JP2003091094A - Toner for developing electrostatic latent image - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide toner for developing an electrostatic latent image whose fixing temperature area is wide, which does not cause hot offset and cold offset and besides which does not cause offset even in the case of using an oil-less fixing device. SOLUTION: The toner incorporates at least fixing resin, a colorant and two kinds of wax whose softening points are different, and the softening point of the fixing resin is set between the softening points of two kinds of wax, and a difference between the softening point of the fixing resin and the weighted mean value of the softening points of two kinds of wax is set within 10 deg.C.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、電子写真装置に使
用する静電潜像現像用トナー（以下、単に「トナー」と
記すことがある）に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an electrostatic latent image developing toner (hereinafter sometimes simply referred to as "toner") used in an electrophotographic apparatus.

【０００２】[0002]

【従来の技術】複写機などの画像形成装置として、光源
からの光を原稿に照射し、その反射光を感光体に照射す
ることにより感光体上に静電潜像を形成するアナログ方
式のものが従来から一般に使用されている。また最近で
は、コンピューター端末の出力に使用するプリンター
や、イメージリーダーによって読み取った画像情報に基
づいて画像形成を行うデジタル複写機、電子写真方式の
ファクシミリ等の画像形成装置として、デジタル書き込
みされて得られた静電潜像にトナーを含む現像剤を供給
して現像を行うデジタル方式のものがよく使用されてい
る。2. Description of the Related Art An image forming apparatus such as a copying machine of an analog type which forms an electrostatic latent image on a photoconductor by irradiating a document with light from a light source and irradiating the photoconductor with the reflected light. Has been commonly used. In addition, recently, a printer used for output from a computer terminal, a digital copying machine that forms an image based on image information read by an image reader, an image forming apparatus such as an electrophotographic facsimile, and the like are obtained by digital writing. A digital system in which a developer containing toner is supplied to the electrostatic latent image for development is often used.

【０００３】これらの装置に使用されるトナーには、加
熱定着時にオフセット現象による画像汚染が生じないこ
と、即ち耐オフセット性に優れていることが要求され
る。耐オフセット性を向上させるためにはワックス等の
離型剤をトナーに含有させることが有効であるが、単に
ワックスを含有させるだけではオフセットを容易には防
止できない。ここで、オフセットには大きく分けてコー
ルドオフセットとホットオフセットとがある。コールド
オフセットとは、トナーの加熱ローラ接触面のみが溶け
て、トナーが加熱ローラに付着してしまう現象のことで
ある。一方ホットオフセットとは、トナーが溶けすぎる
ことによりトナー自体の凝集力が弱まって、加熱ローラ
への付着力に負けて加熱ローラに付着してしまう現象の
ことである。Toners used in these apparatuses are required to have no image contamination due to an offset phenomenon at the time of heat fixing, that is, have excellent offset resistance. In order to improve the offset resistance, it is effective to add a release agent such as wax to the toner, but the offset cannot be easily prevented by simply adding the wax. Here, the offset is roughly classified into a cold offset and a hot offset. Cold offset is a phenomenon in which only the contact surface of the heating roller with the toner melts and the toner adheres to the heating roller. On the other hand, hot offset is a phenomenon in which the toner itself melts too much to weaken the cohesive force of the toner itself and loses the adhesive force to the heating roller to adhere to the heating roller.

【０００４】ところで、社会の省エネルギー化に呼応し
て、トナーの低温定着性の向上が最近強く要求されてい
る。トナーの低温定着性を向上させるには、トナー構成
材料の熱特性を下げればよいが、やみくもに熱特性を下
げるとホットオフセットが発生してしまう。By the way, in response to energy saving in society, improvement of low temperature fixing property of toner has been strongly demanded recently. In order to improve the low-temperature fixability of the toner, the thermal characteristics of the toner constituent material may be lowered, but if the thermal characteristics are blindly lowered, hot offset occurs.

【０００５】また、高画質に対応した高グロス画像が従
来求められていたが、近年、ビジネス用途での使用が増
すにつれて、フルカラー画像上の加筆性が求められるよ
うになってきた。画像上の加筆性を向上させるには、加
熱ローラに塗布するオイル量を低減したり、あるいは加
熱ローラにオイルをまったく塗布をしない、いわゆるオ
イルレス定着装置の使用が望まれるようになってきてい
る。加熱ローラへのオイル塗布量を低減した定着装置や
オイルレス定着装置で加熱ローラへの巻き付きを防止す
るには、高温度でのトナーの弾性を強くしなけらばなら
ない。しかし高温度でのトナーの弾性を強くすると、ト
ナーの熱特性が高くなってコールドオフセットが発生し
やすくなる。Further, although a high gloss image corresponding to a high image quality has been demanded in the past, in recent years, as the use for business purposes has increased, the additivity on a full color image has come to be demanded. In order to improve the writing property on the image, it has been desired to use a so-called oilless fixing device that reduces the amount of oil applied to the heating roller or does not apply oil to the heating roller at all. . In order to prevent wrapping around the heating roller in a fixing device or an oilless fixing device in which the amount of oil applied to the heating roller is reduced, the elasticity of the toner at high temperatures must be increased. However, if the elasticity of the toner at high temperature is increased, the thermal characteristics of the toner are improved and cold offset is likely to occur.

【０００６】[0006]

【発明が解決しようとする課題】本発明はこのような従
来の問題に鑑みてなされたものであり、その目的は、オ
イル量を低減したり、あるいはオイル塗布を行わない定
着装置を用いて定着を行っても、ホットオフセット及び
コールドオフセットが発生しない、定着温度領域幅の広
いトナーを提供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of such a conventional problem, and an object thereof is to reduce the amount of oil or fix it by using a fixing device which does not apply oil. It is to provide a toner having a wide fixing temperature range in which hot offset and cold offset do not occur even if the above is performed.

【０００７】[0007]

【課題を解決するための手段】前記目的を達成するた
め、本発明の静電潜像現像用トナーでは、定着樹脂、着
色剤及び軟化点の異なる２種類のワックスを少なくとも
含有し、前記定着樹脂の軟化点を前記２種類のワックス
の軟化点の間とし、且つ前記定着樹脂の軟化点と前記２
種類のワックスの軟化点の加重平均との差を１０℃以内
とした。なお、本発明におけるワックスの軟化点とは、
ＤＳＣにおけるワックス吸熱ピーク温度をいい、ワック
スの軟化点の加重平均（Ｔ_m）とは下記式から算出され
るものをいう。In order to achieve the above object, the electrostatic latent image developing toner of the present invention contains at least a fixing resin, a colorant, and two kinds of waxes having different softening points, The softening point of the wax is between the softening points of the two types of wax, and the softening point of the fixing resin is
The difference from the weighted average of the softening point of each type of wax was set within 10 ° C. The softening point of the wax in the present invention means
It refers to the wax endothermic peak temperature in DSC, and the weighted average (T _m ) of the softening point of the wax refers to that calculated from the following formula.

【０００８】 Ｔ_m＝（Ｗ₁×Ｔ_m1＋Ｗ₂×Ｔ_m2）／（Ｗ₁＋Ｗ₂） Ｗ₁：ワックス１の配合量（重量） Ｔ_m1：ワックス１の軟化点 Ｗ₂：ワックス２の配合量（重量） Ｔ_m2：ワックス２の軟化点T _m = (W ₁ × T _m1 + W ₂ × T _m2 ) / (W ₁ + W ₂ ) W ₁ : compounding amount (weight) of wax 1 T _m1 : softening point of wax 1 W ₂ : wax 2 Compounding amount (weight) T _m2 : Softening point of wax 2

【０００９】ここで、オフセットの発生を一層抑える観
点から、軟化点の低い方のワックス（「ワックス１」と
記すことがある）の軟化点を７５℃以上とする、あるい
は軟化点の高い方のワックス（「ワックス２」と記すこ
とがある）の軟化点を１４０℃以下とするのが好まし
い。また、これら２種類のワックスの軟化点の温度差を
６５℃以内とするのが望ましい。そしてまた、これら２
種類のワックスの配合比は重量比で１：２〜２：１の範
囲であるのが好ましい。From the viewpoint of further suppressing the occurrence of offset, the wax having a lower softening point (sometimes referred to as "wax 1") has a softening point of 75 ° C. or higher, or has a higher softening point. The softening point of wax (sometimes referred to as “wax 2”) is preferably 140 ° C. or lower. Further, it is desirable that the temperature difference between the softening points of these two types of wax be within 65 ° C. And again these 2
The mixing ratio of the waxes is preferably in the range of 1: 2 to 2: 1 by weight.

【００１０】一方、トナーの低温定着性の観点からは、
定着樹脂の軟化点は１１０〜１３０℃の範囲が望まし
い。また、定着樹脂の軟化点と前記２種類のワックスの
軟化点との温度差はそれぞれ１０℃以上であるのが好ま
しい。On the other hand, from the viewpoint of the low temperature fixing property of the toner,
The softening point of the fixing resin is preferably in the range of 110 to 130 ° C. The temperature difference between the softening point of the fixing resin and the softening point of the two types of waxes is preferably 10 ° C. or more.

【００１１】[0011]

【発明の実施の形態】本発明者らは、オイル量を低減し
たり、あるいはオイル塗布を行わない定着装置を用いて
定着を行っても、ホットオフセット及びコールドオフセ
ットが発生しない、定着温度領域幅の広いトナーを提供
するべく鋭意検討した結果、定着樹脂およびワックスの
熱特性の関係を明確にすることにより、画像の光沢度を
コントロールする場合であっても、オフセットのない良
好な画像が得られることを見出し本発明をなすに至っ
た。BEST MODE FOR CARRYING OUT THE INVENTION The present inventors have found that hot offset and cold offset do not occur even if the amount of oil is reduced or fixing is performed using a fixing device that does not apply oil. As a result of intensive studies to provide a wide toner, a clear image without offset can be obtained even when controlling the glossiness of the image by clarifying the relationship between the thermal characteristics of the fixing resin and the wax. This has led to the present invention.

【００１２】すなわち本発明の一つの大きな特徴は、軟
化点の異なる２種類のワックスを定着樹脂に混合分散
し、定着樹脂の軟化点をワックス１よりは高く且つワッ
クス２よりは低くした点にある。そしてさらにもう一つ
の大きな特徴は定着樹脂の軟化点と前記２種類のワック
スの軟化点の加重平均との差を１０℃以内にした点にあ
る。That is, one of the major features of the present invention is that two kinds of waxes having different softening points are mixed and dispersed in the fixing resin so that the fixing resin has a softening point higher than that of the wax 1 and lower than that of the wax 2. . Yet another major feature is that the difference between the softening point of the fixing resin and the weighted average of the softening points of the two types of waxes is set within 10 ° C.

【００１３】本発明のトナーが転写紙に定着する機構を
説明する。まず定着初期には定着樹脂よりも早くワック
ス１が溶け出して、転写紙上のトナー画像と加熱ローラ
との間にワックス１の膜を形成し、加熱ローラへの転写
紙の巻き付き及びコールドオフセットを防止する。定着
中期には定着樹脂が溶融し、転写紙の紙繊維中に浸み込
んでトナーを転写紙にしっかりと定着させる。加えて、
ワックス１の効果により、トナー画像の表面が均一に平
らになり、フルカラー画像に平滑性と光沢性を付与す
る。そして定着終期には、ワックス２が溶け出して、転
写紙上に定着したトナー画像と加熱ローラとの間に介在
してホットオフセットを防止する。A mechanism for fixing the toner of the present invention on the transfer paper will be described. First, in the initial stage of fixing, the wax 1 melts earlier than the fixing resin to form a film of the wax 1 between the toner image on the transfer paper and the heating roller to prevent winding of the transfer paper around the heating roller and cold offset. To do. In the middle stage of fixing, the fixing resin melts and soaks into the paper fibers of the transfer paper to firmly fix the toner to the transfer paper. in addition,
Due to the effect of the wax 1, the surface of the toner image is uniformly flattened, and smoothness and gloss are imparted to the full-color image. Then, at the final stage of fixing, the wax 2 melts out and intervenes between the toner image fixed on the transfer sheet and the heating roller to prevent hot offset.

【００１４】（定着樹脂成分）本発明に用いられる定着
樹脂としては、例えば、ポリスチレン、クロロポリスチ
レン、ポリ−α−メチルスチレン、スチレン−クロロス
チレン共重合体、スチレン−プロピレン共重合体、スチ
レン−ブタジエン共重合体、スチレン−塩化ビニル共重
合体、スチレン−酢酸ビニル共重合体、スチレン−マレ
イン酸共重合体、スチレン−アクリル酸系共重合体（ス
チレン−アクリル酸共重合体、スチレン−アクリル酸メ
チル共重合体、スチレン−アクリル酸エチル共重合体、
スチレン−アクリル酸ブチル共重合体、スチレン−アク
リル酸オクチル共重合体、スチレン−アクリル酸フェニ
ル共重合体）、スチレン−メタクリル酸系共重合体（ス
チレン−メタクリル酸共重合体、スチレン−メタクリル
酸メチル共重合体、スチレン−メタクリル酸エチル共重
合体、スチレン−メタクリル酸ブチル共重合体、スチレ
ン−メタクリル酸オクチル共重合体、スチレン−メタク
リル酸フェニル共重合体）、スチレン−α−クロロアク
リル酸メチル共重合体、スチレン−アクリロニトリル−
アクリル酸エステル共重合体等のスチレン系樹脂（スチ
レンまたはスチレン置換体を含む単独重合体または共重
合体）、ポリ塩化ビニル、低分子量ポリエチレン、低分
子量ポリプロピレン、エチレン−アクリル酸エチル共重
合体、ポリビニルブチレール、エチレン−酢酸ビニル共
重合体、ロジン変性マレイン酸樹脂、フェノール樹脂、
エポキシ樹脂、ポリエステル樹脂、アイオノマー樹脂、
ポリウレタン樹脂、シリコーン樹脂、ケトン樹脂、キシ
レン樹脂、ポリアミド樹脂等があげられ、これらが単独
でまたは２種以上を混合して用いられる。また、トナー
の低温定着性を考慮すると、定着樹脂の軟化点は１００
〜１３０℃の範囲が好ましい。(Fixing Resin Component) Examples of the fixing resin used in the present invention include polystyrene, chloropolystyrene, poly-α-methylstyrene, styrene-chlorostyrene copolymer, styrene-propylene copolymer and styrene-butadiene. Copolymer, styrene-vinyl chloride copolymer, styrene-vinyl acetate copolymer, styrene-maleic acid copolymer, styrene-acrylic acid copolymer (styrene-acrylic acid copolymer, styrene-methyl acrylate) Copolymer, styrene-ethyl acrylate copolymer,
Styrene-butyl acrylate copolymer, styrene-octyl acrylate copolymer, styrene-phenyl acrylate copolymer), styrene-methacrylic acid copolymer (styrene-methacrylic acid copolymer, styrene-methyl methacrylate) Copolymer, styrene-ethyl methacrylate copolymer, styrene-butyl methacrylate copolymer, styrene-octyl methacrylate copolymer, styrene-phenyl methacrylate copolymer), styrene-α-methyl chloroacrylate copolymer Polymer, styrene-acrylonitrile-
Styrene resins such as acrylate copolymers (homopolymers or copolymers containing styrene or styrene substitutes), polyvinyl chloride, low molecular weight polyethylene, low molecular weight polypropylene, ethylene-ethyl acrylate copolymer, polyvinyl Butyral, ethylene-vinyl acetate copolymer, rosin-modified maleic acid resin, phenol resin,
Epoxy resin, polyester resin, ionomer resin,
Examples thereof include polyurethane resin, silicone resin, ketone resin, xylene resin, polyamide resin, and the like, and these may be used alone or in combination of two or more kinds. Considering the low temperature fixability of the toner, the softening point of the fixing resin is 100.
The range of ˜130 ° C. is preferable.

【００１５】（ワックス）本発明に用いられるワックス
１及びワックス２としては従来公知のものが使用でき
る。例えば、パラフィンワックス、石油系ワックス、ポ
リエチレンワックス、ポリプロピレンワックス、酸化ポ
リエチレンワックス、フィッシャートロプシュワックス
などの合成ワックスや、モンタンワックス、カルナバワ
ックス、ライスワックス等の天然ワックスが挙げられ
る。これらの中から、使用する定着樹脂に合わせて軟化
点の異なる２種類のワックスを適宜選択使用すればよ
い。(Wax) As the wax 1 and the wax 2 used in the present invention, conventionally known waxes can be used. Examples thereof include synthetic waxes such as paraffin wax, petroleum wax, polyethylene wax, polypropylene wax, oxidized polyethylene wax and Fischer-Tropsch wax, and natural waxes such as montan wax, carnauba wax and rice wax. Of these, two kinds of waxes having different softening points may be appropriately selected and used according to the fixing resin used.

【００１６】ここで、トナーの保存安定性の観点から、
ワックス１は軟化点が７５℃以上のものが好ましい。一
方、ホットオフセットをより効率的に防止する観点か
ら、ワックス２は軟化点が１４０℃以下のものが好まし
い。また、オフセットを防止すると同時に定着樹脂の選
択裕度を確保する観点から、２種類のワックスの軟化点
の温度差が６５℃以内になるようにワックスを選択する
のが望ましい。さらに２種類のワックスの配合比は重量
比で１：２〜２：１の範囲が好ましい。Here, from the viewpoint of toner storage stability,
Wax 1 preferably has a softening point of 75 ° C. or higher. On the other hand, from the viewpoint of more effectively preventing hot offset, the wax 2 preferably has a softening point of 140 ° C. or lower. Further, from the viewpoint of preventing offset and securing the selection margin of the fixing resin, it is desirable to select the wax so that the temperature difference between the softening points of the two types of wax is within 65 ° C. Furthermore, the mixing ratio of the two kinds of waxes is preferably in the range of 1: 2 to 2: 1 by weight.

【００１７】（着色剤）本発明に用いられる着色剤とし
ては、以下のようなものが一般的に使用される。ブラッ
クトナー用着色剤としてはカーボンブラック、アセチレ
ンブラック、ランプブラック、アニリンブラック等が挙
げられる。(Colorant) The following colorants are generally used as the colorant used in the present invention. Examples of the colorant for black toner include carbon black, acetylene black, lamp black and aniline black.

【００１８】イエロートナー用着色剤としては、Ｃ．
Ｉ．ピグメントイエロー１、Ｃ．Ｉ．ピグメントイエロ
ー５、Ｃ．Ｉ．ピグメントイエロー１２、Ｃ．Ｉ．ピグ
メントイエロー１５、Ｃ．Ｉ．ピグメントイエロー１
７、Ｃ．Ｉ．ピグメントイエロー１８０、Ｃ．Ｉ．ピグ
メントイエロー７４、Ｃ．Ｉ．ピグメントイエロー４、
Ｃ．Ｉ．ピグメントイエロー８１、Ｃ．Ｉ．ピグメント
イエロー９７、Ｃ．Ｉ．ピグメントイエロー９３等のア
ゾ系顔料；黄色酸化鉄、黄土等の無機系顔料；Ｃ．Ｉ．
アシッドイエロー１等のニトロ系染料；Ｃ．Ｉ．ソルベ
ントイエロー２、Ｃ．Ｉ．ソルベントイエロー６、Ｃ．
Ｉ．ソルベントイエロー１４、Ｃ．Ｉ．ソルベントイエ
ロー１５、Ｃ．Ｉ．ソルベントイエロー１９、Ｃ．Ｉ．
ソルベントイエロー２１等の油溶性染料などが挙げられ
る。この中でも色味等の点で、Ｃ．Ｉ．ピグメントイエ
ロー１２等のベンジジン系顔料が好適である。As the colorant for yellow toner, C.I.
I. Pigment Yellow 1, C.I. I. Pigment Yellow 5, C.I. I. Pigment Yellow 12, C.I. I. Pigment Yellow 15, C.I. I. Pigment Yellow 1
7, C.I. I. Pigment Yellow 180, C.I. I. Pigment Yellow 74, C.I. I. Pigment Yellow 4,
C. I. Pigment Yellow 81, C.I. I. Pigment Yellow 97, C.I. I. Pigment Yellow 93 and other azo pigments; yellow iron oxide, ocher and other inorganic pigments; C.I. I.
Nitro dyes such as Acid Yellow 1; C.I. I. Solvent Yellow 2, C.I. I. Solvent Yellow 6, C.I.
I. Solvent Yellow 14, C.I. I. Solvent Yellow 15, C.I. I. Solvent Yellow 19, C.I. I.
An oil-soluble dye such as Solvent Yellow 21 may be used. Among them, C.I. I. Pigment Yellow 12 and other benzidine pigments are suitable.

【００１９】マゼンタトナー用着色剤としては、Ｃ．
Ｉ．ピグメントレッド４９、Ｃ．Ｉ．ピグメントレッド
５７、Ｃ．Ｉ．ピグメントレッド８１、Ｃ．Ｉ．ピグメ
ントレッド１２２、Ｃ．Ｉ．ピグメントレッド１８４、
Ｃ．Ｉ．ピグメントレッド２３８、Ｃ．Ｉ．ソルベント
レッド１９、Ｃ．Ｉ．ソルベントレッド４９、Ｃ．Ｉ．
ソルベントレッド５２、Ｃ．Ｉ．ベーシックレッド１
０、Ｃ．Ｉ．ディスパーズレッド１５等が挙げられる。
この中でも色味等の点で、Ｃ．Ｉ．ピグメントレッド１
２２等のキナクリドン系顔料が好適である。As the colorant for magenta toner, C.I.
I. Pigment Red 49, C.I. I. Pigment Red 57, C.I. I. Pigment Red 81, C.I. I. Pigment Red 122, C.I. I. Pigment Red 184,
C. I. Pigment Red 238, C.I. I. Solvent Red 19, C.I. I. Solvent Red 49, C.I. I.
Solvent Red 52, C.I. I. Basic red 1
0, C.I. I. Examples include Disperse Red 15 and the like.
Among them, C.I. I. Pigment Red 1
Quinacridone pigments such as No. 22 are suitable.

【００２０】シアントナー用着色剤としては、Ｃ．Ｉ．
ピグメントブルー１５、Ｃ．Ｉ．ピグメントブルー１
６、Ｃ．Ｉ．ソルベントブルー５５、Ｃ．Ｉ．ソルベン
トブルー７０、Ｃ．Ｉ．ダイレクトブルー２５、Ｃ．
Ｉ．ダイレクトブルー８６等が挙げられる。この中でも
色味等の点で、Ｃ．Ｉ．ピグメントブルー１５等の銅フ
タロシアニン系顔料が好適である。As the colorant for cyan toner, C.I. I.
Pigment Blue 15, C.I. I. Pigment Blue 1
6, C.I. I. Solvent Blue 55, C.I. I. Solvent Blue 70, C.I. I. Direct Blue 25, C.I.
I. Direct Blue 86 and the like can be mentioned. Among them, C.I. I. Pigment Blue 15 and other copper phthalocyanine pigments are suitable.

【００２１】また、本発明では、トナーの電荷を制御す
るために、ニグロシンベース（ＣＩ５０４１５）、オイ
ルブラック（ＣＩ ２６１５０）、スピロンブラック等
の油溶性染料や、金属錯塩染料、第４級アンモニウム
塩、ポリイミダゾール塩、ナフテン酸金属塩、脂肪酸金
属石鹸、樹脂酸石鹸、（メタ）アクリル酸エステル樹脂
などの電荷制御剤を必要により使用してもよい。Further, in the present invention, in order to control the charge of the toner, an oil-soluble dye such as nigrosine base (CI 50415), oil black (CI 26150) and spirone black, a metal complex dye, a quaternary ammonium salt. A charge control agent such as a polyimidazole salt, a naphthenic acid metal salt, a fatty acid metal soap, a resin acid soap, or a (meth) acrylic acid ester resin may be used if necessary.

【００２２】本発明のトナーは、上述した各種成分を溶
融混練し、得られた溶融混練物（トナー用樹脂組成物）
を粉砕、分級することにより得られる。そのまま一成分
系現像剤として使用してもよいし、フェライト、鉄粉等
の磁性キャリヤと混合して二成分系現像剤としてもよ
い。好ましくは二成分系現像剤とし、フルカラー現像に
用いるのがよい。なお、ワックスを定着樹脂中に微分散
させるために、ワックス成分の一部または全部を、定着
樹脂として使用する樹脂の製造段階で添加配合しておい
てもよい。The toner of the present invention is a melt-kneaded product (resin composition for toner) obtained by melt-kneading the above-mentioned various components.
It is obtained by crushing and classifying. It may be used as it is as a one-component developer, or may be mixed with a magnetic carrier such as ferrite or iron powder to give a two-component developer. A two-component developer is preferably used for full-color development. Incidentally, in order to finely disperse the wax in the fixing resin, a part or all of the wax component may be added and blended at the production stage of the resin used as the fixing resin.

【００２３】トナーの粒径は、一般に５〜２０μｍの範
囲、特に７〜１３μｍの範囲がよく、また、その流動性
を向上させるために、疎水性シリカやＴｉＯ₂などの無
機酸化物から成る流動性向上剤をトナー粒子表面に外添
してもよい。また、トナーを磁性キャリヤと混合して使
用する場合には、トナー：キャリヤ＝３：９７〜８：９
２（重量比）とするのがよい。The particle size of the toner is generally in the range of 5 to 20 [mu] m, in particular in the range of 7~13μm good, also in order to improve its flowability, flow composed of an inorganic oxide such as hydrophobic silica and TiO ₂ The property improver may be externally added to the surface of the toner particles. When the toner is mixed with the magnetic carrier to be used, toner: carrier = 3: 97 to 8: 9.
2 (weight ratio) is preferable.

【００２４】本発明のトナーをフルカラー現像に用いる
場合には、その色に応じてフルカラー画像形成装置の各
現像装置内に充填し、正極性又は負極性に帯電させて、
フルカラー現像を行う。When the toner of the present invention is used for full-color development, it is filled in each developing device of a full-color image forming apparatus according to the color and charged to a positive or negative polarity,
Perform full color development.

【００２５】本発明のトナーは幅広い定着条件下で優れ
た定着性、耐オフセット性を示すので、ユーザーの要求
に応じて定着条件を種々変更することができる。例え
ば、黒トナーのみを用いてのモノクロ画像形成時には、
定着速度（加熱ローラ周速）を８０〜２００ｍｍ／ｍｉ
ｎ、定着圧力（加圧ローラ圧）を５〜２０ｋｇ／ｃ
ｍ²、定着温度（加熱ローラ温度）を１００〜１６０℃
程度に設定することにより、光沢度（グロス）が５以下
のモノクロ画像を形成することができる。また、定着速
度（加熱ローラ周速）を２０〜１５０ｍｍ／ｍｉｎ、定
着圧力（加圧ローラ圧）を２０〜５０ｋｇ／ｃｍ²、定
着温度（加熱ローラ温度）を１６０〜２２０℃程度に設
定するとにより、光沢度が２５以上のフルカラー画像を
形成することができる。また、本発明のトナーは耐オフ
セット性に著しく優れているため、加熱ローラへのオイ
ル塗布量を従来よりも低減した定着装置、あるいは加熱
ローラにオイルを全く塗布しないオイルレス定着装置に
も適応できる。Since the toner of the present invention exhibits excellent fixability and anti-offset property under a wide range of fixing conditions, the fixing conditions can be variously changed according to the user's request. For example, when forming a monochrome image using only black toner,
Fixing speed (heat roller peripheral speed) of 80 to 200 mm / mi
n, fixing pressure (pressure roller pressure) 5 to 20 kg / c
m ² , fixing temperature (heating roller temperature) 100 to 160 ° C.
By setting the degree to about, a monochrome image having a glossiness (gloss) of 5 or less can be formed. Further, by setting the fixing speed (heating roller peripheral speed) to 20 to 150 mm / min, the fixing pressure (pressure roller pressure) to 20 to 50 kg / cm ² , and the fixing temperature (heating roller temperature) to about 160 to 220 ° C. A full-color image having a glossiness of 25 or more can be formed. Further, since the toner of the present invention is extremely excellent in anti-offset property, it can be applied to a fixing device in which the amount of oil applied to the heating roller is smaller than that of the conventional one, or an oilless fixing device in which no oil is applied to the heating roller. .

【００２６】[0026]

【実施例】以下、この発明を実施例、比較例に基づいて
さらに説明する。なお、以下の実施例では本発明のトナ
ーを二成分現像剤として実験を行っているが、もちろん
これに限定されるものではない。EXAMPLES The present invention will be further described below based on Examples and Comparative Examples. In the following examples, experiments were conducted using the toner of the present invention as a two-component developer, but of course the invention is not limited to this.

【００２７】実施例１〜９及び比較例１〜７のトナー粒
子は、各トナー成分をミキサーで乾式混合し、加熱ロー
ラにて溶融混練した後、気流式粉砕機で粉砕し、更に風
力分級機で分級して作製した。以下に各実施例及び比較
例のトナー成分及び配合比について説明する。定着樹
脂、ワックス１及びワックス２の軟化点については表１
に記載する。In the toner particles of Examples 1 to 9 and Comparative Examples 1 to 7, the respective toner components were dry mixed by a mixer, melted and kneaded by a heating roller, pulverized by an air stream type pulverizer, and further, an air classifier. It was prepared by classifying with. The toner components and compounding ratios of the examples and comparative examples will be described below. Table 1 shows the softening points of the fixing resin, wax 1 and wax 2.
Described in.

【００２８】定着樹脂の軟化点は、高化式フローテスタ
（「ＣＦＴ−５００」島津製作所社製）を用いて、荷重
２０ｋｇｆ、ダイ径１ｍｍ、ダイ長さ１ｍｍ、昇温速度
６℃／分の条件で測定した。また、ＤＳＣにて測定した
ワックス吸熱ピーク温度をワックスの軟化点とした。The softening point of the fixing resin was measured by using a Koka type flow tester ("CFT-500" manufactured by Shimadzu Corporation) under a load of 20 kgf, a die diameter of 1 mm, a die length of 1 mm, and a heating rate of 6 ° C / min. It was measured under the conditions. The wax endothermic peak temperature measured by DSC was used as the softening point of the wax.

【００２９】実施例１、２、比較例１、２ 定着樹脂、着色剤（シアン顔料）、電荷制御剤、ワック
スを下記配合比で分散配合してトナー粒子を作製した。 スチレン−アクリル樹脂 １００重量部 着色剤 ５重量部 電荷制御剤 ２重量部 ワックス１（ポリエチレン） ４．５重量部 ワックス２（ポリプロピレン） ４．５重量部Examples 1 and 2 and Comparative Examples 1 and 2 A fixing resin, a colorant (cyan pigment), a charge control agent and a wax were dispersed and blended at the following blending ratio to prepare toner particles. Styrene-acrylic resin 100 parts by weight Colorant 5 parts by weight Charge control agent 2 parts by weight Wax 1 (polyethylene) 4.5 parts by weight Wax 2 (polypropylene) 4.5 parts by weight

【００３０】 実施例３、比較例３ スチレン−アクリル樹脂 １００重量部 着色剤 ５重量部 電荷制御剤 ２重量部 ワックス１（ポリエチレン） ３重量部 ワックス２（ポリプロピレン） ６重量部[0030]   Example 3, Comparative Example 3   Styrene-acrylic resin 100 parts by weight   Colorant 5 parts by weight   Charge control agent 2 parts by weight   Wax 1 (polyethylene) 3 parts by weight   Wax 2 (polypropylene) 6 parts by weight

【００３１】実施例４〜５、比較例４ 定着樹脂、着色剤（シアン顔料）、電荷制御剤、ワック
スを下記配合比で分散配合してトナー粒子を作製した。 スチレン−アクリル樹脂 １００重量部 着色剤 ５重量部 電荷制御剤 ２重量部 ワックス１（フィッシャートロプシュ） ５重量部 ワックス２（ポリプロピレン） ４重量部Examples 4 to 5 and Comparative Example 4 Toner particles were prepared by dispersing and fixing a fixing resin, a colorant (cyan pigment), a charge control agent and a wax in the following mixing ratio. Styrene-acrylic resin 100 parts by weight Colorant 5 parts by weight Charge control agent 2 parts by weight Wax 1 (Fischer-Tropsch) 5 parts by weight Wax 2 (polypropylene) 4 parts by weight

【００３２】実施例６〜７、比較例５ 定着樹脂、着色剤（シアン顔料）、電荷制御剤、ワック
スを下記配合比で分散配合してトナー粒子を作製した。 ポリエステル樹脂 １００重量部 着色剤 ５重量部 電荷制御剤 ２重量部 ワックス１（フィッシャートロプシュ） ２重量部 ワックス２（ポリプロピレン） ３重量部Examples 6 to 7 and Comparative Example 5 Toner particles were prepared by dispersing and fixing a fixing resin, a colorant (cyan pigment), a charge control agent and a wax in the following mixing ratio. Polyester resin 100 parts by weight Colorant 5 parts by weight Charge control agent 2 parts by weight Wax 1 (Fischer-Tropsch) 2 parts by weight Wax 2 (polypropylene) 3 parts by weight

【００３３】実施例８〜９、比較例７ 定着樹脂、着色剤（シアン顔料）、電荷制御剤、ワック
スを下記配合比で分散配合してトナー粒子を作製した。 ポリエステル樹脂 １００重量部 着色剤 ５重量部 電荷制御剤 ２重量部 ワックス１（カルナバ） ２重量部 ワックス２（ポリプロピレン） ２重量部Examples 8 to 9 and Comparative Example 7 Toner particles were prepared by dispersing and fixing a fixing resin, a colorant (cyan pigment), a charge control agent and a wax in the following mixing ratio. Polyester resin 100 parts by weight Colorant 5 parts by weight Charge control agent 2 parts by weight Wax 1 (carnauba) 2 parts by weight Wax 2 (polypropylene) 2 parts by weight

【００３４】比較例６ 定着樹脂、着色剤（シアン顔料）、電荷制御剤、ワック
スを下記配合比で分散配合してトナー粒子を作製した。
ワックス１、２ともポリプロピレンであるが、軟化点が
異なるものであり、同一のワックスではない。 ポリエステル樹脂 １００重量部 着色剤 ５重量部 電荷制御剤 ２重量部 ワックス１（ポリプロピレン） ２．５重量部 ワックス２（ポリプロピレン） ２．５重量部Comparative Example 6 A fixing resin, a colorant (cyan pigment), a charge control agent and a wax were dispersed and compounded at the following compounding ratio to prepare toner particles.
The waxes 1 and 2 are polypropylene, but they have different softening points and are not the same wax. Polyester resin 100 parts by weight Colorant 5 parts by weight Charge control agent 2 parts by weight Wax 1 (polypropylene) 2.5 parts by weight Wax 2 (polypropylene) 2.5 parts by weight

【００３５】 実施例１０ ポリエステル樹脂 １００重量部 着色剤 ５重量部 電荷制御剤 ２重量部 ワックス１（炭化水素系ワックス） ２重量部 ワックス２（ポリプロピレン） ３重量部[0035]   Example 10   100 parts by weight of polyester resin   Colorant 5 parts by weight   Charge control agent 2 parts by weight   Wax 1 (hydrocarbon wax) 2 parts by weight   Wax 2 (polypropylene) 3 parts by weight

【００３６】前記の各実施例、比較例で作製したトナー
粒子に対し、トナー粒子１００重量部当たり０．４重量
部の疎水性シリカを外添してトナーとした。そして、こ
のトナー５重量部と、フェライトキャリヤ（パウダーテ
ック社製）９５重量部を摩擦混合して二成分系現像剤と
した。To the toner particles prepared in each of the above Examples and Comparative Examples, 0.4 part by weight of hydrophobic silica was added externally per 100 parts by weight of the toner particles to obtain a toner. Then, 5 parts by weight of this toner and 95 parts by weight of a ferrite carrier (manufactured by Powder Tech Co., Ltd.) were frictionally mixed to prepare a two-component developer.

【００３７】前記作製した現像剤を、市販複写機（「Ｃ
ｉ−９５００」京セラミタ社製）の改造機の現像器に投
入し、青色の単色カラー画像を形成して以下の評価を行
った。その結果を表１に示す。なお、この改造機では、
定着装置の加熱ローラ及び加圧ローラのそれぞれに表面
が含フッ素樹脂で形成されたソフトローラを使用した。
また加熱ローラにはオイルを全く塗布せずに画像形成を
行った。A commercially available copying machine ("C
i-9500 "manufactured by Kyocera Mita Co., Ltd.) was put into a developing device of a modified machine, a blue single color image was formed, and the following evaluation was performed. The results are shown in Table 1. In this modified machine,
Soft rollers each having a surface formed of a fluorine-containing resin were used as the heating roller and the pressure roller of the fixing device.
An image was formed without applying any oil to the heating roller.

【００３８】耐コールドオフセット性 加熱ローラの周速及び加熱ローラの圧力を一定にして、
加熱ローラの温度を１２０℃にして画像の定着を行い、
加熱ローラへのトナー付着が生じない場合は「○」、ト
ナー付着が生じた場合は「×」として耐コールドオフセ
ット性の評価を行った。Cold offset resistance The peripheral speed of the heating roller and the pressure of the heating roller are kept constant,
Fix the image by setting the temperature of the heating roller to 120 ℃.
When the toner adhesion to the heating roller did not occur, "O" was evaluated, and when the toner adhesion occurred, "X" was evaluated to evaluate the cold offset resistance.

【００３９】耐ホットオフセット性：加熱ローラの周速
及び加熱ローラの圧力を一定にして、加熱ローラの温度
を２１０℃にして画像の定着を行い、加熱ローラへのト
ナー付着が生じない場合は「○」、トナー付着が生じた
場合は「×」として耐ホットオフセット性の評価を行っ
た。Hot-offset resistance: When the peripheral speed of the heating roller and the pressure of the heating roller are kept constant and the temperature of the heating roller is 210 ° C. to fix an image, and toner does not adhere to the heating roller, “ ◯ ”, and when toner adhesion occurred,“ × ”was evaluated for hot offset resistance.

【００４０】[0040]

【表１】 [Table 1]

【００４１】表１から明らかなように、定着樹脂の軟化
点がワックス１とワックス２の軟化点の間にある実施例
１〜１０の各トナーでは、耐コールドオフセット性及び
耐ホットオフセット性共に良好な結果であった。これに
対し、定着樹脂の軟化点がワックス１の軟化点よりも低
い比較例１及び比較例３、比較例５、比較例６の各トナ
ーではコールドオフセットが発生した。また定着樹脂の
軟化点がワックス２の軟化点よりも高い比較例２及び比
較例４、比較例７の各トナーではホットオフセットが発
生した。As is clear from Table 1, the toners of Examples 1 to 10 in which the softening point of the fixing resin is between the softening points of Wax 1 and Wax 2 are good in both cold offset resistance and hot offset resistance. It was a good result. On the other hand, cold offset occurred in each of the toners of Comparative Example 1, Comparative Example 3, Comparative Example 5, and Comparative Example 6, in which the softening point of the fixing resin was lower than that of Wax 1. Further, hot offset occurred in each of the toners of Comparative Example 2, Comparative Example 4, and Comparative Example 7 in which the softening point of the fixing resin was higher than that of the wax 2.

【００４２】[0042]

【発明の効果】本発明の静電潜像現像用トナーでは、定
着樹脂の軟化点を使用する２種類のワックスの軟化点の
間とし、さらに定着樹脂の軟化点とこれら２種類のワッ
クスの軟化点の加重平均との差を１０℃以内としたの
で、定着温度領域の幅が広がり、ホットオフセット及び
コールドオフセットが発生せず、しかもオイルレス定着
装置を用いた場合であってもオフセットの発生が有効に
防止される。In the electrostatic latent image developing toner of the present invention, the softening point of the fixing resin is set between the softening points of the two kinds of waxes used, and the softening point of the fixing resin and the softening points of these two kinds of waxes are used. Since the difference from the weighted average of the points is within 10 ° C., the width of the fixing temperature region is widened, hot offset and cold offset do not occur, and even when the oilless fixing device is used, the offset occurs. Effectively prevented.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 松井 謙之 大阪府大阪市中央区玉造１丁目２番28号 京セラミタ株式会社内 Ｆターム(参考） 2H005 AA01 AA06 CA04 CA08 CA14 EA03 EA07    ─────────────────────────────────────────────────── ─── Continued front page    (72) Inventor Kenyuki Matsui             1-22 Tamatsukuri, Chuo-ku, Osaka-shi, Osaka Prefecture             Kyocera Mita Co., Ltd. F-term (reference) 2H005 AA01 AA06 CA04 CA08 CA14                       EA03 EA07

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 定着樹脂、着色剤及び軟化点の異なる２
種類のワックスを含有した静電潜像現像用トナーにおい
て、 前記定着樹脂の軟化点を前記２種類のワックスの軟化点
の間とし、且つ前記定着樹脂の軟化点と前記２種類のワ
ックスの軟化点の加重平均との差を１０℃以内としたこ
とを特徴とする静電潜像現像用トナー。1. A fixing resin, a colorant, and 2 having different softening points.
In a toner for developing an electrostatic latent image containing two kinds of waxes, the softening point of the fixing resin is between the softening points of the two kinds of wax, and the softening point of the fixing resin and the softening points of the two kinds of waxes. The toner for developing an electrostatic latent image has a difference from the weighted average of 10 ° C. or less. 【請求項２】 軟化点の低い方のワックスの軟化点が７
５℃以上である請求項１記載の静電潜像現像用トナー。2. A wax having a lower softening point has a softening point of 7
The toner for developing an electrostatic latent image according to claim 1, which has a temperature of 5 ° C or higher. 【請求項３】 軟化点の高い方のワックスの軟化点が１
４０℃以下である請求項１又は２記載の静電潜像現像用
トナー。3. The wax having a higher softening point has a softening point of 1
The toner for developing an electrostatic latent image according to claim 1, which has a temperature of 40 ° C. or lower. 【請求項４】 前記２種類のワックスの軟化点の温度差
が６５℃以内である請求項１〜３のいずれかに記載の静
電潜像現像用トナー。4. The toner for developing an electrostatic latent image according to claim 1, wherein the temperature difference between the softening points of the two kinds of wax is within 65 ° C. 【請求項５】 ２種類のワックスの配合比が重量比で
１：２〜２：１の範囲である請求項１〜４のいずれかに
記載の静電潜像現像用トナー。5. The toner for developing an electrostatic latent image according to claim 1, wherein the compounding ratio of the two types of wax is in the range of 1: 2 to 2: 1 by weight. 【請求項６】 前記定着樹脂の軟化点が１１０〜１３０
℃の範囲である請求項１〜５のいずれかに記載の静電潜
像現像用トナー。6. The softening point of the fixing resin is 110 to 130.
The toner for developing an electrostatic latent image according to any one of claims 1 to 5, which is in the range of ° C. 【請求項７】 前記定着樹脂の軟化点と前記２種類のワ
ックスの軟化点との温度差がそれぞれ１０℃以上である
請求項１〜６のいずれかに記載の静電潜像現像用トナ
ー。7. The toner for developing an electrostatic latent image according to claim 1, wherein the temperature difference between the softening point of the fixing resin and the softening point of the two kinds of wax is 10 ° C. or more.