JP2002294525A - Twisted crimped yarn, carpet and moquette - Google Patents
Twisted crimped yarn, carpet and moquetteInfo
- Publication number
- JP2002294525A JP2002294525A JP2001102177A JP2001102177A JP2002294525A JP 2002294525 A JP2002294525 A JP 2002294525A JP 2001102177 A JP2001102177 A JP 2001102177A JP 2001102177 A JP2001102177 A JP 2001102177A JP 2002294525 A JP2002294525 A JP 2002294525A
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- carpet
- crimped yarn
- twisted
- moquette
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、撚糸セットを施し
た捲縮糸、この捲縮糸を用いてなるカーペットおよびモ
ケットに関するものである。詳しくは、柔らかな風合い
で肌触りが良く、特に温湿度の高い季節においても快適
な肌触りを提供し、さらに腰が強いと共に耐久性に優れ
たカーペットまたはモケットを与え得る捲縮糸、並びに
該捲縮糸を使用した家庭用ラグカーペット、モケットに
関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a crimped yarn provided with a twisted yarn set, and a carpet and a moquette using the crimped yarn. In detail, a crimped yarn that can provide a soft touch and a good touch, provides a comfortable touch even in a high temperature and humidity season, and gives a carpet or moquette that is strong and durable, and the crimped yarn. It relates to household rug carpets and moquettes using yarn.
【0002】[0002]
【従来の技術】カーペットの主な使用目的は、インテリ
アとして用途によく適応した雰囲気を提供することであ
り、色や柄はもちろん、風合いやタッチ、ボリューム感
などの種々の特性が、用途に合わせて要求されている。
特に家庭で使用するラグカーペットにおいては、そのク
ッション性や、インテリアとしての空間の演出が優れる
こと以外に、保温性に優れ、しかも直接肌がカーペット
に接触することから、肌触りが良く、柔らかな風合いの
カーペットが好まれている。2. Description of the Related Art The main purpose of using carpets is to provide an atmosphere that is well suited to the application as an interior. Various characteristics such as texture, touch, and volume, as well as colors and patterns, are tailored to the application. Required.
Especially for rug carpets used at home, in addition to its excellent cushioning and interior space effects, it also has excellent heat retention, and because the skin directly contacts the carpet, it feels good and soft texture Carpets are preferred.
【0003】家庭用ラグカーペットに上記の要求特性を
付与することを目的として、近年ではポリエステル繊維
やポリプロピレン繊維を主原料とする捲縮糸を使用した
カーペットが作製されている。すなわち、ポリエステル
繊維やポリプロピレン繊維の捲縮糸からなるカーペット
は、その風合いが柔らかく、一般には原着糸を使用する
ことから鮮やかな色調を発現することができる。しか
し、これらの繊維素材からなるカーペットは、確かにカ
ーペットを製造した直後の未使用のときには、風合いが
柔らかく肌触りが優れているが、捲縮糸の捲縮耐久性が
劣るため、すぐに捲縮がへたり、カーペットとしての品
質や高級感が低下してしまうという問題があった。For the purpose of imparting the above-mentioned required properties to household rug carpets, carpets using crimped yarns mainly made of polyester fibers or polypropylene fibers have been produced in recent years. That is, a carpet made of a crimped yarn of a polyester fiber or a polypropylene fiber has a soft texture, and generally can exhibit a vivid color tone because it uses an original yarn. However, carpets made of these fiber materials have a soft texture and excellent touch when not in use immediately after the production of the carpet, but are immediately crimped because of poor crimp durability of the crimped yarn. There is a problem in that the quality and luxury of the carpet are deteriorated.
【0004】また、これらのなかでも特にポリエステル
繊維からなる捲縮糸においては、短繊維を使用する場合
が多く、このためにカーペットの遊び毛が発生して汚く
なると共に、ボリューム感も低下してしまうという問題
があった。[0004] Among these, particularly in the case of crimped yarns made of polyester fibers, short fibers are often used, and as a result, carpet play hairs are generated and become dirty, and the volume feeling is reduced. There was a problem that it would.
【0005】一方、家庭用としての風合が柔らかで肌触
りのすぐれたカーペットを作製するために、ポリアミド
捲縮糸を使用し、この捲縮糸の繊度を細くしたり、また
は断面を異形にすることについても従来からも数多く提
案されている。単繊維繊度を細くしたものをカットパイ
ルとして使用すると、確かにカーペットの風合いは柔ら
かくなるものの、単に細繊度にしただけでは清涼感に乏
しく、特に高温多湿のシーズンには肌への接触が暑苦し
く快適な使用にはほど遠いものであった。[0005] On the other hand, in order to produce a carpet having a soft feel and good touch for home use, a polyamide crimped yarn is used, and the fineness of the crimped yarn is reduced or the cross section is made irregular. Many things have been proposed in the past. If you use a cut fiber with a single fiber fineness as a cut pile, the texture of the carpet will certainly be softer, but simply making it fine will not give a refreshing feeling, especially when it is hot and humid season, the contact with the skin will be hot and comfortable It was far from perfect use.
【0006】また、カーペット用捲縮糸の単繊維の断面
を扁平にする試みについても、従来から数多くなされて
はいる。例えば、特開昭57−66134号公報には、
扁平度が1.2以上で捲縮率が4.0%以上の捲縮糸を
芯部に、この捲縮糸より小さい扁平度と捲縮率を有する
捲縮糸を鞘部に配置したカーペット用複合捲縮糸の提案
がなされている。しかし、この提案では2種の捲縮糸を
混繊することにより、ある程度のスパンタッチの風合い
を達成することが可能であるが、具体的な記載例におい
ても捲縮糸の断面扁平度が1.2程度と小さいために、
単糸の曲げ剛性が高く肌触りの良い柔軟なタッチのカー
ペットを得ることは困難であった。[0006] In addition, many attempts have been made to flatten the cross section of a single fiber of a crimped yarn for carpet. For example, JP-A-57-66134 discloses that
A carpet in which a crimped yarn having a flatness of 1.2 or more and a crimping rate of 4.0% or more is disposed in a core portion, and a crimped yarn having a flatness and a crimping ratio smaller than the crimped yarn is disposed in a sheath portion. Of composite crimped yarns has been proposed. However, in this proposal, by blending two types of crimped yarns, it is possible to achieve a certain degree of span-touch texture. However, even in a specific description example, the cross-sectional flatness of the crimped yarn is 1%. .2 so small
It has been difficult to obtain a carpet with a soft touch that has a high bending stiffness of a single yarn and a good touch.
【0007】また、特開昭62−117505号公報に
は、断面の長軸が50μ以上、長軸と短軸の長さの比が
15:1〜3:1の扁平形状であり、かつ実質的に捩れ
のないパイル糸を用いたカーペットが提案されている。
この提案によるカーペットは確かにベロア感、ソフト感
が従来品よりも改良されたものではあるが、長軸の長さ
が50μ以上と単繊維繊度が太くいため、柔らかい風合
いには限界があり、直接肌が接触する家庭用のラグカー
ペットとしては不適当なものであった。Japanese Patent Application Laid-Open No. Sho 62-117505 discloses a flat shape in which the major axis of the cross section is 50 μm or more, and the ratio of the major axis to the minor axis is 15: 1 to 3: 1. There has been proposed a carpet using a pile yarn having no twist.
Although the carpet according to this proposal has certainly improved the velor feeling and the soft feeling compared to the conventional product, the length of the major axis is 50μ or more and the single fiber fineness is large, so there is a limit to the soft texture, It was unsuitable as a household rug carpet that comes in contact with the skin.
【0008】さらに、特開平4−272268号公報に
も、光沢改善を主目的とした扁平糸使いのカーペットの
提案がなされているが、この提案においても、扁平糸の
単繊維繊度については何ら考慮が払われていないため、
カーペットの光沢は改善されるものの、その触感は十分
に柔らかいといえるものではなかった。Further, Japanese Patent Application Laid-Open No. 4-272268 also proposes a carpet using a flat yarn mainly for improving the gloss. In this proposal, however, no consideration is given to the single fiber fineness of the flat yarn. Has not been paid,
Although the gloss of the carpet was improved, its touch was not sufficiently soft.
【0009】つまり、上記ポリアミド捲縮糸を用いる従
来の提案は、いずれも家庭用の直接肌の触れる肌触りの
優しいカーペットを意識したものではなく、またこれら
の提案に記載されている扁平糸の単繊維繊度はいずれも
10デニール以上と太いものであった。In other words, none of the conventional proposals using the above-described polyamide crimped yarns are conscious of carpets which are easy to use for home use and which are in direct contact with the skin. The fiber fineness was as thick as 10 denier or more.
【0010】さらに特開平2000−220050号公
報には、単糸繊度を3.0デニール〜8.0デニールと
細くすることでより柔軟な風合いの家庭用カーペットが
提案されている。Further, Japanese Patent Application Laid-Open No. 2000-220050 proposes a carpet for domestic use having a softer texture by reducing the fineness of single yarn to 3.0 denier to 8.0 denier.
【0011】[0011]
【発明が解決しようとする課題】しかし、該提案に記載
の内容では、風合いを柔らかくすることのみに注目して
いるため、確かにカットパイルを用いるなどにより肌触
りは優れているものの、ともすれば該カットパイルであ
ることが高温多湿状況では暑苦しくなり、清涼感を得る
にはほど遠いものであった。すなわち、上記提案のカー
ペットは日本の冬場においては好ましく使用できても、
相対的に高温多湿である夏を中心とした春から秋にかけ
てのシーズンに好ましく使用できるカーペットではなか
ったものである。また、上記カーペットにおいては、カ
ットパイルであるためパイルがへたりやすく家庭用のカ
ーぺットにふさわしい耐久性は持ち合わせていなかっ
た。However, in the content of the proposal, attention is paid only to softening the texture, and although the touch is excellent by using a cut pile, etc. The cut pile was hot and hot in hot and humid conditions, and was far from a refreshing feeling. In other words, even if the carpet proposed above can be used preferably in winter in Japan,
It is not a carpet that can be used preferably in the spring and autumn seasons, mainly in summer, when the temperature is relatively high and high. Further, in the above carpet, since the pile is a cut pile, the pile is easily set and has no durability suitable for a carpet for home use.
【0012】一方、地組織にパイルを織り込むことで得
られるモケットにおいて、綿やレーヨンを使用した家庭
用ラグの提案は数多くされている。しかし、これらはい
ずれも短繊維を使用しているため、使用中のパイルを構
成している繊維の脱落が激しく、耐久性に乏しいという
欠点があった。このモケットのパイルに捲縮を付与した
ポリアミドの細繊度捲縮糸を使用する例は見あたらな
い。On the other hand, in moquettes obtained by weaving a pile into a ground structure, there have been many proposals for household rugs using cotton or rayon. However, since all of them use short fibers, there is a drawback that fibers constituting the pile in use fall off sharply and have poor durability. There is no example in which a crimped yarn of polyamide having a crimp applied to the pile of this moquette is used.
【0013】本発明は、上述した従来技術における問題
点の解決を課題として検討した結果、達成されたもので
ある。したがって、本発明の課題は、柔らかな風合いで
清涼感のある肌触りであり、かつ耐久性に優れたカーペ
ットまたはモケットを与え得る捲縮糸、および特に春か
ら秋にかけての高温多湿の環境化においても好ましく使
用可能な家庭用ラグカーペット、家庭用モケット提供す
ることにある。[0013] The present invention has been achieved as a result of studying solving the problems in the above-mentioned prior art as a problem. Therefore, an object of the present invention is to provide a crimped yarn that can provide a carpet or moquette having a soft texture and a refreshing feel and excellent durability, and particularly in an environment of high temperature and high humidity from spring to autumn. An object of the present invention is to provide a household rug carpet and a home moquette which can be preferably used.
【0014】[0014]
【課題を解決するための手段】上記課題を解決するため
に、本発明の捲縮糸は、主として次の構成を有する。す
なわち、単糸繊度が3.0〜7.0デシテックス、総繊
度が200〜700デシテックス、沸騰水処理後の捲縮
伸長率が5〜20%のポリアミドマルチフィラメント捲
縮糸であり、撚数が200〜2000t/mの片撚り、
または撚数が200〜2000t/mの下撚りと上撚り
が施された諸撚りを有することを特徴とする撚り捲縮糸
である。Means for Solving the Problems In order to solve the above problems, the crimped yarn of the present invention mainly has the following constitution. That is, it is a polyamide multifilament crimped yarn having a single yarn fineness of 3.0 to 7.0 decitex, a total fineness of 200 to 700 decitex, and a crimp elongation of 5 to 20% after boiling water treatment. 200-2000 t / m single twist,
Alternatively, it is a twisted crimped yarn having a twist of 200 to 2000 t / m, which is subjected to priming and plying.
【0015】そして、本発明の撚り捲縮糸においては、
次の(1)〜(2)がそれぞれ好ましい態様として挙げ
られる。 (1)諸撚りを有する撚り捲縮糸が2本または3本から
構成されていること。 (2)ポリアミドマルチフィラメントの単繊維断面が、
変形度が1.5〜5.0のY型断面もしくは扁平度が
1.5〜5.0の扁平断面であること。In the twisted crimped yarn of the present invention,
The following (1) and (2) are each preferred embodiments. (1) Twisted crimped yarns having multiple twists are composed of two or three. (2) The single fiber cross section of the polyamide multifilament is
A Y-shaped section having a degree of deformation of 1.5 to 5.0 or a flat section having a flatness of 1.5 to 5.0.
【0016】また、本発明のカーペットはループパイル
である表糸と、この表糸をタフトした基布と、この基布
の裏に貼りつけたバッキング材とから構成されたカーペ
ットであって、表糸が、前記記載の撚り捲縮糸を含むこ
とを特徴とする。さらに本発明のループパイルは主とし
て次の構成を有する。ループパイルである表糸と、この
表糸を支持する基材と、この基材の裏に貼りつけたバッ
キング材とから構成されたモケットであって、表糸が前
記記載の撚り捲縮糸を含むことを特徴とする。また本発
明のカーペットまたはモケットは、起毛処理またはウォ
ータージェットパンチ処理を施したものであることがよ
り好ましい。Further, the carpet of the present invention is a carpet comprising a surface yarn which is a loop pile, a base fabric obtained by tufting the surface yarn, and a backing material adhered to the back of the base fabric. The yarn includes the twisted crimped yarn described above. Further, the loop pile of the present invention mainly has the following configuration. A surface yarn that is a loop pile, a substrate supporting the surface yarn, and a moquette composed of a backing material attached to the back of the substrate, wherein the surface yarn is the twisted crimped yarn described above. It is characterized by including. Further, the carpet or moquette of the present invention is more preferably subjected to a brushing treatment or a water jet punch treatment.
【0017】[0017]
【発明の実施の形態】以下に、本発明についてさらに詳
細に説明する。本発明の捲縮糸は、ポリアミドマルチフ
ィラメントにより構成されるが、従来のカーペット用捲
縮糸からみると単糸繊度、総繊度とも特定の細い範囲の
捲縮糸撚糸し、かつループパイルとして用いることによ
り、柔軟な肌触りでかつ清涼感があり、さらに耐久性に
優れた風合いのカーペットとすることができる。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in more detail. The crimped yarn of the present invention is composed of polyamide multifilament, but when viewed from the conventional crimped yarn for carpet, the single yarn fineness and the total fineness are both crimped yarns in a specific narrow range and used as a loop pile. This makes it possible to provide a carpet having a soft touch, a refreshing feeling, and a texture excellent in durability.
【0018】具体的には単糸繊度が3.0〜7.0デシ
テックス、総繊度が200〜700デシテックスの細繊
度のポリアミドマルチフィラメントを単独で片撚りした
捲縮糸、もしくは下撚×上撚が施された諸撚りを有する
撚り捲縮糸である。Specifically, a crimped yarn obtained by single twisting a polyamide multifilament having a fineness of single yarn fineness of 3.0 to 7.0 dtex and a total fineness of 200 to 700 dtex alone, or a priming × twisting Is a twisted crimped yarn having a ply twist.
【0019】本発明の撚り捲縮糸を構成するポリアミド
マルチフィラメントは、単繊維繊度が3.0〜7.0デ
シテックス、好ましくは4.5〜6.5デシテックスと
するものである。3.0デシテックスより細い単繊維繊
度であると、製糸が困難であるとともに、撚糸する際の
工程通過性も低下する。また使用に際しても摩擦に弱く
単糸切れが多発してしまい好ましくない。一方、単繊維
繊度が7.0デシテックスを越えると、本発明の特徴の
ひとつである柔らかな風合いが達成できなくなる。The polyamide multifilament constituting the twisted crimped yarn of the present invention has a single fiber fineness of 3.0 to 7.0 dtex, preferably 4.5 to 6.5 dtex. If the single fiber fineness is smaller than 3.0 decitex, it is difficult to make a yarn, and the processability in twisting is reduced. Also, it is not preferable because it is susceptible to friction and frequently breaks single yarns. On the other hand, when the single fiber fineness exceeds 7.0 decitex, the soft texture, which is one of the features of the present invention, cannot be achieved.
【0020】本発明の撚り捲縮糸を構成するポリアミド
マルチフィラメントは、総繊度が200〜700デシテ
ックス、好ましくは300〜500デシテックスとする
ものである。200デシテックスより細い総繊度である
と、製糸において毛羽が多く安定な捲縮糸が生産困難
で、かつ撚り数を多くしなければならず撚糸工程も不安
定となる。さらに該撚り捲縮糸としても総繊度が低く、
パイルとしてカーペットやモケットに使用する際、打ち
込み本数を多くする必要があり、工程が複雑となるなど
の問題を生じる。一方、総繊度が700デシテックスを
越えると、往々にして撚り捲縮糸の繊度が高くなり、カ
ーペットもしくはモケットにした際のパイルのタッチが
重厚になり清涼感に乏しくなってしまう。風合いが本発
明の最大の特徴である柔らかな風合いが達成できなくな
る。本発明における重厚感のないさらりとした肌触りを
得るためには、撚糸後の総繊度は400デシテックスか
ら1600デシテックス、好ましくは600デシテック
スから900デシテックスが好ましい範囲である。The polyamide multifilament constituting the twisted crimped yarn of the present invention has a total fineness of 200 to 700 dtex, preferably 300 to 500 dtex. If the total fineness is smaller than 200 decitex, it is difficult to produce a stable crimped yarn having a large amount of fluff in the yarn production, and the number of twists must be increased, and the twisting process becomes unstable. Furthermore, the total fineness is low even as the twisted crimped yarn,
When used as a pile for carpets and moquettes, it is necessary to increase the number of shots, causing problems such as complicated processes. On the other hand, when the total fineness exceeds 700 decitex, the fineness of the twisted and crimped yarn often increases, and the pile touch when carpet or moquette is formed becomes heavy, resulting in poor refreshing feeling. The soft texture, which is the most important feature of the present invention, cannot be achieved. In order to obtain a smooth touch without profound feeling in the present invention, the total fineness after twisting is preferably in the range of 400 to 1600 decitex, and more preferably 600 to 900 decitex.
【0021】さらに、本発明の撚り捲縮糸は、沸騰水処
理後の捲縮伸長率が5〜20%、好ましくは7.0〜1
5.0%とするものである。Further, the twisted crimped yarn of the present invention has a crimp elongation after boiling water treatment of 5 to 20%, preferably 7.0 to 1%.
5.0%.
【0022】本発明における沸騰水処理後の捲縮伸長率
とは、捲縮糸を無荷重状態で30分間沸騰水で浸漬処理
した後、平衡水分率まで乾燥し、次式により算出した値
であり、捲縮発現の程度を表す指標である。 捲縮伸長率(%)=[(L2−L1)/L1]×100 (ここで、L1、L2とは、L1:試料糸に2mg/dの
初荷重をかけ30秒経過した後に試料長50cmにマー
キングしたその長さ、L2:同試料に100mg/dの
定荷重をかけて30秒経過後に伸びた試料長をそれぞれ
意味する。The crimp elongation after boiling water treatment in the present invention is a value calculated by the following equation after immersing a crimped yarn in boiling water for 30 minutes under no load and then drying to equilibrium moisture content. Yes, and is an index indicating the degree of crimp development. Crimp elongation rate (%) = [(L 2 −L 1 ) / L 1 ] × 100 (where L 1 and L 2 are L 1 : an initial load of 2 mg / d is applied to the sample yarn for 30 seconds. The length marked at a sample length of 50 cm after the passage of time, L 2 : the length of the sample which elongated after a lapse of 30 seconds with a constant load of 100 mg / d applied to the sample.
【0023】沸騰水処理後の捲縮伸長率が5%に満たな
いと、撚糸後の捲縮発現が不足して最終的にカーペット
やモケットのパイルに用いたときに柔らかな風合いが得
られなくなる。一方、沸騰水処理後の捲縮伸長率が20
%を越えると、風合いが堅く、本発明の目的とする清涼
感が得られない。If the crimp elongation after the boiling water treatment is less than 5%, the crimping after twisting is insufficient and a soft texture cannot be finally obtained when used for piles of carpets and moquettes. . On the other hand, the crimp elongation after boiling water treatment is 20
%, The texture becomes firm and the desired refreshing feeling of the present invention cannot be obtained.
【0024】捲縮付与された捲縮糸において、巻き取り
直後に沸騰水処理後の伸長率が20%を越える場合であ
っても、例えば、捲縮原糸を別工程にて解舒しながら低
張力下で熱処理したり、チーズの状態で熱処理を施し
て、沸騰水処理後の捲縮率を20%以下に下げることに
より、本発明に用いることができるようになる。この低
張力下での熱処理は、チーズやボビンの状態で行っても
よいし、一旦巻き取った捲縮糸を解舒しながらセットし
てもよい。ここで付与する張力は、細かな微捲縮を残し
つつ、捲縮を適度におとすためのものであり、捲縮糸の
捲縮レベルや断面構造にもよるが、通常0.01g/d
〜0.15g/dの張力が選択される。熱処理の温度は
80〜130℃が好ましい。熱処理は、該当温度での浴
中処理や、乾熱・スチーム中の雰囲気内での処理、ある
いはこれらの雰囲気を通過させることなどの方法が採用
される。Even if the elongation of the crimped crimped yarn after the boiling water treatment immediately after winding exceeds 20%, for example, the unwound crimped yarn is unwound in a separate step. Heat treatment under low tension or heat treatment in the state of cheese to reduce the crimp rate after the boiling water treatment to 20% or less enables use in the present invention. The heat treatment under low tension may be performed in a cheese or bobbin state, or may be set while unwinding a crimped yarn once wound. The tension applied here is for keeping crimp moderately while leaving fine fine crimp, and although it depends on the crimp level and cross-sectional structure of the crimped yarn, it is usually 0.01 g / d.
A tension of 0.10.15 g / d is selected. The temperature of the heat treatment is preferably from 80 to 130C. As the heat treatment, a method such as a treatment in a bath at a corresponding temperature, a treatment in an atmosphere of dry heat or steam, or a method of passing through such an atmosphere is employed.
【0025】本発明においては、要は、撚糸する前の時
点において捲縮糸の沸騰水処理後の捲縮率が5〜20%
であれば、通常、撚り捲縮糸としての沸騰水処理後の捲
縮率が5〜20%となる。In the present invention, the point is that the crimping ratio of the crimped yarn after the boiling water treatment before the twisting is 5 to 20%.
If so, the crimping ratio after the boiling water treatment as a twisted crimped yarn is usually 5 to 20%.
【0026】本発明の撚り捲縮糸においては、単独で片
撚りを施した撚り捲縮糸である。該片撚りにおいては、
撚り数は200〜2000個/m、好ましくは400〜
1500個/mである。200個/mより小さいと、撚
りの効果が小さく、カーペットまたはモケットにした
際、パイルが横方向に広がり、肌触りとしての清涼感が
乏しいものになってしまう。また、2000個/mより
多いと、撚り捲縮糸の捩れが強くなりすぎ、タフトが困
難になったり、カーペット上でフリーズ感が強くなり柔
軟な感触がなくなってしまう。The twisted crimped yarn of the present invention is a single twisted crimped yarn. In the single twist,
The number of twists is 200 to 2000 pieces / m, preferably 400 to
It is 1500 pieces / m. If it is less than 200 pieces / m, the effect of twisting is small, and when carpet or moquette is used, the pile spreads in the horizontal direction, and the refreshing feeling as a touch is poor. On the other hand, if it is more than 2000 pieces / m, the twist of the twisted and crimped yarn becomes too strong, and the tuft becomes difficult, and the feeling of freezing on the carpet becomes strong, and the soft touch is lost.
【0027】さらに本発明の撚り捲縮糸は、上記200
〜2000t/mの撚りを施した片撚り捲縮糸を下撚と
して得られたものを2本または3本合わせて上撚りを施
し諸撚りした撚り捲縮縮糸である。2本または3本の諸
撚りとすることにより、しっかりした撚り捲縮糸とな
る。カーペットやモケットのパイルとして用いた際、肌
触り感がよく、柔軟な風合いと耐久性が両立したものと
することができる。撚り数は、特に制限なく甘撚り、中
撚り、強撚りが適用でき、目的に応じて適宜設定すれば
よい。撚り数としては、200〜2000t/m、より
好ましくは300〜1500t/mが採用される。Further, the twisted crimped yarn of the present invention is characterized in that
This is a twisted crimped yarn obtained by twisting single-twisted crimped yarn having a twist of 20002000 t / m as a lower twist and then twisting and twisting the two or three twisted yarns. By using two or three twists, a firm twisted crimped yarn is obtained. When used as a pile for carpets and moquettes, it has a good touch and can achieve both a soft texture and durability. The number of twists is not particularly limited, and sweet twisting, medium twisting, and strong twisting can be applied, and may be appropriately set according to the purpose. As the number of twists, 200 to 2000 t / m, more preferably 300 to 1500 t / m is employed.
【0028】本発明の撚り捲縮糸は、カーペットもしく
はモケットのパイルにしたとき、ループパイルとする必
要がある。一般にカットパイルの場合、カットされた切
断面が肌に接触すると暑苦しく清涼感は感じられにく
い。When the twisted crimped yarn of the present invention is made into a carpet or moquette pile, it must be a loop pile. Generally, in the case of a cut pile, when the cut surface cuts into contact with the skin, it is hot and hard to feel a refreshing feeling.
【0029】本発明において撚りを実施するに際して
は、熱セットなど撚りを固定させるために公知の熱処理
を組合わせることが可能である。これは上述の微細捲縮
を残しつつ捲縮をある程度弱くする熱処理の場合と同様
の効果を引き出すことにもなることから、好ましい手法
であるといえる。When twisting is carried out in the present invention, it is possible to combine a known heat treatment such as heat setting to fix the twist. This can be said to be a preferable method because it can bring out the same effect as in the case of the heat treatment for weakening the crimp to some extent while leaving the fine crimp as described above.
【0030】本発明のカーペット用捲縮糸は、ポリアミ
ドマルチフィラメントからなり、これにより一定の捲縮
を安定に付与でき、かつその耐久性を優れたものとする
ことができる。The crimped yarn for carpet of the present invention is composed of polyamide multifilaments, whereby a certain amount of crimp can be stably imparted and the durability thereof can be improved.
【0031】ポリアミドとしては、具体的にはポリカプ
ラミド(ナイロン6)やポリヘキサメチレンアジパミド
(ナイロン66)などが挙げられる。また、本発明の効
果を損なわない程度に共重合成分を含むポリアミドのコ
ポリマーであってもよい。さらには、製糸性改善や最終
製品の品質改善のために、共重合成分を添加したり、そ
の他顔料などの粒子を添加したポリアミドであっても何
ら差し支えない。具体的な共重合成分としては、ε−カ
プロアミド、テトラメチレンアジパミド、ヘキサメチレ
ンセバカミド、ヘキサメチレンイソフタラミド、テトラ
メチレンテレフタラミド、およびキシリレンフタラミド
などが挙げられる。また、汚染性を改善するために、U
SP5108684号に記載されるようなアルカリ金属
塩を含有するスルホン化した共重合ポリアミドを使用し
てもよい。Specific examples of the polyamide include polycapramide (nylon 6) and polyhexamethylene adipamide (nylon 66). Further, a polyamide copolymer containing a copolymer component to the extent that the effects of the present invention are not impaired may be used. Furthermore, in order to improve the spinning property and the quality of the final product, a polyamide to which a copolymer component is added or other particles such as a pigment are added may be used. Specific copolymerization components include ε-caproamide, tetramethylene adipamide, hexamethylene sebacamide, hexamethylene isophthalamide, tetramethylene terephthalamide, xylylene phthalamide, and the like. In order to improve the pollution,
Sulfonated copolymerized polyamides containing alkali metal salts as described in SP5108864 may be used.
【0032】なお、顔料としては、有機物および無機物
のどらちでも差し支えないが、一般には、カーボンブラ
ックやベンガラ、フタロシアニン系の顔料が好ましく用
いられる。As the pigment, any of an organic substance and an inorganic substance may be used, but generally, carbon black, redwood and phthalocyanine pigments are preferably used.
【0033】原料ポリアミド中には、必要に応じて艶消
し剤、例えば酸化チタン、上記着色用顔料などに加え
て、染料、耐候剤、耐熱剤、および酸化防止剤などの添
加剤を併用添加してもよい。If necessary, additives such as a dye, a weathering agent, a heat-resistant agent, and an antioxidant may be added to the raw material polyamide in addition to a matting agent, for example, titanium oxide, the above-mentioned coloring pigment, and the like. You may.
【0034】本発明における捲縮糸は、撚り捲縮糸を構
成する単糸断面の形状が、変形度が1.5〜5.0のY
型断面もしくは扁平度が1.5〜5.0の扁平断面であ
ることが好ましい。Y型断面は単糸断面に3方向に突起
を有する糸をいう。断面に中空部を1つ以上含んでいて
も差し支えない。Y断面はその3つの突起のため見掛け
の外郭が大きくなり、バルキー性に優れた糸となる。変
形度を1.5〜5.0とすることで該バルキー性と製糸
性がともに優れた捲縮糸とすることができる。In the crimped yarn of the present invention, the shape of the cross section of a single yarn constituting the twisted crimped yarn is Y having a deformation degree of 1.5 to 5.0.
It is preferable that the mold section or the flat section has a flatness of 1.5 to 5.0. The Y-shaped cross section refers to a yarn having protrusions in three directions in a single yarn cross section. The cross section may include one or more hollow portions. In the Y section, the apparent outer shape becomes large due to the three projections, and the yarn becomes excellent in bulkiness. By setting the degree of deformation to 1.5 to 5.0, it is possible to obtain a crimped yarn excellent in both the bulkiness and the yarn forming property.
【0035】また、扁平断面糸とは、特単繊維断面が扁
平形状をした糸をいう。その扁平断面糸としての特性を
損ねない範囲であれば、光沢や製糸性改善のために断面
に突起やくぼみが存在していても何ら差し支えない。扁
平断面糸とすることによって、単繊維の屈曲性が三角断
面、丸断面、および四角断面などに比較して高まり、よ
り柔軟性に優れ、肌触りのよいタッチのカーペットにす
ることができる。特に本発明においては撚り糸とするた
め、扁平の柔軟性を保持しつつへたりや倒れといった扁
平糸や細繊度糸にありがちな欠点は発現しない。断面を
外接する長方形に近似させた場合のタテとヨコの長さの
比で扁平度を算出した場合、1.5〜5.0の範囲が好
ましく、2.5〜4.5の範囲がより好ましい。The flat cross section yarn is a yarn having a cross section of a special single fiber having a flat shape. As long as the properties of the flat cross-section yarn are not impaired, any protrusions or depressions may be present in the cross section for improving the gloss and the spinnability. By using a flat cross-section yarn, the flexibility of a single fiber is increased as compared with a triangular cross section, a round cross section, a square cross section, and the like, so that a carpet having more flexibility and a soft touch can be obtained. In particular, in the present invention, since the yarn is a twisted yarn, defects that are common to flat yarns and fine yarns, such as sagging and falling while maintaining flat flexibility, do not appear. When the flatness is calculated by the ratio of the length of the length and the width when the cross section is approximated to a circumscribed rectangle, the range of 1.5 to 5.0 is preferable, and the range of 2.5 to 4.5 is more preferable. preferable.
【0036】本発明において、撚糸された捲縮糸は撚り
を固定する目的で、撚糸後に熱セットを施すことは何ら
差し支えない。セット温度は、用いる捲縮糸の融点や糸
物性に応じて設定すれば良く、ポリカプラミドの場合、
170℃〜230℃、ポリヘキサメチレンアジパミドの
場合、210℃〜270℃が好ましく用いられる。In the present invention, the twisted crimped yarn may be subjected to heat setting after twisting for the purpose of fixing the twist. The setting temperature may be set according to the melting point and yarn physical properties of the crimped yarn used, and in the case of polycapramide,
170 ° C to 230 ° C, and in the case of polyhexamethylene adipamide, 210 ° C to 270 ° C are preferably used.
【0037】本発明のカーペットは、ループパイルであ
る表糸と、この表糸をタフトした基布と、この基布の裏
に貼りつけたバッキング材とから構成されたカーペット
であって、表糸が、本発明の撚り捲縮糸を含むことを特
徴とするものである。あるいはまた本発明のモケットは
ループパイルである表糸と、この表糸を支持する基材
と、この基材の裏に貼りつけたバッキング材とから構成
されたモケットであって、表糸が本発明の撚り捲縮糸を
含むことを特徴とするものである。The carpet of the present invention is a carpet composed of a surface yarn which is a loop pile, a base fabric obtained by tufting the surface yarn, and a backing material adhered to the back of the base fabric. However, it is characterized by including the twisted crimped yarn of the present invention. Alternatively, the moquette of the present invention is a moquette composed of a surface yarn that is a loop pile, a base material that supports the surface yarn, and a backing material attached to the back of the base material. It is characterized by containing the twisted crimped yarn of the invention.
【0038】そして、本発明のカーペット及びモケット
は、表糸中に上記撚り捲縮糸でかつループパイルである
ポリアミドマルチフィラメント捲縮糸を70%以上、さ
らには85%以上用いるのが好ましい。上記した本発明
の撚り捲縮糸をループパイルとして70%以上使用する
ことで、きわめて柔軟で肌触りが良く、特に家庭用ラグ
カーペット、モケットとして好適なカーペット、モケッ
トを得ることができる。上記した本発明の撚り捲縮糸を
ループパイルとして100%使う場合においても、もち
ろんカーペット及びモケットの風合いは非常に柔らかい
ものとなるが、少なくとも70%使用することで本発明
の効果を得ることが十分に可能である。[0038] In the carpet and moquette of the present invention, it is preferable to use 70% or more, more preferably 85% or more, of the above-described twisted crimped yarn and loop pile polyamide multifilament crimped yarn in the surface yarn. By using the above-described twisted crimped yarn of the present invention as a loop pile in an amount of 70% or more, a carpet or moquette that is extremely flexible and has a good touch and that is particularly suitable as a home rug carpet and moquette can be obtained. When the twisted crimped yarn of the present invention is used 100% as a loop pile, the texture of the carpet and the moquette is of course very soft, but the effect of the present invention can be obtained by using at least 70%. It is possible enough.
【0039】本発明のカーペットのパイル高さは、目的
に応じて適宜設定すればよいが、肌触りが重要であり、
1mmから10mm、好ましくは2mmから5mmの範
囲が通常選択される。また、目付も高すぎると重厚感が
あり、暑苦しい感触となるので、好ましくは300〜8
00g/m2、より好ましくは400〜700g/m2と
するのがよい。The pile height of the carpet of the present invention may be appropriately set according to the purpose, but the touch is important.
A range of 1 mm to 10 mm, preferably 2 mm to 5 mm, is usually selected. Also, if the basis weight is too high, there is a profound feeling and a hot feeling is felt.
It is good to be 00 g / m 2 , more preferably 400 to 700 g / m 2 .
【0040】本発明のカーペット及びモケットにおいて
は、表面の柔らかなタッチを十分引き出し、かつ肌触り
が良好で、清涼感を出すために、上記撚り捲縮糸を含む
パイル糸としての表糸をループパイルとして用いるもの
である。本発明におけるカーペットは、特に家庭用のラ
グ用途に好ましく用いられる。カーペットにタフトする
場合、撚り糸の繊度に応じてタフトの条件を決めればよ
い。In the carpet and moquette of the present invention, the surface yarn as the pile yarn containing the above twisted crimped yarn is formed into a loop pile in order to sufficiently draw out a soft touch on the surface, to give a good touch, and to give a cool feeling. Is used. The carpet in the present invention is particularly preferably used for home rug applications. When tufting a carpet, the tuft conditions may be determined according to the fineness of the twisted yarn.
【0041】本発明において、カーペットの風合いや肌
触りをさらに良好なものにするため、パイルを構成する
撚り捲縮糸の単糸の集束性を少し乱す目的で、パイルの
表層の単糸をランダムに乱す加工を施すことはより好ま
しい手法となる。例えば、公知の起毛処理、高圧の水流
を衝突させるウォータージェットパンチなどが好ましく
採用されうる。このときの起毛条件やウォータージェッ
トパンチの条件は、単糸を切断しないよう撚り捲縮糸の
繊度や撚り数を考慮して決定すればよい。ウォータージ
ェットパンチの具体的な方法は、ノズルよりパイル表面
に水を高圧で噴射させるものである。水圧は、50〜1
30kg/cm2、より好ましくは、70〜110kg
/cm2である。水圧が低いと単糸の乱れが小さく、ま
た130kg・cm2を越える高圧では、カーペットま
たはもむっとの収縮が著しく発生したり、単糸の切断、
毛羽発生の原因になり好ましくない。該ウォータージェ
ットパンチでは、撚糸したパイルを構成する表層の単糸
が多少ランダムになるため、嵩高性も増し、またスパン
糸のような風合いを出すことも可能になる。In the present invention, in order to further improve the feel and feel of the carpet, the single yarn of the surface layer of the pile is randomly dispersed for the purpose of slightly disturbing the convergence of the single yarn of the twisted crimped yarn constituting the pile. Performing disturbing processing is a more preferable method. For example, a known brushing treatment, a water jet punch for colliding a high-pressure water stream, or the like can be preferably employed. The raising conditions and the water jet punch conditions at this time may be determined in consideration of the fineness and the number of twists of the twisted crimped yarn so as not to cut the single yarn. A specific method of the water jet punch is to jet water at high pressure from a nozzle onto the pile surface. Water pressure is 50-1
30 kg / cm 2 , more preferably 70 to 110 kg
/ Cm 2 . When the water pressure is low, the turbulence of the single yarn is small, and at a high pressure exceeding 130 kg · cm 2 , the contraction of the carpet or the mud becomes remarkable, the cutting of the single yarn,
It is not preferable because it causes fluff. In the water jet punch, since the single yarn of the surface layer constituting the twisted pile is somewhat random, the bulkiness is increased, and a texture like a spun yarn can be obtained.
【0042】本発明のカーペットには、静電気抑制のた
めなどの目的で、上記した本発明のカーペット用捲縮糸
以外の他の糸を混繊しても何ら差し支えない。特に好ま
しくは、比抵抗の低い導電性繊維などが混繊され得る。
また、防汚性を高めるために、防汚剤を塗布することも
好ましい。The carpet of the present invention may be mixed with any yarn other than the above-described crimped yarn for carpet of the present invention for the purpose of suppressing static electricity or the like. Particularly preferably, conductive fibers having a low specific resistance can be mixed.
It is also preferable to apply an antifouling agent in order to enhance the antifouling property.
【0043】次に、本発明の柔らかな風合いで清涼感の
ある肌触りであり、かつ耐久性に優れたカーペットまた
はモケットを与え得る捲縮糸、および特に春から秋にか
けての高温多湿の環境化においても好ましく使用可能な
家庭用ラグカーペット、家庭用モケットの代表的な製造
方法について説明する。Next, the crimped yarn of the present invention which can provide a carpet or moquette which has a soft texture and a refreshing feel and which is excellent in durability, and especially in an environment of high temperature and high humidity from spring to autumn A typical method for producing a home rug carpet and a home moquette that can also be preferably used will be described.
【0044】まず、捲縮糸は、基本的に公知の溶融紡
糸、冷却、給油、延伸、捲縮付与の各工程からなる通常
の方法によって製造される。本発明で用いる溶融紡糸装
置は、エクストルーダー型紡糸機およびプレッシャー型
紡糸機のどちらも使用可能であるが、製品の均一性およ
び製糸工程における収率の点から前者が好ましい。特に
原着ポリマーを用いる場合はエクストルーダー型紡糸機
が有利である。First, the crimped yarn is produced by a conventional method basically comprising the steps of melt spinning, cooling, oil supply, drawing and crimping. As the melt spinning device used in the present invention, both an extruder type spinning machine and a pressure type spinning machine can be used, but the former is preferable in terms of product uniformity and yield in the spinning process. In particular, an extruder-type spinning machine is advantageous when a soaked polymer is used.
【0045】そして、撚り捲縮糸の糸断面を本発明の変
形度とあるいは扁平度の範囲内とし、総繊度・単繊維繊
度を目的の繊度にするためには、溶融吐出する際の口金
の吐出孔形状と吐出量、引取り速度などの紡糸条件を目
的に合わせて調節すればよい。Y型の単糸断面を作製す
るための代表的な吐出孔形状、扁平断面にするための代
表的な吐出孔形状を図1、図2、図3に示す。In order to make the yarn cross section of the twisted crimped yarn within the range of the degree of deformation and / or the degree of flatness of the present invention, and to obtain the desired fineness of the total fineness / single fiber fineness, it is necessary to use a die for melting and discharging. The spinning conditions such as the shape of the discharge hole, the discharge amount, and the take-up speed may be adjusted according to the purpose. Typical discharge hole shapes for producing a Y-shaped single yarn cross section and typical discharge hole shapes for forming a flat cross section are shown in FIGS.
【0046】溶融紡糸された糸条は、冷却、給油の後、
必要に応じて延伸、熱固定が施される。延伸に際して
は、補助的に延伸点を固定するなどの目的でスチーム処
理装置などを併用してもよい。ポリアミドの場合、後の
工程で高い捲縮を付与するためには、ある程度の配向と
結晶化が必要であるので、通常2倍から4倍の延伸を行
うことが好ましい。After the melt-spun yarn is cooled and refueled,
Stretching and heat setting are performed as necessary. At the time of stretching, a steam processing device or the like may be used in combination for the purpose of fixing the stretching point. In the case of polyamide, a certain degree of orientation and crystallization is required in order to impart a high crimp in a later step, and therefore it is usually preferable to perform stretching by 2 to 4 times.
【0047】次いで、延伸されたポリアミド糸に、捲縮
付与装置によって捲縮を付与する。捲縮は通常の加熱流
体加工処理により付与すればよく、例えば、ジェットノ
ズルタイプ、ジェットスタッファタイプ、さらにはギヤ
方式など各種の捲縮付与方法が採用されうるが、高い捲
縮付与とその顕在化を達成するためにはジェットノズル
方式が好ましい。なかでも米国特許第3,781,94
9号明細書に記載のように、ニードル内を通過する糸条
に周囲から加熱蒸気などの高圧の高温流体を接触させ、
大気中に放出し冷却することで捲縮を付与するタスラン
型捲縮ノズルなどが好ましく使用される。さらには、捲
縮を固定する目的から、捲縮ノズルを通過した糸条に冷
水を付与したり、さらには吸引するロータリーフィルタ
表面に糸条を堆積させて冷却するような方式を採用して
もよい。Next, the drawn polyamide yarn is crimped by a crimping device. The crimp may be applied by ordinary heating fluid processing, and for example, various crimping methods such as a jet nozzle type, a jet stuffer type, and a gear system may be adopted. The jet nozzle method is preferable in order to achieve the conversion. U.S. Pat. No. 3,781,94
As described in the specification of No. 9, a high-pressure high-temperature fluid such as heated steam is brought into contact with the yarn passing through the needle from the surroundings,
A Taslan-type crimping nozzle that gives a crimp by releasing it into the air and cooling it is preferably used. Furthermore, for the purpose of fixing the crimp, it is also possible to apply cold water to the yarn that has passed through the crimp nozzle, or to adopt a method in which the yarn is deposited on the surface of the rotary filter to be sucked and cooled. Good.
【0048】上記の溶融紡糸、延伸および捲縮付与は、
糸条を途中で巻取らずに連続して行ってもよいし、未延
伸糸段階あるいは延伸糸段階で一旦巻取ってもよい。The melt spinning, stretching and crimping are performed as described above.
The yarn may be continuously wound without being wound in the middle, or may be wound once in an undrawn yarn stage or a drawn yarn stage.
【0049】また、捲縮糸を製造する際、その工程通過
性や捲縮特性をコントロールする目的のために、捲縮ノ
ズルに導入する糸条に予め原糸交絡を付与しても差し支
えない。In producing a crimped yarn, the yarn introduced into the crimping nozzle may be preliminarily entangled with the yarn for the purpose of controlling the processability and the crimping characteristics.
【0050】得られた特定の総繊度と単繊維繊度を有す
るポリアミドマルチフィラメント捲縮糸は、撚糸され
る。撚糸は片撚りもしくは、片撚りしたものを2本もし
くは3本撚り合わせた諸撚りとすることができる。撚糸
は公知の方法を採りうる。使用する捲縮糸の総繊度とプ
ライ数に応じて、片撚り数は本発明の範囲内において適
宜決定することができる。また上撚り数は、繊度や下撚
り数に応じて決定すればよい。The obtained polyamide multifilament crimped yarn having the specific total fineness and single fiber fineness is twisted. The twisted yarn may be a single twist or a single twist of two or three twists. For the twisting yarn, a known method can be employed. The number of single twists can be appropriately determined within the scope of the present invention according to the total fineness and the number of plies of the crimped yarn used. The number of twists may be determined according to the fineness and the number of twists.
【0051】次いで必要に応じ、撚り構造を固定する目
的で、熱セットを施す。通常、熱セット時の雰囲気温度
は用いる捲縮糸のポリマに応じて決定され、前述のよう
にポリカプラミドの場合、170℃〜230℃、ポリヘ
キサメチレンアジパミドの場合、210℃〜270℃の
範囲が通常用いられる。低温ではセット性が劣り、高温
すぎると糸自体が融着したり劣化するので好ましくな
い。Then, if necessary, heat setting is performed for the purpose of fixing the twisted structure. Usually, the ambient temperature at the time of heat setting is determined according to the polymer of the crimped yarn to be used, and as described above, 170 ° C. to 230 ° C. for polycapramide and 210 ° C. to 270 ° C. for polyhexamethylene adipamide. Ranges are commonly used. If the temperature is low, the setting property is inferior. If the temperature is too high, the yarn itself is undesirably fused or deteriorated.
【0052】得られた撚り捲縮糸は、次いでカーペット
用にタフトもしくはモケット用に製織される。タフティ
ングは公知の方法で行うことが可能である。目的の目付
に応じて、撚り捲縮糸の繊度を考慮して、ステッチ、ゲ
ージ、パイル高さを決定する。本発明のカーペット用捲
縮糸はループパイルとしてタフトされた時に効果を発現
するためループパイルとする。少なくとも表糸を形成す
るパイルの70%以上は本発明の撚り捲縮糸を用いたル
ープパイルであることが必要である。The obtained twisted crimped yarn is then woven for tuft or moquette for carpet. Tufting can be performed by a known method. Stitches, gauges, and pile heights are determined according to the desired basis weight in consideration of the fineness of the twisted crimped yarn. The crimped yarn for carpet of the present invention is a loop pile in order to exhibit an effect when tufted as a loop pile. At least 70% or more of the pile forming the surface yarn must be a loop pile using the twisted crimped yarn of the present invention.
【0053】またモケットの場合においても公知の製織
機による製造することが可能である。In the case of a moquette, it can be manufactured by a known weaving machine.
【0054】続いて、公知の方法により、染色・バッキ
ングが施される。染色方法は、連続染色、ウィンス染
色、さらにはロープ染色などが、特に制限なく使用可能
である。もちろん、原着糸を使用している場合や、タフ
ト前にチーズ染色を施している場合などには、タフト後
の染色は省略することができ、直接バッキングが実施さ
れる。Subsequently, dyeing and backing are performed by a known method. As the dyeing method, continuous dyeing, Winth dyeing, and rope dyeing can be used without any particular limitation. Of course, when the original yarn is used or the cheese is dyed before the tuft, the dyeing after the tuft can be omitted, and the backing is directly performed.
【0055】次いで、必要に応じて、単糸の集束性を少
し乱す目的で、起毛処理またはウォータージェットパン
チ処理を施す。該処理は、バッキング工程に連続して実
施しても、一旦巻き取って別工程で実施してもよい。タ
フト反または製織反を一定速度で移動させながら、針ま
たは高圧水流を機械的にパイル面に衝突させ、撚り捲縮
糸の表層の単糸を乱す。処理の条件は、撚り捲縮糸の繊
度や撚り数に因るが、ウォータージェットパンチの場
合、通常水圧は、50〜130kg/cm2が採用され
る。Then, if necessary, a brushing treatment or a water jet punch treatment is performed for the purpose of slightly disturbing the convergence of the single yarn. The treatment may be carried out continuously with the backing step, or may be carried out once and carried out in another step. While moving the tufting or weaving cloth at a constant speed, a needle or a high-pressure water stream is made to impinge on the pile surface mechanically to disturb the surface yarn of the twisted crimped yarn. The processing conditions depend on the fineness and the number of twists of the twisted crimped yarn, but in the case of a water jet punch, a water pressure of usually 50 to 130 kg / cm 2 is employed.
【0056】[0056]
【実施例】以下、本発明を実施例によりさらに詳細に説
明する。上述の説明中、および以下に述べる実施例にお
ける各物性値は、具体的には下記の方法で測定した値で
ある。 [硫酸相対粘度]ポリマ試料を98%硫酸に1重量%の
濃度で溶解し、オストワルド粘度計を用いて25℃で測
定した。The present invention will be described in more detail with reference to the following examples. Each physical property value in the above description and in the following examples is specifically a value measured by the following method. [Sulfuric acid relative viscosity] A polymer sample was dissolved in 98% sulfuric acid at a concentration of 1% by weight, and measured at 25 ° C using an Ostwald viscometer.
【0057】[総繊度]JIS L 1090により測
定した。[Total fineness] Measured according to JIS L 1090.
【0058】[単繊維繊度]JIS L 1090によ
り測定した総繊度を、単繊維数で除して求めた。[Single fiber fineness] The total fineness measured according to JIS L 1090 was divided by the number of single fibers.
【0059】[沸騰水処理後の捲縮伸長率]温度20
℃、相対湿度65%の雰囲気中に20時間以上放置され
ていたパッケージから解舒した捲縮扁平糸を、無荷重状
態で30分間沸騰水で浸漬処理した後、平衡水分率まで
乾燥し、これを沸騰水処理後捲縮糸の試料とする。この
試料糸に2mg/dの初荷重をかけ30秒経過した後
に、試料長50cm(L1)にマーキングをする。次い
で、同試料に100mg/dの定荷重をかけて30秒経
過後に、伸びた試料長(L2)を測定する。次いで、下
記式により、捲縮伸長率(%)を求める。 捲縮伸長率(%)=[(L2−L1)/L1]×100 なお、沸騰水処理前に糸条を放置する際の雰囲気条件
は、実際のカーペット製造工程において使用される時の
捲縮糸状態、つまり吸湿により捲縮特性が平衡状態に達
した状態とするためのものであり、平衡状態に達するの
に時間がかかり過ぎず、かつ結露を生じないという点か
ら選定したものである。[Crimp elongation after boiling water treatment] Temperature 20
A crimped flat yarn unwound from a package that has been left in an atmosphere at a temperature of 65 ° C. and a relative humidity of 65% for 20 hours or more is immersed in boiling water for 30 minutes under no load, and then dried to an equilibrium moisture content. Is a sample of the crimped yarn after the boiling water treatment. After an initial load of 2 mg / d is applied to this sample yarn and 30 seconds have elapsed, marking is performed on a sample length of 50 cm (L 1 ). Next, a constant load of 100 mg / d is applied to the sample, and after elapse of 30 seconds, the elongated sample length (L 2 ) is measured. Next, the crimp elongation rate (%) is determined by the following equation. The crimp elongation rate (%) = [(L 2 −L 1 ) / L 1 ] × 100 The atmosphere conditions when leaving the yarn before the boiling water treatment are the same as those used in the actual carpet manufacturing process. Crimped yarn state, that is, a state in which the crimping property reaches an equilibrium state due to moisture absorption, selected from the point that it does not take too much time to reach the equilibrium state and does not cause condensation. It is.
【0060】[扁平断面糸の変形度]単繊維断面を長方
形に近似させ、そのタテとヨコの比から扁平度を算出し
た。単繊維5本の測定の平均値とする。[Degree of Deformation of Flat Cross Section Yarn] The cross section of a single fiber was approximated to a rectangle, and the flatness was calculated from the ratio of the warp to the weft. The average value of five single fibers is measured.
【0061】[Y型断面糸の変形度]単糸断面を切断
後、光学顕微鏡を用いて単繊維凸部を外接円の直径
(A)と単繊維凹部の内接円の直径(B)を測定し、A
/Bにより算出した。単繊維5本の測定の平均値とす
る。[Degree of Deformation of Y-Shaped Yarn] After cutting the cross section of the single yarn, the diameter of the circumscribed circle (A) and the diameter of the inscribed circle (B) of the single fiber concave portion are determined using an optical microscope. Measure and A
/ B. The average value of five single fibers is measured.
【0062】[カーペットの腰・バルキー性]カーペッ
トを静置し、素手による触感によった官能評価で、その
弾力性、反発性を家庭用ラグという用途を意識して、相
対的に下記のように評価した。 ◎…弾力性、反発性が高く、腰がきわめて強い ○…弾力性、反発性が優れ、腰が強い △…弾力性、反発性がやや低く、腰が弱い ×…弾力性、反発性が低く、腰がきわめて弱い。[Carpet waist / bulky property] The carpet is left standing, and the elasticity and resilience of the carpet are evaluated by sensory evaluation using bare hands, and the elasticity and resilience of the carpet are relatively conscious as shown below. Was evaluated. ◎: High elasticity and resilience, extremely strong waist ○: Excellent elasticity, resilience, strong waist △: Slightly low elasticity, resilience, weak waist ×: Low elasticity, low resilience The waist is very weak.
【0063】[カーペットの柔軟性]カーペットを静置
し、素手による触感によった官能評価で、その柔らか
さ、肌触りなどを家庭用ラグという用途を意識して、相
対的に下記のように評価した。 ◎…きわめて柔らかく、肌触りがきわめてよい ○…柔らかく、肌触りがきわめてよい △…やや柔らかさに劣り、肌触りは普通 ×…柔らかさに劣り、肌触りが悪い。[Carpet Flexibility] The carpet was allowed to stand still, and its softness, touch, etc. were evaluated relatively as follows, taking into account the use of household rugs, by sensory evaluation based on the tactile sensation with bare hands. did. ◎: Extremely soft and extremely soft to the touch…: Soft and extremely soft to the touch や: Inferior to softness and normal to the touch ×: Poor to soft and poor to the touch.
【0064】[カーペットの清涼感]カーペットを25
℃の雰囲気中に静置し、素手による触感によった官能評
価で、その清涼感を相対的に下記のように評価した。 ◎…パイルの触感が冷たく感じられ、清涼感大。 ○…パイルの触感がやや冷たく感じられ、清涼感あり。 △…ややまとわりつく感触となり、清涼感少。 ×…暑苦しく清涼感に乏しい。[Refreshing feeling of carpet]
The sample was allowed to stand still in an atmosphere of ° C., and the refreshing feeling was relatively evaluated as follows by a sensory evaluation based on a tactile sensation with bare hands. ◎: The feel of the pile is cold, and the refreshing feeling is large. ○: The feel of the pile is somewhat cold, and there is a refreshing feeling. △: The feel is slightly sticky, and the refreshing feeling is small. ×: It is hot and lacks a refreshing feeling.
【0065】[製糸性]糸切れの回数から相対的に下記
のように評価した。 ◎…糸切れが発生しない ○…糸切れがほとんど発生しない △…糸切れがやや発生する ×…糸切れが頻発する。[Yarn-producing property] The following evaluation was made relatively based on the number of times of yarn breakage. ◎: Thread break does not occur.…: Thread break hardly occurs.…: Thread break occurs slightly. X: Thread break occurs frequently.
【0066】[カーペットの総合評価]清涼感ある家庭
用ラグカーペットとしての適合性を相対的に下記のよう
に総合評価した。 ◎…適合性きわめて良好 ○…適合性良好 △…適合性やや不良 ×…適合性不良。[Comprehensive Evaluation of Carpet] The suitability as a home rug carpet with a refreshing feeling was relatively comprehensively evaluated as follows. …: Extremely good suitability…: good suitability △: slightly poor suitability ×: poor suitability
【0067】[実施例1]硫酸相対粘度2.8のナイロ
ン6のチップを、エクストルーダータイプの紡糸機によ
り溶融紡糸し、扁平度4.0の断面が楕円扁平の扁平断
面糸を溶融紡糸した。紡糸に連続して冷却し、給油し、
延伸し、引き続き巻き取ることなくジェットノズル(J
N)を用いて捲縮を付与してから巻取り、総繊度650
デシテックス、120フィラメントのポリアミドマルチ
フィラメント捲縮糸を得た。このとき製糸性は特に問題
なく、得られた捲縮糸の単繊維繊度は5.4デシテック
スと計算された。この捲縮糸の沸騰水処理後の捲縮伸長
率は10.5%であった。Example 1 A nylon 6 chip having a sulfuric acid relative viscosity of 2.8 was melt-spun by an extruder type spinning machine, and a flat cross-section yarn having a flatness of 4.0 and an elliptical flat cross-section was melt-spun. . Cooling and refueling continuously after spinning,
Stretch and continue to take up the jet nozzle (J
N) to give a crimp and then wind it up to give a total fineness of 650
A decitex, polyamide multifilament crimped yarn of 120 filaments was obtained. At this time, the spinnability was not particularly problematic, and the single fiber fineness of the obtained crimped yarn was calculated to be 5.4 dtex. The crimp elongation of the crimped yarn after the boiling water treatment was 10.5%.
【0068】上記の捲縮糸に、公知のリング撚糸機を用
い、撚り数300t/mで片撚りを施し、次いで125
℃で熱セットを行った。該撚り捲縮糸を用い、通常のレ
ベルループタフト機にて、5/64ゲージ、目付が45
0g/m2、パイル高さが2.5mmになるようにステ
ッチを調節してタフトを実施した。その後、常法に従い
染色、バッキングを実施した。このようにして得られた
カーペットの「腰・バルキー性」、「柔軟性」、「清涼
感」「製糸性」について評価した結果を表1に示す。The above-mentioned crimped yarn is subjected to single twisting at a twist number of 300 t / m using a known ring twisting machine, and then 125 twisted.
Heat setting was performed at 0 ° C. Using the twisted crimped yarn, with a normal level loop tufting machine, 5/64 gauge, basis weight 45
Tufting was performed by adjusting the stitches so that the pile height became 0 g / m 2 and the pile height became 2.5 mm. Thereafter, staining and backing were performed according to a conventional method. Table 1 shows the results of evaluating the carpet obtained in this manner for “lumbar / bulky properties”, “flexibility”, “coolness”, and “filtration properties”.
【0069】[実施例2]実施例1で得られた片撚り糸
を2本引きそろえて、320t/mの上撚りを施し、次
いで、熱セットを施し2プライの諸撚り捲縮糸とした。
実施例1と同様にして、該撚り捲縮糸を用い、通常のレ
ベルループタフト機にて、1/10ゲージ、目付が50
0g/m2、パイル高さが2.5mmになるようにステ
ッチを調節してタフトを実施した。その後、常法に従い
染色、バッキングを実施した。このとき上撚りは320
t/mで行い、次いで128℃で熱セットした。Example 2 Two single-twisted yarns obtained in Example 1 were aligned and subjected to an upper twist of 320 t / m, and then heat set to obtain a two-ply twisted crimped yarn.
In the same manner as in Example 1, using the twisted crimped yarn, with a normal level loop tufting machine, 1/10 gauge and basis weight of 50 were used.
Tufting was performed by adjusting the stitches so that the pile height became 0 g / m 2 and the pile height became 2.5 mm. Thereafter, staining and backing were performed according to a conventional method. At this time, the twist is 320
t / m and then heat set at 128 ° C.
【0070】次いで、得られた撚り捲縮糸を通常のレベ
ルループにて、1/10ゲージ、目付が500g/
m2、パイル高さが2.5mmになるようにステッチを
調節してタフトした。その後、常法に従い染色、バッキ
ングを実施した。このようにして得られたカーペットの
「腰」、「柔軟性」、「清涼感」「製糸性」について評
価した結果を表1に示す。Next, the obtained twisted crimped yarn was subjected to a 1/10 gauge and a basis weight of 500 g /
The tuft was adjusted by adjusting the stitch so that the m 2 and the pile height became 2.5 mm. Thereafter, staining and backing were performed according to a conventional method. Table 1 shows the results of evaluating the carpet thus obtained for “hip”, “flexibility”, “coolness”, and “filtration”.
【0071】[実施例3]長方形型の吐出スリットを用
い対外は実施例1と同様にして、単糸の断面形状が扁平
率4.5の扁平糸である500デシテックス、96フィ
ラメントの捲縮糸を得た。この扁平捲縮糸の沸騰水処理
後の捲縮発現率は、10.2%であった。上記の捲縮糸
を2本用い、下撚り数、上撚り数とも350t/mで2
プライの撚糸を行い、次いで128℃で熱セットを行っ
た。Example 3 Using a rectangular discharge slit, the outside is the same as in Example 1, except that the cross section of the single yarn is a flat yarn having a flatness of 4.5, 500 decitex, and a crimped yarn of 96 filaments. I got The crimp development rate of this flat crimped yarn after the boiling water treatment was 10.2%. Using the two crimped yarns described above, both the number of twists and the number of twists are 350 t / m and 2
The plies were twisted and then heat set at 128 ° C.
【0072】該撚り捲縮糸を用い、通常のレベルループ
タフト機にて、1/10ゲージ、目付が550g/
m2、パイル高さが2.5mmになるようにステッチを
調節してタフトを実施した。その後、常法に従い染色、
バッキングを実施した。その後、水圧80kg/cm2
で、濾過水を使用して、ウォータージェットパンチ加工
を行った。このようにして得られたカーペットの「腰・
バルキー性」、「柔軟性」、「清涼感」「製糸性」につ
いて評価した結果を表1に示す。Using the twisted crimped yarn, with a normal level loop tufting machine, 1/10 gauge and a basis weight of 550 g /
Tufting was performed by adjusting stitches so that m 2 and the pile height became 2.5 mm. Then, dye according to the usual method,
Backing was implemented. Then, water pressure 80kg / cm 2
Then, water jet punching was performed using filtered water. The carpet obtained in this way is
Table 1 shows the results of the evaluation of "bulky properties", "flexibility", "coolness", and "filamentability".
【0073】[比較例1〜3]実施例1と同様にして、
硫酸相対粘度2.8のナイロン6のチップを、エクスト
ルーダータイプの紡糸機により溶融紡糸し、断面がY型
断面糸を溶融紡糸した。紡糸に連続して冷却し、給油
し、延伸し、引き続き巻き取ることなくジェットノズル
(JN)を用いて捲縮を付与してから巻取り、比較例1
〜3の特性をもつポリアミドマルチフィラメント捲縮糸
を得た。比較例4においては捲縮付与における熱処理温
度を低くし、沸騰水処理後の捲縮発現を低くした。ま
た、比較例5では、撚り数を少なくした水準を、比較例
6ではパイルをカットパイルにした水準をテストした。
上記の捲縮糸に表1に示す条件で撚りセットを施した後
カーペットを製作し、「腰・バルキー性」、「柔軟
性」、「清涼感」「製糸性」について評価した結果をあ
わせて表1に示す。[Comparative Examples 1 to 3]
A chip of nylon 6 having a sulfuric acid relative viscosity of 2.8 was melt-spun by an extruder-type spinning machine, and a cross-section Y-shaped cross-section yarn was melt-spun. Cooling was performed continuously after spinning, oil supply was performed, stretching was performed, and a crimp was applied using a jet nozzle (JN) without winding, followed by winding.
Polyamide multifilament crimped yarns having the following properties were obtained. In Comparative Example 4, the heat treatment temperature during crimping was lowered, and the appearance of crimp after boiling water treatment was lowered. Further, in Comparative Example 5, the level at which the number of twists was reduced was tested, and in Comparative Example 6, the level at which the pile was a cut pile was tested.
After applying a twist set to the above-mentioned crimped yarn under the conditions shown in Table 1, a carpet was manufactured, and the results of evaluation of “waist / bulkyness”, “flexibility”, “coolness”, and “yarnability” were added. It is shown in Table 1.
【0074】[0074]
【表1】 表1の結果から明らかなように、本発明の実施例におい
ては、いずれもカーペットの腰、柔軟性、清涼感が共に
家庭用のラグとして満足できるレベルであり、かつ製糸
性も問題のないレベルであった。比較例1においては扁
平断面糸の単糸繊度が太いため、パイルの柔軟性に劣る
カーペットとなった。また、比較例2は、単糸繊度が逆
に細すぎ、糸切れが多発し安定な製糸ができなかった。
比較例3は、扁平断面糸の総繊度が太いため、感触が重
厚で清涼感に乏しいものとなった。また、比較例4にお
いては、沸騰水処理後の捲縮発現率が低く、バルキー性
に劣るカーペットとなった。一方、比較例5は、撚り数
が少ないためパイルに腰がなく、さらに触感においてパ
イルが手にまとわりつく感じが強く清涼感に乏しいもの
であった。さらに比較例6においては、カットパイルと
したため、手触りにザラツキ感があり、やはり清涼感に
乏しいものであった。[Table 1] As is evident from the results in Table 1, in the examples of the present invention, the waist, flexibility, and refreshing feeling of the carpet are all at a level that can be satisfied as a household rug, and the yarn-making properties do not cause any problem. Met. In Comparative Example 1, the carpet was inferior in pile flexibility because the single-fiber fineness of the flat cross-section yarn was large. On the other hand, in Comparative Example 2, the single-fiber fineness was too small, and thread breakage occurred frequently, so that stable yarn could not be produced.
In Comparative Example 3, since the total fineness of the flat cross-section yarn was large, the touch was heavy and the refreshing feeling was poor. In Comparative Example 4, the rate of crimping after the boiling water treatment was low, and the carpet was inferior in bulkiness. On the other hand, in Comparative Example 5, since the number of twists was small, the pile had no firmness, and furthermore, the pile had a strong feeling of clinging to the hand and a poor cooling feeling. Further, in Comparative Example 6, since the cut pile was used, the texture was rough and the refreshing feeling was also poor.
【0075】[0075]
【発明の効果】本発明の捲縮糸は、柔らかな風合いで清
涼感のある肌触りであり、かつ耐久性に優れたカーペッ
トやモケットを与えることができる。また、本発明のカ
ーペットまたはモケットは、素肌に接触して使用する家
庭用ラグカーペットとして好適であり、特に春から秋に
かけての高温多湿の環境化においても好ましく使用可能
な家庭用ラグカーペット、家庭用モケットを提供する。Industrial Applicability The crimped yarn of the present invention can give a carpet or moquette which has a soft texture and a refreshing touch and is excellent in durability. Further, the carpet or moquette of the present invention is suitable as a home rug carpet to be used in contact with bare skin, particularly a home rug carpet that can be preferably used in a high-temperature and high-humidity environment from spring to autumn. Provide moquette.
【図1】代表的なY型断面糸用の吐出孔形状を示す概略
図。FIG. 1 is a schematic view showing the shape of a discharge hole for a typical Y-shaped section yarn.
【図2】代表的な扁平断面糸用の吐出孔形状(突起有
り)を示す概略図。FIG. 2 is a schematic diagram showing a typical ejection hole shape (with projections) for a flat cross-section yarn.
【図3】代表的な扁平断面糸用の吐出孔形状(突起無
し)を示す概略図。FIG. 3 is a schematic view showing a typical flat-section yarn discharge hole shape (without protrusions).
───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 3B120 AA15 AA35 BA02 BA15 BA24 BA29 CA12 CA13 EB14 4L036 MA06 MA20 PA21 RA04 UA01 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 3B120 AA15 AA35 BA02 BA15 BA24 BA29 CA12 CA13 EB14 4L036 MA06 MA20 PA21 RA04 UA01
Claims (7)
総繊度が200〜700デシテックス、沸騰水処理後の
捲縮伸長率が5〜20%のポリアミドマルチフィラメン
ト捲縮糸から構成され、撚数が200〜2000t/m
の片撚り、または撚数が200〜2000t/mの下撚
りと上撚りが施された諸撚りを有することを特徴とする
撚り捲縮糸。(1) a single yarn fineness of 3.0 to 7.0 decitex;
It is composed of a polyamide multifilament crimped yarn having a total fineness of 200 to 700 decitex and a crimp elongation of 5 to 20% after boiling water treatment, and a twist number of 200 to 2000 t / m.
A twisted crimped yarn characterized in that the twisted crimped yarn has a single twist or a twist of 200 to 2000 t / m in which the lower twist and the upper twist are applied.
本から構成されていることを特徴とする請求項1記載の
撚り捲縮糸。2. Twisted or crimped yarn having two or more twists
The twisted crimped yarn according to claim 1, wherein the twisted crimped yarn is constituted by a book.
面が、変形度が1.5〜5.0のY型断面もしくは扁平
度が1.5〜5.0の扁平断面であることを特徴とする
請求項1または2に記載の撚り捲縮糸。3. The monofilament section of the polyamide multifilament is a Y-shaped section having a deformation degree of 1.5 to 5.0 or a flat section having a flatness of 1.5 to 5.0. Item 3. The twisted crimped yarn according to item 1 or 2.
フトした基布と、この基布の裏に貼りつけたバッキング
材とから構成されたカーペットであって、表糸が、請求
項1〜3のいずれかに記載の撚り捲縮糸を含むことを特
徴とするカーペット4. A carpet comprising a face yarn that is a loop pile, a base fabric obtained by tufting the surface yarn, and a backing material adhered to the back of the base fabric, wherein the face yarn is formed by a carpet. A carpet comprising the twisted crimped yarn according to any one of claims 1 to 3.
持する基材と、この基材の裏に貼りつけたバッキング材
とから構成されたモケットであって、表糸が請求項1〜
3のいずれかに記載の撚り捲縮糸を含むことを特徴とす
るモケット。5. A moquette comprising a face yarn that is a loop pile, a base material for supporting the surface yarn, and a backing material attached to the back of the base material, wherein the face yarn is formed. ~
A moquette comprising the twisted crimped yarn according to any one of the above items 3.
処理を施した請求項4に記載のカーペット。6. The carpet according to claim 4, which has been subjected to a raising treatment or a water jet punching treatment.
処理を施した請求項5に記載のモケット。7. The moquette according to claim 5, wherein a brushing treatment or a water jet punching treatment is performed.