JP2002057488A - Material having both sound absorbing characteristic and electromagnetic wave shielding characteristic - Google Patents
Material having both sound absorbing characteristic and electromagnetic wave shielding characteristicInfo
- Publication number
- JP2002057488A JP2002057488A JP2000244259A JP2000244259A JP2002057488A JP 2002057488 A JP2002057488 A JP 2002057488A JP 2000244259 A JP2000244259 A JP 2000244259A JP 2000244259 A JP2000244259 A JP 2000244259A JP 2002057488 A JP2002057488 A JP 2002057488A
- Authority
- JP
- Japan
- Prior art keywords
- electromagnetic wave
- sheet
- aluminum foil
- wave shielding
- characteristic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、吸音特性と電磁波
シールド特性を兼備した材料に関する。The present invention relates to a material having both a sound absorbing property and an electromagnetic wave shielding property.
【０００２】[0002]
【従来の技術】最近のディジタル電子機器の急速な普及
により、室外からの妨害電磁波による電磁波障害と同時
に、今後はオフィス内から外部に漏洩する各種デジタル
信号が企業活動を阻害する可能性が出現している。これ
らの電磁波障害を室レベルで防止する方法としては、従
来、銅あるいはアルミニウムのような電気抵抗の低い材
料で作った薄板で部屋全体を包むか、あるいは薄鋼鈑等
の磁性材料で包む方法が一般的であった。2. Description of the Related Art With the rapid spread of digital electronic devices in recent years, there is a possibility that various digital signals leaking from inside an office to outside will interfere with corporate activities at the same time as electromagnetic interference caused by electromagnetic interference from outside. ing. As a method of preventing these electromagnetic wave disturbances at a room level, conventionally, a method of wrapping the entire room with a thin plate made of a material having low electric resistance such as copper or aluminum, or a method of wrapping with a magnetic material such as a thin steel plate is known. Was common.
【０００３】[0003]
【発明が解決しようとする課題】前記したように電磁シ
ールド材料として穴の開いてない電気抵抗の低いアルミ
ニウム等の薄板や、薄鋼鈑等の磁性材料を室内の壁面に
用いた場合には、それらの材料には吸音特性がないの
で、室内騒音の低減や室内の残響調整が必要な場合には
グラスウール等をパネル化する方法等による吸音対策が
別途必要であり、建設コストのアップ等に繋がってい
る。As described above, when a magnetic material such as a thin plate of aluminum or the like having no electric hole and having a low electric resistance, or a thin steel plate is used as an electromagnetic shielding material for the indoor wall surface, Since these materials do not have sound absorption characteristics, if it is necessary to reduce indoor noise or adjust reverberation in the room, it is necessary to take additional measures to absorb sound, such as by making glass wool into panels, leading to an increase in construction costs. ing.
【０００４】本発明の目的は、前記従来技術の問題点を
解決することにあり、吸音特性と電磁波シールド特性を
兼備した材料を提供することである。[0004] An object of the present invention is to solve the above-mentioned problems of the prior art, and to provide a material having both a sound absorbing property and an electromagnetic wave shielding property.
【０００５】[0005]
【課題を解決するための手段】前記したように、吸音特
性と電磁波シールド特性を兼備した材料の提供は、今後
急速に進行するデジタル化社会に好適なものと確信して
いるが、本発明者等は、特開平４−１８６００号公報に
および特開平８−４２０１５公報において、アルミニウ
ム箔に多数の破断部を付与し、この破断部が音波によっ
て振動することを利用する吸音材を開示している。その
後本発明者等は上記公報に開示した吸音材、すなわち、
導電性材料であるアルミニウム箔に吸音を目的とした多
数の破断部を付与しても優れた電磁波シールド特性を兼
備していることを見出し、本発明をなすに至った。As described above, it is believed that the provision of a material having both a sound absorbing property and an electromagnetic wave shielding property is suitable for a digitized society that will rapidly progress in the future. Disclose a sound-absorbing material in Japanese Patent Application Laid-Open Nos. 4-18600 and 8-42015, in which an aluminum foil is provided with a large number of broken portions and the broken portions are vibrated by sound waves. . After that, the present inventors disclosed the sound absorbing material disclosed in the above publication, that is,
The present inventors have found that even when a large number of broken portions for the purpose of sound absorption are imparted to an aluminum foil as a conductive material, the aluminum foil also has excellent electromagnetic wave shielding properties, and the present invention has been accomplished.
【０００６】本発明の態様は、可撓性を有する網状シー
トと多数の破断部を有するアルミニウム箔とを粘着して
なり、かつ前記破断部のアルミニウム箔が音波によって
振動可能であり、かつ前記アルミニウム箔の破断部が電
磁波シールド効果に悪影響を与えることのない、吸音特
性と電磁波シールド特性を兼備したことを特徴とする、
シート状材料である。According to an aspect of the present invention, a flexible net-like sheet is adhered to an aluminum foil having a large number of breaks, and the aluminum foil at the break is vibrated by a sound wave; It is characterized by having both sound absorption characteristics and electromagnetic wave shielding characteristics, where the broken part of the foil does not adversely affect the electromagnetic wave shielding effect,
It is a sheet material.
【０００７】[0007]
【発明の実施の形態】以下、本発明の吸音特性と電磁波
シールド特性を兼備した材料について、添付の図面を参
照して詳細に説明する。図１および図２は本発明の態様
の一例を示す概念図であり、図１はシート状材料１０を
シートのアルミニウム箔１１面方向（正面）から見た図
（正面図）であり、図２はシートの可撓性を有する網状
シート（可撓性スクリーンメッシュ）１２面方向（裏
面）から見た図（正面図）である。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, a material having both a sound absorbing property and an electromagnetic wave shielding property of the present invention will be described in detail with reference to the accompanying drawings. FIGS. 1 and 2 are conceptual views showing an example of the embodiment of the present invention. FIG. 1 is a view (front view) of a sheet-like material 10 viewed from the aluminum foil 11 surface side (front) of the sheet. FIG. 3 is a diagram (front view) viewed from the direction of the surface (the back surface) of the reticulated sheet (flexible screen mesh) 12 having the flexibility of the sheet.
【０００８】図示例の本発明のシート状材料１０は、破
断部を有するアルミニウム箔１１と可撓性を有する網状
シート（可撓性スクリーンメッシュ）１２とを粘着して
なる構成を有する。図３は図１および図２に示す開口部
１３、すなはち（ａ）図はアルミニウム箔１１面方向か
ら見た開口部１３の概念図であり、（ｂ）図は上記
（ａ）図に示すｂ‐ｂ断面図である。The illustrated sheet material 10 of the present invention has a structure in which an aluminum foil 11 having a break portion and a flexible net-like sheet (flexible screen mesh) 12 are adhered. FIG. 3 is a conceptual view of the opening 13 shown in FIGS. 1 and 2, that is, FIG. 3A is a conceptual view of the opening 13 as viewed from the aluminum foil 11 surface direction, and FIG. It is bb sectional drawing shown.
【０００９】ここで、本発明のシート状材料１０はアル
ミニウム箔１１の破断部１３の網状シート１２方向に捲
れ上がった部分（以下、この部分を破断部分１３ａとす
る）が音波によって振動可能である。音波によって振動
可能な破断部分１３ａを有するアルミニウム箔１１と網
状シート１２を全面的に粘着することにより、音波の入
射によって破断部分１３ａが良好かつ極めて細かく振動
して音のエネルギーを良好に吸収することができる。Here, in the sheet-like material 10 of the present invention, a portion of the broken portion 13 of the aluminum foil 11 that is rolled up in the direction of the mesh sheet 12 (hereinafter, this portion is referred to as a broken portion 13a) can be vibrated by sound waves. . By adhering the entire surface of the aluminum foil 11 having the broken portion 13a vibrated by the sound wave and the net-like sheet 12, the broken portion 13a vibrates finely and very finely due to the incidence of the sound wave, thereby absorbing the sound energy well. Can be.
【００１０】本発明に用いるアルミニウム箔１１の厚さ
には特に限定はないが、好ましくは５μｍ〜１０μｍ程
度、より好ましくは７μｍ〜１０μｍ程度である。The thickness of the aluminum foil 11 used in the present invention is not particularly limited, but is preferably about 5 μm to 10 μm, more preferably about 7 μm to 10 μm.
【００１１】また、本発明に用いる網状シート１２の材
料にも特に限定はなく、吊り下げた際に波打ち等を有す
ることなく良好な平面状となり、また巻き取りを容易に
行える程度の可撓性を有するものであれば、各種材料の
網状シート（スクリーンメッシュ）が利用可能である。
具体的には、ビニル系繊維、ポリエチレン系繊維、ポリ
プロピレン系繊維、弗化エチレン系繊維、ポリビニリデ
ン系繊維、アクリル系繊維、ガラス繊維、カーボン繊
維、樹脂繊維等の各種の繊維で織られたメッシュ状の織
物等が好適に例示される。There is no particular limitation on the material of the mesh sheet 12 used in the present invention, and it has a good flat shape without waving when suspended, and has such a flexibility that winding can be easily performed. , A mesh sheet (screen mesh) of various materials can be used.
Specifically, mesh woven with various fibers such as vinyl fiber, polyethylene fiber, polypropylene fiber, ethylene fluoride fiber, polyvinylidene fiber, acrylic fiber, glass fiber, carbon fiber, and resin fiber. A woven fabric or the like is preferably exemplified.
【００１２】網状シート１２の厚さにも特に限定はな
く、網状シート１２の材料や形態等に応じて、吊り下げ
た際に良好な平面となる厚さであれば良い。また、網状
シート１２の開口率（メッシュサイズ）にも特に限定は
ないが、良好な吸音特性を発現するためには、１０〜３
０メッシュ（開口２ｍｍ〜０．５９ｍｍ）程度、好まし
くは１４〜２５メッシュ（開口１．４１ｍｍ〜０．７１
ｍｍ）程度であるのが好ましい。The thickness of the mesh sheet 12 is not particularly limited as long as it is a good plane when suspended, depending on the material and form of the mesh sheet 12. Further, the aperture ratio (mesh size) of the mesh sheet 12 is not particularly limited, but is required to be 10 to 3 in order to exhibit good sound absorption characteristics.
0 mesh (opening 2 mm to 0.59 mm), preferably 14 to 25 mesh (opening 1.41 mm to 0.71)
mm).
【００１３】破断部１３を形成する方法にも特に限定は
なく、破断部１３に応じた突起が形成されたローラを用
いてアルミニウム箔１１と網状シート１２との粘着体を
前記ローラに搬送することによって破断部１３を形成す
る方法、破断部１３に応じた突起が形成されたプレス装
置で前記粘着体を押圧することによって切れ込みを入れ
て破断部１３を形成する方法等が利用可能である。ここ
で重要なのは、破断部１３を形成する際に、可能な限り
破断部１３ａを残すことである。破断部分１３ａが多い
ほど、良好な吸音特性を発現する。There is no particular limitation on the method of forming the rupture portion 13, and the adhesive body between the aluminum foil 11 and the mesh sheet 12 is conveyed to the roller by using a roller having projections corresponding to the rupture portion 13. A method of forming the fractured portion 13 by pressing the pressure-sensitive adhesive with a press device having a projection corresponding to the fractured portion 13 to form a cutout 13 can be used. What is important here is that, when forming the break portion 13, the break portion 13a is left as much as possible. The more the broken portions 13a are, the better the sound absorbing characteristics are expressed.
【００１４】破断部１３のサイズや形状、形成密度（間
隔）には特に限定はなく、網状シート１２のメッシュサ
イズに応じて適宜決定すればよい。なお、破断部１３の
サイズにも特に限定はないが、好ましくは０．１ｍｍ〜
１ｃｍ程度であり、このサイズとすることにより、吸音
特性等の点で好ましい結果を得ることができる。また、
良好な吸音特性を得るためには、破断部１３（破断部１
３ａ）の形成密度は高い（すなわち破断部分１３ａの数
が多い）方が好ましい。The size and shape of the break portion 13 and the formation density (interval) are not particularly limited, and may be appropriately determined according to the mesh size of the mesh sheet 12. The size of the break portion 13 is not particularly limited, but is preferably 0.1 mm to
The size is about 1 cm, and by using this size, a favorable result in terms of sound absorption characteristics and the like can be obtained. Also,
In order to obtain good sound absorption characteristics, the break 13 (break 1
The formation density of 3a) is preferably high (that is, the number of broken portions 13a is large).
【００１５】一方、電磁波シールド特性的には逆に、上
記破断部分１３ａのサイズはより小さく数は少ない方が
好ましい。ところで、電波に対する遮蔽効果は次のよう
に考えることができる。図４に示すように、導体に平面
波が入射すると３種類の損失が発生する。即ち、一部は
表面で反射し、他の一部は導体に進入する。進入した電
波は吸収されながら進み、再反射して導体を透過する。On the other hand, contrary to the electromagnetic wave shielding characteristics, it is preferable that the size of the broken portion 13a is smaller and the number thereof is smaller. By the way, the shielding effect on radio waves can be considered as follows. As shown in FIG. 4, when a plane wave is incident on a conductor, three types of losses occur. That is, some will reflect off the surface and some will enter the conductor. The entered radio waves travel while being absorbed, re-reflected and transmitted through the conductor.
【００１６】導体による遮蔽効果は厳密には導電率、透
磁率及び周波数に依存するが、情報処理装置で要求され
る電波遮蔽帯域（３０〜１０００ＭＨｚ）では磁気遮蔽
と異なり、高い透磁率は必要とされず、主として導電率
の効果による入射波の反射で遮蔽効果を上げることがで
きる。ところで、上記の導体で筐体を構成する場合、導
体との接続部に隙間が存在すると、そこから電磁界がも
れる可能性がある。スリット（隙間）の長さが１／２波
長になると共振し、開口部はマイクロ波帯で使われるス
ロットアンテナのような動作をし、電波の漏れは強くな
る。従って漏れを少なくするためには、１／２波長の共
振を避け、出来るだけ隙間を小さくする。（東京都立工
業技術センター編纂：ＥＭＣ技術の基礎：平成２年３月
より引用）Strictly speaking, the shielding effect of the conductor depends on the electric conductivity, the magnetic permeability and the frequency. However, unlike the magnetic shielding, the radio shielding band (30 to 1000 MHz) required for the information processing device requires a high magnetic permeability. Instead, the shielding effect can be enhanced mainly by the reflection of the incident wave due to the effect of the conductivity. By the way, in the case where the housing is made up of the above conductor, if there is a gap at a connection portion with the conductor, there is a possibility that an electromagnetic field leaks from the gap. When the length of the slit (gap) becomes 波長 wavelength, resonance occurs, the opening operates like a slot antenna used in the microwave band, and the leakage of radio waves increases. Therefore, in order to reduce the leakage, the half wavelength resonance is avoided and the gap is made as small as possible. (Compiled by Tokyo Metropolitan Industrial Technology Center: Basics of EMC technology: Quoted from March 1990)
【００１７】ところで、本発明のシート状材料は図１に
示すようにアルミニウム箔１１と可撓性を有する網状シ
ート１２の積層体であるが、このアルミニウム箔１１は
良好な導電体であり、十分に高い電磁波シールド効果を
具備している。以下に破断部１３（開口部）を有するア
ルミニウム箔１１の電磁波シールド効果について考察す
る。The sheet material of the present invention is a laminate of an aluminum foil 11 and a flexible mesh sheet 12 as shown in FIG. 1. This aluminum foil 11 is a good conductor and High electromagnetic wave shielding effect. Hereinafter, the electromagnetic wave shielding effect of the aluminum foil 11 having the broken portion 13 (opening) will be considered.
【００１８】前記の吸音特性のところで記したように、
破断部１３のサイズや形状、形成密度（間隔）には特に
限定はなく、網状シート１２のメッシュサイズに応じて
適宜決定すればよい。なお、破断部１３のサイズにも特
に限定はないが、好ましくは０．１ｍｍ〜１ｃｍ程度で
あり、このサイズとすることにより、吸音特性等の点で
好ましい結果を得ることができることを述べた。そこ
で、吸音特性的に好ましい上記破断部１３サイズが電磁
波シールド効果に及ぼす影響を計算すると以下のように
なる。As described in the above sound absorption characteristics,
The size, shape, and formation density (interval) of the break portion 13 are not particularly limited, and may be appropriately determined according to the mesh size of the mesh sheet 12. Although the size of the break portion 13 is not particularly limited, it is preferably about 0.1 mm to 1 cm, and it has been described that by setting this size, favorable results can be obtained in terms of sound absorption characteristics and the like. Therefore, the effect of the size of the broken portion 13 which is preferable in terms of sound absorption characteristics on the electromagnetic wave shielding effect is calculated as follows.
【００１９】[0019]
【数１】 (Equation 1)
【００２０】数１においてｆは周波数（Ｈｚ）を、また
λは電磁波の波長（ｍ）を示す。 λ／２＝０．１ｍｍ（１０−4ｍ）を数１に代入すると
ｆ＝１５００ＧＨｚ λ／２＝１ｃｍ（１０−２ｍ）を数１に代入するとｆ＝
１５ＧＨｚIn Equation 1, f represents a frequency (Hz), and λ represents a wavelength (m) of an electromagnetic wave. When λ / 2 = 0.1 mm (10−4 m) is substituted into Equation 1, f = 1500 GHz. When λ / 2 = 1 cm (10−2 m) is substituted into Equation 1, f =
15GHz
【００２１】従って、吸音特性が好適な前記破断部１３
のサイズ、０．１ｍｍ〜１ｃｍの範囲においては、電波
の漏れる共振周波数は前記情報処理装置で要求される遮
蔽帯域（３０〜１０００ＭＨｚ）の外側にあり、本発明
のアルミニウム箔１１に開けられた破断部１３からの電
波漏れは実質的に無視できることが明らかである。Therefore, the breaking portion 13 having a preferable sound absorbing characteristic is provided.
In the size of 0.1 mm to 1 cm, the resonance frequency at which the radio wave leaks is outside the shielding band (30 to 1000 MHz) required by the information processing apparatus, and the breakage opened in the aluminum foil 11 of the present invention. It is clear that the radio wave leakage from the unit 13 is substantially negligible.
【００２２】ところで、吸音特性と電磁波シールド特性
を兼備した材料は本発明の材料にこだわるものではな
く、アルミニウム系エキスパンドメタルおよびアルミニ
ウム系金網から選択される１以上と、アルミニウム系金
属繊維層とアルミニウム箔との積層体で構成され、かつ
前記アルミニウム箔が破断部を有し、この破断部のアル
ミニウム箔が音波によって振動可能であり、かつこの破
断部が電磁波シールド効果に悪影響を与えることのな
い、吸音特性と電磁波シールド特性を兼備したことを特
徴とする、板状材料でもよいし、またアルミニウム系パ
ンチングメタルとアルミニウム系金属繊維層と、アルミ
ニウム箔、およびアルミニウム系エキスパンドメタルと
の積層体で構成され、かつ前記アルミニウム箔が破断部
を有し、この破断部のアルミニウム箔が音波によって振
動可能であり、かつこの破断部が電磁波シールド効果に
悪影響を与えることのない、吸音特性と電磁波シールド
特性を兼備したことを特徴とする、材料であってもかま
わない。By the way, the material having both the sound absorbing property and the electromagnetic wave shielding property is not limited to the material of the present invention, but may be one or more selected from aluminum-based expanded metal and aluminum-based wire mesh, an aluminum-based metal fiber layer and an aluminum foil. And the aluminum foil has a break, the aluminum foil at the break can be vibrated by sound waves, and the break does not adversely affect the electromagnetic wave shielding effect. It may be a plate-like material, which is characterized by having both characteristics and electromagnetic wave shielding characteristics, and is composed of a laminate of an aluminum-based punched metal and an aluminum-based metal fiber layer, an aluminum foil, and an aluminum-based expanded metal, And the aluminum foil has a broken part, and the broken part Aluminum foil is oscillatable by waves, and does not adversely affect the rupture portion is an electromagnetic wave shielding effect, and wherein the having both sound-absorbing properties and electromagnetic wave shielding properties, may be a material.
【００２３】[0023]
【実施例】以下、本発明の具体的実施例を挙げ、本発明
をより詳細に説明する。Hereinafter, the present invention will be described in more detail with reference to specific examples of the present invention.
【００２４】［実施例１］厚さ７μｍのアルミニウム箔
１１とガラス繊維で織られたメッシュ状の織物（平織、
厚さ０．１５ｍｍ、２０メッシュ＝目の開き０．８４ｍ
ｍ）すなわち網状シート１２とを、塩化ビニル系接着剤
を用いて粘着した。次いで、破断部１３に応じた突起が
形成されたローラを用いて、アルミニウム箔１１と網状
シート１２との粘着体を前記ローラに搬送することによ
って、図１に示されるように破断部１３（破断部分１３
ａ）を形成し、本発明のシート状材料１０とした。なお
破断部１３は、図１中上下方向が０．３５ｍｍ、同左右
方向が０．６ｍｍの長方形である。破断部１３の形成間
隔（中心の間隔）は図１中上下方向に４ｍｍ、同左右方
向に５ｍｍとした。[Example 1] A mesh-like woven fabric (plain woven fabric, woven with 7 μm thick aluminum foil 11 and glass fiber)
0.15mm thickness, 20 mesh = 0.84m eye opening
m) That is, the reticulated sheet 12 was adhered using a vinyl chloride adhesive. Then, the adhesive body of the aluminum foil 11 and the mesh sheet 12 is conveyed to the roller by using a roller on which a projection corresponding to the rupture portion 13 is formed. Part 13
a) was formed to obtain a sheet material 10 of the present invention. In addition, the fracture | rupture part 13 is 0.35 mm in the up-down direction in FIG. The formation interval (center interval) of the break portions 13 was 4 mm vertically in FIG. 1 and 5 mm horizontally.
【００２５】上記シート状材料１０を図５に示す空気層
が１００ｍｍの筐体に取りつけて残響室法吸音率を測定
した結果を表１の（ａ）に示す。また、図６に示す厚み
が５０ｍｍの連続気泡型弾性フォーム（商品名：アコウ
スティセル）を筐体に充填し、その上面を上記シート状
材料でカバーして残響室法吸音率を測定した結果を表１
の（ｂ）に示す。表１から明らかなように、１００ｍｍ
以上の空気層を確保すれば、本発明のシート状材料１０
のみでも吸音特性を発揮するが、音源側の背後（シート
状材料１０の背面）に、前記アコウスティセルのような
多孔質吸音材を充填することにより、より高い吸音特性
を発揮することが可能となる。Table 1 (a) shows the results of measuring the sound absorption coefficient by the reverberation chamber method by mounting the sheet-like material 10 on a housing having an air space of 100 mm as shown in FIG. In addition, as shown in FIG. 6, a case was filled with an open-cell elastic foam (trade name: Acousticel) having a thickness of 50 mm, and the upper surface thereof was covered with the sheet-like material, and the reverberation chamber method sound absorption coefficient was measured. Table 1
(B) of FIG. As is clear from Table 1, 100 mm
If the above air layer is secured, the sheet material 10 of the present invention
Although sound absorbing properties are exhibited only by itself, a higher sound absorbing property can be exhibited by filling a porous sound absorbing material such as the above-mentioned acousticell in the back of the sound source side (the back of the sheet-shaped material 10). Becomes
【００２６】[0026]
【表１】 [Table 1]
【００２７】［実施例２］実施例１で製作したものと同
様のシート状材料を、同軸伝送線路法により電磁シール
ド効果を測定した結果を図７に示す。なお測定は都立産
業技術研究所に依頼して実施した。横軸に電磁波の周波
数を、縦軸に電磁波の減衰量をｄＢで示す。電磁波シー
ルド効果が全く認められない場合が減衰量０であり、−
の数値が大きくなるのに従って電磁波シールド効果が大
きくなる。図７から明らかなように、情報処理装置で要
求される遮蔽帯域（３０〜１０００ＭＨｚ）において高
い電磁波シールド効果が得られていることが分かる。[Embodiment 2] FIG. 7 shows the results of measuring the electromagnetic shielding effect of the same sheet-like material manufactured in Embodiment 1 by the coaxial transmission line method. The measurement was performed at the request of Tokyo Metropolitan Industrial Technology Research Institute. The horizontal axis indicates the frequency of the electromagnetic wave, and the vertical axis indicates the attenuation of the electromagnetic wave in dB. When no electromagnetic wave shielding effect is observed, the attenuation is 0, and-
As the value of becomes larger, the electromagnetic wave shielding effect becomes larger. As is clear from FIG. 7, it can be seen that a high electromagnetic wave shielding effect is obtained in a shielding band (30 to 1000 MHz) required for the information processing device.
【００２８】[0028]
【発明の効果】以上詳細に説明したように、可撓性を有
する網状シートと多数の破断部を有するアルミニウム箔
とを粘着し、かつ前記破断部のアルミニウム箔が音波に
よって振動可能であり、また前記アルミニウム箔の破断
部が電磁波シールド効果に悪影響を与えることのない、
吸音特性と電磁波シールド特性を兼備したシート状材料
の製造を可能とする。As described in detail above, the flexible net-like sheet is adhered to the aluminum foil having a large number of breaks, and the aluminum foil at the break can vibrate by sound waves. The broken portion of the aluminum foil does not adversely affect the electromagnetic wave shielding effect,
It is possible to manufacture a sheet-like material having both a sound absorbing property and an electromagnetic wave shielding property.
【図１】本発明の一例を示す概念図であり、アルミニウ
ム箔側から見た図である。FIG. 1 is a conceptual diagram illustrating an example of the present invention, as viewed from the aluminum foil side.
【図２】本発明の一例を示す概念図であり、網状シート
側から見た図である。FIG. 2 is a conceptual diagram illustrating an example of the present invention, as viewed from a mesh sheet side.
【図３】本発明のシート状材料に開けられた開口部を説
明する図であり、（ａ）はアルミニウム箔面方向から見
た開口部の概念図であり、（ｂ）は（ａ）図に示すｂ−
ｂ断面図である。3A and 3B are diagrams illustrating an opening formed in the sheet material of the present invention, wherein FIG. 3A is a conceptual diagram of the opening viewed from the direction of the aluminum foil surface, and FIG. B-
It is b sectional drawing.
【図４】電磁波シールドの考え方を説明する図である。FIG. 4 is a diagram illustrating the concept of an electromagnetic wave shield.
【図５】本発明のシート状材料を空気層（深さ）１００
ｍｍの筐体に取りつけた状態を示す図である。FIG. 5 shows a sheet-like material of the present invention in which an air layer (depth) 100
It is a figure which shows the state attached to the housing | casing of mm.
【図６】深さが５０ｍｍの筐体の中に連続気泡型弾性フ
ォームを充填し、その上面を本発明のシート状材料でカ
バーした状態を示す図である。FIG. 6 is a view showing a state in which an open-cell elastic foam is filled in a housing having a depth of 50 mm, and the upper surface thereof is covered with the sheet-like material of the present invention.
【図７】本発明のシート状材料の電磁波シールド効果を
測定した結果を示す図である。FIG. 7 is a view showing the result of measuring the electromagnetic wave shielding effect of the sheet material of the present invention.
１０ シート状材料 １１ アルミニウム箔 １２ 網状シート １３ 破断部 １３ａ 破断部分 １４ 筐体 １５ 筐体 １６ 連続気泡型弾性フォーム REFERENCE SIGNS LIST 10 sheet material 11 aluminum foil 12 mesh sheet 13 break 13 a break 14 housing 15 housing 16 open-cell elastic foam
───────────────────────────────────────────────────── フロントページの続き (72)発明者 井原 貫示 東京都大田区城南島２丁目２番２号株式会 社ユニックス内 Ｆターム(参考） 5D061 AA16 BB01 5E321 AA23 AA44 BB22 BB25 BB41 BB44 BB51 CC16 GG05 GH05 ────────────────────────────────────────────────── ─── Continuing on the front page (72) Inventor Kanji Ihara 2-2-2 Jonanjima, Ota-ku, Tokyo F-term in Unix Corporation 5D061 AA16 BB01 5E321 AA23 AA44 BB22 BB25 BB41 BB44 BB51 CC16 GG05 GH05
Claims (1)
部を有するアルミニウム箔とを粘着してなり、かつ前記
破断部のアルミニウム箔が音波によって振動可能であ
り、かつ前記アルミニウム箔の破断部が電磁波シールド
効果に悪影響を与えることのない、吸音特性と電磁波シ
ールド特性を兼備したことを特徴とする、シート状材
料。1. A flexible net-like sheet is adhered to an aluminum foil having a large number of breaks, and the aluminum foil at the break is vibrated by sound waves, and the aluminum foil has a break at the break. A sheet-like material characterized by having both sound absorbing characteristics and electromagnetic wave shielding characteristics without adversely affecting the electromagnetic wave shielding effect.