JP2001205761A - Laminate having excellent pinhole resistance and packaging bag using it - Google Patents
Laminate having excellent pinhole resistance and packaging bag using itInfo
- Publication number
- JP2001205761A JP2001205761A JP2000023014A JP2000023014A JP2001205761A JP 2001205761 A JP2001205761 A JP 2001205761A JP 2000023014 A JP2000023014 A JP 2000023014A JP 2000023014 A JP2000023014 A JP 2000023014A JP 2001205761 A JP2001205761 A JP 2001205761A
- Authority
- JP
- Japan
- Prior art keywords
- laminate
- film
- layer
- pinhole resistance
- coating agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、柔軟性に優れた二
軸延伸ポリアミド(ナイロン)フィルムを基材とした包
装用の積層体に関するものであり、さらに詳細には、輸
送中等における屈曲や摩擦等による耐ピンホール性に優
れた積層体を用いた食品や医薬品を収容する包装袋に関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a laminate for packaging based on a biaxially stretched polyamide (nylon) film having excellent flexibility, and more particularly to bending and friction during transportation or the like. The present invention relates to a packaging bag for storing foods and medicines using a laminate excellent in pinhole resistance due to the above.
【0002】[0002]
【従来の技術】従来、バリア性が付与された柔軟な二軸
延伸ポリアミド(ナイロン)フィルムをバリア基材とし
た透明なバリア性包装材が、輸送中等における屈曲や摩
擦による耐ピンホール性に優れていることから、食品や
医薬品等を収容するバリア性包装袋として広く使用され
ている。2. Description of the Related Art Conventionally, a transparent barrier wrapping material using a flexible biaxially stretched polyamide (nylon) film having a barrier property as a barrier substrate is excellent in pinhole resistance due to bending and friction during transportation or the like. Therefore, it is widely used as a barrier packaging bag for storing foods, pharmaceuticals and the like.
【0003】上記耐ピンホール性を有すバリア性包装材
として、例えば最外層がポリ塩化ビニルデン樹脂が塗布
された延伸ナイロンフィルムで、最内層が直鎖低密度ポ
リエチレン樹脂でなるシーラントフィルムをドライラミ
ネーション用接着剤を介してラミネートしたものがあっ
た。As the above-mentioned barrier packaging material having pinhole resistance, for example, a sealant film in which the outermost layer is a stretched nylon film coated with polyvinyl chloride resin and the innermost layer is a linear low-density polyethylene resin is dry-laminated. Some were laminated via an adhesive for use.
【0004】しかし、上記構成の包装材では、バリア層
に用いられているポリ塩化ビニルデンは、使用後の焼却
処理で塩素ガスやダイオキシン等有害ガスの発生等、廃
棄物に係わる環境問題から忌避されるようになった。こ
のポリ塩化ビニルデンに変わるものとしてアルミニウム
箔が延伸ナイロンフィルムにラミネートされたものもあ
ったが、透明でないこともあるが、廃棄物の焼却処理で
アルミニウムのインゴットが焼却炉を傷めたり、その焼
却灰が埋立処分場で有害ガスの発生等、ポリ塩化ビニル
デンと同様廃棄物に係わる環境問題があり、これも忌避
されるようになってきた。However, in the packaging material having the above-mentioned structure, polyvinyldene chloride used in the barrier layer is repelled by environmental problems relating to wastes, such as generation of harmful gases such as chlorine gas and dioxin in incineration treatment after use. It became so. As an alternative to this polyvinyl chloride, aluminum foil was laminated on a stretched nylon film, but in some cases it was not transparent.However, incineration of waste caused the aluminum ingot to damage the incinerator or the incineration ash. However, as with polyvinyl chloride, there are environmental issues related to waste, such as the generation of harmful gases at landfill sites, and this has also been avoided.
【0005】そこで近年では、これらガスバリア層に代
わって無機酸化物、例えば酸化珪素や酸化アルミニウム
等を延伸ナイロンフィルムに蒸着したものが透明なガス
バリアフィルムとして多用されるようになってきた。そ
れを用いた包装材の一例として、酸化珪素が蒸着された
延伸ナイロンフィルムの蒸着面と直鎖低密度ポリエチレ
ン樹脂でなるシーラントフィルムとをドライラミネーシ
ョン用接着剤を介してラミネートした積層フィルムがあ
った。[0005] In recent years, instead of these gas barrier layers, inorganic oxides such as silicon oxide and aluminum oxide deposited on a stretched nylon film have been widely used as transparent gas barrier films. As an example of a packaging material using the same, there was a laminated film obtained by laminating a vapor-deposited surface of a stretched nylon film on which silicon oxide was vapor-deposited and a sealant film made of a linear low-density polyethylene resin via a dry lamination adhesive. .
【0006】しかし、上記構成の積層フィルムを用いた
包装袋では、酸化珪素が蒸着された延伸ナイロンフィル
ムが従来の塩化ビニリデンが塗布された延伸ナイロンフ
ィルムより硬いため、輸送中等における屈曲や段ボール
箱との摩擦等によってピンホールが発生し易く、その結
果としてバリア性に欠け、例えば内容物が生パン粉やス
ライスチーズ等の包装袋ではその内容物に黴が発生した
りするなどの問題があった。However, in the packaging bag using the laminated film having the above-described structure, the stretched nylon film on which silicon oxide is deposited is harder than the conventional stretched nylon film coated with vinylidene chloride. Pinholes are likely to be generated due to friction or the like, resulting in a lack of barrier properties. For example, in the case of packaging bags made of raw bread crumbs, sliced cheese or the like, there is a problem that molds are generated in the contents.
【0007】このような問題を解決するため、上記構成
の包装用積層フィルムの酸化珪素等の金属酸化物が蒸着
された延伸ナイロンフィルムの外面に、柔らかい表面コ
ート剤として、例えばポリアミド系のOPニスを塗布し
た包装用の積層フィルムとし、その積層フィルムを用い
た包装袋の屈曲による耐ピンホール性を試験した結果、
ピンホールの発生は解消されたが、このウエブ状の積層
フィルムの生産にあたり、この積層フィルムを巻き取る
時にブロッキングが発生するという問題があった。In order to solve such a problem, a soft surface coating agent such as polyamide OP varnish is applied on the outer surface of a stretched nylon film of the above-described packaging laminated film on which a metal oxide such as silicon oxide is deposited. As a result of testing the pinhole resistance due to bending of the packaging bag using the laminated film,
Although the occurrence of pinholes has been eliminated, there has been a problem in producing this web-shaped laminated film that blocking occurs when the laminated film is wound up.
【0008】また、輸送中等でピンホールの発生し易い
包装体で、ガスバリア性を必要としないが耐屈曲ピンホ
ール性を必要とする包装袋として、例えば液体スープ等
を収納する包装袋があり、その包装材として、例えば柔
軟な延伸ナイロンフィルムと直鎖低密度ポリエチレンフ
ィルムをドライラミネーション用接着剤でラミネートし
たものがあったが、同様に耐屈曲ピンホール性に劣り、
液体漏れ等が発生するという問題があった。[0008] Further, as a packaging body which is likely to generate pinholes during transportation or the like and does not require gas barrier properties but requires bending pinhole resistance, there is a packaging bag for accommodating, for example, a liquid soup. As the packaging material, for example, there was a material obtained by laminating a flexible stretched nylon film and a linear low-density polyethylene film with an adhesive for dry lamination, but also inferior in bending pinhole resistance,
There is a problem that a liquid leak or the like occurs.
【0009】[0009]
【発明が解決しようとする課題】本発明は、かかる従来
技術の問題点を解決するものであり、その課題とすると
ころは、無機酸化物蒸着層を設けた柔軟な二軸延伸ポリ
アミドフィルムを最外層とし、最内層にシーラントフィ
ルムを最内層とする透明な包装用の積層フィルムにおい
て、廃棄物に係わる環境問題がなく、輸送中等における
屈曲や摩擦によるピンホールの発生しがなく、かつ生産
時の巻き取りにブロッキングのない透明な包装用の積層
体とそれを用いた包装袋を提供することにある。SUMMARY OF THE INVENTION The present invention solves the above-mentioned problems of the prior art, and an object thereof is to provide a flexible biaxially stretched polyamide film provided with an inorganic oxide vapor-deposited layer. An outer layer, a transparent laminated film with a sealant film as the innermost layer in the innermost layer, without environmental problems related to waste, no pinholes due to bending and friction during transportation, etc., and at the time of production An object of the present invention is to provide a transparent packaging laminate having no blocking in winding and a packaging bag using the same.
【0010】[0010]
【課題を解決するための手段】本発明に於いて上記課題
を達成するために、まず請求項1の発明では、少なくと
も最外層が無機酸化物蒸着層を設けた二軸延伸ポリアミ
ドフィルムで、最内層がシーラントフィルムからなる積
層体において、前記二軸延伸ポリアミドフィルムの外面
に表面コート剤が塗布されていることを特徴とする耐ピ
ンホール性に優れた積層体としたものである。Means for Solving the Problems In order to achieve the above object in the present invention, first, in the invention of claim 1, at least the outermost layer is a biaxially stretched polyamide film provided with an inorganic oxide deposition layer. A laminate having excellent pinhole resistance, characterized in that a surface coating agent is applied to the outer surface of the biaxially stretched polyamide film in the laminate having an inner layer made of a sealant film.
【0011】また、請求項2の発明では、前記表面コー
ト剤が、ポリアミド樹脂とニトロセルロースを含むメジ
ウムもしくはウレタン樹脂と塩化ビニル−酢酸ビニル共
重合樹脂(以下塩酢ビ共重合樹脂という)を含むメジウ
ムのいずれかに、ポリエチレンワックス単体もしくはポ
リエチレンワックスと脂肪酸アミドの混合物を添加して
なることを特徴とする請求項1記載の耐ピンホール性に
優れた積層体としたものである。In the invention of claim 2, the surface coating agent comprises a polyamide resin, a medium or urethane resin containing nitrocellulose, and a vinyl chloride-vinyl acetate copolymer resin (hereinafter, referred to as a vinyl chloride-vinyl acetate copolymer resin). 2. A laminate having excellent pinhole resistance according to claim 1, wherein a single substance of polyethylene wax or a mixture of polyethylene wax and fatty acid amide is added to one of the media.
【0012】上記請求項1または2の発明によれば、最
外層の二軸延伸ポリアミドフィルムの外面に柔らかい表
面コート剤を設けることによって、耐屈曲や耐摩擦ピン
ホール性に優れた包装用の積層体とすることができ、そ
の表面コート剤をポリアミド樹脂とニトロセルロースを
含むメジウムあるいはウレタンと塩酢ビ共重合樹脂を含
むメジウムのいずれかに、ポリエチレンワックス等添加
剤を添加した塗布液とすることによって、生産時ウエブ
状積層体の巻き取りにブロッキングのない積層体とする
ことができる。According to the first or second aspect of the present invention, by providing a soft surface coating agent on the outer surface of the biaxially stretched polyamide film as the outermost layer, a laminate for packaging excellent in bending resistance and friction pinhole resistance is provided. The surface coating agent may be a coating liquid in which an additive such as polyethylene wax is added to either a medium containing polyamide resin and nitrocellulose or a medium containing urethane and vinyl chloride-vinyl acetate copolymer resin. Accordingly, a laminate having no blocking in winding the web-like laminate at the time of production can be obtained.
【0013】また、請求項3の発明では、前記請求項1
または2に記載の耐ピンホール性に優れた積層体を用い
た包装袋としたものである。According to the third aspect of the present invention, in the first aspect,
Or a packaging bag using the laminate having excellent pinhole resistance described in 2.
【0014】上記請求項3の発明によれば、耐ピンホー
ル性に優れた積層体を用いているので、輸送中等におけ
る屈曲や摩擦等によってバリア性が欠けたり、液漏れし
たりする危惧のない透明な包装袋とすることができる。According to the third aspect of the present invention, since the laminated body having excellent pinhole resistance is used, there is no fear that the barrier property is lacked or liquid leaks due to bending or friction during transportation or the like. It can be a transparent packaging bag.
【0015】[0015]
【発明の実施の形態】以下本発明の実施の形態を図面を
用いながら説明する。図1は、本発明の耐ピンホール性
に優れた積層体の一実施の形態を側断面で表した説明図
であり、図2は、本発明の耐ピンホール性に優れた積層
体の他の一実施の形態を側断面で表わした説明図であ
る。Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is an explanatory view showing an embodiment of the laminate excellent in pinhole resistance of the present invention in a side cross section, and FIG. 2 is a diagram showing another embodiment of the laminate excellent in pinhole resistance of the present invention. FIG. 2 is an explanatory diagram showing one embodiment in a side cross section.
【0016】まず本発明の耐ピンホール性に優れた積層
体は、図1の側断面図に示すように、例えば、最外層に
無機酸化物の蒸着層(10a)を有する延伸ナイロンフ
ィルム(10b)をバリアフィルム(10)とし、その
蒸着層(10a)面と接着層(20)を介して、最内層
としてのシーラントフィルム(40)とをラミネートし
た包装用の積層体(1)において、前記延伸ナイロンフ
ィルム(10b)の外面に表面コート剤層(30)が設
けられているものである。First, as shown in the side sectional view of FIG. 1, for example, a stretched nylon film (10b) having a vapor-deposited layer (10a) of an inorganic oxide as an outermost layer, as shown in the side sectional view of FIG. ) As a barrier film (10), and a laminate (1) for packaging obtained by laminating a sealant film (40) as an innermost layer via a vapor deposition layer (10a) surface and an adhesive layer (20). The surface coating agent layer (30) is provided on the outer surface of the stretched nylon film (10b).
【0017】また、上記バリアフィルム(10)とし
て、例えばその基材である延伸ナイロンフィルム(10
b)と蒸着層(10a)の間にアンカーコート層(図示
せず)を施し、さらに蒸着層(10a)の上に被覆層
(図示せず)を施して、この蒸着層(10a)の揉み等
によるクラックの発生を防止するバリアフィルム(2
0)とすることもできる。As the barrier film (10), for example, a stretched nylon film (10
b) An anchor coat layer (not shown) is applied between the vapor deposition layer (10a) and a coating layer (not shown) is further applied on the vapor deposition layer (10a) to rub the vapor deposition layer (10a). Film (2) to prevent cracks
0).
【0018】上記アンカーコート層として、例えば少な
くともアクリルポリオール、イソシアネート化合物、お
よび一般式:R’SI(OR)3 (式中R’はアルキル
基、ビニル基、グリシオキシプロピル基の一種、Rはア
ルキル基)で表される3官能オルガノシランあるいはオ
ルガノシランの加水分解物を含む組成物、または前記組
成物に一般式:M(OR)n (式中Mは金属元素、Rは
CH3 、C2 H5 等のアルキル基、nは金属元素の酸化
数)で表せる金属アルコキシド、あるいは金属アルコキ
シドの加水分解物を含む組成物を用いることができる。As the anchor coat layer, for example, at least an acrylic polyol, an isocyanate compound, and a compound represented by the general formula: R'SI (OR) 3 (where R 'is an alkyl group, a vinyl group, or a glycyoxypropyl group, and R is an alkyl group) Or a composition containing a trifunctional organosilane or a hydrolyzate of an organosilane represented by the following formula: or a general formula: M (OR) n (where M is a metal element, R is CH 3 , C 2) An alkyl group such as H 5 , and n is a metal alkoxide represented by the oxidation number of the metal element) or a composition containing a hydrolyzate of the metal alkoxide can be used.
【0019】また、上記被覆層として、例えば水溶性高
分子と、(a)1種以上の金属アルコキシド及びその加
水分解物、(b)塩化錫の少なくとも一方を含む水溶
液、あるいは水/アルコール混合液を主剤とするコーテ
ィング剤からなるものを用いることができる。The coating layer may be, for example, an aqueous solution containing at least one of a water-soluble polymer and (a) at least one metal alkoxide and its hydrolyzate, and (b) tin chloride, or a water / alcohol mixture. Can be used.
【0020】上記のようなガスバリア性を必要とする包
装用の積層体は、例えば生パン粉、餅、スライスチーズ
等を収容する耐屈曲、耐摩擦ピンホール性を有する透明
な包装袋として好適に用いられる。The above-mentioned laminate for packaging requiring gas barrier properties is suitably used as a transparent packaging bag having a resistance to bending and a resistance to pinholes for accommodating, for example, raw bread crumbs, rice cakes, sliced cheese and the like. Can be
【0021】また、図2の側断面図に示すように、例え
ば、最外層に延伸ナイロンフィルム(10b)を、その
延伸ナイロンフィルム(10b)の裏面と接着層(2
0)を介して、最内層としてのシーラントフィルム(4
0)とをラミネートした包装用の積層体(1)におい
て、前記延伸ナイロンフィルム(10b)の外面に表面
コート剤層(30)が設けられているものである。As shown in the side sectional view of FIG. 2, for example, a stretched nylon film (10b) is formed as the outermost layer, and the back surface of the stretched nylon film (10b) and the adhesive layer (2b).
0), the sealant film (4) as the innermost layer
0), wherein a surface coating agent layer (30) is provided on the outer surface of the stretched nylon film (10b).
【0022】上記のような構成のガスバリア性を必要と
しない包装用の積層体は、例えば液体スープ等を収容す
る耐屈曲、耐摩擦ピンホール性を有する透明な包装袋と
して好適に用いられる。The packaging laminate having the above-described structure that does not require gas barrier properties is suitably used as a transparent packaging bag having, for example, a bending resistance and a friction pinhole resistance for accommodating a liquid soup or the like.
【0023】本発明の耐ピンホール性に優れた積層体を
構成する最外層に用いられる二軸延伸ポリアミド(ナイ
ロン)フィルム(10b)としては、厚さ15μm程度
のフィルムが好適で、例えば市販の柔軟剤が添加された
商品名ONP(ユニチカ社製)、商品名N2102(東
洋紡績社製)などがより好適に使用することができる。
また、これら延伸ナイロンフィルムの他に、例えば共押
しバリアナイロンフィルム、バリアコーティングフィル
ム(バリア層を塗布したフィルム)またはその他ナイロ
ン系フィルムでも構わない。The biaxially stretched polyamide (nylon) film (10b) used as the outermost layer constituting the laminate having excellent pinhole resistance of the present invention is preferably a film having a thickness of about 15 μm. ONP (trade name, manufactured by Unitika) and N2102 (trade name, manufactured by Toyobo Co., Ltd.) to which a softener is added can be more preferably used.
In addition to these stretched nylon films, for example, a co-pressed barrier nylon film, a barrier coating film (a film coated with a barrier layer), or another nylon film may be used.
【0024】また、バリアフィルム(10)を構成する
無機酸化物の蒸着層(10a)としては、SiO2 、S
iO、Al2 O3 等を蒸着材料として物理蒸着法や化学
蒸着法により得られ、透明なバリアフィルム(10)と
することができる。The inorganic oxide deposited layer (10a) constituting the barrier film (10) may be SiO 2 , S
The transparent barrier film (10) can be obtained by a physical vapor deposition method or a chemical vapor deposition method using iO, Al 2 O 3 or the like as a deposition material.
【0025】また、本発明の耐ピンホール性に優れた積
層体(1)を構成する表面コート剤層(30)として
は、例えばニトロセルロースメジウムに溶解しているポ
リアミド樹脂に、添加剤としてポリエチレンワックス単
体もしくはポリエチレンワックスと脂肪酸アミドの混合
物を約3重量%添加した塗布液を5μm程度になるよう
にグラビアコート法等で全面ベタ(全面均一の厚さ)に
あるいは必要部分に部分塗布して得られる。The surface coating agent layer (30) constituting the laminate (1) having excellent pinhole resistance according to the present invention is, for example, a polyamide resin dissolved in nitrocellulose medium, and polyethylene as an additive. A coating solution obtained by adding about 3% by weight of a simple substance of wax or a mixture of polyethylene wax and fatty acid amide to a thickness of about 5 μm by gravure coating or the like on the entire surface (the entire surface has a uniform thickness) or by applying a partial coating on necessary portions. Can be
【0026】また、ウレタン樹脂と塩酢ビ共重合樹脂と
のブレンド樹脂に、上記と同様の添加剤を添加した塗布
液としてもよい。A coating solution in which the same additives as described above are added to a blend resin of a urethane resin and a vinyl chloride-vinyl acetate copolymer resin may be used.
【0027】また、本発明の耐ピンホール性に優れた積
層体(1)を構成する最内層のシーラントフィルム(4
0)としては、直鎖低密度ポリエチレンフィルム、低密
度ポリエチレンフィルム、高密度ポリエチレンフィルム
あるいは無延伸ポリプロピレンフィルム等が用いられ、
その中でも直鎖低密度ポリエチレンフィルムは、積層体
(1)を柔らかくするという点から、耐屈曲ピンホール
性の改善には好適に用いることができる。Further, the innermost sealant film (4) constituting the laminate (1) having excellent pinhole resistance of the present invention.
As 0), a linear low-density polyethylene film, a low-density polyethylene film, a high-density polyethylene film or an unstretched polypropylene film is used,
Among them, the linear low-density polyethylene film can be suitably used for improving the bending pinhole resistance from the viewpoint of softening the laminate (1).
【0028】[0028]
【実施例】次に実施例により、本発明を具体的に説明す
る。Next, the present invention will be described in detail with reference to examples.
【0029】〈実施例1〉図1の側断面図に示すよう
に、最外層のバリアフィルム(10)として、表面に厚
さ約0.1μmの下記組成でなるアンカーコート層(図
示せず)を設け、その上にAl2 03 からなる蒸着層
(10a)が真空蒸着法により形成され、さらにその上
に下記組成からなる被覆層(図示せず)が設けられ、さ
らにアンカーコート剤:商品名AD980A/AD98
0B(東洋モートン社製)が塗布された厚さ15μmの
延伸ナイロンフィルム(10b):商品名ON(ユニチ
カ社製)のアンカーコート剤側に、絵柄や説明文等の印
刷を施して、積層体の外側基材とした。Example 1 As shown in the side sectional view of FIG. 1, as an outermost barrier film (10), an anchor coat layer (not shown) having a thickness of about 0.1 μm and having the following composition was formed on the surface. the provided, deposition layer made of Al 2 0 3 (10a) is formed by vacuum deposition thereon, further (not shown) covering layer having the following composition thereon is provided, further anchor coating agent: product AD980A / AD98
15B stretched nylon film (10b) coated with OB (manufactured by Toyo Morton Co., Ltd.): A pattern or explanatory text is printed on the anchor coat agent side of trade name ON (manufactured by Unitika) to obtain a laminate. Outside substrate.
【0030】上記アンカーコート層の成分:希釈溶媒中
で、2−(エポキシシクロヘキサン)エチルトリメチル
シラン(以下EETMSとする)にアクリルポリオール
を2.5倍量(重量比)を混合し、さらに塩化錫/メタ
ノール溶液(0.003mol/gに調整)をEETM
Sに対して1.135molとなるように添加し、次い
でトリレンジイソシアネートを前記アクリルポリオール
のOH基に対して、NCO基が等量となるように混合し
た。 上記被覆層の成分:テトラエトキシシラン10.4gに
塩酸(0.1N)を89.6gを加え、30分攪拌し、
加水分解した固形分3wt%(SiO2 換算)の溶液
と、ポリビニルアルコール溶液を混合した。Components of the anchor coat layer: In a diluent solvent, 2- (epoxycyclohexane) ethyltrimethylsilane (hereinafter referred to as EETMS) was mixed with 2.5 times (weight ratio) of acrylic polyol, and tin chloride was further added. / Methanol solution (adjusted to 0.003 mol / g) with EETM
S was added so as to be 1.135 mol with respect to S, and then tolylene diisocyanate was mixed so that the NCO group was equivalent to the OH group of the acrylic polyol. Ingredients of the coating layer: To 10.4 g of tetraethoxysilane, 89.6 g of hydrochloric acid (0.1N) was added, and the mixture was stirred for 30 minutes.
A solution having a hydrolyzed solid content of 3 wt% (in terms of SiO 2 ) and a polyvinyl alcohol solution were mixed.
【0031】続いて上記で得られた積層体の外側基材を
構成する延伸ナイロンフィルム(10b)の外面に、下
記組成の塗布液を5μmになるようにグラビアコート法
で全面に塗布し表面コート剤層(30)を形成した。Subsequently, a coating solution having the following composition was applied to the entire outer surface of the stretched nylon film (10b) constituting the outer substrate of the laminate obtained above by a gravure coating method so as to have a thickness of 5 μm. An agent layer (30) was formed.
【0032】上記表面コート剤層(30)の液組成:ポ
リアミド樹脂70部とニトロセルロース30部のメジウ
ムに、ポリエチレンワックスと脂肪酸アミドからなる添
加剤:商品名添加剤#150(東洋インキ製造社製)を
3重量%添加して塗布液としたもの。Liquid composition of the above-mentioned surface coating agent layer (30): 70 parts of polyamide resin and 30 parts of nitrocellulose in a medium, polyethylene wax and fatty acid amide Additive: trade name Additive # 150 (manufactured by Toyo Ink Mfg. Co., Ltd.) ) Was added as a coating liquid by adding 3% by weight.
【0033】続いて上記で表面コート剤層(30)が塗
布された外側基材を構成するバリアフィルム(10)の
アンカーコート剤面にドライラミネーション用接着剤:
商品名A969V/A5(武田薬品工業社製)を接着層
(20)とし、シーラントフィルム(40)としての厚
さ40μmの直鎖低密度ポリエチレンフィルム:商品名
TUX−TCS(密度0.915、東セロ社製)をラミ
ネートして耐ピンホール性に優れた積層体(1)を得
た。Subsequently, an adhesive for dry lamination is applied to the anchor coating agent surface of the barrier film (10) constituting the outer substrate coated with the surface coating agent layer (30) as described above:
A969V / A5 (trade name, manufactured by Takeda Pharmaceutical Co., Ltd.) as an adhesive layer (20), and a linear low-density polyethylene film having a thickness of 40 μm as a sealant film (40): TUX-TCS (trade name: 0.915, East Sello Was laminated to obtain a laminate (1) having excellent pinhole resistance.
【0034】〈実施例2〉表面コート剤層(30)を形
成する表面コート剤の液組成をウレタン樹脂と塩化ビニ
ル−酢酸ビニル共重合樹脂とのブレンド樹脂に、ポリエ
チレンワックスと脂肪酸アミドからなる添加剤:商品名
添加剤#150(東洋インキ製造社製)を3重量%添加
して塗布液とした以外は、実施例1と同様にして耐ピン
ホール性に優れた積層体(1)を得た。Example 2 A liquid composition of a surface coating agent for forming a surface coating agent layer (30) was added to a blend resin of a urethane resin and a vinyl chloride-vinyl acetate copolymer resin comprising a polyethylene wax and a fatty acid amide. Agent: A laminate (1) having excellent pinhole resistance was obtained in the same manner as in Example 1, except that 3% by weight of an additive # 150 (manufactured by Toyo Ink Mfg. Co., Ltd.) was added as a coating solution. Was.
【0035】〈実施例3〉表面コート剤層(30)を形
成する耐ピンホール性コート剤の液組成をウレタン樹脂
と塩化ビニル−酢酸ビニル共重合体とのブレンド樹脂
に、ポリエチレンワックスと脂肪酸アミドからなる添加
剤:商品名添加剤#150(東洋インキ製造社製)(2
液タイプ)を3重量%添加して塗布液とした以外は、実
施例1と同様にして耐ピンホール性に優れた積層体
(1)を得た。Example 3 The composition of the pinhole-resistant coating agent for forming the surface coating agent layer (30) was changed to a blend resin of a urethane resin and a vinyl chloride-vinyl acetate copolymer, a polyethylene wax and a fatty acid amide. Additive consisting of: trade name additive # 150 (manufactured by Toyo Ink Manufacturing Co., Ltd.) (2
Liquid type) was added in the same manner as in Example 1 except that 3% by weight was added to obtain a coating liquid, thereby obtaining a laminate (1) having excellent pinhole resistance.
【0036】〈比較例1〉表面コート剤層(30)を形
成する表面コート剤の液組成を2液タイプウレタン系樹
脂からなる塗布液:商品名X331カセットOPニス
(東洋インキ製造社製)とした以外は、実施例1と同様
にして積層体を得た。<Comparative Example 1> The liquid composition of the surface coating agent for forming the surface coating agent layer (30) was a coating liquid composed of a two-part type urethane resin: trade name X331 cassette OP varnish (manufactured by Toyo Ink Mfg. Co., Ltd.). A laminate was obtained in the same manner as in Example 1 except that the above procedure was repeated.
【0037】〈比較例2〉図1に示す表面コート剤層
(30)を除いた以外は、実施例1と同様にして積層体
を得た。Comparative Example 2 A laminate was obtained in the same manner as in Example 1 except that the surface coating agent layer (30) shown in FIG. 1 was omitted.
【0038】上記実施例1〜3および比較例1、2で得
られた積層体を、四つ折りにして角を尖らせたテストサ
ンプルを作成し、学振型摩擦試験機にて、振幅:100
mm、振幅速度:20回/分、加重:50g、摩擦対
象:段ボール内面、摩擦回数:50〜200回、n数:
3の条件で積層耐の角部の摩擦試験を行い、その結果ピ
ンホール有りを×、ピンホール無しを○として表1に示
した。Each of the laminates obtained in Examples 1 to 3 and Comparative Examples 1 and 2 was folded in four to form a test sample having sharpened corners.
mm, amplitude speed: 20 times / min, load: 50 g, friction object: inner surface of cardboard, number of times of friction: 50 to 200 times, n number:
Under the condition of 3, a friction test was performed on the corner portions of the laminated structure, and the results are shown in Table 1 as x when there was a pinhole and ○ when there was no pinhole.
【0039】また、耐ブロッキング性の試験として、得
られた積層体のシーラントフィルム面と表面コート剤層
(30)面(比較例2ではシーラントフィルム面と延伸
ナイロンフィルム外面)を合わせて、1kg/cm2 お
よび10kg/cm2 の条件下で各々2回繰り返し、5
を良好とし1を不良とする5段階法で評価し、その結果
を表2に示した。Further, as a test for blocking resistance, a total of 1 kg / liter of the sealant film surface and the surface coating agent layer (30) surface (the sealant film surface and the stretched nylon film outer surface in Comparative Example 2) of the obtained laminate was tested. 2 times each under the conditions of cm 2 and 10 kg / cm 2 ,
Was evaluated by a five-step method in which 1 was evaluated as good and 1 was evaluated as poor. The results are shown in Table 2.
【0040】[0040]
【表1】 [Table 1]
【0041】[0041]
【表2】 [Table 2]
【0042】表1よりいずれの表面コート剤層(30)
を施した積層体でも耐屈曲ピンホール性に優れているも
のであり、それに対し比較例2の積層体のように表面コ
ート剤層(30)を除いた積層体では耐屈曲ピンホール
性に劣るものであった。また、表2より表面コート剤
が、ポリアミド樹脂とニトロセルロースとを含むメジウ
ムあるいはウレタン樹脂と塩酸ビ共重合樹脂を含むメジ
ウムのいずれかに、ポリエチレンワックス等でなる添加
剤を添加したものは、耐ブロッキング性に優れるもので
あった。From Table 1, any surface coating agent layer (30)
Is also excellent in the flex pinhole resistance, whereas the laminate excluding the surface coating agent layer (30) as in the laminate of Comparative Example 2 is inferior in the flex pinhole resistance. Was something. Also, from Table 2, the surface coating agent was prepared by adding an additive such as polyethylene wax to either a medium containing a polyamide resin and nitrocellulose or a medium containing a urethane resin and a bihydrochloride copolymer resin. It had excellent blocking properties.
【0043】[0043]
【発明の効果】本発明は以上の構成であるから、下記に
示す如き効果がある。即ち、少なくとも最外層が無機酸
化物蒸着層を有する二軸延伸ポリアミドフィルムで、最
内層がシーラントフィルムからなる包装用の積層体にお
いて、前記二軸延伸ポリアミドフィルムの外面に柔らか
い表面コート剤層を設けたので、輸送中等における耐屈
曲や耐摩擦ピンホール性に優れた包装用の積層体とする
ことができる。As described above, the present invention has the following effects. That is, at least the outermost layer is a biaxially stretched polyamide film having an inorganic oxide vapor-deposited layer, and in a packaging laminate in which the innermost layer is a sealant film, a soft surface coating agent layer is provided on the outer surface of the biaxially stretched polyamide film. Therefore, a laminate for packaging having excellent bending resistance and pinhole resistance during transportation or the like can be obtained.
【0044】また、その表面コート剤をポリアミド樹脂
とニトロセルロースを含むメジウムあるいはウレタンと
塩酢ビ共重合樹脂を含むメジウムのいずれかにポリエチ
レンワックス等添加剤を添加した塗布液とすることによ
って、生産時ウエブ状積層体の巻き取りにブロッキング
のない積層体とすることができる。Further, the surface coating agent may be prepared as a coating liquid in which an additive such as polyethylene wax is added to either a medium containing polyamide resin and nitrocellulose or a medium containing urethane and vinyl chloride-vinyl acetate copolymer resin. When the web-like laminate is wound, a laminate having no blocking can be obtained.
【0045】従って本発明は、特にガスバリア性を必要
とする食品や医薬品等を収容し、輸送中等での耐屈曲や
耐摩擦ピンホール性に優れる透明な包装袋として、優れ
た実用上の効果を発揮する。Accordingly, the present invention has an excellent practical effect as a transparent packaging bag which accommodates foods and medicines which require gas barrier properties, and has excellent bending resistance and friction pinhole resistance during transportation. Demonstrate.
【図1】本発明の耐ピンホール性に優れた積層体の一実
施の形態を示す積層断面図である。FIG. 1 is a cross-sectional view showing an embodiment of a laminate having excellent pinhole resistance according to the present invention.
【図2】本発明の耐ピンホール性に優れた積層体の他の
一実施の形態を示す積層断面図である。FIG. 2 is a cross-sectional view showing another embodiment of the laminate having excellent pinhole resistance according to the present invention.
1‥‥耐ピンホール性に優れた積層体 10‥‥バリアフィルム 10a‥‥蒸着層 10a‥‥延伸ナイロンフィルム 20‥‥接着層 30‥‥表面コート剤層 40‥‥シーラントフィルム 1) Laminate having excellent pinhole resistance 10) Barrier film 10a {Vapor deposition layer 10a} Stretched nylon film 20} Adhesive layer 30} Surface coating agent layer 40} Sealant film
フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) C09D 123/06 C09D 127/08 127/08 131/04 B 131/04 175/04 175/04 177/00 177/00 A61J 1/00 331C Fターム(参考) 3E086 AD01 BA04 BA15 BA24 BA33 BA40 BB51 BB90 CA01 CA28 4F100 AA01A AA17A AA19 AH02D AH03D AJ06D AK04D AK15D AK22D AK46B AK46D AK51D AK63 AL01D BA04 BA10A BA10C BA13 CC00D EH46 EH66A EJ38B GB17 GB23 GB66 JK04 JK09 JK14 JL00 JL12C JN01 4J038 BA081 BA082 CB021 CB022 CD061 CD062 CF041 CF042 DG001 DG002 DH001 DH002 JB12 NA10 NA11 PB04 PC08Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat II (Reference) C09D 123/06 C09D 127/08 127/08 131/04 B 131/04 175/04 175/04 177/00 177/00 A61J 1/00 331C F-term (reference) 3E086 AD01 BA04 BA15 BA24 BA33 BA40 BB51 BB90 CA01 CA28 4F100 AA01A AA17A AA19 AH02D AH03D AJ06D AK04D AK15D AK22D AK46B AK46B14E17 BAK18B14A01 JL00 JL12C JN01 4J038 BA081 BA082 CB021 CB022 CD061 CD062 CF041 CF042 DG001 DG002 DH001 DH002 JB12 NA10 NA11 PB04 PC08
Claims (3)
する二軸延伸ポリアミドフィルムで、最内層がシーラン
トフィルムからなる積層体において、前記二軸延伸ポリ
アミドフィルムの外面に表面コート剤が塗布されている
ことを特徴とする耐ピンホール性に優れた積層体。1. A laminate comprising at least an outermost layer of a biaxially stretched polyamide film having an inorganic oxide vapor-deposited layer and an innermost layer of a sealant film, wherein a surface coating agent is applied to the outer surface of the biaxially stretched polyamide film. A laminate having excellent pinhole resistance.
トロセルロースとを含むメジウムもしくはウレタン樹脂
と塩化ビニル−酢酸ビニル共重合体を含むメジウムのい
ずれかに、ポリエチレンワックス単体もしくはポリエチ
レンワックスと脂肪酸アミドの混合物を添加してなるこ
とを特徴とする請求項1記載の耐ピンホール性に優れた
積層体。2. A method according to claim 1, wherein the surface coating agent is a medium containing a polyamide resin and nitrocellulose, or a medium containing a urethane resin and a vinyl chloride-vinyl acetate copolymer. 2. The laminate having excellent pinhole resistance according to claim 1, wherein a mixture is added.
ル性に優れた積層体を用いたことを特徴とする包装袋。3. A packaging bag using the laminate having excellent pinhole resistance according to claim 1 or 2.