JP2002341141A - Adhesion type optical film and liquid crystal display device - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide an adhesion type optical film with excellent heat resistance and stress relaxation, i.e., an adhesion type optical film generating no display unevenness on a liquid crystal display device and generating no defect such as foaming or the like in an adhesive layer in the case it is left under a heating condition. SOLUTION: In the adhesion type optical film comprising an adhesive layer laminated on a surface of an optical film, the adhesion type optical film is characterized by having the adhesive layer formed of a body of an acrylic polymer with a carboxylic group cross-linked with a polyfunctional metal chelate and by having the acrylic polymer with 600,000-2,000,000 weight-average molecular weight (Mw) and >=4 (Mw/Mn) ratio of the weight-average molecular weight to a number average molecular weight (Mn).

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、光学フィルムの一
方の面に粘着層が積層されている粘着型光学フィルムに
関する。前記光学フィルムとしては、偏光フィルム、位
相差フィルム、光学補償フィルム、輝度向上フィルム、
防眩シートまたはこれらが複数積層されているものがあ
げられ、前記粘着型光学フィルムは液晶表示装置の液晶
セル等に適用される。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an adhesive type optical film in which an adhesive layer is laminated on one side of an optical film. As the optical film, a polarizing film, a retardation film, an optical compensation film, a brightness enhancement film,
An anti-glare sheet or a sheet in which a plurality of these sheets are laminated is mentioned, and the adhesive optical film is applied to a liquid crystal cell of a liquid crystal display device or the like.

【０００２】[0002]

【従来の技術】液晶ディスプレイは、その画像形成方式
から液晶パネルの最表面を形成するガラス基板の両側に
偏光素子を配置することが必要不可欠であり、一般的に
は偏光フィルムが液晶パネルの最表面に貼着されてい
る。また液晶パネルの最表面には偏光フィルムの他に、
ディスプレイの表示品位を向上させるために様々な光学
素子が用いられるようになってきている。例えば、着色
防止としての位相差フィルム、液晶ディスプレイの視野
角を改善するための視野角拡大フィルム、さらにはディ
スプレイのコントラストを高めるための輝度向上フィル
ム等が用いられる。これらのフィルムは総称して光学フ
ィルムと呼ばれる。2. Description of the Related Art In a liquid crystal display, it is indispensable to arrange polarizing elements on both sides of a glass substrate forming the outermost surface of a liquid crystal panel in view of an image forming method. Affixed to the surface. In addition to the polarizing film on the outermost surface of the liquid crystal panel,
Various optical elements have been used to improve the display quality of a display. For example, a retardation film for preventing coloration, a viewing angle widening film for improving the viewing angle of a liquid crystal display, and a brightness enhancement film for increasing the contrast of the display are used. These films are collectively called optical films.

【０００３】前記光学フィルムを液晶パネルの最表面に
貼着する際には、通常、粘着剤が使用される。また、光
学フィルムを液晶パネルの最表面に瞬時に固定できるこ
と、光学フィルムを固着させるのに乾燥工程を必要とし
ないこと等のメリットを有することから、粘着剤は、光
学フィルムの片面に予め粘着層として設けられている。
すなわち、液晶パネルの最表面への光学フィルムの貼着
には粘着型光学フィルムが一般的に用いられる。When the optical film is attached to the outermost surface of a liquid crystal panel, an adhesive is usually used. In addition, since the optical film can be instantly fixed to the outermost surface of the liquid crystal panel and does not require a drying step for fixing the optical film, the adhesive is provided with an adhesive layer on one side of the optical film in advance. It is provided as.
That is, an adhesive optical film is generally used for attaching the optical film to the outermost surface of the liquid crystal panel.

【０００４】前記粘着型光学フィルムは液晶パネルメー
カーにおいて液晶表示装置に装着されるが、その際に粘
着型光学フィルムは各工程で加熱条件下におかれる。し
かし、光学フィルムはその材料特性から寸法安定性に乏
しく、特に加熱条件下では収縮による寸法変化が大き
い。光学フィルムに寸法変化が生じると、粘着剤による
応力緩和性が低い場合、光学フィルムに応力ムラが発生
し、その結果、表示ムラが生じ視認性を低下させるとい
う問題があった。The adhesive optical film is mounted on a liquid crystal display device by a liquid crystal panel maker. At that time, the adhesive optical film is subjected to heating conditions in each step. However, optical films have poor dimensional stability due to their material properties, and particularly under heating conditions, dimensional changes due to shrinkage are large. When the dimensional change occurs in the optical film, when the stress relaxation property of the pressure-sensitive adhesive is low, stress unevenness occurs in the optical film, and as a result, display unevenness occurs and visibility deteriorates.

【０００５】前記表示ムラを防止すべく、従来の粘着剤
では引張り弾性率を低下させた比較的柔らかい粘着剤組
成を用いて応力を緩和させることにより上記の問題を解
決してきた。柔らかい粘着剤組成とする方法の１つの方
法として、たとえば架橋度を低下、すなわち架橋点を減
少させる方法がある。しかし、架橋点を減少させると、
それとともに一般的に低分子量ポリマーの含有量が増加
する。低分子量ポリマーが多くなると凝集力が不十分と
なるため粘着層において発泡、剥がれ等の不具合を生じ
易くなるという問題があった。In order to prevent the display unevenness, the above-mentioned problem has been solved by using a relatively soft pressure-sensitive adhesive composition having a reduced tensile modulus in the conventional pressure-sensitive adhesive to relieve stress. As one method of preparing a soft pressure-sensitive adhesive composition, for example, there is a method of reducing the degree of crosslinking, that is, a method of reducing the number of crosslinking points. However, when the crosslinking point is reduced,
Along with this, the content of low molecular weight polymers generally increases. When the amount of the low molecular weight polymer is increased, the cohesive force becomes insufficient, so that a problem such as foaming or peeling in the adhesive layer is apt to occur.

【０００６】[0006]

【発明が解決しようとする課題】このように光学フィル
ムに用いる粘着剤では、加熱条件下における耐久性と応
力緩和性を両立させることが困難であった。そこで本発
明は、加熱耐久性と応力緩和性の良好な粘着型光学フィ
ルム、すなわち加熱条件下におかれた場合にも、液晶表
示装置に表示ムラが生じず、粘着層に発泡等の不具合が
生じない粘着型光学フィルムを提供することを目的とす
る。As described above, it has been difficult for the pressure-sensitive adhesive used for the optical film to achieve both durability and stress relaxation under heating conditions. Therefore, the present invention provides a pressure-sensitive adhesive optical film having good heat durability and stress relaxation properties, that is, even when placed under heating conditions, display unevenness does not occur in the liquid crystal display device, and the pressure-sensitive adhesive layer has problems such as foaming. An object of the present invention is to provide a pressure-sensitive adhesive optical film that does not occur.

【０００７】[0007]

【課題を解決するための手段】本発明者らは、前記課題
を解決すべく、鋭意研究したところ、以下に示す粘着型
光学フィルムにより上記目的を達成できることを見出
し、本発明を完成するに至った。Means for Solving the Problems The present inventors have conducted intensive studies in order to solve the above-mentioned problems. As a result, they have found that the above object can be achieved by the following adhesive optical film, and have completed the present invention. Was.

【０００８】すなわち本発明は、光学フィルムの一方の
面に粘着層が積層されている粘着型光学フィルムにおい
て、前記粘着層が、カルボキシル基を有するアクリル系
ポリマーの多官能性金属キレートによる架橋物により形
成されており、かつ前記アクリル系ポリマーが重量平均
分子量（Ｍｗ）６０万〜２００万、重量平均分子量と数
平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）が４以上を有
するものであることを特徴とする粘着型光学フィルム、
に関する。That is, the present invention provides a pressure-sensitive adhesive optical film in which a pressure-sensitive adhesive layer is laminated on one surface of an optical film, wherein the pressure-sensitive adhesive layer comprises a cross-linked product of an acrylic polymer having a carboxyl group with a polyfunctional metal chelate. Being formed, and the acrylic polymer has a weight average molecular weight (Mw) of 600,000 to 2,000,000 and a ratio (Mw / Mn) of the weight average molecular weight to the number average molecular weight (Mn) of 4 or more. Adhesive optical film,
About.

【０００９】本発明の粘着型光学フィルムにおいて、粘
着層を形成するベースポリマーであるアクリル系ポリマ
ーは、重量平均分子量（Ｍｗ）６０万〜２００万を有
し、かつ重量平均分子量と数平均分子量（Ｍｎ）との比
（Ｍｗ／Ｍｎ）が４以上であり、分子量分布が比較的広
く、低い引張り弾性率を有するものである。この低い引
張り弾性率により良好な応力緩和性が奏され、表示ムラ
を有効に防止する。かかる観点より前記比（Ｍｗ／Ｍ
ｎ）は、さらに４．５以上であるのが好適である。一
方、前記比（Ｍｗ／Ｍｎ）が大きくなりすぎると、低分
子量ポリマーが増加し、発泡が生じやすくなるため前記
比（Ｍｗ／Ｍｎ）は２５以下、さらには２０以下である
のが好適である。また、重量平均分子量（Ｍｗ）は９０
万〜１８０万であるのが好適である。In the pressure-sensitive adhesive optical film of the present invention, the acrylic polymer as the base polymer forming the pressure-sensitive adhesive layer has a weight average molecular weight (Mw) of 600,000 to 2,000,000, and has a weight average molecular weight and a number average molecular weight (Mw). Mn) (Mw / Mn) is 4 or more, the molecular weight distribution is relatively wide, and the tensile modulus is low. Due to this low tensile modulus, good stress relaxation is exhibited, and display unevenness is effectively prevented. From this viewpoint, the ratio (Mw / M
n) is preferably 4.5 or more. On the other hand, if the ratio (Mw / Mn) is too large, the amount of the low-molecular-weight polymer increases, and foaming is likely to occur. . The weight average molecular weight (Mw) is 90
It is preferably between 10,000 and 1.8 million.

【００１０】また前記粘着層においてアクリル系ポリマ
ーを架橋している多官能性金属キレートは、高架橋度の
粘着層を形成することができ、アクリル系ポリマーが前
記比（Ｍｗ／Ｍｎ）４以上の、低い引張り弾性率を有す
るものであっても低分子量ポリマー量の少ない粘着層を
形成する。多官能性金属キレートは、架橋に関与する官
能基が４〜６官能とすることもでき、通常の多官能性化
合物（たとえば、イソシアネート系架橋剤、エポキシ系
架橋剤）の官能基が２〜３官能であるのに比べ官能基数
が多いことによる。しかも多官能性金属キレートは、架
橋機能を有するとともに、ガラスとの化学結合を生じる
ことができ、ガラスとある程度の接着性が得られるた
め、前記粘着層と液晶パネル最表面のガラスとの界面の
端部での発泡、剥がれが抑えられ良好な加熱耐久性を示
す。このように本発明の粘着型光学フィルムは応力緩和
性および耐久性の両特性に優れた粘着層を形成してい
る。The polyfunctional metal chelate in which the acrylic polymer is cross-linked in the pressure-sensitive adhesive layer can form a pressure-sensitive adhesive layer having a high degree of cross-linking, and the acrylic polymer has a ratio (Mw / Mn) of 4 or more, An adhesive layer having a low amount of low molecular weight polymer is formed even if it has a low tensile modulus. In the polyfunctional metal chelate, the functional groups involved in crosslinking may be 4 to 6 functional groups, and the functional groups of ordinary polyfunctional compounds (for example, isocyanate-based crosslinking agents and epoxy-based crosslinking agents) may have 2 to 3 functional groups. This is because the number of functional groups is larger than that of functional groups. Moreover, the polyfunctional metal chelate has a cross-linking function and can form a chemical bond with the glass, and a certain degree of adhesiveness with the glass is obtained, so that the interface between the adhesive layer and the glass on the outermost surface of the liquid crystal panel is formed. Foaming and peeling at the end are suppressed and good heat durability is exhibited. As described above, the pressure-sensitive adhesive optical film of the present invention forms a pressure-sensitive adhesive layer having both excellent properties of stress relaxation and durability.

【００１１】なお、アクリル系ポリマーの前記比（Ｍｗ
／Ｍｎ）が４より小さい場合、または重量平均分子量
（Ｍｗ）が２００万を超える場合には、アクリル系ポリ
マーの柔軟性が低下し、粘着層が収縮応力を十分に緩和
することができなくなり、表示ムラが生じる。重量平均
分子量が６０万未満では、低分子量ポリマーが多く、粘
着層中の低分子量ポリマーの増加により凝集力が不十分
となり加熱条件下で発泡等の不具合を生じる。一方、ア
クリル系ポリマーの前記比（Ｍｗ／Ｍｎ）が４以上であ
っても、前記例示の通常の多官能性化合物を用いた場合
には、架橋が不十分であり粘着層中の低分子量ポリマー
の増加により凝集力が不十分となり加熱条件下で発泡等
の不具合を生じる。The ratio (Mw) of the acrylic polymer
/ Mn) is less than 4, or when the weight average molecular weight (Mw) exceeds 2,000,000, the flexibility of the acrylic polymer is reduced, and the pressure-sensitive adhesive layer cannot sufficiently reduce the shrinkage stress, Display unevenness occurs. If the weight average molecular weight is less than 600,000, the amount of the low molecular weight polymer is large, and the cohesive force becomes insufficient due to the increase of the low molecular weight polymer in the pressure-sensitive adhesive layer. On the other hand, even when the ratio (Mw / Mn) of the acrylic polymer is 4 or more, when the ordinary polyfunctional compound exemplified above is used, the crosslinking is insufficient and the low molecular weight polymer in the adhesive layer is insufficient. Increases, the cohesive force becomes insufficient, causing problems such as foaming under heating conditions.

【００１２】前記粘着型光学フィルムにおいて、多官能
性金属キレートが、多官能性アルミニウムキレートであ
ることが好ましい。特に、多官能性金属キレートが、ア
ルミニウムトリスアセチルアセトネートであることが好
ましい。かかる多官能性金属キレートは高い架橋構造を
形成し、また耐久性のうえでも好ましい。In the pressure-sensitive adhesive optical film, it is preferable that the polyfunctional metal chelate is a polyfunctional aluminum chelate. In particular, it is preferred that the polyfunctional metal chelate is aluminum trisacetylacetonate. Such a polyfunctional metal chelate forms a highly crosslinked structure and is preferable in terms of durability.

【００１３】さらに本発明は、前記粘着型光学フィルム
を用いた液晶表示装置、に関する。本発明の粘着型光学
フィルムは、液晶パネル最表面のガラス基板に貼り合わ
せて用いられる。Further, the present invention relates to a liquid crystal display device using the above-mentioned adhesive optical film. The pressure-sensitive adhesive optical film of the present invention is used by being bonded to a glass substrate on the outermost surface of a liquid crystal panel.

【００１４】[0014]

【発明の実施の形態】本発明の粘着型光学フィルムの粘
着層を形成する粘着剤は、カルボキシル基を有するアク
リル系ポリマーをベースポリマーとする。カルボキシル
基を有するアクリル系ポリマーは、アルキル（メタ）ア
クリレートを主モノマーとし、これにカルボキシル基含
有のモノマーを共重合させることにより得られる。ま
た、アクリル系ポリマー中の官能基を利用した高分子反
応によって、アクリル系ポリマー中にカルボキシル基を
導入することもできる。なお、（メタ）アクリレートは
アクリレートおよび／またはメタクリレートをいい、本
発明の（メタ）とは同様の意味である。BEST MODE FOR CARRYING OUT THE INVENTION The pressure-sensitive adhesive for forming the pressure-sensitive adhesive layer of the pressure-sensitive adhesive optical film of the present invention uses an acrylic polymer having a carboxyl group as a base polymer. The acrylic polymer having a carboxyl group can be obtained by copolymerizing an alkyl (meth) acrylate as a main monomer with a carboxyl group-containing monomer. In addition, a carboxyl group can be introduced into the acrylic polymer by a polymer reaction using a functional group in the acrylic polymer. In addition, (meth) acrylate means acrylate and / or methacrylate, and has the same meaning as (meth) in the present invention.

【００１５】アクリル系ポリマーの主骨格を構成する、
アルキル（メタ）アクリレートのアルキル基の平均炭素
数は１〜１２程度のものであり、アルキル（メタ）アク
リレートの具体例としては、メチル（メタ）アクリレー
ト、エチル（メタ）アクリレート、ブチル（メタ）アク
リレート、２−エチルヘキシル（メタ）アクリレート等
を例示でき、これらは単独または組合せて使用できる。Constituting the main skeleton of the acrylic polymer,
The average number of carbon atoms in the alkyl group of the alkyl (meth) acrylate is about 1 to 12. Specific examples of the alkyl (meth) acrylate include methyl (meth) acrylate, ethyl (meth) acrylate, and butyl (meth) acrylate. , 2-ethylhexyl (meth) acrylate and the like, which can be used alone or in combination.

【００１６】カルボキシル基を有するモノマーとしては
アクリル酸、メタクリル酸、フマル酸、マレイン酸、イ
タコン酸等があげられる。Examples of the monomer having a carboxyl group include acrylic acid, methacrylic acid, fumaric acid, maleic acid and itaconic acid.

【００１７】その他、アクリル系ポリマーには、粘着剤
の性能を損なわない範囲で、２−ヒドロキシエチル（メ
タ）アクリレート、Ｎ−メチロール（メタ）アクリルア
ミド等の水酸基含有モノマー、グリシジル（メタ）アク
リレート等のエポキシ基を含有モノマー等の官能基を有
するモノマー、さらには酢酸ビニル、スチレン等を用い
ることもできる。Other acrylic polymers include hydroxyl-containing monomers such as 2-hydroxyethyl (meth) acrylate and N-methylol (meth) acrylamide and glycidyl (meth) acrylate as long as the performance of the pressure-sensitive adhesive is not impaired. Monomers having a functional group such as a monomer containing an epoxy group, and vinyl acetate, styrene and the like can also be used.

【００１８】アクリル系ポリマー中の前記カルボキシル
基を有するモノマーユニット（ａ）の割合は特に制限さ
れないが、アクリル系ポリマーを構成するモノマーユニ
ット（Ａ）（但し、前記モノマーユニット（ａ）を除
く）との重量比（ａ／Ａ）で、０．００１〜０．１２程
度となるように調整するのが、耐久性の点で好ましい。
特に、０．００５〜０．０８とするのが好ましい。The ratio of the monomer unit (a) having a carboxyl group in the acrylic polymer is not particularly limited, but is not limited to the monomer unit (A) (excluding the monomer unit (a)) constituting the acrylic polymer. It is preferable from the viewpoint of durability that the weight ratio (a / A) is adjusted to be about 0.001 to 0.12.
In particular, it is preferably 0.005 to 0.08.

【００１９】前述の通りアクリル系ポリマーの重量平均
分子量（Ｍｗ）は６０万〜２００万、重量平均分子量と
数平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）は４以上で
あるが、その製造方法は特に制限されず、各種公知の方
法により反応条件を適宜に調整して行うことができる。
重合方法としては、たとえば、バルク重合法、溶液重合
法、懸濁重合法等のラジカル重合法を適宜に選択でき
る。ラジカル重合開始剤としては、アゾ系、過酸化物系
の各種公知のものを使用でき、反応温度は通常５０〜８
５℃程度、反応時間は１〜８時間程度とされる。反応温
度、反応時間は、得られるアクリル系ポリマーが前記分
子量になるように適宜に調整する。前記製造法のなかで
も溶液重合法が好ましく、アクリル系ポリマーの溶媒と
しては一般に酢酸エチル、トルエン等の極性溶剤が用い
られる。溶液濃度は通常２０〜８０重量％程度とされ
る。As described above, the acrylic polymer has a weight average molecular weight (Mw) of 600,000 to 2,000,000 and a ratio (Mw / Mn) of the weight average molecular weight to the number average molecular weight (Mn) of 4 or more. The method is not particularly limited, and the reaction can be performed by appropriately adjusting the reaction conditions by various known methods.
As the polymerization method, for example, a radical polymerization method such as a bulk polymerization method, a solution polymerization method, and a suspension polymerization method can be appropriately selected. As the radical polymerization initiator, various known azo-based and peroxide-based ones can be used, and the reaction temperature is usually 50 to 8
The reaction time is about 5 ° C. and the reaction time is about 1 to 8 hours. The reaction temperature and reaction time are appropriately adjusted so that the obtained acrylic polymer has the above-mentioned molecular weight. Among the above production methods, a solution polymerization method is preferable, and a polar solvent such as ethyl acetate or toluene is generally used as a solvent for the acrylic polymer. The solution concentration is usually about 20 to 80% by weight.

【００２０】多官能性金属キレートは、多価金属が有機
化合物と共有結合または配位結合しているものである。
多価金属原子としては、Ａｌ、Ｚｒ、Ｃｏ、Ｃｕ、Ｆ
ｅ、Ｎｉ、Ｖ、Ｚｎ、Ｉｎ、Ｃａ、Ｍｇ、Ｍｎ、Ｙ、Ｃ
ｅ、Ｓｒ、Ｂａ、Ｍｏ、Ｌａ、Ｓｎ、Ｔｉ等があげられ
る。これらのなかでも、Ａｌ、Ｚｒ、Ｔｉが好ましい。
特にＡｌが着色がなく透明性がよい点で好ましい。ま
た、共有結合または配位結合する有機化合物中の原子と
しては酸素原子等があげられ、有機化合物としてはアル
キルエステル、アルコール化合物、カルボン酸化合物、
エーテル化合物、ケトン化合物等があげられる。特に、
安定で取り扱いが容易なアルミニウムトリスアセチルア
セトネートなどが好適に用いられる。これら多官能性金
属キレートは、粘着層において、アクリル系ポリマーと
架橋している。The polyfunctional metal chelate is a polyvalent metal having a covalent bond or a coordination bond with an organic compound.
As the polyvalent metal atoms, Al, Zr, Co, Cu, F
e, Ni, V, Zn, In, Ca, Mg, Mn, Y, C
e, Sr, Ba, Mo, La, Sn, Ti and the like. Of these, Al, Zr, and Ti are preferred.
In particular, Al is preferable because it is free from coloring and has good transparency. Examples of atoms in the organic compound to be covalently bonded or coordinated include an oxygen atom and the like. Examples of the organic compound include an alkyl ester, an alcohol compound, a carboxylic acid compound,
Examples include ether compounds and ketone compounds. In particular,
Aluminum trisacetylacetonate, which is stable and easy to handle, is preferably used. These polyfunctional metal chelates are crosslinked with the acrylic polymer in the adhesive layer.

【００２１】アクリル系ポリマーと多官能性金属キレー
トの配合割合は特に制限されないが、多官能性金属キレ
ートの使用が多くなると、過剰に含まれる多官能性金属
キレートにより、架橋が進みすぎ耐久性で不具合が生じ
るおそれがあるため、アクリル系ポリマー (固形分）１
００重量部に対して、多官能性金属キレート（固形分）
は２重量部程度以下、さらには１．５重量部程度以下と
するのが好適である。一方、粘着層を十分な架橋度とす
るには、多官能性金属キレート（固形分）の前記配合割
合は０．０５重量部程度以上、さらには０．２重量部程
度以上とするのが好適である。The blending ratio of the acrylic polymer and the polyfunctional metal chelate is not particularly limited. However, if the use of the polyfunctional metal chelate increases, the excessively contained polyfunctional metal chelate causes excessive cross-linking, leading to poor durability. Acrylic polymer (solid content) 1
Polyfunctional metal chelate (solid content) based on 00 parts by weight
Is preferably about 2 parts by weight or less, more preferably about 1.5 parts by weight or less. On the other hand, in order for the adhesive layer to have a sufficient degree of crosslinking, the blending ratio of the polyfunctional metal chelate (solid content) is preferably about 0.05 parts by weight or more, and more preferably about 0.2 parts by weight or more. It is.

【００２２】さらには、前記粘着剤組成物には、必要に
応じて、粘着付与剤、可塑剤、充填剤、酸化防止剤、紫
外線吸収剤等を、また本発明の目的を逸脱しない範囲で
各種の添加剤、架橋剤を適宜に使用することもできる。The pressure-sensitive adhesive composition may further contain, if necessary, a tackifier, a plasticizer, a filler, an antioxidant, an ultraviolet absorber, and the like, and a variety of additives within a range not departing from the object of the present invention. Can be used as appropriate.

【００２３】本発明の粘着型光学フィルムは、図１に示
すように、光学フィルム１に前記粘着剤組成物による粘
着層２が設けられている。また、前記粘着層２には離型
シート３を設けることができる。In the pressure-sensitive adhesive optical film of the present invention, as shown in FIG. 1, a pressure-sensitive adhesive layer 2 made of the pressure-sensitive adhesive composition is provided on an optical film 1. Further, a release sheet 3 can be provided on the adhesive layer 2.

【００２４】光学フィルム１としては液晶表示装置等の
形成に用いられるものが使用され、その種類は特に制限
されない。たとえば、光学フィルムとしては偏光フィル
ム、の他に楕円偏光フィルム、光学補償機能を有する偏
光フィルム、視角拡大機能を有する偏光フィルム、輝度
向上機能を有する偏光フィルムなどが挙げられる。これ
らは偏光フィルムに位相差フィルム、光学補償フィル
ム、輝度向上フィルムまたは防眩シート等が積層されて
いる。As the optical film 1, a film used for forming a liquid crystal display device or the like is used, and its type is not particularly limited. For example, examples of the optical film include a polarizing film, an elliptically polarizing film, a polarizing film having an optical compensation function, a polarizing film having a viewing angle expanding function, a polarizing film having a brightness improving function, and the like. In these, a retardation film, an optical compensation film, a brightness enhancement film, an antiglare sheet, and the like are laminated on a polarizing film.

【００２５】偏光フィルムを構成する偏光子としては、
特に制限されず、各種のものを使用できる。偏光子とし
ては、たとえば、ポリビニルアルコール系フィルムや部
分ホルマール化ポリビニルアルコール系フィルム、エチ
レン・酢酸ビニル共重合体系部分ケン化フィルムの如き
親水性高分子フィルムにヨウ素や二色性染料等の二色性
物質を吸着させて延伸したもの、ポリビニルアルコール
の脱水処理物やポリ塩化ビニルの脱塩酸処理物の如きポ
リエン系配向フィルム等があげられる。偏光子の厚さも
特に制限されないが、５〜８０μｍ程度が一般的であ
る。As the polarizer constituting the polarizing film,
There is no particular limitation, and various types can be used. Examples of the polarizer include dichroic dyes such as iodine and dichroic dyes on hydrophilic polymer films such as polyvinyl alcohol-based films, partially formalized polyvinyl alcohol-based films, and ethylene / vinyl acetate copolymer-based partially saponified films. Examples thereof include a film obtained by adsorbing a substance and stretched, and a polyene-based oriented film such as a dehydrated product of polyvinyl alcohol and a dehydrochlorinated product of polyvinyl chloride. Although the thickness of the polarizer is not particularly limited, it is generally about 5 to 80 μm.

【００２６】前記偏光子の片面または両面には、透明保
護層を耐水性等の目的で、ポリマーによる塗布層とし
て、またはフィルムのラミネート層等として設ることが
できる。透明保護層を形成する、透明ポリマーまたはフ
ィルム材料としては、適宜な透明材料を用いうるが、透
明性や機械的強度、熱安定性や水分遮断性などに優れる
ものが好ましく用いられる。透明保護層の厚さは特に制
限されないが、１０〜３００μｍ程度が一般的である。On one or both surfaces of the polarizer, a transparent protective layer may be provided as a coating layer of a polymer or a laminate layer of a film for the purpose of water resistance or the like. As the transparent polymer or film material for forming the transparent protective layer, an appropriate transparent material can be used, but a material having excellent transparency, mechanical strength, heat stability, moisture barrier property and the like is preferably used. Although the thickness of the transparent protective layer is not particularly limited, it is generally about 10 to 300 μm.

【００２７】前記透明保護層を形成する材料としては、
例えばポリエチレンテレフタレートやポリエチレンナフ
タレート等のポリエステル系ポリマー、二酢酸セルロー
スや三酢酸セルロース等のセルロース系ポリマー、ポリ
メチルメタクリレート等のアクリル系ポリマー、ポリス
チレンやアクリロニトリル・スチレン共重合体（ＡＳ樹
脂）等のスチレン系ポリマー、ポリカーボネート系ポリ
マーなどがあげられる。また、ポリエチレン、ポリプロ
ピレン、シクロ系ないしはノルボルネン構造を有するポ
リオレフィン、エチレン・プロピレン共重合体の如きポ
リオレフィン系ポリマー、塩化ビニル系ポリマー、ナイ
ロンや芳香族ポリアミド等のアミド系ポリマー、イミド
系ポリマー、スルホン系ポリマー、ポリエーテルスルホ
ン系ポリマー、ポリエーテルエーテルケトン系ポリマ
ー、ポリフェニレンスルフィド系ポリマー、ビニルアル
コール系ポリマー、塩化ビニリデン系ポリマー、ビニル
ブチラール系ポリマー、アリレート系ポリマー、ポリオ
キシメチレン系ポリマー、エポキシ系ポリマー、あるい
は前記ポリマーのブレンド物なども前記透明保護層を形
成するポリマーの例としてあげられる。Materials for forming the transparent protective layer include:
For example, polyester polymers such as polyethylene terephthalate and polyethylene naphthalate, cellulosic polymers such as cellulose diacetate and cellulose triacetate, acrylic polymers such as polymethyl methacrylate, and styrene such as polystyrene and acrylonitrile-styrene copolymer (AS resin) Polymers, polycarbonate polymers and the like. In addition, polyethylene, polypropylene, polyolefin having a cyclo- or norbornene structure, polyolefin polymers such as ethylene-propylene copolymer, vinyl chloride polymers, amide polymers such as nylon and aromatic polyamide, imide polymers, and sulfone polymers , Polyether sulfone polymer, polyether ether ketone polymer, polyphenylene sulfide polymer, vinyl alcohol polymer, vinylidene chloride polymer, vinyl butyral polymer, arylate polymer, polyoxymethylene polymer, epoxy polymer, or the above Blends of polymers and the like are also examples of the polymer forming the transparent protective layer.

【００２８】位相差フィルムとしては、高分子素材を一
軸または二軸延伸処理してなる複屈折性フィルムや液晶
ポリマーフィルムなどがあげられる。位相差フィルムの
厚さも特に制限されないが、２０〜１５０μｍ程度が一
般的である。位相差板は、二層以上の延伸フィルムの重
畳体などとして形成して位相差等の光学特性を制御した
ものとして形成することもでき、着色防止や視角範囲の
拡大等を目的に液晶セルの位相差を補償するためなどに
偏光フィルムと積層してなる楕円偏光フィルムとして用
いることもできる。Examples of the retardation film include a birefringent film and a liquid crystal polymer film obtained by uniaxially or biaxially stretching a polymer material. Although the thickness of the retardation film is not particularly limited, it is generally about 20 to 150 μm. The retardation plate can be formed as a superimposed body of two or more stretched films to control the optical properties such as retardation, etc. It can also be used as an elliptically polarizing film laminated with a polarizing film to compensate for a phase difference or the like.

【００２９】高分子素材としては、たとえば、ポリビニ
ルアルコール、ポリビニルブチラール、ポリメチルビニ
ルエーテル、ポリヒドロキシエチルアクリレート、ヒド
ロキシエチルセルロース、ヒドロキシプロピルセルロー
ス、メチルセルロース、ポリカーボネート、ポリアリレ
ート、ポリスルホン、ポリエチレンテレフタレート、ポ
リエチレンナフタレート、ポリエーテルスルホン、ポリ
フェニレンスルファイド、ポリフェニレンオキサイド、
ポリアリルスルホン、ポリビニルアルコール、ポリアミ
ド、ポリイミド、ポリオレフィン、ポリ塩化ビニル、セ
ルロース系重合体、またはこれらの二元系、三元系各種
共重合体、グラフト共重合体、ブレンド物などがあげら
れる。これら高分子素材は延伸等により配向物（延伸フ
ィルム）となる。Examples of the polymer material include polyvinyl alcohol, polyvinyl butyral, polymethyl vinyl ether, polyhydroxyethyl acrylate, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl cellulose, polycarbonate, polyarylate, polysulfone, polyethylene terephthalate, polyethylene naphthalate, and polyethylene naphthalate. Ether sulfone, polyphenylene sulfide, polyphenylene oxide,
Examples include polyallyl sulfone, polyvinyl alcohol, polyamide, polyimide, polyolefin, polyvinyl chloride, cellulose polymers, and various binary and ternary copolymers, graft copolymers, and blends thereof. These polymer materials become oriented products (stretched films) by stretching or the like.

【００３０】液晶性ポリマーとしては、たとえば、液晶
配向性を付与する共役性の直線状原子団（メソゲン）が
ポリマーの主鎖や側鎖に導入された主鎖型や側鎖型の各
種のものなどがあげられる。主鎖型の液晶性ポリマーの
具体例としては、屈曲性を付与するスペーサ部でメソゲ
ン基を結合した構造の、例えばネマチック配向性のポリ
エステル系液晶性ポリマー、ディスコティックポリマー
やコレステリックポリマーなどがあげられる。側鎖型の
液晶性ポリマーの具体例としては、ポリシロキサン、ポ
リアクリレート、ポリメタクリレート又はポリマロネー
トを主鎖骨格とし、側鎖として共役性の原子団からなる
スペーサ部を介してネマチック配向付与性のパラ置換環
状化合物単位からなるメソゲン部を有するものなどがあ
げられる。これら液晶性ポリマーは、たとえば、ガラス
板上に形成したポリイミドやポリビニルアルコール等の
薄膜の表面をラビング処理したもの、酸化珪素を斜方蒸
着したものなどの配向処理面上に液晶性ポリマーの溶液
を展開して熱処理することにより行われる。Examples of the liquid crystalline polymer include various types of main chain type and side chain type in which a conjugated linear atomic group (mesogen) imparting liquid crystal orientation is introduced into the main chain or side chain of the polymer. And so on. Specific examples of the main chain type liquid crystalline polymer include a structure in which a mesogen group is bonded by a spacer portion that imparts flexibility, such as a nematic-oriented polyester-based liquid crystalline polymer, a discotic polymer, and a cholesteric polymer. . Specific examples of the side-chain type liquid crystalline polymer include polysiloxane, polyacrylate, polymethacrylate or polymalonate having a main chain skeleton, and a paraffin-imparting paraffin having a conjugated atomic group as a side chain. And those having a mesogen moiety composed of a substituted cyclic compound unit. These liquid crystalline polymers are prepared by, for example, rubbing the surface of a thin film of polyimide or polyvinyl alcohol formed on a glass plate, or applying a liquid crystalline polymer solution on an alignment-treated surface such as obliquely deposited silicon oxide. It is performed by developing and heat-treating.

【００３１】前記偏光フィルム、位相差フィルムは積層
して用いることもでき反射型偏光フィルム、半透過層型
偏光フィルム、偏光分離偏光フィルム等とすることがで
きる。また、前記例示の光学フィルムは、光学補償フィ
ルム、その他の各種視野角拡大フィルムとして使用する
こともでき、さらには光学フィルムとしては、輝度向上
フィルム等があげられる。また偏光フィルムは、表面上
に微細凹凸構造の反射層を設けて防眩シートとすること
もできる。The polarizing film and the retardation film may be laminated and used, and may be a reflection type polarizing film, a semi-transmissive layer type polarizing film, a polarized light separating polarizing film and the like. In addition, the above-described optical films can be used as optical compensation films and other various viewing angle widening films, and examples of the optical films include brightness enhancement films and the like. Further, the polarizing film may be provided with a reflection layer having a fine uneven structure on the surface to form an antiglare sheet.

【００３２】粘着層２の形成は、液晶パネルのガラス基
板に貼着する光学フィルム１の片面に行う。形成方法は
特に制限されず、光学フィルム１に粘着剤組成物（溶
液）を塗布し乾燥する方法、粘着層２を設けた離型シー
ト３により転写する方法等があげられる。粘着層２（乾
燥膜厚）の厚さは、特に限定されないが、１０〜４０μ
ｍ程度とするのが好ましい。The formation of the adhesive layer 2 is performed on one side of the optical film 1 to be adhered to a glass substrate of a liquid crystal panel. The forming method is not particularly limited, and examples thereof include a method of applying and drying the pressure-sensitive adhesive composition (solution) on the optical film 1 and a method of transferring the pressure-sensitive adhesive composition with the release sheet 3 having the pressure-sensitive adhesive layer 2. The thickness of the adhesive layer 2 (dry film thickness) is not particularly limited.
m is preferable.

【００３３】離型シート３の構成材料としては、紙、ポ
リエチレン、ポリプロピレン、ポリエチレンテレフタレ
ート等の合成樹脂フィルム等があげられる。離型シート
３の表面には、粘着剤層２からの剥離性を高めるため、
必要に応じてシリコーン処理、長鎖アルキル処理、フッ
素処理な剥離処理が施されていても良い。Examples of the constituent material of the release sheet 3 include paper, synthetic resin films such as polyethylene, polypropylene and polyethylene terephthalate. On the surface of the release sheet 3, in order to enhance the releasability from the pressure-sensitive adhesive layer 2,
If necessary, a release treatment such as a silicone treatment, a long-chain alkyl treatment, or a fluorine treatment may be performed.

【００３４】[0034]

【実施例】以下、本発明の構成と効果を具体的に示す実
施例等について説明する。なお、各例中、部および％は
重量基準である。DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments and the like specifically showing the configuration and effects of the present invention will be described below. In addition, in each example, parts and% are based on weight.

【００３５】（重量平均分子量（Ｍｗ）および数平均分
子量（Ｍｎ）の測定）実施例および比較例で得られたア
クリル系ポリマーの重量平均分子量（Ｍｗ）および数平
均分子量（Ｍｎ）の測定は、ゲル・パーミエーション・
クロマトグラフィー法（カラム：東ソー製，ＴＳＫｇｅ
ｌ，Ｇ７０００ＨＸＬ＋ＧＭＨＸＬ＋ＧＭＨＸＬ）によ
り、標準架橋ポリスチレンを基準とし、テトラヒドロフ
ランを分離剤として用いて、ＪＩＳＡはＪＩＳ−Ｋ６３
０１により、屈折計を用いて検出することにより測定し
た値である。(Measurement of Weight Average Molecular Weight (Mw) and Number Average Molecular Weight (Mn)) The weight average molecular weight (Mw) and number average molecular weight (Mn) of the acrylic polymers obtained in Examples and Comparative Examples were measured as follows. Gel permeation
Chromatography method (column: TSKge, manufactured by Tosoh Corporation)
1, G7000HXL + GMHXL + GMHXL), based on standard crosslinked polystyrene, using tetrahydrofuran as a separating agent, and JISA conforming to JIS-K63.
01 is a value measured by detection using a refractometer.

【００３６】実施例１ （粘着剤組成物の調製）ブチルアクリレート１００部、
アクリル酸０．６部およびアゾビスイソブチロニトリル
０．４部を、得られるアクリル系ポリマーの固形分が３
０％となる酢酸エチル中で攪拌しながら６０℃で７時間
反応を行ったのち、さらに７０℃で２時間反応を行いア
クリル系ポリマー溶液を得た。得られたアクリル系ポリ
マーは重量平均分子量（Ｍｗ）１３０万、重量平均分子
量と数平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）が６．
４であった。上記アクリル系ポリマー溶液に、アルミニ
ウムトリスアセチルアセトネートをポリマー固形分１０
０部に対して０．３部加え、粘着剤組成物溶液を調製し
た。Example 1 (Preparation of PSA composition)
Acrylic acid (0.6 part) and azobisisobutyronitrile (0.4 part) were mixed with an acrylic polymer having a solid content of 3
After reacting at 60 ° C. for 7 hours while stirring in 0% ethyl acetate, the reaction was further performed at 70 ° C. for 2 hours to obtain an acrylic polymer solution. The obtained acrylic polymer has a weight average molecular weight (Mw) of 1.3 million and a ratio (Mw / Mn) of the weight average molecular weight to the number average molecular weight (Mn) of 6.
It was 4. Aluminum trisacetylacetonate was added to the above acrylic polymer solution at a polymer solid content of 10%.
0.3 part was added to 0 part to prepare an adhesive composition solution.

【００３７】（粘着型光学フィルムの作製）厚さ８０μ
ｍのポリビニルアルコールフィルムをヨウ素水溶液中で
５倍に延伸したのち乾燥させ，両側にトリアセチルセル
ロースフィルムを接着剤を介して接着し、偏光フィルム
を得た。上記により作製された粘着剤組成物溶液を、３
５μｍの厚みを有する離型紙上に乾燥後の厚みが２５μ
ｍとなるよう塗布、乾燥して粘着層を形成した。これを
上記により作製された偏光フィルムにラミネートし粘着
型偏光フィルムを得た。(Preparation of Adhesive Optical Film) Thickness 80 μm
m was stretched 5 times in an aqueous iodine solution and dried, and a triacetyl cellulose film was adhered to both sides via an adhesive to obtain a polarizing film. The pressure-sensitive adhesive composition solution prepared above was
25 μm after drying on release paper having a thickness of 5 μm
m and dried to form an adhesive layer. This was laminated on the polarizing film produced as described above to obtain an adhesive polarizing film.

【００３８】実施例２ 実施例１の（粘着剤組成物の調製）において、５０℃で
７時間反応した後、さらに７０℃で２時間反応したこと
以外は実施例１と同様にして、アクリル系ポリマー溶液
を得た。得られたアクリル系ポリマーは重量平均分子量
（Ｍｗ）９５万、重量平均分子量と数平均分子量（Ｍ
ｎ）との比（Ｍｗ／Ｍｎ）が４．９であった。また、実
施例１と同様にして、粘着剤組成物溶液を調製したの
ち、粘着型光学フィルムを作製した。Example 2 An acrylic resin was prepared in the same manner as in Example 1 except that the reaction was carried out at 50 ° C. for 7 hours and then at 70 ° C. for 2 hours. A polymer solution was obtained. The obtained acrylic polymer had a weight average molecular weight (Mw) of 950,000, a weight average molecular weight and a number average molecular weight (Mw).
n) was 4.9. Further, in the same manner as in Example 1, after preparing a pressure-sensitive adhesive composition solution, a pressure-sensitive adhesive optical film was produced.

【００３９】比較例１ 実施例１の（粘着剤組成物の調製）において、アクリル
系ポリマーの重合反応を６０℃で２時間行うことで反応
終了としたこと以外は実施例１に準じてアクリル系ポリ
マー溶液を得た。得られたアクリル系ポリマーは重量平
均分子量（Ｍｗ）１４０万、重量平均分子量と数平均分
子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）は３．１であった。
上記アクリル系ポリマー溶液を用いて実施例１と同様に
して粘着剤組成物溶液を調製した。また、実施例１と同
様にして粘着型偏光フィルムを作製した。Comparative Example 1 An acrylic polymer was prepared in the same manner as in Example 1 except that the polymerization reaction of the acrylic polymer was carried out at 60 ° C. for 2 hours to complete the reaction. A polymer solution was obtained. The obtained acrylic polymer had a weight average molecular weight (Mw) of 1.4 million and a ratio (Mw / Mn) of the weight average molecular weight to the number average molecular weight (Mn) of 3.1.
Using the acrylic polymer solution, a pressure-sensitive adhesive composition solution was prepared in the same manner as in Example 1. Further, an adhesive type polarizing film was produced in the same manner as in Example 1.

【００４０】比較例２ 実施例１の（粘着剤組成物の調製）において、アルミニ
ウムトリスアセチルアセトネートのかわりにトリレンジ
イソシアネート0 ．3 部を用いたこと以外は実施例１と
同様にして粘着剤組成物溶液を調製した。また、実施例
１と同様にして粘着型偏光フィルムを作製した。COMPARATIVE EXAMPLE 2 In Example 1 (Preparation of PSA composition), instead of aluminum trisacetylacetonate, tolylene diisocyanate was used. A pressure-sensitive adhesive composition solution was prepared in the same manner as in Example 1 except that three parts were used. Further, an adhesive type polarizing film was produced in the same manner as in Example 1.

【００４１】比較例３ 実施例１の（粘着剤組成物の調製）において、酢酸エチ
ルの量がアクリル系ポリマーの固形分の７０％となるよ
うに変えたこと以外は実施例１と同様にして、アクリル
系ポリマー溶液を得た。得られたアクリル系ポリマーは
重量平均分子量（Ｍｗ）２２０万、重量平均分子量と数
平均分子量（Ｍｎ）との比（Ｍｗ／Ｍｎ）が４．２であ
った。また、実施例１と同様にして、粘着剤組成物溶液
を調製したのち、粘着型光学フィルムを作製した。Comparative Example 3 In the same manner as in Example 1 except that the amount of ethyl acetate was changed to 70% of the solid content of the acrylic polymer in (Preparation of adhesive composition) of Example 1, Thus, an acrylic polymer solution was obtained. The obtained acrylic polymer had a weight average molecular weight (Mw) of 2.2 million and a ratio (Mw / Mn) of the weight average molecular weight to the number average molecular weight (Mn) of 4.2. Further, in the same manner as in Example 1, after preparing a pressure-sensitive adhesive composition solution, a pressure-sensitive adhesive optical film was produced.

【００４２】上記実施例および比較例で得られた粘着型
偏光フィルムについて以下の評価を行った。評価結果を
表１に示す。The following evaluations were made on the pressure-sensitive adhesive polarizing films obtained in the above Examples and Comparative Examples. Table 1 shows the evaluation results.

【００４３】（表示ムラ）上記により作製された粘着剤
付偏光フィルムを所定の軸角度（４５°）、サイズ（１
００ｍｍ×１５０ｍｍ）に切断し、ＴＦＴ−ＬＣＤセル
の両面に貼り合わせた後、８０℃雰囲気下に１６時間放
置した。このＬＣＤパネルを点灯して黒表示とし１時間
放置後に、ミノルタ株式会社製液晶色分布測定装置ＣＡ
−１０００を用いて面内の輝度分布を測定し、面内輝度
の標準偏差（％）を求めた。輝度標準偏差が小さいほ
ど、表示ムラが少なく良好である。(Display unevenness) The polarizing film with the pressure-sensitive adhesive prepared as described above was subjected to a predetermined axial angle (45 °) and a size (1).
(00 mm × 150 mm), bonded to both sides of the TFT-LCD cell, and left in an atmosphere at 80 ° C. for 16 hours. The LCD panel is turned on to display black, and after standing for 1 hour, a liquid crystal color distribution measuring device CA manufactured by Minolta Co., Ltd.
The in-plane luminance distribution was measured using -1000, and the standard deviation (%) of the in-plane luminance was determined. The smaller the luminance standard deviation, the better the display unevenness is reduced.

【００４４】（加熱耐久性）上記により作製された粘着
剤付偏光フィルム１２インチサイズに切断したものを、
ガラス板に貼り付けた後、オートクレーブ処理（５０℃
×０．５Ｍｐａ×１５ｍｉｎ）を行った。さらに、９０
℃の雰囲気下に５００時間投入した後の粘着層の状態を
以下の基準で評価した。 ○：不具合発生なし。 ×：発泡、剥がれなどの不具合が見られる。(Heat Durability) The polarizing film with the pressure-sensitive adhesive prepared as described above was cut into a 12-inch size.
After sticking to a glass plate, autoclave treatment (50 ° C
× 0.5 Mpa × 15 min). In addition, 90
The state of the pressure-sensitive adhesive layer after being put in an atmosphere of 500C for 500 hours was evaluated according to the following criteria. ：: No failure occurred. X: Defects such as foaming and peeling are observed.

【００４５】[0045]

【表１】 [Table 1]

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の粘着型光学フィルムの断面図である。FIG. 1 is a sectional view of an adhesive optical film of the present invention.

【符号の説明】[Explanation of symbols]

１ 光学フィルム ２ 粘着層 ３ 離型シート DESCRIPTION OF SYMBOLS 1 Optical film 2 Adhesive layer 3 Release sheet

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.⁷ 識別記号 ＦＩ テーマコート゛(参考） Ｇ０２Ｆ 1/13363 Ｇ０２Ｆ 1/13363 (72)発明者 小林 茂生 大阪府茨木市下穂積１丁目１番２号 日東 電工株式会社内 (72)発明者 高橋 寧 大阪府茨木市下穂積１丁目１番２号 日東 電工株式会社内 Ｆターム(参考） 2H049 BA02 BA06 BB43 BB51 BC22 2H091 FA08X FA08Z FA11X FA11Z FA16Z FA37X FA37Z FB02 FD15 LA18 4J004 AA10 CA01 CA03 CA05 CC02 CC03 CD05 CD06 DA02 DA04 DA05 DB02 FA05 FA10 4J040 DF031 GA07 HD41 JA09 JB09 KA16 LA01 LA06 LA08 NA17 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. ⁷ Identification FI FI Theme Court ゛ (Reference) G02F 1/13363 G02F 1/13363 (72) Inventor Shigeo Kobayashi 1-1-2 Shimohozumi, Ibaraki-shi, Osaka Nitto Denko Co., Ltd. (72) Inventor Yasushi Takahashi 1-2-1, Shimohozumi, Ibaraki-shi, Osaka Nitto Denko Corporation F-term (reference) 2H049 BA02 BA06 BB43 BB51 BC22 2H091 FA08X FA08Z FA11X FA11Z FA16Z FA37X FA37Z FB02 FD15 LA18 4J004 AA10 CA01 CA03 CA05 CC02 CC03 CD05 CD06 DA02 DA04 DA05 DB02 FA05 FA10 4J040 DF031 GA07 HD41 JA09 JB09 KA16 LA01 LA06 LA08 NA17

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 光学フィルムの一方の面に粘着層が積層
されている粘着型光学フィルムにおいて、前記粘着層
が、カルボキシル基を有するアクリル系ポリマーの多官
能性金属キレートによる架橋物により形成されており、
かつ前記アクリル系ポリマーが重量平均分子量（Ｍｗ）
６０万〜２００万、重量平均分子量と数平均分子量（Ｍ
ｎ）との比（Ｍｗ／Ｍｎ）が４以上を有するものである
ことを特徴とする粘着型光学フィルム。1. An adhesive optical film in which an adhesive layer is laminated on one surface of an optical film, wherein the adhesive layer is formed of a crosslinked product of a polyfunctional metal chelate of an acrylic polymer having a carboxyl group. Yes,
And the acrylic polymer has a weight average molecular weight (Mw)
600,000-2,000,000, weight average molecular weight and number average molecular weight (M
a pressure-sensitive adhesive optical film having a ratio (Mw / Mn) of at least 4 to n). 【請求項２】 多官能性金属キレートが、多官能性アル
ミニウムキレートであることを特徴とする請求項１記載
の粘着型光学フィルム。2. The adhesive optical film according to claim 1, wherein the polyfunctional metal chelate is a polyfunctional aluminum chelate. 【請求項３】 請求項１または２記載の粘着型光学フィ
ルムを用いた液晶表示装置。3. A liquid crystal display device using the pressure-sensitive adhesive optical film according to claim 1.