JP2001277355A - Resin part with laser mark for personal computer or peripheral apparatus of personal computer - Google Patents
Resin part with laser mark for personal computer or peripheral apparatus of personal computerInfo
- Publication number
- JP2001277355A JP2001277355A JP2000093526A JP2000093526A JP2001277355A JP 2001277355 A JP2001277355 A JP 2001277355A JP 2000093526 A JP2000093526 A JP 2000093526A JP 2000093526 A JP2000093526 A JP 2000093526A JP 2001277355 A JP2001277355 A JP 2001277355A
- Authority
- JP
- Japan
- Prior art keywords
- personal computer
- resin
- mark
- laser
- resin part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、パーソナルコンピ
ューター又はパーソナルコンピューター周辺機器用のレ
ーザーマーク付き樹脂部品の改良に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an improvement in a resin part having a laser mark for a personal computer or a peripheral device of a personal computer.
【０００２】[0002]
【従来の技術】現在、パーソナルコンピューターやパー
ソナルコンピューター周辺機器にはより意匠性の高い外
観を有するデザインが求められ、透明あるいは半透明な
筐体が増加している。これら透明樹脂からなる成形品
に、視覚的に認知可能な加飾を行う方法として、例え
ば、被加飾部の裏面全体に加飾塗膜層を形成した後、レ
ーザー光により加飾塗膜層を部分的に除去して打ち抜き
部を形成する方法（特公昭６４−５８３７７号公報）
や、成形品本体の裏面にレーザー光を吸収し得る着色層
を形成し、着色層にレーザー光線を照射して部分的に燃
焼除去する方法（特公昭６４−５８５２９号公報）など
が提案されている。2. Description of the Related Art At present, personal computers and peripheral devices for personal computers are required to have a design having a more aesthetic appearance, and transparent or translucent cases are increasing. As a method of performing visually recognizable decoration on a molded product made of these transparent resins, for example, after forming a decoration coating layer on the entire back surface of the part to be decorated, the decoration coating layer by laser light Method of forming a punched portion by partially removing the material (Japanese Patent Publication No. 64-58377)
Alternatively, a method has been proposed in which a colored layer capable of absorbing laser light is formed on the back surface of a molded article main body, and the colored layer is irradiated with a laser beam to partially burn off (JP-B 64-58529). .
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、透明樹
脂成形品に加飾塗膜層を塗布した場合、透明樹脂成形品
部分と加飾塗膜層部分とを分別することが非常に難し
く、リサイクル性に問題があった。さらに、レーザー光
線で加飾塗膜層を除去する際には、成形品本体の透明樹
脂成形品部分にはレーザー光線の侵食を及ばせずに加飾
塗膜層のみが除去されるようにレーザー光線照射条件を
調整する必要があるので、とり得る照射条件巾が狭くそ
の調整作業も容易ではなかった。However, when the decorative coating layer is applied to the transparent resin molded product, it is very difficult to separate the transparent resin molded product portion from the decorative coating layer portion, and the recyclability is high. Had a problem. Furthermore, when removing the decorative coating layer with a laser beam, the laser beam irradiation conditions are such that only the decorative coating layer is removed without eroding the transparent resin molded part of the molded product body by the laser beam. Therefore, the range of possible irradiation conditions is narrow, and the adjustment operation is not easy.
【０００４】そこで、本発明は、上記問題を解消し、樹
脂成形部品のリサイクル性、レーザーマーキングされた
部位の視認性、および体裁面の平滑性に優れ、かつ、意
匠性に富んだ深みのある漆黒感鮮明な黒色マークを形成
することができ、さらに、マーキング時に黒色発色する
レーザー光線照射条件幅を著しく広くとることが可能な
パーソナルコンピューター又はパーソナルコンピュータ
ー周辺機器用樹脂部品を提供することを主な目的とす
る。Therefore, the present invention solves the above-mentioned problems, and is excellent in recyclability of resin molded parts, visibility of a laser-marked portion, and smoothness of appearance, and has a rich design. A main object of the present invention is to provide a resin component for a personal computer or a peripheral device for a personal computer, which can form a jet-black vivid black mark, and can remarkably widen a laser beam irradiation condition width for producing a black color at the time of marking. And
【０００５】[0005]
【課題を解決するための手段】上記目的の達成のために
は、透明あるいは半透明な熱可塑性樹脂よりなる、パー
ソナルコンピューター又はパーソナルコンピューター周
辺機器用の樹脂部品に対し、体裁面の裏側より目的とす
る所定形状の鏡像となる形状をレーザー光線の照射によ
り現出させることが有効であることを見出し、本発明を
なすに至った。In order to achieve the above object, a resin part for a personal computer or a peripheral device of a personal computer, which is made of a transparent or translucent thermoplastic resin, is formed from the back side of the appearance surface. The present inventors have found that it is effective to make a mirror image of a predetermined shape appear by irradiating a laser beam, and have accomplished the present invention.
【０００６】即ち、本発明のレーザーマーキングされた
パーソナルコンピューター又はパーソナルコンピュータ
ー周辺機器用樹脂部品は、透明又は半透明な熱可塑性樹
脂からなり、レーザー光線照射によるマーク部が形成さ
れた成形品において、レーザー光線照射によるマーク部
が成形品の体裁面に対する裏面側に所定形状の鏡像の形
状で形成され、所定形状が体裁面側から視覚的に認知さ
れることを特徴とする。That is, the resin part for a personal computer or a personal computer peripheral device which is laser-marked according to the present invention is made of a transparent or translucent thermoplastic resin. Is formed in a mirror image of a predetermined shape on the back side of the molding surface of the molded product, and the predetermined shape is visually recognized from the formatting surface side.
【０００７】[0007]
【発明の実施の形態】本発明で用いる透明又は半透明な
熱可塑性樹脂は、成形品の体裁面に対する裏面側に施さ
れたマーク部の文字や図形等の形状が体裁面側から視覚
的に認知できる程度の透明度を有する熱可塑性樹脂であ
ればよく、例えば、当該樹脂の肉厚１ｍｍの成形品にお
ける６００〜１１００ｎｍ光線の透過率が３０％以上の
ものであればよい。さらにその光線透過率が５０％以上
が好ましい。成形品の肉厚が１ｍｍの場合における、光
線透過率が３０％未満であると成形品の透明性が著しく
劣るので、体裁面側からマーキングを視覚的に認知する
ことが難しくなる。BEST MODE FOR CARRYING OUT THE INVENTION The transparent or translucent thermoplastic resin used in the present invention is characterized in that the shape of characters, figures, etc. of a mark portion provided on the back surface side with respect to the appearance surface of a molded product is visually recognized from the appearance surface side. Any thermoplastic resin having a recognizable degree of transparency may be used. For example, a resin having a thickness of 1 mm and a transmittance of 600 to 1100 nm light rays of 30% or more may be used. Further, the light transmittance is preferably 50% or more. If the light transmittance is less than 30% when the thickness of the molded product is 1 mm, the transparency of the molded product is extremely poor, and it is difficult to visually recognize the marking from the appearance surface side.
【０００８】本発明の対象とする樹脂部品は、パーソナ
ルコンピューター又はパーソナルコンピューター周辺機
器（以下、ＰＣ機器類と総称する）に組込まれる樹脂部
品であって、その樹脂部品の体裁面に対応する裏面側に
レーザー光照射によるマーク部を形成することが可能な
らば特に限定はされず、表示部の視認性に優れることが
要求される部品や意匠性の高い装飾を付加したい部品、
例えば、パーソナルコンピューター、ノート型パソコ
ン、ＤＶＤドライブやＣＤドライブなどの各種外部記録
装置およびそのトレー、液晶ディスプレイ、外部スピー
カーシステム、スキャナー、プリンター、インターネッ
トモデム等の筐体など、各種機器の装飾用部品、表示用
部品、操作用部品が挙げられる。[0008] The resin component to be used in the present invention is a resin component to be incorporated into a personal computer or a personal computer peripheral device (hereinafter collectively referred to as PC devices), and has a back surface corresponding to the appearance surface of the resin component. There is no particular limitation as long as it is possible to form a mark portion by laser light irradiation, a component that is required to be excellent in visibility of the display portion, a component to which a highly decorative design is to be added,
For example, personal computer, notebook computer, various external recording devices such as DVD drive and CD drive and their trays, liquid crystal displays, external speaker systems, scanners, printers, housings such as Internet modems, decorative parts of various devices, Display components and operation components are included.
【０００９】本発明の樹脂部品における体裁面とは、こ
の部品に付された所定形状のマークを認知するために視
線が注がれる面であり、例えば操作パネルの表示・操作
用部品の場合には操作のために見て触れる外側表面が体
裁面となる。The appearance surface of the resin component of the present invention is a surface on which a line of sight is poured in order to recognize a mark of a predetermined shape attached to the component. For example, in the case of a display / operation component of an operation panel, The outer surface seen and touched for operation is the appearance surface.
【００１０】また、本発明のＰＣ機器類用樹脂部品にお
いてレーザーマークを付す部分の肉厚は特に限定されな
いが、成形品肉厚は５ｍｍ以下であることが、透明性お
よびマーク部を体裁面から見た時の深みのある漆黒感
（高級感）を得るために好ましく、成形品肉厚０．５〜
３ｍｍがより好ましい。In the resin part for PC equipment of the present invention, the thickness of the portion to be laser-marked is not particularly limited. It is preferable to obtain a deep jet-black feeling (luxury feeling) when viewed.
3 mm is more preferred.
【００１１】本発明の透明又は半透明な熱可塑性樹脂の
種類としては、具体的には、ポリエチレン系樹脂、ポリ
プロピレン系樹脂、ポリスチレン系樹脂、ポリエチレン
テレフタレート系樹脂、ポリメチルメタクリレート系樹
脂、ポリカーボネート系樹脂、透明ＡＢＳ樹脂などの各
種透明な熱可塑性樹脂が挙げられる。なかでも、ポリメ
チルメタクリレート系樹脂や透明ＡＢＳ樹脂などのよう
な不飽和カルボン酸アルキルエステル系（共）重合体、
およびポリカーボネート系樹脂が好ましい。The transparent or translucent thermoplastic resin of the present invention may be, for example, a polyethylene resin, a polypropylene resin, a polystyrene resin, a polyethylene terephthalate resin, a polymethyl methacrylate resin, or a polycarbonate resin. And various transparent thermoplastic resins such as transparent ABS resin. Among them, unsaturated carboxylic acid alkyl ester-based (co) polymers such as polymethyl methacrylate-based resin and transparent ABS resin,
And polycarbonate resins.
【００１２】本発明においては熱可塑性樹脂に着色剤と
してカーボンブラック及び／又は四酸化三鉄を１〜１０
０ｐｐｍ程度配合することが好ましい。１ｐｐｍ未満の
配合量ではマーキング性が不十分であり、１００ｐｐｍ
を超えると透明性が低下する。また、カーボンブラック
や四酸化三鉄の粒子径は特に限定されないが、粒子径５
〜１００ｎｍのカーボンブラックや、粒子径２０〜１０
００ｎｍの四酸化三鉄が好ましく用いられる。また、視
認性や意匠性を高めるため、有機染料等を当該熱可塑性
樹脂に使用することも可能である。In the present invention, carbon black and / or triiron tetroxide may be added as a colorant to the thermoplastic resin in an amount of 1 to 10%.
It is preferable to add about 0 ppm. If the amount is less than 1 ppm, the marking property is insufficient, and 100 ppm
If it exceeds, the transparency is reduced. Further, the particle size of carbon black or triiron tetroxide is not particularly limited.
~ 100 nm carbon black, particle size 20 ~ 10
00 nm triiron tetroxide is preferably used. Further, in order to enhance visibility and design, an organic dye or the like can be used for the thermoplastic resin.
【００１３】本発明のレーザーマーク付き樹脂部品は、
その優れた視認性や意匠性をさらに発揮するためには、
マークが付された樹脂部品の内部側に光源が配設されて
なるＰＣ機器類に適用し、光源から照射される光がレー
ザーマーク付き樹脂部品の裏面側から体裁面へと通過す
るようにして、所定形状が体裁面側から視覚的に認知さ
れ易い構造とすることが好ましい。なお、その光源とし
ては、発光ダイオードが好ましく、さらに、発光の異な
る２種類以上の発光ダーオードを使用することが、視認
性および意匠性をより高めるために好ましく、表示用部
品、操作用部品、装飾用部品への適用が好適である。The resin part with a laser mark of the present invention is:
In order to further demonstrate its excellent visibility and design,
Applied to PC devices in which a light source is provided inside the resin part with the mark, so that the light emitted from the light source passes from the back side of the resin part with the laser mark to the appearance surface It is preferable to adopt a structure in which the predetermined shape is easily visually recognized from the appearance surface side. As the light source, a light-emitting diode is preferable, and it is preferable to use two or more types of light-emitting diodes that emit different light in order to further enhance the visibility and design. It is suitable for application to parts for use.
【００１４】本発明のレーザーマーク付き樹脂部品では
所定形状のマーク部分が遮光性で黒色となるので、所定
形状をポジ型表示とする場合には、裏面側から光が照射
されると、所定形状のマーク部分は遮光され、それ以外
の部分は光が透過されるので白地に黒形状として所定形
状が視覚的に認知させるものとなる。また、逆に、所定
形状をネガ型表示とする場合には、裏面側から光が照射
されると、所定形状のマーク部分は光が透過され、それ
以外の部分は遮光されるので、黒地に白形状として所定
形状が視覚的に認知させるものとなる。In the resin part with a laser mark according to the present invention, the mark portion of a predetermined shape is light-shielding and black, so that when the predetermined shape is to be a positive display, when light is irradiated from the back side, the predetermined shape is obtained. Is shielded from light, and light is transmitted through the other portions, so that a predetermined shape is visually recognized as a black shape on a white background. Conversely, when the predetermined shape is a negative type display, when light is irradiated from the back side, the mark portion of the predetermined shape transmits light, and the other portions are shielded, so that the black portion is formed on a black background. The predetermined shape is visually recognized as the white shape.
【００１５】なお、本発明にいうポジ型、ネガ型はそれ
ぞれ写真における陽画、陰画と同じ像を意味する。Incidentally, the positive type and the negative type in the present invention mean the same images as positive and negative in a photograph, respectively.
【００１６】本発明のＰＣ機器類用樹脂部品は、射出成
形、押出成形、ブロー成形、真空成形、圧縮成形、ガス
アシスト成形等の熱可塑性樹脂成形に用いられる通常の
方法によって成形して製造すればよく、特に制限される
ものではない。The resin component for PC equipment of the present invention is manufactured by molding by a usual method used for thermoplastic resin molding such as injection molding, extrusion molding, blow molding, vacuum molding, compression molding, gas assist molding and the like. What is necessary is just, and it does not specifically limit.
【００１７】成形して得られた樹脂部品には、その体裁
面に対応する裏面側に、所定形状の鏡像の形状のマーク
部が形成されるようにレーザー光線を照射することによ
り、所定形状が体裁面側から視覚的に認知されるマーク
付きの樹脂部品を製造することができる。The resin part obtained by molding is irradiated with a laser beam so as to form a mark part having a mirror image of a predetermined shape on the back side corresponding to the surface of the resin part. A resin part with a mark visually recognized from the surface side can be manufactured.
【００１８】そのレーザー光線照射の方法は、通常の方
法で行えばよく、例えば、Ｎｄ：ＹＡＧレーザーマーカ
ー（レーザー光線波長１０６４ｎｍ）等により印字が可
能である。具体的には、Ｎｄ：ＹＡＧレーザーマーカー
（ｅｌｅｃｔｒｏｘ社製“Ｓｃｒｉｂａ２”）を用い
て、波長１０６４ｎｍのレーザー光線により、レーザー
出力５０〜１００％（１００％＝１７Ｗ）でマーキング
を行い、レーザーマーキングによるマーク部が裏面側に
形成された当該成形品を製造することができる。The laser beam may be irradiated by a usual method, for example, by using an Nd: YAG laser marker (laser beam wavelength 1064 nm) or the like. Specifically, using a Nd: YAG laser marker (“Scriba2” manufactured by electrox) with a laser beam having a wavelength of 1064 nm, marking is performed at a laser output of 50 to 100% (100% = 17 W), and the mark portion is formed by laser marking. Can be manufactured on the back side.
【００１９】このようにして得られたマーク付き樹脂部
品は、通常の方法により種々のＰＣ機器類の中に組み込
まれ、ＰＣ機器類が製造される。The resin parts with marks thus obtained are incorporated into various PC devices by a usual method, and PC devices are manufactured.
【００２０】[0020]
【実施例】以下に本発明を実施例によって説明するが、
本発明はこれら実施例に制限されるものではない。EXAMPLES The present invention will be described below with reference to examples.
The present invention is not limited to these embodiments.
【００２１】以下の実施例においては次の方法によって
特性を測定し評価した。In the following examples, characteristics were measured and evaluated by the following methods.
【００２２】（１）光線透過率 （株）日立製作所製Ｕ−２０００形ダブルビーム分光光
度計により、射出成形により作成した角板（縦８０ｍｍ
×横８０ｍｍ×肉厚１ｍｍｔ）の光線波長が７５０ｎｍ
における光線透過率を測定した。(1) Light transmittance A square plate (80 mm long) formed by injection molding using a U-2000 double beam spectrophotometer manufactured by Hitachi, Ltd.
X Width 80 mm x Wall thickness 1 mmt)
Was measured for light transmittance.
【００２３】（参考例１）透明ＡＢＳ樹脂（東レ（株）
製“トヨラック”９２０−３１９）１００重量部に対
し、平均粒子径が８４ｎｍのカーボンブラック（三菱化
学（株）製三菱カーボンブラック＃１０）を０．０００
５重量部をヘンシェルミキサーで混合した後、４０ｍｍ
φ押出機で溶融・混練して熱可塑性樹脂Ａ１を得た。こ
の熱可塑性樹脂Ａ１の光線透過率は８２％であった。Reference Example 1 Transparent ABS resin (Toray Industries, Inc.)
100 parts by weight of "Toyolac" (manufactured by Mitsubishi Chemical Corporation, Mitsubishi Carbon Black # 10) is 0.000 parts by weight with respect to 100 parts by weight of "Toyolac" 920-319 manufactured by Mitsubishi Chemical Corporation.
After mixing 5 parts by weight with a Henschel mixer, 40 mm
The mixture was melted and kneaded with a φ extruder to obtain a thermoplastic resin A1. The light transmittance of this thermoplastic resin A1 was 82%.
【００２４】（参考例２）透明ＡＢＳ樹脂（東レ（株）
製“トヨラック”９２０−３１９）１００重量部に対
し、平均粒子径が８４ｎｍのカーボンブラック（三菱化
学（株）製三菱カーボンブラック＃１０）を０．０００
５重量部、黄色有機染料（有本化学工業社製Ｐｌａｓｔ
Ｙｅｌｌｏｗ８０００）０．０１重量部をヘンシェルミ
キサーで混合した後、４０ｍｍφ押出機で溶融・混練し
て熱可塑性樹脂Ａ２を得た。この熱可塑性樹脂Ａ２の光
線透過率は６０％であった。Reference Example 2 Transparent ABS resin (Toray Industries, Inc.)
100 parts by weight of "Toyolac" (manufactured by Mitsubishi Chemical Corporation, Mitsubishi Carbon Black # 10) is 0.000 parts by weight with respect to 100 parts by weight of "Toyolac" 920-319 manufactured by Mitsubishi Chemical Corporation.
5 parts by weight, yellow organic dye (Plast manufactured by Arimoto Chemical Industry Co., Ltd.)
After mixing 0.01 parts by weight of Yellow 8000) with a Henschel mixer, the mixture was melted and kneaded with a 40 mmφ extruder to obtain a thermoplastic resin A2. The light transmittance of the thermoplastic resin A2 was 60%.
【００２５】（参考例３）ＰＭＭＡ樹脂（クラレ（株）
製“パラペット”Ｇ）１００重量部に対し、平均粒子径
が８４ｎｍのカーボンブラック（三菱化学（株）製三菱
カーボンブラック＃１０）を０．０００５重量部、赤色
有機染料（有本化学工業社製ＰｌａｓｔＲｅｄ８３７
０）をヘンシェルミキサーで混合した後、４０ｍｍφ押
出機で溶融・混練して熱可塑性樹脂Ｂ１を得た。この熱
可塑性樹脂Ｂ１の光線透過率は７１％であった。Reference Example 3 PMMA resin (Kuraray Co., Ltd.)
"Parapet G" manufactured by Arimoto Chemical Industries Co., Ltd .; 0.0005 parts by weight of carbon black having an average particle diameter of 84 nm (Mitsubishi Chemical Corporation's Mitsubishi Carbon Black # 10) per 100 parts by weight. PlastRed837
After mixing 0) with a Henschel mixer, the mixture was melted and kneaded with a 40 mmφ extruder to obtain a thermoplastic resin B1. The light transmittance of this thermoplastic resin B1 was 71%.
【００２６】（参考例４）ＰＣ樹脂（出光化学（株）製
“タフロン”Ａ１９００）１００重量部に対し、平均粒
子径が８４ｎｍのカーボンブラック（三菱化学（株）製
三菱カーボンブラック＃１０）を０．０００５重量部、
青色有機染料（有本化学工業社製“ＰｌａｓｔＢｌｕ
ｅ”８５２０）０．０１重量部をヘンシェルミキサーで
混合した後、４０ｍｍφ押出機で溶融・混練して熱可塑
性樹脂Ｃ１を得た。この熱可塑性樹脂Ｃ１の光線透過率
は４１％であった。Reference Example 4 Carbon black having an average particle diameter of 84 nm (Mitsubishi Chemical Corporation's Mitsubishi Carbon Black # 10) was added to 100 parts by weight of a PC resin ("Teflon" A1900 manufactured by Idemitsu Chemical Co., Ltd.). 0.0005 parts by weight,
Blue organic dye ("PlastBlue" manufactured by Arimoto Chemical Industry Co., Ltd.)
e ″ 8520) After mixing 0.01 part by weight with a Henschel mixer, the mixture was melted and kneaded with a 40 mmφ extruder to obtain a thermoplastic resin C1. The light transmittance of the thermoplastic resin C1 was 41%.
【００２７】［実施例１］参考例１で得られた熱可塑性
樹脂Ａ１を用いて通常の射出成形方法により操作用マウ
スの装飾用部品を製造した。得られた樹脂部品の肉厚２
ｍｍの部分の内面側に、Ｎｄ：ＹＡＧレーザー（ｅｌｅ
ｃｔｒｏｘ社製“ Ｓｃｒｉｂａ２”）を用いて所定形
状（“二十日鼠”の写真）の鏡像の形状をレーザー光線
により印字した。こうして印字したマーク付きの樹脂部
品を、通常の方法で組み込んで操作用マウスを製造し
た。[Example 1] Using the thermoplastic resin A1 obtained in Reference Example 1, decorative parts for an operation mouse were manufactured by a usual injection molding method. Thickness 2 of obtained resin part
mm, an Nd: YAG laser (ele
A mirror image of a predetermined shape (a photograph of “20 days mouse”) was printed with a laser beam using “Scriba2” manufactured by trox. The resin part with the mark printed in this manner was assembled by a usual method to produce an operation mouse.
【００２８】得られた操作用マウスのマーク部を外側よ
り見た場合、マーク部の視認性、印字された写真の緻密
性、および深みのある漆黒感（高級感）に優れていた。
なお、この印字された内面側は印字部分が発泡により隆
起、かつ薄いグレー色を呈していた。When the mark portion of the obtained operation mouse was viewed from the outside, the visibility of the mark portion, the denseness of the printed photograph, and the deep jet-black feeling (luxury feeling) were excellent.
The printed portion had a raised printed portion on the inner surface side and a light gray color.
【００２９】［実施例２］参考例２で得られた熱可塑性
樹脂Ａ２を用いて通常の射出成形方法によりディスクト
ップ型パソコン用モニターの操作用樹脂部品を製造し
た。得られた樹脂部品の肉厚１ｍｍの部分の内面側に、
Ｎｄ：ＹＡＧレーザー（ｅｌｅｃｔｒｏｘ社製“Ｓｃｒ
ｉｂａ２”）を用いて所定形状（”＋、−、←、＊”の
文字）の鏡像の形状をレーザー光線により印字した。こ
うして印字したマーク付きの樹脂部品を、通常の方法で
組み込み、その樹脂部品の裏面側印字部より１ｍｍ離れ
た位置に黄色発光ダイオードを置き点灯させるような構
造で、ディスクトップ型パソコン用モニターを製造し
た。Example 2 Using the thermoplastic resin A2 obtained in Reference Example 2, a resin part for operating a desktop personal computer monitor was manufactured by a usual injection molding method. On the inner surface side of the 1 mm thick part of the obtained resin part,
Nd: YAG laser (“Scr” manufactured by electrox)
iba2 ″) was used to print a mirror image of a predetermined shape (characters of “+, −, ←, *”) with a laser beam. A desktop type personal computer monitor was manufactured with a structure in which a yellow light emitting diode was placed and lit at a position 1 mm away from the printed portion on the back side.
【００３０】得られたディスクトップ型パソコン用モニ
ターのマーク部を外側より見た場合、透過光の中にマー
クが黒色に浮かび上がる様相を呈し、視認性、印字され
た文字輪郭の緻密性および深みのある漆黒感（高級感）
に優れていた。なお、この印字された内面側は印字部分
が発泡により***、かつ薄いグレー色を呈していた。When the mark portion of the obtained desktop type personal computer monitor is viewed from the outside, the mark appears in black in transmitted light, and the visibility, the fineness and depth of the printed character outline are obtained. Dark black (luxury)
Was excellent. The printed portion had a raised printed portion on the inner surface side and a light gray color.
【００３１】［実施例３］参考例３で得られた熱可塑性
樹脂Ｂ１を用いて通常の射出成形方法により外付け型Ｄ
ＶＤドライブ用の装飾用樹脂部品を製造した。得られた
樹脂部品の肉厚２ｍｍの部分の内面側に、Ｎｄ：ＹＡＧ
レーザー（ｅｌｅｃｔｒｏｘ社製“Ｓｃｒｉｂａ２”）
を用いて、表示文字（”ＤＶＤ”の文字）が赤文字表示
されるように、そのネガ型の鏡像の形状部分をレーザー
光線により印字し、不透明化した。こうして印字したマ
ーク付きの樹脂部品を、通常の方法で組み込み、その樹
脂部品の裏面側印字部より３ｍｍ離れた位置に赤色発光
ダイオードを置き点灯させるようにして、外付け型ＤＶ
Ｄドライブを製造した。Example 3 Using the thermoplastic resin B1 obtained in Reference Example 3, an external die D was formed by a usual injection molding method.
A decorative resin part for a VD drive was manufactured. On the inner surface side of the 2 mm thick portion of the obtained resin component, Nd: YAG
Laser (“Scriba2” manufactured by electrox)
Using a laser beam, the negative mirror image was printed with a laser beam so that the display characters ("DVD" characters) were displayed in red. The resin component with the mark printed in this manner is incorporated by a normal method, and a red light emitting diode is placed at a position 3 mm away from the printed portion on the back side of the resin component so as to light up, so that the external type DV is mounted.
D drive was manufactured.
【００３２】得られた外付け型ＤＶＤドライブの表示・
操作面を外側より見た場合、遮光された黒地の中に赤色
光の文字が浮かび上がる様相を呈し、視認性、ネガ型表
示された文字輪郭の緻密性、および深みのある漆黒感
（高級感）に優れていた。なお、この印字された内面側
は印字部分が発泡により***、かつ薄いグレー色を呈し
ていた。Display of the obtained external DVD drive
When the operation surface is viewed from the outside, the appearance of red light characters appears in a shaded black background, and the visibility, the denseness of the negative type character outline, and the deep jet-black feeling (luxury feeling) Was excellent. The printed portion had a raised printed portion on the inner surface side and a light gray color.
【００３３】［実施例４］参考例４で得られた熱可塑性
樹脂Ｃ１を用いて通常の射出成形方法によりノート型パ
ソコンモニターカバー用の装飾用部品を製造した。得ら
れた樹脂部品の肉厚１ｍｍの部分の内面側に、Ｎｄ：Ｙ
ＡＧレーザー（ｅｌｅｃｔｒｏｘ社製“Ｓｃｒｉｂａ
２”）を用いて所定形状（”Ｎｏｔｅ”の文字）の鏡像
の形状をレーザー光線により印字した。こうして印字し
たマーク付きの樹脂部品を、通常の方法で組み込み、そ
の樹脂部品の裏面側印字部より０．５ｍｍ離れた位置に
青色発光ダイオードを置き点灯させるような構造で、ノ
ート型パソコンモニターカバーを製造した。Example 4 The thermoplastic resin C1 obtained in Reference Example 4 was used to manufacture a decorative part for a notebook computer monitor cover by a usual injection molding method. On the inner surface side of the 1-mm-thick portion of the obtained resin part, Nd: Y
AG laser (Electrox “Scriba”
2 ”) was used to print a mirror image of a predetermined shape (letter“ Note ”) using a laser beam. The resin part with the mark thus printed was assembled in a usual manner, and the resin part was printed from the back side printing part. A notebook-type personal computer monitor cover was manufactured with a structure in which a blue light emitting diode was placed at a position 0.5 mm apart and turned on.
【００３４】得られたノート型パソコンモニターカバー
のマーク部を外側より見た場合、透過光の中にマークが
黒色に浮かび上がる様相を呈し、視認性、印字された文
字輪郭の緻密性、および深みのある漆黒感（高級感）に
優れていた。なお、この印字された内面側は印字部分が
ざらつき感を生じ、かつ黒色を呈していた。When the mark portion of the obtained notebook-type personal computer monitor cover is viewed from the outside, the mark appears as a black color in the transmitted light, and the visibility, the denseness of the printed character outline, and the depth Excellent jet-black feeling (luxury feeling). In addition, on the inner surface side on which the printing was performed, the printed portion had a rough feeling and had a black color.
【００３５】[0035]
【発明の効果】本発明によるレーザーマーク付きの樹脂
部品は、体裁面側より見たマーク部の視認性および深み
のある漆黒感（高級感）に優れている。しかも、体裁面
の裏側から印字を行うため、体裁面側は平滑性を保ち、
かつ取扱いによる印字面の摩耗が小さいので印字部の摩
滅を生じない。The resin part with the laser mark according to the present invention is excellent in the visibility of the mark part viewed from the appearance side and the deep jet-black feeling (luxury feeling). Moreover, since printing is performed from the back side of the appearance surface, the appearance surface side maintains smoothness,
In addition, since the abrasion of the printed surface due to handling is small, the printed portion is not worn.
【００３６】また、緻密な形状のマーキングが難しい材
料や、体裁面側に平滑性が要求される用途においても、
レーザー照射条件幅を非常に広くすることができるため
容易にマーキングを行うことができる。[0036] Further, even in a material in which it is difficult to mark a dense shape or in an application in which smoothness is required on the appearance side,
Since the laser irradiation condition width can be made very wide, marking can be easily performed.
【００３７】さらにまた、レーザーマーキングされる成
形品は単一の透明樹脂で構成することができるので、樹
脂材料のリサイクル性向上にも有効である。Furthermore, since the molded article to be laser-marked can be composed of a single transparent resin, it is effective in improving the recyclability of the resin material.
【００３８】このように、リサイクル性および体裁面の
平滑性に優れ、かつ深みのある漆黒感鮮明な黒色マーキ
ングを呈することができるので、文字・記号等の表示が
付されるＰＣ機器類用樹脂部品として有効である。As described above, since it is excellent in recyclability and smoothness of the appearance surface and can provide a deep black jet-clear vivid black marking, a resin for PC devices to which characters and symbols are displayed is provided. It is effective as a part.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4F209 AA13 AA21 AA28 AG05 AH42 PA15 PB01 PC05 5C096 AA11 BA06 BC12 CA12 CC06 EB11 FA12 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 4F209 AA13 AA21 AA28 AG05 AH42 PA15 PB01 PC05 5C096 AA11 BA06 BC12 CA12 CC06 EB11 FA12
Claims (6)
り、レーザー光線照射によるマーク部が形成された樹脂
成形部品であって、レーザー光線照射によるマーク部が
樹脂成形部品の体裁面に対する裏面側に所定形状の鏡像
の形状で形成され所定形状が体裁面側から視覚的に認知
されることを特徴とする、パーソナルコンピューター又
はパーソナルコンピューター周辺機器用のレーザーマー
ク付き樹脂部品。1. A resin molded part made of a transparent or translucent thermoplastic resin and having a mark formed by laser beam irradiation, wherein the mark formed by laser beam irradiation has a predetermined shape on the back side with respect to the appearance surface of the resin molded part. A resin part with a laser mark for a personal computer or a peripheral device of a personal computer, wherein the resin part is formed in a mirror image shape and is visually recognized from a presentation surface side.
請求項１記載の、パーソナルコンピューター又はパーソ
ナルコンピューター周辺機器用のレーザーマーク付き樹
脂部品。2. The resin part with a laser mark for a personal computer or a peripheral device of a personal computer according to claim 1, wherein the predetermined shape is a positive type or a negative type display.
された樹脂部品として、請求項１又は２記載のレーザー
マーク付き樹脂部品を組込んでなることを特徴とするパ
ーソナルコンピューター又はパーソナルコンピューター
周辺機器。3. A personal computer or a peripheral of a personal computer, wherein the resin part with the laser mark according to claim 1 or 2 is incorporated as a resin part with a mark for decoration, operation or display. machine.
された樹脂部品が組込まれ、該樹脂部品の内部側に光源
が配設されてなるパーソナルコンピューター又はパーソ
ナルコンピューター周辺機器であって、マークが付され
た樹脂部品として、請求項１又は２記載のレーザーマー
ク付き樹脂部品を組込んでなることを特徴とするパーソ
ナルコンピューター又はパーソナルコンピューター周辺
機器。4. A personal computer or a personal computer peripheral device comprising a resin component with a mark for decoration, operation or display incorporated therein and a light source disposed inside the resin component. A personal computer or a peripheral device for a personal computer, wherein the resin part with the laser mark according to claim 1 or 2 is incorporated as the resin part with a mark.
載のパーソナルコンピューター又はパーソナルコンピュ
ーター周辺機器。5. The personal computer or personal computer peripheral according to claim 4, wherein the light source is a light emitting diode.
ードの少なくとも２種類以上を使用する請求項５記載の
パーソナルコンピューター又はパーソナルコンピュータ
ー周辺機器。6. The personal computer or personal computer peripheral device according to claim 5, wherein at least two types of light emitting diodes having different emission colors are used as the light source.