JP2003064568A - Nonwoven fabric and simple clothing, wiper using the nonwoven fabric - Google Patents
Nonwoven fabric and simple clothing, wiper using the nonwoven fabricInfo
- Publication number
- JP2003064568A JP2003064568A JP2002139742A JP2002139742A JP2003064568A JP 2003064568 A JP2003064568 A JP 2003064568A JP 2002139742 A JP2002139742 A JP 2002139742A JP 2002139742 A JP2002139742 A JP 2002139742A JP 2003064568 A JP2003064568 A JP 2003064568A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- sheet
- woven fabric
- wiper
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、生分解性を有する
繊維から構成されるメルトブロー不織布と、生分解性を
有する繊維から構成されるスパンボンド不織布からなる
不織布、および該不織布を用いてなる簡易衣料またはワ
イパーに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a melt blown nonwoven fabric composed of biodegradable fibers, a spunbonded nonwoven fabric composed of biodegradable fibers, and a simple fabric using the nonwoven fabric. It concerns clothing or wipers.
【０００２】本発明により供される不織布は、構成繊維
が全て生分解性を有するため、簡易衣料あるいはワイパ
ーとして使用された後、廃棄処分が容易であり、かつ、
簡易衣料さらにはワイパーとして必要な特性を兼ね備え
たものである。In the nonwoven fabric provided by the present invention, all the constituent fibers have biodegradability, so that it can be easily disposed of after being used as simple clothing or wiper, and
It has the characteristics required for simple clothing and wipers.
【０００３】[0003]
【従来の技術】従来、汚れ作業時の作業着、発塵を嫌う
クリーンルーム用作業着、さらには衣料用の手術着など
の簡易衣料材料として、いわゆる使い捨ての簡易衣料用
不織布が種々提案されている。2. Description of the Related Art Conventionally, various so-called disposable non-woven fabrics for simple clothing have been proposed as simple clothing materials such as work clothes for dirty work, work clothes for clean rooms where dust is disliked, and surgical clothes for clothes. .
【０００４】簡易衣料用不織布に必要とされる特性とし
ては、良好な着心地を保有するための風合い、着用時に
破れが生じないための強度、さらには作業時に作業着内
部への汚れの付着を防ぐための防塵性などが挙げられ
る。また、通常１回から数回の使用後廃棄処分されるた
め、低コストなものが好ましく用いられる。The properties required of a non-woven fabric for simple clothing include a texture for maintaining good wearing comfort, a strength so as not to be broken during wearing, and a stain adhered to the inside of work clothes during work. For example, dustproof property for prevention. Moreover, since it is usually disposed of after one to several times of use, it is preferably used at low cost.
【０００５】また、フローリングワイパーなどのワイパ
ー材料としても、いわゆる使い捨てのワイパー用不織布
が種々提案されている。Also, as a wiper material such as a flooring wiper, various so-called disposable nonwoven fabrics for wipers have been proposed.
【０００６】ワイパー用不織布に必要とされる特性とし
ては、良好な拭き取り作業性を保有するための柔軟性や
風合い、使用時に破れが生じないための強度、さらには
拭き取り性能を向上させるためには、構成繊維が極細で
あることが必要である。Nonwoven fabrics for wipers are required to have such properties as flexibility and texture for maintaining good wiping workability, strength for preventing tearing during use, and further for improving wiping performance. It is necessary that the constituent fibers are extremely fine.
【０００７】[0007]
【発明が解決しようとする課題】上記簡易衣料用不織
布、あるいはワイパー用不織布の必要特性を満足させる
ため、これまで一般に使用される不織布はポリプロピレ
ン、ポリエステル、ナイロン等を主原料としていた。こ
れら従来の不織布は、使用後一般的に埋め立て処理や焼
却処理が行われているが、埋め立てられた場合、化学的
に安定なため長期間に渡ってそのままの形状を保ち続け
てしまうという問題点があった。In order to satisfy the necessary characteristics of the above-mentioned non-woven fabric for simple clothing or non-woven fabric for wipers, non-woven fabrics generally used so far have mainly used polypropylene, polyester, nylon and the like as a main raw material. These conventional non-woven fabrics are generally subjected to landfill treatment or incineration treatment after use, but when they are landfilled, they remain chemically stable for a long period of time. was there.
【０００８】また、使用後の不織布を焼却処理した場合
には、焼却時の発熱量が高いため焼却炉を傷めるだけで
なく、ナイロン系の不織布を焼却した場合にはシアンガ
スなどの有害ガスが発生するという問題点もある。When the used non-woven fabric is incinerated, the calorific value at the time of incineration is high, which not only damages the incinerator, but also when the nylon-based non-woven fabric is incinerated, harmful gas such as cyan gas is generated. There is also the problem of doing.
【０００９】一方、近年、環境志向の高まりとともに、
生分解性を有する繊維からなる種々の不織布が提案され
ているが、簡易衣料用不織布として十分な柔軟性、強
度、防塵性、さらにはワイパー用不織布として十分な柔
軟性、風合い、強度、拭き取り性能などを兼ね備えるも
のではなかった。On the other hand, in recent years, with the increase in environmental orientation,
Various non-woven fabrics made of biodegradable fibers have been proposed, but they have sufficient flexibility, strength and dust resistance as non-woven fabrics for simple clothing, and further have sufficient flexibility, texture, strength and wiping performance as non-woven fabrics for wipers. It wasn't something that had both.
【００１０】本発明は、かかる従来技術の背景に鑑み、
生分解性を有する繊維からなり、かつ、簡易衣料用材
料、さらにはワイパー用材料として十分な強度、風合
い、防塵性、拭き取り性能などをもつ不織布を提供せん
とするものである。The present invention has been made in view of such background of the prior art.
It is intended to provide a non-woven fabric composed of biodegradable fibers and having sufficient strength, texture, dustproofness and wiping performance as a material for simple clothing and a material for wipers.
【００１１】[0011]
【課題を解決するための手段】本発明は、かかる課題を
解決するために、次のような手段を採用するものであ
る。The present invention employs the following means in order to solve the above problems.
【００１２】すなわち、本発明の不織布は、生分解性を
有する繊維から構成されるメルトブロー不織布の少なく
とも片面に、生分解性を有する繊維から構成されるスパ
ンボンド不織布が積層されたシートが、部分的熱接着に
より一体化されてなることを特徴とする不織布である。That is, the nonwoven fabric of the present invention is a sheet in which a spunbonded nonwoven fabric composed of biodegradable fibers is laminated on at least one surface of a melt-blown nonwoven fabric composed of biodegradable fibers. It is a nonwoven fabric characterized by being integrated by thermal bonding.
【００１３】また、かかる該メルトブロー不織布および
スパンボンド不織布を構成する繊維が、ポリ乳酸系樹脂
からなることを特徴とする不織布である。Further, the fibers constituting the melt-blown nonwoven fabric and the spunbonded nonwoven fabric are made of polylactic acid type resin.
【００１４】さらに、該メルトブロー不織布の目付が１
０〜１００ｇ／ｍ2 で、構成繊維の平均繊維径が１０μ
ｍ以下であり、かつ、該スパンボンド不織布の目付が１
０〜１００ｇ／ｍ2 で、構成繊維の平均繊維径が１０〜
４０μｍであることを特徴とする不織布である。さらに
また、該メルトブロー不織布と該スパンボンド不織布の
熱接着面積が５〜４０％の範囲であることを特徴とする
不織布である。Furthermore, the basis weight of the meltblown nonwoven fabric is 1
The average fiber diameter of the constituent fibers is 0 to 100 g / m 2
m or less, and the basis weight of the spunbonded nonwoven fabric is 1
The average fiber diameter of the constituent fibers is 10 to 100 g / m 2.
The nonwoven fabric is characterized by having a thickness of 40 μm. Furthermore, the heat-bonded area of the meltblown nonwoven fabric and the spunbonded nonwoven fabric is in the range of 5 to 40%.
【００１５】またさらに、上記いずれかの不織布を、簡
易衣料、あるいはワイパーの材料とするものである。Furthermore, any of the above-mentioned non-woven fabrics is used as a material for simple clothing or wipers.
【００１６】[0016]
【発明の実施の形態】本発明は、前記課題、つまり、簡
易衣料用材料、さらにはワイパー用材料として十分な風
合い、強度、防塵性などを有し、かつ、生分解性を有す
る繊維から構成されるため使用後の廃棄処分が容易であ
る不織布について鋭意検討し、生分解性を有する繊維か
ら構成される数種類の不織布を積層することにより、か
かる課題を一挙に解決することを究明したものである。BEST MODE FOR CARRYING OUT THE INVENTION The present invention comprises the above-mentioned problems, namely, fibers having sufficient texture, strength, dustproofness and the like as materials for simple clothing and wipers, and having biodegradability. Therefore, we have made a thorough study on a non-woven fabric that is easy to dispose of after use, and have clarified that such problems can be solved all at once by laminating several types of non-woven fabrics composed of biodegradable fibers. is there.
【００１７】本発明において、「簡易衣料」とは、汚れ
作業時の作業着、発塵を嫌うクリーンルーム用の作業
着、さらには衣料用の手術着など、１回から数回の使用
後、廃棄処分される、いわゆる使い捨ての作業用衣服で
あり、「簡易衣料用不織布」とは、かかる簡易衣料の材
料として好適な風合い、強度、防塵性を有する不織布で
ある。 また本発明において、「ワイパー」とは、フロ
ーリングワイパーなど、１回から数回の使用後、廃棄処
分される、いわゆる使い捨てタイプのワイパーであり、
「ワイパーに用いられる不織布」とは、かかるワイパー
の材料として優れた柔軟性、十分な風合い、強度、拭き
取り性能を有する不織布である。本発明にかかる該不織
布は、使用後の廃棄処分において自然環境を汚染するこ
とがないよう生分解性能を有していることが重要であ
る。In the present invention, "simple clothing" means work clothing for dirty work, work clothing for clean rooms that do not like dust, and surgical clothing for clothing, which is discarded after one to several times of use. It is a so-called disposable work garment that is disposed of, and the "nonwoven fabric for simple clothing" is a nonwoven fabric having a texture, strength, and dust resistance suitable as a material for such simple clothing. Further, in the present invention, the “wiper” is a so-called disposable wiper, such as a flooring wiper, which is discarded after being used once to several times,
The “nonwoven fabric used for the wiper” is a nonwoven fabric having excellent flexibility, sufficient texture, strength and wiping performance as a material for such wiper. It is important that the non-woven fabric according to the present invention has biodegradability so as not to pollute the natural environment when it is discarded after use.
【００１８】本発明にて使用されるメルトブロー不織布
は、特に限定されるものではないが、溶融したポリマー
に加熱高速ガス流体を吹き当てることにより該溶融ポリ
マーを引き伸ばして極細繊維化し、捕集してシートとす
る、いわゆるメルトブロー法により製造されたものが好
ましい。The melt blown non-woven fabric used in the present invention is not particularly limited, but the molten polymer is stretched by spraying a heated high-speed gas fluid onto the molten polymer to form ultrafine fibers and collected. A sheet, which is produced by a so-called melt blow method, is preferable.
【００１９】該メルトブロー不織布の目付量は特に限定
されるものではないが、１０〜１００ｇ／ｍ2 が好まし
い。目付が１０ｇ／ｍ2 よりも低い場合には防塵性が著
しく低下するため、簡易衣料用材料として使用に耐えな
いものとなる。また目付が１００ｇ／ｍ2 よりも高い場
合は、防塵性は向上するものの、シート全体の重量が重
く、嵩張り、柔軟性や着心地に劣り、さらに製造コスト
も高くなるため好ましくない。より好ましい該メルトブ
ロー不織布の目付量は、簡易衣料用材料としては１５〜
８０ｇ／ｍ2 、ワイパー用材料としては１５〜６０ｇ／
ｍ2 である。さらに該メルトブロー不織布を構成する繊
維の平均繊維径は１０μｍ以下であることが好ましい。
平均繊維径が１０μｍを超えると該メルトブロー不織布
の空隙率が増加し、防塵性が著しく低下するため、簡易
衣料用材料として使用に耐えないものとなる。さらにワ
イパー用材料として使用する場合、拭き取り性能が低下
する傾向であり好ましくない。より好ましい該メルトブ
ロー不織布を構成する繊維の平均繊維径は８μｍ以下で
ある。The basis weight of the meltblown nonwoven fabric is not particularly limited, but is preferably 10 to 100 g / m 2 . When the basis weight is lower than 10 g / m 2 , the dustproof property is remarkably reduced, and it cannot be used as a material for simple clothing. Further, if the fabric weight is higher than 100 g / m 2 , the dustproof property is improved, but the weight of the entire sheet is heavy, bulky, inferior in flexibility and wearing comfort, and further the manufacturing cost becomes high, which is not preferable. The more preferable weight per unit area of the melt blown nonwoven fabric is 15 to 15 as a material for simple clothing.
80 g / m 2 , as a wiper material 15-60 g /
m 2 . Further, the average fiber diameter of the fibers constituting the meltblown nonwoven fabric is preferably 10 μm or less.
When the average fiber diameter exceeds 10 μm, the porosity of the melt-blown nonwoven fabric increases and the dustproof property is remarkably reduced, so that it cannot be used as a material for simple clothing. Further, when it is used as a wiper material, the wiping performance tends to deteriorate, which is not preferable. A more preferable average fiber diameter of the fibers constituting the meltblown nonwoven fabric is 8 μm or less.
【００２０】また、本発明にて使用されるスパンボンド
不織布は、特に規定されるものではないが、溶融したポ
リマーをノズルより押し出し、これを高速吸引ガスによ
り吸引延伸した後、移動コンベア上に捕集してウェブと
し、さらに連続的に熱処理、絡合等を施すことによりシ
ートとする、いわゆるスパンボンド法により製造された
ものが好ましい。The spunbonded nonwoven fabric used in the present invention is not particularly limited, but the molten polymer is extruded from a nozzle, drawn and drawn by a high-speed suction gas, and then captured on a moving conveyor. A web manufactured by a so-called spunbond method, in which the web is collected and continuously heat-treated and entangled to form a sheet, is preferable.
【００２１】該スパンボンド不織布の目付量は特に限定
されるものではないが、１０〜１００ｇ／ｍ2 が好まし
い。目付が１０ｇ／ｍ2 よりも低い場合には、シートの
強度が低くなり、用途によっては使用することが難しい
場合がある。また、目付が１００ｇ／ｍ2 よりも高い場
合には、シート全体の重量が重く、嵩張り、柔軟性や着
心地に劣り、さらに製造コストも高くなる方向にあり好
ましくない。さらに好ましい該スパンボンド不織布の目
付量は、簡易衣料用材料としては２０〜８０ｇ／ｍ2 、
ワイパー用材料としては２０〜６０ｇ／ｍ2 である。該
スパンボンド不織布を構成する繊維の平均繊維径は１０
〜４０μｍであることが好ましい。The basis weight of the spunbonded nonwoven fabric is not particularly limited, but is preferably 10 to 100 g / m 2 . When the basis weight is lower than 10 g / m 2 , the strength of the sheet becomes low and it may be difficult to use depending on the application. On the other hand, when the fabric weight is higher than 100 g / m 2 , the weight of the entire sheet is heavy, bulky, inferior in flexibility and wearing comfort, and further, the manufacturing cost tends to be high, which is not preferable. A more preferable basis weight of the spunbonded nonwoven fabric is 20 to 80 g / m 2 as a material for simple clothing,
The material for the wiper is 20 to 60 g / m 2 . The average fiber diameter of the fibers constituting the spunbonded nonwoven fabric is 10
It is preferably ˜40 μm.
【００２２】平均繊維径が１０μｍよりも小さい場合に
は、シートにコシがなく柔軟になり過ぎて使用用途が限
られてくること、さらに生産安定性の面からも好ましく
ない方向である。また、平均繊維径が４０μｍを超える
場合には、柔軟性が低下し、シートが嵩張り、いわゆる
骨立ちが発生する場合があり、簡易衣料用材料、あるい
はワイパー用材料としては不向きとなってくる。さらに
好ましい該不織布を構成する繊維の平均繊維径は、簡易
衣料用材料としては１２〜２５μｍ、ワイパー用材料と
しては１２〜３０μｍである。When the average fiber diameter is smaller than 10 μm, the sheet is not elastic and is too flexible, which limits the use purpose and is also unfavorable from the viewpoint of production stability. If the average fiber diameter exceeds 40 μm, the flexibility may decrease, the sheet may become bulky, and so-called bone formation may occur, which makes it unsuitable as a material for simple clothing or a material for wipers. . More preferably, the average fiber diameter of the fibers constituting the non-woven fabric is 12 to 25 μm as a material for simple clothing and 12 to 30 μm as a material for wipers.
【００２３】本発明において供される不織布としては、
前記メルトブロー不織布の少なくとも片面に前記スパン
ボンド不織布を積層したシートを、部分的に熱接着し一
体化したものが好ましい。ここで、本発明におけるメル
トブロー不織布とスパンボンド不織布の部分的熱接着に
よる一体化とは、メルトブロー不織布を構成する繊維と
スパンボンド不織布を構成する繊維とが、部分的に溶融
し一体化していることを表すものである。本発明におけ
る該メルトブロー不織布を構成する繊維、および該スパ
ンボンド不織布を構成する繊維の平均繊維径は、それぞ
れの不織布の繊維断面を走査型電子顕微鏡により観察
し、測定した。The non-woven fabric provided in the present invention includes:
It is preferable that a sheet in which the spunbonded nonwoven fabric is laminated on at least one surface of the meltblown nonwoven fabric is partially heat-bonded and integrated. Here, the integration of the meltblown nonwoven fabric and the spunbonded nonwoven fabric by partial thermal bonding in the present invention means that the fibers constituting the meltblown nonwoven fabric and the fibers constituting the spunbonded nonwoven fabric are partially melted and integrated. It represents. The average fiber diameter of the fibers forming the meltblown nonwoven fabric and the fibers forming the spunbonded nonwoven fabric in the present invention was measured by observing the cross section of each nonwoven fabric with a scanning electron microscope.
【００２４】前記メルトブロー不織布の両面に前記スパ
ンボンド不織布を積層したシートを部分的熱接着により
一体化したものも、本発明の不織布として必要な風合
い、強度、防塵性は有しているが、製造コストの面か
ら、前記メルトブロー不織布の片面に前記スパンボンド
不織布を積層したシートを部分的熱接着により一体化さ
せたものの方がより好ましい。A sheet in which the spunbonded non-woven fabric is laminated on both sides of the melt-blown non-woven fabric by partial heat-bonding to integrate it has the texture, strength and dust resistance required for the non-woven fabric of the present invention. From the viewpoint of cost, it is more preferable that a sheet obtained by laminating the spunbonded nonwoven fabric on one surface of the meltblown nonwoven fabric is integrated by partial thermal bonding.
【００２５】本発明における部分的熱接着の面積は、簡
易衣料用不織布さらにはワイパー用不織布として十分な
柔軟性、強度、防塵性等を満たしていれば特に限定され
るものではないが、５〜４０％の範囲であることが好ま
しい。該熱接着面積が５％より低い場合は、前記メルト
ブロー不織布と前記スパンボンド不織布の層間が剥離し
やすくなってきて、さらに不織布の表面に毛羽立ちが発
生しやすくなったり、また接着したシートの強度が低く
なる方向であるため好ましくない。また、該熱接着面積
が４０％を超えると、前記メルトブロー不織布と前記ス
パンボンド不織布の層間剥離は発生しにくく、強度も高
くなるが、一方で、接着したシートが硬くなる方向であ
るので、簡易衣料用の不織布としては風合いの点で好ま
しくない方向であり、またワイパー用の不織布としても
柔軟性の点で好ましくない方向である。さらに好ましい
該接着面積は１０〜３０％の範囲である。The area of partial heat-bonding in the present invention is not particularly limited as long as it satisfies sufficient flexibility, strength, dustproofness and the like as a nonwoven fabric for simple clothing and further as a nonwoven fabric for wipers. It is preferably in the range of 40%. When the heat-bonded area is less than 5%, the layer between the melt-blown nonwoven fabric and the spunbonded nonwoven fabric is likely to be peeled off, fluffing is likely to occur on the surface of the nonwoven fabric, and the strength of the bonded sheet is increased. It is not preferable because it tends to decrease. Further, when the heat-bonded area exceeds 40%, delamination of the meltblown nonwoven fabric and the spunbonded nonwoven fabric is less likely to occur and the strength is increased, but on the other hand, the bonded sheet tends to be hard, which is simple. The nonwoven fabric for clothing is unfavorable in terms of texture, and the nonwoven fabric for wipers is also unfavorable in terms of flexibility. The more preferable adhesion area is in the range of 10 to 30%.
【００２６】ここで、不織布を部分的に熱接着させる方
法は、上記熱接着面積を満たしていれば、特別に限定さ
れるものではないが、加工の簡便さから、熱エンボスロ
ールでニップすることによる接着あるいは超音波発生装
置による接着が好ましい。The method of partially heat-bonding the non-woven fabric is not particularly limited as long as the above-mentioned heat-bonding area is satisfied, but nipping with a hot embossing roll is performed for ease of processing. Adhesion by means of or by an ultrasonic generator is preferred.
【００２７】本発明にて使用されるメルトブロー不織布
およびスパンボンド不織布を構成する繊維は、生分解性
を有することが必要である。The fibers constituting the meltblown nonwoven fabric and the spunbonded nonwoven fabric used in the present invention are required to have biodegradability.
【００２８】さらに該メルトブロー不織布および該スパ
ンボンド不織布を構成する生分解性繊維は、ポリ乳酸系
樹脂からなることが最も好ましい。簡易衣料用不織布や
ワイパー用不織布は通常１回から数回の使用後廃棄処分
されるため、その処分量は膨大なものとなる。Further, the biodegradable fibers constituting the meltblown nonwoven fabric and the spunbonded nonwoven fabric are most preferably made of polylactic acid resin. The non-woven fabric for simple clothing and the non-woven fabric for wipers are usually discarded after being used once or several times, and the amount of disposal is enormous.
【００２９】生分解性を有さないポリエステル、ポリプ
ロピレン、ナイロン等を原料として使用した場合は、焼
却あるいは埋め立て処分が必要であるが、焼却処理をし
た場合、焼却時の発熱量が高いため焼却炉を傷めるとい
う問題点があり、また埋め立て処分をした場合には、こ
れら原料が化学的に安定なため、長期間に渡って形状を
保ち続けてしまうという環境上の問題点がある。When non-biodegradable polyester, polypropylene, nylon or the like is used as a raw material, incineration or landfill disposal is required, but when incinerated, the calorific value at the time of incineration is high, so the incinerator However, there is an environmental problem in that, when these materials are disposed of in a landfill, these raw materials are chemically stable, and therefore they retain their shape for a long period of time.
【００３０】本発明にて供される不織布においては、ポ
リ乳酸などの生分解性を有する樹脂を原料として使用す
ることにより、簡易衣料用材料やワイパー用材料として
使用した後、焼却処分の必要はなく、埋め立て等の処分
後、化学的に分解され自然環境を汚染することがない。In the nonwoven fabric provided by the present invention, by using a biodegradable resin such as polylactic acid as a raw material, it is not necessary to incinerate it after using it as a material for simple clothing or a material for wipers. None, it will not be chemically decomposed and pollute the natural environment after disposal such as landfill.
【００３１】[0031]
【実施例】以下、本発明をさらに実施例により詳細に説
明する。実施例において、得られたシートが簡易衣料用
不織布、あるいはワイパー用不織布として適当なシート
特性を有しているかは、シートの引張強度と引裂強度、
風合いおよび防塵性から評価した。また、実施例におい
て、得られたシートが簡易衣料用不織布あるいはワイパ
ー用不織布として使用後、廃棄された際に、シートの形
状を保ったまま残存し、自然環境を汚染するかは、不織
布の生分解性から評価した。EXAMPLES The present invention will now be described in more detail with reference to Examples. In the example, whether the obtained sheet has suitable sheet characteristics as a nonwoven fabric for simple clothing or a nonwoven fabric for wipers, the tensile strength and tear strength of the sheet,
The texture and dust resistance were evaluated. In addition, in the examples, after the obtained sheet is used as a non-woven fabric for simple clothing or a non-woven fabric for wipers, when it is discarded, the sheet remains to retain its shape and pollutes the natural environment. It was evaluated from the degradability.
【００３２】また不織布を構成する繊維の平均繊維径
は、株式会社日立製作所製Ｓ−５１０形走査型電子顕微
鏡により４００倍の倍率で繊維断面の観察を行い、任意
の繊維５０本の断面直径の平均値からそれぞれ算出し
た。The average fiber diameter of the fibers constituting the non-woven fabric was measured by observing the fiber cross section at a magnification of 400 with a scanning electron microscope S-510 manufactured by Hitachi, Ltd., and measuring the cross-sectional diameter of 50 arbitrary fibers. Each was calculated from the average value.
【００３３】それぞれの評価結果は表１に示し、強度、
風合い、防塵性および生分解性の全ての項目について合
格（○印）したものを、簡易衣料用不織布あるいはワイ
パー用不織布として適していると判定した。各評価の方
法は下記の通りである。
（１）引張強度：不織布の長さ方向の引張強度をＪＩＳ
Ｌ １０９６に基づき測定し、８０Ｎ／５０ｍｍ以上
のものは○、８０Ｎ／５０ｍｍ未満のものは×とした。
（２）引裂強度：不織布の長さ方向の引裂強度をＪＩＳ
Ｌ １０９６のトラペゾイド法に基づき測定し、５Ｎ
以上のものは○、５Ｎ未満のものは×とした。
（３）風合い：５名のモニターにより官能評価を行っ
た。モニターは不織布シート表面の手触り感、シートの
柔軟性を、次の基準により評価し、１５点以上のものは
○、１５点未満のものは×とした。The respective evaluation results are shown in Table 1, and the strength,
Those that passed (○) for all the items of texture, dust resistance and biodegradability were judged to be suitable as a nonwoven fabric for simple clothing or a nonwoven fabric for wipers. The method of each evaluation is as follows. (1) Tensile strength: The tensile strength of the nonwoven fabric in the longitudinal direction is defined by JIS
It was measured based on L 1096, and those having 80 N / 50 mm or more were evaluated as ◯, and those less than 80 N / 50 mm were evaluated as x. (2) Tear strength: The tear strength of the nonwoven fabric in the longitudinal direction is defined by JIS
Measured based on the trapezoid method of L 1096, 5N
The above-mentioned items were marked with ◯, and those less than 5N were marked with x. (3) Texture: Sensory evaluation was performed by 5 monitors. The monitor evaluated the feel of the surface of the non-woven fabric sheet and the flexibility of the sheet according to the following criteria.
【００３４】４点：シート表面の手触り感が優れ、シー
トの柔軟性も優れている。4 points: The feel of the surface of the sheet is excellent, and the flexibility of the sheet is also excellent.
【００３５】３点：シート表面の手触り感は優れている
が、シートの柔軟性は普通である、あるいは、シート表
面の手触り感は普通であるが、シートの柔軟性は優れて
いる。3 points: The feel of the sheet surface is excellent, but the flexibility of the sheet is normal, or the feel of the sheet surface is normal, but the flexibility of the sheet is excellent.
【００３６】２点：シート表面の手触り感は普通であ
り、シートの柔軟性も普通である。2 points: The feel of the surface of the sheet is normal, and the flexibility of the sheet is also normal.
【００３７】１点：シート表面の手触り感は普通である
が、シートの柔軟性は劣る、あるいは、シート表面の手
触り感は劣るが、シートの柔軟性は普通である。1 point: The feel of the sheet surface is normal, but the flexibility of the sheet is poor, or the feel of the sheet surface is poor, but the flexibility of the sheet is normal.
【００３８】０点：シート表面の手触り感が劣り、シー
トの柔軟性も劣る。
（４）防塵性：風速３．０ｍ／ｍｉｎの条件で、不織布
シートの厚さ方向に直径０．３μｍのポリスチレン粒子
を通過させ、その際の捕集効率を測定した。捕集効率は
次式より算出し、３０％以上の捕集効率を示したものを
○、３０％未満のものを×とした。
捕集効率（％）＝｛１−（フィルター下流の粒子数／フ
ィルター上流の粒子数）｝×１００
（５）生分解性：温度５８℃、通気量４０ｍｌ／ｍｉｎ
の条件のコンポスト中に不織布シートを埋没させ、１年
以内に生分解したものを○、１年たっても生分解しなか
ったものを×と判定した。
実施例１
平均繊維径が５μｍ、目付が３０ｇ／ｍ2 で、ポリ乳酸
樹脂を原料としたメルトブロー不織布の片面に、平均繊
維径が１５μｍ、目付が７０ｇ／ｍ2 で、ポリ乳酸樹脂
を原料としたスパンボンド不織布を、熱接着面積が２０
％となるようエンボスロールを用いて超音波接着装置に
より接着して一体化させシートを得た。0 point: The feel of the surface of the sheet is poor, and the flexibility of the sheet is poor. (4) Dustproofness: Under the condition of a wind speed of 3.0 m / min, polystyrene particles having a diameter of 0.3 μm were passed through the nonwoven fabric sheet in the thickness direction, and the collection efficiency at that time was measured. The collection efficiency was calculated by the following formula, and those showing a collection efficiency of 30% or more were evaluated as ◯, and those less than 30% were evaluated as x. Collection efficiency (%) = {1- (number of particles downstream of filter / number of particles upstream of filter)} × 100 (5) Biodegradability: temperature 58 ° C, aeration rate 40 ml / min
The non-woven fabric sheet was buried in the compost under the conditions of No. 1 and biodegraded within 1 year was evaluated as ○, and those not biodegraded after 1 year were evaluated as ×. Example 1 The average fiber diameter was 5 μm, the basis weight was 30 g / m 2 , and the average fiber diameter was 15 μm, the basis weight was 70 g / m 2 , and the polylactic acid resin was used as the raw material on one side of a melt-blown nonwoven fabric made from the polylactic acid resin. The spunbonded non-woven fabric has a heat-bonded area of 20
% By using an ultrasonic bonding device using an embossing roll to integrate and obtain a sheet.
【００３９】得られたシートの評価結果は表１の通りで
あり、簡易衣料用不織布あるいはワイパー用不織布とし
て適したものであった。
比較例１
平均繊維径が５μｍ、目付が３０ｇ／ｍ2 で、ポリプロ
ピレン樹脂を原料としたメルトブロー不織布の片面に、
平均繊維径が５０μｍ、目付が１５０ｇ／ｍ2で、ポリ
プロピレン樹脂を原料としたスパンボンド不織布を、熱
接着面積が５５％となるようエンボスロールを用いて超
音波接着装置により接着して一体化させシートを得た。The evaluation results of the obtained sheet are shown in Table 1 and were suitable as a nonwoven fabric for simple clothing or a nonwoven fabric for wipers. Comparative Example 1 An average fiber diameter of 5 μm, a basis weight of 30 g / m 2 , and one side of a melt blown nonwoven fabric made of polypropylene resin
Spunbonded non-woven fabrics with an average fiber diameter of 50 μm and a basis weight of 150 g / m 2 and made of polypropylene resin as the raw material are bonded and integrated by an ultrasonic bonding device using an embossing roll so that the thermal bonding area becomes 55%. Got the sheet.
【００４０】得られたシートの評価結果は表１の通りで
あるが、シート強度と防塵性は優れていたが、シートに
柔軟性がなく、風合いが堅く、さらに生分解性もなく簡
易衣料用不織布あるいはワイパー用不織布としては不適
当なものであった。
比較例２
平均繊維径が１５μｍ、目付が３０ｇ／ｍ2 で、ポリ乳
酸樹脂を原料としたメルトブロー不織布の片面に、平均
繊維径が２０μｍ、目付が７０ｇ／ｍ2 で、ポリプロピ
レン樹脂を原料としたスパンボンド不織布を、熱接着面
積が２０％となるようエンボスロールを用いて超音波接
着装置により接着して一体化させシートを得た。The evaluation results of the obtained sheet are as shown in Table 1. It was found that the sheet had excellent strength and dust resistance, but the sheet was not flexible, had a soft texture, and had no biodegradability. It was unsuitable as a nonwoven fabric or a nonwoven fabric for wipers. Comparative Example 2 The average fiber diameter was 15 μm, the basis weight was 30 g / m 2 , and the average fiber diameter was 20 μm and the basis weight was 70 g / m 2 on one side of a melt-blown nonwoven fabric made from a polylactic acid resin. The spunbonded nonwoven fabric was bonded by an ultrasonic bonding device using an embossing roll so that the heat bonded area would be 20%, and integrated to obtain a sheet.
【００４１】得られたシートの評価結果は表１の通りで
あるが、防塵性に劣り、また生分解性もないため簡易衣
料用不織布あるいはワイパー用不織布としては不適当な
ものであった。
実施例２
平均繊維径が８μｍ、目付が４０ｇ／ｍ2 で、ポリ乳酸
樹脂を原料としたメルトブロー不織布の片面に、平均繊
維径が２５μｍ、目付が５０ｇ／ｍ2 で、ポリ乳酸樹脂
を原料としたスパンボンド不織布を、熱接着面積が１８
％となるようエンボスロールを用いて超音波接着装置に
より接着して一体化させシートを得た。The evaluation results of the obtained sheet are shown in Table 1. However, the sheet was inferior in dustproof property and was not biodegradable, so that it was unsuitable as a nonwoven fabric for simple clothing or a nonwoven fabric for wipers. Example 2 The average fiber diameter was 8 μm, the basis weight was 40 g / m 2 , and the average fiber diameter was 25 μm and the basis weight was 50 g / m 2 , and the polylactic acid resin was used as the raw material on one side of the melt-blown nonwoven fabric made from the polylactic acid resin. The spunbonded non-woven fabric has a heat bonded area of 18
% By using an ultrasonic bonding device using an embossing roll to integrate and obtain a sheet.
【００４２】得られたシートの評価結果は表１の通りで
あり、簡易衣料用不織布あるいはワイパー用不織布とし
て適したものであった。
比較例３
平均繊維径が８μｍ、目付が４０ｇ／ｍ2 で、ポリプロ
ピレン樹脂を原料としたメルトブロー不織布の片面に、
平均繊維径が５０μｍ、目付が１４０ｇ／ｍ2で、ポリ
エステル樹脂を原料としたスパンボンド不織布を、熱接
着面積が５０％となるようエンボスロールを用いて超音
波接着装置により接着して一体化させシートを得た。The evaluation results of the obtained sheet are shown in Table 1 and were suitable as a nonwoven fabric for simple clothing or a nonwoven fabric for wipers. Comparative Example 3 The average fiber diameter was 8 μm, the basis weight was 40 g / m 2 , and one side of a meltblown nonwoven fabric made of polypropylene resin was used.
Spunbonded non-woven fabric with an average fiber diameter of 50 μm and a basis weight of 140 g / m 2 and made of polyester resin as a raw material is bonded and integrated by an ultrasonic bonding device using an embossing roll so that the thermal bonding area becomes 50%. Got the sheet.
【００４３】得られたシートの評価結果は表１の通りで
あるが、シートに柔軟性がなく、風合いが堅く、さらに
生分解性もなく簡易衣料用不織布あるいはワイパー用不
織布としては不適当なものであった。
比較例４
平均繊維径が１５μｍ、目付が４０ｇ／ｍ2 で、ポリプ
ロピレン樹脂を原料としたメルトブロー不織布の片面
に、平均繊維径が２５μｍ、目付が５０ｇ／ｍ2で、ポ
リ乳酸樹脂を原料としたスパンボンド不織布を、熱接着
面積が１８％となるようエンボスロールを用いて超音波
接着装置により接着して一体化させシートを得た。The evaluation results of the obtained sheet are as shown in Table 1. However, the sheet is not flexible, has a hard texture, and is not biodegradable, and is unsuitable as a nonwoven fabric for simple clothing or a nonwoven fabric for wipers. Met. Comparative Example 4 Polylactic acid resin having an average fiber diameter of 15 μm and a basis weight of 50 g / m 2 on one side of a melt-blown nonwoven fabric made of polypropylene resin having an average fiber diameter of 15 μm and a basis weight of 40 g / m 2 . The spunbonded non-woven fabric was bonded and integrated by an ultrasonic bonding device using an embossing roll so that the heat bonded area was 18% to obtain a sheet.
【００４４】得られたシートの評価結果は、表１の通り
であるが、防塵性に劣り、また生分解性もないため簡易
衣料用不織布あるいはワイパー用不織布としては不適当
なものであった。
比較例５
平均繊維径が８μｍ、目付が４０ｇ／ｍ2 で、ポリプロ
ピレン樹脂を原料としたメルトブロー不織布の片面に、
平均繊維径が２０μｍ、目付が５ｇ／ｍ2 で、ポリプロ
ピレン樹脂を原料としたスパンボンド不織布を、熱接着
面積が１８％となるようエンボスロールを用いて超音波
接着装置により接着して一体化させシートを得た。The evaluation results of the obtained sheet are as shown in Table 1, but they were unsuitable as a nonwoven fabric for simple clothing or a nonwoven fabric for wipers because they were inferior in dustproof property and did not have biodegradability. Comparative Example 5 The average fiber diameter was 8 μm, the basis weight was 40 g / m 2 , and one side of a melt blown nonwoven fabric made of polypropylene resin was used.
Spunbonded non-woven fabrics with an average fiber diameter of 20 μm and a basis weight of 5 g / m 2 and made of polypropylene resin as the raw material are bonded and integrated by an ultrasonic bonding device using an embossing roll so that the thermal bonding area becomes 18%. Got the sheet.
【００４５】得られたシートの評価結果は表１の通りで
あるが、風合い、防塵性は良好であったが、生分解性が
なく、またシートの引張強度が低いため簡易衣料用不織
布あるいはワイパー用不織布としては不適当なものであ
った。さらにシートの引裂強力が低いため、ワイパー用
不織布として使用した場合、シートが裂けやすくワイパ
ー材料としては不適当なものであった。The evaluation results of the obtained sheet are as shown in Table 1. It was found that the texture and the dust resistance were good, but the sheet was not biodegradable and the sheet had low tensile strength. It was unsuitable as a non-woven fabric. Further, since the tear strength of the sheet is low, when used as a nonwoven fabric for a wiper, the sheet is liable to tear and is unsuitable as a wiper material.
【００４６】[0046]
【表１】 [Table 1]
【００４７】[0047]
【発明の効果】本発明によれば、生分解性を有する数種
類の不織布を積層し、部分的に熱圧着させることによ
り、簡易衣料用不織布あるいはワイパー用不織布として
十分な強度、風合い、柔軟性、防塵性を有するシートを
供することができる。According to the present invention, by laminating several kinds of non-woven fabrics having biodegradability and partially thermocompressing them, sufficient strength, texture, flexibility, as a non-woven fabric for simple clothing or a non-woven fabric for wipers, It is possible to provide a sheet having a dustproof property.
【００４８】また、本発明にかかる不織布は、原料とし
て生分解性を有する樹脂を使用しているため、簡易衣料
あるいはワイパーとしての使用後廃棄しても自然環境を
汚染することがない。Further, since the nonwoven fabric according to the present invention uses a biodegradable resin as a raw material, it does not pollute the natural environment even if it is discarded after being used as simple clothing or wiper.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ａ４１Ｄ 31/00 ５０２ Ａ４１Ｄ 31/00 ５０２Ｅ ５０３ ５０３Ｅ Ａ４７Ｌ 13/16 Ａ４７Ｌ 13/16 Ａ Ｂ３２Ｂ 5/26 Ｂ３２Ｂ 5/26 Ｄ０４Ｈ 3/16 Ｄ０４Ｈ 3/16 Ｆターム(参考） 3B030 AA01 AB01 3B074 AA08 AB01 BB01 4F100 AK41A AK41B AK41C BA02 BA03 BA06 BA07 BA10B BA10C BA32 DG01A DG01B DG01C DG15A DG15B DG15C GB32 GB72 JC00A JC00B JC00C JK01 YY00A YY00B YY00C 4L047 AB07 BA08 BA23 CA19 CC01 CC16 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) A41D 31/00 502 A41D 31/00 502E 503 503E A47L 13/16 A47L 13/16 A B32B 5/26 B32B 5 / 26 D04H 3/16 D04H 3/16 F-term (reference) 3B030 AA01 AB01 3B074 AA08 AB01 BB01 4F100 AK41A AK41B AK41C BA02 BA03 BA06 BA07 BA10B BA10C BA32 DG01A DG01B DG01C DG15A DG15B DG15C GB32 GB72 JC00A JC00B JC00C JK01 YY00A YY00B YY00C 4L047 AB07 BA08 BA23 CA19 CC01 CC16
Claims (6)
トブロー不織布の少なくとも片面に、生分解性を有する
繊維から構成されるスパンボンド不織布が積層されたシ
ートが部分的熱接着により一体化されてなることを特徴
とする不織布。1. A sheet in which a spunbonded non-woven fabric composed of biodegradable fibers is laminated on at least one surface of a melt-blown non-woven fabric composed of biodegradable fibers by partial thermal bonding. Non-woven fabric characterized by being.
ド不織布を構成する繊維が、ポリ乳酸系樹脂からなるこ
とを特徴とする請求項１記載の不織布。2. The non-woven fabric according to claim 1, wherein fibers constituting the melt-blown non-woven fabric and the spun-bonded non-woven fabric are made of polylactic acid resin.
０ｇ／ｍ2 で構成繊維の平均繊維径が１０μｍ以下であ
り、かつ、該スパンボンド不織布の目付が１０〜１００
ｇ／ｍ2 で構成繊維の平均繊維径が１０〜４０μｍであ
ることを特徴とする請求項１または２記載の不織布。3. The basis weight of the meltblown nonwoven fabric is 10 to 10.
The average fiber diameter of the constituent fibers is 0 μm or less at 0 g / m 2 , and the basis weight of the spunbonded nonwoven fabric is 10 to 100.
The non-woven fabric according to claim 1 or 2, wherein the average fiber diameter of the constituent fibers is 10 to 40 µm in g / m 2 .
織布の熱接着面積が５〜４０％の範囲であることを特徴
とする請求項１、２または３記載の不織布。4. The non-woven fabric according to claim 1, 2 or 3, wherein the heat-bonded area of the melt-blown non-woven fabric and the spun-bonded non-woven fabric is in the range of 5 to 40%.
用いて形成されていることを特徴とする簡易衣料。5. A simple garment formed by using the non-woven fabric according to claim 1, 2, 3, or 4.
用いて形成されていることを特徴とするワイパー。6. A wiper formed by using the nonwoven fabric according to claim 1, 2, 3 or 4.