JP2002328230A - Polarizing plate and method for manufacturing the same, protective film for polarizing plate, optical film and liquid crystal display device using polarizing plate - Google Patents
Polarizing plate and method for manufacturing the same, protective film for polarizing plate, optical film and liquid crystal display device using polarizing plateInfo
- Publication number
- JP2002328230A JP2002328230A JP2001134156A JP2001134156A JP2002328230A JP 2002328230 A JP2002328230 A JP 2002328230A JP 2001134156 A JP2001134156 A JP 2001134156A JP 2001134156 A JP2001134156 A JP 2001134156A JP 2002328230 A JP2002328230 A JP 2002328230A
- Authority
- JP
- Japan
- Prior art keywords
- polarizing plate
- film
- protective film
- transparent protective
- polarizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、偏光板およびその
製造方法に関する。また、当該偏光板に用いられる偏光
板用保護フィルムに関する。本発明の偏光板はこれ単独
でまたはこれを積層した光学フイルムとして液晶表示装
置を形成しうる。[0001] The present invention relates to a polarizing plate and a method for producing the same. The present invention also relates to a polarizing plate protective film used for the polarizing plate. The polarizing plate of the present invention can form a liquid crystal display device alone or as an optical film in which the polarizing plate is laminated.
【０００２】[0002]
【従来の技術】液晶表示装置には、その画像形成方式か
ら液晶パネルの最表面を形成するガラス基板の両側に偏
光子を配置することが必要不可欠であり、一般的には、
ポリビニルアルコール系フイルムとヨウ素などの二色性
物質からなる偏光子にトリアセチルセルロースなどの透
明保護フイルムを貼り合わせた偏光板が用いられてい
る。2. Description of the Related Art In a liquid crystal display device, it is indispensable to dispose polarizers on both sides of a glass substrate forming the outermost surface of a liquid crystal panel due to its image forming method.
A polarizing plate is used in which a polarizer made of a dichroic substance such as a polyvinyl alcohol film and iodine is bonded to a transparent protective film such as triacetyl cellulose.
【０００３】前記透明保護フイルムとして用いられるト
リアセチルセルロースフイルムと偏光子として用いられ
るポリビニルアルコール系フイルムとは接着性が良くな
い。そのため、トリアセチルセルロースフイルムはアル
カリ液に浸漬することにより表面をケン化して接着性を
改善したものが用いられている。しかし、ケン化処理は
高濃度のアルカリ溶液を使用するため危険が伴い、その
設備に対しても負荷が大きく故障などのトラブルが発生
しやすい。またケン化処理を長時間行うとアルカリ溶液
の濃度が低下して、ケン化処理による接着性の改善効果
が不十分になることがある。さらには廃アルカリ溶液の
処分には大量の廃水を発生させてしまうなどの問題があ
った。[0003] The triacetyl cellulose film used as the transparent protective film and the polyvinyl alcohol-based film used as the polarizer have poor adhesion. For this reason, a triacetylcellulose film whose surface is saponified by immersion in an alkaline solution to improve the adhesiveness is used. However, the saponification treatment involves a danger due to the use of a high-concentration alkaline solution, and the load on the equipment is large, and troubles such as failures are likely to occur. In addition, when the saponification treatment is performed for a long time, the concentration of the alkali solution decreases, and the effect of improving the adhesiveness by the saponification treatment may be insufficient. Further, disposal of the waste alkaline solution has a problem that a large amount of waste water is generated.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、ケン化処理
に係わる問題のない偏光板およびその製造方法を提供す
ることを目的とする。また、当該偏光板に用いられる透
明保護フイルムを提供することを目的とする。さらに
は、前記偏光板を積層した光学フイルム、液晶表示装置
を提供することを目的とする。SUMMARY OF THE INVENTION An object of the present invention is to provide a polarizing plate free from problems relating to saponification and a method for producing the same. Another object of the present invention is to provide a transparent protective film used for the polarizing plate. Still another object of the present invention is to provide an optical film and a liquid crystal display in which the polarizing plates are laminated.
【０００５】[0005]
【課題を解決するための手段】本発明者らは前記課題を
解決すべく鋭意検討を重ねた結果、以下に示す処理の施
された透明保護フイルムを用いることにより前記目的を
達成できることを見出し、本発明を完成するに至った。Means for Solving the Problems The present inventors have made intensive studies to solve the above-mentioned problems, and as a result, have found that the above-mentioned object can be achieved by using a transparent protective film having been subjected to the following treatment. The present invention has been completed.
【０００６】すなわち本発明は、偏光子の少なくとも一
方の面に接着層を介して透明保護フイルムが設けられて
いる偏光板において、前記透明保護フイルムの偏光子と
接着する面に、ゼラチン系塗布層が形成されていること
を特徴とする偏光板、に関する。That is, the present invention relates to a polarizing plate having a transparent protective film provided on at least one surface of a polarizer via an adhesive layer, wherein a surface of the transparent protective film that adheres to the polarizer is coated with a gelatin-based coating layer. Is formed on the polarizing plate.
【０００７】前記偏光板において、ゼラチン系塗布層
が、透明保護フイルム材料を溶解しうる溶剤を分散媒と
して含有するゼラチン分散液により形成されたものであ
ることが好ましい。In the above-mentioned polarizing plate, it is preferable that the gelatin-based coating layer is formed by a gelatin dispersion containing a solvent capable of dissolving the transparent protective film material as a dispersion medium.
【０００８】前記偏光板において、透明保護フイルム
が、トリアセチルセルロースフイルムであることが好ま
しい。In the above polarizing plate, the transparent protective film is preferably a triacetyl cellulose film.
【０００９】前記偏光板において、透明保護フイルムと
偏光子とを接着する接着層が、ゼラチンを含有する接着
剤により形成されたものであることが好ましい。In the above polarizing plate, it is preferable that the adhesive layer for bonding the transparent protective film and the polarizer is formed of an adhesive containing gelatin.
【００１０】前記偏光板において、透明保護フイルムと
偏光子とを接着する接着層が、ポリビニルアルコールを
含有する接着剤により形成されたものであることが好ま
しい。In the above-mentioned polarizing plate, it is preferable that the adhesive layer for bonding the transparent protective film and the polarizer is formed of an adhesive containing polyvinyl alcohol.
【００１１】また本発明は、偏光子の少なくとも一方の
面に接着層を介して透明保護フイルムが設けられている
偏光板の製造方法であって、透明保護フイルムの偏光子
と接着する面に、ゼラチン系塗布層を形成した後、接着
剤を用いて透明保護フイルムと偏光子を貼り合わせるこ
とを特徴とする前記偏光板の製造方法、に関する。The present invention also relates to a method for producing a polarizing plate comprising a polarizer and a transparent protective film provided on at least one surface of the polarizer via an adhesive layer, the method comprising: The present invention also relates to a method for producing the above-mentioned polarizing plate, which comprises, after forming a gelatin-based coating layer, laminating a transparent protective film and a polarizer using an adhesive.
【００１２】また本発明は、透明保護フイルムの偏光子
と接着する面に、ゼラチン分散液による塗布層が形成さ
れていることを特徴とする前記偏光板に用いられる偏光
板用保護フィルム、に関する。[0012] The present invention also relates to a protective film for a polarizing plate used for the polarizing plate, wherein a coating layer of a gelatin dispersion is formed on a surface of the transparent protective film which adheres to the polarizer.
【００１３】また本発明は、前記偏光板が、少なくとも
１枚積層されている光学フイルム、に関する。The present invention also relates to an optical film in which at least one polarizing plate is laminated.
【００１４】さらには本発明は、前記偏光板または光学
フイルムが用いられていることを特徴とする液晶表示装
置、に関する。Further, the present invention relates to a liquid crystal display device using the above-mentioned polarizing plate or optical film.
【００１５】上記本発明は、透明保護フイルムの表面を
ケン化処理する代わりに、透明保護フイルムの表面層に
ゼラチン系塗布層を設けることにより投錨効果を発現
し、接着剤を用いて偏光子との接着性を向上させたもの
である。ゼラチン系塗布層の形成は、透明保護フイルム
材料を溶解しうる溶剤を分散媒として含有するゼラチン
分散液を用いることにより、透明保護フイルムの表面層
のみを溶解して当該表面層にゼラチンを埋没させ、投錨
効果をより発現させることができる。According to the present invention, instead of saponifying the surface of the transparent protective film, a gelatin-based coating layer is provided on the surface layer of the transparent protective film to exhibit an anchoring effect. Is improved. The gelatin-based coating layer is formed by dissolving only the surface layer of the transparent protective film by using a gelatin dispersion containing a solvent capable of dissolving the transparent protective film material as a dispersion medium, and embedding gelatin in the surface layer. In addition, the anchor effect can be more developed.
【００１６】[0016]
【発明の実施の形態】本発明の偏光板は、図１に示すよ
うに、偏光子１の少なくとも一方の面に、ゼラチンを含
む接着剤により形成された接着層２を介して透明保護フ
イルム３が設けられているものである。図１では、偏光
子１の片側に透明保護フイルム３が設けられているが、
透明保護フイルム３は偏光子１の両側に設けられていて
もよい。図１の透明保護フイルム３の偏光子１と接着す
る面には、ゼラチン系塗布層ａが設けられている。BEST MODE FOR CARRYING OUT THE INVENTION As shown in FIG. 1, a polarizing plate of the present invention comprises a transparent protective film 3 on at least one surface of a polarizer 1 through an adhesive layer 2 formed of an adhesive containing gelatin. Is provided. In FIG. 1, a transparent protective film 3 is provided on one side of the polarizer 1,
The transparent protective film 3 may be provided on both sides of the polarizer 1. A gelatin-based coating layer a is provided on the surface of the transparent protective film 3 of FIG. 1 that adheres to the polarizer 1.
【００１７】偏光子は、特に制限されず、各種のものを
使用できる。偏光子としては、たとえば、ポリビニルア
ルコール系フイルム、部分ホルマール化ポリビニルアル
コール系フイルム、エチレン・酢酸ビニル共重合体系部
分ケン化フイルム等の親水性高分子フイルムに、ヨウ素
や二色性染料等の二色性物質を吸着させて一軸延伸した
もの、ポリビニルアルコールの脱水処理物やポリ塩化ビ
ニルの脱塩酸処理物等ポリエン系配向フイルム等があげ
られる。これらのなかでもポリビニルアルコール系フイ
ルムとヨウ素などの二色性物質からなる偏光子が好適で
ある。これら偏光子の厚さは特に制限されないが、一般
的に、５〜８０μｍ程度である。The polarizer is not particularly limited, and various types can be used. Examples of polarizers include hydrophilic polymer films such as polyvinyl alcohol-based films, partially formalized polyvinyl alcohol-based films, ethylene-vinyl acetate copolymer-based partially saponified films, and dichromatic dyes such as iodine and dichroic dyes. Uniaxially stretched by adsorbing a hydrophilic substance, or a polyene-based oriented film such as a dehydrated product of polyvinyl alcohol or a dehydrochlorination product of polyvinyl chloride. Among these, a polarizer comprising a dichroic substance such as a polyvinyl alcohol film and iodine is preferable. The thickness of these polarizers is not particularly limited, but is generally about 5 to 80 μm.
【００１８】ポリビニルアルコール系フイルムをヨウ素
で染色し一軸延伸した偏光子は、たとえば、ポリビニル
アルコールをヨウ素の水溶液に浸漬することによって染
色し、元長の３〜７倍に延伸することで作製することが
できる。必要に応じてホウ酸やヨウ化カリウムなどの水
溶液に浸漬することもできる。さらに必要に応じて染色
の前にポリビニルアルコール系フイルムを水に浸漬して
水洗してもよい。ポリビニルアルコール系フイルムを水
洗することでポリビニルアルコール系フイルム表面の汚
れやブロッキング防止剤を洗浄することができるほか
に、ポリビニルアルコール系フイルムを膨潤させること
で染色のムラなどの不均一を防止する効果もある。延伸
はヨウ素で染色した後に行っても良いし、染色しながら
延伸してもよし、また延伸してからヨウ素で染色しても
よい。ホウ酸やヨウ化カリウムなどの水溶液中や水浴中
でも延伸することができる。A polarizer which is obtained by dyeing a polyvinyl alcohol-based film with iodine and uniaxially stretching is produced by, for example, dyeing polyvinyl alcohol by immersing it in an aqueous solution of iodine, and stretching the film to 3 to 7 times its original length. Can be. If necessary, it can be immersed in an aqueous solution of boric acid or potassium iodide. If necessary, the polyvinyl alcohol-based film may be immersed in water and washed with water before dyeing. By washing the polyvinyl alcohol film with water, dirt on the surface of the polyvinyl alcohol film and an anti-blocking agent can be washed, and by swelling the polyvinyl alcohol film, it also has an effect of preventing unevenness such as uneven dyeing. is there. Stretching may be performed after dyeing with iodine, may be performed while dyeing, or may be dyed with iodine after stretching. Stretching can be performed in an aqueous solution of boric acid or potassium iodide or in a water bath.
【００１９】前記偏光子の片側または両側に設けられて
いる透明保護フイルムは、透明性、機械的強度、熱安定
性、水分遮蔽性、等方性などに優れるものが好ましい。
透明保護フイルムの材料としては、例えばポリエチレン
テレフタレートやポリエチレンナフタレート等のポリエ
ステル系ポリマー、ジアセチルセルロースやトリアセチ
ルセルロース等のセルロース系ポリマー、ポリメチルメ
タクリレート等のアクリル系ポリマー、ポリスチレンや
アクリロニトリル・スチレン共重合体（ＡＳ樹脂）等の
スチレン系ポリマー、ポリカーボネート系ポリマーなど
があげられる。また、ポリエチレン、ポリプロピレン、
シクロ系ないしはノルボルネン構造を有するポリオレフ
ィン、エチレン・プロピレン共重合体の如きポリオレフ
ィン系ポリマー、塩化ビニル系ポリマー、ナイロンや芳
香族ポリアミド等のアミド系ポリマー、イミド系ポリマ
ー、スルホン系ポリマー、ポリエーテルスルホン系ポリ
マー、ポリエーテルエーテルケトン系ポリマー、ポリフ
ェニレンスルフィド系ポリマー、ビニルアルコール系ポ
リマー、塩化ビニリデン系ポリマー、ビニルブチラール
系ポリマー、アリレート系ポリマー、ポリオキシメチレ
ン系ポリマー、エポキシ系ポリマー、または前記ポリマ
ーのブレンド物なども前記透明保護フイルムを形成する
ポリマーの例としてあげられる。アクリル系やウレタン
系、アクリルウレタン系やエポキシ系、シリコーン系等
の熱硬化型ないし紫外線硬化型樹脂などをフィルム化し
たものなどがあげられる。The transparent protective film provided on one or both sides of the polarizer preferably has excellent transparency, mechanical strength, heat stability, moisture shielding property, isotropy and the like.
Examples of the material of the transparent protective film include polyester polymers such as polyethylene terephthalate and polyethylene naphthalate; cellulose polymers such as diacetyl cellulose and triacetyl cellulose; acrylic polymers such as polymethyl methacrylate; polystyrene and acrylonitrile / styrene copolymer. Styrene-based polymers such as (AS resin) and polycarbonate-based polymers. Also, polyethylene, polypropylene,
Polyolefin having cyclo or norbornene structure, polyolefin polymer such as ethylene / propylene copolymer, vinyl chloride polymer, amide polymer such as nylon or aromatic polyamide, imide polymer, sulfone polymer, polyether sulfone polymer , A polyether ether ketone polymer, a polyphenylene sulfide polymer, a vinyl alcohol polymer, a vinylidene chloride polymer, a vinyl butyral polymer, an arylate polymer, a polyoxymethylene polymer, an epoxy polymer, or a blend of the above polymers. Examples of the polymer forming the transparent protective film are given below. A film formed of a thermosetting or ultraviolet curable resin such as an acrylic resin, a urethane resin, an acrylic urethane resin, an epoxy resin, or a silicone resin may be used.
【００２０】透明保護フイルムの厚さは、一般には５０
０μｍ以下であり、１〜３００μｍが好ましい。特に５
〜２００μｍとするのが好ましい。The thickness of the transparent protective film is generally 50
0 μm or less, preferably 1 to 300 μm. Especially 5
It is preferable to set it to 200 μm.
【００２１】透明保護フイルムとしては、偏光特性や耐
久性などの点より、トリアセチルセルロース等のセルロ
ース系ポリマーが好ましい。特にトリアセチルセルロー
スフイルムが好適である。なお、偏光子の両側に透明保
護フイルムを設ける場合、その表裏で同じポリマー材料
からなる透明保護フイルムを用いてもよく、異なるポリ
マー材料等からなる透明保護フイルムを用いてもよい。As the transparent protective film, a cellulosic polymer such as triacetylcellulose is preferred from the viewpoints of polarization characteristics and durability. Particularly, a triacetyl cellulose film is preferable. When transparent protective films are provided on both sides of the polarizer, a transparent protective film made of the same polymer material may be used on the front and back sides, or a transparent protective film made of a different polymer material or the like may be used.
【００２２】透明保護フイルムの偏光子と接着する面に
は、ゼラチン系塗布層を形成する。ゼラチン系塗布層の
厚みは、通常、０. ０１〜１０μｍ程度とするのが好ま
しい。A gelatin-based coating layer is formed on the surface of the transparent protective film that adheres to the polarizer. Usually, the thickness of the gelatin-based coating layer is preferably about 0.01 to 10 μm.
【００２３】ゼラチン系塗布層の形成には各種手段を使
用できるが、ゼラチン分散液を用いるのが好ましい。特
にゼラチン分散液の調製に用いる分散媒として、透明保
護フイルム材料を溶解しうる溶剤を含有するものが好ま
しい。当該溶剤は、透明保護フイルム材料に応じて適宜
に選択できるが、たとえば、透明保護フイルム材料がト
リアセチルセルロースの場合にはメタノール、アセト
ン、塩化メチレン、シクロヘキサノンおよびこれらの混
合液等を例示できる。ゼラチン分散液中には、水を含有
することもできるが、分散媒中水の割合は、５０重量％
以下、特に５〜４０重量％とするのが好ましい。ゼラチ
ン分散液は、通常、ゼラチンを０. ０１〜５重量％含有
してなる。ゼラチン分散液は塗布乾燥層などとして形成
される。Various means can be used for forming the gelatin-based coating layer, but it is preferable to use a gelatin dispersion. In particular, a dispersion medium containing a solvent capable of dissolving the transparent protective film material is preferable as the dispersion medium used for preparing the gelatin dispersion liquid. The solvent can be appropriately selected according to the transparent protective film material. For example, when the transparent protective film material is triacetyl cellulose, methanol, acetone, methylene chloride, cyclohexanone, and a mixture thereof can be exemplified. The gelatin dispersion may contain water, but the proportion of water in the dispersion medium is 50% by weight.
Hereinafter, it is particularly preferable to be 5 to 40% by weight. The gelatin dispersion usually contains 0.01 to 5% by weight of gelatin. The gelatin dispersion is formed as a coating dry layer or the like.
【００２４】また、ゼラチンは、たんぱく質であるコラ
ーゲンの加水分解物等を含む両性電解質であるため、ゼ
ラチン分散液にはアミノ基やカルボキシル基と反応する
官能基を有する水溶性架橋剤を含有することができる。
水溶性架橋剤としては、ホルムアルデヒド、グルタルア
ルデヒド、グリオキザール等のアルデヒド化合物、メラ
ミン等のアミノ化合物、シュウ酸等のカルボンキシル化
合物、ケトン類、キノン類、クロム、アルミニウム等の
第二鉄属等の金属類等を例示できる。これら水溶性架橋
剤の添加量は特に制限されないが、通常、ゼラチンの固
形分１００重量部に対して、５０重量部以下である。好
ましくは２〜３０重量部である。また、ゼラチン分散液
には架橋を進行させるためにｐＨを変化させることもで
きる。ゼラチン分散液の調製に際しては必要に応じて、
ギ酸、フェノール、サリチル酸、ベンズアルデヒド等の
防腐剤等の添加剤を配合することができる。Since gelatin is an amphoteric electrolyte containing a hydrolyzate of collagen which is a protein, the gelatin dispersion should contain a water-soluble crosslinking agent having a functional group which reacts with an amino group or a carboxyl group. Can be.
Examples of the water-soluble crosslinking agent include aldehyde compounds such as formaldehyde, glutaraldehyde and glyoxal, amino compounds such as melamine, carboxyl compounds such as oxalic acid, ketones, quinones, and metals such as ferric metals such as chromium and aluminum. And the like. The amount of the water-soluble crosslinking agent is not particularly limited, but is usually 50 parts by weight or less based on 100 parts by weight of the solid content of gelatin. Preferably it is 2 to 30 parts by weight. In addition, the pH of the gelatin dispersion can be changed in order to promote crosslinking. When preparing a gelatin dispersion, if necessary,
Additives such as preservatives such as formic acid, phenol, salicylic acid and benzaldehyde can be added.
【００２５】前記透明保護フイルムの偏光子を接着させ
ない面（ゼラチン系塗布層も設けない面）には、ハード
コート層や反射防止処理、スティッキング防止や、拡散
ないしアンチグレアを目的とした処理を施したものであ
ってもよい。The surface of the transparent protective film on which the polarizer is not adhered (the surface on which no gelatin-based coating layer is provided) was subjected to a hard coat layer, an antireflection treatment, a treatment for preventing sticking, and a treatment for diffusion or antiglare. It may be something.
【００２６】ハードコート処理は偏光板表面の傷付き防
止などを目的に施されるものであり、例えばアクリル
系、シリコーン系などの適宜な紫外線硬化型樹脂による
硬度や滑り特性等に優れる硬化皮膜を透明保護フイルム
の表面に付加する方式などにて形成することができる。
反射防止処理は偏光板表面での外光の反射防止を目的に
施されるものであり、従来に準じた反射防止膜などの形
成により達成することができる。また、スティッキング
防止処理は隣接層との密着防止を目的に施される。The hard coat treatment is performed for the purpose of preventing the polarizing plate surface from being scratched. For example, a hardened film excellent in hardness and sliding properties by an appropriate UV-curable resin such as an acrylic or silicone resin is used. It can be formed by a method of adding to the surface of the transparent protective film.
The anti-reflection treatment is performed for the purpose of preventing reflection of external light on the polarizing plate surface, and can be achieved by forming an anti-reflection film or the like according to the related art. The anti-sticking treatment is performed for the purpose of preventing adhesion to an adjacent layer.
【００２７】またアンチグレア処理は偏光板の表面で外
光が反射して偏光板透過光の視認を阻害することの防止
等を目的に施されるものであり、例えばサンドブラスト
方式やエンボス加工方式による粗面化方式や透明微粒子
の配合方式などの適宜な方式にて透明保護フイルムの表
面に微細凹凸構造を付与することにより形成することが
できる。前記表面微細凹凸構造の形成に含有させる微粒
子としては、例えば平均粒径が０．５〜５０μｍのシリ
カ、アルミナ、チタニア、ジルコニア、酸化錫、酸化イ
ンジウム、酸化カドミウム、酸化アンチモン等からなる
導電性のこともある無機系微粒子、架橋又は未架橋のポ
リマー等からなる有機系微粒子などの透明微粒子が用い
られる。表面微細凹凸構造を形成する場合、微粒子の使
用量は、表面微細凹凸構造を形成する透明樹脂１００重
量部に対して一般的に２〜５０重量部程度であり、５〜
２５重量部が好ましいである。アンチグレア層は、偏光
板透過光を拡散して視角などを拡大するための拡散層
（視角拡大機能など）を兼ねるものであってもよい。The anti-glare treatment is performed for the purpose of preventing external light from being reflected on the surface of the polarizing plate and hindering the visibility of light transmitted through the polarizing plate. For example, the anti-glare treatment is performed by a sandblasting method or an embossing method. The transparent protective film can be formed by giving a fine uneven structure to the surface of the transparent protective film by an appropriate method such as a surface forming method or a method of blending transparent fine particles. As the fine particles to be contained in the formation of the surface fine uneven structure, for example, a conductive material composed of silica, alumina, titania, zirconia, tin oxide, indium oxide, cadmium oxide, antimony oxide and the like having an average particle size of 0.5 to 50 μm. Transparent fine particles such as inorganic fine particles that may be used and organic fine particles made of a crosslinked or uncrosslinked polymer or the like are used. When forming the fine surface unevenness structure, the amount of the fine particles is generally about 2 to 50 parts by weight based on 100 parts by weight of the transparent resin forming the fine surface unevenness structure.
25 parts by weight are preferred. The anti-glare layer may also serve as a diffusion layer (such as a viewing angle expanding function) for diffusing light transmitted through the polarizing plate to increase the viewing angle and the like.
【００２８】なお、前記反射防止層、スティッキング防
止層、拡散層やアンチグレア層等は、透明保護フイルム
そのものに設けることができるほか、別途光学層として
透明保護層とは別体のものとして設けることもできる。The anti-reflection layer, anti-sticking layer, diffusion layer, anti-glare layer and the like can be provided on the transparent protective film itself, or can be separately provided as an optical layer separately from the transparent protective layer. it can.
【００２９】前記偏光子と透明保護フイルムとの接着処
理には、各種の水系接着剤を使用することができる。水
系接着剤としては、ポリビニルアルコール系接着剤、ゼ
ラチン系接着剤、ビニル系ラテックス系、水系ポリウレ
タン、水系ポリエステル等を例示できる。前記接着剤
は、通常、水溶液からなる接着剤として用いられ、通
常、１〜１０重量％の固形分を含有してなる。これら接
着剤は組み合わせて使用することもできる。Various water-based adhesives can be used for the bonding treatment between the polarizer and the transparent protective film. Examples of the water-based adhesive include a polyvinyl alcohol-based adhesive, a gelatin-based adhesive, a vinyl latex-based, an aqueous polyurethane, and an aqueous polyester. The adhesive is usually used as an adhesive composed of an aqueous solution, and usually contains 1 to 10% by weight of solid content. These adhesives can be used in combination.
【００３０】前記接着剤には水溶性架橋剤を含有するこ
とによりゲル強度が増し、接着性を向上させることがで
きる。ポリビニルアルコール系接着剤には、ホウ酸、ホ
ウ砂、グルタルアルデヒド、メラミン、シュウ酸などの
水溶性架橋剤を含有することができる。またゼラチン系
接着剤には、ゼラチンがたんぱく質であるコラーゲンの
加水分解物等を含む両性電解質であることから、アミノ
基やカルボキシル基と反応する官能基を有する水溶性架
橋剤を含有することができる。たとえば、ホルムアルデ
ヒド、グルタルアルデヒド、グリオキザール等のアルデ
ヒド化合物、メラミン等のアミノ化合物、シュウ酸等の
カルボンキシル化合物、ケトン類、キノン類、クロム、
アルミニウム等の第二鉄属等の金属類等を例示できる。
水溶性架橋剤の添加量は特に制限されないが、通常、ゼ
ラチンやポリビニルアルコール等の主材の固形分１００
重量部に対して、４０重量部以下である。好ましくは
０．５〜３０重量部である。また、前記接着剤は架橋を
進行させるためにｐＨを変化させることもできる。さら
には前記接着剤にはその水溶液の調製に際して必要に応
じて、ギ酸、フェノール、サリチル酸、ベンズアルデヒ
ド等の防腐剤等の添加剤を配合することができる。When the adhesive contains a water-soluble crosslinking agent, the gel strength is increased and the adhesiveness can be improved. The polyvinyl alcohol-based adhesive may contain a water-soluble crosslinking agent such as boric acid, borax, glutaraldehyde, melamine, and oxalic acid. In addition, the gelatin-based adhesive can contain a water-soluble cross-linking agent having a functional group that reacts with an amino group or a carboxyl group because gelatin is an amphoteric electrolyte containing a hydrolyzate of collagen, which is a protein. . For example, formaldehyde, glutaraldehyde, aldehyde compounds such as glyoxal, amino compounds such as melamine, carboxyl compounds such as oxalic acid, ketones, quinones, chromium,
Examples thereof include metals such as ferric metals such as aluminum.
The amount of the water-soluble crosslinking agent to be added is not particularly limited, but usually, the solid content of the main material such as gelatin or polyvinyl alcohol is 100%.
It is 40 parts by weight or less based on parts by weight. Preferably it is 0.5 to 30 parts by weight. Further, the adhesive can change the pH in order to promote crosslinking. Furthermore, additives such as preservatives such as formic acid, phenol, salicylic acid, and benzaldehyde can be added to the adhesive as needed when preparing the aqueous solution.
【００３１】本発明の偏光板は、ゼラチン系塗布層を形
成した透明保護フイルムの当該ゼラチン系塗布層と偏光
子を、接着剤を用いて貼り合わせることにより製造す
る。接着剤の塗布は、透明保護フイルム、偏光子のいず
れに行ってもよく、両者に行ってもよい。貼り合わせ後
には、乾燥工程を施し、水溶液の塗布乾燥層からなる接
着層を形成する。偏光子と透明保護フイルムの貼り合わ
せは、ロールラミネーター等により行うことができる。
接着層の厚さは、特に制限されないが、通常０．１〜５
μｍ程度である。The polarizing plate of the present invention is produced by laminating the gelatin-based coating layer of a transparent protective film having a gelatin-based coating layer formed thereon and a polarizer using an adhesive. The application of the adhesive may be performed on either the transparent protective film or the polarizer, or may be performed on both. After bonding, a drying step is performed to form an adhesive layer composed of a coating and drying layer of an aqueous solution. The bonding of the polarizer and the transparent protective film can be performed by a roll laminator or the like.
The thickness of the adhesive layer is not particularly limited, but is usually 0.1 to 5
It is about μm.
【００３２】本発明の偏光板は、実用に際して他の光学
層と積層した光学フイルムとして用いることができる。
その光学層については特に限定はないが、例えば反射板
や半透過板、位相差板（1 ／2 や1 ／４等の波長板を含
む）、視角補償フイルムなどの液晶表示装置等の形成に
用いられることのある光学層を１層または２層以上用い
ることができる。特に、本発明の偏光板に更に反射板ま
たは半透過反射板が積層されてなる反射型偏光板または
半透過型偏光板、偏光板に更に位相差板が積層されてな
る楕円偏光板または円偏光板、偏光板に更に視角補償フ
イルムが積層されてなる広視野角偏光板、あるいは偏光
板に更に輝度向上フイルムが積層されてなる偏光板が好
ましい。The polarizing plate of the present invention can be used as an optical film laminated with another optical layer in practical use.
The optical layer is not particularly limited. For example, it is used for forming a liquid crystal display device such as a reflection plate, a semi-transmission plate, a retardation plate (including a wavelength plate such as 1/2 or 1/4), and a viewing angle compensation film. One or more optical layers that may be used may be used. In particular, a reflective polarizing plate or a transflective polarizing plate in which a reflecting plate or a transflective reflecting plate is further laminated on the polarizing plate of the present invention, an elliptically polarizing plate or a circularly polarized light in which a retardation plate is further laminated on a polarizing plate A wide viewing angle polarizing plate in which a viewing angle compensation film is further laminated on a plate or a polarizing plate, or a polarizing plate in which a brightness enhancement film is further laminated on a polarizing plate is preferable.
【００３３】反射型偏光板は、偏光板に反射層を設けた
もので、視認側（表示側）からの入射光を反射させて表
示するタイプの液晶表示装置などを形成するためのもの
であり、バックライト等の光源の内蔵を省略できて液晶
表示装置の薄型化を図りやすいなどの利点を有する。反
射型偏光板の形成は、必要に応じ透明保護層等を介して
偏光板の片面に金属等からなる反射層を付設する方式な
どの適宜な方式にて行うことができる。The reflection type polarizing plate is provided with a reflection layer on the polarizing plate, and is used for forming a liquid crystal display device of a type which reflects and reflects an incident light from a viewing side (display side). In addition, there is an advantage that the incorporation of a light source such as a backlight can be omitted and the thickness of the liquid crystal display device can be easily reduced. The reflective polarizing plate can be formed by an appropriate method such as a method in which a reflective layer made of metal or the like is provided on one surface of the polarizing plate via a transparent protective layer or the like as necessary.
【００３４】反射型偏光板の具体例としては、必要に応
じマット処理した透明保護フイルムの片面に、アルミニ
ウム等の反射性金属からなる箔や蒸着膜を付設して反射
層を形成したものなどがあげられる。また前記透明保護
フイルムに微粒子を含有させて表面微細凹凸構造とし、
その上に微細凹凸構造の反射層を有するものなどもあげ
られる。前記した微細凹凸構造の反射層は、入射光を乱
反射により拡散させて指向性やギラギラした見栄えを防
止し、明暗のムラを抑制しうる利点などを有する。また
微粒子含有の透明保護フイルムは、入射光及びその反射
光がそれを透過する際に拡散されて明暗ムラをより抑制
しうる利点なども有している。透明保護フイルムの表面
微細凹凸構造を反映させた微細凹凸構造の反射層の形成
は、例えば真空蒸着方式、イオンプレーティング方式、
スパッタリング方式等の蒸着方式やメッキ方式などの適
宜な方式で金属を透明保護層の表面に直接付設する方法
などにより行うことができる。Specific examples of the reflective polarizing plate include a transparent protective film that has been matted as necessary, and a reflective layer formed by attaching a foil or a vapor-deposited film made of a reflective metal such as aluminum on one surface. can give. In addition, the transparent protective film contains fine particles to form a fine surface uneven structure,
There may be mentioned those having a reflective layer having a fine uneven structure thereon. The reflection layer having the fine uneven structure described above has an advantage of diffusing incident light by irregular reflection, preventing directivity and glare, and suppressing unevenness in brightness and darkness. Further, the transparent protective film containing fine particles also has an advantage that the incident light and the reflected light thereof are diffused when transmitted through the film, so that the uneven brightness can be further suppressed. The formation of the reflective layer having a fine uneven structure reflecting the fine uneven structure on the surface of the transparent protective film includes, for example, a vacuum deposition method, an ion plating method,
It can be performed by a method of directly attaching a metal to the surface of the transparent protective layer by an appropriate method such as a vapor deposition method such as a sputtering method or a plating method.
【００３５】反射板は前記の偏光板の透明保護フイルム
に直接付与する方式に代えて、その透明フイルムに準じ
た適宜なフイルムに反射層を設けてなる反射シートなど
として用いることもできる。なお反射層は、通常、金属
からなるので、その反射面が透明保護フイルムや偏光板
等で被覆された状態の使用形態が、酸化による反射率の
低下防止、ひいては初期反射率の長期持続の点や、保護
層の別途付設の回避の点などより好ましい。The reflecting plate may be used as a reflecting sheet in which a reflecting layer is provided on an appropriate film conforming to the transparent film, instead of the method of directly applying the reflecting film to the transparent protective film of the polarizing plate. Since the reflective layer is usually made of a metal, the use form in which the reflective surface is covered with a transparent protective film, a polarizing plate, or the like is intended to prevent a decrease in the reflectance due to oxidation and to maintain the initial reflectance for a long time. It is more preferable to avoid separately providing a protective layer.
【００３６】なお、半透過型偏光板は、上記において反
射層で光を反射し、かつ透過するハーフミラー等の半透
過型の反射層とすることにより得ることができる。半透
過型偏光板は、通常液晶セルの裏側に設けられ、液晶表
示装置などを比較的明るい雰囲気で使用する場合には、
視認側（表示側）からの入射光を反射させて画像を表示
し、比較的暗い雰囲気においては、半透過型偏光板のバ
ックサイドに内蔵されているバックライト等の内蔵光源
を使用して画像を表示するタイプの液晶表示装置などを
形成できる。すなわち、半透過型偏光板は、明るい雰囲
気下では、バックライト等の光源使用のエネルギーを節
約でき、比較的明るい雰囲気下においても内蔵光源を用
いて使用できるタイプの液晶表示装置などの形成に有用
である。It should be noted that the transflective polarizing plate can be obtained by forming a transflective reflective layer such as a half mirror that reflects and transmits light on the reflective layer. The transflective polarizing plate is usually provided on the back side of the liquid crystal cell, and when a liquid crystal display device or the like is used in a relatively bright atmosphere,
An image is displayed by reflecting the incident light from the viewing side (display side). In a relatively dark atmosphere, the image is displayed using a built-in light source such as a backlight built in the back side of the transflective polarizing plate. A liquid crystal display device or the like of a type that displays the information can be formed. That is, the transflective polarizing plate can save energy for use of a light source such as a backlight in a bright atmosphere, and is useful for forming a liquid crystal display device of a type that can be used with a built-in light source even in a relatively bright atmosphere. It is.
【００３７】偏光板に更に位相差板が積層されてなる楕
円偏光板または円偏光板について説明する。直線偏光を
楕円偏光または円偏光に変えたり、楕円偏光または円偏
光を直線偏光に変えたり、あるいは直線偏光の偏光方向
を変える場合に、位相差板などが用いられる。特に、直
線偏光を円偏光に変えたり、円偏光を直線偏光に変える
位相差板としては、いわゆる1 ／4 波長板（λ／4 板と
も言う）が用いられる。1 ／2 波長板（λ／2 板とも言
う）は、通常、直線偏光の偏光方向を変える場合に用い
られる。An elliptically polarizing plate or a circularly polarizing plate in which a retardation plate is further laminated on a polarizing plate will be described. When changing linearly polarized light to elliptically or circularly polarized light, changing elliptically or circularly polarized light to linearly polarized light, or changing the polarization direction of linearly polarized light, a phase difference plate or the like is used. In particular, a so-called quarter-wave plate (also referred to as a λ / 4 plate) is used as a retardation plate that changes linearly polarized light into circularly polarized light or converts circularly polarized light into linearly polarized light. A half-wave plate (also called a λ / 2 plate) is usually used to change the polarization direction of linearly polarized light.
【００３８】楕円偏光板はスパーツイストネマチック
（ＳＴＮ）型液晶表示装置の液晶層の複屈折により生じ
た着色（青又は黄）を補償（防止）して、前記着色のな
い白黒表示する場合などに有効に用いられる。更に、三
次元の屈折率を制御したものは、液晶表示装置の画面を
斜め方向から見た際に生じる着色も補償（防止）するこ
とができて好ましい。円偏光板は、例えば画像がカラー
表示になる反射型液晶表示装置の画像の色調を整える場
合などに有効に用いられ、また、反射防止の機能も有す
る。上記した位相差板の具体例としては、ポリカーボネ
ート、ポリビニルアルコール、ポリスチレン、ポリメチ
ルメタクリレート、ポリプロピレンやその他のポリオレ
フィン、ポリアリレート、ポリアミドの如き適宜なポリ
マーからなるフイルムを延伸処理してなる複屈折性フイ
ルムや液晶ポリマーの配向フイルム、液晶ポリマーの配
向層をフイルムにて支持したものなどがあげられる。位
相差板は、例えば各種波長板や液晶層の複屈折による着
色や視角等の補償を目的としたものなどの使用目的に応
じた適宜な位相差を有するものであってよく、２種以上
の位相差板を積層して位相差等の光学特性を制御したも
のなどであってもよい。The elliptically polarizing plate compensates (prevents) the coloring (blue or yellow) caused by the birefringence of the liquid crystal layer of the Spartist Nematic (STN) type liquid crystal display device, and is used for a monochrome display without the coloring. Used effectively. Further, the one in which the three-dimensional refractive index is controlled is preferable because coloring which occurs when the screen of the liquid crystal display device is viewed from an oblique direction can be compensated (prevented). The circularly polarizing plate is effectively used, for example, when adjusting the color tone of an image of a reflection type liquid crystal display device for displaying an image in color, and also has an antireflection function. Specific examples of the above retardation plate include polycarbonate, polyvinyl alcohol, polystyrene, polymethyl methacrylate, polypropylene and other polyolefins, polyarylate, a birefringent film obtained by stretching a film made of an appropriate polymer such as polyamide. And an alignment film of a liquid crystal polymer, and an alignment layer of a liquid crystal polymer supported by a film. The retardation plate may have an appropriate retardation according to the purpose of use such as, for example, various wavelength plates or those intended for compensation of a viewing angle or the like due to birefringence of a liquid crystal layer, and may have two or more types. A retardation plate may be laminated to control optical characteristics such as retardation.
【００３９】また上記の楕円偏光板や反射型楕円偏光板
は、偏光板又は反射型偏光板と位相差板を適宜な組合せ
で積層したものである。かかる楕円偏光板等は、（反射
型）偏光板と位相差板の組合せとなるようにそれらを液
晶表示装置の製造過程で順次別個に積層することによっ
ても形成しうるが、前記の如く予め楕円偏光板等の光学
フイルムとしたものは、品質の安定性や積層作業性等に
優れて液晶表示装置などの製造効率を向上させうる利点
がある。The above-mentioned elliptically polarizing plate and reflection type elliptically polarizing plate are obtained by laminating a polarizing plate or a reflection type polarizing plate and a retardation plate in an appropriate combination. Such an elliptically polarizing plate or the like can also be formed by sequentially and separately laminating a (reflection type) polarizing plate and a retardation plate in a manufacturing process of a liquid crystal display device so as to form a combination. An optical film such as a polarizing plate has an advantage that it is excellent in quality stability, laminating workability, and the like, and can improve the manufacturing efficiency of a liquid crystal display device and the like.
【００４０】視角補償フイルムは、液晶表示装置の画面
を、画面に垂直でなくやや斜めの方向から見た場合で
も、画像が比較的鮮明にみえるように視野角を広げるた
めのフイルムである。このような視角補償位相差板とし
ては、例えば位相差フイルム、液晶ポリマー等の配向フ
イルムや透明基材上に液晶ポリマー等の配向層を支持し
たものなどからなる。通常の位相差板は、その面方向に
一軸に延伸された複屈折を有するポリマーフイルムが用
いられるのに対し、視角補償フイルムとして用いられる
位相差板には、面方向に二軸に延伸された複屈折を有す
るポリマーフイルムとか、面方向に一軸に延伸され厚さ
方向にも延伸された厚さ方向の屈折率を制御した複屈折
を有するポリマーや傾斜配向フイルムのような二方向延
伸フイルムなどが用いられる。傾斜配向フイルムとして
は、例えばポリマーフイルムに熱収縮フイルムを接着し
て加熱によるその収縮力の作用下にポリマーフイルムを
延伸処理又は／及び収縮処理したものや、液晶ポリマー
を斜め配向させたものなどが挙げられる。位相差板の素
材原料ポリマーは、先の位相差板で説明したポリマーと
同様のものが用いられ、液晶セルによる位相差に基づく
視認角の変化による着色等の防止や良視認の視野角の拡
大などを目的とした適宜なものを用いうる。The viewing angle compensating film is a film for widening the viewing angle so that an image can be seen relatively clearly even when the screen of the liquid crystal display device is viewed not obliquely but perpendicularly to the screen. Such a viewing angle compensating retardation plate includes, for example, a retardation film, an alignment film such as a liquid crystal polymer, and a transparent substrate on which an alignment layer such as a liquid crystal polymer is supported. The ordinary retardation plate is a polymer film having birefringence uniaxially stretched in the plane direction, whereas the retardation plate used as a viewing angle compensation film is biaxially stretched in the plane direction. Polymer films having birefringence, biaxially stretched films such as uniaxially stretched in the plane direction and birefringent polymers in which the refractive index in the thickness direction is also stretched in the thickness direction and controlled in the thickness direction, etc. Used. Examples of the obliquely oriented film include a film obtained by bonding a heat shrinkable film to a polymer film and subjecting the polymer film to a stretching treatment and / or a shrinking treatment under the action of the shrinking force by heating, or a film obtained by obliquely aligning a liquid crystal polymer. No. As the raw material polymer of the retardation plate, the same polymer as that described in the above retardation plate is used. Prevention of coloring due to a change in the viewing angle based on the phase difference by the liquid crystal cell and expansion of the viewing angle for good visibility. Any suitable one for the purpose can be used.
【００４１】また、良視認の広い視野角を達成する点な
どより、液晶ポリマーの配向層、特にディスコティック
液晶ポリマーの傾斜配向層からなる光学的異方性層をト
リアセチルセルロースフイルムにて支持した光学補償位
相差板が好ましく用いうる。In order to achieve a wide viewing angle with good visibility, an optically anisotropic layer composed of a liquid crystal polymer alignment layer, particularly a tilted alignment layer of a discotic liquid crystal polymer, was supported by a triacetyl cellulose film. An optical compensation retardation plate can be preferably used.
【００４２】偏光板と輝度向上フイルムを貼り合わせた
偏光板は、通常液晶セルの裏側サイドに設けられて使用
される。輝度向上フイルムは、液晶表示装置などのバッ
クライトや裏側からの反射などにより自然光が入射する
と所定偏光軸の直線偏光または所定方向の円偏光を反射
し、他の光は透過する特性を示すもので、輝度向上フイ
ルムを偏光板と積層した偏光板は、バックライト等の光
源からの光を入射させて所定偏光状態の透過光を得ると
共に、前記所定偏光状態以外の光は透過せずに反射され
る。この輝度向上フイルム面で反射した光を更にその後
ろ側に設けられた反射層等を介し反転させて輝度向上フ
イルムに再入射させ、その一部又は全部を所定偏光状態
の光として透過させて輝度向上フイルムを透過する光の
増量を図ると共に、偏光子に吸収させにくい偏光を供給
して液晶表示画像表示等に利用しうる光量の増大を図る
ことにより輝度を向上させうるものである。すなわち、
輝度向上フイルムを使用せずに、バックライトなどで液
晶セルの裏側から偏光子を通して光を入射した場合に
は、偏光子の偏光軸に一致していない偏光方向を有する
光は、ほとんど偏光子に吸収されてしまい、偏光子を透
過してこない。すなわち、用いた偏光子の特性によって
も異なるが、およそ５０％の光が偏光子に吸収されてし
まい、その分、液晶画像表示当に利用しうる光量が減少
し、画像が暗くなる。輝度向上フイルムは、偏光子に吸
収されるような偏光方向を有する光を偏光子に入射させ
ずに 輝度向上フイルムで一旦反射させ、更にその後ろ
側に設けられた反射層等を介して反転させて輝度向 上
を板に再入射させることを繰り返し、この両者間で反
射、反転している光の偏光方向が偏光子を通過し得るよ
うな偏光方向になった偏光のみを．輝度向上フイルムは
透過させて偏光子に吸収するので、バックライトなどの
光を効率的に液晶表示装置の画像の表示に使用でき、画
面を明るくすることができる。A polarizing plate obtained by bonding a polarizing plate and a brightness enhancement film is usually provided on the back side of a liquid crystal cell and used. The brightness enhancement film reflects linearly polarized light of a predetermined polarization axis or circularly polarized light of a predetermined direction when natural light is incident due to reflection from a backlight or a back side of a liquid crystal display device, and has a property of transmitting other light. A polarizing plate obtained by laminating a brightness enhancement film and a polarizing plate, while receiving light from a light source such as a backlight to obtain transmitted light of a predetermined polarization state, light other than the predetermined polarization state is reflected without transmitting. You. The light reflected on the surface of the brightness enhancement film is further inverted through a reflection layer or the like provided on the rear side thereof and re-entered on the brightness enhancement film. The brightness can be improved by increasing the amount of light transmitted through the enhancement film and by increasing the amount of light that can be used for liquid crystal display image display by supplying polarized light that is hardly absorbed by the polarizer. That is,
When light is incident from the back side of a liquid crystal cell through a polarizer with a backlight or the like without using a brightness enhancement film, light having a polarization direction that does not coincide with the polarization axis of the polarizer is hardly applied to the polarizer. It is absorbed and does not pass through the polarizer. That is, although it depends on the characteristics of the polarizer used, about 50% of the light is absorbed by the polarizer, and accordingly, the amount of light that can be used for displaying a liquid crystal image is reduced, and the image becomes dark. The brightness enhancement film is such that light having a polarization direction that is absorbed by the polarizer is once reflected by the brightness enhancement film without being incident on the polarizer, and further inverted through a reflection layer or the like provided on the rear side. The light is repeatedly incident on the plate to improve the brightness, and only the polarized light whose polarization direction has been changed so that the polarization direction of the light reflected and inverted between the two can pass through the polarizer. Since the brightness enhancement film is transmitted and absorbed by the polarizer, light from a backlight or the like can be efficiently used for displaying an image on the liquid crystal display device, and the screen can be brightened.
【００４３】前記の輝度向上フイルムとしては、例えば
誘電体の多層薄膜や屈折率異方性が相違する薄膜フイル
ムの多層積層体の如き、所定偏光軸の直線偏光を透過し
て他の光は反射する特性を示すもの、コレステリック液
晶ポリマーの配向フイルムやその配向液晶層をフイルム
基材上に支持したものの如き、左回り又は右回りのいず
れか一方の円偏光を反射して他の光は透過する特性を示
すものなどの適宜なものを用いうる。As the above-mentioned brightness improving film, for example, a multilayer thin film of a dielectric or a multilayer laminate of thin films having different refractive index anisotropy transmits linearly polarized light having a predetermined polarization axis and reflects other light. Reflecting one of the left-handed or right-handed circularly polarized light and transmitting the other light, such as those exhibiting the characteristic of cholesteric liquid crystal polymer or those having the oriented liquid crystal layer supported on a film substrate Appropriate materials such as those exhibiting characteristics can be used.
【００４４】従って、前記した所定偏光軸の直線偏光を
透過させるタイプの輝度向上フイルムでは、その透過光
をそのまま偏光板に偏光軸を揃えて入射させることによ
り、偏光板による吸収ロスを抑制しつつ効率よく透過さ
せることができる。一方、コレステリック液晶層の如く
円偏光を投下するタイプの輝度向上フイルムでは、その
まま偏光子に入射させることもできるが、吸収ロスを抑
制する点よりその円偏光を位相差板を介し直線偏光化し
て偏光板に入射させることが好ましい。なお、その位相
差板として１／４波長板を用いることにより、円偏光を
直線偏光に変換することができる。Therefore, in the brightness enhancement film of the type that transmits linearly polarized light having a predetermined polarization axis, the transmitted light is incident on the polarization plate with the polarization axis aligned as it is, thereby suppressing absorption loss by the polarization plate. It can be transmitted efficiently. On the other hand, in a brightness enhancement film of the type that emits circularly polarized light, such as a cholesteric liquid crystal layer, it can be directly incident on a polarizer, but from the viewpoint of suppressing absorption loss, the circularly polarized light is linearly polarized through a phase difference plate. It is preferable that the light is incident on a polarizing plate. By using a quarter-wave plate as the retardation plate, circularly polarized light can be converted to linearly polarized light.
【００４５】可視光域等の広い波長範囲で１／４波長板
として機能する位相差板は、例えば波長５５０ｎｍの淡
色光に対して１／４波長板として機能する位相差層と他
の位相差特性を示す位相差層、例えば１／２波長板とし
て機能する位相差層とを重畳する方式などにより得るこ
とができる。従って、偏光板と輝度向上フイルムの間に
配置する位相差板は、１層又は２層以上の位相差層から
なるものであってよい。A retardation plate that functions as a quarter-wave plate in a wide wavelength range such as a visible light region is, for example, a retardation layer that functions as a quarter-wave plate for light-color light having a wavelength of 550 nm and another retardation layer It can be obtained by a method of superimposing a retardation layer exhibiting characteristics, for example, a retardation layer functioning as a half-wave plate. Therefore, the retardation plate disposed between the polarizing plate and the brightness enhancement film may be composed of one or more retardation layers.
【００４６】なお、コレステリック液晶層についても、
反射波長が相違するものの組み合わせにして２層又は３
層以上重畳した配置構造とすることにより、可視光領域
等の広い波長範囲で円偏光を反射するものを得ることが
でき、それに基づいて広い波長範囲の透過円偏光を得る
ことができる。Note that the cholesteric liquid crystal layer is also
Two layers or three layers in combination with different reflection wavelengths
By adopting an arrangement structure in which layers are superimposed, it is possible to obtain circularly polarized light in a wide wavelength range such as a visible light region, and to obtain transmitted circularly polarized light in a wide wavelength range based on the reflected light.
【００４７】また、偏光板は、上記の偏光分離型偏光板
の如く、偏光板と２層又は３層以上の光学層とを積層し
たものからなっていてもよい。従って、上記の反射型偏
光板や半透過型偏光板と位相差板を組み合わせた反射型
楕円偏光板や半透過型楕円偏光板などであってもよい。Further, the polarizing plate may be formed by laminating a polarizing plate and two or three or more optical layers as in the above-mentioned polarized light separating type polarizing plate. Therefore, a reflective elliptically polarizing plate or a transflective elliptically polarizing plate obtained by combining the above-mentioned reflective polarizing plate, transflective polarizing plate and retardation plate may be used.
【００４８】偏光板に前記光学層を積層した光学フィル
ムは、液晶表示装置等の製造過程で順次別個に積層する
方式にても形成することができるが、予め積層して光学
フィルムとしたのものは、品質の安定性や組立作業等に
優れていて液晶表示装置などの製造工程を向上させうる
利点がある。積層には粘着層等の適宜な接着手段を用い
うる。前記の偏光板やその他の光学フィルムの接着に際
し、それらの光学軸は目的とする位相差特性などに応じ
て適宜な配置角度とすることができる。An optical film in which the optical layer is laminated on a polarizing plate can be formed by a method in which the optical film is laminated in advance in the process of manufacturing a liquid crystal display device or the like. Has an advantage that it is excellent in quality stability, assembling work, and the like, and can improve a manufacturing process of a liquid crystal display device or the like. Appropriate bonding means such as an adhesive layer can be used for lamination. When bonding the above-mentioned polarizing plate or other optical films, their optical axes can be arranged at an appropriate angle depending on the intended retardation characteristics and the like.
【００４９】前述した偏光板や、偏光板を少なくとも１
層積層されている光学フイルムには、液晶セル等の他部
材と接着するための粘着層を設けることもできる。粘着
層を形成する粘着剤は特に制限されないが、例えばアク
リル系重合体、シリコーン系ポリマー、ポリエステル、
ポリウレタン、ポリアミド、ポリエーテル、フッ素系や
ゴム系などのポリマーをベースポリマーとするものを適
宜に選択して用いることができる。特に、アクリル系粘
着剤の如く光学的透明性に優れ、適度な濡れ性と凝集性
と接着性の粘着特性を示して、耐候性や耐熱性などに優
れるものが好ましく用いうる。The above-described polarizing plate or at least one polarizing plate
The laminated optical film may be provided with an adhesive layer for bonding to another member such as a liquid crystal cell. The pressure-sensitive adhesive forming the pressure-sensitive adhesive layer is not particularly limited, for example, an acrylic polymer, a silicone-based polymer, a polyester,
Polyurethane, polyamide, polyether, and those based on polymers such as fluorine-based and rubber-based polymers can be appropriately selected and used. In particular, an acrylic adhesive having excellent optical transparency, exhibiting appropriate wettability, cohesiveness and adhesive adhesive properties, and having excellent weather resistance and heat resistance can be preferably used.
【００５０】また上記に加えて、吸湿による発泡現象や
剥がれ現象の防止、熱膨張差等による光学特性の低下や
液晶セルの反り防止、ひいては高品質で耐久性に優れる
液晶表示装置の形成性などの点より、吸湿率が低くて耐
熱性に優れる粘着層が好ましい。In addition to the above, prevention of foaming and peeling phenomena due to moisture absorption, deterioration of optical characteristics due to difference in thermal expansion and prevention of liquid crystal cell warpage, and formation of a liquid crystal display device having high quality and excellent durability. In view of the above, an adhesive layer having a low moisture absorption rate and excellent heat resistance is preferable.
【００５１】粘着層は、例えば天然物や合成物の樹脂
類、特に、粘着性付与樹脂や、ガラス繊維、ガラスビー
ズ、金属粉、その他の無機粉末等からなる充填剤や顔
料、着色剤、酸化防止剤などの粘着層に添加されること
の添加剤を含有していてもよい。また微粒子を含有して
光拡散性を示す粘着層などであってもよい。The adhesive layer is made of, for example, a natural or synthetic resin, in particular, a tackifier resin, or a filler, a pigment, a colorant, an oxidant, a glass fiber, glass beads, metal powder, or other inorganic powder. It may contain an additive such as an inhibitor added to the adhesive layer. Further, an adhesive layer containing fine particles and exhibiting light diffusibility may be used.
【００５２】偏光板や光学フィルムの片面又は両面への
粘着層の付設は、適宜な方式で行いうる。その例として
は、例えばトルエンや酢酸エチル等の適宜な溶剤の単独
物又は混合物からなる溶媒にベースポリマーまたはその
組成物を溶解又は分散させた１０〜４０重量％程度の粘
着剤溶液を調製し、それを流延方式や塗工方式等の適宜
な展開方式で偏光板上または光学フィルム上に直接付設
する方式、あるいは前記に準じセパレータ上に粘着層を
形成してそれを偏光板上または光学フィルム上に移着す
る方式などがあげられる。The attachment of the adhesive layer to one or both sides of the polarizing plate or the optical film can be performed by an appropriate method. As an example, an adhesive solution of about 10 to 40% by weight is prepared by dissolving or dispersing a base polymer or a composition thereof in a solvent composed of a single substance or a mixture of appropriate solvents such as toluene and ethyl acetate. A method of directly attaching it on a polarizing plate or an optical film by an appropriate developing method such as a casting method or a coating method, or forming an adhesive layer on a separator according to the above and forming it on a polarizing plate or an optical film. There is a method of transferring to the top.
【００５３】粘着層は、異なる組成又は種類等のものの
重畳層として偏光板や光学フィルムの片面又は両面に設
けることもできる。また両面に設ける場合に、偏光板や
光学フィルムの表裏において異なる組成や種類や厚さ等
の粘着層とすることもできる。粘着層の厚さは、使用目
的や接着力などに応じて適宜に決定でき、一般には１〜
５００μｍであり、５〜２００μｍが好ましく、特に１
０〜１００μｍが好ましい。The adhesive layer may be provided on one or both sides of a polarizing plate or an optical film as a superposed layer of different compositions or types. When provided on both surfaces, it is also possible to form an adhesive layer having a different composition, type and thickness on the front and back of the polarizing plate or the optical film. The thickness of the pressure-sensitive adhesive layer can be appropriately determined depending on the purpose of use, adhesive strength, and the like.
500 μm, preferably 5 to 200 μm, particularly preferably 1 to 200 μm.
0-100 μm is preferred.
【００５４】粘着層の露出面に対しては、実用に供する
までの間、その汚染防止等を目的にセパレータが仮着さ
れてカバーされる。これにより、通例の取扱状態で粘着
層に接触することを防止できる。セパレータとしては、
上記厚さ条件を除き、例えばプラスチックフイルム、ゴ
ムシート、紙、布、不織布、ネット、発泡シートや金属
箔、それらのラミネート体等の適宜な薄葉体を、必要に
応じシリコーン系や長鏡アルキル系、フッ素系や硫化モ
リブデン等の適宜な剥離剤でコート処理したものなど
の、従来に準じた適宜なものを用いうる。A separator is temporarily attached to the exposed surface of the pressure-sensitive adhesive layer for the purpose of preventing its contamination and the like until it is practically used, and is covered. Thus, it is possible to prevent the adhesive layer from coming into contact with the adhesive layer in a normal handling state. As a separator,
Except for the above thickness conditions, for example, a suitable thin leaf such as a plastic film, rubber sheet, paper, cloth, non-woven fabric, net, foam sheet or metal foil, or a laminate thereof may be replaced with a silicone-based or long-mirror alkyl-based as required. An appropriate material according to the related art, such as one coated with an appropriate release agent such as fluorine or molybdenum sulfide, may be used.
【００５５】なお本発明において、上記した偏光板を形
成する偏光子や透明保護フイルムや光学フイルム等、ま
た粘着層などの各層には、例えばサリチル酸エステル系
化合物やべンゾフェノール系化合物、ベンゾトリアゾー
ル系化合物やシアノアクリレート系化合物、ニッケル錯
塩系化合物等の紫外線吸収剤で処理する方式などの方式
により紫外線吸収能をもたせたものなどであってもよ
い。In the present invention, each layer such as a polarizer, a transparent protective film, an optical film, etc., which forms the above-mentioned polarizing plate, and an adhesive layer, for example, may be provided with a salicylate compound, a benzophenol compound, a benzotriazole compound, etc. And those having an ultraviolet absorbing ability by a method such as a method of treating with an ultraviolet absorber such as a cyanoacrylate compound or a nickel complex compound.
【００５６】本発明の偏光板または光学フイルムは液晶
表示装置等の各種装置の形成などに好ましく用いること
ができる。液晶表示装置の形成は、従来に準じて行いう
る。すなわち液晶表示装置は一般に、液晶セルと偏光板
または光学フイルム、及び必要に応じての照明システム
等の構成部品を適宜に紬立てて駆動回路を組込むことな
どにより形成されるが、本発明においては本発明による
偏光板または光学フイルムを用いる点を除いて特に限定
はなく、従来に準じうる。液晶セルについても、例えば
ＴＮ型やＳＴＮ型、π型などの任意なタイプのものを用
いうる。The polarizing plate or optical film of the present invention can be preferably used for forming various devices such as a liquid crystal display device. The formation of the liquid crystal display device can be performed according to a conventional method. That is, a liquid crystal display device is generally formed by appropriately setting up components such as a liquid crystal cell and a polarizing plate or an optical film, and an illumination system as needed, and incorporating a drive circuit. There is no particular limitation except that a polarizing plate or an optical film according to the present invention is used, and it can be in accordance with the conventional one. As for the liquid crystal cell, any type such as TN type, STN type and π type can be used.
【００５７】液晶セルの片側又は両側に偏光板または光
学フィルムを配置した液晶表示装置や、照明システムに
バックライトあるいは反射板を用いたものなどの適宜な
液晶表示装置を形成することができる。その場合、本発
明による偏光板または光学フイルムは液晶セルの片側又
は両側に設置することができる。両側に偏光板または光
学フイルムを設ける場合、それらは同じものであっても
よいし、異なるものであってもよい。さらに、液晶表示
装置の形成に際しては、例えば拡散板、アンチグレア
層、反射防止膜、保護板、プリズムアレイ、レンズアレ
イシート、光拡散板、バックライトなどの適宜な部品を
適宜な位置に１層又は２層以上配置することができる。An appropriate liquid crystal display device such as a liquid crystal display device in which a polarizing plate or an optical film is disposed on one or both sides of a liquid crystal cell, or a device using a backlight or a reflector for an illumination system can be formed. In that case, the polarizing plate or the optical film according to the present invention can be installed on one side or both sides of the liquid crystal cell. When polarizing plates or optical films are provided on both sides, they may be the same or different. Further, when forming the liquid crystal display device, for example, a suitable component such as a diffusion plate, an anti-glare layer, an antireflection film, a protection plate, a prism array, a lens array sheet, a light diffusion plate, a backlight, etc. Two or more layers can be arranged.
【００５８】[0058]
【実施例】以下、本発明の構成と効果を具体的に示す実
施例等について説明する。なお、各例中、部および％は
重量基準である。DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments and the like specifically showing the configuration and effects of the present invention will be described below. In addition, in each example, parts and% are based on weight.
【００５９】実施例１ （偏光子の調製）厚さ８０μｍのポリビニルアルコール
フイルムを０．３％のヨウ素水溶液中で染色した後、４
％のホウ酸水溶液、２％のヨウ化カリウム水溶液中で５
倍まで延伸し、次いで５０℃で４分間乾燥させて偏光子
を得た。Example 1 (Preparation of Polarizer) A polyvinyl alcohol film having a thickness of 80 μm was dyed in a 0.3% aqueous solution of iodine.
5% aqueous boric acid solution and 5% aqueous 2% potassium iodide solution.
The film was stretched up to 2 times and then dried at 50 ° C. for 4 minutes to obtain a polarizer.
【００６０】（透明保護フイルムの調製）厚さ８０μｍ
のトリアセチルセルロースフイルム（以下、ＴＡＣフイ
ルムという）の片面に、ゼラチン１部、サリチル酸１
部、水１０部、メタノール３０部およびアセトン６０部
からなるゼラチン分散液を塗布し、乾燥してゼラチン系
塗布層を形成した。乾燥後のゼラチン系塗布層の厚さは
０．３μｍであった。(Preparation of Transparent Protective Film) Thickness 80 μm
On one side of a triacetyl cellulose film (hereinafter referred to as TAC film)
, 10 parts of water, 30 parts of methanol, and 60 parts of acetone, were coated and dried to form a gelatin-based coating layer. The thickness of the gelatin-based coating layer after drying was 0.3 μm.
【００６１】（偏光板の作成）前記透明保護フイルムの
ゼラチン系塗布層に、ポリビニルアルコール４部、メラ
ミン１部および水１００部からなるポリビニルアルコー
ル系接着剤を塗布した後、偏光子の両面にロールラミネ
ーターを用いて貼りあわせ、６０℃で４分間乾燥乾する
ことで偏光板を得た。接着剤層の厚みは０．１μｍであ
った。(Preparation of Polarizing Plate) A polyvinyl alcohol-based adhesive consisting of 4 parts of polyvinyl alcohol, 1 part of melamine and 100 parts of water was applied to the gelatin-based coating layer of the transparent protective film, and then rolled on both surfaces of the polarizer. The sheets were bonded using a laminator and dried at 60 ° C. for 4 minutes to obtain a polarizing plate. The thickness of the adhesive layer was 0.1 μm.
【００６２】実施例２ 実施例１の（偏光板の作成）において、ポリビニルアル
コール系接着剤の代わりに、ゼラチン５部、ホルムアル
デヒド２部および水１００部からなるゼラチン系接着剤
を用い、またゼラチン系接着剤を４０℃で塗布してか
ら、２０℃に冷却してゼラチン系接着剤をゲル化した後
に、偏光子の両面に貼りあわせたこと以外は実施例１の
（偏光板の作成）に準じて偏光板を作成した。Example 2 In Example 1 (Preparation of Polarizing Plate), instead of the polyvinyl alcohol-based adhesive, a gelatin-based adhesive consisting of 5 parts of gelatin, 2 parts of formaldehyde and 100 parts of water was used. An adhesive was applied at 40 ° C. and then cooled to 20 ° C. to gel the gelatin-based adhesive, and then adhered to both surfaces of the polarizer, according to Example 1 (Preparation of Polarizing Plate). To produce a polarizing plate.
【００６３】比較例１ 実施例１の（偏光板の作成）において、前記透明保護フ
イルムとしてゼラチン系塗布層を設けていないＴＡＣフ
イルムを用いたこと以外は実施例１の（偏光板の作成）
に準じて偏光板を作成した。Comparative Example 1 (Preparation of Polarizing Plate) Except that a TAC film having no gelatin coating layer was used as the transparent protective film in (Preparation of Polarizing Plate) in Example 1.
A polarizing plate was prepared in accordance with
【００６４】比較例２ 実施例１の（偏光板の作成）において、前記透明保護フ
イルムとしてゼラチン系塗布層を設けていないＴＡＣフ
イルムを用い、ポリビニルアルコール系接着剤の代わり
に、ゼラチン５部、ホルムアルデヒド２部および水１０
０部からなるゼラチン系接着剤を用い、またゼラチン系
接着剤を４０℃で塗布してから、２０℃に冷却してゼラ
チン系接着剤をゲル化した後に、偏光子の両面に貼りあ
わせたこと以外は実施例１の（偏光板の作成）に準じて
偏光板を作成した。Comparative Example 2 In Example 1 (Preparation of Polarizing Plate), a TAC film having no gelatin-based coating layer was used as the transparent protective film, and instead of the polyvinyl alcohol-based adhesive, 5 parts of gelatin and formaldehyde were used. 2 parts and water 10
Using a gelatin adhesive consisting of 0 parts, applying the gelatin adhesive at 40 ° C., cooling the gelatin adhesive to 20 ° C., gelling the gelatin adhesive, and then bonding the polarizer to both surfaces. Except for the above, a polarizing plate was prepared according to (Preparation of Polarizing Plate) of Example 1.
【００６５】参考例１ 実施例１の（偏光板の作成）において、透明保護フイル
ムとして、ＴＡＣフイルムを５０℃の７％の水酸化カリ
ウム水溶液に３分間浸漬した後に水洗して乾燥したもの
を用いたこと以外は実施例１の（偏光板の作成）に準じ
て偏光板を作成した。Reference Example 1 In Example 1, (Preparation of Polarizing Plate), a transparent protective film obtained by immersing a TAC film in a 7% aqueous solution of potassium hydroxide at 50 ° C. for 3 minutes, followed by washing with water and drying was used. A polarizing plate was prepared in the same manner as in Example 1 (Preparation of Polarizing Plate) except that it was not used.
【００６６】参考例２ 実施例１の（偏光板の作成）において、透明保護フイル
ムとして、ＴＡＣフイルムを５０℃の７％の水酸化カリ
ウム水溶液に1 分間浸漬した後に水洗して乾燥したもの
を用いたこと以外は実施例１の（偏光板の作成）に準じ
て偏光板を作成した。Reference Example 2 In Example 1, (Preparation of Polarizing Plate), a TAC film, which was immersed in a 7% aqueous potassium hydroxide solution at 50 ° C. for 1 minute, washed with water, and dried, was used as a transparent protective film. A polarizing plate was prepared in the same manner as in Example 1 (Preparation of Polarizing Plate) except that it was not used.
【００６７】（接着力）実施例および比較例で得られた
偏光板を２５ｍｍ巾に切断したものについて、引っ張り
試験機を用いて引っ張り速度３００ｍｍ／ｍｉｎ、常温
（２５℃）、剥離角１８０°で偏光板からＴＡＣフイル
ムを剥離した。このとき、接着が強く、ＴＡＣフイルム
が剥離せずに破断したものは「破断」とした。結果を表
１に示す。(Adhesive force) The polarizing plates obtained in Examples and Comparative Examples were cut to a width of 25 mm, using a tensile tester at a pulling speed of 300 mm / min, a normal temperature (25 ° C.), and a peel angle of 180 °. The TAC film was peeled from the polarizing plate. At this time, the TAC film which was strongly adhered and broke without peeling was regarded as "broken". Table 1 shows the results.
【００６８】[0068]
【表１】 表１より透明保護フィルムにゼラチン系塗布層を設けた
偏光板は、アルカリ処理を施したものと同様に接着強度
が十分高いことが認められる。[Table 1] From Table 1, it can be seen that the polarizing plate in which the gelatin-based coating layer was provided on the transparent protective film had sufficiently high adhesive strength as in the case of the alkali-treated polarizing plate.
【図１】本発明の偏光板である。FIG. 1 is a polarizing plate of the present invention.
１ 偏光子 ２ 接着層 ３ 透明保護フイルム ａ ゼラチン系塗布層 DESCRIPTION OF SYMBOLS 1 Polarizer 2 Adhesive layer 3 Transparent protective film a Gelatin type coating layer
【手続補正書】[Procedure amendment]
【提出日】平成１４年５月２８日（２００２．５．２
８）[Submission Date] May 28, 2002 (2002.5.2)
8)
【手続補正１】[Procedure amendment 1]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００３６[Correction target item name] 0036
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００３６】なお、半透過型偏光板は、上記において反
射層で光を反射し、かつ透過するハーフミラー等の半透
過型の反射層とすることにより得ることができる。半透
過型偏光板は、通常液晶セルの裏側に設けられ、液晶表
示装置などを比較的明るい雰囲気で使用する場合には、
視認側（表示側）からの入射光を反射させて画像を表示
し、比較的暗い雰囲気においては、半透過型偏光板のバ
ックサイドに内蔵されているバックライト等の内蔵光源
を使用して画像を表示するタイプの液晶表示装置などを
形成できる。すなわち、半透過型偏光板は、明るい雰囲
気下では、バックライト等の光源使用のエネルギーを節
約でき、比較的暗い雰囲気下においても内蔵光源を用い
て使用できるタイプの液晶表示装置などの形成に有用で
ある。The transflective polarizing plate can be obtained by forming a transflective reflective layer such as a half mirror that reflects and transmits light on the reflective layer. The transflective polarizing plate is usually provided on the back side of the liquid crystal cell, and when a liquid crystal display device or the like is used in a relatively bright atmosphere,
An image is displayed by reflecting the incident light from the viewing side (display side). In a relatively dark atmosphere, the image is displayed using a built-in light source such as a backlight built in the back side of the transflective polarizing plate. A liquid crystal display device or the like of a type that displays the information can be formed. That is, the transflective polarizing plate can save energy for use of a light source such as a backlight in a bright atmosphere and is useful for forming a liquid crystal display device of a type that can be used with a built-in light source even in a relatively dark atmosphere. It is.
【手続補正２】[Procedure amendment 2]
【補正対象書類名】明細書[Document name to be amended] Statement
【補正対象項目名】００４２[Correction target item name] 0042
【補正方法】変更[Correction method] Change
【補正内容】[Correction contents]
【００４２】偏光板と輝度向上フイルムを貼り合わせた
偏光板は、通常液晶セルの裏側サイドに設けられて使用
される。輝度向上フイルムは、液晶表示装置などのバッ
クライトや裏側からの反射などにより自然光が入射する
と所定偏光軸の直線偏光または所定方向の円偏光を反射
し、他の光は透過する特性を示すもので、輝度向上フイ
ルムを偏光板と積層した偏光板は、バックライト等の光
源からの光を入射させて所定偏光状態の透過光を得ると
共に、前記所定偏光状態以外の光は透過せずに反射され
る。この輝度向上フイルム面で反射した光を更にその後
ろ側に設けられた反射層等を介し反転させて輝度向上フ
イルムに再入射させ、その一部又は全部を所定偏光状態
の光として透過させて輝度向上フイルムを透過する光の
増量を図ると共に、偏光子に吸収させにくい偏光を供給
して液晶表示画像表示等に利用しうる光量の増大を図る
ことにより輝度を向上させうるものである。すなわち、
輝度向上フイルムを使用せずに、バックライトなどで液
晶セルの裏側から偏光子を通して光を入射した場合に
は、偏光子の偏光軸に一致していない偏光方向を有する
光は、ほとんど偏光子に吸収されてしまい、偏光子を透
過してこない。すなわち、用いた偏光子の特性によって
も異なるが、およそ５０％の光が偏光子に吸収されてし
まい、その分、液晶画像表示等に利用しうる光量が減少
し、画像が暗くなる。輝度向上フイルムは、偏光子に吸
収されるような偏光方向を有する光を偏光子に入射させ
ずに輝度向上フイルムで一旦反射させ、更にその後ろ側
に設けられた反射層等を介して反転させて輝度向上フイ
ルムに再入射させることを繰り返し、この両者間で反
射、反転している光の偏光方向が偏光子を通過し得るよ
うな偏光方向になった偏光のみを、輝度向上フイルムは
透過させて偏光子に供給するので、バックライトなどの
光を効率的に液晶表示装置の画像の表示に使用でき、画
面を明るくすることができる。A polarizing plate obtained by bonding a polarizing plate and a brightness enhancement film is usually provided on the back side of a liquid crystal cell and used. The brightness enhancement film reflects linearly polarized light of a predetermined polarization axis or circularly polarized light of a predetermined direction when natural light is incident due to reflection from a backlight or a back side of a liquid crystal display device, and has a property of transmitting other light. A polarizing plate obtained by laminating a brightness enhancement film and a polarizing plate, while receiving light from a light source such as a backlight to obtain transmitted light of a predetermined polarization state, light other than the predetermined polarization state is reflected without transmitting. You. The light reflected on the surface of the brightness enhancement film is further inverted through a reflection layer or the like provided on the rear side thereof and re-entered on the brightness enhancement film. The brightness can be improved by increasing the amount of light transmitted through the enhancement film and by increasing the amount of light that can be used for liquid crystal display image display by supplying polarized light that is hardly absorbed by the polarizer. That is,
When light is incident from the back side of a liquid crystal cell through a polarizer with a backlight or the like without using a brightness enhancement film, light having a polarization direction that does not coincide with the polarization axis of the polarizer is hardly applied to the polarizer. It is absorbed and does not pass through the polarizer. That is, although it depends on the characteristics of the polarizer used, about 50% of the light is absorbed by the polarizer, and accordingly, the amount of light available for liquid crystal image display and the like is reduced, and the image becomes dark. The brightness enhancement film is such that light having a polarization direction that is absorbed by the polarizer is once reflected by the brightness enhancement film without being incident on the polarizer, and further inverted through a reflection layer or the like provided on the rear side thereof. Repeatedly re-entering the brightness enhancement film, the brightness enhancement film transmits only the polarized light whose polarization direction is reflected and inverted between the two so that it can pass through the polarizer. Since light is supplied to the polarizer, light from a backlight or the like can be efficiently used for displaying an image on the liquid crystal display device, and the screen can be brightened.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 正田 位守 大阪府茨木市下穂積１丁目１番２号 日東 電工株式会社内 (72)発明者 藤村 保夫 大阪府茨木市下穂積１丁目１番２号 日東 電工株式会社内 (72)発明者 長塚 辰樹 大阪府茨木市下穂積１丁目１番２号 日東 電工株式会社内 (72)発明者 三原 尚史 大阪府茨木市下穂積１丁目１番２号 日東 電工株式会社内 Ｆターム(参考） 2H049 BA02 BA27 BB18 BB33 BB43 BB51 BC03 BC14 BC22 2H091 FA08X FA08Y FB02 GA16 GA17 LA02 4J040 BA161 DD011 DN001 ED001 EF001 JA01 KA16 MA09 MA11 ──────────────────────────────────────────────────続 き Continuing from the front page (72) Inventor: Masami Masada 1-1-1, Shimohozumi, Ibaraki-shi, Osaka Nitto Denko Corporation (72) Inventor: Yasuo Fujimura 1-2-1, Shimohozumi, Ibaraki-shi, Osaka No. Nitto Denko Corporation (72) Inventor Tatsuki Nagatsuka 1-1-2 Shimohozumi, Ibaraki-shi, Osaka Nitto Denko Corporation (72) Inventor Naofumi Mihara 1-1-2 Shimohozumi, Ibaraki-shi, Osaka Nitto F-term (Reference) 2H049 BA02 BA27 BB18 BB33 BB43 BB51 BC03 BC14 BC22 2H091 FA08X FA08Y FB02 GA16 GA17 LA02 4J040 BA161 DD011 DN001 ED001 EF001 JA01 KA16 MA09 MA11
Claims (9)
介して透明保護フイルムが設けられている偏光板におい
て、前記透明保護フイルムの偏光子と接着する面に、ゼ
ラチン系塗布層が形成されていることを特徴とする偏光
板。1. A polarizing plate having a transparent protective film provided on at least one surface of a polarizer via an adhesive layer, wherein a gelatin-based coating layer is formed on a surface of the transparent protective film that adheres to the polarizer. A polarizing plate, characterized in that:
材料を溶解しうる溶剤を分散媒として含有するゼラチン
分散液により形成されたものであることを特徴とする請
求項１記載の偏光板。2. The polarizing plate according to claim 1, wherein the gelatin-based coating layer is formed by a gelatin dispersion containing a solvent capable of dissolving the transparent protective film material as a dispersion medium.
ロースフイルムであることを特徴とする請求項１または
２記載の偏光板。3. The polarizing plate according to claim 1, wherein the transparent protective film is a triacetyl cellulose film.
接着層が、ゼラチンを含有する接着剤により形成された
ものであることを特徴とする請求項１〜３のいずれかに
記載の偏光板。4. The polarizing plate according to claim 1, wherein the adhesive layer for adhering the transparent protective film and the polarizer is formed by an adhesive containing gelatin. .
接着層が、ポリビニルアルコールを含有する接着剤によ
り形成されたものであることを特徴とする請求項１〜３
のいずれかに記載の偏光板。5. An adhesive layer for bonding a transparent protective film and a polarizer, wherein the adhesive layer is formed of an adhesive containing polyvinyl alcohol.
The polarizing plate according to any one of the above.
介して透明保護フイルムが設けられている偏光板の製造
方法であって、透明保護フイルムの偏光子と接着する面
に、ゼラチン系塗布層を形成した後、接着剤を用いて透
明保護フイルムと偏光子を貼り合わせることを特徴とす
る請求項１〜５のいずれかに記載の偏光板の製造方法。6. A method for producing a polarizing plate, wherein a transparent protective film is provided on at least one surface of a polarizer via an adhesive layer, wherein a gelatin-based coating is applied to the surface of the transparent protective film that adheres to the polarizer. The method for producing a polarizing plate according to any one of claims 1 to 5, wherein after forming the layer, the transparent protective film and the polarizer are bonded together using an adhesive.
に、ゼラチン系塗布層が形成されていることを特徴とす
る請求項１〜５のいずれかに記載の偏光板に用いられる
偏光板用保護フィルム。7. A polarizing plate for use in a polarizing plate according to claim 1, wherein a gelatin-based coating layer is formed on a surface of the transparent protective film that adheres to the polarizer. Protective film.
偏光板が、少なくとも１枚積層されていることを特徴と
する光学フイルム。8. An optical film, wherein at least one polarizing plate according to claim 1 is laminated.
偏光板または請求項８記載の光学フイルムが用いられて
いることを特徴とする液晶表示装置。9. A liquid crystal display device comprising the polarizing plate according to claim 1 or the optical film according to claim 8.