JP2001321722A - Method for coating internal and external plate of automotive body - Google Patents
Method for coating internal and external plate of automotive bodyInfo
- Publication number
- JP2001321722A JP2001321722A JP2000146121A JP2000146121A JP2001321722A JP 2001321722 A JP2001321722 A JP 2001321722A JP 2000146121 A JP2000146121 A JP 2000146121A JP 2000146121 A JP2000146121 A JP 2000146121A JP 2001321722 A JP2001321722 A JP 2001321722A
- Authority
- JP
- Japan
- Prior art keywords
- coating
- paint
- cured
- resin
- automobile body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、自動車車体の外板
部及び内板部の塗装法に関し、特に、内板部用中塗り塗
料の品種構成を少なくすることができ、かつ外板部と内
板部との色彩的違和感を少なくすることができる新規な
自動車車体内外板の塗装方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for coating an outer plate portion and an inner plate portion of an automobile body, and more particularly to a method for coating an intermediate coating material for an inner plate portion capable of reducing a variety of types. The present invention relates to a novel method for coating an inner / outer panel of an automobile body, which can reduce a sense of color discomfort with an inner panel.
【０００２】[0002]
【従来の技術とその課題】自動車車体の内板部及び外板
部にカチオン電着塗料を塗装し加熱硬化して下塗り塗膜
を形成し、ついで、外板部及び内板部のそれぞれに中塗
り塗料を塗装し、加熱してこれらの両塗膜を同時に硬化
させた後、外板部に上塗り塗料を塗装し、その上塗り塗
膜を硬化させることからなる自動車車体の塗装方法はす
でに知られており、広く採用されている。しかも、外板
部と内板部との色彩的違和感を少なくするために、内板
部塗装用の中塗り塗料の塗色と外板部塗装用の上塗り塗
料の塗色とを近似又は一致させていた。しかしながら、
かかる方式では、上塗り塗料の塗色と同数の中塗り塗料
を準備しなければならず、そのために、資材的、人材
的、時間的に多大の経費が必要であるという欠点があ
る。2. Description of the Related Art A cationic electrodeposition coating is applied to the inner and outer plates of an automobile body and heat-cured to form an undercoating film. A coating method for an automobile body, which comprises applying a coating material, heating and curing both of these coating films at the same time, then applying a top coating material on the outer panel and curing the top coating film, is already known. And is widely adopted. In addition, in order to reduce the discomfort of colors between the outer panel and the inner panel, the coating color of the intermediate coating for the inner panel and the coating of the top coating for the outer panel are approximated or matched. I was However,
Such a system has the drawback that the same number of intermediate coats as the color of the top coat must be prepared, which requires a large amount of material, personnel and time.
【０００３】本発明の目的は、自動車車体の外板部及び
内板部の塗装法における上記の如き欠点を解消すること
である。An object of the present invention is to eliminate the above-mentioned drawbacks in a method for coating an outer plate and an inner plate of an automobile body.
【０００４】[0004]
【課題を解決するための手段】本発明者らは、鋭意研究
の結果、内板部塗装用の中塗り塗料として黒色ツヤ消し
塗料を使用することにより、上記の目的を達成すること
ができることを見出し、本発明を完成するに至った。Means for Solving the Problems As a result of earnest studies, the present inventors have found that the above object can be achieved by using a black matting paint as an intermediate coating for coating the inner plate. As a result, the present invention has been completed.
【０００５】かくして、本発明は、自動車車体の内板部
塗装用の中塗り塗料（Ｃ）として黒色ツヤ消し塗料を使
用することを特徴とする自動車車体内外板の塗装方法を
提供するものである。Thus, the present invention provides a method for coating the inner and outer panels of an automobile body, which comprises using a black matting paint as the intermediate coating (C) for coating the interior panel of the automobile body. .
【０００６】本発明はさらに、自動車車体の内板部及び
外板部にカチオン電着塗料（Ａ）を塗装し加熱硬化して
から、外板部に中塗り塗料（Ｂ）を塗装し、硬化させる
ことなく、内板部に中塗り塗料（Ｃ）を塗装してから、
加熱して内板部及び外板部の両塗膜を同時に硬化させた
後、外板部に上塗り塗料（Ｄ）を塗装し、その上塗り塗
膜を硬化させることからなる自動車車体内外板の塗装方
法において、内板部塗装用の中塗り塗料（Ｃ）として黒
色ツヤ消し塗料を使用することを特徴とする自動車車体
内外板の塗装方法を提供するものである。The present invention further applies a cationic electrodeposition coating (A) to the inner and outer plates of an automobile body, heat-curs, and then applies an intermediate coating (B) to the outer plates to cure. Without applying the intermediate coating (C) to the inner plate,
After heating and simultaneously curing both the coatings of the inner plate and the outer plate, the outer plate is coated with a top coating (D), and the coating is cured. In the method, there is provided a method for coating the inner and outer panels of an automobile body, wherein a black mat paint is used as an intermediate coating (C) for coating an inner panel.
【０００７】[0007]
【発明の実施の形態】以下、本発明の塗装方法について
さらに詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the coating method of the present invention will be described in more detail.
【０００８】本発明が対象とする自動車車体は乗用車、
軽自動車、バスなどの車体である。外板部はドア、フー
ド、ボンネットなどの車体の外側に面している部分であ
って、例えば、ボンネットフード、パネルルーフ、トラ
ンクリッド、フェンダー、バンパー、ドア外側、ピラ
ー、エプロンなどがあげられ、また、内板部としては、
例えば、ボンネット裏面、トランクリッド裏面、ドア開
口部、ガソリン注入裏面などがあげられる。これらの車
体を構成する外板部及び内板部の材質は、主に金属製で
あるが、プラスチック製品が併存することもある。[0008] The present invention is directed to an automobile body for a passenger car,
It is the body of a mini car, bus, etc. The outer plate portion is a portion facing the outside of the vehicle body such as a door, a hood, a hood, and, for example, a hood, a panel roof, a trunk lid, a fender, a bumper, a door outside, a pillar, an apron, and the like. Also, as the inner plate,
For example, the back of the hood, the back of the trunk lid, the door opening, the back of the gasoline injection, and the like can be given. The material of the outer plate portion and the inner plate portion constituting these vehicle bodies is mainly made of metal, but plastic products may be present together.
【０００９】本発明の方法では、一般に、まず、これら
の車体内外板部の金属製部分に下塗り塗料として、カチ
オン電着塗料（Ａ）が塗装される。カチオン電着塗料
（Ａ）としてはそれ自体既知のものを使用することがで
きる。例えば、カチオン性高分子化合物の塩の水溶液又
は水分散液に、必要に応じて架橋剤や顔料、その他の各
種添加剤を配合してなるカチオン電着塗料を使用するこ
とができる。カチオン性高分子化合物としては、例え
ば、エポキシ樹脂やアクリル樹脂などの基体樹脂をアミ
ノ化合物で変性することによりカチオン性基を導入した
ものがあげられ、これを有機酸や無機酸などで中和して
水溶液又は水分散液にすることができる。架橋剤として
はブロックポリイソシアネート化合物や脂環式エポキシ
樹脂などが好適に使用できる。In the method of the present invention, first, a cationic electrodeposition paint (A) is first applied as a primer to the metal parts of the inner and outer panels of the vehicle body. As the cationic electrodeposition coating material (A), a known one can be used. For example, a cationic electrodeposition paint obtained by blending a crosslinking agent, a pigment, and other various additives with an aqueous solution or aqueous dispersion of a salt of a cationic polymer compound, if necessary, can be used. Examples of the cationic polymer compound include those in which a cationic group is introduced by modifying a base resin such as an epoxy resin or an acrylic resin with an amino compound, which is neutralized with an organic acid or an inorganic acid. Into an aqueous solution or dispersion. As the crosslinking agent, a blocked polyisocyanate compound, an alicyclic epoxy resin, or the like can be suitably used.
【００１０】電着塗装は、例えば、固形分含有率が５〜
４０重量％に調整されたカチオン電着塗料（Ａ）の浴中
に、内板部及び外板部を主たる構成部材とする金属製自
動車車体を陰極として浸漬し、陽極との間に通常の条件
で通電することにより行なうことができる。電着塗膜の
膜厚は硬化塗膜で１０〜４０μｍの範囲内が好ましく、
約１４０〜約２００℃で１０〜４０分程度加熱すること
によりその塗膜を硬化させることができる。この電着塗
膜は内板部及び外板部の両者に形成される。[0010] The electrodeposition coating has, for example, a solid content of 5 to 5%.
In a bath of the cationic electrodeposition paint (A) adjusted to 40% by weight, a metal automobile body having an inner plate portion and an outer plate portion as main constituent members is immersed as a cathode, and a normal condition is applied to the anode. Can be carried out by energizing with. The thickness of the electrodeposition coating film is preferably in the range of 10 to 40 μm in the cured coating film,
The coating film can be cured by heating at about 140 to about 200 ° C. for about 10 to 40 minutes. This electrodeposition coating film is formed on both the inner plate portion and the outer plate portion.
【００１１】本発明では、かくして形成された外板部及
び内板部の硬化電着塗膜にそれぞれ中塗り塗料（Ｂ）及
び中塗り塗料（Ｃ）が塗装される。In the present invention, the intermediate coating (B) and the intermediate coating (C) are applied to the cured electrodeposition coating films on the outer plate portion and the inner plate portion thus formed.
【００１２】外板部用の中塗り塗料（Ｂ）としては、例
えば、熱硬化性樹脂組成物及び有機溶剤を含有し、さら
に必要に応じて、着色顔料、体質顔料及びその他の塗料
用添加剤を配合してなるそれ自体既知の液状中塗り塗料
を使用することができる。The intermediate coating material (B) for the outer panel portion contains, for example, a thermosetting resin composition and an organic solvent, and, if necessary, further contains a coloring pigment, an extender pigment and other additives for the coating material. Can be used a liquid intermediate coating material known per se.
【００１３】熱硬化性樹脂組成物としては、例えば、水
酸基などの架橋性官能基を有するアクリル樹脂、ポリエ
ステル樹脂、アルキド樹脂などの基体樹脂に、メラミン
樹脂、尿素樹脂などのアミノ樹脂やブロックポリイソシ
アネート化合物などの架橋剤を配合したものがあげられ
る。有機溶剤としては、例えば、炭化水素系、アルコー
ル系、エステル系、エーテル系、ケトン系などの通常の
塗料用溶剤を使用することができる。中塗り塗料（Ｂ）
の色調は、上塗り塗料（Ｄ）と同一又は近似している
か、又はグレー色であることが好ましい。The thermosetting resin composition includes, for example, a base resin such as an acrylic resin, a polyester resin, and an alkyd resin having a crosslinkable functional group such as a hydroxyl group, an amino resin such as a melamine resin and a urea resin, and a block polyisocyanate. Compounds containing a crosslinking agent such as a compound may be used. As the organic solvent, for example, ordinary paint solvents such as hydrocarbons, alcohols, esters, ethers, and ketones can be used. Intermediate paint (B)
Is preferably the same as or close to that of the top coat (D), or a gray color.
【００１４】中塗り塗料（Ｂ）の塗装は、例えば、静電
塗装、エアレススプレー塗装、エアスプレー塗装などの
既知の方法で行なうことができ、その膜厚は硬化塗膜に
基いて１０〜４０μｍの範囲内にあることが好ましい。The intermediate coating (B) can be applied by a known method such as electrostatic coating, airless spray coating or air spray coating, and its film thickness is 10 to 40 μm based on the cured coating film. Is preferably within the range.
【００１５】本発明では、外板部に中塗り塗料（Ｂ）を
塗装し、その塗膜を硬化させることなく、引き続き、内
板部の電着硬化塗膜面に中塗り塗料（Ｃ）が塗装され
る。In the present invention, the intermediate coating (B) is applied to the outer plate portion, and the intermediate coating (C) is continuously applied to the electrodeposition cured coating surface of the inner plate portion without curing the coating film. Painted.
【００１６】内板部用の中塗り塗料（Ｃ）は、その色調
が黒色でかつツヤ消しの塗膜を形成しうる塗料であり、
具体的には、例えば、熱硬化性樹脂組成物、黒色顔料及
び有機溶剤を含有し、さらに必要に応じて、その他の着
色顔料、体質顔料及び塗料用添加剤を配合してなる液状
塗料を使用することができる。The intermediate coating (C) for the inner plate portion is a coating having a black color tone and capable of forming a matte coating film.
Specifically, for example, a liquid paint containing a thermosetting resin composition, a black pigment, and an organic solvent, and further containing, if necessary, other coloring pigments, extenders and paint additives is used. can do.
【００１７】熱硬化性樹脂組成物としては、例えば、水
酸基などの架橋性官能基を有するアクリル樹脂、ポリエ
ステル樹脂、アルキド樹脂などの基体樹脂に、メラミン
樹脂、尿素樹脂などのアミノ樹脂やブロックポリイソシ
アネート化合物などの架橋剤を配合したものがあげられ
る。黒色顔料としては、例えば、カーボンブラック、ラ
ンプブラック、黒鉛、鉄黒などがあげられる。また、有
機溶剤としては、例えば、炭化水素系、アルコール系、
エステル系、エーテル系、ケトン系などの通常の塗料用
溶剤を使用することができる。Examples of the thermosetting resin composition include a base resin such as an acrylic resin, a polyester resin and an alkyd resin having a crosslinkable functional group such as a hydroxyl group, an amino resin such as a melamine resin and a urea resin, and a block polyisocyanate. Compounds containing a crosslinking agent such as a compound may be used. Examples of the black pigment include carbon black, lamp black, graphite, iron black and the like. Further, as the organic solvent, for example, hydrocarbon-based, alcohol-based,
Usable paint solvents such as ester, ether and ketone can be used.
【００１８】中塗り塗料（Ｃ）は、単独塗膜の状態で、
その色調が黒色でかつツヤ消しの塗膜を形成するもので
あり、具体的には、例えば、上記の如き黒色顔料、さら
に必要に応じて黒色以外のその他の着色顔料を併用し
て、塗膜の色調がマンセルチャートのＮ値で０〜５、特
に０〜３の範囲内にあり、しかも塗面の光沢が６０度鏡
面反射率で６０％以下、特に３０％以下のツヤ消し塗膜
が形成されるようにすることが好ましい。The intermediate coating (C) is a single coated film,
The color tone is to form a black and matte coating film, specifically, for example, a black pigment as described above, if necessary, in combination with other coloring pigments other than black, the coating film The matte color of the Munsell chart is in the range of 0 to 5, especially 0 to 3, and the gloss of the coated surface is 60% or less in terms of a 60-degree specular reflectance, particularly 30% or less. Preferably.
【００１９】中塗り塗料（Ｃ）の塗装は、例えば、静電
塗装、エアレススプレー塗装、エアスプレー塗装などの
既知の方法で行なうことができ、その膜厚は硬化塗膜に
基いて５〜２０μｍの範囲内にあることが好ましい。The intermediate coating (C) can be applied by a known method such as electrostatic coating, airless spray coating or air spray coating, and its film thickness is 5 to 20 μm based on the cured coating film. Is preferably within the range.
【００２０】ついで、上記のようにして外板部に塗装さ
れた中塗り塗膜及び内板部に塗装された中塗り塗膜の両
塗膜を加熱して同時に硬化させる。加熱は約１００〜約
１７０℃で１０〜４０分間程度行なうことが好ましく、
この加熱によって、両中塗り塗膜を同時に硬化させるこ
とができる。Next, both the intermediate coating applied to the outer plate and the intermediate coating applied to the inner plate as described above are heated and simultaneously cured. Heating is preferably performed at about 100 to about 170 ° C. for about 10 to 40 minutes,
By this heating, both intermediate coating films can be cured simultaneously.
【００２１】本発明の方法では、上記のようにして中塗
り塗料（Ｂ）が塗装された外板部の硬化中塗り塗膜上に
上塗り塗料（Ｄ）を塗装し、その上塗り塗膜を硬化させ
る。In the method of the present invention, a top coat (D) is applied on the cured middle coat of the outer plate portion coated with the middle coat (B) as described above, and the top coat is cured. Let it.
【００２２】上塗り塗料（Ｄ）は、外板部に美粧性、耐
候性などを付与するために塗装されるものであって、こ
れらの機能を有する既知の上塗り塗料を使用することが
できる。具体的には、熱硬化性樹脂組成物及び有機溶剤
を含有し、さらに必要に応じて、着色顔料、体質顔料及
び塗料用添加剤を配合してなる液状塗料を使用すること
ができる。The top coat (D) is applied to impart aesthetics, weather resistance and the like to the outer plate, and a known top coat having these functions can be used. Specifically, a liquid paint containing a thermosetting resin composition and an organic solvent, and further containing a coloring pigment, an extender pigment, and a paint additive as necessary can be used.
【００２３】熱硬化性樹脂組成物としては、例えば、水
酸基などの架橋性官能基を有するアクリル樹脂、ポリエ
ステル樹脂、アルキド樹脂などの基体樹脂に、メラミン
樹脂、尿素樹脂などのアミノ樹脂やブロックポリイソシ
アネート化合物などの架橋剤を配合したものがあげられ
る。着色顔料としては、例えば、ソリッドカラー顔料、
メタリック顔料及び光干渉性顔料などの既知の塗料用顔
料が包含される。また、有機溶剤としては、例えば、炭
化水素系、アルコール系、エステル系、エーテル系、ケ
トン系などの通常の塗料用溶剤を使用することができ
る。Examples of the thermosetting resin composition include a base resin such as an acrylic resin, a polyester resin and an alkyd resin having a crosslinkable functional group such as a hydroxyl group, an amino resin such as a melamine resin and a urea resin, and a block polyisocyanate. Compounds containing a crosslinking agent such as a compound may be used. As the color pigment, for example, a solid color pigment,
Known pigments for paints such as metallic pigments and light interference pigments are included. As the organic solvent, for example, ordinary paint solvents such as hydrocarbons, alcohols, esters, ethers and ketones can be used.
【００２４】上塗り塗料（Ｄ）としては、無色透明塗
膜、着色透明塗膜、ソリッドカラー不透明塗膜、メタリ
ック塗膜、光干渉性塗膜などを形成するものを使用する
ことができ、これらを単独で又は２以上を組み合せて、
それ自体既知の方法で、１コート１ベイク方式（1Ｃ1
Ｂ）、２コート１ベイク方式（２Ｃ1Ｂ）、２コート２
ベイク方式（２Ｃ２Ｂ）、３コート１ベイク方式（３Ｃ
1Ｂ）、３コート２ベイク方式（３Ｃ２Ｂ）などにより
塗装して、単層又は２層以上の複層塗膜の上塗り塗膜を
形成することができる。As the top coat (D), those which form a colorless transparent coating, a colored transparent coating, a solid color opaque coating, a metallic coating, a light interference coating and the like can be used. Alone or in combination of two or more
In a method known per se, one coat one bake method (1C1
B) 2 coats 1 bake method (2C1B), 2 coats 2
Bake method (2C2B), 3 coats 1 bake method (3C
1B) It is possible to form an overcoat film of a single layer or a multi-layer coating of two or more layers by coating by a three-coat two-bake method (3C2B) or the like.
【００２５】上塗り塗膜の合計膜厚は硬化塗膜で２０〜
１００μｍの範囲内が好ましく、約１００〜約１８０℃
で１０〜４０分程度加熱することによりその塗膜を硬化
させることができる。The total thickness of the top coat is 20 to 20 for the cured coat.
Preferably within the range of 100 μm, from about 100 to about 180 ° C.
By heating for about 10 to 40 minutes.
【００２６】[0026]
【発明の効果】以上に述べた本発明の方法によれば、
（１）内板部用の中塗り塗料（Ｃ）として、黒色でかつ
ツヤ消しの塗膜を形成しうる塗料を使用することによ
り、外板部に、上塗り塗料（Ｄ）により種々の任意の着
色された上塗りが形成されても、内板部との色彩的違和
感は殆ど認められず、（２）したがって、外板部に塗装
される上塗り塗料（Ｄ）の塗色が種々に変化しても、内
板部の塗装に使用される中塗り塗料は上記の中塗り塗料
（Ｃ）単独であってもよく、内板部用の中塗り塗料の品
数を極めて少なくすることができ、極端な場合ツヤ消し
塗料1種類でもよい、という顕著な効果が得られる。According to the method of the present invention described above,
(1) By using a paint capable of forming a black and matte coating film as the intermediate coating material (C) for the inner plate portion, various arbitrary coatings can be applied to the outer plate portion with the top coating material (D). Even if a colored top coat is formed, almost no color discomfort with the inner plate part is recognized. (2) Therefore, the coating color of the top coat (D) applied to the outer plate part is changed variously. However, the intermediate coating used for coating the inner plate may be the above intermediate coating (C) alone, and the number of intermediate coatings for the inner plate can be extremely reduced. In this case, a remarkable effect is obtained that one type of matte paint may be used.
【００２７】[0027]
【実施例】以下、実施例及び比較例により本発明をさら
に具体的に説明する。なお、部及び％はいずれも重量基
準であり、塗膜の膜厚は硬化塗膜についてのものであ
る。The present invention will be described more specifically with reference to examples and comparative examples. All parts and percentages are based on weight, and the thickness of the coating film is that of a cured coating film.
【００２８】実施例 １ 脱脂及びりん酸亜鉛化成処理を行なった厚さ０．８ｍｍ
（大きさ３０×４０ｃｍ）のダル鋼板の全面に、カチオ
ン電着塗料（Ａ）（「エレクロン２０００」、関西ペイ
ント社製、商品名、エポキシ樹脂ポリアミン・ブロック
ポリイソシアネート化合物系）を膜厚が２０μｍになる
ように電着塗装し、１７０℃で３０分間加熱して塗膜を
硬化せしめた。Example 1 0.8 mm thick after degreasing and zinc phosphate conversion treatment
(Electron 2000, manufactured by Kansai Paint Co., Ltd., trade name, epoxy resin polyamine / block polyisocyanate compound system) with a film thickness of 20 μm on the entire surface of a dull steel plate (30 × 40 cm in size). The coating was cured by heating at 170 ° C. for 30 minutes.
【００２９】ついで、鋼板の片面（外板部に相当）に中
塗り塗料（Ｂ）( ポリエステル樹脂・メラミン樹脂系
有機溶剤型、グレー色 )を膜厚１５μｍになるように塗
装し、硬化せることなく、他面（内板部に相当）中塗り
塗料（Ｃ）( ポリエステル樹脂・メラミン樹脂系有機
溶剤型、黒色、マアンセルチャートＮ値１、硬化塗膜の
６０度鏡面反射率１５％ )を膜厚１５μｍになるように
塗装し、室温で2分間放置してから、１４０℃で３０分
間加熱して両中塗り塗膜を同時に硬化せしめた。Next, an intermediate coating (B) (polyester resin / melamine resin organic solvent type, gray color) is applied to one side (corresponding to the outer plate portion) of the steel sheet so as to have a thickness of 15 μm and cured. No other surface (corresponding to the inner plate portion) intermediate coating (C) (polyester resin / melamine resin organic solvent type, black, Maansell chart N value 1, 60 ° mirror reflectance of cured coating film 15%) The coating was applied to a thickness of 15 μm, left at room temperature for 2 minutes, and then heated at 140 ° C. for 30 minutes to simultaneously cure both intermediate coating films.
【００３０】その後、中塗り塗料（Ｂ）の塗面に「マジ
クロンシルバー」（関西ペイント社製、商品名、アクリ
ル樹脂・メラミン樹脂系有機溶剤型メタリック塗料）を
膜厚１５μｍになるように塗装し、硬化させることな
く、「マジクロンクリヤ」（関西ペイント社製、商品
名、アクリル樹脂・メラミン樹脂系有機溶剤型クリヤ塗
料）を膜厚３０μｍになるように塗装した後、室温で2
分間放置してから、１４０℃で３０分間加熱して両上塗
り塗膜を同時に硬化せしめた。Thereafter, "Magiclon Silver" (manufactured by Kansai Paint Co., trade name, acrylic resin / melamine resin organic solvent type metallic paint) is applied to the coated surface of the intermediate paint (B) to a thickness of 15 μm. Then, without curing, "Magiclon Clear" (manufactured by Kansai Paint Co., Ltd., trade name, acrylic resin / melamine resin organic solvent type clear paint) was applied to a film thickness of 30 μm, and then cured at room temperature.
Then, the mixture was heated at 140 ° C. for 30 minutes to simultaneously cure both top coats.
【００３１】得られた塗装鋼板の外板部相当面と内板部
相当面とを比較すると、色彩的な違和感は認められなか
った。When the surface corresponding to the outer plate portion and the surface corresponding to the inner plate portion of the obtained coated steel sheet were compared, no discomfort in color was recognized.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 岡田 栄作 愛知県豊田市トヨタ町１番地 トヨタ自動 車株式会社内 (72)発明者 中村 茂 愛知県西加茂郡三好町大字莇生字平地１番 地 関西ペイント株式会社内 (72)発明者 中尾 泰志 愛知県西加茂郡三好町大字莇生字平地１番 地 関西ペイント株式会社内 Ｆターム(参考） 4D075 AE06 BB89X CA47 CB02 DA06 DB02 DC12 EA05 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Eisaku Okada 1 Toyota Town, Toyota City, Aichi Prefecture Inside Toyota Motor Corporation (72) Inventor Shigeru Shigeru Shigeru Nakamura, 1st place in Miyoshi-cho, Nishikamo-gun, Aichi Prefecture Kansai Paint Kanji Paint Co., Ltd. (72) Inventor Yasushi Nakao Aichi, Nishikamo-gun, Miyoshi-cho, Oaza, 1st floor, Kanji Paint Co., Ltd. F term (reference) 4D075 AE06 BB89X CA47 CB02 DA06 DB02 DC12 EA05
Claims (2)
（Ｃ）として黒色ツヤ消し塗料を使用することを特徴と
する自動車車体内外板の塗装方法。1. A method for coating an inner / outer panel of an automobile body, wherein a black mat paint is used as an intermediate coating (C) for coating an inner panel portion of the automobile body.
ン電着塗料（Ａ）を塗装し加熱硬化してから、外板部に
中塗り塗料（Ｂ）を塗装し、硬化させることなく、内板
部に中塗り塗料（Ｃ）を塗装してから、加熱して内板部
及び外板部の両塗膜を同時に硬化させた後、外板部に上
塗り塗料（Ｄ）を塗装し、その上塗り塗膜を硬化させる
ことからなる自動車車体の内外板塗装方法において、内
板部塗装用の中塗り塗料（Ｃ）として黒色ツヤ消し塗料
を使用することを特徴とする自動車車体内外板の塗装方
法。2. An inner coating portion and an outer coating portion of an automobile body are coated with a cationic electrodeposition coating material (A) and heat-cured, and then an outer coating portion is coated with an intermediate coating material (B) and cured. After applying the intermediate coating (C) to the inner plate, heating and simultaneously curing the coatings of the inner plate and the outer plate, and then applying the top coating (D) to the outer plate. A method for coating the inner and outer panels of an automobile body, comprising curing the top coat, wherein a black mat paint is used as an intermediate coating (C) for coating the inner panel. Painting method.