JP2002244347A - Method of manufacturing kneaded matter for manufacturing toner - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a method of manufacturing kneaded matter for manufacturing toners which permits setting of the feeding width of raw materials despondently upon supply conditions of the raw materials, is capable of stably kneading the raw materials under suppression of the generation of lumps, is capable of manufacturing the kneaded matter uniformly dispersed with the raw materials and is capable of preventing the degradation in the performance of the toners using the kneaded matter. SOLUTION: The manufacturing apparatus 10 has an open roll kneading machine 11 and a screw feeder 12. When the supply rate of the raw materials is defined as M (kg/h), the average temperature of the kneaded matter as T( deg.C), the glass transition temperature of a binder resin as Tg( deg.C) and a constant as k (500) in melting and kneading the raw materials by the open roll kneading machine 11, the feeding width Lf (mm) of the raw materials supplied from the screw feeder 12 is set according to the equation shown by Lf>=k.M/(T-Tg)...(1).

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】この発明は、例えば電子写真
法、静電印刷法等に用いられるトナー製造のための混練
物の製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a kneaded product for producing a toner used in, for example, an electrophotographic method, an electrostatic printing method and the like.

【０００２】[0002]

【従来の技術】一般に、電子写真法においては、光導電
性物質を利用し、種々の方法により感光体上に電気的潜
像を形成し、次いで、前記潜像をトナーを用いて現像す
る。さらに、紙等の被転写材にトナー画像を転写した
後、種々の方法でトナー画像を定着させて被写物を得る
方法が採用されている。2. Description of the Related Art Generally, in electrophotography, a photoconductive substance is used to form an electric latent image on a photoreceptor by various methods, and then the latent image is developed using toner. Further, a method of transferring a toner image to a transfer material such as paper and then fixing the toner image by various methods to obtain an object is adopted.

【０００３】前記トナー（乾式トナー）は、結着樹脂及
び顔料を主原料とし、その他の原料としての荷電制御
剤、ワックス等の添加剤が添加されて調製されている。
このトナーの原料はオープンロール混練機により混練さ
れる。そして、トナーを製造するには、スクリューフィ
ーダーにより原料をオープンロール間に供給する。する
と、原料が両オープンロールの一端供給側の間に滞留し
てバンクが形成されるとともに、そのバンクにおいてオ
ープンロールの回転によりバンク内に原料が飲み込まれ
て対流が形成される。[0003] The toner (dry toner) is prepared by using a binder resin and a pigment as main raw materials and adding additives such as a charge control agent and wax as other raw materials.
The toner raw material is kneaded by an open roll kneader. Then, in order to manufacture the toner, a raw material is supplied between open rolls by a screw feeder. Then, the raw material stays between the one supply sides of the two open rolls to form a bank, and at the bank, the raw material is swallowed into the bank by the rotation of the open roll, and convection is formed.

【０００４】また、バンクにおいて、対流に飲み込まれ
た原料がオープンロールの加熱により溶融し、結着樹脂
は粘性を有する流体となる。そして、溶融した結着樹脂
は高温側のオープンロール表面に巻き着き、その結着樹
脂に顔料、添加剤が付着し、さらに、オープンロールの
回転により他端側へ移送されるうちに結着樹脂内に練り
込まれて混練物が調製される。In the bank, the raw material swallowed by convection is melted by the heating of the open roll, and the binder resin becomes a viscous fluid. Then, the molten binder resin is wound around the surface of the open roll on the high temperature side, pigments and additives are attached to the binder resin, and the binder resin is transported to the other end by the rotation of the open roll. The kneaded material is prepared by kneading the mixture.

【０００５】このとき、オープンロール混練機において
原料の溶融混練が低温で行われるため、結着樹脂の溶融
が進まず、高粘性流体の結着樹脂が練り込まれて大きな
圧縮力、せん断力が発生する。その圧縮力、せん断力に
より顔料、添加剤が微細化されるとともに、結着樹脂中
に均一に分散される。そして、原料が溶融混練されて調
製された混練物はオープンロールの他端排出側から排出
され、その混練物は冷却、固化された後、混練物の粉砕
工程、分級工程、外添工程等が行われてトナーが製造さ
れる。At this time, the melting and kneading of the raw materials are performed at a low temperature in the open roll kneading machine, so that the melting of the binder resin does not proceed, and the binder resin of the high-viscosity fluid is kneaded so that a large compressive force and shear force are generated. appear. The pigment and the additive are miniaturized by the compressive force and the shear force, and are uniformly dispersed in the binder resin. The kneaded material prepared by melting and kneading the raw materials is discharged from the other end discharge side of the open roll, and after the kneaded material is cooled and solidified, a pulverizing step, a classifying step, an external adding step, etc. of the kneaded substance are performed. To produce a toner.

【０００６】[0006]

【発明が解決しようとする課題】ところが、上記混練物
の製造工程において、原料は一定量ずつまとまった状態
でオープンロール混練機に供給され、その原料は外気と
の接触により冷却される。そのため、原料はオープンロ
ールの加熱のみでは溶融されにくく、さらに、原料が溶
融しきっていない状態で供給され続けると固形状の原料
がバンク上に滞留してしまう。However, in the above-mentioned kneaded material production process, the raw materials are supplied to the open roll kneader in a fixed amount, and the raw materials are cooled by contact with the outside air. Therefore, the raw material is hardly melted only by heating the open roll, and if the raw material is continuously supplied in a state where the raw material is not completely melted, the solid raw material stays on the bank.

【０００７】さらに、固形状の原料はバンクからの伝熱
により若干溶融し原料同士で固着してバンク上で固まり
となる。そして、この固まりがバンクの幅よりも大きく
なるとギャップ間に巻き込まれにくくなり、溶融混練さ
れにくくなる。加えて、固まりが発生した状態で原料が
供給され続けるため、原料は固まり上に落下し、原料が
バンクからオープンロール間に均一かつ定量的に巻き込
まれなくなる。その結果、得られる混練物における結着
樹脂中への顔料、添加剤の分散性が悪化し、その混練物
を使用したトナーの性能が低下してしまうという問題が
あった。Further, the solid raw material is slightly melted by the heat transfer from the bank, and is fixed together by the raw materials to be solidified on the bank. If the mass is larger than the width of the bank, it is difficult to be caught in the gap, and it is difficult to melt and knead. In addition, since the raw material is continuously supplied in a state in which the mass is generated, the raw material falls on the mass, and the raw material is not uniformly and quantitatively caught between the bank and the open roll. As a result, there is a problem that the dispersibility of the pigment and the additive in the binder resin in the obtained kneaded material is deteriorated, and the performance of the toner using the kneaded material is reduced.

【０００８】この発明は、このような従来技術に存在す
る問題点に着目してなされたものである。その目的とす
るところは、原料の供給条件に依存して原料の投入幅を
設定することが可能となり、固まりの発生を抑制して安
定した混練ができ、原料が均一に分散された混練物を製
造することができるとともに、その混練物を使用したト
ナーの性能の低下を防止することができるトナー製造の
ための混練物の製造方法を提供することにある。[0008] The present invention has been made by focusing on the problems existing in such prior art. The purpose is to be able to set the feed width of the raw material depending on the raw material supply conditions, to suppress the occurrence of agglomeration, to perform stable kneading, and to obtain a kneaded material in which the raw material is uniformly dispersed. It is an object of the present invention to provide a method for producing a kneaded material for producing a toner, which can be produced and can prevent a decrease in the performance of a toner using the kneaded material.

【０００９】[0009]

【課題を解決するための手段】上記の目的を達成するた
めに、請求項１に記載の発明のトナー製造のための混練
物の製造方法は、少なくとも結着樹脂及び顔料よりなる
原料を搬送し、搬送された原料を次工程に供給する原料
搬送供給装置と、原料搬送供給装置から供給された原料
を複数のオープンロールの間に供給して当該オープンロ
ールからの加熱及び回転により原料を溶融混練して混練
物を製造するように構成した溶融混練装置とよりなる製
造装置を使用してトナー製造のための混練物を製造する
方法であって、前記原料搬送供給装置からの原料のオー
プンロールへの供給の際の同オープンロールの軸線方向
に沿った原料の投入幅をＬｆ（ｍｍ）、原料の供給量を
Ｍ（ｋｇ／ｈ）、オープンロール間で溶融混練される混
練物の平均温度をＴ（℃）、前記結着樹脂のガラス転移
温度をＴｇ（℃）、定数をｋとするとき、Ｌｆ≧ｋ・Ｍ
／（Ｔ−Ｔｇ）に示される関係となるように投入幅を設
定したことを特徴とするものである。In order to achieve the above object, a method for producing a kneaded product for producing a toner according to the present invention according to the first aspect of the present invention comprises conveying a raw material comprising at least a binder resin and a pigment. And a raw material transport / supply device for supplying the transported raw material to the next process, and a raw material supplied from the raw material transport / feed device is supplied between a plurality of open rolls, and the raw materials are melted and kneaded by heating and rotation from the open rolls. A method for producing a kneaded material for toner production using a production device consisting of a melt kneading device configured to produce a kneaded material, and wherein the raw material from the raw material transport and supply device is rolled to an open roll. The supply width of the raw material along the axial direction of the open roll at the time of supply of L is Lf (mm), the supply amount of the raw material is M (kg / h), and the average temperature of the kneaded material melt-kneaded between the open rolls is (° C.), the glass transition temperature Tg (° C.) of the binder resin, when the constant is k, Lf ≧ k · M
/ (T-Tg) is characterized in that the input width is set so as to satisfy the relationship shown in FIG.

【００１０】請求項２に記載の発明のトナー製造のため
の混練物の製造方法は、請求項１に記載の発明におい
て、前記オープンロールの軸線方向へ沿った長さをＬｏ
（ｍｍ）としたとき、前記Ｌｆ（ｍｍ）を０．０５〜
０．５Ｌｏに設定したことを特徴とするものである。According to a second aspect of the present invention, in the method for producing a kneaded product for producing a toner according to the first aspect, the length of the open roll in the axial direction is Lo.
(Mm), the Lf (mm) is 0.05 to
It is characterized by being set to 0.5 Lo.

【００１１】請求項３に記載の発明のトナー製造のため
の混練物の製造方法は、請求項１又は請求項２に記載の
発明において、前記複数のオープンロールのうち相対向
するオープンロールの加熱温度に温度差を形成し、加熱
温度が高温側のオープンロールの上端から内側端まで
を、オープンロールの幅方向への原料の投入範囲に設定
したことを特徴とするものである。According to a third aspect of the present invention, there is provided a method for producing a kneaded material for producing a toner according to the first or second aspect, wherein the opposing open rolls of the plurality of open rolls are heated. The temperature difference is formed, and the heating temperature is set from the upper end to the inner end of the open roll on the high-temperature side within the range for charging the raw material in the width direction of the open roll.

【００１２】[0012]

【発明の実施の形態】図１及び図２はトナー製造のため
の混練物の製造装置１０（以下、単に製造装置１０と称
す）を示す概略図である。図１及び図２に示すように、
製造装置１０は、溶融混練装置としてのオープンロール
混練機１１と、原料搬送供給装置としてのスクリューフ
ィーダー１２とを備えたものである。1 and 2 are schematic views showing an apparatus 10 for producing a kneaded material for producing a toner (hereinafter simply referred to as a production apparatus 10). As shown in FIGS. 1 and 2,
The manufacturing apparatus 10 includes an open roll kneader 11 as a melt kneading apparatus and a screw feeder 12 as a raw material transport / supply apparatus.

【００１３】そして、前記スクリューフィーダー１２は
結着樹脂、顔料及び添加剤（なお、以下に示す添加剤は
ワックス及び荷電制御剤を含む概念とする。）よりなる
原料を搬送し、搬送された原料を次工程に供給するもの
である。一方、前記オープンロール混練機１１はスクリ
ューフィーダー１２から供給された原料を一対のオープ
ンロール１１ａ，１１ｂの間に供給して両オープンロー
ル１１ａ，１１ｂからの加熱及び回転により原料を溶融
混練して混練物を製造するものである。The screw feeder 12 conveys a raw material comprising a binder resin, a pigment and an additive (additives shown below include a wax and a charge control agent). Is supplied to the next step. On the other hand, the open roll kneader 11 supplies the raw material supplied from the screw feeder 12 between the pair of open rolls 11a and 11b, melts and kneads the raw material by heating and rotation from the two open rolls 11a and 11b. It manufactures things.

【００１４】まず、前記スクリューフィーダー１２につ
いて説明すると、スクリューフィーダー１２は一対のオ
ープンロール１１ａ，１１ｂの一端供給側（図１では上
側）の外側方に設置された載置台１３上に載置され、前
記原料を収容可能な本体部１４を備えている。本体部１
４の外面には同本体部１４内と連通するとともに、本体
部１４から前記オープンロール混練機１１側へ筒状に延
びる搬送路１５が設けられ、その搬送路１５の先端側は
一方のオープンロール１１ａの一端供給側の上方に配置
されている。First, the screw feeder 12 will be described. The screw feeder 12 is mounted on a mounting table 13 installed outside the one end supply side (the upper side in FIG. 1) of a pair of open rolls 11a and 11b. There is a main body 14 capable of storing the raw material. Main unit 1
4 is provided on the outer surface thereof with a transfer path 15 which communicates with the inside of the main body section 14 and extends cylindrically from the main body section 14 to the open roll kneader 11 side. 11a is arranged above one end supply side.

【００１５】図２及び図３に示すように、搬送路１５の
下面には、その搬送路１５の基端側から先端側へ向かう
に連れて幅広に延びる供給口１５ａが下方へ開口する状
態に切り欠き形成されている。この供給口１５ａは一方
のオープンロール１１ａの上端から内側端との間に位置
するとともに、一方のオープンロール１１ａの軸線方向
に沿って延びるように配置されている。また、搬送路１
５内には本体部１４側から搬送路１５の先端側へ螺旋状
に延びるスクリュー１６が回転可能に備えられている。As shown in FIGS. 2 and 3, on the lower surface of the transport path 15, a supply port 15a extending from the base end of the transport path 15 toward the distal end thereof is opened downward. Notches are formed. The supply port 15a is located between the upper end and the inner end of the one open roll 11a, and is arranged so as to extend along the axial direction of the one open roll 11a. In addition, transport path 1
A screw 16 helically extending from the main body 14 to the tip end of the transport path 15 is rotatably provided in 5.

【００１６】そして、スクリュー１６の所定方向への回
転により、原料は本体部１４側から搬送路１５の先端側
の供給口１５ａへ搬送される。さらに、搬送された原料
は前記供給口１５ａから落下して一方のオープンロール
１１ａの一端供給側に供給されるようになっている。ま
た、オープンロール１１ａ，１１ｂの他端排出側の下方
位置には溶融混練して製造された混練物を回収する回収
部（図示せず）が設けられている。The raw material is conveyed from the main body 14 side to the supply port 15a on the front end side of the conveying path 15 by the rotation of the screw 16 in a predetermined direction. Further, the conveyed raw material falls from the supply port 15a and is supplied to one end supply side of one open roll 11a. A collecting section (not shown) for collecting the kneaded material produced by melt-kneading is provided below the other ends of the open rolls 11a and 11b.

【００１７】次いで、前記オープンロール混練機１１に
ついて説明する。図１に示すように、一対のオープンロ
ール１１ａ，１１ｂは、それぞれ表面に螺旋状の溝（図
示せず）を有した円筒状をなしている。各オープンロー
ル１１ａ，１１ｂにはその長さ方向へ延びる中心線、即
ち軸線方向に沿ってそれぞれ軸１１ｄが突設され、一対
の軸１１ｄが互いに平行となるようにそれぞれ両端が軸
受け１１ｃに支持されている。そして、両オープンロー
ル１１ａ，１１ｂは図示しないモータにより互いに図３
の矢印に示す方向に回転可能に構成されている。Next, the open roll kneader 11 will be described. As shown in FIG. 1, each of the pair of open rolls 11a and 11b has a cylindrical shape having a spiral groove (not shown) on its surface. Each of the open rolls 11a and 11b has a shaft 11d protruding along a center line extending in the length direction, that is, an axial direction. ing. The two open rolls 11a and 11b are connected to each other by a motor (not shown) as shown in FIG.
It is configured to be rotatable in the direction indicated by the arrow.

【００１８】一方のオープンロール１１ａ内には蒸気、
温水等の熱媒体を供給可能に形成されているとともに、
他方のオープンロール１１ｂ内には冷却水等の冷媒を供
給可能に形成され、それぞれ表面温度を任意に調整可能
に構成されている。そして、一対のオープンロール１１
ａ，１１ｂの間で一方のオープンロール１１ａは高温側
に設定され、他方のオープンロール１１ｂは低温側に設
定される。また、各オープンロール１１ａ，１１ｂはそ
れぞれ一端供給側と他端排出側の設定温度を調整可能に
構成されている。Steam is contained in one open roll 11a.
While being formed to be able to supply a heat medium such as hot water,
The other open roll 11b is formed such that a coolant such as cooling water can be supplied therein, and is configured such that the surface temperature can be adjusted arbitrarily. And a pair of open rolls 11
a and 11b, one open roll 11a is set on the high temperature side, and the other open roll 11b is set on the low temperature side. Further, each of the open rolls 11a and 11b is configured to be able to adjust the set temperature on one end supply side and the other end discharge side, respectively.

【００１９】溶融混練時における一方のオープンロール
１１ａの加熱温度は、溶融混練中の結着樹脂の温度が、
その結着樹脂の溶融温度（Ｔｍ）以下となるように設定
されるのが好ましい。溶融温度Ｔｍを越えると、結着樹
脂の溶融が促進されて低粘性流体となり、結着樹脂の分
子の切断が促進され、顔料、添加剤に作用する圧縮力、
せん断力が小さくなり好ましくない。The heating temperature of one of the open rolls 11a during melt-kneading depends on the temperature of the binder resin during melt-kneading.
It is preferable that the temperature is set to be equal to or lower than the melting temperature (Tm) of the binder resin. When the melting temperature Tm is exceeded, the melting of the binder resin is promoted to become a low-viscosity fluid, the cutting of the molecules of the binder resin is promoted, and the compressive force acting on the pigment and the additive,
It is not preferable because the shearing force becomes small.

【００２０】図１に示すように、一対のオープンロール
１１ａ，１１ｂ間には、それらオープンロール１１ａ，
１１ｂの軸線方向に沿って一定間隔で延びるギャップが
形成され、このギャップは０．１〜０．５ｍｍに設定さ
れるのが好ましい。ギャップが０．１ｍｍより狭いと、
オープンロール１１ａ，１１ｂ間に形成されるバンクが
小さくなるとともに、ギャップ間に巻き込み可能な原料
量が少なくなり、混練物の生産性が低下して好ましくな
い。一方、ギャップが０．５ｍｍを越えると、オープン
ロール１１ａ，１１ｂ間に供給される原料が落下しやす
く、バンクを形成しにくくなり好ましくない。As shown in FIG. 1, between the pair of open rolls 11a and 11b, the open rolls 11a and 11b are provided.
A gap extending at regular intervals along the axial direction of 11b is formed, and this gap is preferably set to 0.1 to 0.5 mm. If the gap is smaller than 0.1mm,
The size of the bank formed between the open rolls 11a and 11b is reduced, and the amount of the raw material that can be wound between the gaps is reduced. On the other hand, if the gap exceeds 0.5 mm, the raw material supplied between the open rolls 11a and 11b tends to fall, and it is difficult to form a bank, which is not preferable.

【００２１】上記構成の製造装置１０を使用して原料の
溶融混練を行う際、スクリューフィーダー１２からの原
料の供給量をＭ（ｋｇ／ｈ）、一方（高温側）のオープ
ンロール１１ａの一端供給側の混練物の平均温度をＴ
（℃）とする。なお、前記平均温度Ｔ（℃）は放射温度
計で計測される。また、結着樹脂のガラス転移温度をＴ
ｇ（℃）、定数ｋ（５００）とした場合、供給口１５ａ
から供給される原料の投入幅Ｌｆ（ｍｍ）、即ちオープ
ンロール１１ａ，１１ｂの基端側から軸線方向へ沿って
延びる距離としての原料の投入幅Ｌｆ（ｍｍ）は Ｌｆ≧ｋ・Ｍ／（Ｔ−Ｔｇ）…（１） に示す式に従って設定される。When the raw material is melted and kneaded using the manufacturing apparatus 10 having the above configuration, the supply amount of the raw material from the screw feeder 12 is set to M (kg / h), and one end of the one (high temperature side) open roll 11a is supplied. The average temperature of the kneaded material on the side
(° C). The average temperature T (° C.) is measured by a radiation thermometer. Further, the glass transition temperature of the binder resin is T
g (° C.) and constant k (500), the supply port 15a
Width Lf (mm) of the raw material supplied from, ie, the raw material feeding width Lf (mm) as a distance extending along the axial direction from the base end side of the open rolls 11a and 11b, is Lf ≧ k · M / (T −Tg)... Is set according to the equation shown in (1).

【００２２】なお、前記定数ｋ（５００）は、原料の供
給量Ｍに比例して投入幅Ｌｆが広くなり、Ｔ−Ｔｇに反
比例して広くなるという一般的な知見のもとに、本発明
者らが実験を行って導き出した数値である。The constant k (500) is based on the general knowledge that the input width Lf is increased in proportion to the raw material supply amount M and is increased in inverse proportion to T-Tg. These are numerical values derived by conducting experiments.

【００２３】式（１）において、供給量Ｍ及びガラス転
移温度Ｔｇを一定とした場合、投入幅Ｌｆは混練物の平
均温度Ｔに依存し、平均温度Ｔが高くなる、即ちＴ−Ｔ
ｇが大きくなると投入幅Ｌｆは狭くなり、平均温度Ｔが
低くなる、即ちＴ−Ｔｇが小さくなると投入幅Ｌｆは広
く設定される。従って、原料の溶融混練時における混練
物の平均温度Ｔに対応して投入幅Ｌｆを設定することが
可能となる。また、供給量Ｍ、平均温度Ｔを一定とした
場合、投入幅Ｌｆは使用される結着樹脂のガラス転移温
度Ｔｇに依存し、ガラス転移温度Ｔｇが高くなると投入
幅Ｌｆは広く、低くなると投入幅Ｌｆは狭く設定され
る。従って、使用される結着樹脂に対応して投入幅Ｌｆ
を決定することが可能となる。In the formula (1), when the supply amount M and the glass transition temperature Tg are constant, the charging width Lf depends on the average temperature T of the kneaded material, and the average temperature T increases, that is, TT
As g increases, the charging width Lf decreases, and the average temperature T decreases. That is, as T-Tg decreases, the charging width Lf is set wide. Therefore, it is possible to set the charging width Lf corresponding to the average temperature T of the kneaded material at the time of melt-kneading the raw materials. In addition, when the supply amount M and the average temperature T are constant, the charging width Lf depends on the glass transition temperature Tg of the binder resin used. The charging width Lf increases when the glass transition temperature Tg increases, and decreases when the glass transition temperature Tg decreases. The width Lf is set narrow. Therefore, the input width Lf corresponding to the binder resin used is
Can be determined.

【００２４】さらに、平均温度Ｔを一定とした場合、投
入幅Ｌｆは原料の供給量Ｍに依存し、供給量Ｍが多くな
ると投入幅Ｌｆは広くなり、少なくなると投入幅Ｌｆは
狭くなる。従って、原料の供給量Ｍに対応して投入幅Ｌ
ｆを決定することが可能となる。Further, when the average temperature T is constant, the supply width Lf depends on the supply amount M of the raw material. The supply width Lf increases as the supply amount M increases, and the supply width Lf decreases as the supply amount M decreases. Therefore, the input width L corresponding to the raw material supply amount M
f can be determined.

【００２５】オープンロール１１ａ，１１ｂの軸線方向
への長さをＬｏ（ｍｍ）としたとき、投入幅Ｌｆ（ｍ
ｍ）は０．０５〜０．５Ｌｏに設定されるのが好まし
く、０．１〜０．１５Ｌｏに設定されるのがより好まし
い。投入幅Ｌｆが０．０５Ｌｏより短くなると、原料の
供給量Ｍが少なくなり、混練物の生産性が低下して好ま
しくない。一方、投入幅Ｌｆが０．５Ｌｏより長くなる
と、原料の投入幅Ｌｆが広くなりすぎ、原料が排出側へ
移送されるまでの間に原料に作用する圧縮力、せん断力
が小さくなる。従って、顔料、添加物等を十分に微細化
できず好ましくない。When the length of the open rolls 11a and 11b in the axial direction is Lo (mm), the input width Lf (m
m) is preferably set to 0.05 to 0.5 Lo, more preferably 0.1 to 0.15 Lo. When the charging width Lf is shorter than 0.05 Lo, the supply amount M of the raw material decreases, and the productivity of the kneaded material is undesirably reduced. On the other hand, when the charging width Lf is longer than 0.5 Lo, the charging width Lf of the raw material becomes too wide, and the compressive force and the shearing force acting on the raw material before the raw material is transferred to the discharge side are reduced. Therefore, pigments, additives, and the like cannot be sufficiently miniaturized, which is not preferable.

【００２６】次いで、トナー製造のための混練物の原料
について説明すると、まず、結着樹脂としては、その種
類は特に限定されるものではなく、黒トナー又はカラー
トナー用の公知の結着樹脂を使用することができ、例え
ばポリエステル樹脂、ポリスチレン樹脂、スチレン−ア
クリル酸エステル共重合樹脂等のスチレン系樹脂、ポリ
メチルメタクリレート等のアクリル系樹脂、ポリエチレ
ン等のポリオレフィン系樹脂、ポリウレタン樹脂、エポ
キシ樹脂等が挙げられる。これらの結着樹脂は単独又は
二種以上混合して使用される。結着樹脂はトナー中に通
常８０〜９５重量％配合される。Next, the raw material of the kneaded material for producing the toner will be described. First, the kind of the binder resin is not particularly limited, and a known binder resin for black toner or color toner may be used. It can be used, for example, polyester resin, polystyrene resin, styrene resin such as styrene-acrylate copolymer resin, acrylic resin such as polymethyl methacrylate, polyolefin resin such as polyethylene, polyurethane resin, epoxy resin and the like. No. These binder resins are used alone or in combination of two or more. The binder resin is usually blended in the toner in an amount of 80 to 95% by weight.

【００２７】顔料としては特に限定されるものではな
く、キナクリドン、ブリリアントカーミン６Ｂ、パーマ
ネントレッド等の赤色顔料、ベンズイミダゾロン、ジク
ロロベンジジン等の黄色顔料、コバルトブルー、銅フタ
ロシアニン等の青色顔料、クロムグリーン、酸化クロ
ム、ピグメントグリーンＢ等の緑色顔料、カーボンブラ
ック、アセチレンブラック等の黒色顔料が挙げられる。
これらの顔料は単独又は二種以上混合して使用される。
顔料はトナー中に通常３〜１０重量％配合される。The pigment is not particularly limited. Red pigments such as quinacridone, brilliant carmine 6B and permanent red; yellow pigments such as benzimidazolone and dichlorobenzidine; blue pigments such as cobalt blue and copper phthalocyanine; And green pigments such as chromium oxide and Pigment Green B, and black pigments such as carbon black and acetylene black.
These pigments are used alone or in combination of two or more.
The pigment is usually blended in the toner in an amount of 3 to 10% by weight.

【００２８】前記結着樹脂及び顔料以外の添加剤として
の前記荷電制御剤は特に限定されるものではなく、黒ト
ナー又はカラートナー用の公知の負帯電又は正帯電トナ
ー用の荷電制御剤を使用することができる。負帯電トナ
ー用の荷電制御剤としては、サリチル酸又はその誘導体
のクロム、亜鉛、ジルコニウム錯体若しくは塩化合物、
アゾ錯体染料、長鎖アルキルカルボン酸塩等の界面活性
剤等が挙げられる。正帯電トナー用の荷電制御剤として
はニグロシン染料又はその誘導体、四級アンモニウム
塩、グアニジン塩等が挙げられる。また、前記ワックス
はカルナウバワックス等の天然ワックス及び合成ワック
ス類、シリコーン系重合体、高級脂肪酸、ポリオレフィ
ン系重合体、低分子重合体等が挙げられる。The charge control agent as an additive other than the binder resin and pigment is not particularly limited, and a known charge control agent for negatively charged or positively charged toner for black toner or color toner may be used. can do. As a charge control agent for negatively charged toner, chromium, zinc, zirconium complex or salt compound of salicylic acid or a derivative thereof,
Examples include surfactants such as azo complex dyes and long-chain alkylcarboxylates. Examples of the charge control agent for a positively charged toner include a nigrosine dye or a derivative thereof, a quaternary ammonium salt, and a guanidine salt. Examples of the wax include natural and synthetic waxes such as carnauba wax, silicone-based polymers, higher fatty acids, polyolefin-based polymers, and low-molecular-weight polymers.

【００２９】次に、前記製造装置１０を使用した混練物
の製造方法について記載する。Next, a method for producing a kneaded material using the production apparatus 10 will be described.

【００３０】さて、結着樹脂、顔料及び添加剤を所定量
計量し、それら原料を本体部１４内に供給する。その
後、製造装置１０を稼動させて本体部１４側からオープ
ンロール混練機１１側へ原料を搬送させる。搬送路１５
内ではスクリュー１６が回転して原料を常に攪拌してい
るため、搬送路１５内での原料の滞留が防止される。A predetermined amount of the binder resin, the pigment, and the additive are measured, and the raw materials are supplied into the main body 14. Thereafter, the production apparatus 10 is operated to transport the raw materials from the main body 14 to the open roll kneader 11. Transport path 15
In this case, the screw 16 rotates to constantly stir the raw material, so that the raw material is prevented from staying in the transport path 15.

【００３１】次いで、一方のオープンロール１１ａを加
熱して高温側とし、他方のオープンロール１１ｂを加熱
するとともに、一方のオープンロール１１ａより低温側
に設定して両オープンロール１１ａ，１１ｂ間において
加熱温度に温度差を発生させる。なお、一方のオープン
ロール１１ａにおいては、一端供給側の加熱温度は混練
物の平均温度Ｔが所定の温度になるように適宜調整さ
れ、他端排出側の加熱温度は一定温度に調整される。そ
れと同時に、一方のオープンロール１１ａをその回転数
が他方のオープンロール１１ｂの回転数より大きくなる
ように回転させる。Next, one open roll 11a is heated to a high temperature side, the other open roll 11b is heated, and a lower temperature than the one open roll 11a is set to a heating temperature between the two open rolls 11a and 11b. Causes a temperature difference. In one open roll 11a, the heating temperature on the one end supply side is appropriately adjusted so that the average temperature T of the kneaded material becomes a predetermined temperature, and the heating temperature on the other end discharge side is adjusted to a constant temperature. At the same time, one of the open rolls 11a is rotated so that its rotational speed is higher than the rotational speed of the other open roll 11b.

【００３２】すると、原料が一方のオープンロール１１
ａの一端供給側に落下して供給され、さらに、図３に示
すように、オープンロール１１ａ，１１ｂ間に堆積して
バンクが形成される。このとき、供給口１５ａが一方の
オープンロール１１ａの上端よりギャップ側に配置され
ているため、ギャップと反対側に落下する原料がほとん
どなくなる。次に、バンクにおける混練物の平均温度Ｔ
（℃）を放射温度計により計測し、その平均温度Ｔ
（℃）、結着樹脂のガラス転移温度Ｔｇ（℃）及び原料
の供給量Ｍ（ｋｇ／ｈ）を上記式（１）に代入して投入
幅Ｌｆ（ｍｍ）を算出する。Then, the raw material is changed to the one open roll 11
a is dropped and supplied to the one supply side, and is further deposited between the open rolls 11a and 11b to form a bank as shown in FIG. At this time, since the supply port 15a is disposed closer to the gap than the upper end of one of the open rolls 11a, almost no raw material falls to the opposite side to the gap. Next, the average temperature T of the kneaded material in the bank
(° C) is measured with a radiation thermometer, and the average temperature T
(° C.), the glass transition temperature Tg (° C.) of the binder resin and the supply amount M (kg / h) of the raw material are substituted into the above equation (1) to calculate the charging width Lf (mm).

【００３３】そして、供給口１５ａから供給される原料
の投入幅Ｌｆ、即ち一方のオープンロール１１ａ上に配
置される供給口１５ａの長さ方向への長さが式（１）か
ら算出された投入幅Ｌｆと同じ又は長くなるように載置
台１３の位置を調節して搬送路１５の位置を調節する。Then, the input width Lf of the raw material supplied from the supply port 15a, that is, the length in the length direction of the supply port 15a disposed on one of the open rolls 11a, is calculated from the formula (1). The position of the mounting table 13 is adjusted so as to be equal to or longer than the width Lf, and the position of the transport path 15 is adjusted.

【００３４】算出された投入幅Ｌｆで原料が帯状に供給
されると、まとまった状態で原料が供給される場合と比
較して、バンクにおける原料に対する加熱状況が良好に
なり、固形状のままでバンクに存在する原料が少なくな
って固まりの発生が抑制される。そして、固まりになら
ないバンク上の原料は相対向するオープンロール１１
ａ，１１ｂの内側への回転により前記バンク内に飲み込
まれ、その飲み込まれた原料によりバンク内に対流が発
生する。バンク内の結着樹脂は、一方のオープンロール
１１ａ表面における伝熱作用により加熱溶融してその一
方のオープンロール１１ａ表面に巻き着く。When the raw material is supplied in a belt shape with the calculated input width Lf, the heating condition of the raw material in the bank is improved as compared with the case where the raw material is supplied in a lump, and the solid state is maintained. The amount of raw materials present in the bank is reduced, and the occurrence of lump is suppressed. The raw material on the bank that does not clump is the opposing open roll 11
The inward rotation of a and 11b swallows into the bank, and convection occurs in the bank due to the swallowed raw material. The binder resin in the bank is heated and melted by the heat transfer effect on the surface of the one open roll 11a and winds around the surface of the one open roll 11a.

【００３５】このとき、一方のオープンロール１１ａの
一端供給側の加熱温度は、溶融混練中の結着樹脂の温度
が、同結着樹脂の溶融温度Ｔｍ以下となるように設定さ
れるため、結着樹脂の溶融が促進されず結着樹脂の分子
の切断が促進されることが抑制される。そして、高粘性
流体の結着樹脂がギャップ内で練り込まれることにより
圧縮力、せん断力が生じ、その圧縮力、せん断力により
顔料、添加剤等が微細化されながら結着樹脂中へ分散さ
れる。At this time, the heating temperature of the one end supply side of the one open roll 11a is set so that the temperature of the binder resin during the melt-kneading is equal to or lower than the melting temperature Tm of the binder resin. It is suppressed that the melting of the binder resin is not promoted and the cutting of the molecules of the binder resin is promoted. A compressive force and a shearing force are generated by kneading the binder resin of the high-viscosity fluid in the gap, and the compressive force and the shearing force disperse the pigments and additives into the binder resin while being miniaturized. You.

【００３６】続いて、結着樹脂表面に顔料、添加剤が練
り込まれた状態で、繰り返し圧縮力、せん断力を受けて
混練されながら、原料は一対のオープンロール１１ａ，
１１ｂの回転速度の差により排出側へ移送される。そし
て、微細化された顔料、添加剤等が結着樹脂中に強力に
練り込まれ、均一に分散された混練物が回収部に回収さ
れる。Subsequently, while the pigment and the additive are kneaded on the surface of the binder resin, the material is repeatedly kneaded under a compressive force and a shearing force, and the raw material is supplied to the pair of open rolls 11a,
It is transferred to the discharge side by the difference in the rotation speed of 11b. Then, the finely divided pigment, additives, and the like are strongly kneaded into the binder resin, and the kneaded material uniformly dispersed is collected in the collection unit.

【００３７】得られた混練物を冷却して固化させた後、
混練物を粗粉砕、微粉砕して分級した後、表面処理が行
われてトナーが製造される。得られるトナーは結着樹脂
中に微細化された顔料、添加剤が均一に分散されてい
る。After cooling and solidifying the obtained kneaded material,
After the kneaded material is roughly pulverized and finely pulverized and classified, a surface treatment is performed to produce a toner. In the obtained toner, finely divided pigments and additives are uniformly dispersed in the binder resin.

【００３８】前記実施形態によって発揮される効果につ
いて、以下に記載する。The effects exerted by the above embodiment will be described below.

【００３９】・ 式（１）を設定したため、原料の供給
量Ｍ、ガラス転移温度Ｔｇを一定にした場合、混練物の
平均温度Ｔに依存して投入幅Ｌｆを設定することが可能
となった。そのため、その投入幅Ｌｆと同じ又は広い投
入幅Ｌｆで原料をオープンロール混練機１１に供給する
ことにより混練物の加熱温度を必要以上に上昇させない
条件でも、混練物の加熱状況を良好にして固まりの発生
を抑制することができる。Since the formula (1) is set, when the supply amount M of the raw material and the glass transition temperature Tg are kept constant, it is possible to set the charging width Lf depending on the average temperature T of the kneaded material. . Therefore, even if the heating temperature of the kneaded material is not increased more than necessary by supplying the raw materials to the open roll kneader 11 with the same or wider charging width Lf, the heating condition of the kneaded material is improved and the consolidation occurs. Can be suppressed.

【００４０】従って、得られる混練物における原料の分
散性の悪化を防止してその混練物を使用したトナーの性
能の低下を防止することができる。その結果、得られた
混練物より調製したトナーを使用して電子写真法により
形成された電気的潜像を現像したとき、被転写材に転写
されるトナー画像の解析度を向上させることができると
ともに、画質のムラ、くすみ、透明感の阻害をなくして
画質の低下を防止することができる。Therefore, it is possible to prevent the deterioration of the dispersibility of the raw material in the obtained kneaded material and to prevent the performance of the toner using the kneaded material from deteriorating. As a result, when an electric latent image formed by electrophotography is developed using the toner prepared from the obtained kneaded material, the resolution of the toner image transferred to the transfer material can be improved. At the same time, it is possible to prevent the image quality from deteriorating by eliminating unevenness, dullness, and transparency of the image quality.

【００４１】・ 原料の投入幅Ｌｆに幅を持たせて設定
することにより、原料をオープンロール混練機１１に帯
状に供給することができる。従って、原料がまとまった
状態で供給された従来と異なり、原料を効率良く加熱し
て固まりの発生を抑制することができ、一方のオープン
ロール１１ａを必要以上に加熱するのに必要なエネルギ
ーを節約することができる。The raw material can be supplied to the open-roll kneader 11 in a belt shape by setting the width Lf of the raw material to have a certain width. Therefore, unlike the conventional method in which the raw material is supplied in a lump, the raw material can be efficiently heated to suppress the occurrence of agglomeration, and the energy required to heat one open roll 11a more than necessary can be saved. can do.

【００４２】・ 原料の供給量Ｍ、ガラス転移温度Ｔｇ
を一定とした場合、混練物の平均温度Ｔに依存して投入
幅Ｌｆを設定することができ、溶融温度Ｔｍより低い温
度で原料の溶融混練を行うことができる。そのため、結
着樹脂を高粘性流体の状態に維持でき、結着樹脂の練り
込みにより発生する圧縮力、せん断力を低粘性流体の結
着樹脂よりも大きくすることができる。The raw material supply amount M and the glass transition temperature Tg
Is constant, the charging width Lf can be set depending on the average temperature T of the kneaded material, and the raw material can be melt-kneaded at a temperature lower than the melting temperature Tm. Therefore, the binder resin can be maintained in a high-viscosity fluid state, and the compressive force and the shear force generated by kneading the binder resin can be made larger than those of the low-viscosity fluid.

【００４３】・ 供給口１５ａは先端に向かうに連れて
幅広に延びているため、原料が供給されたばかりの位置
には供給を少なくして、溶融が進むに連れて供給を多く
することができる。従って、投入幅Ｌｆの設定とともに
固まりの発生を確実に抑制することができる。Since the supply port 15a extends toward the tip end, the supply can be reduced at the position where the raw material has just been supplied, and can be increased as the melting progresses. Therefore, it is possible to reliably suppress the occurrence of the lump together with the setting of the input width Lf.

【００４４】・ 一対のオープンロール１１ａ，１１ｂ
間のギャップは０．１〜０．５ｍｍに設定されている。
そのため、ギャップ間で溶融混練される混練物の量を確
保して混練物の生産性の低下を防止することができる。
また、オープンロール１１ａ，１１ｂ間に供給される原
料の落下量を少なくして混練物の生産性の低下を防止す
ることができるとともに、バンクを確実に形成して混練
物の溶融混練を確実に行うことができる。A pair of open rolls 11a, 11b
The gap between them is set to 0.1 to 0.5 mm.
Therefore, it is possible to secure the amount of the kneaded material that is melt-kneaded between the gaps and prevent the productivity of the kneaded material from lowering.
Further, the amount of the raw material supplied between the open rolls 11a and 11b can be reduced to prevent a reduction in the productivity of the kneaded material, and a bank can be reliably formed to reliably melt and knead the kneaded material. It can be carried out.

【００４５】・ 結着樹脂、顔料及び添加剤はスクリュ
ーフィーダー１２から一括してオープンロール混練機１
１に供給される。そのため、各材料をそれぞれ別々の装
置を使用してオープンロール混練機１１に供給する場合
と比較して製造装置１０の構成を簡易化することができ
る。The binder resin, the pigment and the additives are collectively fed from the screw feeder 12 to the open roll kneader 1
1 is supplied. Therefore, the configuration of the manufacturing apparatus 10 can be simplified as compared with the case where the respective materials are supplied to the open roll kneader 11 using separate apparatuses.

【００４６】・ 投入幅Ｌｆは０．０５〜０．５Ｌｏに
設定されている。そのため、原料の供給量Ｍが少なくな
るのを防止して混練物の生産性の低下を防止することが
できる。また、原料が排出側へ移送されるまでの間に圧
縮力、せん断力が原料に作用する時間を長く取って顔
料、添加物等を十分に微細化することができる。The charging width Lf is set to 0.05 to 0.5 Lo. For this reason, it is possible to prevent the supply amount M of the raw material from decreasing and to prevent the productivity of the kneaded material from decreasing. In addition, the time required for the compressive force and the shear force to act on the raw material before the raw material is transferred to the discharge side can be extended to sufficiently reduce the size of the pigment, additive, and the like.

【００４７】・ 供給口１５ａは一方のオープンロール
１１ａのギャップ側半分までの間に配置されているた
め、原料がギャップと反対側に落下することなくギャッ
プ間に確実に供給される。従って、原料の浪費を少なく
することができる。Since the supply port 15a is arranged up to the gap half of one of the open rolls 11a, the raw material is reliably supplied to the gap without falling to the opposite side of the gap. Therefore, waste of raw materials can be reduced.

【００４８】[0048]

【実施例】以下、実施例及び比較例により、前記実施形
態をさらに具体的に説明する。The above embodiment will be described more specifically with reference to examples and comparative examples.

【００４９】（実施例１〜４及び比較例１〜４）実施例
１〜４では、結着樹脂及び顔料よりなる原料において、
結着樹脂のガラス転移温度Ｔｇを６６℃、原料の供給量
Ｍを１０ｋｇ／ｈ（実施例１及び２）、２０ｋｇ／ｈ
（実施例３及び４）に設定した状態で、混練物の平均温
度Ｔを適宜設定して投入幅Ｌｆを算出した。そして、算
出された投入幅Ｌｆより広い投入幅Ｌｆで原料を供給
し、バンクにおける固まりの発生状況を目視により下記
の３段階で判定した。さらに、調製された混練物の顔料
の分散性を測定するため、分光光度計により波長７００
ｎｍにおける光透過度を測定した。一方、比較例１〜４
では実施例１〜４でそれぞれ算出された投入幅Ｌｆより
狭い投入幅Ｌｆで原料を供給し、バンクにおける固まり
の発生状況を実施例と同様の判定基準で判定した。(Examples 1 to 4 and Comparative Examples 1 to 4) In Examples 1 to 4, the raw materials comprising the binder resin and the pigment
The glass transition temperature Tg of the binder resin is 66 ° C., the raw material supply amount M is 10 kg / h (Examples 1 and 2), 20 kg / h.
In the state set in (Examples 3 and 4), the average width T of the kneaded material was appropriately set, and the charging width Lf was calculated. Then, the raw material was supplied with an input width Lf wider than the calculated input width Lf, and the occurrence of lump in the bank was visually determined in the following three stages. Further, in order to measure the dispersibility of the pigment in the prepared kneaded material, a wavelength of 700 was measured with a spectrophotometer.
The light transmittance in nm was measured. On the other hand, Comparative Examples 1 to 4
In the example, the raw material was supplied with the input width Lf smaller than the input width Lf calculated in each of Examples 1 to 4, and the state of occurrence of lump in the bank was determined based on the same criterion as in the example.

【００５０】具体的には、結着樹脂として不飽和ポリエ
ステル樹脂｛商品名 ＨＰ−３１３Ｈ 日本合成化学
（株）製｝を使用し、顔料としてキナクリドン（ピグメ
ントレッド１２２）を使用した。また、不飽和ポリエス
テル樹脂の溶融温度Ｔｍは１３５℃である。このオープ
ンロール混練機１１は外径２１０ｍｍの一対のオープン
ロール１１ａ，１１ｂを備え、ギャップは０．１ｍｍで
あった。Specifically, an unsaturated polyester resin (trade name: HP-313H, manufactured by Nippon Synthetic Chemical Co., Ltd.) was used as a binder resin, and quinacridone (Pigment Red 122) was used as a pigment. The melting temperature Tm of the unsaturated polyester resin is 135 ° C. This open roll kneader 11 was provided with a pair of open rolls 11a and 11b having an outer diameter of 210 mm, and the gap was 0.1 mm.

【００５１】また、一方のオープンロール１１ａの一端
供給側の設定温度を適宜調整し、他端排出側の設定温度
を３５℃に設定するとともに、回転数を７０ｒｐｍに設
定した。他方のオープンロール１１ｂの一端供給側及び
他端排出側の温度を２０℃に設定するとともに、回転数
を６０ｒｐｍに設定した。The set temperature of one supply side of one open roll 11a was appropriately adjusted, the set temperature of the other end discharge side was set at 35 ° C., and the rotation speed was set at 70 rpm. The temperature of the one end supply side and the other end discharge side of the other open roll 11b was set to 20 ° C., and the rotation speed was set to 60 rpm.

【００５２】まず、前記結着樹脂７０質量部、顔料３０
質量部をヘンシェルミキサー｛ＦＭ７５Ｊ 三井鉱山
（株）製｝にて混合した。次いで、混合した原料をスク
リューフィーダー１２の本体部１４に供給し、搬送路１
５から搬送された原料を、算出された投入幅Ｌｆより広
い投入幅Ｌｆでオープンロール混練機１１に供給した。
そして、バンクでの固まりの発生状況を目視で測定し
た。判定基準としては固まりが発生しなかったものを
◎、小さい固まりが発生したが、やがてバンクに飲み込
まれて消滅したものを○、固まりが発生し、バンク上に
滞留するものを×とした。その結果を表１に示す。First, 70 parts by mass of the binder resin, pigment 30
The parts by mass were mixed with a Henschel mixer {FM75J manufactured by Mitsui Mining Co., Ltd.}. Next, the mixed raw material is supplied to the main body 14 of the screw feeder 12, and
The raw material conveyed from No. 5 was supplied to the open roll kneader 11 with an input width Lf wider than the calculated input width Lf.
Then, the occurrence state of the lump in the bank was visually measured. As a criterion, ◎ indicates that no lump was generated, ○ indicates that a small lump was generated, but eventually was swallowed by the bank and disappeared, and x indicates that lump was generated and stayed on the bank. Table 1 shows the results.

【００５３】さらに、混練物を２枚のスライドガラス間
に挟み、２００℃で２分間混練物を加熱、溶融させて押
しつぶし膜厚６０±５μｍの薄膜状に調製した。そし
て、この薄膜の波長７００ｎｍの光透過度を分光光度計
｛Ｕ−２０１０ 日立製作所（株）製｝を使用して測定
した。その結果を表１に示す。Further, the kneaded material was sandwiched between two slide glasses, heated and melted at 200 ° C. for 2 minutes to prepare a thin film having a crushed film thickness of 60 ± 5 μm. The light transmittance of the thin film at a wavelength of 700 nm was measured using a spectrophotometer (U-2010, manufactured by Hitachi, Ltd.). Table 1 shows the results.

【００５４】[0054]

【表１】 [Table 1]

【００５５】（実施例５〜８及び比較例５〜８）実施例
５〜８では、結着樹脂｛商品名 ＨＰ−３２５ 日本合
成化学（株）製｝及び前記実施例１〜４と同じ顔料より
なる原料において、結着樹脂のガラス転移温度Ｔｇを６
１℃、原料の供給量Ｍを１０ｋｇ／ｈ（実施例５及び
６）、２０ｋｇ／ｈ（実施例７及び８）に設定した状態
で、混練物の平均温度Ｔを適宜設定して投入幅Ｌｆを算
出した。そして、算出された投入幅Ｌｆより広い投入幅
Ｌｆで原料を供給し、バンクにおける固まりの発生状況
を実施例１〜４と同様の判定基準で判定した。さらに、
調製された混練物の光透過度を実施例１〜４と同様の方
法で測定した。一方、比較例５〜８では実施例５〜８で
それぞれ算出された投入幅Ｌｆより狭い投入幅Ｌｆで原
料を供給し、バンクにおける固まりの発生状況を実施例
１〜４と同様の判定基準で判定した。その結果を表２に
示す。(Examples 5 to 8 and Comparative Examples 5 to 8) In Examples 5 to 8, a binder resin (trade name: HP-325, manufactured by Nippon Synthetic Chemical Co., Ltd.) and the same pigments as in Examples 1 to 4 were used. Of the binder resin, the glass transition temperature Tg of the binder resin is 6
At 1 ° C., the raw material supply amount M was set at 10 kg / h (Examples 5 and 6) and 20 kg / h (Examples 7 and 8), and the average temperature T of the kneaded material was appropriately set and the charging width Lf was set. Was calculated. Then, the raw material was supplied with an input width Lf wider than the calculated input width Lf, and the occurrence of lump in the bank was determined based on the same determination criteria as in Examples 1 to 4. further,
The light transmittance of the prepared kneaded material was measured in the same manner as in Examples 1 to 4. On the other hand, in Comparative Examples 5 to 8, the raw material is supplied with an input width Lf smaller than the input width Lf calculated in Examples 5 to 8, respectively, and the state of occurrence of lump in the bank is determined based on the same criteria as in Examples 1 to 4. Judged. Table 2 shows the results.

【００５６】[0056]

【表２】 [Table 2]

【００５７】表１及び表２に示すように、平均温度Ｔに
依存して算出された投入幅Ｌｆより広い投入幅Ｌｆで原
料を供給したとき、バンク上に固まりが発生するのを抑
制することができることが示された。また、固まりが発
生してもバンクに飲み込まれて消滅することが示され
た。一方、投入幅Ｌｆより狭い投入幅Ｌｆで原料を供給
したとき、バンク上に固まりが発生してしまうことが示
された。As shown in Tables 1 and 2, when the raw material is supplied with a supply width Lf wider than the supply width Lf calculated depending on the average temperature T, it is possible to suppress the occurrence of agglomeration on the bank. It was shown that it could be. In addition, it was shown that even if a mass occurs, it is swallowed by the bank and disappears. On the other hand, it has been shown that when the raw material is supplied with the input width Lf smaller than the input width Lf, a lump is generated on the bank.

【００５８】なお、本実施形態は、次のように変更して
具体化することも可能である。The present embodiment can be embodied with the following modifications.

【００５９】・ 供給口１５ａを本体部１４側から先端
側へ向かうに連れて幅広に形成したが、供給口１５ａを
本体部１４側から先端側へ向かうに連れて同一幅で形成
してもよく、本体部１４側から先端側へ向かうに連れて
幅狭に形成してもよい。Although the supply port 15a is formed to be wider from the main body 14 toward the distal end, the supply port 15a may be formed to have the same width from the main body 14 to the distal end. Alternatively, it may be formed to be narrower as going from the main body portion 14 side to the distal end side.

【００６０】・ 供給口１５ａを一方のオープンロール
１１ａの上端から内側端までの間に配置したが、供給口
１５ａを一対のオープンロール１１ａ，１１ｂの間に配
置してもよい。Although the supply port 15a is arranged between the upper end and the inner end of one open roll 11a, the supply port 15a may be arranged between the pair of open rolls 11a and 11b.

【００６１】・ 実施形態では一対のオープンロール１
１ａ，１１ｂを備えたオープンロール混練機１１を使用
してトナー製造のための混練物の製造装置１０とした
が、３本以上のオープンロールを使用したオープンロー
ル混練機１１を使用してもよい。In the embodiment, a pair of open rolls 1
Although the kneaded material manufacturing apparatus 10 for toner production is made using the open roll kneading machine 11 provided with 1a and 11b, an open roll kneading machine 11 using three or more open rolls may be used. .

【００６２】・ 実施形態では原料搬送供給装置として
スクリューフィーダー１２を使用したが、テーブルフィ
ーダー、振動フィーダー、モーノポンプ等を使用してオ
ープンロール混練機１１に原料を供給してもよい。In the embodiment, the screw feeder 12 is used as the raw material transporting / supplying device. However, the raw material may be supplied to the open roll kneader 11 using a table feeder, a vibration feeder, a mono pump or the like.

【００６３】・ 実施形態では、原料として結着樹脂、
顔料、ワックス及び荷電制御剤を使用して混練物を製造
する際に、その原料の投入幅Ｌｆを設定したが、原料と
して結着樹脂及び顔料のみを使用して混練物を製造する
際に、その原料の投入幅Ｌｆを設定してもよい。さら
に、原料として結着樹脂及び顔料よりマスターバッチを
調製した後、そのマスターバッチとワックス及び荷電制
御剤のうちの少なくともいずれか一方よりなる原料を希
釈混練する際に、その原料の投入幅Ｌｆを設定してもよ
い。In the embodiment, a binder resin is used as a raw material,
When manufacturing the kneaded material using the pigment, the wax and the charge control agent, the input width Lf of the raw material was set, but when manufacturing the kneaded material using only the binder resin and the pigment as the raw material, The input width Lf of the raw material may be set. Further, after preparing a masterbatch from a binder resin and a pigment as a raw material, when diluting and kneading the raw material composed of the masterbatch and at least one of the wax and the charge control agent, the input width Lf of the raw material is adjusted. May be set.

【００６４】・ 原料搬送供給装置として図４に示すテ
ーブルフィーダー２０を使用してもよい。テーブルフィ
ーダー２０は本体２１を備え、その本体２１には同本体
２１からオープンロール混練機１１へ延びるテーブル２
２が備えられている。テーブル２２は所定幅を有し、そ
のテーブル２２の先端は開放形成され、先端は一方のオ
ープンロール１１ａの一端供給側の上方に配置されてい
る。そして、本体２１から供給される原料はテーブル２
２から一方のオープンロール１１ａの一端供給側に供給
されるように構成され、テーブル２２の先端の幅を投入
幅Ｌｆと設定し、上記式（１）により、投入幅Ｌｆを設
定してもよい。The table feeder 20 shown in FIG. 4 may be used as a raw material transport / supply device. The table feeder 20 includes a main body 21, and a table 2 extending from the main body 21 to the open roll kneader 11.
2 are provided. The table 22 has a predetermined width, the tip of the table 22 is formed open, and the tip is disposed above one end supply side of one of the open rolls 11a. The raw material supplied from the main body 21 is a table 2
2 is supplied to one end supply side of one of the open rolls 11a, the width of the tip of the table 22 is set as the input width Lf, and the input width Lf may be set by the above equation (1). .

【００６５】・ 実施形態では、原料の投入幅Ｌｆをオ
ープンロール１１ａ，１１ｂの基端側から軸線方向へ沿
って延びる距離としたが、オープンロール１１ａ，１１
ｂの中央部等の任意の位置でのオープンロール１１ａ，
１１ｂの軸線方向へ沿って延びる距離としてもよい。そ
して、原料をオープンロール１１ａ，１１ｂの任意の位
置から供給してもよい。In the embodiment, the width Lf of the raw material is set to the distance extending in the axial direction from the base end side of the open rolls 11a, 11b.
open roll 11a at an arbitrary position such as the center of b,
The distance may extend along the axial direction of 11b. Then, the raw material may be supplied from any position of the open rolls 11a and 11b.

【００６６】さらに、前記実施形態より把握できる技術
的思想について以下に記載する。Further, the technical ideas that can be grasped from the above embodiment will be described below.

【００６７】・ 前記原料搬送供給装置にはオープンロ
ールの軸線方向に沿って延び、少なくとも結着樹脂及び
顔料よりなる原料を搬送する搬送路が設けられていると
ともに、その搬送路には同搬送路の基端側から先端側に
向かうに連れて幅広に延びる供給口が形成され、オープ
ンロールの供給側から排出側に向かうに連れて前記供給
口からの原料の供給量が多くなるように構成したことを
特徴とする請求項１〜請求項３のいずれか一項に記載の
トナー製造のための混練物の製造方法。このように構成
した場合、原料が溶融されにくいオープンロールの一端
供給側には原料の供給量が少なく、溶融が進む他端排出
側に向かうに連れて原料の供給量を多くすることができ
る。従って、原料を確実に溶融しながら混練物の溶融混
練を行うことができる。The raw material transport / supply device is provided with a transport path extending along the axial direction of the open roll and transporting at least a raw material composed of a binder resin and a pigment. A supply port extending from the base end side toward the tip end side is formed so that the supply amount of the raw material from the supply port increases from the supply side to the discharge side of the open roll. The method for producing a kneaded product for producing a toner according to any one of claims 1 to 3, characterized in that: With this configuration, the supply amount of the raw material is small at one end supply side of the open roll in which the raw material is not easily melted, and the supply amount of the raw material can be increased toward the other end discharge side where the melting proceeds. Therefore, the melt-kneading of the kneaded material can be performed while the raw material is reliably melted.

【００６８】・ 前記複数のオープンロールのうち相対
向するオープンロール間のギャップを０．１〜０．５ｍ
ｍに設定したことを特徴とする請求項１〜請求項３のい
ずれか一項に記載のトナー製造のための混練物の製造方
法。このように構成した場合、ギャップ間で溶融混練さ
れる混練物の量を確保して混練物の生産性の低下を防止
することができる。また、オープンロール間に供給され
た原料の落下量を少なくして混練物の生産性の低下を防
止することができるとともに、バンクを確実に形成して
混練物の溶融混練を確実に行うことができる。The gap between opposing open rolls of the plurality of open rolls is 0.1 to 0.5 m;
The method for producing a kneaded product for producing a toner according to any one of claims 1 to 3, wherein m is set to m. With this configuration, it is possible to secure the amount of the kneaded material that is melt-kneaded between the gaps and prevent the productivity of the kneaded material from lowering. In addition, it is possible to prevent the decrease in the productivity of the kneaded material by reducing the fall amount of the raw material supplied between the open rolls, and to reliably form the bank to reliably perform the melt-kneading of the kneaded material. it can.

【００６９】[0069]

【発明の効果】以上詳述したように、この発明によれ
ば、次のような効果を奏する。As described above in detail, according to the present invention, the following effects can be obtained.

【００７０】請求項１に記載の発明のトナー製造のため
の混練物の製造方法によれば、原料の供給条件に依存し
て原料の投入幅を設定することが可能となり、固まりの
発生を抑制して安定した混練ができ、原料が均一に分散
された混練物を製造することができるとともに、その混
練物を使用したトナーの性能の低下を防止することがで
きる。According to the method for producing a kneaded material for producing a toner according to the first aspect of the present invention, it is possible to set the width of the raw material to be supplied depending on the raw material supply conditions, thereby suppressing the occurrence of agglomeration. As a result, a kneaded material in which the raw materials are uniformly dispersed can be manufactured, and a decrease in the performance of the toner using the kneaded material can be prevented.

【００７１】請求項２に記載の発明のトナー製造のため
の混練物の製造方法によれば、請求項１に記載の発明の
効果に加えて、オープンロール間への原料の供給量が少
なくなるのを防止して混練物の生産性の低下を防止する
ことができる。また、原料が排出側へ移送されるまでの
間に圧縮力、せん断力が原料に作用する時間を長く取る
ことができ、顔料、添加物等を十分に微細化することが
できる。According to the method for producing a kneaded product for producing a toner according to the second aspect of the invention, in addition to the effect of the first aspect, the amount of the raw material supplied between the open rolls is reduced. And the productivity of the kneaded material can be prevented from lowering. In addition, it is possible to take a long time for the compressive force and the shear force to act on the raw material before the raw material is transferred to the discharge side, and it is possible to sufficiently reduce the size of pigments, additives, and the like.

【００７２】請求項３に記載の発明のトナー製造のため
の混練物の製造方法によれば、請求項１又は請求項２に
記載の発明の効果に加えて、原料を相対向するオープン
ロール間に効率良く供給して原料の浪費を少なくするこ
とができる。According to the method for producing a kneaded material for producing a toner according to the third aspect of the present invention, in addition to the effects of the first or second aspect of the present invention, the raw material is placed between the open rolls opposed to each other. And waste of raw materials can be reduced.

【図面の簡単な説明】[Brief description of the drawings]

【図１】実施形態の混練物の製造装置を模式的に示す概
略平面図。FIG. 1 is a schematic plan view schematically showing a kneaded material manufacturing apparatus according to an embodiment.

【図２】実施形態の混練物の製造装置を模式的に示す概
略部分斜視図。FIG. 2 is a schematic partial perspective view schematically showing a kneaded material manufacturing apparatus according to the embodiment.

【図３】実施形態の混練物の溶融混練状態を模式的に示
す概略正面図。FIG. 3 is a schematic front view schematically showing a melt-kneaded state of the kneaded material of the embodiment.

【図４】別例の混練物の製造装置を模式的に示す概略側
面図。FIG. 4 is a schematic side view schematically showing a kneaded material manufacturing apparatus of another example.

【符号の説明】[Explanation of symbols]

ｋ 定数 Ｌｏ オープンロールの軸線方向へ沿った長さ Ｌｆ 投入幅 Ｍ 原料の供給量 Ｔ 混練物の平均温度 Ｔｇ 結着樹脂のガラス転移温度 １０ トナー製造のための混練物の製造装置 １１ 溶融混練装置としてのオープンロール混練機 １１ａ，１１ｂ オープンロール １２ 原料搬送供給装置としてのスクリューフィーダー k constant Lo length of the open roll in the axial direction Lf feeding width M raw material supply amount T average temperature of the kneaded material Tg glass transition temperature of the binder resin 10 kneaded material manufacturing apparatus for toner production 11 melt kneading apparatus Roll kneader 11a, 11b open roll 12 Screw feeder as raw material transfer and supply device

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 少なくとも結着樹脂及び顔料よりなる原
料を搬送し、搬送された原料を次工程に供給する原料搬
送供給装置と、原料搬送供給装置から供給された原料を
複数のオープンロールの間に供給して当該オープンロー
ルからの加熱及び回転により原料を溶融混練して混練物
を製造するように構成した溶融混練装置とよりなる製造
装置を使用してトナー製造のための混練物を製造する方
法であって、 前記原料搬送供給装置からの原料のオープンロールへの
供給の際の同オープンロールの軸線方向に沿った原料の
投入幅をＬｆ（ｍｍ）、原料の供給量をＭ（ｋｇ／
ｈ）、オープンロール間で溶融混練される混練物の平均
温度をＴ（℃）、前記結着樹脂のガラス転移温度をＴｇ
（℃）、定数をｋとするとき、 Ｌｆ≧ｋ・Ｍ／（Ｔ−Ｔｇ） に示される関係となるように投入幅を設定したことを特
徴とするトナー製造のための混練物の製造方法。1. A raw material transport / supply device for transporting a raw material comprising at least a binder resin and a pigment and supplying the transported raw material to a next process, and a raw material supplied from the raw material transport / supply device between a plurality of open rolls. To produce a kneaded material for toner production by using a manufacturing apparatus comprising a melt-kneading device configured to melt-knead the raw materials by heating and rotation from the open roll to produce a kneaded material. In the method, when the raw material is supplied from the raw material transport / supply device to the open roll, the input width of the raw material along the axial direction of the open roll is Lf (mm), and the supply amount of the raw material is M (kg /
h), the average temperature of the kneaded material melt-kneaded between the open rolls is T (° C.), and the glass transition temperature of the binder resin is Tg.
(° C.) and the constant is k. The method for producing a kneaded material for producing a toner is characterized in that the charging width is set so as to satisfy the following relationship: Lf ≧ k · M / (T−Tg). . 【請求項２】 前記オープンロールの軸線方向へ沿った
長さをＬｏ（ｍｍ）としたとき、前記Ｌｆ（ｍｍ）を
０．０５〜０．５Ｌｏに設定したことを特徴とする請求
項１に記載のトナー製造のための混練物の製造方法。2. The method according to claim 1, wherein when the length of the open roll along the axial direction is Lo (mm), the Lf (mm) is set to 0.05 to 0.5 Lo. A method for producing a kneaded product for producing the toner described in the above. 【請求項３】 前記複数のオープンロールのうち相対向
するオープンロールの加熱温度に温度差を形成し、加熱
温度が高温側のオープンロールの上端から内側端まで
を、オープンロールの幅方向への原料の投入範囲に設定
したことを特徴とする請求項１又は請求項２に記載のト
ナー製造のための混練物の製造方法。3. A temperature difference is formed between the heating temperatures of the opposing open rolls of the plurality of open rolls, and the heating temperature extends from the upper end to the inner end of the open roll on the high temperature side in the width direction of the open roll. The method for producing a kneaded product for producing a toner according to claim 1, wherein the material is set within a charging range of the raw material.