JP2001287305A - Resin laminate, leather like sheet and trim material for car - Google Patents
Resin laminate, leather like sheet and trim material for carInfo
- Publication number
- JP2001287305A JP2001287305A JP2000103381A JP2000103381A JP2001287305A JP 2001287305 A JP2001287305 A JP 2001287305A JP 2000103381 A JP2000103381 A JP 2000103381A JP 2000103381 A JP2000103381 A JP 2000103381A JP 2001287305 A JP2001287305 A JP 2001287305A
- Authority
- JP
- Japan
- Prior art keywords
- resin laminate
- leather
- sheet
- layer
- tpo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、樹脂積層体、レザ
ー調シートおよび自動車用内装材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a resin laminate, a leather-like sheet, and an interior material for an automobile.
【０００２】[0002]
【背景技術】近年、自動車用内装材、家具等には、樹脂
製のレザー調シートが多用されるようになってきてい
る。このような樹脂製レザー調シートとしては、比較的
表面強度が高い塩化ビニル樹脂系、ウレタン系の素材
が、一般的に用いられ、表面強度の低いポリオレフィン
系熱可塑性エラストマー（以下、ＴＰＯという）は使用
されていなかった。2. Description of the Related Art In recent years, resinous leather seats have been frequently used for interior materials and furniture for automobiles. As such a resin-made leather-like sheet, a vinyl chloride resin-based material or a urethane-based material having relatively high surface strength is generally used, and a polyolefin-based thermoplastic elastomer (hereinafter, referred to as TPO) having low surface strength is used. Had not been used.
【０００３】しかしながら、塩化ビニル樹脂は、焼却の
際に塩素系ガス等の有害物質を発生する等環境適応性が
低く、また、ウレタンは高価である等の問題があり、Ｔ
ＰＯを主材料とする樹脂製レザー調シートの出現が望ま
れていた。このような要望から、ＴＰＯ層とウレタン系
の表面処理層とからなる樹脂製レザー調シートが開発さ
れ、現在家具用を中心に使用されるようになっている。[0003] However, vinyl chloride resin has problems of low environmental adaptability such as generation of harmful substances such as chlorine-based gas upon incineration, and urethane is expensive.
The appearance of a resin-made leather-like sheet mainly composed of PO has been desired. From such a demand, a resin-made leather-like sheet comprising a TPO layer and a urethane-based surface treatment layer has been developed, and is now used mainly for furniture.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、上述の
樹脂製レザー調シートにおいても、表面処理層が１０μ
ｍ未満と非常に薄いため、表面強度（耐摩耗性）は、Ｔ
ＰＯそのものと比べて、それほど改善されていないとい
う問題がある。このため、高い表面強度を要求される用
途に、上記樹脂製レザー調シートを採用することは困難
であり、高い表面強度を有し、ＴＰＯを主材料とした樹
脂製レザー調シートの開発が望まれている。However, even in the above-mentioned resin-made leather-like sheet, the surface treatment layer has a thickness of 10 μm.
m, the surface strength (wear resistance) is T
There is a problem that it is not so much improved compared to PO itself. For this reason, it is difficult to employ the above-mentioned resin-made leather-like sheet for applications requiring high surface strength. It is rare.
【０００５】本発明の目的は、高い表面強度（耐摩耗
性）を有する樹脂積層体、レザー調シートおよび自動車
用内装材を提供することにある。An object of the present invention is to provide a resin laminate, a leather-like sheet and an interior material for automobiles having high surface strength (abrasion resistance).
【０００６】[0006]
【課題を解決するための手段】本発明に係る樹脂積層体
は、ポリオレフィン系熱可塑性エラストマー層と、ファ
ブリック層とを備えることを特徴とする。本発明におけ
るＴＰＯとしては、(1)ハードセグメントとしてポリプ
ロピレンを、ソフトセグメントとしてポリエチレンを有
するエラストマー、(2)エチレンと少量のジエン成分を
有するエラストマー、(3)エチレン−プロピレン−ジエ
ンゴム（ＥＰＤＭ）、(4)エチレン−プロピレンゴム
（ＥＰＲ）、(5)ブチルゴムグラフトポリエチレン、(6)
スチレン系エラストマー、(7)(1)〜(6)の各エラストマ
ー（ゴム）を、ブレンドしたもの、(8)有機過酸化物を
(1)〜(7)に添加して部分的に架橋したもの、(9)不飽和
ヒドロキシ単量体や不飽和カルボン酸誘導体でグラフト
変性されたもの等を採用することができる。The resin laminate according to the present invention comprises a polyolefin-based thermoplastic elastomer layer and a fabric layer. As the TPO in the present invention, (1) an elastomer having polypropylene as a hard segment and polyethylene as a soft segment, (2) an elastomer having ethylene and a small amount of a diene component, (3) an ethylene-propylene-diene rubber (EPDM), 4) Ethylene-propylene rubber (EPR), (5) butyl rubber grafted polyethylene, (6)
Styrene-based elastomer, (7) Each elastomer (rubber) of (1) to (6) blended, (8) Organic peroxide
(1) to (7), partially crosslinked, (9) graft modified with an unsaturated hydroxy monomer or an unsaturated carboxylic acid derivative, and the like can be used.
【０００７】本発明における、ファブリックとは、最表
面に繊維等を接着または埋め込んで耐摩耗性を向上させ
るために用いられ、直接手で触れる等する部分に設けら
れるものであり、後述する基材層とは異なるものであ
る。具体的には、例えば、織物（ドビー、ジャカー
ド）、モケット（ドビー、ジャカード）、トリコット、
ダブルラッセル、シンカーパイルニット等が挙げられ
る。The fabric in the present invention is used to improve abrasion resistance by adhering or embedding fibers or the like on the outermost surface, and is provided at a portion which is directly touched by hand. It is different from a layer. Specifically, for example, textile (dobby, jacquard), moquette (dobby, jacquard), tricot,
Double Russell, sinker pile knit, and the like.
【０００８】ここで、ファブリックを構成する繊維とし
ては、種々の天然繊維、合成繊維を採用できるが、特
に、ポリエステル、ナイロン、レーヨン、ポリプロピレ
ン、アクリルおよびポリエステル／レーヨン混紡糸のい
ずれかであることが好ましい。[0008] Here, various natural fibers and synthetic fibers can be used as the fibers constituting the fabric. In particular, the fibers may be any of polyester, nylon, rayon, polypropylene, acrylic and polyester / rayon blended yarn. preferable.
【０００９】これによれば、ＴＰＯ層とファブリック層
とを備えた樹脂積層体を採用しているから、樹脂積層体
の表面強度（耐摩耗性）を向上することができ、表面強
度が要求される自動車の内装材等の用途に適用すること
が可能となる。また、本発明の樹脂積層体はポリオレフ
ィンを主体とする材料により構成されているから、焼却
の際にも有害ガス等を発生することが無く、環境適応性
が高い。According to this, since a resin laminate having a TPO layer and a fabric layer is employed, the surface strength (abrasion resistance) of the resin laminate can be improved, and the surface strength is required. It can be applied to applications such as interior materials for automobiles. In addition, since the resin laminate of the present invention is made of a material mainly composed of polyolefin, it does not generate harmful gas or the like even when incinerated, and has high environmental adaptability.
【００１０】このような樹脂積層体は、表面強度が高い
ため、自動車用内装材として用いられることが好まし
い。自動車用内装材としては、例えば、ドアトリム、イ
ンパネ、サンバイザー、天井、座席シート用レザー等が
挙げられる。Such a resin laminate has a high surface strength, and is therefore preferably used as an interior material for automobiles. Examples of interior materials for automobiles include door trims, instrument panels, sun visors, ceilings, and leather for seats.
【００１１】本発明に係るレザー調シートは、請求項１
または請求項２に記載の樹脂積層体と、基材とを備える
ことを特徴とする。ここで、基材とは、布（基布）であ
り、その糸質としては、ポリエステルとレーヨンの混
紡、アクリル、スフ、ポリプロピレン、ポリエステル、
ポリエステルとスフとの混紡、ポリプロピレン発泡体、
ポリプロピレン発泡体不織布等を採用できる。The leather-like sheet according to the present invention is defined in claim 1.
Alternatively, a resin laminate according to claim 2 and a base material are provided. Here, the base material is a cloth (base cloth), and the yarn quality is a blend of polyester and rayon, acrylic, swoof, polypropylene, polyester,
Blend of polyester and soup, polypropylene foam,
A polypropylene foam nonwoven fabric or the like can be employed.
【００１２】また、基材の組織としては、片面メリヤ
ス、両面メリヤス、特殊編み、あや織、平織、ラッセル
編み、天竺編み等を採用できる。このレザー調シート
は、例えば、基材上に接着剤を塗布し、その上にカレン
ダー加工で樹脂積層体を積層する方法や、基材上に接着
剤を塗布し、この上にカレンダ加工によりＴＰＯ層を積
層した後、この上にファブリックを接着剤によりさらに
積層する方法で製造できる。これによれば、前述の樹脂
積層体と、基材とを備えたレザー調シートであるから、
表面強度の高いＴＰＯ系レザー調シートを提供できる。As the structure of the base material, one side knitting, two sided knitting, special knitting, twill weaving, plain weaving, Russell knitting, sheet knitting, or the like can be adopted. This leather-like sheet is, for example, a method in which an adhesive is applied on a base material, and a resin laminate is laminated on the base material by calendering, or an adhesive is applied on the base material, and the TPO is applied thereon by calendaring. After laminating the layers, the fabric can be manufactured by further laminating the fabric with an adhesive. According to this, since it is a leather-like sheet including the above-described resin laminate and a base material,
A TPO-based leather sheet having high surface strength can be provided.
【００１３】本発明のレザー調シートは、表面強度が高
いため、自動車用内装材として用いられることが好まし
い。自動車用内装材としては、例えば、座席シート用レ
ザー、ドアトリム用レザー、インパネ用レザー、サンバ
イザ用レザー、天井用レザー等に用いることができる。Since the leather-like sheet of the present invention has a high surface strength, it is preferably used as an interior material for automobiles. As interior materials for automobiles, for example, leather for seats, leather for door trims, leather for instrument panels, leather for sun visors, leather for ceilings and the like can be used.
【００１４】[0014]
【発明の実施の形態】以下、本発明の実施の形態を図面
に基づいて説明する。 ［第１実施形態］図１には、本発明の第１実施形態に係
る樹脂積層体１が示されている。樹脂積層体１は、ＴＰ
Ｏ層１０と、ファブリック層２０との２層から構成され
ている。Embodiments of the present invention will be described below with reference to the drawings. [First Embodiment] FIG. 1 shows a resin laminate 1 according to a first embodiment of the present invention. The resin laminate 1 is made of TP
It is composed of two layers, an O layer 10 and a fabric layer 20.
【００１５】以上のように構成された樹脂積層体１は、
次のように製造する。まず、予め、カレンダー加工、Ｔ
ダイ押出等によりシート状に成形されたＴＰＯ層１０の
上に、カレンダー加工にてファブリック層２０を積層し
て樹脂積層体１を得る。なお、この際、ＴＰＯ層の上に
は、適宜、接着剤を塗布しておくことも可能である。こ
のようにして得られた樹脂積層体１は、表面強度（耐摩
耗性）が高いため、ドアトリム、サンバイザー、天井、
座席シート用レザー等の自動車用内装品として好適に利
用できる。The resin laminate 1 constructed as described above is
It is manufactured as follows. First, calendar processing, T
On the TPO layer 10 formed into a sheet by die extrusion or the like, the fabric layer 20 is laminated by calendering to obtain the resin laminate 1. At this time, it is possible to appropriately apply an adhesive on the TPO layer. The resin laminate 1 thus obtained has a high surface strength (abrasion resistance), so that the door trim, sun visor, ceiling,
It can be suitably used as automotive interior parts such as leather for seats.
【００１６】上述のような第１実施形態によれば、次の
ような効果がある。 (1)ＴＰＯ層１０とファブリック層２０とを備えた樹脂
積層体１を採用しているから、樹脂積層体１の表面強度
（耐摩耗性）を向上することができ、表面強度が要求さ
れる自動車用内装材等の用途に適用することが可能とな
る。 (2)樹脂積層体１は、ポリオレフィンを主体とする材料
により構成されているから、焼却の際にも有害ガス等を
発生することが無く、環境適応性が高い。According to the above-described first embodiment, the following effects can be obtained. (1) Since the resin laminate 1 including the TPO layer 10 and the fabric layer 20 is employed, the surface strength (abrasion resistance) of the resin laminate 1 can be improved, and the surface strength is required. It can be applied to applications such as interior materials for automobiles. (2) Since the resin laminate 1 is made of a material mainly composed of polyolefin, it does not generate harmful gases even when incinerated, and has high environmental adaptability.
【００１７】［第２実施形態］図２には、本発明の第２
実施形態に係るレザー調シート２が示されている。レザ
ー調シート２は、第１実施形態の樹脂積層体１の表面に
ポリエステル製の基材３０を貼付した以外は、前記第１
実施形態と同一構造を備えているので、その詳細な説明
を省略する。[Second Embodiment] FIG. 2 shows a second embodiment of the present invention.
The leather tone sheet 2 according to the embodiment is shown. The leather-like sheet 2 is the same as the first embodiment except that a polyester base material 30 is attached to the surface of the resin laminate 1 of the first embodiment.
Since it has the same structure as the embodiment, detailed description thereof will be omitted.
【００１８】以上のように構成されたレザー調シート２
は、次のように製造する。まず、基材３０上に接着剤を
塗布し、この上に、予めカレンダー加工、Ｔダイ押出等
によりシート状に成形されたＴＰＯ層１０を積層する。
続いて、同様にしてファブリック層２０を積層してレザ
ー調シート２を得る。Leather-like sheet 2 constructed as described above
Is manufactured as follows. First, an adhesive is applied to the base material 30, and the TPO layer 10 formed in a sheet shape by calendering, T-die extrusion, or the like is laminated on the adhesive.
Subsequently, the leather layered sheet 2 is obtained by laminating the fabric layers 20 in the same manner.
【００１９】上述のような第２実施形態によれば、前記
第１実施形態の(1)、(2)と同様の効果が得られる他、次
のような効果も得られる。 (3)樹脂積層体１と、基材３０とを備えたレザー調シー
ト２であるから、表面強度の高いＴＰＯ系レザー調シー
ト２を提供できる。According to the above-described second embodiment, the same effects as (1) and (2) of the first embodiment can be obtained, and also the following effects can be obtained. (3) Since the leather-like sheet 2 includes the resin laminate 1 and the substrate 30, the TPO-based leather-like sheet 2 having high surface strength can be provided.
【００２０】なお、本発明は前記実施形態に限定される
ものではなく、本発明の目的を達成できる範囲での変
形、改良は、本発明に含まれるものである。例えば、前
記各実施形態では、樹脂積層体１としてＴＰＯ層１０と
ファブリック層２０の２層からなるものを用いていた
が、これに限られず、例えば、ＴＰＯ層とファブリック
層の間に接着層を備える等の、３層構造以上のシートを
採用してもよい。It should be noted that the present invention is not limited to the above-described embodiment, and modifications and improvements as long as the object of the present invention can be achieved are included in the present invention. For example, in each of the above embodiments, the resin laminate 1 is composed of the two layers of the TPO layer 10 and the fabric layer 20, but is not limited to this. For example, an adhesive layer may be provided between the TPO layer and the fabric layer. For example, a sheet having a three-layer structure or more may be employed.
【００２１】また、ＴＰＯ層１０とファブリック層２０
の積層および基材３０とＴＰＯ層１０との積層をラミネ
ート加工により行っていたが、これに限られず、各層を
積層できる種々の装置、方法を採用することができる。
その他、本発明を実施する際の具体的な構造および形状
等は、本発明の目的を達成できる範囲内で他の構造とし
てもよい。The TPO layer 10 and the fabric layer 20
Although the lamination and the lamination of the base material 30 and the TPO layer 10 are performed by lamination, the present invention is not limited to this, and various apparatuses and methods capable of laminating each layer can be adopted.
In addition, the specific structure, shape, and the like when implementing the present invention may be other structures within a range that can achieve the object of the present invention.
【００２２】[0022]
【実施例】以下、本発明を実施例および比較例を挙げ
て、より具体的に説明する。 ［実施例］ （ポリオレフィン系熱可塑性エラストマー層）ポリオレ
フィン系熱可塑性エラストマー（Ｅ２６４０ 出光石油
化学（株）製）とプロセスオイル（ＰＷ９０ 出光興産
（株）製）を、表面温度を１６０℃に設定した径３イン
チの２本ロールで十分に混練し、厚さ０．５ｍｍのＴＰ
Ｏシート（ＴＰＯ層１０）を得た。EXAMPLES The present invention will be described more specifically with reference to examples and comparative examples. [Example] (Polyolefin-based thermoplastic elastomer layer) Polyolefin-based thermoplastic elastomer (E2640, manufactured by Idemitsu Petrochemical Co., Ltd.) and process oil (PW90, manufactured by Idemitsu Kosan Co., Ltd.) with a surface temperature of 160 ° C. Knead well with two 3 inch rolls, TP 0.5mm thick
An O sheet (TPO layer 10) was obtained.
【００２３】（ファブリック層）上記ＴＰＯ層１０上
に、ファブリック層２０としてポリエステル織物（ドビ
ー）をプレスにて圧力２ＭＰａ、温度１４０℃の条件で
３０秒間加圧して樹脂積層体１を得た。(Fabric Layer) On the TPO layer 10, a polyester woven fabric (dobby) was pressed as a fabric layer 20 with a press at a pressure of 2 MPa and a temperature of 140 ° C. for 30 seconds to obtain a resin laminate 1.
【００２４】［比較例］実施例１のＴＰＯシート（ＴＰ
Ｏ層）を、そのまま後述する耐摩耗性試験に供した。Comparative Example The TPO sheet of Example 1 (TP
O layer) was directly subjected to a wear resistance test described below.
【００２５】上記各実施例で得られた樹脂積層体および
ＴＰＯシートについて表面強度（耐摩耗性の試験を行
い、その結果を表１にまとめた。なお、試験は、ＪＩＳ
Ｌ−０８２３（染色堅ろう度試験用摩擦試験器）の
３．２に規定する摩擦試験器II型を用い、ＪＩＳ Ｌ−
３１０２の綿帆布６号を摩擦子に取り付け、９．８Ｎ
（実測値１ｋｇｆをＳＩ単位に換算した値）の力を１万
回繰り返し加えることにより測定した。The resin laminate and the TPO sheet obtained in each of the above examples were subjected to surface strength tests (wear tests were conducted, and the results are summarized in Table 1. The tests were conducted according to JIS.
L-0823 (friction tester for dye fastness test), using a friction tester type II specified in 3.2, JIS L-
Attach the 3102 cotton canvas No. 6 to the friction element, 9.8N
The force was measured by repeatedly applying a force of (measured value 1 kgf in SI units) 10,000 times.
【００２６】[0026]
【表１】 [Table 1]
【００２７】ここで、等級を決定するのに用いた判定基
準は以下の通りである。 ５等級：変化が認められない ４等級：変化がわずかに認められる ３等級：変化が明らかに認められる ２等級：変化がやや著しい １等級：変化が著しいHere, the criteria used to determine the grade are as follows. 5th grade: no change 4th grade: slight change 3rd grade: change is clearly seen 2nd grade: slight change 1st grade: change
【００２８】表１に示されるように、実施例で得られた
樹脂積層体は、ＴＰＯ層の表面にファブリック層を備え
ているので、表面強度が高く、耐摩耗性試験においても
表面には変化が認められていない（５等級）ことがわか
る。一方、ファブリック層を備えていないＴＰＯシート
をそのまま用いた場合には、表面強度が著しく低下し
て、耐摩耗性試験において著しい変化が見られているこ
とがわかる（１等級）。As shown in Table 1, the resin laminate obtained in the examples has a fabric layer on the surface of the TPO layer, so that the surface strength is high and the surface changes even in the abrasion resistance test. Is not recognized (grade 5). On the other hand, when a TPO sheet without a fabric layer is used as it is, the surface strength is remarkably reduced, and it can be seen that a remarkable change is observed in the abrasion resistance test (grade 1).
【００２９】[0029]
【発明の効果】本発明によれば、ＴＰＯ層とファブリッ
ク層とを備えた樹脂積層体を採用しているから、ＴＰＯ
シートの表面強度（耐摩耗性）を向上することができ、
表面強度が要求される自動車の内装材等の用途に適用す
ることが可能となるという効果がある。According to the present invention, a resin laminate having a TPO layer and a fabric layer is employed.
The surface strength (wear resistance) of the sheet can be improved,
This has the effect that it can be applied to applications such as interior materials for automobiles requiring surface strength.
【図１】本発明の第１実施形態の樹脂積層体を示す部分
断面図である。FIG. 1 is a partial cross-sectional view illustrating a resin laminate according to a first embodiment of the present invention.
【図２】本発明の第２実施形態のレザー調シートを示す
部分断面図である。FIG. 2 is a partial sectional view showing a leather-like sheet according to a second embodiment of the present invention.
１ 樹脂積層体 ２ レザー調シート １０ ポリオレフィン系熱可塑性エラストマー層 ２０ ファブリック層 ３０ 基材 DESCRIPTION OF SYMBOLS 1 Resin laminated body 2 Leather-like sheet 10 Polyolefin thermoplastic elastomer layer 20 Fabric layer 30 Substrate
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 3D023 BA01 BB02 BB08 BD01 BD03 BD12 BE06 4F100 AJ05B AK03A AK07B AK25B AK41 AK41B AK48B AL09A AT00C BA02 BA03 BA10B BA10C CB00 DG01B DG11B DG11C DG12 DG18B EJ202 EJ422 GB33 JB16A JK09 ──────────────────────────────────────────────────続 き Continued on the front page F-term (reference)
Claims (5)
と、ファブリック層とを備えることを特徴とする樹脂積
層体。1. A resin laminate comprising a polyolefin-based thermoplastic elastomer layer and a fabric layer.
ナイロン、レーヨン、ポリプロピレン、アクリルおよび
ポリエステル／レーヨン混紡糸のいずれかから選択され
たものであることを特徴とする樹脂積層体。2. The resin laminate according to claim 1, wherein the fibers constituting the fabric layer are polyester,
A resin laminate characterized by being selected from any of nylon, rayon, polypropylene, acrylic and polyester / rayon blended yarn.
体を用いたことを特徴とする自動車内装材。3. An automotive interior material comprising the resin laminate according to claim 1 or 2.
体と、基材とを備えることを特徴とするレザー調シー
ト。4. A leather-like sheet comprising the resin laminate according to claim 1 or 2 and a base material.
ことを特徴とする自動車用内装材。5. An interior material for an automobile, wherein the leather-like sheet according to claim 4 is used.