JP2002177424A - Shaft for golf club - Google Patents
Shaft for golf clubInfo
- Publication number
- JP2002177424A JP2002177424A JP2000383399A JP2000383399A JP2002177424A JP 2002177424 A JP2002177424 A JP 2002177424A JP 2000383399 A JP2000383399 A JP 2000383399A JP 2000383399 A JP2000383399 A JP 2000383399A JP 2002177424 A JP2002177424 A JP 2002177424A
- Authority
- JP
- Japan
- Prior art keywords
- shaft
- golf club
- layer
- braid
- orientation angle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、繊維強化樹脂製の
ゴルフクラブ用シャフトに関する。The present invention relates to a golf club shaft made of fiber reinforced resin.
【０００２】[0002]
【従来の技術】従来より、繊維強化樹脂製のゴルフクラ
ブ用シャフトにおいては、種々の製造方法により形成さ
れたゴルフクラブ用シャフトが提案されている。例え
ば、シートワインディング法と呼ばれる製造方法によっ
て形成されたゴルフクラブ用シャフトは、一般に、強化
繊維を引揃え、樹脂を含浸させてプリプレグ化したプリ
プレグシートをマンドレルに巻回せしめた後、テーピン
グを施して加熱硬化させて成形されるものである。2. Description of the Related Art Conventionally, as a golf club shaft made of fiber reinforced resin, golf club shafts formed by various manufacturing methods have been proposed. For example, a golf club shaft formed by a manufacturing method called a sheet winding method, generally, a reinforcing fiber is aligned, a prepreg sheet impregnated with resin and prepreg is wound around a mandrel, and then subjected to taping. It is molded by heating and curing.
【０００３】また、図２に示すように、３軸ブレーディ
ング法と呼ばれる製造方法によって形成されたゴルフク
ラブ用シャフト５０は、樹脂を含浸させた強化繊維の束
からなる糸を用いて、シャフト軸５１に対して左右対称
の配向角度５５を有する組糸５２と、シャフト軸５１に
対して０°の配向角度をもつ中央糸５３とを組機により
編み組み形成される３軸組物層５４を複数層積層して形
成されるものである。As shown in FIG. 2, a golf club shaft 50 formed by a manufacturing method called a triaxial braiding method uses a yarn made of a bundle of reinforcing fibers impregnated with a resin to form a shaft shaft. A triaxial braided layer 54 is formed by braiding a braided yarn 52 having a symmetrical orientation angle 55 with respect to 51 and a central yarn 53 having an orientation angle of 0 ° with respect to the shaft axis 51 by a braiding machine. It is formed by laminating a plurality of layers.
【０００４】[0004]
【発明が解決しようとする課題】ところが、上記従来製
造方法によって形成されたゴルフクラブ用シャフトにお
いては、以下のような欠点を有するものであった。However, the golf club shaft formed by the above conventional manufacturing method has the following disadvantages.
【０００５】即ち、シートワインディング法によって形
成されたゴルフクラブ用シャフトにおいては、その製法
上、一方向ごとに強化繊維を積層できることにより、必
要とされる高い曲げ剛性や捩り剛性を保ちながら、軽量
なものを形成しやすいといった反面、プリプレグシート
の巻着開始部分と巻着終了部分とが重なり合ったり、重
なり合わなかったりして段差が生じることや、一方向引
揃えのプリプレグシートを台形状にカットして巻着する
ため、巻着角度が、巻き始めと巻き終りで異なってしま
うことなどによってシャフトの曲げ剛性が円周方向にお
いて均一となり難く、安定した品質のシャフトが得られ
難いという問題があった。That is, in a golf club shaft formed by a sheet winding method, a reinforcing fiber can be laminated in one direction in the manufacturing method, so that a light weight while maintaining necessary high bending rigidity and torsional rigidity can be obtained. While it is easy to form things, the winding start part and the winding end part of the prepreg sheet overlap or do not overlap, causing a step, or cutting the prepreg sheet in one direction alignment into a trapezoidal shape. Since the winding angle is different between the winding start and the winding end, the bending rigidity of the shaft is hardly uniform in the circumferential direction, and it is difficult to obtain a shaft of stable quality. .
【０００６】また、３軸ブレーディング法によって形成
されたゴルフクラブ用シャフトにおいては、ゴルフクラ
ブ用シャフトの全長にわたり連続した中央糸や組糸を編
み組みしてなる組物層を積層したものであるので、ゴル
フクラブ用シャフトとしてねばり・柔軟性があり、か
つ、シャフト軸方向に配向された中央糸により良好な曲
げ強度及び、剛性が得られると共に、シャフト軸に対し
て左右に角度を有する組糸によって良好な捩り剛性が発
現でき、しかも、円周方向の曲げ剛性を均一に出来るた
め、フィーリングの良好なゴルフクラブ用シャフトが得
られるといったメリットを有する。しかしその反面、例
えば、上級者のゴルファーに対応した、より高い曲げ剛
性を得ようとした場合においては、３軸組物層の積層数
を増やすといった方法が用いられるが、使用する強化繊
維量の増大分、ゴルフクラブ用シャフト自体の質量が著
しく大きくなってしまうといった問題があった。他の方
法としては、図３に示すように、組物層の積層数を増や
さないで、組物層を構成しているシャフト軸５１に対し
て左右に角度を有する組糸５２の配向角度５５を、シャ
フト軸方向に近づけるように配向させるなどの方法も用
いられるが、この場合においては、必要な曲げ剛性は得
られるが、前記組糸が捩り方向に寄与しなくなることか
ら、捩り剛性が大幅に低下してしまうといった問題もあ
った。In a golf club shaft formed by a triaxial braiding method, a braid layer formed by braiding a continuous central yarn or braid over the entire length of the golf club shaft is laminated. Therefore, a braided yarn having a toughness and flexibility as a golf club shaft, good bending strength and rigidity can be obtained by a central yarn oriented in the shaft axis direction, and having a left and right angle with respect to the shaft axis. As a result, good torsional rigidity can be obtained, and bending rigidity in the circumferential direction can be made uniform. Therefore, there is an advantage that a golf club shaft having a good feeling can be obtained. However, on the other hand, for example, when trying to obtain higher bending rigidity corresponding to an advanced golfer, a method of increasing the number of layers of the triaxial braided layer is used, but the amount of reinforcing fiber used is There is a problem that the mass of the golf club shaft itself becomes extremely large due to the increase. As another method, as shown in FIG. 3, without increasing the number of laminated braid layers, the orientation angle 55 of the braid 52 having an angle to the left and right with respect to the shaft axis 51 constituting the braid layer. In such a case, the required bending rigidity can be obtained, but the torsional rigidity is significantly reduced because the braid does not contribute to the torsional direction. There was also a problem that it was lowered.
【０００７】また、前記組物層をマンドレルに積層する
際には、組機の回転数とマンドレルの移送速度を可変す
ることで、組糸の巻着角度をある程度自由に調整するこ
とができるが、その製法上、組糸の配向角度をゴルフク
ラブ用シャフトの軸方向に対して６０°を越えて配向さ
せることは難しく、更には、９０゜方向に配向させるこ
とができない。したがって、軽量なシャフトを得ようと
して、該シャフトの肉厚を薄くしようとすると、潰れ強
度を充分に発現させることが難しいといった問題も有し
ていた。When laminating the braid layer on the mandrel, the winding angle of the braid can be adjusted to some extent by changing the rotation speed of the braiding machine and the transfer speed of the mandrel. Due to its manufacturing method, it is difficult to orient the braid at an angle exceeding 60 ° with respect to the axial direction of the golf club shaft, and furthermore, it is not possible to orient the braid at 90 °. Therefore, there is also a problem that it is difficult to sufficiently develop crushing strength when trying to reduce the thickness of the shaft in order to obtain a lightweight shaft.
【０００８】そこで本発明は、このような従来の問題点
に鑑み、上級者向けのゴルフクラブ用シャフトに対応し
た高い曲げ剛性と、充分な捩り剛性が得られ、且つ、充
分な潰れ強度を有し、しかも軽量で安定した品質が得ら
れるゴルフクラブ用シャフトを提供することを目的とす
る。In view of the above problems, the present invention has high bending rigidity and sufficient torsional rigidity corresponding to golf club shafts for advanced users, and has sufficient crushing strength. Another object of the present invention is to provide a golf club shaft that is lightweight and has stable quality.
【０００９】[0009]
【課題を解決するための手段】上記目的を達成するため
に、本発明の請求項１に係るゴルフクラブ用シャフト
は、繊維強化樹脂製のゴルフクラブ用シャフトにおい
て、樹脂を含浸させた強化繊維の束からなる糸を編み組
みして構成された組物層と、引き揃えられた強化繊維に
樹脂を含浸させてなるプリプレグシートを巻回して構成
された繊維層とからなるゴルフクラブ用シャフトであ
る。According to a first aspect of the present invention, there is provided a golf club shaft made of a fiber-reinforced resin-made golf club shaft. A golf club shaft comprising a braided layer formed by braiding yarns in a bundle and a fiber layer formed by winding a prepreg sheet formed by impregnating a resin with aligned reinforcing fibers. .
【００１０】請求項２は、前記請求項１に係るゴルフク
ラブ用シャフトにおいて、前記組物層は、シャフト軸に
対し左右対称の配向角度を有する組糸と前記シャフト軸
に対し０°の配向角度を有する中央糸とが編み組みして
構成された３軸組物層と、前記シャフト軸に対し左右対
称の配向角度を有する組糸のみで構成された２軸組物層
とからなるゴルフクラブ用シャフトである。According to a second aspect of the present invention, in the golf club shaft according to the first aspect, the braid layer has a braid having a symmetrical orientation angle with respect to the shaft axis and an orientation angle of 0 ° with respect to the shaft axis. For a golf club, comprising: a three-axis braided layer formed by braiding a central yarn having a braid; and a two-axis braided layer formed only by a braided yarn having a symmetrical orientation angle with respect to the shaft axis. It is a shaft.
【００１１】請求項３は、前記請求項１に係るゴルフク
ラブ用シャフトにおいて、前記組物層は、シャフト軸に
対し左右対称の配向角度を有する組糸と前記シャフト軸
に対し０°の配向角度を有する中央糸とが編み組みして
構成された３軸組物層であるゴルフクラブ用シャフトで
ある。According to a third aspect of the present invention, in the golf club shaft according to the first aspect, the braided layer has a braid having an symmetrical orientation angle with respect to the shaft axis and an orientation angle of 0 ° with respect to the shaft axis. The golf club shaft is a triaxial braided layer formed by braiding a central yarn having
【００１２】請求項４は、前記請求項１に係るゴルフク
ラブ用シャフトにおいて、前記組物層は、前記シャフト
軸に対し左右対称の配向角度を有する前記組糸のみで構
成された２軸組物層であるゴルフクラブ用シャフトであ
る。According to a fourth aspect of the present invention, in the golf club shaft according to the first aspect, the braid layer is composed of only the braid having a symmetrical orientation angle with respect to the shaft axis. The golf club shaft is a layer.
【００１３】請求項５は、前記請求項２、３又は４に係
るゴルフクラブ用シャフトにおいて、前記組糸の配向角
度は、シャフト軸に対し０°より大きく２０°以下に配
向されていることを特徴とするものである。According to a fifth aspect of the present invention, in the golf club shaft according to the second, third or fourth aspect, the orientation angle of the braid is greater than 0 ° and less than 20 ° with respect to the shaft axis. It is a feature.
【００１４】請求項６は、前記請求項１、２、３、４又
は５に係るゴルフクラブ用シャフトにおいて、前記繊維
層を構成する強化繊維の配向角度は、シャフト軸に対し
３０°〜９０°に配向されていることを特徴とするもの
である。According to a sixth aspect, in the golf club shaft according to the first, second, third, fourth, or fifth aspect, the orientation angle of the reinforcing fibers constituting the fiber layer is 30 ° to 90 ° with respect to the shaft axis. Characterized in that they are oriented in
【００１５】請求項７は、前記請求項１、２、３、４、
５又は６に係るゴルフクラブ用シャフトにおいて、前記
繊維層の構成比率がシャフト全体の体積の２０％〜８０
％であることを特徴とするものである。[0015] Claim 7 is the above-mentioned claim 1, 2, 3, 4,
In the golf club shaft according to 5 or 6, the composition ratio of the fiber layer is 20% to 80% of the entire shaft volume.
%.
【００１６】[0016]
【発明の実施の形態】以下、本発明の実施の形態を図面
に基づき詳細に説明する。図１は本発明のゴルフクラブ
用シャフトの一実施例を示す斜視図である。Embodiments of the present invention will be described below in detail with reference to the drawings. FIG. 1 is a perspective view showing one embodiment of the golf club shaft of the present invention.
【００１７】本発明のゴルフクラブ用シャフト１は、
図１に示すように、シャフト軸１１に対し左右対称に０
°より大きく２０°以下の配向角度を有する組糸１２
と、前記シャフト軸１１に対し０°の配向角度を有する
中央糸１３とを編み組みして構成された３軸組物層１４
を有し、さらに、前記シャフト軸１１に対し左右対称に
０°より大きく２０°以下の配向角度を有する前記組糸
１２のみで構成された２軸組物層１８を有し、前記３軸
組物層１４と前記２軸組物層１８とが組み合わされて複
数層積層されることによって組物層１９が構成されてい
る。さらに、該組物層１９の内層側には、強化繊維を引
揃え、樹脂を含浸させてプリプレグ化したプリプレグシ
ートを巻回して形成された繊維層２０が構成されてい
る。該繊維層２０においては、前記強化繊維の配向角度
が前記シャフト軸１１に対し３０°〜８０°未満に配向
された第一繊維層１６と、前記シャフト軸１１に対し８
０°〜９０°に配向された第二繊維層１７とから構成さ
れている。The golf club shaft 1 of the present invention comprises:
As shown in FIG.
Braided yarn 12 having an orientation angle greater than 20 ° and less than 20 °
And a three-axis braided layer 14 formed by braiding a central thread 13 having an orientation angle of 0 ° with respect to the shaft axis 11.
And a biaxial braid layer 18 composed solely of the braided yarns 12 having an orientation angle of more than 0 ° and not more than 20 ° symmetrically with respect to the shaft axis 11, The assembly layer 19 is formed by combining the assembly layer 14 and the biaxial assembly layer 18 into a plurality of layers. Further, on the inner layer side of the braid layer 19, there is formed a fiber layer 20 formed by winding a prepreg sheet prepared by arranging reinforcing fibers, impregnating with a resin, and prepreg. In the fiber layer 20, the first fiber layer 16 in which the orientation angle of the reinforcing fibers is oriented at 30 ° to less than 80 ° with respect to the shaft axis 11,
And a second fiber layer 17 oriented at 0 ° to 90 °.
【００１８】本実施の形態における組物層においては、
３軸組物層及び２軸組物層の組糸の配向角度をシャフト
軸に対し０°より大きく２０°以下とさせたことで、該
組糸は曲げ剛性に寄与させることとなり、上級者に対応
した高い曲げ剛性を得ることが可能となった。また、前
記配向角度がシャフト軸に対し０°より大きく２０°以
下とした理由においては、０°とすると、組糸を編み組
みできず、編み組み構造によるねばりや柔軟性などの効
果が得難いためであり、２０°を越えると曲げ剛性より
も捩り剛性に寄与する割合が増し、集中的に曲げ剛性を
得ることが難しい。したがって、上級者に対応した高い
曲げ剛性を得るための配向角度の上限は２０°以下が最
適である。In the braid layer according to the present embodiment,
By setting the orientation angle of the braids of the triaxial braid layer and the biaxial braid layer to be greater than 0 ° and not more than 20 ° with respect to the shaft axis, the braid contributes to the bending rigidity. It has become possible to obtain a correspondingly high bending rigidity. In addition, the reason why the orientation angle is larger than 0 ° and not more than 20 ° with respect to the shaft axis is that if the angle is 0 °, the braid cannot be braided, and it is difficult to obtain effects such as toughness and flexibility by the braided structure. When the angle exceeds 20 °, the ratio of contributing to the torsional rigidity increases more than the flexural rigidity, and it is difficult to obtain the flexural rigidity intensively. Therefore, the upper limit of the orientation angle for obtaining high bending stiffness corresponding to advanced users is optimally 20 ° or less.
【００１９】さらに、本実施の形態における第一繊維層
においては、その強化繊維の配向角度を３０°〜８０°
未満の範囲としたことによって、上述のような組物層の
配向角度がシャフト軸方向に近づくことによって発生す
る捩り剛性の不足を、質量の増加を最小限に押さえなが
ら補うとともに、より高い捩り剛性を得ることができ
る。この範囲外では、捩り剛性に寄与する割合が減少し
てしまい、集中的に捩り剛性を得られない。さらに、よ
り捩り剛性に集中させるためには、３０°〜６０°の範
囲とさせることが好ましい。Further, in the first fiber layer in the present embodiment, the orientation angle of the reinforcing fibers is 30 ° to 80 °.
By setting the range to less than the above, the shortage of torsional rigidity caused by the orientation angle of the braid layer approaching the shaft axial direction as described above is compensated for while minimizing the increase in mass, and the torsional rigidity is increased. Can be obtained. Outside this range, the rate of contribution to torsional rigidity decreases, and it is not possible to obtain torsional rigidity intensively. Further, in order to concentrate on torsional rigidity, it is preferable that the angle is in the range of 30 ° to 60 °.
【００２０】また、第二繊維層においては、強化繊維の
配向角度を８０°〜９０°の範囲としたことで、質量の
増加を最小限に押さえて、組物層における潰れ強度の不
足を補うことが可能となった。つまり、前記強化繊維が
シャフト軸に対し略直角方向に配向されることによっ
て、必要とされる高い潰れ強度を得られる。第二繊維層
の強化繊維の配向角度を８０°〜９０°の範囲とした理
由においては、強化繊維を引揃え、樹脂を含浸させてプ
リプレグ化した引揃えシートを、テーパー状のマンドレ
ルに巻回させる都合上、前記配向角度は、実質８０°〜
９０°の範囲で許容誤差を有するものであり、また、前
記範囲内であれば、充分な潰れ強度を得ることができ
る。この範囲以外では、充分な潰れ強度を得ることは難
しい。In the second fiber layer, the orientation angle of the reinforcing fibers is in the range of 80 ° to 90 °, so that an increase in mass is suppressed to a minimum, and the insufficient crushing strength in the braid layer is compensated. It became possible. That is, the required high crushing strength can be obtained by orienting the reinforcing fibers in a direction substantially perpendicular to the shaft axis. The reason why the orientation angle of the reinforcing fibers of the second fiber layer is in the range of 80 ° to 90 ° is that the reinforcing fibers are aligned, and a resin-impregnated prepreg-aligned sheet is wound around a tapered mandrel. For convenience, the orientation angle is substantially 80 ° to
It has an allowable error in the range of 90 °, and within the above range, a sufficient crushing strength can be obtained. Outside this range, it is difficult to obtain sufficient crushing strength.
【００２１】尚、本実施の形態における組物層は、３軸
組物層と２軸組物層とを組み合わせた構成としたこと
で、高い曲げ剛性を必要とする上級者に対応することは
可能となったが、さらに、前記上級者におけるゴルフク
ラブをスイングした時に感じるシャフトのフィーリング
の好みは千差万別であり、それらフィーリングの好みに
も対応する必要がある。したがって、さらに剛いフィー
リングを得たい上級ゴルファーにおいては、前記組物層
をシャフト軸に対し０°の配向角度を持つ中央糸を有す
る３軸組物層のみで構成させるとで対応し、やや剛さを
弱めたい上級ゴルファーにおいては、前記組物層をシャ
フト軸に対し左右対称の配向角度を有する前記組糸で構
成された２軸組物層のみで構成させることで対応し、様
々な上級ゴルファーの細かい要求にも対応することが可
能である。Incidentally, the braid layer in the present embodiment has a structure in which the triaxial braid layer and the biaxial braid layer are combined, so that it is possible to cope with advanced users who require high bending rigidity. Although it has become possible, the taste of the shaft felt by the advanced player when swinging a golf club varies widely, and it is necessary to cope with the taste preference. Therefore, for a golfer who wants to obtain a more rigid feeling, the braid layer is constituted by only a triaxial braid layer having a central yarn having an orientation angle of 0 ° with respect to the shaft axis. For advanced golfers who want to weaken the stiffness, the braid layer is made up of only a biaxial braid layer composed of the braid yarns having a symmetrical orientation angle with respect to the shaft axis. It is possible to respond to the fine requirements of golfers.
【００２２】さらに、強化繊維を引揃え、樹脂を含浸さ
せてなるプリプレグシートを巻回して形成された繊維層
においては、ゴルフクラブを構成させるシャフト全体の
体積に対する該繊維層の構成比率が２０％〜８０％であ
ることが望ましい。８０％を越えるとシャフトの曲げ剛
性が円周方向において均一となり難く、安定した品質の
シャフトが得られ難いといった前記繊維層の特性が顕著
に現れてしまうため、３軸組物層や２軸組物層による安
定した品質を維持させるという特性を発現できないとい
った問題を有し、２０％を下回ると、質量の増加を回避
させ、且つ、高い捩り剛性や充分な潰れ強度を発現させ
るといった効果を得られないためである。Further, in the fiber layer formed by winding up a prepreg sheet made by aligning the reinforcing fibers and impregnating the resin, the composition ratio of the fiber layer to the entire volume of the shaft constituting the golf club is 20%. It is desirably about 80%. If it exceeds 80%, the characteristics of the fiber layer such that the bending rigidity of the shaft is hardly uniform in the circumferential direction and a shaft of stable quality is hardly obtained, so that the triaxial braided layer or the biaxial braid There is a problem that the property of maintaining a stable quality by the material layer cannot be exhibited, and if it is less than 20%, the effect of avoiding an increase in mass, and exhibiting high torsional rigidity and sufficient crushing strength is obtained. This is because it cannot be done.
【００２３】本発明のゴルフクラブ用シャフトは、樹脂
を含浸させた強化繊維の束からなる糸を編み組みして構
成された組物層によって、安定した品質を維持したまま
高い曲げ剛性を発現させ、さらに強化繊維を引揃え、樹
脂を含浸させてなるプリプレグシートを巻回して形成さ
れた繊維層によって、質量の増大を回避させながら、高
い捩り剛性や、充分な潰れ強度を発現させたことによっ
て、従来のゴルフクラブ用シャフトでは実現できなかっ
た曲げ剛性、捩り剛性、潰れ強度といった全ての要求特
性を満足させることが可能となった。つまり、前記３軸
組物層や前記２軸組物層などが複数層積層された組物層
に、前記繊維層を組み合わせたことに加えて、さらに、
それぞれの組糸や強化繊維を最適な配向角度で限定的に
集中して構成させたことで、軽量性を維持しながら充分
な潰れ強度を確保するとともに、高い曲げ剛性や捩り剛
性を必要とする上級者にも満足が得られるゴルフクラブ
用シャフトを提供することができるものである。In the golf club shaft of the present invention, a braid layer formed by braiding a yarn comprising a bundle of reinforcing fibers impregnated with a resin exhibits high bending rigidity while maintaining stable quality. In addition, by arranging reinforcing fibers and winding a prepreg sheet impregnated with resin, a fiber layer formed by forming high torsional rigidity and sufficient crushing strength while avoiding increase in mass Further, it has become possible to satisfy all the required characteristics such as bending rigidity, torsional rigidity, and crushing strength which cannot be realized by the conventional golf club shaft. That is, in addition to combining the fiber layer with a braided layer in which the triaxial braided layer and the biaxial braided layer are stacked in a plurality of layers,
By concentrating each braid and reinforcing fiber at an optimal orientation angle, it is necessary to secure sufficient crushing strength while maintaining light weight and high bending rigidity and torsional rigidity. It is possible to provide a golf club shaft that can satisfy even advanced users.
【００２４】[0024]
【発明の効果】以上により、本発明におけるゴルフクラ
ブ用シャフトにおいては、樹脂を含浸させた強化繊維の
束からなる糸を編み組みして構成された組物層によって
形成されたゴルフクラブ用シャフトに、強化繊維を引揃
え、樹脂を含浸させてなるプリプレグシートを巻回して
形成された繊維層を組み合わせ、構成させたことで、ゴ
ルフクラブ用シャフトの質量の増大を押さえたまま、曲
げ剛性や捩り剛性を向上させるとともに、安定した品質
のゴルフクラブ用シャフトが得られる効果を奏する。As described above, in the golf club shaft according to the present invention, a golf club shaft formed by a braided layer formed by braiding a yarn made of a bundle of reinforcing fibers impregnated with a resin. By arranging reinforcing fibers, winding a prepreg sheet impregnated with resin, and combining and forming a fiber layer, the bending rigidity and torsion can be maintained while suppressing an increase in the mass of the golf club shaft. The effect of improving rigidity and obtaining a golf club shaft of stable quality is achieved.
【００２５】さらに、前記組物層が、３軸組物層や２軸
組物層などから構成され、前記３軸組物層や前記２軸組
物層における組糸の配向角度を、０°より大きく２０°
以下と構成させたことで、該配向角度がシャフト軸方向
に近づく事となり、よって、上級者にも対応できる高い
曲げ剛性が得られる効果を奏する。Further, the braid layer is composed of a triaxial braid layer or a biaxial braid layer, and the orientation angle of the braid in the triaxial braid layer or the biaxial braid layer is 0 °. Greater than 20 °
With the configuration described below, the orientation angle becomes closer to the shaft axis direction, so that an effect of obtaining high bending rigidity that can be handled by advanced users can be obtained.
【００２６】また、前記繊維層を構成する強化繊維の配
向角度が３０°〜９０°と構成されたことで、前記３軸
組物層や前記２軸組物層よって得られた曲げ剛性に加え
て、高い捩り剛性や潰れ強度を質量の増大を回避させな
がら得られる効果を奏する。Further, since the orientation angle of the reinforcing fibers constituting the fiber layer is set to 30 ° to 90 °, in addition to the bending rigidity obtained by the triaxial braided layer and the biaxial braided layer, Thus, an effect is obtained in which high torsional rigidity and crushing strength can be obtained while avoiding an increase in mass.
【００２７】また、前記繊維層の構成比率が、シャフト
全体の２０％〜８０％とした事によって、安定した品質
を維持できるといった効果を奏する。[0027] Further, when the composition ratio of the fiber layer is set to 20% to 80% of the entire shaft, an effect that stable quality can be maintained can be obtained.
【図１】本発明のゴルフクラブ用シャフトにおける実施
例を表わす説明図である。FIG. 1 is an explanatory view showing an embodiment of a golf club shaft of the present invention.
【図２】従来例を示す説明図である。FIG. 2 is an explanatory diagram showing a conventional example.
【図３】従来例を示す説明図である。FIG. 3 is an explanatory diagram showing a conventional example.
１ ゴルフクラブ用シャフト １１ シャフト軸 １２ 組糸 １３ 中央糸 １４ ３軸組物層 １６ 第一繊維層 １７ 第二繊維層 １８ ２軸組物層 １９ 組物層 ２０ 繊維層 ５０ ゴルフクラブ用シャフト ５１ シャフト軸 ５２ 組糸 ５３ 中央糸 ５４ ３軸組物層 ５５ 配向角度 DESCRIPTION OF SYMBOLS 1 Golf club shaft 11 Shaft shaft 12 Braided yarn 13 Central yarn 14 Triaxial braided layer 16 First fibrous layer 17 Second fibrous layer 18 Biaxial braided layer 19 Braided layer 20 Fiber layer 50 Golf club shaft 51 Shaft Axis 52 Braided yarn 53 Center yarn 54 Triaxial braided layer 55 Orientation angle
Claims (7)
トにおいて、樹脂を含浸させた強化繊維の束からなる糸
を編み組みして構成された組物層と、引き揃えられた強
化繊維に樹脂を含浸させてなるプリプレグシートを巻回
して構成された繊維層とからなるゴルフクラブ用シャフ
ト。1. A golf club shaft made of a fiber-reinforced resin, a braided layer formed by braiding a yarn made of a bundle of reinforcing fibers impregnated with a resin, and a resin in the aligned reinforcing fibers. A golf club shaft comprising a fiber layer formed by winding a prepreg sheet impregnated.
称の配向角度を有する組糸と前記シャフト軸に対し０°
の配向角度を有する中央糸とが編み組みして構成された
３軸組物層と、前記シャフト軸に対し左右対称の配向角
度を有する組糸のみで構成された２軸組物層とからなる
請求項１記載のゴルフクラブ用シャフト。2. The braid layer has a braid having an symmetrical orientation angle with respect to a shaft axis and a 0 ° angle with respect to the shaft axis.
A three-axis braided layer formed by braiding a central yarn having an orientation angle of, and a two-axis braided layer composed only of a braided yarn having a symmetrical orientation angle with respect to the shaft axis. The golf club shaft according to claim 1.
称の配向角度を有する組糸と前記シャフト軸に対し０°
の配向角度を有する中央糸とが編み組みして構成された
３軸組物層である請求項１記載のゴルフクラブ用シャフ
ト。3. The braid layer has a symmetrical orientation angle with respect to a shaft axis and a braided yarn at 0 ° with respect to the shaft axis.
The golf club shaft according to claim 1, wherein the shaft is a triaxial braided layer formed by braiding a central yarn having an orientation angle of:
右対称の配向角度を有する前記組糸のみで構成された２
軸組物層である請求項１記載のゴルフクラブ用シャフ
ト。4. The braid layer is composed of only the braid having a symmetrical orientation angle with respect to the shaft axis.
The golf club shaft according to claim 1, wherein the shaft is a frame layer.
し０°より大きく２０°以下に配向されていることを特
徴とする請求項２、３又は４記載のゴルフクラブ用シャ
フト。5. The golf club shaft according to claim 2, wherein the orientation angle of the braid is greater than 0 ° and less than 20 ° with respect to the shaft axis.
度は、シャフト軸に対し３０°〜９０°に配向されてい
ることを特徴とする請求項１、２、３、４又は５記載の
ゴルフクラブ用シャフト。6. The fiber according to claim 1, 2, 3, 4, or 5, wherein an orientation angle of the reinforcing fiber constituting the fiber layer is oriented at 30 ° to 90 ° with respect to a shaft axis. Golf club shaft.
体積の２０％〜８０％であることを特徴とする請求項
１、２、３、４、５、又は６記載のゴルフクラブ用シャ
フト。7. The golf club shaft according to claim 1, wherein the composition ratio of the fiber layer is 20% to 80% of the total volume of the shaft.