JP2002212323A - Molded product with gel coat and method for producing the same - Google Patents
Molded product with gel coat and method for producing the sameInfo
- Publication number
- JP2002212323A JP2002212323A JP2001009064A JP2001009064A JP2002212323A JP 2002212323 A JP2002212323 A JP 2002212323A JP 2001009064 A JP2001009064 A JP 2001009064A JP 2001009064 A JP2001009064 A JP 2001009064A JP 2002212323 A JP2002212323 A JP 2002212323A
- Authority
- JP
- Japan
- Prior art keywords
- gel coat
- molded product
- resin
- producing
- molded article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、不飽和ポリエステ
ル樹脂、無機質充てん材、強化材を主成分としたゲルコ
ート付き成形品に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a molded article with a gel coat containing an unsaturated polyester resin, an inorganic filler and a reinforcing material as main components.
【0002】[0002]
【従来の技術】不飽和ポリエステル樹脂、無機質充てん
材、強化材を主成分とした成形品の表面にゲルコートを
付ける公知の製法として、あらかじめ型にラジカル重合
系樹脂を塗布し、硬化させた後、不飽和ポリエステル樹
脂、無機質充てん材、強化材を主成分とする成形品を成
形する製法がなる。2. Description of the Related Art As a known method of applying a gel coat to the surface of a molded article mainly composed of an unsaturated polyester resin, an inorganic filler, and a reinforcing material, a radical polymerizable resin is applied to a mold in advance, and then cured. It is a manufacturing method of molding a molded product mainly composed of an unsaturated polyester resin, an inorganic filler, and a reinforcing material.
【0003】[0003]
【発明が解決しようとする課題】従来のあらかじめ型に
ラジカル重合系樹脂を塗布し、硬化させた後、不飽和ポ
リエステル樹脂、無機質充てん材、強化材を主成分とす
る成形品を成形する製法は、型に塗布されたラジカル重
合系樹脂の塗布および硬化時間、成形品の成形時間両者
において型を含有しているため、ゲルコート付き成形品
の生産性が低い問題があった。本発明は、成形品を型か
らはずした後ゲルコートを付ける生産性優れたゲルコー
ト付き成形品および製法を提供するものである。A conventional method of applying a radical polymerizable resin to a mold in advance, curing the resin, and then molding a molded article containing an unsaturated polyester resin, an inorganic filler, and a reinforcing material as main components is known. In addition, since the mold is contained in both the application and curing time of the radical polymerization resin applied to the mold and the molding time of the molded article, there is a problem that the productivity of the molded article with the gel coat is low. SUMMARY OF THE INVENTION The present invention provides a molded article with a gel coat having excellent productivity for applying a gel coat after removing the molded article from a mold and a production method.
【0004】[0004]
【課題を解決するための手段】本発明は、次のものに関
する。 (1) 不飽和ポリエステル樹脂、無機質充てん材、強
化材を主成分とし得られる成形品表面に、エポキシ樹脂
(I)とカチオン系紫外線開始剤(II)よりなる樹脂
組成物を塗布し、紫外線を照射するゲルコート付き成形
品の製法。 (2) (1)記載の製法により得られるゲルコート付
き成形品。The present invention relates to the following. (1) A resin composition composed of an epoxy resin (I) and a cationic ultraviolet initiator (II) is applied to the surface of a molded article obtained by using an unsaturated polyester resin, an inorganic filler and a reinforcing material as main components, and applying ultraviolet rays. Manufacturing method of molded article with gel coat to be irradiated. (2) A molded article with a gel coat obtained by the production method according to (1).
【0005】[0005]
【発明の実施の形態】本発明の成形品は公知の材料およ
び製法により得られるものであり、特に制約はない。本
発明のエポキシ樹脂(I)は、ビスフェノールA型エポ
キシ樹脂、ビスフェノールF型エポキシ樹脂、ビスフェ
ノールAD型エポキシ樹脂、フェノールノボラック型エ
ポキシ樹脂、クレゾールノボラック型エポキシ樹脂、脂
環式エポキシ樹脂、単官能エポキシ樹脂など公知のエポ
キシ樹脂が挙げられ、目的とする特性に合わせて選らば
れる。BEST MODE FOR CARRYING OUT THE INVENTION The molded article of the present invention is obtained by known materials and manufacturing methods, and is not particularly limited. The epoxy resin (I) of the present invention is a bisphenol A epoxy resin, a bisphenol F epoxy resin, a bisphenol AD epoxy resin, a phenol novolak epoxy resin, a cresol novolak epoxy resin, an alicyclic epoxy resin, a monofunctional epoxy resin. A known epoxy resin may be used, and is selected according to the desired properties.
【0006】本発明のカチオン系紫外線開始剤(II)
は、芳香族ジアゾニウム塩、芳香族スルホニウム塩、芳
香族ヨードニウム塩、メタロセン化合物などの公知のカ
チオン系紫外線開始剤が挙げられ、目的とする特性に合
わせて選ばれる。本発明のゲルコート付き成形品の製法
は、不飽和ポリエステル樹脂、無機質充てん材、強化材
を主成分として公知の成形法で得られた成形品表面に、
エポキシ樹脂(I)とカチオン系紫外線開始剤(II)
よりなる樹脂組成物をスプレーなどに塗布した後、紫外
線を照射することである。The cationic UV initiator of the present invention (II)
Are known cationic ultraviolet initiators such as aromatic diazonium salts, aromatic sulfonium salts, aromatic iodonium salts, and metallocene compounds, and are selected in accordance with the desired properties. The method for producing a molded article with a gel coat of the present invention is performed on a molded article surface obtained by a known molding method using an unsaturated polyester resin, an inorganic filler, and a reinforcing material as main components,
Epoxy resin (I) and cationic UV initiator (II)
UV irradiation after applying the resin composition comprising a spray or the like.
【0007】[0007]
【実施例】ガラス板上にポリセット2198(日立化成
工業(株)商品名、不飽和ポリエステル樹脂)メチルエ
チルケトンパーオキサイド、ガラスマットを用い、常法
によりガラス繊維強化プラスチック(FRP)成形品を
得た。FRP成形品をガラス板よりはずし、ガラス板側
のFRP表面に、エピコートR−140(油化シェルエ
ポキシ(株)商品名、ビスフェノールA型エポキシ樹
脂)90質量部、ブチルグリシジルエーテル10質量
部、アデカオプトマ−S−150(旭電化工業(株)商
品名、カチオン系紫外線開始剤)4質量部よりなる樹脂
組成物を厚さ50μmに塗布した。これに紫外線120
0mJ/cm2を照射し、ベタ付きがなく90℃/10
0時間の耐熱水性に優れたゲルコート付き成形品が得ら
れた。EXAMPLE A glass fiber reinforced plastic (FRP) molded product was obtained on a glass plate by a conventional method using methyl ethyl ketone peroxide and glass mat on a polyset 2198 (trade name of Hitachi Chemical Co., Ltd., unsaturated polyester resin). . The FRP molded article was removed from the glass plate, and 90 parts by mass of Epicoat R-140 (trade name of Yuka Shell Epoxy Co., Ltd., bisphenol A type epoxy resin), 10 parts by mass of butyl glycidyl ether, ADEKA OPTOMA A resin composition comprising 4 parts by mass of -S-150 (trade name of Asahi Denka Kogyo KK, cationic ultraviolet initiator) was applied to a thickness of 50 µm. UV 120
Irradiate 0 mJ / cm 2 , 90 ° C / 10 without stickiness
A molded article with a gel coat having excellent hot water resistance for 0 hours was obtained.
【0008】比較例 実施例と同様にして得られたFRPに、ポリセット22
12(日立化成工業(株)商品名、不飽和ポリエステル
樹脂)、100質量部、イルガキュア651(チバ・ス
ペシャリティ・ケミカルズ(株)商品名、ラジカル系紫
外線開始剤)4質量部よりなる樹脂組成物を厚さ50μ
mに塗布した。これに紫外線1200mJ/cm2を照
射した。ゲルコート表面にややベタ付きがあり、90℃
/100時間の耐熱水性において、ゲルコートがはく離
した。Comparative Example Polyset 22 was added to FRP obtained in the same manner as in the example.
A resin composition comprising 12 parts (trade name of Hitachi Chemical Co., Ltd., unsaturated polyester resin), 100 parts by mass, and 4 parts by mass of Irgacure 651 (trade name of Ciba Specialty Chemicals, radical ultraviolet initiator) Thickness 50μ
m. This was irradiated with ultraviolet rays at 1200 mJ / cm 2 . The gel coat surface is slightly sticky, 90 ° C
The gel coat was peeled off in hot water resistance of / 100 hours.
【0009】[0009]
【発明の効果】不飽和ポリエステル樹脂、無機質充てん
材、強化材を主成分として得られる成形品表面に、エポ
キシ樹脂とカチオン系紫外線開始剤よりなる樹脂組成物
を塗布し、紫外線を照射することにより、効率良く、表
面のベタ付きのない耐熱水性に優れたゲルコート付き成
形品を得ることができる。According to the present invention, a resin composition comprising an epoxy resin and a cationic ultraviolet initiator is applied to the surface of a molded article obtained by using an unsaturated polyester resin, an inorganic filler and a reinforcing material as main components, and irradiated with ultraviolet rays. It is possible to efficiently obtain a molded article with a gel coat which is excellent in hot water resistance without stickiness on the surface.
Claims (2)
材、強化材を主成分とし得られる成形品表面に、エポキ
シ樹脂(I)とカチオン系紫外線開始剤(II)よりな
る樹脂組成物を塗布し、紫外線を照射するゲルコート付
き成形品の製法。1. A resin composition comprising an epoxy resin (I) and a cationic ultraviolet initiator (II) is applied to the surface of a molded product obtained by using an unsaturated polyester resin, an inorganic filler and a reinforcing material as main components, A method of manufacturing molded products with gel coat that is irradiated with ultraviolet light.
コート付き成形品。2. A molded article with a gel coat obtained by the production method according to claim 1.