JP2002371452A - Raised fabric - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an epoch-making blanket that retains the soft and bulk feeling of the acryl Mayer blanket and can reduce the quilt cover slipping down. SOLUTION: The raised fabric includes >=30 wt.% of shrinkable synthetic fiber with a shrinkage of >=15% and at least 10 wt.% of animal hair and the mixed yarn forms piles. In the raised fabric, >=20 wt.% of animal hair fibers distributes on the pile face within 1 mm range from the top edge of the raised fabric and the static friction coefficients F1, F2, F3, and F4 are all >=2.0 (wherein F1 and F2 show the static friction coefficients in the vertically upward and downward directions, while F3 and F4 indicate the static friction coefficients in the two left and right transverse directions.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、掛け毛布として使
用する立毛布帛に関し、特に着用時に布団がずれにくい
性能を有する立毛布帛に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a napped fabric used as a blanket, and more particularly to a napped fabric having a performance in which a futon hardly slips when worn.

【０００２】[0002]

【従来の技術】近年立毛布帛、特に毛布分野において
は、合成繊維、特にアクリル系合成繊維の紡績糸からな
るマイヤー毛布が主流である。しかし、ソフトな風合い
と相反して、毛布の上に掛ける布団が滑り落ちやすいと
いう問題がある。これについては、立毛面の隣り合う領
域が逆方向に傾くように、編組織が互いに逆となる状態
で編成する方法（特開平１０−１８５３号公報）が提案
されている。この方法は技術的には優れているが、編組
織が煩雑で、汎用性に乏しい。一方、ウールの織り毛布
は従来から根強い人気があるが、ソフトでボリュウムが
あると言う点ではポリッシャーによる毛伸び加工を受け
たアクリルマイヤー毛布には及ばない。2. Description of the Related Art In recent years, in the field of napped fabrics, particularly in the field of blankets, a Meyer blanket made of spun yarn of synthetic fibers, particularly acrylic synthetic fibers, has become the mainstream. However, contrary to the soft texture, there is a problem that the futon on the blanket easily slips off. Regarding this, there has been proposed a method of knitting in a state where the knitted structures are opposite to each other such that adjacent regions of the napped surface are inclined in the opposite direction (Japanese Patent Laid-Open No. 10-1853). Although this method is technically excellent, the knitting structure is complicated and versatility is poor. On the other hand, wool woven blankets have long been popular, but they are not as good as acrylic-meyer blankets that have been stretched by a polisher in that they are soft and have a volume.

【０００３】[0003]

【発明が解決しようとする課題】本発明は、アクリルマ
イヤー毛布のソフトさとボリュウム感を持ちつつ、か
つ、布団のずれおちを低減する画期的な毛布を得ること
に有る。SUMMARY OF THE INVENTION It is an object of the present invention to provide an epoch-making blanket which has the softness and voluminous feel of an acrylic Meyer blanket and reduces slippage of a futon.

【０００４】[0004]

【課題を解決するための手段】本発明は、収縮率１５％
以上の収縮性合成繊維（Ａ）を３０ｗｔ％以上含有し、
獣毛系繊維（Ｂ）を少なくとも１０ｗｔ％以上含有する
混紡糸がパイルを形成する立毛布帛であって、立毛布帛
の先端１ｍｍの範囲にあるパイル面に獣毛繊維が２０ｗ
ｔ％以上偏在しており、かつＦ１、Ｆ２、Ｆ３、Ｆ４で
表されるタテの上下方向、ヨコの左右方向の、４方向の
静摩擦係数が、全て２．０以上であることを特徴とする
立毛布帛である。但し、ここでＦ１及びＦ２がタテの上
下２方向、Ｆ３及びＦ４がヨコの左右２方向の静摩擦係
数を示す。According to the present invention, a shrinkage ratio of 15% is provided.
The above-mentioned shrinkable synthetic fiber (A) contains 30 wt% or more,
A blended yarn containing at least 10 wt% or more of animal hair-based fibers (B) is a napping fabric forming a pile, and the woolen hair has a weight of 20 w
t% or more, and the coefficient of static friction in four directions of the vertical direction and the horizontal direction of the horizontal represented by F1, F2, F3, and F4 is all 2.0 or more. It is a napping cloth. Here, F1 and F2 indicate the vertical friction coefficients of the vertical direction, and F3 and F4 indicate the static friction coefficients of the horizontal direction of the horizontal.

【０００５】以下、本発明の立毛布帛を詳細に説明す
る。本発明の収縮性合成繊維において、熱水収縮率は１
５％以上必要である。熱水収縮率が１５％以上の場合
は、獣毛繊維を表面に偏在させる効果が向上する。収縮
性合成繊維の含有率は３０ｗｔ％以上であることが必要
である。収縮性合成繊維の含有量が３０ｗｔ％以上であ
る場合は、獣毛繊維を表面に偏在させる効果が向上す
る。収縮性合成繊維は、熱収縮率を満足すれば、素材は
ポリエステル系、ナイロン系、アクリル系のいづれでも
良い。素材のソフトさと、熱収縮性を発現させやすい点
で、アクリル系繊維が好ましい。Hereinafter, the napped fabric of the present invention will be described in detail. In the shrinkable synthetic fiber of the present invention, the hot water shrinkage rate is 1
5% or more is required. When the hot water shrinkage is 15% or more, the effect of unevenly distributing animal hair fibers on the surface is improved. It is necessary that the content of the shrinkable synthetic fiber is 30 wt% or more. When the content of the shrinkable synthetic fiber is 30% by weight or more, the effect of distributing the animal hair fibers to the surface is improved. The material of the shrinkable synthetic fiber may be any of polyester, nylon and acrylic as long as the heat shrinkage is satisfied. Acrylic fibers are preferred because of the softness of the material and the ease with which heat shrinkage can be exhibited.

【０００６】全体の風合いをソフトに保つ点から、収縮
性合成繊維の平均繊度は、３．３ｄｔｅｘ以下のものが
好ましく、より好ましくは２．２ｄｔｅｘ以下である。
獣毛系繊維としては、ウール、カシミア、ラム、などが
挙げられる。ソフト性という点ではファインデニールの
繊維素材が好ましいが、比較的安価に入手しやすいと言
う点では、ウールを推奨する。ウールとして、脱キュー
ティクル加工されたものを用いてもよいが、価格及びエ
ッジ効果の点から、脱キューティクル加工されていない
ものが好ましい。これ以外の繊維としては、天然繊維、
合成繊維のいずれであっても良い。獣毛系繊維の平均繊
度としては、８ｄｔｅｘ以下が好ましく、より好ましく
は６ｄｔｅｘ以下である。上記の繊維を２種以上用い
て、混紡して紡績糸を得る。この紡績糸を糸染めしてか
らボアを作成する方法や、紡績糸をマイヤー編機で編
み、通常の染色仕上げ工程を用いて、マイヤー毛布状の
立毛布帛を得ることができる。From the viewpoint of keeping the overall texture soft, the average fineness of the shrinkable synthetic fiber is preferably 3.3 dtex or less, more preferably 2.2 dtex or less.
Animal hair fibers include wool, cashmere, rum, and the like. Fine denier fiber material is preferred in terms of softness, but wool is recommended because it is relatively inexpensive and easily available. Wool that has been subjected to de-cuticle processing may be used, but is preferably not subjected to de-cuticle processing in terms of price and edge effect. Other fibers include natural fibers,
Any of synthetic fibers may be used. The average fineness of the animal hair fiber is preferably 8 dtex or less, more preferably 6 dtex or less. A spun yarn is obtained by blending two or more of the above fibers. A method of dyeing the spun yarn and then forming a bore, or knitting the spun yarn with a Meyer knitting machine and using a normal dyeing and finishing step, can obtain a Mayer blanket-like napped fabric.

【０００７】毛布としての使用にあたり、毛抜けが少な
いという点から、ダブルラッセルのマイヤー編み機で編
まれた、マイヤー毛布を推奨する。さらに、ソフト性を
確保するために、ポリッシャー加工されていることが好
ましい。ポリッシャー加工を行った後、シャーリング工
程で表面を刈りそろえるが、この時、イーブンカットで
仕上げても、獣毛繊維は偏在しているが、アンイーブン
カットに仕上げるとさらに偏在割合が増し、摩擦効果が
大きくなり滑り防止効果が増大する。カット仕上げにお
いて、カットの刈り込みが大きすぎると、偏在の効果が
失われるため注意を要する。さらに、獣毛繊維を表層に
偏在させたまま、タンブラーシープ加工をすることによ
り、獣毛繊維を表層に偏在させることができ、意匠性の
ある布帛を得ることもできる。For use as a blanket, a Meyer blanket knitted with a double Russell Meyer knitting machine is recommended because of less hair loss. Further, in order to secure softness, it is preferable that polisher processing is performed. After performing polisher processing, the surface is trimmed in the shirring process, but at this time, even if finished with even cut, animal hair fibers are unevenly distributed, but if uneven finish is applied, the uneven distribution ratio further increases, and the friction effect And the slip prevention effect increases. In the cut finishing, care must be taken if the cut is too large because the effect of uneven distribution is lost. Furthermore, by performing tumbler sheep processing while keeping the animal hair fibers unevenly distributed on the surface layer, the animal hair fibers can be unevenly distributed on the surface layer, and a designable fabric can be obtained.

【０００８】[0008]

【発明の実施の形態】以下、本発明を実施例などを用い
て更に具体的に説明する。実施例、比較例の評価法は以
下の方法による。 （１）静摩擦係数 添付白布（ＪＩＳ−Ｌ−０８０３に準拠）：綿（かなき
ん３号）を７×４×１. ５ｃｍの木片にはりつけ、これ
を用いて静摩擦係数を調べる。立毛布帛を３０×３０ｃ
ｍに切りだし、これを３０×３０ｃｍの板状物に固定
し、布帛の４方向（Ｆ１、Ｆ２、Ｆ３、Ｆ４）について
静摩擦係数を調べる。但し、Ｆ１及びＦ２がタテの上下
２方向、Ｆ３及びＦ４がヨコの左右２方向の静摩擦係数
を示す。静摩擦係数の測定としては、立毛布帛を固定し
た板を傾斜してゆき、すべりはじめる角度θを求め、静
摩擦係数＝ｔａｎθ、で静摩擦係数を算出する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described more specifically with reference to embodiments. The evaluation method of Examples and Comparative Examples is based on the following method. (1) Coefficient of static friction Attached white cloth (according to JIS-L-0803): Cotton (Kanakin No. 3) is attached to a 7 × 4 × 1.5 cm piece of wood, and the static friction coefficient is examined using this. 30x30c napping cloth
m, which is fixed on a 30 × 30 cm plate, and the coefficient of static friction is examined in four directions (F1, F2, F3, F4) of the fabric. However, F1 and F2 represent the vertical friction coefficients of the vertical direction, and F3 and F4 represent the static friction coefficients of the horizontal direction of the horizontal. As the measurement of the static friction coefficient, the plate on which the napped fabric is fixed is inclined to determine the angle θ at which slipping starts, and the static friction coefficient is calculated by the static friction coefficient = tan θ.

【０００９】（２）風合い パネラ５名により、ソフト性とボリュウム感を官能評価
にて以下の４段階に判定した。 ソフト性 ◎ 非常にソフトである。 ○ ソフトである。 △ まあまあソフトである。 × がさがさする。 ボリュウム感 ◎ 非常にボリュウム感がある。 ○ ボリュウム感がある。 △ まあまあボリュウム感がある。 × ボリュウム感が無い（ぺちゃっとした感じ）。(2) Texture The softness and the voluminous feel were evaluated by five panelists in the following four stages by sensory evaluation. Softness ◎ Very soft. ○ It is soft. △ Somewhat soft. × Finds. Volume feeling ◎ There is a very volume feeling. ○ There is a sense of volume. △ Somewhat voluminous. × There is no volume feeling (chubby feeling).

【００１０】（３）着用ずれ落ち性 パネラ５名により、立毛布帛と布団のずり落ち性を官能
評価にて以下の４段階に判定した。 ◎ 全くずれ落ちが無かった。 ○ ずれ落ちが殆どなかった。 △ ややずれ落ちた。 × すぐにずれ落ちて困った。 （４）獣毛繊維のパイル表面層の偏在割合 立毛布帛のパイル面の先端１ｍｍの範囲を、バリカンで
刈り取り、その重量を測定したのち、ＤＭＦ中でアクリ
ル繊維を溶解除去し、ウール成分だけとし、これを水洗
＆乾燥しウールの重量を求め、立毛布帛のパイル面の先
端１ｍｍの範囲での獣毛繊維の偏在割合を求めた。[0010] (3) Wear-slip-off property The sliding properties of the napped fabric and the futon were evaluated by sensory evaluation by five panelists according to the following four grades. ◎ There was no slippage. ○ There was almost no slippage. △ Slightly dropped. × I was in trouble because I fell off immediately. (4) Uneven distribution ratio of pile surface layer of animal hair fiber A range of 1 mm at the tip of the pile surface of the napkin is cut off with a clipper, and the weight is measured. This was washed with water and dried to determine the weight of the wool, and the uneven distribution ratio of animal hair fibers within a range of 1 mm at the tip of the pile surface of the napping fabric was determined.

【００１１】[0011]

【実施例１〜６、比較例１〜５】パイル糸として、所定
の繊度（ｄｔｅｘ）の丸断面の収縮性アクリル系繊維
（熱収縮率が２５％）と、種々の非収縮性アクリル系繊
維（いづれも旭化成（株）製）と、所定の繊度（ｄｔｅ
ｘ）のウールを各々表１に示す所定量の重量比で混紡し
て、紡績糸（メートル番手２／３２Ｓ（３７０／２１
０））とする。この紡績糸を用いて、さらに、インレイ
糸及びチェーン糸としてポリエステル繊維（１１０ｄｔ
ｅｘ／２４ｆ）を用い、カールマイヤーダブルラッセル
機を使用して、毛布を編み立てし（１飛び、１８ＧＧ、
釜間２２ｍｍ、１５Ｃ／ｉｎｃｈ）、その後、染色、水
洗、乾燥後ブラッシング、シャーリング、ポリッシン
グ、シャーリングを行い、各種マイヤー毛布用の生地を
作った。この生地を用いて、静摩擦係数の測定を行なっ
た。さらに、この生地のパイル面を外側にして２枚を合
わせて毛布を作った。この合わせ毛布を用いて着用テス
ト、官能評価を行なった。その結果を表１に示す。表１
に示すように、本発明の立毛布帛は、４方向の静摩擦係
数がいずれも２以上であり、掛け毛布として着用した場
合に、布団がずれ落ちにくく、かつ、ソフトでボリュウ
ム感がある。Examples 1 to 6 and Comparative Examples 1 to 5 Pile yarns of a predetermined size (dtex) of a round cross-sectional shrinkable acrylic fiber (heat shrinkage of 25%) and various non-shrinkable acrylic fibers (Both made by Asahi Kasei Corporation) and a predetermined fineness (dte
x) is mixed and spun at a predetermined weight ratio shown in Table 1 to give a spun yarn (meter count 2 / 32S (370/21).
0)). Using this spun yarn, a polyester fiber (110 dt) is used as an inlay yarn and a chain yarn.
ex / 24f), knit a blanket using a Karl-Meier double Russell machine (one jump, 18GG,
The distance between the kettles was 22 mm, 15 C / inch), followed by dyeing, washing with water, and drying, followed by brushing, shearing, polishing, and shearing to prepare various types of fabrics for Mayer blankets. Using this dough, the coefficient of static friction was measured. Further, a blanket was made by combining the two pieces with the pile surface of the dough facing outward. Using this blanket, a wearing test and a sensory evaluation were performed. Table 1 shows the results. Table 1
As shown in the figure, the raised fabric of the present invention has a coefficient of static friction in all four directions of 2 or more. When worn as a hanging blanket, the futon hardly slips off and has a soft and voluminous feel.

【００１２】[0012]

【表１】 [Table 1]

【００１３】[0013]

【発明の効果】本発明により、アクリルマイヤー毛布の
ソフトさとボリュウム感を持ちつつ、かつ、静摩擦係数
が高いことにより布団のずれおちを低減する画期的な毛
布を提供することができた。According to the present invention, it is possible to provide an epoch-making blanket having the softness and the voluminous feel of the acrylic Meyer blanket and reducing the slippage of the futon due to its high static friction coefficient.

Claims (5)

【特許請求の範囲】[Claims] 【請求項１】 収縮率１５％以上の収縮性合成繊維
（Ａ）を３０ｗｔ％以上含有し、獣毛系繊維（Ｂ）を少
なくとも１０ｗｔ％以上含有する混紡糸がパイルを形成
する立毛布帛であって、該立毛布帛の先端１ｍｍの範囲
におけるパイル面に獣毛繊維（Ｂ）が２０％ｗｔ以上偏
在しており、かつＦ１、Ｆ２、Ｆ３、Ｆ４の静摩擦係数
が全て２．０以上であることを特徴とする立毛布帛。但
し、Ｆ１及びＦ２がタテの上下２方向、Ｆ３及びＦ４が
ヨコの左右２方向の静摩擦係数を示す。1. A napping fabric in which a blended yarn containing 30% by weight or more of shrinkable synthetic fibers (A) having a shrinkage of 15% or more and at least 10% by weight of animal hair fibers (B) forms a pile. The animal hair fibers (B) are unevenly distributed on the pile surface within a range of 1 mm at the tip of the napping fabric by 20% wt or more, and the static friction coefficients of F1, F2, F3 and F4 are all 2.0 or more. A napped fabric characterized by the following. Here, F1 and F2 indicate the vertical friction coefficients in the vertical two directions, and F3 and F4 indicate the static friction coefficients in the horizontal left and right directions. 【請求項２】 獣毛系繊維（Ｂ）の平均繊度が８ｄｔｅ
ｘ以下であることを特徴とする請求項１記載の立毛布
帛。2. The average fineness of the animal hair fiber (B) is 8 dte.
The napped fabric according to claim 1, wherein x is equal to or less than x. 【請求項３】 合成繊維（Ａ）の平均繊度が３．３ｄｔ
ｅｘ以下であることを特徴とする請求項１又は２記載の
立毛布帛。3. The synthetic fiber (A) has an average fineness of 3.3 dt.
ex. It is less than or equal to ex. 【請求項４】 合成繊維（Ａ）がアクリル系繊維である
ことを特徴とする請求項１〜３のいずれかに記載の立毛
布帛。4. The raised fabric according to claim 1, wherein the synthetic fiber (A) is an acrylic fiber. 【請求項５】 立毛布帛のパイル面がアンイーブンカッ
トされていることを特徴とする請求項１〜４のいずれか
に記載の立毛布帛。5. The napped fabric according to claim 1, wherein the pile surface of the napped fabric is uneven-cut.