JP2002322464A - Sealing composition - Google Patents
Sealing compositionInfo
- Publication number
- JP2002322464A JP2002322464A JP2001127807A JP2001127807A JP2002322464A JP 2002322464 A JP2002322464 A JP 2002322464A JP 2001127807 A JP2001127807 A JP 2001127807A JP 2001127807 A JP2001127807 A JP 2001127807A JP 2002322464 A JP2002322464 A JP 2002322464A
- Authority
- JP
- Japan
- Prior art keywords
- separate plate
- sealant composition
- automatic transmission
- control valve
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、優れたシール機能
を有する自動変速機内コントロールバルブ用セパレート
プレートを提供することができるシール剤組成物並びに
該シール剤組成物を使用した自動変速機内コントロール
バルブ用セパレートプレートに関する。The present invention relates to a sealant composition capable of providing a separate plate for a control valve in an automatic transmission having an excellent sealing function, and to a control valve in an automatic transmission using the sealant composition. Related to a separate plate.
【０００２】自動変速機内コントロールバルブ用セパレ
ートプレートのシール機構として従来から紙製のガスケ
ットが用いられ、所定のパターンに打ち抜かれた紙製ガ
スケットを金属板の表裏に接着した構成の自動変速機内
コントロールバルブ用セパレートプレートが現在で最も
広く利用されている。このような構成を有する自動変速
機内コントロールバルブ用セパレートプレートは、優れ
た耐熱性、耐油性、耐破断性、耐トルクダウン性を有す
るとされている。しかしながら、所定のパターンに打ち
抜かれた紙製ガスケットを金属板の所定の位置に正確に
接着する操作は煩雑であると共に多大な費用を要し、更
に、紙製ガスケットは湿気に対して弱いという問題点が
ある。Conventionally, a paper gasket has been used as a seal mechanism of a separate plate for a control valve in an automatic transmission, and a paper gasket punched in a predetermined pattern is bonded to the front and back of a metal plate. Separate plates are currently most widely used. The separate plate for a control valve in an automatic transmission having such a configuration is said to have excellent heat resistance, oil resistance, rupture resistance, and torque down resistance. However, the operation of accurately bonding a paper gasket punched in a predetermined pattern to a predetermined position on a metal plate is complicated and expensive, and furthermore, the paper gasket is vulnerable to moisture. There is a point.
【０００３】そこで、自動変速機内コントロールバルブ
用セパレートプレートのシール機構をゴム系弾性材、発
泡ゴム、フェノール樹脂のような熱硬化性物質の硬化層
を用いて形成することが試みられている。例えば、特許
第２６９７５６９号には、自動変速機のコントロールバ
ルブユニットのセパレートプレートとバルブボディ間を
液密状又は気密状にシールするシール構造であって、前
記バルブボディに対するセパレートプレートの合わせ面
に、バルブボディに形成した油溝や溝部側へ露出しない
ようにバルブボディの合わせ面に応じたパターンで、パ
ターン印刷によりシール層を形成したことを特徴とする
シール構造が開示されている。この特許によれば、パタ
ーン印刷として、凸版印刷、平板印刷、凹版印刷、スク
リーン印刷、植毛印刷、磁気印刷、ホットスタンピング
等が使用されることが記載されている。また、パターン
印刷に使用されるインクは、天然樹脂材料、合成樹脂材
料、合成ゴム材料などからなるインクであることも記載
されている。Accordingly, attempts have been made to form a sealing mechanism for a separate plate for a control valve in an automatic transmission using a cured layer of a thermosetting substance such as a rubber-based elastic material, foamed rubber, or phenol resin. For example, Japanese Patent No. 2697569 discloses a seal structure that seals between a separate plate and a valve body of a control valve unit of an automatic transmission in a liquid-tight or air-tight manner. There is disclosed a seal structure in which a seal layer is formed by pattern printing in a pattern corresponding to a mating surface of a valve body so as not to be exposed to an oil groove or a groove portion formed in the valve body. According to this patent, it is described that letterpress printing, lithographic printing, intaglio printing, screen printing, flocking printing, magnetic printing, hot stamping and the like are used as pattern printing. It also describes that the ink used for pattern printing is an ink made of a natural resin material, a synthetic resin material, a synthetic rubber material, or the like.
【０００４】また、特許第２９９３４４５号には、２つ
の部材間を液密状又は気密状にシールするシール構造で
あって、前記２つの部材の合わせ面の少なくとも一方
に、該合わせ面のシール部位に沿って連続的にプリント
にてシール部を形成し、前記シール部の幅方向の途中部
であって、少なくとも複数のシール部が交わる合流部に
凹部又は条溝を形成したことを特徴とするシール構造が
開示されている。この特許によれば、プリント技術とし
て、パターン印刷として、凸版印刷、平板印刷、凹版印
刷、スクリーン印刷、植毛印刷、磁気印刷、ホットスタ
ンピングなどによる印刷技術やディスペンサーによる材
料塗布技術を採用できることが記載されている。また、
シール部を構成する素材としては、例えばフッ素ゴム、
ＮＢＲゴム、ＳＢＲゴム、シリコンゴムなどの合成ゴム
材料や、エポキシ系樹脂、シリコン系樹脂、フェノール
系樹脂、ウレタン系樹脂、ポリイミド系樹脂、塩化ビニ
ル系樹脂、アクリル系樹脂、ポリウレタン系樹脂、ＡＢ
Ｓ系樹脂、ＰＴＦＥ（四フッ化エチレン）系樹脂などの
合成樹脂材料や、紫外線硬化型の合成樹脂材料や、これ
ら合成ゴム材料や合成樹脂材料にアルミニウム合金、
銅、真鍮、ステンレス等の金属粉末、ガラス粉末やガラ
ス繊維、セラミック粉末やセラミック繊維、二硫化モリ
ブデン粉末等を混入した複合材料を用いることができる
ことも開示されている。[0004] Japanese Patent No. 2993445 discloses a seal structure for sealing between two members in a liquid-tight or air-tight manner, wherein at least one of the mating surfaces of the two members has a sealing portion on the mating surface. A seal portion is formed by continuous printing along the width of the seal portion, and a concave portion or a groove is formed at a merging portion where at least a plurality of seal portions intersect at an intermediate portion in the width direction of the seal portion. A seal structure is disclosed. According to this patent, it is described that as a printing technique, it is possible to employ a printing technique such as letterpress printing, lithographic printing, intaglio printing, screen printing, flocking printing, magnetic printing, hot stamping, or a material application technique using a dispenser as pattern printing. ing. Also,
As a material constituting the seal portion, for example, fluoro rubber,
Synthetic rubber materials such as NBR rubber, SBR rubber, silicone rubber, epoxy resin, silicone resin, phenol resin, urethane resin, polyimide resin, vinyl chloride resin, acrylic resin, polyurethane resin, AB
Synthetic resin materials such as S-based resin and PTFE (tetrafluoroethylene) -based resin, ultraviolet-curable synthetic resin materials, and aluminum alloys for these synthetic rubber materials and synthetic resin materials
It is also disclosed that a composite material mixed with metal powder such as copper, brass, stainless steel, glass powder or glass fiber, ceramic powder or ceramic fiber, molybdenum disulfide powder or the like can be used.
【０００５】更に、特開平９−３０３５６２号公報に
は、２つの部材間を液密状又は気密状にシールするシー
ル構造であって、前記２つの部材の合わせ面の少なくと
も一方に、第１シール層をプリントにて形成するととも
に、第１シール層よりも軟質な素材からなり、第１シー
ル層の上側に少なくとも一部を重ね、第１シール層より
もプリント高さを高くした第２シール層を第１シール層
に沿ってプリントにて形成し、両シール層よりなるシー
ル部で２つの部材間を液密状又は気密状にシールしたシ
ール構造が開示されている。そして、プリント技術やシ
ール層の材質としては上記特許第２９９３４４５号と同
様の技術や素材を使用できることが記載されている。Further, Japanese Patent Application Laid-Open No. 9-303562 discloses a seal structure for sealing between two members in a liquid-tight or air-tight manner, wherein at least one of the mating surfaces of the two members has a first seal. A second seal layer formed by printing and made of a material softer than the first seal layer, at least partially overlapping the first seal layer, and having a print height higher than the first seal layer; Is formed by printing along a first seal layer, and a seal portion including both seal layers seals between two members in a liquid-tight or air-tight manner. It is described that the same techniques and materials as those in the above-mentioned Japanese Patent No. 2993445 can be used as the printing technique and the material of the seal layer.
【０００６】[0006]
【発明が解決しようとする課題】上記公報には、プリン
ト技術によるシール部材の形成に使用可能な素材とし
て、紫外線硬化型の合成樹脂材料が開示されているが、
具体的に該合成樹脂材料を使用した例はなく、上記公報
ではシール部材の素材としては熱硬化性のゴムや樹脂が
実際には使用されている。しかしながら、熱硬化性の素
材を使用すると、当然のことながらプリント技術により
シール部材を形成した後に加熱・硬化する工程を設ける
必要があり、この工程には大規模な設備を必要とし、自
動変速機内コントロールバルブ用セパレートプレートの
製造コストの上昇を招く。また、熱硬化性の素材には、
通常溶剤が配合されており、加熱・硬化時に発生する溶
剤の回収処理には大掛かりな設備と多大なコストを要す
る。更に、シール特性もセパレートプレートに紙製のガ
スケットを接着するタイプのものと比較して充分とは言
えず、プリント技術を使用したシール部材を備えている
自動変速機内コントロールバルブ用セパレートプレート
は軽自動車等要求特性の低い車種にわずかに採用されて
いるにすぎないのが現状である。The above publication discloses an ultraviolet curable synthetic resin material as a material that can be used for forming a seal member by a printing technique.
There is no specific example of using the synthetic resin material, and in the above-mentioned publication, a thermosetting rubber or resin is actually used as a material of the seal member. However, if a thermosetting material is used, it is necessary to provide a step of heating and curing after forming a seal member by a printing technique, which naturally requires a large-scale facility, and the inside of an automatic transmission is required. This leads to an increase in the manufacturing cost of the control valve separate plate. In addition, thermosetting materials include:
Usually, a solvent is blended, and a large-scale facility and a large cost are required for the process of recovering the solvent generated during heating and curing. Furthermore, the sealing characteristics are not sufficient compared to the type in which a paper gasket is bonded to the separate plate, and the separate plate for the control valve in an automatic transmission equipped with a seal member using printing technology is a mini vehicle. At present, it is only slightly used for vehicle models with low required characteristics.
【０００７】また、上述のように、自動変速機内コント
ロールバルブ用セパレートプレートのシール部材の素材
として、紫外線硬化型の合成樹脂材料を適用可能である
ことが先行技術文献に記載されている。確かに、自動変
速機内コントロールバルブ用セパレートプレートの製造
コストを抑制するためにシール部材を加熱・硬化する工
程を削除するためには、シール部材の素材として、単に
紫外線を照射するだけでシール部材を硬化させることが
できる紫外線硬化型の合成樹脂材料を使用することは有
利である。また、熱硬化性の素材とは異なり無溶剤化が
容易で１００％に近い硬化体として使用できるという利
点もある。Further, as described above, it is described in the prior art that an ultraviolet-curable synthetic resin material can be used as a material for a seal member of a separate plate for a control valve in an automatic transmission. Certainly, in order to eliminate the process of heating and curing the seal member in order to reduce the manufacturing cost of the separate plate for the control valve in the automatic transmission, the seal member must be made by simply irradiating ultraviolet rays as the material of the seal member. It is advantageous to use a UV curable synthetic resin material that can be cured. Further, unlike a thermosetting material, there is also an advantage that it can be easily used without a solvent and can be used as a cured body of nearly 100%.
【０００８】しかしながら、本発明者らの研究によれ
ば、現在他の分野で一般的に用いられている紫外線硬化
型塗料や紫外線硬化型樹脂を単独で自動変速機内コント
ロールバルブ用セパレートプレート表面に塗布してシー
ル部材を形成しても充分な接着強度が得られず、自動変
速機内コントロールバルブ用セパレートプレートとして
充分な諸特性が得られないことが判明した。However, according to the study of the present inventors, it has been found that an ultraviolet curable paint or an ultraviolet curable resin generally used in other fields at present is applied alone to the surface of a separate plate for a control valve in an automatic transmission. It was found that even if a seal member was formed, sufficient adhesive strength could not be obtained, and that various characteristics could not be obtained as a separate plate for a control valve in an automatic transmission.
【０００９】従って、本発明の目的は、自動変速機内コ
ントロールバルブ用セパレートプレートを安価に製造す
ることができ、且つ優れたシール特性を提供することが
できるシール剤組成物並びに該シール剤組成物を用いて
形成されたシール部を備えてなる自動変速機内コントロ
ールバルブ用セパレートプレートを提供することにあ
る。Accordingly, an object of the present invention is to provide a sealant composition and a sealant composition capable of providing an inexpensive manufacture of a separate plate for a control valve in an automatic transmission and providing excellent sealing properties. An object of the present invention is to provide a separate plate for a control valve in an automatic transmission, which is provided with a seal portion formed using the seal portion.
【００１０】[0010]
【課題を解決するための手段】本発明者らは、上記課題
を解決するために鋭意研究した結果、紫外線硬化樹脂組
成物に接着用密着剤を配合したシール剤組成物を用いて
自動変速機内コントロールバルブ用セパレートプレート
にシール部を形成すると良好な特性が得られることを見
出し、本発明を完成するに至ったものである。Means for Solving the Problems The inventors of the present invention have made intensive studies to solve the above-mentioned problems, and as a result, have found that an automatic transmission using a sealant composition obtained by mixing an adhesive for adhesion with an ultraviolet-curable resin composition. The present inventors have found that good characteristics can be obtained by forming a seal portion on a separate plate for a control valve, and have completed the present invention.
【００１１】即ち、本発明のシール剤組成物は、紫外線
硬化樹脂組成物４０〜９７質量％、接着用密着剤２〜２
０質量％及び顔料１〜４０質量％よりなることを特徴と
する。That is, the sealant composition of the present invention comprises 40 to 97% by mass of the ultraviolet-curable resin composition, and 2 to 2 adhesive bonding agents.
0% by mass and 1 to 40% by mass of a pigment.
【００１２】また、本発明のシール剤組成物は、紫外線
硬化樹脂組成物中の紫外線硬化樹脂が、ラジカル重合系
紫外線硬化樹脂であることを特徴とする。The sealant composition of the present invention is characterized in that the ultraviolet curable resin in the ultraviolet curable resin composition is a radical polymerization type ultraviolet curable resin.
【００１３】更に、本発明のシール剤組成物は、接着用
密着剤が、モノイソシアネート、ジイソシアネート及び
トリイソシアネートからなる群から選択された１種また
は２種以上よりなることを特徴とする。Further, the sealant composition of the present invention is characterized in that the adhesive agent for adhesion comprises one or more selected from the group consisting of monoisocyanate, diisocyanate and triisocyanate.
【００１４】また、本発明のシール剤組成物は、顔料
が、有機顔料または無機顔料であることを特徴とする。[0014] The sealant composition of the present invention is characterized in that the pigment is an organic pigment or an inorganic pigment.
【００１５】また、本発明のシール剤組成物は、熱膨張
材を外割で０．２〜２０質量％の量で含有してなること
を特徴とする。Further, the sealant composition of the present invention is characterized in that it contains a thermal expansion material in an amount of 0.2 to 20% by mass on an outer basis.
【００１６】また、本発明の自動変速機内コントロール
バルブ用セパレートプレートは、セバレートプレートの
少なくとも片面の所定の位置に前記シール剤組成物の硬
化層よりなるシール部を設けたことを特徴とする。Further, the separate plate for a control valve in an automatic transmission according to the present invention is characterized in that a seal portion made of a cured layer of the sealant composition is provided at a predetermined position on at least one surface of the separate plate.
【００１７】更に、本発明の自動変速機内コントロール
バルブ用セパレートプレートは、シール剤組成物の硬化
層の厚さが２０〜１５０μｍであることを特徴とする。Further, the separate plate for a control valve in an automatic transmission according to the present invention is characterized in that the cured layer of the sealant composition has a thickness of 20 to 150 μm.
【００１８】[0018]
【発明の実施の形態】本発明のシール剤組成物は、紫外
線硬化樹脂組成物、接着用硬化剤及び顔料よりなること
を特徴とするものである。ここで、紫外線硬化樹脂組成
物の配合割合は、４０〜９７質量％、好ましくは４５〜
９４質量％の範囲内である。ここで、紫外線硬化樹脂組
成物の配合割合が４０質量％未満であると、樹脂として
の機能を発揮することができないために好ましくなく、
また、該配合割合が９７質量％を超えると、シール性の
低下や基材（芯材）との密着力が不足するために好まし
くない。BEST MODE FOR CARRYING OUT THE INVENTION The sealant composition of the present invention comprises an ultraviolet curable resin composition, an adhesive curing agent and a pigment. Here, the compounding ratio of the ultraviolet curable resin composition is 40 to 97% by mass, preferably 45 to 97% by mass.
It is in the range of 94% by mass. Here, when the blending ratio of the ultraviolet curable resin composition is less than 40% by mass, it is not preferable because the function as a resin cannot be exhibited.
On the other hand, if the mixing ratio exceeds 97% by mass, it is not preferable because the sealing property is lowered and the adhesion to the base material (core material) is insufficient.
【００１９】本発明に使用する紫外線硬化樹脂組成物に
使用する紫外線硬化樹脂としては、ラジカル重合系紫外
線硬化樹脂が好適である。該ラジカル重合系紫外線硬化
重合としては、例えばイソボニルアクリレート、アクリ
ロイルモルボリン、Ｎ−ビニルカプロラクタム等の単官
能アクリレート、ノナンジオールジアクリレート、トリ
プロピレングリコールジアクリレート、トリシクロデカ
ンジメタノールジアクリレート等の二官能アクリレー
ト、トリメチロールプロパントリアクリレート、ジトリ
メチロールプロパンテトラアクリレート等の多官能アク
リレート、ポリエステルアクリレート、ウレタンアクリ
レート、エポキシアクリレート等のアクリル系オリゴマ
ー、フマル酸やマレイン酸を使用した不飽和ポリエステ
ルを挙げることができる。なお、紫外線硬化樹脂は、水
性エマルジョンや水溶性紫外線硬化樹脂のような水性タ
イプのものてあっても良い。また、紫外線硬化樹脂組成
物は、上記紫外線硬化樹脂、重合開始剤、重合開始助剤
等の必須成分と、安定剤、重合禁止剤、レベリング剤等
の任意成分より構成されるものである。本発明のシール
剤組成物に使用される紫外線硬化樹脂組成物は、特に限
定されるものではないが、例えば日本ペイント（株）社
製の商品名ユーピコート６０等を挙げることができる。As the ultraviolet curable resin used in the ultraviolet curable resin composition used in the present invention, a radical polymerization type ultraviolet curable resin is preferable. Examples of the radical polymerization type ultraviolet curing polymerization include monofunctional acrylates such as isobornyl acrylate, acryloyl morpholine, and N-vinylcaprolactam; Examples include polyfunctional acrylates such as functional acrylates, trimethylolpropane triacrylate, and ditrimethylolpropane tetraacrylate; acrylic oligomers such as polyester acrylate, urethane acrylate, and epoxy acrylate; and unsaturated polyesters using fumaric acid and maleic acid. . The UV-curable resin may be of an aqueous type such as an aqueous emulsion or a water-soluble UV-curable resin. The UV-curable resin composition is composed of essential components such as the UV-curable resin, a polymerization initiator and a polymerization initiation auxiliary, and optional components such as a stabilizer, a polymerization inhibitor and a leveling agent. The UV-curable resin composition used in the sealant composition of the present invention is not particularly limited, and may include, for example, UPICOAT 60 (trade name) manufactured by Nippon Paint Co., Ltd.
【００２０】また、本発明のシール剤組成物に使用する
ことができる接着用密着剤としては、例えばイソシアン
酸エステル類であるイソシアン酸メチル、イソシアン酸
エチル、イソシアン酸イソプロピル、イソシアン酸フェ
ニル、イソシアン酸ナフチル等のようなモノイソシアネ
ート及びその誘導体や、１，６−ヘキサメチレンジイソ
シアネート（ＨＭＤＩ）、イソホロンジイソシアネート
（ＩＰＤＩ）、トリレンジイソシアネート（ＴＤＩ）、
キシレンジイソシアネート（ＸＤＩ）などのジイソシア
ネート及びその誘導体や、トリイソシアネート及びその
誘導体が使用できる。接着用密着剤の配合量は２〜２０
質量％、好ましくは５〜１５質量％の範囲内である。接
着用密着剤の配合量が２質量％未満の場合、密着力不足
となり、芯材からの剥離が発生するために好ましくな
い。また、該配合量が２０質量％を超えると、主材であ
る紫外線硬化樹脂組成物の紫外線による硬化を妨害する
ために好ましくない。Examples of the adhesive agent for adhesion which can be used in the sealant composition of the present invention include, for example, methyl isocyanates such as methyl isocyanate, ethyl isocyanate, isopropyl isocyanate, phenyl isocyanate, and isocyanate. Monoisocyanates such as naphthyl and derivatives thereof, 1,6-hexamethylene diisocyanate (HMDI), isophorone diisocyanate (IPDI), tolylene diisocyanate (TDI),
Diisocyanates such as xylene diisocyanate (XDI) and derivatives thereof, and triisocyanates and derivatives thereof can be used. The compounding amount of the adhesive for adhesion is 2 to 20.
%, Preferably in the range of 5 to 15% by weight. If the blending amount of the adhesive for adhesion is less than 2% by mass, the adhesion becomes insufficient, and peeling from the core material occurs, which is not preferable. On the other hand, if the compounding amount exceeds 20% by mass, it is not preferable because the ultraviolet curable resin composition as the main material is hardened by ultraviolet rays.
【００２１】また、本発明のシール剤組成物に使用する
ことができる顔料は、紫外線硬化樹脂組成物の硬化を阻
害しないものであれば特に限定されるものではなく、艶
消剤、体質顔料、着色顔料等の機能を有する有機顔料ま
たは無機顔料を使用でき、通常の塗料に使用される顔
料、例えば二酸化チタン、シアニンブルー、シンカシャ
レッド、カーボンブラック、弁柄等を挙げることができ
る。顔料の配合量は１〜４０質量％、好ましくは２〜３
５質量％である。顔料の配合量が１質量％未満である
と、製造時の不適合箇所の検出が困難となるために好ま
しくなく、また、４０質量％を超えると、主材である紫
外線硬化樹脂組成物の紫外線による硬化を阻害したり、
得られる硬化層が脆くなることがあるために好ましくな
い。The pigment that can be used in the sealant composition of the present invention is not particularly limited as long as it does not inhibit the curing of the ultraviolet-curable resin composition. An organic pigment or an inorganic pigment having a function such as a coloring pigment can be used, and examples thereof include pigments used in ordinary paints, for example, titanium dioxide, cyanine blue, Shinkasha red, carbon black, and red iron oxide. The amount of the pigment is 1 to 40% by mass, preferably 2 to 3% by mass.
5% by mass. If the blending amount of the pigment is less than 1% by mass, it is not preferable because it is difficult to detect a nonconforming portion at the time of production. Inhibits curing,
This is not preferred because the resulting cured layer may become brittle.
【００２２】本発明のシール剤組成物には、更なるシー
ル性向上の目的で、熱膨張材を外割で０．２〜２０質量
％の量で配合することができる。ここで、熱膨張材の配
合量が外割で０．２質量％未満であると、添加・配合効
果がないために好ましくなく、また、該配合量が２０質
量％を超えると脆さが増大するために好ましくない。な
お、熱膨張材としては例えば膨張性黒鉛、熱膨張性マイ
クロカプセル、膨張性樹脂ビーズ等を例示することがで
きる。The sealant composition of the present invention may contain a thermal expansion material in an amount of 0.2 to 20% by mass in order to further improve the sealing property. Here, if the blending amount of the thermal expansion material is less than 0.2% by mass, it is not preferable because there is no effect of addition and blending, and if the blending amount exceeds 20% by mass, brittleness increases. It is not preferable to do. Examples of the thermal expansion material include expandable graphite, thermally expandable microcapsules, and expandable resin beads.
【００２３】次に、本発明の自動変速機内コントロール
バルブ用セパレートプレートは、セバレートプレートの
少なくとも片面の所定の位置に本発明のシール剤組成物
の硬化層よりなるシール部を設けたことを特徴とする。Next, the separate plate for a control valve in an automatic transmission according to the present invention is characterized in that a seal portion made of a cured layer of the sealant composition of the present invention is provided at a predetermined position on at least one surface of the separate plate. And
【００２４】ここで、本発明の自動変速機内コントロー
ルバルブ用セパレートプレートは、上述のような成分配
合を有する本発明のシール剤組成物を、慣用の方法によ
り自動変速機内コントロールバルブ用セパレートプレー
トへ塗布して紫外線を照射して硬化させることにより得
られる硬化層をシール部とすることにより製造すること
ができる。Here, the separate plate for a control valve in an automatic transmission of the present invention is obtained by applying the sealant composition of the present invention having the above-mentioned composition to a separate plate for a control valve in an automatic transmission by a conventional method. It can be manufactured by forming a cured layer obtained by irradiating ultraviolet rays to cure the cured layer as a seal portion.
【００２５】なお、自動変速機内コントロールバルブ用
セパレートプレートへの塗布方法は、特に限定されるも
のではなく、慣用の公知の方法を採用することができ、
例えば凸版印刷、平板印刷、凹版印刷、スクリーン印
刷、植毛印刷、磁気印刷、ホットスタンピングのような
パターン印刷や、ディスペンサーによる材料塗布技術等
を用いることができる。The method of applying the liquid to the separate plate for the control valve in the automatic transmission is not particularly limited, and a commonly known method can be adopted.
For example, pattern printing such as letterpress printing, lithographic printing, intaglio printing, screen printing, flocking printing, magnetic printing, hot stamping, or a material application technique using a dispenser can be used.
【００２６】また、本発明の自動変速機内コントロール
バルブ用セパレートプレートにおいて、シール剤組成物
の硬化層、即ち、シール部の厚さは２０〜１５０μｍ、
好ましくは５０〜１２０μｍの範囲内である。ここで、
硬化層の厚さが２０μｍ未満では、シール性が低下する
ために好ましくなく、また、該硬化層の厚さが１５０μ
ｍを超えると、紫外線がシール剤組成物と芯材の接着面
まで到達できなくなることによる硬化ムラや、締結時の
耐圧力不足、応力緩和増大となるために好ましくない。In the separate plate for a control valve in an automatic transmission according to the present invention, the cured layer of the sealant composition, that is, the thickness of the seal portion is 20 to 150 μm.
Preferably it is in the range of 50 to 120 μm. here,
When the thickness of the hardened layer is less than 20 μm, the sealing property is deteriorated, which is not preferable.
When m exceeds m, it is not preferable because ultraviolet rays cannot reach the bonding surface between the sealant composition and the core material, resulting in uneven curing, insufficient pressure resistance during fastening, and increased stress relaxation.
【００２７】本発明の自動変速機内コントロールバルブ
用セパレートプレートの本体となる芯材の材質は特に限
定されるものではなく、例えば鋼板、合金板、合成樹脂
板、セラミックス板等を利用することができる。なお、
芯材へシール剤組成物を塗布する際には、芯材を脱脂処
理及びブラスト処理することが好ましい。また、ブラス
ト処理の代わりに薬品処理やプライマー処理を施すこと
もできる。更に、芯材として市販の化粧用鋼板を用いる
こともできる。The material of the core material serving as the main body of the separate plate for the control valve in the automatic transmission of the present invention is not particularly limited. . In addition,
When applying the sealant composition to the core, the core is preferably subjected to a degreasing treatment and a blast treatment. Further, a chemical treatment or a primer treatment may be performed instead of the blast treatment. Further, a commercially available decorative steel plate can be used as the core material.
【００２８】[0028]
【実施例】以下に、実施例を挙げて本発明のシール剤組
成物並びに自動変速機内コントロールバルブ用セパレー
トプレートを更に説明する。 実施例１ 以下の表１及び２に本発明品並びに比較品のシール剤組
成物の配合を示す。EXAMPLES The sealant composition of the present invention and a separate plate for a control valve in an automatic transmission will be further described below with reference to examples. Example 1 The following Tables 1 and 2 show the formulations of the sealant compositions of the present invention and comparative products.
【００２９】[0029]
【表１】 [Table 1]
【００３０】表１中、紫外線硬化樹脂組成物は、ユービ
コート６０［日本ペイント（株）社製］であり、接着用
密着剤は１，６−ヘキサメチレンジイソシアネートであ
り、顔料はタルク：硫酸バリウム：カーボンブラック＝
１０：１０：１（質量割合）調整品である。In Table 1, the UV-curable resin composition is Ubicoat 60 (manufactured by Nippon Paint Co., Ltd.), the adhesive agent for adhesion is 1,6-hexamethylene diisocyanate, and the pigment is talc: barium sulfate: Carbon black =
It is a 10: 10: 1 (mass ratio) adjusted product.
【００３１】[0031]
【表２】 [Table 2]
【００３２】表２中、熱膨張材の配合割合は、表１中の
本発明品２に対する外割の割合である。なお、熱膨張材
としては熱膨張性マイクロカプセルを使用した。In Table 2, the compounding ratio of the thermal expansion material is the ratio of the outer part to the product 2 of the present invention in Table 1. In addition, a heat-expandable microcapsule was used as the heat-expanding material.
【００３３】次に、上記表１及び２に示す本発明品並び
に比較品のシール剤組成物をスクリーン印刷機にて、化
粧用ＳＰＣＣ基材［商品名シルバートップ：東洋鋼板
（株）製：厚さ１ｍｍ］の両面に膜厚８０μｍに塗布
し、紫外線照射装置にて塗膜を硬化させた。得られた塗
膜について、諸特性を評価した。なお、従来品１は、紙
ガスケットを鉄板の表裏に接着したタイプであり、従来
品２は、スクリーン印刷にて熱硬化性樹脂を鉄板の両面
に所定のパターンとして印刷し、溶剤乾燥後、加熱処理
して得たものである。得られた結果を表３及び４に記載
する。Next, the sealant composition of the present invention and the comparative product shown in Tables 1 and 2 above was applied to a cosmetic SPCC substrate [trade name: Silver Top: Toyo Steel Co., Ltd .: [1 mm] to a film thickness of 80 μm, and the coating film was cured with an ultraviolet irradiation device. Various characteristics were evaluated about the obtained coating film. The conventional product 1 is a type in which a paper gasket is adhered to the front and back of an iron plate. The conventional product 2 is obtained by printing a thermosetting resin in a predetermined pattern on both surfaces of the iron plate by screen printing, drying the solvent, and then heating. It is obtained by processing. The results obtained are described in Tables 3 and 4.
【００３４】[0034]
【表３】 [Table 3]
【００３５】[0035]
【表４】 [Table 4]
【００３６】表３及び４中、鉛筆硬度は、ＪＩＳ Ｋ５
４００ ８．４．３の鉛筆引っかき値手かき法に準拠す
るものであり、碁盤目試験は、ＪＩＳ Ｋ５４００
８．５．３の碁盤目テープ法に準拠するものであり、数
値は点数を表し、エアーシール性は、エアーシール性差
圧検出方式により面圧１１．８ＭＰａ、内圧０．０５Ｍ
Ｐａで測定した結果である（単位：ｃｃ／分）。In Tables 3 and 4, the pencil hardness is JIS K5
400 Pencil scratch value conforming to 8.4.3 Pencil scribing method, and the cross cut test is based on JIS K5400
The value is based on the cross-cut tape method of 8.5.3, the numerical value represents a point, and the air sealability is 11.8 MPa, inner pressure 0.05 M by air sealability differential pressure detection method.
It is a result measured in Pa (unit: cc / min).
【００３７】実施例２ 表１の本発明品２を用い、硬化層の厚さを表５に記載す
る厚さに変更した以外は実施例１と同様の方法にて、化
粧用ＳＰＣＣ基材［商品名シルバートップ：東洋鋼板
（株）製：厚さ１ｍｍ］の両面に塗膜を硬化させた。得
られた塗膜について、諸特性を評価した。得られた結果
を表６に記載する。Example 2 A cosmetic SPCC substrate [in the same manner as in Example 1 except that the thickness of the cured layer was changed to the thickness shown in Table 5 using the product 2 of the present invention shown in Table 1, (Trade name: Silver Top: manufactured by Toyo Steel Co., Ltd .: thickness: 1 mm). Various characteristics were evaluated about the obtained coating film. Table 6 shows the obtained results.
【００３８】[0038]
【表５】 [Table 5]
【００３９】[0039]
【表６】 [Table 6]
【００４０】[0040]
【発明の効果】本発明のシール剤組成物を用いることに
より、従来品の紙ガスケット接着品や熱硬化性樹脂を用
いた自動変速機内コントロールバルブ用セパレートプレ
ートと比べて、優れたシール性と、芯材との密着性を兼
ね備えた自動変速機内コントロールバルブ用セパレート
プレートを安価に製造することができる。また、熱硬化
性樹脂に比べ、本発明のシール剤組成物は、硬化工程で
有機溶剤の飛散がないので、環境負荷が少ない。更に、
紙ガスケット接着品や熱硬化性樹脂を用いた自動変速機
内コントロールバルブ用セパレートプレートと比べて油
圧に対する耐摩耗性も良好である。EFFECTS OF THE INVENTION By using the sealant composition of the present invention, excellent sealing properties are obtained as compared with conventional paper gasket adhesive products and a separate plate for a control valve in an automatic transmission using a thermosetting resin. A separate plate for a control valve in an automatic transmission having a close contact with a core material can be manufactured at low cost. In addition, compared to thermosetting resins, the sealant composition of the present invention has less environmental load because no organic solvent is scattered in the curing step. Furthermore,
The wear resistance to hydraulic pressure is also better than a separate plate for a control valve in an automatic transmission using a paper gasket adhesive or a thermosetting resin.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０８Ｋ 5/29 Ｃ０８Ｋ 5/29 Ｃ０８Ｌ 101/00 Ｃ０８Ｌ 101/00 // Ｆ１６Ｈ 57/02 ３０２ Ｆ１６Ｈ 57/02 ３０２Ｆ (72)発明者 新島 智紀 山梨県西八代郡市川大門町1488番地 株式 会社アスクテクニカ内 Ｆターム(参考） 3J063 AA02 AB01 AC03 BB01 CA01 CC14 4H017 AA04 AA24 AA27 AA29 AB03 AD01 AE05 4J002 AA001 AA002 BG041 BG071 BJ001 CD191 CD201 CF221 CF271 CK021 DA028 ER006 FA082 FB288 FD097 FD146 FD322 FD328 GJ02 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C08K 5/29 C08K 5/29 C08L 101/00 C08L 101/00 // F16H 57/02 302 F16H 57/02 302F (72) Inventor Tomoki Niijima 1488 Kawadaimon-cho, Nishi-Yatsushiro-gun, Yamanashi Prefecture F-term in Askeknica Co., Ltd. CF221 CF271 CK021 DA028 ER006 FA082 FB288 FD097 FD146 FD322 FD328 GJ02
Claims (7)
％、接着用密着剤２〜２０質量％及び顔料１〜４０質量
％よりなることを特徴とするシール剤組成物。1. A sealant composition comprising 40 to 97% by mass of an ultraviolet curable resin composition, 2 to 20% by mass of an adhesive agent for adhesion, and 1 to 40% by mass of a pigment.
脂が、ラジカル重合系紫外線硬化樹脂である、請求項１
記載のシール剤組成物。2. The ultraviolet curable resin in the ultraviolet curable resin composition is a radical polymerization type ultraviolet curable resin.
The sealant composition as described in the above.
ジイソシアネート及びトリイソシアネートからなる群か
ら選択された１種または２種以上よりなる、請求項１ま
たは２項記載のシール剤組成物。3. The adhesive curing agent is a monoisocyanate,
3. The sealant composition according to claim 1, comprising one or more selected from the group consisting of diisocyanates and triisocyanates.
る、請求項１ないし３のいずれか１項記載のシール剤組
成物。4. The sealant composition according to claim 1, wherein the pigment is an organic pigment or an inorganic pigment.
量で含有してなる、請求項１ないし４のいずれか１項記
載のシール剤組成物。5. The sealant composition according to claim 1, which further comprises a thermal expansion material in an amount of 0.2 to 20% by mass.
レートプレートにおいて、セバレートプレートの少なく
とも片面の所定の位置に請求項１ないし５のいずれか１
項記載のシール剤組成物の硬化層よりなるシール部を設
けたことを特徴とする自動変速機内コントロールバルブ
用セパレートプレート。6. A separate plate for a control valve in an automatic transmission according to claim 1, wherein the separate plate is provided at a predetermined position on at least one surface of the separate plate.
A separate plate for a control valve in an automatic transmission, comprising a seal portion comprising a cured layer of the sealant composition according to any one of the preceding claims.
１５０μｍである、請求項６記載の自動変速機内コント
ロールバルブ用セパレートプレート。7. The cured layer of the sealant composition has a thickness of 20 to 20.
The separate plate for a control valve in an automatic transmission according to claim 6, which is 150 µm.