JP2001136843A - Lining material of green house for agriculture - Google Patents
Lining material of green house for agricultureInfo
- Publication number
- JP2001136843A JP2001136843A JP32183299A JP32183299A JP2001136843A JP 2001136843 A JP2001136843 A JP 2001136843A JP 32183299 A JP32183299 A JP 32183299A JP 32183299 A JP32183299 A JP 32183299A JP 2001136843 A JP2001136843 A JP 2001136843A
- Authority
- JP
- Japan
- Prior art keywords
- lining material
- tape
- light
- house
- woven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、農業用ハウスの内
部に展張するシート体であり、遮光、遮熱、保温、防霧
を目的として使用される農業用ハウスの内張り材に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a sheet body that is spread inside an agricultural house, and relates to a lining material for an agricultural house used for shading, heat shielding, heat insulation, and fog prevention.
【０００２】[0002]
【従来の技術】従来、果物や花卉などの栽培において、
促成栽培や防寒、防霜を目的として、ポリ塩化ビニル、
ポリエチレン、エチレン−酢酸ビニル共重合体などの被
覆材を外側に被覆したいわゆるハウス栽培が広く行われ
ている。しかし、この種の被覆材を被覆した農業用ハウ
スは、赤外線の透過率が大きいため昼間の温度上昇が大
きすぎる傾向にあり、たとえ低温期であっても農作物の
生育適温を超えることがあり、また、夜間には放射冷却
により温度が低下しすぎるという問題があり、このよう
な問題に対処する方法として、ハウス内において遮光性
および保温性を備えた内張り材を展張するケースが多
い。2. Description of the Related Art Conventionally, in the cultivation of fruits and flowers,
For the purpose of forcing cultivation, cold protection and frost protection, polyvinyl chloride,
So-called house cultivation in which a coating material such as polyethylene or ethylene-vinyl acetate copolymer is coated on the outside has been widely performed. However, agricultural houses coated with this type of coating material tend to have too large a daytime temperature rise because of high infrared transmittance, and even in a low temperature period, the temperature may exceed the optimum temperature for growing crops. In addition, there is a problem that the temperature is excessively lowered by radiant cooling at night, and as a method for dealing with such a problem, a lining material having a light-shielding property and a heat retaining property is often spread in a house.
【０００３】そして、ハウスの被覆材に用いられる上記
ポリ塩化ビニル、ポリエチレン、エチレン−酢酸ビニル
共重合体などには、被覆材の表面張力を低下させる界面
活性剤が添加されて、いわゆる防曇性が一般的に付与さ
れており、ハウス内の水分が結露して生じる水滴が被覆
材内面に沿って流れ落ちるようにしているが、冬季に限
らず夏季の早朝など急激に気温が低下してハウス内外の
温度差が大きくなるなどの気象条件とハウス内の湿度な
どが関連して、被覆材に結露しきれない水分が霧となっ
て空中に拡散する現象がみられる。このように発生した
霧は、ハウス内で栽培中の果物や花卉を濡らして損傷す
る原因となり、また、霧のためハウス内の視界が低下し
て作業に支障をきたすなどの問題があった。[0003] To the above-mentioned polyvinyl chloride, polyethylene, ethylene-vinyl acetate copolymer and the like used for the coating material of the house, a surfactant for reducing the surface tension of the coating material is added, so-called antifogging property. Is generally applied, so that water droplets generated by condensation of water in the house flow down along the inner surface of the coating material.However, not only in winter but also in the early morning of summer, the temperature suddenly drops and the inside and outside of the house Due to weather conditions, such as a large temperature difference, and the humidity in the house, there is a phenomenon in which moisture that cannot be dewed on the coating material diffuses into the air as fog. The fog generated in this manner causes the fruits and flowers cultivated in the house to be wet and damaged, and the fog lowers the visibility in the house and hinders the work.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、上記事情に
鑑み、遮光性、保温性を備え、かつ防霧性にすぐれた農
業用ハウスの内張り材を提供することを目的とする。SUMMARY OF THE INVENTION In view of the above circumstances, an object of the present invention is to provide a lining material for an agricultural house having a light-shielding property, a heat-retaining property and an excellent anti-fog property.
【０００５】[0005]
【課題を解決するための手段】本発明は、上記の目的を
達成するためになされたもので、合成樹脂の長繊維フィ
ラメントが高密度にかつ無方向に堆積接合された不織布
を細幅にスリットした遮光性テープおよび３０℃、６５
％ＲＨでの吸湿率が５％以上の吸湿性テープを経糸に、
他の合成繊維を緯糸に用いた織布からなることを特徴と
する農業用ハウスの内張り材を提供して、上記課題を解
消する。DISCLOSURE OF THE INVENTION The present invention has been made to achieve the above-mentioned object, and a non-woven fabric in which synthetic resin long fiber filaments are densely and non-directionally deposited and bonded is slit into a narrow width. Light-shielding tape and 30 ° C, 65
% RH at 5% or more moisture-absorbing tape to warp,
An object of the present invention is to solve the above problem by providing a lining material for an agricultural house, which is made of a woven fabric using other synthetic fibers for the weft.
【０００６】[0006]
【発明の実施の形態】以下、本発明を詳細に説明する。
本発明において、遮光性テープに用いられる不織布は合
成樹脂としてポリオレフィンの他、ポリエステル、ポリ
アミドなどが用いられ、これら合成樹脂よりなるフィラ
メント形状の長繊維で構成される必要がある。長繊維か
らなる不織布は、繊維長がｃｍ或いはｍｍ単位のステー
プル形状の短繊維からなる不織布に比べて表面の摩擦抵
抗性にすぐれるため、耐久性にすぐれハウス用内張り材
として好適に使用されるからである。不織布の坪量とし
ては、３０〜２００ｇ／ｍ２が好ましく、坪量３０ｇ／
ｍ２未満であると機械的強度が著しく低下し、部分的な
強度差が大きく、テープ状の糸条として生産効率が悪化
する。一方２００ｇ／ｍ２を超えると重量が増加し柔軟
性に劣り取扱い性が困難となり好ましくない。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail.
In the present invention, the nonwoven fabric used for the light-shielding tape uses polyester, polyamide, or the like in addition to polyolefin as a synthetic resin, and needs to be composed of filament-shaped long fibers made of these synthetic resins. Non-woven fabrics made of long fibers have excellent surface friction resistance compared to non-woven fabrics made of staple-shaped short fibers having a fiber length of cm or mm, and therefore have excellent durability and are preferably used as a lining material for a house. Because. The nonwoven fabric preferably has a basis weight of 30 to 200 g / m 2 , and a basis weight of 30 g / m 2.
mechanical strength is remarkably lowered to be less than m 2, partial intensity difference is large, the production efficiency is deteriorated as a tape-like yarn. On the other hand, if it exceeds 200 g / m 2 , the weight increases, the flexibility becomes poor, and the handling becomes difficult.
【０００７】上記不織布は、紡糸、延伸、開繊、接着の
工程を連続的に行なう直接紡糸法により、長繊維委をラ
ンダムに堆積しボンディングして得られるものであり、
具体的には、紡糸可能な熱可塑性樹脂を押出機にて溶融
し、紡糸ノズルから押出された繊維をローラー法または
エアジェット法で延伸繊維化するスパンボンド法による
不織布や、溶融樹脂を高圧ガス流とともに紡糸ノズルか
ら噴射して延伸繊維化するメルトブロー法による不織布
や、紡糸可能な熱可塑性樹脂を溶媒に高温高圧下に熔解
した溶液を紡糸ノズルを通して大気中に放出し、溶媒を
気化させて繊維化するフラッシュ紡糸法による不織布な
どが挙げられるが、高強力を有し遮光性テープとしての
取扱い性が良好な点でフラッシュ紡糸法による不織布が
特に好適である。The nonwoven fabric is obtained by randomly depositing and bonding long fibers by a direct spinning method in which spinning, drawing, opening, and bonding steps are continuously performed.
Specifically, a non-woven fabric by a spun bond method in which a spinnable thermoplastic resin is melted by an extruder and the fiber extruded from a spinning nozzle is drawn into a fiber by a roller method or an air jet method, or a molten resin is converted into a high-pressure gas. Non-woven fabric by the melt-blowing method, which is sprayed from the spinning nozzle together with the flow to form drawn fiber, or a solution obtained by dissolving a spinnable thermoplastic resin in a solvent under high temperature and high pressure, is released into the atmosphere through the spinning nozzle, and the solvent is vaporized. Non-woven fabrics formed by the flash spinning method can be used, but non-woven fabrics formed by the flash spinning method are particularly preferable because they have high strength and are easy to handle as a light-shielding tape.
【０００８】フラッシュ紡糸法は、高密度ポリエチレン
やポリプロピレンなどの合成樹脂をハロゲン化炭化水
素、芳香族炭化水素、脂肪族炭化水素などの低沸点の溶
媒に高温高圧下に溶解して得た溶液を用い、より加圧し
た状態で圧力降下室を設けた紡糸ノズルを通して低温低
圧域の大気中に放出し、溶媒が瞬間的に気化することで
その膨張力によって繊維に配向を与えたものであるか
ら、単糸繊度が０.１〜０.３ｄｒ程度の極細で高強力な
繊維が形成され、この繊維を交差させながら堆積して熱
圧着して得られる不織布は、高密度に接合した緻密な構
造を有する。In the flash spinning method, a solution obtained by dissolving a synthetic resin such as high-density polyethylene or polypropylene in a solvent having a low boiling point such as a halogenated hydrocarbon, an aromatic hydrocarbon, or an aliphatic hydrocarbon under high temperature and high pressure is used. It is released into the atmosphere at low temperature and low pressure through a spinning nozzle equipped with a pressure drop chamber in a more pressurized state, and the solvent evaporates instantaneously, giving the fiber orientation by its expansion force. An ultrafine and high-strength fiber having a single-fiber fineness of about 0.1 to 0.3 dr is formed. The nonwoven fabric obtained by depositing the fibers while intersecting and thermocompression bonding has a dense structure bonded at a high density. Having.
【０００９】この不織布は、長繊維を高密度に堆積接合
したものであるから、不透明性で白化度が高いものであ
るが、光に対する分光特性として、光吸収率５％以下で
あるものが好ましい。即ち、遮光性テープの構成部材と
して、光吸収率が５％以下と低いことで、不織布自体が
蓄熱することが少なく、遮光性テープで覆われた内部の
異常な昇温を抑制できるのである。This non-woven fabric is formed by depositing and joining long fibers at a high density, so that it is opaque and has a high degree of whitening. However, it is preferable that the non-woven fabric has a light absorption rate of 5% or less as a light spectral characteristic. . That is, since the light absorptivity as a constituent member of the light-shielding tape is as low as 5% or less, the nonwoven fabric itself is less likely to accumulate heat, and an abnormal rise in temperature of the inside covered with the light-shielding tape can be suppressed.
【００１０】不織布は、溝付きロールまたは２本のガイ
ドロール間で、カッタ刃または丸刃により所定の幅に合
わせて多数本にスリットすることで遮光性テープとす
る。スリット幅としては２〜３０ｍｍ幅、好ましくは４
〜２０ｍｍ幅である。２ｍｍより小さいと遮光性テープ
及びネット構造物としての取扱い上の強度及び実用的な
強度が不十分なものとなる。一方、３０ｍｍより大きい
と織成の効率が著しく悪化し、実用上取扱い難いものと
なる。The non-woven fabric is formed into a light-shielding tape by slitting a large number of grooves between a grooved roll or two guide rolls with a cutter blade or a round blade to a predetermined width. The slit width is 2 to 30 mm width, preferably 4
幅 20 mm width. If it is smaller than 2 mm, the handling strength and practical strength as a light-shielding tape and a net structure become insufficient. On the other hand, when it is larger than 30 mm, the weaving efficiency is remarkably deteriorated, and it is practically difficult to handle.
【００１１】次に、本発明において用いる吸湿性テープ
は、３０℃、６５％ＲＨでの吸湿率が５％以上であるこ
とが必要であり、これより吸湿率が低いと本発明の目的
を達成することが困難となる。３０℃、６５％ＲＨでの
吸湿率は好ましくは１０％以上、より好ましくは１５％
以上である。Next, the moisture-absorbing tape used in the present invention must have a moisture absorption of 5% or more at 30 ° C. and 65% RH. If the moisture absorption is lower than this, the object of the present invention is achieved. It will be difficult to do. The moisture absorption at 30 ° C. and 65% RH is preferably 10% or more, more preferably 15%.
That is all.
【００１２】吸湿性テープに用いられる素材としては、
親水性素材であるポリビニルアルコール、ポリアクリロ
ニトリル、レーヨンなどが挙げられ、吸湿性テープとし
ては、これら素材からなるフィルムまたは不織布を細断
したテープが挙げられる。これらのうちでは、ポリビニ
ルアルコールからなるフィルムを細断して形成したテー
プが最も好ましい。Materials used for the hygroscopic tape include:
Examples include hydrophilic materials such as polyvinyl alcohol, polyacrylonitrile, and rayon. Examples of the hygroscopic tape include tapes obtained by shredding a film or nonwoven fabric made of these materials. Among these, a tape formed by shredding a film made of polyvinyl alcohol is most preferable.
【００１３】上記ポリビニルアルコールとは、ポリビニ
ルアルコール１００重量％であるもの、またはビニルア
ルコールとエチレンなどの他のモノマーとの共重合体、
あるいはそれらのブレンド物を包含するものである。The above-mentioned polyvinyl alcohol is 100% by weight of polyvinyl alcohol, or a copolymer of vinyl alcohol and another monomer such as ethylene,
Alternatively, it includes a blend thereof.
【００１４】上記ポリビニルアルコール、ポリアクリロ
ニトリルを用いて溶融押出法にて容易にフィルムを形成
することができる。また、ビスコースレーヨンを凝固液
中に押し出してフィルム化したセロハンも吸湿性テープ
として好適に用いることができる。A film can be easily formed by a melt extrusion method using the above-mentioned polyvinyl alcohol and polyacrylonitrile. Cellophane formed by extruding viscose rayon into a coagulating liquid to form a film can also be suitably used as a hygroscopic tape.
【００１５】上記ポリビニルアルコール、ポリアクリロ
ニトリル、レーヨンからなる不織布の製造方法として
は、繊度が１〜１０デニールの繊維を公知のニードルパ
ンチ法、スパンレース法、メルトブロー法、スパンボン
ド法等により交絡結合して得ることができる。As a method for producing a non-woven fabric comprising the above-mentioned polyvinyl alcohol, polyacrylonitrile and rayon, a fiber having a fineness of 1 to 10 denier is entangled by a known needle punching method, a spunlace method, a melt blow method, a spun bond method or the like. Can be obtained.
【００１６】上記親水性素材からなるフィルムまたは不
織布は、溝付きロールまたは２本のガイドロール間で、
カッタ刃または丸刃により所定の幅に合わせて多数本に
スリットして吸湿性テープとする。スリット幅としては
２〜３０ｍｍ幅、好ましくは４〜２０ｍｍ幅である。吸
湿性テープ幅は、遮光性テープ幅とほぼ同等であると、
外観上、または織成効率上好ましい。The film or nonwoven fabric made of the hydrophilic material is provided between a grooved roll or two guide rolls.
It is slit into a large number of pieces in accordance with a predetermined width by a cutter blade or a round blade to form a hygroscopic tape. The width of the slit is 2 to 30 mm, preferably 4 to 20 mm. When the hygroscopic tape width is almost equal to the light-shielding tape width,
It is preferable in terms of appearance or weaving efficiency.
【００１７】本発明において、他の合成繊維としては、
延伸糸条として高強力の得られる熱可塑性樹脂を用いて
形成された繊維であって、熱可塑性樹脂として具体的に
は、ポリオレフィン、ポリエステル、ポリアミドなどが
挙げられるが、成形性、廉価性などの点でポリオレフィ
ンが好ましく、具体的には、高密度ポリエチレン、ポリ
プロピレンなどが好ましい。In the present invention, other synthetic fibers include:
Fiber formed using a thermoplastic resin obtained as high strength as a drawn yarn, specifically, as the thermoplastic resin, polyolefins, polyesters, polyamides and the like are mentioned, but moldability, low cost, etc. In this respect, polyolefin is preferable, and specifically, high-density polyethylene, polypropylene, and the like are preferable.
【００１８】上記合成繊維の糸条形態としては、モノフ
ィラメント、マルチフィラメント、フラットヤーン、ス
プリットヤーンなどいずれも使用できるが、成形性、生
産性、などの点からモノフィラメントが好ましい。ま
た、これら糸条の製造方法は、公知の技術を採用すれば
よく、モノフィラメントはダイスから押し出されたモノ
フィラメントを縦一軸延伸し、その後の熱処理を施すこ
とによって得ることができる。As the yarn form of the synthetic fiber, any of monofilaments, multifilaments, flat yarns, split yarns and the like can be used, but monofilaments are preferred in view of moldability, productivity and the like. In addition, a known technique may be adopted for the method of producing these yarns, and the monofilament can be obtained by uniaxially stretching a monofilament extruded from a die and then performing a heat treatment.
【００１９】上記合成繊維の繊度としては、１００〜１
０００デニール（以下、ｄと記載）が好ましく、２００
〜５００ｄがより好ましい。繊度が１００ｄ未満では本
発明の用途としての強力が不充分となり、１０００ｄを
超えると織成効率が劣るだけでなく、織布として柔軟性
が劣り好ましくない。The fineness of the synthetic fiber is 100 to 1
000 denier (hereinafter referred to as d) is preferred, and 200
~ 500d is more preferable. If the fineness is less than 100d, the strength of the use of the present invention is insufficient, and if it exceeds 1000d, not only the weaving efficiency is poor, but also the woven fabric is inferior in flexibility, which is not preferable.
【００２０】本発明において、上記遮光性テープおよび
吸湿性テープを経糸に用い、他の合成繊維を緯糸に用い
て織布を形成し、防霧性農業用ハウスの内張り材を形成
するものである。In the present invention, a woven fabric is formed by using the light-shielding tape and the moisture-absorbing tape for the warp and other synthetic fibers for the weft to form a lining material for a mist-proof agricultural house. .
【００２１】上記織布の織組織としては、平織、綾織、
絡み織など種々の織組織が採用できるが、広幅の遮光性
テープおよび吸湿性テープを経糸として用いたときに、
経糸は反転しないことが好ましい。また、織密度として
は、目的とする保温性の程度に依り異なり、密組織〜粗
目組織まで任意である。なお、このとき、経糸として他
の合成繊維を補強用として、遮光性テープおよび吸湿性
テープと交織しても差し支えない。The weaving structure of the woven fabric is plain weave, twill weave,
Various weaving structures such as entangled weaving can be adopted, but when a wide light-shielding tape and a hygroscopic tape are used as warps,
Preferably, the warp does not reverse. The weaving density varies depending on the desired degree of heat retention, and is arbitrary from a dense structure to a coarse structure. At this time, another synthetic fiber may be used as a warp for reinforcement and interwoven with the light-shielding tape and the hygroscopic tape.
【００２２】経糸として用いる遮光性テープと吸湿性テ
ープを配置する割合は、目的とする内張り材の遮光性お
よび吸湿性の程度に依り異なり任意の交織割合を取り得
るが、通常、打込本数の割合として、遮光性テープ／吸
湿性テープが５／１〜１／５の範囲が好ましい。The proportion of the light-shielding tape and the moisture-absorbing tape used as the warp varies depending on the degree of the light-shielding property and the moisture-absorbing property of the intended lining material, and can take an arbitrary weaving rate. As the ratio, the ratio of the light-shielding tape / the hygroscopic tape is preferably in the range of 5/1 to 1/5.
【００２３】上記のような構成になる農業用ハウスの内
張り材は、例えば、図３に示すように、ハウスの内張り
材として展張して使用するものである。このような内張
り材を展張することにより、所望により適宜の遮光性、
保温性を備え、かつ防霧性にすぐれており、農業用ハウ
スの内張り材として好適に用いられる。The lining material of the agricultural house having the above-described configuration is, for example, as shown in FIG. 3, used as a lining material for a house. By expanding such a lining material, if necessary, appropriate light shielding properties,
It has a heat retaining property and is excellent in fog resistance, and is suitably used as a lining material for an agricultural house.
【００２４】[0024]
【実施例】実施例１：遮光性テープ２として、フラッシ
ュ紡糸法により高密度ポリエチレンを繊維化して製造さ
れる坪量５８ｇ／ｍ２の不織布を選び、２本のガイドロ
ール間に７.２ｍｍ幅のディスタンスピースにカッタ刃
を取付けたスリッタを通過させて７.２ｍｍ幅の遮光性
テープ２を得た。この遮光性テープ２は、積分球を装着
したライカ社製波長別光学エネルギー分析装置により測
定した波長域４００〜７００ｎｍにおける光反射率は平
均９４％であった。EXAMPLES Example 1: A non-woven fabric having a basis weight of 58 g / m 2 produced by fiberizing high-density polyethylene by flash spinning was selected as the light-shielding tape 2, and a width of 7.2 mm was provided between two guide rolls. Was passed through a slitter having a cutter blade attached to the distance piece to obtain a light-shielding tape 2 having a width of 7.2 mm. This light-shielding tape 2 had an average light reflectance of 94% in a wavelength range of 400 to 700 nm measured by a wavelength-dependent optical energy analyzer manufactured by Leica equipped with an integrating sphere.
【００２５】吸湿性テープ３として、平均重合度１７０
０、けん化度９９.９％のポリビニルアルコールからな
る厚み４０μｍのフィルムを選び、２本のガイドロール
間に７.２ｍｍ幅のディスタンスピースにカッタ刃を取
付けたスリッタを通過させて７.２ｍｍ幅の吸湿性テー
プ３を得た。この吸湿性テープ３は、３０℃、６５％Ｒ
Ｈでの吸湿率が１５.５％であった。The hygroscopic tape 3 has an average degree of polymerization of 170
0, a film having a thickness of 40 μm made of polyvinyl alcohol having a saponification degree of 99.9% was selected, and a slitter having a cutter blade attached to a 7.2 mm-wide distance piece was passed between two guide rolls to form a 7.2 mm-wide film. A hygroscopic tape 3 was obtained. This hygroscopic tape 3 is 30 ° C., 65% R
The moisture absorption in H was 15.5%.
【００２６】合成繊維として、高密度ポリエチレン（Ｍ
ＦＲ＝１.０、密度＝０.９６１ｇ／１０ｍｉｎ.、Ｔｍ
＝１３２℃）を用いて、２７０ｄのモノフィラメント４
を形成した。このモノフィラメントの強力は５.４ｇ／
ｄであった。As synthetic fibers, high density polyethylene (M
FR = 1.0, density = 0.961 g / 10 min., Tm
= 132 ° C.) using a 270d monofilament 4
Was formed. The strength of this monofilament is 5.4 g /
d.
【００２７】上記遮光性テープ２本に対して、吸湿性テ
ープ１本の割合でテープ間隔を２.３ｍｍに配置して経
糸とし、上記高密度ポリエチレン製モノフィラメントを
緯糸として打込密度１０本／インチで織成し、図１示す
ような平織の織布を得た。With respect to the two light-shielding tapes, one hygroscopic tape is arranged at a ratio of 2.3 mm at a ratio of one hygroscopic tape to warp yarns, and the high-density polyethylene monofilament is used as a weft yarn for a driving density of 10 yarns / inch. To obtain a plain woven fabric as shown in FIG.
【００２８】上記織布をポリエチレンを被覆材とした農
業用ハウス５の内張り材１として、図３に示すように展
張して使用したところ、冬季において昼間は遮光性テー
プ２による遮光効果により、生育適温を超える温度上昇
を防止し、夜間は保温性にすぐれて温度が低下しすぎる
こともなく、また、早朝に急激な日光の照射によりハウ
ス内外の温度差が生じても、吸湿性テープ３の吸湿効果
により霧の発生も見ず、農業用ハウスの内張り材として
好適に使用された。As shown in FIG. 3, when the woven fabric was used as the lining material 1 of an agricultural house 5 made of polyethylene as a covering material, the woven fabric was used as a lining material. The temperature rise exceeding the appropriate temperature is prevented, the temperature is excellent at night and the temperature is not excessively lowered, and even if the temperature difference between the inside and outside of the house occurs due to rapid sunlight irradiation in the early morning, the hygroscopic tape 3 can be used. No fog was generated due to the moisture absorption effect, and it was suitably used as a lining material for an agricultural house.
【００２９】実施例２：実施例１で用いた遮光性テープ
２、吸湿性テープ３、高密度ポリエチレン製モノフィラ
メント４を用い、経糸として遮光性テープ２本に対し
て、吸湿性テープ１本の割合でテープ間間隔を３.０ｍ
ｍに配置したその間隔に高密度ポリエチレン製モノフィ
ラメント４を絡み織りで２対（４条）配置し、高密度ポ
リエチレン製モノフィラメント４を緯糸として打込密度
１０本／インチで織成し、図２示すような織布を得た。
この織布は、縦方向の強力も十分で、遮光性、保温性、
防霧性にすぐれ、農業用ハウスの内張り材１として好適
に使用された。Example 2: Using the light-shielding tape 2, the moisture-absorbing tape 3, and the high-density polyethylene monofilament 4 used in Example 1, the ratio of one moisture-absorbing tape to two light-shielding tapes as warp yarns 3.0m spacing between tapes
The two high-density polyethylene monofilaments 4 are arranged in a weaving manner at the interval of m, and the high-density polyethylene monofilaments 4 are woven as wefts at a driving density of 10 / inch, as shown in FIG. A woven fabric was obtained.
This woven fabric has sufficient strength in the vertical direction, light shielding, heat retention,
It has excellent anti-fog properties and was suitably used as a lining material 1 for an agricultural house.
【００３０】[0030]
【発明の効果】以上説明したように、本発明の防霧性農
業用ハウスの内張り材は、合成樹脂の長繊維フィラメン
トが高密度にかつ無方向に堆積接合された不織布を細幅
にスリットした遮光性テープおよび親水性素材からなる
吸湿性テープを経糸に用い、他の合成繊維を緯糸に用い
た織布からなる構成であって、ポリ塩化ビニル、ポリエ
チレン、エチレン−酢酸ビニル共重合体などの被覆材に
覆われたハウスの内部に展張することにより、所望によ
り適宜の遮光性、保温性を備え、かつ防霧性にすぐれて
おり、農業用ハウスの内張り材として好適に用いられ
る。As described above, the lining material of the mist-proof agricultural house of the present invention is obtained by slitting a nonwoven fabric in which synthetic resin long fiber filaments are deposited and bonded in a non-directional manner in a narrow width. Using a light-absorbing tape made of a light-shielding tape and a hydrophilic material for the warp, and composed of a woven fabric using other synthetic fibers for the weft, such as polyvinyl chloride, polyethylene, and ethylene-vinyl acetate copolymer. By extending the inside of the house covered with the covering material, it has appropriate light-shielding properties and heat-retaining properties as required, and is excellent in anti-fog properties, and is suitably used as a lining material for an agricultural house.
【図１】本発明に係る業用ハウスの内張り材の一例を示
す平面構成図である。FIG. 1 is a plan view showing an example of a lining material for an industrial house according to the present invention.
【図２】本発明に係る農業用ハウスの内張り材の他の例
であって、経糸に補強用モノフィラメントを絡み織で織
り込んだ説明図である。FIG. 2 is another example of the lining material of the agricultural house according to the present invention, which is an explanatory view in which a reinforcing monofilament is woven into a warp with a weaving weave.
【図３】本発明に係る農業用ハウスの内張り材をハウス
内に展張した一例を示す説明図である。FIG. 3 is an explanatory view showing an example in which the lining material of the agricultural house according to the present invention is extended in the house.
１ 農業用ハウスの内張り材 ２ 遮光性テープ ３ 吸湿性テープ ４ 高密度ポリエチレン製モノフィラメント ５ 農業用ハウス Reference Signs List 1 lining material for agricultural house 2 light-shielding tape 3 hygroscopic tape 4 monofilament made of high-density polyethylene 5 agricultural house
フロントページの続き (72)発明者 桜井 尚史 東京都千代田区神田須田町二丁目５番２号 丸和バイオケミカル株式会社内 Ｆターム(参考） 2B024 DA03 DB03 DB04 2B029 EB08 EC02 EC03 EC06 EC12 EC17 EC18 RA07 Continued on the front page (72) Inventor Naofumi Sakurai 2-5-2 Kandasudacho, Chiyoda-ku, Tokyo Maruwa Biochemical Co., Ltd. F-term (reference) 2B024 DA03 DB03 DB04 2B029 EB08 EC02 EC03 EC06 EC12 EC17 EC18 RA07
Claims (1)
にかつ無方向に堆積接合された不織布を細幅にスリット
した遮光性テープおよび３０℃、６５％ＲＨでの吸湿率
が５％以上の吸湿性テープを経糸に用い、他の合成繊維
を緯糸に用いた織布からなることを特徴とする農業用ハ
ウスの内張り材。1. A light-shielding tape obtained by slitting a nonwoven fabric in which synthetic resin long fiber filaments are deposited and bonded in a non-directional manner at a high density, and a moisture absorption rate of 5% or more at 30 ° C. and 65% RH. A lining material for an agricultural house, wherein the lining material is made of a woven fabric using a flexible tape as a warp and other synthetic fibers as a weft.