JP2002316921A - Rice fermented extract-immobilized fabric and method for producing the same - Google Patents
Rice fermented extract-immobilized fabric and method for producing the sameInfo
- Publication number
- JP2002316921A JP2002316921A JP2001119809A JP2001119809A JP2002316921A JP 2002316921 A JP2002316921 A JP 2002316921A JP 2001119809 A JP2001119809 A JP 2001119809A JP 2001119809 A JP2001119809 A JP 2001119809A JP 2002316921 A JP2002316921 A JP 2002316921A
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- group
- rice
- extract
- fermented extract
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、米発酵エキスを固
定化した布帛およびその製造方法に関する。TECHNICAL FIELD The present invention relates to a fabric on which a fermented rice extract is immobilized and a method for producing the same.
【０００２】[0002]
【従来の技術】米発酵エキスは、玄米を精米する際の副
産物である赤ヌカ、白ヌカ等を含めた米ヌカを原料と
し、酵素等を加えて液化し、糖化した後、麹、酵母等に
より発酵させ、発酵末期に塩化ナトリウムを加えた後、
ろ過することにより生成される。かかる米発酵エキス
は、酵素や微生物の代謝作用により生成したアミノ酸
（保湿成分）やアルコールだけでなく、γ−オリザノー
ル（生理活性物質）やフェルラ酸（抗酸化物質）や各種
のミネラルをも含んでおり、入浴剤、石けん、シャンプ
ー、シェービングフォーム、養毛剤などに用いられ、ス
キンケア効果（皮膚に対する保湿効果）のほか、保温効
果、洗浄効果や血行促進効果に優れている。2. Description of the Related Art Fermented rice extract is made from rice bran including red bran and white bran, which are by-products of brown rice milling, and is liquefied by adding enzymes and the like, saccharified, and then koji, yeast, etc. After adding sodium chloride at the end of fermentation,
Produced by filtration. Such a fermented rice extract contains not only amino acids (moisturizing components) and alcohols generated by metabolism of enzymes and microorganisms, but also γ-oryzanol (bioactive substance), ferulic acid (antioxidant) and various minerals. It is used for bath salts, soaps, shampoos, shaving foams, hair tonics, etc., and has excellent skin care effects (moisturizing effect on the skin), heat retaining effect, washing effect and blood circulation promoting effect.
【０００３】米発酵エキスを使用した製品としては、例
えば、特開平１１−１８９５２６号公報に５０〜６０℃
の高温でも保存安定性の優れたエチルアルコールまたは
食塩が配合されたＯ／Ｗエマルジョンタイプの入浴剤が
開示されているし、特開２０００−２８１５６０号公報
には米発酵エキスに粒径が０．１〜２００μｍの粉末状
絹繊維を含有させた入浴剤が開示されている。[0003] As a product using a rice fermented extract, for example, Japanese Patent Application Laid-Open No. 11-189526 discloses a product at 50 to 60 ° C.
An O / W emulsion type bathing agent containing ethyl alcohol or salt excellent in storage stability even at high temperatures is disclosed. Japanese Patent Application Laid-Open No. 2000-281560 discloses a fermented rice extract having a particle size of 0.1. A bath agent containing 1 to 200 μm of powdered silk fiber is disclosed.
【０００４】一方、繊維素材への吸水性能を向上させる
試みとして、ビニルモノマーをはじめとする各種のモノ
マーを繊維素材上で重合させる方法が知られており、特
開昭５８−１６９５６９号公報、特開平８−４８７３５
号公報、特開平８−２０９５４０号公報などに開示され
ている。また、特開平１１−６１６４７号公報には、架
橋されたビニルスルホン酸ポリマーと変性オルガノシリ
ケート等の薬剤を用いて繊維素材上で重合させ、耐久性
のある吸水性能と同時に、汚れ防止（黒ずみ防止）の加
工布帛を得る方法も開示されている。しかし、これらの
方法は、主にアクリル系モノマーを繊維素材上で重合さ
せることによって、繊維素材に吸水性能を付与すること
を企図したものであり、かかる方法によって顕著な吸放
湿性能やさらには保湿性、スキンケア効果を付与するこ
とまでは期待できない。On the other hand, as an attempt to improve the water absorption performance of a fiber material, a method of polymerizing various monomers such as a vinyl monomer on a fiber material has been known, as disclosed in JP-A-58-169569. Kaihei 8-48735
And Japanese Patent Application Laid-Open No. 8-209540. Japanese Patent Application Laid-Open No. 11-61647 discloses that a crosslinked vinyl sulfonic acid polymer and a modified organosilicate are used to polymerize on a fiber material so as to have a durable water-absorbing property and a stain prevention (a darkening prevention). Also disclosed is a method for obtaining the processed fabric of the above (1). However, these methods are intended to impart a water absorbing property to the fiber material mainly by polymerizing an acrylic monomer on the fiber material, and by such a method, a remarkable moisture absorbing / releasing performance and furthermore It cannot be expected to provide moisturizing properties and skin care effects.
【０００５】[0005]
【発明が解決しようとする課題】本発明者らは、米発酵
エキスが有する物性や特長を繊維素材に付与することを
課題として鋭意研究した結果、本発明を完成させたもの
である。すなわち、本発明の目的は、優れた吸放湿性能
や保湿性、スキンケア効果を持ち、しかもそれらの特性
の耐久性に優れた布帛およびそのような布帛を工業的に
容易かつ安価に製造することのできる方法を提供するこ
とにある。DISCLOSURE OF THE INVENTION The present inventors have made intensive studies on imparting the physical properties and characteristics of a rice fermented extract to a fiber material, and have completed the present invention. That is, an object of the present invention is to provide a fabric having excellent moisture absorption / desorption performance, moisture retention, and skin care effects, and also having excellent durability of those characteristics and industrially easily and inexpensively producing such a fabric. It is to provide a method that can do.
【０００６】[0006]
【課題を解決するための手段】本発明は、上記課題を達
成するため、下記の成分、（ａ）米発酵エキス、（ｂ）
下記一般式（１）Means for Solving the Problems To achieve the above object, the present invention provides the following components: (a) a fermented rice extract;
The following general formula (1)
【０００７】[0007]
【化５】 Embedded image
【０００８】〔上式中、Ｒは直接結合された[Wherein R is directly bonded
【０００９】[0009]
【化６】 Embedded image
【００１０】または−Ｃn Ｈ2n−（ここでｎは１〜６の
整数を表す）を表し、ＺはＨまたは−ＣＨ3 を表し、ａ
およびｂはそれぞれａ＋ｂが０〜５０となるような０ま
たは正の整数を表し、ｘおよびｙはそれぞれｘ＋ｙが０
〜３０となるような０または正の整数を表す。ただし、
ａ＋ｂ＋ｘ＋ｙは１０以上であるものとする〕で示され
る２官能性化合物、（ｃ）水酸基、カルボキシル基、ア
ミノ基、スルホン酸基またはリン酸基を含む化合物、お
よび（ｄ）アジリジン基を含む化合物、の重合体を布帛
上に固定化してなる米発酵エキス固定化布帛を提供す
る。Or —C n H 2n — (where n represents an integer of 1 to 6); Z represents H or —CH 3 ;
And b each represent 0 or a positive integer such that a + b is 0 to 50;
Represents 0 or a positive integer such as to be 30. However,
a + b + x + y is 10 or more], (c) a compound containing a hydroxyl group, a carboxyl group, an amino group, a sulfonic acid group or a phosphoric acid group, and (d) a compound containing an aziridine group, The present invention provides a rice fermented extract-immobilized fabric obtained by immobilizing the polymer on a fabric.
【００１１】本発明は、また、下記の成分、（ａ）米発
酵エキス、（ｂ）下記一般式（１）The present invention also provides the following components: (a) a fermented rice extract; (b) the following general formula (1):
【００１２】[0012]
【化７】 Embedded image
【００１３】〔上式中、Ｒは直接結合された[Wherein R is directly bonded
【００１４】[0014]
【化８】 Embedded image
【００１５】または−Ｃn Ｈ2n−（ここでｎは１〜６の
整数を表す）を表し、ＺはＨまたは−ＣＨ3 を表し、ａ
およびｂはそれぞれａ＋ｂが０〜５０となるような０ま
たは正の整数を表し、ｘおよびｙはそれぞれｘ＋ｙが０
〜３０となるような０または正の整数を表す。ただし、
ａ＋ｂ＋ｘ＋ｙは１０以上であるものとする〕で示され
る２官能性化合物、（ｃ）水酸基、カルボキシル基、ア
ミノ基、スルホン酸基またはリン酸基を含む化合物、お
よび（ｄ）アジリジン基を含む化合物、を含む水性処理
液を布帛に付与した後、上記各成分を布帛上で重合せし
めることを含む米発酵エキス固定化布帛の製造方法を提
供する。Or -C n H 2n- (where n represents an integer of 1 to 6); Z represents H or -CH 3 ;
And b each represent 0 or a positive integer such that a + b is 0 to 50;
Represents 0 or a positive integer such as to be 30. However,
a + b + x + y is 10 or more], (c) a compound containing a hydroxyl group, a carboxyl group, an amino group, a sulfonic acid group or a phosphate group, and (d) a compound containing an aziridine group, The present invention provides a method for producing a rice-fermented extract-immobilized cloth, which comprises applying an aqueous treatment liquid containing the above to a cloth, and polymerizing the above components on the cloth.
【００１６】[0016]
【発明の実施の形態】以下、本発明を詳細に説明する。
本発明の米発酵エキス固定化布帛は、米発酵エキス−グ
ラフト重合体よりなる均一な薄い皮膜が、布帛を構成す
る繊維表面を包み込んでいるもので、この表面重合体皮
膜は、水にもはや溶解乃至脱落せず、耐洗濯性のあるも
のである。そして、このような耐久性のある米発酵エキ
スの架橋皮膜は、後述する混合物をグラフト重合するこ
とにより形成される。上記加工布帛において、布帛の重
量に対する米発酵エキスの付着量は、布帛の柔軟性およ
び風合いを考慮すると布帛の重量に対し高々５重量％で
あるのが好ましく、より好ましくは０．０５〜３．０重
量％、さらに好ましくは０．１〜２．０重量％である。
また、布帛の柔軟性および風合いの点から、上記の米発
酵エキス−グラフト重合体よりなる皮膜の付着量は、布
帛の重量に対し０．２〜１０．０重量％であるのが好ま
しい。また、皮膜の厚みは、通常、０．０１〜１０μｍ
であるのが好ましい。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail.
The rice fermented extract-immobilized fabric of the present invention has a uniform thin film made of a rice fermented extract-graft polymer wrapping around the fiber surface constituting the fabric, and this surface polymer film is no longer soluble in water. It does not fall off and has washing resistance. And such a durable crosslinked film of the fermented rice extract is formed by graft polymerization of a mixture described below. In the above-mentioned processed cloth, the amount of the rice fermented extract attached to the weight of the cloth is preferably at most 5% by weight, more preferably 0.05 to 3.0%, based on the weight of the cloth in consideration of the flexibility and texture of the cloth. 0% by weight, more preferably 0.1 to 2.0% by weight.
In addition, from the viewpoint of the flexibility and texture of the fabric, the amount of the film formed of the above-mentioned rice fermented extract-graft polymer is preferably 0.2 to 10.0% by weight based on the weight of the fabric. The thickness of the coating is usually 0.01 to 10 μm
It is preferred that
【００１７】本発明において、上記皮膜が形成される布
帛の素材としては、綿、レーヨン、麻等のセルロース繊
維、アセテート、トリアセテート等の半合成繊維、ポリ
エステル、ナイロン、アクリル等の合成繊維及び各種繊
維の混紡もしくは混繊品が挙げられる。また、その形態
としては、織物、編物、不織布等が挙げられる。それら
のうちでも、特に、通常の加工方法では改質困難なナイ
ロン等のポリアミド繊維を用いた布帛やポリエステル布
帛において、本発明の効果が顕著である。In the present invention, the material of the fabric on which the film is formed includes cellulose fibers such as cotton, rayon and hemp, semi-synthetic fibers such as acetate and triacetate, synthetic fibers such as polyester, nylon and acrylic, and various fibers. Or mixed fiber products. Examples of the form include a woven fabric, a knitted fabric, and a nonwoven fabric. Among them, the effect of the present invention is remarkable particularly in a fabric using a polyamide fiber such as nylon or a polyester fabric, which is difficult to modify by a normal processing method.
【００１８】上記の如き米発酵エキス固定化布帛は、前
述した本発明の方法により製造することができる。ここ
で、成分（ａ）の米発酵エキスは、一般に、米発酵エキ
スの水溶液または分散液として入手することができる。
従って、本発明の方法の実施に当たっては、成分（ａ）
の米発酵エキスをその水溶液または分散液として用い、
これに成分（ｂ）〜（ｄ）を混合して処理液とし、この
処理液を布帛に付与した後、上記成分（ａ）〜（ｄ）を
布帛上で重合せしめるのがよい。The above-mentioned cloth for immobilizing rice fermented extract can be produced by the method of the present invention described above. Here, the fermented rice extract of the component (a) can be generally obtained as an aqueous solution or dispersion of the fermented rice extract.
Therefore, in carrying out the method of the present invention, component (a)
Using the rice fermented extract as an aqueous solution or dispersion thereof,
It is preferable that the components (b) to (d) are mixed with each other to form a treatment liquid, and that this treatment liquid is applied to a cloth, and then the above components (a) to (d) are polymerized on the cloth.
【００１９】本発明の製造方法によれば、上記成分
（ｂ）〜（ｄ）を布帛上でラジカル重合させることによ
り、布帛を構成する繊維の表面および/ または表面に近
い内部に、米発酵エキスがグラフト重合された不溶性の
架橋性皮膜が形成される。この皮膜により、数十回の家
庭洗濯およびドライクリーニングに耐え得る、米発酵エ
キスが固定された布帛を与えることが可能となる。そし
て、これにより、通常の加工手段を用いて、容易に、吸
放湿性能やさらには保湿性、スキンケア効果を、耐久性
良く付与することができる。また、本発明の方法では、
合成繊維布帛の欠点である、帯電し易い、吸水性が悪
い、汚れが落ちにくい等の欠点も同時に解消することが
できるのである。According to the production method of the present invention, the above components (b) to (d) are subjected to radical polymerization on a fabric, so that the fermented rice extract is added to the surface of the fibers constituting the fabric and / or to the interior close to the surface. Is graft-polymerized to form an insoluble crosslinkable film. With this film, it is possible to provide a fabric in which the fermented rice extract is fixed, which can withstand several tens of home washings and dry cleanings. Thus, it is possible to easily impart moisture absorption / desorption performance, furthermore, moisture retention and skin care effects with good durability using ordinary processing means. Further, in the method of the present invention,
The drawbacks of the synthetic fiber fabric, such as easy charging, poor water absorption, and difficulty in removing dirt, can be eliminated at the same time.
【００２０】本発明の方法において使用される米発酵エ
キス水溶液としては、公知のものを広く使用することが
でき、例えば、特開２０００−８００２５号公報や特開
平８−３５９１号公報に記載されたものを用いることが
できる。本発明の方法においては、成分（ａ）〜（ｄ）
を含む水性処理液に対する米発酵エキス水溶液の添加量
は、通常、０．５〜３０．０重量％、特に１．０〜２
０．０重量％であるのが好ましい。かかる米発酵エキス
水溶液としては、上記のものをそのまま使用してもよい
が、例えば、チューブまたはフィルムの半透膜を用いて
透析することにより処理したものを用いるのがさらに好
ましい。As the aqueous solution of the rice fermented extract used in the method of the present invention, known ones can be widely used, and for example, those described in JP-A-2000-80025 and JP-A-8-3591 are described. Can be used. In the method of the present invention, components (a) to (d)
The amount of the aqueous solution of the rice fermented extract added to the aqueous treatment solution containing is usually 0.5 to 30.0% by weight, particularly 1.0 to 2% by weight.
Preferably it is 0.0% by weight. As the aqueous solution of rice fermented extract, the above-mentioned aqueous solution may be used as it is, but for example, an aqueous solution treated by dialysis using a tube or a semipermeable membrane of a film is more preferably used.
【００２１】一方、米発酵エキス分散液は、上記の如き
米発酵エキス水溶液からの脆化粗粉体などの、十分に加
水分解されてないものや結晶化されているものであって
よく、公知のものを広く用いることができる。米発酵エ
キス分散液の改質には、水または有機溶媒を分散媒とし
て、ボールミル等で湿式粉砕することにより得られた、
米発酵エキスの水または有機溶媒分散液であって、体積
平均粒子径が５μｍ以下のものであれば、米発酵エキス
水溶液と同様に使用することができる。On the other hand, the dispersion of the fermented rice extract may be one that is not sufficiently hydrolyzed or crystallized, such as embrittled coarse powder from the aqueous fermented rice extract solution as described above. Can be widely used. The modified rice fermented extract dispersion was obtained by wet grinding with a ball mill or the like, using water or an organic solvent as a dispersion medium,
If it is a water or organic solvent dispersion of the rice fermentation extract and has a volume average particle diameter of 5 μm or less, it can be used in the same manner as the rice fermentation extract aqueous solution.
【００２２】次に、成分（ｂ）〜（ｄ）について説明す
るが、以下に示される化合物は、前記成分（ｂ）、
（ｃ）および（ｄ）の化合物の具体例であって、本発明
はこれらに限定されるものではない。まず、前記成分
（ｂ）の化合物の例としては、下記式（２）〜（５）Next, components (b) to (d) will be described.
These are specific examples of the compounds (c) and (d), and the present invention is not limited to these. First, examples of the compound of the component (b) include the following formulas (2) to (5).
【００２３】[0023]
【化９】 Embedded image
【００２４】[0024]
【化１０】 Embedded image
【００２５】[0025]
【化１１】 Embedded image
【００２６】[0026]
【化１２】 Embedded image
【００２７】の化合物等がある。また、成分（ｃ）の化
合物の例としては、アクリル酸、メタクリル酸、スチレ
ンスルホン酸、マレイン酸、イタコン酸、クルトン酸、
ビニルスルホン酸、２−アリルオキシ−２−ヒドロキシ
プロパンスルホン酸、２−アクリルアミド−２−メチル
プロパンスルホン酸、２−ヒドロキシエチルメタクリレ
ート、ヒドロキシプロピルメタクリレート、並びに下記
式（６）〜（８）And the like. Examples of the compound of the component (c) include acrylic acid, methacrylic acid, styrenesulfonic acid, maleic acid, itaconic acid, croutonic acid,
Vinylsulfonic acid, 2-allyloxy-2-hydroxypropanesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, 2-hydroxyethyl methacrylate, hydroxypropyl methacrylate, and the following formulas (6) to (8)
【００２８】[0028]
【化１３】 Embedded image
【００２９】〔上式中、ｃ＋ｄはそれぞれ５以上の整数
を表す〕[In the above formula, c + d represents an integer of 5 or more.]
【００３０】[0030]
【化１４】 Embedded image
【００３１】〔上式中、ｅは５以上の整数を表す〕[In the above formula, e represents an integer of 5 or more.]
【００３２】[0032]
【化１５】 Embedded image
【００３３】の化合物等があり、成分（ｄ）の化合物の
例としては、下記式（９）〜（１３）Examples of the compound of the component (d) include the following formulas (9) to (13)
【００３４】[0034]
【化１６】 Embedded image
【００３５】[0035]
【化１７】 Embedded image
【００３６】[0036]
【化１８】 Embedded image
【００３７】[0037]
【化１９】 Embedded image
【００３８】[0038]
【化２０】 Embedded image
【００３９】の化合物等がある。具体的な処理方法とし
ては、成分（ａ）の米発酵エキスと成分（ｂ）〜（ｄ）
の化合物およびラジカル重合触媒とを含む水性溶液およ
び/ または分散液を布帛に付与した後、乾熱処理、水蒸
気処理、放射線照射、紫外線照射またはマイクロ波照射
等により重合させる方法がある。And the like. As a specific treatment method, the fermented rice extract of the component (a) and the components (b) to (d)
After applying an aqueous solution and / or dispersion containing the compound of formula (1) and a radical polymerization catalyst to the fabric, the fabric is polymerized by dry heat treatment, steam treatment, radiation irradiation, ultraviolet irradiation, microwave irradiation, or the like.
【００４０】成分（ｂ）の使用量は水性処理液中１〜１
０重量％の範囲であるのが好ましく、また成分（ｂ）：
（ｃ）：（ｄ）の重量割合は１：０．１〜１：０．１〜
１の範囲であるのが好ましい。溶媒としては、水もしく
は可溶性の溶媒（アルコール類、ジメチルホルムアミ
ド、アセトン、ジメチルスルホキシド等）の混合溶媒を
使用することができる。ラジカル重合触媒としては、水
溶性もしくは水不溶性の過酸化物やアゾ化合物が用いら
れる。これらの成分の混合物が水に易溶性でない場合
は、ノニオン、アニオン等の界面活性剤を添加してもよ
い。The amount of component (b) used is 1 to 1 in the aqueous treating solution.
It is preferably in the range of 0% by weight, and component (b):
The weight ratio of (c) :( d) is 1: 0.1-1: 0.1-
It is preferably in the range of 1. As the solvent, water or a mixed solvent of a soluble solvent (alcohols, dimethylformamide, acetone, dimethylsulfoxide, etc.) can be used. As the radical polymerization catalyst, a water-soluble or water-insoluble peroxide or azo compound is used. If the mixture of these components is not readily soluble in water, a surfactant such as nonionic or anionic may be added.
【００４１】本発明の方法において、米発酵エキス成分
として、その水溶液を用いる場合、この水溶液の安定化
のため、すなわち、ガムアップを防止するために、異種
の蛋白質、例えば、アテロコラーゲン、加水分解コラー
ゲン、ゼラチン、カゼイン等を添加してもよい。そし
て、この異種蛋白質の使用量は、米発酵エキスに対して
２０〜１００重量％であるのが好ましい。１００重量％
以上の場合には、皮膜形成が悪く、また風合が粗硬にな
ることがある。In the method of the present invention, when an aqueous solution thereof is used as a rice fermentation extract component, in order to stabilize the aqueous solution, that is, to prevent gumming up, different types of proteins such as atelocollagen and hydrolyzed collagen are used. , Gelatin, casein and the like may be added. The amount of the heterologous protein used is preferably 20 to 100% by weight based on the fermented rice extract. 100% by weight
In the above cases, the film formation is poor and the feeling may be coarse and hard.
【００４２】[0042]
【実施例】以下、実施例により本発明を具体的に説明す
る。なお、例中、部は重量部を示す。また、例中に示し
た特性の表示は次の方法によったものである。 （１）固着率 〔（処理後の重量−処理前の重量）／処理前の重量〕×
１００（％） （２）米発酵エキスの固着率 実施例の固着率−比較例（米発酵エキスを含まないも
の）の固着率（％） （３）洗濯試験 ＪＩＳ Ｌ−０２１７ １０３法 （４）吸水試験 滴下法：ＪＩＳ Ｌ−１０９６ Ａ法 （５）吸放湿試験 出光法：絶乾状態にした布帛を２３℃×３０％ＲＨと４
０℃×８０％ＲＨの状態にして、吸放湿量差を評価す
る。The present invention will be described below in detail with reference to examples. In addition, in an example, a part shows a weight part. The display of the characteristics shown in the examples is based on the following method. (1) Fixing rate [(weight after treatment-weight before treatment) / weight before treatment] x
100 (%) (2) Sticking rate of rice fermented extract Sticking rate of Example-Sticking rate of comparative example (without rice fermented extract) (%) (3) Washing test JIS L-0217103 method (4) Water absorption test Drop method: JIS L-1096 A method (5) Moisture absorption / desorption test Idemitsu method: Cloth in absolutely dry state is stored at 23 ° C. × 30% RH and 4
Under the condition of 0 ° C. × 80% RH, the difference in moisture absorption / release is evaluated.
【００４３】（６）制電性試験 摩擦帯電圧：ＪＩＳ Ｌ−１０９４ Ｂ法 （７）呈色判定 ＣＢＢ（クーマシー・ブリリアント・ブルー）によるプ
ロティン呈色反応の手順 １. クーマシー・ブリリアント・ブルーＲ２５０（和光
純薬工業（株）製）０．５ｇをメタノール２５０ｍｌに
攪拌溶解し、次いで水２５０ｍｌを加えてＣＢＢ呈色指
示薬とする。(6) Antistatic Test Friction Charge Voltage: JIS L-1094 B Method (7) Color Determination Judgment of Protein Color Reaction by CBB (Coomassie Brilliant Blue) 1. Coomassie Brilliant Blue R250 ( 0.5 g of Wako Pure Chemical Industries, Ltd.) is stirred and dissolved in 250 ml of methanol, and then 250 ml of water is added to obtain a CBB color indicator.
【００４４】２. 試験片にスポイトで１滴のＣＢＢ呈色
液を滴下する。 ３. 速やかに水洗し、乾燥する。 また、下記の実施例で用いた米発酵エキス水溶液は、米
発酵エキス成分としてアミノ酸１．４％、γ−オリザノ
ール０．１％、フェルラ酸０．１％を含み、さらにアル
コール１９．０％および各種ミネラル３．０％を含む水
溶液であり、アミノ酸組成成分として、アルギニン、リ
ジン、トリプトファン、ヒスチジン、フェニルアラニ
ン、チロシン、ロイシン、イソロイシン、メチオニン、
バリン、アラニン、グリシン、プロリン、グルタミン
酸、セリン、スレオニン、アスパラギン酸を含むもので
ある。2. One drop of the CBB coloring solution is dropped on the test piece with a dropper. 3. Rinse immediately with water and dry. The aqueous solution of rice fermented extract used in the following examples contains 1.4% amino acid, 0.1% γ-oryzanol, 0.1% ferulic acid as components of the rice fermented extract, and further contains 19.0% alcohol and It is an aqueous solution containing 3.0% of various minerals. As amino acid composition components, arginine, lysine, tryptophan, histidine, phenylalanine, tyrosine, leucine, isoleucine, methionine,
It contains valine, alanine, glycine, proline, glutamic acid, serine, threonine, and aspartic acid.
【００４５】実施例１ 次の組成の処理液を調製した。 米発酵エキス水溶液（（株）相生発酵製） １５．０部 前記構造式（２）の化合物（第一工業製薬（株）製） ４．０部 前記構造式（１２）の化合物（日本触媒（株）製） ０．２部 アゾ系重合触媒（和光純薬工業（株）製Ｖ−５０） ０．２部 水を加えて １００部 上記の処理液をポリエステルデシン織物（目付１２２ｇ
／ｍ2 ）に含浸させ、マングルで含浸率６０％に絞った
後、水蒸気熱処理を１１０℃で８分間行い、湯洗、乾
燥、ヒートセットを行った。得られた加工布帛は、１．
８％の固着率（すなわち処理前と比較して１．８％の重
量増加）を示した。また、米発酵エキスの固着率は０．
１３％であった。Example 1 A treatment liquid having the following composition was prepared. Rice fermented extract aqueous solution (manufactured by Aioi Fermentation) 15.0 parts Compound of the structural formula (2) (Daiichi Kogyo Seiyaku Co., Ltd.) 4.0 parts Compound of the structural formula (12) (Nippon Shokubai ( Co., Ltd.) 0.2 parts Azo-based polymerization catalyst (W-50, manufactured by Wako Pure Chemical Industries, Ltd.) 0.2 parts Water is added to 100 parts.
/ M 2 ), and squeezed by a mangle to an impregnation rate of 60%, followed by steam heat treatment at 110 ° C. for 8 minutes, washing with hot water, drying and heat setting. The obtained processed fabric is:
An adhesion rate of 8% (i.e. a 1.8% weight increase compared to before treatment) was shown. Moreover, the sticking rate of the rice fermented extract is 0.1.
13%.
【００４６】比較例１ 米発酵エキス水溶液を用いなかった以外は全く同じ条件
下に、実施例１の操作を繰り返した。得られた加工布帛
は１．６７％の固着率を示した。 比較例２ 次の組成の処理液を調製した。Comparative Example 1 The procedure of Example 1 was repeated under exactly the same conditions except that the aqueous solution of rice fermented extract was not used. The obtained processed fabric showed a sticking ratio of 1.67%. Comparative Example 2 A treatment liquid having the following composition was prepared.
【００４７】 米発酵エキス水溶液（（株）相生発酵製） １５．０部 ブロック化イソシアネートのウレタンポリマー ４．０部 （第一工業製薬（株）製エラストロンＭＦ−９） 脂肪酸金属塩ウレタン触媒 ０．５部 （第一工業製薬（株）製エラストロンキャタリスト６４） 水を加えて １００部 上記の処理液をポリエステルデシン織物（目付１２２ｇ
／ｍ2 ）に含浸させ、マングルで含浸率６０％に絞った
後、１２０℃で１分間の乾燥後、１６０℃で３０秒間熱
処理を行った。得られた加工布帛は１．６％の固着率を
示した。また、米発酵エキスの固着率は０．０５％であ
った。Aqueous solution of rice fermented extract (manufactured by Aioi Fermentation Co., Ltd.) 15.0 parts Urethane polymer of blocked isocyanate 4.0 parts (Elastron MF-9 manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) Fatty acid metal salt urethane catalyst 0. 5 parts (Elastron Catalyst 64, manufactured by Daiichi Kogyo Seiyaku Co., Ltd.) 100 parts by adding water.
/ M 2 ), squeezed to an impregnation rate of 60% with a mangle, dried at 120 ° C. for 1 minute, and then heat-treated at 160 ° C. for 30 seconds. The obtained processed fabric showed a fixation rate of 1.6%. Moreover, the sticking rate of the rice fermented extract was 0.05%.
【００４８】実施例２ 次の組成の処理液を調製した。 米発酵エキス水溶液（（株）相生発酵製） ２０．０部 前記構造式（４）の化合物（第一工業製薬（株）製） ５．０部 前記構造式（９）の化合物（日本触媒（株）製） １．０部 過硫酸アンモニウム ０．５部 水を加えて １００部 上記の処理液をポリエステルスパン織物（目付１３０ｇ
／ｍ2 ）に含浸させ、マングルで含浸率６５％に絞った
後、マイクロ波処理装置アポロテックス（市金工業
（株）製、周波数２４５０ＭＨｚ、出力６．０ｋＷで照
射しながら、直接水蒸気１．０ｋｇ／ｃｍ2 、間接水蒸
気３．０ｋｇ／ｃｍ2 の条件）で、１５分間の水蒸気処
理を行った。次いで、湯洗、乾燥、ヒートセットを行っ
た。得られた加工布帛は２．０％の固着率を示した。ま
た、米発酵エキスの固着率は０．２％であった。Example 2 A treatment liquid having the following composition was prepared. Rice fermented extract aqueous solution (manufactured by Aioi Fermentation Co., Ltd.) 20.0 parts Compound of the structural formula (4) (Daiichi Kogyo Seiyaku Co., Ltd.) 5.0 parts Compound of the structural formula (9) (Nippon Shokubai ( 1.0 part Ammonium persulfate 0.5 part Water was added to 100 parts The above-mentioned treatment liquid was applied to a polyester spun fabric (basis weight: 130 g).
/ M 2 ), narrowed to an impregnation ratio of 65% with a mangle, and then directly irradiated with steam at a power of 6.0 kW while irradiating with a microwave processing apparatus Apollo-Tex (manufactured by Ichikin Industry Co., Ltd., frequency 2450 MHz, output 6.0 kW). 0 kg / cm 2 and indirect steam 3.0 kg / cm 2 ) for 15 minutes. Next, washing with hot water, drying and heat setting were performed. The obtained processed fabric showed a sticking rate of 2.0%. The sticking rate of the rice fermented extract was 0.2%.
【００４９】比較例３ 米発酵エキス水溶液を用いなかった以外は全く同じ条件
下に、実施例２の操作を繰り返した。得られた加工布帛
は１．８％の固着率を示した。 実施例３ 次の組成の処理液を調製した。Comparative Example 3 The procedure of Example 2 was repeated under exactly the same conditions except that the aqueous solution of rice fermented extract was not used. The obtained processed fabric showed a sticking ratio of 1.8%. Example 3 A treatment liquid having the following composition was prepared.
【００５０】 米発酵エキス水溶液（（株）相生発酵製） １０．０部 前記構造式（５）の化合物 ４．５部 前記構造式（１２）の化合物（日本触媒（株）製） １．０部 メタクリル酸 １．０部 過硫酸アンモニウム ０．７部 水を加えて １００部 上記の処理液をポリエステルニット織物（天竺組織）に
含浸させ、マングルで含浸率１００％に絞った後、窒素
雰囲気中でハンデグラフ型静電加速器により１．５Ｍｅ
Ｖ、５０μＡの電子線を３Ｍｒａｄ照射した。次いで、
９０℃で１分間湯洗し、次いで乾燥、ヒートセット（１
８０℃×３０秒）を行った。得られた加工布帛は２．４
％の固着率を示した。また、米発酵エキスの固着率は
０．２％であった。Rice fermented extract aqueous solution (manufactured by Aioi Fermentation) 10.0 parts Compound of the structural formula (5) 4.5 parts Compound of the structural formula (12) (manufactured by Nippon Shokubai Co., Ltd.) 1.0 Part 1.0 part of methacrylic acid 0.7 part of ammonium persulfate 100 parts by adding water 100 parts of the above treatment liquid is impregnated into a polyester knitted fabric (sheet woven structure), squeezed with a mangle to an impregnation rate of 100%, and then in a nitrogen atmosphere. 1.5Me with a handicap type electrostatic accelerator
V, an electron beam of 50 μA was irradiated at 3 Mrad. Then
Wash with hot water at 90 ° C for 1 minute, then dry and heat set (1
(80 ° C. × 30 seconds). The obtained processed fabric is 2.4
% Sticking rate. The sticking rate of the rice fermented extract was 0.2%.
【００５１】比較例４ 米発酵エキス水溶液を用いなかった以外は全く同じ条件
下に、実施例３の操作を繰り返した。得られた加工布帛
は２．２％の固着率を示した。上記実施例１〜３および
比較例１〜４で得られた加工布帛について、前記の評価
方法により性能評価を行った。その結果を表に示す。Comparative Example 4 The procedure of Example 3 was repeated under exactly the same conditions except that the aqueous solution of rice fermented extract was not used. The obtained processed fabric exhibited a sticking ratio of 2.2%. Performance evaluation was performed on the processed fabrics obtained in Examples 1 to 3 and Comparative Examples 1 to 4 by the above-described evaluation method. The results are shown in the table.
【００５２】[0052]
【表１】 [Table 1]
【００５３】上記の結果から、本発明の米発酵エキスを
重合させた加工布帛（実施例１〜３）は、比較例１〜４
で得られた加工布帛に比べて、帯電し易く、吸水性が悪
いなどの欠点が解消され、吸放湿性が顕著に改善されて
おり、また耐洗濯性にも優れるものであることがわか
る。From the above results, the processed fabrics obtained by polymerizing the fermented rice extract of the present invention (Examples 1 to 3) were compared with Comparative Examples 1 to 4.
As compared with the processed cloth obtained in the above, the drawbacks such as easy charging and poor water absorption are eliminated, the moisture absorption / release properties are remarkably improved, and the washing resistance is excellent.
【００５４】[0054]
【発明の効果】以上に詳述したように、本発明の米発酵
エキス固定化布帛は、帯電し易く、吸水性が悪いなどの
欠点がなく、吸放湿性が顕著に改善されており、また天
然由来の米発酵エキスが繊維表面に固定されていること
により、触ったときの触感がしっとり、暖かく感じら
れ、米発酵エキスの付着率が低いにもかかわらずソフト
な風合いを呈するものであり、保湿性、スキンケア効果
も期待でき、しかもグラフト重合による固着のため、耐
洗濯性にも優れる。As described in detail above, the rice-fermented extract-immobilized fabric of the present invention is easily charged, has no disadvantages such as poor water absorption, and has a remarkably improved moisture absorption / desorption property. Because the naturally-derived fermented rice extract is fixed to the fiber surface, the feel when touched is moist and felt warm, and it has a soft texture despite the low adhesion of the fermented rice extract, It can be expected to have moisturizing properties and skin care effects, and also has excellent washing resistance due to fixation by graft polymerization.
【００５５】本発明によって、このような優れた特性を
有する布帛を効率良く加工することができ、この布帛は
肌着、インナー、ベビー服、寝具、フェイスマスクなど
肌と直接に触れる繊維素材であっても、快適に、安心し
て着用することができ、広く応用が期待される。According to the present invention, a cloth having such excellent characteristics can be processed efficiently, and this cloth can be a fiber material that directly touches the skin, such as underwear, innerwear, baby clothes, bedding, and face mask. It can be worn comfortably and safely, and is expected to be widely applied.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ａ６１Ｋ 7/00 Ａ６１Ｋ 7/00 Ｌ Ｄ０６Ｍ 13/00 Ｄ０６Ｍ 13/00 13/48 13/48 15/27 15/27 (72)発明者 滝ヶ浦 良成 石川県能美郡根上町浜町ヌ167番地 小松 精練株式会社内 Ｆターム(参考） 4C083 AA111 AA112 AB37 AC181 AC182 AC851 AC852 AC901 AC902 CC02 DD12 EE13 FF04 4L033 AA02 AA04 AA07 AA08 AB05 AB06 AB07 AC10 AC15 BA00 BA91 CA18 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) A61K 7/00 A61K 7/00 L D06M 13/00 D06M 13/00 13/48 13/48 15/27 15 / 27 (72) Inventor, Yoshinari Takigaura 167, Hamacho, Negami-cho, Nomi-gun, Ishikawa Prefecture F-term (reference) 4C083 AA111 AA112 AB37 AC181 AC182 AC851 AC852 AC901 AC902 CC02 DD12 EE13 FF04 4L033 AA02 AA04 AA07 AA08 AB05 AB06 AB07 AC10 AC15 BA00 BA91 CA18
Claims (2)
を表し、ＺはＨまたは−ＣＨ3 を表し、ａおよびｂはそ
れぞれａ＋ｂが０〜５０となるような０または正の整数
を表し、ｘおよびｙはそれぞれｘ＋ｙが０〜３０となる
ような０または正の整数を表す。ただし、ａ＋ｂ＋ｘ＋
ｙは１０以上であるものとする〕で示される２官能性化
合物、 （ｃ）水酸基、カルボキシル基、アミノ基、スルホン酸
基またはリン酸基を含む化合物、および （ｄ）アジリジン基を含む化合物、の重合体を布帛上に
固定化してなる米発酵エキス固定化布帛。1. The following components: (a) a fermented rice extract; (b) the following general formula (1): [In the above formula, R is directly bonded. Or -C n H 2n - (where n is an integer of 1 to 6)
Z represents H or —CH 3 , a and b each represent 0 or a positive integer such that a + b is 0 to 50, and x and y are each 0 such that x + y is 0 to 30. Or represents a positive integer. However, a + b + x +
y is 10 or more], (c) a compound containing a hydroxyl group, a carboxyl group, an amino group, a sulfonic acid group or a phosphoric acid group, and (d) a compound containing an aziridine group, A cloth fixed with a rice fermented extract obtained by immobilizing the polymer of Example 1 on a cloth.
を表し、ＺはＨまたは−ＣＨ3 を表し、ａおよびｂはそ
れぞれａ＋ｂが０〜５０となるような０または正の整数
を表し、ｘおよびｙはそれぞれｘ＋ｙが０〜３０となる
ような０または正の整数を表す。ただし、ａ＋ｂ＋ｘ＋
ｙは１０以上であるものとする〕で示される２官能性化
合物、 （ｃ）水酸基、カルボキシル基、アミノ基、スルホン酸
基またはリン酸基を含む化合物、および （ｄ）アジリジン基を含む化合物、を含む水性処理液を
布帛に付与した後、上記各成分を布帛上で重合せしめる
ことを含む米発酵エキス固定化布帛の製造方法。2. The following components: (a) a fermented rice extract; (b) the following general formula (1): [In the above formula, R is directly bonded. Or -C n H 2n - (where n is an integer of 1 to 6)
The stands, Z is H or -CH 3, a and b are respectively a + b represents 0 or a positive integer such that 0 to 50, respectively x and y are as x + y is 0 to 30 0 Or represents a positive integer. However, a + b + x +
y is 10 or more], (c) a compound containing a hydroxyl group, a carboxyl group, an amino group, a sulfonic acid group or a phosphoric acid group, and (d) a compound containing an aziridine group, A method for producing a rice-fermented extract-immobilized cloth, comprising applying an aqueous treatment liquid containing the composition to a cloth and polymerizing the above components on the cloth.