JP2002224652A - Method for recycling waste household electrical appliance and article to be recycled - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a method for classifying and reusing the shredded dust of waste household electrical appliances while both good classification precision and low cost are realized. SOLUTION: Waste household electrical appliances are crushed, iron and a nonferrous metal are classified and recovered from the crushed appliances and two components of at least olefinic resins and styrenic resins are then classified and recovered from the shredded dust comprising contaminants such as resins and metal. The olefinic resins are formed into a regenerated resin by using a screw type extruder and the styrenic resins are reused as a styrene monomer by thermal decomposition or formed into another regenerated resin by using the screw type extruder.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、廃家電製品のリサ
イクル技術に関し、更に詳しくは、既存技術で再利用が
可能な鉄、非鉄金属、ガラス等に加えて、従来再利用が
困難とされてきた混合廃プラスチックのリサイクル技術
を提供することで、高いリサイクル率を実現可能な廃家
電製品のリサイクル方法に関する。[0001] The present invention relates to a technology for recycling used home appliances, and more particularly, it has been considered difficult to reuse in addition to iron, non-ferrous metal, glass, etc. which can be reused by existing technologies. The present invention relates to a method of recycling waste home appliances that can achieve a high recycling rate by providing a recycling technology of mixed waste plastic.

【０００２】[0002]

【従来の技術】我が国における廃棄物処理の問題は近年
ますます深刻化しつつあり、焼却時のダイオキシン発
生、埋立地の逼迫等が社会問題として大きくクローズア
ップされている。これら廃棄物の主要な発生源として
は、容器包装材、建材、自動車、家電等が挙げられ、特
に家庭から廃棄される使用済み家電製品の量は、冷蔵
庫、洗濯機、テレビ、エアコンのいわゆる「４家電」に
限定しても、１９９７年度で１８００万台、重量にして
６５万トンにも上っており（家電製品協会調べ）、その
処理は喫緊の課題となっている。2. Description of the Related Art The problem of waste disposal in Japan has become increasingly serious in recent years, and the generation of dioxin during incineration, the tightness of landfills, and the like have been greatly highlighted as social problems. The main sources of these wastes include container and packaging materials, building materials, automobiles, home appliances, and the like. Even if it is limited to "four home appliances", it has reached 18 million units and weighed 650,000 tons in 1997 (according to a survey by the Home Appliances Association), and its processing is an urgent issue.

【０００３】こうした背景を受けて、上記４家電を対象
として特定家庭用機器再商品化法、いわゆる「家電リサ
イクル法」が２００１年４月から施行されることとな
り、リサイクル率としては冷蔵庫５０％、洗濯機５０
％、テレビ５５％、エアコン６０％の目標が定められ、
またこれらリサイクル率にカウントすることができるの
は有価物として販売されたもののみで、リサイクル事業
者が処理費用を支払って処理を委託する、いわゆる「逆
有償品」は対象外とされることが規定されている。[0003] Against this background, the Law on the Recycling of Specific Home Appliances, the so-called "Household Appliance Recycling Law," was enacted in April 2001 for the above four home appliances. Washing machine 50
%, Television 55%, air conditioner 60%,
In addition, only products sold as valuables can be counted in these recycling rates, and so-called "reverse paid products" that recycling companies pay for processing costs and outsource the processing may be excluded. Stipulated.

【０００４】ここで廃家電製品の素材別構成比を見る
と、４家電の平均では、鉄４７％、非鉄金属７％、プラ
スチック２９％、ガラス９％、その他８％（家電製品協
会調べ）となっており、現時点で経済的に再利用が可能
な鉄、非鉄金属、ガラスを合計してもリサイクル率は６
３％に留まる。従って今後のリサイクル率目標値の引き
上げを考慮するとリサイクル率の向上は焦眉の急であ
り、これを実現するにはプラスチックの処理技術を確立
することが最大の課題となっている。Looking at the composition ratio of waste home appliances by material, the average of the four home appliances is 47% iron, 7% non-ferrous metal, 29% plastic, 9% glass, and 8% other (according to the Association of Home Appliances). At present, the recycling rate is 6 even if iron, non-ferrous metals, and glass, which can be economically reused, are combined.
Stays at 3%. Therefore, considering the future increase of the recycling rate target, the improvement of the recycling rate is urgently urgent, and establishing the processing technology for plastics is the biggest issue to achieve this.

【０００５】家電に使用されるプラスチックの構成比
は、ポリプロピレン３６％、ポリスチレン２８％、ＡＢ
Ｓ樹脂１７％、ポリウレタン５％、塩化ビニル樹脂４
％、その他１０％（家電製品協会調べ）である。不特定
多数の廃家電製品を破砕し鉄及び非鉄金属を分別回収し
た後、樹脂や金属等の混入物からなる破砕残渣（以下、
シュレッダーダストという）には、当然のことながら、
これら多様な樹脂の混合物が含有され、このことがプラ
スチックの有効な再利用を妨げる主原因となっている。[0005] The composition ratio of plastics used in home appliances is 36% polypropylene, 28% polystyrene, AB
S resin 17%, polyurethane 5%, vinyl chloride resin 4
% And other 10% (according to a survey by the Home Appliances Association). After crushing an unspecified large number of waste home appliances and separating and recovering iron and non-ferrous metals, crushed residues composed of contaminants such as resins and metals
Shredder dust), of course,
It contains a mixture of these various resins, which is a major factor preventing effective recycling of plastics.

【０００６】かかるプラスチック分別の問題点を解決す
る目的で、様々な分離・分別技術が提案されている。例
えば、比重分離（プラスチックスエージ、１９９７・
臨時増刊号、ｐ６７）、溶剤・溶解分離、静電分
離、選択的浮遊分離、スクリーンチェンジャー／メ
ルトフィルター（プラスチックスエージ、１９９８・臨
時増刊号、ｐ５１）などである。[0006] For the purpose of solving such a problem of plastic separation, various separation / separation techniques have been proposed. For example, specific gravity separation (Plastic Swage, 1997
Extra edition, p. 67), solvent / dissolution separation, electrostatic separation, selective floating separation, screen changer / melt filter (Plastic Swage, 1998 extra edition, p. 51).

【０００７】の比重分離は、液体や気体等の媒体中に
おけるプラスチックの比重差を利用して分別する技術で
あり、比重差の小さいものを分離することはできない。
しかし、水や塩水等の液体を使用する湿式の比重分離
は、廃棄プラスチックの洗浄も兼ねることができるの
で、単独や他の方式との組み合わせによるシステム化
等、幅広く活用されている。特に、シュレッダーダスト
を、より付加価値の高い製品に再生するために分離・分
別する方法として有効である。の溶剤・溶解分離は、
特定の溶剤に対する溶解度の差を、の静電分離は、プ
ラスチック粒子が摩擦により正又は負に帯電する性質
を、の選択的浮遊分離は、プラスチック表面の水ぬれ
性の差を利用してそれぞれ分別する技術であり、とは
異なり比重差の小さいものにも適用できる。のスクリ
ーンチェンジャーは、プラスチック相互を分別する技術
ではないが、押出機で溶融したプラスチックから金属等
の未溶融物を除去することができる。[0007] The specific gravity separation is a technique of separating using a specific gravity difference of a plastic in a medium such as a liquid or a gas, and cannot separate a plastic having a small specific gravity difference.
However, since wet specific gravity separation using a liquid such as water or salt water can also serve as washing of waste plastic, it is widely used, for example, as a system alone or in combination with another method. In particular, it is effective as a method for separating and separating shredder dust in order to regenerate it into a product with higher added value. Solvent and dissolution separation of
The electrostatic separation of the difference in solubility in a specific solvent, the property of plastic particles being positively or negatively charged due to friction, and the selective floating separation, using the difference in the wettability of the plastic surface, This technique is different from that of the first embodiment in that the difference in specific gravity is small. The screen changer is not a technique for separating plastics from each other, but can remove unmelted substances such as metals from plastics melted in an extruder.

【０００８】これらの分離・分別技術はそれぞれ一長一
短があるため、対象とするプラスチックに応じて複数方
式を組み合わせたシステムを構築するのが一般的であ
る。例えば、リサイクル率向上を実現するリサイクル技
術開発を目指して、家電製品協会が通産省の補助を受け
て建設した実証プラントにおいては、廃家電を一括粉砕
し、先ず風力選別機で冷蔵庫断熱材であるウレタン系樹
脂を、次いで磁力選別機で鉄、渦電流選別機で銅、アル
ミニウム等の非鉄金属をそれぞれ回収し、最後に残さで
あるシュレッダーダストを水流による比重選別（シンク
アンド フロート方式）によって、オレフィン系樹
脂、スチレン系樹脂、塩化ビニル系樹脂の３成分に分別
するシステムが提案され、１９９９年３月まで実証試験
が行われた（プラスチックスエージ、１９９７・臨時増
刊号、ｐ９８）。[0008] Each of these separation / separation techniques has advantages and disadvantages, and therefore, it is common to construct a system combining a plurality of methods according to the target plastic. For example, in a demonstration plant constructed with the assistance of the Ministry of International Trade and Industry, with the aim of developing a recycling technology that can improve the recycling rate, the Japan Home Appliances Association crushed waste home appliances at once, and first used a wind separator to remove urethane, a refrigerator insulation material. The resin is then recovered by a magnetic separator, and non-ferrous metals such as copper and aluminum are recovered by an eddy current separator. Finally, the remaining shredder dust is separated by gravitational water separation (sink-and-float method) to obtain an olefin-based resin. A system for separating into three components, a resin, a styrene resin, and a vinyl chloride resin, was proposed, and a verification test was conducted until March 1999 (Plastic Swage, 1997, extra edition, p98).

【０００９】しかしながら、上記のシステムにおいて
は、分別回収したオレフィン系樹脂にはスチレン系樹脂
が、スチレン系樹脂にはオレフィン系樹脂が多量に混入
するなどシュレッダーダストの分別精度が十分ではな
く、分別回収したウレタン系樹脂、オレフィン系樹脂、
スチレン系樹脂、塩化ビニル系樹脂のいずれについても
有効な再利用法が見出せていない。事実、上記の実証プ
ラントにおいても分別した樹脂の一部を熱分解油化し、
工場内ボイラーの燃料として再利用するに留まっていた
のが現状である。[0009] However, in the above system, the separation accuracy of the shredder dust is not sufficient, for example, a large amount of styrene resin is mixed in the olefin resin and the styrene resin is mixed in a large amount. Urethane resin, olefin resin,
No effective recycling method has been found for any of the styrene resins and the vinyl chloride resins. In fact, even in the above demonstration plant, part of the separated resin was pyrolyzed to oil,
At present, it has only been reused as fuel for boilers in factories.

【００１０】一方、シュレッダーダストを効率良く再利
用する方法として、これを製鉄業において高炉の還元剤
として再利用する方法や、同じく製鉄業においてコーク
ス炉の原料として再利用する方法や、シュレッダーダス
トを熱分解ガス化して一酸化炭素、水素を生成させ、こ
れをメタノール、酢酸、アンモニア等の合成原料として
再利用する方法等が提案されており（ＪＣＩＩ ＮＥＷ
Ｓ、第４９号、ＶＯＬ１３ Ｎｏ．３、１９９９年１０
月）、これらケミカルリサイクル方法は広義のマテリア
ルリサイクル技術として注目を集めている。On the other hand, as a method for efficiently recycling shredder dust, a method for reusing the same as a reducing agent for a blast furnace in the steelmaking industry, a method for reusing it as a raw material for a coke oven in the steelmaking industry, and a method for recycling shredder dust. A method has been proposed in which carbon monoxide and hydrogen are generated by pyrolysis gasification and reused as a synthesis raw material such as methanol, acetic acid, and ammonia (JCII NEW).
S, No. 49, VOL13 No. 3, 1999 10
Mon), these chemical recycling methods are attracting attention as material recycling technology in a broad sense.

【００１１】上記のように、廃家電製品リサイクルにお
ける最大の問題点は、シュレッダーダストの再利用方法
が現時点で見出せないことにある。シュレッダーダスト
を分別しないでケミカルリサイクルする方法はあるが、
再生品としての付加価値が低いため逆有償処理にならざ
るを得ない。また、マテリアルリサイクルが可能な状態
にまで分別すれば再生品としての付加価値が高まること
から有価物として処理できる可能性があるが、分別精度
とコストを両立するプロセスを見出せるかどうかが課題
となっている。[0011] As described above, the biggest problem in the recycling of waste home electric appliances is that a recycling method of shredder dust cannot be found at present. There is a chemical recycling method without separating shredder dust,
Since the added value as a recycled product is low, it is inevitably a reverse paid process. In addition, if the material is separated to a state where it can be recycled, the added value as a recycled product increases, so it may be possible to treat it as a valuable resource.However, it is an issue whether a process that can balance separation accuracy and cost can be found. ing.

【００１２】[0012]

【発明が解決しようとする課題】したがって、本発明の
目的は、分別精度とコストを両立するシュレッダーダス
トの分別方法を提供することにあり、それによって、マ
テリアルリサイクルが可能な廃家電製品リサイクル方法
を提供することにある。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a method for separating shredder dust, which achieves both separation accuracy and cost. To provide.

【００１３】[0013]

【課題を解決するための手段】そこで、本発明者らは、
廃家電製品リサイクル技術における課題の解決を図るた
め、シュレッダーダストを構成する各種樹脂成分を如何
に再利用可能な状態で分離・分別するかという課題につ
いて鋭意検討した結果、手選別、風力選別、磁力選別、
渦電流選別、比重選別等の選別手段を巧みに組み合わせ
ることで、プラスチックを複数の成分に分別し、それぞ
れの成分に最適な再生技術を開発且つ適用することで、
従来技術では到達不可能なリサイクル率を実現し、本発
明を完成した。Means for Solving the Problems Accordingly, the present inventors have:
In order to solve the issues in the recycling technology of waste home appliances, we conducted intensive studies on how to separate and separate the various resin components that constitute shredder dust in a reusable state. Sorting,
By skillfully combining sorting means such as eddy current sorting and specific gravity sorting, plastics are separated into multiple components, and by developing and applying the optimal regeneration technology for each component,
The present invention has been achieved by achieving a recycling rate that cannot be achieved by the conventional technology.

【００１４】すなわち、請求項１に係る発明は、不特定
多数の廃家電製品を破砕して鉄及び非鉄金属を分別回収
した後の樹脂や金属等の混入物からなるシュレッダーダ
ストから、少なくともオレフィン系樹脂とスチレン系樹
脂の２成分を分別回収し、オレフィン系樹脂については
スクリュー式押出機を用いて混練造粒することで再生樹
脂化し、スチレン系樹脂については熱分解して油を生成
させ、この生成油を蒸留して得られるスチレンモノマー
を化学原料として再利用することを特徴とする廃家電製
品のリサイクル方法である。[0014] That is, the invention according to claim 1 provides at least an olefin-based shredder dust composed of contaminants such as resin and metal after crushing an unspecified large number of waste home appliances and separating and recovering iron and non-ferrous metals. The resin and the styrene resin are separated and recovered, and the olefin resin is converted into a regenerated resin by kneading and granulating using a screw-type extruder, and the styrene resin is thermally decomposed to generate oil. This is a method for recycling waste home appliances, wherein a styrene monomer obtained by distilling a produced oil is reused as a chemical raw material.

【００１５】請求項２に係わる発明は、不特定多数の廃
家電製品を破砕して鉄及び非鉄金属を分別回収した後の
樹脂や金属等の混入物からなるシュレッダーダストか
ら、少なくともオレフィン系樹脂とスチレン系樹脂の２
成分を分別回収し、オレフィン系樹脂及びスチレン系樹
脂をそれぞれスクリュー式押出機を用いて混練造粒する
ことで再生樹脂化することを特徴とする廃家電製品のリ
サイクル方法である。[0015] The invention according to claim 2 is to provide an at least olefin-based resin from shredder dust composed of contaminants such as resin and metal after crushing an unspecified large number of waste home appliances and separating and recovering iron and non-ferrous metals. Styrene resin 2
A recycling method for waste home appliances, wherein components are separated and collected, and an olefin-based resin and a styrene-based resin are kneaded and granulated by using a screw-type extruder to form a regenerated resin.

【００１６】請求項３に係わる発明は、廃家電製品の少
なくとも一部が冷蔵庫であって、それらの製品から鉄及
び非鉄金属を分別回収した後のシュレッダーダストか
ら、少なくともウレタン系樹脂、オレフィン系樹脂及び
スチレン系樹脂の３成分を分別回収し、ウレタン系樹脂
については熱分解して炭化物、各種留出油及びガスを生
成させ、これらを燃料又は化学原料として再利用する請
求項１又は２記載の廃家電製品のリサイクル方法であ
る。According to a third aspect of the present invention, at least a part of a waste household electric appliance is a refrigerator, and at least a urethane-based resin and an olefin-based resin are obtained from shredder dust after separating and recovering iron and non-ferrous metals from those products. 3. The method according to claim 1 or 2, wherein the three components of styrene-based resin and styrene-based resin are separated and recovered, and the urethane-based resin is thermally decomposed to generate carbides, various distillate oils and gases, and these are reused as fuels or chemical raw materials. It is a method of recycling waste home appliances.

【００１７】請求項４に係わる発明は、廃家電製品を破
砕する前に予め樹脂製部品の一部を分離回収し、スクリ
ュー式押出機を用いて混練造粒することで再生樹脂化す
る請求項１〜３のいずれかに記載の廃家電製品のリサイ
クル方法である。なお、この分離回収した樹脂製部品
は、樹脂種毎に再生樹脂化してもよいし、樹脂種毎に上
記のシュレッダーダストから分別回収した樹脂と混合し
た後、再生樹脂化してもよい。According to a fourth aspect of the present invention, a part of a resin component is separated and recovered in advance before crushing a waste home appliance, and is kneaded and granulated by using a screw type extruder to be converted into a regenerated resin. It is a recycling method of the waste electric home appliances described in any one of 1 to 3. The separated and recovered resin part may be converted into a recycled resin for each resin type, or may be mixed with the resin separated and recovered from the shredder dust for each resin type and then converted to a recycled resin.

【００１８】請求項５に係わる発明は、廃家電製品の少
なくとも一部が、テレビ、パソコン、複写機等の難燃樹
脂製部品を用いた製品であって、廃家電製品を破砕する
前に予め分離回収される樹脂製部品の少なくとも一部が
当該難燃樹脂製部品である請求項４記載の廃家電製品の
リサイクル方法である。According to a fifth aspect of the present invention, at least a part of the waste home appliances is a product using a flame-retardant resin part such as a television, a personal computer, a copying machine, etc. The method according to claim 4, wherein at least a part of the resin parts separated and recovered is the flame-retardant resin parts.

【００１９】請求項６に係わる発明は、廃家電製品を破
砕した後、磁力選別機を用いて鉄を、渦電流選別機を用
いて非鉄金属をそれぞれ分別回収する請求項１〜５のい
ずれかに記載の廃家電製品のリサイクル方法である。[0019] The invention according to claim 6 is the method according to any one of claims 1 to 5, wherein after the waste home appliances are crushed, iron is separated using a magnetic separator and non-ferrous metal is separated using an eddy current separator. The recycling method of waste home electric appliances described in (1).

【００２０】請求項７に係わる発明は、シュレッダーダ
ストから発泡ウレタン樹脂を分別回収する際、風力選別
機を用いる請求項３〜６のいずれかに記載の廃家電製品
のリサイクル方法である。[0020] The invention according to claim 7 is the method for recycling waste household electrical appliances according to any one of claims 3 to 6, wherein when separating and recovering the urethane foam resin from the shredder dust, a wind separator is used.

【００２１】請求項８に係わる発明は、分別回収された
発泡ウレタン樹脂から、当該樹脂を製造する際に使用さ
れたフロンを除去する請求項７記載の廃家電製品のリサ
イクル方法である。[0021] The invention according to claim 8 is the method for recycling waste electrical home appliances according to claim 7, wherein fluorocarbon used in producing the resin is removed from the separated and recovered urethane foam resin.

【００２２】請求項９に係わる発明は、シュレッダーダ
ストからオレフィン系樹脂とスチレン系樹脂を分別回収
する際、該シュレッダーダストを平均粒子径２０mmφ以
下まで粉砕した後、先ず液体１を用いて主としてオレフ
ィン系樹脂とスチレン系樹脂を浮上させ、浮上しない塩
化ビニル系樹脂等のその他の樹脂や金属等の混入物から
分別し、更に浮上した樹脂混合物を上記と比重の異なる
液体２を用いて主としてオレフィン系樹脂を浮上させ、
浮上しないスチレン系樹脂とに分別する請求項１〜８の
いずれかに記載の廃家電製品のリサイクル方法である。According to a ninth aspect of the present invention, when the olefin-based resin and the styrene-based resin are separated and recovered from the shredder dust, the shredder dust is pulverized to an average particle diameter of 20 mmφ or less, and then the olefin-based resin and The resin and the styrene resin are levitated, separated from other resins such as vinyl chloride resin that do not float, and contaminants such as metals, and the levitated resin mixture is mainly separated from the olefin resin by using a liquid 2 having a specific gravity different from the above. Surfaced,
The recycling method of waste home electric appliances according to any one of claims 1 to 8, wherein the method is separated into non-floating styrene resins.

【００２３】請求項１０に係わる発明は、液体１が比重
１．０を超えて１．３未満に調整された無機塩類の水溶
液であり、且つ液体２が比重１．０の水である請求項９
記載の廃家電製品のリサイクル方法である。According to a tenth aspect of the present invention, the liquid 1 is an aqueous solution of an inorganic salt adjusted to have a specific gravity of more than 1.0 and less than 1.3, and the liquid 2 is water having a specific gravity of 1.0. 9
It is a recycling method of the waste home appliances described in the description.

【００２４】請求項１１に係わる発明は、不特定多数の
廃家電製品をリサイクルする際に、先ずテレビやパソコ
ンモニター等のブラウン管ガラスと冷蔵庫やエアコン等
の冷媒フロン及び樹脂製部品の一部を分離回収し、次に
残された製品を破砕した後、風力選別機を用いて発泡ウ
レタン樹脂を、磁力選別機を用いて鉄を、渦電流選別機
を用いて非鉄金属をそれぞれ分別回収し、残さであるシ
ュレッダーダストを平均粒子径２０mmφ以下まで粉砕し
た後、先ず液体１を用いて主としてオレフィン系樹脂と
スチレン系樹脂を浮上させ、浮上しない塩化ビニル系樹
脂やその他の樹脂や金属等の混入物から分別し、更にこ
の浮上した樹脂混合物を上記と比重の異なる液体２を用
いて浮上するオレフィン系樹脂と浮上しないスチレン系
樹脂の２成分に分別し、分別された樹脂又は樹脂製部品
については請求項１〜４記載の方法で再生樹脂化するこ
とを特徴とする廃家電製品のリサイクル方法である。According to the eleventh aspect of the present invention, when recycling an unspecified large number of waste home appliances, first, a CRT glass such as a television and a personal computer monitor is separated from a refrigerant Freon and a part of resin parts such as a refrigerator and an air conditioner. After collecting and then crushing the remaining product, urethane foam resin is separated using a wind separator, iron is separated using a magnetic separator, and non-ferrous metal is separated and collected using an eddy current separator. After shredding the shredder dust to an average particle diameter of 20 mmφ or less, first use the liquid 1 to float mainly the olefin resin and the styrene resin, and remove the non-floating vinyl chloride resin and other contaminants such as resin and metal. The resin mixture thus floated is further separated into two components, an olefin resin that floats and a styrene resin that does not float, using a liquid 2 having a specific gravity different from that described above. A method for recycling waste household electrical appliances, characterized in that the separated resin or resin parts are converted into recycled resin by the method according to claims 1 to 4.

【００２５】請求項１２に係わる発明は、請求項１〜１
１のいずれかにおいて分別回収されたオレフィン系樹脂
をスクリュー式押出機に供給し、ＡＳＴＭ式標準ふるい
でNo.２０以上（篩目の開き０．８４mm以下）のスクリ
ーンメッシュフィルターによって金属異物等の固形異物
を除去しながら混練造粒することを特徴とするオレフィ
ン系樹脂組成物よりなるリサイクル製品である。The twelfth aspect of the present invention relates to the first to first aspects.
The olefin-based resin separated and recovered in any one of 1) is supplied to a screw-type extruder, and solids such as metal foreign matter are passed through a screen mesh filter of No. 20 or more (with a sieve opening of 0.84 mm or less) with an ASTM standard sieve. A recycled product comprising an olefin-based resin composition characterized by kneading and granulating while removing foreign matter.

【００２６】請求項１３に係わる発明は、請求項２〜１
１のいずれかにおいて分別回収されたスチレン系樹脂を
スクリュー式押出機に供給し、ＡＳＴＭ式標準ふるいで
No.２０以上（篩目の開き０．８４mm以下）のスクリー
ンメッシュフィルターによって金属異物等の固形異物を
除去しながら混練造粒することを特徴とするスチレン系
樹脂組成物よりなるリサイクル製品である。The invention according to claim 13 is the invention according to claims 2-1.
The styrene-based resin separated and recovered in any one of 1) is supplied to a screw-type extruder, and passed through an ASTM standard sieve.
A recycled product comprising a styrene-based resin composition characterized by kneading and granulating while removing solid foreign substances such as metal foreign substances using a screen mesh filter of No. 20 or more (a sieve opening of 0.84 mm or less).

【００２７】請求項１４に係わる発明は、請求項１又は
３〜１１のいずれかにおいて分別回収されたスチレン系
樹脂を熱分解し、得られた生成油を蒸留してスチレンモ
ノマーを得るプロセスにおいて、収率が８０％以上であ
って、且つスチレンモノマー濃度が５０％以上である熱
分解生成油を蒸留して純度９９％以上のスチレンモノマ
ーとしたことを特徴とするリサイクル製品としての純度
９９％以上のスチレンモノマーである。According to a fourteenth aspect of the present invention, there is provided a process for thermally decomposing the styrene-based resin separated and recovered in any one of the first to third aspects and distilling the resulting oil to obtain a styrene monomer. Purity 99% or more as a recycled product, wherein a pyrolysis oil having a yield of 80% or more and a styrene monomer concentration of 50% or more is distilled to give a styrene monomer having a purity of 99% or more. Is a styrene monomer.

【００２８】請求項１５に係わる発明は、請求項３〜１
１記載のいずれかの方法によって分別回収されたウレタ
ン樹脂を熱分解して得られる炭化物、各種留出油又はガ
スよりなるリサイクル製品である。The invention according to claim 15 is the invention according to claims 3-1.
A recycled product comprising a carbide, various distillate oils or gases obtained by pyrolyzing a urethane resin separated and recovered by any one of the methods described in 1.

【００２９】請求項１６に係わる発明は、請求項９〜１
１記載のいずれかの方法においてシュレッダーダストか
らオレフィン系樹脂とスチレン系樹脂を分別回収した
後、残さである塩化ビニル系樹脂等のその他の樹脂や金
属等の混入物をスクリュー式押出機に供給し、塩化ビニ
ル系樹脂に含まれる塩素を熱分解により塩化水素として
回収し、残さを必要により加えられる非塩素系の他の樹
脂と共に混練造粒することを特徴とする固形プラスチッ
ク燃料として使用可能な樹脂組成物よりなるリサイクル
製品である。The invention according to claim 16 is the invention according to claims 9-1.
After separating and recovering the olefin-based resin and the styrene-based resin from the shredder dust by any of the methods described in 1, the remaining contaminants such as other resins such as vinyl chloride-based resins and metals are supplied to a screw type extruder. Resin usable as solid plastic fuel characterized by recovering chlorine contained in vinyl chloride resin as hydrogen chloride by thermal decomposition and kneading and granulating the residue with other non-chlorine resin added as necessary It is a recycled product comprising the composition.

【００３０】以下、本発明を具体的に説明する。本発明
でいう不特定多数の廃家電製品とは、いわゆる「家電リ
サイクル法」の規制対象となる冷蔵庫、洗濯機、テレ
ビ、エアコンの４種に限定されるものではなく、パソコ
ン、プリンター、複写機、電話機、ファックス機、ビデ
オテープレコーダー、オーディオ機器、衣類乾燥機、電
気掃除機、扇風機、電子レンジ、電気炊飯器、電気カー
ペット、ヘアードライヤーなどあらゆる種類の家電製品
が含まれる。Hereinafter, the present invention will be described specifically. The unspecified large number of waste home appliances referred to in the present invention are not limited to four types of refrigerators, washing machines, televisions, and air conditioners that are subject to the so-called "Home Appliance Recycling Law", and include personal computers, printers, and copiers. Includes all kinds of home appliances such as telephones, fax machines, video tape recorders, audio equipment, clothes dryers, vacuum cleaners, electric fans, microwave ovens, electric rice cookers, electric carpets, hair dryers, etc.

【００３１】本発明においては、これらの不特定多数の
廃家電製品を一括破砕する前に、環境への影響を考慮
し、必要に応じて特定の部品や物質を手作業で分離回収
することができる。かかる部品や物質としては、鉛入り
ガラス回収を目的とするテレビやパソコンモニター等の
ブラウン管、難燃樹脂回収を目的とするテレビ、パソコ
ン、複写機等の筐体、及び冷蔵庫やエアコンの冷媒フロ
ン等を例示することができる。In the present invention, before crushing these unspecified and large number of waste home appliances at once, it is possible to manually separate and collect specific parts and substances as necessary in consideration of the effect on the environment. it can. Examples of such parts and substances include cathode ray tubes such as televisions and personal computer monitors for collecting lead-containing glass, televisions, personal computers, copiers and the like for collecting flame-retardant resins, and refrigerants for refrigerators and air conditioners. Can be exemplified.

【００３２】また、より純度の高い再生プラスチックを
得る目的で、手作業で容易に分解が可能な部品を回収
し、粉砕した後スクリュー式押出機を用いて混練造粒す
ることで再生樹脂化することも可能であり、本発明に属
する。For the purpose of obtaining a higher-purity recycled plastic, parts that can be easily decomposed are collected manually, pulverized, and then kneaded and granulated using a screw-type extruder to form a recycled resin. It is also possible and belongs to the invention.

【００３３】特定部品を分離回収した後、残りの廃家電
製品は一括破砕する。その破砕方法については、特に制
限されるものではなく、例えば常温切断・破砕、冷凍切
断・破砕、せん断破砕等の手段で破砕されたものでよ
く、その形状についても、不定形状、カレット形状、細
長形状、粒子形状などいかなる形状のものでもよい。After the specific parts are separated and collected, the remaining waste home appliances are crushed at once. The crushing method is not particularly limited, for example, may be crushed by means such as room temperature cutting and crushing, frozen cutting and crushing, shear crushing and the like, and its shape is also irregular, cullet-shaped, and elongated. Any shape such as shape and particle shape may be used.

【００３４】破砕粒子の平均粒子径の上限は、金属異物
除去の観点から５０mm以下、好ましくは４０mm以下であ
る。平均粒子径が５０mmを超えると、金属部品とプラス
チック部品の分離が不十分となり、分別精度が低下する
ので好ましくない。また、その下限は、破砕処理速度の
観点から２０mm以上、好ましくは３０mm以上である。平
均粒子径が２０mm未満の大きさまで破砕しようとする
と、破砕装置として必要以上に大きな能力の設備が必要
となり設備コストが上昇すること、また破砕作業に長時
間を要することからランニングコストが上昇すること等
の点から好ましくない。The upper limit of the average particle size of the crushed particles is 50 mm or less, preferably 40 mm or less, from the viewpoint of removing metallic foreign matter. If the average particle diameter exceeds 50 mm, separation of metal parts and plastic parts becomes insufficient, and the separation accuracy is undesirably reduced. The lower limit is at least 20 mm, preferably at least 30 mm, from the viewpoint of the crushing speed. Attempting to crush to an average particle size of less than 20 mm requires equipment with an unnecessarily large capacity as a crushing device, increasing equipment costs, and increasing the running cost due to the long time required for crushing work. It is not preferable from the point of view.

【００３５】次いで、上記の破砕粒子から、風力選別機
を用いて、低比重物、主に冷蔵庫の断熱材を発生源とす
る発泡ウレタン系樹脂を分別する。かかる目的で使用さ
れる風力選別機の機種、構造等は特に制限されるもので
はなく、汎用の装置がそのまま使用できる。Next, from the above-mentioned crushed particles, a low specific gravity material, mainly a urethane foam resin mainly made of a heat insulating material of a refrigerator, is separated using a wind separator. The model, structure, etc. of the wind separator used for this purpose are not particularly limited, and a general-purpose device can be used as it is.

【００３６】ウレタン系樹脂を分別した後の破砕混合物
の中には鉄、銅、アルミニウム等の金属が混入している
ため、磁力選別機により鉄を、渦電流選別機により銅、
アルミニウム等の非鉄金属を除去することが好ましく、
かかる目的で使用される磁力選別機や渦電流選別機の機
種、構造等は特に制限されるものではなく、汎用の装置
がそのまま使用できる。Since metals such as iron, copper, and aluminum are mixed in the crushed mixture after the urethane resin is separated, iron is separated by a magnetic separator, and copper and eddy current is separated by an eddy current separator.
It is preferable to remove non-ferrous metals such as aluminum,
The type and structure of the magnetic separator and eddy current separator used for this purpose are not particularly limited, and general-purpose devices can be used as they are.

【００３７】こうして得られたシュレッダーダストは、
少量のウレタン系樹脂を含む樹脂、磁力選別機や渦電流
選別機で除去しきれなかった金属やその他様々な材料の
混合物となっており、これらを全てリサイクルするのは
困難であった。本発明においては、このシュレッダーダ
ストを比重選別機によって分別することで、新たな再生
用途を見出し、リサイクル率の向上を実現した。The shredder dust thus obtained is
It is a resin containing a small amount of urethane resin, a mixture of metals and other various materials that could not be removed by a magnetic separator or an eddy current separator, and it was difficult to recycle all of them. In the present invention, this shredder dust is separated by a specific gravity sorter, thereby finding a new use for recycling and realizing an improvement in the recycling rate.

【００３８】まず、上記のシュレッダーダストを比重選
別の精度を高める目的で２次粉砕する。この粉砕方法に
ついては、特に制限されるものではなく、例えば、常温
切断・破砕、冷凍切断・破砕、せん断破砕等の手段で粉
砕されたものでよく、その形状についても、不定形状、
カレット形状、細長形状、粒子形状等、いかなる形状の
ものでもよいが、その後の単軸押出機や２軸押出機にお
ける混練作業性の面から、望ましくはカレット形状や粒
子形状がよい。First, the above shredder dust is secondarily pulverized for the purpose of increasing the accuracy of specific gravity selection. This pulverization method is not particularly limited, for example, room temperature cutting and crushing, frozen cutting and crushing, may be crushed by means such as shearing crushing, the shape may be an irregular shape,
Any shape such as a cullet shape, an elongated shape, and a particle shape may be used, but from the viewpoint of kneading workability in a single screw extruder or a twin screw extruder thereafter, a cullet shape or a particle shape is preferable.

【００３９】粉砕粒子の平均粒子径の上限は、比重分離
における分別精度の観点から、２０mm以下、好ましくは
１０mm以下である。平均粒子径が２０mmを超えると、異
種材料で構成されたプラスチック部品の場合、材料の分
離が不十分となり、比重分離の分別精度が低下するので
好ましくない。その下限は、特に制限されるものではな
いが、粉砕処理に関るコスト低減の観点から、１mm以
上、好ましくは５mm以上である。平均粒子径が１mm未満
の大きさまで粉砕しようとすると、粉砕装置として必要
以上に大きな能力の設備が必要となり設備コストが上昇
すること、また粉砕作業に長時間を要することからラン
ニングコストが上昇すること等の点から好ましくない。The upper limit of the average particle size of the pulverized particles is 20 mm or less, preferably 10 mm or less from the viewpoint of the separation accuracy in specific gravity separation. If the average particle diameter exceeds 20 mm, in the case of plastic parts composed of different materials, the separation of the materials becomes insufficient, and the separation accuracy of the specific gravity separation is undesirably reduced. Although the lower limit is not particularly limited, it is 1 mm or more, preferably 5 mm or more, from the viewpoint of cost reduction relating to the pulverization treatment. If the average particle diameter is to be crushed to a size of less than 1 mm, crushing equipment requires equipment with a larger capacity than necessary and equipment costs will increase, and running costs will increase due to the long time required for crushing work. It is not preferable from the point of view.

【００４０】２次粉砕されたシュレッダーダストは、比
重の異なる２種類の液体を用いて２段階で分別を行う。
まず比重が約１．０を超えて１．３未満に調整された液
体１を用いて、塩化ビニル系樹脂と磁力選別機や渦電流
選別機で除去しきれなかった金属を主体に構成される重
量成分と、オレフィン系樹脂とスチレン系樹脂を主体に
構成されるその他の成分とに比重分別する。次に、その
他の成分を比重が約１．０に調整された液体２を用い
て、オレフィン系樹脂を主体に構成される軽量成分とス
チレン系樹脂を主体に構成される中量成分とに比重分別
する。ここで、液体１及び２は、上記の比重分別を可能
とする比重を有するものであり、且つ分別されるプラス
チック類を化学的に変質させるような性質のものでない
限りは、どのような液体を用いてもよいが、経済性の観
点から、液体１は水にソーダ灰（炭酸ナトリウム）等の
無機塩類を溶解し前記比重範囲に調整したものが、液体
２は水がそれぞれ好適に用いられる。The secondary pulverized shredder dust is separated in two stages using two kinds of liquids having different specific gravities.
First, the liquid 1 whose specific gravity is adjusted to be more than about 1.0 and less than 1.3 is mainly composed of a vinyl chloride resin and a metal that cannot be completely removed by a magnetic force sorter or an eddy current sorter. The specific gravity is separated into a weight component and other components mainly composed of an olefin resin and a styrene resin. Next, using the liquid 2 whose specific gravity is adjusted to about 1.0, the other components are used to separate the specific gravity of the light component mainly composed of the olefin resin and the medium component mainly composed of the styrene resin. Separate. Here, as long as the liquids 1 and 2 have a specific gravity capable of separating the above specific gravity, and do not have a property of chemically changing the plastics to be separated, any liquid can be used. Although liquid 1 may be used, from the viewpoint of economy, liquid 1 is prepared by dissolving inorganic salts such as soda ash (sodium carbonate) in water and adjusted to the above specific gravity range, but water is preferably used as liquid 2.

【００４１】２次粉砕されたシュレッダーダストの分別
精度は、再生プラスチックの物性維持の観点から高けれ
ば高いほどよく、各成分に対する他成分の混入率は、１
０％以下、好ましくは５％以下、より好ましくは１％以
下である。The separation accuracy of the secondary pulverized shredder dust is preferably as high as possible from the viewpoint of maintaining the physical properties of the recycled plastic.
0% or less, preferably 5% or less, more preferably 1% or less.

【００４２】かかる目的で使用される比重選別機の機
種、構造等は、上記の分別精度を実現できるものであれ
ば特に制限されるものではなく、汎用の装置がそのまま
使用できる。但し、高精度の分別が可能であること、汚
れの激しい材料の洗浄も可能であること等の点から、水
又は水溶液を使用した湿式の比重選別機が好適に用いら
れる。The model, structure, and the like of the specific gravity separator used for this purpose are not particularly limited as long as the above-described separation accuracy can be realized, and a general-purpose device can be used as it is. However, a wet specific gravity sorter using water or an aqueous solution is preferably used in terms of being capable of high-precision separation and of being able to wash highly dirty materials.

【００４３】これまで述べてきた分別方法によって、廃
家電製品を構成するプラスチック類は、破砕前回収樹
脂、ウレタン系樹脂、塩化ビニル系樹脂、スチレ
ン系樹脂、オレフィン系樹脂の５成分に分別すること
が可能である。以下、それぞれの成分についての再生、
再商品化方法について詳しく説明する。According to the separation method described above, the plastics constituting the waste electric home appliances should be separated into five components, that is, a recovered resin before crushing, a urethane resin, a vinyl chloride resin, a styrene resin, and an olefin resin. Is possible. Hereinafter, regeneration of each component,
The re-commercialization method will be described in detail.

【００４４】一括破砕する前に手作業等によって分離回
収された樹脂製部品は、樹脂の種類毎に分別し、それぞ
れ粉砕した後必要に応じて水洗浄などにより汚れを除去
し、スクリュー式押出機を用いて混練造粒し、再生樹脂
として再利用する。かかる目的で使用されるスクリュー
式押出機の機種、構造等は特に制限されるものではな
く、汎用の単軸又は二軸押出機が好適に用いられる。な
お、この樹脂製部品が複数の樹脂からなる場合や樹脂種
が不明な場合は、２次粉砕に供し、比重分別などを行う
こともできる。The resin parts separated and recovered by manual work or the like before the crushing at a time are separated for each type of resin, and after each pulverization, if necessary, dirt is removed by washing with water or the like. And kneaded and granulated for reuse as recycled resin. The type and structure of the screw type extruder used for this purpose are not particularly limited, and a general-purpose single-screw or twin-screw extruder is preferably used. When the resin component is made of a plurality of resins or when the type of the resin is unknown, it can be subjected to secondary pulverization to perform specific gravity separation and the like.

【００４５】本発明においては、不特定多数の廃家電製
品中の樹脂成分を上記のようにして分別回収する。分別
回収される樹脂は、ウレタン系樹脂、塩化ビニル系樹
脂、スチレン系樹脂及びオレフィン系樹脂に大別され
る。少量含まれる樹脂は、まとまれば別途分別すること
が有利であるが、微量であれば多くの場合許容限度内で
上記樹脂に混入するか、最終廃棄物中に混入して燃料と
なったり、焼却などする。In the present invention, resin components in an unspecified number of waste home appliances are separated and recovered as described above. Resin to be separated and recovered is roughly classified into urethane resin, vinyl chloride resin, styrene resin and olefin resin. It is advantageous to separate the resin contained in a small amount separately when it is collected.However, if the amount is small, it is often mixed with the above resin within the allowable limit, or mixed into the final waste to become fuel or incinerated. And so on.

【００４６】分別回収される樹脂の内、熱可塑性樹脂で
ある塩化ビニル系樹脂、スチレン系樹脂及びオレフィン
系樹脂は、造粒して再生樹脂として使用することが可能
であるが、スチレン系樹脂は、再生樹脂とする他に、熱
分解してスチレンモノマー含有油とし、蒸留精製してポ
リスチレン製造グレードのスチレンモノマーに再生する
ことができる。Among the separated and recovered resins, thermoplastic resins such as vinyl chloride resin, styrene resin and olefin resin can be granulated and used as a regenerated resin. In addition to a regenerated resin, it can be thermally decomposed into a styrene monomer-containing oil and purified by distillation to regenerate polystyrene production grade styrene monomer.

【００４７】塩化ビニル系樹脂は熱分解して、塩素又は
塩化水素を含むガスと油分と固体とにし、脱塩素又は脱
塩化水素処理したガス及び油分は燃料又は化学原料にす
ると共に、固体分は必要により他の樹脂を加えて混練造
粒して再生樹脂とすることが有利である。The vinyl chloride resin is thermally decomposed into a gas containing chlorine or hydrogen chloride, an oil, and a solid, and the dechlorinated or dehydrochlorinated gas and the oil are converted into a fuel or a chemical raw material. It is advantageous to knead and granulate by adding other resins as necessary to obtain a regenerated resin.

【００４８】ウレタン系樹脂は熱分解して、ガスと油分
と炭化物を生成させ、これらを燃料又は化学原料にする
ことが有利である。It is advantageous that the urethane resin is thermally decomposed to generate gas, oil, and carbide, which are used as a fuel or a chemical raw material.

【００４９】一方、オレフィン系樹脂は、スクリュー式
押出機を用いて混練造粒して再生樹脂とする。以下、混
練造粒して再生樹脂とする方法について説明する。On the other hand, the olefin resin is kneaded and granulated by using a screw type extruder to obtain a regenerated resin. Hereinafter, a method of kneading and granulating a recycled resin will be described.

【００５０】廃家電製品を粉砕した後、磁力選別、渦電
流選別、比重選別の各工程を経て回収された比重１以下
の粉砕粒子を「使用済みポリオレフィン樹脂粉砕品」と
呼称する。使用済みポリオレフィン樹脂粉砕品は、その
選別工程において金属異物の混入率が２％未満まで低減
されていることが好ましい。金属異物の混入率が２％以
上であると、押出機による混練造粒工程において金属異
物に起因する閉塞が多発し、効率のよい運転が不可能と
なるからである。[0050] The crushed particles having a specific gravity of 1 or less, which are collected through the respective steps of magnetic force sorting, eddy current sorting and specific gravity sorting after crushing the waste home appliances, are referred to as "used polyolefin resin crushed products". In the used polyolefin resin pulverized product, it is preferable that the mixing ratio of metal foreign substances is reduced to less than 2% in the sorting step. If the mixing ratio of the metallic foreign matter is 2% or more, clogging due to the metallic foreign matter frequently occurs in the kneading and granulating step using an extruder, and efficient operation becomes impossible.

【００５１】本発明の使用済みポリオレフィン樹脂粉砕
品を混練造粒する目的で使用されるスクリュー式押出機
の機種、構造等は、金属異物を含めた未溶融物を濾過す
るためのスクリーンメッシュフィルター（以下、ＳＭＦ
という）が設置可能であれば特に制限されるものではな
く、汎用の単軸又は二軸押出機が好適に用いられる。本
発明においては、ＳＭＦによって、金属異物を含めた大
量の未溶融物が濾過され、これら未溶融物がフィルター
の（樹脂の流れに対する）上流側に堆積し最終的にはフ
ィルターを閉塞させることになる。したがって、ＳＭＦ
部分は、混練造粒作業を中断することなくフィルター交
換ができるように、複数のフィルター面を切り替えて濾
過できる、いわゆる「オートスクリーンチェンジャー方
式」となっていることが好ましい。また、閉塞したフィ
ルターに下流から上流方向に圧力をかけることで堆積し
た未溶融物を洗浄し押出機外に排出させる、いわゆる
「逆洗機構」を有するオートスクリーンチェンジャーで
あることがより好ましい。The screw extruder used for the purpose of kneading and granulating the used polyolefin resin pulverized product of the present invention has a model, a structure, etc., of a screen mesh filter for filtering unmelted matter including metal foreign matter. Hereinafter, SMF
Is not particularly limited as long as it can be installed, and a general-purpose single-screw or twin-screw extruder is suitably used. In the present invention, the SMF filters a large amount of unmelted matter including metal foreign matter, and the unmelted matter accumulates on the upstream side (with respect to the resin flow) of the filter, and eventually blocks the filter. Become. Therefore, SMF
The part is preferably of a so-called "auto screen changer type" in which a plurality of filter surfaces can be switched and filtered so that the filter can be replaced without interrupting the kneading and granulating operation. Further, it is more preferable that the filter is an auto screen changer having a so-called “backwashing mechanism” in which the unmelted material deposited by applying pressure from the downstream to the upstream of the closed filter is washed and discharged outside the extruder.

【００５２】本発明で使用されるＳＭＦは、再生品の外
観や機械的物性の観点から、ＡＳＴＭ式標準ふるいでN
o.２０以上（篩目の開き０．８４mm以下）であることが
好ましく、より好ましくはNo.１００以上（篩目の開き
０．１４９mm以下）である。No.２０未満の番手のＳＭ
Ｆであると、大きな粒子径の異物が通過し、再生品の外
観を損ね、機械的物性、特に耐衝撃性や引張破断伸びと
いった靭性に関する物性値が著しく低下するので好まし
くない。ＳＭＦの番手の上限値は、特に制限されるもの
ではないが、No.２５０以下（篩目の開き０．０６２mm
以上）であることが好ましい。No.２５０を超える番手
のＳＭＦであると、フィルターの閉塞が起こる頻度が増
し、生産効率が著しく低下するので好ましくない。The SMF used in the present invention is manufactured using an ASTM standard sieve from the viewpoint of the appearance and mechanical properties of the recycled product.
It is preferable that it is o.20 or more (a sieve opening of 0.84 mm or less), and more preferably No. 100 or more (a sieve opening of 0.149 mm or less). SM of number less than No.20
When F is used, foreign substances having a large particle size pass through, which impairs the appearance of the recycled product, and significantly degrades mechanical properties, particularly physical properties relating to toughness such as impact resistance and tensile elongation at break. Although the upper limit of the SMF count is not particularly limited, it is No. 250 or less (a sieve opening of 0.062 mm
Or more). If the SMF has a count higher than No. 250, the frequency of clogging of the filter increases, and the production efficiency is remarkably reduced.

【００５３】本発明においては、使用済みポリオレフィ
ン樹脂粉砕品をスクリュー式押出機に供給し、ＡＳＴＭ
式標準ふるいでNo.２０以上（篩目の開き０．８４mm以
下）のスクリーンメッシュフィルターによって更に金属
異物を除去しながら混練造粒することで製造されたもの
を「再生ポリオレフィン樹脂」と呼称する。In the present invention, a used polyolefin resin pulverized product is supplied to a screw type extruder and subjected to ASTM.
A product manufactured by kneading and granulating while using a screen mesh filter of No. 20 or more (with a sieve opening of 0.84 mm or less) with a formula standard sieve while removing metal foreign substances is referred to as "recycled polyolefin resin".

【００５４】本発明における再生ポリオレフィン樹脂
は、物性に対する要求スペックが高くない汎用製品であ
れば、そのまま使用可能な物性レベルを有しているが、
バージン樹脂と比較すると耐衝撃性がかなり低下してい
る。その主原因は、前述したようにポリエチレンとポリ
プロピレンとの相溶性の低さにある。The recycled polyolefin resin of the present invention has a physical property level that can be used as it is as long as it is a general-purpose product that does not have high requirements for physical properties.
Impact resistance is considerably reduced as compared with virgin resin. The main cause is the low compatibility between polyethylene and polypropylene as described above.

【００５５】本発明者らは、使用済みポリオレフィン樹
脂粉砕品を混練造粒する際、副材料として熱可塑性エラ
ストマー（以下、ＴＰＥという）を少量添加することで
この問題を解決した。ＴＰＥはそれ自体高い耐衝撃性を
有しており、脆性樹脂に対して２０〜３０％の大量添加
することで耐衝撃性を改良する、いわゆる「インパクト
・モディファイヤー」として知られている。しかし、本
発明においては、ＴＰＥはポリエチレンとポリプロピレ
ンの相溶化剤として機能しているため、その添加量は１
〜１０％の小量でよい。添加量が１％未満であると相溶
化剤としての効果が小さく十分な物性改善ができないた
め好ましくない。また、添加量が１０％を超えると、耐
衝撃性は徐々に増大するものの弾性率が急激に低下する
こと、更に高価な熱可塑性エラストマーを大量添加する
ことにより再生コストの上昇を招くこと等からやはり好
ましくない。The present inventors have solved this problem by adding a small amount of a thermoplastic elastomer (hereinafter referred to as TPE) as an auxiliary material when kneading and granulating a used polyolefin resin pulverized product. TPE itself has high impact resistance, and is known as an "impact modifier" which improves impact resistance by adding a large amount of 20 to 30% to a brittle resin. However, in the present invention, since TPE functions as a compatibilizer for polyethylene and polypropylene, the amount of TPE added is one.
A small amount of 10% to 10% is sufficient. If the addition amount is less than 1%, the effect as a compatibilizer is small and sufficient physical properties cannot be improved, which is not preferable. On the other hand, if the addition amount exceeds 10%, the impact resistance gradually increases, but the elastic modulus drops sharply, and the addition of a large amount of an expensive thermoplastic elastomer leads to an increase in the regeneration cost. After all it is not desirable.

【００５６】本発明に使用されるＴＰＥとしては、具体
的には、低密度ポリエチレン（ＬＤＰＥ）、線状低密度
ポリエチレン（ＬＬＤＰＥ）、エチレン−プロピレン−
ラバー（ＥＰＲ）、エチレン−プロピレン−ジエンモノ
マー共重合体（ＥＰＤＭ）、スチレン−ブタジエン−ス
チレン共重合体（ＳＢＳ）、スチレン−イソプレン−ス
チレン共重合体（ＳＩＳ）、スチレン−エチレンブチレ
ン−スチレン共重合体（ＳＥＢＳ）、塩ビ系ＴＰＥ、ウ
レタン系ＴＰＥ、ポリエステル系ＴＰＥ、ポリアミド系
ＴＰＥ、フッ素樹脂系ＴＰＥなどを例示することがで
き、これらは単独で使用してもよく、２種類以上の混合
物としても使用することができるが、これに何ら制限さ
れるものではない。ただし、相溶化剤としての効果と価
格のバランスの観点から、エチレン−プロピレン−ラバ
ー（ＥＰＲ）及びその類縁体が好適に用いられる。As the TPE used in the present invention, specifically, low density polyethylene (LDPE), linear low density polyethylene (LLDPE), ethylene-propylene-
Rubber (EPR), ethylene-propylene-diene monomer copolymer (EPDM), styrene-butadiene-styrene copolymer (SBS), styrene-isoprene-styrene copolymer (SIS), styrene-ethylenebutylene-styrene copolymer Coalesced (SEBS), PVC-based TPE, urethane-based TPE, polyester-based TPE, polyamide-based TPE, fluororesin-based TPE, and the like. These may be used alone or as a mixture of two or more. It can be used, but is not limited to this. However, from the viewpoint of the balance between the effect as a compatibilizer and the price, ethylene-propylene-rubber (EPR) and its analogs are preferably used.

【００５７】本発明の再生ポリオレフィン樹脂組成物
は、以上に述べてきた再生ポリオレフィン樹脂の製造方
法により混練造粒された再生樹脂であって、曲げ弾性率
（ＡＳＴＭ Ｄ７９０準拠）が１０００ＭＰａ以上であ
り、且つアイゾット衝撃強さ（ＡＳＴＭ Ｄ２５６準
拠）が３kg/m²以上のものである。上記のように、バー
ジン樹脂にも匹敵する剛性と靭性の良好な物性バランス
を有しているため、様々な用途の製品に利用可能であ
る。本発明の再生ポリオレフィン樹脂組成物の排出元で
ある包装材料、自動車、家電製品やＯＡ機器、建築物等
のプラスチック部品としての再利用も可能であるが、い
わゆるカスケード・リサイクルとして、公園のベンチ、
擬木、枕木、樹脂パレット、コンテナー、コンクリート
型枠などへの使用も可能である。The reclaimed polyolefin resin composition of the present invention is a reclaimed resin kneaded and granulated by the method for producing a reclaimed polyolefin resin described above, and has a flexural modulus (according to ASTM D790) of 1000 MPa or more; In addition, the Izod impact strength (according to ASTM D256) is 3 kg / m ² or more. As described above, since it has a good balance of rigidity and good physical properties comparable to virgin resin, it can be used for products for various uses. Packaging materials from which the recycled polyolefin resin composition of the present invention is discharged, automobiles, home appliances and OA equipment, can be reused as plastic parts such as buildings, but as a so-called cascade recycling, park bench,
It can also be used for artificial wood, sleepers, resin pallets, containers, concrete forms, etc.

【００５８】本発明によって製造された再生ポリオレフ
ィン樹脂組成物は、そのままでも様々な用途に使用可能
であるが、更に美麗な外観、高い機械的物性等が要求さ
れる製品に使用する目的で、バージン樹脂と任意の比率
に混合して使用することも可能であり、本発明に含まれ
る。かかる目的で使用される再生ポリオレフィン樹脂組
成物における、バージン樹脂の混合比率は、１０〜９０
重量％、好ましくは２０〜６０重量％である。再生樹脂
が全体の１０重量％より少ないと、プラスチックリサイ
クルの推進という本発明の意義が失われてしまうので好
ましくない。The reclaimed polyolefin resin composition produced according to the present invention can be used for various applications as it is, but virgin resin is used for products requiring more beautiful appearance and high mechanical properties. It is also possible to mix and use the resin in an arbitrary ratio, and it is included in the present invention. In the recycled polyolefin resin composition used for this purpose, the mixing ratio of the virgin resin is 10 to 90.
% By weight, preferably 20 to 60% by weight. If the content of the recycled resin is less than 10% by weight, the significance of the present invention of promoting plastic recycling is lost, which is not preferable.

【００５９】本発明の再生ポリオレフィン樹脂組成物に
は、本発明の目的から外れない範囲で、必要に応じて熱
可塑性以外の樹脂成分、顔料、有機・無機充填剤、各種
添加剤なども添加することができる。これらのうち、成
形品に剛性を付与する目的で使用される有機・無機充填
剤としては、板状、粒状、繊維状のいずれを用いてもよ
い。具体的には、板状又は粒状の充填剤としては、アル
ミニウム粉等の金属粉末、酸化マグネシウム、酸化チタ
ン、アルミナ等の金属酸化物、水酸化マグネシウム、水
酸化アルミニウム等の金属水酸化物、炭酸カルシウム、
炭酸マグネシウム、硫酸バリウム等の炭酸・硫酸塩、ケ
イ酸マグネシウム、ケイ酸アルミニウム等の合成ケイ酸
塩、タルク、マイカ、カオリン等の天然ケイ酸塩、炭化
ケイ素粉、合成・天然シリカ、カーボンブラック、木
粉、綿粉などが挙げられる。また、繊維状充填剤として
は、ナイロン、ＰＥＴ繊維、アラミド繊維、テフロン
（登録商標）繊維等の合成高分子繊維、羊毛、木綿、パ
ルプ等の天然高分子繊維、ガラス繊維、カーボンウィス
カー、グラファイト繊維等のカーボン繊維、シリカ・ア
ルミナファイバー、チタン酸カリウム繊維等のセラミッ
ク繊維、炭化ケイ素繊維・ウィスカー、ボロン繊維、ス
チール繊維、アルミニウム繊維等の金属繊維などを例示
することができる。また、各種添加剤としては、可塑
剤、難燃剤、熱安定剤、酸化防止剤、光安定剤、紫外線
吸収剤、滑剤、帯電防止剤、離型剤、発泡剤、核剤、着
色剤、架橋剤、分散助剤などを例示することができる。To the reclaimed polyolefin resin composition of the present invention, resin components other than thermoplastics, pigments, organic / inorganic fillers, various additives, etc. may be added as required, without departing from the object of the present invention. be able to. Among these, as the organic / inorganic filler used for the purpose of imparting rigidity to the molded product, any of plate-like, granular, and fibrous shapes may be used. Specifically, examples of the plate-like or granular filler include metal powders such as aluminum powder, metal oxides such as magnesium oxide, titanium oxide, and alumina; metal hydroxides such as magnesium hydroxide and aluminum hydroxide; calcium,
Carbonates and sulfates such as magnesium carbonate and barium sulfate; synthetic silicates such as magnesium silicate and aluminum silicate; natural silicates such as talc, mica and kaolin; silicon carbide powder; synthetic and natural silica; carbon black; Wood flour, cotton flour and the like can be mentioned. Examples of the fibrous filler include synthetic polymer fibers such as nylon, PET fibers, aramid fibers, and Teflon (registered trademark) fibers, natural polymer fibers such as wool, cotton, and pulp, glass fibers, carbon whiskers, and graphite fibers. And carbon fibers such as silica / alumina fibers and potassium titanate fibers, and metal fibers such as silicon carbide fibers / whiskers, boron fibers, steel fibers, and aluminum fibers. In addition, various additives include a plasticizer, a flame retardant, a heat stabilizer, an antioxidant, a light stabilizer, an ultraviolet absorber, a lubricant, an antistatic agent, a release agent, a foaming agent, a nucleating agent, a colorant, and a crosslinking agent. Agents, dispersing aids and the like.

【００６０】スチレン系樹脂については、上記のオレフ
ィン系樹脂と同様な方法で、スクリュー式押出機を用い
て混練造粒して再生樹脂とすることができる。The styrenic resin can be kneaded and granulated by using a screw type extruder in the same manner as the above-mentioned olefin resin to obtain a regenerated resin.

【００６１】[0061]

【実施例】実施例１ 数種類の廃家電製品をシュレッダーにより破砕する前に
樹脂製品部品を取り外し、使用された樹脂種、ポリスチ
レンＧＰ、ポリスチレンＨＩ、ポリプロピレン（ＰＰ）
毎に分別した。各樹脂をシュレッダーにより破砕し、こ
れを水洗した後ＡＳＴＭ式標準ふるいでNo.２０以上
（篩目の開き０．８４mm以下）のＳＭＦを装着したオー
トスクリーンチェンジャーによって更に金属異物を除去
しながら、平均粒径５mm程度に混練造粒し、再生ＧＰ、
再生ＨＩ及び再生ＰＰよりなる３種類の再生ペレットを
得た。各再生ペレットを射出成形した試験片について、
引っ張り試験（ＡＳＴＭ Ｄ６３８準拠）、曲げ試験
（ＡＳＴＭ Ｄ７９０準拠）、ＩＺ衝撃強度試験（ＡＳ
ＴＭ Ｄ２５６準拠）及びＭＦＲ測定（ＡＳＴＭ Ｄ１
２３８準拠）を行った結果を表１に示す。EXAMPLES Example 1 Resin product parts were removed before shredding several kinds of waste home appliances by a shredder, and the used resin type, polystyrene GP, polystyrene HI, polypropylene (PP)
Separated every time. Each resin was crushed by a shredder, washed with water, and further polished with an ASTM type standard sieve. The metal screen was further removed by an auto screen changer equipped with an SMF of No. 20 or more (with a sieve opening of 0.84 mm or less). Knead and granulated to a particle size of about 5 mm, regenerated GP,
Three types of regenerated pellets composed of regenerated HI and regenerated PP were obtained. For test specimens obtained by injection molding each regenerated pellet,
Tensile test (according to ASTM D638), bending test (according to ASTM D790), IZ impact strength test (AS
TM D256) and MFR measurement (ASTM D1)
238) is shown in Table 1.

【００６２】上記により樹脂製品部品を取り外した廃家
電製品を、シュレッダーにより破砕し、この破砕粒子を
磁力選別機により鉄を、渦電流選別機により銅、アルミ
ニウム等の非鉄金属を除去し、平均粒子径４０mmのシュ
レッダーダストとした。次いで、シュレッダーダストを
市販のせん断破砕機により２次破砕し、平均粒子径１０
mm程度とした。これを気流分離により発泡ウレタンを分
離したのち、２段階の比重選別により分別した。液体１
として比重１．１の炭酸ナトリウム水溶液を用いて金属
異物及び塩化ビニル樹脂を除去した後、液体２として水
道水を用いてスチレン系樹脂とオレフィン系樹脂とに分
別した。The waste home appliances from which the resin product parts have been removed as described above are crushed by a shredder, and the crushed particles are used to remove iron by a magnetic separator and non-ferrous metals such as copper and aluminum by an eddy current separator to remove average particles. Shredder dust having a diameter of 40 mm was used. Next, the shredder dust was secondarily crushed by a commercially available shear crusher, and the average particle size was 10
mm. The urethane foam was separated by airflow separation, and then separated by two-stage specific gravity selection. Liquid 1
After removing metallic foreign matter and vinyl chloride resin using an aqueous solution of sodium carbonate having a specific gravity of 1.1, the liquid 2 was separated into a styrene resin and an olefin resin using tap water.

【００６３】分別したオレフィン系樹脂を、ＡＳＴＭ式
標準ふるいでNo.２０以上（篩目の開き０．８４mm以
下）のＳＭＦを装着したオートスクリーンチェンジャー
によって更に金属異物を除去しながら、平均粒径５mm程
度に混練造粒し、主としてポリプロピレンよりなる再生
ＰＰペレットと得た。また、分別したスチレン系樹脂を
オレフィン系樹脂と同じ方法により混練造粒して再生Ｐ
Ｓペレットと得た。再生ＰＰペレット及び再生ＰＳペレ
ットについて、実施例１と同様に引っ張り試験、曲げ試
験、ＩＺ衝撃強度試験及びＭＦＲ測定を行った結果を表
２に示す。The separated olefin-based resin was further removed by an automatic screen changer equipped with an SMF of No. 20 or more (with a sieve opening of 0.84 mm or less) using an ASTM standard sieve. The mixture was kneaded and granulated to a degree to obtain a recycled PP pellet mainly composed of polypropylene. Also, the separated styrene resin is kneaded and granulated by the same method as the olefin resin to obtain
S pellets were obtained. Table 2 shows the results of the tensile test, the bending test, the IZ impact strength test, and the MFR measurement performed on the recycled PP pellet and the recycled PS pellet in the same manner as in Example 1.

【００６４】また、分別したスチレン系樹脂について
は、混練造粒により再生ＰＳペレット化するのとは別
に、フラスコ試験により熱分解処理した。フラスコ試験
は、投入量３００g、熱分解温度３００〜４００℃、圧
力５０Toorのバッチ式である。熱分解処理により、暗黒
色の液状生成物８７重量％、残渣５重量％、冷却管付着
物１重量％が得られ、残りは分解ガスであった。この液
状生成物をガスクロマトグラーフィーにより分析したと
ころ、スチレン５５重量％、アクリロニトリル０．７重
量％、トルエン２．６重量％、エチルベンゼン２．６重
量％、α−メチルスチレン４．９重量％、残りは高沸点
油であった。また、液状生成物の塩素含有量は２００pp
m程度であった。分析結果から、液状生成物を、必要に
応じて水洗等により塩素化合物を除去した後、スチレン
モノマー製造設備の精密蒸留装置で蒸留することによ
り、再使用可能な純度のスチレンモノマーが回収できる
ことが確認された。The separated styrene resin was subjected to a thermal decomposition treatment by a flask test, separately from the formation of a regenerated PS pellet by kneading and granulation. The flask test is a batch type with an input amount of 300 g, a thermal decomposition temperature of 300 to 400 ° C., and a pressure of 50 Toor. By the thermal decomposition treatment, 87% by weight of a dark black liquid product, 5% by weight of a residue, and 1% by weight of a substance attached to a cooling pipe were obtained, and the remainder was a decomposition gas. When this liquid product was analyzed by gas chromatography, 55% by weight of styrene, 0.7% by weight of acrylonitrile, 2.6% by weight of toluene, 2.6% by weight of ethylbenzene, 4.9% by weight of α-methylstyrene, and the balance Was a high boiling oil. The chlorine content of the liquid product is 200pp
m. From the analysis results, it was confirmed that the styrene monomer with a reusable purity can be recovered by distilling the liquid product, if necessary, by removing chlorine compounds by washing with water, etc., and then distilling it with a precision distillation device of a styrene monomer production facility. Was done.

【００６５】さらに、気流分離された廃棄冷蔵庫に多量
に含まれる発泡ウレタンは、コークス原料評価用チュー
ビングボンベを用いて熱分解試験を行った。試料を充填
したチュービングボンベを４８０℃の流動浴槽に浸漬
し、圧力２kg/cm²で１６時間保持し、発生した高温ガス
をボンベ頂部から氷水に浸漬した受け器に導き液状物を
凝縮させて留出油を得、未凝縮のガスをガス捕集器に導
き捕集した。生成した炭化物、留出油及びガスの歩留り
は３６．１重量％、４３．１重量％及び２３．３％重量
であった。留出油及びガスはガスクロマトグラーフィー
により分析した。留出油の組成（容量％）を表３に、回
収ガスの組成（容量％）を表４に示す。なお、回収ガス
の組成は、熱分解試験時に混入した空気によるものと考
えられる酸素及び窒素を除去した後の組成で示す。Further, a thermal decomposition test was performed on a large amount of urethane foam contained in the waste refrigerator separated from the airflow by using a tubing cylinder for evaluating a coke raw material. The tubing cylinder filled with the sample is immersed in a fluidized bath at 480 ° C., maintained at a pressure of 2 kg / cm ² for 16 hours, and the generated high-temperature gas is guided from the top of the cylinder into a receiver immersed in ice water to condense the liquid material and be retained. Oil was obtained and uncondensed gas was led to a gas collector and collected. The yields of char, distillate and gas produced were 36.1%, 43.1% and 23.3% by weight. Distillate oil and gas were analyzed by gas chromatography. Table 3 shows the composition (% by volume) of the distillate oil, and Table 4 shows the composition (% by volume) of the recovered gas. The composition of the recovered gas is shown by the composition after removing oxygen and nitrogen, which are considered to be due to air mixed in during the thermal decomposition test.

【００６６】[0066]

【表１】 [Table 1]

【００６７】[0067]

【表２】 [Table 2]

【００６８】[0068]

【表３】 [Table 3]

【００６９】[0069]

【表４】 [Table 4]

【００７０】[0070]

【発明の効果】本発明によれば、廃家電製品に由来する
シュレッダーダストをより高い分別精度でより低コスト
で分別することができ、また、分別品は組成・性状に応
じた再利用技術を適用することにより効率的な再資源化
を達成することができた。これによって、廃家電製品か
ら、既存技術で再利用が可能な鉄、非鉄金属、ガラス等
に加えて、従来再利用が困難とされてきた混合廃プラス
チックのリサイクルを実現した。According to the present invention, shredder dust derived from waste home appliances can be separated at a higher separation accuracy and at a lower cost, and the separated products can be reused according to the composition and properties. Efficient recycling could be achieved by applying. As a result, in addition to iron, non-ferrous metals, glass, and the like that can be reused with existing technology, mixed waste plastic that has been difficult to reuse has been realized from waste home appliances.

フロントページの続き (51)Int.Cl.⁷ 識別記号 ＦＩ テーマコート゛(参考） Ｂ０３Ｃ 1/00 Ｂ２９Ｂ 17/00 1/23 17/02 Ｂ０９Ｂ 3/00 Ｃ０７Ｃ 4/22 Ｂ２９Ｂ 17/00 15/06 17/02 Ｃ０８Ｊ 11/12 Ｃ０７Ｃ 4/22 Ｃ１０Ｇ 1/10 15/06 Ｂ２９Ｋ 23:00 Ｃ０８Ｊ 11/12 25:00 Ｃ１０Ｇ 1/10 75:00 // Ｂ２９Ｋ 23:00 Ｃ０８Ｌ 25:04 25:00 75:04 75:00 Ｂ０９Ｂ 5/00 ＺＡＢＣ Ｃ０８Ｌ 25:04 Ｂ０３Ｃ 1/24 Ａ 75:04 Ｂ０９Ｂ 3/00 Ｚ Ｆターム(参考） 4D004 AA22 AA28 AC05 BA02 BA03 BA06 BA10 CA04 CA08 CA09 CA10 CA12 CA14 CA25 CA26 CA27 DA03 DA20 4D071 AA43 AA46 AB14 CA03 DA15 4F301 AA12 AA15 AA17 AA29 AB03 BC13 BC25 BC26 BC40 BD06 BD31 BF08 BF09 BF12 BF26 BF27 BF32 BG53 CA09 CA25 CA26 CA33 CA68 4H006 AA02 AC91 4H029 CA01 CA14 CA16 Continuation of the front page (51) Int.Cl. ⁷ Identification symbol FI Theme coat II (reference) B03C 1/00 B29B 17/00 1/23 17/02 B09B 3/00 C07C 4/22 B29B 17/00 15/06 17 / 02 C08J 11/12 C07C 4/22 C10G 1/10 15/06 B29K 23:00 C08J 11/12 25:00 C10G 1/10 75:00 // B29K 23:00 C08L 25:04 25:00 75: 04 75:00 B09B 5/00 ZABC C08L 25:04 B03C 1/24 A 75:04 B09B 3/00 Z F term (reference) 4D004 AA22 AA28 AC05 BA02 BA03 BA06 BA10 CA04 CA08 CA09 CA10 CA12 CA14 CA25 CA26 CA27 DA03 DA20 4D071 AA43 AA46 AB14 CA03 DA15 4F301 AA12 AA15 AA17 AA29 AB03 BC13 BC25 BC26 BC40 BD06 BD31 BF08 BF09 BF12 BF26 BF27 BF32 BG53 CA09 CA25 CA26 CA33 CA68 4H006 AA02 AC91 4H029 CA01 CA14 CA16

Claims (16)

【特許請求の範囲】[Claims] 【請求項１】 不特定多数の廃家電製品を破砕して鉄及
び非鉄金属を分別回収した後の樹脂や金属等の混入物か
らなるシュレッダーダストから、少なくともオレフィン
系樹脂とスチレン系樹脂の２成分を分別回収し、オレフ
ィン系樹脂についてはスクリュー式押出機を用いて混練
造粒することで再生樹脂化し、スチレン系樹脂について
は熱分解して油を生成させ、この生成油を蒸留して得ら
れるスチレンモノマーを化学原料として再利用すること
を特徴とする廃家電製品のリサイクル方法。At least two components of olefin-based resin and styrene-based resin from shredder dust composed of contaminants such as resin and metal after crushing an unspecified large number of waste home appliances and separating and recovering iron and non-ferrous metals. Are separated and recovered, and the olefin resin is converted into a regenerated resin by kneading and granulating using a screw extruder, and the styrene resin is thermally decomposed to produce oil, and the resulting oil is obtained by distillation. A method for recycling waste home appliances, characterized by reusing styrene monomer as a chemical raw material. 【請求項２】 不特定多数の廃家電製品を破砕して鉄及
び非鉄金属を分別回収した後の樹脂や金属等の混入物か
らなるシュレッダーダストから、少なくともオレフィン
系樹脂とスチレン系樹脂の２成分を分別回収し、オレフ
ィン系樹脂及びスチレン系樹脂をそれぞれスクリュー式
押出機を用いて混練造粒することで再生樹脂化すること
を特徴とする廃家電製品のリサイクル方法。2. A shredder dust consisting of a mixture of resins and metals after crushing an unspecified large number of waste home appliances and separating and recovering iron and non-ferrous metals, at least two components of an olefin resin and a styrene resin. Characterized by separating and recovering olefin-based resin and styrene-based resin into a regenerated resin by kneading and granulating the olefin-based resin and the styrene-based resin, respectively, using a screw-type extruder. 【請求項３】 廃家電製品の少なくとも一部が冷蔵庫で
あって、それらの製品から鉄及び非鉄金属を分別回収し
た後のシュレッダーダストから、少なくともウレタン系
樹脂、オレフィン系樹脂及びスチレン系樹脂の３成分を
分別回収し、ウレタン系樹脂については熱分解して炭化
物、各種留出油及びガスを生成させ、これらを燃料又は
化学原料として再利用する請求項１又は２記載の廃家電
製品のリサイクル方法。At least a part of the waste home appliances is a refrigerator, and at least three urethane-based resins, olefin-based resins and styrene-based resins are obtained from shredder dust after separating and recovering iron and non-ferrous metals from those products. 3. The method of claim 1 or 2, wherein the components are separated and recovered, and the urethane-based resin is thermally decomposed to generate carbides, various distillate oils and gases, and these are reused as fuels or chemical raw materials. . 【請求項４】 廃家電製品を破砕する前に予め樹脂製部
品の一部を分離回収し、スクリュー式押出機を用いて混
練造粒することで再生樹脂化する請求項１〜３のいずれ
かに記載の廃家電製品のリサイクル方法。4. The method according to claim 1, wherein a part of the resin component is separated and recovered in advance before the waste home appliances are crushed, and kneaded and granulated by using a screw type extruder to be converted into a regenerated resin. How to recycle waste home appliances described in 4. 【請求項５】 廃家電製品の少なくとも一部が、テレ
ビ、パソコン、複写機等の難燃樹脂製部品を用いた製品
であって、廃家電製品を破砕する前に予め分離回収され
る樹脂製部品の少なくとも一部が当該難燃樹脂製部品で
ある請求項４記載の廃家電製品のリサイクル方法。5. At least a part of a waste home appliance is a product using a flame-retardant resin component such as a television, a personal computer, a copying machine, etc., and is made of a resin separated and recovered in advance before crushing the waste home appliance. The method according to claim 4, wherein at least a part of the component is the flame-retardant resin component. 【請求項６】 廃家電製品を破砕した後、磁力選別機を
用いて鉄を、渦電流選別機を用いて非鉄金属をそれぞれ
分別回収する請求項１〜５のいずれかに記載の廃家電製
品のリサイクル方法。6. The waste home appliance according to claim 1, wherein after the waste home appliance is crushed, iron is separated and a non-ferrous metal is separated and recovered using a magnetic separator and an eddy current separator, respectively. Recycling method. 【請求項７】 シュレッダーダストから発泡ウレタン樹
脂を分別回収する際、風力選別機を用いる請求項３〜６
のいずれかに記載の廃家電製品のリサイクル方法。7. A method for separating and recovering urethane foam resin from shredder dust using a wind separator.
A method for recycling waste home appliances according to any of the above. 【請求項８】 分別回収された発泡ウレタン樹脂から、
当該樹脂を製造する際に使用されたフロンを除去する請
求項７記載の廃家電製品のリサイクル方法。8. From the urethane foam resin separated and recovered,
The recycling method for waste home appliances according to claim 7, wherein the fluorocarbon used in producing the resin is removed. 【請求項９】 シュレッダーダストからオレフィン系樹
脂とスチレン系樹脂を分別回収する際、該シュレッダー
ダストを平均粒子径２０mmφ以下まで粉砕した後、先ず
液体１を用いて主としてオレフィン系樹脂とスチレン系
樹脂を浮上させ、浮上しない塩化ビニル系樹脂等のその
他の樹脂や金属等の混入物から分別し、更に浮上した樹
脂混合物を上記と比重の異なる液体２を用いて主として
オレフィン系樹脂を浮上させ、浮上しないスチレン系樹
脂とに分別する請求項１〜８のいずれかに記載の廃家電
製品のリサイクル方法。9. When the olefin resin and the styrene resin are separated and recovered from the shredder dust, the shredder dust is pulverized to an average particle diameter of 20 mmφ or less. Floating, separating from non-floating non-floating resin and other contaminants such as metals, and further floating the resin mixture using the liquid 2 having a specific gravity different from the above, mainly floating the olefin-based resin and not floating The method for recycling waste home appliances according to any one of claims 1 to 8, wherein the method is separated into styrene-based resins. 【請求項１０】 液体１が比重１．０を超えて１．３未
満に調整された無機塩類の水溶液であり、且つ液体２が
比重１．０の水である請求項９記載の廃家電製品のリサ
イクル方法。10. The waste electrical home appliance according to claim 9, wherein the liquid 1 is an aqueous solution of an inorganic salt adjusted to have a specific gravity of more than 1.0 and less than 1.3, and the liquid 2 is water having a specific gravity of 1.0. Recycling method. 【請求項１１】 不特定多数の廃家電製品をリサイクル
する際に、先ずテレビやパソコンモニター等のブラウン
管ガラスと冷蔵庫やエアコン等の冷媒フロン及び樹脂製
部品の一部を分離回収し、次に残された製品を破砕した
後、風力選別機を用いて発泡ウレタン樹脂を、磁力選別
機を用いて鉄を、渦電流選別機を用いて非鉄金属をそれ
ぞれ分別回収し、残さであるシュレッダーダストを平均
粒子径２０mmφ以下まで粉砕した後、先ず液体１を用い
て主としてオレフィン系樹脂とスチレン系樹脂を浮上さ
せ、浮上しない塩化ビニル系樹脂やその他の樹脂や金属
等の混入物から分別し、更にこの浮上した樹脂混合物を
上記と比重の異なる液体２を用いて浮上するオレフィン
系樹脂と浮上しないスチレン系樹脂とに分別し、分別さ
れた樹脂又は樹脂製部品については請求項１〜４記載の
方法で再生樹脂化することを特徴とする廃家電製品のリ
サイクル方法。11. When recycling an unspecified large number of waste home appliances, first, a CRT glass such as a television and a personal computer monitor and a part of a refrigerant Freon and a resin component such as a refrigerator and an air conditioner are separated and collected, and then the remaining part is recovered. After crushing the product, the urethane foam resin is separated using a wind separator, iron is separated using a magnetic separator, and non-ferrous metal is separated and collected using an eddy current separator.The remaining shredder dust is averaged. After crushing to a particle diameter of 20 mmφ or less, first, the olefin-based resin and the styrene-based resin are first floated using the liquid 1, separated from non-floating vinyl chloride-based resin and other contaminants such as metals and metals, and further lifted. The separated resin mixture is separated into an olefin resin that floats and a styrene resin that does not float using the liquid 2 having a specific gravity different from the above, and the separated resin or resin Recycling method of waste household appliances, characterized in that the recycled resin of the claims 1-4, wherein the method is for goods. 【請求項１２】 請求項１〜１１のいずれかにおいて分
別回収されたオレフィン系樹脂をスクリュー式押出機に
供給し、ＡＳＴＭ式標準ふるいでNo.２０以上（篩目の
開き０．８４mm以下）のスクリーンメッシュフィルター
によって金属異物等の固形異物を除去しながら混練造粒
することを特徴とするオレフィン系樹脂組成物よりなる
リサイクル製品。12. The olefin resin fractionated and recovered in any one of claims 1 to 11 is supplied to a screw type extruder, and is passed through an ASTM type standard sieve with a size of No. 20 or more (mesh size of 0.84 mm or less). A recycled product comprising an olefin-based resin composition, which is kneaded and granulated while removing solid foreign matter such as metal foreign matter by a screen mesh filter. 【請求項１３】 請求項２〜１１のいずれかにおいて分
別回収されたスチレン系樹脂をスクリュー式押出機に供
給し、ＡＳＴＭ式標準ふるいでNo.２０以上（篩目の開
き０．８４mm以下）のスクリーンメッシュフィルターに
よって金属異物等の固形異物を除去しながら混練造粒す
ることを特徴とするスチレン系樹脂組成物よりなるリサ
イクル製品。13. The styrenic resin separated and recovered in any one of claims 2 to 11 is supplied to a screw type extruder, and the styrenic resin having a size of No. 20 or more (a sieve opening of 0.84 mm or less) is passed through an ASTM standard sieve. A recycled product comprising a styrene-based resin composition, which is kneaded and granulated while removing a solid foreign substance such as a metallic foreign substance using a screen mesh filter. 【請求項１４】 請求項１又は３〜１１のいずれかにお
いて分別回収されたスチレン系樹脂を熱分解し、得られ
た生成油を蒸留してスチレンモノマーを得るプロセスに
おいて、収率が８０％以上であって、且つスチレンモノ
マー濃度が５０％以上である熱分解生成油を蒸留して純
度９９％以上のスチレンモノマーとしたことを特徴とす
るリサイクル製品としての純度９９％以上のスチレンモ
ノマー。14. A process for thermally decomposing the styrene resin fractionated and recovered in any one of claims 1 or 3 to 11 and distilling the obtained oil to obtain a styrene monomer, wherein the yield is 80% or more. A styrene monomer having a purity of 99% or more as a recycled product, wherein a pyrolysis oil having a styrene monomer concentration of 50% or more is distilled into a styrene monomer having a purity of 99% or more. 【請求項１５】 請求項３〜１１記載のいずれかの方法
によって分別回収されたウレタン樹脂を熱分解して得ら
れる炭化物、各種留出油又はガスよりなるリサイクル製
品。15. A recycled product comprising a carbide, various distillate oils or gases obtained by pyrolyzing a urethane resin fractionated and recovered by the method according to any one of claims 3 to 11. 【請求項１６】 請求項９〜１１記載のいずれかの方法
においてシュレッダーダストからオレフィン系樹脂とス
チレン系樹脂を分別回収した後、残さである塩化ビニル
系樹脂等のその他の樹脂や金属等の混入物をスクリュー
式押出機に供給し、塩化ビニル系樹脂に含まれる塩素を
熱分解により塩化水素として回収し、残さを必要により
加えられる非塩素系の他の樹脂と共に混練造粒すること
を特徴とする固形プラスチック燃料として使用可能な樹
脂組成物よりなるリサイクル製品。16. The method according to claim 9, wherein after separating and recovering the olefin resin and the styrene resin from the shredder dust, the remaining resin such as a vinyl chloride resin or a metal is mixed. The product is supplied to a screw type extruder, chlorine contained in the vinyl chloride resin is recovered as hydrogen chloride by thermal decomposition, and the residue is kneaded and granulated with other non-chlorine resin added as necessary. A recycled product comprising a resin composition that can be used as a solid plastic fuel.