JP2001262407A - Clothing and method for producing fiber sheet to be used therefor - Google Patents
Clothing and method for producing fiber sheet to be used thereforInfo
- Publication number
- JP2001262407A JP2001262407A JP2000071962A JP2000071962A JP2001262407A JP 2001262407 A JP2001262407 A JP 2001262407A JP 2000071962 A JP2000071962 A JP 2000071962A JP 2000071962 A JP2000071962 A JP 2000071962A JP 2001262407 A JP2001262407 A JP 2001262407A
- Authority
- JP
- Japan
- Prior art keywords
- breast cup
- less
- thickness
- clothing
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、ブラジャー、ボデ
ィスーツなど***カップを有する衣類および成形用繊維
シートの製造方法に関する。特に、薄くて、軽くて、通
気性、透湿性、保形性と肌触りが良好であり、かつバス
トのシルエットを美しく表現でき、洗濯耐久性の優れた
***カップを有する衣類および成形用繊維シートに関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a garment having a breast cup, such as a bra and a body suit, and a method for producing a fiber sheet for molding. In particular, the present invention relates to a garment and a molding fiber sheet having a breast cup that is thin, light, has good breathability, moisture permeability, shape retention, and feel, can beautifully express a bust silhouette, and has excellent washing durability. .
【0002】[0002]
【従来の技術】従来より、***カップを有する女性用衣
料類、例えば、ブラジャー、ロングラインブラジャー、
ビスチェ、ボディスーツ、スリーインワン、ブラテデ
ィ、ブラキャミソールあるいはブラスリップなどがあ
る。***カップを有する衣類は、着用者の***にあてが
われるため、柔らかい感触と膨らみのある立体形状が要
求され、女性の衣服として広く普及している。2. Description of the Related Art Conventionally, women's clothing having a breast cup, for example, a bra, a long line bra,
There are bustiers, bodysuits, three-in-ones, teddies, bra camisoles or bra slips. Clothing with a breast cup is applied to the breasts of the wearer, and is required to have a soft touch and a swelling three-dimensional shape, and is widely used as clothing for women.
【0003】その素材は、従来より、不織布、発泡ポリ
ウレタンシート、ポリエステル繊維編物などが用いられ
ている。Conventionally, nonwoven fabrics, foamed polyurethane sheets, knitted polyester fibers and the like have been used as such materials.
【0004】これらは、***の形を美しく表現するため
に、***の形に近い立体曲面を有するカップの形が要求
され、ダーツを入れた縫製品、各種布帛を多層に積層し
たもの、熱成形したものなどがある。[0004] In order to beautifully express the shape of the breast, these require the shape of a cup having a three-dimensional curved surface close to the shape of the breast. And others.
【0005】かかる従来技術では、***形状を美しく表
現するためには、その形状保持のため硬く、厚く、しか
も多種の縫い合わせたものとならざるを得なかった。ま
た、繰り返し洗濯により形が保持できないこと、風合い
が変化することなどの問題があった。特に、***カップ
に求められる特性を有しかつダーツを有しない一枚使い
のものはこれまでなかった。[0005] In the prior art, in order to beautifully express the breast shape, the breast shape had to be hardened, thickened, and stitched together in various types to maintain the shape. There are also problems such as the inability to maintain the shape due to repeated washing and the change in texture. In particular, there has not been a single-piece type having the characteristics required for a breast cup and having no darts.
【0006】[0006]
【発明が解決しようとする課題】本発明は、上記した従
来の欠点や問題点を解消することを目的とするものであ
る。特に、薄くて、軽くて、保形性と肌触りが良好であ
り、かつバストのシルエットを美しく表現でき、洗濯耐
久性の優れた***カップを有する衣類および成形用繊維
シートを提供するものである。SUMMARY OF THE INVENTION An object of the present invention is to solve the above-mentioned conventional disadvantages and problems. In particular, an object of the present invention is to provide clothing and a fiber sheet for molding having a breast cup that is thin, light, has good shape retention and feel, can express a beautiful bust silhouette, and has excellent washing durability.
【0007】[0007]
【課題を解決するための手段】本発明は、次のとおりの
構成をとるものである。The present invention has the following configuration.
【0008】(1)ダーツを有しない一枚使い***カッ
プを有する衣料において、***カップが少なくとも非晶
配向度が0.35以下、見掛ヤング率が1960N/m
m2以下であるポリエステル繊維を用いてなり、高さが
40mm以上、幅が80mm以上であり、厚さが0.5
〜2.0mmであって、その厚さ変動が30%以下であ
ることを特徴とする衣類。(1) In a garment having a single-use breast cup without darts, the breast cup has at least an amorphous orientation degree of 0.35 or less and an apparent Young's modulus of 1960 N / m.
it using the polyester fiber is m 2 or less, is more than 40mm height, and the width is 80mm or more and a thickness of 0.5
Clothing having a thickness variation of up to 2.0 mm and a thickness variation of 30% or less.
【0009】(2)ダーツを有しない一枚使い***カッ
プを有する衣料において、***カップが少なくとも非晶
配向度が0.35以下、見掛ヤング率が1960N/m
m2以下であるポリエステル繊維と、非晶配向度が0.
45以上、見掛ヤング率が2940N/mm2 以上であ
るポリエステル繊維を用いてなり、高さが40mm以
上、幅が80mm以上であり、厚さが0.5〜2.0m
mであって、その厚さ変動が30%以下であることを特
徴とする衣類。(2) In a garment having a single-use breast cup without darts, the breast cup has at least an amorphous orientation degree of 0.35 or less and an apparent Young's modulus of 1960 N / m.
m 2 or less, and a degree of amorphous orientation of 0.1.
45 or more, using a polyester fiber having an apparent Young's modulus of 2940 N / mm 2 or more, a height of 40 mm or more, a width of 80 mm or more, and a thickness of 0.5 to 2.0 m
m, the thickness of which is not more than 30%.
【0010】(3)***カップにおいて、少なくとも一
種のポリエステル繊維の単糸太さが2デシテックス以下
であることを特徴とする前記(1)または(2)記載の
衣類。(3) The garment according to (1) or (2), wherein in the breast cup, the single yarn thickness of at least one kind of polyester fiber is 2 dtex or less.
【0011】(4)***カップにおいて、少なくとも一
種のポリエステル繊維がポリエチレンテレフタレート繊
維であることを特徴とする前記(1)〜(3)のいずれ
かに記載の衣類。(4) The clothing according to any one of (1) to (3), wherein in the breast cup, at least one kind of polyester fiber is polyethylene terephthalate fiber.
【0012】(5)***カップにおいて、少なくとも非
晶配向度0.35以下で見掛ヤング率が1960N/m
m2 以下のポリエステル繊維と、非晶配向度0.45以
上で見掛ヤング率が2940N/mm2 以上のポリエス
テル繊維の両方がブラジャーカップの表面に露出してい
ることを特徴とする前記(1)〜(3)のいずれかに記
載の衣類。(5) In the breast cup, the apparent Young's modulus is at least 1960 N / m when the degree of amorphous orientation is 0.35 or less.
(1) Both the polyester fiber having a m 2 or less and the polyester fiber having an amorphous orientation degree of 0.45 or more and an apparent Young's modulus of 2940 N / mm 2 or more are exposed on the surface of the brassiere cup. The clothing according to any one of (1) to (3).
【0013】(6)***カップが、分散染料で染色され
たことを特徴とする前記(1)〜(5)のいずれかに記
載の衣類。(6) Clothing according to any one of (1) to (5), wherein the breast cup is dyed with a disperse dye.
【0014】(7)***カップが、分散染料で染色され
発色性が異なる2種以上のポリエステル繊維からなるこ
とを特徴とする前記(1)〜(5)のいずれかに記載の
衣類。(7) The garment as described in any one of (1) to (5) above, wherein the breast cup is made of two or more kinds of polyester fibers dyed with a disperse dye and having different coloring properties.
【0015】(8)***カップが、ポリエステル繊維フ
ィラメントであることを特徴とする前記(1)〜(5)
のいずれかに記載の衣類。(8) The above-mentioned (1) to (5), wherein the breast cup is a polyester fiber filament.
Clothing according to any of the above.
【0016】(9)***カップが、織物、編物、または
不織布から構成されていることを特徴とする前記(1)
〜(5)のいずれかに記載の衣類。(9) The breast cup is made of a woven fabric, a knitted fabric, or a non-woven fabric.
Clothing according to any one of (1) to (5).
【0017】(10)前記(1)〜(9)のいずれかに
記載の衣類が、ブラジャー、ボディスーツ、ビスチェ、
ブラテディ、スリーインワン、ブラキャミソール、ブラ
スリップ、ロングラインブラジャー、および水着から選
ばれたものであることを特徴とする衣類。(10) The clothing according to any one of (1) to (9) is a bra, a body suit, a bustier,
A garment characterized by being selected from a teddy, a three-in-one, a bra camisole, a bra slip, a long line bra, and a swimsuit.
【0018】(11)複屈折率Δnが0.02〜0.0
83 のポリエチレンテレフタレート繊維を有するシート
を、60〜90℃の乾式および/または湿式雰囲気下
で、タテ、ヨコ方向とも、2%/秒以下の収縮速度で1
0〜25%収縮させた後、少なくとも染色液温55℃〜
70℃において、0.5℃/分以下の速度で昇温し染色
することを特徴とする繊維シートの製造方法。(11) Birefringence Δn is 0.02 to 0.0
8 3 a sheet having a polyethylene terephthalate fiber, of 60 to 90 ° C. Dry and / or under a wet atmosphere, vertical, both horizontal direction, 1 2% / second or less shrinkage rate
After shrinking by 0 to 25%, at least the dyeing solution temperature is 55 ° C.
A method for producing a fiber sheet, comprising heating and dyeing at 70 ° C at a rate of 0.5 ° C / min or less.
【0019】(12)複屈折率Δnが0〜0.083 の
ポリエチレンテレフタレート繊維を有するシートを、6
0〜90℃の乾式および/または湿式雰囲気下で、タ
テ、ヨコ方向とも、2%/秒以下の収縮速度で10〜2
5%収縮させた後、少なくとも室温〜50℃において
0.3℃/分以上の速度で昇温し、55℃〜70℃にお
いて0.5℃/分以下の速度で昇温し、および75〜1
20℃において0.3℃/分以上の速度で昇温すること
を特徴とする繊維シートの製造方法。[0019] (12) a sheet birefringence Δn has a polyethylene terephthalate fiber of 0 to 0.08 3, 6
In a dry and / or wet atmosphere at 0 to 90 ° C, a shrinkage rate of 2% / sec or less in both the vertical and horizontal directions is 10 to 2
After shrinking by 5%, the temperature is increased at a rate of at least 0.3 ° C./min from room temperature to 50 ° C., and at a rate of 0.5 ° C./min or less at 55 ° C. to 70 ° C .; 1
A method for producing a fiber sheet, wherein the temperature is increased at a rate of 0.3 ° C./min or more at 20 ° C.
【0020】[0020]
【発明の実施の形態】以下、さらに詳しく本発明につい
て説明をする。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in more detail.
【0021】本発明は、ダーツを有しない一枚使い***
カップを有する衣類であり、特に、***カップ(***形
状をした芯材)が一枚使いである。それを実現する繊維
シートは、深絞りの成形が可能であり、薄くて、軽く
て、身体の動きによく順応できるものである。さらに、
好みの色に自在に染色が可能であり、長期間の着用や繰
り返し洗濯により、型くずれがし難いという特徴を有す
るものである。The present invention is a garment having a single-use breast cup without darts, and particularly, a single breast cup (a breast-shaped core material). A fiber sheet that achieves this can be formed by deep drawing, is thin, light, and can adapt well to body movements. further,
It has the characteristic that it can be dyed freely to the desired color and it is difficult to lose its shape due to long-term wearing or repeated washing.
【0022】かかる本発明の構成は、***カップに用い
る繊維は少なくともポリエステル繊維であって、非晶配
向度が0.35以下、好ましくは0.30以下、見掛ヤ
ング率が1960N/mm2 以下、好ましくは980N
/mm2 以下である。いずれもこの値を上回ると成形に
おける追随性が不十分であり、均一な深絞り加工はでき
ない。According to the constitution of the present invention, the fibers used in the breast cup are at least polyester fibers, the degree of amorphous orientation is 0.35 or less, preferably 0.30 or less, and the apparent Young's modulus is 1960 N / mm 2 or less. , Preferably 980N
/ Mm 2 or less. In any case, when the value exceeds this value, followability in molding is insufficient, and uniform deep drawing cannot be performed.
【0023】また、カップの高さが40mm以上、好ま
しくは50mm以上、幅が80mm以上、好ましくは9
0mm以上の***形状の立体曲面を有するものである。
これは、従来技術では達成できない均一な深絞りが可能
であることを示すものであり、***カップにおいて、そ
のカップの形を保つための芯材が他の布帛と併用しない
一枚使いであっても、***のサイズに広く対応でき、ま
た、***の形を美しく表現できる***カップとすること
が可能である。The height of the cup is 40 mm or more, preferably 50 mm or more, and the width is 80 mm or more, preferably 9 mm or more.
It has a three-dimensional curved surface of a breast shape of 0 mm or more.
This indicates that uniform deep drawing that is not possible with the prior art is possible, and in a breast cup, the core material for maintaining the shape of the cup is a single piece that is not used in combination with other fabrics. It is also possible to provide a breast cup that can widely correspond to the size of the breast and that can beautifully express the shape of the breast.
【0024】本発明でいうポリエステル繊維とは、ポリ
エチレンテレフタレート、ポリブチレンテレフタレー
ト、ポリプロピレンテレフタレートなどの芳香族ポリエ
ステルが好ましく適用でき、特にポリエチレンテレフタ
レートが好ましく適用できる。また、ポリエチレンテレ
フタレートにポリアルキレングリコールが共重合された
共重合体や、ポリエチレンテレフタレートに5−ナトリ
ウムスルホイソフタル酸が共重合された共重合体も好ま
しく適用できる。As the polyester fiber referred to in the present invention, aromatic polyesters such as polyethylene terephthalate, polybutylene terephthalate, and polypropylene terephthalate can be preferably used, and polyethylene terephthalate can be particularly preferably used. Further, a copolymer in which polyethylene terephthalate is copolymerized with polyalkylene glycol or a copolymer in which polyethylene terephthalate is copolymerized with 5-sodium sulfoisophthalic acid can be preferably applied.
【0025】さらに、カップの厚さが0.5〜2.0m
m好ましくは0.8〜1.5mmであって厚さ変動が3
0%以下、好ましくは20%以下と薄い繊維シートであ
っても極めて厚さの差が小さいものである。Further, the thickness of the cup is 0.5 to 2.0 m
m is preferably 0.8 to 1.5 mm and the thickness variation is 3
Even if the fiber sheet is as thin as 0% or less, preferably 20% or less, the difference in thickness is extremely small.
【0026】ここで、ポリエステル繊維の非晶配向度と
は次の方法にて測定された値である。Here, the degree of amorphous orientation of the polyester fiber is a value measured by the following method.
【0027】測定法:偏光蛍光法 装 置:日本分光工業製FOM−1 光学系:透過法(励起光波長:365nm、蛍光波長:
420nm) 測定系:偏光子‖検光子、および偏光子〓検光子で回転
して、面内の偏光蛍光強度(I‖、I〓)の角度分布を
得た。 ここで、‖は平行を示し、〓は垂直を示す。 非晶配向度は下記式からの一軸配向係数f2 で求めた。Measurement method: polarized fluorescence method Apparatus: FOM-1 manufactured by JASCO Corporation Optical system: transmission method (excitation light wavelength: 365 nm, fluorescence wavelength:
(420 nm) Measurement system: Rotation was performed using a polarizer 偏光 analyzer and a polarizer〓analyzer to obtain an angular distribution of in-plane polarized fluorescence intensity (I‖, I〓). Here, ‖ indicates parallel, and 〓 indicates vertical. The degree of amorphous orientation was determined by a uniaxial orientation coefficient f 2 from the following equation.
【0028】f2 =3/2[{I‖(0)+2I〓
(0)}/K−1/3] 但し、K={I‖(0)+4I〓(0)+8/3I‖
(90)} I‖(0) :‖測定での軸方向の相対偏光蛍光強度 I‖(90):‖測定での上記と直交方向の相対偏光蛍
光強度 I〓(0) :〓測定での軸方向の相対偏光蛍光強度 また、見掛ヤング率は、JIS−L−1013、7.1
0に準じて測定された値である。F 2 = 3/2 [{I {(0) + 2I}}
(0)} / K- /] where K = {I‖ (0) + 4I〓 (0) + 8 / 3I‖
(90)} I‖ (0): ‖Measured relative polarized fluorescence intensity in the axial direction I‖ (90): ‖Measured relative polarized fluorescence intensity in the orthogonal direction to the above I〓 (0): 〓Measured The relative polarized fluorescence intensity in the axial direction The apparent Young's modulus is JIS-L-1013, 7.1.
It is a value measured according to 0.
【0029】本発明でいう***カップの高さは、成形加
工を行った繊維シートからカップ部のみを裁断あるいは
くり抜き、図1に示すように、底部からトップまでの長
さ(H)である。また、***カップの幅は同様にカップ
底部間における最短内径(W)である。The height of the breast cup referred to in the present invention is the length (H) from the bottom to the top as shown in FIG. 1 by cutting or hollowing out only the cup portion from the formed fiber sheet. The width of the breast cup is also the shortest inner diameter (W) between the cup bottoms.
【0030】***カップの厚さは、厚さ計(尾崎製作所
製商品名「PEACOCK」)を用いて、カップ部の1
0箇所の厚さを偏りなく測定し、下記式により厚さ平均
値と、厚さ変動の最高値を算出したものである。The thickness of the breast cup was measured using a thickness gauge (trade name "PEACOCK" manufactured by Ozaki Seisakusho).
The thickness at zero point was measured without bias, and the average value of the thickness and the maximum value of the thickness variation were calculated by the following formula.
【0031】厚さ平均値(mm)= 厚さの合計(m
m)/測定数(n) 厚さ変動率= (各部位の厚さ / 厚さ平均値 )×10
0 本発明がダーツを有しない***カップとする理由をブラ
ジャーに例をとって説明する。図2に示すように、カッ
プ部に縫い目が存在しないものであり、縫い目部の凹凸
による肌こすれが少なく、***とよくフィットし感触が
良好である。また、スポーツなどのによる発汗を伴う場
合、通気性と透湿性が良好であり、抜群の快適性を有す
る。強度面でも有利であり、着用時の大きく激しい動き
に対しても、繰り返し洗濯に対しても好ましい耐久性を
有する。Average thickness (mm) = total thickness (m
m) / number of measurements (n) Thickness variation rate = (thickness of each part / thickness average value) × 10
0 The reason why the present invention adopts a dartless breast cup will be described with reference to a bra. As shown in FIG. 2, the seam does not exist in the cup portion, the skin is not rubbed due to the unevenness of the seam portion, the breast fits well, and the feel is good. In addition, when sweating due to sports or the like is involved, the air permeability and the moisture permeability are good, and there is excellent comfort. It is also advantageous in terms of strength, and has favorable durability against large and violent movements during wearing and repeated washing.
【0032】もちろん、ダーツを有しない一枚使いであ
る本発明の構成は、縫製工程での手間が省け、省人化と
低コスト化に貢献できることは言うまでもない。Needless to say, the configuration of the present invention, which is a single-piece use without darts, can save labor in the sewing process and contribute to labor saving and cost reduction.
【0033】本***カップを構成するポリエステル繊維
は、ステープル形態であってもよく、また、フィラメン
ト形態であってもよいが、好ましくは繰り返し洗濯に対
する耐久性や染色加工のしやすさからフィラメント形態
が望ましい。The polyester fiber constituting the breast cup may be in the form of a staple or a filament, but is preferably in the form of a filament in view of durability against repeated washing and ease of dyeing. desirable.
【0034】また、本発明の好ましい態様の一つとして
は、ダーツを有しない一枚使い***カップを有する衣料
であって、***カップが少なくとも非晶配向度が0.3
5以下、見掛ヤング率が1960N/mm2 以下である
ポリエステル繊維と、非晶配向度が0.4以上であり、
かつ見掛ヤング率が2960以上であるポリエステル繊
維(高非晶配向度・高見掛ヤング率側ポリエステル繊
維)、との混繊糸(引揃糸、エア交絡糸、交撚糸、合撚
糸など)として用い、高さが40mm以上、幅が80m
m以上であり、厚さが0.5〜2.0mmであって厚さ
変化率が30%以下である***カップを有する衣類であ
る。One preferred embodiment of the present invention is a garment having a single-use breast cup having no darts, wherein the breast cup has at least an amorphous orientation degree of 0.3.
5 or less, a polyester fiber having an apparent Young's modulus of 1960 N / mm 2 or less, and an amorphous orientation degree of 0.4 or more;
As a mixed fiber with a polyester fiber having an apparent Young's modulus of 2960 or more (a polyester fiber having a high degree of amorphous orientation and high apparent Young's modulus), such as a aligned yarn, an air entangled yarn, a twisted yarn, and a twisted yarn. Use, height 40mm or more, width 80m
m or more, the thickness is 0.5 to 2.0 mm, and the thickness change rate is 30% or less.
【0035】ここで、前述と異なる点は、一方のポリエ
ステル繊維が、非晶配向度0.45以上、好ましくは
0.55以上、特に好ましくは0.60以上であって、
見掛ヤング率が2940N/mm2以上、好ましくは3
430N/mm2以上、特に好ましくは3920N/m
m2 以上のポリエステル繊維を併用した混繊糸を用いる
ことである。Here, the difference from the above is that one of the polyester fibers has an amorphous orientation degree of 0.45 or more, preferably 0.55 or more, particularly preferably 0.60 or more.
Apparent Young's modulus is 2940 N / mm 2 or more, preferably 3
430 N / mm 2 or more, particularly preferably 3920 N / m
It is to use a mixed fiber using polyester fibers having a m 2 or more in combination.
【0036】かかる理由は、非晶配向度および見掛ヤン
グ率が異なる二種以上のポリエステル繊維を用いること
により、***カップの表面に両方のポリエステル繊維が
露出し、その発色性が異なるため、テカテカとした光沢
が抑えられ自然観を有する高級感の色相が得られるこ
と、また繊維シートの内部構造に膨らみを発現させ柔軟
で感触のよい***カップとすることができるためであ
る。The reason for this is that by using two or more types of polyester fibers having different degrees of amorphous orientation and apparent Young's modulus, both polyester fibers are exposed on the surface of the breast cup and their coloring properties are different. This is because a high-quality hue having a natural appearance can be suppressed and a swelling is developed in the internal structure of the fiber sheet, so that a soft and comfortable breast cup can be obtained.
【0037】ポリエステル繊維の太さは、全てあるいは
いずれかが2デシテックス以下、好ましくは1デシテッ
クス以下の極細繊維であることが好ましい。特に、高非
晶配向度・高見掛ヤング率側のポリエステル繊維は細い
ことが、肌との感触の点で特に好ましい。As for the thickness of the polyester fiber, it is preferable that all or any of the polyester fibers is an ultrafine fiber of 2 dtex or less, preferably 1 dtex or less. In particular, it is particularly preferable that the polyester fiber having a high degree of amorphous orientation and a high apparent Young's modulus is thin from the viewpoint of feeling with the skin.
【0038】また、本発明の***カップは、ポリエステ
ル繊維から構成されることから、分散染料でフルカラー
に染色できかつ高い染色堅牢度が得られ好ましい。しか
も、二種以上の異なるポリエステル繊維を用いることか
ら、その発色性が異なり、ポリエステル繊維独特のテカ
テカした光沢や深みのない色相の欠点を改善することが
できる。Further, since the breast cup of the present invention is composed of polyester fiber, it can be dyed in full color with a disperse dye and has high dyeing fastness, which is preferable. Moreover, since two or more different polyester fibers are used, the coloring properties of the polyester fibers are different, and the disadvantages of the glossy and deep hue peculiar to the polyester fibers can be improved.
【0039】***カップを構成する布帛は、織物、編物
あるいは不織布など従来公知の繊維シートが用いられ特
に限定されない。特に、***カップ材は良好な保形性を
得るためには、織物、編物とも嵩の高い多重組織が好ま
しく適用される。その具体的な例としては、織物では、
タテ二重織物、ヨコ二重織物、タテヨコ二重織物など、
編物では、ジャージ生地特にダブルジャージ生地、ダブ
ルラッセル生地、モケット生地あるいはダンボールニッ
ト生地などが好ましく適用される。ここでダンボールニ
ットとは、表地と裏地を中糸(繋ぎ糸、ジョイント糸あ
るいは連結糸と呼ばれるもの)で連結した多重編物ある
いは立体編物のことである。The fabric constituting the breast cup is not particularly limited, and a conventionally known fiber sheet such as a woven fabric, a knitted fabric, or a non-woven fabric is used. In particular, in order to obtain good shape retention of the breast cup material, a bulky multiple structure is preferably applied to both woven fabric and knitted fabric. As a specific example, in textiles,
Vertical double woven fabric, horizontal double woven fabric, vertical horizontal double woven fabric, etc.
For knitted fabrics, jersey fabrics, particularly double jersey fabrics, double Russell fabrics, moquette fabrics or cardboard knit fabrics are preferably applied. Here, the corrugated cardboard knit refers to a multi-layered knitted or three-dimensional knitted fabric in which a surface material and a lining are connected by a middle yarn (called a connecting yarn, a joint yarn or a connecting yarn).
【0040】本発明の***カップを有する衣類として
は、前記***カップを有するブラジャ、ボディスーツ、
ビスチェ、ブラテディ、スリーインワン、ブラキャミソ
ール、ブラスリップ、ロングラインブラ、水着(図2〜
図11参照)などであり、一枚使いで薄くて、軽くて、
良好な保形性を活かしたエレガントで機能性を有し、従
来技術では得難い衣類を提供することができる。The clothing having the breast cup of the present invention includes a bra, a body suit, and the like having the breast cup.
Bustier, Blatdy, Three in One, Bra Camisole, Bra Slip, Long Line Bra, Swimsuit (Figure 2
(See Fig. 11)
It is possible to provide clothing that is elegant and functional with good shape retention and is difficult to obtain with conventional techniques.
【0041】次に、本発明の***カップを有する衣類を
製造する好ましい方法を以下述べる。Next, a preferred method of manufacturing a garment having the breast cup of the present invention will be described below.
【0042】ポリエステル繊維として、複屈折率Δnが
0.02〜0.08 好ましくはΔnが0.03〜0.
06の高配向未延伸糸と、単糸繊度が2デシテックス以
下のポリエチレンテレフタレート極細繊維フィラメント
延伸糸の混繊糸とし、これを多重編物を編成し生機を作
製する。The polyester fiber has a birefringence Δn of 0.02 to 0.08. Preferably, Δn is 0.03-0.
A highly-oriented undrawn yarn of No. 06 and a drawn yarn of a polyethylene terephthalate ultrafine fiber filament having a single yarn fineness of 2 dtex or less are knitted into a multi-knitted fabric to produce a greige machine.
【0043】ここで複屈折率ΔnはNa電球によりD線
色光を用い、セルナモン法およびコンペンセータ法で測
定された値である。Here, the birefringence index Δn is a value measured by the Cernamon method and the compensator method using D-line color light with a Na bulb.
【0044】次いで、この生機を60〜95℃の乾式お
よび/または湿式雰囲気下で熱処理し2%/秒以下、好
ましくは1%/秒以下、特に好ましくは0.5%/秒の
極めて緩やかに収縮せしめタテ、ヨコとも10〜25%
収縮させる。このように、繊維シートが抵抗を受けつつ
収縮させるように、制限収縮させることが好ましい。い
きなり高温の雰囲気下に曝すことや急激に収縮させるこ
とは、***カップの特性およびスムース表面や柔軟な繊
維シートとするに好ましくない。この特殊な加工条件
が、後の工程である成形において、厚さムラの少ない深
絞り加工を可能し、本発明の***カップを作製するのに
重要である。この点も従来技術とは全く異なる点であ
る。Then, the greige is heat-treated in a dry and / or wet atmosphere at 60 to 95 ° C., and is gently heated to 2% / sec or less, preferably 1% / sec or less, particularly preferably 0.5% / sec. 10-25% for both shrunk length and width
Shrink. As described above, it is preferable to limit the contraction so that the fiber sheet contracts while receiving the resistance. Sudden exposure to a high-temperature atmosphere or sudden shrinkage is not preferable for the characteristics of a breast cup, a smooth surface, and a flexible fiber sheet. These special processing conditions enable deep drawing with little thickness unevenness in the subsequent molding step, and are important for producing the breast cup of the present invention. This point is also completely different from the prior art.
【0045】次いで、染色機を用いて、分散染料浴中
で、少なくとも55℃〜70℃において、0.5℃/分
以下、好ましくは0.3℃/分以下、特に好ましくは
0.2℃/分という極めて緩やかに速度で昇温させる。
本発明の***カップを作製する繊維シートとするには、
この染色昇温条件が重要であり本発明の特異な特性を発
現する要件である。つまり、この条件も後の工程である
成形において厚さムラの少ない深絞りを可能とする一つ
の要件である。また、さらにこの染色においては少なく
とも室温〜50℃では0.3℃/分以上好ましくは0.
5℃/以上の速度で昇温し、少なくとも55℃〜70℃
では0.5℃/分以下、好ましくは0.3℃/分以下、
特に好ましくは0.2℃/分以下という極めて緩やかに
な速度で昇温し、少なくとも75〜120℃では0.3
℃/分以上好ましくは0.5℃/以上の速度で昇温する
方法が好ましく適用される。昇温が完了したら110〜
130℃にて10〜60分染色を行う。もちろん、必要
に応じて余剰染料を除去するために従来公知の還元洗浄
を行ってもよい。Then, using a dyeing machine, in a disperse dye bath at a temperature of at least 55 ° C. to 70 ° C., 0.5 ° C./min or less, preferably 0.3 ° C./min or less, particularly preferably 0.2 ° C./min. / Minute at a very slow rate.
To make a fiber sheet for producing the breast cup of the present invention,
These conditions for raising the temperature of dyeing are important and are the requirements for expressing the unique characteristics of the present invention. In other words, this condition is also one of the requirements for enabling deep drawing with less thickness unevenness in the subsequent forming step. Further, in this dyeing, at least at room temperature to 50 ° C, 0.3 ° C / min or more, preferably at least 0.3 ° C / min.
Temperature is raised at a rate of 5 ° C./or more, at least 55 ° C. to 70 ° C.
0.5 ° C./min or less, preferably 0.3 ° C./min or less,
Particularly preferably, the temperature is raised at an extremely slow rate of 0.2 ° C./min or less,
A method of increasing the temperature at a rate of at least 0.5 ° C./min, preferably at least 0.5 ° C./min is preferably applied. When the heating is completed,
Stain at 130 ° C. for 10-60 minutes. Of course, conventionally known reduction washing may be performed to remove excess dye, if necessary.
【0046】また、帯電防止剤、柔軟剤、抗菌剤などの
機能性剤を付与し従来公知の仕上げセットを施してもよ
い。Further, a functional agent such as an antistatic agent, a softening agent and an antibacterial agent may be provided to give a conventionally known finishing set.
【0047】得られた加工済み繊維シートは、***カッ
プ形状の金型にセットし130〜230℃、クリアラン
ス0〜3.0mm、10〜180秒プレス処理される。
それをカップ形状に裁断し衣類に応じた部材を用いて縫
製することにより作られる。The obtained processed fiber sheet is set in a breast cup-shaped mold and pressed at 130 to 230 ° C. with a clearance of 0 to 3.0 mm for 10 to 180 seconds.
It is made by cutting it into a cup shape and sewing it using a member suitable for clothing.
【0048】もちろん、本発明の***カップを芯材とし
て表面にレースを配したり、プリントを行って装飾や柄
を付与したものであってもよい。Of course, the breast cup of the present invention may be used as a core material, and a lace may be provided on the surface, or a decoration or pattern may be provided by printing.
【0049】[0049]
【実施例】実施例1、実施例2 139デシテックス、36フィラメントのポリエチレン
テレフタレート高配向未延伸糸(Δnが0.03)と8
3デシテックス、72フィラメントのポリエチレンテレ
フタレート延伸糸(Δnが0.15)をエア交絡して複
合糸Aを作製した。266デシテックス、48フィラメ
ントのポリエチレンテレフタレート高配向未延伸糸(Δ
nが0.03)と83デシテックス、72フィラメント
のポリエチレンテレフタレートフィラメント延伸糸(Δ
nが0.15)をエア交絡して複合糸Bを作製した。A
糸を表地および裏地に用い、B糸を中糸に用いてダンボ
ールニット組織に編成し生機を作製した。Examples 1 and 2 139 dtex, 36-filament polyethylene terephthalate highly oriented undrawn yarn (Δn 0.03) and 8
A composite yarn A was prepared by entanglement of 3 dtex, 72-filament drawn polyethylene terephthalate yarn (Δn: 0.15) with air. 266 decitex, 48-filament polyethylene terephthalate highly oriented undrawn yarn (Δ
n is 0.03) and 83 dtex, 72 filament drawn polyethylene terephthalate filament (Δ
n was 0.15) by air entanglement to prepare a composite yarn B. A
The yarn was used for the outer material and the lining, and the B yarn was used for the middle yarn to form a cardboard knit structure to produce a greige machine.
【0050】かかる生機をテンターにて80℃で45秒
処理し、タテ、ヨコそれぞれ15%収縮させた。その後
ネットコンベアを有する熱風乾燥機内を通過させて13
0℃、60秒間熱処理した。The greige was treated with a tenter at 80 ° C. for 45 seconds, and contracted by 15% each in the vertical and horizontal directions. After that, it is passed through a hot air dryer having a net conveyor and 13
Heat treatment was performed at 0 ° C. for 60 seconds.
【0051】次いで、液流染色機内で分散染料を用いて
染色した。そのときの昇温条件は、40℃から55℃ま
で3℃/分、55℃から60℃まで0.2℃/分、60
℃から70℃まで0.15℃/分、70℃から110℃
まで1.0℃/分であり、110℃にて30分間とし染
色した。Next, dyeing was carried out using a disperse dye in a jet dyeing machine. The temperature raising conditions at this time were 3 ° C./min from 40 ° C. to 55 ° C., 0.2 ° C./min from 55 ° C. to 60 ° C., and 60 ° C.
0.15 ℃ / min from 70 ℃ to 70 ℃, 70 ℃ to 110 ℃
The dyeing was performed at 110 ° C./min for 30 minutes.
【0052】その染色シートを制電防止剤と柔軟剤を有
する液浴中に浸せきした後、マングルで絞液し130℃
で3分間乾燥した。その表面を顕微鏡で拡大して観察し
たところ、二種のポリエステル繊維の発色性が異なり、
二種のポリエステル繊維間および高配向未延伸ポリエス
テル繊維の単糸間が密着することなく間隙を有するもの
であった。After immersing the dyed sheet in a liquid bath having an antistatic agent and a softening agent, the dyed sheet was squeezed with a mangle and heated at 130 ° C.
For 3 minutes. When the surface was enlarged and observed with a microscope, the two types of polyester fibers differed in color development,
There was a gap between the two types of polyester fibers and between the single yarns of the highly oriented undrawn polyester fibers without adhesion.
【0053】かかる生地を***カップ形状を有する金型
を用いて、クリアランス1.0mm、温度180℃、6
0秒間プレスする成形加工を行った。その成形品は、高
さが56mm、幅97mmであり、10箇所を測定した
厚さは、最低厚さが0.93mm、最高厚さが1.24
mm、平均値が1.09mmであり厚さ変動は最高で1
4.7%であった。表面品位は、スムースであり、光沢
の抑えられた色相を有するものであった。また、柔軟で
ありながらしっかりとしたカップ形状を有するものであ
った。Using a mold having a breast cup shape, such a dough was prepared, with a clearance of 1.0 mm, a temperature of 180 ° C., and a temperature of 180 ° C.
A molding process of pressing for 0 seconds was performed. The molded product had a height of 56 mm and a width of 97 mm, and the thickness measured at 10 points was 0.93 mm for the minimum thickness and 1.24 for the maximum thickness.
mm, the average value is 1.09 mm and the thickness variation is 1 at the maximum.
It was 4.7%. The surface quality was smooth and had a hue with reduced gloss. Moreover, it had a firm cup shape while being flexible.
【0054】カップ状を有する成形品から2種の糸を抜
き出して、非晶配向度と見掛けヤング率を測定したとこ
ろ次のとおりであった。Two kinds of yarns were extracted from the cup-shaped molded product, and the degree of amorphous orientation and apparent Young's modulus were measured. The results were as follows.
【0055】 高配向未延伸糸部 延伸糸部 非晶配向度 0.26 0.52 見掛ヤング率(N/mm2 ) 882 4508 得られた成形加工品を***カップ状に裁断し、カップを
一枚使いとして、ストラップ、土台布、ワイヤーなど用
いてダーツのないブラジャーに縫製した(実施例1)。Highly oriented unstretched yarn portion Stretched yarn portion Amorphous orientation degree 0.26 0.52 Apparent Young's modulus (N / mm 2 ) 882 4508 The obtained molded product is cut into a breast cup shape, and the cup is cut. One piece was sewn into a dart-free bra using a strap, a base cloth, a wire, or the like (Example 1).
【0056】さらに、このカップの表面にレースを積層
して縫製した。レースを積層しても嵩張り感がなく、エ
レガントな外観を有するものであった(実施例2)。Further, a lace was laminated on the surface of the cup and sewn. Even when the laces were laminated, they did not have a bulky feeling and had an elegant appearance (Example 2).
【0057】このブラジャーを着用したところ、身体に
良くフィットし、肌触りがよく、軽くて、動きやすく、
通気性、透湿性が良好であり、スポーツをするのに極め
て快適であった。さらに、家庭用洗濯機を用いて30回
分水洗濯(水流:強、洗濯:5分間、濯ぎ:5分間、洗
剤:(株)花王ザブ)したところ、カップ形状が崩れる
ことなく洗濯前の形状がよく保持されていた。また、寸
法変化もほとんど認められなかった。When this bra was worn, it fitted well to the body, had a good touch, was light, was easy to move,
It had good breathability and moisture permeability, and was extremely comfortable to play sports. Furthermore, when the laundry was washed 30 times with a home washing machine (water flow: strong, washing: 5 minutes, rinsing: 5 minutes, detergent: Kao Zab Co., Ltd.), the shape before washing was maintained without the cup shape being collapsed. Well held. Also, almost no dimensional change was observed.
【0058】また、強制の圧縮試験(荷重:100g/
cm2 、時間:60分間)においても、徐重後変形が認
められず、カップ形状を維持していた。 比較例1、比較例2 ***カップに、発泡ポリウレタンシートの熱成形したも
の(比較例1)、繊維の一成分に熱接着性を有するいわ
ゆるサーマルボンド不織布を用いて熱成形したもの(比
較例2)を用いて、実施例1と同じ部材構成にてブラジ
ャーを縫製した。これを実施例1と同様の繰り返し洗濯
を行ったところ、比較例1は型くずれが著しく当初の形
を留めていなかった。また、通気性および透湿性が不良
であり、むれ感のあるものであった。比較例2はカップ
部が破れてカップの形状を留めていなかった。 比較例3 20ゲージの2列の針床を有するダブルラッセル編機を
用い、表地および裏地糸に138デシテックス、24フ
ィラメントポリエチレンテレフタレート延伸糸の双糸を
用い、中糸(連結糸)に165デシテックス、36フィ
ラメントポリエチレンテレフタレート延伸糸の双糸を用
いてダンボールニットを作製した。得られた編地を90
℃で5分熱水リラックスの後、180℃で30秒熱処理
し、その後、分散染料を用いて130℃で30分染色し
た。Further, a forced compression test (load: 100 g /
(cm 2 , time: 60 minutes), no deformation was observed after gradual weighting, and the cup shape was maintained. Comparative Examples 1 and 2 A breast cup was thermoformed from a foamed polyurethane sheet (Comparative Example 1), and a so-called thermal bonded nonwoven fabric having thermal adhesion to one component of a fiber (Comparative Example 2). ), A brassiere was sewn with the same member configuration as in Example 1. This was repeatedly washed in the same manner as in Example 1. As a result, in Comparative Example 1, the shape was significantly lost and the initial shape was not retained. In addition, the air permeability and the moisture permeability were poor and there was a feeling of discomfort. In Comparative Example 2, the cup portion was broken and the shape of the cup was not retained. Comparative Example 3 Using a double Russell knitting machine having two rows of needle beds of 20 gauge, using 138 decitex for the outer material and lining yarn, using twin yarn of a 24-filament polyethylene terephthalate drawn yarn, and using 165 decitex for the middle yarn (connecting yarn). A corrugated cardboard knit was prepared using a twin yarn of a 36 filament polyethylene terephthalate drawn yarn. The obtained knitted fabric is 90
After relaxing with hot water at 5 ° C. for 5 minutes, heat treatment was performed at 180 ° C. for 30 seconds, followed by dyeing with a disperse dye at 130 ° C. for 30 minutes.
【0059】この染色布を用いて実施例1と同様の成形
加工を行い、***カップ形状に成形した。この成形品
は、風合いがくたくた状であり、***カップとしての形
状を維持するものではなかった。また、色相はポリエス
テル繊維特有のテカテカとした光沢を有するものであ
り、色に深みのないものであった。表面を顕微鏡で観察
したところ、単一の発色性からなるものであった。 比較例4 実施例1の生機を用いて、テンターにて130℃で20
秒処理し、タテ、ヨコそれぞれ25%収縮させた。次い
で、液流染色機内で分散染料を用いて染色した。そのと
きの昇温条件は、40℃から55℃まで3℃/分、55
℃から60℃まで0.2℃/分、60℃から70℃まで
0.15℃/分、70℃から110℃まで1.0℃/分
であり、110℃にて30分間とし染色した。Using this dyed cloth, the same forming process as in Example 1 was performed to form a breast cup shape. This molded product had a damp texture and did not maintain the shape of a breast cup. The hue had a shiny luster peculiar to the polyester fiber, and the color had no depth. Observation of the surface with a microscope revealed that the surface consisted of a single color. Comparative Example 4 Using the greige fabric of Example 1, a tenter was used at 130 ° C. for 20 minutes.
Secondly, each was contracted by 25% vertically and horizontally. Subsequently, it was dyed with a disperse dye in a jet dyeing machine. The temperature was raised at a rate of 3 ° C./min from 40 ° C. to 55 ° C. and 55 ° C.
The dyeing was performed at 0.2 ° C / min from 60 ° C to 60 ° C, 0.15 ° C / min from 60 ° C to 70 ° C, 1.0 ° C / min from 70 ° C to 110 ° C, and 30 minutes at 110 ° C.
【0060】その染色シートを制電防止剤と柔軟剤を有
する液浴中に浸せきした後、マングルで絞液し130℃
で3分間乾燥した。得られた繊維シートは硬くまた収縮
ムラと思われるシワが全面に発生した。After immersing the dyed sheet in a liquid bath having an antistatic agent and a softening agent, the dyed sheet was squeezed with a mangle and the solution was heated at 130 ° C.
For 3 minutes. The obtained fiber sheet was hard and had wrinkles on the entire surface which seemed to be uneven shrinkage.
【0061】かかる生地を***カップ形状を有する金型
を用いて、クリアランス1.0mm、温度180℃、6
0秒間プレスする成形加工を行った。その成形品は、高
さが56mm、幅97mmであり、10箇所を測定した
厚さは、最低厚さが0.50mm、最高厚さが1.76
mm、平均値が1.11mmであり厚さ変動は最高で5
8.6%であった。比較例4は厚さ変動が高く、しかも
全面にシワが発生しておりブラジャカップに供しえるも
のではなかった。 比較例5 実施例1の生機を用いて、テンターにて100℃で20
秒処理し、タテ、ヨコそれぞれ20%収縮させた。次い
で、液流染色機内で分散染料を用いて染色した。そのと
きの昇温条件は、40℃から110℃まで3℃/分と
し、110℃にて30分間とし染色した。この染色中6
5〜75℃において染色機内で繊維シートが3度停止し
た。Using a mold having a breast cup shape, such a dough was prepared with a clearance of 1.0 mm, a temperature of 180 ° C., and a temperature of 180 ° C.
A molding process of pressing for 0 seconds was performed. The molded product had a height of 56 mm and a width of 97 mm, and the thickness measured at 10 points was 0.50 mm for the minimum thickness and 1.76 for the maximum thickness.
mm, the average value is 1.11 mm and the thickness variation is 5 at the maximum.
It was 8.6%. In Comparative Example 4, thickness variation was high, and wrinkles occurred on the entire surface, so that it could not be used for a brassiere cup. Comparative Example 5 The greige machine of Example 1 was used at 100 ° C. for 20 minutes with a tenter.
Secondly, each was shrunk by 20% in the vertical and horizontal directions. Subsequently, it was dyed with a disperse dye in a jet dyeing machine. The temperature was raised at a rate of 3 ° C./min from 40 ° C. to 110 ° C., and the dyeing was performed at 110 ° C. for 30 minutes. 6 during this dyeing
The fiber sheet stopped three times in the dyeing machine at 5-75 ° C.
【0062】その染色シートを制電防止剤と柔軟剤を有
する液浴中に浸せきした後、マングルで絞液し130℃
で3分間乾燥した。得られた繊維シートは硬くまた収縮
ムラと思われるシワが全面に発生した。After immersing the dyed sheet in a liquid bath having an antistatic agent and a softening agent, the dyed sheet was squeezed with a mangle,
For 3 minutes. The obtained fiber sheet was hard and had wrinkles on the entire surface which seemed to be uneven shrinkage.
【0063】かかる生地を***カップ形状を有する金型
を用いて、クリアランス1.0mm、温度180℃、6
0秒間プレスする成形加工を行った。その成形品は、高
さが50mm、幅93mmであり、10箇所を測定した
厚さは、最低厚さが0.65mm、最高厚さが1.55
mm、平均値が1.07mmであり厚さ変動は最高で4
6.2%であった。比較例5は厚さ変動が高く、シワが
目立ちブラジャカップに供しえる品位ではなかった。Using a mold having a breast cup shape, such a dough was prepared with a clearance of 1.0 mm, a temperature of 180 ° C., and a temperature of 180 ° C.
A molding process of pressing for 0 seconds was performed. The molded product had a height of 50 mm and a width of 93 mm, and the thickness measured at 10 points was 0.65 mm for the minimum thickness and 1.55 for the maximum thickness.
mm, the average value is 1.07 mm, and the thickness variation is 4 at the maximum.
6.2%. In Comparative Example 5, the thickness variation was high, wrinkles were noticeable, and the quality was not such that it could be used for a brassiere cup.
【0064】[0064]
【発明の効果】本発明の***カップを有する衣類は、軽
くて薄く、肌触り、通気性、透湿性が良好であり、かつ
バストのシルエットを美しく表現でき、フルカラーに染
色が可能で、繰り返し洗濯による型くずれがし難い***
カップを有する衣類を提供するものである。The garment having the breast cup of the present invention is light and thin, has good touch, good breathability, good moisture permeability, can express the bust silhouette beautifully, can be dyed in full color, and can be repeatedly washed. An object of the present invention is to provide clothing having a breast cup that is difficult to lose its shape.
【図1】本発明における***カップ部の高さ、幅の説明
をする横断面図である。FIG. 1 is a cross-sectional view for explaining the height and width of a breast cup portion according to the present invention.
【図2】本発明における***カップを有するブラジャー
の例を示す概略図である。FIG. 2 is a schematic view showing an example of a brassiere having a breast cup according to the present invention.
【図3】本発明における***カップを有するレース付き
ブラジャーの例を示す概略図である。FIG. 3 is a schematic view showing an example of a brassier with a lace having a breast cup according to the present invention.
【図4】本発明における***カップを有するボディスー
ツの例を示す概略図である。FIG. 4 is a schematic view showing an example of a body suit having a breast cup according to the present invention.
【図5】本発明における***カップを有するビスチェの
例を示す概略図である。FIG. 5 is a schematic view showing an example of a bustier having a breast cup according to the present invention.
【図6】本発明における***カップを有するスリーイン
ワンの例を示す概略図である。FIG. 6 is a schematic view showing an example of a three-in-one having a breast cup according to the present invention.
【図7】本発明における***カップを有するブラキャミ
ソールの例を示す概略図である。FIG. 7 is a schematic view showing an example of a bra camisole having a breast cup according to the present invention.
【図8】本発明における***カップを有するブラスリッ
プの例を示す概略図である。FIG. 8 is a schematic diagram showing an example of a brush slip having a breast cup according to the present invention.
【図9】本発明における***カップを有するロングライ
ンブラジャーの例を示す概略図である。FIG. 9 is a schematic view showing an example of a long line brassiere having a breast cup according to the present invention.
【図10】本発明における***カップを有する水着の例
を示す概略図である。FIG. 10 is a schematic view showing an example of a swimsuit having a breast cup according to the present invention.
1:***カップ 2:土台布 3:肩紐 4:ワイヤー 5.レース 1: Breast cup 2: Base cloth 3: Shoulder strap 4: Wire 5 race
フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) A41C 3/08 A41C 3/08 A41D 7/00 A41D 7/00 G Fターム(参考) 3B154 AA07 AB20 AB21 AB22 AB31 BA07 BA39 BB12 BE02 BF01 BF07 BF14 BF18 BF21 BF23 DA09 DA10 DA13 DA18 4L035 EE08 EE20 Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat II (reference) A41C 3/08 A41C 3/08 A41D 7/00 A41D 7/00 GF term (reference) 3B154 AA07 AB20 AB21 AB22 AB31 BA07 BA39 BB12 BE02 BF01 BF07 BF14 BF18 BF21 BF23 DA09 DA10 DA13 DA18 4L035 EE08 EE20
Claims (12)
する衣料において、***カップが少なくとも非晶配向度
が0.35以下、見掛ヤング率が1960N/mm2 以
下であるポリエステル繊維を用いてなり、高さが40m
m以上、幅が80mm以上であり、厚さが0.5〜2.
0mmであって、その厚さ変動が30%以下であること
を特徴とする衣類。In a garment having a single-use breast cup without darts, the breast cup is made of a polyester fiber having a degree of amorphous orientation of at most 0.35 and an apparent Young's modulus of at most 1960 N / mm 2. And height is 40m
m or more, a width of 80 mm or more, and a thickness of 0.5 to 2.
Clothing having a thickness of 0 mm and a thickness variation of 30% or less.
する衣料において、***カップが少なくとも非晶配向度
が0.35以下、見掛ヤング率が1960N/mm2 以
下であるポリエステル繊維と、非晶配向度が0.45以
上、見掛ヤング率が2940N/mm2 以上であるポリ
エステル繊維を用いてなり、高さが40mm以上、幅が
80mm以上であり、厚さが0.5〜2.0mmであっ
て、その厚さ変動が30%以下であることを特徴とする
衣類。2. A garment having a single-use breast cup without darts, wherein the breast cup has at least an amorphous orientation degree of 0.35 or less and an apparent Young's modulus of 1960 N / mm 2 or less. A polyester fiber having a degree of crystal orientation of 0.45 or more, an apparent Young's modulus of 2940 N / mm 2 or more, a height of 40 mm or more, a width of 80 mm or more, and a thickness of 0.5 to 2. Clothing having a thickness of 0 mm and a thickness variation of 30% or less.
リエステル繊維の単糸太さが2デシテックス以下である
ことを特徴とする請求項1または2記載の衣類。3. The garment according to claim 1, wherein in the breast cup, the single yarn thickness of at least one kind of polyester fiber is 2 dtex or less.
リエステル繊維がポリエチレンテレフタレート繊維であ
ることを特徴とする請求項1〜3のいずれかに記載の衣
類。4. The garment according to claim 1, wherein at least one kind of polyester fiber in the breast cup is polyethylene terephthalate fiber.
度0.35以下で見掛ヤング率が1960N/mm2 以
下のポリエステル繊維と、非晶配向度0.45以上で見
掛ヤング率が2940N/mm2 以上のポリエステル繊
維の両方がブラジャーカップの表面に露出していること
を特徴とする請求項1〜3のいずれかに記載の衣類。5. A breast cup having at least an amorphous orientation degree of 0.35 or less and an apparent Young's modulus of 1960 N / mm 2 or less, and an amorphous orientation degree of 0.45 or more and an apparent Young's modulus of 2940 N / mm 2. The clothing according to any one of claims 1 to 3, wherein both of the polyester fibers having a size of 2 mm2 or more are exposed on the surface of the brassiere cup.
を特徴とする請求項1〜5のいずれかに記載の衣類。6. The garment according to claim 1, wherein the breast cup is dyed with a disperse dye.
が異なる2種以上のポリエステル繊維からなることを特
徴とする請求項1〜5のいずれかに記載の衣類。7. The garment according to claim 1, wherein the breast cup is made of two or more polyester fibers dyed with a disperse dye and having different coloring properties.
ントであることを特徴とする請求項1〜5のいずれかに
記載の衣類。8. The garment according to claim 1, wherein the breast cup is a polyester fiber filament.
から構成されていることを特徴とする請求項1〜5のい
ずれかに記載の衣類。9. The garment according to claim 1, wherein the breast cup is made of a woven fabric, a knitted fabric, or a nonwoven fabric.
が、ブラジャー、ボディスーツ、ビスチェ、ブラテデ
ィ、スリーインワン、ブラキャミソール、ブラスリッ
プ、ロングラインブラジャー、および水着から選ばれた
ものであることを特徴とする衣類。10. The garment according to any one of claims 1 to 9, wherein the garment is selected from a bra, a bodysuit, a bustier, a teddy, a three-in-one, a bra camisole, a bra slip, a long line bra, and a swimsuit. Clothing characterized by that.
ポリエチレンテレフタレート繊維を有するシートを、6
0〜90℃の乾式および/または湿式雰囲気下で、タ
テ、ヨコ方向とも、2%/秒以下の収縮速度で10〜2
5%収縮させた後、少なくとも染色液温55℃〜70℃
において、0.5℃/分以下の速度で昇温し染色するこ
とを特徴とする繊維シートの製造方法。11. birefringence Δn is a sheet having a polyethylene terephthalate fiber of 0.02 to 0.08 3, 6
In a dry and / or wet atmosphere at 0 to 90 ° C, a shrinkage rate of 2% / sec or less in both the vertical and horizontal directions is 10 to 2
After shrinking by 5%, at least the dyeing solution temperature is 55 ° C to 70 ° C.
The method for producing a fiber sheet according to any one of claims 1 to 3, wherein the temperature is raised at a rate of 0.5 ° C / min or less and dyed.
ポリエチレンテレフタレート繊維を有するシートを、6
0〜90℃の乾式および/または湿式雰囲気下で、タ
テ、ヨコ方向とも、2%/秒以下の収縮速度で10〜2
5%収縮させた後、少なくとも室温〜50℃において
0.3℃/分以上の速度で昇温し、55℃〜70℃にお
いて0.5℃/分以下の速度で昇温し、および75〜1
20℃において0.3℃/分以上の速度で昇温すること
を特徴とする繊維シートの製造方法。12. birefringence Δn is a sheet having a polyethylene terephthalate fiber of 0.02 to 0.08 3, 6
In a dry and / or wet atmosphere at 0 to 90 ° C, a shrinkage rate of 2% / sec or less in both the vertical and horizontal directions is 10 to 2
After shrinking by 5%, the temperature is increased at a rate of at least 0.3 ° C./min from room temperature to 50 ° C., and at a rate of 0.5 ° C./min or less at 55 ° C. to 70 ° C .; 1
A method for producing a fiber sheet, wherein the temperature is increased at a rate of 0.3 ° C./min or more at 20 ° C.