JP2001338709A - Conductive wire for rubber connector, and the rubber connector - Google Patents
Conductive wire for rubber connector, and the rubber connectorInfo
- Publication number
- JP2001338709A JP2001338709A JP2000197278A JP2000197278A JP2001338709A JP 2001338709 A JP2001338709 A JP 2001338709A JP 2000197278 A JP2000197278 A JP 2000197278A JP 2000197278 A JP2000197278 A JP 2000197278A JP 2001338709 A JP2001338709 A JP 2001338709A
- Authority
- JP
- Japan
- Prior art keywords
- rubber connector
- wire
- conductive wire
- rubber
- connector
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、電気・電子機器の
電気的接続に好適なゴムコネクター用導電線およびそれ
を使用したゴムコネクターに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a conductive wire for a rubber connector suitable for electrical connection of electric / electronic devices and a rubber connector using the same.
【０００２】[0002]
【従来の技術】従来より、各種電気・電子機器の電気的
接続にシリコーンゴム中に導電線を埋め込んだあるいは
シリコーンゴムの板と板の間に導電線を設置し、接着剤
で接合したゴムコネクターが使用されている。導電線と
しては、一般に真鍮やリン青銅などの金属線が使用され
ている。2. Description of the Related Art Conventionally, a rubber connector in which a conductive wire is embedded in silicone rubber or a conductive wire is placed between silicone rubber plates and bonded with an adhesive has been used for electrical connection of various electric and electronic devices. Have been. Generally, a metal wire such as brass or phosphor bronze is used as the conductive wire.
【０００３】金属線を使用した従来のゴムコネクター
は、図１および図２に示したように直線状に配置したも
のおよび屈曲状に配置したものである。Conventional rubber connectors using metal wires are arranged linearly and bent as shown in FIGS. 1 and 2.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、従来の
金属線を使用したゴムコネクターにおいて、金属線を直
線状に配置したものはゴムコネクターを加圧して電気的
接合を行う場合、金属線が直線状のため加圧力を大きく
する必要があり、また加圧力が強すぎた場合には金属線
が座屈するという不具合があった。However, in a conventional rubber connector using a metal wire, in which the metal wire is arranged in a straight line, when the rubber connector is pressurized and electrically connected, the metal wire is straightened. Therefore, it is necessary to increase the pressing force, and when the pressing force is too strong, there is a problem that the metal wire buckles.
【０００５】一方、金属線を屈曲状に配置したものは、
金属線を直線状に配置したゴムコネクターを加圧して金
属線を屈曲させたものであるため、各々のゴムコネクタ
ーにおいて金属線の屈曲点が図２に示したように一様で
ないことから、ゴムコネクターを加圧して電気的接合を
する際の加圧力がそれぞれ異なってしまうという不具合
があった。[0005] On the other hand, when the metal wires are arranged in a bent shape,
Since the metal wire is bent by pressing a rubber connector in which metal wires are arranged in a straight line, the bending point of the metal wire is not uniform in each rubber connector as shown in FIG. There has been a problem that the pressing force at the time of electrical connection by pressurizing the connector differs from one another.
【０００６】本発明は、このような従来のゴムコネクタ
ーの問題点を解決するためになされたものであり、ゴム
コネクターを加圧して電気的に接続する際に加圧力が小
さくてすみ、また加圧力が大きすぎた場合でも導電線が
座屈することがないゴムコネクター用導電線およびゴム
コネクターを提供することを目的としている。The present invention has been made in order to solve the problems of the conventional rubber connector, and requires only a small pressing force when pressing and electrically connecting the rubber connector. An object of the present invention is to provide a conductive wire for a rubber connector and a rubber connector in which the conductive wire does not buckle even when the pressure is too large.
【０００７】[0007]
【課題を解決するための手段】本発明に係るゴムコネク
ター用導電線は、図３に示したように金属線と合成樹脂
線とを撚り合せた構造を有することを特徴としている。
また、本発明のゴムコネクターは金属線と合成樹脂線と
を撚り合せた導電線をシリコーンゴム中に設置したこと
を特徴としている。A conductive wire for a rubber connector according to the present invention is characterized in that it has a structure in which a metal wire and a synthetic resin wire are twisted as shown in FIG.
Further, the rubber connector of the present invention is characterized in that a conductive wire obtained by twisting a metal wire and a synthetic resin wire is provided in silicone rubber.
【０００８】本発明のゴムコネクター用導電線に使用さ
れる金属線としては、電気信号を伝えることができれば
どのような金属でも良いが、伸線加工が容易で強度も比
較的高い真鍮、リン青銅、ニッケル等が望ましい。な
お、強度は高いが電気抵抗も高い金属線を使用する場合
には、電気抵抗を低くするために金属線に金メッキや銅
メッキ等を行えば良い。The metal wire used for the conductive wire for a rubber connector of the present invention may be any metal as long as it can transmit an electric signal, but brass and phosphor bronze which are easy to wire and have relatively high strength. , Nickel and the like are desirable. When a metal wire having a high strength and a high electric resistance is used, the metal wire may be plated with gold or copper to reduce the electric resistance.
【０００９】金属線と撚り合せる合成樹脂線としては、
どのような種類のものでも良いが、使用する金属と同等
以上の強度を有するものが望ましい。As a synthetic resin wire to be twisted with a metal wire,
Any type may be used, but a material having a strength equal to or higher than that of the metal to be used is desirable.
【００１０】本発明に係る金属線ならびに合成樹脂線の
線径は、ゴムコネクターに要求される特性に応じて変化
させることができる。The wire diameter of the metal wire and the synthetic resin wire according to the present invention can be changed according to the characteristics required for the rubber connector.
【００１１】[0011]
【発明の実施の形態】以下、本発明の実施例について説
明する。 ［第１の実施例］表面に０．１μｍの金メッキを施した
直径３０μｍ、引張強さ１１５ｋｇ／ｍｍ２の真鍮線と
直径３０μｍ、引張強さ１８０ｋｇ／ｍｍ２の合成樹脂
線とを撚糸機で撚り合せてゴムコネクター用導電線を得
た。Embodiments of the present invention will be described below. First Embodiment diameter 30 [mu] m gold-plated of 0.1μm on the surface, the tensile strength 115 kg / mm 2 brass wire and a diameter of 30 [mu] m, and a synthetic resin line of tensile strength 180 kg / mm 2 in twister Twisted to obtain a conductive wire for a rubber connector.
【００１２】この導電線をシリコーンゴムの板と板の間
に接着剤で固定し、ゴムコネクターを得た。このゴムコ
ネクターを加圧し電気的接続を行ったところ、直線的に
配置した従来のゴムコネクターに比べ加圧力が少なくて
も均一な電気的接続ができた。また、座屈もなく良好な
結果であった。The conductive wire was fixed between the silicone rubber plates with an adhesive to obtain a rubber connector. When this rubber connector was pressurized and made an electrical connection, a uniform electrical connection was achieved even with a smaller pressing force than a conventional rubber connector arranged linearly. The results were good without buckling.
【００１３】［第２の実施例］引張強さが１１０ｋｇ／
ｍｍ２を有する直径３０μｍの１８金線と直径が３０μ
ｍ、引張強さ１８０ｋｇ／ｍｍ２の合成樹脂線とを第１
の実施例と同様に撚糸機で撚り合せてゴムコネクター用
導電線を得た。Second Embodiment Tensile strength is 110 kg /
18 gold wire and the diameter of the diameter 30μm with mm 2 is 30μ
m, a synthetic resin wire having a tensile strength of 180 kg / mm 2
In the same manner as in Example 1, the conductive wire for a rubber connector was obtained by twisting with a twisting machine.
【００１４】この導電線をシリコーンゴムの板と板の間
に接着剤で固定し、ゴムコネクターを得た。第１の実施
例と同様にこのゴムコネクターを加圧し電気的接続を行
ったところ、直線的に配置した従来のゴムコネクターに
比べ加圧力が少なくても均一な電気的接続ができた。ま
た、座屈もなく良好な結果であった。The conductive wire was fixed between the silicone rubber plates with an adhesive to obtain a rubber connector. When the rubber connector was pressurized and electrically connected as in the first embodiment, uniform electrical connection was achieved even with a smaller pressing force than a conventional rubber connector arranged linearly. The results were good without buckling.
【００１５】[0015]
【発明の効果】本発明によれば、ゴムコネクターを加圧
して電気的接続をする際に加圧力が小さくてすむととも
に、導電線が座屈することがなくなり、何回も繰り返し
使用することができる。According to the present invention, when a rubber connector is pressurized to make an electrical connection, a small pressing force is required, and the conductive wire does not buckle, and can be used repeatedly. .
【図１】導電線が直線状に配置されたゴムコネクターの
断面模式図である。FIG. 1 is a schematic cross-sectional view of a rubber connector in which conductive wires are linearly arranged.
【図２】導電線が屈曲状に配置されたゴムコネクターの
断面模式図である。FIG. 2 is a schematic cross-sectional view of a rubber connector in which conductive wires are arranged in a bent shape.
【図３】本発明に係る金属線と合成樹脂線を撚り合せた
ゴムコネクター用導電線の断面模式図である。FIG. 3 is a schematic cross-sectional view of a conductive wire for a rubber connector obtained by twisting a metal wire and a synthetic resin wire according to the present invention.
１ 金属線 ２ シリコーンゴム ３ 合成樹脂線 DESCRIPTION OF SYMBOLS 1 Metal wire 2 Silicone rubber 3 Synthetic resin wire
Claims (2)
を特徴とするゴムコネクター用導電線。1. A conductive wire for a rubber connector, wherein a metal wire and a synthetic resin wire are twisted.
を特徴とするゴムコネクター。2. A rubber connector using claim 1.