JP2003135351A - Cleaning sheet - Google Patents
Cleaning sheetInfo
- Publication number
- JP2003135351A JP2003135351A JP2001332026A JP2001332026A JP2003135351A JP 2003135351 A JP2003135351 A JP 2003135351A JP 2001332026 A JP2001332026 A JP 2001332026A JP 2001332026 A JP2001332026 A JP 2001332026A JP 2003135351 A JP2003135351 A JP 2003135351A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- cleaning
- fiber
- regions
- sheet according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は全面積が活用できる
凹凸付きの清掃用シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cleaning sheet having an uneven surface which can be utilized over its entire area.
【0002】[0002]
【従来の技術】専用の掃除具に装着して使用するフロー
リング清掃用シートとしては、スパンレース不織布が一
般に利用されている。しかし、模様付けをしていないフ
ラットタイプのスパンレース不織布は、実質的に平坦な
シートであり、清掃作業時にはモップ移動方向に対し前
端の部分しか利用されず、集塵性能が低い。2. Description of the Related Art Spunlaced nonwoven fabric is generally used as a flooring cleaning sheet which is attached to a dedicated cleaning tool for use. However, the non-patterned flat type spunlace nonwoven fabric is a substantially flat sheet, and only the front end portion with respect to the mop moving direction is used during the cleaning operation, and the dust collection performance is low.
【0003】また、メッシュパターンのスパンレース不
織布はメッシュ部分から捕集したダストの裏抜け(脱
落)が起こり好ましくない。この問題に対し、フラット
なスパンレース不織布にエンボス加工を行うことで全体
を凹凸に形成したシートが提案されているが、この場合
附形処理を行った部分で繊維密度が高くなりすぎ、比較
的剛直な毛髪の捕集性能が低下し、風合いも損なう問題
点があった。Further, in the spun lace nonwoven fabric having a mesh pattern, strike-through (falling off) of dust collected from the mesh portion is not preferable. In response to this problem, a sheet in which unevenness is formed on the whole by performing embossing on a flat spunlaced nonwoven fabric has been proposed, but in this case, the fiber density becomes too high in the portion subjected to the shaping treatment, There was a problem that the performance of collecting rigid hair was deteriorated and the texture was impaired.
【0004】[0004]
【発明が解決しようとする課題】本発明はこれらの問題
を解決するためのもので、シート全体に実質的にほぼ同
等の繊維密度を持つ凹凸を形成することで清掃作業時に
全面積が有効に活用できるようにしたものである。SUMMARY OF THE INVENTION The present invention is intended to solve these problems, and by forming irregularities having substantially the same fiber density on the entire sheet, the entire area can be effectively used during cleaning work. It can be used.
【0005】[0005]
【課題を解決するための手段】本発明は水流交絡により
形成した不繊布シートを、レーザー加工機で繊維配行を
変化させ、該シート全面に実質的にほぼ同等の繊維密度
を持つ凹凸を形成したことを特徴とする清掃用シートに
関するものである。また本発明のシートは少くとも2つ
の厚みの異なる領域からなってシート全面に非圧縮の凹
凸を形成し、かつ各領域は夫々厚みを異にするが、全領
域とも実質的にほぼ同等の繊維密度を持つことを特徴と
する清掃用シートに関するものである。本発明のシート
全面に非圧縮の凹凸を形成する方法は交絡不繊布に対す
るレーザー加工により、例えばこの交絡不繊布に対する
レーザー加工はpolymer Group,Inc.のAPEX Technology
により達成される。この技術を利用してダスト及び毛髪
捕集性能に最適化したデザインを付与することができ
る。According to the present invention, a non-woven cloth sheet formed by hydroentangling is changed in fiber distribution by a laser processing machine to form irregularities having substantially the same fiber density on the entire surface of the sheet. The present invention relates to a cleaning sheet characterized by the above. Further, the sheet of the present invention has at least two regions having different thicknesses to form uncompressed unevenness on the entire surface of the sheet, and each region has a different thickness, but all regions have substantially the same fiber. The present invention relates to a cleaning sheet having a density. The method of forming the non-compressed unevenness on the entire surface of the sheet of the present invention is by laser processing for the entangled non-woven fabric, for example, the laser processing for the entangled non-woven fabric is performed by polymer Group, Inc. APEX Technology.
Achieved by Utilizing this technique, a design optimized for dust and hair collection performance can be provided.
【0006】[0006]
【作用】本発明シートの繊維組成はスパンレース不繊布
に利用される繊維であれば何でもよく、例えばポリエス
テル系、ポリアミド系、ポリオレフィン系等の熱可塑性
繊維、あるいはこれらの複合繊維や分割繊維、キュプ
ラ、レーヨン等の再生繊維、アセテート等の半合成繊
維、コットン等の天然繊維が用いられる。また本発明シ
ートの繊度および繊維長については、繊維長は5〜10
0mmが適しており、この範囲を超えるとカード工程へ
の適性が悪化し操業性を損なうこととなる。繊度は0.
5〜5.0dが適しており、繊度が低いときは繊維密度
が高くなり髪の毛等の捕集性が低下し、繊度が高いとき
は微細ダストの捕集性・保持性が低下する。本発明のシ
ートはシート全面に形成した凹凸が一般的なフローリン
グワイパー清掃時にシートにかかる加重下(加重2g/
cm2)において厚みの異なる複数の領域を形成する。
シート両面を使用する場合凹凸の断面形状としては、図
2のように両面凹凸の状態が好ましい。しかし、本発明
の繊維構成では適度にシート剛性が低いため実際の清掃
作業時の圧力分布は片面凹凸のケースでも表裏で大きな
違いは無く、両面使用可能である。また厚みの異なる複
数の領域(凹部および凸部)の形状は特に制約はなく、
線状、丸形、多角形、星形等の幾何学模様、ロゴ、文字
列、意匠、キャラクター等の各種パターンや不定形パタ
ーン等が利用可能である。The fiber composition of the sheet of the present invention may be any fiber as long as it is a fiber used in spunlace non-woven fabrics, for example, thermoplastic fibers such as polyester, polyamide and polyolefin, or their composite fibers, split fibers and cupra. Recycled fiber such as rayon, semi-synthetic fiber such as acetate, and natural fiber such as cotton are used. Regarding the fineness and fiber length of the sheet of the present invention, the fiber length is 5 to 10
0 mm is suitable, and if it exceeds this range, the suitability for the card process is deteriorated and the operability is impaired. The fineness is 0.
5 to 5.0 d is suitable. When the fineness is low, the fiber density is high and the ability to collect hair or the like is reduced, and when the fineness is high, the ability to collect and retain fine dust is reduced. In the sheet of the present invention, the unevenness formed on the entire surface of the sheet is generally applied to the sheet during cleaning of the flooring wiper.
cm 2 ), a plurality of regions having different thicknesses are formed.
When both sides of the sheet are used, the cross-sectional shape of the irregularities is preferably a state of irregularities on both sides as shown in FIG. However, in the fiber constitution of the present invention, since the sheet rigidity is appropriately low, the pressure distribution during the actual cleaning work does not significantly differ between the front and back even in the case of one-sided unevenness, and both sides can be used. In addition, there are no particular restrictions on the shape of the plurality of regions (recesses and protrusions) having different thicknesses,
It is possible to use geometric patterns such as lines, circles, polygons, and stars, various patterns such as logos, character strings, designs, characters, and irregular patterns.
【0007】以上のようにして、シート全体に凹凸を形
成することで、清掃作業時に全面積が活用できるととも
に凹部(厚みの小さい領域)は比較的大きな物体の捕集
にも寄与できる。しかもこれらの凹部は非圧縮で形成さ
れているので、凸部と同等の繊維密度を持ち、その捕集
シート全体にダストの捕集性および毛髪等の絡め取り性
に対するデッドスペースなしに最適化した繊維密度を持
たせることができる。By forming the unevenness on the entire sheet as described above, the entire area can be utilized at the time of cleaning work, and the concave portion (area having a small thickness) can also contribute to the collection of a relatively large object. Moreover, since these recesses are formed by non-compression, they have the same fiber density as the projections, and are optimized without dust space for dust collecting property and entanglement property of hair etc. in the entire collecting sheet. It can have a fiber density.
【0008】[0008]
【実施例】以下に実施例によって本発明を説明するが、
本発明はこれに限定されるものではない。EXAMPLES The present invention will be described below with reference to examples.
The present invention is not limited to this.
【0009】繊度1.5デニール、繊維長51mmのポ
リエステル繊維100%を構成繊維とする坪量70g/
m2のスパンレース不織布をレーザー加工によりその繊
維配行を調整し、図1〜3に示すように凹凸を持つ不織
布に形成した。この不織布は比較的厚みの大きい第1領
域(凸部)(1)と厚みの小さい第2領域(凹部)
(2)を持ち、第1領域の厚みが91μm、第2領域の
厚みが65μmとした。第1領域、第2領域共に14m
m×11mmの四角形とし、これらを交互に配した格子
状パターンとした。この不織布の両面に流動パラフィン
2g/m2塗工して清掃用シートとした。70 g / gram of basis weight with 100% polyester fiber having a fineness of 1.5 denier and a fiber length of 51 mm
The fiber distribution of the m 2 spunlaced nonwoven fabric was adjusted by laser processing to form a nonwoven fabric having irregularities as shown in FIGS. This non-woven fabric has a relatively thick first region (convex portion) (1) and a relatively thin second region (concave portion).
(2), the thickness of the first region is 91 μm, and the thickness of the second region is 65 μm. 14m for both the first and second areas
A square pattern of m × 11 mm was formed, and a grid pattern in which these were alternately arranged was formed. Liquid paraffin (2 g / m 2) was applied to both surfaces of this nonwoven fabric to form a cleaning sheet.
【0010】<比較例>繊度1.5デニール、繊維長5
1mmのポリエステル繊維100%を構成繊維とする坪
量70g/m2でワイヤーによるメッシュパターンを付
与したスパンレース不織布を得た。この不織布の両面に
流動パラフィン2g/m2塗工して清掃用シートとし
た。実施例および比較例の集塵性および絡め取り性を比
較した結果を下記の表1に示した。<Comparative example> Fineness of 1.5 denier, fiber length of 5
A spunlaced nonwoven fabric having a mesh pattern of wires with a basis weight of 70 g / m 2 and having 100% of 1 mm polyester fiber as a constituent fiber was obtained. Liquid paraffin (2 g / m 2) was applied to both surfaces of this nonwoven fabric to form a cleaning sheet. The results of comparing the dust collecting properties and the entanglement properties of Examples and Comparative Examples are shown in Table 1 below.
【0011】[0011]
【表1】 [Table 1]
【0012】測定方法
・絡め取り性
長さ10cmの人頭毛髪を模した糸5本を拭き取り方向
と平行に5本並べ、拭き取り操作によりワイパーに絡め
取ることの出来た本数を測定した(N=5)。絡め取り
率を以下の式で算出した。
絡め取り率(%)=(絡め取った毛髪の本数)/5×1
00
・集塵性、裏抜け
JIS標準ダスト(7種)0.1gを30cm×4cm
の範囲に均一に散布し、シートを70cmの距離を移動
した時の捕集量を観測した。集塵率を以下の式で算出し
た(N=3)。同時に裏抜けについて目視にて判定し
た。
集塵率(%)=((試験後のシート重量)−(試験前の
シート重量))/0.1×100Measuring Method: Tangleability Five yarns simulating a human head hair having a length of 10 cm were arranged in parallel with the wiping direction, and the number of the yarns that could be entangled with the wiper by the wiping operation was measured (N = 5). The entanglement rate was calculated by the following formula. Entanglement removal rate (%) = (number of hairs entangled) / 5 x 1
00 ・ Dust collection, strike-through JIS standard dust (7 types) 0.1g 30cm × 4cm
Was evenly dispersed in the above range, and the trapped amount was measured when the sheet was moved a distance of 70 cm. The dust collection rate was calculated by the following formula (N = 3). At the same time, strike-through was visually determined. Dust collection rate (%) = ((sheet weight after test)-(sheet weight before test)) / 0.1 x 100
【0013】[0013]
【発明の効果】本発明の効果を要約して列記すると次の
通りである。
(1)シート全体に凹凸を形成することで清掃作業時に
全面積が有効に活用できる。
(2)凹部(厚みの小さい領域)は比較的大きな物体の
捕集にも寄与できる。
(3)圧縮加工によるデッドスペースなしにシート全体
がダストの捕集性及び毛髪等の絡め取り性に最適化した
繊維密度を有する。The effects of the present invention are summarized and listed as follows. (1) By forming unevenness on the entire sheet, the entire area can be effectively utilized during cleaning work. (2) The recesses (areas of small thickness) can also contribute to the collection of relatively large objects. (3) The entire sheet has a fiber density optimized for dust collection and entanglement of hair etc. without dead space due to compression processing.
【図1】 本発明シートの模式的平面略図。FIG. 1 is a schematic plan view of the sheet of the present invention.
【図2】 図1のa−a断面図。FIG. 2 is a sectional view taken along line aa of FIG.
【図3】 図1のb−b断面図。3 is a sectional view taken along line bb of FIG.
1…凸部(第1領域) 2…凹部(第2領域) 1 ... Convex portion (first area) 2 ... Recessed portion (second region)
フロントページの続き Fターム(参考) 3B074 AA01 AA02 AA08 AB01 CC03 3B154 AA02 AA06 AA11 AB22 BA37 BB19 DA30 4L047 AB02 AB07 BA04 CC16 DA00 EA22 Continued front page F term (reference) 3B074 AA01 AA02 AA08 AB01 CC03 3B154 AA02 AA06 AA11 AB22 BA37 BB19 DA30 4L047 AB02 AB07 BA04 CC16 DA00 EA22
Claims (9)
を、レーザー加工機で繊維配行を変化させ、該シート全
面に実質的にほぼ同等の繊維密度を持つ凹凸を形成した
ことを特徴とする清掃用シート。1. A cleaning characterized in that a non-woven cloth sheet formed by hydroentangling is changed in fiber distribution by a laser processing machine, and irregularities having substantially the same fiber density are formed on the entire surface of the sheet. Sheet.
域からなってシート全面に非圧縮の凹凸を形成し、かつ
各領域は夫々厚みを異にするが、全領域とも実質的にほ
ぼ同等の繊維密度を持つことを特徴とする清掃用シー
ト。2. The sheet is formed of at least two regions having different thicknesses to form uncompressed unevenness on the entire surface of the sheet, and the regions have different thicknesses, but the regions are substantially the same. A cleaning sheet characterized by having a fiber density.
に利用される繊維である請求項1または2記載の清掃用
シート。3. The cleaning sheet according to claim 1, wherein the fiber composition of the sheet is a fiber used for a spunlace non-woven fabric.
ある請求項1から3までのいずれか1項記載の清掃用シ
ート。4. The cleaning sheet according to claim 1, wherein the fiber length of the sheet fiber is 5 to 100 mm.
ある請求項1から4までのいずれか1項記載の清掃用シ
ート。5. The cleaning sheet according to claim 1, wherein the fineness of the sheet fiber is 0.5 to 5.0 d.
グワイパー清掃時にシートにかかる加重下において厚み
の異なる複数の領域を持つ請求項1から5までのいずれ
か1項記載の清掃用シート。6. The cleaning sheet according to claim 1, wherein the unevenness formed on the entire surface of the sheet has a plurality of regions having different thicknesses under a load applied to the sheet during cleaning of the flooring wiper.
に形成されている請求項1から6までのいずれか1項記
載の清掃用シート。7. The cleaning sheet according to claim 1, wherein the unevenness is formed on both sides or one side of the sheet.
角形、星形その他の幾何学的模様、ロゴ、文字列、意
匠、キャラクターその他の各種パターンまたは不定形パ
ターンである請求項1から7までのいずれか1項記載の
清掃用シート。8. The concave or convex shape is linear, round, polygonal, star-shaped or other geometric patterns, logos, character strings, designs, characters or other various patterns or irregular patterns. The cleaning sheet according to any one of 1 to 7.
ラフィンその他の清掃用油剤を適用した請求項1から8
までのいずれか1項記載の清掃用シート。9. A liquid paraffin or other cleaning oil is applied to both sides or one side of the non-woven cloth sheet.
The cleaning sheet according to any one of 1 to 6 above.