JP2002356633A - Ink for forming hiding layer accepting ink-jet ink and recording sheet using the same - Google Patents
Ink for forming hiding layer accepting ink-jet ink and recording sheet using the sameInfo
- Publication number
- JP2002356633A JP2002356633A JP2001161139A JP2001161139A JP2002356633A JP 2002356633 A JP2002356633 A JP 2002356633A JP 2001161139 A JP2001161139 A JP 2001161139A JP 2001161139 A JP2001161139 A JP 2001161139A JP 2002356633 A JP2002356633 A JP 2002356633A
- Authority
- JP
- Japan
- Prior art keywords
- ink
- printed
- postcard
- forming
- concealing layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、インクジェットイ
ンク受容性隠蔽層形成用インクおよびそれを用いた記録
用シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink for forming an ink-jet ink receptive concealing layer and a recording sheet using the same.
【０００２】[0002]
【従来の技術】図１１〜２０に従来の記録用シートの構
成の一例を示す。ここで、図１１は、三つ折りハガキの
表面展開図、図１２はこのハガキの裏面展開図、図１３
は図１１のＸ−Ｘ線断面図、図１４は図１１のハガキを
折り込む際の状態説明図、図１５は二つ折りハガキの表
面展開図、図１６はこのハガキの裏面展開図、図１７は
図１５のハガキを折り込む際の状態説明図、図１８は部
分二つ折りハガキの表面展開図、図１９はこのハガキの
裏面展開図、図２０は図１８のハガキを折り込む際の状
態説明図である。2. Description of the Related Art FIGS. 11 to 20 show an example of the configuration of a conventional recording sheet. Here, FIG. 11 is a developed front view of the three-fold postcard, FIG. 12 is a developed rear view of the postcard, and FIG.
11 is a cross-sectional view taken along the line XX of FIG. 11, FIG. 14 is a state explanatory view when the postcard of FIG. 11 is folded, FIG. 15 is a front view of the folded double postcard, FIG. 16 is a rear view of this postcard, and FIG. 15 is a front view of the partially folded postcard of FIG. 15, FIG. 18 is a front view of the partially folded postcard, FIG. 19 is a rear view of the postcard, and FIG. 20 is a front view of the postcard of FIG. .
【０００３】先ず、図１１ないし図１３に示す三つ折り
ハガキ１は、定型ハガキサイズの３倍のサイズを有する
基体シート２から構成され、折り線３ａ、３ｂによって
３つの領域に区画されるものである。左側区画領域Ａの
表面には、郵便番号、宛て名、住所等の宛て先情報印刷
４がインクジェットインクを用いて印刷され、また中央
区画領域Ｂの表裏面及び右側区画領域Ｃの表面には隠蔽
情報印刷５が、基体シート２に直接印刷されている。さ
らに、この印刷された基体シート２の区画領域Ｂ及びＣ
の表面全体と区画領域Ａ及びＢの裏面全体に対し、感圧
接着剤が塗布されて剥離可能な接着層６が形成されてい
る。このように構成された三つ折りハガキ１は、図１４
に示すように、各区画の重ね合わせ面を折り線３ａ、３
ｂにてＺ型に折り込んで接着層同士を対接させ、この状
態でドライシーラーをもって加圧することにより、その
接着層６が活性化されて接着される。First, a three-fold postcard 1 shown in FIGS. 11 to 13 is composed of a base sheet 2 having a size three times the size of a standard postcard, and is divided into three regions by folding lines 3a and 3b. is there. A destination information print 4 such as a zip code, a destination name, and an address is printed on the front surface of the left-side partitioned area A using ink-jet ink, and is hidden on the front and back surfaces of the central partitioned area B and the front face of the right-side partitioned area C. An information print 5 is printed directly on the base sheet 2. Further, the divided areas B and C of the printed base sheet 2
A pressure-sensitive adhesive is applied to the entire front surface and the entire back surface of the divided areas A and B to form a peelable adhesive layer 6. The three-fold postcard 1 configured as described above is similar to that of FIG.
As shown in FIG.
The adhesive layer 6 is folded into a Z-shape at b, and the adhesive layers are brought into contact with each other. In this state, the adhesive layer 6 is activated and bonded by pressing with a dry sealer.
【０００４】次に、図１５及び図１６に示す二つ折りハ
ガキ１１は、定型ハガキサイズの２倍のサイズを有する
基体シート２から構成され、中央部の折り線３によって
２つの領域Ｄ及びＥに区画されるものである。左側区画
領域Ｄの表面には、郵便番号、宛て名、住所等の宛て先
情報印刷４がインクジェットインクを用いて印刷され、
また区画領域Ｄ及びＥの裏面には隠蔽情報印刷５が、基
体シート２に直接印刷されている。さらに、この印刷さ
れた基体シート２の区画領域Ｄ及びＥの裏面全体に対
し、感圧接着剤が塗布されて剥離可能な接着層６が形成
されている。このように構成された二つ折りハガキ１１
は、図１７に示すように、上記の三つ折りハガキと同様
に、左右区画裏面の接着層同士が対接するように折り線
３で折り込んで加圧することにより、その接着層６が活
性化されて接着される。[0005] Next, a two-fold postcard 11 shown in FIGS. 15 and 16 is composed of a base sheet 2 having a size twice as large as a standard postcard, and is divided into two regions D and E by a folding line 3 at the center. It is what is divided. A destination information print 4 such as a postal code, a destination name, and an address is printed on the surface of the left-side partitioned area D using inkjet ink.
In addition, the concealment information print 5 is printed directly on the base sheet 2 on the back surfaces of the divided areas D and E. Further, a pressure-sensitive adhesive is applied to the entire back surface of the divided areas D and E of the printed base sheet 2 to form an adhesive layer 6 that can be peeled off. Folded postcard 11 configured in this way
As shown in FIG. 17, similarly to the above-described three-fold postcard, the adhesive layer 6 is activated by folding at the folding line 3 so that the adhesive layers on the back surfaces of the left and right sections are in contact with each other and pressing. Glued.
【０００５】また、図１８及び図１９に示す部分二つ折
りハガキ２１は、定型ハガキサイズの１．５倍のサイズ
を有する基体シート２から構成され、折り線３によって
サイズの異なる左右２つの領域Ｆ及びＧに区画されるも
のである。左側区画領域Ｆの表面には、郵便番号、宛て
名、住所等の宛て先情報印刷４がインクジェットインク
を用いて印刷され、また右側区画領域Ｇの裏面には隠蔽
情報印刷５が、基体シート２に直接印刷されている。さ
らに、この印刷された基体シート２の区画領域Ｇの裏面
全体及び区画領域Ｇを折り線３で折り込んだ際に重ね合
わされる区画領域Ｆの一部裏面に対し、感圧接着剤が塗
布されて剥離可能な接着層６が形成されている。このよ
うに構成された部分二つ折りハガキ２１は、図２０に示
すように、上記の二つ折りハガキと同様に、左右区画裏
面の接着層同士が対接するように折り線３で折り込んで
加圧することにより、その接着層６が活性化されて接着
される。A partial two-fold postcard 21 shown in FIGS. 18 and 19 is composed of a base sheet 2 having a size 1.5 times the size of a standard postcard. And G. A destination information print 4 such as a zip code, a destination name, an address, etc. is printed on the front surface of the left partitioned area F using an inkjet ink, and a concealed information print 5 is printed on the back surface of the right partitioned area G. Is printed directly on the Further, a pressure-sensitive adhesive is applied to the entire back surface of the divided region G of the printed base sheet 2 and a part of the back surface of the divided region F which is overlapped when the divided region G is folded along the folding line 3. A peelable adhesive layer 6 is formed. As shown in FIG. 20, the partially folded postcard 21 configured as described above is folded and pressed at the folding line 3 so that the adhesive layers on the back surfaces of the left and right sections are in contact with each other, similarly to the above-described two-fold postcard. Thereby, the adhesive layer 6 is activated and adhered.
【０００６】しかし、図１１〜１４に示す三つ折りハガ
キ１の場合、区画領域Ｃの表面に印刷した隠蔽情報印刷
５が区画領域Ｃの裏面側から透けて見えないように区画
領域Ｃの裏面に色インクを用いて字紋などを予め濃く印
刷するが、区画領域Ａの表面には郵便番号、宛て名、住
所等の宛て先情報印刷４を印刷するので色インクを用い
て字紋などを濃く印刷できないために区画領域Ｂの裏面
に印刷した隠蔽情報印刷５が区画領域Ａの宛て先情報印
刷４を印刷した表面側から透けて見えるという問題があ
った。However, in the case of the three-fold postcard 1 shown in FIGS. 11 to 14, the concealment information print 5 printed on the front surface of the partitioned area C is printed on the back side of the partitioned area C so that it cannot be seen through from the back side of the partitioned area C. A character pattern or the like is printed in dark using color ink in advance, but a destination information print 4 such as a postal code, a destination name, and an address is printed on the surface of the partitioned area A, so the character pattern and the like are dark using color ink. Since printing cannot be performed, the concealment information print 5 printed on the back surface of the partition area B is seen through from the front side of the partition area A on which the destination information print 4 is printed.
【０００７】同様に図１５〜１７に示す二つ折りハガキ
１１の場合は、区画領域Ｅの表面に印刷した隠蔽情報印
刷５が区画領域Ｅの裏面側から透けて見えないように区
画領域Ｅの裏面に色インクを用いて字紋などを予め濃く
印刷するが、区画領域Ｄの表面には郵便番号、宛て名、
住所等の宛て先情報印刷４を印刷するので色インクを用
いて字紋などを濃く印刷できないために区画領域Ｄの裏
面に印刷した隠蔽情報印刷５が区画領域Ｄの宛て先情報
印刷４を印刷した表面側から透けて見えるという問題が
あった。Similarly, in the case of the two-fold postcard 11 shown in FIGS. 15 to 17, the concealment information print 5 printed on the front surface of the divided area E is not seen through from the back side of the divided area E. Is printed in dark using color ink in advance, but the postal code, address,
Since the address information print 4 such as an address is printed, the concealment information print 5 printed on the back surface of the section area D prints the address information print 4 of the section area D because character prints and the like cannot be printed densely using color ink. There is a problem that it can be seen through from the surface side.
【０００８】同様に図１８〜２０に示す部分二つ折りハ
ガキ２１の場合は、区画領域Ｇの表面に印刷した隠蔽情
報印刷５が区画領域Ｇの裏面側から透けて見えないよう
に区画領域Ｇの裏面に色インクを用いて字紋などを予め
濃く印刷するが、区画領域Ｆの表面には郵便番号、宛て
名、住所等の宛て先情報印刷４を印刷するので色インク
を用いて字紋などを濃く印刷できないために区画領域Ｆ
の裏面に印刷した隠蔽情報印刷５が区画領域Ｆの宛て先
情報印刷４を印刷した表面側から透けて見えるという問
題があった。Similarly, in the case of the partially folded postcard 21 shown in FIGS. 18 to 20, the concealment information print 5 printed on the front surface of the divided area G is not seen through from the back side of the divided area G. A character pattern or the like is printed in dark using color ink on the back surface in advance, but a destination information print 4 such as a zip code, a destination name, and an address is printed on the front surface of the partitioned area F. Area F
There is a problem that the concealment information print 5 printed on the back side of the print area can be seen through from the front side of the destination area print 4 of the partitioned area F.
【０００９】一方、インクジェットインクを使用するイ
ンクジェットプリンタはカラー化が容易で、安価であ
り、高解像度が可能である、保存性に優れているなどの
多くの優れた点を持っているが、上質紙に印字するとイ
ンクの定着性に劣り、印字したインクが基材表面に残る
ため、連続的に印字された場合などにはガイドロールが
汚れたり、印字画像の汚れ発生する問題があり、またイ
ンクジェット印字が滲んだり、耐水性に劣る問題があっ
た。特に情報産業分野で使用する場合、インクジェット
印字されたバーコードなどが滲んで読み取り難くなった
り、インクジェット印字された郵便物などが野外にて雨
に曝されたり、あるいは誤って水が掛かってしまった場
合などには、溶けて印字内容が見えなくなる問題があっ
た。On the other hand, an ink-jet printer using an ink-jet ink has many advantages such as easy colorization, low cost, high resolution, and excellent storage stability. When printing on paper, the ink fixability is poor, and the printed ink remains on the substrate surface.Therefore, when printing is performed continuously, there is a problem that the guide roll becomes dirty, and the printed image becomes dirty. There were problems such as blurred printing and poor water resistance. In particular, when used in the information industry, ink-printed barcodes and the like are blurred and difficult to read, and mail-printed articles and the like are exposed to rain outdoors or accidentally splashed with water. In some cases, there is a problem that the printed content is melted and the printed content becomes invisible.
【００１０】[0010]
【発明が解決しようとする課題】本発明の第１の目的
は、従来の問題を解決し、隠蔽情報印刷５が先情報印刷
４を印刷した側から透けて見えないようにするととも
に、インクジェットインク吸収性に優れ、印字したイン
クジェットインクの耐水性が改善でき、しかも印字画像
の滲みが起こらないような、優れたインクジェットイン
ク受容性および隠蔽性を併せ持った隠蔽層形成用インク
を提供することであり、本発明の第２の目的は、そのよ
うなインクを用いて基材の所定部に形成され優れたイン
クジェットインク受容性および隠蔽性を併せ持った隠蔽
層を有する記録用シートを提供することである。SUMMARY OF THE INVENTION It is a first object of the present invention to solve the conventional problems and to prevent the concealment information print 5 from being seen through from the side on which the previous information print 4 was printed, and to provide an ink jet ink. An object of the present invention is to provide an ink for forming a concealing layer that has excellent absorbability, can improve the water resistance of a printed inkjet ink, and does not cause bleeding of a printed image. A second object of the present invention is to provide a recording sheet having a concealing layer formed on a predetermined portion of a substrate by using such an ink and having both excellent ink-jet ink receptivity and concealing property. .
【００１１】[0011]
【課題を解決するための手段】本発明者等は前記課題を
解決すべく鋭意研究を重ねた結果、特定の溶剤を主とし
て含むビヒクルを用い、このビヒクルに対して、白色微
粒子および蛍光物質を配合したインクを用いることによ
り解決できることを見出し、本発明を完成するに至っ
た。The present inventors have conducted intensive studies to solve the above-mentioned problems, and as a result, used a vehicle mainly containing a specific solvent, and blended white fine particles and a fluorescent substance with this vehicle. It has been found that the problem can be solved by using the prepared ink, and the present invention has been completed.
【００１２】すなわち、本発明の請求項１記載のインク
ジェットインク受容性隠蔽層形成用インクは、沸点１０
０℃以上のグリコール系溶剤を主成分として含むビヒク
ルに対して、白色微粒子および蛍光物質を配合したこと
を特徴とする。That is, the ink for forming an ink-jet ink receptive concealing layer according to claim 1 of the present invention has a boiling point of 10%.
It is characterized in that white fine particles and a fluorescent substance are blended with a vehicle containing a glycol-based solvent at 0 ° C. or higher as a main component.
【００１３】本発明の請求項２記載のインクジェットイ
ンク受容性隠蔽層形成用インクは、請求項１記載の隠蔽
層形成用インクにおいて、沸点１００℃以上のグリコー
ル系溶剤を主成分として含むビヒクル１００質量部に対
して、白色微粒子５〜４０質量部および蛍光物質０．１
〜１０質量部を配合したことを特徴とする。The ink for forming an ink-jet ink receptive concealing layer according to the second aspect of the present invention is the ink for forming a concealing layer according to the first aspect, which is a 100-mass vehicle containing a glycol-based solvent having a boiling point of 100 ° C. or higher as a main component. 5 to 40 parts by mass of white fine particles and 0.1
-10 parts by mass.
【００１４】本発明の請求項３記載の記録用シートは、
基材の少なくとも一方の面の所定部に請求項１あるいは
請求項２記載の隠蔽層形成用インクを用いて形成された
インクジェットインク受容性および隠蔽性を併せ持った
隠蔽層を有してなることを特徴とする。According to the third aspect of the present invention, there is provided a recording sheet comprising:
A concealing layer having both inkjet ink receptivity and concealing property formed by using the concealing layer forming ink according to claim 1 or 2 on a predetermined portion of at least one surface of the substrate. Features.
【００１５】特定の溶剤を主成分として含むビヒクルに
対して、白色微粒子および蛍光物質を配合したインクを
用いることにより、特別な乾燥装置が必要でなくなり、
そして隠蔽情報印刷５が先情報印刷４を印刷した側から
透けて見えないため情報が漏洩せず親展性が向上すると
ともに、基材に形成された隠蔽層へのインクジェットイ
ンク吸収性が優れ、印字画像の滲みが起こらず、印字し
たインクジェットインクの耐水性が改善でき、インクジ
ェット印字の印字品質を向上できる上、白色度が高く鮮
明なカラー印字ができる。さらに、印刷インク適性に優
れるため基材の必要な所定の箇所に容易に隠蔽層を形成
できるのでコストダウンを計ることができる上、オフセ
ット印刷に影響を与えない。By using an ink containing white fine particles and a fluorescent substance for a vehicle containing a specific solvent as a main component, a special drying device is not required,
Since the concealment information print 5 cannot be seen through from the side on which the previous information print 4 is printed, information does not leak and the confidentiality is improved, and the concealment layer formed on the base material has excellent ink-jet ink absorption, and Bleeding of the image does not occur, the water resistance of the printed inkjet ink can be improved, the printing quality of the inkjet printing can be improved, and clear color printing with high whiteness can be performed. Furthermore, since the concealing layer can be easily formed at a required portion of the base material due to its excellent printing ink suitability, the cost can be reduced and the offset printing is not affected.
【００１６】[0016]
【発明の実施の形態】本発明の優れたインクジェットイ
ンク受容性隠蔽層形成用インクは、沸点１００℃以上の
グリコール系溶剤を主として含有するビヒクルを用いる
ことが肝要であり、このビヒクルに対して、少なくとも
白色微粒子および蛍光物質を配合して調製される。この
ようなグリコール系溶剤を用いることにより特別な乾燥
装置が必要でなくなる。BEST MODE FOR CARRYING OUT THE INVENTION It is essential for the excellent ink for forming an ink-jet ink receptive concealing layer of the present invention to use a vehicle mainly containing a glycol-based solvent having a boiling point of 100 ° C. or higher. It is prepared by blending at least white fine particles and a fluorescent substance. The use of such a glycol solvent eliminates the need for a special drying device.
【００１７】本発明で用いるグリコール系溶剤は、水と
混合可能な中沸点および高沸点溶剤（沸点が１００℃以
上のもの）であり、具体的には、例えばグリコール（グ
リセリン、エチレングリコール、ジエチレングリコー
ル、トリエチレングリコール、ポリエチレングリコー
ル、プロピレングリコール、ジプロピレングリコール）
やグリコール誘導体（エチレングリコールモノメチルエ
ーテル、エチレングリコールモノエチルエーテル、エチ
レングリコールモノブチルエーテル、ジエチレングリコ
ールモノエチルエーテル、ジエチレングリコールモノブ
チルエーテル、エチレングリコールモノエチルエーテル
アセテート、エチレングリコールモノブチルエーテルア
セテート、ジエチレングリコールモノエチルエーテルア
セテート、ジエチレングリコールモノブチルエーテルア
セテート）などおよびこれらの２つ以上の混合物を挙げ
ることができる。The glycol solvent used in the present invention is a medium- and high-boiling solvent (having a boiling point of 100 ° C. or higher) which can be mixed with water. Specifically, for example, glycol (glycerin, ethylene glycol, diethylene glycol, Triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol)
And glycol derivatives (ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, ethylene glycol monoethyl ether acetate, ethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, diethylene glycol monoethyl Butyl ether acetate) and mixtures of two or more of these.
【００１８】本発明で用いる白色微粒子としては、具体
的には、例えばシリカ微粒子、二酸化チタン微粒子、ア
ルミナ微粒子、天然ゼオライト微粒子、合成ゼオライト
微粒子、炭酸カルシウム微粒子、活性白土微粒子など、
あるいはこれらの中から選ばれる２種以上の混合物など
を挙げることができる。Examples of the white fine particles used in the present invention include silica fine particles, titanium dioxide fine particles, alumina fine particles, natural zeolite fine particles, synthetic zeolite fine particles, calcium carbonate fine particles, activated clay fine particles, and the like.
Alternatively, a mixture of two or more kinds selected from these can be exemplified.
【００１９】本発明で用いる蛍光物質としては、具体的
には、例えばスチルベン、４，４’−ジアミノスチルベ
ン、ビフェニル、複素５員環（トリアゾール、オキサゾ
ール、イミダゾールなど）、複素６員環（クマリン、ナ
フタルイミド、ｓ−トリアジンなど）の誘導体などの蛍
光増白剤（メーカー名；例えば昭和化学社、昭和化工
社、日曹社、化薬社、三井社、住友社、大東社、チバ
社、バイエル社など）、蛍光顔料、蛍光染料などを挙げ
ることができる。Specific examples of the fluorescent substance used in the present invention include stilbene, 4,4'-diaminostilbene, biphenyl, 5-membered heterocyclic ring (triazole, oxazole, imidazole, etc.), and 6-membered heterocyclic ring (coumarin, Fluorescent whitening agents such as derivatives of naphthalimide, s-triazine, etc. (manufacturer names; for example, Showa Chemical Co., Showa Kakosha, Nisso, Kayaku, Mitsui, Sumitomo, Daitosha, Ciba, Bayer) And the like, fluorescent pigments, fluorescent dyes and the like.
【００２０】本発明で用いる白色微粒子および蛍光物質
の配合量は特に限定されるものではない。しかし、沸点
１００℃以上のグリコール系溶剤を主成分として含むビ
ヒクル１００質量部に対して、白色微粒子５〜４０質量
部、好ましくは１０〜３０質量部および蛍光物質０．１
〜１０質量部、好ましくは０．５〜８質量部を配合する
ことが好ましい。白色微粒子および蛍光物質の配合量が
下限値未満では隠蔽性が劣る恐れがあり、配合量が上限
値を超えると耐水性や印刷適性が劣る恐れがあるので好
ましくない。The amounts of the white fine particles and the fluorescent substance used in the present invention are not particularly limited. However, 5 to 40 parts by weight, preferably 10 to 30 parts by weight, and 0.1 to 30 parts by weight of white fine particles and 100 parts by weight of a vehicle containing a glycol solvent having a boiling point of 100 ° C. or higher as a main component are used.
It is preferable to add 10 to 10 parts by mass, preferably 0.5 to 8 parts by mass. If the blending amount of the white fine particles and the fluorescent substance is less than the lower limit, the concealing property may be deteriorated, and if the blending amount exceeds the upper limit, the water resistance and printability may be deteriorated, which is not preferable.
【００２１】本発明の隠蔽層形成用インクには、さらに
必要に応じて白色微粒子および蛍光物質のバインダーと
してバインダー樹脂を配合することができる。バインダ
ー樹脂としては、前記グリコール系溶剤とともに使用可
能なものであれば特に限定されない。具体的には、例え
ば、アルブミン、ゼラチン、カゼイン、でんぷん、アラ
ビアゴム、アルギン酸ソーダなどの天然樹脂、カルボキ
シメチルセルロース、ヒドロキシエチルセルロースなど
のセルロース誘導体、ポリアミド、ポリアクリルアミ
ド、ポリヒドロキシエチルメタクリレート、ポリフェニ
ルアセトアセタール、ポリエチレンイミン、ポリビニル
ピロリドン、ポリビニルピリジウムハライド、メラミン
樹脂、ポリウレタン、ポリビニルアルコールおよびその
誘導体、ポリエステル、ポリアクリル酸ソーダ、アクリ
ル酸エステル共重合体などの合成樹脂、ジメチルアミン
・エピクロルヒドリン重縮合物、アクリルアミド・ジア
リルアミン共重合物、ポリビニルアミン共重合物、ジシ
アンジアミド、ジメチル・ジアリル・アンモニウムクロ
ライドを主成分とする化合物あるいはこれらの２種以上
の混合物などのカチオン性樹脂、その他、電子線硬化型
インク、紫外線硬化型インク、スルホン酸基、カルボキ
シル基、硫酸エステル基、燐酸エステル基などのアニオ
ン性基を有する例えばロジン変成マレイン酸などのアニ
オン性樹脂などを挙げることができる。The ink for forming a concealing layer of the present invention may further contain a binder resin as a binder for white fine particles and a fluorescent substance, if necessary. The binder resin is not particularly limited as long as it can be used together with the glycol-based solvent. Specifically, for example, albumin, gelatin, casein, starch, gum arabic, natural resins such as sodium alginate, carboxymethyl cellulose, cellulose derivatives such as hydroxyethyl cellulose, polyamide, polyacrylamide, polyhydroxyethyl methacrylate, polyphenylacetoacetal, Polyethyleneimine, polyvinylpyrrolidone, polyvinylpyridium halide, melamine resin, polyurethane, polyvinyl alcohol and its derivatives, polyester, sodium polyacrylate, synthetic resin such as acrylate copolymer, dimethylamine / epichlorohydrin polycondensate, acrylamide Diallylamine copolymer, polyvinylamine copolymer, dicyandiamide, dimethyl diallyl ammonium chloride Cationic resin such as a compound containing as a main component or a mixture of two or more of these, electron beam curable ink, ultraviolet curable ink, sulfonic acid group, carboxyl group, sulfate group, phosphate group, etc. Anionic resins having anionic groups, such as rosin-modified maleic acid, can be mentioned.
【００２２】本発明の隠蔽層形成用インクには、さら
に、所望に応じてカチオン性樹脂や慣用されている添加
成分、例えば、粘着付与剤、粘度調整剤、酸化防止剤、
ｐＨ調節剤、消泡剤、各種安定剤、着色剤、滑剤などを
含有させることができる。The ink for forming a concealing layer according to the present invention may further contain, if desired, a cationic resin or a commonly used additive component such as a tackifier, a viscosity modifier, an antioxidant,
A pH adjuster, an antifoaming agent, various stabilizers, a coloring agent, a lubricant and the like can be contained.
【００２３】本発明の隠蔽層形成用インクは、グラビア
コーター、フレキソ、エアナイフコーター、バーコータ
ーなどの塗工手段により基材の少なくとも一方の面の所
定部に塗工し、隠蔽層を有する記録用シートを形成する
ことができる。したがって本発明においては、特別な乾
燥装置を必要としない。The ink for forming a concealing layer of the present invention is applied to a predetermined portion of at least one surface of a substrate by a coating means such as a gravure coater, flexo, air knife coater, bar coater, etc. Sheets can be formed. Therefore, a special drying device is not required in the present invention.
【００２４】本発明で用いる基材としては、通常の紙の
他に、合成紙、あるいはポリエチレン、透明性を有する
ポリエチレンテレフタレート、ポリプロピレン、塩化ビ
ニルなどの合成フィルムを用いることもできる。これら
の合成フィルムを用いる場合には基材の表面をマット処
理、コロナ処理などの表面処理を施すのが好ましい。ま
た、基材面への塗工量は、特に限定されないが、例えば
０．５〜３０ｇ／ｍ2、好ましくは３〜２０ｇ／ｍ2 、
さらに好ましくは５〜１５ｇ／ｍ2 とする。As the substrate used in the present invention, in addition to ordinary paper, synthetic paper or a synthetic film of polyethylene, transparent polyethylene terephthalate, polypropylene, vinyl chloride or the like can be used. When using these synthetic films, the surface of the substrate is preferably subjected to a surface treatment such as a mat treatment or a corona treatment. The coating amount on the substrate surface is not particularly limited, but is, for example, 0.5 to 30 g / m 2 , preferably 3 to 20 g / m 2 ,
More preferably, it is 5 to 15 g / m 2 .
【００２５】本発明において用いるインクジェットイン
クとしては、たとえば特開平７−２２８８０８号公報、
同７−２２８８０９号公報に記載のものを用いることが
できる。特に、アントラキノン系、ベンゾキノン系、ナ
フトキシキノン系、キサンテン系、トリフェニルメタン
系、キノリン系、インジゴイド系、アジン系、オキサジ
ン系、チアジン系およびメチン系染料からなる群から選
ばれた少なくとも１種のアニオン性インクが好適に用い
られる。これらの具体例については特開平７−２２８８
０９号公報の段落番号００１５に例示されている。この
インクに使用する媒体としては、水と水溶性有機溶媒と
の混合溶媒を用いることができる。このほかに、ｐＨ調
整剤、粘度調整剤、表面張力調整剤などを含有させるこ
とができる。As the ink-jet ink used in the present invention, for example, JP-A-7-228808,
No. 7,228,809 can be used. In particular, at least one anionic selected from the group consisting of anthraquinone, benzoquinone, naphthoxyquinone, xanthene, triphenylmethane, quinoline, indigoid, azine, oxazine, thiazine and methine dyes Ink is preferably used. These specific examples are described in JP-A-7-2288.
No. 09, paragraph No. 0015. As a medium used for this ink, a mixed solvent of water and a water-soluble organic solvent can be used. In addition, a pH adjuster, a viscosity adjuster, a surface tension adjuster and the like can be contained.
【００２６】図１〜１０は、本発明の記録用シートの一
実施形態を説明する説明図である。ここで、図１は、三
つ折りハガキの表面展開図、図２はこのハガキの裏面展
開図、図３は図１のＸ−Ｘ線断面図、図４は図１のハガ
キを折り込む際の状態説明図、図５は二つ折りハガキの
表面展開図、図６はこのハガキの裏面展開図、図７は図
５のハガキを折り込む際の状態説明図、図８は部分二つ
折りハガキの表面展開図、図９はこのハガキの裏面展開
図、図１０は図８のハガキを折り込む際の状態説明図で
ある。FIGS. 1 to 10 are explanatory views for explaining an embodiment of the recording sheet of the present invention. Here, FIG. 1 is a front view of a three-fold postcard, FIG. 2 is a rear view of the postcard, FIG. 3 is a cross-sectional view taken along line XX of FIG. 1, and FIG. 4 is a state when the postcard of FIG. Explanatory drawing, FIG. 5 is a front development view of the two-fold postcard, FIG. 6 is a rear development view of this postcard, FIG. 7 is a state explanatory view when the postcard of FIG. 5 is folded, and FIG. FIG. 9 is a developed view of the back of the postcard, and FIG. 10 is a state explanatory view when the postcard of FIG. 8 is folded.
【００２７】先ず、図１ないし図３に示す三つ折りハガ
キ１は、定型ハガキサイズの３倍のサイズを有する基体
シート２から構成され、折り線３ａ、３ｂによって３つ
の領域に区画されるものである。左側区画領域Ａの表面
には本発明のインクを用いて隠蔽層３０が形成されてお
り、隠蔽層３０の上に郵便番号、宛て名、住所等の宛て
先情報印刷４がインクジェットインクを用いて印刷さ
れ、また中央区画領域Ｂの表裏面及び右側区画領域Ｃの
表面には隠蔽情報印刷５が、基体シート２に直接印刷さ
れている。さらに、この印刷された基体シート２の区画
領域Ｂ及びＣの表面全体と区画領域Ａ及びＢの裏面全体
に対し、感圧接着剤が塗布されて剥離可能な接着層６が
形成されている。このように構成された三つ折りハガキ
１は、図４に示すように、各区画の重ね合わせ面を折り
線３ａ、３ｂにてＺ型に折り込んで接着層同士を対接さ
せ、この状態でドライシーラーをもって加圧することに
より、その接着層６が活性化されて接着される。First, a three-fold postcard 1 shown in FIGS. 1 to 3 is composed of a base sheet 2 having a size three times the size of a standard postcard, and is divided into three regions by folding lines 3a and 3b. is there. A concealing layer 30 is formed on the surface of the left-side partitioned area A using the ink of the present invention. On the concealing layer 30, a destination information print 4 such as a postal code, a destination name, and an address is formed using inkjet ink. The concealment information print 5 is printed directly on the base sheet 2 on the front and back surfaces of the center section area B and the front face of the right section area C. Further, a pressure-sensitive adhesive is applied to the entire front surfaces of the divided regions B and C and the whole back surfaces of the divided regions A and B of the printed base sheet 2 to form a peelable adhesive layer 6. As shown in FIG. 4, the three-fold postcard 1 configured as described above folds the overlapping surface of each section into a Z shape at folding lines 3a and 3b to bring the adhesive layers into contact with each other. By pressing with a sealer, the adhesive layer 6 is activated and adhered.
【００２８】図１〜４に示す三つ折りハガキ１の場合、
左側区画領域Ａの表面には本発明のインクを用いて隠蔽
層３０が形成されており、この隠蔽層３０の上に郵便番
号、宛て名、住所等の宛て先情報印刷４がインクジェッ
トインクを用いて印刷されている。隠蔽層３０へのイン
クジェットインク吸収性が優れ、印字画像の滲みが起こ
らず、印字したインクジェットインクの耐水性が改善で
き、インクジェット印字の印字品質を向上できる上、白
色度が高く鮮明なカラー印字などもできるとともに、区
画領域Ｂの裏面に印刷した隠蔽情報印刷５が区画領域Ａ
の宛て先情報印刷４を印刷した表面側から透けて見えな
いため情報が漏洩せず親展性に優れている。In the case of the tri-fold postcard 1 shown in FIGS.
A concealing layer 30 is formed on the surface of the left side partitioned area A using the ink of the present invention. On the concealing layer 30, a destination information print 4 such as a postal code, a destination name, and an address is formed using inkjet ink. Printed. The ink-absorbing ink absorbability to the concealing layer 30 is excellent, the bleeding of the printed image does not occur, the water resistance of the printed ink-jet ink can be improved, the printing quality of the ink-jet printing can be improved, and the whiteness is high and clear color printing can be performed. The concealment information print 5 printed on the back surface of the divided area B is
The information is not leaked out from the front side on which the destination information print 4 is printed, so that information is not leaked and the confidentiality is excellent.
【００２９】次に、図５及び図６に示す二つ折りハガキ
１１は、定型ハガキサイズの２倍のサイズを有する基体
シート２から構成され、中央部の折り線３によって２つ
の領域Ｄ及びＥに区画されるものである。左側区画領域
Ｄの表面には本発明のインクを用いて隠蔽層３０が形成
されており、この隠蔽層３０の上に、郵便番号、宛て
名、住所等の宛て先情報印刷４がインクジェットインク
を用いて印刷され、また区画領域Ｄ及びＥの裏面には隠
蔽情報印刷５が、基体シート２に直接印刷されている。
さらに、この印刷された基体シート２の区画領域Ｄ及び
Ｅの裏面全体に対し、感圧接着剤が塗布されて剥離可能
な接着層６が形成されている。このように構成された二
つ折りハガキ１１は、図７に示すように、上記の三つ折
りハガキと同様に、左右区画裏面の接着層同士が対接す
るように折り線３で折り込んで加圧することにより、そ
の接着層６が活性化されて接着される。Next, a two-fold postcard 11 shown in FIGS. 5 and 6 is composed of a base sheet 2 having a size twice as large as a standard postcard size, and is divided into two regions D and E by a folding line 3 at the center. It is what is divided. A concealing layer 30 is formed on the surface of the left side partitioned area D using the ink of the present invention. On the concealing layer 30, a destination information print 4 such as a postal code, a destination name, and an address is printed with an inkjet ink. The concealment information print 5 is printed directly on the base sheet 2 on the back surfaces of the divided areas D and E.
Further, a pressure-sensitive adhesive is applied to the entire back surface of the divided areas D and E of the printed base sheet 2 to form an adhesive layer 6 that can be peeled off. As shown in FIG. 7, the two-fold postcard 11 configured as described above is folded and pressed at the fold line 3 so that the adhesive layers on the right and left rear surfaces are in contact with each other, similarly to the above-described three-fold postcard. The adhesive layer 6 is activated and adhered.
【００３０】図５〜７に示す二つ折りハガキ１１の場合
は、左側区画領域Ｄの表面には本発明のインクを用いて
隠蔽層３０が形成されており、この隠蔽層３０の上に、
郵便番号、宛て名、住所等の宛て先情報印刷４が印刷さ
れている。隠蔽層３０へのインクジェットインク吸収性
が優れ、印字画像の滲みが起こらず、印字したインクジ
ェットインクの耐水性が改善でき、インクジェット印字
の印字品質を向上できる上、白色度が高く鮮明なカラー
印字などもできるとともに、区画領域Ｄの裏面に印刷し
た隠蔽情報印刷５が区画領域Ｄの宛て先情報印刷４を印
刷した表面側から透けて見えないため情報が漏洩せず親
展性に優れる。In the case of the two-fold postcard 11 shown in FIGS. 5 to 7, the concealing layer 30 is formed on the surface of the left-side partitioned area D using the ink of the present invention.
A destination information print 4 such as a postal code, a destination name, and an address is printed. The ink-absorbing ink absorbability to the concealing layer 30 is excellent, the bleeding of the printed image does not occur, the water resistance of the printed ink-jet ink can be improved, the printing quality of the ink-jet printing can be improved, and the whiteness is high and clear color printing can be performed. In addition, since the concealment information print 5 printed on the back surface of the partitioned area D cannot be seen through from the front side of the partitioned area D on which the destination information print 4 is printed, the information does not leak and the confidentiality is excellent.
【００３１】また、図８及び図９に示す部分二つ折りハ
ガキ２１は、定型ハガキサイズの１．５倍のサイズを有
する基体シート２から構成され、折り線３によってサイ
ズの異なる左右２つの領域Ｆ及びＧに区画されるもので
ある。左側区画領域Ｆの表面には本発明のインクを用い
て隠蔽層３０が形成されており、この隠蔽層３０の上
に、郵便番号、宛て名、住所等の宛て先情報印刷４がイ
ンクジェットインクを用いて印刷され、また右側区画領
域Ｇの裏面には隠蔽情報印刷５が、基体シート２に直接
印刷されている。さらにこの印刷された基体シート２の
区画領域Ｇの裏面全体及び区画領域Ｇを折り線３で折り
込んだ際に重ね合わされる区画領域Ｆの一部裏面に対
し、感圧接着剤が塗布されて剥離可能な接着層６が形成
されている。このように構成された部分二つ折りハガキ
２１は、図１０に示すように、上記の二つ折りハガキと
同様に、左右区画裏面の接着層同士が対接するように折
り線３で折り込んで加圧することにより、その接着層６
が活性化されて接着される。8 and 9 is composed of a base sheet 2 having a size 1.5 times the size of a standard postcard. And G. A concealing layer 30 is formed on the surface of the left side partitioned area F using the ink of the present invention. On the concealing layer 30, a destination information print 4 such as a postal code, a destination name, an address, etc. The concealment information print 5 is printed directly on the base sheet 2 on the back surface of the right side divided area G. Further, a pressure-sensitive adhesive is applied to the entire back surface of the divided region G of the printed base sheet 2 and a part of the back surface of the divided region F to be overlapped when the divided region G is folded along the folding line 3 and peeled off. A possible adhesive layer 6 has been formed. As shown in FIG. 10, the partially folded postcard 21 configured in this manner is folded and pressed at the folding line 3 so that the adhesive layers on the back surfaces of the left and right sections are in contact with each other, similarly to the above-described two-fold postcard. The adhesive layer 6
Are activated and adhered.
【００３２】図８〜１０に示す部分二つ折りハガキ２１
の場合は、左側区画領域Ｆの表面には本発明のインクを
用いて隠蔽層３０が形成されており、この隠蔽層３０の
上に、郵便番号、宛て名、住所等の宛て先情報印刷４が
インクジェットインクを用いて印刷されている。隠蔽層
３０へのインクジェットインク吸収性が優れ、印字画像
の滲みが起こらず、印字したインクジェットインクの耐
水性が改善でき、インクジェット印字の印字品質を向上
できる上、白色度が高く鮮明なカラー印字などもできる
とともに、区画領域Ｆの裏面に印刷した隠蔽情報印刷５
が区画領域Ｆの宛て先情報印刷４を印刷した表面側から
透けて見えないため情報が漏洩せず親展性に優れる。The partially folded postcard 21 shown in FIGS.
In the case of (1), a concealing layer 30 is formed on the surface of the left-side partitioned area F using the ink of the present invention, and on the concealing layer 30, a destination information print 4 such as a postal code, a destination name, and an address is formed. Are printed using inkjet ink. The ink-absorbing ink absorbability to the concealing layer 30 is excellent, the bleeding of the printed image does not occur, the water resistance of the printed ink-jet ink can be improved, the printing quality of the ink-jet printing can be improved, and the whiteness is high and clear color printing is performed. Concealment information printing 5 printed on the back of the partitioned area F
Cannot be seen through from the front side of the destination area print 4 on which the destination information print 4 is printed, so that the information does not leak and the confidentiality is excellent.
【００３３】[0033]
【実施例】以下実施例および比較例により本発明を更に
詳しく説明するが、本発明はこれら実施例に何ら制約さ
れるものではない。 （実施例１）プロピレングリコール９４質量部にロジン
変性マレイン酸〈商品名：テスポール１１５４（日立化
成ポリマー社製）〉６質量部を溶解させる。得られたビ
ヒクル液１００質量部に二酸化チタン白色微粒子〈商品
名：二酸化チタンＰ２５（日本エアロジル社製）〉２８
質量部を混練する。これにロール転写性向上剤としてジ
エチレングリコール８質量部とグリセリン４質量部を加
えた。さらに隠蔽性能を向上させるために蛍光増白剤
〈商品名：ＫａｙａｐｈｏｒＢ（日本化薬社製）〉２質
量部を添加し、三本ロールミルを使用して、本発明の隠
蔽層形成用インクを調製した。得られた本発明の隠蔽層
形成用インクを樹脂凸版を使用して上質紙（７０Ｋｇ連
量）上に２ｇ／ｍ2 になるようにオフセット印刷を行っ
て隠蔽層を有する本発明の記録用シートを作った。得ら
れた本発明の記録用シートの隠蔽層の隠蔽性を評価する
とともに白色度を下記の方法により測定した。本発明の
記録用シートの隠蔽層にサイテックス社インクジェット
プリンタで印字（黒、赤、青および緑染料インク）を行
ったあと、下記の評価方法により耐水性およびＳＴＩグ
レード（％）（印字品質）の評価を行った。評価結果を
隠蔽性および白色度とともに表１に示す。The present invention will be described in more detail with reference to the following Examples and Comparative Examples, but the present invention is not limited to these Examples. (Example 1) 6 parts by mass of rosin-modified maleic acid (trade name: Tespol 1154 (manufactured by Hitachi Chemical Co., Ltd.)) is dissolved in 94 parts by mass of propylene glycol. Titanium dioxide white fine particles (trade name: titanium dioxide P25 (manufactured by Nippon Aerosil Co., Ltd.)) are added to 100 parts by mass of the obtained vehicle liquid.
Mix parts by mass. To this, 8 parts by mass of diethylene glycol and 4 parts by mass of glycerin were added as a roll transferability improver. In order to further improve the hiding performance, 2 parts by mass of a fluorescent whitening agent (trade name: Kayaphor B (manufactured by Nippon Kayaku Co., Ltd.)) is added, and the ink for forming the hiding layer of the present invention is prepared using a three-roll mill. did. The obtained ink for forming a concealing layer of the present invention is subjected to offset printing on a high-quality paper (70 kg continuous mass) using a resin relief plate so as to have a concentration of 2 g / m 2, and the recording sheet of the present invention having a concealing layer made. The concealing properties of the concealing layer of the obtained recording sheet of the present invention were evaluated, and the whiteness was measured by the following method. After printing (black, red, blue, and green dye inks) on the concealing layer of the recording sheet of the present invention using an inkjet printer manufactured by Cytex Corporation, water resistance and STI grade (%) (print quality) were evaluated by the following evaluation methods. Was evaluated. The evaluation results are shown in Table 1 together with hiding power and whiteness.
【００３４】（白色度の測定法）分光白色度測色計［Ｓ
Ｃ−１０ＷＮ型（スガ試験機社製）］を用い４００ｎｍ
の反射率を測定し、白色度とする。(Measurement method of whiteness) Spectral whiteness colorimeter [S
C-10WN type (manufactured by Suga Test Instruments Co., Ltd.)]
Is measured and defined as whiteness.
【００３５】（評価方法） 〈隠蔽性〉本発明の記録用シートの隠蔽層を形成した裏
面にデータ印字を行う。この記録用シートを白い台紙の
上にデータ印字面を下にして置く。このデータ印字部を
隠蔽層を形成した側から見た場合、データ印字の内容が
判読不可能なものを◎、データ印字の内容は判読不可能
であるが文字がわずかに見えるものを○、データ印字の
内容が部分的に判読可能であるものを△、データ印字の
内容が完全に判読可能であるものを×と判定した。(Evaluation Method) <Hiding Property> Data printing is performed on the back surface of the recording sheet of the present invention on which the concealing layer is formed. This recording sheet is placed on a white backing paper with the data printing side down. When the data printed portion was viewed from the side on which the concealing layer was formed, ◎ indicates that the content of the data print was unreadable, and O indicates that the content of the data print was unreadable but characters were slightly visible. When the content of the print was partially legible, it was judged as Δ, and when the content of the data print was completely legible, it was judged as x.
【００３６】〈耐水性〉印字箇所を一定時間流水で洗い
流すか、印字箇所に水滴を一定時間滴下したのち、拭き
取ってインクの状態を目視により判定する。印字が完全
に残っているものを◎、印字がほぼ完全に残っているも
のを○、印字が少し薄くなってきているものを△、印字
が薄くなっているものを×と判定した。<Water resistance> The printed area is washed away with running water for a predetermined time, or a water drop is dropped on the printed area for a predetermined time, and then wiped off to visually determine the state of the ink. When the print completely remained, it was judged as ◎, when the print almost completely remained, as ○, when the print became slightly thinner, as Δ, and when the print became thinner, as ×.
【００３７】〈ＳＴＩグレード（％）（印字品質）〉イ
ンクジェットプリンタにてバーコードを印字し、その読
み取り品質をバーコードテスタ（ＬＡＳＥＲ ＣＨＥＫ
ＩＩ）にて、ＳＴＩグレード（％）を測定することに
より評価した。なお、一般的にはＳＴＩグレードで５０
％以上が標準的な良好品質と評価することができる。<STI Grade (%) (Print Quality)> A bar code is printed by an ink jet printer, and the read quality is checked with a bar code tester (LASER CHEK).
In II), evaluation was made by measuring the STI grade (%). In general, STI grade 50
% Or more can be evaluated as standard good quality.
【００３８】（実施例２）実施例１で使用した二酸化チ
タン白色微粒子をアルミナ白色微粒子〈商品名：酸化ア
ルミニウムＣ（日本エアロジル社製）〉に変更した以外
は実施例１と同様にして、本発明の隠蔽層形成用インク
を調製した後、同様にして本発明の記録用シートを作
り、白色度を測定し、隠蔽性、耐水性およびＳＴＩグレ
ード（％）（印字品質）の評価を行った。評価結果を表
１に示す。(Example 2) The procedure of Example 1 was repeated, except that the titanium dioxide white fine particles used in Example 1 were changed to alumina white fine particles (trade name: aluminum oxide C (manufactured by Nippon Aerosil Co., Ltd.)). After preparing the ink for forming a concealing layer of the present invention, a recording sheet of the present invention was prepared in the same manner, the whiteness was measured, and the concealing property, water resistance and STI grade (%) (print quality) were evaluated. . Table 1 shows the evaluation results.
【００３９】（実施例３）実施例１で使用した二酸化チ
タン白色微粒子をシリカ白色微粒子〈商品名：ＮＩＰＳ
ＩＬ Ｅ２００（日本シリカ工業社製）〉に変更し、配
合量を３０質量部にした以外は実施例１と同様にして、
本発明の隠蔽層形成用インクを調製した後、同様にして
本発明の記録用シートを作り、白色度を測定し、隠蔽
性、耐水性およびＳＴＩグレード（％）（印字品質）の
評価を行った。評価結果を表１に示す。Example 3 The titanium dioxide white fine particles used in Example 1 were replaced with silica white fine particles (trade name: NIPS)
ILE200 (manufactured by Nippon Silica Industry Co., Ltd.)> In the same manner as in Example 1 except that the blending amount was changed to 30 parts by mass.
After preparing the ink for forming a concealing layer of the present invention, a recording sheet of the present invention is prepared in the same manner, the whiteness is measured, and the concealing property, water resistance and STI grade (%) (print quality) are evaluated. Was. Table 1 shows the evaluation results.
【００４０】（実施例４）実施例１で使用した蛍光増白
剤を４質量部に変更した以外は実施例１と同様にして、
本発明の隠蔽層形成用インクを調製した後、同様にして
本発明の記録用シートを作り、白色度を測定し、隠蔽
性、耐水性およびＳＴＩグレード（％）（印字品質）の
評価を行った。評価結果を表１に示す。(Example 4) The procedure of Example 1 was repeated, except that the amount of the fluorescent whitening agent used in Example 1 was changed to 4 parts by mass.
After preparing the ink for forming a concealing layer of the present invention, a recording sheet of the present invention is prepared in the same manner, the whiteness is measured, and the concealing property, water resistance and STI grade (%) (print quality) are evaluated. Was. Table 1 shows the evaluation results.
【００４１】（実施例５）実施例１で使用した蛍光増白
剤を０．５質量部に変更した以外は実施例１と同様にし
て、本発明の隠蔽層形成用インクを調製した後、同様に
して本発明の記録用シートを作り、白色度を測定し、隠
蔽性、耐水性およびＳＴＩグレード（％）（印字品質）
の評価を行った。評価結果を表１に示す。Example 5 An ink for forming a concealing layer of the present invention was prepared in the same manner as in Example 1 except that the amount of the fluorescent whitening agent used in Example 1 was changed to 0.5 part by mass. Similarly, the recording sheet of the present invention was prepared, the whiteness was measured, and the opacity, water resistance and STI grade (%) (print quality) were measured.
Was evaluated. Table 1 shows the evaluation results.
【００４２】（実施例６）実施例１で使用した蛍光増白
剤をＫａｙａｐｈｏｒ ＰＡＳ〈商品名：日本化薬社
製）〉に変更した以外は実施例１と同様にして、本発明
の隠蔽層形成用インクを調製した後、同様にして本発明
の記録用シートを作り、白色度を測定し、隠蔽性、耐水
性およびＳＴＩグレード（％）（印字品質）の評価を行
った。評価結果を表１に示す。Example 6 The concealing layer of the present invention was prepared in the same manner as in Example 1 except that the fluorescent brightener used in Example 1 was changed to Kayaphor PAS (trade name: manufactured by Nippon Kayaku Co., Ltd.). After preparing the forming ink, the recording sheet of the present invention was prepared in the same manner, the whiteness was measured, and the opacity, water resistance, and STI grade (%) (print quality) were evaluated. Table 1 shows the evaluation results.
【００４３】（比較例１）隠蔽層を形成しなかった以外
は実施例１と同様にして上質紙の白色度を測定し、隠蔽
性、耐水性およびＳＴＩグレード（％）（印字品質）の
評価を行った。評価結果を表１に示す。Comparative Example 1 The whiteness of woodfree paper was measured in the same manner as in Example 1 except that the concealing layer was not formed, and the opacity, water resistance and STI grade (%) (print quality) were evaluated. Was done. Table 1 shows the evaluation results.
【００４４】（比較例２）実施例１で使用した二酸化チ
タン白色微粒子を用いなかった以外は実施例１と同様に
して、比較のインクを調製した後、同様にして比較の記
録用シートを作り、白色度を測定し、隠蔽性、耐水性お
よびＳＴＩグレード（％）（印字品質）の評価を行っ
た。評価結果を表１に示す。Comparative Example 2 A comparative ink was prepared in the same manner as in Example 1 except that the titanium dioxide fine white particles used in Example 1 were not used, and a comparative recording sheet was similarly produced. , Whiteness was measured, and opacity, water resistance, and STI grade (%) (print quality) were evaluated. Table 1 shows the evaluation results.
【００４５】（比較例３）実施例１で使用した蛍光増白
剤を用いなかった以外は実施例１と同様にして、比較の
インクを調製した後、同様にして比較の記録用シートを
作り、白色度を測定し、隠蔽性、耐水性およびＳＴＩグ
レード（％）（印字品質）の評価を行った。評価結果を
表１に示す。Comparative Example 3 A comparative recording sheet was prepared in the same manner as in Example 1 except that the fluorescent whitening agent used in Example 1 was not used, and a comparative ink was prepared. , Whiteness was measured, and opacity, water resistance, and STI grade (%) (print quality) were evaluated. Table 1 shows the evaluation results.
【００４６】（比較例４）実施例５で使用した二酸化チ
タン白色微粒子を用いなかった以外は実施例５と同様に
して、比較のインクを調製した後、同様にして比較の記
録用シートを作り、白色度を測定し、隠蔽性、耐水性お
よびＳＴＩグレード（％）（印字品質）の評価を行っ
た。評価結果を表１に示す。Comparative Example 4 A comparative recording sheet was prepared in the same manner as in Example 5, except that the titanium dioxide fine white particles used in Example 5 were not used. , Whiteness was measured, and opacity, water resistance, and STI grade (%) (print quality) were evaluated. Table 1 shows the evaluation results.
【００４７】[0047]
【表１】 [Table 1]
【００４８】実施例１〜６の隠蔽層形成用インクは、印
刷インク適性に優れる上、表１から隠蔽性および白色度
が高く、インクジェットプリンタで印字（黒、赤、青お
よび緑染料インク）した印字の耐水性およびＳＴＩグレ
ード（％）（印字品質）に優れていることが判る。それ
に対して、比較例１〜４のインクは隠蔽性、印字の耐水
性およびＳＴＩグレード（％）（印字品質）に劣る。The inks for forming the concealing layer of Examples 1 to 6 are excellent in printing ink suitability and have high concealing properties and whiteness as shown in Table 1, and were printed by an ink jet printer (black, red, blue and green dye inks). It can be seen that the printing is excellent in water resistance and STI grade (%) (print quality). In contrast, the inks of Comparative Examples 1 to 4 are inferior in concealing properties, water resistance of printing, and STI grade (%) (printing quality).
【００４９】[0049]
【発明の効果】本発明の請求項１記載のインクジェット
インク受容性隠蔽層形成用インクは、沸点１００℃以上
のグリコール系溶剤を主成分として含むビヒクルに対し
て、白色微粒子および蛍光物質を配合したインクである
ので、特別な乾燥装置が必要でなくなり、そして隠蔽情
報印刷が先情報印刷を印刷した側から透けて見えないた
め情報が漏洩せず親展性に優れるとともに、基材に形成
された隠蔽層へのインクジェットインク吸収性が優れ、
印字画像の滲みが起こらず、印字したインクジェットイ
ンクの耐水性が改善でき、インクジェット印字の印字品
質を向上できる上、白色度が高く鮮明なカラー印字がで
き、また印刷インク適性に優れるため基材の必要な所定
の箇所に容易に隠蔽層を形成できるのでコストダウンを
計ることができる上、オフセット印刷に影響を与えない
という顕著な効果を奏する。The ink for forming an ink-jet ink receptive concealing layer according to claim 1 of the present invention comprises white fine particles and a fluorescent substance mixed with a vehicle containing a glycol solvent having a boiling point of 100 ° C. or higher as a main component. Since it is ink, a special drying device is not required, and the concealment information printing is not visible from the side on which the previous information printing was printed, so that information is not leaked and excellent in confidentiality, and the concealment formed on the base material Excellent ink-jet ink absorption to the layer,
Bleeding of the printed image does not occur, the water resistance of the printed ink-jet ink can be improved, the printing quality of the ink-jet printing can be improved, the whiteness is high and clear color printing is possible, and the printing ink suitability is excellent. Since the concealing layer can be easily formed at the required predetermined portion, the cost can be reduced, and the remarkable effect of not affecting the offset printing can be obtained.
【００５０】本発明の請求項２記載のインクジェットイ
ンク受容性隠蔽層形成用インクは、請求項１記載の隠蔽
層形成用インクにおいて、沸点１００℃以上のグリコー
ル系溶剤を主成分として含むビヒクル１００質量部に対
して、白色微粒子５〜４０質量部および蛍光物質０．１
〜１０質量部を配合したので、請求項１記載の隠蔽層形
成用インクと同じ効果を奏する上、隠蔽性、耐水性およ
び印刷適性を確実に向上できるという、さらなる顕著な
効果を奏する。The ink for forming an ink-jet ink receptive concealing layer according to the second aspect of the present invention is the ink for forming a concealing layer according to the first aspect, which is a 100-mass vehicle containing a glycol-based solvent having a boiling point of 100 ° C. or higher as a main component. 5 to 40 parts by mass of white fine particles and 0.1
The addition of from 10 to 10 parts by mass provides the same effect as the ink for forming a concealing layer according to claim 1, and also has a further remarkable effect that concealing properties, water resistance and printability can be surely improved.
【００５１】本発明の請求項３の記録用シートは、基材
の少なくとも一方の面の所定部に請求項１あるいは請求
項２記載の隠蔽層形成用インクを用いて形成されたイン
クジェットインク受容性および隠蔽性を併せ持った隠蔽
層を有するので、隠蔽情報印刷が先情報印刷を印刷した
側から透けて見えないため情報が漏洩せず親展性が優れ
るとともに、隠蔽層へのインクジェットインク吸収性が
優れ、印字画像の滲みが起こらず、印字したインクジェ
ットインクの耐水性が改善でき、インクジェット印字の
印字品質を向上できる上、白色度が高く鮮明なカラー印
字ができるという顕著な効果を奏する。According to a third aspect of the present invention, there is provided an ink-jet recording sheet formed by using the ink for forming a concealing layer according to the first or second aspect on a predetermined portion of at least one surface of a substrate. And a concealing layer having both concealing properties, so that concealed information printing is not seen through from the side on which the previous information printing was printed, so that information is not leaked, so that confidentiality is excellent, and ink-jet ink absorption to the concealing layer is excellent. In addition, the bleeding of the printed image does not occur, the water resistance of the printed ink-jet ink can be improved, the printing quality of the ink-jet printing can be improved, and clear color printing with high whiteness can be achieved.
【図１】本発明の三つ折りハガキの表面展開図。FIG. 1 is a surface development view of a three-fold postcard according to the present invention.
【図２】図１のハガキの裏面展開図。FIG. 2 is a developed rear view of the postcard of FIG. 1;
【図３】図１のＸ−Ｘ線断面図。FIG. 3 is a sectional view taken along line XX of FIG. 1;
【図４】図１のハガキを折り込む際の状態説明図。FIG. 4 is an explanatory diagram of a state when the postcard of FIG. 1 is folded.
【図５】本発明の二つ折りハガキの表面展開図。FIG. 5 is a surface development view of the two-fold postcard of the present invention.
【図６】図５のハガキの裏面展開図。FIG. 6 is a developed rear view of the postcard of FIG. 5;
【図７】図５のハガキを折り込む際の状態説明図。FIG. 7 is an explanatory diagram of a state when the postcard of FIG. 5 is folded.
【図８】本発明の部分二つ折りハガキの表面展開図。FIG. 8 is a surface development view of a partially folded postcard according to the present invention.
【図９】図８のハガキの裏面展開図。FIG. 9 is a developed rear view of the postcard of FIG. 8;
【図１０】図８のハガキを折り込む際の状態説明図。FIG. 10 is an explanatory view of the state when the postcard of FIG. 8 is folded.
【図１１】従来の三つ折りハガキの表面展開図。FIG. 11 is a surface development view of a conventional three-fold postcard.
【図１２】図１１のハガキの裏面展開図。FIG. 12 is a developed rear view of the postcard of FIG. 11;
【図１３】図１１のＸ−Ｘ線断面図。FIG. 13 is a sectional view taken along line XX of FIG. 11;
【図１４】図１１のハガキを折り込む際の状態説明図。FIG. 14 is an explanatory view of the state when the postcard of FIG. 11 is folded.
【図１５】従来の二つ折りハガキの表面展開図。FIG. 15 is a surface development view of a conventional two-fold postcard.
【図１６】図１５のハガキの裏面展開図。FIG. 16 is a developed rear view of the postcard of FIG. 15;
【図１７】図１５のハガキを折り込む際の状態説明図。FIG. 17 is an explanatory view of the state when the postcard of FIG. 15 is folded.
【図１８】従来の部分二つ折りハガキの表面展開図。FIG. 18 is a surface development view of a conventional partially folded postcard.
【図１９】図１８のハガキの裏面展開図。FIG. 19 is a developed rear view of the postcard of FIG. 18;
【図２０】図１８のハガキを折り込む際の状態説明図。20 is an explanatory view of the state when the postcard of FIG. 18 is folded.
１ 三つ折りハガキ １１ 二つ折りハガキ ２１ 他の二つ折りハガキ ２、１２、２２ 基体シート ３、３ａ、３ｂ 折り線 ５ 隠蔽情報印刷 ６ 剥離可能な接着層 ３０ 隠蔽層 DESCRIPTION OF SYMBOLS 1 Tri-fold postcard 11 Two-fold postcard 21 Other two-fold postcard 2, 12, 22 Base sheet 3, 3a, 3b Folding line 5 Concealment information printing 6 Peelable adhesive layer 30 Concealment layer
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2C005 WA03 2C056 EA13 FC01 FC06 2H086 BA15 BA31 BA33 BA45 4J038 EA011 HA216 HA286 HA446 HA466 HA556 JA20 JA26 JA57 KA06 KA08 KA20 4J039 BA13 BA16 BA21 BA23 BA26 BA30 BA32 BA35 BC03 BC09 BC10 BC11 BC14 BC15 BC20 BC33 BC52 BC53 BC65 BC74 BE12 EA18 EA28 EA38 EA47 EA48 GA24 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 2C005 WA03 2C056 EA13 FC01 FC06 2H086 BA15 BA31 BA33 BA45 4J038 EA011 HA216 HA286 HA446 HA466 HA556 JA20 JA26 JA57 KA06 KA08 KA20 4J039 BA13 BA16 BA21 BA23 BA26 BA30 BC10 BC10 BC10 BC15 BC20 BC33 BC52 BC53 BC65 BC74 BE12 EA18 EA28 EA38 EA47 EA48 GA24
Claims (3)
主成分として含むビヒクルに対して、白色微粒子および
蛍光物質を配合したことを特徴とするインクジェットイ
ンク受容性隠蔽層形成用インク。1. An ink for forming an ink-jet ink receptive concealing layer, comprising white particles and a fluorescent substance mixed with a vehicle containing a glycol-based solvent having a boiling point of 100 ° C. or higher as a main component.
主成分として含むビヒクル１００質量部に対して、白色
微粒子５〜４０質量部および蛍光物質０．１〜１０質量
部を配合したことを特徴とする請求項１記載の隠蔽層形
成用インク。2. A method according to claim 1, wherein 5 to 40 parts by mass of white fine particles and 0.1 to 10 parts by mass of a fluorescent substance are blended with 100 parts by mass of a vehicle containing a glycol solvent having a boiling point of 100 ° C. or higher as a main component. The ink for forming a concealing layer according to claim 1.
求項１あるいは請求項２記載の隠蔽層形成用インクを用
いて形成されたインクジェットインク受容性および隠蔽
性を併せ持った隠蔽層を有してなる記録用シート。3. A concealing layer having both ink jet ink receptivity and concealing property formed by using the concealing layer forming ink according to claim 1 or 2 on a predetermined portion of at least one surface of the substrate. A recording sheet made of