and the platen roll 12 by heating with the thermal head 11, and in this case, the thermal transfer ink layer 8 of the thermal transfer recording medium 7 is provided. The thermal head 11 imagewise heats from the side opposite to a certain surface. (See Figure 5 (1))
【００１５】上記の加熱後に、熱転写フィルム１と熱転
写記録媒体７とを重ね合せた状態から、両者を離して、
熱転写記録媒体７の熱転写インク層８または熱転写イン
ク層８に含有する着色剤が像９として熱転写フィルム１
の熱転写層３に転写する。但し、この像９はＡに示す向
きで見た場合、逆像（鏡像）として形成し、Ｂの方向か
らこの像９を観察すれば正像となる。（図５（２）参
照）
次に上記の画像９を形成した熱転写フィルム１の熱転写
層３と被画像形成体１０の画像形成面とを対向するよう
に重ね合せ、熱転写フィルム１の熱転写層３とは反対側
から、ヒートロール１３の熱源により加熱する。尚、ヒ
ートロール１３による加熱において、熱転写フィルム１
と被画像形成体１０は、ヒートロール１３とプラテンロ
ール１２との間に挟まれて、加熱及び加圧される。（図
５（３）参照）
そして、その加熱後に、熱転写フィルム１と被画像形成
体１０とを重ね合せた状態から、両者を離して、熱転写
フィルム１の像９、熱転写層３が、ヒートロール１３で
加熱された部分で、被画像形成体１０上に転写される。
（図５（４）参照）After the above heating, the thermal transfer film 1 and the thermal transfer recording medium 7 are placed on top of each other and separated from each other.
The thermal transfer ink layer 8 of the thermal transfer recording medium 7 or the colorant contained in the thermal transfer ink layer 8 forms an image 9 in the thermal transfer film 1
And transferred to the thermal transfer layer 3. However, when this image 9 is viewed in the direction A, it is formed as a reverse image (mirror image), and when this image 9 is observed from the direction B, it becomes a normal image. (See FIG. 5 (2)) Next, the thermal transfer layer 3 of the thermal transfer film 1 on which the image 9 is formed and the image forming surface of the image forming body 10 are superposed so as to face each other, and the thermal transfer layer 3 of the thermal transfer film 1 is placed. It is heated by the heat source of the heat roll 13 from the opposite side. In the heating by the heat roll 13, the thermal transfer film 1
The image forming body 10 is sandwiched between the heat roll 13 and the platen roll 12, and is heated and pressed. (See FIG. 5C.) Then, after heating, the thermal transfer film 1 and the image forming body 10 are separated from each other, and the two are separated from each other, and the image 9 of the thermal transfer film 1 and the thermal transfer layer 3 are heated by the heat roll. The portion heated by 13 is transferred onto the image forming body 10.
(See Fig. 5 (4))
【００１６】上記のような画像形成方法で使用する熱転
写記録媒体７は、基材２２上に熱溶融性インク層または
昇華性染料インク層の熱転写インク層８を形成したもの
であり、いずれのインク層でも選択することができる。
基材上に熱溶融性インク層を設けた熱転写記録媒体の場
合、印字の際に、その熱溶融性インク層が被転写体に転
写される。また、基材上に昇華性染料インク層を設けた
熱転写記録媒体の場合は、印字の際に、昇華性染料イン
ク層に含有する着色剤である昇華性染料が被転写体に転
写される。上記の熱転写記録媒体は、熱転写インク層が
熱溶融性インク層または昇華性染料インク層でも、従来
から使用されているものが用いることができ、限定して
用いるものではない。The thermal transfer recording medium 7 used in the image forming method as described above is one in which a thermal transfer ink layer 8 of a heat-fusible ink layer or a sublimable dye ink layer is formed on a substrate 22, and which ink is used. It can also be selected in layers.
In the case of a thermal transfer recording medium having a heat-meltable ink layer provided on a base material, the heat-meltable ink layer is transferred to the transfer target at the time of printing. Further, in the case of a thermal transfer recording medium in which a sublimable dye ink layer is provided on a substrate, the sublimable dye, which is a colorant contained in the sublimable dye ink layer, is transferred to the transfer target at the time of printing. Regarding the above-mentioned thermal transfer recording medium, even if the thermal transfer ink layer is a heat-fusible ink layer or a sublimable dye ink layer, those conventionally used can be used, and the present invention is not limited to use.
【００１７】次に、熱転写フィルムを構成する各層等に
ついて、詳細に説明する。
（基材）本発明の熱転写フィルムに用いられる基材２、
２１としては、従来の熱転写フィルムに使用されている
ものと同じ基材を、そのまま用いることができると共
に、基材の表面に易接着処理のしてあるものやその他の
ものも使用することができ、特に制限はされない。好ま
しい基材の具体例としては、例えば、ポリエチレンテレ
フタレートを始めとするポリエステル、ポリカーボネー
ト、ポリアミド、ポリイミド、酢酸セルロース、ポリ塩
化ビニリデン、ポリ塩化ビニル、ポリスチレン、フッ素
樹脂、ポリプロピレン、ポリエチレン、アイオノマー等
のプラスチックフィルム、および、グラシン紙、コンデ
ンサー紙、パラフィン紙等の紙類、セロファン等があ
り、また、これらの２種以上を積層した複合フィルムな
ども挙げられる。これらの基材２の厚さは、その強度お
よび耐熱性が適切になるように材料に応じて適宜変更し
ているが、通常は、２〜１００μｍ程度が好ましい。Next, each layer constituting the thermal transfer film will be described in detail. (Substrate) Substrate 2 used for the thermal transfer film of the present invention,
As the material 21, the same base material as used in the conventional thermal transfer film can be used as it is, and also a material having an easy adhesion treatment on the surface of the base material or other materials can be used. , There is no particular limitation. Specific examples of preferable substrates include, for example, polyester films including polyethylene terephthalate, polycarbonate, polyamide, polyimide, cellulose acetate, polyvinylidene chloride, polyvinyl chloride, polystyrene, fluororesin, polypropylene, polyethylene, plastic films such as ionomers. , And papers such as glassine paper, condenser paper, and paraffin paper, cellophane, and the like, and also a composite film in which two or more kinds of these are laminated. The thickness of these base materials 2 is appropriately changed depending on the material so that the strength and heat resistance thereof are appropriate, but normally, about 2 to 100 μm is preferable.
【００１８】（熱転写層）本発明の熱転写フィルムにお
ける基材上に設ける熱転写層３は、基材から最も遠い位
置に、設けられている。熱転写層に形成した熱転写画像
を熱転写層毎、被転写体に転写して、熱転写層がその画
像の保護層として機能し、その画像の耐摩耗性、耐光性
等の耐久性に寄与する。熱転写層は、転写された後の耐
摩擦性、透明性、硬度等に優れ、また転写感度が良好
で、熱転写フィルムの巻取り保管中のブロッキングを防
止できるようにした。すなわち、基材上の一方の面に、
基材から最も遠い位置に、メタクリレート系モノマーの
単独重合体または共重合体を主成分とする熱転写層を形
成した。(Thermal Transfer Layer) The thermal transfer layer 3 provided on the substrate in the thermal transfer film of the present invention is provided at a position farthest from the substrate. The thermal transfer image formed on the thermal transfer layer is transferred to the transfer target for each thermal transfer layer, and the thermal transfer layer functions as a protective layer for the image, and contributes to durability such as abrasion resistance and light resistance of the image. The thermal transfer layer has excellent abrasion resistance, transparency, hardness and the like after being transferred, and has good transfer sensitivity, so that blocking during winding and storage of the thermal transfer film can be prevented. That is, on one side of the substrate,
A thermal transfer layer containing a homopolymer or copolymer of a methacrylate monomer as a main component was formed at a position farthest from the substrate.
【００１９】上記のメタクリレート系モノマーの単独重
合体または共重合体のガラス転移点が４０〜１１０℃、
数平均分子量が１５０００〜８００００であることが好
ましく、得られる画像形成物の耐久性向上、転写感度の
向上、巻取り保管中の耐ブロッキング性の向上等が図ら
れ、優れた効果を発揮できる。上記のメタクリレート系
モノマーの単独重合体または共重合体のガラス転移点が
４０℃未満、あるいは数平均分子量が１５０００未満で
あると、熱転写フィルムの巻取り状態で保管中、ブロッ
キングが生じやすくなる。また、メタクリレート系モノ
マーの単独重合体または共重合体のガラス転移点が１１
０℃を越えたり、あるいは数平均分子量が８００００を
越えると、転写性が低下してくる。The homopolymer or copolymer of the above-mentioned methacrylate monomer has a glass transition point of 40 to 110 ° C.,
The number average molecular weight is preferably from 15,000 to 80,000, whereby the durability of the obtained image-formed product, the transfer sensitivity, the blocking resistance during winding and storage, and the like can be improved, and an excellent effect can be exhibited. If the glass transition point of the homopolymer or copolymer of the above-mentioned methacrylate monomer is less than 40 ° C. or the number average molecular weight is less than 15,000, blocking is likely to occur during storage of the thermal transfer film in a wound state. Further, the glass transition point of a homopolymer or copolymer of a methacrylate monomer is 11
If the temperature exceeds 0 ° C. or the number average molecular weight exceeds 80,000, the transferability will decrease.
【００２０】上記のメタクリレート系モノマーの単独重
合体または共重合体におけるメタクリレート成分として
は、メチルメタアクリレート、エチルメタアクリレー
ト、ノルマルプロピルメタアクリレート、イソプロピル
メタアクリレート、ノルマルブチルメタアクリレート、
イソブチルメタアクリレート、ターシャリーブチルメタ
クリレート、ペンチルメタアクリレート、ノルマルヘキ
シルメタアクリレート、シクロヘキシルメタアクリレー
ト、２−エチルヘキシルメタアクリレート、ノルマルオ
クチルメタアクリレート、イソオクチルメタアクリレー
ト、ラウリルメタアクリレート等が挙げられ、これらは
単独または２種類以上組み合わせて用いることができ
る。上記のメタクリレート成分の中でも、イソブチルメ
タクリレート、ノルマルブチルメタクリレート、及びタ
ーシャリーブチルメタクリレートから選ばれる少なくと
も１種以上を含有することが好ましく、得られる画像形
成物で熱転写層が保護層となった時の耐摩耗性、耐光性
等の耐久性により優れたものとなる。As the methacrylate component in the homopolymer or copolymer of the above-mentioned methacrylate-based monomer, methyl methacrylate, ethyl methacrylate, normal propyl methacrylate, isopropyl methacrylate, normal butyl methacrylate,
Examples thereof include isobutyl methacrylate, tertiary butyl methacrylate, pentyl methacrylate, normal hexyl methacrylate, cyclohexyl methacrylate, 2-ethylhexyl methacrylate, normal octyl methacrylate, isooctyl methacrylate and lauryl methacrylate, which may be used alone or Two or more types can be used in combination. Among the above-mentioned methacrylate components, it is preferable that at least one selected from isobutyl methacrylate, normal butyl methacrylate, and tertiary butyl methacrylate is contained, and the resulting image-formed product is resistant to the thermal transfer layer becoming a protective layer. It becomes more excellent in durability such as abrasion resistance and light resistance.
【００２１】熱転写層に含有するメタクリレート系モノ
マーの単独重合体または共重合体においは、そのメタク
リレート系モノマーとしては、例えば、メチルメタクリ
レート、エチルメタクリレート、ノルマルプロピルメタ
クリレート、イソプロピルメタクリレート、ノルマルブ
チルメタクリレート、イソブチルメタクレリレート、ｓ
ｅｃ−ブチルメタクリレート、シクロヘキシルメタクリ
レート、ベンジルメタクリレート、２−エチルヘキシル
メタクリレート、２−ヒドロキシエチルメタクリレー
ト、２−ヒドロキシプロピルメタクリレート等が挙げら
れる。上記のメタクリレート系モノマーの中でも、メチ
ルメタクリレート／イソブチルメタクリレート共重合体
を用いることが特に好ましく、得られる画像形成物で熱
転写層が保護層となった時の耐摩耗性、耐光性等の耐久
性や、転写性、定着性が優れ、また、ガラス転移点を４
０〜１１０℃、数平均分子量を１５０００〜８００００
の範囲のメタクリレート系モノマーの共重合体に調整し
やすい。In the homopolymer or copolymer of the methacrylate-based monomer contained in the thermal transfer layer, examples of the methacrylate-based monomer include methyl methacrylate, ethyl methacrylate, normal propyl methacrylate, isopropyl methacrylate, normal butyl methacrylate and isobutyl meta. Clerate, s
Examples thereof include ec-butyl methacrylate, cyclohexyl methacrylate, benzyl methacrylate, 2-ethylhexyl methacrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate and the like. Among the above-mentioned methacrylate-based monomers, it is particularly preferable to use a methyl methacrylate / isobutyl methacrylate copolymer, and the resulting image-formed product has durability such as abrasion resistance and light resistance when the thermal transfer layer serves as a protective layer. It has excellent transferability and fixability, and has a glass transition point of 4
0 to 110 ° C, number average molecular weight of 15,000 to 80,000
It is easy to adjust to a copolymer of a methacrylate monomer in the range of.
【００２２】熱転写フィルムの熱転写層には、その熱転
写層が被画像形成体に転写した後の画像形成物における
耐摩擦性を向上させるために、滑剤を加えることができ
る。その滑剤としては、ワックス、界面活性剤等が挙げ
られる。ワックスを具体的に例示すると、蜜蝋、鯨蝋、
木蝋、米ぬか蝋、カルナバワックス、キャンデリラワッ
クス、モンタンワックス等の天然ワックス；パラフィン
ワックス、マイクロクリスタリンワックス、酸化ワック
ス、オゾケライト、セレシン、エステルワックス、ポリ
エチレンワックス等の合成ワックスが挙げられる。特
に、融点７０℃以上のワックスが好ましく、熱転写フィ
ルムの巻取り状態での保管中、あるいは画像形成物の保
管中、ブロッキングが生じにくい。A lubricant can be added to the thermal transfer layer of the thermal transfer film in order to improve the abrasion resistance of the image-formed product after the thermal transfer layer has been transferred to the image forming body. Examples of the lubricant include waxes and surfactants. Specific examples of waxes include beeswax, spermaceti,
Natural waxes such as wood wax, rice bran wax, carnauba wax, candelilla wax, and montan wax; synthetic waxes such as paraffin wax, microcrystalline wax, oxidized wax, ozokerite, ceresin, ester wax, and polyethylene wax. In particular, a wax having a melting point of 70 ° C. or higher is preferable, and blocking is less likely to occur during storage of the thermal transfer film in a wound state or during storage of the image formed product.
【００２３】また、上記滑剤として、界面活性剤として
は、燐酸系やフッ素系のものが挙げられる。また滑剤と
して、高級脂肪族アルコール、オルガノポリシロキサン
等も挙げられる。このような滑剤は、乾燥状態の熱転写
層に対して、０．５〜１０重量％の割合で含有すること
が好ましく、この範囲より少ないと、充分な耐摩擦性が
付与できず、またこの範囲より多すぎる含有量になる
と、熱転写層の被画像形成体への接着性が低下してくる
等、支障が出てくる。As the above-mentioned lubricant, examples of the surfactant include phosphoric acid type and fluorine type. Further, examples of the lubricant include higher aliphatic alcohols and organopolysiloxanes. Such a lubricant is preferably contained in a proportion of 0.5 to 10% by weight with respect to the dry heat transfer layer, and if it is less than this range, sufficient abrasion resistance cannot be imparted, and in this range If the content is too large, problems such as a decrease in the adhesiveness of the thermal transfer layer to the image forming body may occur.
【００２４】熱転写層は、上記の熱転写層用の樹脂に必
要な添加剤を加えたものを、適当な有機溶剤に溶解した
り或いは有機溶剤や水に分散した分散体を、例えば、グ
ラビアコート、グラビアリバースコート、ロールコート
等の形成手段により、基材上に塗布及び乾燥することに
より形成される。熱転写層は任意の厚みに形成すること
ができるが、好ましくは、乾燥後の厚みで０．１〜５０
ｇ／ｍ2であり、更に好ましくは０．２〜１０ｇ／ｍ2で
ある。The thermal transfer layer is prepared by dissolving the above resin for the thermal transfer layer with necessary additives in an appropriate organic solvent or dispersing it in an organic solvent or water, for example, a gravure coat, It is formed by coating and drying the base material by a forming means such as gravure reverse coat or roll coat. The thermal transfer layer can be formed to have an arbitrary thickness, but the thickness after drying is preferably 0.1 to 50.
g / m 2 , and more preferably 0.2 to 10 g / m 2 .
【００２５】本発明における熱転写フィルムは、基材上
に剥離可能に熱転写層を設けるが、基材上に離型層４を
介して、熱転写層を設けて、加熱により熱転写層を基材
からより剥離し易くすることができる。この離型層は熱
転写の際に、基材から剥離せずに、基材側に残存する。
（離型層）熱転写フィルムにおいて、基材と熱転写性層
の材質の組合せによっては熱転写の際の離型性が十分で
ない場合がある。このような場合、基材上に予め離型層
４を設けることができる。離型層は、ポリビニルアセタ
ール樹脂、ポリビニルブチラール樹脂、ポリビニルアル
コール樹脂、シリコーン樹脂、フッ素樹脂、アクリル樹
脂、ウレタン樹脂、酢酸セルロース等のセルロース系樹
脂や、ワックス類、シリコーンワックス等から構成する
ことができる。熱転写層の転写性をより向上させるため
に、離型層の主成分をポリビニルアセタール、ポリビニ
ルブチラール、ポリビニルアルコールから選ばれる少な
くとも１種以上の樹脂であることが好ましい。In the heat transfer film of the present invention, a heat transfer layer is provided on a base material in a peelable manner. The heat transfer layer is provided on the base material via the release layer 4, and the heat transfer layer is removed from the base material by heating. It can be easily peeled off. This release layer does not separate from the substrate during thermal transfer and remains on the substrate side. (Release Layer) In the thermal transfer film, the releasability at the time of thermal transfer may not be sufficient depending on the combination of the material of the substrate and the thermal transfer layer. In such a case, the release layer 4 can be provided in advance on the base material. The release layer can be composed of polyvinyl acetal resin, polyvinyl butyral resin, polyvinyl alcohol resin, silicone resin, fluororesin, acrylic resin, urethane resin, cellulose resin such as cellulose acetate, waxes, silicone wax and the like. . In order to further improve the transferability of the thermal transfer layer, the main component of the release layer is preferably at least one resin selected from polyvinyl acetal, polyvinyl butyral and polyvinyl alcohol.
【００２６】上記のような離型層を構成する成分の塗布
液を、従来公知のグラビアコート、グラビアリバースコ
ート等の方法で塗布、乾燥することにより形成でき、塗
膜の厚さは０．０１〜２ｇ／ｍ2程度で充分である。
尚、離型層に使用する材料を選択する際に、注意しなけ
ればならない点としては、熱転写層と適切な離型性を有
することは勿論のことであるが、更に、熱転写層との接
着力よりも基材との接着力を高くすることが重要であ
り、もし基材との接着力が十分でない場合には、離型層
ごと熱転写層が転写される等の異常転写の原因となる。
また、転写後の印画物において艶消しの表面外観が望ま
しい場合には、離型層中に各種の粒子を包含させるか、
或いは、離型層側表面をマット処理した基材を使用する
ことにより、熱転写層を転写した印画物の表面をマット
状にすることもできる。It can be formed by applying and drying the coating solution of the components constituting the release layer as described above by a conventionally known method such as gravure coating and gravure reverse coating. The thickness of the coating film is 0.01. About 2 g / m 2 is sufficient.
It should be noted that when selecting the material used for the release layer, it should be noted that the material has proper release properties with respect to the thermal transfer layer. It is important to increase the adhesive strength with the base material rather than the force, and if the adhesive strength with the base material is insufficient, it may cause abnormal transfer such as transfer of the thermal transfer layer with the release layer. .
When a matte surface appearance is desired in the printed matter after transfer, various particles may be included in the release layer, or
Alternatively, the surface of the printed matter on which the thermal transfer layer has been transferred can be made into a mat-like shape by using a base material having the release layer side surface matte-treated.
【００２７】本発明における熱転写フィルムは、基材上
に剥離可能に熱転写層を設けるが、基材上に剥離層５を
介して、熱転写層を設けて、加熱により熱転写層を基材
からより剥離し易くすることができる。この剥離層は熱
転写の際に、基材から剥離可能なものである。
（剥離層）剥離層５は、アクリル樹脂、ポリビニルアル
コール樹脂、ポリビニルアセタール樹脂、ポリビニルブ
チラール樹脂、塩化ビニル−酢酸ビニル共重合体、塩素
化ポリオレフィン、シリコーン樹脂、フッ素樹脂、セル
ロース誘導体樹脂等、及びこれらの樹脂群の共重合体、
ワックス類、シリコーンワックス等を含有することがで
きる。剥離層は、その主成分がメタクリレート系モノマ
ーの単独重合体または共重合体であることが好ましく、
熱転写層、剥離層の転写された画像形成物の耐摩耗性等
の耐久性がより向上する。In the heat transfer film of the present invention, a heat transfer layer is provided on a base material so that it can be peeled off. A heat transfer layer is provided on the base material via a release layer 5, and the heat transfer layer is peeled from the base material by heating. It can be made easier. This peeling layer can be peeled off from the substrate during thermal transfer. (Release Layer) The release layer 5 is an acrylic resin, a polyvinyl alcohol resin, a polyvinyl acetal resin, a polyvinyl butyral resin, a vinyl chloride-vinyl acetate copolymer, a chlorinated polyolefin, a silicone resin, a fluororesin, a cellulose derivative resin, or the like, and these. Copolymer of resin group,
Waxes, silicone wax, etc. may be contained. The release layer, the main component is preferably a homopolymer or copolymer of a methacrylate monomer,
Durability such as abrasion resistance of the image formed by transferring the thermal transfer layer and the release layer is further improved.
【００２８】上記のメタクリレート系モノマーとして
は、例えば、メチルメタクリレート、エチルメタクリレ
ート、ｎ−プロピルメタクリレート、ｉ−プロピルメタ
クリレート、ｎ−ブチルメタクリレート、ｉ−ブチルメ
タクレリレート、ｓｅｃ−ブチルメタクリレート、シク
ロヘキシルメタクリレート、ベンジルメタクリレート、
２−エチルヘキシルメタクリレート、２−ヒドロキシエ
チルメタクリレート、２−ヒドロキシプロピルメタクリ
レート等が挙げられる。上記のような剥離層を構成する
成分を含有する塗工液を、従来公知のグラビア印刷法、
スクリーン印刷法、グラビア版を用いたリバースロール
コーティング法等の形成手段により、塗布し、乾燥し
て、形成することができる。剥離層の厚みは、乾燥状態
で０．０１〜５ｇ／ｍ2程度である。Examples of the above-mentioned methacrylate-based monomers include methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, i-propyl methacrylate, n-butyl methacrylate, i-butyl methacrylic acid, sec-butyl methacrylate, cyclohexyl methacrylate and benzyl. Methacrylate,
2-ethylhexyl methacrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate and the like can be mentioned. A coating liquid containing the components constituting the release layer as described above, a conventionally known gravure printing method,
It can be formed by coating and drying by a forming means such as a screen printing method or a reverse roll coating method using a gravure plate. The thickness of the release layer is about 0.01 to 5 g / m 2 in a dry state.
【００２９】また、熱転写フィルムには、基材上に設け
た熱転写層の上に接着層を設けて、熱転写の際に被転写
体との定着性を向上させることも可能である。この接着
層は、加熱により接着性を発現する材料を選択すること
が好ましく、例えば、熱可塑性の合成樹脂、天然樹脂、
ゴム、ワックス等を用いて、上記の剥離層と同様の形成
手段により、形成することができる。接着層の厚みは、
０．０１〜５ｇ／ｍ2程度である。Further, in the thermal transfer film, it is possible to provide an adhesive layer on the thermal transfer layer provided on the base material to improve the fixing property to the transferred material at the time of thermal transfer. For this adhesive layer, it is preferable to select a material that exhibits adhesiveness by heating, and examples thereof include thermoplastic synthetic resin, natural resin,
It can be formed using rubber, wax or the like by the same forming means as the above-mentioned release layer. The thickness of the adhesive layer is
It is about 0.01 to 5 g / m 2 .
【００３０】（背面層）また、熱転写フィルムの基材に
対し、その基材の熱転写層の設けてある面と反対側の面
に、サーマルヘッド等との粘着を防止し、且つ、滑り性
を良くするために、背面層６を設けることが可能であ
る。この背面層に用いる樹脂としては、例えば、エチル
セルロース、ヒドロキシセルロース、ヒドロキシプロピ
ルセルロース、メチルセルロース、酢酸セルロース、酢
酪酸セルロース、ニトロセルロース等のセルロース系樹
脂、ポリビニルアルコール、ポリ酢酸ビニル、ポリビニ
ルブチラール、ポリビニルアセタール、ポリビニルピロ
リドン等のビニル系樹脂、ポリメタクリル酸メチル、ポ
リアクリル酸エチル、ポリアクリルアミド、アクリロニ
トリルースチレン共重合体等のアクリル系樹脂、ポリア
ミド樹脂、ポリビニルトルエン樹脂、クマロンインデン
樹脂、ポリエステル系樹脂、ポリウレタン樹脂、シリコ
ーン変性又はフッ素変性ウレタン等の天然又は合成樹脂
の単体又は混合物が用いられる。背面層の耐熱性をより
高めるために上記の樹脂のうち、水酸基系の反応性基を
有している樹脂を使用し、架橋剤としてポリイソシアネ
ート等を併用して、架橋樹脂層とすることが好ましい。(Back Layer) Further, with respect to the base material of the heat transfer film, the surface of the base material opposite to the surface on which the heat transfer layer is provided is prevented from sticking to a thermal head or the like and has a slip property. It is possible to provide a back layer 6 for the sake of improvement. Examples of the resin used for the back surface layer include ethyl cellulose, hydroxycellulose, hydroxypropyl cellulose, methyl cellulose, cellulose acetate, cellulose acetate butyrate, cellulose resins such as nitrocellulose, polyvinyl alcohol, polyvinyl acetate, polyvinyl butyral, polyvinyl acetal, and the like. Vinyl-based resin such as polyvinylpyrrolidone, acrylic-based resin such as polymethylmethacrylate, polyethylacrylate, polyacrylamide, acrylonitrile-styrene copolymer, polyamide resin, polyvinyltoluene resin, coumarone-indene resin, polyester-based resin, polyurethane A single substance or a mixture of natural or synthetic resins such as resin, silicone-modified or fluorine-modified urethane is used. Among the above resins to further improve the heat resistance of the back layer, a resin having a hydroxyl group reactive group is used, and a polyisocyanate or the like is used in combination as a crosslinking agent to form a crosslinked resin layer. preferable.
【００３１】さらに、サーマルヘッドとの摺動性を付与
するために、背面層に固形あるいは液状の離型剤又は滑
剤を加えて耐熱滑性をもたせてもよい。離型剤又は滑剤
としては、例えば、ポリエチレンワックス、パラフィン
ワックス等の各種ワックス類、高級脂肪族アルコール、
オルガノポリシロキサン、アニオン系界面活性剤、カチ
オン系界面活性剤、両性界面活性剤、ノニオン系界面活
性剤、フッ素系界面活性剤、有機カルボン酸およびその
誘導体、フッ素系樹脂、シリコーン系樹脂、タルク、シ
リカ等の無機化合物の微粒子等を用いることができる。
背面層に含有される滑剤の量は５〜５０重量％、好まし
くは１０〜３０重量％程度である。背面層を形成する手
段は、上記のごとき、樹脂に必要に応じて離型剤や滑剤
等を、適当な溶剤中に溶解または分散させて、塗工液を
調製し、この塗工液をグラビアコーター、ロールコータ
ー、ワイヤーバーなどの慣用の塗工手段により、塗工
し、乾燥するものである。その背面層の塗工量は、乾燥
状態で０．１〜１０ｇ／ｍ2程度である。Further, in order to provide slidability with the thermal head, a solid or liquid release agent or lubricant may be added to the back surface layer so as to have heat resistant slipping property. Examples of the release agent or lubricant include various waxes such as polyethylene wax and paraffin wax, higher aliphatic alcohols,
Organopolysiloxane, anionic surfactant, cationic surfactant, amphoteric surfactant, nonionic surfactant, fluorine surfactant, organic carboxylic acid and its derivatives, fluorine resin, silicone resin, talc, Fine particles of an inorganic compound such as silica can be used.
The amount of lubricant contained in the back layer is 5 to 50% by weight, preferably about 10 to 30% by weight. The means for forming the back layer is prepared by dissolving or dispersing a releasing agent, a lubricant or the like in the resin in a suitable solvent as described above to prepare a coating solution and gravure the coating solution. It is coated and dried by a conventional coating means such as a coater, a roll coater, and a wire bar. The coating amount of the back surface layer is about 0.1 to 10 g / m 2 in a dry state.
【００３２】以下に、熱転写記録媒体を構成する各層等
について、詳細に説明する。本発明の熱転写記録媒体
は、基材上の少なくとも一方にメタクリレート系モノマ
ーの単独重合体または共重合体の熱可塑性樹脂と着色剤
とを含有する熱転写インク層を形成したものである。
（基材）熱転写記録媒体で使用する基材２２としては、
熱転写インク層を支持し、強度や耐熱性を有するもので
あれば、従来から熱転写記録媒体の基材として使用され
ているものを用いることができ、具体的には上記の熱転
写フィルムの基材で挙げたような材料を同様に挙げるこ
とができる。基材の厚さは、その強度および耐熱性等が
適切になるように、材料に応じて適宜選択することがで
きるが、通常は１〜５０μｍ程度のものが好ましく用い
られる。The layers and the like constituting the thermal transfer recording medium will be described in detail below. The thermal transfer recording medium of the present invention has a thermal transfer ink layer containing a thermoplastic resin of a homopolymer or copolymer of a methacrylate monomer and a colorant formed on at least one side of a substrate. (Substrate) As the substrate 22 used in the thermal transfer recording medium,
As long as it supports the thermal transfer ink layer and has strength and heat resistance, those conventionally used as the base material of the thermal transfer recording medium can be used. Specifically, as the base material of the thermal transfer film, Materials such as those mentioned may likewise be mentioned. The thickness of the base material can be appropriately selected depending on the material so that the strength, heat resistance and the like are appropriate, but normally, a thickness of about 1 to 50 μm is preferably used.
【００３３】（熱転写インク層）上記に説明した基材上
に設けられる熱転写インク層８は、メタクリレート系モ
ノマーの単独重合体または共重合体を主体とした熱可塑
性樹脂と着色剤、さらに必要に応じて、ワックス類等の
滑剤、分散剤、沈降防止剤等の添加剤を加えた塗工液に
より形成することができる。上記の着色剤としては、各
種の従来公知の着色剤を用いることができる。着色剤と
しては、有機または無機の顔料、もしくは染料のうち、
記録材料として良好な特性を有するもの、例えば、十分
な着色濃度を有し、光、熱、温度などにより変褪色しな
いものが好ましい。着色剤としては、シアン、マゼン
タ、イエロー、ブラックなどの色相を任意に選択するこ
とができる。また、金色、銀色、銅色等の金属光沢を有
した顔料や、蛍光性を有する無機顔料や有機顔料、染
料、そして白色系や、緑色、橙色、紫色等の中間色系の
顔料、染料も使用できる。(Thermal Transfer Ink Layer) The thermal transfer ink layer 8 provided on the above-mentioned substrate is composed of a thermoplastic resin mainly composed of a homopolymer or copolymer of a methacrylate monomer and a colorant, and further, if necessary. Then, it can be formed with a coating liquid to which additives such as lubricants such as waxes, dispersants and anti-settling agents are added. As the colorant, various conventionally known colorants can be used. As the colorant, of organic or inorganic pigments or dyes,
A recording material having good characteristics, for example, a recording material having a sufficient coloring density and not discolored by light, heat, temperature or the like is preferable. As the colorant, hues such as cyan, magenta, yellow and black can be arbitrarily selected. In addition, pigments with metallic luster such as gold, silver, copper, fluorescent inorganic pigments and organic pigments, dyes, and intermediate colors such as white, green, orange, and purple are also used. it can.
【００３４】金、銀、銅、亜鉛、アルミニウム、クロム
等の金属又は合金の粉末である金属顔料の中で、アルミ
ニウム顔料を用いることが好ましく、優れた金属光沢性
や、隠蔽性（被画像形成体の転写面の地色等に影響され
ない）を発揮できる。そのアルミニウム顔料は、球状の
形態やそれに類似した形状でもよいが、板状のものが金
属光沢性、隠蔽性に優れていて、好ましく用いられる。
熱転写層で使用するアルミニウムの大きさは、長さで平
均１〜２０μｍ程度、厚さで平均０．０１〜５μｍ程度
が、塗工液中の分散性や、得られる画像の金属光沢性に
優れ、好ましい。Among the metal pigments which are powders of metals or alloys such as gold, silver, copper, zinc, aluminum and chromium, it is preferable to use aluminum pigments, which have excellent metallic luster and hiding power (image formation). (It is not affected by the background color of the transfer surface of the body). The aluminum pigment may have a spherical shape or a shape similar thereto, but a plate-shaped one is preferably used because it has excellent metallic luster and concealment.
The average size of aluminum used in the thermal transfer layer is about 1 to 20 μm in length and about 0.01 to 5 μm in thickness, which is excellent in dispersibility in the coating liquid and the metallic luster of the obtained image. ,preferable.
【００３５】本発明の熱転写記録媒体は、基材の一方の
面に熱転写インク層を設けたもので、その熱転写インク
層は熱溶融性インク層または昇華性染料インク層の２種
類に大別される。まず、熱溶融性インク層は、従来公知
の着色剤とバインダーよりなり、必要に応じて、鉱物
油、植物油、ステアリン酸等の高級脂肪酸、可塑剤、充
填剤等の種々の添加剤を加えたものが使用される。バイ
ンダーとして用いられる樹脂成分としては、メタクリレ
ート系モノマーの単独重合体または共重合体を主体とし
て、その他に、エチレン−酢酸ビニル共重合体、エチレ
ン−アクリル酸エステル共重合体、ポリエチレン、ポリ
スチレン、ポリプロピレン、ポリブデン、石油樹脂、塩
化ビニル樹脂、塩化ビニル−酢酸ビニル共重合体、ポリ
ビニルアルコール、塩化ビニリデン樹脂、メタクリル樹
脂、ポリアミド、ポリカーボネート、フッ素樹脂、ポリ
ビニルフォルマール、ポリビニルブチラール、アセチル
セルロース、ニトロセルロース、ポリ酢酸ビニル、ポリ
イソブチレン、エチルセルロース又はポリアセタール等
を必要に応じて加えることができる。The thermal transfer recording medium of the present invention is provided with a thermal transfer ink layer on one surface of a substrate, and the thermal transfer ink layer is roughly classified into a heat-meltable ink layer and a sublimable dye ink layer. It First, the heat-meltable ink layer is composed of a conventionally known colorant and a binder, and if necessary, various additives such as mineral oil, vegetable oil, higher fatty acid such as stearic acid, plasticizer, and filler are added. Stuff used. As the resin component used as the binder, mainly a homopolymer or copolymer of a methacrylate monomer, in addition, ethylene-vinyl acetate copolymer, ethylene-acrylic acid ester copolymer, polyethylene, polystyrene, polypropylene, Polybutene, petroleum resin, vinyl chloride resin, vinyl chloride-vinyl acetate copolymer, polyvinyl alcohol, vinylidene chloride resin, methacrylic resin, polyamide, polycarbonate, fluororesin, polyvinyl formal, polyvinyl butyral, acetyl cellulose, nitrocellulose, polyacetic acid Vinyl, polyisobutylene, ethyl cellulose, polyacetal or the like can be added if necessary.
【００３６】またバインダーとしてワックス成分を加え
ることができ、例えば、マイクロクリスタリンワック
ス、カルナバワックス、パラフィンワックス等がある。
更に、フィッシャートロプシュワックス、各種低分子量
ポリエチレン、木ロウ、ミツロウ、鯨ロウ、イボタロ
ウ、羊毛ロウ、セラックワックス、キャンデリラワック
ス、ペトロラクタム、ポリエステルワックス、一部変性
ワックス、脂肪酸エステル、脂肪酸アミド等、種々のワ
ックスが用いられる。本発明では、熱溶融性インク層に
含有するバインダーである熱可塑性樹脂として、メタク
リレート系モノマーの単独重合体または共重合体を主体
に使用し、該インク層が転写される熱転写層のバインダ
ー樹脂も、メタクリレート系モノマーの単独重合体また
は共重合体を主成分としているため、互いに近似した構
造を有するメタクリレート系モノマーの単独重合体また
は共重合体同士で、両者は相溶性の高いものとなり、熱
転写層に対する転写性と定着性に優れたものとなる。A wax component may be added as a binder, and examples thereof include microcrystalline wax, carnauba wax, and paraffin wax.
In addition, Fischer-Tropsch wax, various low molecular weight polyethylene, wood wax, beeswax, spermaceti wax, ivowa wax, wool wax, shellac wax, candelilla wax, petrolactam, polyester wax, partially modified wax, fatty acid ester, fatty acid amide, etc. Wax is used. In the present invention, a homopolymer or copolymer of a methacrylate-based monomer is mainly used as the thermoplastic resin that is a binder contained in the heat-meltable ink layer, and the binder resin of the heat transfer layer to which the ink layer is transferred is also used. Since the main component is a homopolymer or copolymer of a methacrylate-based monomer, homopolymers or copolymers of a methacrylate-based monomer having a structure similar to each other are highly compatible with each other, and the thermal transfer layer It has excellent transferability and fixing property.
【００３７】着色剤としては、上記に挙げたような公知
の有機または無機の顔料、あるいは染料の中から適宜選
択することができる。さらに、熱溶融性インク層に、良
好な熱伝導性および熱溶融転写性を与えるため、バイン
ダーの充填剤として熱伝導性物質を配合してもよい。こ
のような充填剤としては、例えばカーボンブラック等の
炭素質物質、アルミニウム、銅、酸化錫、二硫化モリブ
デン等の金属および金属化合物等がある。熱溶融性イン
ク層の形成は、上記のような着色剤成分とメタクリレー
ト系モノマーの単独重合体または共重合体を主体とした
バインダー成分と、さらに、これに必要に応じて水、有
機溶剤等の溶媒成分を配合調整した熱溶融性インク層形
成用塗工液を、従来公知のホットメルトコート、ホット
ラッカーコート、グラビアコート、グラビアリバースコ
ート、ロールコート等の方法で行う。また、水系又は非
水系のエマルジョン塗液を用いて形成する方法もある。
熱溶融性インク層の厚みは、必要な印字濃度と熱感度と
の調和がとれるように、決定すべきであって、０．１ｇ
／ｍ2〜３０ｇ／ｍ2の範囲、好ましくは、０．５ｇ／ｍ
2〜２０ｇ／ｍ2程度が、好ましい。The colorant can be appropriately selected from the known organic or inorganic pigments or dyes listed above. Furthermore, in order to provide the heat-meltable ink layer with good heat conductivity and heat-melt transferability, a heat-conductive substance may be added as a binder filler. Examples of such fillers include carbonaceous materials such as carbon black, metals such as aluminum, copper, tin oxide, molybdenum disulfide, and metal compounds. The heat-fusible ink layer is formed by a binder component mainly composed of a colorant component and a homopolymer or copolymer of a methacrylate monomer as described above, and further, if necessary, water, an organic solvent, or the like. The hot-melt ink layer-forming coating liquid in which the solvent components are blended and adjusted is applied by a conventionally known method such as hot melt coating, hot lacquer coating, gravure coating, gravure reverse coating, or roll coating. There is also a method of forming using an aqueous or non-aqueous emulsion coating liquid.
The thickness of the heat-fusible ink layer should be determined so that the required print density and heat sensitivity can be balanced, and is 0.1 g.
/ M 2 to 30 g / m 2 in range, preferably 0.5 g / m
About 2 to 20 g / m 2 is preferable.
【００３８】次に、熱転写インク層が昇華性染料インク
層の場合、昇華性染料をバインダー樹脂で担持させた層
である。使用する染料は、従来公知の熱転写記録媒体に
使用される染料はいずれも本発明に有効に使用可能であ
り、特に限定されない。例えば、幾つかの好ましい染料
としては、赤色染料として、ＭＳ Ｒｅｄ Ｇ、Ｍａｃ
ｒｏｌｅｘ ＲｅｄＶｉｏｒｅｔ Ｒ、Ｃｅｒｅｓ Ｒ
ｅｄ ７Ｂ、Ｓａｍａｒｏｎ Ｒｅｄ ＨＢＳＬ、Ｒｅ
ｓｏｌｉｎ Ｒｅｄ Ｆ３ＢＳ等が挙げられ、又、黄色
の染料としては、ホロンブリリアントイエロー６ＧＬ、
ＰＴＹ−５２、マクロレックスイエロー６Ｇ等が挙げら
れ、又、青色染料としては、カヤセットブルー７１４、
ワクソリンブルーＡＰ−ＦＷ、ホロンブリリアントブル
ーＳ−Ｒ、ＭＳブルー１００等が挙げられる。Next, when the thermal transfer ink layer is a sublimable dye ink layer, it is a layer in which a sublimable dye is carried by a binder resin. The dye used is not particularly limited, and any dye used in a conventionally known thermal transfer recording medium can be effectively used in the present invention. For example, some preferred dyes include red dyes such as MS Red G, Mac
rolex RedVioret R, Ceres R
ed 7B, Samaron Red HBSL, Re
Solin Red F3BS and the like, and as the yellow dye, Holon Brilliant Yellow 6GL,
PTY-52, Macrolex Yellow 6G and the like, and as the blue dye, Kayaset Blue 714,
Waxolin blue AP-FW, holon brilliant blue SR, MS blue 100 and the like can be mentioned.
【００３９】上記の如き昇華性染料を担持するためのバ
インダー樹脂（熱可塑性樹脂）として、メタクリレート
系モノマーの単独重合体または共重合体を主体に使用
し、その他必要に応じて、エチルセルロース、ヒドロキ
シエチルセルロース、エチルヒドロキシセルロース、ヒ
ドロキシプロピルセルロース、メチルセルロース、酢酸
セルロース、酢酪酸セルロース等のセルロース系樹脂、
ポリビニルアルコール、ポリ酢酸ビニル、ポリビニルブ
チラール、ポリビニルアセタール、ポリビニルピロリド
ン、ポリアクリルアミド等のビニル系樹脂等を加えるこ
とができる。As the binder resin (thermoplastic resin) for supporting the sublimable dye as described above, a homopolymer or copolymer of a methacrylate monomer is mainly used, and if necessary, ethyl cellulose or hydroxyethyl cellulose is used. , Ethylhydroxycellulose, hydroxypropylcellulose, methylcellulose, cellulose acetate, cellulose acetate butyrate and other cellulose resins,
Vinyl-based resins such as polyvinyl alcohol, polyvinyl acetate, polyvinyl butyral, polyvinyl acetal, polyvinyl pyrrolidone, and polyacrylamide can be added.
【００４０】また、熱転写画像形成時の受容側である熱
転写層との離型性を高める為に、メタクリレート系モノ
マーの単独重合体または共重合体の主鎖にグラフト結合
したポリシロキサンセグメント、フッ化炭素セグメン
ト、及び長鎖アルキルセグメントから選ばれる少なくと
も１種の離型性セグメントを有するグラフトコポリマー
を、熱移行性染料を担持するためのバインダー樹脂とし
てもよい。但し、このような昇華性染料インク層の染料
を受容する熱転写層には、染料染着性を有する熱可塑性
樹脂のバインダーが必要であり、また必要に応じて昇華
性染料インク層と熱転写層とが画像形成の加熱時に、熱
融着せずにスムーズに剥離するように、フッ素系界面活
性剤や、シリコーンオイル及び／又はその硬化物等の離
型剤を含有させることができる。フッ素系界面活性剤と
しては、Ｆｌｕｏｒａｄ ＦＣ−４３０、ＦＣ−４３１
（３Ｍ社）が挙げられ、シリコーンオイルとしては、
「シリコーンハンドブック」日刊工業新聞社に記載され
ているような各種変性シリコーンオイルや、その硬化物
が使用できる。特にフッ素系界面活性剤や、未硬化シリ
コーンオイルは接着性が強く、好ましく用いられる。も
ちろん、上記の離型性セグメントを有するグラフトコポ
リマーのバインダー樹脂を熱転写層に用いれば、離型剤
を添加する必要がなく、被画像形成体と画像付き熱転写
層との接着性が高く、好ましい。Further, in order to enhance the releasability from the thermal transfer layer which is the receiving side at the time of thermal transfer image formation, a polysiloxane segment grafted to the main chain of a homopolymer or copolymer of a methacrylate monomer, or a fluorinated polymer is used. A graft copolymer having a carbon segment and at least one releasable segment selected from long-chain alkyl segments may be used as a binder resin for supporting the heat transferable dye. However, the thermal transfer layer that receives the dye of the sublimable dye ink layer requires a binder of a thermoplastic resin having dye dyeability, and if necessary, a sublimable dye ink layer and a thermal transfer layer. A release agent such as a fluorine-based surfactant and a silicone oil and / or a cured product thereof may be contained so that the product can be smoothly peeled off without heat fusion when heated during image formation. As the fluorine-based surfactant, Fluorad FC-430, FC-431
(3M company), and as the silicone oil,
Various modified silicone oils as described in "Silicone Handbook", Nikkan Kogyo Shimbun, and cured products thereof can be used. Fluorine-based surfactants and uncured silicone oils are particularly preferred because of their strong adhesiveness. Of course, when the binder resin of the graft copolymer having a releasable segment is used for the thermal transfer layer, it is not necessary to add a releasing agent, and the adhesiveness between the image forming body and the image-bearing thermal transfer layer is high, which is preferable.
【００４１】昇華性染料インク層は、上記の染料、メタ
クリレート系モノマーの単独重合体または共重合体を主
体としたバインダー樹脂の他に必要に応じて従来公知の
種々の添加剤を含めることができる。そして、適当な溶
剤中に、上記の染料、バインダー樹脂、添加剤を加えて
各成分を溶解または分散させてインクを調整し、これを
上記の基材上に、熱溶融性インキ層で挙げた従来公知の
塗工形成方法と同様の方法により、昇華性染料インク層
を形成する。昇華性染料インク層の厚みは０．１〜５．
０ｇ／ｍ2、好ましくは０．４〜２．０ｇ／ｍ2程度であ
る。The sublimable dye ink layer may contain, if necessary, various conventionally known additives in addition to the binder resin mainly composed of the above-mentioned dye or a homopolymer or copolymer of a methacrylate monomer. . Then, the above dye, binder resin, and additive were added to a suitable solvent to dissolve or disperse each component to prepare an ink, which was listed on the above base material in the heat-meltable ink layer. The sublimable dye ink layer is formed by the same method as a conventionally known coating forming method. The sublimable dye ink layer has a thickness of 0.1 to 5.
0 g / m 2, preferably from 0.4 to 2.0 g / m 2 approximately.
【００４２】（背面層）また、熱転写記録媒体の基材に
対し、その基材の熱転写インク層の設けてある面と反対
側の面に、サーマルヘッドの粘着を防止し、且つ、滑り
性を良くするために、背面層を設けることが可能であ
る。この背面層は熱転写フィルムに設けることができる
背面層と同様の材料で構成することができる。本発明で
使用する熱溶融性インク層による熱転写インク層を有す
る熱転写記録媒体では、基材上に熱転写インク層を設け
るが、基材上に剥離層を介して、熱転写インク層を設け
て、加熱により熱転写インク層を基材からより剥離し易
くすることができる。また、熱転写記録媒体の熱転写イ
ンク層の上に接着層やその他中間層等を設けることが可
能である。また、昇華性染料インク層による熱転写イン
ク層を有する熱転写記録媒体では、基材上に熱転写イン
ク層を設けるが、基材と熱転写インク層との間に両者の
接着性を高めるプライマー層等の中間層を設けたりする
ことができる。尚、熱転写記録媒体で用いる剥離層、接
着層は、前記の熱転写フィルムで使用する剥離層、接着
層と同様の材料及び形成方法が適用できる。(Back Layer) Further, with respect to the base material of the thermal transfer recording medium, the surface of the base material opposite to the surface on which the thermal transfer ink layer is provided prevents adhesion of the thermal head and has a slip property. It is possible to provide a back layer for the sake of improvement. This back layer can be made of the same material as the back layer that can be provided in the thermal transfer film. In the thermal transfer recording medium having a thermal transfer ink layer of the heat-meltable ink layer used in the present invention, the thermal transfer ink layer is provided on the substrate, but the thermal transfer ink layer is provided on the substrate via the release layer and heated. This makes it easier to peel the thermal transfer ink layer from the substrate. Further, it is possible to provide an adhesive layer or other intermediate layer on the thermal transfer ink layer of the thermal transfer recording medium. Further, in a thermal transfer recording medium having a thermal transfer ink layer of a sublimable dye ink layer, the thermal transfer ink layer is provided on the base material, but an intermediate layer such as a primer layer which enhances the adhesiveness between the base material and the thermal transfer ink layer is provided. Layers can be provided. For the release layer and the adhesive layer used in the thermal transfer recording medium, the same materials and forming methods as those for the release layer and the adhesive layer used in the thermal transfer film can be applied.
【００４３】本発明において、熱転写フィルムの熱転写
層に、熱転写記録媒体の熱転写インク層を熱転写して画
像形成する際の、像様に加熱する手段は、サーマルヘッ
ド加熱やレーザー光照射等の従来公知の熱転写を行う際
の熱エネルギーの付与手段が使用できる。また、上記の
熱転写インク層により画像形成された熱転写層を被画像
形成体に転写する手段は、転写画像を形成する際のサー
マルヘッドやラインヒーター、ヒートロールあるいはホ
ットスタンプ等の方法が挙げられる。尚、本発明で最終
的に得られる被画像形成体上の画像が正しい向きになる
ように、熱転写フィルム上の熱転写層の上に画像形成す
る時に、その最終的に得られる被画像形成体での画像と
は鏡像の画像を形成する必要がある。In the present invention, when the image is formed by thermally transferring the thermal transfer ink layer of the thermal transfer recording medium to the thermal transfer layer of the thermal transfer film, the means for imagewise heating is conventionally known such as thermal head heating or laser light irradiation. A means for applying thermal energy when performing the thermal transfer can be used. Examples of means for transferring the thermal transfer layer image-formed with the thermal transfer ink layer to the image forming body include methods such as a thermal head, a line heater, a heat roll and a hot stamp when forming a transferred image. When the image is formed on the thermal transfer layer on the thermal transfer film so that the image on the image formed body finally obtained in the present invention has the correct orientation, It is necessary to form a mirror image of the image of.
【００４４】上記のような画像形成方法により、被画像
形成体に画像が形成されたものが、画像形成物となる。
この被画像形成体としては、特に限定されず、例えば、
普通紙、上質紙、トレーシングペーパー、各種プラスチ
ック等、いずれのシートや立体成型物でもよく、また形
状的にはカード、葉書、パスポート、便箋、レポート用
紙、ノート、カタログ、コップ、ケース、建材、パネ
ル、電話、ラジオ、テレビ等の電子部品や二次電池等い
ずれのものでもよい。By the image forming method as described above, an image is formed on the image forming body as an image formed article.
The image formed body is not particularly limited, and for example,
Any sheet or three-dimensional molding such as plain paper, high-quality paper, tracing paper, various plastics, etc., and in terms of shape, cards, postcards, passports, stationery, report paper, notebooks, catalogs, cups, cases, building materials, It may be an electronic component such as a panel, a telephone, a radio, a television, or a secondary battery.
【００４５】[0045]
【実施例】以下に実施例及び比較例をあげて、本発明を
さらに具体的に説明する。尚、文中部または％とあるの
は重量基準である。
（熱転写フィルム１〜熱転写フィルム１０の作製）表５
に示す各層の条件により、熱転写フィルム１〜熱転写フ
ィルム１０を作製する。すなわち、表５に示す基材上
に、表４に示す組成で背面層を固形分０．２ｇ／ｍ2に
なるように塗布し、その基材の他方の面に、表５に示す
条件で、離型層、剥離層、熱転写層を順次形成する。
尚、離型層の組成は表５の通りであり、使用する樹脂の
詳細は表２に示した。また剥離層の組成は表５の通りで
あり、使用する樹脂の詳細を表３に示した。熱転写層の
組成は表５の通りであり、使用する樹脂の詳細は表１に
示した。EXAMPLES The present invention will be described more specifically with reference to Examples and Comparative Examples below. In addition, "parts" and "%" are based on weight. (Production of Thermal Transfer Film 1 to Thermal Transfer Film 10) Table 5
The thermal transfer film 1 to the thermal transfer film 10 are produced under the conditions of each layer shown in. That is, a back layer having the composition shown in Table 4 was coated on the base material shown in Table 5 so that the solid content was 0.2 g / m 2, and the other surface of the base material was coated under the conditions shown in Table 5. , A release layer, a release layer, and a thermal transfer layer are sequentially formed.
The composition of the release layer is as shown in Table 5, and the details of the resin used are shown in Table 2. The composition of the release layer is shown in Table 5, and the details of the resin used are shown in Table 3. The composition of the thermal transfer layer is as shown in Table 5, and the details of the resin used are shown in Table 1.
【００４６】[0046]
【表１】 [Table 1]
【００４７】[0047]
【表２】 [Table 2]
【００４８】[0048]
【表３】 [Table 3]
【００４９】[0049]
【表４】 [Table 4]
【００５０】[0050]
【表５】 [Table 5]
【００５１】（熱転写インクシート１の作製）着色画像
形成用として熱転写インクシート１を、表６に示す各層
の条件で、作製した。(Production of Thermal Transfer Ink Sheet 1) A thermal transfer ink sheet 1 for forming a colored image was produced under the conditions of each layer shown in Table 6.
【表６】 [Table 6]
【００５２】（被転写体）熱転写フィルムの評価を行な
う際に、使用する被転写体として、厚さ２００μｍの白
色軟質塩化ビニルシートを用いた。(Transfer Material) When the thermal transfer film was evaluated, a white soft vinyl chloride sheet having a thickness of 200 μm was used as a transfer material to be used.
【００５３】（実施例１〜実施例８、比較例１）前述の
方法と表７に示す組み合わせで作成した熱転写層を設け
た熱転写フィルムと熱転写インクシートとを熱転写フィ
ルムの熱転写層と熱転写インクシートの着色層とが対向
するように重ね合わせ、熱転写インクシートの背面側か
らサーマルヘッドで像様に加熱し、着色剤のみ、または
着色剤とバインダーとを熱転写フィルムの熱転写層上に
像様に転写することで熱転写フィルムの熱転写層上に着
色画像を形成する。その後、被転写体と、着色画像が熱
転写層上に形成された熱転写フィルムの熱転写層とが対
向するように重ね合わせ、熱転写フィルムの背面側から
１８０℃に加熱されたゴムで被覆されたヒートロールで
全面加熱し、熱転写フィルムの熱転写層を全面転写する
ことで被転写体に熱転写層で保護された着色画像を形成
する。尚、着色画像の印画条件は、サーマルヘッド加熱
の評価用プリンタを用い、ライン速度２．８ｍｓｅｃ／
ｌｉｎｅ、パルスデューティ８０％、またサーマルヘッ
ドの解像度は３００ＤＰＩ、サーマルヘッド抵抗値は１
６００Ω、印加電圧１７．５Ｖである。また印画パター
ンは、７ポイントのサイズで「ＡＢＣ」という文字とし
た。(Examples 1 to 8 and Comparative Example 1) The thermal transfer film and the thermal transfer ink sheet provided with the thermal transfer layer prepared by the combination of the above method and Table 7 are the thermal transfer layer of the thermal transfer film and the thermal transfer ink sheet. The heat transfer ink sheet is imagewise heated with a thermal head from the back side of the thermal transfer ink sheet so that the colorant alone or the colorant and the binder are imagewise transferred onto the thermal transfer layer of the thermal transfer film. By doing so, a colored image is formed on the thermal transfer layer of the thermal transfer film. Then, the transferred material and the colored image are superposed so that the colored image and the thermal transfer layer of the thermal transfer film formed on the thermal transfer layer face each other, and a heat roll covered with rubber heated to 180 ° C. from the back side of the thermal transfer film. The entire surface of the thermal transfer layer of the thermal transfer film is heated by, and a colored image protected by the thermal transfer layer is formed on the transfer target. In addition, the printing condition of the colored image is the line speed of 2.8 msec / using a thermal head heating evaluation printer.
line, pulse duty 80%, thermal head resolution is 300 DPI, thermal head resistance is 1
The applied voltage is 600Ω and the applied voltage is 17.5V. In addition, the print pattern is a character of "ABC" with a size of 7 points.
【００５４】[0054]
【表７】 [Table 7]
【００５５】実施例１〜実施例８及び比較例１として、
各例で用意した熱転写層を設けた熱転写フィルム、着色
画像形成用の熱転写インクシート、被転写体を表７に示
す条件で組み合わせて使用し、着色画像と熱転写層を被
転写体に転写形成した。上記の得られた被転写体及び熱
転写フィルムを用いて、以下に示す評価を行なった。As Examples 1 to 8 and Comparative Example 1,
A thermal transfer film provided with a thermal transfer layer prepared in each example, a thermal transfer ink sheet for forming a colored image, and a transfer target were used in combination under the conditions shown in Table 7, and the colored image and the thermal transfer layer were transferred to the transfer target. . The following evaluations were carried out using the transferred material and the thermal transfer film obtained above.
【００５６】（転写性）前述の方法で得られた被転写体
において、
・転写不良（熱転写フィルムの熱転写層が転写していな
い部分がある）
・尾引き（被転写体に転写した熱転写層が被転写体の端
面からはみ出している）の有無を目視にて観察し、転写
性の評価をした。(Transferability) In the transferred material obtained by the above-described method, transfer failure (there is a portion of the thermal transfer film where the thermal transfer layer is not transferred), tailing (the thermal transfer layer transferred to the transferred material is The presence or absence of (protruding from the end surface of the transferred material) was visually observed to evaluate transferability.
【００５７】（耐摩耗性）着色画像と熱転写層が転写形
成された被転写体に対して、ＴＡＢＥＲ試験機で、摩耗
輪ＣＳ−１０Ｆを使用し、荷重５００ｇｆにて、２００
回転の耐摩耗性試験を行ない、着色画像の欠損の有無を
評価した。
（耐熱性）熱転写フィルムの熱転写層と熱転写フィルム
の背面層とを重ね合わせ、５０℃で２日間保存試験を行
ない、ブロッキングの有無を評価した。(Abrasion resistance) With respect to the transferred material on which the colored image and the thermal transfer layer are transferred and formed, a wearer wheel CS-10F is used in a TABER tester, and a load of 500 gf is applied to 200.
A rotation abrasion resistance test was performed to evaluate the presence or absence of defects in the colored image. (Heat resistance) The thermal transfer layer of the thermal transfer film and the back layer of the thermal transfer film were superposed and a storage test was carried out at 50 ° C. for 2 days to evaluate the presence or absence of blocking.
【００５８】各実施例及び比較例の評価結果は表７に示
した。The evaluation results of each Example and Comparative Example are shown in Table 7.
【００５９】[0059]
【発明の効果】本発明の熱転写フィルム及び熱転写記録
媒体は、基材上の一方の面に、熱可塑性樹脂を主成分と
する熱転写層を基材から最も遠い位置に形成した熱転写
フィルムと、基材上の少なくとも一方に熱可塑性樹脂と
着色剤とを含有する熱転写インク層を形成した熱転写記
録媒体とを、互いに熱転写層と熱転写インク層が対向す
るように重ね合せ、像様に加熱することによって熱転写
記録媒体の熱転写インク層または熱転写インク層に含有
する着色剤を像様に熱転写フィルムの熱転写層に転写す
ることで一旦熱転写フィルムに逆像を画像形成した後、
画像形成された熱転写フィルムの熱転写層と被画像形成
体の画像形成面とを対向するように重ね合せ、画像形成
された熱転写層ごと被画像形成体に転写することによっ
て、被画像形成体に画像形成するものであり、熱転写フ
ィルムの熱転写層に含有される熱可塑性樹脂と、熱転写
記録媒体の熱転写インク層に含有される熱可塑性樹脂と
が、いずれもメタクリレート系モノマーの単独重合体ま
たは共重合体とした。The thermal transfer film and the thermal transfer recording medium of the present invention include a thermal transfer film having a thermal transfer layer containing a thermoplastic resin as a main component formed on one surface of a substrate at a position farthest from the substrate. A thermal transfer recording medium on which a thermal transfer ink layer containing a thermoplastic resin and a colorant is formed on at least one side of the material is superposed such that the thermal transfer layer and the thermal transfer ink layer face each other, and imagewise heating is performed. After the thermal transfer ink layer of the thermal transfer recording medium or the colorant contained in the thermal transfer ink layer is imagewise transferred to the thermal transfer layer of the thermal transfer film to form an inverse image on the thermal transfer film,
The thermal transfer layer of the imaged thermal transfer film and the image forming surface of the image forming body are superposed so as to face each other, and the image formed thermal transfer layer is transferred to the image forming body to form an image on the image forming body. The thermoplastic resin contained in the thermal transfer layer of the thermal transfer film and the thermoplastic resin contained in the thermal transfer ink layer of the thermal transfer recording medium are both homopolymers or copolymers of methacrylate monomers. And
【００６０】これにより、熱転写フィルムの熱転写層と
熱転写記録媒体の熱転写インク層との両者の相溶性が高
くなり、熱転写層に転写される熱転写インク層の定着性
が高まり、得られる画像形成物の耐摩耗性、耐光性等の
耐久性に優れ、かつ転写感度が良好で、巻取り保管中の
ブロッキングを防止した。また、中間転写記録媒体とし
て機能する熱転写フィルムを用いて、１回の転写で画像
形成された熱転写層を被画像形成体に転写できるため、
被画像形成体への転写によるダメージが少なく、画像形
成物の品質劣化等を抑えることができる。As a result, the compatibility of both the thermal transfer layer of the thermal transfer film and the thermal transfer ink layer of the thermal transfer recording medium becomes high, the fixability of the thermal transfer ink layer transferred to the thermal transfer layer is enhanced, and the resulting image-formed product is obtained. It has excellent durability such as abrasion resistance and light resistance, and has good transfer sensitivity, preventing blocking during winding and storage. In addition, since the thermal transfer film functioning as an intermediate transfer recording medium can be used to transfer the thermal transfer layer image-formed by one transfer to the image forming body,
The damage due to the transfer to the image forming body is small, and the quality deterioration of the image formed material can be suppressed.
【図１】本発明の熱転写フィルムである一つの実施形態
を示す断面図である。FIG. 1 is a cross-sectional view showing one embodiment of a thermal transfer film of the present invention.
【図２】本発明の熱転写フィルムである他の実施形態を
示す断面図である。FIG. 2 is a cross-sectional view showing another embodiment of the thermal transfer film of the present invention.
【図３】本発明の熱転写フィルムである他の実施形態を
示す断面図である。FIG. 3 is a cross-sectional view showing another embodiment of the thermal transfer film of the present invention.
【図４】本発明の熱転写フィルムである他の実施形態を
示す断面図である。FIG. 4 is a cross-sectional view showing another embodiment of the thermal transfer film of the present invention.
【図５】本発明で行なう画像形成方法の一例を説明する
概略図である。FIG. 5 is a schematic diagram illustrating an example of an image forming method according to the present invention.
【符号の説明】 １ 熱転写フィルム ２、２１、２２ 基材 ３ 熱転写層 ４ 離型層 ５ 剥離層 ６ 背面層 ７ 熱転写記録媒体 ８ 熱転写インク層 ９ 像 １０ 被画像形成体 １１ サーマルヘッド １２ プラテンロール １３ ヒートロール[Explanation of symbols] 1 Thermal transfer film 2, 21, 22 base material 3 Thermal transfer layer 4 Release layer 5 Release layer 6 back layer 7 Thermal transfer recording medium 8 Thermal transfer ink layer 9 statues 10 Image forming body 11 thermal head 12 Platen roll 13 heat roll
フロントページの続き Ｆターム(参考） 2C068 AA06 BC34 2H111 AA05 AA08 AA10 AA16 AA26 AA33 AA50 AA52 BA03 BA53 BA71 Continued front page F-term (reference) 2C068 AA06 BC34 2H111 AA05 AA08 AA10 AA16 AA26 AA33 AA50 AA52 BA03 BA53 BA71
Claims (4)
成分とする熱転写層を基材から最も遠い位置に形成した
熱転写フィルムと、基材上の少なくとも一方に熱可塑性
樹脂と着色剤とを含有する熱転写インク層を形成した熱
転写記録媒体とを、熱転写フィルムの熱転写層と熱転写
記録媒体の熱転写インク層が対向するように重ね合せ、
像様に加熱することによって熱転写記録媒体の熱転写イ
ンク層または熱転写インク層に含有する着色剤を像様に
熱転写フィルムの熱転写層に転写することで一旦熱転写
フィルムに逆像を画像形成した後、画像形成された熱転
写フィルムの熱転写層と被画像形成体の画像形成面とを
対向するように重ね合せ、熱転写フィルムの熱転写層と
は反対側から加熱することによって、画像形成された熱
転写層ごと被画像形成体に転写することによって、被画
像形成体に画像形成する画像形成方法に用いる熱転写フ
ィルム及び熱転写記録媒体において、熱転写フィルムの
熱転写層に含有される熱可塑性樹脂と、熱転写記録媒体
の熱転写インク層に含有される熱可塑性樹脂とが、いず
れもメタクリレート系モノマーの単独重合体または共重
合体であることを特徴とする熱転写フィルム及び熱転写
記録媒体。1. A thermal transfer film having a thermal transfer layer containing a thermoplastic resin as a main component formed on one surface of a substrate at a position farthest from the substrate, and at least one of the substrates is colored with the thermoplastic resin. A thermal transfer recording medium on which a thermal transfer ink layer containing an agent is formed, and the thermal transfer layer of the thermal transfer film and the thermal transfer ink layer of the thermal transfer recording medium are superposed so as to face each other,
By imagewise heating, the thermal transfer ink layer of the thermal transfer recording medium or the colorant contained in the thermal transfer ink layer is imagewise transferred to the thermal transfer layer of the thermal transfer film to form a reverse image on the thermal transfer film. The thermal transfer layer of the formed thermal transfer film and the image forming surface of the image forming body are superposed so as to face each other, and heating is performed from the side opposite to the thermal transfer layer of the thermal transfer film, so that the image formed thermal transfer layer is imaged together. In a thermal transfer film and a thermal transfer recording medium used in an image forming method for forming an image on an image forming body by transferring to a formed body, a thermoplastic resin contained in the thermal transfer layer of the thermal transfer film and a thermal transfer ink layer of the thermal transfer recording medium. That the thermoplastic resin contained in is a homopolymer or copolymer of methacrylate monomers. Heat transfer film and thermal transfer recording medium according to symptoms.
写層に含有されるメタクリレート系モノマーの単独重合
体または共重合体のガラス転移点が４０〜１１０℃、数
平均分子量が１５０００〜８００００であることを特徴
とする熱転写フィルム及び熱転写記録媒体。2. The glass transition point of a homopolymer or copolymer of a methacrylate monomer contained in the thermal transfer layer of the thermal transfer film according to claim 1, has a glass transition point of 40 to 110 ° C. and a number average molecular weight of 15,000 to 80,000. A thermal transfer film and a thermal transfer recording medium characterized by the above.
熱転写層に含有されるメタクリレート系モノマーの単独
重合体または共重合体、または熱転写記録媒体の熱転写
インク層に含有されるメタクリレート系モノマーの単独
重合体または共重合体の少なくともいずれか一方に、メ
タクリレート成分としてイソブチルメタクリレート、ノ
ルマルブチルメタクリレート、及びターシャリーブチル
メタクリレートから選ばれる少なくとも１種以上を含有
することを特徴とする熱転写フィルム及び熱転写記録媒
体。3. A homopolymer or copolymer of a methacrylate monomer contained in the thermal transfer layer of the thermal transfer film according to claim 1, or a methacrylate monomer contained in a thermal transfer ink layer of a thermal transfer recording medium. At least one of a homopolymer and a copolymer contains at least one selected from isobutyl methacrylate, normal butyl methacrylate, and tertiary butyl methacrylate as a methacrylate component, and a thermal transfer film and a thermal transfer recording medium. .
熱転写層に含有されるメタクリレート系モノマーの単独
重合体または共重合体、または熱転写記録媒体の熱転写
インク層に含有されるメタクリレート系モノマーの単独
重合体または共重合体の少なくともいずれか一方が、メ
チルメタクリレート／イソブチルメタクリレート共重合
体であることを特徴とする熱転写フィルム及び熱転写記
録媒体。4. A homopolymer or copolymer of a methacrylate monomer contained in the thermal transfer layer of the thermal transfer film according to claim 1, or a methacrylate monomer contained in a thermal transfer ink layer of a thermal transfer recording medium. At least one of a homopolymer and a copolymer is a methyl methacrylate / isobutyl methacrylate copolymer, and a thermal transfer film and a thermal transfer recording medium.