JP2002018992A - Coated glass cloth - Google Patents
Coated glass clothInfo
- Publication number
- JP2002018992A JP2002018992A JP2000204194A JP2000204194A JP2002018992A JP 2002018992 A JP2002018992 A JP 2002018992A JP 2000204194 A JP2000204194 A JP 2000204194A JP 2000204194 A JP2000204194 A JP 2000204194A JP 2002018992 A JP2002018992 A JP 2002018992A
- Authority
- JP
- Japan
- Prior art keywords
- glass cloth
- flame
- resin
- coated glass
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明が属する技術分野】本発明は、ガラス繊維布帛に
ポリオレフィン系樹脂および防炎難燃化合物を含有した
樹脂組成物を積層させた、防炎難燃性を有するコーテッ
ドガラス布帛に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a flame-retardant, coated glass cloth obtained by laminating a resin composition containing a polyolefin resin and a flame-retardant flame-retardant compound on a glass fiber cloth.
【０００２】[0002]
【従来の技術】従来、溶接火花・ノロ受けまたはロール
ブラインドなどに用いられている防炎性シートはガラス
繊維のフィラメント糸を用いた織編布にポリ塩化ビニル
フィルムを積層したシートが一般的に用いられている。
かかるシートは、ポリ塩化ビニル層により防炎性が付与
されており、その上織編布の強力が十分であるうえに柔
軟性があるという利点がある。しかし、かかるシートに
は可塑剤がブリードすることによる汚れや臭い等の問題
がある。また、近年環境問題がますます深刻化するなか
で、塩化ビニル樹脂製品から燃焼条件によっては塩素ガ
スや塩化水素ガス等の有毒ガスが発生し、また約８００
℃以下で焼却するとダイオキシンが発生することが判明
し、更には「環境ホルモン」との関連性も問題視される
に至っている。2. Description of the Related Art Conventionally, a flameproof sheet used for welding sparks / scrapers, roll blinds, etc. is generally a sheet obtained by laminating a polyvinyl chloride film on a woven or knitted fabric using filament yarn of glass fiber. Used.
Such a sheet is provided with flameproofness by a polyvinyl chloride layer, and has an advantage that the woven knitted fabric has sufficient strength and is flexible. However, such a sheet has problems such as dirt and odor caused by bleeding of the plasticizer. In recent years, as environmental problems have become more serious, toxic gases such as chlorine gas and hydrogen chloride gas have been generated from vinyl chloride resin products depending on the combustion conditions.
It has been found that dioxin is generated when incinerated at a temperature of less than ℃, and the relationship with “environmental hormones” has been regarded as a problem.
【０００３】ポリ塩化ビニルフィルムを積層した防炎シ
ートの替わりに、織編布にシリコン樹脂を積層させたシ
ートも従来から存在するが、非常に高価である。また、
上記防炎シートの耐溶接火花・ノロ受け性を向上するた
めに、耐炎化繊維を用いたシートも存在するが、かかる
シートに火花等が飛んだり、該シートが燃えたりする
と、シアンガスが発生し、人体および環境に有害である
という問題がある。[0003] In place of a flameproof sheet laminated with a polyvinyl chloride film, a sheet composed of a woven or knitted fabric and a silicone resin has conventionally existed, but is very expensive. Also,
In order to improve the resistance of the flameproof sheet to welding sparks and slag, there are also sheets using flame-resistant fibers.However, when sparks or the like fly on such a sheet or the sheet burns, cyan gas is generated. Harmful to the human body and the environment.
【０００４】[0004]
【発明が解決しようとする課題】本発明の目的は、防炎
性および難燃性に優れ、人体および環境にやさしく、し
かも安価なコーテッドガラス布帛を提供することにあ
る。SUMMARY OF THE INVENTION An object of the present invention is to provide an inexpensive coated glass fabric which is excellent in flame resistance and flame retardancy, is friendly to the human body and the environment, and is inexpensive.
【０００５】[0005]
【課題を解決するための手段】本発明者らは、従来織編
布に用いられていたガラス繊維のフィラメント糸のかわ
りに、防炎性および難燃性に優れた耐炎化繊維、炭素繊
維または金属繊維等を用いることを検討したが、これら
の繊維については燃焼時に有毒ガスが発生したり、また
は高価であったりなどの問題点が生じた。したがって、
かかる問題点の比較的少ないガラス繊維が、防炎難燃性
シートに最も適しているという知見を得た。Means for Solving the Problems The inventors of the present invention have replaced flame-resistant fibers, carbon fibers or flame-resistant fibers having excellent flame resistance and flame retardancy in place of glass fiber filament yarns conventionally used in woven and knitted fabrics. The use of metal fibers and the like has been considered, but these fibers have problems such as generation of toxic gas during combustion or being expensive. Therefore,
It has been found that glass fibers having relatively few such problems are most suitable for flameproof and flame retardant sheets.
【０００６】さらに本発明者らは、積層させる樹脂につ
いても検討した結果、従来用いられていた塩化ビニル樹
脂のかわりにポリオレフィン系樹脂を用いれば、燃焼時
の塩素ガスの発生や、焼却時のダイオキシン発生の可能
性をなくすことができるという知見を得た。また、該ポ
リオレフィン系樹脂に、例えば金属水酸化物などのハロ
ゲン元素を含まない防炎難燃化合物を加えることによ
り、製品の防炎性および難燃性をさらに向上させること
ができるとともに、該シートが燃焼等した際に有毒ガス
がほとんど発生しないという知見を得た。本発明者ら
は、さらに検討を重ねて本発明を完成した。The present inventors have also studied the resin to be laminated. As a result, if a polyolefin resin is used in place of the conventionally used vinyl chloride resin, generation of chlorine gas during combustion and dioxin during incineration will occur. We have found that the possibility of occurrence can be eliminated. Further, by adding a flame-retardant and flame-retardant compound containing no halogen element such as a metal hydroxide to the polyolefin-based resin, the flame retardancy and the flame retardancy of the product can be further improved, and the sheet can be further improved. It has been found that toxic gas is hardly generated when burned. The present inventors have further studied and completed the present invention.
【０００７】すなわち、本発明は、（１）ガラス布帛
に、ポリオレフィン系樹脂および防炎難燃化合物を含有
する樹脂組成物を積層したコーテッドガラス布帛、
（２）ガラス布帛が平織ガラスクロスである前記（１）
に記載のコーテッドガラス布帛、（３）防炎難燃化合物
が金属水酸化物である前記（１）または（２）に記載の
コーテッドガラス布帛、（４）金属水酸化物が水酸化マ
グネシウムまたは水酸化アルミニウムである前記（３）
に記載のコーテッドガラス布帛、および、（５）ポリオ
レフィン系樹脂が変性ポリオレフィン系樹脂を含有する
ことを特徴とする前記（１）〜（４）に記載のコーテッ
ドガラス布帛、（６）ガラス布帛がプライマー剤で処理
されていることを特徴とする前記（１）〜（５）に記載
のコーテッドガラス布帛、および、（７）プライマー剤
がポリオレフィン系樹脂である前記（６）に記載のコー
テッドガラス布帛、に関する。That is, the present invention provides (1) a coated glass cloth obtained by laminating a resin composition containing a polyolefin resin and a flame-retardant and flame-retardant compound on a glass cloth.
(2) The above (1), wherein the glass fabric is a plain-woven glass cloth.
(3) The coated glass fabric according to the above (1) or (2), wherein the flame-retardant and flame-retardant compound is a metal hydroxide, and (4) the metal hydroxide is magnesium hydroxide or water. (3) which is aluminum oxide
And (5) the coated glass cloth according to (1) to (4), wherein the polyolefin-based resin contains a modified polyolefin-based resin, and (6) the glass cloth is a primer. (1) to (5), and (7) the coated glass fabric according to (6), wherein the primer agent is a polyolefin-based resin; About.
【０００８】[0008]
【発明の実施の形態】本発明で用いられるガラス繊維と
しては、アルカリ含有率によって無アルカリタイプと含
アルカリタイプに大別されるが、前者はホウ素とフッ素
系の融剤が配合されているため電気的及び機械的特性が
優れており、電気関係の分野で使用される関係でＥガラ
スと称され、また後者は耐薬品性が高く化学的用途に用
いられるためＣガラスと称されている。いずれも本発明
で使用できる。なお、Ｃガラスはアルカリ含有率が高い
ため、アルカリ含量を下げると同時にチタンと亜鉛系の
融剤を用いたＥＣＲガラスが開発され、Ｃガラスを代替
して汎用されている。従って、ＥＣＲガラスも本発明で
使用できる。さらにＡガラス、ＬガラスまたはＳガラス
等も本発明において使用できる。BEST MODE FOR CARRYING OUT THE INVENTION The glass fibers used in the present invention are roughly classified into alkali-free type and alkali-containing type according to the alkali content. The former is based on the fact that boron and fluorine-based flux are blended. It has excellent electrical and mechanical properties and is called E-glass because it is used in the field of electrical-related fields, and the latter is called C-glass because it has high chemical resistance and is used for chemical applications. Either can be used in the present invention. Since C glass has a high alkali content, an ECR glass using a titanium and zinc-based flux has been developed at the same time as reducing the alkali content, and is commonly used instead of C glass. Therefore, ECR glass can also be used in the present invention. Further, A glass, L glass or S glass can be used in the present invention.
【０００９】本発明で用いられるガラス繊維は、モノフ
ィラメントを単に引き揃えただけのフィラメントであっ
てもよいし、これに撚りをかけたものであってもよい
し、これを編んだものであってもよい。また、下撚りを
かけた後、上撚りをかけてもよい。The glass fiber used in the present invention may be a filament obtained by simply arranging monofilaments, may be a twisted filament, or may be a knitted one. Is also good. Further, after the first twist, the first twist may be applied.
【００１０】本発明で用いられるガラス布帛としては、
例えば、織物、編物、直交積層ネット、多軸積層ネット
または不織布等が挙げられる。織物としては、例えば、
平織、朱子織、綾織、横縞織、からみ織または斜こ織な
どが挙げられる。本発明においては、平織のガラス織物
が好ましい。編物としては、例えば、平編み、ゴム編み
もしくはパール編みなどの横編み、シングルデンビー編
みもしくはシングルデンビー編みなどの縦編み、または
レース編み等が挙げられる。不織布は、繊維の集合体で
あるウェブを織ったり編んだりしないで、ウェブの繊維
同士を化学的、物理的もしくは熱や接着剤によって接着
または絡ませて作られたシート状の構造体であり、例え
ば、湿式法不織布、乾式法不織布または直接法不織布な
どが挙げられる。これら布帛は、公知の方法またはそれ
に準じる方法で製造することができる。The glass cloth used in the present invention includes:
For example, a woven fabric, a knitted fabric, an orthogonal laminated net, a multiaxial laminated net, a nonwoven fabric, and the like can be given. As a woven fabric, for example,
Examples include plain weave, satin weave, twill weave, horizontal stripe weave, leno weave, and inclined weave. In the present invention, a plain-woven glass fabric is preferred. Examples of the knitted material include flat knitting such as flat knitting, rubber knitting or pearl knitting, vertical knitting such as single denby knitting or single denby knitting, and lace knitting. Nonwoven fabric is a sheet-like structure made by bonding or tangling the fibers of the web chemically, physically or by heat or an adhesive without weaving or knitting the web which is an aggregate of fibers, for example, , Wet-process nonwoven fabric, dry-process nonwoven fabric, and direct-process nonwoven fabric. These fabrics can be manufactured by a known method or a method analogous thereto.
【００１１】本発明で用いられるガラス繊維布帛は、ガ
ラス長繊維を用いたものであっても、ガラス短繊維を用
いたものであってもよい。すなわち、例えば、ヤーンか
ら織成された平織、からみ織、朱子織もしくは綾織等の
ガラスクロス、ロービングから織成されたロービングク
ロス、ガラス直交積層ネット、または編物などの織編布
状のもの；チョップドストランドマットやサーフェ−シ
ングマット等の短繊維マット、もしくはダイヤモンドマ
ットやスワールマット等の長繊維マットなどによる不織
布状のもの；または、ガラスペーパーなどが挙げられ
る。これらは、公知またはそれに準ずる方法で製造で
き、また一般市販品が便宜に適用される。The glass fiber fabric used in the present invention may be one using long glass fibers or one using short glass fibers. That is, for example, glass cloth such as plain weave, leno weave, satin weave or twill weave woven from yarn, roving cloth woven from roving, glass cross laminated net, or woven or knitted cloth such as knitted fabric; chopped Nonwoven fabrics such as short fiber mats such as strand mats and surfacing mats, or long fiber mats such as diamond mats and swirl mats; and glass paper. These can be produced by a known method or a method analogous thereto, and generally commercially available products are conveniently applied.
【００１２】本発明で用いられるガラス繊維布帛は、樹
脂組成物との親和性を高めるために、プライマー処理を
行うのが好ましい。プライマー処理は通常、プライマー
剤をガラス布帛の片面または両面に所望量塗布するか、
バスの中に充填したプライマー剤に浸漬して、引き上げ
て余剰量をしぼり取って乾燥することにより行われる。
塗布の方法としては、公知の方法を用いることができる
が、例えば、その塗布方法としては、例えばアプリケー
ター、ナイフコーター、リバースロールコーター、グラ
ビアコーター、フローコーター、ロッドコーターまたは
刷毛など公知の手段を用いて行う方法が挙げられる。The glass fiber cloth used in the present invention is preferably subjected to a primer treatment in order to increase the affinity with the resin composition. Priming is usually performed by applying a desired amount of a primer agent to one or both sides of a glass cloth,
It is carried out by dipping in a primer filled in a bath, pulling it up, squeezing out an excess amount, and drying.
As a method of application, a known method can be used.For example, as the application method, for example, a known means such as an applicator, a knife coater, a reverse roll coater, a gravure coater, a flow coater, a rod coater, or a brush is used. Method.
【００１３】プライマー剤としては、公知のプライマー
剤を用いてよいが、ポリオレフィン系樹脂が好ましい。
該ポリオレフィン樹脂は、ディスパージョンであっても
よいし、エマルジョンであってもよい。ポリオレフィン
系樹脂としては、ポリエチレン系樹脂またはポリプロピ
レン系樹脂等が挙げられる。また、プライマー剤として
は、これらの樹脂を公知手段に従って酸変性させたもの
であってもよいし、さらにアイオノマー化されたもので
あってもよい。より具体的には、ケミパール（三井化学
株式会社製）、アクアテックス（中央理化工株式会社
製）またはマレイン酸変性ポリプロピレン樹脂ディスパ
ージョン（ＭＧＰ−１６５０；丸芳化成品株式会社製）
などが挙げられる。なお、通常本発明においてガラス布
帛に積層する樹脂組成物にポリエチレン系樹脂が含有さ
れている場合は、プライマー剤としてポリエチレン系プ
ライマー剤を用いるのが好ましく、また、樹脂組成物に
ポリプロピレン系樹脂が含有されている場合は、プライ
マー剤としてポリプロピレン系プライマー剤を用いるの
が好ましい。As the primer, known primers may be used, but polyolefin resins are preferred.
The polyolefin resin may be a dispersion or an emulsion. Examples of the polyolefin-based resin include a polyethylene-based resin and a polypropylene-based resin. The primer may be a resin obtained by acid-modifying these resins according to known means, or may be an ionomer. More specifically, Chemipearl (manufactured by Mitsui Chemicals, Inc.), Aquatex (manufactured by Chuo Rika Co., Ltd.) or maleic acid-modified polypropylene resin dispersion (MGP-1650; manufactured by Maruyoshi Kaseihin Co., Ltd.)
And the like. In general, when a polyethylene resin is contained in the resin composition to be laminated on the glass cloth in the present invention, it is preferable to use a polyethylene primer as a primer, and the resin composition contains a polypropylene resin. In such a case, it is preferable to use a polypropylene primer as the primer.
【００１４】ガラス布帛に対するプライマー剤の割合
は、乾燥後のガラス布帛の重量に対し、プライマー剤の
付着率が約０．５〜６０重量％程度、好ましくは約５〜
３０重量％程度である。The ratio of the primer to the glass cloth is such that the adhesion of the primer is about 0.5 to 60% by weight, preferably about 5 to 60% by weight, based on the weight of the dried glass cloth.
It is about 30% by weight.
【００１５】本発明で用いられるポリオレフィン樹脂と
しては、例えば、低密度、中密度もしくは高密度ポリエ
チレン、超高分子量ポリエチレン、直鎖状低密度ポリエ
チレン樹脂またはメタロセン触媒系直鎖状低密度ポリエ
チレン樹脂などのポリエチレン樹脂が挙げられる。ま
た、エチレン−酢酸ビニル共重合体、エチレン−アクリ
ル酸共重合体、エチレン−メタクリル酸共重合体、アイ
オノマー樹脂、エチレン−メチルアクリレート共重合
体、エチレン−メチルメタクリレート共重合体、エチレ
ン−エチルアクリレート共重合体、エチレン−ビニルア
ルコール共重合体などのポリエチレン共重合体樹脂も挙
げられる。ポリプロピレン樹脂、マレイン酸変性ポリプ
ロピレン樹脂、リアクターＴＰＯまたはＴＰＯも、本発
明におけるポリオレフィン樹脂として用いることができ
る。また、架橋ポリエチレン、エチレン−プロピレンコ
ポリマー、エチレン−プロピレン−ジエンターポリマ
ー、プロピレンのホモポリマーおよびコポリマーからな
る各種熱可塑性オレフィン、ブタジエン、イソプレンと
スチレンをベースとした各種熱可塑性エラストマー類な
どもポリオレフィン樹脂として用いることができる。こ
れらは、単独で用いてもよいし、２種以上を混合しても
よい。The polyolefin resin used in the present invention includes, for example, low density, medium density or high density polyethylene, ultra high molecular weight polyethylene, linear low density polyethylene resin or metallocene catalyst linear low density polyethylene resin. A polyethylene resin may be used. Further, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, ethylene-methacrylic acid copolymer, ionomer resin, ethylene-methyl acrylate copolymer, ethylene-methyl methacrylate copolymer, ethylene-ethyl acrylate copolymer A polyethylene copolymer resin such as a polymer and an ethylene-vinyl alcohol copolymer is also included. Polypropylene resin, maleic acid-modified polypropylene resin, reactor TPO or TPO can also be used as the polyolefin resin in the present invention. In addition, crosslinked polyethylene, ethylene-propylene copolymer, ethylene-propylene-diene terpolymer, various thermoplastic olefins composed of homopolymers and copolymers of propylene, butadiene, various thermoplastic elastomers based on isoprene and styrene are also polyolefin resins. Can be used. These may be used alone or as a mixture of two or more.
【００１６】本発明で用いられるポリオレフィン樹脂と
しては、中でも、メタロセン触媒系直鎖状低密度ポリエ
チレン樹脂のＣ８コポリマーもしくはＣ６コポリマー、
エチレン−酢酸ビニル共重合体、エチレン−アクリル酸
共重合体、エチレン−メタクリル酸共重合体、アイオノ
マー樹脂、エチレン−ビニルアルコール共重合体または
リアクターＴＰＯなどが好ましい。[0016] The polyolefin resin used in the present invention, among others, C 8 copolymer or C 6 copolymers of metallocene catalyzed linear low density polyethylene resin,
Preferred are an ethylene-vinyl acetate copolymer, an ethylene-acrylic acid copolymer, an ethylene-methacrylic acid copolymer, an ionomer resin, an ethylene-vinyl alcohol copolymer or a reactor TPO.
【００１７】これらのオレフィン樹脂は、所望により用
いる樹脂に応じて分解性発泡剤または石油系溶剤などの
揮発性発泡剤を用いて低発泡成形法または高発泡成形法
などの公知の方法で発泡プラスチックとし、断熱機能、
衝撃吸収機能、軽量機能、遮音・吸音機能、弾性機能ま
たは装飾機能などを付与してもよい。These olefin resins can be foamed by a known method such as a low-foaming molding method or a high-foaming molding method using a decomposable foaming agent or a volatile foaming agent such as a petroleum-based solvent, depending on the resin used if desired. And insulation function,
A shock absorbing function, a lightweight function, a sound insulation / sound absorbing function, an elastic function, a decorative function, or the like may be provided.
【００１８】本発明においては、上記ポリオレフィン系
樹脂に防炎難燃化合物を含有させる。防炎難燃化合物と
しては、ハロゲン原子を含まないものが好ましい。燃焼
等したときに有毒ガスが発生しないからである。中で
も、金属水酸化物や含水無機結晶化合物が好ましい。そ
のような化合物としては、水酸化アルミニウム、水酸化
マグネシウム、水酸化カルシウム、塩基性炭酸マグネシ
ウム、ハイドロタルク石群、二水和石こうまたはアルミ
ン酸化カルシウム等を挙げることができる。ハイドロタ
ルク石群は含水炭酸塩鉱物で、例えば、ハイドロタルク
石、スチヒタイトまたはパイロオーライト等が挙げられ
る。In the present invention, the polyolefin resin contains a flame-retardant and flame-retardant compound. As the flame-retardant flame-retardant compound, those containing no halogen atom are preferred. This is because no toxic gas is generated when burning or the like. Among them, metal hydroxides and hydrous inorganic crystal compounds are preferred. Examples of such compounds include aluminum hydroxide, magnesium hydroxide, calcium hydroxide, basic magnesium carbonate, hydrotalcite, gypsum dihydrate and calcium aluminate. The hydrotalcite group is a hydrated carbonate mineral, and examples thereof include hydrotalcite, stichitite, and pyroaurite.
【００１９】これらの化合物は、その種類によって分解
温度及び吸熱量に幾分差があるが、高温加熱時に分解し
て吸熱作用により難燃化効果を示すという点では全く共
通している。従って、基本的に前記した化合物のいずれ
を用いてもよいが入手価格等の経済性をも考慮すると、
水酸化マグネシウムまたは水酸化アルミニウムが最適で
ある。これらは、単独で用いてもよいし、２種以上を混
合してもよい。防炎難燃化合物の粒子径は細かいほどよ
いが、約０．００１〜１０μｍ程度が好ましい。These compounds have some differences in decomposition temperature and endothermic amount depending on the kind thereof, but they are completely common in that they decompose when heated at a high temperature and exhibit a flame-retarding effect by an endothermic effect. Therefore, basically any of the compounds described above may be used, but also considering the economics such as the acquisition price,
Optimum is magnesium hydroxide or aluminum hydroxide. These may be used alone or as a mixture of two or more. The finer the particle size of the flame-retardant and flame-retardant compound, the better, but preferably about 0.001 to 10 μm.
【００２０】また、防炎難燃化合物として、さらに鉱物
質を含有させてもよい。鉱物質としては、具体的には微
細な粉末状雲母、微細な鱗片状又は針状もしくは繊維状
（ウィスカー）雲母が好ましく、微細な人工雲母、マイ
カ、グラファイト、雲母状グラファイト、雲母状ガラ
ス、チタン化合物、砒素化合物、タルク、石炭またはセ
ッコウ等であってもよい。粒径は約１〜２５μｍ程度の
ものが好適である。Further, a mineral substance may be further contained as a flame-retardant flame-retardant compound. As the mineral substance, specifically, fine powdered mica, fine scale-like or needle-like or fibrous (whisker) mica is preferable, fine artificial mica, mica, graphite, mica-like graphite, mica-like glass, titanium It may be a compound, an arsenic compound, talc, coal or gypsum. The particle size is preferably about 1 to 25 μm.
【００２１】このような雲母として、例えばコープケミ
カル株式会社製ミクロマイカＭＫ−１００等が挙げられ
る。チタン化合物としては、ウィスカー状のチタンカリ
ウム（例えば大塚化学株式会社製ティスモ（登録商
標））、硼素化合物としては、ホウ酸アルミニウム（例
えば四国化成株式会社製アルボレックス（登録商
標））、雲母状ガラスとしては、例えば日本板硝子株式
会社製のフレカREF−０１５A、雲母状グラファイトとし
ては例えば住友ケミカル株式会社製５０LTUN、SS−３N
等が例示される。Examples of such mica include Micromica MK-100 manufactured by Corp Chemical Co., Ltd. As the titanium compound, whisker-like titanium potassium (for example, Tismo (registered trademark) manufactured by Otsuka Chemical Co., Ltd.), and as the boron compound, aluminum borate (for example, Albolex (registered trademark) manufactured by Shikoku Chemicals Co., Ltd.), mica-like glass For example, Fleca REF-015A manufactured by Nippon Sheet Glass Co., Ltd., and as mica-like graphite, for example, 50LTUN, SS-3N manufactured by Sumitomo Chemical Co., Ltd.
Etc. are exemplified.
【００２２】防炎難燃化合物の配合量は、樹脂組成物１
００重量部に対して約３０〜８０重量部程度、より好ま
しくは約５０〜７０重量部程度である。The amount of the flame-retardant and flame-retardant compound is as follows:
The amount is about 30 to 80 parts by weight, more preferably about 50 to 70 parts by weight, per 100 parts by weight.
【００２３】上記ポリオレフィン系樹脂は、防炎難燃化
合物との相溶性を高めるために、所望により変性ポリオ
レフィン系樹脂を含有していてもよい。変性ポリオレフ
ィン系樹脂としては、例えばマレイン酸、（メタ）アク
リル酸、フマル酸、テトラヒドロフタル酸、イタコン
酸、クロトン酸、イソクロトン酸、シトラコン酸等で変
性させたポリプロピレン樹脂、アイオノマー変性させた
ポリエチレン等が挙げられる。とくに、酸変性させたポ
リオレフィン系樹脂、中でもマレイン酸変性ポリオレフ
ィン樹脂が好ましい。変性ポリオレフィン系樹脂は、変
性させていないポリオレフィン系樹脂に対して、約０．
１〜２０重量部程度混合させることが好ましい。The above-mentioned polyolefin resin may optionally contain a modified polyolefin resin in order to increase the compatibility with the flame-retardant and flame-retardant compound. Examples of the modified polyolefin-based resin include a polypropylene resin modified with maleic acid, (meth) acrylic acid, fumaric acid, tetrahydrophthalic acid, itaconic acid, crotonic acid, isocrotonic acid, citraconic acid, etc., and an ionomer-modified polyethylene. No. In particular, an acid-modified polyolefin resin, particularly a maleic acid-modified polyolefin resin, is preferable. The modified polyolefin-based resin is about 0.
It is preferable to mix about 1 to 20 parts by weight.
【００２４】他方、防炎難燃化合物に対しても、ポリオ
レフィン系樹脂との相溶性を高める表面処理剤、例えば
オレイン酸、ラウリン酸、ミリスチン酸、パルミチン
酸、ベヘニン酸、ステアリン酸、イソステアリン酸、ダ
イマー酸のような各種脂肪酸を添加することができる。
中でも、オレイン酸またはステアリン酸が好ましい。On the other hand, also for the flame retardant and flame retardant compounds, surface treatment agents for improving the compatibility with the polyolefin resin, for example, oleic acid, lauric acid, myristic acid, palmitic acid, behenic acid, stearic acid, isostearic acid, Various fatty acids such as dimer acid can be added.
Among them, oleic acid or stearic acid is preferred.
【００２５】樹脂組成物には、さらに所望により、例え
ば、酸化防止剤、光安定剤、顔料、無機充填剤、紫外線
吸収剤、帯電防止剤、滑剤、分散剤、架橋剤、発泡剤ま
たは核剤等の通常用いられる添加剤を配合してもよい。
酸化防止剤としては、例えばフェノール系またはアミン
系の酸化防止剤等が挙げられる。光安定剤としては、例
えばヒンダードアミン系光安定剤等が挙げられる。顔料
としては、例えば、酸化チタン、酸化鉄もしくはカーボ
ンブラック等の無機顔料またはフタロシアニンブルー等
の有機顔料などが挙げられる。無機充填剤としては例え
ば、炭酸カルシウム、シリカ、タルク、硫酸バリウム、
クレー、マイカまたは珪砂などが挙げられる。紫外線吸
収剤としては、例えば、ベンゾフェノン系、ベンゾトリ
アゾール系、サルチレート系またはアクリロニトリル系
紫外線吸収剤等が挙げられる。帯電防止剤としては、例
えば、アニオン系、カチオン系または非イオン系界面活
性剤等が挙げられる。滑剤としては、例えば、炭化水素
系、脂肪酸系、脂肪酸アミド系、エステル系、アルコー
ル系または金属石鹸系滑剤等が挙げられる。発泡剤とし
ては、例えば、ペンタンもしくはヘキサン等の揮発性発
泡剤、または、重炭酸ナトリウム等の無機系発泡剤もし
くはアゾ系やニトロソ系の有機系発泡剤等が挙げられ
る。If desired, the resin composition may further contain, for example, an antioxidant, a light stabilizer, a pigment, an inorganic filler, an ultraviolet absorber, an antistatic agent, a lubricant, a dispersant, a crosslinking agent, a foaming agent or a nucleating agent. And other commonly used additives.
Examples of the antioxidant include phenol-based or amine-based antioxidants. Examples of the light stabilizer include a hindered amine light stabilizer and the like. Examples of the pigment include inorganic pigments such as titanium oxide, iron oxide and carbon black, and organic pigments such as phthalocyanine blue. As the inorganic filler, for example, calcium carbonate, silica, talc, barium sulfate,
Clay, mica or quartz sand may be used. Examples of the ultraviolet absorber include a benzophenone-based, benzotriazole-based, sulfylate-based, or acrylonitrile-based ultraviolet absorber. Examples of the antistatic agent include an anionic, cationic or nonionic surfactant. Examples of the lubricant include a hydrocarbon-based, fatty acid-based, fatty acid amide-based, ester-based, alcohol-based, or metal soap-based lubricant. Examples of the foaming agent include a volatile foaming agent such as pentane or hexane, an inorganic foaming agent such as sodium bicarbonate, and an azo- or nitroso-based organic foaming agent.
【００２６】本発明における樹脂組成物は、上記ポリオ
レフィン系樹脂に、上記防炎難燃化合物および所望によ
り上記の添加剤を、ヘンシェルミキサーなど公知の機器
を用いて混合し、製造する。The resin composition of the present invention is produced by mixing the above-mentioned flame-retardant flame-retardant compound and, if desired, the above-mentioned additives with the above-mentioned polyolefin resin using a known device such as a Henschel mixer.
【００２７】本発明においては、上記樹脂組成物を上記
ガラス布帛の両面または片面に積層させる。積層させる
方法としては、公知またはそれに準ずる方法を用いてよ
いが、溶融押し出し法またはカレンダー法により積層す
るのが好ましい。また、該ガラス布帛に該樹脂組成物を
公知の方法により塗布したり、または浸漬させた後余剰
分を絞りとったりして、乾燥させることにより積層して
もよい。樹脂組成物の厚さは、約１０μｍ〜３ｍｍ程度
が好ましい。約１０μｍ未満では後加工における溶着強
度が不十分となり、３ｍｍ程度を超えると柔軟性が損な
われる。In the present invention, the above resin composition is laminated on both sides or one side of the above glass cloth. As a method of laminating, a known method or a method similar thereto may be used, but it is preferable to laminate by a melt extrusion method or a calender method. Alternatively, the resin composition may be applied to the glass cloth by a known method, or the resin composition may be immersed and then squeezed out, and then dried and laminated. The thickness of the resin composition is preferably about 10 μm to 3 mm. If it is less than about 10 μm, the welding strength in post-processing will be insufficient, and if it exceeds about 3 mm, the flexibility will be impaired.
【００２８】上記のようにして形成した積層体に公知の
処理を行ってもよい。例えば、上記積層体を所定寸法に
裁断し、高周波ウエルダにより接合および周縁の折り返
し加工等を行い、次いで鳩目を打設するなどの処理が挙
げられる。このようにして得られたコーテッドガラス布
帛は、ＪＩＳＡ１３２３「建築工事用シートの溶接及び
溶断火花に対する難燃性試験」に規定する難燃性規格に
合格する性能を有しているものが好ましい。A known treatment may be applied to the laminate formed as described above. For example, the laminate may be cut into a predetermined size, bonded and wrapped around the periphery by a high-frequency welder, and then an eyelet may be placed. The coated glass fabric thus obtained preferably has a performance that meets the flame retardancy standard specified in JIS A1323 “Test for flame resistance against welding and fusing sparks of building construction sheets”.
【００２９】本発明にかかるコーテッドガラス布帛は、
難燃性または防炎性を必要とする用途であれば、いかな
る用途にでも用いることができるが、例えば、溶接火花
・ノロ受け、テント、ロールブラインド、バーチカルブ
ラインド、仏壇用ローソク・線香の下敷き、非常持出袋
・貴重品袋、防火衣・炉前作業衣、フレキシブルダク
ト、断熱フトンカバー・ラギング、カーテン、防火・防
煙シャッター、映写幕、危険物カバーまたはケーブルカ
バー等の用途に好適に使用される。[0029] The coated glass fabric according to the present invention comprises:
It can be used for any purpose as long as it requires flame retardancy or flame resistance.For example, welding sparks / scrapers, tents, roll blinds, vertical blinds, candles for inscriptions on Buddhist altars, incense sticks, Suitable for use in emergency take-out bags, valuables bags, fire protection clothing / work clothes in front of furnaces, flexible ducts, insulated futon covers / lagging, curtains, fire / smoke protection shutters, projection screens, hazardous material covers, cable covers, etc. Is done.
【００３０】[0030]
【実施例】平織ガラスクロスＨ３３０ Ｆ６ １１２Ｌ
（ユニチカグラスファイバー株式会社製）を、マレイン
酸変性ポリプロピレン樹脂ディスパージョン（ＭＧＰ−
１６５０；丸芳化成品株式会社製）に浸漬し、余剰分を
縛って、ドライヤーで１５０℃の温風を３分間あて乾燥
させた。このとき樹脂の固形分濃度は３０重量％であっ
た。また、プライマー剤の付着率は９重量％であった。[Example] Plain-woven glass cloth H330 F6 112L
(Manufactured by Unitika Glass Fiber Co., Ltd.) using maleic acid-modified polypropylene resin dispersion (MGP-
1650; Maruyoshi Kaseihin Co., Ltd.), tied the excess, and dried with hot air at 150 ° C. for 3 minutes. At this time, the solid content of the resin was 30% by weight. The adhesion rate of the primer was 9% by weight.
【００３１】リアクターＴＰＯ（キャタロイ ＫＳ−３
５９Ｐ；モンテル エスディーケーサンライズ株式会社
製）３０重量部、マレイン酸変性ポリプロピレン樹脂３
重量部および水酸化マグネシウム（キスマ５Ａ；協和化
学株式会社製）６７重量部を、ヘンシェルミキサーにて
混合し、溶融押し出し法にて上記平織ガラスクロスの片
面に、２００μｍの厚さに積層した。Reactor TPO (Cataroy KS-3)
59P, manufactured by Montell SDK Sunrise Co., Ltd.) 30 parts by weight, maleic acid-modified polypropylene resin 3
Parts by weight and 67 parts by weight of magnesium hydroxide (Kisuma 5A; manufactured by Kyowa Chemical Industry Co., Ltd.) were mixed with a Henschel mixer, and laminated on one side of the plain woven glass cloth to a thickness of 200 μm by a melt extrusion method.
【００３２】上記のように製造されたコーテッドガラス
布帛について、ＪＩＳＡ１３２３「建築工事用シートの
溶接及び溶断火花に対する難燃性試験」に規定する難燃
性試験を行ったところ、Ｂ種合格であった。The coated glass fabric produced as described above was subjected to a flame retardancy test specified in JIS A1323 "Flame retardancy test for welding and fusing sparks of building construction sheets". .
【００３３】[0033]
【発明の効果】本発明に係るコーテッドガラス布帛は防
炎性および難燃性に優れているので、防炎性または難燃
性が要求される用途に好適なコーテッドガラス布帛を提
供できるという効果を奏す。本発明に係るコーテッドガ
ラス布帛は安価に製造できるため、産業上有利である。
また、本発明に係るコーテッドガラス布帛は、火花が飛
んだり、燃やしたりしても有毒ガスをほとんど発生する
ことがないので、本発明は人体および環境にやさしい製
品を提供できる。The coated glass fabric according to the present invention is excellent in flame retardancy and flame retardancy, so that it is possible to provide a coated glass fabric suitable for applications requiring flame retardancy or flame retardancy. Play. Since the coated glass fabric according to the present invention can be manufactured at low cost, it is industrially advantageous.
In addition, the coated glass fabric according to the present invention hardly generates toxic gas even when a spark flies or burns, so that the present invention can provide a product that is friendly to the human body and the environment.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０８Ｌ 23/00 Ｃ０８Ｌ 23/00 ４Ｌ０３３ Ｃ０９Ｋ 21/02 Ｃ０９Ｋ 21/02 // Ｄ０６Ｍ 11/44 Ｄ０６Ｍ 15/227 11/45 Ｄ０６Ｍ 101:00 15/227 11/14 Ｄ０６Ｍ 101:00 Ｆターム(参考） 4F072 AB09 AB28 AD04 AF03 AF04 AH46 AK05 AL09 4F100 AA01B AA17B AA18B AA19B AG00A AK03A AK03B AK07 AL06B AL07 BA02 DG11A EJ65A GB90 JJ07 JJ07B JL01 JL02 4H028 AA10 AA12 AA43 BA05 4J002 BB031 BB051 BB061 BB071 BB081 BB121 BB211 DE076 DE146 FD206 4L031 AA26 AB32 BA11 DA16 4L033 AA09 AB05 AC05 CA12 CA70 DA07 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C08L 23/00 C08L 23/00 4L033 C09K 21/02 C09K 21/02 // D06M 11/44 D06M 15/227 11/45 D06M 101: 00 15/227 11/14 D06M 101: 00 F term (reference) 4F072 AB09 AB28 AD04 AF03 AF04 AH46 AK05 AL09 4F100 AA01B AA17B AA18B AA19B AG00A AK03A AK03B AK07 AL06B AL07 BA02 DG11J01 EJ90J01 4H028 AA10 AA12 AA43 BA05 4J002 BB031 BB051 BB061 BB071 BB081 BB121 BB211 DE076 DE146 FD206 4L031 AA26 AB32 BA11 DA16 4L033 AA09 AB05 AC05 CA12 CA70 DA07
Claims (7)
よび防炎難燃化合物を含有する樹脂組成物を積層したコ
ーテッドガラス布帛。1. A coated glass cloth obtained by laminating a resin composition containing a polyolefin resin and a flame retardant compound on a glass cloth.
求項１に記載のコーテッドガラス布帛。2. The coated glass cloth according to claim 1, wherein the glass cloth is a plain-woven glass cloth.
求項１または２に記載のコーテッドガラス布帛。3. The coated glass fabric according to claim 1, wherein the flame-retardant flame-retardant compound is a metal hydroxide.
は水酸化アルミニウムである請求項３に記載のコーテッ
ドガラス布帛。4. The coated glass fabric according to claim 3, wherein the metal hydroxide is magnesium hydroxide or aluminum hydroxide.
ィン系樹脂を含有することを特徴とする請求項１〜４に
記載のコーテッドガラス布帛。5. The coated glass cloth according to claim 1, wherein the polyolefin-based resin contains a modified polyolefin-based resin.
いることを特徴とする請求項１〜５に記載のコーテッド
ガラス布帛。6. The coated glass cloth according to claim 1, wherein the glass cloth is treated with a primer.
ある請求項６に記載のコーテッドガラス布帛。7. The coated glass cloth according to claim 6, wherein the primer agent is a polyolefin resin.