JP2002166408A - Pattern-transferring board for concrete decorative form and method for constructing decorative concrete molded body using the board - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a pattern-transferring board for a concrete decorative pattern which is good in release from a concrete molded product, can be repeti tively used, can accelerate a curing reaction of concrete and can prevent the concrete from leakage in placing the concrete. SOLUTION: A pattern transferring board 14 for applying decoration composes a decorative form 10 for placing concrete together with a rigid form main body 12, and transfers a recessed and projected pattern to a surface in placing the concrete. A front layer 28 coming in contact with the concrete comprises a non-foam having an irregular pattern, and a rear surface layer 30 comprises a foam.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】この発明はコンクリート打設
時にその表面に化粧を施すコンクリート用化粧型枠、詳
しくはその化粧型枠に用いる模様転写板及びこれを用い
た化粧コンクリート成形体の施工方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative formwork for concrete for applying a decorative surface to concrete during casting, and more particularly to a pattern transfer plate used for the decorative formwork and a method for applying a decorative concrete molding using the same. .

【０００２】[0002]

【従来の技術】従来、ダムや各種擁壁等のコンクリート
構造物或いは各種のコンクリートブロック等のコンクリ
ート成形体を打設成形するに際して、化粧型枠を用いコ
ンクリート打設時にその表面に凹凸形状模様を転写形成
し、化粧するといったことが行われている。通例この化
粧型枠は、コンクリートの打設圧力を受ける剛性の型枠
本体と、コンクリート打設時に凹凸形状模様を転写する
模様転写板とを含んで構成されている。2. Description of the Related Art Conventionally, when a concrete structure such as a dam or various retaining walls or a concrete molded body such as various concrete blocks is cast and formed, an irregular shape pattern is formed on the surface of the concrete when the concrete is cast. Transfer formation and makeup are performed. Usually, the decorative formwork is configured to include a rigid formwork body that receives a concrete placing pressure and a pattern transfer plate that transfers an uneven pattern at the time of concrete placing.

【０００３】[0003]

【発明が解決しようとする課題】而してこの模様転写板
として、従来、発泡樹脂製のものを用いてこれを剛性の
型枠本体に両面テープ等で固定することが行われている
が、この場合発泡樹脂製の模様転写板の強度が弱く、加
えてこの模様転写板はコンクリートに強く付着した状態
となってしまうため、打設後に化粧コンクリート成形体
を脱型する際に模様転写板が簡単に破砕してしまって、
繰り返し使用が効かず、これがため模様転写板に要する
コストが高くなってしまうといった問題が生じていた。
一方、剛性の型枠本体自体に模様転写板を一体に構成す
ることも考えられるが、この場合その化粧型枠に要する
コストが高くなるとともに模様が専用化してしまい、模
様（デザイン）を変えるときには型枠全体を変えければ
ならなくなってしまって費用が高くなってしまう。Conventionally, as the pattern transfer plate, one made of a foamed resin is used and fixed to a rigid mold body with a double-sided tape or the like. In this case, the strength of the pattern transfer plate made of foamed resin is low, and in addition, the pattern transfer plate is strongly adhered to the concrete. Easily crushed,
There has been a problem that the repetitive use is not effective and the cost required for the pattern transfer plate is increased.
On the other hand, it is conceivable to form a pattern transfer plate integrally with the rigid form body itself. However, in this case, the cost required for the decorative form is increased and the pattern is specialized, so that when changing the pattern (design), The entire form must be changed and the costs rise.

【０００４】[0004]

【課題を解決するための手段】本発明のコンクリート化
粧型枠用の模様転写板及びこれを用いた施工方法はこの
ような課題を解決するために案出されたものである。而
して請求項１は模様転写板に関するもので、剛性の型枠
本体とともにコンクリート打設用化粧型枠を構成し、コ
ンクリート打設時に表面に凹凸形状模様を転写し、化粧
を施すための模様転写板であって、コンクリートに接す
る表面層が凹凸形状模様を有する無発泡体で構成される
とともに、裏面層が発泡体で構成されていることを特徴
とする。The pattern transfer plate for a decorative decorative formwork of the present invention and a construction method using the same have been devised to solve such problems. Claim 1 relates to a pattern transfer plate, which comprises a decorative formwork for concrete casting together with a rigid formwork body, and a pattern for transferring a concave and convex shape pattern to the surface at the time of concrete placing to apply makeup. The transfer plate is characterized in that the surface layer in contact with the concrete is made of a non-foamed material having an uneven pattern, and the back surface layer is made of a foamed material.

【０００５】請求項２のものは、請求項１において、前
記発泡体から成る裏面層が、前記無発泡体から成る表面
層よりも厚く形成されていることを特徴とする。A second aspect of the present invention is characterized in that, in the first aspect, the back layer made of the foam is formed thicker than the surface layer made of the non-foam.

【０００６】請求項３のものは、請求項１，２の何れか
において、前記模様転写板が熱可塑性樹脂にて構成され
ていることを特徴とする。According to a third aspect of the present invention, in any one of the first and second aspects, the pattern transfer plate is made of a thermoplastic resin.

【０００７】請求項４は施工方法に関するもので、請求
項１〜３の何れかの模様転写板を縁部で重ね合せて該模
様転写板を複数枚ジョイントし、コンクリート打設を行
ってコンクリートの硬化後脱型し、化粧コンクリート成
形体を得ることを特徴とする。A fourth aspect of the present invention relates to a construction method, wherein the pattern transfer plates of any one of the first to third aspects are overlapped at an edge portion, a plurality of the pattern transfer plates are jointed, and concrete is cast by concrete casting. It is characterized in that it is demolded after curing to obtain a decorative concrete molded product.

【０００８】[0008]

【作用及び発明の効果】上記のように本発明の模様転写
板は、凹凸形状模様を有する無発泡体から成る表面層
と、発泡体から成る裏面層との積層構造となしたもので
ある。かかる本発明の模様転写板は、表面層が緻密な無
発泡体から成っているため、コンクリートの剥離性が良
好であるとともに強度が強く、従って化粧コンクリート
成形体を脱型する際に模様転写板と化粧コンクリート成
形体とが容易に離れ、しかもその脱型時に模様転写板が
破砕するのを良好に防止ないし抑制することができる。
従って本発明の模様転写板は繰り返して使用することが
可能であり、模様転写板に要するコストを低減すること
ができる。As described above, the pattern transfer plate of the present invention has a laminated structure of a surface layer made of a non-foamed material having an uneven pattern and a back surface layer made of a foamed material. Such a pattern transfer plate of the present invention has a high surface strength and a high strength because the surface layer is made of a dense non-foamed body, and thus has a high strength. And the decorative concrete molded body can easily be separated from each other, and the pattern transfer plate can be satisfactorily prevented or suppressed from being crushed at the time of demolding.
Therefore, the pattern transfer plate of the present invention can be used repeatedly, and the cost required for the pattern transfer plate can be reduced.

【０００９】本発明の模様転写板はまた次のような特徴
も有している。コンクリート打設後におけるコンクリー
トの硬化は自己発熱を伴って進行し且つその発熱により
硬化反応が促進される。この場合模様転写板を通して熱
が外部に逃げてしまうと硬化が遅延してしまうが、本発
明の模様転写板は裏面層が発泡体にて構成されているた
め、コンクリートの自己発熱を型枠内に良好に閉じ込め
得、これによりコンクリートの硬化反応に良好な状況を
作り出すことができる。The pattern transfer plate of the present invention also has the following features. The hardening of the concrete after the concrete is cast proceeds with self-heating, and the heat generation promotes the hardening reaction. In this case, if heat escapes to the outside through the pattern transfer plate, the curing is delayed. However, the pattern transfer plate of the present invention has a back surface layer made of a foam, so that the self-heating of concrete is suppressed in the formwork. And thus create a favorable situation for the hardening reaction of concrete.

【００１０】更にまた本発明の模様転写板は裏面層が発
泡体にて構成されているため、模様転写板を縁部で重ね
合せるようにしてジョイントする際に裏面層の発泡体が
シール材として働き、模様転写板と模様転写板との間の
ジョイント部分からコンクリートが外部に漏出するのを
良好に防止することができる。Further, since the back surface layer of the pattern transfer plate of the present invention is formed of a foam, the foam of the back surface layer is used as a sealing material when the pattern transfer plates are joined at the edges so as to be overlapped. It is possible to prevent the concrete from leaking to the outside from the joint between the pattern transfer plate and the pattern transfer plate.

【００１１】この場合において、発泡体から成る裏面層
を無発泡体から成る表面層よりも厚く形成しておくこと
ができる（請求項２）。このようにしておくと上記断熱
効果及びシール材としての機能をより高めることができ
る。In this case, the back layer made of foam can be formed thicker than the front layer made of non-foam. By doing so, the heat insulating effect and the function as a sealing material can be further enhanced.

【００１２】本発明では、上記模様転写板を熱可塑性樹
脂にて構成することができ（請求項３）、これにより模
様転写板を安価に製造することができる。尚この場合に
おいて模様転写板を真空成形にて成形するのが好適であ
る。勿論他の成形手法を用いることも可能である。In the present invention, the pattern transfer plate can be made of a thermoplastic resin (claim 3), whereby the pattern transfer plate can be manufactured at low cost. In this case, it is preferable to form the pattern transfer plate by vacuum forming. Of course, other molding techniques can be used.

【００１３】次に請求項４の施工方法は、上記模様転写
板を縁部で重ね合せて模様転写板を複数枚ジョイント
し、その状態で型枠内部にコンクリート打設を行ってコ
ンクリートの硬化後脱型し、化粧コンクリート成形体を
得るもので、この施工方法によれば、模様転写板のジョ
イント部分でコンクリートが漏出するのを防止して良好
な化粧コンクリート成形体を得ることができる。Next, in a construction method according to a fourth aspect of the present invention, a plurality of pattern transfer plates are jointed by overlapping the pattern transfer plates at an edge portion, and concrete is poured into a formwork in that state, and concrete is cured. The mold is removed to obtain a decorative concrete molded article. According to this construction method, it is possible to prevent the concrete from leaking at the joint portion of the pattern transfer plate and obtain a good decorative concrete molded article.

【００１４】[0014]

【実施例】次に本発明の実施例を図面に基づいて詳しく
説明する。図1において、１０はコンクリート用の化粧
型枠で鋼製の（剛性の）型枠本体１２と、コンクリート
打設時にその表面に凹凸形状模様を転写し、化粧するた
めの模様転写板１４とから成っている。ここで模様転写
板１４はポリプロピレン製，ポリエチレン製等の熱可塑
性樹脂製のもので、この例では真空成形により成形され
ている。但し他の成形手法にて成形することも可能であ
る。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Next, embodiments of the present invention will be described in detail with reference to the drawings. In FIG. 1, reference numeral 10 denotes a decorative formwork for concrete, which includes a steel (rigid) formwork main body 12 and a pattern transfer plate 14 for transferring an uneven pattern onto the surface of the concrete when casting concrete to make it decorative. Made up of Here, the pattern transfer plate 14 is made of a thermoplastic resin such as polypropylene or polyethylene, and is formed by vacuum forming in this example. However, it is also possible to mold by another molding method.

【００１５】この模様転写板１４は、成形面１６に多数
の凹部１８と凸部２０とを有し、成形面１６全面に亘っ
て所定の凹凸形状模様が形成してある。この模様転写板
１４は、成形面１６に対し直角方向に折れ曲った形態の
フランジ部２２を四周縁に有しており、このフランジ部
２２において、型枠本体１２の四周縁のフランジ部２４
に外嵌する形態をなしている。尚、図１に示しているよ
うにこの例では化粧型枠１０と１０とがクリップ２６に
て連結されるようになっている。The pattern transfer plate 14 has a large number of concave portions 18 and convex portions 20 on a molding surface 16, and a predetermined uneven pattern is formed over the entire molding surface 16. The pattern transfer plate 14 has a flange portion 22 formed on the four peripheral edges thereof in a form bent at a right angle to the molding surface 16. In the flange portion 22, the flange portions 24 of the four peripheral edges of the form body 12 are formed.
It is in the form of external fitting. In this example, as shown in FIG. 1, the decorative mold frames 10 and 10 are connected by a clip 26.

【００１６】図２に模様転写板１４の断面構造が示して
ある。図に示しているようにこの例において模様転写板
１４は、表面層２８と裏面層３０との積層構造をなして
いる。ここで表面層２８は緻密な無発泡体から成ってお
り、また裏面層３０は発泡体にて構成されている。この
例において、表面層２８は厚みが０．１〜２ｍｍとされ
ており、また裏面層３０はその厚みが０．５〜５ｍｍと
されている。即ち裏面層３０の厚みが表面層２８の厚み
に対して厚くされている。尚、裏面層３０の厚みは表面
層２８の厚みに対して５〜２０倍程度とするのが望まし
い。FIG. 2 shows a sectional structure of the pattern transfer plate 14. As shown in the figure, in this example, the pattern transfer plate 14 has a laminated structure of a surface layer 28 and a back layer 30. Here, the surface layer 28 is made of a dense non-foamed body, and the back surface layer 30 is made of a foamed body. In this example, the surface layer 28 has a thickness of 0.1 to 2 mm, and the back surface layer 30 has a thickness of 0.5 to 5 mm. That is, the thickness of the back surface layer 30 is made larger than the thickness of the surface layer 28. Note that the thickness of the back surface layer 30 is desirably about 5 to 20 times the thickness of the surface layer 28.

【００１７】図３及び図４は上記化粧型枠１０を用いた
施工方法の具体的手順を表している。図に示しているよ
うに化粧型枠１０を用いてコンクリートの打設成形を行
うに際して、先ず図３（Ｉ）に示しているように型枠本
体１２に対して模様転写板１４を固定し、図３（II）に
示すように別の型枠３２とともにコンクリートの打設空
間Ｓをそれらの間に形成する。そしてその打設空間Ｓの
内部に流動状態のコンクリートＣの打設を行う。図３
（III）はこのときの状態を示している。FIGS. 3 and 4 show a specific procedure of a construction method using the decorative formwork 10. FIG. When casting concrete using the decorative formwork 10 as shown in the figure, first, the pattern transfer plate 14 is fixed to the formwork body 12 as shown in FIG. As shown in FIG. 3 (II), a concrete casting space S is formed between them together with another formwork 32. Then, the concrete C in a flowing state is cast into the casting space S. FIG.
(III) shows the state at this time.

【００１８】その後所定時間かけて打設したコンクリー
トＣを硬化させ、そしてその硬化が終了したところで、
図４（Ｖ）に示しているように化粧コンクリート成形体
３４を脱型する。ここにおいて表面に模様転写板１４の
凹凸形状模様が転写形成され、化粧の施された化粧コン
クリート成形体３４が得られる。After that, the concrete C put in is hardened for a predetermined time, and when the hardening is completed,
As shown in FIG. 4 (V), the decorative concrete molded body 34 is released. Here, the concave and convex pattern of the pattern transfer plate 14 is transferred and formed on the surface, and a decorative concrete molded body 34 on which makeup is applied is obtained.

【００１９】図５は本発明の他の実施例を示したもの
で、この例では模様転写板１４の縁部に凸部２０を形成
しておいて、その凸部２０において隣り合う模様転写板
１４同士を嵌合状態に重ね合せ、それら模様転写板１４
をジョイントするようになした例である。FIG. 5 shows another embodiment of the present invention. In this embodiment, a convex portion 20 is formed at the edge of the pattern transfer plate 14, and the pattern transfer plate adjacent to the convex portion 20 is formed. 14 are overlapped with each other in a fitted state, and the pattern transfer plates 14
This is an example in which are joined.

【００２０】尚ここでは模様転写板１４の縁部に凸部２
０を形成してそれらを嵌合状態に重ね合せるようにして
いるが、勿論凹部を形成してそれら凹部同士を嵌合状態
に重ね合せるようになすこともできる。Here, the convex portion 2 is formed at the edge of the pattern transfer plate 14.
Although 0 is formed to superimpose them in the fitted state, it is of course possible to form recesses and superimpose these recesses in the fitted state.

【００２１】或いはまたそのような凸部２０や凹部を形
成することなく、平面状態の部分において隣り合う模様
転写板１４同士を重ね合せジョイントするようになすこ
とも可能である。Alternatively, the adjacent pattern transfer plates 14 can be overlapped and jointed in a planar state without forming such convex portions 20 and concave portions.

【００２２】このように本例では表面層２８が緻密な無
発泡体から成っているためにコンクリートの剥離性が良
好であるとともに強度が強く、従って化粧コンクリート
成形体３４を脱型する際に模様転写板１４と化粧コンク
リート成形体３４とが容易に離れ、また脱型時に模様転
写板１４が破砕するのを防止ないし抑制でき、従って本
例の模様転写板１４は繰り返して使用することが可能で
あり、模様転写板１４に要するコストを低減できる。As described above, in this embodiment, since the surface layer 28 is formed of a dense non-foamed body, the concrete has good releasability and high strength. The transfer plate 14 and the decorative concrete molded body 34 can be easily separated from each other, and the crushing of the pattern transfer plate 14 at the time of demolding can be prevented or suppressed. Therefore, the pattern transfer plate 14 of this embodiment can be used repeatedly. In addition, the cost required for the pattern transfer plate 14 can be reduced.

【００２３】更に本例の模様転写板１４は、裏面層３０
が発泡体で構成されているために硬化反応に有効な断熱
効果が期待でき、良好なコンクリートを得ることができ
る。Further, the pattern transfer plate 14 of the present embodiment is
Is composed of a foam, a heat insulating effect effective for a curing reaction can be expected, and good concrete can be obtained.

【００２４】更にまた本例の模様転写板１４は裏面層３
０が発泡体で構成されているため、模様転写板１４を縁
部で重ね合せるようにしてジョイントすることで裏面層
３０の発泡体をシール材として働かせることができ、模
様転写板１４と模様転写板１４との間のジョイント部分
からコンクリートが外部に漏出するのを良好に防止する
ことができる。Furthermore, the pattern transfer plate 14 of the present embodiment is
Since the reference numeral 0 is made of a foam, the foam of the back surface layer 30 can be used as a sealing material by joining the pattern transfer plates 14 so as to overlap each other at the edges, so that the pattern transfer plate 14 and the pattern transfer Leakage of concrete from the joint portion between the plate 14 and the outside can be effectively prevented.

【００２５】以上本発明の実施例を詳述したがこれはあ
くまで一例示である。例えば本発明においては模様転写
板１４の表面層２８と裏面層３０との間に必要に応じて
中間層を設けるといったことも可能であるし、また模様
転写板１４或いはその表面層２８，裏面層３０を様々な
材質で構成することが可能であるなど、本発明はその主
旨を逸脱しない範囲において種々変更を加えた形態対応
で構成実施可能である。The embodiment of the present invention has been described in detail above, but this is merely an example. For example, in the present invention, it is possible to provide an intermediate layer between the surface layer 28 and the back surface layer 30 of the pattern transfer plate 14 as necessary, or the pattern transfer plate 14 or the surface layer 28 and the back surface layer thereof. The present invention can be configured and implemented in various modified forms without departing from the gist of the present invention, for example, it is possible to configure the 30 from various materials.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の一実施例である化粧型枠を示す図であ
る。FIG. 1 is a view showing a decorative formwork according to one embodiment of the present invention.

【図２】図１の化粧型枠の縦断面図である。FIG. 2 is a vertical sectional view of the decorative formwork of FIG. 1;

【図３】図１及び図２の化粧型枠を用いた施工方法の手
順を示す図である。FIG. 3 is a diagram showing a procedure of a construction method using the decorative formwork of FIGS. 1 and 2;

【図４】図３に続く手順を示す図である。FIG. 4 is a diagram showing a procedure following FIG. 3;

【図５】本発明の他の実施例の施工方法の要部説明図で
ある。FIG. 5 is an explanatory view of a main part of a construction method according to another embodiment of the present invention.

【符号の説明】[Explanation of symbols]

１０ 化粧型枠 １２ 型枠本体 １４ 模様転写板 ２８ 表面層 ３０ 裏面層 ３４ 化粧コンクリート成形体 Reference Signs List 10 decorative formwork 12 formwork body 14 pattern transfer plate 28 surface layer 30 backside layer 34 decorative concrete molding

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 剛性の型枠本体とともにコンクリート打
設用化粧型枠を構成し、コンクリート打設時に表面に凹
凸形状模様を転写し、化粧を施すための模様転写板であ
って、 コンクリートに接する表面層が凹凸形状模様を有する無
発泡体で構成されるとともに、裏面層が発泡体で構成さ
れていることを特徴とする積層構造のコンクリート化粧
型枠用の模様転写板。1. A pattern transfer plate for forming a decorative formwork for concrete placement together with a rigid formwork body, transferring a pattern of irregularities onto the surface during concrete placement, and applying a make-up, which is in contact with concrete. A pattern transfer plate for a decorative concrete formwork having a laminated structure, wherein the surface layer is made of a non-foamed material having an uneven pattern and the back surface layer is made of a foamed material. 【請求項２】 請求項１において、前記発泡体から成る
裏面層が、前記無発泡体から成る表面層よりも厚く形成
されていることを特徴とするコンクリート化粧型枠用の
模様転写板。2. The pattern transfer plate for a decorative decorative formwork according to claim 1, wherein the back layer made of the foam is formed thicker than the surface layer made of the non-foam. 【請求項３】 請求項１，２の何れかにおいて、前記模
様転写板が熱可塑性樹脂にて構成されていることを特徴
とするコンクリート化粧型枠用の模様転写板。3. The pattern transfer plate for a decorative decorative formwork according to claim 1, wherein the pattern transfer plate is made of a thermoplastic resin. 【請求項４】 請求項１〜３の何れかの模様転写板を縁
部で重ね合せて該模様転写板を複数枚ジョイントし、コ
ンクリート打設を行ってコンクリートの硬化後脱型し、
化粧コンクリート成形体を得ることを特徴とする化粧コ
ンクリート成形体の施工方法。4. The pattern transfer plate according to any one of claims 1 to 3 is overlapped at an edge portion, a plurality of the pattern transfer plates are jointed, concrete is cast, concrete is cured, and the mold is released.
A method for constructing a decorative concrete molding, characterized by obtaining a decorative concrete molding.