JP2003110252A - Housing, cover and case - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a housing material of housing, cover or case exhibiting excellent transparency, impact resistance, chemical resistance, weatherability and the balance thereof. SOLUTION: The housing, cover or case comprises a thermoplastic resin composition including alicyclic group polyester. Preferably, the housing, cover or case is a plastic component of an automobile, and the alicyclic group polyester is polycyclohexane dimethanolcyclohexane dicarboxylate (hereinafter, referred to PCCD).

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の技術分野】本発明は脂環族ポリエステルを含む
樹脂組成物からなるハウジング、カバーあるいはケース
に関する。TECHNICAL FIELD The present invention relates to a housing, a cover or a case made of a resin composition containing an alicyclic polyester.

【０００２】[0002]

【発明の技術的背景】テレビ、プリンターなどの家電・
ＯＡ機器のハウジング材および部品、トランス、コイル
などの部品、建築用材料などの成形品には、透明性、難
燃性、耐候性、耐衝撃性、耐薬品性などに優れているこ
とが望まれており、またこのような成形品は薄肉化も望
まれている。TECHNICAL BACKGROUND OF THE INVENTION Home appliances such as televisions and printers
Housings and parts for office automation equipment, parts such as transformers and coils, and molded products such as building materials should have excellent transparency, flame retardancy, weather resistance, impact resistance, and chemical resistance. In addition, such molded products are also desired to be thin.

【０００３】このような成形品には、従来ポリカーボネ
ート、ポリブチレンテレフタレート（ＰＢＴ）、アクリ
ロニトリル・ブタジエン・スチレン(ABS)樹脂などを主
成分とする樹脂組成物が使用されている。しかしなが
ら、これらの従来より使用されていた樹脂組成物では、
必ずしも前記特性のバランスが優れているものを得るこ
とはできなったたとえば、ＰＢＴの成形品では耐薬品性
に優れるものの衝撃強度が低く、製品肉厚を増やさねば
ならないという問題点がある。また、このようなＰＢＴ
では設計寸法精度が低く、製品の薄肉化を充分に行うこ
とができないという問題点があった。またABS樹脂で
は、耐候性が充分ではなく、このため、表面塗工が必要
であるなど問題点が多い。For such molded articles, resin compositions containing polycarbonate, polybutylene terephthalate (PBT), acrylonitrile butadiene styrene (ABS) resin, etc. as main components have been used. However, in these conventionally used resin compositions,
It has not always been possible to obtain a product having a good balance of the above-mentioned properties. For example, a molded article of PBT has a problem that it has a low chemical resistance but a low impact strength, and the product thickness must be increased. In addition, such PBT
However, there is a problem in that the design dimensional accuracy is low and the product cannot be made sufficiently thin. In addition, ABS resin does not have sufficient weather resistance, so that there are many problems such as surface coating is required.

【０００４】そこで、本発明者らはこのような従来技術
に伴う問題点を解決すべく鋭意検討した結果、脂環族ポ
リエステル樹脂を含む組成物を使用して、ハウジング、
カバーあるいはケースなどのハウジング材を成形する
と、透明性、耐衝撃性、耐薬品性、耐候性などのバラン
スに優れた成形品が得られることを見出し、本発明を完
成するに至った。Then, the present inventors have conducted extensive studies to solve the problems associated with the prior art, and as a result, a composition containing an alicyclic polyester resin was used to
It has been found that when a housing material such as a cover or a case is molded, a molded product having an excellent balance of transparency, impact resistance, chemical resistance, weather resistance and the like can be obtained, and the present invention has been completed.

【０００５】[0005]

【発明の目的】本発明は、透明性、耐衝撃性、耐薬品
性、耐候性に優れ、しかもこれらの特性のバランスなど
に優れたのバランスに優れたハウジング、カバーあるい
はケースなどのハウジング材を提供することを目的とし
ている。It is an object of the present invention to provide a housing material such as a housing, a cover or a case, which is excellent in transparency, impact resistance, chemical resistance and weather resistance, and also has a good balance of these characteristics. It is intended to be provided.

【０００６】[0006]

【発明の概要】本発明に係るハウジング、カバーあるい
はケースは、脂環族ポリエステルを含む熱可塑性樹脂組
成物からなる。前記ハウジング、カバーあるいはケース
が電子電気機器、家電機器またはOA機器のプラスチック
部品用として好適である。SUMMARY OF THE INVENTION The housing, cover or case according to the present invention comprises a thermoplastic resin composition containing an alicyclic polyester. The housing, cover or case is suitable for plastic parts of electronic and electrical equipment, home appliances and OA equipment.

【０００７】前記脂環族ポリエステルがポリシクロヘキ
サンジメタノールシクロヘキサンジカルボキシレート
(以後、PCCDと略す)であることが好ましい。また、前記
熱可塑性樹脂組成物は、脂環族ポリエステルとともにポ
リカーボネートを含んでいてもよい。熱可塑性樹脂組成
物中のポリカーボネート(以後、PCと略す)と脂環族ポリ
エステルとのブレンド物の総量を１００重量％としたと
きに、PC:脂環族ポリエステル重量比が5:95〜95:5の範
囲にあることが好ましい。The alicyclic polyester is polycyclohexanedimethanol cyclohexanedicarboxylate
(Hereinafter, abbreviated as PCCD) is preferable. Further, the thermoplastic resin composition may include a polycarbonate together with the alicyclic polyester. When the total amount of the blend of the polycarbonate (hereinafter abbreviated as PC) and the alicyclic polyester in the thermoplastic resin composition is 100% by weight, the weight ratio of PC: alicyclic polyester is 5:95 to 95: It is preferably in the range of 5.

【０００８】ポリカーボネートがビスフェノールＡ、ス
ピロビインダンビスフェノール、アリール基置換ビスフ
ェノール、脂環式ビスフェノールまたはこれらの混合物
から誘導される構成単位を含むことが好ましい。ブレン
ド物は、７０%以上の光線透過率を有することが好まし
く、また前記ブレンド物のガラス転移温度は５０〜150
℃の範囲にあることが好ましい。It is preferred that the polycarbonate comprises constituent units derived from bisphenol A, spirobiindane bisphenol, aryl group substituted bisphenols, alicyclic bisphenols or mixtures thereof. The blend preferably has a light transmittance of 70% or more, and the blend has a glass transition temperature of 50 to 150.
It is preferably in the range of ° C.

【０００９】前記樹脂組成物は、20重量%未満の量で耐
衝撃改良剤を含んでいてもよい。耐衝撃改良剤の屈折率
は1.51〜1.58の範囲にあることが好ましく、このような
耐衝撃改良剤としては、アクリロニトリル・ブタジエン
・スチレンが好適である。本発明に係るハウジング、カ
バーあるいはケースは、射出成形品、インジェクション
成形品、ブロー成形品、押出成形品、または真空・圧空
成形品が好適である。The resin composition may contain impact modifiers in an amount of less than 20% by weight. The refractive index of the impact resistance improver is preferably in the range of 1.51 to 1.58, and acrylonitrile butadiene styrene is preferable as such an impact resistance improver. The housing, cover or case according to the present invention is preferably an injection molded product, an injection molded product, a blow molded product, an extrusion molded product, or a vacuum / compressed air molded product.

【００１０】[0010]

【発明の具体的説明】以下、本発明に係るハウジング、
カバーあるいはケースについて具体的に説明する。 ［熱可塑性樹脂組成物］本発明では、熱可塑性樹脂組成
物としては、脂環族ポリエステルを含むものが使用され
る。 a)脂環族ポリエステル樹脂 脂環式ポリエステル樹脂としては、下記式(I)で表され
る繰返単位を有するポリエステルが挙げられる。DETAILED DESCRIPTION OF THE INVENTION Hereinafter, a housing according to the present invention,
The cover or case will be specifically described. [Thermoplastic Resin Composition] In the present invention, a thermoplastic resin composition containing an alicyclic polyester is used. a) Alicyclic polyester resin Examples of the alicyclic polyester resin include polyesters having a repeating unit represented by the following formula (I).

【００１１】[0011]

【化１】 [Chemical 1]

【００１２】式中Rはジオールから誘導される二価の残
基であり、R¹は二価酸（二価カルボン酸）から誘導され
る２価の残基であり、RまたはR¹の少なくとも1つはシク
ロアルキル環を含む基である。具体的には、Rは６〜２
０の炭素原子を有するジオールを含むアリール、アルカ
ンまたはシクロアルカン残基であり、RあるいはR¹の少
なくとも１方が脂環基である。特に、RおよびR¹の両方
が、脂環基であることが望ましい。In the formula, R is a divalent residue derived from diol, R ¹ is a divalent residue derived from divalent acid (divalent carboxylic acid), and at least R or R ¹ One is a group containing a cycloalkyl ring. Specifically, R is 6 to 2
An aryl, alkane or cycloalkane residue containing a diol having 0 carbon atoms, wherein at least one of R and R ¹ is an alicyclic group. In particular, it is desirable that both R and R ¹ are alicyclic groups.

【００１３】このようなRおよびR¹としては、下記で示
されるものが挙げられる。Examples of such R and R ¹ include those shown below.

【００１４】[0014]

【化２】 [Chemical 2]

【００１５】このような脂環族ポリエステルは、二価酸
とジオールとの縮合物であり、二価酸とジオールとが化
学当量で反応したものであっても、いずれかが過量に含
まれていてもよく、５０モル％以上の脂環族ジオールお
よび／または脂環族二価酸成分を含んでいれば、他の成
分は、線形（環状ではない）脂肪族二価酸および／また
は脂肪族ジオールからなる成分を含んでいてもよい。本
発明のように脂環族成分を含んでいると、ポリエステル
は高い剛性を有するともに、たとえばポリカーボネート
と混合したときに透明性が低下することもない。Such an alicyclic polyester is a condensate of a divalent acid and a diol, and even if the divalent acid and the diol are reacted in a chemical equivalent amount, one of them is contained in an excessive amount. May contain 50 mol% or more of the alicyclic diol and / or alicyclic divalent acid component, the other component is a linear (non-cyclic) aliphatic diacid and / or aliphatic It may contain a component consisting of a diol. When the alicyclic component is contained as in the present invention, the polyester has high rigidity and the transparency is not deteriorated when mixed with, for example, polycarbonate.

【００１６】脂環族ジオールとしては、ＨＯ-Ｒ-ＯＨ
（Ｒは前記(I)と同じ）で表され、たとえば、ジメタノ
ールデカリン、ジメタノールビシクロオクタン;1,4-シ
クロヘキサンジメタノール、特にそのcis-異性体および
trans異性体;2,2,4,4-テトラメチル-1,3-シクロブタン
ジオール(TMCBD)；トリエチレングリコール;1,10-デカ
ンジオール;またこれらの混合物が挙げられる。Examples of the alicyclic diol include HO-R-OH
(R is the same as the above (I)), and includes, for example, dimethanol decalin, dimethanol bicyclooctane; 1,4-cyclohexanedimethanol, especially its cis-isomer and
trans isomers; 2,2,4,4-tetramethyl-1,3-cyclobutanediol (TMCBD); triethylene glycol; 1,10-decanediol; and mixtures thereof.

【００１７】他のジオールとしては、直鎖、分岐のアル
カンジオールであり、2〜16の炭素原子を含んでいるも
のが望ましい。このようなジオールの具体例としては、
特に制限されるものではないが、エチレングリコール;
プロピレングリコール(1、2-および1、3-プロピレング
リコール);2,2-ジメチル-1,3-プロパンジオール;2-エチ
ル-2-メチル-1,3-プロパンジオール;1,3-および1,5-ペ
ンタンジオール;ジプロピレングリコール;2-メチル-1,5
-ペンタンジオール;1,6-ヘキサンジオールなどが挙げら
れる。The other diol is a straight-chain or branched alkane diol, and preferably contains 2 to 16 carbon atoms. Specific examples of such diols include:
Although not particularly limited, ethylene glycol;
Propylene glycol (1,2- and 1,3-propylene glycol); 2,2-dimethyl-1,3-propanediol; 2-ethyl-2-methyl-1,3-propanediol; 1,3- and 1 , 5-Pentanediol; Dipropylene glycol; 2-Methyl-1,5
-Pentanediol; 1,6-hexanediol and the like.

【００１８】これらのジオール類はアルキルエステル、
ジアリールエステルなどの誘導体であってもよい。脂環
族二価酸は、飽和炭素に結合した2つのカルボキシル基
を含むカルボン酸であり、好ましい二価酸としては、環
状または二環状脂肪族酸；たとえばデカヒドロナフタレ
ンジカルボン酸、ノルボルネンジカルボン酸、ビシクロ
オクタンジカルボン酸、1,4-シクロヘキサンジカルボン
酸またはこれらの誘導体が挙げられ、最も好ましくは、
1,4-シクロヘキサンジカルボン酸あるいはその誘導体で
ある。These diols are alkyl esters,
It may be a derivative such as a diaryl ester. The alicyclic divalent acid is a carboxylic acid containing two carboxyl groups bonded to saturated carbon, and preferable divalent acids include cyclic or bicyclic aliphatic acids; for example, decahydronaphthalene dicarboxylic acid, norbornene dicarboxylic acid, Bicyclooctanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid or derivatives thereof, most preferably,
1,4-cyclohexanedicarboxylic acid or its derivative.

【００１９】またアジピン酸、アゼライン酸、ドデカン
ジカルボン酸およびコハク酸のような直鎖ジカルボン酸
も使用してもよい。二価酸としては、アルキルエステル
(たとえばジアルキルエステル、ジアリールエステル)、
無水物、塩類、酸クロライド、酸ブロマイドなどの誘導
体が含まれていてもよい。Linear dicarboxylic acids such as adipic acid, azelaic acid, dodecanedicarboxylic acid and succinic acid may also be used. Alkyl ester as diacid
(For example, dialkyl ester, diaryl ester),
Derivatives such as anhydrides, salts, acid chlorides and acid bromides may be contained.

【００２０】このうち脂環族二価酸のジアルキルエステ
ルが好ましく、このうち最も好ましいのは、ジメチル-
1,4-シクロヘキサン-ジカルボキシレートである。好ま
しい脂環基R¹は、1,4-シクロヘキシル二価酸から誘導さ
れ、最も好ましくは、その７０モル％以上がトランス異
性体形状のものである。好ましい脂環基Rは、1,4-シク
ロヘキシルジメタノールなどの1,4-シクロヘキシル第１
ジオールから誘導され、最も好ましくは、その70モル％
以上がtrans異性体形状のものである。Of these, dialkyl esters of alicyclic diacids are preferred, of which the most preferred is dimethyl-
It is 1,4-cyclohexane-dicarboxylate. Preferred alicyclic groups R ¹ are derived from 1,4-cyclohexyl diacid, most preferably at least 70 mol% of which is in the trans isomer form. Preferred alicyclic groups R are 1,4-cyclohexyl primary such as 1,4-cyclohexyldimethanol
Derived from a diol, most preferably 70 mol% thereof
The above is the trans isomer form.

【００２１】本発明では、脂環族ポリエステル樹脂とし
て、下記式(II)で表されるポリ（シクロヘキサン-1,4-
ジメタノールシクロヘキサン-1,4-ジカルボキシレー
ト）［ポリ(1,4-シクロヘキサン-ジメタノール-1,4-ジ
カルボキシレート)、PCCDともいう］が好適である。In the present invention, as the alicyclic polyester resin, poly (cyclohexane-1,4-) represented by the following formula (II) is used.
Dimethanol cyclohexane-1,4-dicarboxylate) [poly (1,4-cyclohexane-dimethanol-1,4-dicarboxylate), also called PCCD] is preferable.

【００２２】[0022]

【化３】 [Chemical 3]

【００２３】上記式(II)で表される脂環族ポリエステル
樹脂は、上記した式(I)中、Ｒが1,4-シクロヘキサンジ
メタノールから誘導される基であり、R¹がシクロヘキサ
ンジカルボキシレートから誘導されるシクロヘキサン環
である。このようなポリエステル樹脂は、上記成分を用
いて、重縮合反応またはエステル交換反応によって製造
することができる。In the alicyclic polyester resin represented by the above formula (II), R in the above formula (I) is a group derived from 1,4-cyclohexanedimethanol, and R ¹ is cyclohexanedicarboxyl. It is a cyclohexane ring derived from rate. Such a polyester resin can be produced by a polycondensation reaction or a transesterification reaction using the above components.

【００２４】ポリエステルの重合反応は、一般に、テト
エラキス(2-エチルヘキシル)チタネートなどのチタン系
触媒の存在下、溶融状態で行われる。このようなチタン
系触媒量は、最終製造樹脂に対し、チタン原子換算で５
０〜２００ppmの量で含まれていることが好ましい。本
発明で使用される脂環族ポリエステル樹脂は、50℃以
上、好ましくは８０℃以上、さらに好ましくは１００℃
以上のガラス転移温度(Tg)を有していることが望まし
い。The polymerization reaction of polyester is generally carried out in the molten state in the presence of a titanium-based catalyst such as tetellokis (2-ethylhexyl) titanate. Such a titanium-based catalyst amount is 5 in terms of titanium atom based on the final resin.
It is preferably contained in an amount of 0 to 200 ppm. The alicyclic polyester resin used in the present invention has a temperature of 50 ° C or higher, preferably 80 ° C or higher, more preferably 100 ° C.
It is desirable to have the above glass transition temperature (Tg).

【００２５】また、上記のポリエステルは、約1〜50重
量％の量の重合性脂肪族酸および/または脂肪族ポリオ
ールに由来した構成単位を有して、コポリエステルが形
成されていてもよい。なお脂肪族ポリオールとしては、
ポリエチレングリコール、ポリブチレングリコールなど
が例示される。このようなポリエステルの製造方法は、
たとえば米国特許2,465,319号明細書、同3,047,539号明
細書に記載されている。Further, the above polyester may have a constitutional unit derived from a polymerizable aliphatic acid and / or an aliphatic polyol in an amount of about 1 to 50% by weight to form a copolyester. As the aliphatic polyol,
Examples thereof include polyethylene glycol and polybutylene glycol. The method for producing such a polyester is
For example, it is described in US Pat. Nos. 2,465,319 and 3,047,539.

【００２６】本発明では、前記脂環族ポリエステル樹脂
とともにポリカーボネートを含んでいる。 b)ポリカーボネート系樹脂 本発明において使用されるポリカーボネート系樹脂(Ａ)
は、芳香族ジヒドロキシ化合物とカーボネート前駆体と
を反応させて得られる芳香族ホモポリカーボネートまた
は芳香族コポリカーボネートである。In the present invention, polycarbonate is contained together with the alicyclic polyester resin. b) Polycarbonate resin Polycarbonate resin (A) used in the present invention
Is an aromatic homopolycarbonate or aromatic copolycarbonate obtained by reacting an aromatic dihydroxy compound with a carbonate precursor.

【００２７】ポリカーボネート系樹脂は一般に、下記式
（１）で示される繰り返し構造単位を有するものであ
る。Polycarbonate resins generally have a repeating structural unit represented by the following formula (1).

【００２８】[0028]

【化４】 [Chemical 4]

【００２９】（上記式中、Ａは芳香族ジヒドロキシ化合
物から誘導される２価の残基である） 芳香族ジヒドロキシ化合物としては、官能基であるヒド
ロキシ基を２個含有し、各ヒドロキシ基が芳香核の炭素
原子に直接接合した単核または多核の芳香族化合物が挙
げられ、たとえば下記式（２）で表される。(In the above formula, A is a divalent residue derived from an aromatic dihydroxy compound) The aromatic dihydroxy compound contains two hydroxyl groups which are functional groups, and each hydroxy group is aromatic. Examples thereof include mononuclear or polynuclear aromatic compounds directly bonded to the carbon atom of the nucleus, which are represented by the following formula (2).

【００３０】[0030]

【化５】 [Chemical 5]

【００３１】式中、Aは、1〜15の炭素原子からなる二価
炭化水素基、または1〜15の炭素原子に含む置換二価炭
化水素基である。Xは、１以上の場合、互いに同一であ
っても、異なっていてもよく、水素、ハロゲンおよび１
〜８の炭素原子を有するアルキル基、6〜18の炭素原子
を有するアリール基、7〜14の炭素原子を有するアリー
ルアルキル基、１〜８の炭素原子を含むアルコキシ基な
どの1価炭化水素基から選択される。In the formula, A is a divalent hydrocarbon group consisting of 1 to 15 carbon atoms or a substituted divalent hydrocarbon group containing 1 to 15 carbon atoms. When X is 1 or more, they may be the same or different from each other, and are hydrogen, halogen and 1
A monovalent hydrocarbon group such as an alkyl group having 8 to 8 carbon atoms, an aryl group having 6 to 18 carbon atoms, an arylalkyl group having 7 to 14 carbon atoms, and an alkoxy group having 1 to 8 carbon atoms Selected from.

【００３２】ｍは0または1であり、nは、０〜５の整数
である。組成物の調製 本発明に係る組成物は、上記した脂環族ポリエステル樹
脂とポリカーボネート系樹脂とを混合する。混合方法と
しては特に制限されるものではないが、通常、常圧、減
圧あるいは加圧下での溶融混練が採用される。M is 0 or 1, and n is an integer of 0-5. Preparation of Composition The composition according to the present invention is a mixture of the alicyclic polyester resin and the polycarbonate resin described above. The mixing method is not particularly limited, but usually melt kneading under normal pressure, reduced pressure or pressure is adopted.

【００３３】混合装置としては特に押出機、バンバリー
ミキサー、ローラー、ニーダーなどを例として挙げるこ
とができ、これらを回分的または連続的に運転する。こ
のとき、成分の混合順は特に限定されない。脂環族ポリ
エステル樹脂とポリカーボネートとの重量比（ポリエス
テル：ポリカーボネート）は、5:95〜95:5の範囲、好ま
しくは50:50〜30:70の範囲にあることが望ましい。70重
量％未満のポリエステル量は、ポリカーボネート単独の
ものと比較して、結果として特性を向上させるという点
で、より低熱たわみ温度になるので望ましい。脂環式ポ
リエステルを加えることで、ポリカーボネート単独から
なる場合に比べて、高耐薬品性、高耐紫外線特性（耐候
性）を付与することができる。As the mixing device, an extruder, a Banbury mixer, a roller, a kneader and the like can be mentioned by way of example, and these are operated batchwise or continuously. At this time, the order of mixing the components is not particularly limited. The weight ratio of the alicyclic polyester resin to the polycarbonate (polyester: polycarbonate) is preferably in the range of 5:95 to 95: 5, more preferably 50:50 to 30:70. A polyester content of less than 70% by weight is desirable as it results in a lower heat deflection temperature in terms of improved properties as compared to polycarbonate alone. By adding the alicyclic polyester, high chemical resistance and high ultraviolet resistance (weather resistance) can be imparted, as compared with the case of using polycarbonate alone.

【００３４】上記した組成物は、７０%以上、好ましく
は８０％以上の光線透過率を有することが好ましい。こ
のような光線透過率であれば、透明性に優れたハウジン
グ、カバーあるいはケースを作製することができる。ま
た上記組成物は、５０〜１５０℃の範囲のガラス転移温
度を有していることが望ましい。通常ポリカーボネート
はガラス転移温度が高いが、ガラス転移温度が低い脂環
族ポリエステルを含んでいるので、ガラス転移温度が低
くなり、このためこのため組成物自体が流動性に優れる
ようになり薄肉の成形品を成形することが可能となる。The above composition preferably has a light transmittance of 70% or more, preferably 80% or more. With such a light transmittance, a housing, cover or case having excellent transparency can be manufactured. Further, it is desirable that the composition has a glass transition temperature in the range of 50 to 150 ° C. Normally, polycarbonate has a high glass transition temperature, but since it contains an alicyclic polyester having a low glass transition temperature, it has a low glass transition temperature, which makes the composition itself excellent in fluidity and molding a thin wall. It becomes possible to mold the product.

【００３５】また、このような組成物は、従来の熱可塑
性樹脂に比べて非常に耐候性に優れた脂環族ポリエステ
ルを含んでいるので、得られた成形品は紫外線領域での
光の吸収が少なく紫外線を吸収して変色することがな
い。特に、従来より使用されていたポリカーボネート、
ポリエステル、ポリスチレンなどの熱可塑性樹脂に比べ
て、優れた耐候性を有している。このような本発明で使
用される樹脂組成物の紫外線吸収特性を図１に示す。Further, since such a composition contains an alicyclic polyester which is much more excellent in weather resistance than conventional thermoplastic resins, the obtained molded article absorbs light in the ultraviolet region. It does not discolor by absorbing UV rays. In particular, the polycarbonate that has been used conventionally,
It has superior weather resistance compared to thermoplastic resins such as polyester and polystyrene. The ultraviolet absorption characteristics of such a resin composition used in the present invention are shown in FIG.

【００３６】なお、紫外線吸収特性は、所定の成形品か
ら作成した試験片、もしくは有機溶剤に溶解させた試料
を用いて分光光度計により、紫外部領域の吸収を測定す
ることで評価される。有機溶剤として、クロロホルム、
塩化メチレン等が使用される。（なお図１では有機溶媒
として、クロロホルムを使用し、また、脂環族ポリエス
テル組成物として、脂環族ポリエステル：２０重量部、
ポリカーボネート：８０重量部とを、溶融混練して得ら
れた組成物、すなわち実施例で使用される組成物を使用
した。） このような樹脂組成物には、安定剤が含まれていること
が好ましい。このような安定剤は、樹脂成分（特にポリ
カーボネート樹脂）に含まれる触媒を失活させるための
ものであり、たとえば米国特許5,441,997号明細書に詳
細に記載されている。The ultraviolet absorption characteristic is evaluated by measuring the absorption in the ultraviolet region with a spectrophotometer using a test piece prepared from a predetermined molded product or a sample dissolved in an organic solvent. As an organic solvent, chloroform,
Methylene chloride or the like is used. (Note that in FIG. 1, chloroform was used as the organic solvent, and the alicyclic polyester composition was alicyclic polyester: 20 parts by weight,
A composition obtained by melt-kneading polycarbonate: 80 parts by weight, that is, the composition used in the examples was used. ) It is preferable that such a resin composition contains a stabilizer. Such stabilizers are for deactivating the catalyst contained in the resin component (particularly polycarbonate resin), and are described in detail in, for example, US Pat. No. 5,441,997.

【００３７】このような安定剤は、樹脂成分に対して、
0.001〜10重量％、好ましくは0.005〜2重量％の量で含
まれていることが望ましい。耐衝撃改良剤としては、共
役ジエンまたはアクリルエラストマーのアクリル酸また
はメタクリル酸変性物、またはその芳香族ビニル共重合
物が挙げられる。一般に、これらの耐衝撃改良剤は、ブ
タジエンまたはイソプレン、ブチルアクリレート、また
は必要に応じて芳香族ビニル化合物から誘導される構成
単位を含んでいる。具体的な耐衝撃改良剤としては、エ
チレン・酢酸ビニル、エチレン・エチルアクリレート共
重合体、SEBS(スチレン・エチレン・ブチレン・スチレ
ン)、およびSBS(スチレン・ブタジエン・スチレン)ブロ
ック共重合体、EPDM(エチレン・プロピレン・ジエン・
モノマー)、EPR(エチレン・プロピレン・ゴム)共重合体
などが挙げられるが、これらに制限されるものではな
い。Such a stabilizer is used for the resin component.
It is desirable that it is contained in an amount of 0.001 to 10% by weight, preferably 0.005 to 2% by weight. Examples of impact modifiers include acrylic acid or methacrylic acid modified products of conjugated dienes or acrylic elastomers, or aromatic vinyl copolymers thereof. Generally, these impact modifiers contain building blocks derived from butadiene or isoprene, butyl acrylate, or optionally vinyl aromatic compounds. Specific impact modifiers include ethylene / vinyl acetate, ethylene / ethyl acrylate copolymer, SEBS (styrene / ethylene / butylene / styrene), and SBS (styrene / butadiene / styrene) block copolymer, EPDM ( Ethylene / propylene / diene /
Examples thereof include monomers) and EPR (ethylene / propylene / rubber) copolymers, but are not limited thereto.

【００３８】本発明で使用される耐衝撃改良剤の屈折率
は、1.51〜1.58、好ましくは1.53〜1.56の範囲にあるこ
とが望ましい。このような特定の屈折率を有する耐衝撃
改良剤としては、ABS（アクリロニトリル・ブタジエン
・スチレン）樹脂、MBS（ブタジエン・スチレン・メチ
ルメタクリレート）樹脂、PVC（塩化ビニル）樹脂など
が挙げられ、このうち、ABSが好ましい。The impact modifier used in the present invention preferably has a refractive index in the range of 1.51 to 1.58, preferably 1.53 to 1.56. Examples of impact modifiers having such a specific refractive index include ABS (acrylonitrile-butadiene-styrene) resin, MBS (butadiene-styrene-methylmethacrylate) resin, PVC (vinyl chloride) resin and the like. , ABS are preferred.

【００３９】また組成物には、離型剤、酸化防止剤、安
定剤、紫外線吸収剤、などが含まれていてもよい。離型
剤としてはメチルフェニルシリコーンオイルなどのシリ
コーン系離型剤、ペンタエリスリトールテトラステアレ
ートやグリセリンモノステアレート、モンタン酸ワック
スなど多価アルコールのカルボン酸エステル、ポリα-
オレフィンもしくはその誘導体などのオレフィン系離型
剤などが挙げられる。Further, the composition may contain a releasing agent, an antioxidant, a stabilizer, an ultraviolet absorber and the like. Examples of the release agent include silicone-based release agents such as methylphenyl silicone oil, pentaerythritol tetrastearate and glycerin monostearate, carboxylic acid esters of polyhydric alcohols such as montanic acid wax, and poly α-
Examples thereof include olefin-based mold release agents such as olefins and their derivatives.

【００４０】安定剤としては、少なくとも１個の水素又
はアルキル基をもつ酸性ホスファイト、アルキルホスフ
ァイト、アリールホスファイト又は混合ホスファイト、
第ＩＢ族又は第IIＢ族金属のリン酸塩、リンのオキソ
酸、酸性ピロリン酸金属塩又はそれらの混合物が挙げら
れる。酸化防止剤としては、3-(3,5-ジtert-ブチル4-ヒ
ドロキシフェニル)プロピオン酸または3-(3-tert-ブチ
ル4-ヒドロキシ-5-メチルフェニル)プロピオン酸と1価
ないし4価のアルコールのエステル化合物などが挙げら
れる。フェノール系抗酸化剤の具体例としては、たとえ
ば、ステアリル-3-(3,5-ジtert-ブチル4-ヒドロキシフ
ェニル)プロピオネート、チオジエチレングリコールビ
ス〔3-(3,5-ジtert-ブチル4-ヒドロキシフェニル)プロ
ピオネート〕、1,6-ヘキサメチレンビス〔3-(3,5-ジter
t-ブチル4-ヒドロキシフェニル)プロピオネート〕、1,
3,5-トリス〔3-(3,5-ジtert-ブチル4-ヒドロキシフェニ
ル)プロピオニルオキシエチル〕イソシアヌレート、テ
トラキス〔メチレン-3-(3,5-ジtert-ブチル4-ヒドロキ
シフェニル)プロピオネート〕メタン、3,9-ビス〔1,1-
ジメチル-2-｛3-(3-tert-ブチル4-ヒドロキシ-5-メチル
フェニル)プロピオニルオキシ｝エチル〕-2,4,8,10-テ
トラオキサスピロ〔5. 5〕ウンデカン、トリエチレング
リコールビス〔3-(3-tert-ブチル4-ヒドロキシ-5-メチ
ルフェニル)プロピオネート〕などが好適に用いられ
る。As stabilizers, acidic phosphites, alkyl phosphites, aryl phosphites or mixed phosphites having at least one hydrogen or alkyl group,
Mention may be made of Group IB or Group IIB metal phosphates, phosphorus oxoacids, acidic pyrophosphate metal salts or mixtures thereof. As the antioxidant, 3- (3,5-ditert-butyl 4-hydroxyphenyl) propionic acid or 3- (3-tert-butyl 4-hydroxy-5-methylphenyl) propionic acid and monovalent or tetravalent Examples thereof include ester compounds of alcohols. Specific examples of the phenolic antioxidant include, for example, stearyl-3- (3,5-ditert-butyl 4-hydroxyphenyl) propionate, thiodiethylene glycol bis [3- (3,5-ditert-butyl 4- Hydroxyphenyl) propionate], 1,6-hexamethylenebis [3- (3,5-diter
t-butyl 4-hydroxyphenyl) propionate], 1,
3,5-Tris [3- (3,5-ditert-butyl 4-hydroxyphenyl) propionyloxyethyl] isocyanurate, tetrakis [methylene-3- (3,5-ditert-butyl 4-hydroxyphenyl) propionate ] Methane, 3,9-bis [1,1-
Dimethyl-2- {3- (3-tert-butyl 4-hydroxy-5-methylphenyl) propionyloxy} ethyl] -2,4,8,10-tetraoxaspiro [5.5] undecane, triethylene glycol bis [3- (3-tert-butyl 4-hydroxy-5-methylphenyl) propionate] and the like are preferably used.

【００４１】紫外線吸収剤としては、ベンゾトリアゾー
ル系紫外線吸収剤ベンゾフェノン系紫外線吸収剤、サリ
チレート系紫外線吸収剤などが用いられるが、特に2-(5
-メチル-2-ヒドロキシフェニル)ベンゾトリアゾール、2
-(3,5-ジ-tert-ブチル-2-ヒドロキシフェニル)ベンゾト
リアゾール、2-(3-tert-ブチル-5-メチル-2-ヒドロキシ
フェニル)-5-クロロベンゾトリアゾール、2-(3,5-ジ-te
rt-ブチル-2-ヒドロキシフェニル)-5-クロロベンゾトリ
アゾール、2-(2’-ヒドロキシ-5-オクチルフェニル)ベ
ンゾトリアゾールなどのベンゾトリアゾール系紫外線吸
収剤が好適に用いられる。As the ultraviolet absorber, a benzotriazole type ultraviolet absorber, a benzophenone type ultraviolet absorber, a salicylate type ultraviolet absorber, etc. are used, but especially 2- (5
-Methyl-2-hydroxyphenyl) benzotriazole, 2
-(3,5-di-tert-butyl-2-hydroxyphenyl) benzotriazole, 2- (3-tert-butyl-5-methyl-2-hydroxyphenyl) -5-chlorobenzotriazole, 2- (3, 5-di-te
Benzotriazole-based UV absorbers such as rt-butyl-2-hydroxyphenyl) -5-chlorobenzotriazole and 2- (2'-hydroxy-5-octylphenyl) benzotriazole are preferably used.

【００４２】エポキシ系安定剤も用いることができる。
さらに、無機及び有機燐系もしくはチォエステル系の安
定剤、チオール系、金属塩系などの安定剤を用いること
もできる。樹脂組成物には、その物性を損なわない限
り、目的に応じて樹脂組成物の混合時または成形時に、
公知の添加剤、たとえば着色剤（カーボンブラック、酸
化チタンなどの顔料、染料）、充填剤、補強剤（ガラス
繊維、炭素繊維、タルク、クレー、マイカ、ガラスフレ
ーク、ミルドガラス、ガラスビーズなど）、滑剤、可塑
剤、難燃剤、流動性改良剤などが、添加されていてもよ
い。Epoxy stabilizers can also be used.
Furthermore, inorganic and organic phosphorus-based or thioester-based stabilizers, thiol-based stabilizers, and metal salt-based stabilizers can also be used. The resin composition, as long as it does not impair the physical properties, at the time of mixing or molding the resin composition depending on the purpose,
Known additives, for example, colorants (carbon black, pigments such as titanium oxide, dyes), fillers, reinforcing agents (glass fiber, carbon fiber, talc, clay, mica, glass flakes, milled glass, glass beads, etc.), Lubricants, plasticizers, flame retardants, fluidity improvers and the like may be added.

【００４３】これらの添加剤の添加量は、ポリエステル
成分、ポリカーボネート成分などの使用量に応じて適宜
選択される。 ［ハウジング、カバーあるいはケース］本発明に係るハ
ウジング、カバーあるいはケースは、上記した熱可塑性
樹脂組成物からなる。The amount of these additives added is appropriately selected according to the amounts of the polyester component, the polycarbonate component and the like used. [Housing, Cover or Case] The housing, cover or case according to the present invention comprises the above-mentioned thermoplastic resin composition.

【００４４】前記した樹脂組成物から形成された成形品
は、耐衝撃性と耐薬品性とのバランスに優れている。ま
た、耐候性にも優れているので、表面に必ずしも耐候性
塗膜を形成する必要がなく、このため意匠性（加工性）
に優れている。さらに、前記した樹脂組成物は、流動性
が高く成形性に優れているので薄肉の成形品を作製する
ことが可能である このような本発明に係るハウジング、カバーあるいはケ
ースが電子電気機器、家電機器またはOA機器のプラスチ
ック部品用に好適である。より具体的には、テレビハウ
ジング、テレビシャーシー、デフレションヨーク、他の
テレビ部品、ＡＣアダプター、電源ボックス、エアコン
部品、オーティオ部品、照明カバー、モニターハウジン
グ、モニターシャーシー、ノート型ＰＣハウジング、ノ
ート型ＰＣバッテリー、アンテナカバー、プリンターハ
ウジング、プリンターシャーシー、トナーカートリッ
ジ、インクタンク、給紙用トレイ、スキャナーハウジン
グ、スキャナーフレーム、携帯電話ハウジング、携帯電
話バッテリー等の用途に好適である。A molded article formed from the above resin composition has an excellent balance between impact resistance and chemical resistance. Also, since it has excellent weather resistance, it is not always necessary to form a weather resistant coating film on the surface, and therefore designability (workability)
Is excellent. Furthermore, since the above-mentioned resin composition has high fluidity and excellent moldability, it is possible to produce a thin-walled molded article. Such a housing, cover or case according to the present invention can be used for electronic and electrical equipment and home appliances. Suitable for plastic parts of equipment or OA equipment. More specifically, TV housings, TV chassis, deflection yokes, other TV parts, AC adapters, power supply boxes, air conditioner parts, audio parts, lighting covers, monitor housings, monitor chassis, notebook PC housings, notebooks. It is suitable for applications such as type PC batteries, antenna covers, printer housings, printer chassis, toner cartridges, ink tanks, paper feed trays, scanner housings, scanner frames, mobile phone housings and mobile phone batteries.

【００４５】本発明に係るハウジング、カバーあるいは
ケースが、射出成形品、インジェクション成形品、ブロ
ー成形品、押出成形品、または真空・圧空成形品である
ことが好ましい。The housing, cover or case according to the present invention is preferably an injection molded product, an injection molded product, a blow molded product, an extrusion molded product, or a vacuum / compressed air molded product.

【００４６】[0046]

【発明の効果】本発明によれば、特定の樹脂組成物から
成形品を形成しているので、従来製造できなかった耐衝
撃性もあり耐薬品性もありそして耐候性もあるハウジン
グ、カバーあるいはケースを得ることができる。また、
耐候性にも優れているので、従来品のように表面塗装を
必ずしも行う必要がない。また、本発明で使用される樹
脂組成物は成形性（高流動）にも優れているため、薄肉
化も可能であり、また、それによって生産性も向上させ
ることができる。EFFECTS OF THE INVENTION According to the present invention, since a molded product is formed from a specific resin composition, a housing, a cover, or a weather-resistant housing, a cover or You can get the case. Also,
Since it also has excellent weather resistance, it is not necessary to apply surface coating unlike conventional products. Moreover, since the resin composition used in the present invention is also excellent in moldability (high flowability), it is possible to reduce the wall thickness, and thereby improve the productivity.

【００４７】さらに成形品自体の透明性が高いため、意
匠性に幅が広がり製品に付加価値を付けられるという優
れた特性を有する。Further, since the molded product itself has high transparency, it has an excellent property that the product can be broadened in design and added value can be added to the product.

【００４８】[0048]

【実施例】以下、本発明を実施例により、より詳細に説
明するが、本発明はこれらの実施例に何ら限定されるも
のではない。なお、実施例、比較例では、以下の樹脂材
料を使用した。脂環族ポリエステル 脂環族ポリエステルとしては、ポリシクロヘキサンジメ
タノールシクロヘキサンジカルボキシレートを使用し
た。EXAMPLES The present invention will now be described in more detail with reference to examples, but the present invention is not limited to these examples. The following resin materials were used in Examples and Comparative Examples. Alicyclic Polyester As the alicyclic polyester, polycyclohexanedimethanol cyclohexanedicarboxylate was used.

【００４９】ポリカーボネート ポリカーボネートとして、日本ジーイープラスチックス
（株）製、レキサン123およびレキサンSP1010、ＨＦＰ
Ｃを使用した。脂環族ポリエステル組成物 脂環族ポリエステル組成物として、前記脂環族ポリエス
テル：２０重量部、前記ポリカーボネート（レキサン12
3）：８０重量部とを、溶融混練して得られた組成物を
使用した。 Polycarbonate Polycarbonate as a product of Nippon GE Plastics Co., Ltd., Lexan 123 and Lexan SP1010, HFP
C was used. Alicyclic polyester composition As the alicyclic polyester composition, the alicyclic polyester: 20 parts by weight, the polycarbonate (Lexane 12
3): 80 parts by weight of the composition obtained by melt-kneading.

【００５０】ＡＢＳ樹脂 ABS樹脂として、旭化成工業（株）製、スタイラック321
を使用した。ＰＣ／ＡＢＳ樹脂 ＰＣ／ＡＢＳ樹脂として、日本ジーイープラスチックス
（株）製、サイコロイ1200を使用した。 ABS resin As ABS resin, Stylak 321 manufactured by Asahi Kasei Kogyo Co., Ltd.
It was used. PC / ABS resin As the PC / ABS resin, Psycholoy 1200 manufactured by Nippon GE Plastics Co., Ltd. was used.

【００５１】[0051]

【実施例１、比較例１および２】上記各樹脂のうち、脂
環族ポリエステル組成物（実施例１）、ABS樹脂（比較
例１）、ポリカーボネート樹脂（比較例２）を用いて、
以下試験用の所定の試験片を作成した。引張試験 ASTM D638に準拠し、常温で引張強度（降伏点強度およ
び引張伸び（破断点）を測定した。Example 1, Comparative Examples 1 and 2 Of the above resins, an alicyclic polyester composition (Example 1), an ABS resin (Comparative Example 1) and a polycarbonate resin (Comparative Example 2) were used.
A predetermined test piece for the test was prepared below. Tensile test According to ASTM D638, tensile strength (yield point strength and tensile elongation (break point) was measured at room temperature.

【００５２】曲げ試験 ASTM D790に準じて、曲げ強度、曲げ弾性率を測定し
た。アイゾット衝撃強度 得られた成形品から、厚さが1/8インチの試験片を作成
し、０．０５ｍｍのノッチを入れた後、２３℃±２℃、
５０％±５％ＲＨで４８時間以上調整し、衝撃強度を測
定した。 Bending Test Bending strength and flexural modulus were measured according to ASTM D790. Izod impact strength A test piece with a thickness of 1/8 inch was made from the obtained molded product, and a notch of 0.05 mm was inserted into the test piece.
The impact strength was measured by adjusting at 50% ± 5% RH for 48 hours or more.

【００５３】荷重たわみ温度 ASTM D648に準拠し、曲げ試験と同様にして、試験片の
中央に1,820MPaの曲げ応力がかかるようにおもりをの
せ、周りの温度（油槽温度）を上昇させて、たわむ温度
を測定した。結果をいずれも表１に示す。 Deflection temperature under load According to ASTM D648, in the same manner as in the bending test, a weight is placed on the center of the test piece so that a bending stress of 1,820 MPa is applied, and the surrounding temperature (oil tank temperature) is increased to bend the test piece. The temperature was measured. The results are shown in Table 1.

【００５４】[0054]

【表１】 [Table 1]

【００５５】表１より、実施例１で得られた成形品は、
ポリカーボネートまたはABSからなる成形品と同程度
の、機械的特性、耐衝撃性、耐熱性を有していることが
判明した。From Table 1, the molded article obtained in Example 1 is
It was found to have mechanical properties, impact resistance, and heat resistance comparable to those of molded products made of polycarbonate or ABS.

【００５６】[0056]

【実施例２、比較例３および４】上記各樹脂のうち、脂
環族ポリエステル組成物（実施例２）、ABS/PC樹脂（比
較例３）、ポリカーボネート樹脂（比較例４）を用い
て、以下試験用の所定の試験片を作成した。アイゾット衝撃強度 得られた成形品から、厚さが1/8インチの試験片を作成
し、０．０５ｍｍのノッチを入れた後、２３℃±２℃、
５０％±５％ＲＨで４８時間以上調整し、衝撃強度を測
定した。Example 2, Comparative Examples 3 and 4 Of the above resins, an alicyclic polyester composition (Example 2), an ABS / PC resin (Comparative Example 3), and a polycarbonate resin (Comparative Example 4) were used. A predetermined test piece for the test was prepared below. Izod impact strength A test piece with a thickness of 1/8 inch was made from the obtained molded product, and a notch of 0.05 mm was inserted into the test piece.
The impact strength was measured by adjusting at 50% ± 5% RH for 48 hours or more.

【００５７】メルトフローレート JIS K 7112に準拠して、1.2ｋｇ荷重、３００℃におい
てメルトフローレートを測定した。結果を表２に示す。[0057] in compliance with a melt flow rate JIS K 7112, to measure the melt flow rate at 1.2kg load, 300 ° C.. The results are shown in Table 2.

【００５８】[0058]

【表２】 [Table 2]

【００５９】表２より、脂環式ポリエステル組成物から
得られる成形品は、耐衝撃性が高く、また流動性に優れ
ているので成形性にも優れている。このため、本発明で
は、薄肉で衝撃強度の大きい成形品を製造することがで
きる。As shown in Table 2, the molded product obtained from the alicyclic polyester composition has high impact resistance and excellent flowability, and therefore has excellent moldability. Therefore, according to the present invention, it is possible to manufacture a molded product that is thin and has high impact strength.

【図面の簡単な説明】[Brief description of drawings]

【図１】 本発明で使用される脂環族ポリエステルの紫
外線吸収特性を示す。FIG. 1 shows ultraviolet absorption characteristics of an alicyclic polyester used in the present invention.

───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4E360 GA30 GB02 GB48 GC08 GC12 4F071 AA44 AA50 BA01 BB05 BB06 BC07 4J002 CF031 CG012 CG022 GQ00   ─────────────────────────────────────────────────── ─── Continued front page    F-term (reference) 4E360 GA30 GB02 GB48 GC08 GC12                 4F071 AA44 AA50 BA01 BB05 BB06                       BC07                 4J002 CF031 CG012 CG022 GQ00

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】脂環族ポリエステルを含む熱可塑性樹脂組
成物からなるハウジング、カバー及びケース。1. A housing, a cover and a case made of a thermoplastic resin composition containing an alicyclic polyester. 【請求項２】前記ハウジング、カバーあるいはケースが
電子電気機器、家電機器またはOA機器のプラスチック部
品用であることを特徴とする請求項１に記載のハウジン
グ、カバー及びケース。2. The housing, the cover and the case according to claim 1, wherein the housing, the cover or the case is for a plastic part of an electronic / electrical device, a home electric appliance or an OA device. 【請求項３】前記脂環族ポリエステルが、ポリシクロヘ
キサンジメタノールシクロヘキサンジカルボキシレート
(以後、PCCDと略す)であることを特徴とする請求項１に
記載のハウジング、カバー及びケース。3. The cycloaliphatic polyester is polycyclohexanedimethanol cyclohexanedicarboxylate.
The housing, the cover and the case according to claim 1, which are (hereinafter abbreviated as PCCD). 【請求項４】前記熱可塑性樹脂組成物が、脂環族ポリエ
ステルとともにポリカーボネートを含むことを特徴とす
る請求項１〜３のいずれかに記載のハウジング、カバー
及びケース。4. The housing, cover and case according to claim 1, wherein the thermoplastic resin composition contains a polycarbonate together with an alicyclic polyester.