JP2003052254A - Weeding sheet - Google Patents
Weeding sheetInfo
- Publication number
- JP2003052254A JP2003052254A JP2001245543A JP2001245543A JP2003052254A JP 2003052254 A JP2003052254 A JP 2003052254A JP 2001245543 A JP2001245543 A JP 2001245543A JP 2001245543 A JP2001245543 A JP 2001245543A JP 2003052254 A JP2003052254 A JP 2003052254A
- Authority
- JP
- Japan
- Prior art keywords
- cloth
- sheet according
- weeding sheet
- weeding
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、除草シート、さら
に詳しくは、強度が高く、耐久性に優れ、除草効果の高
い除草シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a weeding sheet, and more particularly to a weeding sheet having high strength, excellent durability and a high weeding effect.
【０００２】[0002]
【従来の技術】従来、河川の土手、田畑の畦畔、あるい
は、鉄道、道路の盛土法面は、土砂の流失が多くその防
止が必要となる。また、雑草が繁茂すると病害虫の発生
のおそれが生じることから、頻繁に刈り取りを必要と
し、あるいは、雑草の防止措置が必要となっている。し
かし、草の刈り取りには労力を必要とし、また、除草剤
の散布は環境破壊の面から好ましいものでない。2. Description of the Related Art Conventionally, there is a lot of sediment loss on the bank of rivers, ridges of fields, or embankment slopes of railways and roads, and it is necessary to prevent it. In addition, since weeds may cause pests to grow, weeds need to be frequently cut or weed prevention measures must be taken. However, cutting grass is labor intensive, and spraying herbicides is not preferable in terms of environmental damage.
【０００３】このような課題を解決する方法として、合
成繊維長繊維からなる不織布を敷設することが提案され
ている（特公平４−５２７２７）。As a method for solving such a problem, it has been proposed to lay a nonwoven fabric made of synthetic long fibers (Japanese Patent Publication No. 4-52727).
【０００４】かかるシートを敷設して雑草の繁茂を防止
するためには、除草シートとしては各種の性能が要求さ
れ、例えば、その上を歩行するためには機械的強度が要
求され、また、耐蝕性に優れ、耐久性のよいものである
ことも必要となる。さらに、雑草防止のためには光線の
透過率が低いことが要求されると共に、日光の反射によ
って環境に悪影響を与えないことも必要となる。In order to prevent weeds from growing by laying such a sheet, the weeding sheet is required to have various performances. For example, walking on it requires mechanical strength and corrosion resistance. It is also necessary to have excellent durability and durability. Furthermore, in order to prevent weeds, low light transmittance is required, and it is also necessary that the reflection of sunlight does not adversely affect the environment.
【０００５】また、除草シートを法面に敷設した場合、
強風によって吹き上げられたり、吸い上げられたり、風
の力のために耐久性に問題が生じる。これに耐えるよう
にするためには、除草シートの機械的強度を高くすると
共にある程度の通気性を与えることが必要となる。When the weeding sheet is laid on the slope,
It is blown up by strong winds, sucked up, and wind power causes durability problems. In order to withstand this, it is necessary to increase the mechanical strength of the weeding sheet and to give it some breathability.
【０００６】本発明者の知るところでは、従来の除草シ
ートでは、かかる要請を全て満たすものとしては不充分
であった。To the inventor of the present invention, the conventional weeding sheets were not sufficient to satisfy all the above requirements.
【０００７】[0007]
【発明が解決しようとする課題】本発明は、機械的強
度、耐久性に優れ、光線の透過率が低く、従って除草効
果が高く、また、日光の反射による環境阻害のない除草
シートを提供するものである。DISCLOSURE OF THE INVENTION The present invention provides a weeding sheet which is excellent in mechanical strength and durability, has a low light ray transmittance, and therefore has a high weeding effect, and is free from environmental inhibition due to reflection of sunlight. It is a thing.
【０００８】[0008]
【課題を解決するための手段】本発明は、かかる目的を
達成するために鋭意検討した結果なされたもので、具体
的には、着色された合成樹脂を一軸延伸して形成された
延伸糸によって形成され、光透過率が１０％未満、質量
が５０〜５００ｇ／ｍ2の布状体からなることを特徴と
する除草シート、延伸糸がフラットヤーンからなる上記
の除草シート、延伸糸が異種組成物からなる積層フラッ
トヤーンからなる上記の除草シート、延伸糸が縦方向に
小さな切れ目が多数形成されたスプリットヤーンからな
る上記の除草シート、及び、延伸糸が艶消処理されてな
る上記の除草シートを提供するものである。Means for Solving the Problems The present invention has been made as a result of extensive studies to achieve such an object. Specifically, a drawn yarn formed by uniaxially drawing a colored synthetic resin is used. A herbicidal sheet formed of a cloth-like material having a light transmittance of less than 10% and a mass of 50 to 500 g / m 2 , the above-mentioned herbicidal sheet in which the drawn yarn is a flat yarn, and the drawn yarn has a different composition. The above-mentioned weeding sheet made of a laminated flat yarn made of a material, the above-mentioned weeding sheet made of a split yarn in which a plurality of small cuts are formed in the longitudinal direction of the drawn yarn, and the above-mentioned weeding sheet obtained by matting the drawn yarn. Is provided.
【０００９】また、本発明は、布状体が熱刃によってヒ
ートカットされることによりほつれ防止されてなる上記
の除草シート、布状体がタックインされることによりほ
つれ防止されてなる上記の除草シート、布状体が溶融熱
可塑性樹脂を積層することによりほつれ防止されてなる
上記の除草シート、布状体がホットメルト剤を塗布する
ことによりほつれ防止されてなる上記の除草シート、布
状体が水系接着剤を塗布することによりほつれ防止され
てなる上記の除草シート、及び、布状体の縦横の延伸糸
が熱融着されることによりほつれ防止されてなる上記の
除草シートを提供するものである。The present invention also relates to the above weeding sheet in which the cloth-like body is heat-cut by a hot blade to prevent fraying, and the above-mentioned weeding sheet in which the cloth-like body is tucked in to prevent fraying. The above-mentioned weeding sheet in which the cloth-like body is prevented from fraying by laminating a molten thermoplastic resin, the above-mentioned weeding sheet in which the cloth-like body is prevented from fraying by applying a hot-melting agent, and the cloth-like body is To provide the above-mentioned herbicidal sheet which is prevented from fraying by applying an aqueous adhesive, and the above-mentioned herbicidal sheet which is prevented from fraying by heat fusion of longitudinal and transverse stretched yarns of a cloth-like body. is there.
【００１０】さらに、本発明は、布状体に不織布が積層
されてなる上記の除草シート、布状体に所定の間隔をお
いて色彩の異なる延伸糸が織り込まれてなる上記の除草
シート、布状体表面に所定の間隔をおいてラインマーク
が印刷されてなる上記の除草シート、複数の布状体が所
定の重ね代をもって敷設されてなる上記の除草シート、
及び、布状体が合成樹脂製杭材で係止されてなる上記の
除草シートを提供するものである。The present invention further relates to the above weeding sheet in which a non-woven fabric is laminated on a cloth, the above weeding sheet and cloth in which stretched yarns of different colors are woven into the cloth at predetermined intervals. The above-mentioned weeding sheet in which line marks are printed at predetermined intervals on the surface of the sheet, the above-mentioned weeding sheet in which a plurality of cloth-like articles are laid with a predetermined overlap margin,
Further, the present invention provides the above weeding sheet in which the cloth-like body is locked by a synthetic resin pile material.
【００１１】[0011]
【発明の実施の形態】本発明の除草シート１は、図１に
示すように、着色された合成樹脂を一軸延伸して形成さ
れた延伸糸２を布状として形成される。BEST MODE FOR CARRYING OUT THE INVENTION As shown in FIG. 1, a herbicidal sheet 1 of the present invention is formed with a stretched yarn 2 formed by uniaxially stretching a colored synthetic resin as a cloth.
【００１２】延伸糸２としては、延伸効果の優れた合成
樹脂が用いられ、一般には、高密度ポリエチレン、ポリ
プロピレン、ポリエステル、ポリアミド等を用いること
ができる。As the drawn yarn 2, a synthetic resin having an excellent drawing effect is used, and in general, high density polyethylene, polypropylene, polyester, polyamide or the like can be used.
【００１３】本発明において除草シートを構成する延伸
糸２とは、除草シートを構成し得る長尺状物を広く意味
し、フィルム状体、紐状体、帯状体、モノフィラメント
等の線条体を含むものであり、これらは撚りが付与され
たものでもまた撚りのないものであってもよい。In the present invention, the drawn yarn 2 constituting the weeding sheet broadly means a long object which can constitute the weeding sheet, and includes filaments such as film, string, strip and monofilament. It is included, and these may be twisted or untwisted.
【００１４】延伸糸２の構造はいかなるものであっても
よく、例えば、図３（Ａ）に示すように、合成樹脂フィ
ルムを所定の幅にスリットして一軸延伸することによっ
てテープ状として用いることができ、また、図３（Ｂ）
に示すように、テープ状体に多数の切れ目５、５を入れ
たスプリットヤーンを用いることもできる。さらに、図
３（Ｃ）に示すように、テープ状体に極細の縦方向リブ
６、６を設けることもでき、リブを設けることによって
太陽の反射光が散乱され、環境への影響を低減すること
ができる。The drawn yarn 2 may have any structure. For example, as shown in FIG. 3A, a synthetic resin film is slit into a predetermined width and uniaxially stretched to be used as a tape. Can be made, and also FIG. 3 (B)
It is also possible to use a split yarn in which a large number of cuts 5 and 5 are formed in a tape-shaped body as shown in FIG. Further, as shown in FIG. 3C, the tape-shaped body may be provided with extremely fine vertical ribs 6, 6, and by providing the ribs, the reflected light of the sun is scattered and the influence on the environment is reduced. be able to.
【００１５】また、その他、丸型、長球状、方形、多角
形、その他異型体とすることができ、さらに、異種樹脂
の混合物を線条に押出し成形し、その樹脂間を***せし
めてフィブリル化したダンラインを用いることによって
しなやかさを上げることもできる。In addition, other shapes such as a round shape, an oblong shape, a square shape, a polygonal shape, and other irregular shapes can be obtained. Furthermore, a mixture of different resins is extruded into filaments, and the resins are divided to form fibrils. You can also increase suppleness by using this Dunline.
【００１６】一軸延伸された延伸糸２は、一本を単独で
織布として使用することも可能であり、また、数本を束
ねて用いることも可能である。The uniaxially drawn drawn yarn 2 can be used alone as a woven fabric, or can be used by bundling several yarns.
【００１７】延伸糸２は、図４（Ａ）に示すように、単
層であってもよく、また、図４（Ｂ）、図４（Ｃ）に示
すように、基層７の片面、又は両面に表面層８を形成す
ることができ、表面層８は、接合層、あるいは艶消層と
して機能させることができる。更に表面層８は、図４
（Ｄ）に示すようにシースコア構造、図４（Ｅ）に示す
ようにサイドバイサイド方式とすることも可能である。The drawn yarn 2 may be a single layer as shown in FIG. 4 (A), or one side of the base layer 7 as shown in FIGS. 4 (B) and 4 (C), or The surface layer 8 can be formed on both surfaces, and the surface layer 8 can function as a bonding layer or a matting layer. Further, the surface layer 8 is shown in FIG.
It is also possible to adopt a sheath core structure as shown in (D) and a side-by-side system as shown in FIG. 4 (E).
【００１８】接合層として機能する表面層８を設けたと
きは、延伸糸２が布状とされた後、延伸糸２間を接合す
ることができる。接合層として機能する表面層８として
用いられる合成樹脂とはしては、ポリエチレン、ポリプ
ロピレン、エチレン・プロピレン共重合体等のポリオレ
フィン、ポリエチレンテレフタレート、ポリブチレンテ
レフタレート等のポリエステル、ナイロン６、ナイロン
６６のポリアミド等を挙げることができ、基層７の合成
樹脂との関係で基層より低融点の合成樹脂が選択され
る。When the surface layer 8 functioning as a joining layer is provided, the drawn yarns 2 can be joined together after the drawn yarns 2 are made into a cloth shape. Examples of the synthetic resin used as the surface layer 8 functioning as a bonding layer include polyolefins such as polyethylene, polypropylene and ethylene-propylene copolymer, polyesters such as polyethylene terephthalate and polybutylene terephthalate, polyamides such as nylon 6 and nylon 66. Etc., and a synthetic resin having a lower melting point than that of the base layer is selected in relation to the synthetic resin of the base layer 7.
【００１９】本発明においては、延伸糸２を構成する基
層７又は表面層８、あるいはその両者には顔料を添加し
て着色することによって光透過率が調整されるところに
特徴を有する。着色の色彩は、本発明を制限するもので
はないが、環境を損なわないように、落ち着いた色合い
とすることが好ましく、黒、緑、茶等とすることが望ま
しい。The present invention is characterized in that the light transmittance is adjusted by adding a pigment to the base layer 7 and / or the surface layer 8 constituting the drawn yarn 2 or both of them. Although the coloring color is not a limitation of the present invention, it is preferably a calm color so as not to damage the environment, and is preferably black, green, brown or the like.
【００２０】さらに、延伸糸２には無機充填材を添加す
ることができ、無機充填材を添加することによって艶消
しができ、太陽光の反射を弱めることができる。無機充
填材としては、タルク、カーボンブラック、グラファイ
ト、二酸化チタン、シリカ、マイカ、炭酸カルシウウ
ム、硫酸カルシウム、炭酸バリウム、炭酸マグネシウ
ム、硫酸マグネシウム、硫酸バリウム、アルミナ、カオ
リン、炭化ケイ素、金属粉末等を用いることができる。
無機充填材の添加は、延伸糸２全体であってもよく、ま
た、前述のように、表面を形成する表面層８に添加する
こともできる。Further, an inorganic filler can be added to the drawn yarn 2, and by adding the inorganic filler, it can be matted and the reflection of sunlight can be weakened. As the inorganic filler, talc, carbon black, graphite, titanium dioxide, silica, mica, calcium carbonate, calcium sulfate, barium carbonate, magnesium carbonate, magnesium sulfate, barium sulfate, alumina, kaolin, silicon carbide, metal powder or the like is used. be able to.
The inorganic filler may be added to the entire drawn yarn 2 or, as described above, may be added to the surface layer 8 forming the surface.
【００２１】延伸糸２として用いられる基層７又は表面
層８を形成する合成樹脂には、目的に応じて各種の添加
剤を添加することができる。Various additives can be added to the synthetic resin forming the base layer 7 or the surface layer 8 used as the drawn yarn 2 depending on the purpose.
【００２２】具体的には、フェノール系、有機ホスファ
イト系等の有機リン系、チオエーテル系等の酸化防止
剤；ヒンダードアミン系等の光安定剤；ベンゾフェノン
系、ベンゾトリアゾール系、ベンゾエート系等の紫外線
吸収剤；ノニオン系、カチオン系、アニオン系等の帯電
防止剤；ビスアミド系、ワックス系、有機金属塩系等の
分散剤；アミド系、ワックス系、有機金属塩系、エステ
ル系等の滑剤；含臭素有機系、リン酸系、三酸化アンチ
モン、水酸化マグネシウム、赤リン等の難燃剤等が挙げ
られる。Specifically, antioxidants such as phenol-based and organic phosphite-based organic phosphorus-based and thioether-based antioxidants; hindered amine-based light stabilizers; benzophenone-based, benzotriazole-based, benzoate-based ultraviolet absorption, etc. Agents; nonionic, cationic, anionic, etc. antistatic agents; bisamide, wax, organometallic salt, etc. dispersants; amide, wax, organometallic salt, ester, etc. lubricants, bromine-containing Examples of the flame retardant include organic compounds, phosphoric acid compounds, antimony trioxide, magnesium hydroxide and red phosphorus.
【００２３】これら添加剤は、適宜組み合わせて、基層
７や表面層８の材料組成物を製造するいずれかの工程で
配合される。添加剤の配合は、従来の公知の二軸スクリ
ュー押出機、バンバリーミキサー、ニーダーミキシング
ロール等の混練装置を用いて所定割合に混合して、これ
を溶融混練して調製してもよいし、高濃度のいわゆるマ
スターバッチを調製し、これを希釈して使用するように
してもよい。These additives are appropriately combined and blended in any step of manufacturing the material composition of the base layer 7 and the surface layer 8. The additives are mixed in a known ratio by using a kneading device such as a conventionally known twin screw extruder, Banbury mixer, kneader mixing roll, etc., which may be melt-kneaded to prepare. A so-called masterbatch having a concentration may be prepared, and this may be diluted before use.
【００２４】延伸糸２として積層体が使用される場合、
積層フラットヤーン、又は、スプリットヤーンの成形材
料となる積層フィルムを成形する手段としては、予め基
層７となるフイルムと表面層８となるフイルムを形成し
てドライラミネート法や熱ラミネート法を用いて複層化
する手段や、基層７となるフイルムの表面に表面層８と
なる合成樹脂をコーティングする方法、予め形成した基
層７となるフイルムに表面層８を押出ラミネートする方
法、あるいは、多層共押出法によって積層フイルムとし
て押出成形するなどの公知の手段から適宜選択して用い
ればよいが、成形の容易さやコスト面、並びに、製品の
各層間の接着性の点では、多層共押出法によって基層７
と表面層８の積層体を一段で得る方法が望ましい。シー
スコア構造、あるいは、サイドバイサイド構造について
は共押出法によるのが一般的である。When a laminated body is used as the drawn yarn 2,
As a means for molding a laminated film which is a molding material for a laminated flat yarn or a split yarn, a film to be a base layer 7 and a film to be a surface layer 8 are formed in advance and a dry laminating method or a thermal laminating method is used. Layering means, a method of coating the surface of the film to be the base layer 7 with a synthetic resin to form the surface layer 8, a method of extrusion laminating the surface layer 8 to a film to be the base layer 7 formed in advance, or a multi-layer coextrusion method. It may be appropriately selected from known means such as extrusion molding as a laminated film by using a base layer 7 by a multi-layer coextrusion method in view of easiness of molding, cost, and adhesiveness between each layer of the product.
A method of obtaining a laminate of the surface layer 8 and the surface layer 8 in one step is desirable. For the sheath core structure or the side-by-side structure, the coextrusion method is generally used.
【００２５】また、延伸して延伸糸２とする手段として
は、基層７となるフイルムを一軸方向に延伸した後、表
面層８となる合成樹脂を積層し、これをテープ状にスリ
ットしてもよく、あるいは、基層７と表面層８が積層さ
れた積層フィルムをスリットする前、又は、スリットし
た後、一軸方向に延伸することによって得ることもでき
る。延伸倍率は、通常３〜１０倍程度とされる。As a means for drawing the drawn yarn 2, a film to be the base layer 7 is uniaxially drawn, and then a synthetic resin to be the surface layer 8 is laminated and slit into a tape shape. Alternatively, it may be obtained by slitting the laminated film in which the base layer 7 and the surface layer 8 are laminated or before or after slitting, and then stretching in a uniaxial direction. The draw ratio is usually about 3 to 10 times.
【００２６】延伸糸２の太さはなんらの制限はなく目的
に応じて任意に設定することができるが、一般的には、
５００〜１００００デシテックス、好ましくは１０００
〜５０００デシテックス、糸幅が０．３〜２００ｍｍ、
好ましくは１．０〜１００ｍｍ、糸厚５〜５００μｍの
範囲とされる。The thickness of the drawn yarn 2 is not limited and can be set arbitrarily according to the purpose, but generally,
500 to 10,000 decitex, preferably 1000
~ 5000 decitex, thread width 0.3 ~ 200mm,
The range is preferably 1.0 to 100 mm and the yarn thickness is 5 to 500 μm.
【００２７】延伸糸２は、図１に示すように、織成して
織布として用いることができ、また、図２に示すよう
に、延伸糸２を一方向に並列させ、その上に交差する方
向に延伸糸２を並列させてその交点を結着することによ
ってソフとして用いることもできる。また、極細繊維と
したときは不織布として用いることも可能である。As shown in FIG. 1, the drawn yarns 2 can be woven and used as a woven fabric. Further, as shown in FIG. 2, the drawn yarns 2 are arranged in parallel in one direction and intersect with each other. It can also be used as a sof by arranging the drawn yarns 2 in parallel with each other and binding the intersections thereof. When it is made into ultrafine fibers, it can be used as a non-woven fabric.
【００２８】本発明において、除草シート１は光線透過
率が１０％未満、質量が５０〜５００ｇ／ｍ2の布状体
とされる。光線透過率が１０％以上では除草効果が得難
く、また、質量が５０ｇ／ｍ2未満では遮光性の確保が
難しくなり、質量が５００ｇ／ｍ2を越えると経済性が
悪くなる。In the present invention, the weeding sheet 1 is a cloth-like body having a light transmittance of less than 10% and a mass of 50 to 500 g / m 2 . When the light transmittance is 10% or more, it is difficult to obtain the herbicidal effect, and when the mass is less than 50 g / m 2, it is difficult to secure the light-shielding property, and when the mass exceeds 500 g / m 2 , the economical efficiency is deteriorated.
【００２９】織布、あるいは、不織布は、端部のほつれ
を防止するために、熱刃を用いてヒートカットすること
によって端部を熱溶着することも望ましく、また、タッ
クインすることによってほつれを防止することもでき
る。In order to prevent the fray of the end portion of the woven fabric or the non-woven fabric, it is also preferable that the end portion is heat-welded by heat cutting with a hot blade, and tuck-in prevents the fray. You can also do it.
【００３０】さらに、布状体に溶融熱可塑性樹脂、ホッ
トメルト剤、あるいは、水系接着剤を塗布することによ
ってほつれを防止することもでき、ほつれ防止のための
積層、塗布は通常所定の間隔をおいて線状に行なうこと
が望ましい。また、延伸糸２として積層体を用いたとき
は熱溶着によってほつれを防止することも可能である。Furthermore, it is possible to prevent fraying by applying a molten thermoplastic resin, a hot-melting agent, or an aqueous adhesive to the cloth-like body. Lamination and application for preventing fraying are usually performed at predetermined intervals. It is desirable to carry out linearly. Further, when a laminated body is used as the drawn yarn 2, it is possible to prevent fraying by heat welding.
【００３１】また、図５（Ａ）に示すように、除草シー
ト１には、所定の間隔をおいて色違いの糸９を織り込ん
でおくことが好ましい。色違いの糸９を織り込むことに
よってシートを敷設したり、ピン、杭等１３で係止する
際に位置決めが容易となる。位置決め用標識は印刷イン
クを用いて表面にラインマークを印刷することによって
も設けることもできる。Further, as shown in FIG. 5 (A), it is preferable that the weeding sheet 1 be woven with different-colored threads 9 at predetermined intervals. By weaving the yarns 9 of different colors, it becomes easy to position the sheet when laying the sheet or when locking the sheet with pins 13 and the like 13. The positioning mark can also be provided by printing a line mark on the surface using printing ink.
【００３２】さらに、本発明除草シート１には、図５
（Ｂ）に示すように、必要に応じて不織布等の排水材１
０を添着することも可能であり、さらに、シート１の側
部に、図５（Ｃ）に示すように補強用ロープ１１を取り
付けることも可能である。Further, the weeding sheet 1 of the present invention has the composition shown in FIG.
As shown in (B), drainage material 1 such as non-woven fabric, if necessary.
It is also possible to attach 0, and it is also possible to attach a reinforcing rope 11 to the side portion of the seat 1 as shown in FIG. 5 (C).
【００３３】本発明除草シート１は、田畑の畦畔、河川
の土手、鉄道線路の盛土の裏面、道路盛土法面、道路中
央分離帯、鉄塔下部等に敷設して除草機能を果たすこと
ができる。The weeding sheet 1 of the present invention can be laid on a ridge of a field, a bank of a river, a backside of an embankment of a railroad track, a road embankment slope, a road median strip, a lower part of a steel tower, etc. to perform a weeding function. .
【００３４】本発明除草シート１は、除草処理すべき場
所に重ね代をもって敷設し、ピン、杭等１３で係止する
ことによって固定することができる。ピン、杭等１３と
しては金属、合成樹脂等の船釘状体、あるいは、Ｕ字状
体を用いることができる。The weeding sheet 1 of the present invention can be fixed by laying it at a place to be weeded with an overlap margin and locking it with pins, piles 13 or the like. As the pins, piles 13 and the like, a ship-nail-shaped body made of metal, synthetic resin or the like, or a U-shaped body can be used.
【００３５】また、本発明除草シート１は除草処理すべ
き場所の表面に敷設されるのが一般的であるが、栗石等
の敷設場所に下敷材として敷設することも可能である。Further, the weeding sheet 1 of the present invention is generally laid on the surface of a place to be weeded, but it can also be laid as an underlaying material on a laying place such as a cobblestone.
【００３６】[0036]
【実施例】（実施例１）緑色顔料（シアニングリーン
系）を１．０重量％を含有するポリエチレン（日本ポリ
ケム社製）を溶融押出機を用いて、インフレーション成
形法によってフィルムを成形し、レザーを用いてスリッ
トした。スリットされた樹脂テープは温度１１０〜１２
０℃の熱板上で７倍に延伸した後、温度１２０度の熱風
循環式オーブン内で６％の弛緩熱処理を行ない、ワイン
ダーに巻き取った。得られた延伸テープの単糸繊度は１
９００ｄｔ、糸幅は８ｍｍであった。Example 1 Polyethylene (manufactured by Japan Polychem) containing 1.0% by weight of a green pigment (cyanine green type) was melt-extruded to form a film by an inflation molding method, and a leather was prepared. Was used to slit. Temperature of slit resin tape is 110-12
After being stretched 7 times on a hot plate at 0 ° C., a relaxation heat treatment of 6% was performed in a hot air circulation type oven at a temperature of 120 ° C., and wound on a winder. The drawn yarn has a single yarn fineness of 1
The yarn width was 900 dt and the yarn width was 8 mm.
【００３７】得られた延伸テープを表１に示す本数を用
いて織成して２ｍ×２ｍの織布を形成して、これを１．
５ｍ×１．５ｍ間に籾１００を播種した上に敷設した。
その３０日後に緑化した苗の本数を数え、発芽成長率を
調査した。光線透過率と発芽成長率の関係を表１に示
す。The drawn tape thus obtained was woven using the number shown in Table 1 to form a 2 m × 2 m woven fabric.
The paddy 100 was sown for 5 m × 1.5 m and laid.
Thirty days after that, the number of seedlings that had been greened was counted and the germination growth rate was investigated. Table 1 shows the relationship between the light transmittance and the germination growth rate.
【００３８】[0038]
【表１】 [Table 1]
【００３９】[0039]
【発明の効果】本発明は、かかる構成からなるから、機
械強度が高く、耐久性に優れると共に、遮光性がよく、
除草効果の大きい除草シートが得られる。EFFECTS OF THE INVENTION Since the present invention has such a constitution, it has high mechanical strength, excellent durability, and good light-shielding property.
A weeding sheet having a great weeding effect can be obtained.
【図１】本発明除草シートを示す（Ａ）は平面図、
（Ｂ）は縦断面図FIG. 1A is a plan view showing a weeding sheet of the present invention,
(B) is a vertical sectional view
【図２】本発明除草シートの他の例を示す縦断面図FIG. 2 is a vertical sectional view showing another example of the weeding sheet of the present invention.
【図３】本発明除草シートに使用される延伸糸の例を示
す斜視図FIG. 3 is a perspective view showing an example of a drawn yarn used for the weeding sheet of the present invention.
【図４】本発明除草シートに使用される延伸糸の例を示
す縦断面図FIG. 4 is a longitudinal sectional view showing an example of a drawn yarn used for the weeding sheet of the present invention.
【図５】本発明除草シートを示す（Ａ）は斜視図、
（Ｂ）、（Ｃ）は縦断面図FIG. 5 is a perspective view showing the weeding sheet of the present invention,
(B) and (C) are longitudinal sectional views.
【図６】本発明除草シートの敷設例を示す斜視図FIG. 6 is a perspective view showing an example of laying the weeding sheet of the present invention.
１：除草シート ２：延伸糸 ５：切れ込み ６：リブ ７：基層 ８：表面層 １１：補強用ロープ １３：杭 1: Weeding sheet 2: Stretched yarn 5: Notch 6: Rib 7: Base layer 8: Surface layer 11: Reinforcing rope 13: Pile
フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） // Ｄ０３Ｄ 1/00 Ｄ０３Ｄ 1/00 Ｚ Ｆターム(参考） 2B024 DA02 DB04 DD01 DD04 2B121 AA19 BB28 BB35 EA21 EA25 FA12 4H011 AB01 BC19 BC23 DA07 DA08 DH02 4L048 AA15 AB10 AB28 BA01 BA02 CA00 CA15 DA29 Front page continuation (51) Int.Cl. 7 Identification code FI theme code (reference) // D03D 1/00 D03D 1/00 Z F term (reference) 2B024 DA02 DB04 DD01 DD04 2B121 AA19 BB28 BB35 EA21 EA25 FA12 4H011 AB01 BC19 BC23 DA07 DA08 DH02 4L048 AA15 AB10 AB28 BA01 BA02 CA00 CA15 DA29
Claims (16)
れた延伸糸から形成され、光透過率が１０％未満、質量
が５０〜５００ｇ／ｍ2の布状体からなることを特徴と
する除草シート。1. A stretched yarn formed by uniaxially stretching a colored synthetic resin, comprising a cloth-like body having a light transmittance of less than 10% and a mass of 50 to 500 g / m 2. Weeding sheet to do.
１に記載の除草シート。2. The weeding sheet according to claim 1, wherein the drawn yarn comprises a flat yarn.
ンからなる請求項１又は２に記載の除草シート。3. The herbicidal sheet according to claim 1, wherein the drawn yarn comprises a laminated flat yarn of different composition.
成されたスプリットヤーンからなる請求項１〜３のいず
れかに記載の除草シート。4. The weeding sheet according to claim 1, wherein the drawn yarn comprises a split yarn having a large number of small cuts formed in the longitudinal direction.
４のいずれかに記載の除草シート。5. The drawn yarn is matt-treated.
The weeding sheet according to any one of 4 above.
ることによりほつれ防止されてなる請求項１〜５のいず
れかに記載の除草シート。6. The weeding sheet according to claim 1, wherein the cloth-like body is heat-cut by a hot blade to prevent fraying.
つれ防止されてなる請求項１〜５のいずれかに記載の除
草シート。7. The weeding sheet according to claim 1, wherein the cloth-like body is tucked in to prevent fraying.
とによりほつれ防止されてなる請求項１〜５のいずれか
に記載の除草シート。8. The weeding sheet according to claim 1, wherein the cloth-like body is fray-prevented by laminating a molten thermoplastic resin.
によりほつれ防止されてなる請求項１〜５のいずれかに
記載の除草シート。9. The weeding sheet according to claim 1, wherein the cloth-like body is prevented from fraying by applying a hot melt agent.
よりほつれ防止されてなる請求項１〜５のいずれかに記
載の除草シート。10. The weeding sheet according to claim 1, wherein the cloth-like body is prevented from fraying by applying an aqueous adhesive.
とによりほつれ防止されてなる請求項１〜５のいずれか
に記載の除草シート。11. The weeding sheet according to any one of claims 1 to 5, wherein the longitudinally and transversely drawn yarns of the cloth-like body are heat-sealed to prevent fraying.
項１〜１１のいずれかに記載の除草シート。12. The weeding sheet according to claim 1, wherein a non-woven fabric is laminated on the cloth body.
なる延伸糸が織り込まれてなる請求項１〜１２のいずれ
かに記載の除草シート。13. The weeding sheet according to any one of claims 1 to 12, wherein the cloth-like body is formed by weaving drawn yarns of different colors at predetermined intervals.
ンマークが印刷されてなる請求項１〜１２のいずれかに
記載の除草シート。14. The weeding sheet according to claim 1, wherein line marks are printed at predetermined intervals on the surface of the cloth-like body.
敷設されてなる請求項１〜１４のいずれかに記載の除草
シート。15. The weeding sheet according to claim 1, wherein a plurality of cloth-like bodies are laid with a predetermined overlap margin.
係止されてなる請求項１〜１５のいずれかに記載の除草
シート。16. The weeding sheet according to any one of claims 1 to 15, wherein the cloth-like body is locked with a pile material made of synthetic resin or metal.