JP2002512817A - Mineral wool composition - Google Patents
Mineral wool compositionInfo
- Publication number
- JP2002512817A JP2002512817A JP2000546574A JP2000546574A JP2002512817A JP 2002512817 A JP2002512817 A JP 2002512817A JP 2000546574 A JP2000546574 A JP 2000546574A JP 2000546574 A JP2000546574 A JP 2000546574A JP 2002512817 A JP2002512817 A JP 2002512817A
- Authority
- JP
- Japan
- Prior art keywords
- mineral
- mineral wool
- mgo
- content
- measured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】 本発明は、生理学的媒体中で分解可能であり、下記成分を以下の重量百分率：ＳｉＯ2 ３８〜４６％；Ａｌ2Ｏ3 １６〜２４％；ＭｇＯ １０〜２０％；ＲＯ（ＣａＯ＋ＭｇＯ） １６〜４０％；ＭｇＯ／ＣａＯ≧０．８；Ｒ2Ｏ（Ｎａ2Ｏ＋Ｋ2Ｏ）≧０．３％；Ｐ2Ｏ5 ０〜５％；Ｆｅ2Ｏ3≧０．５％；ＴｉＯ2 ０〜３％；ＭｎＯ ０〜２％；ＳＯ3 ０〜２％で含有する鉱滓綿に関する。 (57) Abstract: The present invention can be degraded in a physiological medium, the following weight percentages of the following components: SiO 2 38~46%; Al 2 O 3 16~24%; 10~20% MgO; RO (CaO + MgO) 16~40% ; MgO / CaO ≧ 0.8; R 2 O (Na 2 O + K 2 O) ≧ 0.3%; P 2 O 5 0~5%; Fe 2 O 3 ≧ 0.5 %; about mineral wool containing at SO 3 0~2%; TiO 2 0~3 %; 0~2% MnO.
Description
【０００１】[0001]
本発明は、人工鉱滓綿に関する。それは、より詳細には、断熱及び／または防
音材料或いは土壌を用いない培地（soilless-culture medium）の製造用の鉱滓
綿を対象とする。The present invention relates to artificial mineral slag wool. It is more particularly directed to mineral wool for the production of insulating and / or soundproofing materials or soilless-culture media.
【０００２】 それは、より詳細には、岩綿或いは玄武岩綿タイプの鉱滓綿、すなわち、高い
液相線温度とそれらの繊維化温度（fiberizing temperature）における高い流動
性とを伴う化学組成物に関する。It more particularly relates to mineral wool of the rock wool or basalt wool type, ie a chemical composition with a high liquidus temperature and a high fluidity at their fiberizing temperature.
【０００３】[0003]
従来から、このタイプの鉱滓綿は、例えば、静的繰出デバイスにより溶融した
材料を供給される縦続遠心ホイールを用いたタイプの、特にはＥＰ−０，４６５
，３１０或いはＥＰ−０，４３９，３８５に記載されるような、所謂「外部」遠
心プロセスにより繊維化（fiberize）されている。Conventionally, mineral wool of this type has for example been of the type using a cascaded centrifugal wheel supplied with molten material by means of a static dispensing device, in particular EP-0,465.
, 310 or EP-0,439,385 by a so-called "external" centrifugation process.
【０００４】 近年、工業的及び経済的実行可能性並びに品質水準の公知の判断基準に、吸入
による身体中への微細な繊維の予想される蓄積に関連する潜在的な病原性リスク
を防ぐために、鉱滓綿の生分解性、すなわち、生理学的媒体中で速く分解される
その能力が加えられている。[0004] In recent years, known criteria of industrial and economic viability and quality levels have been set to prevent the potential pathogenic risk associated with the expected accumulation of fine fibers in the body by inhalation. Added is the biodegradability of mineral wool, that is, its ability to rapidly degrade in physiological media.
【０００５】[0005]
本発明の目的は、それゆえに、岩綿或いは玄武岩綿タイプの鉱滓綿の化学組成
物を改良することにあり、その改良は、特には、生分解性を増加させること及び
／または生分解性を外部遠心処理により繊維化される能力と調和させること（し
かしながら、他の繊維化方法を除外するものではない）へと向けられている。The object of the present invention is therefore to improve the chemical composition of mineral wool, of the rock wool or basalt wool type, the improvement being in particular to increase the biodegradability and / or to increase the biodegradability. It is directed towards harmonizing with the ability to be fibrillated by external centrifugation (but does not preclude other fiberization methods).
【０００６】[0006]
【課題を解決するための手段】 本発明の主題は、生理学的媒体中で分解され得て、下記成分を以下の重量百分
率：The subject of the present invention is that it can be degraded in a physiological medium and comprises the following components in the following weight percentages:
【表１】 [Table 1]
【０００７】 で含有する鉱滓綿にある（テキストの残りを通して、組成物の成分のどの百分率
も重量百分率を意味することが理解されるべきである）。[0007] It is to be understood that throughout the remainder of the text any percentage of the components of the composition means weight percentage.
【０００８】 そのような組成物の選択は、特にはその幾つかの特定の成分が演ずる多くの複
雑な役割を変えることにより、多くの利益が増大させられることを可能としてい
る。[0008] The choice of such compositions allows many benefits to be increased, especially by altering the many complex roles played by some of the specific components.
【０００９】 それゆえ、アルカリ金属酸化物（Ｒ2Ｏ），特にはＮａ2Ｏ及び／またはＫ2Ｏ
の形態のものの含有量が、中程度或いは低い，一般には６％である岩綿タイプの
鉱滓綿組成物が含まれる。同時に、そのアルカリ土類金属酸化物（ＲＯ），特に
はＣａＯ及び／またはＭｇＯの形態のものの含有量は高く、一般には少なくとも
２０％であり、さらには少なくとも２２％である。Therefore, alkali metal oxides (R 2 O), especially Na 2 O and / or K 2 O
The mineral wool composition of the rock wool type having a medium or low content in the form of (i) is generally 6%. At the same time, its content of alkaline earth metal oxides (RO), especially in the form of CaO and / or MgO, is high, generally at least 20% and even at least 22%.
【００１０】 任意のＭｎＯ、ＴｉＯ2、及びＳＯ3の含有量は、この組成物のグループでしば
しば遭遇する不純物含有量，一般には３％までの不純物総含有量がそれら組成物
中で見出される，よりも多いものと見なされる。The content of any MnO, TiO 2 , and SO 3 is determined by the impurity content often encountered in this group of compositions, typically up to 3%, in those compositions. Is considered more.
【００１１】 そのような組成物の繊維化時の粘性は外部遠心処理に適している。[0011] The viscosity of such compositions during fiberization is suitable for external centrifugation.
【００１２】 その生分解性に関しては、特に岩綿タイプの組成物において、Ｐ2Ｏ5のような
ある化合物はこれを相当に改良することができ、他の酸化物はこれとは逆に少な
くとも中性のｐＨにおいてそれを減少させる傾向を有しているように思われるこ
とはすでに公知である。例えば、ＥＰ−０，４５９，８９７及びＷＯ９３／２２
２５１への参照がなされてもよい。しかしながら、大量のＰ2Ｏ5の添加は、本発
明のコンテクストにおいて、最も適切なアプローチであることを証明していない
。これは、他の問題点が生じるかもしれないからである。例えば、経済的なもの
（Ｐ2Ｏ5は高価な原料から得られる）及び技術的なもの−組成物中のＰ2Ｏ5と例
えばアルミナとの割合の変化−は、その他の特性を不所望な或いは未知の方法で
変化させるかも知れない。それゆえ、Ｐ2Ｏ5は、アルミナのように組成物の粘性
に影響がない訳ではない。しかしながら、本発明が最も有利に適用される外部遠
心処理によって岩綿タイプの組成物が繊維化される場合、その組成物の粘性的挙
動は制御されるべき重要な条件である。With regard to its biodegradability, especially in compositions of the rock wool type, certain compounds such as P 2 O 5 can considerably improve this, while other oxides conversely at least It is already known that at neutral pH it seems to have a tendency to decrease it. For example, EP-0,459,897 and WO93 / 22
Reference to 251 may be made. However, the addition of large amounts of P 2 O 5 has not proven to be the most appropriate approach in the context of the present invention. This is because other problems may arise. For example, economic ones (P 2 O 5 is obtained from expensive raw materials) and technical ones - the change in the percentage of the P 2 O 5 in the composition, for example, alumina - may undesirably other characteristics Or may change it in unknown ways. Therefore, P 2 O 5 is not without affecting the viscosity of the composition like alumina. However, when the composition of the rock wool type is fibrillated by external centrifugation, where the present invention is most advantageously applied, the viscous behavior of the composition is an important condition to be controlled.
【００１３】 その上、ある化合物はある特性について有利であるかもしれないが、高度な生
分解性を得るには不都合である。例えば、鉄の場合は、鉱滓綿に高い耐火性を与
えるのに有利であるが岩綿の生分解性を減少させる傾向にあり、アルミナの場合
は、組成物の粘性を調節するのに適切であるが特に中性のｐＨでのインビトロ試
験により測定された場合に生分解性に関して非常に都合良い訳ではない。Moreover, while certain compounds may be advantageous for certain properties, they are disadvantageous for obtaining a high degree of biodegradability. For example, iron is advantageous for imparting high fire resistance to mineral wool, but tends to reduce the biodegradability of rock wool, and alumina is suitable for adjusting the viscosity of the composition. However, it is not very convenient with regard to biodegradability, especially as determined by in vitro tests at neutral pH.
【００１４】 本発明は、それゆえに、これらデータの全ての間で特に以下の方法で適切な歩
みよりを達成した：その組成物はＰ2Ｏ5を、せいぜい５％の或いはどちらかと言
えばせいぜい４％の適度な量で含有しても良い。また、それは、生分解性以外の
理由で、有利であることが分かっている（或いは微量で不可避である）少なくと
も少量の酸化鉄を含有してもよい。しかしながら、その組成物は、過剰な量のＰ 2 Ｏ5を添加することなく或いはＰ2Ｏ5（または生分解性に好都合であると見なさ
れている他の非常に特別な化合物）なしで、特にはＣａＯに対するＭｇＯの相対
比を変化させることからなる他の手段により高水準の生分解性を達成する。実際
、岩綿タイプの組成物は、一般に、マグネシアＭｇＯに比べて極めて著しく多量
の石灰ＣａＯを含有している。この割合を変更することにより、従来は、甚大な
アルミナ及び／または鉄含有量を「補償する」ための高いＰ2Ｏ5含有量でしか得
られなかった高水準の生分解性が達成され得ることが見出されている。低いＰ2
Ｏ5含有量に関連する副次的であり且つ重要ではない利益、すなわち、過剰に多
いＰ2Ｏ5は実際に組成物の液相線温度を増加させる傾向にあることが記されるべ
きである。The present invention therefore provides a suitable step between all of these data, especially in the following manner.
Achieved: The composition is PTwoOFiveSay at most 5% or either
For example, it may be contained in an appropriate amount of at most 4%. It is also non-biodegradable
For the reason, it has proven to be advantageous (or at least insignificant in traces)
May also contain a small amount of iron oxide. However, the composition contains excessive amounts of P Two OFiveWithout the addition ofTwoOFive(Or deemed favorable for biodegradability
Without other very special compounds), especially the relative of MgO to CaO
A high level of biodegradability is achieved by other means consisting of varying the ratio. Actual
In general, rock wool-type compositions are significantly more abundant than magnesia MgO.
Contains lime CaO. By changing this ratio, the conventional
High P to "compensate" for alumina and / or iron contentTwoOFiveObtained only by content
It has been found that unseen high levels of biodegradability can be achieved. Low PTwo
OFiveSecondary and insignificant benefits related to content, i.e.
I PTwoOFiveShould actually tend to increase the liquidus temperature of the composition.
It is.
【００１５】 本発明に係る他の特徴的な側面は、このＭｇＯ／ＣａＯ比と、かなり高いアル
ミナ含有量，これは少なくとも１６％である，との組み合わせに関する。この組
み合わせが、中性のｐＨでのインビトロ試験及び酸性のｐＨでのインビボ試験で
測定された双方の生分解性の基準を十分に満足させることが見出されている。実
際、どのｐＨがインビボ生理学的媒体，特には肺の領域を最も代表するものであ
るかを知るという問題は完全には解決されていない。高いアルミナ含有量は、今
日まで、中性のｐＨではなく酸性のｐＨでの速い分解に好都合であると思われて
いる。Another characteristic aspect of the present invention relates to the combination of this MgO / CaO ratio with a fairly high alumina content, which is at least 16%. It has been found that this combination satisfies both the biodegradability criteria measured in in vitro tests at neutral pH and in vivo tests at acidic pH. Indeed, the problem of knowing which pH is most representative of the in vivo physiological medium, especially the lung area, has not been completely solved. A high alumina content has, to date, been considered favorable for fast decomposition at acidic rather than neutral pH.
【００１６】 本発明は、高いアルミナ含有量を選択し、中性のｐＨにおける損害を被ること
なく、酸性のｐＨにおけるその有利な効果を維持するように特にアルカリ土類金
属酸化物の含有量を適合させることにより、少なくともインビトロで測定され、
どのようなｐＨであっても高水準の生分解性を得ることを可能とする。The present invention selects a high alumina content and, in particular, reduces the content of alkaline earth metal oxides so as to maintain its advantageous effect at acidic pH without damaging at neutral pH. By measuring at least in vitro,
It is possible to obtain a high level of biodegradability at any pH.
【００１７】 ＳｉＯ2とＡｌ2Ｏ3との和が本組成物の粘性的挙動が大きく制御されることを
可能とすること及びそれは好ましくは少なくとも５８％であり、特には５９乃至
６４％であることが記されるべきである。The sum of SiO 2 and Al 2 O 3 allows the viscous behavior of the composition to be largely controlled and it is preferably at least 58%, especially 59-64% It should be noted.
【００１８】 有利には、本発明に係る鉱滓綿組成物は、１８乃至３２％の、例えば２６乃至
３０％の、或いは３２％より高く４０％までのアルカリ土類金属酸化物（ＣａＯ
及び／またはＭｇＯ）のＲＯ含有量を有する。Advantageously, the mineral wool composition according to the invention has an alkaline earth metal oxide (CaO) content of from 18 to 32%, for example from 26 to 30%, or from more than 32% to 40%.
And / or MgO).
【００１９】 同様に、第１の態様によると、酸化鉄Ｆｅ2Ｏ3含有量は、非常に控えめ、特に
は０．５乃至１．７％であってもよい（これらは一般には３２％よりも多い高い
ＲＯ含有量と組み合わされる）。この低い含有量は、特に建築部材上にスプレー
される鉱滓綿の用途に使用され、ときどき「ホワイトウール」と呼ばれるものを
得ることを可能とする。Similarly, according to the first aspect, the iron oxide Fe 2 O 3 content can be very modest, in particular between 0.5 and 1.7% (these are generally higher than 32%). Also combined with a high RO content). This low content makes it possible to obtain what is used, in particular, for mineral slag wool, which is sprayed on building components, sometimes called "white wool".
【００２０】 第２の態様によると、鉄含有量はより高く、特には１．７％より高く、１２％
までのＦｅ2Ｏ3、及び好ましくは５乃至１０％の或いは５乃至８％のＦｅ2Ｏ3（
一般には１８乃至３２％のＲＯ含有量と組み合わされる）を有する。上述したよ
うに、鉄は、特に鉱滓綿に高い耐火性を与えるかも知れない。本態様において、
鉱滓綿は一般にはフェルトの形態で収集される。According to a second aspect, the iron content is higher, in particular higher than 1.7% and 12%
Fe 2 O 3 , and preferably 5 to 10% or 5 to 8% Fe 2 O 3 (
Typically combined with an RO content of 18 to 32%). As mentioned above, iron may provide high fire resistance, especially to mineral wool. In this embodiment,
Mineral wool is generally collected in the form of felt.
【００２１】 有利には、Ｒ2Ｏ酸化物（Ｎａ2Ｏ及び／またはＫ2Ｏ）含有量は、０．３乃至
１％（好ましくは、上述したホワイトウールの製造の目的で）或いはこれより高
くてもよく、特には１％より高く殆ど６％までであり、たとえば２乃至２．２％
或いは１乃至３％である。Advantageously, the R 2 O oxide (Na 2 O and / or K 2 O) content is between 0.3 and 1% (preferably for the production of white wool as described above) or higher. It can be high, especially higher than 1% and up to almost 6%, for example 2 to 2.2%
Alternatively, it is 1 to 3%.
【００２２】 有利には、本発明に係る組成物は、重量百分率の比で表現される以下の関係も
満足する；ＭｇＯ／ＣａＯは０．８５より高く、特には０．９５または１または
１．１５より高く、一般には殆ど２または３である。それゆえ、ＣａＯに対して
大きすぎるＭｇＯの過剰量がこれら酸化物を原材料として入手することを過度に
複雑化する或いは高価にすることなく、上述した有利な効果が得られる。上述し
たように、幾分低い比、例えば０．７５乃至０．８０のＭｇＯ／ＣａＯ比を用い
ることも可能である。Advantageously, the composition according to the invention also satisfies the following relationship, expressed as a percentage by weight: MgO / CaO is higher than 0.85, in particular 0.95 or 1 or 1. It is higher than 15 and is generally almost 2 or 3. Therefore, the above-mentioned advantageous effects can be obtained without an excessive amount of MgO that is too large relative to CaO excessively complicating or expensively obtaining these oxides as raw materials. As mentioned above, it is also possible to use a somewhat lower ratio, for example an MgO / CaO ratio of 0.75 to 0.80.
【００２３】 また、有利には、本発明に係る組成物は、Ｒ2Ｏ／Ａｌ2Ｏ3が０．０７乃至０
．８、好ましくは０．０９乃至０．３或いは０．０５乃至０．２なる関係を満足
してもよい。Advantageously, the composition according to the present invention has an R 2 O / Al 2 O 3 content of 0.07 to 0.
. 8, preferably 0.09 to 0.3 or 0.05 to 0.2.
【００２４】 本発明に係る組成物は、好ましくは、０．１％よりも高い、特には２乃至３％
までのＰ2Ｏ5含有量を有する。この適度な含有量は、その組成物を経済的に過剰
に不利にすること或いはその液相線温度への大きすぎる影響を有することがなく
、生分解性への非常に有利な影響を有している。The composition according to the invention is preferably higher than 0.1%, in particular 2-3%
P 2 O 5 content up to This moderate content has a very favorable effect on the biodegradability without economically overly penalizing the composition or having too great an effect on its liquidus temperature. ing.
【００２５】 他の態様によると、Ｐ2Ｏ5含有量は、より低い、特にはゼロ或いは僅かに高く
０．１％までであってもよい。According to another embodiment, the P 2 O 5 content may be lower, in particular zero or slightly higher, up to 0.1%.
【００２６】 その組成物の酸化は、例えば、酸化マンガンＭｎＯの、特には０．１乃至４％
の量の任意の添加によって制御されてもよい。Oxidation of the composition is, for example, from 0.1% to 4% of manganese oxide MnO.
May be controlled by the optional addition of an amount of
【００２７】 任意であり且つ特には０．１乃至５％の含有量での酸化ホウ素の添加は、特に
その放熱部品中での熱伝導率を低下させる傾向によって、鉱滓綿の断熱特性が改
良されるのを可能とするかも知れない。The addition of boron oxide, which is optional and in particular at a content of 0.1 to 5%, improves the thermal insulation properties of the mineral wool, especially due to its tendency to reduce the thermal conductivity in the heat-dissipating component. May be able to
【００２８】 任意に、本組成物は、ＴｉＯ2を不純物として或いは意図的な添加物として、
例えば１乃至２％までの量で含有してもよい。ＳＯ3もまた、特にはそれが０．
１％未満の値に制限される場合に、Ｐ2Ｏ5のように不純物として見なされるべき
である。Optionally, the composition comprises TiO 2 as an impurity or as an intentional additive.
For example, it may be contained in an amount of 1 to 2%. SO 3 is also particularly notable when it is present at 0.
When limited to values less than 1%, it should be considered as an impurity, such as P 2 O 5 .
【００２９】 本発明に係る組成物の好ましいＣａＯ含有量は２２％以下であり、特には少な
くとも１０％であり、有利には１１乃至１８％或いは１８％より高く２１％まで
である。The preferred CaO content of the composition according to the invention is not more than 22%, in particular at least 10%, advantageously 11 to 18% or more than 18% and up to 21%.
【００３０】 同様に、本組成物の好ましいＭｇＯ含有量は、好ましくは少なくとも１１％で
あり、一般にはせいぜい１９％であり、好ましい範囲は１２乃至１５％である。[0030] Similarly, the preferred MgO content of the composition is preferably at least 11%, generally at most 19%, with a preferred range of 12 to 15%.
【００３１】 本発明の非制限的な好ましい態様によると、本組成物のアルミナＡｌ2Ｏ3含有
量は少なくとも１８．５％であり、特には少なくとも１９％であり、さらには少
なくとも２０或いは２１％である。According to a non-limiting preferred embodiment of the invention, the composition has an alumina Al 2 O 3 content of at least 18.5%, in particular at least 19%, and even at least 20 or 21%. It is.
【００３２】 差Ｔlog1−Ｔliqは、好ましくは少なくとも１０℃であり、好ましくは２０或
いは３０℃である；この差は本発明の組成物の「使用範囲」、すなわち、それら
が特には外部遠心処理によって繊維化され得る温度範囲を規定している。The difference T log1 −T liq is preferably at least 10 ° C., preferably 20 or 30 ° C .; this difference is the “range of use” of the compositions according to the invention, ie, they are especially It defines the temperature range that can be fiberized by the treatment.
【００３３】 そのような鉱滓綿は、上述したように、測定方法が中性または僅かに塩基性の
ｐＨ或いは酸性のｐＨのいずれを伴おうとも、十分な水準の生分解性を有してい
る。As mentioned above, such mineral wool has a sufficient level of biodegradability, regardless of whether the measurement method involves a neutral or slightly basic pH or an acidic pH. .
【００３４】 それゆえ、本発明に係る鉱滓綿は、一般には、ｐＨ４．５で測定した場合（特
にはシリカで測定して）に１時間当たり少なくとも３０、好ましくは少なくとも
４０、さらには少なくとも５０ｎｇ／ｃｍ2の、及びｐＨ７．５で測定した場合
（特にはシリカで測定して）に１時間当たり少なくとも３０、好ましくは少なく
とも４０、さらには少なくとも５０ｎｇ／ｃｍ2の分解率を有する。The mineral wool thus according to the invention is therefore generally at least 30, preferably at least 40 and even at least 50 ng / h when measured at pH 4.5 (in particular as measured on silica). It has a degradation rate of at least 30, preferably at least 40, and even at least 50 ng / cm 2 per hour when measured at cm 2 and at pH 7.5 (particularly as measured on silica).
【００３５】 一般に、そのような鉱滓綿は、ｐＨ４．５で測定した場合に１時間当たり少な
くとも３０、好ましくは少なくとも４０、さらには少なくとも５０ｎｇ／ｃｍ2
の分解速度を、及びｐＨ６．９で測定した場合に１時間当たり少なくとも３０、
好ましくは少なくとも４０、さらには少なくとも５０ｎｇ／ｃｍ2の分解率を有
する。Generally, such mineral wool is at least 30, preferably at least 40, and even at least 50 ng / cm 2 per hour as measured at pH 4.5.
Of at least 30, as measured at pH 6.9, per hour.
Preferably it has a degradation rate of at least 40, and even at least 50 ng / cm 2 .
【００３６】 一般に、それはまた、ｐＨ７．５で測定した場合に１時間当たり少なくとも６
０、特には少なくとも８０／ｃｍ2の分解速度及び／またはｐＨ６．９及び／ま
たはｐＨ７．５で測定した場合（特にはシリカで測定して）に１時間当たり少な
くとも４０、特には少なくとも６０／ｃｍ2の分解速度を有する。Generally, it will also have at least 6 per hour as measured at pH 7.5.
0, in particular at least a decomposition rate of 80 / cm 2 and / or at least 40, in particular at least 60 / cm, per hour when measured at pH 6.9 and / or pH 7.5 (particularly measured on silica). Has a decomposition rate of 2 .
【００３７】 本鉱滓綿は、断熱及び／または防音製品或いは土壌を用いない培地の製造に主
に使用される。本発明の主題は、少なくとも部分的に上記に規定された鉱滓綿を
備えたどのような製品でもある。The mineral wool is mainly used for the production of heat- and / or sound-insulating products or media without soil. The subject of the invention is any product comprising at least partially the mineral wool as defined above.
【００３８】[0038]
さらなる詳細及び有利な特徴は、以下の非制限的な好ましい態様の記載から明
らかになるであろう。Further details and advantageous features will become apparent from the following description of non-limiting preferred embodiments.
【００３９】 下記表１は、１５の例の化学組成物を重量百分率で与えている。Table 1 below gives the chemical compositions of the 15 examples in weight percentages.
【００４０】 全ての化合物の全ての成分の和が僅かに１００％未満である場合、残りの成分
は、その含有量がせいぜい０．５％乃至１％である少量の不純物／化合物（定量
的に決定されない）に相当する及び／または単に本分野で使用される分析方法で
受け入れられている近似によるものであることが理解されるべきである。If the sum of all components of all compounds is only less than 100%, the remaining components are small amounts of impurities / compounds whose content is at most 0.5% to 1% (quantitatively (Not determined) and / or simply by approximations accepted by analytical methods used in the art.
【００４１】[0041]
【表２】 [Table 2]
【００４２】[0042]
【表３】 [Table 3]
【００４３】 これら例に係る組成物は、外部遠心処理、特には前述した特許の示唆にしたが
う処理によって繊維化された。The compositions according to these examples were fibrillated by external centrifugation, in particular according to the teachings of the aforementioned patent.
【００４４】 それらの差Ｔlog1−Ｔliqによって規定される使用範囲は、十分に正（positiv
e）である。The range of use defined by their difference T log1 −T liq is sufficiently positive.
e).
【００４５】 全ての組成物は、０．８よりも高い及びさらには０．８５よりも高いＭｇＯ／
ＣａＯ比と非常に控えめな（１％未満の）或いはゼロのＰ2Ｏ5含有量とを有して
いる。また、それらは全て、およそ１７乃至２３％の高いアルミナ含有量を有し
ている。例６を除けば、全ての例は、およそ６乃至８％のＦｅ2Ｏ3含有量を有し
ている。殆ど鉄を有しておらず、多量のアルカリ土類金属酸化物を有している例
６は、上述した「ホワイト」ロックウールが製造されるのを可能とする。All compositions have MgO / g higher than 0.8 and even higher than 0.85.
It has a CaO ratio and a very modest (less than 1%) or zero P 2 O 5 content. Also, they all have a high alumina content of approximately 17 to 23%. With the exception of example 6, all examples have an Fe 2 O 3 content of approximately 6-8%. Example 6, which has little iron and high amounts of alkaline earth metal oxides, allows the "white" rock wool described above to be produced.
【００４６】 特には中性または僅かに酸性のｐＨ（ｐＨ６．９或いは７．５）で或いは酸性
のｐＨ（４．５）で測定されたそれらの生分解性は十分である。In particular, their biodegradability, measured at neutral or slightly acidic pH (pH 6.9 or 7.5) or at acidic pH (4.5), is sufficient.
【００４７】 以下の表２は、「ＫSiO2」で示され、１時間当たりのｎｇ／ｃｍ2で表現され
た例９、１０、及び１１に係る鉱滓綿中でのシリカの分解速度の測定結果を与え
ており； → 酸性のｐＨ（４．５）に緩衝された流体中でのインビトロ試験よるものを
「酸性流体」といい、 → およそ７．４乃至７．５のｐＨに緩衝された流体中でのインビトロ試験よ
るものを「中性流体」という。Table 2 below shows the results of measurements of the decomposition rate of silica in the mineral wool according to Examples 9, 10 and 11, designated as “K SiO 2” and expressed in ng / cm 2 per hour. → an in vitro test in a fluid buffered to an acidic pH (4.5) is referred to as an “acidic fluid”; → a fluid buffered to a pH of approximately 7.4 to 7.5. The result of an in vitro test in the medium is called "neutral fluid".
【００４８】[0048]
【表４】 [Table 4]
【００４９】 これら結果から、アルミナ含有量が高くなるのに応じて、酸性ｐＨでの分解速
度がより高くなり、中性のｐＨでもより少ない程度で分解速度がより高くなるこ
とが明らかとなるように思える。From these results it can be seen that the higher the alumina content, the higher the decomposition rate at acidic pH, and the lower the rate at neutral pH, the higher the decomposition rate. Seems to be.
【００５０】 上述した配合を満足し０．７５のＭｇＯ／ＣａＯ比を有する２つの追加の例で
ある例１６及び１７もまた有用であることが証明された。[0050] Two additional examples, Examples 16 and 17, which satisfy the above formulation and have a MgO / CaO ratio of 0.75, have also proven useful.
【００５１】 それら組成物は、以下の表３において表１と同様の成分と共に詳細に与えられ
ている。The compositions are given in detail in Table 3 below with the same components as in Table 1.
【００５２】[0052]
【表５】 [Table 5]
【手続補正書】[Procedure amendment]
【提出日】平成１２年３月２７日（２０００．３．２７）[Submission date] March 27, 2000 (2000.3.27)
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００３６[Correction target item name] 0036
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００３６】 一般に、それはまた、ｐＨ４．５で測定した場合に１時間当たり少なくとも６
０、特には少なくとも８０ｎｇ／ｃｍ2の分解速度及び／またはｐＨ６．９及び
／またはｐＨ７．５で測定した場合（再度、特にはシリカで測定して）に１時間
当たり少なくとも４０、特には少なくとも６０ｎｇ／ｃｍ2の分解速度を有する
。Generally, it will also have at least 6 per hour as measured at pH 4.5.
0, in particular at least 80 ng / cm 2 and / or at least 40, in particular at least 60 ng per hour, as measured at pH 6.9 and / or pH 7.5 (again, especially at silica). / Cm 2 .
───────────────────────────────────────────────────── フロントページの続き (72)発明者 ラフォン、ファブリス フランス国、エフ − 75018 パリ、リ ュ・エルメル 34 (72)発明者 ドゥ・ムランゴ、アラン フランス国、エフ − 75005 パリ、リ ュ・サン・ジャック 294 Ｆターム(参考） 2B022 BA05 BB04 2B314 PC04 PC23 4G062 AA05 BB01 BB06 DA05 DB04 DC01 DC02 DC03 DD01 DD02 DD03 DE01 DF01 EA01 EB01 EB02 EB03 EC01 EC02 EC03 ED04 ED05 EE04 EE05 EF01 EG01 FA01 FA10 FB01 FB02 FB03 FC01 FD01 FE01 FF01 FG01 FH01 FJ01 FK01 FL01 GA01 GA10 GB01 GB02 GB03 GC01 GD01 GE01 HH01 HH03 HH05 HH07 HH09 HH10 HH11 HH12 HH13 HH15 HH17 HH20 JJ01 JJ03 JJ05 JJ07 JJ10 KK01 KK03 KK05 KK07 KK10 MM40 NN29 NN40 ──────────────────────────────────────────────────の Continuing on the front page (72) Inventor Lafon, Fabrice France, F-75018 Paris, Rue Hermer 34 (72) Inventor de Murango, Alain France, F-75005 Paris, Rhu Saint・ Jack 294 F term (reference) 2B022 BA05 BB04 2B314 PC04 PC23 4G062 AA05 BB01 BB06 DA05 DB04 DC01 DC02 DC03 DD01 DD02 DD03 DE01 DF01 EA01 EB01 EB02 EB03 EC01 EC02 EC03 ED04 ED05 EE04 EE05 EF01 FB01 EF01 FB01 FG01 FH01 FJ01 FK01 FL01 GA01 GA10 GB01 GB02 GB03 GC01 GD01 GE01 HH01 HH03 HH05 HH07 HH09 HH10 HH11 HH12 HH13 HH15 HH17 HH20 JJ01 JJ03 JJ05 JJ07 JJ10 KK01 KK03 KK40 NN10 NN07
Claims (16)
率： ＳｉＯ2 ３８〜４６％、特には少なくとも４０％ Ａｌ2Ｏ3 １６〜２４％ ＭｇＯ １０〜２０％ ＲＯ（ＣａＯ＋ＭｇＯ） １６〜４０％ ＭｇＯ／ＣａＯ ≧０．８ Ｒ2Ｏ（Ｎａ2Ｏ＋Ｋ2Ｏ） ≧０．３％ Ｐ2Ｏ5 ０〜５％ Ｆｅ2Ｏ3（全ての鉄） ≧０．５％ ＴｉＯ2 ０〜３％ ＭｎＯ ０〜２％ ＳＯ3 ０〜２％ で含有することを特徴とする鉱滓綿。1. The following components, which can be degraded in physiological media and contain the following components in percentage by weight: 38 to 46% of SiO 2 , in particular at least 40% 16 to 24% of Al 2 O 3 10 to 20% of MgO RO ( CaO + MgO) 16-40% MgO / CaO ≧ 0.8 R 2 O (Na 2 O + K 2 O) ≧ 0.3% P 2 O 5 0-5% Fe 2 O 3 (all iron) ≧ 0.5% Mineral slag wool characterized by containing TiO 2 0-3% MnO 0-2% SO 3 0-2%.
とも２または２．２％ で含有することを特徴とする請求項１ないし３のいずれか１項に記載の鉱滓綿。4. An R 2 O oxide (Na 2 O + K 2 O) having the following weight percentages: 0.3 to 1%, alternatively higher than 1% and up to 6%, in particular at least 2 or 2.2%. The mineral wool according to any one of claims 1 to 3, wherein the mineral wool is contained.
５ を満足することを特徴とする請求項１ないし４のいずれか１項に記載の鉱滓綿。5. The following relationship: MgO / CaO> 0.85, preferably> 0.95, especially> 1 or> 1.1.
5. The mineral wool according to claim 1, which satisfies (5).
を満足することを特徴とする請求項１ないし５のいずれか１項に記載の鉱滓綿。6. The following relationship: R 2 O / Al 2 O 3 = 0.07 to 0.08, preferably 0.09 to 0.3
The mineral wool cotton according to any one of claims 1 to 5, which satisfies the following.
たは３％までのＰ2Ｏ5を含有することを特徴とする請求項１ないし６のいずれか
１項に記載の鉱滓綿。7. The composition according to claim 1, which contains 0 to 0.1% by weight, or more than 0.1% and up to 2 or 3% of P 2 O 5. Mineral slag wool according to the item.
Ｏ3を特には０．１乃至５％の含有量で含有することを特徴とする請求項１ない
し７のいずれか１項に記載の鉱滓綿。8. MnO, in particular in a content of 0.1 to 4% and / or B 2
Mineral wool according to any one of claims 1 to 7 O 3 in particular is characterized in that it contains in a content of 0.1 to 5%.
鉱滓綿。9. The method according to claim 1, wherein MgO is contained in a content by weight of MgO ≧ 11%, in particular 19%, preferably 12 to 15%. Mineral slag wool as described.
鉱滓綿。10. CaO content in the following percentage: CaO = 22%, in particular 10%, preferably 11 to 18%, or higher than 18% and up to 21%. 10. Mineral slag wool according to any one of 1 to 9.
の鉱滓綿。11. The method according to claim 1, wherein the content of Al 2 O 3 is as follows: Al 2 O 3 ≧ 18.5%, in particular ≧ 19% or 20%. Or the mineral waste wool according to claim 1.
ｃｍ2の分解速度とｐＨ７．５で測定して１時間当たり少なくとも３０ｎｇ／ｃ
ｍ2の分解速度とを有していることを特徴とする請求項１ないし１１のいずれか
１項に記載の鉱滓綿。12. At least 30 ng / hour as measured at pH 4.5.
at least 30 ng / c per hour as measured at a decomposition rate of cm 2 and pH 7.5
mineral wool according to any one of claims 1 to 11, characterized in that it has a degradation rate of m 2.
ｃｍ2の分解速度とｐＨ６．９で測定して１時間当たり少なくとも３０ｎｇ／ｃ
ｍ2の分解速度とを有していることを特徴とする請求項１ないし１２のいずれか
１項に記載の鉱滓綿。13. At least 30 ng / hour as measured at pH 4.5.
at least 30 ng / c per hour as measured at a decomposition rate of cm 2 and pH 6.9
mineral wool according to any one of claims 1 to 12, characterized in that it has a degradation rate of m 2.
ｃｍ2の分解速度及び／またはｐＨ７．５で測定して１時間当たり少なくとも４
０ｎｇ／ｃｍ2の分解速度及び／またはｐＨ６．９で測定して１時間当たり少な
くとも４０ｎｇ／ｃｍ2の分解速度を有していることを特徴とする請求項１ない
し１３のいずれか１項に記載の鉱滓綿。14. At least 60 ng / hour as measured at pH 4.5.
at least 4 per hour as measured at a decomposition rate of cm 2 and / or pH 7.5.
Claims 1, characterized in that it has a degradation rate of 0 ng / cm 2 degradation rate and / or measured at pH6.9 for one hour per at least 40 ng / cm 2 according to any one of the 13 Mineral wool.
１ないし１４のいずれか１項に記載の鉱滓綿。15. The mineral wool according to claim 1, which is obtained by an external centrifugation treatment.
記載の鉱滓綿を備えた断熱及び／または防音製品或いは土壌を用いない培地。16. An insulated and / or sound-insulated product or a soil-free medium comprising at least partially the mineral wool of claim 1.