JP2003026156A - Composite container - Google Patents
Composite containerInfo
- Publication number
- JP2003026156A JP2003026156A JP2001219767A JP2001219767A JP2003026156A JP 2003026156 A JP2003026156 A JP 2003026156A JP 2001219767 A JP2001219767 A JP 2001219767A JP 2001219767 A JP2001219767 A JP 2001219767A JP 2003026156 A JP2003026156 A JP 2003026156A
- Authority
- JP
- Japan
- Prior art keywords
- container
- paper
- composite
- resin
- impregnated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、衣料用洗剤などの
トイレタリー用品、および食料品、化粧品、などの内容
物を収納する紙製容器、もしくはプラスチックからなる
内装容器と紙からなる外装容器で被覆接合されている複
合容器に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a toilet container such as a detergent for clothes and a paper container for storing contents such as food and cosmetics, or an inner container made of plastic and an outer container made of paper. The present invention relates to joined composite containers.
【０００２】[0002]
【従来の技術】近年、環境問題が深刻化し、容器類なら
びに包装材料の易廃棄性が必要とされ、易焼却性、リサ
イクル性、またはリサイクル材料使用の需要が高まって
いる。そこでプラスチック製の容器の外側を紙で被覆し
た複合容器が提案されている。また、プラスチック使用
量を大幅に低減した複合容器や、廃棄時には紙とプラス
チックの分別が可能な複合容器が種々提案されている。2. Description of the Related Art In recent years, environmental problems have become more serious and containers and packaging materials are required to be easily disposed of, and there is an increasing demand for easy incineration, recyclability, or use of recycled materials. Therefore, a composite container in which the outside of a plastic container is covered with paper has been proposed. In addition, various composite containers that greatly reduce the amount of plastic used and composite containers that can separate paper and plastic at the time of disposal have been proposed.
【０００３】プラスチックと紙からなる複合容器は、環
境問題、省資源化に対応するため、内装プラスチック容
器に使用するプラスチックの量を極力少なくする傾向に
ある。そのため内装容器自体の容器としての強度物性は
大きく低下するので、紙製の外装容器とプラスチック製
の内装容器を組み合わせることにより、容器自体の強度
物性を確保している。A composite container made of plastic and paper tends to reduce the amount of plastic used for the inner plastic container as much as possible in order to cope with environmental problems and resource saving. Therefore, the strength and physical properties of the inner container itself as a container are significantly deteriorated. Therefore, the strength and physical properties of the container itself are ensured by combining the paper outer container and the plastic inner container.
【０００４】従来の複合容器としては、ボトル、トレイ
が代表的で、この紙製容器は従来のプラスチックボトル
やプラスチックトレーと同等の容器物性、とりわけ容器
の落下強度が要求される。内装容器と外装容器は、接着
剤等を介して接合することにより、一体化することが一
般的である。プラスチック樹脂の使用量が極限近くに減
量化された複合容器において、座屈強度を確保するた
め、外装容器として比較的坪量の大きい紙部材、または
バージンパルプから製造され高強度な紙部材が一般的に
使用されている。Bottles and trays are typical of conventional composite containers, and this paper container is required to have the same physical properties as those of conventional plastic bottles and plastic trays, especially the drop strength of the container. The inner container and the outer container are generally integrated by joining them with an adhesive or the like. In order to secure the buckling strength in a composite container in which the amount of plastic resin used has been reduced to the limit, a paper member having a relatively large basis weight as an outer container or a high-strength paper member manufactured from virgin pulp is generally used. Is being used for.
【０００５】従来の複合容器においては、外装紙容器と
内装プラスチック容器の接合面は、接着性樹脂などの接
着剤により高い接着強度を得ているため、落下衝撃によ
り、接着面が剥離したり容器が破袋することはなかっ
た。しかしながら、外装容器の紙と紙の接合部（製函時
フラップなど）の接着については接着強度が不十分で落
下時に剥離したり、あるいは、接着が十分で紙の層間強
度以上の接着強度が得られていても、その接合部で紙の
層間剥離が発生し、接合部の剥離が発生する。この現象
は、複合容器が食品容器などに用いられて、結露やボイ
ル、レトルト処理により濡れているときに著しく起こり
やすくなる。この接合部の剥離がおこると、その剥離箇
所においては内装プラスチック容器のみで落下衝撃を受
けることになる。この際、外装紙容器の内容物収納部分
である内面に段差があると、内装プラスチック容器成型
時にその段差が転写される。よって、落下衝撃により外
装紙容器の接合部が剥離した場合に、内装プラスチック
容器の段差部分で衝撃を受けることになる。結果的に、
外装紙容器は接合部が剥離して落下衝撃に耐える力を失
ったことにより、成型時に外装紙容器の接合部の段差が
転写された比較的強度が小さい部分で落下衝撃を受ける
ため破袋してしまう。In the conventional composite container, the joint surface between the outer paper container and the inner plastic container has a high adhesive strength due to an adhesive such as an adhesive resin. Never broke the bag. However, with regard to the adhesion between the paper and the paper joint of the outer container (flap during box making, etc.), the adhesive strength is insufficient and peels off when dropped, or the adhesion is sufficient and an adhesive strength equal to or higher than the interlayer strength of the paper is obtained. Even if it is, delamination of the paper occurs at the joint portion and peeling of the joint portion occurs. This phenomenon is likely to occur remarkably when the composite container is used as a food container or the like and is wet due to dew condensation, boiling, or retort treatment. When this peeling of the joint portion occurs, only the inner plastic container is subjected to a drop impact at the peeled portion. At this time, if there is a step on the inner surface of the outer paper container, which is the content storage portion, the step is transferred when the inner plastic container is molded. Therefore, when the joint portion of the outer paper container is separated due to the drop impact, the impact is applied to the step portion of the inner plastic container. as a result,
The outer paper container loses the strength to withstand the drop impact due to the peeling of the joint, and the bag is crushed because the joint of the outer paper container has a relatively small strength to which the step of the joint is transferred during molding. Will end up.
【０００６】[0006]
【発明が解決しようとする課題】本発明は上記の課題を
解決することを目的として、従来の複合容器の落下強度
を著しく向上するのみならず、外装紙容器が濡れた場合
においても著しい落下強度低下をおこさず、十分な容器
強度を有し、耐水性および耐熱水性を有する複合容器を
提供することにある。SUMMARY OF THE INVENTION In order to solve the above problems, the present invention not only remarkably improves the drop strength of a conventional composite container, but also remarkably drops the strength when the outer paper container gets wet. It is an object of the present invention to provide a composite container which does not deteriorate and has sufficient container strength and has water resistance and hot water resistance.
【０００７】[0007]
【課題を解決するための手段】上記の課題は以下の手段
によって解決できる。The above-mentioned problems can be solved by the following means.
【０００８】本発明の第１発明は、製函された紙からな
る外装容器の内側にプラスチックからなる内装容器を設
けた複合容器において、外装紙容器の内容物収納部分で
ある内面が連続した平面からなることを特徴とする複合
容器としたものである。A first aspect of the present invention is a composite container in which an inner container made of plastic is provided inside an outer container made of box-formed paper, and the inner surface of the outer paper container, which is a portion for storing contents, is a flat surface. It is a composite container characterized by comprising:
【０００９】本発明の第２発明は、前記複合容器におい
て、外装紙容器の外側に、製函時の貼り合わせフラップ
を設けたことを特徴とする、請求項１に記載の複合容器
としたものである。A second invention of the present invention is the composite container according to claim 1, characterized in that, in the composite container, a bonding flap at the time of box making is provided outside the outer paper container. Is.
【００１０】本発明の第３発明は、前記外装紙容器の紙
基材が、ポリイソシアネート樹脂を添加あるいは含浸し
た樹脂含浸紙であることを特徴とする、請求項１または
請求項２に記載の複合容器としたものである。The third invention of the present invention is characterized in that the paper base material of the outer paper container is resin-impregnated paper to which polyisocyanate resin is added or impregnated. It is a composite container.
【００１１】本発明の第４発明は、前記イソシアネート
樹脂が、キシリレンジイソシアネート、またはイソホロ
ジイソシアネートのいずれか、またはその混合物からな
ることを特徴とする、請求項３に記載の複合容器とした
ものである。A fourth aspect of the present invention provides the composite container according to claim 3, wherein the isocyanate resin is made of either xylylene diisocyanate or isophorodiisocyanate, or a mixture thereof. Is.
【００１２】本発明の第５発明は、前記樹脂含浸紙にお
いて、樹脂含浸量が含浸紙の重量比１％〜１０％である
ことを特徴とする、請求項１乃至請求項４のいずれか１
項に記載の複合容器としたものである。A fifth aspect of the present invention is characterized in that, in the resin-impregnated paper, the amount of resin impregnated is 1% to 10% by weight of the impregnated paper.
It is a composite container described in the item.
【００１３】本発明の第６発明は、前記内装プラスチッ
ク容器の基材である熱可塑性樹脂が、少なくとも２種以
上の樹脂による２層以上の層構成からなることを特徴と
する、請求項１乃至請求項５のいずれか１項に記載の複
合容器としたものである。The sixth invention of the present invention is characterized in that the thermoplastic resin as a base material of the inner plastic container has a layered structure of two or more layers of at least two kinds of resins. The composite container according to claim 5.
【００１４】本発明の第７発明は、前記内装プラスチッ
ク容器に用いられる熱可塑性樹脂と、前記外装紙容器に
用いられる含浸紙に含浸された樹脂の合計重量比率が、
容器全体重量の５０％未満であることを特徴とする、請
求項１乃至請求項６のいずれか１項に記載の複合容器と
したものである。In a seventh aspect of the present invention, the total weight ratio of the thermoplastic resin used in the inner plastic container and the resin impregnated in the impregnated paper used in the outer paper container is
It is less than 50% of the total weight of the container, and is the composite container according to any one of claims 1 to 6.
【００１５】本発明の第８発明は、前記外装紙製容器が
予め金型内部に装填され、内装プラスチック容器成形と
同時に外装紙容器と一体化してなることを特徴とする、
請求項１乃至請求項７のいずれか１項に記載の複合容器
としたものである。An eighth invention of the present invention is characterized in that the outer paper container is preliminarily loaded in the mold and is integrated with the outer paper container simultaneously with molding of the inner plastic container.
The composite container according to any one of claims 1 to 7.
【００１６】本発明の第９発明は、前記内装プラスチッ
ク容器を、熱可塑性樹脂シートを真空成形あるいは真空
圧空成形して一体化して設けることを特徴とする、請求
項１乃至請求項８のいずれか１項に記載の複合容器とし
たものである。The ninth invention of the present invention is characterized in that the inner plastic container is integrally provided by vacuum forming or vacuum pressure forming of a thermoplastic resin sheet. The composite container according to item 1.
【００１７】[0017]
【発明の実施の形態】以下本発明の実施の形態につい
て、さらに詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described in more detail below.
【００１８】本発明は、製函された紙からなる外装容器
の内側にプラスチックからなる内装容器を設けた複合容
器において、外装紙容器の内容物収納部分である内面が
連続した平面からなる複合容器に関するものである。こ
こでいう連続した平面とは、平らな平面、曲面、また
は、罫線を介して折られた平面、曲面等の、面として段
差のない滑らかな状態の面を指す。外装紙容器と内装プ
ラスチック容器を接合してなる複合容器において、外装
紙容器に貼り合わせフラップ（のりしろ）を設けてその
貼り合わせフラップが外装紙容器の内面になるように製
函した場合、内装プラスチック容器をその外装紙容器内
に成形、接合すると、その貼り合わせフラップによる段
差がそのまま内装プラスチック容器に転写される。内装
プラスチック容器と外装紙容器のほぼ全体が接合された
複合容器の場合、容器の落下衝撃により、その貼り合わ
せフラップ（のりしろ）部分の剥離もしくは外装紙容器
の層間剥離による破損が起こることがある。すると複合
容器は内装のプラスチック容器のみで落下衝撃を受ける
ことになる。この際、内装プラスチック容器に、外装紙
容器の転写による段差が生じていると、落下衝撃により
内装プラスチック容器の段差に応力が集中し、その段差
から破袋が著しく起こりやすくなる。しかし、複合容器
の内装プラスチック容器に外装紙容器の貼り合わせフラ
ップの転写による段差をなくすことにより、落下衝撃を
受けて貼り合わせフラップが剥離、破損しても内装プラ
スチック容器全体に応力が分散され、複合容器の落下強
度は向上する。The present invention relates to a composite container in which an inner container made of plastic is provided inside an outer container made of box-shaped paper, and the inner surface of the outer paper container, which is a content storage portion, is a continuous flat surface. It is about. The continuous plane as used herein refers to a flat surface, a curved surface, a flat surface bent by ruled lines, a curved surface, or the like, which is a smooth surface with no steps. In a composite container made by joining an outer paper container and an inner plastic container, when the outer paper container is provided with a laminating flap and the laminated flap is made inside the outer paper container, the inner plastic When the container is molded and joined in the outer paper container, the step due to the laminating flap is directly transferred to the inner plastic container. In the case of a composite container in which almost all of the inner plastic container and the outer paper container are joined together, the drop impact of the container may cause peeling of the bonding flap (glue) portion or damage due to interlayer peeling of the outer paper container. Then, the composite container is subject to a drop impact only by the plastic container having the interior. At this time, if a step is formed in the inner plastic container due to the transfer of the outer paper container, a stress is concentrated on the step of the inner plastic container due to a drop impact, and the bag is likely to be broken from the step. However, by eliminating the step due to the transfer of the bonding flap of the outer paper container to the inner plastic container of the composite container, the stress is dispersed throughout the inner plastic container even if the bonding flap peels off or is damaged by a drop impact, The drop strength of the composite container is improved.
【００１９】また、内装プラスチック容器に上記の段差
が設けられていると、落下衝撃により、その内装プラス
チック容器は段差部分で応力を緩和できるため、外装紙
容器の貼り合わせフラップの接着部分に応力の集中が起
こり、剥離、破袋しやすくなる。それにより、上述のよ
うに内装プラスチック容器も破袋しやすくなる。すなわ
ち外装紙容器と内装プラスチック容器が一体化された複
合容器では、内装プラスチック容器をその形状に段差を
設けることなく成形することにより落下強度の向上をは
かることができる。Further, when the above-mentioned step is provided on the inner plastic container, the inner plastic container can relieve the stress at the step portion due to the drop impact, so that the stress is applied to the bonding portion of the bonding flap of the outer paper container. Concentration occurs and peeling and bag breakage are easy. As a result, as described above, the inner plastic container can be easily broken. That is, in a composite container in which the outer paper container and the inner plastic container are integrated, the inner plastic container can be molded without forming a step in its shape to improve the drop strength.
【００２０】外装紙容器を得るための板紙基材は、１０
０％バ−ジンパルプのものから古紙を含んだコ−トボ−
ル、片面にクレイコート処理されたものなど様々な種類
の原紙の紙基材を用いることが可能である。これらの紙
基材に、抄紙段階あるいは抄紙後の二次加工として外添
により、剛性、耐水性、耐熱水性を付与できる樹脂を含
浸したものでもよい。ただし、ここでの紙基材はパルプ
からなる板状の繊維構造物を全て包含し、いわゆる紙の
種類に限定されるものではない。そして板紙の厚みは目
的に応じて適宜選択すれば良い。The paperboard base material for obtaining the outer paper container is 10
Coat board containing 0% virgin pulp to recycled paper
It is possible to use various types of base paper for base paper, such as those coated with clay on one side. These paper base materials may be impregnated with a resin capable of imparting rigidity, water resistance, and hot water resistance by external addition as a secondary process at the papermaking stage or after papermaking. However, the paper base material here includes all plate-like fiber structures made of pulp, and is not limited to so-called paper types. The thickness of the paperboard may be appropriately selected according to the purpose.
【００２１】外装紙容器の内側に内装プラスチック容器
を設けることにより、容器の最内層に接合部のない極め
て密封性に優れる容器を得ることができる。ただし、こ
こで内装プラスチック容器の樹脂材料や成形方法は本発
明に限定されるものではない。By providing the inner plastic container inside the outer paper container, it is possible to obtain a container having an excellent sealing property without a joint portion in the innermost layer of the container. However, the resin material and the molding method for the inner plastic container are not limited to the present invention.
【００２２】また本発明は、具体的に外装紙容器を製函
する際に、貼り合わせフラップを外装紙容器の最外部に
設けることにより、その内面が段差のない連続した平面
となり、内装プラスチック容器の段差をなくすことがで
きる。すなわち内装プラスチック容器と外装紙容器の接
合部分はほぼ均一の接着強度を有することになり、落下
衝撃により部分的に応力が集中する部分がなくなり、落
下強度が向上する。Further, according to the present invention, when the outer paper container is concretely manufactured, the laminating flap is provided at the outermost part of the outer paper container so that the inner surface of the outer paper container becomes a continuous flat surface without a step, and the inner plastic container is formed. It is possible to eliminate the level difference. That is, the joint portion between the inner plastic container and the outer paper container has almost uniform adhesive strength, and there is no portion where stress is partially concentrated due to a drop impact, so that the drop strength is improved.
【００２３】また本発明は、紙基材を耐水、耐熱水処理
する処理剤として、イソシアネート系樹脂を用いると、
耐水性、耐熱性が著しく向上し、好ましい。外装紙容器
にポリイソシアネート樹脂を添加あるいは含浸した紙基
材を用いることにより、外装紙容器に耐熱水性が付与で
き、複合容器としてレトルト処理やボイル処理に耐える
ものとなる。Further, according to the present invention, when an isocyanate resin is used as a treating agent for treating a paper base material with water resistance and hot water resistance,
Water resistance and heat resistance are remarkably improved, which is preferable. By using a paper base material to which the polyisocyanate resin is added or impregnated in the outer paper container, it is possible to impart hot water resistance to the outer paper container and to endure retort treatment or boil treatment as a composite container.
【００２４】このイソシアネート樹脂は紙に含浸するこ
とにより紙の湿潤強度が向上し、吸水性も著しく低減す
る。外装紙容器としてイソシアネート樹脂含浸紙を用い
ることにより、外装紙容器が乾燥状態のみならず、湿潤
状態にあっても、保形性、座屈強度などが極めて優れた
外装紙容器とすることができる。また、ボイル殺菌やレ
トルト殺菌工程においても、イソシアネート樹脂含浸紙
を外装紙容器として用いると、それらの熱水条件下にお
いても極めて高い保形性を示し、耐熱水性を有すること
ができる。By impregnating paper with this isocyanate resin, the wet strength of the paper is improved and the water absorption is also significantly reduced. By using an isocyanate resin-impregnated paper as the exterior paper container, it is possible to obtain an exterior paper container having extremely excellent shape retention, buckling strength, etc. even when the exterior paper container is in a wet state as well as in a dry state. . Further, also in the boiling sterilization or retort sterilization step, when the isocyanate resin-impregnated paper is used as the outer paper container, it exhibits extremely high shape retention under hot water conditions and can have hot water resistance.
【００２５】この外装紙容器を耐熱水化した複合容器に
おいても、レトルト処理時には、外装紙容器の貼り合わ
せフラップの接着強度、外装紙容器の層間強度ともに、
乾燥時に比較すると著しい強度低下が起こる。すなわ
ち、落下衝撃に対して強度が著しく低下する。そのため
外装紙容器の内容物収納部分である内面を連続した平面
からなるようにして内装プラスチック容器の段差をなく
し、応力集中が起こらなくすることは、熱水処理時の複
合容器の落下強度の確保に対して極めて有効な手段であ
る。Even in the composite container in which the outer paper container is made heat resistant, both the adhesive strength of the laminating flap of the outer paper container and the interlaminar strength of the outer paper container during the retort treatment,
A significant decrease in strength occurs when compared to when dried. That is, the strength is remarkably reduced against a drop impact. Therefore, by making the inner surface, which is the content storage part of the outer paper container, a continuous flat surface to eliminate steps in the inner plastic container and prevent stress concentration, it is necessary to secure the drop strength of the composite container during hot water treatment. It is a very effective means against.
【００２６】イソシアネート樹脂含浸紙を外添により得
る場合は、使用する紙基材の種類として、１００％バ−
ジンパルプのものや故紙からなるコ−トボ−ル、再生故
紙を一部含むもの、ＮＢＫＰ材やＬＢＫＰ材の使用率、
木材パルプ以外のケナフ、バンブーから抄紙された紙、
片面にクレイコート処理された紙、など様々な種類の原
紙を用いることが可能である。ここでの紙基材はパルプ
からなる板状の繊維構造物を全て包含し、いわゆる紙の
種類に限定されるものではない。すなわち紙容器の形状
や内容物の種類や重量により、基材として使用可能なも
のを任意に選択すればよい。When the isocyanate resin-impregnated paper is obtained by external addition, the type of paper base used is 100% bar.
Coat ball made of gin pulp or recycled paper, partially containing recycled recycled paper, usage rate of NBKP material and LBKP material,
Kenaf other than wood pulp, paper made from bamboo,
It is possible to use various types of base paper, such as clay-coated paper on one side. The paper base material here includes all plate-like fiber structures made of pulp, and is not limited to so-called paper types. That is, a material that can be used as a base material may be arbitrarily selected depending on the shape of the paper container and the type and weight of the contents.
【００２７】そして、抄紙後の二次加工として剛性、耐
水性、耐熱水性を付与できる樹脂を含浸するものであ
る。この外添による含浸方法として、繊維構造物を含浸
剤中に浸し過剰量の含浸剤を一時的に付与できるディッ
ピング法や、好ましくは、含浸剤を一定量だけ塗工また
は含浸させるグラビアコーティング法や、ロールコーテ
ィング法などがあり、基材繊維構造物の表裏から含浸処
理することも可能である。Then, as a secondary processing after papermaking, a resin capable of imparting rigidity, water resistance and hot water resistance is impregnated. As the impregnation method by the external addition, a dipping method capable of temporarily applying an excessive amount of the impregnating agent by immersing the fiber structure in the impregnating agent, or preferably, a gravure coating method for coating or impregnating a certain amount of the impregnating agent, or There is a roll coating method, etc., and it is also possible to impregnate the base fiber structure from the front and back.
【００２８】さらに２ユニット以上あるグラビア含浸方
法では、はじめに紙基材内部に含浸させる含浸剤を片面
もしくは両面より施し、基材内部にまで含浸剤を浸透さ
せる。その後の最後のユニットで紙基材の表面にコーテ
ィング被膜層の形成等が可能となる。そこで得られた含
浸紙は、例えば含浸紙の内部全体にわたり湿潤紙力増強
剤などが含浸され高い湿潤強度を有し、含浸紙表層には
はっ水剤等を配することにより高いはっ水効果を有する
ことができる。すなわち紙基材に含浸剤を供給できる方
法であれば、使用される紙基材や含浸剤の種類にもよる
が、いずれの方法を任意に選択することができる。さら
にはこれらの加工は二次加工的に行われるため、抄紙工
程に比較すると少量の加工が安価に行うことができる。Further, in the gravure impregnation method having two or more units, first, the impregnating agent for impregnating the inside of the paper base material is applied from one side or both sides, and the impregnating agent penetrates into the inside of the base material. In the final unit after that, it becomes possible to form a coating film layer on the surface of the paper substrate. The impregnated paper thus obtained has a high wet strength by, for example, being impregnated with a wet paper strength enhancer etc. throughout the inside of the impregnated paper, and a high water repellency can be obtained by disposing a water repellent agent on the surface layer of the impregnated paper. Can have an effect. That is, any method that can supply the impregnating agent to the paper base material can be arbitrarily selected, depending on the type of the paper base material and the impregnating agent used. Furthermore, since these processes are performed as secondary processes, a small amount of processes can be performed at low cost as compared with the papermaking process.
【００２９】含浸するイソシアネート系樹脂として、ポ
リイソシアネート化合物として、これまで知られている
各種のもの、例えばフェニレンジイソシアネート（ＰＤ
Ｉ）、トリレンジイソシアネート（ＴＤＩ）、ナフタレ
ンジイソシアネート（ＮＤＩ）、４，４‘ジイソシアネ
ートジフェニルメタン（ＭＤＩ）、等の芳香族ジイソシ
アネート、キシリレンジイソシアネート（ＸＤＩ）等の
芳香族脂肪族ジイソシアネート、水添ＴＤＩ、水添ＸＤ
Ｉ、水添ＭＤＩ、ヘキサメチレンジイソシアネート（Ｈ
ＭＤＩ）イソホロンジイソシアネート（ＩＰＤＩ）等の
脂肪族、若しくは脂環状ジイソシアネートおよびこれら
の誘導体であるポリオール付加物、ビュレット体、３量
体である３官能以上のポリイソシアネート、リジントリ
イソシアネート（ＬＴＩ）等の３官能イソシアネートの
他、イソシアネートを含む各種のオリゴマー、ポリマー
を使用することができる。As the isocyanate resin to be impregnated, various known polyisocyanate compounds, for example, phenylene diisocyanate (PD
I), aromatic diisocyanates such as tolylene diisocyanate (TDI), naphthalene diisocyanate (NDI) and 4,4 ′ diisocyanate diphenylmethane (MDI), aromatic aliphatic diisocyanates such as xylylene diisocyanate (XDI), hydrogenated TDI, Hydrogenated XD
I, hydrogenated MDI, hexamethylene diisocyanate (H
MDI) Aliphatic or alicyclic diisocyanates such as isophorone diisocyanate (IPDI) and polyol adducts of these derivatives, burettes, trifunctional or more polyisocyanates that are trimers, lysine triisocyanate (LTI) and the like 3 In addition to the functional isocyanate, various oligomers and polymers containing isocyanate can be used.
【００３０】また、前記イソシアネート樹脂材料の中
で、この含浸紙を用いた複合容器を食品用途に使用する
場合は、ＸＤＩ、またはＩＰＤＩ系のいずれかの樹脂を
用いることが好ましい。Further, among the above isocyanate resin materials, when the composite container using the impregnated paper is used for food use, it is preferable to use either XDI or IPDI resin.
【００３１】本発明の含浸紙に含浸する樹脂の量は、前
述のイソシアネート樹脂などの高度に湿潤強度を向上で
きる薬剤の場合でも含浸紙の重量比で１％〜１０％であ
ることが好ましい。使用する含浸薬剤の構造にもよる
が、前述のイソシアネート樹脂を重量比で１％ないし１
０％含浸することにより、含浸紙の湿潤時引っ張り強度
を乾燥時の３０％以上とすることができる。さらにボイ
ル殺菌処理やレトルト殺菌処理に相当する熱水処理後に
おいても、その湿潤時引っ張り強度を乾燥時の３０％以
上とすることができる。このように設定することによ
り、耐熱性、耐水性が向上し、湿潤時における容器の保
形性、剛性が維持できる。The amount of the resin impregnated in the impregnated paper of the present invention is preferably 1% to 10% in terms of the weight ratio of the impregnated paper even in the case of the above-mentioned isocyanate resin and other chemicals capable of highly improving the wet strength. Depending on the structure of the impregnating agent used, the above-mentioned isocyanate resin may be used in an amount of 1% to 1% by weight.
When the impregnated paper is impregnated with 0%, the wet tensile strength of the impregnated paper can be made 30% or more of the dry tensile strength. Further, even after the hot water treatment corresponding to the boil sterilization treatment or the retort sterilization treatment, the wet tensile strength can be 30% or more of the dry tensile strength. By setting in this way, heat resistance and water resistance are improved, and the shape retention and rigidity of the container when wet can be maintained.
【００３２】本発明の樹脂材料は、単一の樹脂材料だけ
でなく、２種以上の樹脂材料で２層以上の積層構成とす
ることにより、各種機能を付与することができる。The resin material of the present invention is not limited to a single resin material, but can be provided with various functions by forming a laminated structure of two or more layers of two or more resin materials.
【００３３】複合容器の内装プラスチック容器として用
いる樹脂材料として、ポリエチレン樹脂やポリプロピレ
ン樹脂などポリオレフィン系の樹脂のほか、ポリエステ
ル樹脂なども使用される。これらの樹脂と、ポリアミド
樹脂やエチレン−ビニルアルコ−ル共重合体のようなバ
リア性樹脂を、２層以上の多層構成として容器の内面に
設けることにより、複合容器に酸素バリア性や保香性を
付与することができる。また、外装紙容器との接合面に
紙との接着性樹脂を設けることにより、内装容器の成形
と同時に外装容器を一体化することもできる。As the resin material used for the inner plastic container of the composite container, polyester resin and the like are used in addition to polyolefin resin such as polyethylene resin and polypropylene resin. By providing these resins and a barrier resin such as a polyamide resin or an ethylene-vinyl alcohol copolymer on the inner surface of the container as a multi-layer structure having two or more layers, the composite container can be provided with an oxygen barrier property and an aroma retaining property. Can be granted. Further, by providing an adhesive resin for paper on the joint surface with the external paper container, the external container can be integrated with the molding of the internal container at the same time.
【００３４】本発明の複合容器において、内装プラスチ
ック容器と外装紙容器の紙に含浸ないし積層された樹脂
の重量比率を複合容器全体重量の５０％未満とすると、
廃棄時に可燃ゴミ、またはリサイクルゴミとして取り扱
われるので好ましい。In the composite container of the present invention, if the weight ratio of the resin impregnated or laminated on the paper of the inner plastic container and the outer paper container is less than 50% of the total weight of the composite container,
It is preferable because it is handled as combustible waste or recycled waste at the time of disposal.
【００３５】また、外装紙容器として前述のように樹脂
含浸紙を用いることにより、乾燥時の容器剛性および湿
潤時の容器剛性を高めることができる。したがって、複
合容器は内装プラスチック容器のプラスチック肉厚を著
しく薄くすることができ、容器全体としての樹脂使用量
を５０％未満としても、十分な容器強度を備えるものと
なる。さらに好ましくは、充填される内容物や内装プラ
スチック容器の成形方法にもよるが、樹脂使用量を３０
％未満とすることが可能であり、乾燥時や湿潤時におい
ても十分な容器強度を備えることができる。Further, by using the resin-impregnated paper as the outer paper container as described above, the rigidity of the container when dried and the rigidity of the container when wet can be increased. Therefore, the composite container can remarkably reduce the plastic wall thickness of the inner plastic container, and has sufficient container strength even if the amount of resin used as the entire container is less than 50%. More preferably, the amount of resin used is 30 depending on the content to be filled and the method of molding the inner plastic container.
%, And sufficient container strength can be provided even when dry or wet.
【００３６】本発明の容器の最内層を真空成形あるいは
圧空成形したプラスチック容器とすることにより、容器
の最内層に接合部のないきわめて密封性に優れる容器を
得ることができ、さらには既存の目的に応じた機能を有
する真空成型用の多層シート材料等が利用でき、安価に
落下強度に優れる複合容器を得ることができる。By forming the innermost layer of the container of the present invention as a vacuum-molded or pressure-molded plastic container, it is possible to obtain a container having an excellent sealing property with no joint portion in the innermost layer of the container, and further, the existing object. A multilayer sheet material for vacuum forming having a function corresponding to the above can be used, and a composite container excellent in drop strength can be obtained at low cost.
【００３７】さらには、ボイル、レトルト耐性を付与さ
れた複合容器は、トレー形状で利用されることが多く、
真空成形、真空圧空成形は成形方法として好ましいとい
える。Further, the composite container provided with resistance to boiling and retort is often used in a tray shape,
It can be said that vacuum forming and vacuum pressure forming are preferable as forming methods.
【実施例】以下、本発明の具体的な実施例を示して詳細
に説明する。EXAMPLES The present invention will now be described in detail with reference to specific examples.
【００３８】＜実施例１＞外装容器として用いる含浸紙
の紙基材として坪量３００ｇ／ｍ２のノーコートカップ
原紙を使用し、イソシアネート樹脂をグラビアコーティ
ング法により紙基材の両面から含浸処理を行い、含浸紙
を得た。この含浸紙にさらに印刷を施した。これをトレ
イ形状の紙製容器となるよう打ち抜き接着フラップが容
器外側になるよう製函し、本発明の外装紙容器を得た。
この外装紙容器を、真空シート成型器の金型内に挿入
し、容器の内面側から、ポリプロピレン／ＥＶＯＨ／ポ
リプロピレン／接着剤構成のシートにて、真空成形を行
うと同時に外装紙容器と接着し、トレイ形状の複合容器
を得た。複合容器の容量は３００ｍｌである。得られた
複合容器に食品を充填し、蓋材をシールした後にレトル
ト処理を行った。複合容器は、熱水処理においても十分
な強度を有しており、乾燥時には高さ１ｍからの落下衝
撃に、レトルト後の湿潤時（４０℃）では５０ｃｍの落
下衝撃に耐えるものであった。また外装含浸紙端面の層
間剥離等の外観不良もなく、レトルト処理に十分耐えう
るものであった。またトレイ形状の複合容器は、内容物
を食するときの簡便なトレー容器として利用できるもの
であった。（ＥＶＯＨ：エチレン−酢酸ビニルケン化
物）Example 1 An uncoated cup base paper having a basis weight of 300 g / m 2 was used as the paper base material of the impregnated paper used as the outer container, and the isocyanate resin was impregnated from both sides of the paper base material by the gravure coating method. , Impregnated paper was obtained. The impregnated paper was further printed. This was made into a tray-shaped paper container so that the punched adhesive flap was on the outside of the container to obtain an outer paper container of the present invention.
This outer paper container is inserted into the mold of a vacuum sheet molding machine, and from the inner surface of the container, a sheet of polypropylene / EVOH / polypropylene / adhesive composition is used to perform vacuum molding and at the same time bond it to the outer paper container. A tray-shaped composite container was obtained. The capacity of the composite container is 300 ml. The obtained composite container was filled with food, the lid member was sealed, and then retort treatment was performed. The composite container had sufficient strength even in hot water treatment, and was resistant to a drop impact from a height of 1 m when dried and a drop impact of 50 cm when wet (40 ° C.) after retort. Further, there was no appearance defect such as delamination of the end surface of the exterior impregnated paper, and it was able to sufficiently withstand the retort treatment. In addition, the tray-shaped composite container can be used as a simple tray container when eating the contents. (EVOH: saponified ethylene-vinyl acetate)
【００３９】＜比較例１＞外装紙容器として用いる紙と
して実施例１と同じ紙で同じ容器形状となるよう打ち抜
き加工を行った。外装紙容器製函時に貼り合わせフラッ
プを容器内面側に接着し、実施例１と同じ内装材料で同
じ真空成形をおこない、同じ形状、容量の複合容器を得
た。得られた複合容器に食品を充填し、蓋材をシールし
た後にレトルト処理を行った。複合容器は、熱水処理に
おいても十分な強度を有していた。また外装含浸紙端面
の層間剥離等の外観不良もなく、レトルト処理に十分耐
えうるものであった。またトレイ形状の複合容器は、内
容物を食するときの簡便なトレー容器として利用できる
ものであった。しかし、落下強度に関しては、乾燥時に
は高さ５０ｃｍからの落下衝撃に、レトルト後の湿潤時
（４０℃）では３０ｃｍの落下衝撃にしか耐えることは
できなかった。（ＥＶＯＨ：エチレン−酢酸ビニルケン
化物）Comparative Example 1 The same paper as in Example 1 was used as the outer paper container, and punching was performed so that the same container shape was obtained. The laminated flap was adhered to the inner surface of the container during the packaging of the outer paper container, and the same vacuum molding was performed using the same interior material as in Example 1 to obtain a composite container having the same shape and capacity. The obtained composite container was filled with food, the lid member was sealed, and then retort treatment was performed. The composite container had sufficient strength even in hot water treatment. Further, there was no appearance defect such as delamination of the end surface of the exterior impregnated paper, and it was able to sufficiently withstand the retort treatment. In addition, the tray-shaped composite container can be used as a simple tray container when eating the contents. However, with respect to the drop strength, it was only possible to withstand a drop impact from a height of 50 cm when dry and a drop impact of 30 cm when wet (40 ° C.) after retort. (EVOH: saponified ethylene-vinyl acetate)
【００４０】[0040]
【発明の効果】本発明により、製函された紙からなる外
装容器の内側にプラスチックからなる内装容器を設けた
複合容器において、外装紙容器の内容物収納部分である
内面が連続した平面からなることで、落下強度に極めて
優れる複合容器とすることができる。さらには、耐熱水
性紙容器の落下強度を向上するとすることで、その効果
は著しく、極めて落下衝撃に優れる耐熱水性を有する複
合容器とすることができる。According to the present invention, in a composite container in which an inner container made of plastic is provided inside an outer container made of box-made paper, the inner surface of the outer paper container, which is a content storage portion, is a continuous flat surface. As a result, a composite container having extremely excellent drop strength can be obtained. Furthermore, by improving the drop strength of the hot water resistant paper container, the effect is remarkable, and a composite container having hot water resistance that is extremely excellent in drop impact can be obtained.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｂ３１Ｂ 49/02 Ｂ３１Ｂ 49/02 ４Ｆ２０８ Ｂ３２Ｂ 1/02 Ｂ３２Ｂ 1/02 ４Ｌ０５５ 27/00 27/00 Ｈ 27/10 27/10 Ｂ６５Ｄ 5/56 Ｂ６５Ｄ 5/56 Ａ 65/40 65/40 Ａ 65/42 65/42 Ｃ 77/04 77/04 Ｚ Ｄ２１Ｈ 19/24 Ｄ２１Ｈ 19/24 Ｂ // Ｂ２９Ｋ 105:20 Ｂ２９Ｋ 105:20 711:12 711:12 Ｂ２９Ｌ 9:00 Ｂ２９Ｌ 9:00 22:00 22:00 Ｆターム(参考） 3E060 BC04 BC08 DA11 DA21 DA30 EA03 3E067 AA03 AA11 AB01 AB81 BA06A BB02A BB14A BB25A CA07 FA01 FB15 FC01 3E075 BA22 BB02 CA01 DC37 GA03 3E086 AB01 AD05 BA04 BA14 BA15 BA25 BB85 BB87 CA01 4F100 AK01B AK01C AK07 AK51A AK69 AL05A BA02 BA03 BA07 BA10A BA10C BA27 DG10A EH46 EH461 EJ39 EJ392 EJ82A EJ83A GB23 GB66 GB71 JB07 JB16B JB16C JJ03 YY00A 4F208 AD06 AD33 AD34 AG03 AG07 MA01 MA03 MB01 MB11 MG04 MG11 MJ05 4L055 AG77 AH17 AH37 AJ02 BE08 BE10 EA14 FA19 FA20 GA05 GA50 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) B31B 49/02 B31B 49/02 4F208 B32B 1/02 B32B 1/02 4L055 27/00 27/00 H 27 / 10 27/10 B65D 5/56 B65D 5/56 A 65/40 65/40 A 65/42 65/42 C 77/04 77/04 Z D21H 19/24 D21H 19/24 B // B29K 105: 20 B29K 105: 20 711: 12 711: 12 B29L 9:00 B29L 9:00 22:00 22:00 F Term (reference) 3E060 BC04 BC08 DA11 DA21 DA30 EA03 3E067 AA03 AA11 AB01 AB81 BA06A BB02A BB14A BB25A CA07 FA01 FB15 FC01 3E075 BA22 BB02 CA01 DC37 GA03 3E086 AB01 AD05 BA04 BA14 BA15 BA25 BB85 BB87 CA01 4F100 AK01B AK01C AK07 AK51A AK69 AL05A BA02 BA03 BA07 BA10A BA10C BA27 DG10A EH46 EH461 EJ39 EJ392 EJ82A GB6JB16J16BJEJB 6 AD33 AD34 AG03 AG07 MA01 MA03 MB01 MB11 MG04 MG11 MJ05 4L055 AG77 AH17 AH37 AJ02 BE08 BE10 EA14 FA19 FA20 GA05 GA50
Claims (9)
ラスチックからなる内装容器を設けた複合容器におい
て、外装紙容器の内容物収納部分である内面が連続した
平面からなることを特徴とする複合容器。1. A composite container in which an inner container made of plastic is provided inside an outer container made of box-made paper, wherein an inner surface of the outer paper container, which is a content storage portion, is a continuous flat surface. A composite container.
に、製函時の貼り合わせフラップを設けたことを特徴と
する、請求項１に記載の複合容器。2. The composite container according to claim 1, characterized in that, in the composite container, a bonding flap at the time of box making is provided on the outside of the outer paper container.
ネート樹脂を添加あるいは含浸した樹脂含浸紙であるこ
とを特徴とする、請求項１または請求項２に記載の複合
容器。3. The composite container according to claim 1, wherein the paper base material of the outer paper container is a resin-impregnated paper to which a polyisocyanate resin has been added or impregnated.
イソシアネート、またはイソホロジイソシアネートのい
ずれか、またはその混合物からなることを特徴とする、
請求項３に記載の複合容器。4. The isocyanate resin is made of either xylylene diisocyanate or isophorodiisocyanate, or a mixture thereof.
The composite container according to claim 3.
浸紙の重量比１％〜１０％であることを特徴とする、請
求項１乃至請求項４のいずれか１項に記載の複合容器。5. The composite container according to claim 1, wherein the resin-impregnated paper has a resin impregnation amount of 1% to 10% by weight of the impregnated paper. .
可塑性樹脂が、少なくとも２種以上の樹脂による２層以
上の層構成からなることを特徴とする、請求項１乃至請
求項５のいずれか１項に記載の複合容器。6. The thermoplastic resin as a base material of the inner plastic container has a layer structure of two or more layers of at least two kinds of resins, according to any one of claims 1 to 5. The composite container according to item 1.
可塑性樹脂と、前記外装紙容器に用いられる含浸紙に含
浸された樹脂の合計重量比率が、容器全体重量の５０％
未満であることを特徴とする、請求項１乃至請求項６の
いずれか１項に記載の複合容器。7. The total weight ratio of the thermoplastic resin used in the inner plastic container and the resin impregnated in the impregnated paper used in the outer paper container is 50% of the total weight of the container.
The composite container according to any one of claims 1 to 6, which is less than.
れ、内装プラスチック容器成形と同時に外装紙容器と一
体化してなることを特徴とする、請求項１乃至請求項７
のいずれか１項に記載の複合容器。8. The outer paper container is preliminarily loaded in the mold and is integrated with the outer paper container simultaneously with molding of the inner plastic container.
The composite container according to any one of 1.
脂シートを真空成形あるいは真空圧空成形して一体化し
て設けることを特徴とする、請求項１乃至請求項８のい
ずれか１項に記載の複合容器。9. The composite according to claim 1, wherein the inner plastic container is integrally formed by vacuum forming or vacuum pressure forming a thermoplastic resin sheet. container.