JP2003002584A - Counter-weight for construction machine, manufacturing method therefor, and method of recycling used counter- weight for construction machine - Google Patents
Counter-weight for construction machine, manufacturing method therefor, and method of recycling used counter- weight for construction machineInfo
- Publication number
- JP2003002584A JP2003002584A JP2001186917A JP2001186917A JP2003002584A JP 2003002584 A JP2003002584 A JP 2003002584A JP 2001186917 A JP2001186917 A JP 2001186917A JP 2001186917 A JP2001186917 A JP 2001186917A JP 2003002584 A JP2003002584 A JP 2003002584A
- Authority
- JP
- Japan
- Prior art keywords
- iron
- construction machine
- counterweight
- case
- filling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、油圧ショベルや移
動式クレーン等の大型の建設機械用カウンタウエイトお
よびその製造法並びに使用済の建設機械用カウンタウエ
イトのリサイクル法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a counterweight for large construction machines such as hydraulic excavators and mobile cranes, a method for manufacturing the counterweight, and a method for recycling used construction machine counterweights.
【０００２】[0002]
【従来の技術】近年、埋め立て処分場の逼迫、資源枯渇
などの理由から循環型社会への移行の必要性が叫ばれて
おり、リサイクルの必要性は建設機械においても例外で
はない。ところで、建設機械は老朽化により平均して１
０〜１５年程度で廃棄処分されているが、建設機械の主
要部分は金属部品で構成されており、これらの金属部品
は金属資源としてリサイクル使用が可能である。一般に
油圧ショベルや移動式クレーン等の建設機械においては
上部旋回体の後部にケース本体と蓋とからなり、内部に
重量骨材が充填されたカウンタウエイトを装着してフロ
ント重量とのバランスを取るようになっている。しかし
ながら、重量骨材充填型のカウンタウエイトに使用され
る充填骨材は、リサイクルが困難な重量骨材をコンクリ
ートで固めたものであるために、埋め立て処分せざるを
得ないものであった。また、カウンタウエイトの形状、
寸法及び重量などの特徴が建設機械の仕様、デザインに
より異なるために旧機種の廃カウンタウエイトを新機種
に再使用することも甚だ困難なものであった。2. Description of the Related Art In recent years, the necessity of transition to a recycling-oriented society has been sought after due to reasons such as tight landfill sites and resource exhaustion, and the need for recycling is no exception for construction machinery. By the way, construction machinery is aging and on average 1
Although it is disposed of in about 0 to 15 years, the major part of construction machinery is composed of metal parts, and these metal parts can be recycled and used as metal resources. Generally, in construction machines such as hydraulic excavators and mobile cranes, a counterweight consisting of a case body and a lid behind the upper revolving structure, and a counterweight filled with heavy aggregate inside is installed to balance with the front weight. It has become. However, since the filled aggregate used for the counterweight of the heavy aggregate filled type is a hard aggregate that is hard to recycle and hardened with concrete, it must be disposed of by landfill. Also, the shape of the counterweight,
It is very difficult to reuse the old counterweight for the new model because the features such as size and weight differ depending on the specifications and design of the construction machine.
【０００３】そこで、リサイクル可能な重量骨材充填型
のカウンタウエイトとして、特開平６−２６４４７０号
公報には、不要となった建設機械の構成部品、例えば、
ゴムクローラの芯金を重量骨材として使用する建設機械
用カウンタウエイトが開示されているが、廃カウンタウ
エイトの収集、分解および回収した重量骨材の破砕、再
使用にコストが掛かり過ぎるうえに、回収した重量骨材
では所望の密度を確保することが困難で、回収した重量
骨材の極一部しか再使用することができないという問題
があり、従って、安価で、しかも、充填された重量骨材
の全量がリサイクル可能な建設機械用カウンタウエイト
が求められている。Therefore, as a recyclable counterweight of a heavy aggregate filling type, Japanese Unexamined Patent Publication No. 6-264470 discloses a construction component which is no longer necessary, for example,
Although a counterweight for construction machinery that uses a metal core of a rubber crawler as heavy aggregate is disclosed, collection of disassembled counterweight, disassembly, crushing of the recovered heavy aggregate, and re-use are too costly. It is difficult to secure the desired density with the recovered heavy aggregate, and there is a problem that only a very small part of the recovered heavy aggregate can be reused. There is a demand for counterweights for construction machinery that can recycle all materials.
【０００４】ところで、鉄は密度が７．８ｇ／ｃｍ3 と
高く、安価であるために、年間数千万トンもの膨大な量
の鉄スクラップが製鋼用の鉄源として使用されている。
しかし、発生する鉄や酸化鉄などの鉄系廃棄物の全量が
鉄原料としてリサイクルされている訳ではない。例え
ば、鉄鋼を切削、切断、研削して発生したダライ粉、シ
ョットブラストで発生する鉄粉や酸化鉄粉を含む集塵ダ
スト、石材切断に使用されているガングソウより排出さ
れる比較的粒径の小さい廃鉄砂、ショットブラストのセ
ットリングチャンバー廃棄物である比較的粒径の大きい
廃ショットなどの粉末状、粒子状の鉄系廃棄物は、その
発生量が少ない、形状や大きさが鉄源として不向きであ
る、或いはリサイクルに多大な工数を要する等の理由に
より、再利用されることなくそのまま埋め立て処分され
てきた。By the way, since iron has a high density of 7.8 g / cm 3 and is inexpensive, a huge amount of tens of million tons of iron scrap is used as an iron source for steelmaking.
However, not all iron-based wastes such as iron and iron oxide generated are recycled as iron raw materials. For example, Dalai powder generated by cutting, cutting, and grinding steel, dust collection dust containing iron powder and iron oxide powder generated by shot blasting, and comparatively large particle size exhausted from gangsaw used for stone cutting A small amount of iron-based waste, such as small waste iron sand and waste shot with a relatively large particle size, which is waste from the settling chamber of shot blasting, has a small amount of generation. However, it has been disposed of in landfill as it is without being reused because it is unsuitable as the above or because it requires a large number of man-hours for recycling.
【０００５】[0005]
【発明が解決しようとする課題】本発明が解決しようと
するところは上記したような従来の問題点を解消し、こ
れまで埋め立て処分に回されていた微細な鉄系廃棄物で
も重量充填物として利用することにより、安価で、しか
も、リサイクル可能な建設機械用カウンタウエイトを提
供することにある。The problem to be solved by the present invention is to solve the above-mentioned problems of the prior art, and even fine iron-based wastes that have been sent to landfill as heavy packings. An object of the present invention is to provide a cheap and recyclable counterweight for construction machinery by utilizing the counterweight.
【０００６】[0006]
【課題を解決するための手段】上記の課題を解決するた
めになされた本発明は、鉄系の粉粒体と、鉄系の成形体
のいずれか一方または双方を、重量充填物としてケース
内に充填したことを特徴とする建設機械用カウンタウエ
イトを請求項１の発明とし、鉄系の粉粒体と、鉄系の成
形体のいずれか一方または双方を、重量充填物として水
とともにケース内に充填したことを特徴とする建設機械
用カウンタウエイトを請求項２の発明とし、鉄系の粉粒
体と、鉄系の成形体のいずれか一方または双方を、水お
よび製鋼材料として使用可能な水硬性粉粒体とともに重
量充填物としてケース内に充填固化したことを特徴とす
る建設機械用カウンタウエイトを請求項３の発明とし、
前記した請求項１〜３の何れかに記載の発明における鉄
系の粉粒体と、鉄系の成形体を、鉄系廃棄物よりなるも
のとした建設機械用カウンタウエイトを請求項４の発明
とし、請求項１〜４の何れかに記載の発明において、ケ
ース内の重量充填物の密度を４ｇ／ｃｍ3 以上とした建
設機械用カウンタウエイトを請求項５の発明とし、ま
た、前記した請求項１〜５の何れかに記載の発明におけ
る鉄系の粉粒体を、ダライ粉、ショットブラストの集塵
ダスト、ショットブラスト後の廃ショット、ガングソウ
の消耗により排出される廃鉄砂の少なくとも１種を含む
ものとしたものが請求項６の発明であり、これら請求項
１〜６の何れかに記載の発明における鉄系の成形体を、
円相当径で５０ｍｍ以下の塊状成形体とした建設機械用
カウンタウエイトを請求項７の発明とする。また、鉄系
の粉粒体と、鉄系の成形体のいずれか一方または双方を
主材とする充填材料を、ケース内の充填密度が４ｇ／ｃ
ｍ3 以上となるように計量調整する工程と、この充填材
料をケース内に重量充填物として充填する工程とよりな
ることを特徴とする建設機械用カウンタウエイトの製造
法を請求項８の発明とする。さらに、前記した請求項１
〜７の何れかに記載の建設機械用カウンタウエイトが使
用済とされたとき、これを建設機械から取り外して製鋼
用の鉄源として使用することを特徴とする建設機械用カ
ウンタウエイトのリサイクル法を請求項９の発明とし、
使用済の建設機械用カウンタウエイトを解体して所要の
大きさの解体片とする工程と、この解体片を製鋼に用い
る炉の種類に応じたものに分類する工程と、前記工程で
分類された解体片を製鋼用の鉄源の少なくとも一部とし
て所要の炉に投入して製鋼する工程とよりなることを特
徴とする請求項９に記載の使用済の建設機械用カウンタ
ウエイトのリサイクル法を請求項１０の発明とし、請求
項１〜７の何れかに記載の建設機械用カウンタウエイト
が使用済とされたとき、これを建設機械から取り外して
重量充填物をケースから取り出し、この重量充填物をケ
ースの投入口より充填可能な大きさとして新規なケース
に充填し、建設機械用カウンタウエイトとして再使用す
ることを特徴とする使用済の建設機械用カウンタウエイ
トのリサイクル法を請求項１１の発明とする。SUMMARY OF THE INVENTION The present invention, which has been made to solve the above-mentioned problems, provides a case in which one or both of an iron-based powder or granular material and an iron-based compact are used as a heavy packing in a case. The counterweight for construction machine according to claim 1 is characterized in that the iron-based powder or granular material and / or the iron-based molded body, or both of them, are used as a heavy filling together with water in the case. A counterweight for construction machinery characterized in that it is filled in the invention is defined as the invention of claim 2, and either one or both of the iron-based powder and granular material can be used as water and steel-making materials. A counterweight for a construction machine, characterized by being filled and solidified in a case as a heavy filling together with a hydraulic powder and granules.
A counterweight for a construction machine, wherein the iron-based powder or granular material according to any one of claims 1 to 3 and the iron-based compact made of iron-based waste are used. In the invention according to any one of claims 1 to 4, a counterweight for a construction machine, wherein the density of the heavy packing in the case is 4 g / cm 3 or more, is defined as the invention of claim 5, and Item 1. The iron-based powder or granular material according to any one of the items 1 to 5 is used as at least one of waste iron sand discharged by Dalai powder, dust collected by shot blast, waste shot after shot blast, and consumption of gang sow. It is the invention of claim 6 that contains a seed, and the iron-based molded article according to any one of claims 1 to 6,
A counterweight for a construction machine, which is a block-shaped body having a circle equivalent diameter of 50 mm or less, is the invention of claim 7. In addition, the packing density of the iron-based powder and / or the iron-based compact, which is a main material, or both, is 4 g / c.
9. A method of manufacturing a counterweight for construction machinery, comprising: a step of measuring and adjusting so as to be m 3 or more; and a step of filling the filling material as a heavy filling in a case. To do. Further, the above-mentioned claim 1
When the construction machine counterweight according to any one of items 1 to 7 is used, it is removed from the construction machine and used as an iron source for steelmaking. According to the invention of claim 9,
The steps of disassembling the used construction machine counterweight into dismantled pieces of the required size, the step of classifying the disassembled pieces into pieces according to the type of furnace used for steelmaking, and the steps described above The method for recycling used counterweights for construction machinery according to claim 9, characterized in that the method comprises the step of introducing the dismantled pieces into at least a part of an iron source for steelmaking into a required furnace to produce steel. According to the invention of claim 10, when the construction machine counterweight according to any one of claims 1 to 7 has been used, it is detached from the construction machine and the heavy packing is taken out from the case. A method for recycling used construction machine counterweights, characterized by filling a new case with a size that can be filled from the case inlet and reusing it as a construction machine counterweight. The invention of claim 11.
【０００７】このように、鉄系の粉粒体と、鉄系の成形
体のいずれか一方または双方をケース内に充填した建設
機械用カウンタウエイトとすることにより、従来廃棄処
分されていたショットブラストの集塵ダストや廃ショッ
トなどまでもを重量充填材として用いることができ、こ
のためにカウンタウエイトを安価に製造できるうえに、
埋め立て場や廃棄処分に要する費用が不要となる。ま
た、使用済の建設機械からカウンタウエイトを取り外
し、これをそのまま、或いは解体して高炉又は転炉又は
電気炉の鉄源として使用したり、取り出した重量充填物
を別の建設機械のカウンタウエイトの重量骨材として用
いることができるので、資源をリサイクルして有効に利
用することができる。As described above, by using the iron-based powder or granular material and / or the iron-based molded product in the case as the construction machine counterweight, the shot blast that has been conventionally disposed of is used. It is possible to use even the collected dust and waste shots of as a heavy packing material, which makes it possible to manufacture the counterweight at low cost and
There is no need for landfill or disposal costs. Also, remove the counterweight from the used construction machine and use it as it is, or dismantle it to use it as an iron source for the blast furnace, converter or electric furnace, or use the weight filler taken out from the counterweight of another construction machine. Since it can be used as a heavy aggregate, resources can be recycled and effectively used.
【０００８】[0008]
【発明の実施の形態】以下に本発明を詳細に説明する。
本発明は、ケース内に充填される重量充填物として、
鉄、酸化鉄などの鉄系の粉粒体と、これら鉄系の粉粒体
を圧縮成形した圧縮成形体などの鉄系の成形体のいずれ
か一方または双方を用いることに特徴があり、このよう
にすることによって、従来は埋め立て処分されてきた粉
状や粒状などの鉄系廃棄物でも有効利用できるようにし
たものである。このような鉄系廃棄物を原料とすれば、
重量充填材が安価なために建設機械用カウンタウエイト
を安価に提供できるのみならず、従来は廃棄処分とされ
ていた使用済の建設機械用カウンタウエイトのリサイク
ルも可能となる。BEST MODE FOR CARRYING OUT THE INVENTION The present invention is described in detail below.
The present invention, as a heavy filling to be filled in the case,
It is characterized by using one or both of iron-based powders such as iron and iron oxide, and iron-based molded products such as compression molded products obtained by compression molding of these iron-based powders. By doing so, it becomes possible to effectively use the iron-based waste in the form of powder or particles that has been conventionally disposed of in landfill. If such iron-based waste is used as a raw material,
Not only can the counterweight for construction machinery be provided at a low price because the weight filler is inexpensive, but it is also possible to recycle used construction machine counterweight, which was conventionally discarded.
【０００９】本発明において用いる鉄、酸化鉄などの鉄
系の粉粒体としては、鉄鋼を切削、切断、研削して発生
したダライ粉、ショットブラストで発生する鉄粉や酸化
鉄粉を含む集塵ダスト、石材切断に使用されているガン
グソウより排出される比較的粒径の小さい廃鉄砂、ショ
ットブラストのセットリングチャンバー廃棄物である比
較的粒径の大きい廃ショットなどの鉄系廃棄物をも用い
ることができる。この鉄系の粉粒体の粒径は特に限定さ
れるものではないが、ケースへ充填密度を高く保持して
充填するためには、平均粒径が５０ｍｍまでのものが好
ましく、特に、資源の有効利用の面を考慮すると、従来
廃棄処分されていた平均粒径が０．０１ｍｍ〜１０ｍｍ
の鉄系の粉体や粒体、小片などの鉄系の廃棄物を用いる
のが最も好ましい。Examples of iron-based powders such as iron and iron oxide used in the present invention include Dalai powder produced by cutting, cutting and grinding steel, iron powder and iron oxide powder produced by shot blasting. Dust dust, waste iron sand with a relatively small particle size discharged from Gangsaw used for stone cutting, iron-based waste such as waste shot with a relatively large particle size, which is the waste of the set-ring chamber of shot blasting. Can also be used. The particle size of the iron-based powder is not particularly limited, but in order to fill the case while keeping the packing density high, it is preferable that the average particle size is up to 50 mm. Considering effective use, the average particle size that was previously discarded is 0.01 mm to 10 mm.
It is most preferable to use the iron-based waste such as the iron-based powder, granules, and small pieces of
【００１０】なお、前記した重量充填物はケースに充填
された状態における密度である充填密度が４ｇ／ｃｍ3
未満では所望の重量を得るのに大きなケースを必要とす
るから、充填密度が４ｇ／ｃｍ3 以上であることが好ま
しい。ところが、鉄系の粉粒体として、粉末状の酸化鉄
の混入した鉄系廃棄物を用いる場合においてはその見か
け密度は１〜３ｇ／ｃｍ3 と低いので、このように見か
け密度の低い鉄系廃棄物を用いるときは、そのまま充填
しただけでは４ｇ／ｃｍ3 以上の高い充填密度を得るこ
とが困難である。このため、鉄系の粉粒体の見かけ密度
に応じて、次のような所望の高充填密度を有する重量充
填物とする。まず、鉄系の粉粒体の見かけ密度が高く、
そのままで所望の高い充填密度が得られる場合で、この
場合には鉄系の粉粒体をそのまま用いればよい。次に、
鉄系の粉粒体の見かけ密度が低い場合には、見かけ密度
の高い鉄系の粉粒体と混合することによって高い充填密
度の重量充填物とする。また、鉄系の粉粒体が粉末状の
酸化鉄粉が含まれるなどの理由により、見かけ密度の高
い鉄系の粉粒体と混合しても所望の高い充填密度を得る
ことが困難である場合には、プレス成形、ブリケットマ
シン成形などにより鉄系の粉粒体を円相当径が１〜５０
ｍｍの種々の大きさの圧力成形体とし、これらの大きさ
の異なる圧縮成形体を混合することにより充填密度が４
ｇ／ｃｍ3 以上となる重量充填物を製造する。即ち、円
相当径を１〜５０ｍｍで大きさの異なる成形体とするこ
とにより、高い充填密度を有し取り扱いが容易な重量充
填物とすることができる。さらに、このような成形体は
鉄系の粉粒体とを混合すればより高い充填密度を有する
重量充填物を得ることができる。なお、前記説明におい
て、円相当径とは、アーモンド状、棒状、楕円体状、針
状、塊状などの非球状体を同一の体積の球状体とみなし
た時の直径を指すものであって、成形体の形状には何ら
制限がないことは勿論である。The above-mentioned heavy packing has a packing density of 4 g / cm 3 which is a density in a state of being packed in a case.
If it is less than 1, a large case is required to obtain a desired weight, so that the packing density is preferably 4 g / cm 3 or more. However, when an iron-based waste mixed with powdery iron oxide is used as the iron-based powder or granular material, its apparent density is as low as 1 to 3 g / cm 3, and thus the iron-based waste having such a low apparent density is used. When the waste is used, it is difficult to obtain a high packing density of 4 g / cm 3 or more just by filling it as it is. Therefore, according to the apparent density of the iron-based powder or granular material, a heavy packing having the following desired high packing density is prepared. First, the apparent density of iron-based powder is high,
In the case where the desired high packing density is obtained as it is, in this case, the iron-based powder or granular material may be used as it is. next,
When the apparent density of the iron-based powder or granular material is low, it is mixed with the iron-based powder or granular material having a high apparent density to obtain a heavy packing having a high packing density. Further, it is difficult to obtain a desired high packing density even when mixed with an iron-based powder or granular material having a high apparent density because the iron-based powder or granular material contains powdery iron oxide powder. In this case, iron-based powder or granules having a circle equivalent diameter of 1 to 50 are formed by press molding, briquette machine molding, or the like.
The compression density of various sizes of mm and mixing the compression moldings of different sizes, the packing density becomes 4
A weight filling of g / cm 3 or more is produced. That is, by forming a molded body having a circle equivalent diameter of 1 to 50 mm and different sizes, it is possible to obtain a heavy packing having a high packing density and easy to handle. Further, such a molded body can obtain a heavy packing having a higher packing density by mixing with an iron-based powder or granular material. In the above description, the equivalent circle diameter refers to the diameter of a non-spherical body such as an almond shape, a rod shape, an ellipsoidal shape, a needle shape, or a lump shape, which is regarded as a spherical body having the same volume. Of course, there is no limitation on the shape of the molded body.
【００１１】しかして、前記したような建設機械用カウ
ンタウエイトを製造するには、鉄系の粉粒体と、鉄系の
成形体のいずれか一方または双方を主材とする充填材料
を、予め鋼板より成形した箱型のケース内にその投入口
より投入充填したうえ投入口を閉鎖すればよい。この場
合の具体例としては、例えば、、鉄系の粉粒体と、鉄系
の成形体のいずれか一方または双方を主材とする充填材
料を、ケース内の充填密度が４ｇ／ｃｍ3 以上となるよ
うに計量調整する工程と、この充填材料をケース内に重
量充填物として充填する工程とを行い、その後にケース
内の投入口を閉鎖する。なお、箱型のケース内に鉄系の
成形体のいずれか一方または双方を投入充填するとき、
鉄系の粉粒体が微粉末を含むときは、鉄系の粉粒体を水
とともに充填したり、樹脂やセメントなどの製鋼材料と
して使用可能な水硬性粉粒体を水とともに充填して重量
充填物とすれば、投入充填作業を容易化できるうえに、
ケース内で硬化してケース内で重量充填物が移動して建
設機械の機能に不具合を生じさせることがないようにす
ることもできるが、水を含んだ重量充填物に気泡が生じ
ることをなくすためには事前または事後に減圧処理など
を施して気泡を除去することが望ましい。Therefore, in order to manufacture the above-mentioned construction machine counterweight, the iron-based powder or granular material and / or the iron-based molded body are used as the main material in advance. It suffices to fill and fill the box-shaped case formed from a steel plate through the charging port and then close the charging port. As a specific example in this case, for example, a filling material mainly composed of one or both of an iron-based powder or granular material and an iron-based compact is used, and the packing density in the case is 4 g / cm 3 or more. And a step of filling the filling material into the case as a heavy filling, and then closing the charging port in the case. When either or both of the iron-based compacts are charged and filled in the box-shaped case,
If the iron-based powder contains fine powder, fill the iron-based powder with water, or fill with water a hydraulic powder that can be used as a steel-making material such as resin or cement with water. If it is a filling material, the filling and filling work can be facilitated and
It can be cured in the case so that the heavy packing does not move inside the case and cause a malfunction of the construction machine, but it eliminates the formation of bubbles in the heavy packing containing water. Therefore, it is desirable to remove air bubbles by applying a decompression process or the like in advance or after the fact.
【００１２】なお、前記した鉄系の粉粒体と、鉄系の成
形体のいずれか一方または双方を、水、および製鋼材料
として使用可能な水硬性粉粒体とともに重量充填物とし
てケース内に充填固化させる場合に使用する水硬性粉粒
体とは、燃焼熱を利用してエネルギーコストを低減でき
るものとして電炉及び高炉において積極的に使用されて
いる樹脂や、質量％で、ＣａＯ：約６５％、ＳｉＯ2 ：
約２０％、Ａｌ2 Ｏ3：約５％、Ｆｅ2 Ｏ3 ：約３％、
ＳＯ3 ：約２％などの成分より構成され、製鋼の副原料
として精錬に必要な物質であるＣａＯが主成分で、Ｓｉ
Ｏ2 、Ａｌ2 Ｏ 3 についても鉄鉱石に脈石として含まれ
る物質であるセメントなどがあるが、高炉の鉄源として
リサイクルする場合には、脈石に相当する成分、即ちＳ
ｉＯ2 及びＡｌ2 Ｏ3 の量は多くとも鉄鉱石と同等とす
るのが望ましいので、セメントの添加量は２０％以下と
し、また、電炉においてはＳＯ3 中のＳ分が有害成分と
なり鋼の靱性を低下させるので、電炉の鉄源としてリサ
イクルする場合のセメントの添加量は５％以下とするの
が望ましい。[0012] The iron-based powder and granules described above and the iron-based powder are formed.
Either or both of the features, water, and steelmaking materials
As a heavy filling with hydraulic powder that can be used as
Hydraulic powder used when filling and solidifying in a case
The body is able to use the heat of combustion to reduce energy costs
Actively used in electric furnaces and blast furnaces
Of resin, mass%, CaO: about 65%, SiO2:
About 20%, Al2O3: About 5%, Fe2O3: About 3%,
SO3: Auxiliary raw material for steelmaking, which is composed of about 2%
The main component is CaO, which is a substance necessary for refining
O2, Al2O 3Is also included in iron ore as gangue
There is a substance such as cement, but as an iron source for the blast furnace
When recycling, the component corresponding to gangue, ie S
iO2And Al2O3Is at most equivalent to iron ore
Since it is desirable to add 20% or less of cement,
In addition, in the electric furnace, SO3S content in the inside is harmful
As it reduces the toughness of flat steel,
When creking, the amount of cement added should be 5% or less.
Is desirable.
【００１３】また、電炉の鉄源には１トンの単重制限が
あるため、重量充填物の単重は１トン以下に分割できる
構造とするか、容易に解体できる構造とするのが望まし
い。なお、本発明において重量充填物のリサイクル先は
高炉、電気炉などのの鉄源に限定されるものではなく、
例えば、転炉のバブリング防止材や、溶湯の温度調整材
など他用途へのリサイクルも可能であり、また、建設機
械用カウンタウエイトが使用済とされたとき、これを建
設機械から取り外してケースから重量充填物を取り出
し、これを新規なケースに充填して再使用することも可
能である。なお、重量充填物が鉄系の粉粒体や鉄系の成
形体の小片であって、全体が固化されていない場合に
は、ケースを壊すことなく重量充填物をケースから取り
出すことができるうえに破砕などの処理も不要であるた
め、再使用のための工程が極めて容易となる。Since the iron source of the electric furnace has a unit weight limit of 1 ton, it is desirable that the unit weight of the heavy packing be divided into 1 ton or less, or that the structure can be easily disassembled. In the present invention, the recycling destination of heavy packing is not limited to iron sources such as blast furnaces and electric furnaces,
For example, it can be recycled for other purposes such as bubbling prevention material for converters and temperature control material for molten metal.When the construction machine counterweight is used, remove it from the construction machine and remove it from the case. It is also possible to take out the heavy packing, fill it in a new case, and reuse it. In addition, if the heavy packing is a small piece of iron-based powder or iron-based compact and the whole is not solidified, the heavy packing can be taken out from the case without breaking the case. Since the process such as crushing is unnecessary, the process for reuse becomes extremely easy.
【００１４】さらに、老朽化した建設機械から取り外さ
れた使用済の建設機械用カウンタウエイトをリサイクル
するには、先ず、建設機械から取り外したカウンタウエ
イトを回収ステーションに集め、これをそのまま或いは
ケースを取り外したうえ重量充填物の種類、形状などの
品質を基準として所要の大きさの解体片に破壊或いは裁
断し、その後にこの所要の大きさとされた解体片を製鋼
に用いる高炉又は転炉或いは電炉などの炉の種類に応じ
たものに分類して各炉に応じた製鋼用の鉄源とするか、
或いは新規なケースの重量充填物としてケースに前記し
た手段により充填して再使用する。なお、前記した分類
工程で分類された解体片は、製鋼所などのリサイクル先
に輸送されて目的とした用途に使用されるのを普通とす
るが、リサイクル先や再使用先で解体作業を行なうこと
もできるし、その中間工程において行うこともできる。Furthermore, in order to recycle the used construction machine counterweight removed from the aged construction machine, first, the counterweight removed from the construction machine is collected in a collection station, and this is left as it is or the case is removed. In addition, a blast furnace or converter or electric furnace, etc. that uses the dismantled pieces of the required size for steelmaking after destroying or cutting into pieces of the required size based on the quality and type of heavy packing Of iron sources for steelmaking according to each furnace,
Alternatively, the case is filled by a means described above as a heavy packing of a new case and reused. The dismantled pieces classified in the above-mentioned classification process are usually transported to a recycling destination such as a steel mill and used for the intended purpose, but the dismantling work is performed at the recycling destination or the reuse destination. Alternatively, it can be carried out in the intermediate step.
【００１５】[0015]
【実施例】以下、実施例に従い本発明を詳細に説明す
る。
（実施例１）自動車ギヤのショットピーニング工程でセ
ットリングチャンバーより排出された平均粒径０．４ｍ
ｍの廃ショットと、同じショットピーニング工程で集塵
機により排出された平均粒径０．１ｍｍの集塵ダストと
を、容積比で７．５：２．５となるように混合した重量
充填物を、１．６ｍｍの鋼板で作成した１辺の長さが３
００ｍｍで内部が空洞である箱型ケース内にその上部に
設けた直径３０ｍｍの導入口より、振動テーブル上で流
し込み充填して充填密度が５．０ｇ／ｃｍ3 の建設機械
用カウンタウエイトを得た。この建設機械用カウンタウ
エイトは重量充填物がいずれも鉄系の粉粒体であって、
隙間なくケース内に高密度で充填されているため、建設
機械に取り付けて使用したところ、安定した性能を発揮
することが確認された。また、この建設機械用カウンタ
ウエイトをリサイクルテストとして、ケースごと鉄スク
ラップとともに低周波誘導溶解炉に投入したところ、鉄
源として使用するうえでの問題は全く認められなかっ
た。The present invention will be described in detail below with reference to examples. (Example 1) Average particle size of 0.4 m discharged from the set ring chamber in the shot peening process of automobile gears
m of waste shot and dust collected by a dust collector in the same shot peening process and having a mean particle size of 0.1 mm were mixed to obtain a volume ratio of 7.5: 2.5 by weight filling. The length of one side made of 1.6 mm steel plate is 3
A counterweight for construction machinery having a packing density of 5.0 g / cm 3 was obtained by pouring and filling the solution into a box-shaped case having a hollow interior of 00 mm and a diameter of 30 mm, which was provided on the upper part of the box-shaped case. . In this construction machine counterweight, the heavy fillings are all iron-based powders,
It was confirmed that when it was mounted on a construction machine and used, it exhibited stable performance because it was packed in the case with high density without any gaps. In addition, when this counterweight for construction machinery was put into a low-frequency induction melting furnace together with iron scrap as a recycling test, no problem was found in using it as an iron source.
【００１６】（実施例２）磨き棒鋼用素材のショットブ
ラスト工程で回収した見かけ密度２．５ｇ／ｃｍ 3 の集
塵ダストに、粘結材として澱粉１％、水５．８％を添加
した後、ミックスマラーにより混練して成形原料とし
た。この成形原料を、ブリケットマシンを用いロール油
圧１５５ｋｇ／ｃｍ2 にて成形することにより、密度が
４．３ｇ／ｃｍ3 でサイズが２８×１８×４ｍｍの成形
体を得た。この成形体を実施例１で用いたケースと同一
形状のケース内に、実施例１と同じ方法により投入充填
して建設機械用カウンタウエイトを得た。この建設機械
用カウンタウエイトもリサイクルテストとして、ケース
ごと鉄スクラップとともに低周波誘導溶解炉に投入した
ところ、鉄源として使用するうえでの問題は全く認めら
れなかった。(Embodiment 2) A shot bar made of a material for a polished steel bar.
Apparent density 2.5g / cm recovered in the last process 3Collection of
Add 1% starch and 5.8% water as a binder to the dust.
After that, it is kneaded with a mix muller to obtain a molding raw material.
It was This forming raw material is rolled into oil using a briquette machine.
Pressure 155kg / cm2By molding with
4.3 g / cm3With a size of 28 x 18 x 4 mm
Got the body This molded body is the same as the case used in Example 1.
Filling and filling into the case of the same shape by the same method as in Example 1.
I got a counterweight for construction machinery. This construction machine
Counterweight for recycling test as a case
It was put into the low frequency induction melting furnace together with the iron scrap.
However, there was no problem in using it as an iron source.
I couldn't.
【００１７】（実施例３）鋳物の砂落とし工程のセット
リングチャンバー排出物をマグネット選別することによ
り、平均粒径０．６ｍｍの廃ショットを得た。この廃シ
ョットに実施例２において使用した集塵ダストを容積比
で廃ショット６．３に対し集塵ダスト３．７の割合で混
合した。この混合物に、ボルトランドセメント５％と水
１６％を添加、混練して重量骨材とした。次いで、この
重量骨材を実施例１で用いたケースと同一形状のケース
内にその上部に設けた直径３０ｍｍの導入口より投入充
填して建設機械用カウンタウエイトを得た。なお、この
重量充填物を自然乾燥させた時の密度は５．０ｇ／ｃｍ
3 であった。次に、廃カウンタウエイトのリサイクルテ
ストを目的として、このカウンタウエイトを解体し、ケ
ース内の重量充填物を取り出してジョークラッシャーに
より３ｍｍ程度の塊状に破砕後、ロータリーキルンに投
入して還元ばい焼処理を行った。次いで、還元ばい焼し
た重量充填物を鉄源として高炉に投入したが、高炉用鉄
源とした何ら問題なく使用することができた。(Example 3) A waste shot having an average particle size of 0.6 mm was obtained by magnetically selecting the discharge of the settling chamber in the sand removing step of the casting. The dust collection dust used in Example 2 was mixed with this waste shot in a volume ratio of dust collection dust 3.7 to waste shot 6.3. 5% of Boltland cement and 16% of water were added to this mixture and kneaded to obtain a heavy aggregate. Next, this heavy aggregate was charged and filled into a case having the same shape as the case used in Example 1 through an inlet having a diameter of 30 mm provided at the upper part of the case to obtain a counterweight for construction machinery. The density when the heavy packing was naturally dried was 5.0 g / cm.
Was 3 . Next, for the purpose of recycling test of the waste counterweight, this counterweight is disassembled, the heavy packing in the case is taken out, crushed into a lump of about 3 mm by a jaw crusher, and then put into a rotary kiln for reduction roasting treatment. went. Next, the reduction roasted heavy filler was introduced into the blast furnace as an iron source, but it could be used as an iron source for a blast furnace without any problems.
【００１８】[0018]
【発明の効果】以上に説明したように、本発明の建設機
械用カウンタウエイトは、これまで埋め立て処分に回さ
れていたショットブラストの集塵ダストや廃ショットな
どの微細な微細な鉄系廃棄物でも重量充填物として利用
することにより安価に提供できるうえに、鉄資源を有効
に利用したり、新規なケースに充填して再使用するなど
してリサイクルすることにより、埋め立て場や廃棄処分
に要する費用を不要とすることができる。よって、本発
明は従来の建設機械用カウンタウエイトの問題点を解決
した建設機械用カウンタウエイトおよびその製造法並び
に使用済の建設機械用カウンタウエイトのリサイクル法
として業界の発展に寄与するところ極めて大きいものが
ある。As described above, the counterweight for construction machinery according to the present invention is a fine iron-based waste material such as dust collected from shot blasts and waste shots that have been sent to landfill. However, by using it as a heavy packing, it can be provided at a low cost, and it is necessary for landfill and disposal by effectively utilizing iron resources or recycling by filling a new case and reuse. The cost can be eliminated. Therefore, the present invention contributes to the development of the industry as a counterweight for construction machines, a method for manufacturing the same, and a method for recycling used construction machine counterweights, which solves the problems of conventional construction machine counterweights. There is.
─────────────────────────────────────────────────────
─────────────────────────────────────────────────── ───
【手続補正書】[Procedure amendment]
【提出日】平成１３年６月２６日（２００１．６．２
６）[Submission date] June 26, 2001 (2001.6.2)
6)
【手続補正１】[Procedure Amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】請求項３[Name of item to be corrected] Claim 3
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【手続補正２】[Procedure Amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】０００６[Correction target item name] 0006
【補正方法】変更[Correction method] Change
【補正内容】[Correction content]
【０００６】[0006]
【課題を解決するための手段】上記の課題を解決するた
めになされた本発明は、鉄系の粉粒体と、鉄系の成形体
のいずれか一方または双方を、重量充填物としてケース
内に充填したことを特徴とする建設機械用カウンタウエ
イトを請求項１の発明とし、鉄系の粉粒体と、鉄系の成
形体のいずれか一方または双方を、重量充填物として水
とともにケース内に充填したことを特徴とする建設機械
用カウンタウエイトを請求項２の発明とし、鉄系の粉粒
体と、鉄系の成形体のいずれか一方または双方を、樹脂
や水および製鋼材料として使用可能な水硬性粉粒体とと
もに重量充填物としてケース内に充填固化したことを特
徴とする建設機械用カウンタウエイトを請求項３の発明
とし、前記した請求項１〜３の何れかに記載の発明にお
ける鉄系の粉粒体と、鉄系の成形体を、鉄系廃棄物より
なるものとした建設機械用カウンタウエイトを請求項４
の発明とし、請求項１〜４の何れかに記載の発明におい
て、ケース内の重量充填物の密度を４ｇ／ｃｍ3 以上と
した建設機械用カウンタウエイトを請求項５の発明と
し、また、前記した請求項１〜５の何れかに記載の発明
における鉄系の粉粒体を、ダライ粉、ショットブラスト
の集塵ダスト、ショットブラスト後の廃ショット、ガン
グソウの消耗により排出される廃鉄砂の少なくとも１種
を含むものとしたものが請求項６の発明であり、これら
請求項１〜６の何れかに記載の発明における鉄系の成形
体を、円相当径で５０ｍｍ以下の塊状成形体とした建設
機械用カウンタウエイトを請求項７の発明とする。ま
た、鉄系の粉粒体と、鉄系の成形体のいずれか一方また
は双方を主材とする充填材料を、ケース内の充填密度が
４ｇ／ｃｍ3 以上となるように計量調整する工程と、こ
の充填材料をケース内に重量充填物として充填する工程
とよりなることを特徴とする建設機械用カウンタウエイ
トの製造法を請求項８の発明とする。さらに、前記した
請求項１〜７の何れかに記載の建設機械用カウンタウエ
イトが使用済とされたとき、これを建設機械から取り外
して製鋼用の鉄源として使用することを特徴とする建設
機械用カウンタウエイトのリサイクル法を請求項９の発
明とし、使用済の建設機械用カウンタウエイトを解体し
て所要の大きさの解体片とする工程と、この解体片を製
鋼に用いる炉の種類に応じたものに分類する工程と、前
記工程で分類された解体片を製鋼用の鉄源の少なくとも
一部として所要の炉に投入して製鋼する工程とよりなる
ことを特徴とする請求項９に記載の使用済の建設機械用
カウンタウエイトのリサイクル法を請求項１０の発明と
し、請求項１〜７の何れかに記載の建設機械用カウンタ
ウエイトが使用済とされたとき、これを建設機械から取
り外して重量充填物をケースから取り出し、この重量充
填物をケースの投入口より充填可能な大きさとして新規
なケースに充填し、建設機械用カウンタウエイトとして
再使用することを特徴とする使用済の建設機械用カウン
タウエイトのリサイクル法を請求項１１の発明とする。SUMMARY OF THE INVENTION The present invention, which has been made to solve the above-mentioned problems, provides a case in which one or both of an iron-based powder or granular material and an iron-based compact are used as a heavy packing in a case. The counterweight for construction machine according to claim 1 is characterized in that the iron-based powder or granular material and / or the iron-based molded body, or both of them, are used as a heavy filling together with water in the case. The counterweight for construction machine according to claim 2, wherein the iron-based powder or granular material and / or the iron-based compact is used as a resin.
A counterweight for a construction machine, characterized by being filled and solidified in a case as a heavy filling together with a hydraulic powder and granular material that can be used as water, steel and a steel-making material. A counterweight for construction machinery, wherein the iron-based powder or granular material and the iron-based compact according to any one of the inventions are made of iron-based waste.
In the invention according to any one of claims 1 to 4, there is provided a counterweight for construction machine, wherein the density of the heavy packing in the case is 4 g / cm 3 or more, and the invention according to claim 5, The iron-based powder or granular material according to any one of claims 1 to 5 is used as a material for a dry iron powder, dust collected by shot blasting, waste shot after shot blasting, and waste iron sand discharged by exhaustion of gang sow. It is the invention of claim 6 that includes at least one kind, and the iron-based compact according to any one of claims 1 to 6 is a block compact having a circle equivalent diameter of 50 mm or less. According to another aspect of the invention, there is provided a construction machine counterweight. In addition, a step of measuring and adjusting a filling material mainly composed of one or both of the iron-based powder and granular material and the iron-based molded body so that the filling density in the case is 4 g / cm 3 or more. A method of manufacturing a counterweight for a construction machine, which comprises the step of filling the filling material as a heavy filling in a case. Furthermore, when the construction machine counterweight according to any one of claims 1 to 7 is used, it is detached from the construction machine and used as an iron source for steelmaking. According to the invention of claim 9, the method of recycling counter weights for use in construction, the step of dismantling used construction machine counter weights to obtain dismantled pieces of a required size, and the disassembled pieces depending on the type of furnace used for steelmaking. 10. The method according to claim 9, further comprising a step of classifying the dismantled pieces classified in the above step into a required furnace as at least a part of an iron source for steelmaking, and making the steel. The method of recycling a used construction machine counterweight according to claim 10 is the invention of claim 10, and when the construction machine counterweight according to any one of claims 1 to 7 is used, it is taken from the construction machine. After removing the heavy packing from the case, the heavy packing is filled in a new case with a size that can be filled from the charging port of the case and reused as a counterweight for construction machinery. A method of recycling a counterweight for construction machinery is the invention of claim 11.
Claims (11)
か一方または双方を、重量充填物としてケース内に充填
したことを特徴とする建設機械用カウンタウエイト。1. A counterweight for a construction machine, characterized in that either or both of an iron-based powder and granular material and an iron-based compact are filled in a case as a heavy packing.
か一方または双方を、水とともに重量充填物としてケー
ス内に充填したことを特徴とする建設機械用カウンタウ
エイト。2. A counterweight for a construction machine, characterized in that one or both of an iron-based powder and granular material and an iron-based compact are filled in a case together with water as a heavy filling.
か一方または双方を、水、および製鋼材料として使用可
能な水硬性粉粒体とともに重量充填物としてケース内に
充填固化したことを特徴とする建設機械用カウンタウエ
イト。3. An iron-based powder or granular material, an iron-based compact, or both, together with water and a hydraulic powder or granular material that can be used as a steel-making material, is filled and solidified in a case as a heavy packing. The counterweight for construction machinery that is characterized.
廃棄物よりなるものである請求項１〜３の何れかに記載
の建設機械用カウンタウエイト。4. The counterweight for a construction machine according to claim 1, wherein the iron-based powder and granular material and the iron-based compact are made of iron-based waste.
ｃｍ3 以上である請求項１〜４の何れかに記載の建設機
械用カウンタウエイト。5. The density of the heavy packing in the case is 4 g /
The counterweight for construction machinery according to any one of claims 1 to 4, which has a cm 3 or more.
ラストの集塵ダスト、ショットブラスト後の廃ショッ
ト、ガングソウの消耗により排出される廃鉄砂の少なく
とも１種を含むものである請求項１〜５の何れかに記載
の建設機械用カウンタウエイト。6. The iron-based powder or granular material contains at least one kind of Dalai powder, dust collected by shot blast, waste shot after shot blast, and waste iron sand discharged by exhaustion of Gangsou. A counterweight for a construction machine according to any one of items 1 to 5.
下の塊状に成形したものである請求項１〜６の何れかに
記載の建設機械用カウンタウエイト。7. The counterweight for a construction machine according to claim 1, wherein the iron-based molded body is molded into a lump having an equivalent circle diameter of 50 mm or less.
か一方または双方を主材とする充填材料を、ケース内の
充填密度が４ｇ／ｃｍ3 以上となるように計量調整する
工程と、この充填材料をケース内に重量充填物として充
填する工程とよりなることを特徴とする建設機械用カウ
ンタウエイトの製造法。8. A weighing material containing iron-based powder or granular material and / or iron-based compact as a main material so that the filling density in the case is 4 g / cm 3 or more. And a step of filling the case with the filling material as a heavy filling, a method of manufacturing a counterweight for a construction machine.
用カウンタウエイトが使用済とされたとき、これを建設
機械から取り外して製鋼用の鉄源として使用することを
特徴とする建設機械用カウンタウエイトのリサイクル
法。9. A construction characterized in that when the construction machine counterweight according to any one of claims 1 to 8 is used, it is removed from the construction machine and used as an iron source for steelmaking. Machine counterweight recycling method.
設機械用カウンタウエイトを解体して所要の大きさの解
体片とする工程と、この解体片を製鋼に用いる炉の種類
に応じたものに分類する工程と、前記工程で分類された
解体片を製鋼用の鉄源の少なくとも一部として所要の炉
に投入して製鋼する工程とよりなることを特徴とする請
求項９に記載の使用済の建設機械用カウンタウエイトの
リサイクル法。10. A process for disassembling a used construction machine counterweight removed from a construction machine to obtain a dismantled piece of a required size, and a step according to the type of furnace used for steelmaking. The used according to claim 9, which comprises a step of classifying and a step of charging the dismantled pieces classified in the step as at least a part of an iron source for steelmaking into a required furnace to make steel. Law for Recycling Counterweight for Construction Machines in Japan.
械用カウンタウエイトが使用済とされたとき、これを建
設機械から取り外してケースから重量充填物を取り出
し、この重量充填物をケースの投入口より充填可能な大
きさとして新規なケースに充填し、建設機械用カウンタ
ウエイトとして再使用することを特徴とする使用済の建
設機械用カウンタウエイトのリサイクル法。11. When the construction machine counterweight according to any one of claims 1 to 7 has been used, the construction machine counterweight is detached from the construction machine and a heavy packing is taken out from the case. A method for recycling used construction machine counterweights, characterized by filling a new case with a size that can be filled from the charging port and reusing it as construction machine counterweights.