JP2003027004A - Snow and ice accretion preventing paint - Google Patents
Snow and ice accretion preventing paintInfo
- Publication number
- JP2003027004A JP2003027004A JP2001215853A JP2001215853A JP2003027004A JP 2003027004 A JP2003027004 A JP 2003027004A JP 2001215853 A JP2001215853 A JP 2001215853A JP 2001215853 A JP2001215853 A JP 2001215853A JP 2003027004 A JP2003027004 A JP 2003027004A
- Authority
- JP
- Japan
- Prior art keywords
- snow
- ice
- ice adhesion
- preventing
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、雪氷付着防止用塗
料に関し、特に、付着雪氷の離型性に優れ、かつ、耐久
性を確保することができる雪氷付着防止用塗料に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a paint for preventing snow and ice adhesion, and more particularly to a paint for preventing snow and ice adhesion which is excellent in releasing property of adhered snow and ice and can ensure durability.
【０００２】[0002]
【従来の技術】冷凍食品冷蔵用トレー離型コート、冷凍
庫製氷皿離型コート、建築物着雪防止コート、道路標識
着雪防止コートなどの分野において離型用被覆材が用い
られている。このような着氷・着雪防止を目的とする低
温下での離型用途の分野においては、従来、シリコーン
樹脂にアルカリ金属化合物を組み合わせた組成物（特開
昭５９−２５８６８号公報）を用いる方法や、パーフル
オロアルキル基含有アクリル系重合体にアルカリ金属化
合物を組み合わせた組成物（特開昭６１−９５０７７号
公報）を用いる方法が提案されていた。2. Description of the Related Art Release coating materials are used in the fields of tray release coating for frozen food refrigeration, freezer ice tray release coating, building snow-prevention coating, road sign snow-prevention coating and the like. In the field of mold release applications at low temperatures for the purpose of preventing ice accretion and snow accretion, conventionally, a composition in which a silicone resin is combined with an alkali metal compound (JP-A-59-25868) is used. A method and a method of using a composition (Japanese Patent Laid-Open No. 61-95077) in which an alkali metal compound is combined with a perfluoroalkyl group-containing acrylic polymer have been proposed.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、いずれ
の方法も、被膜の強度が小さいことから、凍結付着した
雪氷を離型する際、または、自重等により自然剥落する
際に被膜が破損され、雪氷とともに脱落することがあ
る。したがって、離型を繰り返すうちに被膜が失われ、
耐久性の点で問題があった。さらに、寒冷地車両におい
ても、より高い雪氷付着防止機能が求められていた。However, in any of the methods, since the strength of the coating film is small, the coating film is damaged when the frozen and adhered snow and ice is released from the mold, or when it is naturally peeled off due to its own weight, etc. May fall off with. Therefore, the coating is lost during repeated release,
There was a problem in terms of durability. Further, even in vehicles in cold regions, a higher function of preventing snow and ice from adhering has been required.
【０００４】本発明は、付着雪氷の離型性に優れ、か
つ、耐久性を確保することができる雪氷付着防止用塗料
を提供することを目的とする。An object of the present invention is to provide a coating material for preventing snow and ice adhesion, which is excellent in releasing property of adhered snow and ice and which can secure durability.
【０００５】[0005]
【課題を解決するための手段】このため本発明（請求項
１）は、アスペクト比（厚さに対する長径の比）が１０
〜３００、平均粒子径が３μｍ以下の無機板状粒子およ
び熱可塑性フッ素樹脂水性分散液を含むことを特徴とす
る。Therefore, according to the present invention (claim 1), the aspect ratio (ratio of major axis to thickness) is 10.
.About.300, and an inorganic plate-like particle having an average particle diameter of 3 .mu.m or less, and a thermoplastic fluororesin aqueous dispersion.
【０００６】無機板状粒子の微細な積層構造により熱可
塑性フッ素樹脂との粒子結着性が確保され、強固な結合
組織が形成されるので、熱可塑性フッ素樹脂が確実に結
着されるとともに硬度の確保が可能となる。したがっ
て、基材に対する接着性および熱可塑性フッ素樹脂の離
型性を確保しつつ、硬度性が確保される。The fine laminated structure of the inorganic plate-like particles secures the particle binding property with the thermoplastic fluororesin and forms a strong connective structure, so that the thermoplastic fluororesin is surely bound and has a hardness. Can be secured. Therefore, the hardness is secured while ensuring the adhesiveness to the base material and the releasability of the thermoplastic fluororesin.
【０００７】前記無機板状粒子は、所定の硬度の自己造
膜性を有し、また、比表面積が３０〜５００ｍ２／ｇで
あることが好ましい。具体的には、シリカ−Ｘ、シリカ
−Ｙ、マガジナイト、カネマイト等の層状ポリケイ酸が
該当する。シリカ−Ｘは、被覆層の硬度性、離型性の点
において、雪氷付着防止用塗料に対して５０〜９５％で
あることが好ましい。It is preferable that the inorganic plate-like particles have a self-forming property with a predetermined hardness and a specific surface area of 30 to 500 m 2 / g. Specifically, layered polysilicic acid such as silica-X, silica-Y, magadinite, and kanemite is applicable. Silica-X is preferably 50 to 95% of the coating for preventing snow and ice adhesion in terms of hardness and releasability of the coating layer.
【０００８】さらに、本発明（請求項６）は、前記雪氷
付着防止用塗料に液状の増粘剤を含むことを特徴とす
る。Furthermore, the present invention (claim 6) is characterized in that the paint for preventing snow and ice adhesion contains a liquid thickening agent.
【０００９】無機板状粒子により、基材に対する接着性
および硬度性が確保され、かつ、増粘剤が被膜表面に常
時しみ出すことにより、着氷力が低減される。さらに、
無機板状粒子により増粘剤のしみ出し量が一定範囲に抑
えられるので、長期にわたりしみ出しが維持される。The inorganic plate-like particles secure the adhesiveness and hardness to the substrate, and the thickening agent constantly exudes to the surface of the coating film, thereby reducing the icing force. further,
Since the amount of exudation of the thickener is suppressed within a certain range by the inorganic plate-like particles, exudation is maintained for a long period of time.
【００１０】さらに、本発明（請求項７）は、前記増粘
剤がパーフルオロポリエーテルであることを特徴とす
る。パーフルオロポリエーテルにより、簡易に離型性を
向上し、かつ、繰り返しによっても離型性を維持するこ
とができる。Furthermore, the present invention (claim 7) is characterized in that the thickening agent is a perfluoropolyether. By using the perfluoropolyether, the releasability can be easily improved, and the releasability can be maintained even by repeating.
【００１１】さらに、本発明（請求項８）は、前記パー
フルオロポリエーテルによる増粘剤が雪氷付着防止用塗
料に対して５〜２０％であることを特徴とする。増粘剤
が５％より少ないと着氷力の低減効果が低下し、逆に２
０％より多いと硬度が低下する。Further, the present invention (claim 8) is characterized in that the thickener by the perfluoropolyether is 5 to 20% with respect to the coating for preventing snow and ice adhesion. If the amount of the thickener is less than 5%, the effect of reducing the icing power is reduced, and conversely 2
If it is more than 0%, the hardness decreases.
【００１２】[0012]
【発明の実施の形態】以下、本発明の実施形態について
説明する。本発明に係る雪氷付着防止用塗料は、熱可塑
性フッ素樹脂水性分散液と無機板状粒子との混合体によ
って構成される。また、熱可塑性フッ素樹脂水性分散液
と無機板状粒子との混合体にさらに増粘剤を添加しても
よい。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below. The coating composition for preventing snow and ice adhesion according to the present invention is composed of a mixture of a thermoplastic fluororesin aqueous dispersion and inorganic plate-like particles. Further, a thickener may be further added to the mixture of the thermoplastic fluororesin aqueous dispersion and the inorganic plate-like particles.
【００１３】本発明における熱可塑性フッ素樹脂水性分
散液に用いられるフッ素ポリマーは、ポリテトラフルオ
ロエチレン、ポリクロロトリフルオロエチレンなどのフ
ルオロオレフィンの重合体、または、フルオロオレフィ
ンおよびそれと共重合可能なモノマーとの共重合体が好
ましい。具体的には、以下のものが好ましく採用され
る。テトラフルオロエチレン重合体（以下、ＰＴＦＥと
する）、テトラフルオロエチレン／パーフルオロ（アル
キルビニルエーテル）共重合体（以下、ＰＦＡとす
る）、テトラフルオロエチレン／ヘキサフルオロプロピ
レン共重合体、テトラフルオロエチレン／エチレン共重
合体（以下、ＥＴＦＥとする）、クロロトリフルオロエ
チレン重合体、クロロトリフルオロエチレン／エチレン
共重合体、フッ化ビニリデン重合体、フッ化ビニル重合
体などである。特には、ＰＴＦＥ、ＰＦＡが好ましい。
ここでＰＴＦＥとは、本質的にテトラフルオロエチレン
に基づく繰り返し単位からなる重合体であって、他の繰
り返し単位を含むものであってもよい。The fluoropolymer used in the thermoplastic fluororesin aqueous dispersion in the present invention is a fluoroolefin polymer such as polytetrafluoroethylene or polychlorotrifluoroethylene, or a fluoroolefin and a monomer copolymerizable therewith. Is preferable. Specifically, the following are preferably adopted. Tetrafluoroethylene polymer (hereinafter referred to as PTFE), tetrafluoroethylene / perfluoro (alkyl vinyl ether) copolymer (hereinafter referred to as PFA), tetrafluoroethylene / hexafluoropropylene copolymer, tetrafluoroethylene / ethylene Copolymers (hereinafter referred to as ETFE), chlorotrifluoroethylene polymers, chlorotrifluoroethylene / ethylene copolymers, vinylidene fluoride polymers, vinyl fluoride polymers and the like. Particularly, PTFE and PFA are preferable.
Here, PTFE is a polymer consisting essentially of repeating units based on tetrafluoroethylene, and may contain other repeating units.
【００１４】本発明に用いられる無機板状粒子は、アス
ペクト比（厚さに対する長径の比）が１０〜３００、平
均粒子径が３μｍ以下、比表面積が３０〜５００ｍ２／
ｇを満たすことが好ましい。アスペクト比が１０に満た
ない場合は、十分な閉路効果が得にくい。ここで閉路効
果とは、下塗り剤中への物質の拡散、浸透のし難さをい
う。アスペクト比は２０〜２００（特に２０〜１００）
がさらに好ましい。平均粒子径が３μｍを超える場合
や、比表面積が３０ｍ２／ｇに満たない場合は十分な閉
路効果が得にくい。The inorganic plate-like particles used in the present invention have an aspect ratio (ratio of major axis to thickness) of 10 to 300, an average particle diameter of 3 μm or less, and a specific surface area of 30 to 500 m 2 /.
It is preferable to satisfy g. If the aspect ratio is less than 10, it is difficult to obtain a sufficient closing effect. Here, the closed circuit effect means the difficulty of diffusion and penetration of a substance into the undercoating agent. Aspect ratio is 20-200 (especially 20-100)
Is more preferable. If the average particle diameter exceeds 3 μm or if the specific surface area is less than 30 m 2 / g, it is difficult to obtain a sufficient closing effect.
【００１５】このような無機板状粒子は、特に自己造膜
作用を有するものが好ましい。造膜性の基準は、無機板
状粒子を固形分含量が１５％になるようにイオン交換水
に分散した分散液をポリエチレンテレフタレートフィル
ム上に２５〜３０ｇ／ｍ２の塗工量で塗布・乾燥して得
られる膜の鉛筆硬度が２Ｈ以上であることが好ましい。
この膜の鉛筆硬度は、板状粒子自体の造膜性を規定する
物性であり、鉛筆硬度が２Ｈに満たない場合は、無機板
状粒子による下塗り剤において十分な硬さの塗膜が得ら
れないおそれががあるので好ましくない。この膜の鉛筆
硬度が３Ｈ以上である場合はさらに好ましい。It is particularly preferable that such inorganic plate-like particles have a self-film forming action. The standard of film forming property is to apply a dispersion of inorganic plate-like particles dispersed in ion-exchanged water so that the solid content becomes 15% onto a polyethylene terephthalate film at a coating amount of 25 to 30 g / m 2 and dry. The pencil hardness of the film thus obtained is preferably 2H or more.
The pencil hardness of this film is a physical property that determines the film-forming property of the plate-like particles themselves. When the pencil hardness is less than 2H, a coating film having sufficient hardness can be obtained in an undercoating agent using inorganic plate-like particles. It is not preferable because there is a possibility that it may not exist. It is more preferable that the pencil hardness of this film is 3H or more.
【００１６】無機板状粒子としては、具体的には、シリ
カ−Ｘ、シリカ−Ｙ、マガジナイト、カネマイトなどの
層状ポリケイ酸を用いるのが好ましい。上記シリカ−Ｘ
としては、特願平１１−３５１１８２に述べられた、鱗
片状シリカが例示しうる。鱗片状シリカは、詳細には、
その薄片１次粒子が互いに面間が平行的に配向し、複数
重なって形成される葉状シリカ２次粒子である。たとえ
ば、洞海化学工業社製のもの（商品名：サンラブリーＬ
ＦＳ）が該当する。As the inorganic plate-like particles, specifically, layered polysilicic acid such as silica-X, silica-Y, magazinite, kanemite is preferably used. Silica-X
As an example, the scale-like silica described in Japanese Patent Application No. 11-351182 can be exemplified. The scaly silica is, in detail,
Leaf-like silica secondary particles are formed by laminating a plurality of the flaky primary particles in parallel with each other in a face-to-face direction. For example, those manufactured by Dokai Chemical Industry (trade name: Sun Lovely L
FS) is applicable.
【００１７】鱗片状シリカの場合は、雪氷付着防止用塗
料に対して５０〜９５％であることが好ましい。配合比
が５０％より少ない場合は硬度が低下し、逆に９５％よ
り多い場合は離型性が低下する。この範囲において、硬
度による耐久性および十分な接着力を確保し、かつ、熱
可塑性フッ素樹脂による離型性を確保することができ
る。In the case of scale-like silica, it is preferably 50 to 95% with respect to the paint for preventing snow and ice adhesion. When the compounding ratio is less than 50%, the hardness decreases, and when it is more than 95%, the releasability decreases. Within this range, durability due to hardness and sufficient adhesive strength can be secured, and releasability due to the thermoplastic fluororesin can be secured.
【００１８】本発明における増粘剤としては、グリコー
ル系（ポリエチレングリコール、トリエチレングリコー
ル等）、セルロース系（メチルセルロース、カルボキシ
メチルセルロース等）、フッ素系のものが適用できる。
中でも、フッ素系増粘剤が望ましい。As the thickener in the present invention, glycol type (polyethylene glycol, triethylene glycol etc.), cellulose type (methyl cellulose, carboxymethyl cellulose etc.) and fluorine type can be applied.
Of these, a fluorine-based thickener is desirable.
【００１９】フッ素系増粘剤では、フッ素含有単量体の
低重合物などが採用される。具体的には、パーフルオロ
ポリエーテル、テトラフルオロエチレン低重合物、クロ
ロトリフルオロエチレン低重合物などが例示される。中
でも、パーフルオロポリエーテルが好ましく採用され
る。パーフルオロポリエーテルは、簡易に離型性を向上
し、かつ、繰り返しによっても離型性を維持することが
できる。これらフッ素系増粘剤は、フォンブリン（アウ
ジモント社製）、フロンループ（旭硝子社製）、クライ
トックス（デュポン社製）などの商品名で市販されてい
るフッ素系化合物が適用できる。As the fluorine-based thickener, a low polymer of a fluorine-containing monomer is used. Specific examples thereof include perfluoropolyether, tetrafluoroethylene low polymer, and chlorotrifluoroethylene low polymer. Among them, perfluoropolyether is preferably used. The perfluoropolyether can easily improve the releasability, and can maintain the releasability even when it is repeatedly used. As these fluorine-based thickeners, fluorine-based compounds that are commercially available under trade names such as Fomblin (manufactured by Ausimont), Flonloop (manufactured by Asahi Glass Co., Ltd.), and Krytox (manufactured by DuPont) can be applied.
【００２０】増粘剤がパーフルオロポリエーテルの場合
は、雪氷付着防止用塗料に対して５〜２０％であること
が好ましい。増粘剤が５％より少ないと着氷力の低減効
果が得られず、逆に２０％より多いと硬度が低下する。When the thickener is perfluoropolyether, it is preferably 5 to 20% with respect to the snow and ice adhesion preventing paint. If the amount of the thickening agent is less than 5%, the effect of reducing the icing force cannot be obtained, and if it is more than 20%, the hardness decreases.
【００２１】本発明の塗料は、無機板状粒子の微細な積
層構造により熱可塑性フッ素樹脂等の熱可塑性フッ素樹
脂との粒子結着性を確保して強固な結合組織が形成され
るので、熱可塑性フッ素樹脂が確実に結着されるととも
に、硬度の確保が可能となる。したがって、基材に対す
る接着性および熱可塑性フッ素樹脂の離型性を確保しつ
つ、その硬度の増加により耐久性が向上する。The coating composition of the present invention ensures a particle bondability with a thermoplastic fluororesin such as a thermoplastic fluororesin due to a fine laminated structure of inorganic plate-like particles to form a strong connective structure. The plastic fluororesin is surely bound and the hardness can be secured. Therefore, the durability is improved by increasing the hardness thereof while ensuring the adhesiveness to the base material and the releasability of the thermoplastic fluororesin.
【００２２】このように、本発明の塗料は、熱可塑性フ
ッ素樹脂による離型性とともに、無機板状粒子により被
覆基材との間の接着力および被膜の硬度が確保される。
したがって、凍結付着した雪氷の掻き落とし作業が容易
となる上に、掻き落とし作業が繰り返されても、被膜が
維持されて耐久性を確保することができる。As described above, in the coating material of the present invention, the release property of the thermoplastic fluororesin as well as the adhesive force with the coating substrate and the hardness of the coating film are secured by the inorganic plate-like particles.
Therefore, it is possible to easily scrape off the frozen snow and ice, and even if the scraping operation is repeated, the coating film is maintained and durability can be secured.
【００２３】また、増粘剤を添加することにより、被膜
面に増粘剤がしみ出して常に表面がぬるぬるの状態とな
り、離型性が向上されるので着氷力が低減される。さら
に、無機板状粒子により増粘剤のしみ出し量が一定範囲
に抑えられるので、長期にわたりしみ出しが維持され
る。Further, by adding the thickener, the thickener exudes to the surface of the film and the surface is always slimy, and the releasability is improved, so that the ice accretion is reduced. Furthermore, since the amount of exudation of the thickener is suppressed within a certain range by the inorganic plate-like particles, exudation is maintained for a long period of time.
【００２４】本発明の適用対象は、凍結付着した雪氷を
繰り返し掻き落としする場合に有効である。たとえば、
積雪地帯を走行する鉄道車両等に適用することができ
る。積雪地帯を走行する鉄道車両においては、走行中の
車両から付着雪氷が落下すると危険であり、また、車両
の床下に大量に雪氷が付着すると走行不能となる。した
がって、安全走行しうる範囲内に雪氷の付着を抑えるた
めに、車両下部に雪氷が付着するとその都度、付着雪氷
を掻き落とす必要がある。The object to which the present invention is applied is effective in repeatedly scraping off the frozen snow and ice. For example,
It can be applied to railway vehicles running in snowy areas. In a railroad vehicle that travels in a snowy area, it is dangerous if adhering snow and ice falls from the traveling vehicle, and if a large amount of snow and ice adheres to the underfloor of the vehicle, traveling becomes impossible. Therefore, in order to suppress the adhesion of snow and ice within the safe driving range, it is necessary to scrape off the adhered snow and ice each time the snow and ice adheres to the lower part of the vehicle.
【００２５】このような状況において、本発明の塗料
は、車両の下回りに塗布することにより、スコップ等を
用いて付着雪氷を容易に掻き落としすることができる。
さらに、何度となく繰り返される掻き落とし作業に際
し、塗料被膜の耐久性が高いことにより、熱可塑性フッ
素樹脂の破損、傷付き、脱落を防止することができ、従
って離型性が維持されるので、長期にわたって掻き落と
し作業の労力軽減を図ることができる。In such a situation, the coating material of the present invention can be easily scraped off the adhered snow and ice by using a scoop or the like by applying it to the lower part of the vehicle.
Furthermore, due to the high durability of the paint film during repeated scraping work, it is possible to prevent damage, scratches, and falling off of the thermoplastic fluororesin, thus maintaining releasability. Therefore, the labor of scraping work can be reduced over a long period of time.
【００２６】また、塗料としての被膜硬度と基材接着力
が高いことにより、車両の制輪子による火花や、高圧電
線を支持する碍子の沿面アーク等を受ける環境に適用す
る場合においても有効である。Further, since the coating film as a paint has a high hardness and a high adhesive force to the base material, it is also effective in the case where it is applied to an environment in which a spark of a vehicle brake shoe or a creeping arc of an insulator supporting a high-voltage electric wire is applied. .
【００２７】さらに、増粘剤を添加した場合には、凍結
付着した雪氷が大きく成長する前に自然落下するように
期待される。たとえば、電車架線の支持構造物をはじめ
架空電線、道路標識、建物、パラボラアンテナ、トラッ
クの幌上部等に適用することができる。その他、本発明
の雪氷付着防止用塗料は、雪氷付着防止機能材料として
幅広く適用することができる。Furthermore, when a thickener is added, it is expected that the frozen and adhered snow and ice will fall naturally before they grow large. For example, the present invention can be applied to a supporting structure of an overhead line, an overhead line, a road sign, a building, a parabolic antenna, a truck top, and the like. In addition, the snow / ice adhesion preventing coating material of the present invention can be widely applied as a snow / ice adhesion preventing functional material.
【００２８】なお、本発明の雪氷付着防止用塗料には、
発明の目的を損なわない範囲内で、界面活性剤、顔料、
充填剤など、必要に応じて適宜の添加剤を用いることが
できる。The snow / ice adhesion preventing paint of the present invention comprises:
Within the range that does not impair the object of the invention, a surfactant, a pigment,
Appropriate additives such as a filler can be used if necessary.
【００２９】[0029]
【実施例】つぎに、本発明の雪氷付着防止用塗料の被膜
の着氷力試験について説明する。無機板状粒子は洞海化
学工業社製（商品名：サンラブリーＬＦＳ）の鱗片状シ
リカによるシリカ−Ｘ（アスペクト比１００、比表面積
５０〜８０ｍ２／ｇ）を使用する。また、熱可塑性フッ
素樹脂水性分散液は旭硝子社製ＰＴＦＥ（フルオンＡＤ
−１）、増粘剤は２種類（アウジモント社製のフォンブ
リンＹ−２５Ａを「Ｆ系」、トリエチレングリコールを
「Ｇ系」と表示する）を使用する。EXAMPLES Next, the icing power test of the coating film of the snow / ice adhesion preventing paint of the present invention will be explained. As the inorganic plate-like particles, silica-X (aspect ratio 100, specific surface area 50 to 80 m 2 / g) made of scaly silica manufactured by Dokai Chemical Industry (trade name: Sun Lovely LFS) is used. The thermoplastic fluororesin aqueous dispersion is PTFE (Fluon AD) manufactured by Asahi Glass Co., Ltd.
-1), two types of thickeners are used (Fomblin Y-25A manufactured by Ausimont Co. is represented as "F type" and triethylene glycol as "G type").
【００３０】着氷力は、北海道立工業試験場の試験仕様
（月刊建築仕上技術９５年３月号第３８ページ）によ
り、着氷面の剪断に要する力によって表わす。試験方法
は、氷作成用のステンレスリング（直径２５．４ｍｍ）
を資料表面に置き、所定の温度に十分冷却した後、５℃
の蒸留水を注ぎ、所定の時間放置して氷を試料表面に凍
着させる。その後ステンレスリングに剪断方向より荷重
を負荷することにより材料と凍結面の間を剥離させる。
その時の荷重を付着面積で除した値を着氷力とする。The icing force is represented by the force required to shear the icing surface according to the test specifications of the Hokkaido Industrial Test Institute (Monthly Construction Finishing Technology March 1995 issue, page 38). The test method is a stainless steel ring for making ice (diameter 25.4 mm)
Place the sample on the surface of the material and cool it to the specified temperature, then 5 ℃
Pour distilled water and leave it for a predetermined time to freeze ice on the sample surface. Thereafter, a load is applied to the stainless ring in the shearing direction to separate the material from the frozen surface.
The value obtained by dividing the load at that time by the adhesion area is the icing force.
【００３１】表１に示す配合比で調合し、それぞれステ
ンレス（ＳＵＳ３０４）製テストパネル（６０ｍｍ×６
０ｍｍ×２ｍｍ）上に＃８０バーコーター、１夜風乾
後、３００℃で２Ｈｒ処理することにより被膜を形成し
た。この被覆物について、着氷力（１回目）、鉛筆硬
度、接着力（碁盤目試験）の各試験結果を表１に示す。The test panels (60 mm × 6) made of stainless steel (SUS304) were prepared at the compounding ratios shown in Table 1.
(0 mm × 2 mm), air dried at # 80 bar coater overnight, and then treated for 2 hours at 300 ° C. to form a film. Table 1 shows the test results of the icing force (first time), the pencil hardness, and the adhesive force (cross-cut test) of this coating.
【００３２】[0032]
【表１】 [Table 1]
【００３３】表２に示す配合比で調合し、それぞれステ
ンレス（ＳＵＳ３０４）製テストパネル（６０ｍｍ×６
０ｍｍ×２ｍｍ）上に＃８０バーコーター、１夜風乾
後、３００℃で２Ｈｒ処理することにより被膜を形成し
た。この被覆物について、着氷力（１回目および１００
回目）、鉛筆硬度、接着力（碁盤目試験）の各試験結果
を表２に示す。Compounds were prepared in the mixing ratios shown in Table 2 and made of stainless (SUS304) test panels (60 mm × 6).
(0 mm × 2 mm), air dried at # 80 bar coater overnight, and then treated for 2 hours at 300 ° C. to form a film. For this coating, the icing power (1st and 100th
Table 2 shows the test results of the (second), pencil hardness, and adhesive strength (cross-cut test).
【００３４】[0034]
【表２】 [Table 2]
【００３５】この試験結果に基づき、まず、着氷力につ
いて評価する。着氷力と鱗片状シリカの配合比との関係
は、増粘剤が同条件であれば、１回目の着氷力は、比較
例２と実施例４の対比（増粘剤がＦ系１０％）により、
２０ｋＰａ（配合比０％）および２６ｋＰａ（配合比６
３％）となり、鱗片状シリカの配合比と対応して、着氷
力が多少増加することが認められる。また、比較例３と
実施例６の対比（Ｇ系１０％）についても、５０ｋＰａ
（配合比０％）および５５ｋＰａ（配合比６３％）とな
り、同様に鱗片状シリカの配合比と対応して着氷力が多
少増加することが認められる。Based on the test results, first, the icing force is evaluated. As for the relationship between the icing power and the blending ratio of the flake-like silica, if the thickening agent is in the same condition, the first icing power is the comparison between Comparative Example 2 and Example 4 (the thickening agent is F type 10 %)
20 kPa (mixing ratio 0%) and 26 kPa (mixing ratio 6
3%), and it is recognized that the icing power is increased to some extent in accordance with the blending ratio of the scaly silica. Further, the comparison between Comparative Example 3 and Example 6 (G system 10%) is also 50 kPa.
(Blending ratio 0%) and 55 kPa (blending ratio 63%), and it is recognized that the icing force is slightly increased corresponding to the blending ratio of flake silica.
【００３６】しかし、１回目と１００回目の着氷力の変
化について対比すると、比較例２と実施例４との対比
（Ｆ系１０％）により、鱗片状シリカ０％では２０ｋＰ
ａから３５ｋＰａに増加し、一方、鱗片状シリカ６３％
では２６ｋＰａから２８ｋＰａとほとんど変化がなかっ
た。比較例３と実施例６との対比（Ｇ系１０％）につい
ても、鱗片状シリカ０％では５０ｋＰａから６０ｋＰａ
に増加し、一方、鱗片状シリカ６３％ではいずれも５５
ｋＰａと変化がなかった。However, when the changes in the icing power at the first time and the 100th time are compared with each other, the comparison between Comparative Example 2 and Example 4 (F system 10%) shows that 20% of flake silica is 20 kP.
increased from a to 35 kPa, while scaly silica 63%
There was almost no change from 26 kPa to 28 kPa. Regarding the comparison between Comparative Example 3 and Example 6 (G-based 10%), 0% scaly silica gives 50 to 60 kPa.
On the other hand, with 63% of scaly silica, 55%
There was no change with kPa.
【００３７】この結果によれば、鱗片状シリカ（６３
％）の存在により、１００回目の剪断剥離後においても
試料上の塗料被膜がほとんどそのまま維持され、すなわ
ち、被膜が強化されることが結論付けられる。According to this result, the scale-like silica (63
It is concluded that the presence of%) keeps the paint coating on the sample almost intact, ie strengthens the coating, even after the 100th shear peel.
【００３８】また、着氷力と増粘剤との関係は、実施例
２、３、４、５に示されるように、増粘剤の配合比
（０、５、１０、２０％）と対応して着氷力（１３０ｋ
Ｐａ、５０ｋＰａ、２６ｋＰａ、６ｋＰａ）が低減され
ることが測定結果によって結論付けられる。The relationship between the icing power and the thickener corresponds to the compounding ratio (0, 5, 10, 20%) of the thickener, as shown in Examples 2, 3, 4, and 5. And the icing power (130k
Pa, 50 kPa, 26 kPa, 6 kPa) are reduced by the measurement results.
【００３９】つぎに、硬度について試験結果を評価す
る。被膜の硬度と鱗片状シリカとの関係は、増粘剤無添
加の実施例１、２においては大きな硬度（３Ｈまたは５
Ｈ）が得られた。また、増粘剤が同一条件であれば、比
較例２と実施例４の対比（Ｆ系１０％）において、鉛筆
硬度が２Ｂ（配合比０％）と２Ｈ（配合比６３％）、比
較例３と実施例６の対比（Ｇ系１０％）において、鉛筆
硬度がＢ（配合比０％）とＨ（配合比６３％）に示され
るように、鱗片状シリカの配合比（０％、６３％）と対
応して被膜硬度が増加することが結論付けられる。Next, the test results are evaluated for hardness. The relationship between the hardness of the coating and the scale-like silica is large in Examples 1 and 2 in which the thickener is not added (3H or 5).
H) was obtained. Further, under the same conditions of the thickener, in the comparison of Comparative Example 2 and Example 4 (F type 10%), the pencil hardness is 2B (mixing ratio 0%) and 2H (mixing ratio 63%). In the comparison between Example 3 and Example 6 (G system 10%), the pencil hardness is shown by B (blending ratio 0%) and H (blending ratio 63%), and the blending ratio of scaly silica (0%, 63%). %) And the coating hardness increases.
【００４０】この試験結果によれば、被膜硬度は、鱗片
状シリカ（６３％）により十分な硬度を有しており、着
氷力試験の結果とも符合するものである。この被膜硬度
により、付着雪氷の掻き落としや火花を含む被膜の表面
障害に対する強度が確保され、すなわち、耐久性が向上
される。According to the results of this test, the film hardness has a sufficient hardness due to the scaly silica (63%), which is in agreement with the result of the ice accretion test. This film hardness ensures the strength against scratches of adhered snow and ice and surface damage of the film including sparks, that is, the durability is improved.
【００４１】つぎに、基材との接着力について試験結果
を評価する。碁盤目試験によれば、鱗片状シリカを含ま
ない比較例２、３の場合の８〜９点に対して、鱗片状シ
リカを含む実施例１〜６の場合に９〜１０点が得られ
た。これにより、鱗片状シリカと対応して基材に対する
十分な接着力が得られることが検証された。したがっ
て、付着雪氷の掻き落としや剥落の際における被膜の脱
落が防止されることが結論付けられる。Next, the test results of the adhesive strength with the base material are evaluated. According to the cross-cut test, 9 to 10 points were obtained in Examples 1 to 6 containing scaly silica, compared with 8 to 9 points in Comparative Examples 2 and 3 not containing scaly silica. . As a result, it was verified that a sufficient adhesive force to the substrate was obtained corresponding to the scale-like silica. Therefore, it is concluded that the film is prevented from falling off when the adhered snow and ice are scraped off or peeled off.
【００４２】[0042]
【発明の効果】本発明の雪氷付着防止用塗料は、無機板
状粒子の微細な積層構造により熱可塑性フッ素樹脂との
粒子結着性が確保され、強固な結合組織が形成されるの
で、熱可塑性フッ素樹脂が確実に結着されるとともに硬
度の確保が可能となる。したがって、基材に対する接着
性および熱可塑性フッ素樹脂の離型性を確保しつつ、硬
度の向上によって耐久性が確保される。また、増粘剤の
添加により、離型性をさらに改善することができる。EFFECTS OF THE INVENTION The coating for preventing snow and ice adhesion of the present invention ensures that the particle binding property with the thermoplastic fluororesin is ensured by the fine laminated structure of the inorganic plate-like particles and a strong connective structure is formed. The plastic fluororesin is surely bound and the hardness can be secured. Therefore, durability is secured by improving hardness while securing adhesiveness to the base material and releasability of the thermoplastic fluororesin. Further, the release property can be further improved by adding a thickening agent.
Claims (8)
が１０〜３００、平均粒子径が３μｍ以下の無機板状粒
子および熱可塑性フッ素樹脂水性分散液を含むことを特
徴とする雪氷付着防止用塗料。1. Aspect ratio (ratio of major axis to thickness)
Of 10 to 300 and an average particle diameter of 3 μm or less, and an inorganic plate-like particle, and a thermoplastic fluororesin aqueous dispersion, a paint for preventing snow and ice adhesion.
００ｍ２／ｇである請求項１記載の雪氷付着防止用塗
料。2. The specific surface area of the inorganic plate-like particles is 30-5.
The snow / ice adhesion preventing coating composition according to claim 1, which has a coating amount of 00 m 2 / g.
る請求項１又は２記載の雪氷付着防止用塗料。3. The snow / ice adhesion preventing coating composition according to claim 1, wherein the inorganic plate-like particles are layered polysilicic acid.
リカ−Ｙ、マガジナイトまたはカネマイトである請求項
３に記載の雪氷付着防止用塗料。4. The coating for preventing snow and ice adhesion according to claim 3, wherein the layered polysilicic acid is silica-X, silica-Y, magazinite or kanemite.
に対して５０〜９５％であることを特徴とする請求項４
記載の雪氷付着防止用塗料。5. The silica-X is 50 to 95% of the snow and ice adhesion preventing coating material.
Paint for preventing snow and ice adhesion.
を含むことを特徴とする請求項１〜５のいずれか１項に
記載の雪氷付着防止用塗料。6. The snow / ice adhesion preventing paint according to claim 1, wherein the snow / ice adhesion preventing paint contains a liquid thickening agent.
であることを特徴とする請求項６記載の雪氷付着防止用
塗料。7. The snow / ice adhesion preventing coating composition according to claim 6, wherein the thickener is perfluoropolyether.
着防止用塗料に対して５〜２０％であることを特徴とす
る請求項７記載の雪氷付着防止用塗料。8. The snow / ice adhesion preventing paint according to claim 7, wherein the perfluoropolyether is 5 to 20% of the snow / ice adhesion preventing paint.