JP2003112979A - Composite product of ceramic and glass - Google Patents
Composite product of ceramic and glassInfo
- Publication number
- JP2003112979A JP2003112979A JP2001309334A JP2001309334A JP2003112979A JP 2003112979 A JP2003112979 A JP 2003112979A JP 2001309334 A JP2001309334 A JP 2001309334A JP 2001309334 A JP2001309334 A JP 2001309334A JP 2003112979 A JP2003112979 A JP 2003112979A
- Authority
- JP
- Japan
- Prior art keywords
- ceramics
- glass
- composite product
- ceramic
- pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は陶磁器部分とガラス
部分とが接合一体化した複合製品に関する。TECHNICAL FIELD The present invention relates to a composite product in which a ceramic portion and a glass portion are integrally joined.
【0002】[0002]
【従来技術】従来から、置物や表札などとして陶磁器か
らなるものが知られている。一方、装飾的なガラス製品
としてはステンドグラスが知られている。2. Description of the Related Art Conventionally, ceramics have been known as figurines and nameplates. On the other hand, stained glass is known as a decorative glass product.
【0003】[0003]
【発明が解決しようとする課題】上記したように、従来
から陶磁器製品およびガラス製品は数多く知られている
が、陶磁器とガラスとが一体化した製品は知られていな
い。本発明は陶磁器製品の間にガラス粉体を充填し、加
熱してガラス粉体を溶融することで陶磁器とガラスとが
接合できることに着目してなしたものである。As described above, many ceramic products and glass products have been conventionally known, but no product in which ceramics and glass are integrated is known. The present invention has been made by paying attention to the fact that a ceramic and a glass can be joined by filling glass powder between ceramic products and heating the glass powder to melt it.
【0004】[0004]
【課題を解決するための手段】本発明に係る陶磁器とガ
ラスとの複合製品は、複数の陶磁器からなる部分が離間
し、この離間した部分にガラス成分を充填して陶磁器か
らなる部分とガラスとを接合一体化した構成となってい
る。In a composite product of ceramics and glass according to the present invention, a plurality of portions made of ceramics are separated from each other, and the separated portions are filled with a glass component, and a portion made of ceramics and glass. It is configured to be joined and integrated.
【0005】具体的な形状としては枠状をなす外側陶磁
器の内側に、プレート状をなす内側陶磁器を配置し、こ
れら外側と内側の陶磁器の間をガラスで接合一体化した
ものなどが考えられる。なお、接合強度を十分なものと
するため、外側及び内側陶磁器の厚みは3mm以上にす
ることが好ましい。As a concrete shape, a plate-shaped inner pottery is disposed inside a frame-shaped outer pottery, and the outer pottery and the inner pottery are joined and integrated with glass. The thickness of the outer and inner porcelain is preferably 3 mm or more in order to ensure sufficient bonding strength.
【0006】前記ガラス成分を複数種類の色付ガラス成
分で構成したり、内側陶磁器を透光性を有する材料にて
構成したり、或いは内側陶磁器の表面に絵付けすること
で商品価値が高まる。特に、陶磁器の表面への絵付けを
ガラス粉体の溶融固化と同時に行うようにすれば効率的
である。The commercial value is increased by forming the glass component with a plurality of types of colored glass components, by forming the inner ceramics with a material having a light-transmitting property, or by painting on the surface of the inner ceramics. In particular, it is efficient if the surface of the ceramic is painted simultaneously with the melting and solidification of the glass powder.
【0007】[0007]
【発明の実施の形態】以下に本発明の実施の形態を添付
図面に基づいて説明する。図1は本発明に係る陶磁器と
ガラスとの複合製品の作成手順を示す図であり、先ず、
図1(a)に示すように、内側陶磁器1の写真画像など
の絵付けを行う。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below with reference to the accompanying drawings. FIG. 1 is a diagram showing a procedure for producing a composite product of ceramics and glass according to the present invention.
As shown in FIG. 1A, a photographic image or the like of the inner pottery 1 is painted.
【0008】絵付け方法としては、ガラス粉体用インク
リボンによりガラス粉体を水転写用シートに先に転写し
た後、この水転写用シートに顔料用インクリボンにより
顔料を転写することで反転した画像を作成し、次いで、
この水転写用シートを水につけ転写紙の台紙から画像を
分離し、更に分離した画像面が内側陶磁器1の表面と対
向するように貼り付ける。As a painting method, the glass powder ink ribbon was first transferred to the water transfer sheet, and then the pigment was transferred to the water transfer sheet by the pigment ink ribbon to invert. Create an image, then
The water transfer sheet is soaked in water to separate the image from the mount of the transfer paper, and the separated image surface is attached so as to face the surface of the inner pottery 1.
【0009】また、他の絵付け方法としては、ガラス粉
体用インクリボンによりガラス粉体を熱転写用シートに
先に転写した後、この熱転写用シートに顔料用インクリ
ボンにより顔料を転写することで反転した画像を作成
し、次いで、この熱転写用シートを画像面が内側陶磁器
1の表面に対向するように貼り付ける。As another painting method, the glass powder is first transferred to the thermal transfer sheet by the glass powder ink ribbon, and then the pigment is transferred to the thermal transfer sheet by the pigment ink ribbon. An inverted image is created, and then this thermal transfer sheet is attached so that the image surface faces the surface of the inner pottery 1.
【0010】以上の作業で陶磁器表面に絵付けを行った
後、図1(b)に示すように、棚板10の上に、剥離紙
11を敷き、この剥離紙11の上に内側陶磁器1と外側
陶磁器2を間に隙間ができるように配置する。ここで、
棚板10は焼成炉内で陶磁器を焼成する際の台となるも
のであり、剥離紙11は焼成の際にガラスが溶けて棚板
に付着するのを防止するためのものである。After painting the surface of the ceramics by the above-mentioned work, as shown in FIG. 1B, a release paper 11 is laid on the shelf board 10, and the inner ceramics 1 is placed on the release paper 11. And the outer ceramics 2 are arranged so that there is a gap therebetween. here,
The shelf plate 10 serves as a base for baking ceramics in a baking furnace, and the release paper 11 is for preventing glass from melting and adhering to the shelf plate during baking.
【0011】次いで、図1(c)に示すように、内側陶
磁器1と外側陶磁器2の間の隙間にガラス粉体(色ガラ
ス粉体:粒径2〜3mm)3を充填し、これを焼成炉内
で800〜900℃に加熱して前記ガラス粉体を溶融
し、冷却固化せしめる。このとき内側陶磁器1の表面に
絵付けされた画像も焼成される。そして、図1(d)に
示すような内側陶磁器1と外側陶磁器2の間をガラス層
3にて接合一体化した複合製品が得られる。Then, as shown in FIG. 1 (c), glass powder (colored glass powder: particle diameter 2 to 3 mm) 3 is filled in a gap between the inner pottery 1 and the outer pottery 2 and fired. The glass powder is melted by heating at 800 to 900 ° C. in a furnace and is cooled and solidified. At this time, the image painted on the surface of the inner pottery 1 is also fired. Then, a composite product in which the inside ceramics 1 and the outside ceramics 2 are joined and integrated by the glass layer 3 as shown in FIG. 1D is obtained.
【0012】図2は作成手順の別例を示す図であり、こ
の実施例にあっては、先ず、図2(a)に示すように、
棚板10の上に剥離紙11を敷き、この剥離紙11の上
に内側陶磁器1と外側陶磁器2を間に隙間ができるよう
に配置する。FIG. 2 is a diagram showing another example of the creating procedure. In this embodiment, first, as shown in FIG.
A release paper 11 is laid on the shelf board 10, and the inner pottery 1 and the outer pottery 2 are arranged on the release paper 11 so that a gap is formed therebetween.
【0013】次いで、図2(b)に示すように、内側陶
磁器1と外側陶磁器2の間の隙間にガラス粉体(色ガラ
ス粉体:粒径2〜3mm)3を充填し、これを焼成炉内
で800〜900℃に加熱して前記ガラス粉体を溶融
し、冷却固化せしめて図2(c)に示す中間体を得る。Next, as shown in FIG. 2 (b), a glass powder (colored glass powder: particle diameter 2 to 3 mm) 3 is filled in the gap between the inner pottery 1 and the outer pottery 2 and fired. The glass powder is melted by heating in a furnace at 800 to 900 ° C., and cooled and solidified to obtain an intermediate body shown in FIG. 2 (c).
【0014】この後、中間体の内側陶磁器1表面に前記
と同様にして絵付けを行い、再度焼成することで、図2
(d)に示す複合製品を得る。After that, the surface of the inner pottery 1 of the intermediate body is painted in the same manner as described above and fired again, so that FIG.
The composite product shown in (d) is obtained.
【0015】[0015]
【発明の効果】以上に説明したように本発明に係る陶磁
器とガラスとの複合製品は、ガラス層によって、離間し
た陶磁器同士を接合一体化したことで、陶磁器単独或い
はガラス単独では得られなかった複合的な効果が得られ
る。As described above, the composite product of ceramics and glass according to the present invention cannot be obtained by the ceramics alone or the glass alone because the ceramics separated by the glass layer are joined and integrated. Multiple effects can be obtained.
【図1】本発明に係る陶磁器とガラスとの複合製品の作
成手順を示す図FIG. 1 is a diagram showing a procedure for producing a composite product of ceramics and glass according to the present invention.
【図2】作成手順の別例を示す図FIG. 2 is a diagram showing another example of the creating procedure.
1…内側陶磁器、2…外側陶磁器、3…ガラス、10…
棚板、11…剥離紙。1 ... Inner porcelain, 2 ... Outer porcelain, 3 ... Glass, 10 ...
Shelf, 11 ... Release paper.
Claims (6)
の離間した部分にガラス成分を充填して陶磁器からなる
部分とガラスとを接合一体化したことを特徴とする陶磁
器とガラスとの複合製品。1. A composite product of ceramics and glass, characterized in that a plurality of portions made of ceramics are separated from each other, and the separated portions are filled with a glass component to integrally join the portions made of ceramics and glass. .
合製品において、前記複数の陶磁器は枠状をなす外側陶
磁器とプレート状をなす内側陶磁器からなることを特徴
とする陶磁器とガラスとの複合製品。2. The composite product of ceramics and glass according to claim 1, wherein the plurality of ceramics comprises a frame-shaped outer ceramics and a plate-shaped inner ceramics. Composite product.
とガラスとの複合製品において、前記ガラス成分は複数
種類の色付きガラス成分から構成されることを特徴とす
る陶磁器とガラスとの複合製品。3. The composite product of ceramics and glass according to claim 1 or 2, wherein the glass component is composed of a plurality of types of colored glass components. .
合製品において、前記内側の陶磁器表面にはガラス成分
を溶融する際に同時に写真等の画像が焼成によって絵付
けされていることを特徴とする陶磁器とガラスとの複合
製品。4. The composite product of ceramics and glass according to claim 2, wherein an image such as a photograph is painted on the inside surface of the ceramics by firing when melting the glass component. A composite product of ceramics and glass.
合製品において、前記内側の陶磁器が透光性を有する素
材からなることを特徴とする陶磁器とガラスとの複合製
品。5. The composite product of ceramics and glass according to claim 2, wherein the inner ceramics are made of a light-transmissive material.
合製品において、前記外側の陶磁器及び内側の陶磁器と
も3mm以上の厚みを有することを特徴とする陶磁器と
ガラスとの複合製品。6. The composite product of ceramics and glass according to claim 2, wherein both the outer ceramics and the inner ceramics have a thickness of 3 mm or more.