JP2003128885A - Glass fiber-reinforced cycloolefin-based resin composition and shaped article - Google Patents

Glass fiber-reinforced cycloolefin-based resin composition and shaped article

Info

Publication number
JP2003128885A
JP2003128885A JP2001324001A JP2001324001A JP2003128885A JP 2003128885 A JP2003128885 A JP 2003128885A JP 2001324001 A JP2001324001 A JP 2001324001A JP 2001324001 A JP2001324001 A JP 2001324001A JP 2003128885 A JP2003128885 A JP 2003128885A
Authority
JP
Japan
Prior art keywords
glass fiber
resin
cyclic olefin
olefin resin
olefin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2001324001A
Other languages
Japanese (ja)
Inventor
Hiroyuki Kanai
裕之 金井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Polyplastics Co Ltd
Original Assignee
Polyplastics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Polyplastics Co Ltd filed Critical Polyplastics Co Ltd
Priority to JP2001324001A priority Critical patent/JP2003128885A/en
Publication of JP2003128885A publication Critical patent/JP2003128885A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain a glass fiber-reinforced resin composition for a shaped article excellent in mechanical strength. SOLUTION: This glass fiber-reinforced cycloolefin-based resin composition is composed of a cycloolefin-based resin and a coalesced glass fiber obtained by coalescing a glass fiber using an olefin-based resin as a binding resin.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【発明の属する技術分野】本発明は、主として環状オレ
フィン系樹脂と、オレフィン系樹脂バインダーを使用し
て集束されたガラス繊維からなる熱可塑性樹脂組成物及
びその成形品に関する。本発明のガラス繊維強化環状オ
レフィン系樹脂組成物を使用すると、強度、剛性などの
機械的物性、高い熱変形温度、寸法安定性、低そり変
形、軽量、耐熱水性等に優れた成形品が得られる。
TECHNICAL FIELD The present invention relates to a thermoplastic resin composition mainly composed of a cyclic olefin resin and glass fibers bundled by using an olefin resin binder, and a molded product thereof. When the glass fiber reinforced cyclic olefin resin composition of the present invention is used, a molded product excellent in mechanical properties such as strength and rigidity, high heat distortion temperature, dimensional stability, low warpage deformation, light weight, and hot water resistance is obtained. To be

【0002】[0002]

【従来の技術】環状オレフィン系樹脂は、その主鎖に環
状のオレフィン骨格を持った非晶性で熱可塑性のオレフ
ィン系樹脂であり、その透明性に加え、低複屈折性、高
い熱変形温度、軽量性、寸法安定性、低吸水性、耐加水
分解性、耐薬品性、低誘電率・低誘電損失、環境負荷物
質を含まない等の特徴を持っている。そのため環状オレ
フィン系樹脂は、光ディスク、レンズ、導光板といった
光学用途をはじめ、プレフィルドシリンジ、輸液の容器
や活栓といった医薬関連器材、高周波電子部品、薬品や
食品の包装・容器など広範な用途に用いられている。
2. Description of the Related Art Cyclic olefin resin is an amorphous and thermoplastic olefin resin having a cyclic olefin skeleton in its main chain. In addition to its transparency, it also has low birefringence and high heat distortion temperature. , Light weight, dimensional stability, low water absorption, hydrolysis resistance, chemical resistance, low dielectric constant / low dielectric loss, and no environmental load substances. Therefore, cyclic olefin resins are used in a wide range of applications such as optical applications such as optical disks, lenses, and light guide plates, prefilled syringes, medical-related equipment such as infusion containers and stopcocks, high-frequency electronic components, and packaging and containers for medicines and foods. ing.

【0003】環状オレフィン系樹脂にガラス繊維等の無
機充填剤を添加した熱可塑性樹脂組成物は、環状オレフ
ィン系樹脂の特性に加え、さらに剛性や機械的強度を高
められることで、高い熱変形温度、寸法安定性、低そり
変形、軽量、耐熱水性等に優れた成形品用樹脂組成物と
なるものと期待され、種々の検討がなされてきた。例え
ば、特開平3−207739号公報において、ガラス繊
維と特定の環状オレフィン系樹脂の組成物が開示されて
いるが、ガラス繊維添加による機械的強度の上昇は期待
されるほどではない。
A thermoplastic resin composition obtained by adding an inorganic filler such as a glass fiber to a cyclic olefin resin has a high heat distortion temperature because the rigidity and mechanical strength can be further increased in addition to the characteristics of the cyclic olefin resin. It has been expected that the resin composition for molded articles will be excellent in dimensional stability, low warpage deformation, lightweight, hot water resistance, and the like, and various studies have been made. For example, Japanese Patent Application Laid-Open No. 3-207739 discloses a composition of glass fiber and a specific cyclic olefin resin, but the increase in mechanical strength due to the addition of glass fiber is not so expected.

【0004】ガラス繊維と結晶性ポリオレフィンの組成
物においては、ガラス繊維の改良によって組成物の強度
を向上させる提案がなされている。例えば特開平6−1
16398号公報および特開平7−286050号公報
において、オレフィン系樹脂や変性オレフィン系樹脂の
バインダーで集束されたガラス繊維を用いた樹脂組成物
が提案されているが、いずれもポリプロピレンとガラス
繊維の組成物に関するものであり、環状オレフィン系樹
脂組成物については知られていない。
In the composition of glass fiber and crystalline polyolefin, it has been proposed to improve the strength of the composition by improving the glass fiber. For example, Japanese Patent Laid-Open No. 6-1
16398 and JP-A-7-286050 propose resin compositions using glass fibers bundled with a binder of an olefin resin or a modified olefin resin, both of which are composed of polypropylene and glass fiber. However, no known cycloolefin resin composition is known.

【0005】[0005]

【発明が解決しようとする課題】機械的強度等に優れた
成形品用のガラス繊維強化環状オレフィン系樹脂組成物
を提供する。
The present invention provides a glass fiber reinforced cyclic olefin resin composition for molded articles, which is excellent in mechanical strength and the like.

【0006】[0006]

【課題を解決するための手段】本発明者らの検討によれ
ば、機械的強度が期待されるほど上昇しない原因は、ガ
ラス繊維と環状オレフィン系樹脂の界面の密着力が不十
分であるために、ガラス繊維による効果的な強化ができ
ていないことによるものと推定される。本発明者らは、
ガラス繊維による環状オレフィン系樹脂の強化の効率を
高めるべく鋭意検討した結果、ガラス繊維の集束剤に使
われるバインダー樹脂をオレフィン系樹脂とすることに
よって、ガラス繊維による環状オレフィン系樹脂の強化
の効率を高めることができ、機械的強度に優れた成形品
用ガラス繊維強化環状オレフィン系樹脂組成物が得られ
ることを見出し、本発明を完成するに至った。
According to the studies made by the present inventors, the reason why the mechanical strength does not increase as much as expected is that the adhesive force at the interface between the glass fiber and the cyclic olefin resin is insufficient. It is presumed that this is due to the fact that the glass fiber cannot be effectively reinforced. We have
As a result of intensive studies to enhance the efficiency of strengthening the cyclic olefin resin by the glass fiber, the efficiency of the strengthening of the cyclic olefin resin by the glass fiber was improved by using the olefin resin as the binder resin used as the sizing agent for the glass fiber. The inventors have found that a glass fiber-reinforced cyclic olefin resin composition for molded products, which can be increased and has excellent mechanical strength, can be obtained, and completed the present invention.

【0007】すなわち第1の発明は、環状オレフィン系
樹脂(a)とバインダー樹脂集束ガラス繊維(b)から
なる熱可塑性樹脂組成物において、バインダー樹脂集束
ガラス繊維(b)がオレフィン系樹脂(c)をバインダ
ー樹脂に使用してガラス繊維を集束させたものであるこ
とを特徴とするガラス繊維強化環状オレフィン系樹脂組
成物を提供する。第2の発明は、環状オレフィン系樹脂
(a)が、環状オレフィンの付加(共)重合体またはその
水素添加物(al)、環状オレフィンとα−オレフィン
の付加共重合体またはその水素添加物(a2)、環状オ
レフィンの開環(共)重合体またはその水素添加物(a
3)、及び上記環状オレフィン系樹脂(a1)〜(a
3)に官能基を有する不飽和化合物をグラフ卜及び/又
は共重合した重合体(a4)からなる群から選ばれた少
なくとも一種である第1の発明に記載のガラス繊維強化
環状オレフィン系樹脂組成物を提供する。第3の発明
は、バインダー用のオレフィン系樹脂(c)が、α−オ
レフィン重合体、2種以上のα−オレフィンの共重合
体、環状オレフィン系樹脂、または、これらオレフィン
系樹脂に官能基を有する不飽和化合物をグラフ卜及び/
又は共重合した変性オレフィン系樹脂である第1の発明
に記載のガラス繊維強化環状オレフィン系樹脂組成物を
提供する。第4の発明は、バインダー樹脂集束ガラス繊
維(b)が、ガラス繊維100重量部にオレフィン系樹
脂0.1〜5重量部を使用して集束させたものである第
1の発明に記載のガラス繊維強化環状オレフィン系樹脂
組成物を提供する。第5の発明は、環状オレフィン系樹
脂(a)とバインダー樹脂集束ガラス繊維(b)の重量
組成比がa/b=95/5〜40/60(aとbの合計
は100である。)である第1の発明に記載のガラス繊
維強化環状オレフィン系樹脂組成物を提供する。第6の
発明は、第1〜5のいずれかの発明に記載のガラス繊維
強化環状オレフィン系樹脂組成物を、射出成形、圧縮成
形、射出圧縮成形、押出成形又はブロー成形してなるガ
ラス繊維強化環状オレフィン系樹脂成形品を提供する。
That is, the first invention is a thermoplastic resin composition comprising a cyclic olefin resin (a) and a binder resin-focused glass fiber (b), wherein the binder resin-focused glass fiber (b) is an olefin resin (c). A glass fiber-reinforced cyclic olefin-based resin composition, characterized in that glass fibers are bundled by using as a binder resin. The second invention is that the cyclic olefin resin (a) is an addition (co) polymer of a cyclic olefin or a hydrogenated product thereof (al), an addition copolymer of a cyclic olefin and an α-olefin or a hydrogenated product thereof ( a2), a ring-opening (co) polymer of a cyclic olefin or a hydrogenated product thereof (a
3), and the above cyclic olefin resins (a1) to (a)
The glass fiber reinforced cyclic olefin resin composition according to the first invention, which is at least one selected from the group consisting of a polymer (a4) obtained by graphitizing and / or copolymerizing an unsaturated compound having a functional group in 3). Provide things. A third invention is that the olefin resin (c) for the binder is an α-olefin polymer, a copolymer of two or more kinds of α-olefins, a cyclic olefin resin, or a functional group in these olefin resins. The unsaturated compound having a graph and / or
Alternatively, the glass fiber reinforced cyclic olefin resin composition according to the first invention, which is a copolymerized modified olefin resin, is provided. A fourth invention is the glass according to the first invention, wherein the binder resin-focused glass fiber (b) is focused by using 0.1 to 5 parts by weight of an olefin resin in 100 parts by weight of the glass fiber. A fiber-reinforced cyclic olefin resin composition is provided. In a fifth aspect of the invention, the weight composition ratio of the cyclic olefin resin (a) and the binder resin-focused glass fiber (b) is a / b = 95/5 to 40/60 (the sum of a and b is 100). A glass fiber reinforced cyclic olefin resin composition according to the first invention is provided. A sixth invention is glass fiber reinforced obtained by injection molding, compression molding, injection compression molding, extrusion molding or blow molding of the glass fiber reinforced cyclic olefin resin composition according to any one of the first to fifth inventions. Provided is a cyclic olefin resin molded product.

【0008】[0008]

【発明の実施の形態】(a)環状オレフィン系樹脂 環状オレフィン系樹脂(a)とは、主鎖が炭素−炭素結
合からなり、主鎖の少なくとも一部に環状炭化水素構造
を有する高分子化合物である。この環状炭化水素構造
は、ノルボルネンやテトラシクロドデセンに代表される
ような、環状炭化水素構造中に少なくとも一つのオレフ
ィン性二重結合を有する化合物(環状オレフィン)を単
量体として用いることで導入される。環状オレフィン系
樹脂(a)は、その製造方法から環状オレフィンの付加
(共)重合体またはその水素添加物(al)、環状オレフ
ィンとα−オレフィンの付加共重合体またはその水素添
加物(a2)、環状オレフィンの開環(共)重合体また
はその水素添加物(a3)に分類される。また、環状オ
レフィン系樹脂(a)には、前述の環状オレフィン系樹
脂(a1)〜(a3)に官能基(例えば、カルボキシル
基、酸無水物基、エポキシ基、アミド基、エステル基、
ヒドロキシル基など)を有する不飽和化合物(u)をグ
ラフ卜及び/又は共重合したもの(a4)を含めること
ができる。上記環状オレフィン系樹脂(al)〜(a
4)は、二種以上混合使用してもよい。上記不飽和化合
物(u)としては、後述する(メタ)アクリル酸、マレ
イン酸、無水マレイン酸、無水イタコン酸、グリシジル
(メタ)アクリレート、(メタ)アクリル酸アルキル
(炭素数1〜10)エステル、マレイン酸アルキル(炭
素数1〜10)エステル、(メタ)アクリルアミド、
(メタ)アクリル酸−2−ヒドロキシエチル等が挙げら
れる。環状オレフィン系樹脂(a4)中の不飽和化合物
(u)ユニットの含有率は0.01〜20重量%、好ま
しくは0.1〜10重量%である。
BEST MODE FOR CARRYING OUT THE INVENTION (a) Cyclic olefin-based resin The cyclic olefin-based resin (a) is a polymer compound having a carbon-carbon bond in the main chain and having a cyclic hydrocarbon structure in at least part of the main chain. Is. This cyclic hydrocarbon structure is introduced by using a compound (cyclic olefin) having at least one olefinic double bond in the cyclic hydrocarbon structure, such as norbornene or tetracyclododecene, as a monomer. To be done. The cyclic olefin-based resin (a) is prepared by adding the cyclic olefin from the manufacturing method.
(Co) polymer or its hydrogenated product (al), addition copolymer of cyclic olefin and α-olefin or its hydrogenated product (a2), ring-opened (co) polymer of cyclic olefin or its hydrogenated product ( It is classified into a3). Further, the cyclic olefin resin (a) includes functional groups (for example, a carboxyl group, an acid anhydride group, an epoxy group, an amide group, an ester group) in addition to the above cyclic olefin resins (a1) to (a3).
An unsaturated compound (u) having a hydroxyl group) and / or a copolymerized compound (a4) may be included. The above cyclic olefin resin (al) to (a)
Two or more kinds of 4) may be mixed and used. Examples of the unsaturated compound (u) include (meth) acrylic acid, maleic acid, maleic anhydride, itaconic anhydride, glycidyl (meth) acrylate, alkyl (meth) acrylate (having 1 to 10 carbon atoms) ester, which will be described later. Alkyl maleate (C1-10) ester, (meth) acrylamide,
Examples include 2-hydroxyethyl (meth) acrylate and the like. The content of the unsaturated compound (u) unit in the cyclic olefin resin (a4) is 0.01 to 20% by weight, preferably 0.1 to 10% by weight.

【0009】環状オレフィンの具体例としては、シクロ
ペンテン、シクロヘキセン、シクロオクテン;シクロペ
ンタジエン、1,3−シクロヘキサジエン等の1環の環
状オレフィン;
Specific examples of cyclic olefins include cyclopentene, cyclohexene, cyclooctene; monocyclic cyclic olefins such as cyclopentadiene and 1,3-cyclohexadiene;

【0010】ビシクロ[2.2.1]ヘプタ−2−エン
(慣用名:ノルボルネン)、5−メチル−ビシクロ[2.
2.1]ヘプタ−2−エン、5,5−ジメチル−ビシク
ロ[2.2.1]ヘプタ−2−エン、5−エチル−ビシク
ロ[2.2.1]ヘプタ−2−エン、5−ブチル−ビシク
ロ[2.2.1]ヘプタ−2−エン、5−エチリデン−ビ
シクロ[2.2.1]ヘプタ−2−エン、5−へキシル−
ビシクロ[2.2.1]ヘプタ−2−エン、5−オクチ
ル−ビシクロ[2.2.1]ヘプタ−2−エン、5−オク
タデシル−ビシクロ[2.2.1]ヘプタ−2−エン、
5−メチリデン−ビシクロ[2.2.1]ヘプタ−2−エ
ン、5−ビニル−ビシクロ[2.2.1]ヘプタ−2−エ
ン、5−プロペニル−ビシクロ[2.2.1]ヘプタ−2
−エン、5−メトキシ−カルボニル−ビシクロ[2.
2.1]ヘプタ−2−エン、5−シアノ−ビシクロ[2.
2.1]ヘプタ−2−エン、5−メチル−5−メトキシ
カルボニル−ビシクロ[2.2.1]ヘプタ−2−エン;
5−メトキシカルボニルビシクロ[2.2.1]ヘプタ−
2−エン、5−エトキシカルボニルビシクロ[2.2.
1]ヘプタ−2−エン、5−メチル−5−メトキシカル
ボニルビシクロ[2.2.1]ヘプタ−2−エン、5−メ
チル−5−エトキシカルボニルビシクロ[2.2.1]ヘ
プタ−2−エン、ビシクロ[2.2.1]ヘプタ−5−エ
ニル−2−メチルプロピオネイト、ビシクロ[2.2.
1]ヘプタ−5−エニル−2−メチルオクタネイト、ビ
シクロ[2.2.1]ヘプタ−2−エン−5,6−ジカル
ボン酸無水物、5−ヒドロキシメチルビシクロ[2.
2.1]ヘプタ−2−エン、5,6−ジ(ヒドロキシメチ
ル)ビシクロ[2.2.1]ヘプタ−2−エン、5−ヒド
ロキシ−i−プロピルビシクロ[2.2.1]ヘプタ−2
−エン、5,6−ジカルボキシビシクロ[2.2.1]ヘ
プタ−2−エン;5−シアノビシクロ[2.2.1]ヘ
プタ−2−エン、ビシクロ[2.2.1]ヘプタ−2−エ
ン−5,6−ジカルボン酸イミド等の2環の環状オレフ
ィン;
Bicyclo [2.2.1] hept-2-ene
(Trivial name: norbornene), 5-methyl-bicyclo [2.
2.1] hepta-2-ene, 5,5-dimethyl-bicyclo [2.2.1] hept-2-ene, 5-ethyl-bicyclo [2.2.1] hept-2-ene, 5- Butyl-bicyclo [2.2.1] hept-2-ene, 5-ethylidene-bicyclo [2.2.1] hept-2-ene, 5-hexyl-
Bicyclo [2.2.1] hept-2-ene, 5-octyl-bicyclo [2.2.1] hept-2-ene, 5-octadecyl-bicyclo [2.2.1] hept-2-ene,
5-methylidene-bicyclo [2.2.1] hept-2-ene, 5-vinyl-bicyclo [2.2.1] hept-2-ene, 5-propenyl-bicyclo [2.2.1] hepta- Two
-Ene, 5-methoxy-carbonyl-bicyclo [2.
2.1] hepta-2-ene, 5-cyano-bicyclo [2.
2.1] hepta-2-ene, 5-methyl-5-methoxycarbonyl-bicyclo [2.2.1] hept-2-ene;
5-Methoxycarbonylbicyclo [2.2.1] hepta
2-ene, 5-ethoxycarbonylbicyclo [2.2.
1] hepta-2-ene, 5-methyl-5-methoxycarbonylbicyclo [2.2.1] hept-2-ene, 5-methyl-5-ethoxycarbonylbicyclo [2.2.1] hept-2- Ene, bicyclo [2.2.1] hept-5-enyl-2-methylpropionate, bicyclo [2.2.
1] hepta-5-enyl-2-methyl octaneate, bicyclo [2.2.1] hept-2-ene-5,6-dicarboxylic acid anhydride, 5-hydroxymethylbicyclo [2.
2.1] hepta-2-ene, 5,6-di (hydroxymethyl) bicyclo [2.2.1] hept-2-ene, 5-hydroxy-i-propylbicyclo [2.2.1] hepta- Two
-Ene, 5,6-dicarboxybicyclo [2.2.1] hept-2-ene; 5-cyanobicyclo [2.2.1] hept-2-ene, bicyclo [2.2.1] hepta- A bicyclic cyclic olefin such as 2-ene-5,6-dicarboxylic acid imide;

【0011】トリシクロ[4.3.0.12,5]デカ−
3,7−ジエン(慣用名:ジシクロペンタジエン)、ト
リシクロ[4.3.0.12,5]デカ−3−エン;トリ
シクロ[4.4.0.12,5]ウンデカ−3,7−ジエ
ン若しくはトリシクロ[4.4.0.12,5]ウンデカ
−3,8−ジエンまたはこれらの部分水素添加物(また
はシクロペンタジエンとシクロヘキセンの付加物)であ
るトリシクロ[4.4.0.12,5]ウンデカ−3−エ
ン;5−シクロペンチル−ビシクロ[2.2.1]ヘプ
タ−2−エン、5−シクロヘキシル−ビシクロ[2.
2.1]ヘプタ−2−エン、5−シクロヘキセニルビシ
クロ[2.2.1]ヘプタ−2−エン、5−フェニル−
ビシクロ[2.2.1]ヘプタ−2−エンといった3環
の環状オレフィン;
Tricyclo [4.3.0.1 2,5 ] deca
3,7-diene (common name: dicyclopentadiene), tricyclo [4.3.0.1 2,5 ] dec-3-ene; tricyclo [4.4.0.1 2,5 ] undeca-3, 7-Diene or tricyclo [4.4.0.1 2,5 ] undeca-3,8-diene or a partial hydrogenation product thereof (or an adduct of cyclopentadiene and cyclohexene) tricyclo [4.4.0]. .1, 2,5 ] Undec-3-ene; 5-cyclopentyl-bicyclo [2.2.1] hept-2-ene, 5-cyclohexyl-bicyclo [2.
2.1] hept-2-ene, 5-cyclohexenylbicyclo [2.2.1] hept-2-ene, 5-phenyl-
A tricyclic cyclic olefin such as bicyclo [2.2.1] hept-2-ene;

【0012】テトラシクロ[4.4.0.12,5.1
7,10]ドデカ−3−エン(単にテトラシクロドデセンと
もいう)、8−メチルテトラシクロ[4.4.0.1
2,5.17,1 0]ドデカ−3−エン、8−エチルテトラシ
クロ[4.4.0.12,5.17,10]ドデカ−3−エ
ン、8−メチリデンテトラシクロ[4.4.0.
2,5.17,10]ドデカ−3−エン、8−エチリデンテ
トラシクロ[4.4.0.12,5.17,1 0]ドデカ−3
−エン、8−ビニルテトラシクロ[4.4.0.
2,5.17,10]ドデカ−3−エン、8−プロペニル−
テトラシクロ[4.4.0.12,5.17,1 0]ドデカ−
3−エン、8−メトキシカルボニルテトラシクロ[4.
4.0.12 ,5.17,10]ドデカ−3−エン、8−メチ
ル−8−メトキシカルボニルテトラシクロ[4.4.
0.12,5.17,10]ドデカ−3−エン、8−ヒドロキ
シメチルテトラシクロ[4.4.0.12,5.17,10
ドデカ−3−エン、8−カルボキシテトラシクロ[4.
4.0.12,5.17,10]ドデカ−3−エンといった4
環の環状オレフィン;
Tetracyclo [4.4.0.1 2,5 . 1
7,10 ] dodec-3-ene (also simply referred to as tetracyclododecene), 8-methyltetracyclo [4.4.0.1
2,5 . 1 7,1 0] dodeca-3-ene, 8-ethyl tetracyclo [4.4.0.1 2, 5. 1 7,10 ] dodec-3-ene, 8-methylidene tetracyclo [4.4.0.
1 2,5 . 1 7,10 ] dodec-3-ene, 8-ethylidenetetracyclo [4.4.0.1 2,5 . 1 7,1 0 ] Dodeca-3
-Ene, 8-vinyltetracyclo [4.4.0.
1 2,5 . 1,7,10 ] dodeca-3-ene, 8-propenyl-
Tetracyclo [4.4.0.1 2,5 . 1 7,1 0 ] Dodeca
3-ene, 8-methoxycarbonyltetracyclo [4.
4.0.1 2 , 5 . 1 7,10 ] dodec-3-ene, 8-methyl-8-methoxycarbonyltetracyclo [4.4.
0.1 2,5 . 1 7,10 ] dodec-3-ene, 8-hydroxymethyltetracyclo [4.4.0.1 2,5 . 1 7,10 ]
Dodeca-3-ene, 8-carboxytetracyclo [4.
4.0.1 2,5 . 1 7,10 ] Dodeka-3-en 4
Ring cyclic olefins;

【0013】8−シクロペンチル−テトラシクロ[4.
4.0.12,5.17,10]ドデカ−3−エン、8−シク
ロヘキシル−テトラシクロ[4.4.0.12,5.1
7,10]ドデカ−3−エン、8−シクロヘキセニル−テト
ラシクロ[4.4.0.12,5.17,10]ドデカ−3−
エン、8−フェニル−シクロペンチル−テトラシクロ
[4.4.0.12,5.17,10]ドデカ−3−エン;テ
トラシクロ[7.4.13,6.01,9.02,7]テトラデ
カ−4,9,11,13−テトラエン(1,4−メタノ
−1,4,4a,9a−テトラヒドロフルオレンともい
う)、テトラシクロ[8.4.14,7.01,10.03,8
ペンタデカ−5,10,12,14−テトラエン(1,
4−メタノ−1,4,4a,5,10,10a−へキサ
ヒドロアントラセンともいう);ペンタシクロ[6.
6.1.13,6.02,7.09,14]−4−ヘキサデセン、
ペンタシクロ[6.5.1.13,6.02,7.09,13]−
4−ペンタデセン、ペンタシクロ[7.4.0.
2,7.13,6.110,13]−4−ペンタデセン;ヘプタ
シクロ[8.7.0.12,9.14,7.111,17.03,8
12,16]−5−エイコセン、ヘプタシクロ[8.7.
0.12,9.03,8.14,7.012,17.113,16]−14
−エイコセン;シクロペンタジエンの4量体などの多環
の環状オレフィンが挙げられる。これらの環状オレフィ
ンは、それぞれ単独であるいは2種以上組合わせて用い
ることができる。
8-cyclopentyl-tetracyclo [4.
4.0.1 2,5 . 1 7,10 ] dodeca-3-ene, 8-cyclohexyl-tetracyclo [4.4.0.1 2,5 . 1
7,10 ] Dodeca-3-ene, 8-cyclohexenyl-tetracyclo [4.4.0.1 2,5 . 1 7,10 ] dodeca-3-
Ene, 8-phenyl-cyclopentyl-tetracyclo [4.4.0.1 2,5 . 1 7,10 ] dodeca-3-ene; tetracyclo [7.4.1 3,6 . 0 1,9 . 0 2,7] tetradeca -4,9,11,13- tetraene (1,4-methano -1,4,4a, also referred 9a- tetrahydrofluorene), tetracyclo [8.4.1 4,7. 0 1,10 . 0 3,8 ]
Pentadeca-5,10,12,14-tetraene (1,
4-methano-1,4,4a, 5,10,10a-also referred to as hexahydroanthracene); pentacyclo [6.
6.1.1 3,6 . 0 2,7 . 0 9,14 ] -4-Hexadecene,
Pentacyclo [6.5.1.1 3,6 . 0 2,7 . 0 9,13 ]-
4-pentadecene, pentacyclo [7.4.0.
0 2,7 . 1 3,6 . 1 10,13] -4-pentadecene; heptacyclo [8.7.0.1 2,9. 1 4,7 . 1 11,17 . 0 3,8 .
0 12,16 ] -5-eicosene, heptacyclo [8.7.
0.1 2,9 . 0 3,8 . 1 4,7 . 0 12,17 . 1 13,16 ] -14
-Eicosene; polycyclic cyclic olefins such as cyclopentadiene tetramer. These cyclic olefins may be used alone or in combination of two or more.

【0014】環状オレフィンと共重合可能なα−オレフ
ィンの具体例としては、エチレン、プロピレン、1−ブ
テン、1−ペンテン、1−へキセン、3−メチル−1−
ブテン、3−メチル−1−ペンテン、3−エチル−1−
ペンテン、4−メチル−1−ペンテン、4−メチル−1
−へキセン、4,4−ジメチル−1−ヘキセン、4,4
−ジメチル−1−ペンテン、4−エチル−1−へキセ
ン、3−エチル−1−ヘキセン、1−オクテン、1−デ
セン、1−ドデセン、1−テトラデセン、1−ヘキサデ
セン、1−オクタデセン、1−エイコセンなどの炭素数
2〜20、好ましくは炭素数2〜8のエチレンまたはα
−オレフィンなどが挙げられる。これらのα−オレフィ
ンは、それぞれ単独で、あるいは2種以上を組み合わせ
て使用することができる。
Specific examples of the α-olefin copolymerizable with the cyclic olefin include ethylene, propylene, 1-butene, 1-pentene, 1-hexene and 3-methyl-1-.
Butene, 3-methyl-1-pentene, 3-ethyl-1-
Pentene, 4-methyl-1-pentene, 4-methyl-1
-Hexene, 4,4-dimethyl-1-hexene, 4,4
-Dimethyl-1-pentene, 4-ethyl-1-hexene, 3-ethyl-1-hexene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-hexadecene, 1-octadecene, 1- C2-C20 ethylene such as eicosene, preferably C2-C8 ethylene or α
-Olefins and the like. These α-olefins may be used alone or in combination of two or more.

【0015】環状オレフィンまたは環状オレフィンとα
−オレフィンとの重合方法および得られた重合体の水素
添加方法に、格別な制限はなく、公知の方法に従って行
うことができる。
Cyclic olefin or cyclic olefin and α
There is no particular limitation on the method of polymerizing with an olefin and the method of hydrogenating the obtained polymer, and the known method can be used.

【0016】以上に挙げた環状オレフィン系樹脂(a)
のなかでも、環状オレフィンとα−オレフィンの付加共
重合体またはその水素添加物(a2)が、特性とコスト
のバランスが取れていて特に好ましい。
The above-mentioned cyclic olefin resin (a)
Of these, addition copolymers of cyclic olefins and α-olefins or hydrogenated products (a2) thereof are particularly preferable because they are well balanced in properties and costs.

【0017】環状オレフィン系樹脂は工業的には、トー
パス(独Ticona社)、アペル(三井化学)、ゼオネックス
(日本ゼオン)、ゼオノア(日本ゼオン)、アートン(日本
合成ゴム)などの商品名の市販品を入手することができ
る。
Cyclic olefin resins are industrially used in TOPAS (Ticona, Germany), Apel (Mitsui Chemicals), Zeonex.
Commercial products with trade names such as (Nippon Zeon), Zeonor (Nippon Zeon) and Arton (Nippon Synthetic Rubber) can be obtained.

【0018】(b)バインダー樹脂集束ガラス繊維 ガラス繊維とは、SiO2、B23、A123、Ca
O、Na2O、K2O等の無機酸化物の混合物である無機
ガラスを、溶融状態で急速に引っ張り、細く伸ばした繊
維である。通常繊維径は3〜30μmであり、5〜15
μmが好ましい。ガラス繊維の材質としては、通常ガラ
ス繊維に使用されるガラスをいずれも用いることがで
き、たとえばAガラス、Cガラス、Dガラス、Eガラス
などが挙げられる。ガラス繊維を、環状オレフィン系樹
脂(a)をはじめとする熱可塑性樹脂の強化材として用
いるときには、単独の繊維(フィラメント)で使用する
ことはなく、数百本のフィラメントをバインダー樹脂を
使用して集束させたバインダー樹脂集束ガラス繊維
(b)のロービングをつくり、これを熱可塑性樹脂と混
合する。混合の方法はロービング自体に熱可塑性樹脂の
溶融物ないし溶液を塗布ないし含浸させる、もしくはロ
ービングを長さ1〜10mm、好ましくは3〜6mm、
通常数mmに切断したチョップドストランドを熱可塑性
樹脂と混合する方法が一般的である。
(B) Binder resin-focused glass fiber Glass fiber means SiO 2 , B 2 O 3 , A1 2 O 3 and Ca.
It is a fiber obtained by rapidly pulling an inorganic glass, which is a mixture of inorganic oxides such as O, Na 2 O, and K 2 O, in a molten state into thin fibers. Usually, the fiber diameter is 3 to 30 μm, 5 to 15
μm is preferred. As the material of the glass fiber, any glass generally used for glass fiber can be used, and examples thereof include A glass, C glass, D glass and E glass. When glass fiber is used as a reinforcing material for a thermoplastic resin such as a cyclic olefin resin (a), it is not used as a single fiber (filament) but several hundred filaments are used as a binder resin. A roving of the bound binder resin-focused glass fiber (b) is prepared and mixed with a thermoplastic resin. The mixing method includes coating or impregnating the roving itself with a melt or solution of a thermoplastic resin, or roving having a length of 1 to 10 mm, preferably 3 to 6 mm,
Usually, a method of mixing chopped strands cut into several mm with a thermoplastic resin is common.

【0019】バインダー樹脂 フィラメントを集めてロービングとする過程において、
ガラス繊維の表面にバインダー樹脂を含有した集束剤が
塗布される。バインダー樹脂の役割は、第一義的にはフ
ィラメント同士をつないでロービングの形状を保つとも
に、製造過程や輸送過程での繊維の損傷を防ぐことにあ
る。さらにガラス繊維表面と熱可塑性樹脂との親和性を
高め、溶融混合される際にガラス繊維を樹脂中に分散さ
せやすくする効果も合わせ持っている。バインダー樹脂
としては一般的に、酢酸ビニル樹脂、エポキシ樹脂、ウ
レタン樹脂、アクリル酸エステル樹脂、オレフィン系樹
脂等が用いられている。
In the process of collecting the binder resin filaments into rovings,
A sizing agent containing a binder resin is applied to the surface of the glass fiber. The role of the binder resin is primarily to connect the filaments to each other to maintain the shape of the roving and to prevent damage to the fibers during the manufacturing process and the transportation process. Furthermore, it also has the effect of increasing the affinity between the glass fiber surface and the thermoplastic resin and making it easier to disperse the glass fiber in the resin when melted and mixed. As the binder resin, vinyl acetate resin, epoxy resin, urethane resin, acrylate resin, olefin resin, etc. are generally used.

【0020】(c)オレフィン系樹脂 本発明者らは、いかなるバインダー樹脂を使用するかに
よって、環状オレフィン系樹脂とガラス繊維の組成物の
機械的強度が大きく変わることを見出した。その中で、
オレフィン系樹脂(c)をバインダーとして使用したと
き、該組成物の強度が最も高くなり、最適なバインダー
であることを見出した。何故、バインダー樹脂としてオ
レフィン系樹脂(c)が最適であるのか、詳細には不明
であるが、オレフィン系樹脂(c)と環状オレフィン系
樹脂との親和性が高いため、ガラス繊維(b)と環状オ
レフィン系樹脂(a)との界面の密着力が高くなり、ガ
ラス繊維による強化が効果的に起こるために、本発明の
組成物を使用した成形品の強度が高まるものと推定され
る。
(C) Olefin-based resin The present inventors have found that the mechanical strength of the composition of the cyclic olefin-based resin and the glass fiber largely changes depending on what kind of binder resin is used. inside that,
It was found that when the olefin resin (c) was used as a binder, the composition had the highest strength and was the optimum binder. It is not clear in detail why the olefin resin (c) is the most suitable as the binder resin, but since the olefin resin (c) and the cyclic olefin resin have high affinity, It is presumed that the adhesiveness at the interface with the cyclic olefin resin (a) becomes high and the reinforcement by the glass fiber effectively occurs, so that the strength of the molded product using the composition of the present invention is increased.

【0021】バインダー用のオレフィン系樹脂(c)と
しては、低密度ポリエチレン(LDPE)、直鎖状低密度ポリ
エチレン(LLDPE)、中密度ポリエチレン(MDPE)、高密度
ポリエチレン(HDPE)、ポリプロピレン、ポリ1−ブテ
ン、ポリメチルペンテン、エチレン−プロピレン共重合
体、エチレン−ブテン共重合体、エチレン−オクテン共
重合体等のエチレン−α−オレフィン共重合体、プロピ
レン−α−オレフィン共重合体、エチレン−プロピレン
−ジエン共重合体、ポリブタジエン、ポリイソプレン、
ポリイソブチレン等が挙げられる。もちろん前記環状オ
レフィン系樹脂も好適なバインダー樹脂として使用でき
る。これらのオレフィン系樹脂にカルボキシル基、酸無
水物基、エポキシ基、アミド基、エステル基、ヒドロキ
シル基等の官能基を有する不飽和化合物をグラフ卜及び
/又は共重合した変性オレフィン系樹脂も好適に使用で
きる。これらオレフィン系樹脂(c)は単独であるいは
2種以上を混合して使用してもよい。オレフィン系樹脂
(c)にグラフト及び/又は付加共重合させる官能基を
有する不飽和化合物(v)としては、例えば、(メタ)
アクリル酸、マレイン酸、無水マレイン酸、無水イタコ
ン酸、グリシジル(メタ)アクリレート、(メタ)アク
リル酸アルキル(炭素数1〜10)エステル、マレイン
酸アルキル(炭素数1〜10)エステル、(メタ)アク
リルアミド、(メタ)アクリル酸−2−ヒドロキシエチ
ル等が挙げられる。前記官能基を有する不飽和化合物
(u)と上記官能基を有する不飽和化合物(v)とは、
異なっていても、同じものでもよい。上記変性オレフィ
ン系樹脂中の不飽和化合物(v)ユニットの含有率は
0.01〜20重量%、好ましくは0.1〜10重量%
である。オレフィン系樹脂(c)の中でも、好ましくは
ポリエチレン、ポリプロピレン、エチレン−α−オレフ
ィン共重合体、プロピレン−α−オレフィン共重合体、
環状オレフィン系樹脂、およびこれらの変性物が挙げら
れ、さらに好ましくは低密度ポリエチレン(LDPE)、直鎖
状低密度ポリエチレン(LLDPE)、ポリプロピレン、環状
オレフィン系樹脂、およびこれらの変性物が挙げられ
る。
As the olefin resin (c) for the binder, low density polyethylene (LDPE), linear low density polyethylene (LLDPE), medium density polyethylene (MDPE), high density polyethylene (HDPE), polypropylene, poly 1 -Ethylene-α-olefin copolymers such as butene, polymethylpentene, ethylene-propylene copolymers, ethylene-butene copolymers, ethylene-octene copolymers, propylene-α-olefin copolymers, ethylene-propylene -Diene copolymer, polybutadiene, polyisoprene,
Examples thereof include polyisobutylene. Of course, the above-mentioned cyclic olefin resin can also be used as a suitable binder resin. A modified olefin resin obtained by grafting and / or copolymerizing an unsaturated compound having a functional group such as a carboxyl group, an acid anhydride group, an epoxy group, an amide group, an ester group or a hydroxyl group with these olefin resins is also suitable. Can be used. These olefin resins (c) may be used alone or in combination of two or more. Examples of the unsaturated compound (v) having a functional group to be grafted and / or addition-copolymerized with the olefin resin (c) include (meth)
Acrylic acid, maleic acid, maleic anhydride, itaconic anhydride, glycidyl (meth) acrylate, alkyl (meth) acrylate (C 1-10) ester, alkyl maleate (C 1-10) ester, (meth) Examples thereof include acrylamide and 2-hydroxyethyl (meth) acrylate. The unsaturated compound (u) having a functional group and the unsaturated compound (v) having a functional group are
They may be different or the same. The content of the unsaturated compound (v) unit in the modified olefin resin is 0.01 to 20% by weight, preferably 0.1 to 10% by weight.
Is. Among the olefin resins (c), preferably polyethylene, polypropylene, ethylene-α-olefin copolymer, propylene-α-olefin copolymer,
Examples thereof include cyclic olefin-based resins and modified products thereof, more preferably low density polyethylene (LDPE), linear low-density polyethylene (LLDPE), polypropylene, cyclic olefin-based resins, and modified products thereof.

【0022】バインダー用のオレフィン系樹脂(c)の
数平均分子量としては、例えば500〜10万程度のも
のが使用できる。
The number average molecular weight of the olefin resin (c) for the binder may be, for example, about 500 to 100,000.

【0023】ガラス繊維(b)100重量部に対して、
オレフィン系樹脂(c)のバインダーとしての使用量は
0.1〜5重量部、好ましくは0.2〜3重量部、特に
好ましくは0.5〜2重量部である。オレフィン系樹脂
(c)の使用量が上記範囲より少ないと、ガラス繊維の
集束が十分でなく、毛羽立ちやロービングの分解が生
じ、ガラス繊維の取扱いに障害がでて好ましくない。使
用量が多いと、組成物の強度をかえって低下させてしま
い好ましくない。
With respect to 100 parts by weight of the glass fiber (b),
The amount of the olefin resin (c) used as a binder is 0.1 to 5 parts by weight, preferably 0.2 to 3 parts by weight, and particularly preferably 0.5 to 2 parts by weight. When the amount of the olefin resin (c) used is less than the above range, the glass fibers are not sufficiently bundled, and fluffing and roving are decomposed, which is not preferable because the glass fibers are impaired in handling. When a large amount is used, the strength of the composition is rather lowered, which is not preferable.

【0024】ガラス繊維ロービングは、表面をシランカ
ップリング剤等により処理しておいてもよい。シランカ
ップリング剤はバインダー樹脂に加えて使用されてもよ
い。シランカップリング剤としては、ガラス及び樹脂の
種類に応じて、ビニルトリエトキシシラン、γ−グリシ
ジルオキシプロピルトリエトキシシラン、γ−アミノプ
ロピルトリエトキシシラン、γ−クロルプロピルトリメ
トキシシラン等の各種の市販品が使用できる。
The surface of the glass fiber roving may be treated with a silane coupling agent or the like. The silane coupling agent may be used in addition to the binder resin. As the silane coupling agent, various commercially available vinyltriethoxysilane, γ-glycidyloxypropyltriethoxysilane, γ-aminopropyltriethoxysilane, γ-chloropropyltrimethoxysilane, etc., depending on the type of glass and resin. Goods can be used.

【0025】オレフィン系樹脂(c)をバインダーに使
用して、ガラス繊維(b)を集束させる方法としては、
例えば、バインダー樹脂の溶液または懸濁液(必要に応
じてシランカップリング剤を含んでいてもよい)にガラ
ス繊維を浸漬した後、加熱、乾燥させる方法が挙げられ
る。バインダー樹脂の溶液は、溶剤溶液でもエマルジョ
ン水溶液でもよい。
The method for bundling the glass fibers (b) using the olefin resin (c) as a binder is as follows:
For example, a method of immersing the glass fiber in a solution or suspension of a binder resin (which may optionally contain a silane coupling agent), followed by heating and drying is mentioned. The binder resin solution may be a solvent solution or an emulsion aqueous solution.

【0026】本発明のガラス繊維強化環状オレフィン系
樹脂組成物は、環状オレフィン系樹脂(a)と、オレフ
ィン系樹脂(c)をバインダーに使用して集束されたガ
ラス繊維(b)とからなる。ガラス繊維強化環状オレフ
ィン系樹脂組成物において、バインダー樹脂集束ガラス
繊維(b)の添加量は、環状オレフィン系樹脂(a)と
バインダー樹脂集束ガラス繊維(b)の合計重量(aと
bの合計は100重量%である。)に対し5〜60重量
%、好ましくは10〜40重量%である。ガラス繊維の
添加量が上記範囲より少なすぎると組成物の強度が十分
でなく、多すぎると組成物の成形が困難になり好ましく
ない。
The glass fiber reinforced cyclic olefin resin composition of the present invention comprises a cyclic olefin resin (a) and glass fibers (b) which are bundled using the olefin resin (c) as a binder. In the glass fiber reinforced cyclic olefin resin composition, the addition amount of the binder resin-focused glass fiber (b) is the total weight of the cyclic olefin resin (a) and the binder resin-focused glass fiber (b) (the sum of a and b is It is 5 to 60% by weight, preferably 10 to 40% by weight, based on 100% by weight). If the amount of glass fiber added is less than the above range, the strength of the composition is insufficient, and if it is too large, molding of the composition becomes difficult, which is not preferable.

【0027】ガラス繊維強化環状オレフィン系樹脂組成
物には、その特性を損なわない範囲で、必要に応じて、
エラストマー(e)、その他の熱可塑性樹脂(f)、ガ
ラス繊維以外の無機あるいは有機充填剤(g)、各種配
合剤(h)等を添加することができる。
The glass fiber reinforced cyclic olefin resin composition may be added to the glass fiber reinforced cyclic olefin resin composition, if necessary, within a range not impairing its properties.
Elastomer (e), other thermoplastic resin (f), inorganic or organic filler (g) other than glass fiber, various compounding agents (h) and the like can be added.

【0028】上記エラストマー(e)は、ガラス転移温
度が30℃以下の重合体であって、通常のゴム質重合体
および熱可塑性エラストマーが含まれる。なお、ブロッ
ク共重合したゴム質重合体などでガラス転移温度が2種
以上ある場合は、最も低いガラス転移温度が30℃以下
であれば、上記ガラス転移温度が30℃以下のゴム質重
合体として用いることができる。エラストマー(e)と
しては、エチレン−プロピレン共重合体、エチレン−α
−オレフィン共重合体、プロピレン−α−オレフィン共
重合体などの飽和オレフィン系エラストマー;エチレン
−プロピレン−ジエン共重合体、α−オレフィン−ジエ
ン共重合体、イソブチレン−イソプレン共重合体、イソ
ブチレン−ジエン共重合体などのジエン系共重合体、こ
れらのハロゲン化物、ジエン系重合体またはそのハロゲ
ン化物の水素添加物;アクリロニトリル−ブタジエン共
重合体、その水素添加物;イソプレンゴム、その水素添
加物;クロロプレンゴム、その水素添加物;フッ化ビニ
リデン−三フッ化エチレン共重合体、フッ化ビニリデン
−六フッ化プロピレン共重合体、フッ化ビニリデン−六
フッ化ブロピレン−四フッ化エチレン共重合体;プロピ
レン−四フッ化エチレン共重合体などのフッ素ゴム;ウ
レタンゴム、シリコーンゴム、ポリエーテル系ゴム、ア
クリルゴム、クロルスルホン化ポリエチレンゴム、エピ
クロルヒドリンゴム、プロピレンオキサイドゴム、エチ
レンアクリルゴムなどの特殊ゴム;ノルボルネン系単量
体とエチレンまたはα−オレフィンの共重合体、ノルボ
ルネン系単量体とエチレンとα−オレフィンの三元共重
合体、ノルボルネン系単量体の開環重合体、ノルボルネ
ン系単量体の開環重合体水素添加物などのノルボルネン
系ゴム質重合体;乳化重合または溶液重合したスチレン
−ブタジエンゴム、ハイスチレンゴムなどのランダムま
たはブロック−スチレン−ブタジエン系共重合体、これ
らの水素添加物;スチレン−ブタジエン−スチレンゴ
ム、スチレン−イソプレン−スチレンゴム、スチレン−
エチレン−ブタジエン−スチレンゴムなどの芳香族ビニ
ル系モノマー−共役ジエンのランダム共重合体、これら
の水素添加物;スチレン−ブタジエン−スチレンゴム、
スチレン−イソプレン−スチレンゴム、スチレン−エチ
レン−ブタジエン−スチレンゴムなどの芳香族ビニル系
モノマー−共役ジエンの直鎖状または放射状ブロック共
重合体、それらの水素添加物などのスチレン系熱可塑性
エラストマーをはじめ、ウレタン系熱可塑性エラストマ
ー、ポリアミド系熱可塑性エラストマー、1,2−ポリ
ブタジエン系熱可塑性エラストマー、塩化ビニル系熱可
塑性エラストマー、フッ素系熱可塑性エラストマーなど
の熱可塑性エラストマー等が挙げられる。これらの中で
も、飽和オレフィン系エラストマー、もしくは芳香族ビ
ニル系モノマーと共役ジエン系モノマーの共重合体およ
びその水素添加物が、環状オレフィン系樹脂との親和性
が高く好ましい。芳香族ビニル系モノマーと共役ジエン
系モノマーの共重合体はブロック共重合体でもランダム
共重合体でもよい。耐候性の点から芳香環以外の部分を
水素添加しているものがより好ましい。具体的には、エ
チレン−プロピレン共重合体、エチレン−α−オレフィ
ン共重合体、プロピレン−α−オレフィン共重合体、ス
チレン−ブタジエンブロック共重合体、スチレン−ブタ
ジエン−スチレン−ブロック共重合体、スチレン−イソ
プレン−ブロック共重合体、スチレン−イソプレン−ス
チレン−ブロック共重合体、およびこれらの水素添加
物、スチレン−ブタジエン−ランダム共重合体およびこ
れらの水素添加物などが挙げられる。
The above-mentioned elastomer (e) is a polymer having a glass transition temperature of 30 ° C. or lower, and includes usual rubbery polymers and thermoplastic elastomers. In the case where the block copolymerized rubbery polymer or the like has two or more glass transition temperatures, if the lowest glass transition temperature is 30 ° C. or lower, the rubbery polymer having the glass transition temperature of 30 ° C. or lower is obtained. Can be used. As the elastomer (e), ethylene-propylene copolymer, ethylene-α
-Saturated olefin elastomer such as olefin copolymer and propylene-α-olefin copolymer; ethylene-propylene-diene copolymer, α-olefin-diene copolymer, isobutylene-isoprene copolymer, isobutylene-diene copolymer Diene-based copolymers such as polymers, hydrogenates of these halides, diene-based polymers or their halides; acrylonitrile-butadiene copolymers, hydrogenated products thereof; isoprene rubber, hydrogenated products thereof; chloroprene rubber , Its hydrogenated product; vinylidene fluoride-trifluoroethylene copolymer, vinylidene fluoride-hexafluoropropylene copolymer, vinylidene fluoride-hexafluorobropylene-tetrafluoroethylene copolymer; propylene-4 Fluorine rubber such as fluorinated ethylene copolymer; urethane rubber, silicone Rubbers, polyether rubbers, acrylic rubbers, chlorosulfonated polyethylene rubbers, epichlorohydrin rubbers, propylene oxide rubbers, ethylene acrylic rubbers and other special rubbers; norbornene monomers and ethylene or α-olefin copolymers, norbornene monomers Norbornene rubber polymers such as terpolymers of terpolymers with ethylene and α-olefins, ring-opening polymers of norbornene-based monomers, ring-opening polymers of norbornene-based monomers, and hydrogenated products; emulsion polymerization Random or block-styrene-butadiene copolymers such as solution-polymerized styrene-butadiene rubber and high styrene rubber, and hydrogenated products thereof; styrene-butadiene-styrene rubber, styrene-isoprene-styrene rubber, styrene-
Random copolymer of aromatic vinyl monomer such as ethylene-butadiene-styrene rubber-conjugated diene, hydrogenated product thereof; styrene-butadiene-styrene rubber,
Aromatic vinyl monomers such as styrene-isoprene-styrene rubber and styrene-ethylene-butadiene-styrene rubber, linear or radial block copolymers of conjugated dienes, and styrene-based thermoplastic elastomers such as hydrogenated products thereof. , Thermoplastic elastomers such as urethane-based thermoplastic elastomers, polyamide-based thermoplastic elastomers, 1,2-polybutadiene-based thermoplastic elastomers, vinyl chloride-based thermoplastic elastomers, and fluorine-based thermoplastic elastomers. Among these, a saturated olefin-based elastomer, a copolymer of an aromatic vinyl-based monomer and a conjugated diene-based monomer, and a hydrogenated product thereof are preferable because of their high affinity with the cyclic olefin-based resin. The copolymer of the aromatic vinyl-based monomer and the conjugated diene-based monomer may be a block copolymer or a random copolymer. From the viewpoint of weather resistance, it is more preferable to hydrogenate a portion other than the aromatic ring. Specifically, ethylene-propylene copolymer, ethylene-α-olefin copolymer, propylene-α-olefin copolymer, styrene-butadiene block copolymer, styrene-butadiene-styrene-block copolymer, styrene -Isoprene-block copolymers, styrene-isoprene-styrene-block copolymers, hydrogenated products thereof, styrene-butadiene-random copolymers, hydrogenated products thereof, and the like.

【0029】その他の熱可塑性樹脂(f)としては、例
えば、ポリフェニレンスルフイド、ポリフェニレンエー
テル、ポリエーテルスルホン、ポリスルフォン、ポリカ
ーボネート、ポリアセタールなどの他、液晶プラスチッ
ク、芳香族ポリエステル、ポリアリレート、ポリエチレ
ンテレフタレート、ポリブチレンテレフタレートなどの
ポリエステル系重合体;ポリエチレン、ポリプロピレ
ン、ポリ4−メチルペンテン−1などのポリオレフィン
系重合体;ナイロン6、ナイロン66、芳香族ナイロン
などのポリアミド系重合体;ポリメチルメタクリレー
ト、ポリアクリロニトリルスチレン(AS樹脂)、ポリス
チレンなどが挙げられる。
Other thermoplastic resins (f) include, for example, polyphenylene sulfide, polyphenylene ether, polyether sulfone, polysulfone, polycarbonate, polyacetal, liquid crystal plastic, aromatic polyester, polyarylate, polyethylene terephthalate. Polyester polymers such as polybutylene terephthalate; Polyolefin polymers such as polyethylene, polypropylene and poly 4-methylpentene-1; Polyamide polymers such as nylon 6, nylon 66 and aromatic nylon; polymethyl methacrylate, poly Examples thereof include acrylonitrile styrene (AS resin) and polystyrene.

【0030】上記ガラス繊維以外の無機あるいは有機充
填剤(g)の中、ガラス繊維以外の無機充填剤として
は、特に限定はないが、例えば、軽質炭酸カルシウム、
重質ないし微粉化炭酸カルシウム、特殊カルシウム系充
填剤などの炭酸カルシウム粉末;霞石閃長岩微粉末;モ
ンモリロナイト、ベントナイト等のクレー、焼成クレ
ー、シラン改質クレーなどのクレー(ケイ酸アルミニウ
ム粉末);タルク;溶融シリカ、結晶シリカなどのシリ
カ(二酸化ケイ素)粉末;ケイ藻土、ケイ砂などのケイ酸
含有化合物;軽石粉、スレート粉、マイカ、雲母粉、ア
スベストなどの天然鉱物、及びその粉砕品;アルミナ、
アルミナコロイド(アルミナゾル)、アルミナ・ホワイ
ト、硫酸アルミニウムなどのアルミナ含有化合物;硫酸
バリウム、リトポン、硫酸カルシウム、二硫化モリブデ
ン、グラファイト(黒鉛)などの鉱物;ガラスビーズ、ガ
ラスフレーク、発泡ガラスビーズなどのガラス系フィラ
ー;フライアッシュ球、火山ガラス中空体、軽石バルー
ン、合成無機中空体、炭素中空球;無煙炭粉末、人造氷
晶石(クリオライト)、酸化チタン、酸化マグネシウム、
塩基性炭酸マグネシウム、ドロマイト、チタン酸カリウ
ム、単結晶チタン酸カリ、亜硫酸カルシウム、ケイ酸カ
ルシウム、アルミニウム粉、硫化モリブデン;カーボン
繊維、ボロン繊維、炭化ケイ素繊維などが挙げられる。
上記ガラス繊維以外の無機あるいは有機充填剤(g)の
中、有機充填剤としては、例えば、ポリエチレン繊維、
ポリプロピレン繊維、ポリエステル繊維、ポリアミド繊
維、フッ素繊維、エボナイト粉末、熱硬化性樹脂中空
球、熱硬化性樹脂フィラー、エポキシ樹脂フィラー、シ
リコン系フィラー、サラン中空球、セラック、木粉、コ
ルク粉末、ポリビニルアルコール繊維、セルロースパウ
ダ、木材パルプなどが挙げられる。
Among the inorganic or organic fillers (g) other than the above glass fibers, the inorganic fillers other than the glass fibers are not particularly limited, and examples thereof include light calcium carbonate,
Calcium carbonate powder such as heavy or finely powdered calcium carbonate and special calcium-based filler; nepheline syenite fine powder; clay such as montmorillonite, bentonite, calcined clay, silane modified clay (aluminum silicate powder); Talc: Silica (silicon dioxide) powder such as fused silica and crystalline silica; Silica-containing compounds such as diatomaceous earth and silica sand; Natural minerals such as pumice powder, slate powder, mica, mica powder, and asbestos, and crushed products thereof ;alumina,
Alumina-containing compounds such as alumina colloid (alumina sol), alumina white, aluminum sulfate; minerals such as barium sulfate, lithopone, calcium sulfate, molybdenum disulfide, graphite (graphite); glass such as glass beads, glass flakes and foam glass beads -Based fillers; fly ash spheres, volcanic glass hollow bodies, pumice balloons, synthetic inorganic hollow bodies, carbon hollow spheres: anthracite powder, artificial cryolite (cryolite), titanium oxide, magnesium oxide,
Examples include basic magnesium carbonate, dolomite, potassium titanate, single crystal potassium titanate, calcium sulfite, calcium silicate, aluminum powder, molybdenum sulfide; carbon fiber, boron fiber, silicon carbide fiber and the like.
Among the inorganic or organic fillers (g) other than the above glass fibers, examples of the organic fillers include polyethylene fibers,
Polypropylene fiber, polyester fiber, polyamide fiber, fluorine fiber, ebonite powder, thermosetting resin hollow sphere, thermosetting resin filler, epoxy resin filler, silicone filler, Saran hollow sphere, shellac, wood powder, cork powder, polyvinyl alcohol Fiber, cellulose powder, wood pulp and the like can be mentioned.

【0031】上記各種配合剤(h)としては、熱可塑性
樹脂材料で通常用いられているものであれば格別な制限
はなく、例えば、酸化防止剤、紫外線吸収剤、光安定
剤、可塑剤、滑剤、帯電防止剤、難燃剤、染料や顔料な
どの着色剤、近赤外線吸収剤、蛍光増白剤などの配合剤
が挙げられる。
The above-mentioned various compounding agents (h) are not particularly limited as long as they are usually used in thermoplastic resin materials, and examples thereof include an antioxidant, an ultraviolet absorber, a light stabilizer, a plasticizer, Examples thereof include lubricants, antistatic agents, flame retardants, coloring agents such as dyes and pigments, near-infrared absorbing agents, and compounding agents such as optical brighteners.

【0032】本発明のガラス繊維強化環状オレフィン系
樹脂組成物は、上記成分を必要に応じて混合して調製さ
れる。混合方法はこれらの成分が十分に分散する方法で
あれば、特に限定されない。例えば、ミキサーや二軸混
練機、ロール、ブラベンダー、一軸もしくは二軸押出機
などで溶融状態で混練する方法や、樹脂成分の溶融物を
ガラス繊維ロービングに塗布する方法、適当な溶剤に溶
解して配合剤を分散させた後、凝固法、キャスト法、ま
たは直接乾燥法により溶剤を除去する方法などがある。
特に押出機を用いて溶融状態にて混練した後、棒状に押
出し、これを適当な長さに切ってペレットとする方法
が、生産性が高く、好適である。溶融混練時の温度は使
用する環状オレフィン系樹脂の種類によって異なるが、
通常100〜400℃、好ましくは200〜350℃で
ある。
The glass fiber reinforced cyclic olefin resin composition of the present invention is prepared by mixing the above-mentioned components as necessary. The mixing method is not particularly limited as long as these components are sufficiently dispersed. For example, a method of kneading in a molten state with a mixer, a twin-screw kneader, a roll, a Brabender, a single-screw or twin-screw extruder, a method of applying a melt of a resin component to a glass fiber roving, a method of dissolving in a suitable solvent And the like, and then the solvent is removed by a coagulation method, a casting method, or a direct drying method.
In particular, a method of kneading in a molten state using an extruder, extruding into a rod shape, and cutting this into an appropriate length to obtain pellets is preferable because of high productivity. The temperature during melt-kneading varies depending on the type of cyclic olefin resin used,
It is usually 100 to 400 ° C, preferably 200 to 350 ° C.

【0033】本発明のガラス繊維強化環状オレフィン系
樹脂組成物は、そのまま、好ましくは上記ペレットの形
状にして射出成形、射出圧縮成形、圧縮成形、押出成
形、ブロー成形等により、成形品を得ることができる。
The glass fiber reinforced cyclic olefin resin composition of the present invention is used as it is, preferably in the form of pellets described above, to obtain a molded product by injection molding, injection compression molding, compression molding, extrusion molding, blow molding or the like. You can

【0034】[0034]

【実施例】以下、実施例により本発明を具体的に説明す
るが、本発明はこれらに限定されるものではない。な
お、実施例および比較例の組成物の物性は以下のように
評価した。 引張強度および伸び:JIS K7161に従い測定し
た。 曲げ強度および弾性率:JIS K7171に従い測定
した。 シヤルピー衝撃強度:JIS K7111に従い測定し
た。
EXAMPLES The present invention will now be described in detail with reference to examples, but the present invention is not limited thereto. The physical properties of the compositions of Examples and Comparative Examples were evaluated as follows. Tensile strength and elongation: Measured according to JIS K7161. Bending strength and elastic modulus: Measured according to JIS K7171. Shearpy impact strength: Measured according to JIS K7111.

【0035】環状オレフィン系樹脂として以下の市販の
樹脂を使用した。 A1:トーパス6015(Ticona社製、ノルボルネンとエチ
レンの付加共重合体) A2:トーパス6017(Ticona社製、ノルボルネンとエチ
レンの付加共重合体) A3:アペルAPL6015T(三井化学製、テトラシクロドデ
センとエチレンの付加共重合体) A4:ゼオノア1600R(日本ゼオン製、ノルボルネン系
環状オレフィンの開環重合体の水素添加物) A5:ゼオネックス480R(日本ゼオン製、ノルボルネン
系環状オレフィンの開環重合体の水素添加物) A6:アートンG(日本合成ゴム製、ジシクロペンタジ
エンとメタクリル酸エステルのディールス−アルダー付
加体の開環重合体の水素添加物)
The following commercially available resins were used as the cyclic olefin resin. A1: Topas 6015 (Ticona, an addition copolymer of norbornene and ethylene) A2: Topas 6017 (Ticona, an addition copolymer of norbornene and ethylene) A3: Apel APL6015T (Mitsui Chemicals, tetracyclododecene) Addition Copolymer of Ethylene) A4: Zeonoa 1600R (hydrogenated product of ring-opening polymer of norbornene-based cyclic olefin manufactured by Nippon Zeon) A5: Zeonex 480R (hydrogen of ring-opened polymer of norbornene-based cyclic olefin manufactured by Nippon Zeon) Additives) A6: Arton G (manufactured by Japan Synthetic Rubber, hydrogenated product of ring-opening polymer of Diels-Alder adduct of dicyclopentadiene and methacrylic acid ester)

【0036】バインダー樹脂として表1に示す樹脂を使
用した。 無水マレイン酸変性ポリプロピレン:HYTEC P-5300(東
邦化学製) ビスフェノールA系エポキシ樹脂:エピコート1001(油
化シェルエポキシ製) ノボラック系エポキシ樹脂:エピコート157S70(油化シ
ェルエポキシ製) ウレタン樹脂:ボンディック194ONS(大日本インキ製)
The resins shown in Table 1 were used as the binder resin. Maleic anhydride modified polypropylene: HYTEC P-5300 (manufactured by Toho Kagaku) Bisphenol A epoxy resin: Epicoat 1001 (oil shell epoxy) Novolac epoxy resin: Epicoat 157S70 (oil shell epoxy) Urethane resin: Bondic 194ONS (Manufactured by Dainippon Ink)

【0037】[調製例1〜5](種々のバインダー樹脂で
集束されたガラス繊維の調製) 水に対し、酢酸が0.1重量%およびγ−アミノプロピ
ルトリエトキシシラン(日本ユニカー(株)製A−110
0)が0.5重量%となるように、よく撹拌しながら滴
下して水溶液を調製した。この水溶液に、表1に示すバ
インダー樹脂の水エマルジョンを、固形分濃度が1重量
%になるように加え、混合して集束剤液を調製した。こ
の集束剤液に、600℃で熱処理、脱脂した直径13μ
mのEガラスのガラス繊維ロービングを浸漬した後、1
30℃で10分間乾燥させることにより、異なるバイン
ダー樹脂による集束を行い、種々のバインダー樹脂で集
束されたガラス繊維(B1)〜(B5)を得た。処理さ
れたガラス繊維ロービングを長さ3mmに切断してチョ
ップドストランドとして、以下の実施例および比較例に
供した。表1に、バインダー樹脂の種類、バインダー樹
脂のガラス繊維への付着量(単位:重量%)、処理後の
ガラス繊維の記号を示す。
[Preparation Examples 1 to 5] (Preparation of glass fiber bundled with various binder resins) 0.1% by weight of acetic acid and γ-aminopropyltriethoxysilane (manufactured by Nippon Unicar Co., Ltd.) in water. A-110
0) was 0.5% by weight, and an aqueous solution was prepared by dropwise addition with good stirring. A water emulsion of the binder resin shown in Table 1 was added to this aqueous solution so that the solid content concentration was 1% by weight, and mixed to prepare a sizing agent liquid. This sizing agent liquid was heat-treated at 600 ° C. and degreased to a diameter of 13 μ
After dipping m glass fiber roving of E glass, 1
By drying at 30 ° C. for 10 minutes, different binder resins were bundled to obtain glass fibers (B1) to (B5) bundled with various binder resins. The treated glass fiber roving was cut into a length of 3 mm to obtain chopped strands, which were used in the following examples and comparative examples. Table 1 shows the types of the binder resin, the amount of the binder resin attached to the glass fiber (unit: wt%), and the symbols of the glass fiber after the treatment.

【0038】[0038]

【表1】 [Table 1]

【0039】[実施例1]環状オレフィン系樹脂としてト
ーパス6015(A1)70重量%、および、調製例1
(バインダー樹脂にオレフィン系樹脂を使用)で得られ
たガラス繊維(B1)30重量%を、二軸押出機を使い
シリンダー温度300℃にて、溶融混練し、ガラス繊維
強化環状オレフィン系樹脂組成物のペレットを得た。こ
のペレットを、シリンダー温度300℃、金型温度90
℃にて射出成形して試験片を成形し、物性を評価した。
評価結果を表2に示す。
[Example 1] 70% by weight of TOPAS 6015 (A1) as a cyclic olefin resin, and Preparation Example 1
30% by weight of glass fiber (B1) obtained by (using olefin resin as binder resin) is melt-kneaded at a cylinder temperature of 300 ° C. using a twin-screw extruder to obtain a glass fiber-reinforced cyclic olefin resin composition. Of pellets were obtained. Cylinder temperature 300 ° C, mold temperature 90
The test piece was molded by injection molding at ℃, and the physical properties were evaluated.
The evaluation results are shown in Table 2.

【0040】[比較例1〜4](オレフィン系樹脂以外の
バインダー樹脂の使用) ガラス繊維としてバインダー樹脂がオレフィン系樹脂で
はないガラス繊維(B2〜B5)を用いた以外は、実施
例1と同様にして、組成物のペレットを作成し、射出成
形して得られた試験片の物性を評価した。評価結果を同
じく表2に示す。実施例1および比較例1〜4の結果か
ら明らかなように、バインダー樹脂にオレフィン系樹脂
を用いたガラス繊維を使った場合に、組成物を射出成形
して得られた試験片の機械的強度が最大となっており、
環状オレフィン系樹脂向けのガラス繊維として最適であ
ることがわかる。
[Comparative Examples 1 to 4] (Use of Binder Resin Other Than Olefin Resin) Same as Example 1 except that glass fibers (B2 to B5) whose binder resin is not an olefin resin are used as the glass fibers. Then, a pellet of the composition was prepared, and the physical properties of a test piece obtained by injection molding were evaluated. The evaluation results are also shown in Table 2. As is clear from the results of Example 1 and Comparative Examples 1 to 4, the mechanical strength of the test piece obtained by injection molding the composition when the glass fiber using the olefin resin as the binder resin was used. Is the maximum,
It can be seen that it is most suitable as a glass fiber for cyclic olefin resin.

【0041】[0041]

【表2】 [Table 2]

【0042】[実施例2〜10]表3および表4に示すよ
うに、ガラス繊維の添加量、および環状オレフィン系樹
脂(a)の種類を変えて、実施例1と同様に実験を行っ
た。バインダー樹脂にオレフィン系樹脂を用いたガラス
繊維(B1)は広範な組成比で使用可能であり、また環
状オレフィン系樹脂の種類によらず使用可能である。
[Examples 2 to 10] As shown in Tables 3 and 4, the same experiment as in Example 1 was carried out by changing the addition amount of the glass fiber and the kind of the cyclic olefin resin (a). . The glass fiber (B1) using an olefin resin as the binder resin can be used in a wide range of composition ratios and can be used regardless of the type of cyclic olefin resin.

【0043】[0043]

【表3】 [Table 3]

【0044】[0044]

【表4】 [Table 4]

【0045】[実施例11] (変性環状オレフィン樹脂(AF)の合成)環状オレフ
ィン樹脂トーパス5013(Ticona社製)98重量部、無水
マレイン酸2重量部、および過酸化物としてパーヘキシ
ン25B(日本油脂製)0.2重量部を、二軸押出機にて
シリンダー温度200℃で溶融混練して、無水マレイン酸
をグラフ卜した変性環状オレフィン系樹脂を合成した。
トーパス6015(A1)を63重量%、上記で得られた
変性環状オレフィン系樹脂(AF)を7重量%、調製例
1で得られたガラス繊維(B1)30重量%を、実施例
1と同様に溶融混練、成形し、物性を評価した。結果を
表4に示す。実施例1と比較して明らかに強度が向上し
ており、官能基をグラフ卜した変性環状オレフィン系樹
脂を加えると、組成物のさらなる強度の改善が図れるこ
とが示されている。
[Example 11] (Synthesis of modified cyclic olefin resin (AF)) Cyclic olefin resin Topas 5013 (manufactured by Ticona) 98 parts by weight, maleic anhydride 2 parts by weight, and peroxide Perhexin 25B (NOF Corporation). 0.2 parts by weight) was melt-kneaded with a twin-screw extruder at a cylinder temperature of 200 ° C. to synthesize a modified cyclic olefin resin in which maleic anhydride was graphed.
63% by weight of Topas 6015 (A1), 7% by weight of the modified cycloolefin resin (AF) obtained above, and 30% by weight of the glass fiber (B1) obtained in Preparation Example 1 were used in the same manner as in Example 1. The mixture was melt-kneaded and molded, and the physical properties were evaluated. The results are shown in Table 4. The strength is clearly improved as compared with Example 1, and it is shown that the strength of the composition can be further improved by adding a modified cyclic olefin resin having a functional group.

【0046】[比較例5](線状ポリオレフィン系樹脂と
の比較) 環状ポリオレフィン系樹脂の代りに、線状ポリオレフィ
ン系樹脂であるポリプロピレン(グランドポリマー製J-
105)と調製例1で得られたガラス繊維(B1)を用
い、実施例1と同様にして、二軸押出機でシリンダー温
度240℃にて溶融混練したペレットをシリンダー温度240
℃、金型温度45℃にて射出成形し、物性を評価した。結
果を表5に示す。環状オレフィン樹脂を使用した場合、
線状ポリオレフィン系樹脂を使用した場合に比べ、より
高強度、高剛性であり良好な物性を示すことがわかる。
Comparative Example 5 (Comparison with Linear Polyolefin Resin) Instead of the cyclic polyolefin resin, polypropylene which is a linear polyolefin resin (J-made by Grand Polymer
105) and the glass fiber (B1) obtained in Preparation Example 1 were melt-kneaded at a cylinder temperature of 240 ° C. in a twin-screw extruder in the same manner as in Example 1 to prepare pellets having a cylinder temperature of 240.
Injection molding was carried out at a mold temperature of 45 ° C. and the physical properties were evaluated. The results are shown in Table 5. When using cyclic olefin resin,
It can be seen that, as compared with the case where the linear polyolefin resin is used, the strength and rigidity are higher and the physical properties are better.

【0047】[0047]

【表5】 [Table 5]

【0048】[0048]

【発明の効果】本発明によれば、高い熱変形温度、寸法
安定性、低そり変形、軽量性、耐熱水性に優れ、さらに
強度、剛性といった機械的強度を向上させた、成形品用
のガラス繊維強化環状オレフィン系樹脂組成物が得られ
る。
EFFECT OF THE INVENTION According to the present invention, a glass for a molded article, which has a high heat distortion temperature, dimensional stability, low warpage deformation, light weight, hot water resistance, and improved mechanical strength such as strength and rigidity. A fiber reinforced cyclic olefin resin composition is obtained.

───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 4F071 AA14A AA39 AA69 AB28 AD01 AE17 AF01 AF04 AF30 AF31 AF45 AF54 AH14 4J002 BB002 BB101 BK001 BN002 CE001 FA046 FB266 FD016 FD202 GS02    ─────────────────────────────────────────────────── ─── Continued front page    F-term (reference) 4F071 AA14A AA39 AA69 AB28                       AD01 AE17 AF01 AF04 AF30                       AF31 AF45 AF54 AH14                 4J002 BB002 BB101 BK001 BN002                       CE001 FA046 FB266 FD016                       FD202 GS02

Claims (6)

【特許請求の範囲】[Claims] 【請求項1】 環状オレフィン系樹脂(a)とバインダ
ー樹脂集束ガラス繊維(b)からなる熱可塑性樹脂組成
物において、バインダー樹脂集束ガラス繊維(b)がオ
レフィン系樹脂(c)をバインダー樹脂に使用してガラ
ス繊維を集束させたものであることを特徴とするガラス
繊維強化環状オレフィン系樹脂組成物。
1. A thermoplastic resin composition comprising a cyclic olefin resin (a) and a binder resin-focused glass fiber (b), wherein the binder resin-focused glass fiber (b) uses an olefin resin (c) as a binder resin. A glass fiber reinforced cyclic olefin-based resin composition, characterized in that it is obtained by bundling glass fibers.
【請求項2】 環状オレフィン系樹脂(a)が、環状オ
レフィンの付加(共)重合体またはその水素添加物(a
l)、環状オレフィンとα−オレフィンの付加共重合体
またはその水素添加物(a2)、環状オレフィンの開環
(共)重合体またはその水素添加物(a3)、及び上記
環状オレフィン系樹脂(a1)〜(a3)に官能基を有
する不飽和化合物をグラフ卜及び/又は共重合した重合
体(a4)からなる群から選ばれた少なくとも一種であ
る請求項1記載のガラス繊維強化環状オレフィン系樹脂
組成物。
2. The cyclic olefin resin (a) is a cyclic olefin addition (co) polymer or hydrogenated product (a) thereof.
l), an addition copolymer of a cyclic olefin and an α-olefin or a hydrogenated product thereof (a2), a ring-opened (co) polymer of a cyclic olefin or a hydrogenated product thereof (a3), and the above cyclic olefin resin (a1). ) To (a3) is at least one selected from the group consisting of polymers (a4) obtained by grafting and / or copolymerizing an unsaturated compound having a functional group, and the glass fiber reinforced cyclic olefin resin according to claim 1. Composition.
【請求項3】 バインダー用のオレフィン系樹脂(c)
が、α−オレフィン重合体、2種以上のα−オレフィン
の共重合体、環状オレフィン系樹脂、または、これらオ
レフィン系樹脂に官能基を有する不飽和化合物をグラフ
卜及び/又は共重合した変性オレフィン系樹脂である請
求項1記載のガラス繊維強化環状オレフィン系樹脂組成
物。
3. An olefin resin (c) for a binder
Is an α-olefin polymer, a copolymer of two or more kinds of α-olefins, a cyclic olefin resin, or a modified olefin obtained by grafting and / or copolymerizing an unsaturated compound having a functional group with these olefin resins. The glass fiber reinforced cyclic olefin resin composition according to claim 1, which is a resin.
【請求項4】 バインダー樹脂集束ガラス繊維(b)
が、ガラス繊維100重量部にオレフィン系樹脂0.1
〜5重量部を使用して集束させたものである請求項1記
載のガラス繊維強化環状オレフィン系樹脂組成物。
4. Binder resin-focused glass fiber (b)
However, 0.1 parts by weight of olefin resin is added to 100 parts by weight of glass fiber
The glass fiber reinforced cyclic olefin-based resin composition according to claim 1, wherein the glass fiber-reinforced cyclic olefin-based resin composition is focused by using about 5 parts by weight.
【請求項5】 環状オレフィン系樹脂(a)とバインダ
ー樹脂集束ガラス繊維(b)の重量組成比がa/b=9
5/5〜40/60(aとbの合計は100である。)
である請求項1記載のガラス繊維強化環状オレフィン系
樹脂組成物。
5. The weight composition ratio of the cyclic olefin resin (a) and the binder resin-focused glass fiber (b) is a / b = 9.
5 / 5-40 / 60 (the sum of a and b is 100)
The glass fiber reinforced cyclic olefin resin composition according to claim 1.
【請求項6】 請求項1〜5のいずれか1項に記載のガ
ラス繊維強化環状オレフィン系樹脂組成物を、射出成
形、圧縮成形、射出圧縮成形、押出成形又はブロー成形
してなるガラス繊維強化環状オレフィン系樹脂成形品。
6. A glass fiber reinforced obtained by injection molding, compression molding, injection compression molding, extrusion molding or blow molding of the glass fiber reinforced cyclic olefin resin composition according to any one of claims 1 to 5. Cyclic olefin resin molded product.
JP2001324001A 2001-10-22 2001-10-22 Glass fiber-reinforced cycloolefin-based resin composition and shaped article Pending JP2003128885A (en)