JP2002167308A - Gel type hairdressing agent - Google Patents
Gel type hairdressing agentInfo
- Publication number
- JP2002167308A JP2002167308A JP2000366665A JP2000366665A JP2002167308A JP 2002167308 A JP2002167308 A JP 2002167308A JP 2000366665 A JP2000366665 A JP 2000366665A JP 2000366665 A JP2000366665 A JP 2000366665A JP 2002167308 A JP2002167308 A JP 2002167308A
- Authority
- JP
- Japan
- Prior art keywords
- copolymer
- hair
- mass
- gel
- monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は整髪保持効果に優
れ、毛髪にツヤを与え、乾燥が早く、更に使用時のべた
つきが極めて少なく、フレーキング(被膜が剥離し白粒
状になる)が起こらず、保存安定性にも優れるゲル状整
髪料に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention has an excellent hair styling-retaining effect, imparts gloss to hair, dries quickly, has very little stickiness during use, and does not cause flaking (the film peels off and becomes white granules). And a gel hair styling material having excellent storage stability.
【0002】[0002]
【従来の技術】従来、整髪料として、ヘアーリクイド、
ヘアークリーム、ヘアーチック、ポマード、ヘアースプ
レー、ヘアーフォーム、セットローション、ブローロー
ション等が使用されてきた。これらの成分としては、油
性成分や被膜形成成分が用いられてきた。2. Description of the Related Art Conventionally, hair liquids, hair liquids,
Hair creams, hair tics, pomades, hair sprays, hair foams, set lotions, blow lotions and the like have been used. As these components, oil components and film-forming components have been used.
【0003】しかしながら、油脂、ワックス、ポリオキ
シアルキレンアルキルエーテル系化合物又はそのリン酸
塩等の油性成分を整髪剤成分とするヘアーリクイド、ヘ
アークリーム、ヘアーチック、ポマード等は、整髪保持
効果が弱い、使用時にべたつく、洗い落ちが悪い、仕上
がりが重く汚れた印象を与える、等の欠点があった。[0003] However, hair liquids, hair creams, hair tics, pomades and the like, which use oily components such as oils and fats, waxes, polyoxyalkylene alkyl ether compounds or their phosphates as hair styling ingredients, have weak hair styling retention effects. There were drawbacks such as stickiness during use, poor wash-off, and a heavy finish giving a dirty impression.
【0004】また、被膜形成能を有する高分子化合物と
しては、例えば(メタ)アクリル酸アルキル/ジアセト
ンアクリルアミド共重合体(プラスサイズ、互応化学社
製他)、酢酸ビニル/クロトン酸共重合体(レジン28
−1310、NSC社製他)、酢酸ビニル/クロトン酸
/ビニルネオデカネート共重合体(28−2930、N
SC社製 他)、メチルビニルエーテルマレイン酸ハー
フエステル(ガントレッツES、ISP社製 他)等の
アニオン性高分子化合物や、ジアルキルアミノエチルメ
タクリエート重合体の酢酸両性化物(ユカフォーマー、
三菱化学社製 他)、アクリル酸オクチルアクリルアミ
ド/アクリル酸ヒドロキシプロピル/メタクリル酸ブチ
ルアミノエチル共重合体(AMPHOMER、NSC社
製他)等の両性高分子化合物や、ビニルピロリドン/ジ
メチルアミノエチルメタクリレートの4級化物(GAF
QUAT、ISP社製 他)等のカチオン性高分子化合
物や、ポリビニルピロリドン(ルビスコールK、BAS
F社製 他)、ビニルピロリドン/酢酸ビニル共重合体
(ルビスコールVA、BASF社製 他)、ビニルピロ
リドン/ジメチルアミノエチルメタクリレート共重合体
(コポリマー937、ISP社製 他)等のノニオン高
分子化合物がある。しかし、これらの高分子化合物を整
髪剤成分とするヘアースプレー、ヘアーフォーム、セッ
トローション、ブローローションは、毛髪表面に硬い被
膜を形成し、整髪保持効果は良好であるが、整髪後の髪
のつやがなくなる、ごわつく、フレーキング(被膜が剥
離し白粒状になる)を生じる等の欠点があった。Examples of the polymer compound having a film-forming ability include an alkyl (meth) acrylate / diacetone acrylamide copolymer (plus size, manufactured by Ryo Kagaku Co., Ltd.), a vinyl acetate / crotonic acid copolymer ( Resin 28
1310, manufactured by NSC, etc.), vinyl acetate / crotonic acid / vinyl neodecanoate copolymer (28-2930, N
SC), methyl vinyl ether maleic acid half ester (Gantrez ES, ISP, etc.), and an acetic acid amphoteric dialkylaminoethyl methacrylate polymer (Yuka Former,
Amphoteric polymer compounds such as octylacrylamide acrylate / hydroxypropyl acrylate / butylaminoethyl methacrylate copolymer (AMPHOMER, NSC, etc.), and vinylpyrrolidone / dimethylaminoethyl methacrylate. Grade (GAF
Cationic polymer compounds such as QUAT, ISP, etc., and polyvinylpyrrolidone (Rubiscol K, BAS
Nonionic polymer compounds such as vinylpyrrolidone / vinyl acetate copolymer (rubiscol VA, manufactured by BASF, etc.), vinylpyrrolidone / dimethylaminoethyl methacrylate copolymer (copolymer 937, manufactured by ISP, etc.) There is. However, hair sprays, hair foams, set lotions, and blow lotions containing these high molecular compounds as hair styling ingredients form a hard film on the hair surface and have a good hair styling retention effect, but have a glossy hair after hair styling. There are disadvantages such as disappearance, stiffness, and flaking (the film peels off and becomes white particles).
【0005】従来、ゲル状整髪料は、カルボキシビニル
ポリマーを増粘剤として配合し、整髪基剤として非イオ
ン性高分子化合物を配合するのが一般的であったが、高
湿度下での整髪保持性が悪い、フレーキングを生じる等
の欠点があった。このため、従来、種々の提案がなさ
れ、特定の分子量のポリビニルピロリドンを配合したり
(特開平10−87448号公報)、ポリビニルピロリ
ドンとヒドロキシプロピルグアーガムとを組み合わせた
り(特開2000−34212号公報)、両性高分子と
セルロース誘導体とを組み合わせたり(特開平6−92
827号公報)、特定量のエタノールとアニオン性樹脂
を用いる(特許第2968984号公報)ゲル状整髪料
が提案されているが、ツヤが損なわれたり、べたつきが
増大したり、保存安定性が損なわれる等の欠点があっ
た。Conventionally, a gel-like hairdressing composition generally contains a carboxyvinyl polymer as a thickening agent and a nonionic polymer compound as a hairdressing base. There were drawbacks such as poor retention and flaking. For this reason, various proposals have hitherto been made, such as blending polyvinylpyrrolidone with a specific molecular weight (Japanese Patent Laid-Open No. 10-87448), or combining polyvinylpyrrolidone and hydroxypropyl guar gum (Japanese Patent Laid-Open No. 2000-34212). Or a combination of an amphoteric polymer and a cellulose derivative (JP-A-6-92
No. 827), and a gel-like hairdressing agent using a specific amount of ethanol and an anionic resin (Japanese Patent No. 2968984) has been proposed, but the gloss is impaired, the stickiness is increased, and the storage stability is impaired. There were drawbacks such as
【0006】[0006]
【発明が解決しようとする課題】したがって、斯かる状
況下、本発明の目的は、整髪保持効果に優れ、毛髪にツ
ヤを与え、乾燥が早く、更に使用時のべたつきが極めて
少なく、保存安定性にも優れるゲル状整髪料を提供する
ことにある。SUMMARY OF THE INVENTION Accordingly, under these circumstances, an object of the present invention is to provide a hair styling-retaining effect, which gives the hair a luster, that it dries quickly, that it has very little stickiness when used, and that its storage stability is high. Another object of the present invention is to provide a gel-like hair styling that is excellent in the above.
【0007】[0007]
【課題を解決するための手段】上記目的を達成するため
の、本発明の請求項1は、次の成分(A)〜(D)を含
有することを特徴とするゲル状整髪料である。 (A)共重合成分として、下記一般式(1)で表される
長鎖アルキルアクリレートモノマー1〜50質量%と、Means for Solving the Problems To achieve the above object, claim 1 of the present invention is a gel hairdressing composition containing the following components (A) to (D). (A) 1 to 50% by mass of a long-chain alkyl acrylate monomer represented by the following general formula (1) as a copolymer component;
【0008】[0008]
【化2】 Embedded image
【0009】(但し、Rは炭素数10〜30のアルキル
基であり、R’は水素又はメチル基である。) オレフィン性不飽和カルボン酸モノマー99〜50質量
%とを含むモノマー混合物からの共重合体 (B)該共重合体の中和剤 (C)水溶性アルコール (D)被膜形成能を有するアニオン性高分子化合物(However, R is an alkyl group having 10 to 30 carbon atoms, and R 'is a hydrogen or methyl group.) A monomer mixture containing 99 to 50% by mass of an olefinically unsaturated carboxylic acid monomer is used. Polymer (B) Neutralizing agent for the copolymer (C) Water-soluble alcohol (D) Anionic polymer compound capable of forming a film
【0010】また、請求項2は、更に(E)被膜形成能
を有する非イオン性高分子化合物を含有することを特徴
とする請求項1に記載のゲル状整髪料である。また、請
求項3は、更に(F)非イオン性界面活性剤を含有する
ことを特徴とする請求項1又は請求項2に記載のゲル状
整髪料である。A second aspect of the present invention is the gel hairdressing composition according to the first aspect, further comprising (E) a nonionic polymer compound having a film-forming ability. A third aspect of the present invention is the gel hairdressing composition according to the first or second aspect, further comprising (F) a nonionic surfactant.
【0011】すなわち、本発明は、(A)アルキルアク
リレートモノマーとオレフィン性不飽和カルボン酸モノ
マーとからの共重合体及びその中和剤と、被膜形成能を
有するアニオン性高分子化合物他とを配合することを特
徴とするゲル状整髪料である。That is, the present invention comprises (A) a copolymer of an alkyl acrylate monomer and an olefinically unsaturated carboxylic acid monomer, a neutralizing agent thereof, and an anionic polymer compound having a film forming ability. It is a gel-like hairdressing characterized by performing.
【0012】[0012]
【発明の実施の形態】以下、本発明の構成を詳述する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The configuration of the present invention will be described below in detail.
【0013】本発明に使用する(A)成分の共重合体成
分である長鎖アルキルアクリレートモノマーとしては、
例えばデシルアクリレート、ラウリルアクリレート、パ
ルミチルアクリレート、パルミチルアクリレート、ベヘ
ニルアクリレート等の炭素数10〜30のアルキルアク
リレート、好ましくは炭素数12〜22のアルキルアク
リレートそして相当するメタクリレートの群からから選
ばれる1種以上のモノマーであり、また、オレフィン性
不飽和モノマーとしては、例えばアクリル酸、メタクリ
ル酸、エタアクリル酸、α−クロロ−アクリル酸、α−
フェニルアクリル酸、ソルビン酸、ケイ皮酸、マレイン
酸、フマル酸等、又は無水マレイン酸等のオレフィン系
の二重結合及び少なくとも一つのカルボキシル基を含む
重合性化合物の群から選ばれる1種以上のモノマーであ
り、好ましくは入手し易く優れた重合能力を持つアクリ
ル酸が挙げられる。The long-chain alkyl acrylate monomer which is a copolymer component of the component (A) used in the present invention includes:
For example, one selected from the group consisting of alkyl acrylates having 10 to 30 carbon atoms such as decyl acrylate, lauryl acrylate, palmityl acrylate, palmityl acrylate, and behenyl acrylate, preferably alkyl acrylates having 12 to 22 carbon atoms and corresponding methacrylates. The above monomers, and as the olefinically unsaturated monomer, for example, acrylic acid, methacrylic acid, ethacrylic acid, α-chloro-acrylic acid, α-
Phenylacrylic acid, sorbic acid, cinnamic acid, maleic acid, fumaric acid or the like, or one or more kinds selected from the group of polymerizable compounds containing at least one carboxyl group such as an olefinic double bond such as maleic anhydride. Acrylic acid, which is a monomer, and preferably is easily available and has excellent polymerization ability.
【0014】長鎖アルキルアクリレートとオレフィン性
不飽和カルボン酸モノマーとからの共重合体としては、
上記の必須成分である長鎖アルキルアクリレートモノマ
ーとオレフィン性不飽和カルボン酸モノマーの両モノマ
ー以外に、共重合体の特性を調整するためにメチレンビ
スアクリルアミド、アリルアクリレート、メタリルメタ
クリレート、ジビニルエーテル、アリルショ糖、トリメ
チロールプロパントリアクリレート、トリメチロールプ
ロパントリメタクリレート、グリセリルトリアクリレー
ト等のオレフィン系多官能性モノマーを配合して重合し
た架橋構造をもつ共重合体をも含み、本発明で使用する
ことができる。The copolymer of a long-chain alkyl acrylate and an olefinically unsaturated carboxylic acid monomer includes:
In addition to the long-chain alkyl acrylate monomer and olefinically unsaturated carboxylic acid monomer, which are essential components, methylene bisacrylamide, allyl acrylate, methallyl methacrylate, divinyl ether, allyl Sugars, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, glyceryl triacrylate, and other copolymers having a crosslinked structure obtained by mixing and polymerizing olefinic polyfunctional monomers such as acrylate can also be used in the present invention. .
【0015】該オレフィン系多官能性モノマーの配合量
としては、モノマー混合物総量に対して約0.01〜約
4質量%が好ましく、更に好ましくは0.2〜1.0質
量%である。これら上記の共重合体は、例えば特開昭5
1−6190号公報、特開平4−39312号公報等に
記載された方法で製造することができる。製造される共
重合体の平均分子量としては500,000〜5,00
0,000のものが好ましい。そして、これら共重合体
は架橋構造の有無にかかわらず、下記中和剤と併用する
ことによって水、アルコール水溶液、多価アルコール水
溶液に溶解する。また、これら共重合体の具体的例とし
ては、ペミュレン(PEMULEN)、カーボポール1
342(いずれもB.F.GOODRICH社製)の商
品名で市販されている。The amount of the olefin-based polyfunctional monomer is preferably about 0.01 to about 4% by mass, more preferably 0.2 to 1.0% by mass, based on the total amount of the monomer mixture. These copolymers are described in, for example,
It can be produced by a method described in JP-A No. 1-6190, JP-A-4-39312 or the like. The average molecular weight of the produced copolymer is 500,000 to 5,000.
000 is preferred. Then, regardless of the presence or absence of a crosslinked structure, these copolymers are dissolved in water, an aqueous alcohol solution, or an aqueous polyhydric alcohol solution by using together with the following neutralizing agent. Specific examples of these copolymers include PEMULEN, Carbopol 1
342 (both manufactured by BF GOODRICH).
【0016】尚、本発明における上記共重合体の配合量
としては、ゲル状整髪料の組成物全量に対して0.05
〜2.0質量%が好ましい。この範囲であると、使用上
好ましい粘性が得られる。In the present invention, the amount of the copolymer is 0.05 to 0.05% based on the total amount of the gel hairdressing composition.
~ 2.0 mass% is preferred. Within this range, a preferable viscosity for use is obtained.
【0017】本発明に使用する(B)成分の中和剤とし
ては、例えばジイソプロパノールアミン、トリエタノー
ルアミン、アミノメチルプロパノール等のアルカノール
アミン類、アンモニア、水酸化カリウム、水酸化ナトリ
ウム、塩基性アミノ酸類(リジン、アルギニン等)、塩
基性ポリペプチド等が挙げられる。中和剤の配合量は、
(A)成分の共重合体のカルボキシル基を50〜100
%当量中和する様に調整する。The neutralizing agent of the component (B) used in the present invention includes, for example, alkanolamines such as diisopropanolamine, triethanolamine and aminomethylpropanol, ammonia, potassium hydroxide, sodium hydroxide, basic amino acids (Such as lysine and arginine) and basic polypeptides. The amount of the neutralizing agent
The carboxyl group of the copolymer (A) is 50 to 100.
Adjust to neutralize by% equivalent.
【0018】本発明における(C)成分の水溶性アルコ
ールとは、メタノール、エタノール、プロパノール、イ
ソプロパノール等の低級一価アルコール、グリセリン、
エチレングリコール、ポリエチレングリコール(平均分
子量が1000以下)、プロピレングリコール、1,3
−ブチレングリコール、ジプロピレングリコール、ソル
ビトール、マンニトール等の多価アルコール(平均分子
量が60〜1000)等が挙げられる。水溶性アルコー
ルの好ましい配合量はゲル状整髪料全量に対し0.8〜
60質量%であり、更に好ましくは3.0〜40.0質
量%である。0.8質量%未満であると塗布時の伸び、
フレーキングの無さの点で悪くなる場合があり、60質
量%を越えるとべたつきを生じたり、保存安定性が悪く
なる場合がある。また、水溶性アルコールは、それぞれ
単独又は2種以上を混合して使用することができる。The water-soluble alcohol of the component (C) in the present invention includes lower monohydric alcohols such as methanol, ethanol, propanol and isopropanol, glycerin,
Ethylene glycol, polyethylene glycol (average molecular weight of 1000 or less), propylene glycol, 1,3
-Polyhydric alcohols (average molecular weight: 60 to 1000) such as butylene glycol, dipropylene glycol, sorbitol, and mannitol. The preferred compounding amount of the water-soluble alcohol is 0.8 to
It is 60% by mass, and more preferably 3.0 to 40.0% by mass. If it is less than 0.8% by mass, elongation at the time of application,
In some cases, there is no flaking, and when it exceeds 60% by mass, stickiness may occur or storage stability may deteriorate. In addition, the water-soluble alcohols can be used alone or in combination of two or more.
【0019】本発明における(D)成分の被膜形成能を
有するアニオン性高分子化合物としては、例えば、(メ
タ)アクリル酸アルキル/ジアセトンアクリルアミド共
重合体(プラスサイズ、互応化学工業社製)、酢酸ビニ
ル/クロトン酸共重合体(レジン28−1310、NS
C社製)、酢酸ビニル/クロトン酸/ビニルネオデカネ
ート共重合体(28−2930、NSC社製)、メチル
ビニルエーテルマレイン酸ハーフエステル(ガントレッ
ツES、ISP社製)、t−ブチルアクリレート/アク
リル酸エチル/メタクリル酸共重合体(ルビマー、BA
SF社製)、ビニルピロリドン/ビニルアセテート/ビ
ニルプロピオネート共重合体(ルビスコールVAP、B
ASF社製)、ビニルアセテート/クロトン酸共重合体
(ルビセットCA、BASF社製)、ビニルアセテート
/クロトン酸/ビニルピロリドン共重合体(ルビセット
CAP、BASF社製)、ビニルピロリドン/アクリレ
ート共重合体(ルビフレックス、BASF社製)、アク
リレート/アクリルアミド共重合体(ウルトラホール
ド、BASF社製)、ビニルアセテート/ブチルマレア
ート/イソボルニルアクリラート共重合体(アドバンテ
ージ、ISP社製)等が挙げられる。中でも、(メタ)
アクリル酸アルキル/ジアセトンアクリルアミド共重合
体が整髪保持効果の面で最も望ましい。Examples of the anionic polymer compound having a film-forming ability of the component (D) in the present invention include an alkyl (meth) acrylate / diacetone acrylamide copolymer (plus size, manufactured by Yoyo Chemical Industry Co., Ltd.), Vinyl acetate / crotonic acid copolymer (Resin 28-1310, NS
C), vinyl acetate / crotonic acid / vinyl neodecanoate copolymer (28-2930, manufactured by NSC), methyl vinyl ether maleate half ester (Gantrez ES, manufactured by ISP), t-butyl acrylate / acrylic acid Ethyl / methacrylic acid copolymer (Rubimer, BA
SF), vinylpyrrolidone / vinyl acetate / vinyl propionate copolymer (Ruviscol VAP, B
ASF), vinyl acetate / crotonic acid copolymer (Rubiset CA, manufactured by BASF), vinyl acetate / crotonic acid / vinylpyrrolidone copolymer (Rubiset CAP, manufactured by BASF), vinylpyrrolidone / acrylate copolymer ( Rubiflex, manufactured by BASF), acrylate / acrylamide copolymer (Ultrahold, manufactured by BASF), vinyl acetate / butyl maleate / isobornyl acrylate copolymer (Advantage, manufactured by ISP), and the like. Among them, (meta)
Alkyl acrylate / diacetone acrylamide copolymer is most desirable in terms of hair styling retention effect.
【0020】本発明における被膜形成能を有するアニオ
ン性高分子化合物の配合量は、ゲル状整髪料全量に対し
て0.1〜10質量%が好ましい。この範囲であると、
優れた整髪保持効果、使用時のべたつきが無い等の特性
が得られる。また、上記のアニオン性高分子化合物は、
それぞれ単独で又は2種以上を混合して使用することが
できる。The amount of the anionic polymer compound having a film-forming ability in the present invention is preferably 0.1 to 10% by mass based on the total amount of the gel hairdressing composition. Within this range,
Characteristics such as an excellent hair styling retention effect and no stickiness during use are obtained. Further, the above anionic polymer compound,
Each can be used alone or in combination of two or more.
【0021】本発明において、更に(E)成分として被
膜形成能を有する非イオン性高分子化合物を配合する
と、毛髪につやを与える効果がより向上する。In the present invention, when a nonionic polymer compound having a film-forming ability is further blended as the component (E), the effect of giving gloss to hair is further improved.
【0022】本発明における被膜形成能を有する非イオ
ン性高分子化合物としては、例えば、ポリビニルピロリ
ドン(ルビスコールK、BASF社製)、ビニルピロリ
ドン/酢酸ビニル共重合体(ルビスコールVA、BAS
F社製)、ビニルピロリドン/ジメチルアミノエチルメ
タクリレート共重合体(コポリマー937、ISP社
製)、ビニルピロリドン/ジメチルアミノプロピルメタ
クリルアミド共重合体(スタイリーゼCC−10、IS
P社製)、ビニルカプロラクタム/ビニルピロリドン/
ジメチルアミノエチルメタクリレート共重合体(コポリ
マーVC713、ISP社製)、ビニルカプロラクタム
/ビニルピロリドン/ジメチルアミノプロピルメタクリ
ルアミド共重合体(アクアフレックスSF−40、IS
P社製)等が挙げられる。また、上記の非イオン性高分
子化合物は、それぞれ単独で又は2種以上を混合して使
用することができるExamples of the nonionic polymer compound having a film-forming ability in the present invention include polyvinylpyrrolidone (Rubiscol K, manufactured by BASF), vinylpyrrolidone / vinyl acetate copolymer (Rubiscol VA, BAS)
F), vinylpyrrolidone / dimethylaminoethyl methacrylate copolymer (Copolymer 937, manufactured by ISP), vinylpyrrolidone / dimethylaminopropyl methacrylamide copolymer (Stylase CC-10, IS
P), vinylcaprolactam / vinylpyrrolidone /
Dimethylaminoethyl methacrylate copolymer (Copolymer VC713, manufactured by ISP), vinylcaprolactam / vinylpyrrolidone / dimethylaminopropylmethacrylamide copolymer (Aquaflex SF-40, IS
P company). The above-mentioned nonionic polymer compounds can be used alone or in combination of two or more.
【0023】本発明における被膜形成能を有する非イオ
ン性高分子化合物の配合量は、組成物全量に対して0.
05〜5質量%が好ましい。この範囲であると、毛髪に
ツヤを与える効果の向上が得られる。In the present invention, the compounding amount of the nonionic polymer compound having a film-forming ability is 0.1 to the total amount of the composition.
It is preferably from 0.5 to 5% by mass. Within this range, the effect of giving the hair a gloss can be improved.
【0024】また、本発明において、(D)成分と
(E)成分の配合量の比(D/E)は、質量比で0.5
以上であることが望ましい。(D)成分と(E)成分の
配合量の比(D/E)が0.5未満であると、べたつき
感やフレーキングが生じる場合がある。In the present invention, the ratio (D / E) of the amounts of the components (D) and (E) is 0.5% by mass.
It is desirable that this is the case. If the ratio (D / E) of the blending amount of the component (D) and the component (E) is less than 0.5, sticky feeling and flaking may occur.
【0025】本発明で用いられる(F)成分の非イオン
性界面活性剤としては、例えばソルビタン脂肪酸エステ
ル、グリセリン脂肪酸エステル、ポリグリセリン脂肪酸
エステル、プロピレングリコール脂肪酸エステル、ペン
タエリスリトール脂肪酸エステル、ポリオキシエチレン
ソルビタン脂肪酸エステル、ポリオキシエチレンソルビ
ット脂肪酸エステル、ポリオキシエチレングリセリン脂
肪酸エステル、ポリエチレングリコール脂肪酸エステ
ル、ポリオキシエチレンアルキルエーテル、ポリオキシ
エチレンフィトステロール、ポリオキシエチレンフィト
スタノール、ポリオキシエチレンポリオキシプロピレン
アルキルエーテル、ポリオキシエチレンアルキルフェニ
ルエーテル、ポリオキシエチレンヒマシ油、ポリオキシ
エチレン硬化ヒマシ油、ポリオキシエチレンラノリン、
ポリオキシエチレンラノリンアルコール、ポリオキシエ
チレンミツロウ誘導体、ポリオキシエチレンアルキルア
ミン、ポリオキシエチレン脂肪酸アミド、ポリオキシエ
チレンアルキルフェニルホルムアルデヒド縮合物単一鎖
長ポリオキシエチレンアルキルエーテル、アルキルグル
コシド、ポリオキシアルキレンアルキルグルコシド等が
挙げられ、これらのうち1種又は2種以上が用いられ
る。Examples of the nonionic surfactant (F) used in the present invention include sorbitan fatty acid ester, glycerin fatty acid ester, polyglycerin fatty acid ester, propylene glycol fatty acid ester, pentaerythritol fatty acid ester, and polyoxyethylene sorbitan. Fatty acid ester, polyoxyethylene sorbite fatty acid ester, polyoxyethylene glycerin fatty acid ester, polyethylene glycol fatty acid ester, polyoxyethylene alkyl ether, polyoxyethylene phytosterol, polyoxyethylene phytostanol, polyoxyethylene polyoxypropylene alkyl ether, polyoxy Ethylene alkyl phenyl ether, polyoxyethylene castor oil, polyoxyethylene hardened castor , Polyoxyethylene lanolin,
Polyoxyethylene lanolin alcohol, polyoxyethylene beeswax derivative, polyoxyethylene alkylamine, polyoxyethylene fatty acid amide, polyoxyethylene alkylphenylformaldehyde condensate single chain length polyoxyethylene alkyl ether, alkyl glucoside, polyoxyalkylene alkyl glucoside And the like, and one or more of these are used.
【0026】本発明で用いられる非イオン性界面活性剤
の好ましいHLB値としては8.0〜18.0であり、
より好ましくは10.0〜16.0である。非イオン性
界面活性剤のHLB値が好ましい範囲から外れると、保
存安定性が悪くなったり、べたつきを生じる場合があ
る。The preferred HLB value of the nonionic surfactant used in the present invention is 8.0 to 18.0,
More preferably, it is 10.0 to 16.0. When the HLB value of the nonionic surfactant is out of the preferred range, storage stability may be deteriorated or stickiness may occur.
【0027】本発明における非イオン性界面活性剤の好
ましい配合量としては0.01〜3.0質量%であり、
より好ましくは、0.1〜1.0質量%である。0.0
1質量%未満であると保存安定性が悪くなる場合があ
り、3.0%質量を超えるとべたつきを感じる場合があ
る。The preferred amount of the nonionic surfactant in the present invention is 0.01 to 3.0% by mass.
More preferably, it is 0.1 to 1.0% by mass. 0.0
If it is less than 1% by mass, storage stability may be deteriorated, and if it exceeds 3.0% by mass, stickiness may be felt.
【0028】本発明のゲル状整髪料には、本発明の効果
を損なわない範囲であれば、上記必須成分の他に、植物
抽出物、油性物質、シリコーン及びその誘導体、イオン
性界面活性剤、ガム質、天然水溶性化合物及びその誘導
体、防腐剤、キレート剤、酸化防止剤、紫外線吸収剤、
pH調整剤、色素、香料等を配合することも可能であ
る。これらの中で特に保湿、コンディショニング効果、
なめらかさの付与等の面で植物抽出物が好ましく、特に
好ましくは、セージ、カモミラ、ボダイジュ、アロエ、
ハマメリス、ローズマリー、ニンジン、ビワ、モモ、バ
ラ、ヨモギ、レンゲソウ、ユキノシタ、ゴボウ、レモ
ン、マロニエ、スギナ、ラベンダー、インチンコウ、ヤ
グルマソウの抽出物である。In the gel hairdressing composition of the present invention, in addition to the above essential components, a plant extract, an oily substance, silicone and its derivatives, an ionic surfactant, as long as the effects of the present invention are not impaired. Gum, natural water-soluble compounds and their derivatives, preservatives, chelating agents, antioxidants, ultraviolet absorbers,
It is also possible to mix a pH adjuster, a dye, a fragrance and the like. Of these, especially moisturizing and conditioning effects,
Plant extracts are preferred in terms of imparting smoothness, and particularly preferably, sage, chamomile, bodaige, aloe,
It is an extract of hamamelis, rosemary, carrot, loquat, peach, rose, mugwort, vetch, saxifrage, burdock, lemon, marronnier, horsetail, lavender, cinnamon, and cornflower.
【0029】[0029]
【実施例】以下に実施例、比較例を挙げて本発明を説明
する。尚、本発明は、これらにより限定されるものでは
ない。The present invention will be described below with reference to examples and comparative examples. Note that the present invention is not limited by these.
【0030】実施例、比較例に示した整髪保持効果、官
能試験の試験方法は下記の通りである。尚、以下の表に
示す組成物の配合量は、それぞれ質量%で示す。The test methods of the hair styling retention effect and the sensory test shown in Examples and Comparative Examples are as follows. In addition, the compounding quantity of the composition shown in the following tables is each shown by mass%.
【0031】(1)整髪保持効果 長さ15cm、重さ1gの毛束にゲル状整髪料の試料を
0.5gを均等に塗布し、直径2cmのロッドに巻き、
45℃の高温室内に6時間放置して、完全に乾燥させ
た。乾燥後、ロッドをはずして、毛束の見かけの長さ
(L)を測定した。次に温度25℃湿度90%の恒温恒
湿室に毛束を吊し、30分後に取り出し、再び毛束の見
かけの長さ(L0 )を測定した。(1) Hair styling holding effect A hair styling sample of 0.5 g is evenly applied to a hair bundle of 15 cm in length and 1 g in weight, and wound on a rod of 2 cm in diameter.
It was left in a high-temperature room at 45 ° C. for 6 hours and completely dried. After drying, the rod was removed and the apparent length (L) of the hair bundle was measured. Next, the hair bundle was hung in a thermo-hygrostat at a temperature of 25 ° C. and a humidity of 90%, taken out 30 minutes later, and the apparent length (L 0) of the hair bundle was measured again.
【0032】整髪保持効果を次式にて求めた。 整髪保持力(%)=〔(15−L0 )/(15−
L)〕×100 したがって、この値が100に近いほど整髪保持効果が
高いことを示す。The hair keeping effect was determined by the following equation. Hair holding power (%) = [(15-L0) / (15-
L)] × 100 Therefore, the closer this value is to 100, the higher the hair-keeping effect.
【0033】評価基準は、以下の通りである。 ◎:非常に良好 整髪保持力80%以上 ○:良好 整髪保持力50%以上、80%未満 △:やや悪い 整髪保持力30%以上、50%未満 ×:悪い 整髪保持力30%未満The evaluation criteria are as follows. ◎: Very good Hair holding power of 80% or more ○: Good Hair holding power of 50% or more and less than 80% △: Slightly poor Hair holding power of 30% or more and less than 50% ×: Poor Hair holding power of less than 30%
【0034】(2)官能試験 20名の被験者によってゲル状整髪料の試料を使用し、
整髪を実施した。その後被験者本人が、ツヤ、乾燥の速
さ、べたつきの無さ、フレーキングの無さについて官能
評価した。評価基準は、以下の通りである。 ◎:非常に良好 良いと答えた被験者の数が18人以上 ○:良好 良いと答えた被験者の数が12人以上、18人未満 △:やや悪い 良いと答えた被験者の数が8人以上、12人未満 ×:悪い 良いと答えた被験者の数が8人未満(2) Sensory test A gel hairdressing sample was used by 20 subjects,
Hairdressing was performed. Thereafter, the subject himself / herself evaluated the gloss, the speed of drying, the absence of stickiness, and the absence of flaking. The evaluation criteria are as follows. ◎: Very good The number of subjects who answered good was 18 or more ○: Good The number of subjects who answered good was 12 or more and less than 18 △: Somewhat bad The number of subjects who answered good was 8 or more, Less than 12 ×: Poor Less than 8 subjects answered good
【0035】(3)保存安定性 ゲル状整髪料の試料をガラス製透明容器に充填し、40
℃に保たれた恒温槽に保存し、3ヶ月後の試料の状態
(粘度、外観)を評価した。(3) Storage stability A gel-like hairdressing sample is filled in a transparent glass container,
The sample was stored in a thermostat kept at a temperature of 0 ° C., and the state (viscosity, appearance) of the sample after three months was evaluated.
【0036】評価基準は、以下の通りである。 ◎:粘度の変化が±10%未満 ○:粘度変化が±10以上20未満 △:粘度変化が±20以上30未満 ×:粘度変化が±30%以上、又は分離The evaluation criteria are as follows. :: Change in viscosity is less than ± 10% ○: Change in viscosity is ± 10 or more and less than 20 Δ: Change in viscosity is ± 20 or more and less than 30 ×: Change in viscosity is ± 30% or more, or separation
【0037】実施例1〜10、比較例1〜4 表1に示した処方のゲル状整髪料を常法により作製し、
前記各試験を実施した。その結果を表1に併せて示す。Examples 1 to 10 and Comparative Examples 1 to 4 Gel hair styling materials having the formulations shown in Table 1 were prepared by a conventional method.
Each of the above tests was performed. The results are shown in Table 1.
【0038】[0038]
【表1】 [Table 1]
【0039】表1より明らかなように本発明の成分を用
いた実施例のゲル状整髪料はいずれも優れた性能を有し
ていた。As is clear from Table 1, the gel hair styling compositions of Examples using the components of the present invention all had excellent performance.
【0040】一方、必須成分のいずれかを欠いた比較例
では、整髪保持効果、ツヤ、乾燥性、べたつきの無さ、
フレーキングの無さ、保存安定性のいずれかの面で劣っ
ており、本発明の目的を達成できなかったOn the other hand, in the comparative examples lacking any of the essential components, the hair styling retention effect, gloss, drying property, non-stickiness,
No flaking, poor storage stability either, could not achieve the object of the present invention
【0041】 実施例11 成分 質量% −−−−−−−−−−−−−−−−−−−−−−−−−−−−−−−−−−−− アクリル酸/メタクリル酸アルキル共重合体 0.7 (PEMULEN TR−1:B.F.GOODRICH社製) アミノメチルプロパノール 0.5 アクリル酸アルキル/ジアセトンアクリルアミド共重合体 5.0 (プラスサイズL−4485V:互応化学工業社製) エタノール 10.0 ジプロピレングリコール 2.0 ビニルピロリドン/酢酸ビニル共重合体 1.0 (PVP/VA S−630:ISP社製) 流動パラフィン 3.0 ポリオキシエチレン硬化ヒマシ油(80E.O.) 0.5 ポリオキシエチレンオレイルエーテル(3E.O.) 0.3 メチルフェニルポリシロキサン 0.5 (KF−56:信越化学工業社製) ジメチルポリシロキサン 0.2 (KF−96H(100000cs):信越化学工業社製) エデト酸二ナトリウム 0.05 パラメトキシケイ皮酸2−エチルヘキシル 0.1 セージエキス(商品名:サルビア抽出液、香栄興業社製) 0.5 精製水 残 部Example 11 Ingredients% by Mass ---------------------------------------------------------- Acrylic acid / methacrylic acid Alkyl copolymer 0.7 (PEMULEN TR-1: manufactured by BF GOODRICH) Aminomethylpropanol 0.5 Alkyl acrylate / diacetone acrylamide copolymer 5.0 (Plus size L-4485V: Mutual Chemical Industry) Ethanol 10.0 dipropylene glycol 2.0 vinylpyrrolidone / vinyl acetate copolymer 1.0 (PVP / VAS-630: manufactured by ISP) Liquid paraffin 3.0 polyoxyethylene hydrogenated castor oil (80E. O.) 0.5 Polyoxyethylene oleyl ether (3EO) 0.3 Methylphenylpolysiloxane 0.5 (KF-56: Shin-Etsu) Dimethyl polysiloxane 0.2 (KF-96H (100,000 cs): Shin-Etsu Chemical Co., Ltd.) Disodium edetate 0.05 2-Ethylhexyl paramethoxycinnamate 0.1 Sage extract (trade name: Salvia) (Extract, manufactured by Koei Kogyo) 0.5 purified water balance
【0042】上記組成のゲル状整髪料を常法により調整
し、整髪保持効果、ツヤ、乾燥性、べたつきのなさ、フ
レーキングの無さ、保存安定性について評価したとこ
ろ、優れた性能を有していた。The gel hair styling composition having the above composition was prepared by a conventional method, and evaluated for hair styling retention effect, gloss, drying property, non-stickiness, no flaking, and storage stability. I was
【0043】[0043]
【発明の効果】以上記載のごとく、本発明は、整髪保持
効果に優れ、毛髪にツヤを与え、乾燥が早く、更に使用
時のべたつきが極めて少なく、フレーキングがおこら
ず、保存安定性にも優れるゲル状整髪料を提供すること
ができる。As described above, the present invention is excellent in hair-keeping effect, imparts gloss to hair, dries quickly, has very little stickiness during use, does not cause flaking, and has good storage stability. An excellent gel-like hairdressing composition can be provided.
Claims (3)
を特徴とするゲル状整髪料。 (A)共重合成分として、下記一般式(1)で表される
長鎖アルキルアクリレートモノマー1〜50質量%と、 【化1】 (但し、Rは炭素数10〜30のアルキル基であり、
R’は水素又はメチル基である。) オレフィン性不飽和カルボン酸モノマー99〜50質量
%とを含むモノマー混合物からの共重合体 (B)該共重合体の中和剤 (C)水溶性アルコール (D)被膜形成能を有するアニオン性高分子化合物1. A gel hairdressing composition containing the following components (A) to (D). (A) 1 to 50% by mass of a long-chain alkyl acrylate monomer represented by the following general formula (1) as a copolymerization component: (Where R is an alkyl group having 10 to 30 carbon atoms,
R 'is hydrogen or a methyl group. A) a copolymer from a monomer mixture containing 99 to 50% by mass of an olefinically unsaturated carboxylic acid monomer; (B) a neutralizing agent for the copolymer; (C) a water-soluble alcohol; and (D) an anionic film-forming agent. Polymer compound
性高分子化合物を含有することを特徴とする請求項1に
記載のゲル状整髪料。2. The gel hairdressing composition according to claim 1, further comprising (E) a nonionic polymer compound capable of forming a film.
することを特徴とする請求項1又は請求項2に記載のゲ
ル状整髪料。3. The gel hairdressing composition according to claim 1, further comprising (F) a nonionic surfactant.