JP2001206450A - Cushioning material for packing article - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a cushioning material for packing an article wherein a problem that a required occupied area is large when placing a stage on the cushioning material is solved, an occupied volume when packing the article is reduced, an occupied volume required by the stage which is placed when packing the article can be reduced, and the cushioning material is excellent in cushioning performance and workability in packing and has a small bulk. SOLUTION: The cushioning material 1a for packing an article is integrally molded by fabricating a thermoplastic resin sheet into an uneven structure. A part of the cushioning material 1a is formed with a cushioning wall 34 which is protruding or recessed with respect to a reference plane which is approximately vertical to a bottom face, a side face or a ceiling face of the article.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、家電機器やＯＡ機
器など、精密製品その他の破損し易い物品を梱包する際
に用いて好ましい物品梱包用緩衝材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an article packing cushioning material which is preferably used for packing precision products and other easily breakable articles such as home appliances and office automation equipment.

【０００２】[0002]

【従来の技術】ファクシミリ装置、ノート型パーソナル
コンピュータ、小型液晶テレビジョン装置などの各種精
密製品は、輸送時などに落下や衝突などの衝撃を受ける
ことが少なくない。このため、緩衝材を用いて梱包され
るのが一般的である。2. Description of the Related Art Various precision products, such as facsimile machines, notebook personal computers, and small liquid crystal televisions, are often subjected to impacts such as dropping or collision during transportation. For this reason, it is common to pack using a cushioning material.

【０００３】従来の物品梱包用緩衝材としては、発泡ポ
リスチレン成形体や段ボールシートが知られており、発
泡ポリスチレン成形体で製品を挟み込んだり、段ボール
シートを切り出した緩衝材を製品と梱包箱との間に挿入
することが行われている。[0003] As a conventional cushioning material for packing goods, a foamed polystyrene molded article or a corrugated cardboard sheet is known. A cushioning material obtained by sandwiching a product with a foamed polystyrene molded article or cutting a corrugated cardboard sheet is used as a cushion between a product and a packing box. Inserting in between has been done.

【０００４】しかしながら、発泡ポリスチレン成形体
は、嵩容積が大きくなり積み重ねることも困難であるた
め、緩衝材自体の物流コストが高くなり、また使用後の
廃棄物処理にも嵩が大きいために経済上の問題がある。
また、段ボールシートからなる緩衝材は、段ボールシー
トを切り出す作業や切り出した段ボールシートを立体的
に組み立てる必要があり、製造および梱包作業が煩雑で
あるという問題がある。[0004] However, foamed polystyrene molded articles have a large bulk volume and are difficult to stack, so that the distribution cost of the cushioning material itself is high, and the bulk of the waste material after use is large, so that it is economical. There is a problem.
Further, the cushioning material made of a corrugated cardboard sheet has a problem in that it is necessary to cut the corrugated cardboard sheet and to assemble the cut corrugated cardboard sheet three-dimensionally, which makes the manufacturing and packing work complicated.

【０００５】上記問題を解決するものとして特願平１０
−３０８３１５号では、電機製品や精密機器を保護・包
装する物品梱包用緩衝材として、凸凹部が形成されたシ
ート面が物品と当接し、前記凸凹部の底面が衝撃対象に
対面するように形成され、前記凸凹部の側壁に底面に向
かって縮径する２段以上５段以下の段部が形成されたシ
ート状熱可塑性樹脂成形体が提案されている。As a solution to the above problem, Japanese Patent Application No.
Japanese Patent No. 308315 discloses a cushioning material for articles that protects and packs electrical products and precision equipment, so that the sheet surface on which the projections and depressions are in contact with the article, and the bottom surface of the projections and depressions faces the impact target. There has been proposed a sheet-like thermoplastic resin molded article in which two or more and five or less steps are formed on the side walls of the projections and depressions to reduce the diameter toward the bottom.

【０００６】これらのシート状熱可塑性樹脂成形体の凸
凹状の段部は、梱包されるべき物品の面に対する形で敷
設しており、凸凹部の側壁に底面に向かって縮径するの
を利用して物品を緩衝・保護するものである。しかしな
がら、この段部はその緩衝・保護作用が優れるものの、
段部を敷設する際に必要な占有容積が大きいという問題
がある。The uneven steps of these sheet-like thermoplastic resin moldings are laid in the form of the surface of the article to be packed, and the diameter of the step is reduced toward the bottom of the side wall of the unevenness. To protect and cushion the goods. However, although this step has excellent buffering and protection effects,
There is a problem that the occupied volume required when laying the step portion is large.

【０００７】なお、精密製品を梱包する場合には、７０
ｃｍの高さから、好ましくは９２ｃｍの高さから落下さ
せたときに、梱包されている製品に加わる最大重力加速
度が、たとえば７０Ｇ以下、好ましくは６０Ｇ以下にな
ることが望ましいとされる。[0007] When packing precision products, 70
It is desirable that the maximum gravitational acceleration applied to the packed product when dropped from a height of cm, preferably 92 cm is, for example, 70 G or less, preferably 60 G or less.

【０００８】[0008]

【発明が解決しようとする課題】本発明は、物品梱包用
緩衝材に段部を敷設する際に、必要な占有容積が大きい
という問題を解決し、物品を梱包する際の占有容積を減
らし、物品を梱包する際に敷設する段部が要する占有容
積を減らすことができ、しかも緩衝性能および梱包作業
性に優れ、嵩容積も小さい物品梱包用緩衝材を提供する
ことを目的とする。SUMMARY OF THE INVENTION The present invention solves the problem that the required occupation volume is large when laying a step on the cushioning material for packing articles, and reduces the occupation volume when packing articles. An object of the present invention is to provide an article packing cushioning material which can reduce an occupied volume required by a step portion to be laid when packing articles, is excellent in cushioning performance and packing workability, and has a small bulk volume.

【０００９】[0009]

【課題を解決するための手段】上記目的を達成するため
に、本発明に係る物品梱包用緩衝材は、熱可塑性樹脂シ
ートを凸凹状に加工することにより一体的に成形される
物品梱包用緩衝材であって、前記物品梱包用緩衝材の一
部には、物品の底面、側面または天井面に略垂直な基準
面に対して、凸または凹となる緩衝用壁部が形成してあ
ることを特徴とする。In order to achieve the above object, an article packing cushioning material according to the present invention is provided with an article packing cushion formed integrally by processing a thermoplastic resin sheet into an uneven shape. A part of the article packaging cushioning material, wherein a cushioning wall portion that is convex or concave with respect to a reference plane substantially perpendicular to the bottom face, side face, or ceiling face of the article is formed. It is characterized by.

【００１０】本発明に係る物品包装用緩衝材は、梱包箱
内に梱包されるべき物品の底面と梱包箱の内底面との間
に介在されて緩衝作用を行う底面緩衝部と、前記物品の
底面に略垂直な側面と梱包箱の内側面との間に介在され
て緩衝作用を行う側面緩衝部と、前記物品の天井面の上
に位置し、物品の天井面の緩衝作用を行う天井面緩衝部
とを有し、前記底面緩衝部、側面緩衝部および天井面緩
衝部が、熱可塑性樹脂シートを凸凹状に加工することに
より一体的に成形される物品梱包用緩衝材であって、前
記底面緩衝部、側面緩衝部および天井面緩衝部のいずれ
かには、物品の底面、側面または天井面に略垂直な基準
面に対して、断面が凸または凹となる緩衝用壁部が形成
してあることが好ましい。[0010] The cushioning material for article packaging according to the present invention comprises a bottom cushioning portion interposed between the bottom surface of the article to be packed in the packing box and the inner bottom face of the packing box to perform a buffering action; A side cushioning portion interposed between a side surface substantially perpendicular to the bottom surface and an inner side surface of the packing box to perform a buffering action; and a ceiling surface located on the ceiling face of the article and cushioning the ceiling face of the article. A cushioning material for packaging goods, wherein the bottom cushioning portion, the side cushioning portion, and the ceiling cushioning portion are integrally formed by processing a thermoplastic resin sheet into an uneven shape. In any of the bottom buffer, the side buffer, and the ceiling buffer, a buffer wall having a cross section that is convex or concave with respect to a reference plane substantially perpendicular to the bottom, side, or ceiling of the article is formed. Preferably.

【００１１】前記緩衝用壁部の断面凹凸形状は、特に限
定されず、三角形状、台形形状、半円形状などが例示さ
れる。The cross section of the cushioning wall is not particularly limited, and examples thereof include a triangular shape, a trapezoidal shape, and a semicircular shape.

【００１２】前記緩衝用壁部の断面形状が、三角形状の
場合には、三角形状の頂角（θ）は、好ましくは３０〜
１５０度、さらに好ましくは６０〜１２０度である。When the sectional shape of the buffer wall is triangular, the apex angle (θ) of the triangular shape is preferably 30 to
It is 150 degrees, more preferably 60 to 120 degrees.

【００１３】前記緩衝用壁部の断面形状が、台形形状で
ある場合には、台形形状の底辺に相当する辺の長さ（Ｗ
２）に対する頂上部の辺の長さ（Ｗ１）の比（Ｗ１／Ｗ
２）は、好ましくは０．１〜０．９、さらに好ましくは
０．３〜０．７である。When the cross-sectional shape of the buffer wall is trapezoidal, the length of the side corresponding to the base of the trapezoidal shape (W
The ratio (W1 / W) of the length (W1) of the side of the top portion to 2)
2) is preferably 0.1 to 0.9, more preferably 0.3 to 0.7.

【００１４】前記緩衝用壁部に隣接する緩衝材の外周壁
には、たとえば３〜１５度、好ましくは６度前後の抜き
テーパー角を付けてあることが望ましい。It is desirable that the outer peripheral wall of the cushioning material adjacent to the buffering wall has a taper angle of, for example, 3 to 15 degrees, preferably about 6 degrees.

【００１５】前記底面緩衝部と側面緩衝部とは、一体的
に形成してあっても良いが、これらの間にヒンジ部を一
体的に具備させ、これらを回動自在に連結しても良い。
また、側面緩衝部と天井面緩衝部との関係も同様であ
る。The bottom cushioning portion and the side cushioning portion may be formed integrally, but a hinge portion may be integrally provided between them, and these may be rotatably connected. .
Further, the same applies to the relationship between the side cushioning part and the ceiling cushioning part.

【００１６】[0016]

【作用】本発明によれば、段ボール外箱などの梱包箱内
に、本発明に係る緩衝材と共に物品を収納することで、
輸送時などの落下や衝突などの衝撃から物品を有効に保
護することができる。また、物品を梱包する際の占有容
積を減らすことで物品梱包材を収納する梱包箱の大きさ
も極力少なくすることができ、結果として保管時のスペ
ースを有効に活用することが可能となる。According to the present invention, articles are stored together with the cushioning material according to the present invention in a packing box such as a cardboard outer box.
Articles can be effectively protected from impacts such as dropping or collision during transportation. Further, by reducing the occupied volume when packing the articles, the size of the packing box for storing the article packing material can be reduced as much as possible, and as a result, the space at the time of storage can be effectively utilized.

【００１７】さらにまた、本発明に係る物品梱包用緩衝
材は、製造が容易であることに加えて、物品梱包作業が
極めて容易である。Further, the article packing cushioning material according to the present invention is very easy to manufacture and extremely easy to pack.

【００１８】本発明に係る物品梱包用緩衝材は、たとえ
ば、ファクシミリ装置、ノート型パーソナルコンピュー
タ、小型液晶テレビジョン装置などの各種精密製品の梱
包に好適に用いることができる。The cushioning material for packing articles according to the present invention can be suitably used for packing various precision products such as facsimile machines, notebook personal computers, and small liquid crystal televisions.

【００１９】[0019]

【発明の実施の形態】以下、本発明を、図面に示す実施
形態に基づき説明する。図１は本発明の第１実施形態に
係る物品梱包用緩衝材の使用前の状態を示す斜視図、図
２（Ａ）および（Ｂ）は図１に示すIIA−IIA線およびII
B−IIB線に沿う要部断面図、図２（Ｃ）は図２（Ａ）に
示す緩衝用壁部の要部拡大断面図、図３は図１に示す物
品梱包用緩衝材に物品を載せた状態を示す斜視図、図４
は段ボール外箱の内部に物品及び図１に示す物品梱包用
緩衝材を収納した状態を透視斜視図、図５は本発明の第
２実施形態に係る物品梱包用緩衝材の使用状態を示す斜
視図、図６は本発明の第３実施形態に係る物品梱包用緩
衝材の使用状態を示す斜視図、図７は図６に示す物品梱
包用緩衝材を物品と共に段ボール外箱の内部に収納した
状態を透視側面図、図８は本発明の第４実施形態に係る
物品梱包用緩衝材の使用状態を示す斜視図である。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below based on embodiments shown in the drawings. FIG. 1 is a perspective view showing a state before use of a cushioning material for packaging articles according to a first embodiment of the present invention, and FIGS. 2A and 2B are lines IIA-IIA and II shown in FIG.
FIG. 2 (C) is an enlarged cross-sectional view of a main part of the cushioning wall part shown in FIG. 2 (A), and FIG. 3 is a cross-sectional view of the main part along the line B-IIB. FIG. 4 is a perspective view showing a mounted state,
Is a perspective view showing a state in which the article and the cushioning material for article packing shown in FIG. 1 are housed inside a cardboard outer box, and FIG. 5 is a perspective view showing a use state of the cushioning material for article packing according to the second embodiment of the present invention. FIG. 6 and FIG. 6 are perspective views showing a use state of the article packing cushioning material according to the third embodiment of the present invention. FIG. 7 shows the article packing cushioning article shown in FIG. FIG. 8 is a perspective side view showing a state of use of the cushioning material for packing articles according to the fourth embodiment of the present invention.

【００２０】第１実施形態 図１に示す本実施形態に係る物品梱包用緩衝材１ａは、
図３に示すように、緩衝材１ａに対して物品Ａを挟んで
左右対称な形状となる物品梱包用緩衝材１ｂと共に用い
られる。物品Ａとしては、特に限定されないが、たとえ
ば、直方体形状のＤＶＤ装置などを例示することができ
る。物品梱包用緩衝材１ｂは、物品梱包用緩衝材１ａと
同一な構成を有するので、以下の説明では、一方のみを
説明する。なお、本発明では、緩衝材１ａと１ｂとは、
一体に成形しても良い。 First Embodiment A cushioning material 1a for packing goods according to this embodiment shown in FIG.
As shown in FIG. 3, it is used together with an article packing cushioning material 1b that is symmetrical with respect to the cushioning material 1a with respect to the article A. The article A is not particularly limited, but may be, for example, a rectangular parallelepiped DVD device. The article packaging cushioning material 1b has the same configuration as the article packaging cushioning material 1a, so only one of them will be described in the following description. In the present invention, the cushioning materials 1a and 1b are
It may be formed integrally.

【００２１】梱包材１ａは、物品Ａの片側端部（たとえ
ば、右側端部）を包装・保護するための緩衝材であっ
て、物品Ａの底面を抱囲する底面緩衝部２と、この底面
緩衝部２のＹ方向片側に位置し、物品ＡのＹ方向右側端
部を抱囲する側面緩衝部３とを有する。本実施形態で
は、側面緩衝部３の上部に、天井面緩衝部３ａが一体的
に形成してある。The packing material 1a is a cushioning material for wrapping and protecting one end (for example, the right end) of the article A, and includes a bottom cushioning part 2 surrounding the bottom of the article A, and a bottom surface. A side cushioning portion 3 which is located on one side of the cushioning portion 2 in the Y direction and surrounds the right end of the article A in the Y direction In the present embodiment, a ceiling buffer 3a is integrally formed on the upper part of the side buffer 3.

【００２２】底面緩衝部２および側面緩衝部３は、ヒン
ジ部４により相互に回動自在に設けられている。ヒンジ
部４は底面緩衝部２と側面緩衝部３とを一体成形する際
に、たとえば、線状の薄肉部を成形することで形成する
ことができる。The bottom buffer 2 and the side buffer 3 are rotatably provided to each other by a hinge 4. The hinge portion 4 can be formed by, for example, forming a linear thin portion when the bottom buffer portion 2 and the side buffer portion 3 are integrally formed.

【００２３】底面緩衝部２のＹ方向片側には、後述する
支持部２１ａ、２１ｂに対して４５度の角度で傾斜する
第１傾斜面２２が一体成形してあり、底面緩衝部２のＸ
方向両側には、物品ＡのＸ方向両面を一部抱囲する折り
返し形状の補強リブ（補強用スカート）２３ａ、２３ｂ
が一体成形してある。これらの補強リブ２３ａ、２３ｂ
の外周には、段差２３１ａ、２３１ｂを設け、補強リブ
２３ａ、２３ｂの剛性をさらに向上させることとしても
よい。On one side of the bottom cushioning portion 2 in the Y direction, a first inclined surface 22 inclined at an angle of 45 degrees with respect to support portions 21a and 21b described later is integrally formed.
On both sides in the direction, folded-back reinforcing ribs (reinforcing skirts) 23a, 23b partially enclosing both sides in the X direction of the article A
Is integrally molded. These reinforcing ribs 23a, 23b
Steps 231a, 231b may be provided on the outer circumference of the, and the rigidity of the reinforcing ribs 23a, 23b may be further improved.

【００２４】側面緩衝部３には、第１傾斜面２２に対し
てヒンジ部４を挟んで反対側に、第２傾斜面３１が一体
に成形してある。第２傾斜面３１は、側面緩衝部３を回
動しない状態で、底面緩衝部２の支持部２１ａ、２１ｂ
に対して４５度の角度で傾斜してある。その結果、側面
緩衝部３がヒンジ部４を回動中心として底面緩衝部２に
対して９０度回動した状態で、物品ＡのＹ方向右側端部
を抱囲しつつ、第１傾斜面２２と第２傾斜面３１とが接
触するようになっている。A second inclined surface 31 is formed integrally with the side cushioning portion 3 on the opposite side of the first inclined surface 22 with the hinge portion 4 interposed therebetween. The second inclined surface 31 is supported by the support portions 21a and 21b of the bottom buffer portion 2 in a state where the side buffer portion 3 is not rotated.
At an angle of 45 degrees. As a result, in a state where the side cushioning part 3 is rotated 90 degrees with respect to the bottom cushioning part 2 about the hinge part 4 as the center of rotation, the first inclined surface 22 is surrounded while surrounding the right end in the Y direction of the article A. And the second inclined surface 31 are in contact with each other.

【００２５】第１傾斜面２２には、嵌合凹部（図示省
略）が一体成形してあり、第２傾斜面３１には、前記嵌
合凹部に対して着脱自在に嵌合自在の嵌合凸部（図示省
略）が一体成形してある。これらの嵌合凹部と嵌合凸部
とは、底面緩衝部２および側面緩衝部３のいずれか一方
が、いずれか他方に対してヒンジ部４を回動中心として
約９０度回動した状態で着脱自在に嵌合するようになっ
ている。嵌合用凸部と凹部の嵌合の結果、物品梱包用緩
衝材１ａは、図１の状態を維持する。物品梱包用緩衝材
１ａを、シートの真空成形などにより成形した直後の形
状は、図１の状態ではなく、図１に示すＲ方向に側面緩
衝部３を底面緩衝部２に対して回動して開いた状態であ
る。A fitting recess (not shown) is integrally formed on the first inclined surface 22, and a fitting protrusion removably engageable with the fitting recess is formed on the second inclined surface 31. The part (not shown) is integrally formed. The fitting concave portion and the fitting convex portion are in a state where one of the bottom buffer portion 2 and the side buffer portion 3 is rotated by about 90 degrees about the hinge portion 4 with respect to the other. It is adapted to be detachably fitted. As a result of the fitting of the fitting projection and the recess, the article packing cushioning material 1a maintains the state of FIG. Immediately after the article packing cushioning material 1a is formed by vacuum forming of a sheet, the shape of the side cushioning part 3 is rotated with respect to the bottom cushioning part 2 in the R direction shown in FIG. And open.

【００２６】側面緩衝部３の周囲３方には、補強用リブ
２３ａ、２３ｂと同様な断面構造（図２（Ｂ）参照）を
有する補強リブ（補強用スカート）３２が一体成形して
ある。この補強リブ３２の内壁面近傍に形成される窪み
３３は、側面緩衝部３がヒンジ部４を回動中心として底
面緩衝部２に対して約９０度回動した状態で、図２
（Ａ）に示すように、物品ＡのＹ方向右側端部の上部角
部を抱囲する。補強リブ３２の内、物品Ａの上部に位置
する部分が、天井面緩衝部３ａとなる。なお、補強リブ
３２の外周には、段差３２１を設け、補強リブ３２の剛
性をさらに向上させることとしてもよい。Reinforcing ribs (reinforcing skirts) 32 having the same cross-sectional structure (see FIG. 2B) as the reinforcing ribs 23a and 23b are integrally formed on three sides around the side cushioning portion 3. The depression 33 formed in the vicinity of the inner wall surface of the reinforcing rib 32 is in a state where the side cushioning part 3 is rotated about 90 degrees with respect to the bottom cushioning part 2 about the hinge part 4 as a center of rotation.
As shown in (A), the upper corner of the right end of the article A in the Y direction is enclosed. A portion of the reinforcing rib 32 located above the article A serves as a ceiling cushioning portion 3a. Note that a step 321 may be provided on the outer circumference of the reinforcing rib 32 to further improve the rigidity of the reinforcing rib 32.

【００２７】底面緩衝部２には、第１緩衝用凹部２３２
ａ、２３２ｂが一体成形してあってもよく、側面緩衝部
３には、第２緩衝用凹部３２２ａ、３２２ｂが一体成形
してあってもよい。The bottom buffer 2 has a first buffer recess 232.
a and 232b may be integrally formed, and the side buffer portion 3 may be integrally formed with second buffer recesses 322a and 322b.

【００２８】図２（Ｂ）に示すように、支持部２１ａ、
２１ｂおよび緩衝用凹部２３２ａ、２３２ｂのそれぞれ
周壁には、６度前後の抜き角α（テーパー面）を形成し
てある。As shown in FIG. 2B, the support portions 21a,
A draft angle α (taper surface) of about 6 degrees is formed on each peripheral wall of the recess 21b and the buffer recesses 232a and 232b.

【００２９】こうした底面緩衝部２、側面緩衝部３およ
び天井面緩衝部３ａは、特に限定されないが、ポリプロ
ピレン、ポリエチレン、ポリ塩化ビニル、ポリエチレン
テレフタレート、ＡＢＳ、ポリスチレンその他の熱可塑
性樹脂またはそれらの混合物もしくは各単体シートの積
層体で構成することができる。その成形方法は、特に限
定されないが、真空成形、真空圧空成形、射出成形、プ
レス成形などを例示することができる。The bottom buffer 2, side buffer 3, and ceiling buffer 3a are not particularly limited, but may be polypropylene, polyethylene, polyvinyl chloride, polyethylene terephthalate, ABS, polystyrene, other thermoplastic resins, or a mixture thereof. It can be composed of a laminate of each single sheet. The molding method is not particularly limited, and examples thereof include vacuum molding, vacuum pressure molding, injection molding, and press molding.

【００３０】なお、熱可塑性樹脂には、自己崩壊する合
成樹脂が混合されてもよい。自己崩壊する合成樹脂とし
ては、酢酸セルロース系、ポリカプロラクトン系、ポリ
乳酸系、低級脂肪酸の単独重合体または２種以上低級脂
肪酸の共重合体、でんぷんを５〜５０重量％分散混合し
た合成樹脂などが例示されるが、これらの樹脂の２種以
上の混合物であってもよい。あるいはこれらの自己崩壊
する合成樹脂と他の合成樹脂の混合物であってもよい。The thermoplastic resin may be mixed with a self-disintegrating synthetic resin. Examples of self-disintegrating synthetic resins include cellulose acetates, polycaprolactones, polylactic acids, homopolymers of lower fatty acids or copolymers of two or more lower fatty acids, and synthetic resins in which starch is dispersed and mixed in an amount of 5 to 50% by weight. However, a mixture of two or more of these resins may be used. Alternatively, a mixture of these self-disintegrating synthetic resins and other synthetic resins may be used.

【００３１】こうした単層シートまたは各単層シートの
厚みは、０．３〜３．０ｍｍが好ましく、０．５〜１．
５ｍｍが更に好ましい。厚みが０．３ｍｍより薄いと剛
性が不足する傾向があり、３．０ｍｍを超えると成形時
の賦形性が劣る傾向があり、かつ、成形に要する時間が
長くなって経済的に好ましくない。The single-layer sheet or each single-layer sheet preferably has a thickness of 0.3 to 3.0 mm, more preferably 0.5 to 1.0 mm.
5 mm is more preferred. If the thickness is less than 0.3 mm, the rigidity tends to be insufficient, and if it exceeds 3.0 mm, the shapeability at the time of molding tends to be inferior, and the time required for molding is long, which is economically undesirable.

【００３２】本実施形態では、側面緩衝部３は、通常状
態では、物品Ａのいずれの面にも当接しないように凹凸
状に成形してあるが、部分的な面あるいは全面で当接し
てもよい。底面緩衝部２の補強リブ２３ａ、２３ｂの内
側にそれぞれ、段差状の支持部２１ａ、２１ｂが形成し
てある。支持部２１ａ、２１ｂが物品Ａと当接している
部分である。これらの支持部２１ａ、２１ｂの形成位置
は、特に限定されないが、物品Ａを抱囲する範囲に広く
分散させて形成することが好ましい。In the present embodiment, the side cushioning portion 3 is formed in an uneven shape so as not to abut on any surface of the article A in a normal state. Is also good. Stepped support portions 21a and 21b are formed inside the reinforcing ribs 23a and 23b of the bottom buffer portion 2, respectively. The support portions 21a and 21b are portions in contact with the article A. The positions at which the support portions 21a and 21b are formed are not particularly limited.

【００３３】本発明における支持部２１ａ、２１ｂの横
断面形状は、特に限定されず、たとえば、円形状、楕円
形状、三角形以上の多角形状、もしくはこの組み合わ
せ、または、物品の辺に沿った稜線形状などの各種の形
状を例示することができるが、本実施形態では、支持部
２１ａの横断面形状は、正方形に円弧状が付加した形状
であり、支持部２１ｂは長方形状としてある。The cross-sectional shape of the support portions 21a and 21b in the present invention is not particularly limited. For example, a circular shape, an elliptical shape, a polygonal shape having more than a triangle, or a combination thereof, or a ridge shape along the side of the article In this embodiment, the cross-sectional shape of the support portion 21a is a shape obtained by adding an arc shape to a square, and the support portion 21b is a rectangular shape.

【００３４】本実施形態では、図２（Ａ）に示すよう
に、凸状構造体である天井面緩衝部３ａの凸部頂上に
は、物体Ａの天井面に略垂直な基準面Ａ１に対して凸ま
たは凹となる緩衝用壁部３４が、図１に示すＸ方向に沿
って連続的または断続的に形成してある。本実施形態で
は、この緩衝用壁部３４は、断面が三角形状の山稜構造
となっており、この山稜構造の頂上部の角度θ（図２
（Ｃ）参照）は、３０度以上１５０度以下が好ましく、
６０以上１２０度以下が更に好ましい。角度θが３０度
以下であると、壁部３４の可撓性が高く成りすぎ緩衝性
が劣り、結果として落下時に７０Ｇを超える衝撃が物品
Ａに大きく伝わって、物品Ａが破損しやすくなる。一
方、角度θが１５０度を超えると、逆に可撓性が不足す
る傾向にあり、緩衝性が劣り、落下時に７０Ｇを超える
衝撃が物品Ａに大きく伝わる傾向となる。In this embodiment, as shown in FIG. 2 (A), the top of the convex portion of the ceiling surface buffering portion 3a, which is a convex structure, is placed on a reference surface A1 substantially perpendicular to the ceiling surface of the object A. A convex or concave buffer wall 34 is formed continuously or intermittently along the X direction shown in FIG. In the present embodiment, the cushioning wall portion 34 has a mountain ridge structure having a triangular cross section, and the angle θ at the top of the mountain ridge structure (see FIG. 2).
(C) is preferably 30 degrees or more and 150 degrees or less,
The angle is more preferably from 60 to 120 degrees. If the angle θ is 30 degrees or less, the flexibility of the wall portion 34 becomes too high and the cushioning property is inferior, and as a result, an impact exceeding 70 G is greatly transmitted to the article A when dropped, and the article A is easily damaged. On the other hand, if the angle θ exceeds 150 degrees, on the other hand, the flexibility tends to be insufficient, the buffering property is poor, and an impact exceeding 70 G tends to be transmitted to the article A when dropped.

【００３５】本実施形態では、角度θは約９０度となる
ように形成されている。この緩衝用壁部３４の凸形状
は、必ずしも三角形状である必要はなく、台形形状、半
円形状でも良い。また、この緩衝用壁部３４は、基準面
Ａ１に対して、断面が凸である必要は必ずしもなく、凹
溝であっても良い。凹溝の形状も、特に限定されない。In the present embodiment, the angle θ is formed to be about 90 degrees. The convex shape of the buffer wall 34 does not necessarily need to be triangular, but may be trapezoidal or semicircular. Further, the buffer wall 34 does not necessarily have to have a convex cross section with respect to the reference plane A1, but may be a concave groove. The shape of the groove is not particularly limited.

【００３６】緩衝用壁部の凸または凹形状が台形形状の
場合には、図２（Ｃ）に示すように、台形形状の底辺に
相当する辺の長さＷ２に対する頂上部の辺の長さＷ１の
比（Ｗ１／Ｗ２）が、０．１以上０．９以下になるよう
に形成してあることが好ましく、０．３以上０．７以下
が更に好ましい。When the convex or concave shape of the buffer wall portion is trapezoidal, as shown in FIG. 2C, the length of the top side is equal to the length of the side W2 corresponding to the bottom side of the trapezoidal shape. It is preferable that the ratio of W1 (W1 / W2) is 0.1 or more and 0.9 or less, more preferably 0.3 or more and 0.7 or less.

【００３７】この比（Ｗ１／Ｗ２）が０．１より小さい
と、断面が台形形状の緩衝用壁部３ａの可撓性が高すぎ
るため緩衝性が劣り、結果として落下時に７０Ｇを超え
る衝撃が物品Ａに大きく伝わって、物品Ａが破損しやす
くなる。一方、この比が０．９を超えると、逆に可撓性
が不足するため緩衝性が劣り、落下時に７０Ｇを超える
衝撃が物品Ａに大きく伝わる傾向となる。If this ratio (W1 / W2) is smaller than 0.1, the cushioning wall 3a having a trapezoidal cross section has too high flexibility, so that the cushioning property is inferior. It is transmitted to the article A greatly, and the article A is easily damaged. On the other hand, when this ratio exceeds 0.9, the flexibility is insufficient, and conversely, the cushioning property is inferior, and an impact exceeding 70 G tends to be transmitted to the article A when dropped.

【００３８】以上のように構成された物品梱包用緩衝材
１ａを用いて物品Ａを梱包箱８（図４参照）に収納する
には、まず、図１に示す底面緩衝部２の支持部２１ａ、
２１ｂの上に、物品Ａの右側下面を当接支持させること
により載置する。その後、図１に示すように、側面緩衝
部３を、ヒンジ部４を回動中心として底面緩衝部２に対
して９０度回動させる。その結果、第１傾斜面２２と第
２傾斜面３１とが接触し、嵌合凹部（図示省略）と嵌合
凸部（図示省略）とが嵌合し、側面緩衝部３の窪み３３
内に、物品ＡのＹ方向右側端部の上部角部が収納され
る。In order to store the article A in the packing box 8 (see FIG. 4) by using the article packing cushioning material 1a configured as described above, first, the support section 21a of the bottom cushioning section 2 shown in FIG. ,
The article A is placed on the lower surface 21b by contacting and supporting the lower right surface of the article A. Thereafter, as shown in FIG. 1, the side buffer 3 is rotated by 90 degrees with respect to the bottom buffer 2 around the hinge 4. As a result, the first inclined surface 22 and the second inclined surface 31 come into contact with each other, the fitting concave portion (not shown) and the fitting convex portion (not shown) fit, and the depression 33 of the side cushioning portion 3 is formed.
Inside, the upper corner at the right end in the Y direction of the article A is stored.

【００３９】なお、側面緩衝部３を、ヒンジ部４を回動
中心として底面緩衝部２に対して約９０度回動させて、
図１に示す状態とした後に、物品Ａを緩衝材１ａに挿入
して保持させてもよい。The side buffer 3 is rotated about 90 degrees with respect to the bottom buffer 2 about the hinge 4 as a rotation center.
After the state shown in FIG. 1, the article A may be inserted and held in the cushioning material 1a.

【００４０】物品Ａの左側については、緩衝材１ａとＸ
方向（図１参照）に対して線対称となる同一構造の緩衝
材１ｂを別途用意し、これを用いて同様に行うことがで
きる。その状態で、図４に示すように、段ボール箱など
の梱包箱８に入れればよい。On the left side of the article A, the cushioning material 1a and X
A buffer member 1b having the same structure that is symmetrical with respect to the direction (see FIG. 1) is separately prepared, and the same operation can be performed using this. In that state, as shown in FIG. 4, it may be put in a packing box 8 such as a cardboard box.

【００４１】第２実施形態 図５に示すように、第２実施形態に係る物品梱包用緩衝
材２ａは、図１〜４に示す第１実施形態に係る物品梱包
用緩衝材１ａの変形例であり、底面緩衝部５と、その底
面緩衝部５に対してヒンジ部７を介して回動自在に一体
成形してある側面緩衝部６と、側面緩衝部６の上部に一
体成形してある天井面緩衝部６ａとを有する。天井面緩
衝部６ａには、断面が台形形状の山稜構造の緩衝用壁部
６４が設けてあり、台形形状の頂上部の辺の長さと底面
に相当する辺の長さの比が０．５となっている。 Second Embodiment As shown in FIG. 5, an article packing cushioning material 2a according to the second embodiment is a modification of the article packing cushioning material 1a according to the first embodiment shown in FIGS. A bottom cushioning part 5; a side cushioning part 6 rotatably formed integrally with the bottom cushioning part 5 via a hinge 7; and a ceiling integrally formed on the upper part of the side cushioning part 6. And a surface buffer 6a. The ceiling buffer 6a is provided with a buffer wall 64 having a ridge structure with a trapezoidal cross section, and the ratio of the length of the top of the trapezoid to the length of the side corresponding to the bottom is 0.5. It has become.

【００４２】第２実施形態における緩衝材２ａのその他
の構造は、以下に示す以外は、前記第１実施形態の緩衝
材２と同じである。第２実施形態の緩衝材２ａでは、底
面緩衝部５に横断面形状が長方形である２つの支持部５
１ａ、５１ｂと、横断面形状が略正方形状である１つの
支持部５１ｃ、５１ｄそれぞれとが一体に成形してあ
る。また、底面緩衝部５の５２ａ、５２ｂには、段差５
２１ａ、５２１ｂの他、凹部５２２ａ、５２２ｂが形成
してある。さらに、側面緩衝部６の補強リブ６１には、
段差６３２の他、凹部６３３が設けてある。さらにま
た、底面緩衝部５の略中央部には、物品Ａの底面に当接
した段差状の緩衝用凸部５３が形成してある。The other structure of the cushioning member 2a in the second embodiment is the same as the cushioning member 2 in the first embodiment except for the following. In the cushioning member 2a of the second embodiment, two support portions 5 having a rectangular cross section are formed on the bottom surface buffer portion 5.
1a, 51b and one of the support portions 51c, 51d each having a substantially square cross-sectional shape are integrally formed. Also, steps 5a are provided at 52a and 52b of the bottom buffer section 5.
In addition to 21a and 521b, recesses 522a and 522b are formed. Further, the reinforcing ribs 61 of the side cushioning portions 6 include
A recess 633 is provided in addition to the step 632. Furthermore, a step-shaped buffering convex portion 53 in contact with the bottom surface of the article A is formed at a substantially central portion of the bottom buffer portion 5.

【００４３】以上のように構成された物品梱包用緩衝材
２ａと、この緩衝材２ａと線対称な他方の緩衝材１ｂと
を用い、第１実施形態の緩衝材１ａ、１ｂと同様の方法
で、物品Ａを梱包箱８（図４参照）に収納する。Using the cushioning material 2a for packing goods configured as described above and the other cushioning material 1b which is symmetrical to the cushioning material 2a, a method similar to that of the cushioning materials 1a and 1b of the first embodiment is used. Then, the article A is stored in the packing box 8 (see FIG. 4).

【００４４】本実施形態では、天井面緩衝部６ａに、台
形形状の山稜構造である緩衝用壁部６４を設けており、
台形形状の頂上部の辺の長さと底面に相当する辺の長さ
の比が０．５となるように形成しているが、本実施形態
に係る物品梱包用緩衝材２ａでも、第１実施形態に係る
物品梱包用緩衝材１ａと同様な作用効果を奏する。In this embodiment, a buffer wall 64 having a trapezoidal ridge structure is provided in the ceiling buffer 6a.
Although the trapezoidal shape is formed such that the ratio of the length of the top side to the length of the side corresponding to the bottom surface is 0.5, the cushioning material 2a for goods packing according to the present embodiment also has the first embodiment. The same operational effects as those of the article packaging cushioning material 1a according to the embodiment can be obtained.

【００４５】また、本実施形態によれば、凹部５２２
ａ、５２２ｂ、６３３を形成してあるので、補強リブ５
２ａ、５２ｂ、６１の剛性がさらに向上する。Further, according to the present embodiment, the concave portion 522
a, 522b, and 633, the reinforcing ribs 5
The rigidity of 2a, 52b, 61 is further improved.

【００４６】さらに、本実施形態によれば、底面緩衝部
６の略中央部に、物品Ａに当接する緩衝用凸部５３が形
成してあるので、梱包箱８（図４参照）が万が一落下し
た場合でも、物品Ａの底面が当接した凸部５３が衝撃方
向に縮径して、衝撃を緩和させることができる。Further, according to the present embodiment, since the buffering convex portion 53 which comes into contact with the article A is formed substantially at the center of the bottom buffering portion 6, the packing box 8 (see FIG. 4) should be dropped. Even in this case, the convex portion 53 with which the bottom surface of the article A abuts is reduced in diameter in the impact direction, and the impact can be reduced.

【００４７】第３実施形態 図６に示すように、第３実施形態に係る物品梱包用緩衝
材１０ａは、物品Ａの底面を保持して緩衝作用を行う底
面緩衝部１０１ａと、前記底面緩衝部１０１ａに回動自
在に設けられて前記物品Ａの側面を保持して緩衝作用を
行う側面緩衝部１０２ａと、前記側面緩衝部１０２ａに
回動自在に設けられて前記物品Ａの天井面を保持して緩
衝作用を行う天井面緩衝部１０３ａとを有する。 Third Embodiment As shown in FIG. 6, an article packing cushioning material 10a according to a third embodiment comprises a bottom cushioning section 101a for holding a bottom surface of an article A and cushioning the article A, and the bottom cushioning section. A side buffer portion 102a rotatably provided on 101a and holding a side surface of the article A to perform a buffering action, and a rotatable provided on the side buffer portion 102a to hold a ceiling surface of the article A. And a ceiling buffering portion 103a that performs a buffering action.

【００４８】緩衝材１０ａにおいて、底面緩衝部１０１
ａと側面緩衝部１０２ａとは、ヒンジ部１０４ａで接合
されている。また、天井面緩衝部１０３ａと側面緩衝部
１０２ａとは、ヒンジ部１０５ａで接合されている。In the cushioning member 10a, the bottom cushioning portion 101
a and the side cushioning part 102a are joined by a hinge part 104a. The ceiling buffer 103a and the side buffer 102a are joined by a hinge 105a.

【００４９】側面緩衝部１０２ａには、図１に示す緩衝
材１ａの側面緩衝部３と同じ構造の緩衝用凹部が２つ設
けられている。底面緩衝部１０１ａと側面緩衝部１０２
ａとは、底面緩衝部１０１ａの第１傾斜面１０６ａと側
面緩衝部１０２ａの第２傾斜面１０７ａとで接触してい
る。また、側面緩衝部１０２ａと天井面緩衝部１０３ａ
とは、側面緩衝部１０２ａの第３傾斜面１０８ａと天井
面緩衝部１０３ａの第４傾斜面１０９ａとで接触してい
る。The side buffer 102a is provided with two buffer recesses having the same structure as the side buffer 3 of the buffer 1a shown in FIG. Bottom buffer 101a and side buffer 102
a is in contact with the first inclined surface 106a of the bottom cushioning portion 101a and the second inclined surface 107a of the side cushioning portion 102a. In addition, the side cushioning section 102a and the ceiling cushioning section 103a
Is in contact with the third inclined surface 108a of the side cushioning portion 102a and the fourth inclined surface 109a of the ceiling cushioning portion 103a.

【００５０】第１傾斜面１０６ａには嵌合凹部（図示省
略）、第２傾斜面１０７ａには嵌合凸部（図示省略）が
設けられており、底面緩衝部１０１ａと側面緩衝部１０
２ａの間のヒンジ部１０４ａを回動中心として約９０度
回動させて嵌合させる。また、第３傾斜面１０８ａには
嵌合凸部（図示省略）、第４傾斜面１０９ａには嵌合凹
部（図示省略）が設けられており、側面緩衝部１０２ａ
と天井面緩衝部１０３ａの間のヒンジ部１０５ａを回動
中心として約９０度回動させて嵌合させる。第２傾斜面
１０７ａの嵌合凸部と第３傾斜面１０８ａの嵌合凸部は
線対称な形状（図示省略）である。The first inclined surface 106a is provided with a fitting concave portion (not shown), and the second inclined surface 107a is provided with a fitting convex portion (not shown). The bottom buffer portion 101a and the side buffer portion 10a are provided.
The fitting is performed by rotating the hinge portion 104a between the portions 2a about 90 degrees about the rotation center. A fitting projection (not shown) is provided on the third inclined surface 108a, and a fitting recess (not shown) is provided on the fourth inclined surface 109a.
The hinge part 105a between the head and the ceiling surface buffer part 103a is rotated by about 90 degrees about the hinge part 105a as a rotation center to be fitted. The fitting projection of the second inclined surface 107a and the fitting projection of the third inclined surface 108a have a line-symmetrical shape (not shown).

【００５１】本実施形態では、天井面緩衝部１０３ａの
みでなく、底面緩衝部１０１ａにも、物品Ａの底面また
は天井面に略垂直な基準面に対して、凸または凹となる
緩衝用壁部７４が形成してある。In the present embodiment, not only the ceiling cushioning portion 103a but also the bottom cushioning portion 101a has a cushioning wall portion that is convex or concave with respect to the reference surface substantially perpendicular to the bottom surface or the ceiling surface of the article A. 74 are formed.

【００５２】なお、図６に示す緩衝材１０ｂは、緩衝材
１０ａと同じ構成であり、その詳細な説明は省略する
が、緩衝材１０ａと同様に、底面緩衝部１０１ｂと、側
面緩衝部１０２ｂと、天井面緩衝部１０３ｂとを有す
る。The cushioning member 10b shown in FIG. 6 has the same structure as the cushioning member 10a, and detailed description thereof is omitted. However, like the cushioning member 10a, the bottom cushioning portion 101b and the side cushioning portion 102b are similar to the cushioning member 10a. And a ceiling surface buffering part 103b.

【００５３】以上のように構成された物品梱包用緩衝材
１０ａ、１０ｂを用いて、図１に示す実施形態と同様に
して、物品Ａを緩衝材１０ａ、１０ｂに挿入して保持さ
せ、図７に示すように、段ボール箱などの梱包箱９に収
納することができる。Using the cushioning materials 10a and 10b for packing articles configured as described above, the article A is inserted into the cushioning materials 10a and 10b and held in the same manner as in the embodiment shown in FIG. As shown in (1), it can be stored in a packing box 9 such as a cardboard box.

【００５４】第４実施形態 図８に示すように、第４実施形態に係る物品梱包用緩衝
材６００は、底面緩衝部６０２と、この底面緩衝部６０
２の両端に対して回動自在に一体成形してある側面緩衝
部６０４と、この側面緩衝部６０４に対して一体成形し
てある天井面緩衝部６０６とを有する。本実施形態で
は、天井面緩衝部６０６の側面に、断面三角状の緩衝用
壁部６０８が形成してあると共に、底面緩衝部６０２の
両内側壁面に、緩衝用壁部６１０が形成してある。 Fourth Embodiment As shown in FIG. 8, a cushioning material 600 for packing goods according to a fourth embodiment includes a bottom cushioning portion 602 and a bottom cushioning portion 60.
2 has a side buffer 604 integrally formed rotatably with respect to both ends, and a ceiling buffer 606 integrally formed with the side buffer 604. In the present embodiment, a buffer wall portion 608 having a triangular cross section is formed on a side surface of the ceiling buffer portion 606, and a buffer wall portion 610 is formed on both inner wall surfaces of the bottom buffer portion 602. .

【００５５】本実施形態の緩衝材６００のその他の構造
は、図１に示す緩衝材１ａと同様であり、同様な作用効
果を奏する。The rest of the structure of the cushioning member 600 of the present embodiment is the same as that of the cushioning member 1a shown in FIG.

【００５６】なお、本発明は、上述した実施形態に限定
されるものではなく、本発明の範囲内で種々に改変する
ことができる。It should be noted that the present invention is not limited to the above-described embodiment, but can be variously modified within the scope of the present invention.

【００５７】[0057]

【実施例】以下、本発明を、さらに詳細な実施例に基づ
き説明するが、本発明は、これら実施例に限定されな
い。実施例１ ポリプロピレン３５重量％、高密度ポリエチレン２５重
量％、炭酸カルシウム３８重量％および酸化チタン２重
量％からなるポリオレフィン樹脂材料を用いて、単軸押
出機およびＴダイにより、厚み１．０ｍｍのシートを押
し出した。次いで、このシートを真空成形により、図１
の斜視図で示す物品梱包用緩衝材１ａを成形した。ま
た、同様にして、緩衝材１ａと対を成す緩衝材１ｂも成
形した。EXAMPLES Hereinafter, the present invention will be described based on more detailed examples, but the present invention is not limited to these examples. Example 1 A sheet having a thickness of 1.0 mm was formed using a polyolefin resin material composed of 35% by weight of polypropylene, 25% by weight of high-density polyethylene, 38% by weight of calcium carbonate, and 2% by weight of titanium oxide by a single screw extruder and a T-die. Extruded. Next, this sheet was vacuum-formed to form a sheet shown in FIG.
The cushioning material 1a for packing goods shown in the perspective view of FIG. Similarly, a cushioning material 1b paired with the cushioning material 1a was formed.

【００５８】緩衝材１ａにおける天井面緩衝部３ａに
は、断面が三角形状の山稜構造である緩衝用壁部３４を
設けた。この緩衝用壁部３４の三角形状頂上部の角度は
９０度であった。緩衝材１ｂにも、同様な緩衝用壁部を
設けた。In the cushioning member 1a, the ceiling cushioning portion 3a is provided with a cushioning wall portion 34 having a mountain ridge structure having a triangular cross section. The angle of the triangular top of the buffer wall 34 was 90 degrees. The cushioning member 1b was also provided with a similar cushioning wall.

【００５９】以上のように構成された物品梱包用緩衝材
１ａ、１ｂのそれぞれにて、側面緩衝部３を、ヒンジ部
４を回動中心として底面緩衝部に対して約９０度回動さ
せて、図１に示すような状態とした後に、物品Ａを緩衝
材１ａ、１ｂに挿入して保持させた。この状態のまま
で、図４に示すように、段ボール箱などの梱包箱８に収
納した。In each of the article packaging cushioning materials 1a and 1b configured as described above, the side cushioning part 3 is rotated about 90 degrees with respect to the bottom cushioning part about the hinge part 4 as the center of rotation. After the state as shown in FIG. 1, the article A was inserted and held in the cushioning materials 1a and 1b. In this state, as shown in FIG. 4, it was stored in a packing box 8 such as a cardboard box.

【００６０】前記のように、物品Ａと物品梱包用緩衝材
１ａ、１ｂを収納した段ボール箱の底面と天面を垂直方
向に連続して９２ｃｍの高さから自由落下させ、落下直
後に物品Ａに加わった衝撃加速度（Ｇ値）を測定した。
ここで、Ｇ値とは、重力加速度の倍数の加速度を示す
が、たとえば、６０Ｇとは重力加速度の６０倍の加速度
であることを意味する。As described above, the bottom surface and the top surface of the cardboard box containing the article A and the cushioning material for article packing 1a, 1b are successively vertically dropped freely from a height of 92 cm. The impact acceleration (G value) applied to was measured.
Here, the G value indicates an acceleration that is a multiple of the gravitational acceleration. For example, 60G means an acceleration that is 60 times the gravitational acceleration.

【００６１】衝撃加速度の測定に際して、物品Ａの重心
付近に衝撃加速度センサー（昭和測器社製、２３５８
型）を取付け、加速度計測器（昭和測器、ＭＯＤＥＬ
１６１８型）に接続して衝撃加速度を測定した。なお、
振動等による加速度を除外するために、加速度計測器に
て１００Ｈｚ以上の信号を除外するフィルターを設定し
た。When measuring the impact acceleration, an impact acceleration sensor (2358, manufactured by Showa Sokki Co., Ltd.) was placed near the center of gravity of article A.
Type) and an accelerometer (Showa Sokki, MODEL)
1618) to measure the impact acceleration. In addition,
In order to exclude acceleration due to vibration or the like, a filter was set by an acceleration measuring device to exclude signals of 100 Hz or more.

【００６２】測定された衝撃加速度は、表１に示すよう
に、底面を垂直方向に落下させたときが６５Ｇで、天面
を垂直方向に落下させたときが６０Ｇと良好であった。As shown in Table 1, the measured shock acceleration was as good as 65 G when the bottom surface was dropped vertically and 60 G when the top surface was dropped vertically.

【００６３】図４に示すような、物品Ａと物品梱包用緩
衝材１ａ、１ｂを収納した段ボール箱を複数個作成し、
これらを所定のコンテナに積み重ねて収納したところ、
２０個の段ボール箱を効率よく収納できた。As shown in FIG. 4, a plurality of cardboard boxes containing the article A and the cushioning materials 1a and 1b for packing the articles were prepared.
When these were stacked and stored in a predetermined container,
20 cardboard boxes could be stored efficiently.

【００６４】実施例２ 実施例１で使用したものと同じポリオレフィン樹脂材料
にて、実施例１と同じ方法で、図５の斜視図で示す物品
梱包用緩衝材２ａ、２ｂを成形した。 Example 2 Using the same polyolefin resin material as that used in Example 1, cushioning materials 2a and 2b for article packing shown in the perspective view of FIG.

【００６５】緩衝材２ａの天井面緩衝部６ａには、断面
が台形形状の山稜構造である緩衝用壁部６４を設けた。
この山稜構造６４の台形形状の頂上部の辺の長さと底面
に相当する辺の長さの比は０．５であった。A cushioning wall 64 having a trapezoidal cross section and a mountain ridge structure is provided on the ceiling cushioning portion 6a of the cushioning material 2a.
The ratio of the length of the side of the top of the trapezoidal shape of the mountain ridge structure 64 to the length of the side corresponding to the bottom was 0.5.

【００６６】以上のように構成された物品梱包用緩衝材
２ａ、２ｂのそれぞれにて、側面緩衝部を、ヒンジ部を
回動中心として底面緩衝部に対して約９０度回動させ
て、図５に示すような状態とした後に、物品Ａを緩衝材
２ａ、２ｂに挿入して保持させた。この状態のままで、
図４に示すように、段ボール箱などの梱包箱８に収納し
た。In each of the article packing cushioning materials 2a and 2b configured as described above, the side cushioning part is rotated about 90 degrees with respect to the bottom cushioning part about the hinge part as a rotation center. After the state as shown in FIG. 5, the article A was inserted and held in the cushioning materials 2a and 2b. In this state,
As shown in FIG. 4, it was stored in a packing box 8 such as a cardboard box.

【００６７】物品Ａと物品梱包用緩衝材２ａ、２ｂを収
納した段ボール箱を、実施例１と同じ条件で落下試験を
行い、同様の測定方法で落下直後に物品Ａに加わった衝
撃加速度を測定した。A drop test is performed on the cardboard box containing the article A and the cushioning materials 2a and 2b for article packing under the same conditions as in Example 1, and the impact acceleration applied to the article A immediately after dropping is measured by the same measuring method. did.

【００６８】測定された衝撃加速度は、表１に示すよう
に、底面を垂直方向に落下させたときが６０Ｇで、天面
を垂直方向に落下させたときが６６Ｇと良好であった。As shown in Table 1, the measured shock acceleration was as good as 60 G when the bottom surface was dropped vertically and 66 G when the top surface was dropped vertically.

【００６９】図４に示すような、物品Ａと物品梱包用緩
衝材２ａ、２ｂを収納した段ボール箱を複数個作成し、
これらを所定のコンテナに積み重ねて収納したところ、
２０個の段ボール箱を効率よく収納できた。As shown in FIG. 4, a plurality of cardboard boxes containing article A and article packing cushioning materials 2a and 2b were prepared.
When these were stacked and stored in a predetermined container,
20 cardboard boxes could be stored efficiently.

【００７０】比較例１ 実施例１で使用したものと同じポリオレフィン樹脂材料
にて、実施例１と同じ方法で、図１に示す緩衝用壁部３
４を成形しない以外は、実施例１と同様な一対の物品梱
包用緩衝材を成形した。[0070] Comparative Example 1 with the same polyolefin resin material as used in Example 1, in the same manner as in Example 1, the buffer wall portion 3 shown in FIG. 1
A pair of cushioning materials for packing articles was formed in the same manner as in Example 1 except that No. 4 was not formed.

【００７１】比較例１に係る物品梱包用緩衝材９ａ、９
ｂを用いて物品Ａを収納した段ボール箱を、実施例１と
同じ条件で落下試験を行い、同様の測定方法で落下直後
に物品Ａに加わった衝撃加速度を測定した。The article packing cushioning materials 9a and 9 according to Comparative Example 1
A drop test was performed on the cardboard box containing the article A using b under the same conditions as in Example 1, and the impact acceleration applied to the article A immediately after falling was measured by the same measurement method.

【００７２】また、比較例１に係る物品梱包用緩衝材９
ａ、９ｂを用いて物品Ａを収納した段ボール箱を複数個
作成し、これらを所定のコンテナに積み重ねて収納した
ところ、２０個の段ボール箱を収納できた。しかし、測
定された衝撃加速度は、表１に示すように、底面を垂直
方向に落下させたときが６３Ｇであったものの、天面を
垂直方向に落下させたときが９０Ｇと大きいＧ値が測定
された。The cushioning material 9 for packing articles according to Comparative Example 1
When a plurality of cardboard boxes containing the article A were prepared using the items a and 9b, and these were stacked and stored in a predetermined container, 20 cardboard boxes could be stored. However, as shown in Table 1, the measured impact acceleration was 63 G when the bottom surface was dropped vertically, but was 90 G when the top surface was dropped vertically, and a large G value was measured. Was done.

【００７３】[0073]

【表１】 [Table 1]

【００７４】[0074]

【発明の効果】以上説明してきたように、本発明によれ
ば、物品梱包用緩衝材を収納する段ボール外箱の大きさ
も極力少なくすることができ、結果として保管時のスペ
ースを有効に活用することが可能な物品梱包用緩衝材を
提供することができる。As described above, according to the present invention, the size of the outer corrugated cardboard box for storing the cushioning material for article packing can be reduced as much as possible, and as a result, the storage space can be effectively utilized. It is possible to provide a cushioning material for packaging articles that can be used.

【図面の簡単な説明】[Brief description of the drawings]

【図１】 図１は本発明の第１実施形態に係る物品梱包
用緩衝材の使用前の状態を示す斜視図である。FIG. 1 is a perspective view showing a state before using a cushioning material for packing articles according to a first embodiment of the present invention.

【図２】 図２（Ａ）および（Ｂ）は図１に示すIIA−I
IA線およびIIB−IIB線に沿う要部断面図、図２（Ｃ）は
図２（Ａ）に示す緩衝用壁部の要部拡大断面図である。FIGS. 2A and 2B show IIA-I shown in FIG.
FIG. 2C is a cross-sectional view of a principal part of the cushioning wall shown in FIG. 2A, taken along line IA and IIB-IIB.

【図３】 図３は図１に示す物品梱包用緩衝材に物品を
載せた状態を示す斜視図である。FIG. 3 is a perspective view showing a state where an article is placed on the article packing cushioning material shown in FIG. 1;

【図４】 図４は段ボール外箱の内部に物品及び図１に
示す物品梱包用緩衝材を収納した状態を透視斜視図であ
る。FIG. 4 is a perspective view showing a state in which an article and a cushioning material for article packing shown in FIG. 1 are housed in an outer cardboard box.

【図５】 図５は本発明の第２実施形態に係る物品梱包
用緩衝材の使用状態を示す斜視図である。FIG. 5 is a perspective view showing a use state of a cushioning material for packing articles according to a second embodiment of the present invention.

【図６】 図６は本発明の第３実施形態に係る物品梱包
用緩衝材の使用状態を示す斜視図である。FIG. 6 is a perspective view showing a use state of a cushioning material for packing articles according to a third embodiment of the present invention.

【図７】 図７は図６に示す物品梱包用緩衝材を物品と
共に段ボール外箱の内部に収納した状態を透視側面図で
ある。7 is a transparent side view showing a state in which the cushioning material for packing articles shown in FIG. 6 is stored together with the articles in an outer cardboard box.

【図８】 図８は本発明の第４実施形態に係る物品梱包
用緩衝材の使用状態を示す斜視図である。FIG. 8 is a perspective view showing a use state of a cushioning material for packing articles according to a fourth embodiment of the present invention.

【符号の説明】[Explanation of symbols]

１ａ，１ｂ，２ａ，１０ａ，１０ｂ，６００… 物品梱
包用緩衝材 ２，５，１０１ａ，１０１ｂ，６０２… 底面緩衝部 ３，６，１０２ａ，１０２ｂ，６０４… 側面緩衝部 ３ａ，６ａ，１０３ａ，１０３ｂ… 天井面緩衝部 ４，７，１０４ａ… ヒンジ部 ３４，６４，７４，６０８，６１０… 緩衝用壁部 Ａ… 物品 Ａ１… 基準面1a, 1b, 2a, 10a, 10b, 600 ... cushioning material for article packing 2, 5, 101a, 101b, 602 ... bottom cushioning part 3, 6, 102a, 102b, 604 ... side cushioning part 3a, 6a, 103a, 103b ... Ceiling surface buffer parts 4, 7, 104a ... Hinge parts 34, 64, 74, 608, 610 ... Buffer wall parts A ... Articles A1 ... Reference plane

───────────────────────────────────────────────────── フロントページの続き (72)発明者 江川 亮子 神奈川県川崎市川崎区夜光一丁目２番１号 ゼオン化成株式会社川崎研究所内 (72)発明者 佐藤 克則 神奈川県川崎市川崎区夜光一丁目２番１号 ゼオン化成株式会社川崎研究所内 (72)発明者 大西 和幸 神奈川県川崎市川崎区夜光一丁目２番１号 日本ゼオン株式会社物性加工研究所内 Ｆターム(参考） 3E066 AA44 AA46 CA01 HA01 NA01 NA41 NA60  ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Ryoko Egawa 2-1-1, Yakko, Kawasaki-ku, Kawasaki-shi, Kanagawa Prefecture Zeon Kasei Co., Ltd.Kawasaki Research Institute (72) Inventor Katsunori Sato, 1-chome, Yakko, Kawasaki-ku, Kawasaki-shi, Kanagawa No.2-1 Inside Zeon Kasei Co., Ltd. Kawasaki Research Laboratory (72) Inventor Kazuyuki Onishi 1-1-2, Yakko, Kawasaki-ku, Kawasaki-shi, Kanagawa F-term in Physical Properties Research Laboratory of Zeon Co., Ltd. 3E066 AA44 AA46 CA01 HA01 NA01 NA41 NA60

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 熱可塑性樹脂シートを凸凹状に加工する
ことにより一体的に成形される物品梱包用緩衝材であっ
て、 前記物品梱包用緩衝材の一部には、物品の底面、側面ま
たは天井面に略垂直な基準面に対して、凸または凹とな
る緩衝用壁部が形成してあることを特徴とする物品梱包
用緩衝材。An article packaging cushioning material integrally formed by processing a thermoplastic resin sheet into an irregular shape, wherein a part of the article packaging cushioning material includes a bottom surface, a side surface, or a bottom surface of an article. A cushioning material for packaging articles, wherein a cushioning wall portion that is convex or concave is formed with respect to a reference plane substantially perpendicular to a ceiling surface. 【請求項２】 前記緩衝用壁部の断面形状が、三角形状
であり、三角形状の頂角（θ）が３０〜１５０度である
請求項１に記載の物品梱包用緩衝材。2. The article packaging cushioning material according to claim 1, wherein the cushioning wall section has a triangular cross-section, and the apex angle (θ) of the triangle is 30 to 150 degrees. 【請求項３】 前記緩衝用壁部の断面形状が、台形形状
であり、台形形状の底辺に相当する辺の長さ（Ｗ２）に
対する頂上部の辺の長さ（Ｗ１）の比（Ｗ１／Ｗ２）
が、０．１〜０．９である請求項１に記載の物品梱包用
緩衝材。3. A sectional shape of the buffer wall portion is a trapezoidal shape, and a ratio (W1 / 1/1) of a length (W1) of a top portion to a length (W2) of a side corresponding to a bottom side of the trapezoidal shape. W2)
2. The cushioning material for packaging articles according to claim 1, wherein the number is 0.1 to 0.9.