JP2001202660A - Integrally molded card type cd and method for manufacturing the same - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a CD which may be printed and displayed with the shapes and sizes of cards and is formed as a data recording medium for catalogues outline introduction of companies, histories of individual persons, or clinical histories, etc. SOLUTION: The CD 10 consists of a substrate 13 having the shape and size of the card, arcuate roof-like projections 15, a metallic film layer 17 and a protective layer 19 applied thereon. Documents, designs, voices, videos, etc., are recorded within the CD 10 by ruggedness for recording the digital data formed atop the substrate 17 and the metallic film layer 17 and are read by casting a laser beam thereto by a general CD reader and reading the contents by the reflection thereof. Two lines of the arcuate roof-like projections 15 are fitted and placed to the inner wall at the peripheral edge of a recessed receiving surface of a diameter 8 cm on a CD tray, by which the CD is set on the tray of the general CD reader.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【技術分野】本発明は、非円形のコンパクト・ディス
ク、例えば、読み出し専用として使われるＣＤ‐ＲＯＭ
等、及びその製造方法に関する。特に、非円形の形状を
具えると共に、一体成形してなる名刺型のコンパクト・
ディスク（以下、ＣＤと略称する）及びその製造方法に
関する。The present invention relates to non-circular compact discs, for example CD-ROMs used as read-only.
Etc. and a method for producing the same. In particular, it has a non-circular shape and a business card type compact
The present invention relates to a disk (hereinafter, abbreviated as CD) and a method of manufacturing the same.

【０００２】[0002]

【従来の技術】近年、コンピュータ技術の発達に伴い、
伝送と記憶を要するディジタル化した情報量は日増しに
膨大となり、そのためにデータの伝送及び記憶を行う際
に、常に大容量のディジタル情報記憶媒体を必要とす
る。従来から、大量のデータを記録できるディジタル情
報記憶媒体として、ＣＤがよく知られているが、殆どの
ＣＤは外形形状が円形であり、携帯性から見れば寸法、
形状ともに携帯に便利であるとは言えない。2. Description of the Related Art In recent years, with the development of computer technology,
The amount of digitized information required for transmission and storage is becoming enormous every day, and therefore, when transmitting and storing data, a large-capacity digital information storage medium is always required. Conventionally, CDs are well known as digital information storage media capable of recording a large amount of data. However, most CDs have a circular outer shape, and have dimensions and dimensions from the viewpoint of portability.
Both shapes are not portable.

【０００３】さらに、現今の商業取り引き行為において
は、常に、個人的情報、会社の概要紹介、カタログ等に
関連するデータ、または、医療に関連するデータ、例え
ば、病歴、診察記録、心電図及びレントゲン写真等のイ
メージや文字等の記録データの交換が行なわれている。
そこで、名刺のようなサイズを有するとともに、相当大
量なディジタルデータを供給できる媒体が実現できれ
ば、非常に実用性の高いものであることが言える。この
ため、大容量のディジタルデータを記録できる媒体とし
て、現在通用されているＣＤ読み取り装置支援可能な名
刺型ＣＤは、これらの要求にマッチする。さらに、前記
のＣＤの表面に対して、肌理細かな意匠的印刷を施せ
ば、使用者の使用意欲を盛り上げる効果があるので尚更
好ましい。[0003] Furthermore, in current commercial transactions, data related to personal information, company profile introduction, catalogs, etc., or data related to medical care, such as medical histories, medical records, electrocardiograms, and radiographs, are always present. The recording data such as images and characters are exchanged.
Therefore, if a medium having a size similar to a business card and capable of supplying a considerably large amount of digital data can be realized, it can be said that the medium is extremely practical. For this reason, a business card type CD which is currently used as a medium capable of recording a large amount of digital data and which can support a CD reading device meets these requirements. Further, it is even more preferable to apply finely-designed design printing to the surface of the CD, since this has the effect of increasing the user's willingness to use.

【０００４】そこで、例えば、１９９９年１１月９日
Ｇ.Ａ.Ｐｉｅｒｓｏｎによって提案された米国特許第
５,９８２,７３６号では、「交易カード光コンパクトデ
ィスク及びその使用と成形の方法」（Trading card opt
ical compact disc and method of using and forming
same）が開示されている。これは、前記交易カードの上
面に設けられた突出部２１（図５参照）を利用し、通常
のＣＤ読み取り装置のトレーに嵌合載置できるようにし
たものである。しかし、このように突出部を用いてトレ
ーに設けられた段差部と嵌合させる構成では、その記録
面に装置に載置するための突出部を設けてあるので、使
用の際には常にこの突出部が外力によって損傷しないよ
う気づかう必要がある。また、外力によって損傷を受け
ると、取り引き用カードにおけるディジタルデータの誤
読を生ずる。さらに、この取り引きガードのサイズは、
２．５×３．５吋であるので一般用名刺のサイズより大
きいために、一般用名刺として共用できないという問題
がある。Thus, for example, in US Pat. No. 5,982,736 proposed by GA Pierson on November 9, 1999, "Trading card optical compact disc and method of using and molding the same" opt
ical compact disc and method of using and forming
same). This uses a protruding portion 21 (see FIG. 5) provided on the upper surface of the trading card so that it can be fitted and mounted on a tray of a normal CD reader. However, in such a configuration in which the projection is used to fit the step portion provided on the tray, the projection is provided on the recording surface for mounting on the apparatus. Care must be taken that the protrusions are not damaged by external forces. Further, if the card is damaged by an external force, erroneous reading of digital data in the transaction card occurs. In addition, the size of this trading guard,
Since it is 2.5 × 3.5 inches, it is larger than the size of a general business card, so that it cannot be shared as a general business card.

【０００５】上述した従来の名刺型ＣＤにおいては、先
ず、周知の技術で完全な円形形状をしたディスクを製作
した後、プレス加工により名刺型のディスクを成形す
る。このとき、この名刺型ディスクの４つの隅にそれぞ
れディスクの底面から突出する４つの突起をプレス加工
により同時に形成する。従って、ディスクの上面には、
前記の４つの突起が形成された位置にこれらの突起に対
応した凹部も同時に形成される。そして、これらの４つ
の突出部をＣＤ読み取り装置のトレーにおける直径８ｃ
ｍの円形凹部の外周段差に当接させて位置決めすること
によって、名刺型ＣＤをトレー上にセットできるように
されている。In the above-mentioned conventional business card type CD, first, a completely circular disk is manufactured by a known technique, and then a business card type disk is formed by press working. At this time, four projections projecting from the bottom surface of the disk are simultaneously formed at the four corners of the business card disk by pressing. Therefore, on the top surface of the disc,
At the positions where the four protrusions are formed, concave portions corresponding to these protrusions are also formed at the same time. Then, these four protrusions are connected to the tray of the CD reader with a diameter of 8c.
The business card-type CD can be set on the tray by positioning it in contact with the outer peripheral step of the circular recess of m.

【０００６】[0006]

【発明の課題】しかし、これらの４つの突出部は、プレ
ス加工によって形成されるので、それらの形状及びサイ
ズを精度よくプレス成形することが難しいために、これ
らの４つの突起のみで前記名刺型ＣＤを安定よくトレイ
上に載置させることは不可能である。そのために、読み
出しの際に、よくディジタルデータの誤読が生ずるとい
う問題が起る。更に、その上面には４つの凹部が存在す
るために、オフセット印刷を施すことができず、単にス
クリーン印刷に頼って図案を印刷している。そのため
に、印刷の仕上がりは悪く、視覚を通じて美感を起こさ
せることができないものとなる。また、前記名刺型ＣＤ
は、完全な円形をなすディスクからプレス加工により名
刺型形状に成形されたものであるため、ＣＤの外縁部に
は鋭いバリが形成されるので、使用上不便であるばかり
でなく、プレス成形の段階で内部に残留応力が存在する
ため、データの記録領域が損傷し、記録媒体としての依
頼性を失うという問題があった。However, since these four projections are formed by press working, it is difficult to press-mold their shapes and sizes with high precision, so that the business card type is formed only by these four projections. It is impossible to stably place a CD on a tray. For this reason, there is a problem that erroneous reading of digital data often occurs at the time of reading. Furthermore, since there are four recesses on the upper surface, offset printing cannot be performed, and the pattern is simply printed by screen printing. For this reason, the print quality is poor, and it is not possible to make the aesthetic appearance visible. In addition, the business card type CD
Is formed from a perfect circular disk into a business card shape by pressing, so that sharp burrs are formed on the outer edge of the CD, which is not only inconvenient in use but also in press forming. Since residual stress is present inside at the stage, there is a problem that the data recording area is damaged and the reliability as a recording medium is lost.

【０００７】[0007]

【課題を解決するための手段】本発明は、前記の問題点
に鑑みて提案されたもので、サイズは一般名刺のサイズ
ぐらいで、一般ＣＤ読み取り装置のサポート可能であ
り、携帯便利なサイズと形状を有し、一般名刺として代
替し得る外、ＣＤとしての記録媒体の機能を備え、大量
のデータ、例えば、カタログ、会社の概要紹介、個人の
履歴、または病歴等の記録媒体として使用することので
きる新規なＣＤである。さらに、本発明は、上部表面が
平坦で、スクリーン印刷またはオフセット印刷可能な表
面を有する新規な名刺型ＣＤの提供を目的とする。SUMMARY OF THE INVENTION The present invention has been proposed in view of the above problems, and has a size similar to that of a general business card, which can support a general CD reading device, and has a portable size. In addition to having a shape and being able to be replaced as a general business card, it has the function of a recording medium as a CD, and is used as a recording medium for a large amount of data, such as catalogs, company profile introductions, personal histories, medical histories This is a new CD that can be used. Another object of the present invention is to provide a new business card CD having a flat upper surface and a screen printable or offset printable surface.

【０００８】本発明は、下部表面に、一般のＣＤ読み取
り装置のトレーにおける直径８ｃｍの凹面部に係合させ
て載置するための円弧形の突起を有するＣＤであって、
これを一般のＣＤ読み取り装置のトレーにセットし、記
録してあるディジタルデータをレーザ光線によって読み
取れるようにした新規なＣＤのである。さらに、本発明
は、サイズが約８．５×５．５ｃｍであって、一般名刺
のサイズ９．０×５．５ｃｍより稍少さくして、名刺受
けまたは名刺入れに格納できるようにした名刺型ＣＤで
ある。According to the present invention, there is provided a CD having, on a lower surface thereof, an arc-shaped projection for engaging with a concave portion having a diameter of 8 cm in a tray of a general CD reader and mounting the same.
This is a new CD in which the digital data is set on a tray of a general CD reader so that recorded digital data can be read by a laser beam. Further, the present invention provides a business card type having a size of about 8.5 × 5.5 cm, which is slightly smaller than a general business card size of 9.0 × 5.5 cm, and which can be stored in a business card holder or a business card holder. It is a CD.

【０００９】さらに、本発明は、ＣＤの具えるデータ記
録領域が、直径約５ｃｍの円形領域に収まり、その記録
し得るデータの容量は、或はＣＤフォーマット仕様、例
えば、ＶＣＤまたはＣＤ‐ＲＯＭのフォーマット仕様の
場合では、約４０ＭＢ、其の他のＣＤフォーマット仕
様、例えば、ディジタル映像ディスク（ＤＶＤ）等の場
合、更に大量のデータを記録させることができる。さら
に、本発明は、ＣＤの具えるデータ記録領域が、個人的
データ、例えば、基本データ、学歴・経歴データ、また
は医療及び救急等の医療データ等を記録し、身につけて
携帯できる。Further, the present invention provides that a data recording area of a CD fits in a circular area having a diameter of about 5 cm, and the capacity of the recordable data is based on a CD format specification such as VCD or CD-ROM. In the case of the format specification, about 40 MB, and in the case of other CD format specifications, for example, a digital video disk (DVD), a larger amount of data can be recorded. Further, according to the present invention, the data recording area provided on the CD records personal data, for example, basic data, educational and career data, or medical data such as medical and emergency services, and can be worn and carried.

【００１０】さらに、本発明は、名刺型ＣＤの製造方法
を提供する。前記目的を達成するため、本発明の名刺型
ＣＤの製造方法は、基板と、金属膜層、保護層（パッシ
ベーション層）と印刷層とからなる名刺型ＣＤにおい
て、一体成形により、名刺ぐらいのサイズを有し、その
片方の表面に２つの円弧形屋根状突起を形成した基板を
成形し、他方の表面にディジタルデータを記録する凹凸
を形成するとともに、一体成形された前記基板に対し
て、位置センサ及び位置決め装置を適用して、自動的に
且つ正確に前記に成形された基板を次の金属膜層めっき
工程に移送するステップと、前記成形された基板のディ
ジタルデータを記録する凹凸の上に金属膜層をめっきす
るとともに、この金属膜層がめっきされた基板に対し
て、位置センサ及び位置決め装置を適用して、自動的に
且つ正確に前記に金属膜層めっきされた基板を次の保護
層塗布工程に移送するステップと、前記に金属膜層めっ
きされた基板の表面に保護層を塗布するとともに、この
保護層が塗布された基板に対して、位置センサ及び位置
決め装置を適用して、自動的に且つ正確に前記保護層が
塗布された基板を次の印刷工程に移送するステップと、
前記保護層が塗布されたその上に視覚図案を印刷するス
テップとを含むことを特徴とする。Further, the present invention provides a method for manufacturing a business card CD. In order to achieve the above object, a method for manufacturing a business card CD according to the present invention is directed to a business card CD comprising a substrate, a metal film layer, a protective layer (passivation layer), and a printing layer, which is formed into a business card size by integral molding. Having a substrate having two arc-shaped roof-like projections formed on one surface thereof, and forming irregularities for recording digital data on the other surface, with respect to the integrally molded substrate, Applying a position sensor and a positioning device to automatically and accurately transfer the formed substrate to a next metal film layer plating process; and A metal film layer is plated on the substrate, and a position sensor and a positioning device are applied to the substrate on which the metal film layer is plated, so that the metal film layer is automatically and accurately plated on the substrate. Transferring the substrate to the next protective layer coating step, applying a protective layer to the surface of the substrate plated with the metal film layer, and positioning the position sensor and the positioning device on the substrate coated with the protective layer. Automatically and accurately transferring the substrate coated with the protective layer to the next printing step,
Printing a visual pattern on the protective layer.

【００１１】さらに、本発明は、前記名刺型ＣＤの一体
成形された基板上に設けられた尾根状突起の傾斜面と前
記基板の下部表面のなす角度が約４０°〜５０°で、好
ましくは４５°である名刺型ＣＤの製造方法を提供する
を目的とする。さらに、本発明は、前記名刺型ＣＤの製
造方法において、前記基板は、ブラスチック材で一体に
成形する名刺型ＣＤの製造方法を提供する。さらに、本
発明は、前記名刺型ＣＤの製造方法において、前記名刺
型ＣＤの金属膜層の範囲が直径約５．０ｃｍの円形であ
る名刺型ＣＤの製造方法である。Further, the present invention provides the business card type CD, wherein the angle between the inclined surface of the ridge-like projection provided on the integrally formed substrate and the lower surface of the substrate is about 40 ° to 50 °, preferably It is an object of the present invention to provide a method for manufacturing a business card type CD at 45 °. Further, the present invention provides the method for manufacturing a business card CD, wherein the substrate is integrally molded with a plastic material. Furthermore, the present invention is the method for manufacturing a business card CD, wherein the metal film layer of the business card CD has a circular shape with a diameter of about 5.0 cm.

【００１２】本発明の名刺型ＣＤの製造方法によれば、
従来技術によって製造された円形ＣＤでは、方向性を持
たないため、製造に際しては、単にその円の中心に対す
る位置決めのみを必要とし、また、製造過程において
も、位置センサ、例えば、赤外線測距計も単にその円の
中心についてのみ検出、位置決めを行えば良い。然し、
本発明によって製造されるＣＤは、形状が名刺型、即ち
短冊形（矩形）であるので、それぞれのステップではす
べて位置センサ及び位置決め装置で、各工程においてそ
れぞれの位置検知と位置決めを行なって正確に位置決め
するようにされてある。According to the method for manufacturing a business card CD of the present invention,
In the case of a circular CD manufactured according to the prior art, which has no directionality, it is necessary only to position the center of the circle at the time of manufacturing. In the manufacturing process, a position sensor, for example, an infrared rangefinder is also used. It is sufficient to detect and position only the center of the circle. But
Since the CD manufactured according to the present invention has a business card shape, that is, a rectangular shape (rectangular shape), the position sensor and the positioning device are used in each step, and each position is detected and positioned in each step to accurately perform the processing. It is designed to be positioned.

【００１３】なお、本発明の名刺型ＣＤの製造方法にお
いて、基板としてポリメチルメタクレート（ＰＭＭ
Ａ）、ポリカーボネート（ＰＣ）、ＡＲＴＯＮ®
（ポリエステル類官能基を有するノルボルネン，主鎖：
ＮＯＲＢＯＲＮＥＮＥ,支鎖：官能基がポリエステル
類）を使用することができる。In the method of manufacturing a business card CD according to the present invention, polymethyl methacrylate (PMM) is used as a substrate.
A), polycarbonate (PC), ARTON ®
(Norbornene having polyester functional group, main chain:
NORBORNENE, supporting chain: functional group is polyester).

【００１４】また、本発明の名刺型ＣＤにおいて、一般
のＣＤ読み取り装置では、トレーに読み取りヘッドを通
すための中間開口が設けられてある。古いタイプのＣＤ
読み取り装置の場合、前記トレー上の中間開口は扇形を
なし且つ開口も大きくできているので、本発明の名刺型
ＣＤを適用した場合、この大きな中間開口にＣＤがはま
り込んで読み取りができなくなることがある。しかし、
最近市販されている通常のＣＤ読み取り装置では、前記
トレー上の中間開口は、矩形でしかも小さくなっている
ので本発明の名刺型ＣＤを適用しても問題は起らない。Further, in the business card type CD of the present invention, in a general CD reading device, an intermediate opening for passing a reading head through a tray is provided. Old type CD
In the case of the reading device, since the intermediate opening on the tray has a sector shape and the opening is made large, when the business card type CD of the present invention is applied, the CD is stuck in this large intermediate opening and reading becomes impossible. There is. But,
In an ordinary CD reader recently marketed, the middle opening on the tray is rectangular and small, so that no problem occurs even when the business card type CD of the present invention is applied.

【００１５】[0015]

【発明の実施の態様】図１(ａ)及び図１(ｂ)に本発明の
実施例に基づく名刺型ＣＤが示されている。ここで、図
１(ａ)は、本発明の名刺型ＣＤ１０を下方から見上げた
裏面の平面図である。この名刺型ＣＤ１０は、名刺ぐら
いのサイズを有する基板１３と、円弧形の尾根状突起１
５、及び金属膜層１７とその上に塗布された保護層１９
とから成る。そして、前記基板１７の上面に成形された
ディジタルデータを記録する凹凸及び前記金属膜層１７
とにより、前記ＣＤ１０内に例えば、文書、図案、音声
及び映像等を記録し、さらに、一般のＣＤ読み取り装置
によりレーザ光線を当て、その反射により凹凸を判別し
て読み取れるようになっている。図１(ｂ)は、本発明に
基づく実施例の縦断面図である。前記名刺型ＣＤは、細
長い矩形構造を有し、その下面には、前記基板から突出
した微小な尾根状の突起１５が設けられてある。また、
この名刺形ＣＤの厚みは、一般のＣＤの厚みより薄く、
衣服のポケット、または名刺入れ等一般に用いられる名
刺入れの内部に、従来の名刺同様に入れられるようにな
っている。FIG. 1A and FIG. 1B show a business card type CD according to an embodiment of the present invention. Here, FIG. 1A is a plan view of the back surface of the business card type CD 10 of the present invention as viewed from below. The business card type CD 10 includes a substrate 13 having a size of a business card and an arc-shaped ridge-like projection 1.
5, and the metal film layer 17 and the protective layer 19 applied thereon
Consisting of The unevenness for recording digital data formed on the upper surface of the substrate 17 and the metal film layer 17 are formed.
Thus, for example, a document, a design, a sound, an image, and the like are recorded in the CD 10, and further, a laser beam is applied by a general CD reading device, and irregularities are discriminated and read by the reflection. FIG. 1B is a longitudinal sectional view of an embodiment according to the present invention. The business card CD has an elongated rectangular structure, and a small ridge-like projection 15 protruding from the substrate is provided on the lower surface thereof. Also,
The thickness of this business card CD is thinner than that of a general CD,
A conventional business card can be inserted into a pocket of clothes or a commonly used business card holder such as a business card holder.

【００１６】一般のＣＤ読み取り装置のトレー５０に
は、通常直径１２ｃｍの凹形受け面５１と、この受け面
５１より低くした直径８ｃｍの凹形受け面５２とを有
し、この２つの受け面の間に後者の直径８ｃｍの凹形受
け面５２の垂直周縁内壁５４が形成されてある。そし
て、本発明にかかわる名刺型ＣＤ１０に設けられた前記
２条の円弧形尾根状突起１５を、このトレー５０上の直
径８ｃｍの凹形受け面５２（図４参照）の周縁内壁５４
と嵌合させて載置することで、前記名刺型ＣＤ１０を一
般のＣＤ読み取り装置のトレー５０にセットし、該ＣＤ
読み取り装置でレーザ光線により該名刺型ＣＤ１０に記
録されたディジタルデータを読み取らせることができ
る。前記の如く、本発明の名刺型ＣＤには、円弧形の尾
根状突起１５が設けられてあるので、この名刺型ＣＤを
安定よく一般のＣＤ読み取り装置のトレー５０における
直径８ｃｍの凹形受け面５２にセットすることができ
る。従って、該ＣＤ１０がトレー５０から離脱する虞れ
がなく、誤読を起す懸念もない。The tray 50 of a general CD reader has a concave receiving surface 51 having a diameter of 12 cm and a concave receiving surface 52 having a diameter of 8 cm lower than the receiving surface 51. A vertical peripheral inner wall 54 of the latter concave surface 52 having a diameter of 8 cm is formed therebetween. Then, the two arc-shaped ridge-shaped projections 15 provided on the business card type CD 10 according to the present invention are attached to the peripheral inner wall 54 of the 8 cm diameter concave receiving surface 52 (see FIG. 4) on the tray 50.
The business card type CD 10 is set on a tray 50 of a general CD reader by
Digital data recorded on the business card CD 10 can be read by a reading device using a laser beam. As described above, the business card-type CD of the present invention is provided with the arc-shaped ridge-like projections 15, so that the business card-type CD can be stably received in the tray 8 of a common CD reader with a diameter of 8 cm. It can be set on the surface 52. Therefore, there is no fear that the CD 10 will be detached from the tray 50, and there is no fear of causing erroneous reading.

【００１７】また、前記名刺型ＣＤ１０の尾根状突起１
５の傾斜面の、前記基板１３の下面に対する傾斜角β
（図２参照）は約４０°〜５０°の範囲である。より好
ましくは４５°である。これは、前記名刺型ＣＤ１０が
ＣＤ読み取り装置で読み取りの際に、高速回転させられ
るために、角度βが４０°未満では、不安定で偏り、角
度βが５０°以上では、大きな摩擦力が尾根状突起１５
に作用し、回転がスムーズに行かなくなって、誤読の原
因となるからである。The ridge 1 of the business card type CD 10
Of the inclined surface 5 with respect to the lower surface of the substrate 13
(See FIG. 2) ranges from about 40 ° to 50 °. More preferably, it is 45 °. This is because the business card-type CD 10 is rotated at a high speed when read by a CD reader, and is unstable and biased when the angle β is less than 40 °, and a large frictional force is generated when the angle β is 50 ° or more. Projection 15
This causes rotation to stop going smoothly and causes misreading.

【００１８】また、前記尾根状突起１５を基板１３の下
面より突出させて配置したため、前記基板１３の下部表
面におけるデータ面は、前記名刺型ＣＤ１０を机の上に
置いたり、または名刺入れに格納した場合に、直接これ
らのものと接触することがないので、基板１３のデータ
面を完全な状態に保持することができるとともに、前記
名刺型ＣＤ内部に記録されたデータを保護することがで
きる。Also, since the ridge-like projections 15 are arranged so as to protrude from the lower surface of the substrate 13, the data surface on the lower surface of the substrate 13 can be stored on the desk or the business card type CD10. In this case, there is no direct contact with these elements, so that the data surface of the substrate 13 can be kept in a perfect state and the data recorded inside the business card CD can be protected.

【００１９】また、前記名刺型ＣＤ１０において、デー
タを記録した金属膜層１７が直径５ｃｍの円形であるこ
とは、前記名刺型ＣＤ１０における其の他の周縁部分が
基板１３となるプラスチック層１３のままであることを
意味するので、保持する場合は、指でこの部分を摘め
ば、前記名刺型ＣＤにおけるデータ記録面である金属膜
層１７の外部表面の指による損傷を回避することができ
る。従って、金属膜層１７の清潔と美感を保つことがで
きるとともに、記録されたディジタルデータを完全に保
存することができる。In the business card-type CD 10, the metal film layer 17 on which data is recorded has a circular shape with a diameter of 5 cm, which means that the other peripheral portion of the business card-type CD 10 remains as the plastic layer 13 serving as the substrate 13. In the case of holding, by holding this portion with a finger, damage to the external surface of the metal film layer 17 which is the data recording surface of the business card CD by the finger can be avoided. Therefore, the cleanliness and beauty of the metal film layer 17 can be maintained, and the recorded digital data can be completely preserved.

【００２０】しかし、本発明の其他の実施例（図示せ
ず）として、前記名刺型ＣＤにおける金属膜層は、基板
全体の表面を被覆するように形成することができる。こ
の場合は、本発明の名刺型ＣＤ自体の機能を損なうこと
なく、異なる視覚美感を有する名刺型ＣＤを提供するこ
とができる。However, as another embodiment (not shown) of the present invention, the metal film layer in the business card type CD can be formed so as to cover the entire surface of the substrate. In this case, a business card CD having a different visual aesthetic can be provided without impairing the function of the business card CD itself of the present invention.

【００２１】次に、本発明の名刺型ＣＤの製造方法につ
いて説明する。図３に、本発明の名刺型ＣＤの製造方法
によって製造された名刺型ＣＤを示す分解斜視図であ
る。製造工程の順序に従って下方より上方へと組合わさ
れて行く順序を示している。即ち、本発明では：先ず、
一体成形により、名刺ぐらいのサイズを有し、その片方
の表面に２条の円弧形尾根状突起１５を形成した基板１
３を成形し、他方の表面において直径５ｃｍの円形範囲
内にディジタルデータの凹凸を形成するとともに、一体
成形された前記基板１３に対して、位置センサ及び位置
決め装置を適用して、自動的に且つ正確に前記成形され
た基板１３を次の金属膜層めっき工程に移送するステッ
プを経て；さらに、前記成形された基板１３上における
の直径５ｃｍの円上に成形されたディジタルデータの凹
凸１４の上に、金属膜層１７をめっきするとともに、こ
の金属膜層１７がめっきされた基板１３に対して、位置
センサ及び位置決め装置を適用して、自動的に且つ正確
に前記金属膜層１７がめっきされた基板を次の保護層塗
布工程に移送するステップと；前記金属膜層１７がめっ
きされた基板１３の表面に保護層１９を塗布するととも
に、位置センサ及び４点の幾何学的ＸＹ座標に位置でき
る位置決め装置を適用して、自動的に且つ正確に前記保
護層が塗布された１９の基板１３を次の印刷工程に移送
するステップと；及び、前記保護層が塗布されたその上
に視覚図案２０を印刷するステップを経て、本発明の名
刺型ＣＤが製造される。Next, a method of manufacturing a business card CD according to the present invention will be described. FIG. 3 is an exploded perspective view showing a business card CD manufactured by the method for manufacturing a business card CD of the present invention. The order in which the components are combined upward from below according to the order of the manufacturing process is shown. That is, in the present invention:
A substrate 1 having a size of a business card by integral molding and having two arc-shaped ridge-like projections 15 formed on one surface thereof.
3 is formed, digital data irregularities are formed in a circular area having a diameter of 5 cm on the other surface, and a position sensor and a positioning device are applied to the integrally formed substrate 13 to automatically and automatically. Transferring the formed substrate 13 to the next metal film layer plating process accurately; and furthermore, on the formed substrate 13, on the digital data unevenness 14 formed on a 5 cm diameter circle. Next, the metal film layer 17 is plated, and a position sensor and a positioning device are applied to the substrate 13 on which the metal film layer 17 is plated, so that the metal film layer 17 is automatically and accurately plated. Transferring the substrate to the next protective layer coating step; applying a protective layer 19 on the surface of the substrate 13 on which the metal film layer 17 is plated, Automatically and accurately transferring the nineteen substrates 13 coated with the protective layer to a next printing process by applying a positioning device capable of positioning at four geometric XY coordinates; and The business card type CD of the present invention is manufactured through the step of printing the visual design 20 on the coated layer.

【００２２】ここで、本発明による名刺型ＣＤ１０の円
弧形尾根状突起１５と前記基板１３は、一体成形された
ものであり、さらに、前記円弧形尾根状突起１５は、名
刺型ＣＤを製造する際に、一般によく採用されるダイキ
ャスト法やプレス加工法によって製造されたものとは異
なる。Here, the arc-shaped ridge-shaped projection 15 of the business card-type CD 10 according to the present invention and the substrate 13 are integrally formed. At the time of manufacture, it is different from that manufactured by a die casting method or a press working method which is generally adopted.

【００２３】さらに、基板１３と尾根状突起１５は、製
造の過程において一体に成形され、名刺型ＣＤの外形形
状は、周知の円形とは異なり矩形であって円形ではない
ため、金属膜層形成工程、保護層成形工程及び印刷工程
の何れを問わずすべてが方向性を有する矩形の状態にあ
るため、それぞれの工程において、名刺型ＣＤの方向性
について、バランスと高速回転時のモーメント分布を考
慮すべきである。そのために、本発明の名刺型ＣＤで
は、それぞれのステップにおいて位置センサと位置決め
装置を適用する。また、前記名刺型ＣＤ１０の下部また
はデータ面に金属膜層を形成する工程において、前記基
板１０は預め成形されてあるために、本発明の製造方法
によれば、図１に示すように、単なるマスクの修正のみ
で容易に直径５ｃｍの区域にのみ金属膜層を形成するこ
とができる。Further, the substrate 13 and the ridge-like projections 15 are integrally formed during the manufacturing process, and since the external shape of the business card CD is rectangular and not circular unlike a known circle, the metal film layer is formed. Regardless of the process, protective layer molding process, and printing process, all are in a rectangular state with directionality, so in each process, the balance of the business card CD and the moment distribution during high-speed rotation are considered. Should. Therefore, in the business card type CD of the present invention, a position sensor and a positioning device are applied in each step. In addition, in the step of forming a metal film layer on the lower portion or the data surface of the business card type CD 10, the substrate 10 is deposited and formed. Therefore, according to the manufacturing method of the present invention, as shown in FIG. The metal film layer can be easily formed only in the area having a diameter of 5 cm by simply modifying the mask.

【００２４】本発明の名刺型ＣＤのデータ面に形成され
る金属膜層領域は、約直径５ｃｍの円形である。これに
或る形式のフォーマッティング、例えばＶＣＤまたはＣ
Ｄ−ＲＯＭのフォーマット仕様を行なうと、記録し得る
ディジタルデータの容量が約４０ＭＢである。また、其
他の形式のフォーマットティング、例えばディジタル映
像（ＤＶＤ）等のフォーマット仕様の場合は、さらに、
大量のデータ記録させることができる。これらの技術は
公知である。また、印刷の過程では、名刺型ＣＤは矩形
であって幾何学的に完全な対称形ではなく、方向性を有
しているので、正確な位置決めがなされてこそ、始めて
予期通りの印刷品質が得られる。また、印刷の過程で
は、前記名刺型ＣＤは、上面部または印刷面部が平坦な
面であるため、スクリーン印刷法またはオフセット印刷
法を採用することができる。The metal film layer region formed on the data surface of the business card CD of the present invention is a circle having a diameter of about 5 cm. This has some form of formatting, such as VCD or C
According to the format specification of the D-ROM, the capacity of recordable digital data is about 40 MB. Further, in the case of a format specification of another format, for example, a format specification such as digital video (DVD),
A large amount of data can be recorded. These techniques are well-known. Also, in the printing process, the business card CD is rectangular and not perfectly geometrically symmetrical, but has a directivity. Therefore, the printing quality as expected only after accurate positioning is achieved. can get. In the printing process, the business card CD has a flat top surface or a flat printed surface, so that a screen printing method or an offset printing method can be employed.

【００２５】ここで注意すべきことは、前記本発明の実
施例は、あくまで範例として示したものであって、本発
明はこれらの実施例に限定されるものではなく、これら
の技術に熟知した者なら、本発明の要旨及び範囲逸脱す
ることなく、容易に変形または修正することができる。It should be noted that the above-described embodiments of the present invention are merely examples, and the present invention is not limited to these embodiments. Those skilled in the art can easily make changes or modifications without departing from the spirit and scope of the present invention.

【図面の簡単な説明】[Brief description of the drawings]

【図１】図１(ａ)は、本発明の名刺型ＣＤの裏面を示す
平面図である。図１(ｂ)は、図１(ａ)に示す名刺型ＣＤ
の縦方向断面図である。FIG. 1 (a) is a plan view showing the back surface of a business card CD of the present invention. FIG. 1B shows a business card type CD shown in FIG.
FIG.

【図２】図２は、図１(ｂ)に示すＢ部分の拡大図であ
る。FIG. 2 is an enlarged view of a portion B shown in FIG. 1 (b).

【図３】 図３は、本発明の名刺型ＣＤの製造方法によ
って製造された名刺型ＣＤを示す分解斜視図である。製
造工程の順序に従って下方より上方へと組合わされて行
く順序を示している。FIG. 3 is an exploded perspective view showing a business card CD manufactured by the method for manufacturing a business card CD according to the present invention. The order in which the components are combined upward from below according to the order of the manufacturing process is shown.

【図４】 図４は、本発明の名刺型ＣＤとＣＤ読み取り
装置のトレー上に載置した様子を説明するための図であ
る。名刺型ＣＤの２条の円弧形尾根状突起全体が、これ
と対応するＣＤ読み取り装置のトレーにおける円弧の内
周壁に嵌合載置されている。FIG. 4 is a diagram for explaining a business card type CD and a state of being placed on a tray of a CD reader according to the present invention. The entire two arc-shaped ridge-shaped protrusions of the business card CD are fitted and mounted on the inner peripheral wall of the arc in the tray of the CD reader corresponding thereto.

【図５】 図５は、従来の技術による取り引きカードで
あるＣＤと、ＣＤ読み取り装置におけるトレーの嵌合載
置の様子を説明するための図である。この場合のＣＤ
は、その高く盛り上げた部分でＣＤ読み取り装置のトレ
ーに嵌合載置されている。FIG. 5 is a diagram for explaining a CD which is a transaction card according to a conventional technique, and how a tray is fitted and mounted in a CD reader. CD in this case
Is fitted and mounted on a tray of a CD reader at the raised portion.

【符号の説明】[Explanation of symbols]

１０ 名刺型ＣＤ １３ 基板 １４ ディジタルデータを記録する凹凸 １５ 円弧形尾根状突起 １７ 金属膜層 １９ 保護層 ２０ 図案 ２１ 突出部 ５０ トレー ５１ 凹形受け面（直径１２ｃｍ） ５２ 凹形受け面（直径８ｃｍ） ５４ 受け面の垂直周縁内壁 DESCRIPTION OF SYMBOLS 10 Business card type CD 13 Substrate 14 Concavo-convex for recording digital data 15 Arc-shaped ridge 17 Metal film layer 19 Protective layer 20 Design 21 Projection 50 Tray 51 Concave receiving surface (diameter 12 cm) 52 Concave receiving surface (diameter) 8cm) 54 Vertical peripheral inner wall of receiving surface

Claims (16)

【特許請求の範囲】[Claims] 【請求項１】下部表面に、一般のＣＤ読み取り装置のト
レーにおける直径８ｃｍの凹面部に嵌合させて載置する
ための円弧形の尾根状突起を有するＣＤであって、これ
を一般のＣＤ読み取り装置のトレーにセットし、記録し
てあるディジタルデータをレーザ光線によって読み取れ
るようにしたことを特徴とする名刺型ＣＤ。1. A CD having, on a lower surface thereof, an arc-shaped ridge-like projection for fitting and mounting on a concave portion having a diameter of 8 cm in a tray of a general CD reader. A business card type CD, wherein digital data set on a tray of a CD reader is read by a laser beam. 【請求項２】前記名刺型ＣＤの基板の下部表面における
円弧形の尾根状突起の傾斜面と前記基板の下部表面のな
す角度が約４０°〜５０°であることを特徴とする請求
項１記載の名刺型ＣＤ。2. An angle between an inclined surface of an arc-shaped ridge-like projection on a lower surface of a substrate of the business card type CD and a lower surface of the substrate is about 40 ° to 50 °. The business card type CD according to 1. 【請求項３】前記名刺型ＣＤの基板の下部表面における
円弧形の尾根状突起の傾斜面と前記基板の下部表面のな
す角度が約４５°であることを特徴とする請求項２記載
の名刺型ＣＤ。3. The card according to claim 2, wherein the angle formed between the inclined surface of the arc-shaped ridge on the lower surface of the substrate of the business card type CD and the lower surface of the substrate is about 45 °. Business card type CD. 【請求項４】前記名刺型ＣＤのサイズが８．５×５．５
ｃｍで、名刺受けや名刺入れに収納できるようにしたこ
とを特徴とする請求項１記載の名刺型ＣＤ。4. The size of the business card type CD is 8.5 × 5.5.
The business card type CD according to claim 1, wherein the business card type CD can be stored in a business card holder or a business card holder in cm. 【請求項５】前記名刺型ＣＤの中央の直径約５ｃｍの円
形領域をディジタルデータ記録領域としたことを特徴と
する請求項１記載の名刺型ＣＤ。5. The business card-type CD according to claim 1, wherein a circular area having a diameter of about 5 cm at the center of the business card-type CD is used as a digital data recording area. 【請求項６】前記ディジタルデータ記録領域のディジタ
ルデータフォーマット仕様がＶＣＤまたはＣＤ−ＲＯＭ
のフォーマット仕様であって、記録可能なデータの容量
が約４０ＭＢであることを特徴とする請求項５記載の名
刺型ＣＤ。6. The digital data recording area has a digital data format specification of VCD or CD-ROM.
6. The business card type CD according to claim 5, wherein a format of the data is about 40 MB. 【請求項７】前記データ記録領域のディジタルデータフ
ォーマット仕様がＤＶＤのフォーマット仕様であること
を特徴とする請求項５記載の名刺型ＣＤ。7. The business card type CD according to claim 5, wherein the digital data format specification of the data recording area is a DVD format specification. 【請求項８】前記データ記録領域は、個人基本データ、
学歴・経歴データ及び医療データを記録させることがで
きることを特徴とする請求項５記載の名刺型ＣＤ。8. The data recording area includes personal basic data,
6. The business card-type CD according to claim 5, wherein the educational / history data and medical data can be recorded. 【請求項９】基板と、金属膜層と、保護層、及び印刷層
とからなる名刺型ＣＤの製造方法において、 一体成形により、名刺ぐらいのサイズを有し、その片方
の表面に２条の円弧形尾根状突起を形成した基板を成形
し、他方の表面にディジタルデータを記録する凹凸を形
成するとともに、一体成形された前記基板に対して、位
置センサ及び位置決め装置を適用して、自動的に且つ正
確に前記成形された基板を次の金属膜層めっき工程に移
送するステップと、 前記成形された基板のディジタルデータを記録する凹凸
の上に金属膜層をめっきするとともに、この金属膜層が
めっきされた基板に対して、位置センサ及び位置決め装
置を適用して、自動的に且つ正確に前記金属膜層がめっ
きされた基板を次の保護層塗布工程に移送するステップ
と、 前記金属膜層がめっきされた基板の表面に保護層を塗布
するとともに、この保護層が塗布された基板に対して、
位置センサ及び位置決め装置を適用して、自動的に且つ
正確に前記保護層が塗布された基板を次の印刷工程に移
送するステップと、 前記保護層が塗布されたその上に視覚図案を印刷するス
テップを含むことを特徴とする名刺型ＣＤの製造方法。9. A method for manufacturing a business card type CD comprising a substrate, a metal film layer, a protective layer, and a printing layer, the method comprising: integrally forming a business card type CD having a size similar to a business card; Forming a substrate on which an arc-shaped ridge is formed, forming irregularities for recording digital data on the other surface, and applying a position sensor and a positioning device to the integrally formed substrate, Transferring the formed substrate to the next metal film layer plating step in an accurate and accurate manner; and plating the metal film layer on the irregularities for recording digital data of the formed substrate, Applying a position sensor and a positioning device to the substrate on which the layer has been plated, and automatically and accurately transferring the substrate on which the metal film layer has been plated to the next protective layer application step; With applying a protective layer on the surface of the substrate on which the metal film layer is plated, the substrate of the protective layer is applied,
Automatically and accurately transferring the substrate coated with the protective layer to the next printing process by applying a position sensor and a positioning device, and printing a visual pattern on the substrate coated with the protective layer A method for manufacturing a business card type CD, comprising steps. 【請求項１０】前記名刺型ＣＤの一体成形された基板上
に前記の如き尾根状突起を有することを特徴とする請求
項９記載の名刺型ＣＤの製造方法。10. The method of manufacturing a business card CD according to claim 9, wherein said ridge-shaped projection is provided on a substrate formed integrally with said business card CD. 【請求項１１】前記名刺型ＣＤの基板の下部表面におけ
る円弧形の尾根状突起の傾斜面と前記基板の下部表面の
なす角度が約４０°〜５０°であることを特徴とする請
求項１０記載の名刺型ＣＤの製造方法。11. An angle between an inclined surface of an arc-shaped ridge-like projection on a lower surface of the substrate of the business card CD and a lower surface of the substrate is about 40 ° to 50 °. 10. The method for producing a business card CD according to 10. 【請求項１２】前記名刺型ＣＤの下部表面における円弧
形の尾根状突起の傾斜面と前記基板の下部表面のなす角
度が約４５°であることを特徴とする請求項１１記載の
名刺型ＣＤの製造方法。12. The business card type according to claim 11, wherein the angle between the inclined surface of the arc-shaped ridge-like projection on the lower surface of the business card type CD and the lower surface of the substrate is about 45 °. CD manufacturing method. 【請求項１３】前記名刺型ＣＤの基板材質がポリカーボ
ネート（ＰＣ）であることを特徴とする請求項９記載の
名刺型ＣＤの製造方法。13. The method of manufacturing a business card CD according to claim 9, wherein the substrate material of the business card CD is polycarbonate (PC). 【請求項１４】前記名刺型ＣＤの基板材質がポリメチル
メタクリレート（ＰＭＭＡ）であることを特徴とする請
求項９記載の名刺型ＣＤの製造方法。14. The method for manufacturing a business card CD according to claim 9, wherein the substrate material of the business card CD is polymethyl methacrylate (PMMA). 【請求項１５】前記名刺型ＣＤの基板材質がＡＲＴＯＮ
®（ポリエステル類官能基を有するノルボルネン，
主鎖：ＮＯＲＢＯＲＮＥＮＥ,支鎖：官能基がポリエス
テル類）であることを特徴とする請求項９記載の名刺型
ＣＤの製造方法。15. The business card type CD has a substrate material of ARTON.
® (norbornene having polyester functional groups,
10. The method for producing a business card CD according to claim 9, wherein the main chain is NORBORNENE, and the branch chain is a functional group of polyesters. 【請求項１６】前記名刺型ＣＤの金属膜層の範囲が約５
ｃｍの円形であることを特徴とする請求項９記載の名刺
型ＣＤの製造方法。16. The business card type CD has a metal film layer of about 5
The method for producing a business card type CD according to claim 9, wherein the business card type CD is circular.